Multilayer container, method for producing the same, and method for producing recycled polyester

Abstract

A multi-layer container comprising: a polyester layer comprising a polyester resin (X), and a polyamide layer comprising a polyamide resin (Y) and a yellowing inhibitor (A), wherein the content of the polyamide resin (Y) is 0.05 to 7.0% by mass relative to the total amount of all the polyamide layers and all the polyester layers, and the yellowing inhibitor (A) is a dye, and the content of the yellowing inhibitor (A) is 400 to 800 ppm relative to the polyamide layer, and the L* value of the multi-layer container is 87.5 or more.

Description

Technical Field

[0001] The present invention relates to a multilayer container, a method for producing the same, and a method for producing recycled polyester. Background Art

[0002] Aromatic polyester resins obtained by using aromatic dicarboxylic acid compounds and aliphatic diol compounds as monomers have excellent features such as transparency, mechanical properties, melting stability, solvent resistance, fragrance retention, gas barrier properties, and recyclability. Therefore, aromatic polyester resins such as polyethylene terephthalate (PET) are widely used in various packaging materials such as films, sheets, and hollow containers. Polyester resins have high gas barrier properties, but they may not be sufficient for uses that require further gas barrier properties against oxygen, carbon dioxide gas, etc. Therefore, as a means of improving the gas barrier properties of polyester resins, the following operations have been performed: evaporating aluminum oxide and silicon oxide onto molded bodies and packaging containers formed by polyester resins; applying resins with high gas barrier properties to molded bodies and packaging containers formed by polyester resins and laminating, or performing melt mixing.

[0003] As gas barrier resins, polyamide resins such as nylon 6 and nylon 66, and ethylene-vinyl alcohol copolymers can be cited. Among polyamide resins, polyphenylene adipamide obtained by polymerizing a diamine component with benzylene diamine as the main component and a dicarboxylic acid component with adipic acid as the main component has excellent gas barrier properties. Polyphenylene adipamide not only has high gas barrier properties, but also has a glass transition temperature, a melting point, and a crystallinity similar to polyethylene terephthalate, which is a widely used polyester resin, and is therefore easily laminated and melt-mixed with polyester resins. Thus, polyphenylene adipamide is very suitable as a material for improving the gas barrier properties of polyester resins.

[0004] However, the yellowing caused by the thermal history of the polyester resin composition containing polyamide is more likely to be more serious than that of polyester alone. Therefore, yellowing occurs particularly in the recycling process of recycling the container and reusing the resin. This becomes a factor that reduces the commercial value of the packaging container, and therefore, research on suppressing yellowing is being conducted.

[0005] For example, Patent Document 1 discloses a multilayer container having a polyester resin composition layer containing a polyester resin and an amino compound having yellowing-suppressing ability, and a polyamide resin layer containing a polyamide resin, and a method for producing recycled polyester.

[0006] In addition, Patent Document 2 discloses a resin composition comprising: a polyester resin recycled from a polyester resin molded product, and a resin other than polyester, for the purpose of improving the reduction in transparency caused by yellowing of recycled PET and improving moldability, heat resistance, and strong elongation properties, and the resin composition also contains a specific amount of pigment.

[0007] Prior art literature

[0008] Patent Literature

[0009] Patent Document 1: International Publication No. 2017 / 057463

[0010] Patent Document 2: Japanese Patent Application Publication No. 2004-359914 Summary of the invention

[0011] Problem that the invention aims to solve

[0012] As described above, the yellowing of the polyester resin container containing polyamide is easy to be aggravated, and the recycled polyester obtained by recycling it will also have a yellow tint. As a method for eliminating the yellow, it is conceivable to add a colorant such as a blue pigment as an opposite color (complementary color) as listed in Patent Document 2.

[0013] In order to reduce yellowing, a colorant for suppressing yellowing needs to be added to the container used as the raw material of recycled polyester, but the blue color becomes conspicuous, the colorlessness is deteriorated, and the freedom of design is reduced.

[0014] On the other hand, in a polyester resin container containing polyamide, a multilayer container in which a layer containing a polyamide resin is laminated on a container formed of a polyester resin has excellent barrier properties because the polyamide resin layer functions as a barrier layer.

[0015] Therefore, there is a demand for a multi-layered container made of a polyester resin having a polyamide layer and having a yellow-effectively eliminated recycled polyester and less blue.

[0016] Therefore, an object of the present invention is to provide a method for producing a recycled polyester having low yellowness and excellent colorlessness, a multilayer container having little blue color and excellent colorlessness, and a recycled polyester having excellent colorlessness.

[0017] Solutions for solving problems

[0018] The present inventors have conducted intensive research in view of the above problems and have found that: a polyester layer and a polyamide layer containing a specific amount of a polyamide resin and a dye as a yellowing inhibitor, and L * The multi-layer container having a specific value can solve the above-mentioned problems, thus completing the present invention.

[0019] The present invention provides the following [1] to

[17] .

[0020] [1] A multilayer container comprising: a polyester layer comprising a polyester resin (X), and a polyamide layer comprising a polyamide resin (Y) and a yellowing inhibitor (A), wherein the content of the polyamide resin (Y) is 0.05 to 7.0% by mass relative to the total amount of the polyamide layer and the polyester layer, and the yellowing inhibitor (A) is a dye, and the content of the yellowing inhibitor (A) is 400 to 800 ppm relative to the polyamide layer, wherein the L * The value is above 87.5.

[0021] [2] The multilayer container according to [1], wherein the polyester resin (X) comprises structural units derived from dicarboxylic acid and structural units derived from diol, wherein the structural units derived from the dicarboxylic acid contain 80 mol % or more of structural units derived from terephthalic acid, and the structural units derived from the diol contain 80 mol % or more of structural units derived from ethylene glycol.

[0022] [3] The multilayer container according to [1] or [2], wherein the polyamide resin (Y) comprises a structural unit derived from a diamine and a structural unit derived from a dicarboxylic acid, wherein the structural unit derived from the diamine contains 80 mol % or more of a structural unit derived from xylenediamine, and the structural unit derived from the dicarboxylic acid contains 80 mol % or more of a structural unit derived from adipic acid.

[0023] [4] The multi-layer container according to any one of [1] to [3], wherein the yellowing inhibitor (A) is an anthraquinone-based dye.

[0024] [5] The multilayer container according to any one of [1] to [4], wherein the polyamide layer further contains a greening inhibitor (B).

[0025] [6] The multi-layer container according to [5], wherein the greening inhibitor (B) is at least one selected from the group consisting of anthraquinone dyes and azo dyes.

[0026] [7] The multi-layer container according to any one of [1] to [6], wherein the polyester layer contains substantially no reheat agent.

[0027] [8] The multi-layer container according to any one of [1] to [7], wherein the multi-layer container is a multi-layer hollow container.

[0028] [9] The multilayer container according to any one of [1] to [8], wherein the multilayer container has a 2-5 layer structure, and the outermost layer is a polyester layer.

[0029]

[10] The multilayer container according to any one of [1] to [9], wherein the multilayer container has a 3-5 layer structure, and the outermost layer and the innermost layer are polyester layers.

[0030]

[11] A method for producing a multi-layer container, comprising the following steps 1 to 3:

[0031] Step 1: a step of mixing a polyamide resin (Y) and a yellowing inhibitor (A) to prepare a polyamide resin mixture;

[0032] Step 2: a step of co-injection molding the polyamide resin mixture and the polyester resin composition containing the polyester resin (X) to obtain a multilayer preform;

[0033] Step 3: Blow molding the multi-layer preform.

[0034] The multi-layer container has:

[0035] a polyester layer comprising a polyester resin (X), and

[0036] a polyamide layer comprising a polyamide resin (Y) and a yellowing inhibitor (A),

[0037] The content of the polyamide resin (Y) is 0.05 to 7.0% by mass based on the total amount of the polyamide layer and the polyester layer.

[0038] Yellowing inhibitor (A) is a dye,

[0039] The content of the yellowing inhibitor (A) is 400 to 800 ppm relative to the polyamide layer.

[0040] The L of the multilayer container * The value is above 87.5.

[0041]

[12] The method for producing a multi-layer container according to

[11] , wherein in step 1, the pelletized polyamide resin (Y) and the yellowing inhibitor (A) are mixed at 230° C. or less.

[0042]

[13] The method for producing a multi-layer container according to

[11] or

[12] , wherein in step 1, a greening inhibitor (B) is further mixed.

[0043]

[14] The method for producing a multi-layer container according to

[13] , wherein in step 1, the polyamide resin or polyester resin, the yellowing inhibitor (A) and the greening inhibitor (B) are kneaded and then mixed with the polyamide resin (Y).

[0044]

[15] The method for producing a multi-layer container according to any one of

[11] to

[14] , wherein the yellowing inhibitor (A) is in the form of a powder, a dispersion or a solution.

[0045]

[16] A method for producing recycled polyester, comprising the step of recovering polyester from the multilayer container according to any one of [1] to

[10] .

[0046]

[17] The method for producing a regenerated polyester according to

[16] , wherein after the step of recovering the polyester, one or more steps selected from a crystallization step and a solid phase polymerization step are performed.

[0047] Effects of the Invention

[0048] According to the present invention, there can be provided a method for producing a recycled polyester having low yellowness and excellent colorlessness, a multilayer container having little blue color and excellent colorlessness, and a recycled polyester having excellent colorlessness. DETAILED DESCRIPTION

[0049] [Multi-layer container]

[0050] The multilayer container of the present invention comprises a polyester layer comprising a polyester resin (X), and a polyamide layer comprising a polyamide resin (Y) and a yellowing inhibitor (A), wherein the content of the polyamide resin (Y) is 0.05 to 7.0% by mass relative to the total amount of all the polyamide layers and all the polyester layers, and the yellowing inhibitor (A) is a dye, and the content of the yellowing inhibitor (A) is 400 to 800 ppm relative to the polyamide layer. * The value is above 87.5.

[0051] The “total weight of all polyamide layers and all polyester layers” means the total weight of all polyamide layers and all polyester layers constituting the multilayer container, and when there are multiple layers, it means the total weight of all of them.

[0052] <Polyester layer>

[0053] The polyester layer contains a polyester resin (X).

[0054] (Polyester resin (X))

[0055] The polyester resin (X) contained in the polyester layer is preferably a condensation polymer of dicarboxylic acid and diol, and preferably has a structural unit derived from dicarboxylic acid (dicarboxylic acid unit) and a structural unit derived from diol (diol unit).

[0056] Examples of the dicarboxylic acid unit include a structural unit derived from an aromatic dicarboxylic acid, a structural unit derived from an alicyclic dicarboxylic acid, and a structural unit derived from an aliphatic dicarboxylic acid. A structural unit derived from an aromatic dicarboxylic acid is preferred.

