Landing gear system with composite curved beam

Abstract

The invention relates to a landing gear system with a composite curved beam. A landing gear system for an aircraft includes a composite curved beam having a stitch through a thickness and a curved surface having a radius greater than 5 inches (12.7 cm); and a trunnion connected to the composite curved beam and offset from a neutral surface of the composite curved beam.

Description

[0001] This application is a divisional application of the invention patent application with application date of April 28, 2020, application number 202010348570.5, and invention name “Landing gear system with composite bending beam”. Technical Field

[0002] The present disclosure relates generally to landing gear for aircraft, and more particularly to landing gear for small aircraft. Background Art

[0003] The landing gear for an aircraft absorbs the energy of landing, among many other functions. Current designs for large aircraft may include an Oleo strut, a pneumatic, air-oil hydraulic shock absorber. However, an Oleo strut may be undesirably expensive for smaller aircraft. Oleo struts may also add relatively undesirable weight to some aircraft.

[0004] Some aircraft may utilize metal flex beams to absorb the energy of landing. However, metal flex beams may add undesirable weight to small aircraft.

[0005] Therefore, it would be desirable to have methods and apparatus that take into account at least some of the issues discussed above, as well as other possible issues. Summary of the invention

[0006] An exemplary embodiment of the present disclosure provides a landing gear system for an aircraft. The landing gear system includes: a composite curved beam having a through-thickness stitch and a curved surface having a radius greater than 5 inches (12.7 centimeters (cm)); and a trunnion connected to the composite curved beam and offset from a neutral surface of the composite curved beam.

[0007] Another exemplary embodiment of the present disclosure provides a landing gear system for an aircraft, comprising: a composite curved beam having through-thickness stitching and a curved surface along the entire length of the composite curved beam, wherein the stitching density is greater near the leading edge and the trailing edge of the composite curved beam.

[0008] Another exemplary embodiment of the present disclosure provides a method of forming a landing gear system for an aircraft. Fiber layers are laid into a curved surface, each fiber layer having a corresponding fiber orientation. The fiber layers are stitched along the length of the curved surface to form a plurality of reinforced layers, the density of the stitching being greater near the leading edge and the trailing edge of the curved surface. Resin is injected into the plurality of reinforced layers to form a resin-infused curved structure. The resin-infused curved structure is cured to form a composite curved beam of the landing gear system.

[0009] Another exemplary embodiment of the present disclosure provides a method of operating an aircraft having a landing gear system with a composite flex beam. The aircraft is flown. Dynamic loads from an aircraft landing are absorbed in the composite flex beam by flattening the composite flex beam, the composite flex beam having through-thickness stitching and a curved surface having a radius greater than 5 inches (12.7 cm) in a relaxed state.

[0010] These features and functions can be achieved independently in multiple embodiments of the present disclosure or may be combined in yet other embodiments, in which further details can be seen with reference to the following description and drawings. BRIEF DESCRIPTION OF THE DRAWINGS

[0011] The novel features believed characteristic of the exemplary embodiments are set forth in the appended claims. However, the exemplary embodiments and their preferred modes of use, further objects and features thereof will be best understood by reference to the following detailed description of exemplary embodiments of the disclosure when read in conjunction with the accompanying drawings, in which:

[0012] Figure 1 is an illustration of a block diagram of a manufacturing environment for manufacturing a composite curved beam according to an illustrative embodiment;

[0013] Figure 2 is an illustration of a front view of an aircraft having a composite bending beam in a relaxed state according to an exemplary embodiment;

[0014] Figure 3 is an illustration of a front view of an aircraft having a composite bending beam in a deflected state according to an exemplary embodiment;

[0015] Figure 4 is an illustration of a cross-sectional view of an aircraft having a composite curved beam according to an illustrative embodiment;

[0016] Figure 5 is an illustration of an axonometric view of a landing gear system having a composite curved beam for an aircraft according to an exemplary embodiment;

[0017] Figure 6 is an illustration of a front view of a landing gear system having a composite bending beam for an aircraft according to an exemplary embodiment;

[0018] Figure 7 is an illustration of a front view of a bending beam in a deflected state and a relaxed state of a landing gear system of an aircraft according to an exemplary embodiment;

[0019] Figure 8 is an illustration of a front view of a portion of a bending beam of a landing gear system of an aircraft in a deflected state and a relaxed state according to an illustrative embodiment;

[0020] Fig. 9 is an illustration of a cross-sectional view of a stitching of a leading edge of a composite curved beam of an aircraft according to an illustrative embodiment;

[0021] Fig.10 is an illustration of an axonometric view of the distribution of stitching in a composite curved beam of an aircraft according to an illustrative embodiment;

[0022] Fig.11 is an illustration of a flow chart of a method of forming a landing gear system for an aircraft according to an illustrative embodiment;

[0023] Fig.12 is an illustration of a flow chart of a method of operating an aircraft having a landing gear system with a composite bending beam according to an illustrative embodiment;

[0024] Fig.13 is a block diagram of an aircraft manufacturing and service method according to an illustrative embodiment; and

[0025] Fig.14 is an illustration, in block diagram form, of an aircraft in which an illustrative embodiment may be implemented. DETAILED DESCRIPTION

[0026] The illustrative embodiments recognize and take into account one or more of the various considerations.The illustrative embodiments recognize and take into account that it is desirable to reduce the cost and weight of an aircraft.

