Solid smoke cartridge and preparation method thereof

Abstract

The invention relates to a solid smoke cartridge and a preparation method thereof, the solid smoke cartridge is composed of a smoke cartridge core material and a smoke cartridge outer layer, the dosage of high-acyl gellan gum in the smoke cartridge core material is larger than that of low-acyl gellan gum, so that the hardness of the smoke cartridge core material is smaller than that of the smoke cartridge outer layer, insertion of a heating needle of a smoking set is facilitated, and the heating effect is improved; the smoke cartridge main material and the smoke cartridge auxiliary material are fully mixed, so that the tobacco particles in the smoke cartridge main material absorb sufficient smoke agent, the finally prepared solid smoke cartridge product has higher smoke amount, and a smoker can obtain more smoking times during smoking; two kinds of tobacco particles with different particle sizes and corresponding mesh numbers are selected, so that the air permeability of the cigarette cartridge is determined, the smoking resistance value during smoking is influenced, and meanwhile, the physical characteristics of the cigarette cartridge are influenced. According to the technical scheme, compared with common sheet type smoke cartridges, the solid smoke cartridge is prepared through extrusion forming equipment, the preparation technology is simple, the production process is low in consumption and efficient, and the requirements of enterprises for cost reduction and efficiency improvement are met.

Description

technical field

[0001] The invention belongs to the technical field of new tobacco, and in particular relates to a solid cigarette bomb and a preparation method. Background technique

[0002] In recent years, as the growth rate of traditional cigarette sales has slowed down, new tobacco products have gradually become the future development trend and have received extensive attention and research at home and abroad. Among them, heat-not-burn tobacco has become a research hotspot in the industry because of its use method and flavor characteristics closest to cigarette products. Compared with traditional cigarettes, heat-not-burn tobacco products have the advantages of low heating temperature, less tar, and less harmful to health. At the same time, they have fashionable appearance and excellent consumption experience. They perform well in foreign markets and are especially welcomed by young consumer groups. .

[0003] Existing heat-not-burn products have great similarities in...

Examples

Embodiment 1

[0037] A method for preparing a solid cartridge, comprising the following steps:

[0038] 1) Prepare the main material of the pod

[0039] The 20-mesh tobacco particles and the 60-mesh tobacco particles after pre-drying at 35°C for 2 minutes were uniformly mixed in a mass ratio of 6:4 to obtain the first material.

[0040] 2) Preparation of pod accessories

[0041] Preparation of fuming agent: Mixture A prepared by configuring glycerin and water in a mass ratio of 7:3;

[0042] Preparation of the first binder: the low-acyl gellan gum and the high-acyl gellan gum are made into a mixed gum B in a mass ratio of 4:6;

[0043] Preparation of the second binder: the low acyl gellan gum and the high acyl gellan gum are made into a mixed gum C according to the second set mass ratio of 5:5;

[0044] Mix the mixtures A and B at a mass ratio of 94:6, fully stir and let stand for 5 minutes to obtain the first pod auxiliary material; mix the mixtures A and C at a mass ratio of 94:6, full...

Embodiment 2

[0051] A method for preparing a solid cartridge, comprising the following steps:

[0052] 1) Prepare the main material of the pod

[0053] The 20-mesh tobacco powder and the 20-mesh microwave expanded stem powder after pre-drying at 55°C for 1 min are uniformly mixed in a mass ratio of 8:2 to obtain the first material.

[0054] 2) Preparation of pod accessories

[0055] Preparation of fuming agent: Mixture A prepared by configuring glycerin and water in a mass ratio of 3:7;

[0056] Preparation of the first binder: the low-acyl gellan gum and the high-acyl gellan gum are prepared into a mixed gum B in a mass ratio of 2:8;

[0057] Preparation of the second binder: low-acyl gellan gum and high-acyl gellan gum are made into mixed gum C at a fixed mass ratio of 4:6;

[0058]Mix mixture A and B at a mass ratio of 90:10, stir well, and then let stand for 5 minutes to obtain the first pod auxiliary material; mix mixture A and C at a mass ratio of 90:10, stir thoroughly, and then ...

Embodiment 3

[0065] A method for preparing a solid cartridge, comprising the following steps:

[0066] 1) Prepare the main material of the pod

[0067] The 20-mesh tobacco powder and the 60-mesh tobacco powder after pre-drying at 45°C for 2 minutes are uniformly mixed in a mass ratio of 7:3 to obtain the first material.