[0057] Examples of the aromatic dicarboxylic acid include terephthalic acid, isophthalic acid, phthalic acid, biphenyl dicarboxylic acid, diphenyl ether dicarboxylic acid, diphenyl sulfone dicarboxylic acid, diphenyl ketone dicarboxylic acid, 2,6-naphthalene dicarboxylic acid, 1,4-naphthalene dicarboxylic acid, and 2,7-naphthalene dicarboxylic acid. From the viewpoint of cost and ease of production, terephthalic acid, isophthalic acid, phthalic acid, naphthalene dicarboxylic acid, and 4,4′-biphenyl dicarboxylic acid are preferred, and terephthalic acid, isophthalic acid, and naphthalene dicarboxylic acid are more preferred. From the viewpoint of moldability, terephthalic acid and isophthalic acid are further preferred, and terephthalic acid is still more preferred.

[0058] When the multilayer container of the present invention is reused, it may be melt-kneaded with a conventional single-layer container formed of a polyester resin. By having a unit derived from terephthalic acid as a dicarboxylic acid unit, the multilayer container of the present invention has good compatibility with conventional single-layer containers, and good recyclability can be obtained.

[0059] As the aromatic dicarboxylic acid, sulfophthalic acid and sulfophthalic acid metal salts can be used. The sulfophthalic acid metal salt is a metal salt of sulfophthalic acid, and examples of the metal atom include alkali metals and alkaline earth metals.

[0060] Examples of the alicyclic dicarboxylic acid include cyclohexanedicarboxylic acid, norbornenedicarboxylic acid, and tricyclodecanedicarboxylic acid.

[0061] Examples of the aliphatic dicarboxylic acid include malonic acid, succinic acid, adipic acid, azelaic acid, and sebacic acid.

[0062] Examples of the diol unit include a structural unit derived from an aliphatic diol, a structural unit derived from an alicyclic diol, and a structural unit derived from an aromatic diol. A structural unit derived from an aliphatic diol is preferred.

[0063] Examples of the aliphatic diol include ethylene glycol, 2-butene-1,4-diol, trimethylene glycol, tetramethylene glycol, hexamethylene glycol, neopentyl glycol, methylpentanediol, and diethylene glycol. Among them, ethylene glycol is preferred, and ethylene glycol is more preferred.

[0064] Examples of the alicyclic diol include cyclohexanedimethanol, isosorbide, spirodiol, 2,2,4,4-tetramethyl-1,3-cyclobutanediol, norbornene dimethanol, and tricyclodecanedimethanol.

[0065] Examples of the aromatic diol include bisphenol compounds and hydroquinone compounds.

[0066] The polyester resin (X) may have a structural unit derived from a hydroxycarboxylic acid.

[0067] Examples of the hydroxycarboxylic acid include aliphatic hydroxycarboxylic acids, alicyclic hydroxycarboxylic acids, and aromatic hydroxycarboxylic acids.

[0068] Examples of the aliphatic hydroxycarboxylic acid include 10-hydroxyoctadecanoic acid, lactic acid, hydroxyacrylic acid, 2-hydroxy-2-methylpropionic acid, and hydroxybutyric acid.

[0069] Examples of the alicyclic hydroxycarboxylic acid include hydroxymethylcyclohexanecarboxylic acid, hydroxymethylnorbornenecarboxylic acid, and hydroxymethyltricyclodecanecarboxylic acid.

[0070] Examples of the aromatic hydroxycarboxylic acid include hydroxybenzoic acid, hydroxymethylbenzoic acid, hydroxynaphthoic acid, 3-(hydroxyphenyl)propionic acid, hydroxyphenylacetic acid, and 3-hydroxy-3-phenylpropionic acid.

[0071] The polyester resin (X) may have a structural unit derived from a monofunctional compound and a structural unit derived from a polyfunctional compound.

[0072] Examples of the monofunctional compound include monocarboxylic acids and monoalcohols. Specifically, examples include aromatic monocarboxylic acids, aliphatic monocarboxylic acids, aromatic monoalcohols, aliphatic monoalcohols, and alicyclic monoalcohols.

[0073] Examples of the polyfunctional compound include aromatic polycarboxylic acids, alicyclic polycarboxylic acids, aliphatic polyols, alicyclic polyols, and esters thereof.

[0074] The polyester resin (X) preferably has a dicarboxylic acid-derived structural unit and a diol-derived structural unit, wherein the dicarboxylic acid-derived structural unit contains a terephthalic acid-derived structural unit, and the diol-derived structural unit contains an ethylene glycol-derived structural unit. More preferably, the polyester resin (X) has a dicarboxylic acid-derived structural unit and a diol-derived structural unit, wherein the dicarboxylic acid-derived structural unit contains 80 mol% or more of a terephthalic acid-derived structural unit, and the diol-derived structural unit contains 80 mol% or more of an ethylene glycol-derived structural unit. Further preferably, the polyester resin (X) has a dicarboxylic acid-derived structural unit and a diol-derived structural unit, wherein the dicarboxylic acid-derived structural unit contains 90 mol% or more of a terephthalic acid-derived structural unit, and the diol-derived structural unit contains 90 mol% or more of an ethylene glycol-derived structural unit. Further preferably, the polyester resin (X) has a dicarboxylic acid-derived structural unit and a diol-derived structural unit, wherein the dicarboxylic acid-derived structural unit contains 98 mol% or more of a terephthalic acid-derived structural unit, and the diol-derived structural unit contains substantially 100 mol% of an ethylene glycol-derived structural unit.

[0075] Specific examples of the polyester resin (X) include polyethylene terephthalate (PET).

[0076] Polyethylene terephthalate (PET) may contain structural units derived from aromatic dicarboxylic acids other than terephthalic acid. As aromatic dicarboxylic acids other than terephthalic acid, at least one selected from isophthalic acid, phthalic acid, naphthalene dicarboxylic acid, and 4,4'-biphenyl dicarboxylic acid is preferred. These are low in cost, and copolyester resins containing these are easy to manufacture.

[0077] Among them, isophthalic acid and naphthalene dicarboxylic acid are preferred, and isophthalic acid is more preferred. Polyethylene terephthalate containing a structural unit derived from isophthalic acid is excellent in terms of excellent moldability and slow crystallization rate to prevent whitening of molded products. In addition, polyethylene terephthalate containing a structural unit derived from naphthalene dicarboxylic acid increases the glass transition point of the resin, improves heat resistance, and absorbs ultraviolet rays. Therefore, it is suitable for manufacturing multilayer containers that require resistance to ultraviolet rays. It should be noted that from the perspective of easy manufacturing and high economic efficiency, 2,6-naphthalene dicarboxylic acid components are preferred as naphthalene dicarboxylic acid.

[0078] When polyethylene terephthalate contains structural units derived from aromatic dicarboxylic acids other than terephthalic acid, the proportion of the structural units derived from aromatic dicarboxylic acids other than terephthalic acid is preferably 1 to 20 mol %, more preferably 1 to 10 mol %, and even more preferably 1 to 5 mol % of the dicarboxylic acid units.

[0079] In addition, the polyester resin (X) may be used alone or in combination of two or more kinds of resins.

[0080] The polyester resin (X) can be produced by a known method such as a direct esterification method or an ester exchange method.

[0081] The intrinsic viscosity of the polyester resin (X) is preferably 0.5 to 2.0 dL / g, more preferably 0.6 to 1.5 dL / g. When the intrinsic viscosity is at least 0.5 dL / g, the mechanical properties of the container will be excellent.

[0082] The intrinsic viscosity was measured by dissolving the polyester resin in a phenol / 1,1,2,2-tetrachloroethane (6 / 4 mass ratio) mixed solvent to prepare 0.2 g / dL, 0.4 g / dL, and 0.6 g / dL solutions, and measuring the solutions at 25° C. using an automatic viscosity meter (Viscotek, manufactured by Malvern).

[0083] (Other ingredients)

[0084] The polyester layer may contain other components, such as heat stabilizers, light stabilizers, moisture proof agents, water-proofing agents, lubricants, and spreading agents.

[0085] The polyester layer may contain resins other than the polyester resin (X) as a main component within a range not impairing the effects of the present invention. The content of the polyester resin (X) is preferably 80 to 100% by mass, more preferably 90 to 100% by mass, relative to the total resin amount of the polyester layer.

[0086] On the other hand, the polyester layer preferably contains substantially no reheat agent. Specifically, even if the polyester layer contains a reheat agent, the content of the reheat agent relative to the polyester layer is preferably 5 ppm or less, more preferably 3 ppm or less, further preferably 1 ppm or less, further preferably 0 ppm, and further preferably contains no reheat agent.

[0087] The reheating agent absorbs infrared rays during molding and emits heat to increase the heating rate and manufacturing speed. It is sometimes called an infrared absorber or a heat stability additive. Examples of the reheating agent include carbon black and the like.

[0088] <Polyamide layer>

[0089] The polyamide layer contains a polyamide resin (Y) and a yellowing inhibitor (A). The content of the polyamide resin (Y) contained in the polyamide layer is 0.05 to 7.0% by mass relative to the total amount of the entire polyamide layer and the entire polyester layer, and the content of the yellowing inhibitor (A) is 400 to 800 ppm relative to the polyamide layer.

[0090] By providing the polyamide layer, the multilayer container has high gas barrier properties. Therefore, it is possible to prevent oxygen from invading from the outside and to suppress the volatilization of carbon dioxide in carbonated beverages to the outside air. In addition, by using the polyamide layer, the moldability is improved and the polyester resin can be easily separated and recovered.

[0091] Furthermore, it is believed that by including the yellowing inhibitor (A) in the nitrogen-containing polyamide layer that is likely to cause yellowing of the recycled resin, yellowing can be effectively inhibited. In particular, since the yellowing inhibitor corresponding to the amount of the remaining polyamide resin remains in the polyester resin recovered during recycling, it is believed that a suitable amount of the yellowing inhibitor can be included in the recycled polyester resin to obtain a colorless recycled polyester.

[0092] (Polyamide resin (Y))

[0093] Examples of the polyamide resin (Y) include xylylene-containing polyamide resins, nylon 6, nylon 66, nylon 666, nylon 610, nylon 11, nylon 12, and mixtures thereof. Among them, xylylene-containing polyamide resins are preferred from the viewpoints of improving gas barrier properties and being easily separated from the polyester layer during recycling. The xylylene-containing polyamide resin is preferably a polyamide resin containing a structural unit derived from xylylenediamine.

[0094] The xylylene-containing polyamide resin is obtained by polycondensing a diamine including xylylenediamine and a dicarboxylic acid, and has a structural unit derived from xylylenediamine and a structural unit derived from dicarboxylic acid. The xylylene-containing polyamide resin preferably contains 50 mol% or more of the structural unit derived from diamine (diamine unit), more preferably 70 mol% or more, further preferably 80 to 100 mol%, and further preferably 90 to 100 mol%.

[0095] The xylylenediamine is preferably m-xylylenediamine, p-xylylenediamine, or both thereof, and m-xylylenediamine is more preferred. Furthermore, the diamine unit constituting the xylylenediamine-containing polyamide resin preferably contains 50 mol% or more of a structural unit derived from m-xylylenediamine, more preferably 70 mol% or more, further preferably 80 to 100 mol%, and further preferably 90 to 100 mol%. By making the structural unit derived from m-xylylenediamine in the diamine unit within the above range, the gas barrier properties of the polyamide resin become better.