[0027] The illustrative embodiments recognize and take into account that a composite material is a hard, lightweight material produced by combining two or more functional components. For example, a composite material may include reinforcing fibers bonded in a polymer resin matrix. The fibers may be unidirectional or may take the form of a nonwoven or woven fabric. The fibers and resin are arranged and cured to form a composite material.

[0028] The illustrative embodiments recognize and take into account that when manufacturing composite structures, fiber layers are usually laid on a tool. These layers can be composed of sheet fibers. These layers can take the form of fabrics, tapes, bundles or other suitable forms. In some cases, resins can be injected or pre-impregnated into these layers.

[0029] The layers are stacked and formed in any desired order. The resin in the sheet is then cured using an oven or autoclave.

[0030] The illustrative embodiments recognize and take into account that composite structures are very strong in-plane, and especially very strong when in tension. Fibers such as carbon fibers carry most of the load in-plane. Composite structures are weaker out-of-plane due to their layered nature. The resin carries most of the load between the layers.

[0031] The illustrative embodiments recognize and take into account that composite materials are lighter than metals, but have higher out-of-plane tension than metals. The illustrative embodiments recognize and take into account that composite structures are susceptible to interlaminar tension (ILT). Interlaminar tension in a composite structure is affected by the design of the composite structure. Interlaminar tension (ILT) stress increases with any of the following factors: larger opening moments, narrower radii, or thinner laminates.

[0032] The exemplary embodiments recognize and take into account that any composite structure having a curved flange will experience interlaminar tension if the curved flange is forced open. The exemplary embodiments recognize and take into account that radial forces (Fr) occur when the angle of the curved flange increases due to external forces. Undesirable amounts of radial forces may cause composite material inconsistencies, such as delamination.

[0033] The illustrative embodiments recognize and take into account that radial forces occur equally in metal or composite materials. The illustrative embodiments recognize and take into account that out-of-plane (Z-direction) weakness of composite materials makes this an important consideration when designing composite structures.

[0034] The illustrative embodiments recognize and take into account that resistance to bending in a composite laminate is due, at least in part, to interlaminar shear forces. In a composite laminate, the resin between the layers holds the layers within a desired radius without the layers sliding relative to each other. The layers of the composite laminate tend to delaminate due to loading that flattens the curved surface of the composite laminate.

[0035] The illustrative embodiments recognize and take into account that the radial force thereon can be estimated using classical bending beam theory or composite FEA methods. The illustrative embodiments recognize and take into account that the radial force can be estimated by the following formula:

[0036]

[0037] Where fILT is the interlaminar tensile stress, M is the moment (in this case the moment arm length), R is the radius, and t is the cross-sectional thickness.

[0038] The illustrative embodiments recognize and take into account that by changing the design of the composite structure, the interlaminar tensile stress is changed. The illustrative embodiments recognize and take into account that by increasing the radius of the composite structure, the interlaminar tensile stress is reduced. More specifically, as the size of R (radius) increases relative to M (moment arm length), the interlaminar tensile stress decreases.

[0039] The illustrative embodiments recognize and take into account that stitching in a composite structure improves the out-of-plane strength of the composite material. Stitching in a composite structure improves the strength of the composite material in an out-of-plane (orthogonal / perpendicular) direction relative to the strength of the resin bonding the layers in the laminate. Stitching in a composite structure can provide fibers in a direction perpendicular to the plane of the laminate, thereby linking at least adjacent laminate layers with fibers / stitching. Stitching in a composite structure increases the three-dimensional properties of the laminate. Stitching in a composite structure provides a load path between layers outside of the resin matrix.

[0040] The illustrative examples show a landing gear system having a composite curved beam. The composite curved beam is formed of fiber layers that are stitched and infused with resin. The stitching increases inter-layer strength. In some illustrative examples, the stitching suppresses inconsistencies in the composite curved beam due to inter-layer tensile stresses. In some illustrative examples, the stitching reduces at least one of size or occurrence of out-of-tolerance inconsistencies.