[0068] 2) Preparation of pod accessories

[0069] Preparation of fuming agent: Mixture A prepared by configuring glycerin and water in a mass ratio of 6:4;

[0070] Preparation of the first binder: the low-acyl gellan gum and the high-acyl gellan gum are made into a mixed gum B in a mass ratio of 4:6;

[0071] Preparation of the second binder: low-acyl gellan gum and high-acyl gellan gum are made into mixed gum C at a ratio of 6:4 by mass;

[0072] Mix the mixtures A and B at a mass ratio of 94:6, fully stir and let stand for 5 minutes to obtain the first pod auxiliary material; mix the mixtures A and C at a mass ratio of 94:6, fully stir and let stand Set it aside fo...

technical field

[0001] The invention belongs to the technical field of new tobacco, and in particular relates to a solid cigarette bomb and a preparation method. Background technique

[0002] In recent years, as the growth rate of traditional cigarette sales has slowed down, new tobacco products have gradually become the future development trend and have received extensive attention and research at home and abroad. Among them, heat-not-burn tobacco has become a research hotspot in the industry because of its use method and flavor characteristics closest to cigarette products. Compared with traditional cigarettes, heat-not-burn tobacco products have the advantages of low heating temperature, less tar, and less harmful to health. At the same time, they have fashionable appearance and excellent consumption experience. They perform well in foreign markets and are especially welcomed by young consumer groups. .

[0003] Existing heat-not-burn products have great similarities in...

Examples

Embodiment 1

[0037] A method for preparing a solid cartridge, comprising the following steps:

[0038] 1) Prepare the main material of the pod

[0039] The 20-mesh tobacco particles and the 60-mesh tobacco particles after pre-drying at 35°C for 2 minutes were uniformly mixed in a mass ratio of 6:4 to obtain the first material.

[0040] 2) Preparation of pod accessories

[0041] Preparation of fuming agent: Mixture A prepared by configuring glycerin and water in a mass ratio of 7:3;

[0042] Preparation of the first binder: the low-acyl gellan gum and the high-acyl gellan gum are made into a mixed gum B in a mass ratio of 4:6;

[0043] Preparation of the second binder: the low acyl gellan gum and the high acyl gellan gum are made into a mixed gum C according to the second set mass ratio of 5:5;

[0044] Mix the mixtures A and B at a mass ratio of 94:6, fully stir and let stand for 5 minutes to obtain the first pod auxiliary material; mix the mixtures A and C at a mass ratio of 94:6, full...

Embodiment 2

[0051] A method for preparing a solid cartridge, comprising the following steps:

[0052] 1) Prepare the main material of the pod

[0053] The 20-mesh tobacco powder and the 20-mesh microwave expanded stem powder after pre-drying at 55°C for 1 min are uniformly mixed in a mass ratio of 8:2 to obtain the first material.

[0054] 2) Preparation of pod accessories

[0055] Preparation of fuming agent: Mixture A prepared by configuring glycerin and water in a mass ratio of 3:7;

[0056] Preparation of the first binder: the low-acyl gellan gum and the high-acyl gellan gum are prepared into a mixed gum B in a mass ratio of 2:8;

[0057] Preparation of the second binder: low-acyl gellan gum and high-acyl gellan gum are made into mixed gum C at a fixed mass ratio of 4:6;

[0058]Mix mixture A and B at a mass ratio of 90:10, stir well, and then let stand for 5 minutes to obtain the first pod auxiliary material; mix mixture A and C at a mass ratio of 90:10, stir thoroughly, and then ...

Embodiment 3

[0065] A method for preparing a solid cartridge, comprising the following steps:

[0066] 1) Prepare the main material of the pod

[0067] The 20-mesh tobacco powder and the 60-mesh tobacco powder after pre-drying at 45°C for 2 minutes are uniformly mixed in a mass ratio of 7:3 to obtain the first material.

[0068] 2) Preparation of pod accessories

[0069] Preparation of fuming agent: Mixture A prepared by configuring glycerin and water in a mass ratio of 6:4;

[0070] Preparation of the first binder: the low-acyl gellan gum and the high-acyl gellan gum are made into a mixed gum B in a mass ratio of 4:6;

[0071] Preparation of the second binder: low-acyl gellan gum and high-acyl gellan gum are made into mixed gum C at a ratio of 6:4 by mass;

[0072] Mix the mixtures A and B at a mass ratio of 94:6, fully stir and let stand for 5 minutes to obtain the first pod auxiliary material; mix the mixtures A and C at a mass ratio of 94:6, fully stir and let stand Set it aside fo...