[0096] The diamine unit in the xylylenediamine-containing polyamide resin may be composed only of a structural unit derived from xylylenediamine, or may contain a structural unit derived from a diamine other than xylylenediamine. Here, examples of diamines other than xylylenediamine include linear or branched aliphatic diamines such as ethylenediamine, tetramethylenediamine, pentamethylenediamine, 2-methylpentamethylenediamine, hexamethylenediamine, heptamethylenediamine, octamethylenediamine, nonamethylenediamine, decamethylenediamine, dodecamethylenediamine, 2,2,4-trimethyl-hexamethylenediamine, and 2,4,4-trimethyl-hexamethylenediamine; alicyclic diamines such as 1,3-bis(aminomethyl)cyclohexane, 1,4-bis(aminomethyl)cyclohexane, 1,3-diaminocyclohexane, 1,4-diaminocyclohexane, bis(4-aminocyclohexyl)methane, 2,2-bis(4-aminocyclohexyl)propane, bis(aminomethyl)decahydronaphthalene, and bis(aminomethyl)tricyclodecane; and diamines having an aromatic ring such as bis(4-aminophenyl)ether, p-phenylenediamine, and bis(aminomethyl)naphthalene.

[0097] In the xylene-containing polyamide resin, examples of compounds that can constitute the dicarboxylic acid unit include α,ω-straight-chain aliphatic dicarboxylic acids having 4 to 20 carbon atoms, such as succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, undecanedioic acid, and dodecanedioic acid; alicyclic dicarboxylic acids such as 1,4-cyclohexanedicarboxylic acid; other aliphatic dicarboxylic acids such as dimer acid; aromatic dicarboxylic acids such as terephthalic acid, isophthalic acid, phthalic acid, xylene dicarboxylic acid, and naphthalene dicarboxylic acid. Preferred are α,ω-straight-chain aliphatic dicarboxylic acids having 4 to 20 carbon atoms, more preferred are adipic acid and sebacic acid, and from the viewpoint of achieving good barrier properties, adipic acid is further preferred.

[0098] The xylylene group-containing polyamide resin preferably contains 50 mol% or more, more preferably 70 mol% or more, further preferably 80 to 100 mol%, and further preferably 90 to 100 mol% of adipic acid-derived structural units among structural units derived from dicarboxylic acid (dicarboxylic acid units).

[0099] That is, the polyamide resin (Y) preferably comprises a diamine-derived structural unit and a dicarboxylic acid-derived structural unit, wherein the diamine-derived structural unit contains 50 mol% or more of a xylylenediamine-derived structural unit, and the dicarboxylic acid-derived structural unit contains 50 mol% or more of adipic acid-derived structural unit; more preferably comprises a diamine-derived structural unit and a dicarboxylic acid-derived structural unit, wherein the diamine-derived structural unit contains 80 mol% or more of a xylylenediamine-derived structural unit, and the dicarboxylic acid-derived structural unit contains 80 mol% or more of adipic acid-derived structural unit; further preferably comprises a diamine-derived structural unit and a dicarboxylic acid-derived structural unit, wherein the diamine-derived structural unit contains 90 mol% or more of a xylylenediamine-derived structural unit, and the dicarboxylic acid-derived structural unit contains 90 mol% or more of adipic acid-derived structural unit.

[0100] As the xylylenediamine, meta-xylylenediamine is preferred.

[0101] In addition, as the remaining dicarboxylic acid unit excluding adipic acid, a structural unit derived from an α,ω-linear aliphatic dicarboxylic acid having 4 to 20 carbon atoms is preferred.

[0102] In addition, as a preferred xylylene-containing polyamide resin, there can be exemplified a polyamide resin in which 70 mol% or more of the diamine units are structural units derived from xylylenediamine (preferably m-xylylenediamine), 70 to 99 mol% of the dicarboxylic acid units are structural units derived from adipic acid, and 1 to 30 mol% are structural units derived from isophthalic acid. The polyamide resin is preferably a polyamide resin in which 80 mol% or more of the diamine units are structural units derived from m-xylylenediamine (preferably m-xylylenediamine), 80 to 99 mol% of the dicarboxylic acid units are structural units derived from adipic acid, and 1 to 20 mol% are structural units derived from isophthalic acid, and more preferably a polyamide resin in which 90 mol% or more of the diamine units are structural units derived from m-xylylenediamine (preferably m-xylylenediamine), 80 to 99 mol% of the dicarboxylic acid units are structural units derived from adipic acid, and 1 to 20 mol% are structural units derived from isophthalic acid.

[0103] By adding an isophthalic acid unit as a dicarboxylic acid unit, the melting point is lowered and the molding temperature can be lowered, so that thermal degradation during molding can be suppressed. In addition, the stretching moldability is improved by delaying the crystallization time.

[0104] In addition to the aforementioned diamines and dicarboxylic acids, as components constituting the xylene-containing polyamide resin, lactams such as ε-caprolactam and laurolactam; aliphatic aminocarboxylic acids such as aminocaproic acid and aminoundecanoic acid; and aromatic aminocarboxylic acids such as p-aminomethylbenzoic acid may be used as copolymer components within the range not impairing the effects of the present invention.

[0105] The xylylene-containing polyamide resin is preferably produced by a polycondensation reaction in a molten state (hereinafter, sometimes referred to as "melt polycondensation"). For example, it is preferably produced by the following method: a nylon salt composed of a diamine and a dicarboxylic acid is heated by a pressure method in the presence of water, and polymerized in a molten state while removing the water. In addition, it can also be produced by directly adding a diamine to a dicarboxylic acid in a molten state and performing a polycondensation under normal pressure. In this case, in order to keep the reaction system in a uniform liquid state, it is preferred that the diamine is continuously added to the dicarboxylic acid, during which the reaction system is heated in a manner that the reaction temperature is not lower than the melting point of the generated oligoamide and polyamide, and the polycondensation is performed. In addition, the xylylene-containing polyamide can be further solid-phase polymerized as needed to increase the molecular weight.

[0106] The xylylene group-containing polyamide resin is preferably polycondensed in the presence of a phosphorus atom-containing compound. When the xylylene group-containing polyamide resin is polycondensed in the presence of a phosphorus atom-containing compound, processing stability during melt molding can be improved, and coloration can be easily suppressed.

[0107] As the phosphorus atom-containing compound, a hypophosphorous acid compound and a phosphorous acid compound are preferred, and a hypophosphorous acid compound is more preferred.

[0108] The phosphorus atom-containing compound is preferably an organic metal salt, and among them, an alkali metal salt is more preferred.

[0109] From the viewpoint of promoting the polymerization reaction and preventing coloration, examples of the hypophosphorous acid compound include hypophosphorous acid, metal hypophosphorous acid salts, metal phenylphosphite salts, ethyl hypophosphite, dimethylphosphinic acid, phenylmethylphosphinic acid, phenylphosphite, and ethyl phenylphosphite, and metal hypophosphite is preferred.

[0110] Examples of the metal hypophosphite salt include sodium hypophosphite, potassium hypophosphite, lithium hypophosphite and calcium hypophosphite, and sodium hypophosphite is more preferred.

[0111] Examples of the phenylphosphite metal salt include sodium phenylphosphite, potassium phenylphosphite and lithium phenylphosphite.

[0112] Examples of the phosphorous acid compound include phosphorous acid, pyrophosphorous acid, phosphorous acid metal salts, phenylphosphonic acid metal salts, triethyl phosphite, triphenyl phosphite, ethylphosphonic acid, phenylphosphonic acid, and diethyl phenylphosphonate.

[0113] Examples of the phosphorous acid metal salt include sodium hydrogen phosphite, sodium phosphite, potassium phosphite, and calcium phosphite.

[0114] Examples of the phenylphosphonic acid metal salt include sodium ethylphosphonate, potassium ethylphosphonate, sodium phenylphosphonate, potassium phenylphosphonate, lithium phenylphosphonate and the like.

[0115] The phosphorus atom-containing compound may be used alone or in combination of two or more.

[0116] In addition, the polycondensation of the xylylene-containing polyamide resin is preferably carried out in the presence of a phosphorus atom-containing compound and an alkali metal compound. If the amount of the phosphorus atom-containing compound is too large, there is a concern that the polyamide resin may gel. Therefore, from the viewpoint of adjusting the amidation reaction rate, it is preferred to allow the alkali metal compound to coexist.

[0117] Examples of the alkali metal compound include alkali metal hydroxides and alkali metal acetates. Examples of the alkali metal hydroxides include lithium hydroxide, sodium hydroxide, potassium hydroxide, rubidium hydroxide, and cesium hydroxide. Examples of the alkali metal acetates include lithium acetate, sodium acetate, potassium acetate, rubidium acetate, and cesium acetate.

[0118] When an alkali metal compound is used for polycondensation of a polyamide resin, the amount of the alkali metal compound used is preferably 0.5 to 1, more preferably 0.55 to 0.95, and even more preferably 0.6 to 0.9, from the viewpoint of suppressing the formation of gel, in which the value obtained by dividing the number of moles of the alkali metal compound by the number of moles of the phosphorus atom-containing compound is.

[0119] The number average molecular weight of the polyamide resin can be appropriately selected depending on the application and molding method of the multilayer container, and is preferably 10,000 to 60,000, more preferably 11,000 to 50,000, from the viewpoint of moldability and strength of the multilayer container.

[0120] In addition, the number average molecular weight of the polyamide resin is calculated by the following formula (X).

[0121] Number average molecular weight = 2 × 1,000,000 / ([COOH]+[NH 2 ])…(X)

[0122] (In formula (X), [COOH] represents the terminal carboxyl group concentration (μmol / g) in the polyamide resin, [NH 2 ] represents the terminal amino group concentration in the polyamide resin (μmol / g).

[0123] Here, the terminal carboxyl group concentration used is a value calculated by neutralizing and titrating a solution obtained by dissolving polyamide in benzyl alcohol with an aqueous sodium hydroxide solution.

[0124] In the present invention, from the viewpoint of suppressing yellowing of the regenerated polyester, the terminal amino group concentration of the polyamide resin (Y) is preferably 50 μmol / g or less, more preferably 45 μmol / g or less, further preferably 40 μmol / g or less, further preferably 30 μmol / g or less, further preferably 20 μmol / g or less.

[0125] The terminal amino group concentration of the polyamide resin (Y) is determined as follows: the polyamide resin is accurately weighed, and dissolved in a phenol / ethanol = 4 / 1 volumetric solution at 20-30°C with stirring. After it is completely dissolved, the inner wall of the container is rinsed with 5 mL of methanol while stirring, and the terminal amino group concentration is determined by neutralization titration with a 0.01 mol / L hydrochloric acid aqueous solution.