[0041] An illustrative example provides a landing gear system for an aircraft. The landing gear system includes a composite curved beam having a through-thickness stitch and a curved surface having a radius greater than 5 inches (12.7 centimeters (cm)), and a trunnion offset relative to a neutral surface of the composite curved beam.

[0042] Now go to Figure 1 , an illustration of a block diagram of a manufacturing environment for manufacturing a composite curved beam is depicted in accordance with an exemplary embodiment. The manufacturing environment 100 is an environment for manufacturing a landing gear system 102 for an aircraft 104. The landing gear system 102 for the aircraft 104 includes: a composite curved beam 106 having a through-thickness stitch 108, a curved surface 110 having a radius 112 greater than 5 inches (12.7 cm); and a trunnion 114 offset 116 relative to a neutral surface 118 of the composite curved beam 106.

[0043] A fitting 115 including a trunnion 114 connects a composite curved beam 106 of the landing gear system 102 to a fuselage (not shown) of the aircraft 104. A base 117 of the fitting 115 connects the trunnion 114 to the composite curved beam 106. The base 117 may be any desired size or shape to connect the trunnion 114 to the composite curved beam 106.

[0044] Aircraft 104 is a light aircraft. In some illustrative examples, aircraft 104 is an aircraft having a takeoff weight between 5 kip (2267.96 kilograms (kg)) and 19 kip (8618.25 kg). Aircraft 104 has fixed landing gear and may have up to two engines.

[0045] Prior to designing the composite bending beam 106, the body of the aircraft 104 is designed. The aircraft 104 is designed to include size and weight considerations. After the aircraft 104 is designed, a desired deflection is selected for the landing gear system 102. The composite bending beam 106 is designed to accommodate the desired deflection.

[0046] After setting the desired deflection for the landing gear system 102, a tipping point analysis is performed. The tipping point analysis determines the center of gravity of the aircraft 104. The spacing of the wheel assemblies 150 and 152 in the landing gear system 102 is determined. The spacing of the wheel assemblies 150 and 152 is affected by the tipping point analysis. The spacing of the wheel assemblies 150 and 152 affects the length 148 of the composite bending beam 106. The width 166, length 148, and cross-sectional thickness of the composite bending beam 106 are designed to meet the design features 120 that meet the desired criteria for the landing gear system 102 of the aircraft 104. As the design of the aircraft 104 changes, the design of the landing gear system 102 may also change.

[0047] When designing the landing gear system 102, margin check calculations are performed. One margin check includes the location of the landing gear assembly 102. The margin check calculations for the landing gear assembly 102 include the tip-over point and the spacing of the wheel assembly 150 and the wheel assembly 152. This margin check is performed by drawing a gear triangle between the nose wheel (not shown) and each of the wheels of the main landing gear system, the landing gear system 102 (including the wheel assembly 150 and the wheel assembly 152).

[0048] Another margin check includes the height of the center of gravity (CG) of the aircraft 104. The center of gravity (CG) of the aircraft 104 should be within the gear triangle.

[0049] The "bank" angle is measured in a vertical plane perpendicular to the long side of the gear triangle, through the center of gravity (CG) of the aircraft 104. Another margin check includes the belly height of the aircraft 104 above the ground. Another margin check includes checking the sill height (the distance between the cargo floor and the ground / runway) of the aircraft 104. In performing a margin check of the aircraft 104, the wheel axis height of each of the wheel assemblies 150 and 152 and the position of the fittings and trunnions 114 including the fitting 115 are used to check the sill height of the aircraft 104. In a margin check - the truck sill height must match the cargo aircraft sill height within + / - 2 inches (5.08 cm).

[0050] Other margin checks include the wheel diameter and wheel axis height of wheel assemblies 150 and 152, and the position of fittings / trunnions including fittings 115 and trunnions 114. The position of fittings and trunnions includes the lateral distance (DY, trunnion) between the right trunnion and the left trunnion. The position of fittings and trunnions also includes the vertical distance (DZ, axis) between the center axis 159 of the trunnion 114 and the neutral surface 118 of the composite bending beam 106.

[0051] After performing the design margin check, a deformation margin check is performed on the landing gear system 102. The deformation margin check includes the position of the belly of the aircraft 104 after deflection 124 at landing, whether the G level is within an acceptable range, and whether the stress and strain on the composite bending beam 106 are within an acceptable range.

[0052] The composite bending beam 106 is designed to meet the desired deflection and length determined from previous calculations. The composite bending beam 106 is designed to accommodate landing of the aircraft 104.

