Environment-friendly high-efficiency composite polishing wax and production method thereof

Abstract

The invention relates to environment-friendly high-efficiency composite polishing wax for polishing metal and non-metal surfaces and a production method thereof. The composite polishing wax comprises the following raw materials by weight ratio: 65 to 75 of stearic acid, 8 to 12 of chromic oxide polishing powder, 10 to 25 of paraffin and 2 to 3.5 of lanolin. The method comprises the following steps: putting the paraffin and the stearic acid in proportional amounts into enamelware and heating to 90 DEG C 120 DEG C to melt the paraffin; adding the chromic oxide polishing powder, stirring uniformly and adding the lanolin under the stirring condition for a chemical modified complex reaction under the condition of 110 DEG C + / - 5 DEG C and the reaction time of 2h + / - 0.5h; and guiding discharge grouting to a precast die after the reaction and guiding the die into a water tank for cooling so as to be solidified into a block product. The product does not contain harmful solvent, is safe and convenient to manufacture, reduces energy consumption and does not pollute the environment, thereby being suitable for various polishing modes.

Description

Technical field:

[0001] The invention relates to an environment-friendly and high-efficiency composite polishing wax for polishing metal or non-metal surfaces and a production method thereof. Background technique:

[0002] Existing polishing agents (pastes) for metal or non-metal surfaces are mainly composed of paraffin, abrasives, solvents and additives, but solvent-based polishing agents have disadvantages such as unstable product quality and environmental pollution. Invention content:

[0003] The object of the present invention is to overcome the shortcomings of the existing solvent-based polishing agents, and provide an environmentally friendly and efficient composite polishing wax and a production method thereof.

[0004] The composite polishing wax of the present invention comprises the following raw materials in weight ratio: stearic acid 65-75; chromium oxide polishing powder 8-12; paraffin wax 10-25; lanolin 2-3.5.

[0005] The method for producing environment-f...

Examples

Embodiment Construction

[0008] Put 1.7kg of paraffin wax and 7.0kg of stearic acid into an enamel vessel, heat to 90-120°C, after the paraffin wax and stearic acid are completely melted, add 1.0kg of chromium oxide polishing powder, the particle size of chromium oxide polishing powder is: 0.5 μm~7μm, stir evenly, then add 0.3kg lanolin, keep warm for 120 minutes under stirring state, carry out chemical modification compound reaction, after the reaction, the grout is discharged into the prefabricated mold, the mold is introduced into the water tank to cool, and it becomes a block after solidification product.

[0009] The main technical parameters of the environmentally friendly and efficient composite polishing wax are:

[0010] pH value: 8-10;

[0011] Curing point: 50-60°C;

[0012] Cleaning power: artificial oil ≥ 90%;

[0013] Corrosion performance: 45# steel grade 0;

[0014] Gloss: 38-80 degrees;

[0015] Cutting force: 0.008-0.02N.

Technical field:

[0001] The invention relates to an environment-friendly and high-efficiency composite polishing wax for polishing metal or non-metal surfaces and a production method thereof. Background technique:

[0002] Existing polishing agents (pastes) for metal or non-metal surfaces are mainly composed of paraffin, abrasives, solvents and additives, but solvent-based polishing agents have disadvantages such as unstable product quality and environmental pollution. Invention content:

[0003] The object of the present invention is to overcome the shortcomings of the existing solvent-based polishing agents, and provide an environmentally friendly and efficient composite polishing wax and a production method thereof.

[0004] The composite polishing wax of the present invention comprises the following raw materials in weight ratio: stearic acid 65-75; chromium oxide polishing powder 8-12; paraffin wax 10-25; lanolin 2-3.5.

[0005] The method for producing environment-f...

Examples

Embodiment Construction

[0008] Put 1.7kg of paraffin wax and 7.0kg of stearic acid into an enamel vessel, heat to 90-120°C, after the paraffin wax and stearic acid are completely melted, add 1.0kg of chromium oxide polishing powder, the particle size of chromium oxide polishing powder is: 0.5 μm~7μm, stir evenly, then add 0.3kg lanolin, keep warm for 120 minutes under stirring state, carry out chemical modification compound reaction, after the reaction, the grout is discharged into the prefabricated mold, the mold is introduced into the water tank to cool, and it becomes a block after solidification product.

[0009] The main technical parameters of the environmentally friendly and efficient composite polishing wax are:

[0010] pH value: 8-10;

[0011] Curing point: 50-60°C;

[0012] Cleaning power: artificial oil ≥ 90%;

[0013] Corrosion performance: 45# steel grade 0;

[0014] Gloss: 38-80 degrees;

[0015] Cutting force: 0.008-0.02N.