[0126] The method for adjusting the terminal amino group concentration of the polyamide resin (Y) is not particularly limited, and the terminal amino group concentration can be suppressed to a low level by adjusting the charging ratio (molar ratio) of diamine and dicarboxylic acid to carry out polycondensation reaction, charging a monocarboxylic acid that blocks the amino group together with the diamine and dicarboxylic acid to carry out polycondensation reaction, carrying out a polycondensation reaction and then reacting with a carboxylic acid that blocks the amino group, etc.

[0127] The content of the polyamide resin (Y) contained in the polyamide layer is 0.05 to 7.0% by mass relative to the total amount of all polyamide layers and all polyester layers, and is preferably 0.5 to 6.0% by mass, more preferably 1.0 to 5.0% by mass, and further preferably 1.5 to 4.5% by mass from the viewpoint of gas barrier properties and suppression of yellowing of the recycled polyester.

[0128] (Yellowing Inhibitor (A))

[0129] The polyamide layer of the multi-layer container contains the yellowing inhibitor (A) in an amount of 400 to 800 ppm based on the polyamide layer.

[0130] It should be noted that "ppm" in the present invention means parts per million by mass.

[0131] From the viewpoint of effectively suppressing yellowing of the recycled polyester and suppressing blue color of the multilayer container, the content of the yellowing inhibitor (A) is 400 to 800 ppm, preferably 500 to 700 ppm, based on the polyamide layer.

[0132] The content of the yellowing inhibitor (A) is preferably 1 to 20 ppm, more preferably 7 to 19 ppm, further preferably 10 to 18 ppm, and further preferably 13 to 17 ppm, based on the total amount of all polyamide layers and all polyester layers.

[0133] The yellowing inhibitor (A) is a dye, preferably a blue dye.

[0134] By using a dye, a regenerated polyester having excellent transparency can be obtained.

[0135] Examples of dyes used as the yellowing inhibitor (A) include anthraquinone dyes, pyrazolone dyes, coumarin dyes, perinone dyes, methine dyes, and quinophthalone dyes, and anthraquinone dyes are preferred.

[0136] Examples of the anthraquinone dye include anthraquinone dyes in which the hydrogen atoms of the aromatic ring are substituted with aromatic amines, aliphatic amines, hydroxyl groups and halogens, and anthraquinone dyes in which the hydrogen atoms of the aromatic ring are substituted with aromatic amines are preferred.

[0137] By using an anthraquinone-based dye, yellowing of the regenerated polyester obtained from the multi-layer container of the present invention can be suppressed in an extremely small amount.

[0138] As the anthraquinone-based dye, anthraquinone-based blue dye is more preferred.

[0139] As the anthraquinone dye, a compound represented by the following formula (1) is preferred.

[0140]

[0141] (In formula (1), n ​​represents the number of R, and two n are each independently 1 to 5. R is each independently an alkyl group having 1 to 4 carbon atoms. Two X are each independently a hydrogen atom or a hydroxyl group.)

[0142] In formula (1), n ​​is 1 to 5, preferably 2 to 5, and more preferably 2 to 3. By setting n to the above range, yellowing (Δb * R each independently represents an alkyl group having 1 to 4 carbon atoms, preferably at least one selected from the group consisting of a methyl group and an ethyl group. R preferably replaces at least the ortho position or the para position relative to the amino group, more preferably replaces at least the ortho position, and further preferably replaces the ortho position and the para position. The two Xs each independently represent a hydrogen atom or a hydroxyl group, preferably a hydrogen atom.

[0143] Specific compounds represented by formula (1) include 1,4-bis[(2-ethyl-6-methylphenyl)amino]anthraquinone, Solvent Blue 97, Solvent Blue 104, Solvent Green 3, and Solvent Green 28, with 1,4-bis[(2-ethyl-6-methylphenyl)amino]anthraquinone, Solvent Blue 97, and Solvent Blue 104 being preferred.

[0144] When the yellowing inhibitor (A) is an anthraquinone dye, the content of the anthraquinone dye as the yellowing inhibitor (A) is 400 to 800 ppm, preferably 500 to 700 ppm relative to the polyamide layer, from the viewpoint of effectively suppressing the yellowing of the regenerated polyester and suppressing the blue color of the multilayer container.

[0145] When the yellowing inhibitor (A) is an anthraquinone dye, the content of the anthraquinone dye as the yellowing inhibitor (A) is preferably 1 to 20 ppm, more preferably 7 to 19 ppm, further preferably 10 to 18 ppm, and further preferably 13 to 17 ppm relative to the total amount of all polyamide layers and all polyester layers.

[0146] The yellowing inhibitor (A) may be used alone or in combination of two or more.

[0147] Commercially available products of the yellowing inhibitor (A) include Macrolex Blue RR Gran (anthraquinone dye, manufactured by LANXESS), Macrolex Blue 3R 1,4-bis[(2-ethyl-6-methylphenyl)amino]anthraquinone, anthraquinone dye, manufactured by LANXESS), and Oracet Blue 690 (anthraquinone dye, manufactured by BASF).

[0148] (Greening Inhibitor (B))

[0149] The polyamide layer of the multilayer container preferably comprises a greening inhibitor (B).

[0150] The greening inhibitor (B) is used to inhibit the greening of the recycled polyester formed by recycling the multilayer container of the present invention. * Direction green.

[0151] The content of the greening inhibitor (B) is 1 to 30 ppm relative to the total amount of all polyamide layers and all polyester layers, preferably 1.5 to 25 ppm from the viewpoint of effectively inhibiting the greening of the recycled polyester, more preferably 2 to 22 ppm, and further preferably 3 to 20 ppm from the viewpoint of mixing and molding properties during production.

[0152] It should be noted that "ppm" in the present invention means parts per million by mass.

[0153] From the viewpoint of effectively suppressing greening of the regenerated polyester, the content of the greening inhibitor (B) in the polyamide layer is preferably 0.001 to 1.0 mass %, more preferably 0.005 to 0.5 mass %, further preferably 0.008 to 0.1 mass %, and further preferably 0.01 to 0.08 mass %.

[0154] The mass ratio [(A) / (B)] of the yellowing inhibitor (A) to the greening inhibitor (B) in the polyamide layer of the multi-layer container of the present invention is preferably 20 / 80 to 80 / 20, more preferably 30 / 70 to 70 / 30, and even more preferably 40 / 60 to 60 / 40.

[0155] When the mass ratio is within this range, the color tone of the recycled polyester obtained after recycling is less changed, and in particular, a polyester excellent in colorlessness can be obtained.

[0156] The greening inhibitor (B) is preferably at least one selected from the group consisting of dyes and pigments, and is more preferably a dye from the viewpoint of transparency.

[0157] Among dyes, the dye used as the greening inhibitor (B) is preferably at least one selected from the group consisting of anthraquinone dyes and azo dyes, and anthraquinone dyes are more preferred from the viewpoint of heat resistance.

[0158] The greening inhibitor (B) is preferably a red dye, more preferably at least one selected from the group consisting of anthraquinone red dyes and azo red dyes, and even more preferably anthraquinone red dyes from the viewpoint of heat resistance.

[0159] By using an anthraquinone-based red dye and an azo-based red dye, greening of the regenerated polyester obtained from the multi-layer container of the present invention can be suppressed in an extremely small amount.

[0160] As the anthraquinone-based dye, a compound represented by the following formula (2) is preferred.

[0161]

[0162] (In formula (2), two Ys each independently represent a hydrogen atom or a group represented by formula (2a), and two Xs each independently represent a hydrogen atom or a hydroxyl group. Among them, at least one Y is a group represented by formula (2a).

[0163] In formula (2a), R represents an alkyl group having 1 to 4 carbon atoms.

[0164] In formula (2), two Ys each independently represent a hydrogen atom or a group represented by formula (2a), but at least one Y is a group represented by formula (2a), and preferably one Y is a group represented by formula (2a) and the remaining Ys are hydrogen atoms.

[0165] Two Xs each independently represent a hydrogen atom or a hydroxyl group, but when one Y is a group represented by formula (2a), X bonded to the same aromatic ring is preferably a hydroxyl group.

[0166] In formula (2a), R represents an alkyl group having 1 to 4 carbon atoms, preferably at least one selected from the group consisting of a methyl group and an ethyl group. It should be noted that when two Ys are groups represented by formula (2a), the Rs in the two groups represented by formula (2a) may be the same or different. Preferably, R is substituted in the para position relative to the amino group.

[0167] Specific examples of the compound represented by formula (2) include Solvent Violet 36 and Solvent Violet 13, and Solvent Violet 36 is preferred.

[0168] When the greening inhibitor (B) is an anthraquinone dye, the content of the anthraquinone dye as the greening inhibitor (B) in the polyamide layer is preferably 0.001 to 1.0 mass %, more preferably 0.005 to 0.5 mass %, further preferably 0.008 to 0.1 mass %, and further preferably 0.01 to 0.08 mass %, from the viewpoint of effectively inhibiting the greening of the regenerated polyester.

[0169] The greening inhibitor (B) may be used alone or in combination of two or more.

[0170] Commercially available products of the greening inhibitor (B) include MACROLEX Violet 3R Gran (anthraquinone dye, manufactured by LANXESS), MACROLEX Violet B Gran (anthraquinone dye, manufactured by LANXESS), MACROLEX Red Violet R Gran (Disperse Violet 31, Disperse Violet 26, Solvent Violet 59, anthraquinone dye, manufactured by LANXESS), MACROLEX Red 5B Gran (Disperse Violet 31, Disperse Violet 26, Solvent Violet 59, anthraquinone dye, manufactured by LANXESS), and MACROLEX Red B (Solvent Red 195, azo dye, manufactured by LANXESS).

[0171] (Other ingredients)

[0172] The polyamide layer may contain other components, such as heat stabilizers, light stabilizers, moisture proof agents, water repellents, lubricants, and spreaders.

[0173] The polyamide layer may contain a resin other than the polyamide resin (Y) as a main component within a range not impairing the effects of the present invention.

[0174] When the yellowing inhibitor (A) is mixed using the masterbatch method described later, it is particularly preferred to contain a polyamide resin or polyester resin used in the masterbatch. In this case, the polyamide resin or polyester resin used in the masterbatch is preferably 1 to 20% by mass, more preferably 3 to 15% by mass relative to the total resin amount of the polyamide layer. The content of the polyamide resin (Y) is preferably 80 to 100% by mass, more preferably 90 to 100% by mass relative to the total resin amount of the polyamide layer.

[0175] In the polyamide layer of the multi-layer container of the present invention, the total content of the polyamide resin (Y), the yellowing inhibitor (A) and the greening inhibitor (B) is preferably 80 to 100% by mass, more preferably 90 to 100% by mass, relative to the entire polyamide layer. The polyamide layer may be composed only of the polyamide resin (Y), the yellowing inhibitor (A) and the greening inhibitor (B). In addition, when a polyester resin is used in the masterbatch, in the polyamide layer of the multi-layer container of the present invention, the total content of the polyamide resin (Y), the polyester resin used in the masterbatch, the yellowing inhibitor (A) and the greening inhibitor (B) is preferably 80 to 100% by mass, more preferably 90 to 100% by mass, relative to the entire polyamide layer. The polyamide layer may be composed only of the polyamide resin (Y), the polyester resin used in the masterbatch, the yellowing inhibitor (A) and the greening inhibitor (B).