[0053] The composite bending beam 106 has design features 120. The design features 120 are selected so that the landing gear system 102 functions desirably during operation of the aircraft 104. The design features 120 are selected so that the landing gear system 102 provides desired performance for the aircraft 104. The design features 120 include strength 122 and deflection 124. Designing the composite bending beam 106 to meet the design features 120 takes into account the cross-sectional thickness (not shown) of the composite bending beam 106, the radius 112, and the moment arm length (not shown) of the composite bending beam 106.

[0054] The strength 122 of the composite bending beam 106 is sufficient to carry the loads generated on the composite bending beam 106 during landing of the aircraft 104. The strength 122 takes into account the thickness (not shown), width 166, moment arm length (not shown) of the composite bending beam 106, radius 112, and torsional moment arm (not shown) of the composite bending beam 106. The stitching 108 increases the strength 122 of the composite bending beam 106.

[0055] The composite bending beam 106 has a deflection 124. The deflection 124 is a measure of the bending of the composite bending beam 106. The composite bending beam 106 deflects to absorb the landing energy of the aircraft 104. The deflection 124 can be measured in a Z direction 126 or as an angular deflection 128. The deflection 124 is a maximum acceptable deflection value of the composite bending beam 106. The maximum acceptable deflection value will vary depending on the design of the aircraft 104.

[0056] The composite bending beam 106 is configured to deflect a specified amount. In some illustrative examples, the composite bending beam 106 is configured to have a deflection 124 (maximum acceptable deflection value) between 12 inches (30.48 cm) and 16 inches (40.64 cm) in the Z direction 126 of the composite bending beam 106. In some illustrative examples, the composite bending beam 106 is configured to have a deflection 124 (maximum acceptable deflection value) between 12 inches (30.48 cm) and 14 inches (35.56 cm) in the Z direction 126 of the composite bending beam 106. In some illustrative examples, the composite bending beam 106 is configured to accommodate angular deflections 128 due to bends of up to 15 degrees.

[0057] When a load is applied to the composite curved beam 106, deflection 124 and angular deflection 128 occur. Deflection 124 and angular deflection 128 occur when the aircraft 104 lands. The deflection 124 accommodated by the composite curved beam 106 is accommodated due to the fiber orientation of the fiber layer 134, the material of the resin 136, the material of the fibers in the fiber layer 134, the curved surface 110, the position of the trunnion 114 relative to the composite curved beam 106, and the characteristics of the stitching 108, including the density 142, the material of the stitching 108, and the thickness of the stitching 108.

[0058] The deflection 124 may also be expressed as a difference between a relaxed radius 130 of the composite bend beam 106 and a fully deflected radius 132 of the composite bend beam 106. The relaxed radius 130 is the radius 112 of the composite bend beam 106 when the composite bend beam 106 has minimal or no load, such as when the aircraft 104 is in flight. The relaxed radius 130 is the radius 112 of the composite bend beam 106 when the aircraft 104 is in flight. The fully deflected radius 132 of the composite bend beam 106 is the radius 112 of the composite bend beam 106 when the composite bend beam has a maximum design load. The fully deflected radius 132 of the composite bend beam 106 is the radius 112 of the composite bend beam 106 during dynamic situations, such as landing the aircraft 104.

[0059] In order to form the composite curved beam 106, the fiber layer 134 is laid on a tool (not shown). When laid on the tool, the fiber layer 134 is a dry layer of unidirectional fibers. The unidirectional fibers are oriented in any desired direction relative to the neutral surface. Conventional fiber orientations include 0 degrees, (+ / -) 30 degrees, (+ / -) 45 degrees, (+ / -) 60 degrees, and 90 degrees relative to the neutral surface. In some illustrative examples, the fiber layer 134 includes at least one fiber layer of the fiber layer 134 having a non-traditional fiber orientation.

[0060] Fiber layers of fiber layers 134 within the range of (+ / -) 30 degrees and (+ / -) 60 degrees handle torsional loads (resistance) on composite curved beam 106. Bending is handled by fiber layers of fiber layers 134 having a fiber orientation of approximately 0 degrees. Fiber layers having a fiber orientation of approximately 0 degrees are aligned with length 148 of composite curved beam 106. In some illustrative examples, non-traditional fiber orientations of up to 10 degrees, such as 5 degrees, accommodate bending of composite curved beam 106.

[0061] The (+ / -) 45 degree layers (also referred to as BETA layers) provide several functions in the stack-up. The (+ / -) 45 degree layers reroute the loads around the boreholes, provide shear strength (Fs), provide shear stiffness (G), prevent splitting in the 0 degree layers, and increase bearing strength in the bolted joints. By increasing bearing strength in the bolted joints, the BETA layers prevent splitting and shearing in the bolted joints. The shear stiffness (G) drives the torsional stiffness, which enables the wheels of wheel assembly 150 and wheel assembly 152 to track properly. An undesirably torsional limber leg of the composite flex beam 106 will cause the wheels to undesirably lose tracking.