[0176] <Structure / Characteristics of Multilayer Container>

[0177] The multilayer container of the present invention has a multilayer structure comprising a polyester layer of a polyester resin (X) and a polyamide layer comprising a polyamide resin (Y) and a yellowing inhibitor (A). * The value is above 87.5.

[0178] The multilayer container of the present invention may contain the aforementioned polyester layer and a resin layer other than the aforementioned polyamide layer, but from the viewpoint of facilitating classification during recycling and improving colorlessness, it is preferred that the aforementioned polyester layer and the resin layer other than the aforementioned polyamide layer are contained in a small amount, and preferably substantially no polyester layer and the resin layer other than the aforementioned polyamide layer are contained. In addition, an adhesive layer formed of an adhesive and an inorganic layer formed of an inorganic substance may be provided, but for these, from the viewpoint of facilitating classification during recycling and improving the yellowing suppression effect, it is preferred that the adhesive layer and the inorganic layer are contained in a small amount, and preferably substantially no adhesive layer and the inorganic layer are contained.

[0179] The multilayer container of the present invention has a multilayer structure of two or more layers, preferably a 2-5 layer structure, more preferably a 3-5 layer structure, further preferably a 3-layer structure or a 5-layer structure, and further preferably a 3-layer structure.

[0180] The outermost layer of the multilayer container of the present invention is preferably a polyester layer. In addition, the innermost layer is preferably also a polyester layer, and more preferably both the outermost layer and the innermost layer are polyester layers.

[0181] When the outermost layer is a polyester layer, the multi-layer container will be excellent in impact resistance, appearance, and design.

[0182] Therefore, as for the structure of the multilayer container, it is preferred that the multilayer container has a 2-5 layer structure in which the outermost layer is a polyester layer, and it is more preferred that the multilayer container has a 3-5 layer structure in which the outermost layer and the innermost layer are polyester layers.

[0183] In the case of a two-layer structure, it is preferably polyamide layer / polyester layer from the innermost layer, in the case of a three-layer structure, it is preferably polyester layer / polyamide layer / polyester layer from the innermost layer, and in the case of a five-layer structure, it is preferably polyester layer / polyamide layer / polyester layer / polyamide layer / polyester layer from the innermost layer.

[0184] In the multi-layer container of the present invention, L * The value is 87.5 or more, preferably 89.0 or more, more preferably 89.5 or more, and further preferably 90.0 or more. Also, it is 100.0 or less.

[0185] L * The value indicates brightness, L * When the value is large, the whiteness is high, L * When the value is small, the blackness is high.

[0186] By making the L * The value is within the aforementioned range, thereby being able to effectively reduce blue.

[0187] By making the L * The reason why the blue tint can be reduced and the colorlessness is excellent when the value is within the above range is uncertain, but it is speculated that the reason is that less light is absorbed and scattered on the surface and inside of the multi-layer container, and the influence of the yellowing inhibitor on the light transmitted or reflected by the multi-layer container is reduced.

[0188] As a multi-layer container L * Methods for adjusting the value to the aforementioned range include, for example, a method of reducing the content of pigment contained in the polyester layer and the polyamide layer, preferably a method of making the polyester layer and the polyamide layer substantially free of pigment, and a method of adjusting the molding conditions of the container, a method of making the polyester layer substantially free of reheat agent.

[0189] L for multi-layer container * The value can be determined by measuring in accordance with JIS K 7105. Specifically, it can be determined by the measuring method described in the Examples.

[0190] The multilayer container of the present invention is preferably a hollow container. When the multilayer container is a hollow container, the main body has at least a multilayer structure. In addition, the ratio of the thickness (W) of the polyester layer in the main body to the thickness (S) of the polyamide layer (thickness ratio W / S) is preferably 2.5 or more and 200 or less. It should be noted that the thickness of the polyester layer refers to the average thickness. When there are multiple layers of the polyester layer in the main body, the thickness of the multiple layers is averaged to find the average thickness of each layer. The thickness of the polyamide layer is also the same.

[0191] If the thickness ratio W / S is 2.5 or more, it is preferred that the polyamide resin can be easily classified from the polyester resin in the classification process, especially in the air separation and specific gravity separation in the production method of the recycled polyester. In addition, if the thickness ratio W / S is 200 or less, the gas barrier property of the hollow container is excellent, and the content can be stored for a long time.

[0192] The thickness ratio (W / S) is more preferably 3 to 50, and even more preferably 4 to 15, from the viewpoint of improving the classifying property in the classifying step and improving the gas barrier property of the hollow container.

[0193] In addition, when the multilayer container is a hollow container, the total thickness of the main body of the hollow container (i.e., the total thickness of all layers of the main body) is preferably 100 μm to 5 mm, more preferably 150 μm to 3 mm, and further preferably 200 μm to 2 mm. In addition, the thickness (W) of each polyester layer is preferably 30 μm to 2 mm, more preferably 40 μm to 1 mm, and further preferably 50 μm to 500 μm. The thickness (S) of each polyamide layer is preferably 1 to 200 μm, more preferably 3 to 100 μm, and further preferably 8 to 50 μm. In the present invention, by making the thickness of the polyamide layer within this range, gas barrier properties are ensured, and in the classification process, the polyamide layer becomes easy to be classified from the polyester.

[0194] When the multilayer container of the present invention is a hollow container, it is more preferably a liquid packaging container filled with liquid inside the hollow container, and is further preferably a beverage packaging container. Examples of the liquid filled inside include beverages, liquid flavoring agents, chemicals, medicines, detergents, etc., and beverages that can be effectively prevented from deteriorating due to oxygen by using the multilayer container of the present invention are preferred.

[0195] Examples of beverages include water, carbonated water, oxygenated water, hydrogenated water, milk, dairy products, fruit juices, coffee, coffee drinks, carbonated soft drinks, teas, and alcoholic beverages.

[0196] Examples of liquid seasonings include sauces, soy sauces, syrups, mirin, and seasonings.

[0197] Examples of the chemical products include agricultural chemicals and insecticides.

[0198] The oxygen barrier property of the multilayer container of the present invention can be evaluated according to the oxygen permeability test based on the MOCON method in accordance with ASTM D3985. When a total amount of 25 g of a resin having a mass ratio of the polyester layer to the polyamide layer of 97:3 is made into a three-layer hollow container with an internal volume of 500 mL, the oxygen permeability (cc / (bottle·0.21atm·day)) of the multilayer container of the present invention is preferably 0.040 or less, more preferably 0.035 or less, and further preferably 0.030 or less. It should be noted that the manufacture of the three-layer hollow container can be based on the method of the embodiment.

[0199] The measurement was performed using OX-TRAN2 / 61 manufactured by MOCON. The aforementioned 500 mL container was filled with 100 mL of water. Under conditions of an oxygen partial pressure of 0.21 atm, a temperature of 23°C, a humidity of 100% RH inside the container, and an external humidity of 50% RH, 1 atm of nitrogen was circulated inside the container at a rate of 20 mL / min. The oxygen contained in the nitrogen after circulation inside the container was detected by a coulometric sensor for measurement.

[0200] [Method for manufacturing multi-layer container]

[0201] The method for producing a multilayer container of the present invention comprises the following steps 1 to 3. The multilayer container comprises: a polyester layer comprising a polyester resin (X), and a polyamide layer comprising a polyamide resin (Y) and a yellowing inhibitor (A), wherein the content of the polyamide resin (Y) is 0.05 to 7.0% by mass relative to the total amount of the polyamide layer and the polyester layer, and the yellowing inhibitor (A) is a dye, and the content of the yellowing inhibitor (A) is 400 to 800 ppm relative to the polyamide layer. * The value is above 87.5.

[0202] Step 1: a step of mixing a polyamide resin (Y) and a yellowing inhibitor (A) to prepare a polyamide resin mixture;

[0203] Step 2: a step of co-injection molding the polyamide resin mixture and the polyester resin composition containing the polyester resin (X) to obtain a multilayer preform;

[0204] Step 3: Blow molding the multi-layer preform

[0205] <Step 1 (Step of Preparing a Polyamide Resin Mixture)>

[0206] In step 1, a polyamide resin (Y) and a yellowing inhibitor (A) are mixed to prepare a polyamide resin mixture.

[0207] Generally, in order to spread the yellowing inhibitor throughout the entire container, a device for stirring and mixing or kneading the yellowing inhibitor with all the resins is required. However, in the method for producing a multi-layer container of the present invention, by mixing the yellowing inhibitor (A) with a small amount of the polyamide resin (Y), the yellowing inhibitor can be effectively spread throughout the entire container by mixing on a small scale and in a short time, thereby achieving excellent productivity.

[0208] The mixing method may be dry blending or melt blending (melt kneading). From the viewpoint of reducing the thermal history and preventing the degradation of the resin and the yellowing inhibitor, dry blending and melt blending by the masterbatch method are preferred. In addition, from the viewpoint of preventing the yellowing inhibitor from adhering to the molding machine and the periphery of the molding machine and remaining in step 2, melt blending is preferred. Among them, from the viewpoint of reducing the thermal history and preventing the degradation of the resin and the yellowing inhibitor, the masterbatch method is preferred.

[0209] In step 1, the pelletized polyamide resin (Y) and the yellowing inhibitor (A) are preferably mixed at 230°C or less, more preferably at 150°C or less, and further preferably at 100°C or less. By mixing at 230°C or less, the thermal history can be reduced, and the degradation of the resin and the yellowing inhibitor can be prevented. This is considered to be because the polyamide resin can maintain the pelletized form and thus has less thermal degradation. When mixing at 230°C or less, dry blending is preferably performed.

[0210] The yellowing inhibitor (A) preferably used in the step 1 is the same as described in the above item (yellowing inhibitor (A)), and is a dye, and an anthraquinone-based dye is more preferable.

[0211] From the viewpoint of effectively suppressing yellowing of the recycled polyester and suppressing blue color of the multilayer container, the amount of the yellowing inhibitor (A) is 400 to 800 ppm, preferably 500 to 700 ppm, based on the polyamide resin mixture forming the polyamide layer of the obtained multilayer container.

[0212] The amount of the yellowing inhibitor (A) is preferably 1 to 20 ppm, more preferably 7 to 19 ppm, further preferably 10 to 18 ppm, and further preferably 13 to 17 ppm, based on the total amount of all polyamide layers and all polyester layers of the obtained multilayer container.

[0213] The yellowing inhibitor (A) is preferably in a powder form, a dispersion or a solution, and more preferably in a powder form. When the yellowing inhibitor (A) is in these forms, it can be mixed more easily and uniformly with the polyamide resin (Y).

[0214] By mixing the pelletized polyamide resin (Y) and the powdered yellowing inhibitor (A) at low temperature, deterioration of the resin and the yellowing inhibitor can be prevented, and the yellowing inhibitor and the resin can be uniformly mixed.

[0215] In step 1, it is preferred that a greening inhibitor (B) is further mixed.