[0062] Although the BETA layer can be a (+ / -) 45 degree layer, the BETA layer can range from (+ / -) 15 degrees to (+ / -) 75 degrees. In some illustrative examples, non-traditional fiber orientations between (+ / -) 15 degrees and (+ / -) 75 degrees are provided to redirect loads around the borehole, provide shear strength (Fs), provide shear stiffness (G), prevent splitting in 0 degree layers, and increase bearing strength in bolted joints.

[0063] A certain number of fiber layers 134 and a stacking order (layer order, angles, thicknesses, and layer materials) of the fiber layers 134 are selected based on the design of the aircraft 104. Changing at least one of the size, weight, or desired performance of the aircraft 104 may change the design of the composite curved beam 106. For example, changing at least one of the size, weight, or desired performance of the aircraft 104 may also change the desired number of fiber layers 134 or the desired stacking order.

[0064] The composite bending beam 106 bends to absorb energy. The amount of bending is related to the Young's modulus of elasticity in the length direction (Ex) of the composite bending beam 106. The Young's modulus of elasticity in the length direction (Ex) is affected by the stacking order (layer order, angle, thickness and layer material) of the fiber layer 134. The percentage of 0 degree fiber layers in the fiber layer 134 is determined to produce the desired Young's modulus of elasticity in the length direction (Ex). In an illustrative example, the fiber layers of 0 degrees account for about 50% of the fiber layers 134. In an illustrative example, about 10% of the fiber layers 134 are 90 degree layers. The fiber layers 134 include any desired type of fiber. In some illustrative examples, the fiber layers 134 include carbon fibers. In some illustrative examples, the fiber layers 134 include glass fibers. After laying the fiber layers 134, stitching 108 is applied through the fiber layers 134.

[0065] The stitch 108 is created by inserting a threaded needle (not shown) through the fiber layer 134. The fiber layer 134 is dry when the stitch 108 is applied. Pre-impregnated composite materials or "prepregs" can undesirably transfer resin to the needle, affecting the insertion and removal of the needle. In addition, the resin in the prepreg material can prevent the fibers from temporarily shifting when the needle is inserted, and rebounding after the needle is removed. In the absence of local fiber movement, the fibers will likely be damaged and / or have an undesirable or displaced position. Undesirable transfer of resin to the needle or undesirable displacement of fibers will undesirably affect the quality of the final product.

[0066] Stitching 108 is also referred to as through-thickness reinforcement or through-thickness stitching. Through-thickness stitching (stitching 108) extends throughout composite flex beam 106. In some illustrative examples, stitching 108 passes orthogonally / perpendicularly through each layer of fiber layer 134. As a result, stitching 108 passes orthogonally / perpendicularly through each of the layers of composite flex beam 106. By passing stitching 108 orthogonally / perpendicularly through each of the layers of composite flex beam 106, stitching 108 provides fibers that are orthogonal / perpendicular to the plane of the laminate, composite flex beam 106. Stitching 108 helps resist interlaminar shear stresses.

[0067] Although stitches 108 are described above as extending orthogonally / perpendicularly through each of the layers of composite curved beam 106, in some illustrative examples, stitches 108 extend through each of the layers at an angle. In these illustrative examples, stitches 108 help resist interlaminar shear stresses by providing a load path between the layers outside of the resin matrix. By extending stitches 108 through each of the layers at an angle, stitches 108 increase the three-dimensional nature of the laminate of composite curved beam 106.

[0068] Suture 108 is formed of any desired material. The material for suture 108 is selected to achieve the desired strength 122. The material for suture 108 is selected to be compatible with the material of fiber layer 134. The material for suture 108 is selected to be compatible with resin 136. The material for suture 108 is selected to maintain the desired quality after experiencing the curing temperature. In some illustrative examples, suture 108 is carbon suture. In some illustrative examples, suture 108 is polymer suture. In some illustrative examples, suture 108 is one of polyamide fiber, polyester fiber, polyaramid fiber or other types of polymers. In some illustrative examples, suture 108 is polyester suture. In some illustrative examples, suture 108 is formed of nylon. In some illustrative examples, suture 108 includes more than one material.

[0069] After applying stitching 108 through the fiber layers 134, resin 136 is injected into the fiber layers 134. Applying stitching 108 through the fiber layers 134 along a length 148 of the curved surface 110 forms a plurality of layers 137 of reinforcement. Resin 136 is injected into the plurality of layers 137 of reinforcement. Injecting resin 136 into the plurality of layers 137 of reinforcement forms a resin-infused curved structure (not shown). The resin-infused curved structure (not shown) includes a composite material 140. The resin-infused curved structure (not shown) is cured to produce a composite curved beam 106.