[0216] The greening inhibitor (B) suitably used in step 1 is the same as those described in the item (Greening inhibitor (B)) above, and is preferably at least one selected from the group consisting of dyes and pigments, more preferably at least one selected from the group consisting of anthraquinone dyes and azo dyes, further preferably at least one selected from the group consisting of anthraquinone red dyes and azo red dyes, and from the viewpoint of heat resistance, anthraquinone red dyes are further preferred.

[0217] From the viewpoint of effectively suppressing the greening of the recycled polyester, the amount of the greening inhibitor (B) blended in the polyamide resin mixture to form the polyamide layer of the obtained multi-layer container is preferably 0.001 to 1.0 mass %, more preferably 0.005 to 0.5 mass %, further preferably 0.008 to 0.1 mass %, and further preferably 0.01 to 0.08 mass %.

[0218] The greening inhibitor (B) is preferably in a powder form, a dispersion or a solution, and more preferably in a powder form. The greening inhibitor (B) in these forms can be mixed more easily and uniformly with the polyamide resin (Y).

[0219] The mass ratio [(A) / (B)] of the yellowing inhibitor (A) to the greening inhibitor (B) in the polyamide resin mixture forming the polyamide layer of the obtained multilayer container is preferably 20 / 80 to 80 / 20, more preferably 30 / 70 to 70 / 30, and even more preferably 40 / 60 to 60 / 40.

[0220] Examples of a mixing apparatus used for dry blending include a tumble mixer, a ribbon mixer, a Henschel mixer, and a Banbury mixer.

[0221] In step 1, examples of a method for mixing the polyamide resin (Y) and the yellowing inhibitor (A) by melt blending include a masterbatch method and a full mixing method, and a masterbatch method is preferred.

[0222] The masterbatch method is a method in which a small amount of polyamide resin or polyester resin is kneaded with a yellowing inhibitor (A) to form a masterbatch, and then mixed with the remaining amount of polyamide resin (Y). In addition, when obtaining the masterbatch, a greening inhibitor (B) may be kneaded at the same time. That is, in step 1, it is preferred that the polyamide resin or polyester resin is kneaded with the yellowing inhibitor (A) and then mixed with the polyamide resin (Y). In step 1, it is more preferred that the polyamide resin or polyester resin, the yellowing inhibitor (A) and the greening inhibitor (B) are kneaded and then mixed with the polyamide resin (Y).

[0223] In the masterbatch, polyamide resin or polyester resin is preferably used. From the perspective of compatibility with the polyamide resin (Y), polyamide resin is preferably used, and from the perspective of suppressing yellowing due to thermal history, polyester resin is preferably used. It should be noted that these may be used in mixture.

[0224] The polyamide resin used in the masterbatch is preferably the polyamide resin (Y), and more preferably the same as the remaining polyamide resin (Y).

[0225] The polyester resin used in the masterbatch is preferably the polyester resin (X), and more preferably the same as the polyester resin (X) of the polyester layer.

[0226] The amount of the polyamide resin or polyester resin used in the masterbatch is preferably 1 to 20% by mass, more preferably 3 to 15% by mass, based on the total amount of the polyamide layer.

[0227] As a method for obtaining a masterbatch, when a polyamide resin or a polyester resin and a yellowing inhibitor (A) are kneaded, when the melting point of the resin used for the masterbatch is set to Tm, from the viewpoint of sufficient mixing, the kneading temperature (°C) is preferably Tm+5 to Tm+60, more preferably Tm+10 to Tm+50, and further preferably Tm+15 to Tm+40. Specifically, it is further preferably 245 to 300°C, further preferably 250 to 290°C, and further preferably 255 to 280°C. In addition, from the viewpoint of sufficient mixing, the kneading time is preferably 10 to 600 seconds, more preferably 20 to 400 seconds, and further preferably 30 to 300 seconds. As the apparatus used for kneading, an open type stirring roll, a non-open type Banbury mixer, a kneader, a continuous kneading machine (single screw kneading machine, twin screw kneading machine, multi-screw kneading machine, etc.) and the like can be cited.

[0228] In addition, as a method for mixing the masterbatch with the remaining polyamide resin (Y), dry blending and further kneading are mentioned, and dry blending is preferred. In dry blending, it is preferred that pellets of the masterbatch and pellets of the remaining polyamide resin (Y) are mixed with a mixing device such as a tumble mixer.

[0229] The total mixing method is a method of kneading and mixing the total amount of the polyamide resin (Y) and the yellowing inhibitor (A) used in the polyamide layer.

[0230] From the viewpoint of sufficient mixing, the kneading temperature is preferably 245 to 300° C., more preferably 250 to 290° C., and further preferably 255 to 280° C. From the viewpoint of sufficient mixing, the kneading time is preferably 10 to 600 seconds, more preferably 20 to 400 seconds, and further preferably 30 to 300 seconds. As the apparatus used in kneading, an open type stirring roll, a non-open type Banbury mixer, a kneader, a continuous kneading machine (single screw kneading machine, twin screw kneading machine, multi-screw kneading machine, etc.) and the like can be cited.

[0231] The polyamide resin mixture obtained in this step preferably has the same composition as that of the above-mentioned <polyamide layer>.

[0232] <Step 2 (Step of Obtaining a Multilayer Preform)>

[0233] In step 2, the polyamide resin mixture and the polyester resin composition containing the polyester resin (X) are co-injection molded to obtain a multilayer preform.

[0234] The polyester resin composition preferably has the same composition as that of the above-mentioned <Polyester layer> except for the polyester resin (X).

[0235] In co-injection molding, a mixture of polyester resin and polyamide resin is extruded from a mold separately and co-injection molded to form a multi-layer preform.

[0236] <Step 3 (blow molding step)>

[0237] In step 3, the multi-layer preform is blow-molded.

[0238] In the method for producing a multi-layer container of the present invention, the multi-layer preform (multi-layer parison) obtained in step 2 is preferably molded by stretch blow molding.

[0239] Among them, in step 2, it is preferred to perform stretch blow molding on the multilayer preform obtained by coinjection molding, and it is more preferred to perform biaxial stretch blow molding on the multilayer preform obtained by coinjection molding. It should be noted that as conditions for biaxial stretch blow molding, it is preferred that the preform heating temperature is 95 to 110° C., the primary blow molding pressure is 0.5 to 1.2 MPa, and the secondary blow molding pressure is 2.0 to 2.6 MPa, thereby obtaining a multilayer container with excellent strength and suppressed thickness unevenness and stretch unevenness.

[0240] [Method for producing recycled polyester]

[0241] The multi-layered container of the present invention is suitable for recycling as described above, and the multi-layered container of the present invention can be used as a raw material to produce recycled polyester.

[0242] The method for producing the regenerated polyester of the present invention preferably comprises a step of recovering the polyester from the multi-layer container.

[0243] That is, it is preferred to have a step of recovering polyester from a multilayer container, wherein the multilayer container comprises: a polyester layer comprising a polyester resin (X), and a polyamide layer comprising a polyamide resin (Y) and a yellowing inhibitor (A), wherein the content of the polyamide resin (Y) is 0.05 to 7.0% by mass relative to the total amount of the polyamide layer and the polyester layer, and the yellowing inhibitor (A) is a dye, and the content of the yellowing inhibitor (A) is 400 to 800 ppm relative to the polyamide layer, and the L of the multilayer container is 100 to 150 ppm. * The value is above 87.5.

[0244] The method for producing recycled polyester from a multi-layer container preferably comprises removing all or part of the polyamide layer from the multi-layer container, recovering the polyester constituting the polyester layer, and using the recycled polyester as the recycled polyester. It should be noted that the method for producing recycled polyester from a multi-layer container is not limited to the above method, and may be a method for producing recycled polyester without removing the polyamide resin.

[0245] The regenerated polyester obtained by the present production method can be used for various purposes such as resin molded products and fibers.

[0246] Hereinafter, the method for producing the regenerated polyester of the present invention will be described in detail.

[0247] In the present production method, the multilayer container is usually a used container, but may be an unused container. As the used multilayer container, there can be mentioned those temporarily circulated in the recycling market.

[0248] In the present production method, first, when a cover is attached to the multi-layer container, it is preferred that the cover is removed from the multi-layer container.

[0249] Then, the container is pulverized, washed as necessary, and the polyester is selectively taken out and separated as necessary to be recovered as recycled polyester (recovery step).

[0250] Then, the mixture is granulated as necessary to form pellets (granulation step).

[0251] Furthermore, a crystallization step and a solid phase polymerization step (crystallization / solid phase polymerization step) are performed as necessary.

[0252] Each step is described below.

[0253] <Recycling Process>

[0254] The recycling step is a step of crushing the multilayer container and recovering the recycled polyester.

[0255] Among them, it is preferred to pulverize the multilayer container, remove all or part of the polyamide layer, and selectively extract the polyester, and it is more preferred to classify the polyester and the polyamide resin constituting the polyamide layer.

[0256] The multi-layer container can be crushed using a single screw crusher, a twin screw crusher, a triple screw crusher, a shredder or the like. The crushed product obtained by crushing is, for example, in the form of flakes, powders or blocks. However, since the main body of the multi-layer container and other parts thereof are mostly thin and thick multi-layer stacked structures with a thickness of less than several mm, most of the crushed product is usually in the form of flakes. It should be noted that the flake-shaped crushed product refers to a flake or flat product with a thickness of less than about 2 mm.

[0257] In addition, in the multilayer container, the polyester layer and the polyamide layer are structurally integrated, but they are usually not bonded to each other, and the polyester and polyamide resins are easily separated as independent pulverized products during the pulverization process. In addition, by making the pulverized products into sheets, they can be easily separated by being rolled up by the air flow of the air separation described later.

[0258] However, polyester and polyamide resin may not be completely separated in the pulverization process, and the pulverized product is separated into a product with a relatively high polyester content and a product with a relatively low polyester content and a relatively high polyamide resin content. It should be noted that, hereinafter, for the sake of convenience, the product with a relatively high polyester content is referred to as polyester, and the product with a relatively high polyamide resin content is referred to as polyamide resin.

[0259] As described above, the pulverized product is classified into polyester and polyamide resins (classification step).

[0260] As the classification method, specific gravity screening using the difference in specific gravity between polyester and polyamide resins is preferably used.

[0261] That is, it is preferred that the polyamide layer be removed by pulverizing the multilayer container and then separating by air separation.

[0262] As specific gravity screening, specifically, there can be cited wind separation that uses wind power to screen the pulverized material. For example, the wind separation method can be as follows: in a separation device that can generate a swirling airflow inside, the pulverized material that contacts the airflow generated by the separation device is classified into those with a large specific gravity or a small specific surface area that naturally fall due to their own weight; and those with a small specific gravity or a large specific surface area that are rolled up by the airflow and recovered.

[0263] In this method, the ground polyester naturally falls due to its own weight, while the ground polyamide resin is rolled up, whereby the polyester and the polyamide resin can be separated and recovered.

[0264] In this air separation, the same operation can be repeated for the same pulverized material. For example, the naturally fallen material can be further air separated to increase the polyester content in the recycled polyester.

[0265] It should be noted that the classification method is not limited to air separation, and the following methods can be cited: a method in which the pulverized material is immersed in a liquid such as water and classified according to the difference in specific gravity of the pulverized material relative to the liquid; a method in which constant vibration is applied to the pulverized material, pulverized materials with different specific gravities are separated and classified; etc.

[0266] <Granulation process>

[0267] The recycled polyester after recovery is preferably granulated into pellets in order to facilitate handling during molding and the like.

[0268] Granulation can be performed before or after the crystallization / solid phase polymerization step described below, but is preferably performed before the crystallization / solid phase polymerization step. Performing granulation before the crystallization / solid phase polymerization step improves operability in the crystallization / solid phase polymerization step.

[0269] In the granulation process, the crushed material is preferably plasticized and granulated by melt blending. As the granulating device for plasticization and granulation, single screw extruder, twin screw extruder, multi-screw extruder, etc. can be cited, but any device can be used as long as it is a known device. As the shape of the pellets, cylindrical, spherical, elliptical spherical are preferred.

[0270] Granulation is preferably performed, for example, by extruding the plasticized recycled polyester into strands, cooling them in a water tank, and cutting them in a granulator to form pellets. The pellets taken out of the water tank are usually dried to remove moisture adhering to the surface.

[0271] <Crystallization / Solid Phase Polymerization Step>

[0272] After the polyester recovery step, preferably at least one step selected from a crystallization step and a solid phase polymerization step is performed, and more preferably both the crystallization step and the solid phase polymerization step are performed. The crystallization / solid phase polymerization step is preferably performed on the pelletized polyester, but may also be performed on a non-pelletized polyester (e.g., a pulverized product).

[0273] In addition, when both crystallization and solid phase polymerization are performed, it is preferable to perform solid phase polymerization after crystallizing the polyester.

[0274] The crystallization of the polyester is carried out by keeping the polyester under a certain heating condition. The crystallization is preferably carried out by heating the polyester at, for example, 100 to 230° C. The polyester is crystallized to prevent the polyester from fusing to each other during solid phase polymerization or molding, or to prevent the polyester from adhering to the inner surface of the device.

[0275] Solid phase polymerization is preferably carried out by maintaining the temperature at a temperature of (melting point of polyester - 80°C) or higher and lower than the melting point of polyester for a certain period of time. By setting the temperature lower than the melting point, the polyester is prevented from melting, for example, the polyester is prevented from adhering to the surface of the device and reducing the working efficiency. In addition, by setting the temperature higher than (melting point - 80°C), the polymerization is carried out at a sufficient polymerization rate, and it becomes easy to obtain the desired physical properties.

[0276] Solid phase polymerization can be implemented under vacuum or under an inert gas stream such as nitrogen or argon. When implemented under vacuum, it is preferably 1.0 torr or less, more preferably 0.5 torr or less, and further preferably 0.1 torr or less. In addition, under vacuum or under an inert gas stream such as nitrogen or argon, it is preferred to reduce the residual oxygen concentration in the system as much as possible, and the oxygen concentration is preferably 300 ppm or less, more preferably 30 ppm or less. The oxygen concentration is set to 30 ppm or less, thereby becoming less likely to cause poor appearance such as yellowing.

[0277] When solid phase polymerization is carried out under vacuum, it is preferred to frequently repeat stirring or mixing of the polyester while uniformly conducting heat. When carried out in the presence of an inert gas, it is preferred to frequently keep the surface of the polyester in contact with the dried gas under a flow of the dried gas.

[0278] The solid phase polymerization apparatus used for the crystallization / solid phase polymerization step can include: a drum-type intermittent apparatus equipped with a heating jacket, a drying silo type equipped with an inert gas flow device, a crystallization apparatus and a reactor equipped with stirring blades and a discharge screw inside, etc. It should be noted that crystallization and solid phase polymerization are preferably carried out continuously or simultaneously in the same apparatus.

[0279] The heating time for solid phase polymerization is appropriately determined depending on the apparatus and other conditions, but may be a time for obtaining sufficient physical properties of the polyester.

[0280] Solid phase polymerization keeps the polyester at high temperature for a long time, so if there are impurities in the polyester, the quality of the color tone may be deteriorated. In the above removal step, it is preferred that most of the polyamide resin is removed. In this case, the quality deterioration that may occur during solid phase polymerization is suppressed to a minimum.

[0281] In the method for producing regenerated polyester of the present invention, steps other than the steps described above may be performed, and a washing step may be performed to remove the contents adhering to the inside of the multilayer container. The washing is preferably performed by rinsing with a liquid, washing with water, washing with an alkaline aqueous solution, or both.

[0282] In addition, the cleaning can be performed before the multilayer container is pulverized into a pulverized product, or after the pulverization, and is preferably performed before any of granulation, crystallization, and solid phase polymerization. Furthermore, the cleaning step can be performed simultaneously with the pulverization step in a pulverizer that performs cleaning and pulverization at the same time, which is called a wet pulverizer.

[0283] In addition, when the washing step is performed, a drying step may be performed after the washing step. By performing the drying step, the moisture content of the regenerated polyester obtained by the present method can be reduced, so that high-quality regenerated polyester with high thermal stability can be provided. The drying step can be performed, for example, using air supply or hot air from a dryer.

[0284] When the method for producing recycled polyester includes a step of removing the polyamide resin, the content of the polyamide resin in the obtained recycled polyester is preferably less than 1% by mass, more preferably less than 0.8% by mass, and further preferably less than 0.6% by mass. In this way, the content of the polyamide resin is reduced, and the quality of the recycled polyester becomes good.

[0285] Example

[0286] Hereinafter, the present invention will be described in more detail using Examples and Comparative Examples, but the present invention is not limited to these Examples.

[0287] [raw material]

[0288] The polyester resin, yellowing inhibitor, and greening inhibitor used in the examples and comparative examples are as follows. The polyamide resin used was the one produced in the following Production Example 1.

[0289] <Polyester resin>

[0290] 8912: Isophthalic acid copolymer polyethylene terephthalate (intrinsic viscosity: 0.85 dL / g), trade name: TYPE 8912, manufactured by Indorama Ventures, does not contain a reheat agent

[0291] BK2180: Isophthalic acid copolymer polyethylene terephthalate (intrinsic viscosity: 0.83 dL / g, melting point: 248°C), trade name: BK2180, manufactured by Mitsubishi Chemical Corporation, does not contain a reheat agent

[0292] 1101: Isophthalic acid copolymer polyethylene terephthalate (intrinsic viscosity: 0.83 dL / g), trade name: TYPE 1101, manufactured by Indorama Ventures, contains a reheat agent

[0293] <Yellowing Inhibitor>

[0294] Blue RR: Solvent Blue 97 (anthraquinone dye), trade name: MACROLEX Blue RR Gran, manufactured by LANXESS,

[0295] Blue 690: Solvent Blue 104 (anthraquinone dye), trade name: Oracet Blue 690, manufactured by BASF

[0296] <Greening Inhibitor>

[0297] Violet 3R: Solvent Violet 36 (anthraquinone dye), trade name: MACROLEX Violet 3R Ran, manufactured by LANXESS

[0298] <Polyamide resin>

[0299] Production Example 1 (Production of polyamide resin (Y1))

[0300] In a 50-liter reaction vessel equipped with a stirrer, a partial condenser, a full condenser, a thermometer, a dropping funnel, a nitrogen inlet tube, and a strand die, 15,000 g (102.6 mol) of adipic acid and sodium hypophosphite monohydrate (NaH 2 PO 2 ·H 2 O) 13.06g (123.3mmol, 151ppm based on the phosphorus atom concentration in the polyamide), 6.849g of sodium acetate (83.49mmol, 0.68 based on the molar ratio relative to sodium hypophosphite monohydrate), fully replaced with nitrogen, and then, further heated to 170°C while stirring the system under a small amount of nitrogen flow. Under stirring, 13896g of meta-xylylenediamine (102.0mol, 0.994 based on the input molar ratio) was added dropwise, and the system was continuously heated while the generated condensation water was discharged to the outside of the system. After the addition of meta-xylylenediamine was completed, the internal temperature was set to 260°C and the reaction was continued for 40 minutes. Then, the system was pressurized with nitrogen, the polymer was taken out from the strand die and pelletized to obtain about 24kg of polyamide.

[0301] Then, the polyamide was added to a jacketed drum dryer equipped with a nitrogen inlet pipe, a vacuum line, a vacuum pump, and a thermocouple for measuring the internal temperature. While rotating the drum dryer at a constant speed, the inside of the drum dryer was fully replaced with nitrogen having a purity of 99% by volume or more. Then, the drum dryer was heated under the same nitrogen flow, and the pellet temperature was raised to 150°C in about 150 minutes. When the pellet temperature reached 150°C, the pressure in the system was reduced to less than 1 torr. The temperature was further continued to rise, and after the pellet temperature was raised to 200°C in about 70 minutes, it was maintained at 200°C for 30 to 45 minutes. Then, nitrogen having a purity of 99% by volume or more was introduced into the system, and the drum dryer was kept rotating and cooled to obtain a polyamide resin (Y1). The amino terminal group concentration was measured, and the result was 14.4 μmol / g.

[0302] <Production of Polyamide Resin Mixture by Masterbatch Method>

[0303] Production Example 2

[0304] 98.8% by mass of polyamide resin (Y1), 0.6% by mass of Blue RR as a yellowing inhibitor (A), and 0.6% by mass of Violet 3R as a greening inhibitor (B) were preliminarily dry-blended. The dry-blended mixture was then melt-kneaded at 260° C. using a twin-screw extruder (TEM26SX manufactured by Toshiba Machine Co., Ltd.) to obtain masterbatch pellets. The pellets were then dried in a vacuum dryer at 150° C. for 5 hours to obtain a masterbatch A.

[0305] Next, the obtained master batch A and the remaining amount of the polyamide resin (Y1) were mixed at a mass ratio of 10 / 90 (master batch A / remaining amount of the polyamide resin=10 / 90) to prepare a polyamide resin mixture.

[0306] Production Example 3

[0307] A master batch B was obtained in the same manner as in Production Example 2 except that the blending ratio was 99.2 mass % of the polyamide resin (Y1), 0.4 mass % of Blue RR as the yellowing inhibitor (A), and 0.4 mass % of Violet 3R as the greening inhibitor (B).

[0308] Next, the obtained master batch B and the remaining amount of the polyamide resin (Y1) were mixed at a mass ratio of 10 / 90 (master batch B / remaining amount of the polyamide resin=10 / 90) to prepare a polyamide resin mixture.

[0309] Production Example 4

[0310] A master batch C was obtained in the same manner as in Production Example 2 except that the blending ratio was 98.8% by mass of the polyamide resin (Y1), 0.6% by mass of Blue 690 as the yellowing inhibitor (A), and 0.6% by mass of Violet 3R as the greening inhibitor (B).