[0070] Resin 136 is injected into the reinforced multilayer 137 using a resin injection device 138 to form a composite material 140. The resin injection device 138 takes any desired form. Some non-limiting examples of the resin injection type performed by the resin injection device 138 include resin transfer molding (RTM), resin injection (RI), controlled atmospheric pressure resin injection (CAPRI), vacuum assisted resin transfer molding (VARTM) or any other desired method of injecting resin 136 into the fiber layer 134. In resin transfer molding, the tool surrounds the workpiece. After the fiber layer is placed in the tool, the tool cover is closed, and then the resin is injected into the tool. In resin injection, the dry fiber layer is placed on the tool / mold and then covered by a vacuum bag. Then, the resin flows between the bag and the workpiece or the tool and the workpiece. In controlled atmospheric pressure resin injection, fine adjustment of pressure is used to avoid resin degassing (outgassing).

[0071] The composite material 140 is cured to form the composite curved beam 106. The composite material 140 is cured using at least one of pressure and temperature.

[0072] The stitching 108 increases the strength 122 of the composite curved beam 106 by providing support in the Z direction 126. The stitching 108 helps resist interlaminar shear stresses. The stitching 108 reduces or eliminates out-of-tolerance inconsistencies in the composite curved beam 106 during operation of the aircraft 104. The stitching 108 prevents or inhibits any delamination in the composite curved beam 106 due to loads applied to the composite curved beam 106. The stitching 108 prevents the layers of the composite curved beam 106 from being pulled apart when the composite curved beam 106 is bent. When loads are applied to the composite material 140 of the composite curved beam 106, the stitching 108 prevents the laminate layers from shearing / sliding relative to each other. The stitching 108 helps resist interlaminar shear stresses.

[0073] The stitching 108 has a density 142 in the composite curved beam 106. The density 142 is a measure of how many times the stitching 108 extends through the thickness of the fiber layer 134 in a region. When the density 142 is greater, the stitching 108 extends through the fiber layer 134 more times in the same region.

[0074] In some illustrative examples, density 142 of stitching 108 is greater near leading edge 143 and trailing edge 144 of composite bending beam 106. Leading edge 143 and trailing edge 144 are opposing edges of width 166 of composite bending beam 106.

[0075] In some illustrative examples, stitching 108 is in a grid pattern 154. Grid pattern 154 has a cell size 156. Cell size 156 is the length of each stitch in a plane. In some illustrative examples, cell size 156 can be up to 2 inches (5.08 cm). In some illustrative examples, grid pattern 154 has a cell size 156 between 0.2 inches (0.508 cm) and 0.5 inches (1.27 cm). In some illustrative examples, grid pattern 154 has a cell size 156 between 0.125 inches (0.3175 cm) and 0.5 inches (1.27 cm).

[0076] When the density 142 of the stitching 108 is greater, the cell size 156 is smaller. When the density 142 of the stitching 108 is greater near the leading edge 143 and the trailing edge 144 of the composite bending beam 106, the cell size 156 is smaller near the leading edge 143 and the trailing edge 144 of the composite bending beam 106.

[0077] The trunnion 114 connects the composite curved beam 106 to the fuselage of the aircraft 104. The trunnion 114 is positioned at least 0.1 inches (0.254 cm) above the top surface 158 of the composite curved beam 106. The offset 116 of the trunnion 114 is determined based on the dimensions and design features 120 of the composite curved beam 106.

[0078] In some illustrative examples, offset 116 is determined by considering the loads to be applied to composite bending beam 106. Offset 116 of trunnion 114 is designed to reduce strain introduced to components of aircraft 104. Trunnion 114 is offset from a top surface 158 of composite bending beam 106 by between 0.1 inches (0.254 cm) and 10 inches (25.4 cm).

[0079] By offsetting trunnions 114, movement of trunnions 114 during loading of composite bending beam 106 is reduced. Reducing movement of trunnions 114 reduces strains introduced to components of aircraft 104 when composite bending beam 106 flattens. In some illustrative examples, trunnions 114 are offset 116 such that movement of trunnions 114 due to bending of composite bending beam 106 is reduced.

[0080] Selecting offset 116 is part of designing aircraft 104 and landing gear system 102. Acceptable values ​​for offset 116 will be within desired tolerances for the geometry of landing gear system 102 and the deformation characteristics of landing gear system 102. If other design aspects of aircraft 104 or landing gear system 102 are changed, offset 116 may also change.