[0311] Next, the obtained master batch C and the remaining amount of the polyamide resin (Y1) were mixed at a mass ratio of 10 / 90 (master batch C / remaining amount of the polyamide resin=10 / 90) to prepare a polyamide resin mixture.

[0312] Production Example 5

[0313] A master batch D was obtained in the same manner as in Production Example 2 except that the blending ratio was 98.0 mass % of the polyamide resin (Y1), 1.0 mass % of Blue RR as the yellowing inhibitor (A), and 1.0 mass % of Violet 3R as the greening inhibitor (B).

[0314] Next, the obtained master batch D and the remaining amount of the polyamide resin (Y1) were mixed at a mass ratio of 10 / 90 (master batch D / remaining amount of the polyamide resin=10 / 90) to prepare a polyamide resin mixture.

[0315] Production Example 6

[0316] A master batch E was obtained in the same manner as in Production Example 2 except that the blending ratio was 99.6 mass % of the polyamide resin (Y1), 0.2 mass % of Blue RR as the yellowing inhibitor (A), and 0.2 mass % of Violet 3R as the greening inhibitor (B).

[0317] Next, the obtained master batch E and the remaining amount of the polyamide resin (Y1) were mixed at a mass ratio of 10 / 90 (master batch E / remaining amount of the polyamide resin=10 / 90) to prepare a polyamide resin mixture.

[0318] [Multi-layer container]

[0319] Examples 1 to 4 and Comparative Examples 1 to 4 (Manufacturing of multi-layered containers)

[0320] <Preform Forming>

[0321] An injection molding machine with two injection barrels (manufactured by Sumitomo Heavy Industries, Ltd., model DU130CI) and a two-piece mold (manufactured by Kortec) was used. The polyester resin shown in Table 1 was injected from one injection barrel, and the polyamide resin mixture shown in Table 1 was injected from the other injection barrel. Under the conditions shown below, a three-layer preform (set to be equivalent to 25 g per preform) consisting of a polyester layer / polyamide layer / polyester layer was injection molded in such a way that the mass of the polyamide layer relative to the entire preform became the amount recorded in Table 1. The shape of the preform is as follows: total length 95 mm, outer diameter 22 mm, wall thickness 4.0 mm. The molding conditions of the three-layer preform are shown below.

[0322]

[0323] <Bottle molding>

[0324] The preform obtained above was subjected to biaxial stretch blow molding using a blow molding device (EFB1000ET, manufactured by Frontier) to obtain a bottle (hollow multilayer container). The bottle had a total length of 223 mm, an outer diameter of 65 mm, an internal volume of 500 mL, and a petal-shaped bottom. No shallow concave portion was provided in the main body. The biaxial stretch blow molding conditions were as follows.

[0325] Preform heating temperature: 103℃

[0326] Stretching rod pressure: 0.7MPa

[0327] One blow molding pressure: 1.1MPa

[0328] Secondary blow molding pressure: 2.5MPa

[0329] One blow molding delay time: 0.30 seconds

[0330] Blowing time: 0.30 seconds

[0331] Second blow molding time: 2.0 seconds

[0332] Blow molding exhaust time: 0.6 seconds

[0333] Mold temperature: 30℃

[0334] [Manufacturing of recycled polyester]

[0335] <Recovery / Pelletization Process>

[0336] 10 kg of the hollow multilayer containers obtained in Examples 1 to 4 and Comparative Examples 1 to 4 were pulverized in a pulverizer having a mesh diameter of 8 mm, and the obtained flaky pulverized products were recovered as recycled polyester.

[0337] The recycled polyester was extruded by a twin-screw extruder (TEM26SX manufactured by Toshiba Machine Co., Ltd.) at a heater temperature of 270°C and a discharge rate of 20 kg / hour to form strands, which were then cut in a pelletizer while being cooled in a water tank to form pellets. It should be noted that the polyamide layer was not separated by air separation.

[0338] <Crystallization / Solid Phase Polymerization Step>

[0339] The pellets obtained in the above granulation step were heated at 200°C for 7 hours under a vacuum reduced to less than 1 torr. The pellets after the heat treatment were taken out and the yellowness Δb * The results are shown in Table 1.

[0340] [Measurement method]

[0341] <L * Value>

[0342] The main body of the bottle (multilayer container) obtained in the above-mentioned Examples and Comparative Examples was cut out to a height of 5 to 9 cm from the bottom, and the turbidity of the main body of the bottle was measured using a turbidity meter COH400 (manufactured by Nippon Denshoku Industries) in accordance with JIS K 7105. * value.

[0343] * Value>

[0344] The main body of the bottle (multilayer container) obtained in the above-mentioned Examples and Comparative Examples was cut out to a height of 5 to 9 cm from the bottom, and the turbidimeter COH400 (manufactured by Nippon Denshoku Industries) was used to measure the b of the main body of the bottle in accordance with JIS K 71055. * value.

[0345] It should be noted that b * Value indicates chromaticity. +b * Indicates yellow direction, -b * Indicates the blue direction. * The larger the value, the * The smaller the absolute value, the less blue the color is and the better the colorlessness is.

[0346] <Blue sensory evaluation>

[0347] In a room with white lighting, the bottles (multilayer containers) obtained in the above-mentioned examples and comparative examples were placed upright on white paper. White paper was placed upright 10 cm behind the bottles. The bottles were visually observed from the opposite side of the upright paper, and the blue color of the bottles was evaluated based on the following criteria.

[0348] A: I didn’t feel the blue.

[0349] B: Feeling blue.​

[0350] C: A noticeable blue color was perceived.

[0351] < Yellowness Δb * >

[0352] The yellowness Δb* of the recycled polyester pellets obtained in [Production of Recycled Polyester] was measured by the following method and evaluated based on the following criteria.

[0353] The color tone of the pellets was measured as follows: Based on JIS Z 8722, a 30 mmφ cuvette container was filled with pellets using a colorimeter ZE-2000 (manufactured by Nippon Denshoku Industries, 12V 20W halogen lamp light source) and the color tone was measured as the average value of four measurements by a reflection method.

[0354] It should be noted that the b* value indicates chromaticity. +b* indicates the yellow direction, and -b* indicates the blue direction. The smaller the absolute value of the Δb* value, the more suppressed the yellowing is and the higher the achromaticity is. The Δb* value indicates the difference between the b* value of the sample (recycled polyester recovered from the bottle) of the aforementioned Examples and Comparative Examples and the b* value of the polyester resin alone subjected to the same treatment as the Examples and Comparative Examples.

[0355] [Table 1]

[0356] Table 1

[0357]

[0358] As shown in Table 1, it is understood that the multilayer container of the present invention has less blue color and excellent colorlessness, and the recycled polyester obtained by recycling the multilayer container has less yellow color and excellent colorlessness.

[0359] On the other hand, it can be seen that: L of the multilayer container * The multilayer container of Comparative Example 1, in which the value was less than 87.5, and the multilayer container of Comparative Example 2, in which the content of the yellowing inhibitor (A) relative to the polyamide layer exceeded 800 ppm, had a blue color without a chromaticity difference. It was found that the multilayer containers of Comparative Examples 3 and 4, in which the content of the yellowing inhibitor (A) relative to the polyamide layer was less than 400 ppm, had a high yellowness and no chromaticity difference in the recycled polyester obtained by recycling the multilayer containers.

Claims

1. A multi-layer container, comprising: a polyester layer comprising a polyester resin (X), and a polyamide layer comprising a polyamide resin (Y) and a yellowing inhibitor (A), The content of the polyamide resin (Y) is 0.05 to 7.0% by mass based on the total amount of the polyamide layer and the polyester layer. Yellowing inhibitor (A) is a dye, The content of the yellowing inhibitor (A) is 400 to 800 ppm relative to the polyamide layer. The L* value of the multi-layer container is 87.5 or more.

2. The multi-layer container according to claim 1, wherein The polyester resin (X) has a dicarboxylic acid-derived structural unit containing 80 mol % or more of a terephthalic acid-derived structural unit and a diol-derived structural unit containing 80 mol % or more of an ethylene glycol-derived structural unit.

3. The multi-layer container according to claim 1 or 2, wherein: The polyamide resin (Y) has a diamine-derived structural unit containing 80 mol % or more of a xylylenediamine-derived structural unit and a dicarboxylic acid-derived structural unit containing 80 mol % or more of adipic acid-derived structural unit.

4. The multi-layer container according to claim 1, wherein The yellowing inhibitor (A) is an anthraquinone dye.

5. The multi-layer container according to claim 1, wherein The polyamide layer further comprises a greening inhibitor (B).

6. The multi-layer container according to claim 5, wherein: The greening inhibitor (B) is at least one selected from the group consisting of anthraquinone dyes and azo dyes.

7. The multi-layer container according to claim 5, wherein: The polyester layer is substantially free of reheat agents.

8. The multi-layer container according to claim 5, wherein: The multi-layer container is a multi-layer hollow container.

9. The multi-layer container according to claim 5, wherein: The multi-layer container has a 2-5 layer structure, and the outermost layer is a polyester layer.

10. The multi-layer container according to claim 5, wherein The multi-layer container has a 3-5 layer structure, and the outermost layer and the innermost layer are polyester layers.

11. A method for manufacturing a multi-layer container, comprising the following steps 1 to 3: Step 1: a step of mixing a polyamide resin (Y) and a yellowing inhibitor (A) to prepare a polyamide resin mixture; Step 2: a step of co-injection molding the polyamide resin mixture and a polyester resin composition containing a polyester resin (X) to obtain a multilayer preform; Step 3: a step of blow molding the multi-layer preform. The multi-layer container has: a polyester layer comprising a polyester resin (X), and a polyamide layer comprising a polyamide resin (Y) and a yellowing inhibitor (A), The content of the polyamide resin (Y) is 0.05 to 7.0% by mass based on the total amount of the polyamide layer and the polyester layer. Yellowing inhibitor (A) is a dye, The content of the yellowing inhibitor (A) is 400 to 800 ppm relative to the polyamide layer. The L* value of the multi-layer container is 87.5 or more.

12. The method for manufacturing a multi-layer container according to claim 11, wherein: In step 1, the pelletized polyamide resin (Y) and the yellowing inhibitor (A) are mixed at 230° C. or lower.

13. The method for manufacturing a multi-layer container according to claim 11 or 12, wherein: In step 1, a greening inhibitor (B) is further mixed.

14. The method for manufacturing a multi-layer container according to claim 13, wherein: In step 1, the polyamide resin or polyester resin, the yellowing inhibitor (A) and the greening inhibitor (B) are kneaded and then mixed with the polyamide resin (Y).

15. The method for manufacturing a multi-layer container according to claim 12, wherein: The yellowing inhibitor (A) is in the form of a powder, a dispersion or a solution.

16. A method for producing recycled polyester, comprising the step of recovering polyester from the multi-layer container according to any one of claims 1 to 10.

17. The method for producing regenerated polyester according to claim 16, wherein: After the step of recovering the polyester, one or more steps selected from a crystallization step and a solid phase polymerization step are performed.