[0081] After designing the vehicle 104, determining the deflection 124, performing the tipping point calculation, determining the spacing of the wheel assembly 150 and the wheel assembly 152, the offset 116 is determined. The offset 116 is determined to account for the rotation of the fitting 115, the flattening of the composite bending beam 106, and the angular deflection 128 of the composite bending beam 106. For the deflection 124, the radius 112 varies between the relaxed radius 130 and the fully deflected radius 132. Due to the deflection 124, the center axis 159 of the trunnion 114 has a lateral movement.

[0082] As the composite bending beam 106 experiences deflection, the fitting 115 rotates. As the composite bending beam 106 experiences deflection 124 and transitions from the relaxed radius 130 to the fully deflected radius 132, the fitting 115 rotates. The lateral displacement is caused by the flattening of the composite bending beam 106. The lateral displacement is caused by the rotation of the fitting 115. The lateral displacement is caused by the compressive strain of the composite bending beam 106. The displacement of the central axis 159 is a function of the rotation angle and the vertical offset.

[0083] A margin check is performed on the amount of strain induced by the displacement of fitting 115 of landing gear system 102 on the fuselage (fuselage frame) of aircraft 104 connected to landing gear system 102. The amount of strain takes into account the strain induced by the flattening of composite bending beam 106, the compression of composite bending beam 106, and the rotation of fittings (including fitting 115) connecting composite bending beam 106 to aircraft 104. When the induced strain on the fuselage of aircraft 104 connected to landing gear system 102 is an acceptable value, offset 116 is an acceptable value. In some illustrative examples, offset 116 is selected so as to reduce the induced strain on the fuselage of aircraft 104 connected to landing gear system 102.

[0084] Offset 116 is selected such that the movement of trunnion 114 has an acceptable value, wherein a maximum acceptable value of the movement of the trunnion is based on a design of aircraft 104 having trunnion 114. The maximum acceptable value of offset 116 is such that when a load is applied to composite curved beam 106, strain induced on surrounding aircraft structure due to the movement of trunnion 114 is acceptable based on the design of aircraft 104. In some illustrative examples, the surrounding aircraft structure includes a fuselage of aircraft 104. Determining whether the strain induced on the surrounding aircraft structure due to the movement of trunnion 114 has an acceptable value is part of a margin check of aircraft 104. When the strain induced on the surrounding aircraft structure due to the movement of trunnion 114 passes the margin check, offset 116 has an acceptable value.

[0085] The maximum acceptable value of the induced strain will depend on the design of the aircraft 104. If the design of the aircraft 104 changes, the acceptable value of the induced strain may also change. If the design of the aircraft 104 changes, the design of the landing gear system 102 (including the design of the composite bending beam 106) may change. The design of the landing gear system 102 (including the design of the composite bending beam 106, the offset 116, and the attachment point 168) will affect the amount of induced strain on the surrounding aircraft structure. Even if the acceptable value of the induced strain does not change, the new design of the aircraft 104 is margin checked again to confirm that the induced strain has an acceptable value. When the design of the aircraft 104 is modified, the margin check is repeated. If the margin check results in an out of tolerance condition, at least one of the design of the offset 116, the attachment point 168, the composite bending beam 106, or the design of another component of the aircraft 104 is changed depending on which margin check is out of tolerance.

[0086] The top surface 158 is a convex surface 160. The bottom surface 162 of the composite bending beam 106 is a concave surface 164. When a load is applied to the composite bending beam 106, the radius 112 of the composite bending beam 106 increases from the relaxed radius 130. When a load is applied to the composite bending beam 106, the top surface 158 flattens. As the composite bending beam 106 flattens, strain is introduced into the composite bending beam 106. Portions of the top surface 158 of the composite bending beam 106 experience compression. Figure 8 As shown, when the composite bending beam 106 is flattened, a portion of the composite bending beam 106 rotates. When the composite bending beam 106 is flattened, the distance between the attachment point 168 of the composite bending beam 106 and the second attachment point (not shown) increases. When the composite bending beam 106 is flattened, the attachment point 168 moves outward. When the composite bending beam 106 is flattened, the second attachment point (not shown) of the second fitting (not shown) of the composite bending beam 106 also moves outward. The distance between the attachment point 168 and the second attachment point increases by the sum of the movement of both the attachment point 168 and the second attachment point.

[0087] The offset 116 of the trunnion 114 from the top surface 158 is configured to reduce strain in the vehicle 104 introduced by movement of the trunnion 114 when the composite bending beam 106 is loaded. The offset 116 is the distance between the top surface 158 and the center axis 159 of the trunnion 114.

[0088] The base 117 of the fitting 119 attaches the trunnion 114 to the composite bending beam 106. The base 117 is connected to the composite bending beam 106 at an attachment point 168. The fitting 119 includes the base 117 and the trunnion 114. The base 117 is connected to the composite bending beam 106 at the attachment point 168. The attachment point 168 on the top surface 158 of the composite bending beam 106 is selected to reduce strain in the aircraft 104 introduced by movement of the trunnion 114 when the composite bending beam 106 is loaded. The arrangement of the trunnion 114 relative to the composite bending beam 106 affects the amount of movement of the trunnion 114 due to bending of the composite bending beam 106. The attachment point 168 on the top surface 158 of the composite bending beam 106 is selected to reduce movement of the trunnion 114 when the composite bending beam 106 is loaded.

[0089] The first end 145 and the second end 146 of the composite bending beam 106 are opposite ends of a length 148 of the composite bending beam 106. The first end 145 is associated with a wheel assembly 150 of the landing gear system 102 of the aircraft 104. The second end 146 is associated with a wheel assembly 152 of the landing gear system 102 of the aircraft 104.

[0090] In some illustrative examples, compound curved beam 106 has curved surface 110 that extends across an entire length 148 of compound curved beam 106. With curved surface 110 extending along entire length 148, radius 112 is larger.

[0091] In some illustrative examples, the curved surface 110 is constant 170. When the curved surface 110 is constant 170, the composite curved beam 106 has a radius that is substantially the same across the composite curved beam 106. When the curved surface 110 is constant 170, the composite curved beam 106 is a portion of a circle. In some illustrative examples, when the curved surface 110 is constant 170, the composite curved beam 106 is a semicircle. In some illustrative examples, the curved surface 110 is varying 172. When the curved surface 110 is varying 172, the curved surface 110 has a radius that is not the same across the composite curved beam 106. In one illustrative example, when the curved surface 110 is varying 172, a cross-section through the curved surface 110 between the leading edge 143 and the trailing edge 144 of the composite curved beam 106 is a portion of an ellipse.

[0092] The stitching 108, composite material 140, and curved surface 110 of the composite curved beam 106 are selected based on the design of the aircraft 104, including size, weight, and design loads, to meet the design features 120 for performance. The stitching 108, composite material 140, and curved surface 110 of the composite curved beam 106 are selected to provide repeated bending of the composite curved beam 106 during operation of the aircraft 104. The stitching 108, composite material 140, and curved surface 110 of the composite curved beam 106 are selected to accommodate repeated dynamic loading of the composite curved beam 106 during landing of the aircraft 104 without introducing out-of-tolerance inconsistencies in the composite curved beam 106.

[0093] Figure 1 The illustration of the manufacturing environment 100 in the example is not meant to imply physical or architectural limitations on the manner in which the illustrative embodiments can be implemented. Other components in addition to or in place of the components shown may be used. Some components may not be necessary. Similarly, boxes are provided to illustrate some functional components. When implemented in the illustrative embodiments, one or more of these boxes may be combined, divided, or combined and divided into different boxes. For example, although not shown, in some illustrative examples, the width 166 of the composite curved beam 106 moves toward the first end 145 and the second end 146 of the composite curved beam 106 and becomes narrower. In some illustrative examples, the width 166 is greater at the attachment point 168 and at the first end 145. In these illustrative examples, the width 166 is larger near the midpoint (not shown) of the composite curved beam 106, near where the composite curved beam 106 is connected to the fuselage (not shown) of the aircraft 104.

[0094] Stitching 108 is applied to fiber layer 134 in any desired manner and in any desired pattern. Figure 1The diameter of stitch 108 is not depicted in FIG, but is selected based on design features 120. In some illustrative examples, the diameter (not shown) of stitch 108 varies within composite curved beam 106. In some illustrative examples, through-thickness stitch 108 has more than one thread diameter in composite curved beam 106.

[0095] Trunnions 114 are connected to compound bending beam 106 in any desired manner. The arrangement of trunnions 114 accommodates arc length changes during bending of compound bending beam 106. In some illustrative examples, the attachment type of trunnions 114 is a sliding connection to further accommodate movement of trunnions 114.

[0096] Now go to Figure 2 , depicts an illustration of a front view of an aircraft having a composite bending beam in a relaxed state, according to an exemplary embodiment. Aircraft 200 is Figure 1 A physical realization of the aircraft 104 .

[0097] Aircraft 200 has a landing gear system 202. Landing gear system 202 includes a composite curved beam 204 having a curved surface 206 with a radius greater than 5 inches (12.7 cm). As shown, radius 208 is greater than 100 inches (254 cm). Composite curved beam 204 has curved surface 206 along the entire length of composite curved beam 204.

[0098] As shown, the curved surface 206 is a constant curved surface. As shown, the composite curved beam 204 has a radius 208 across the length of the composite curved beam 204. However, in other illustrative examples not shown, the curved surface 206 is a varying curved surface having a varying radius.

[0099] The composite bending beam 204 is configured to have a maximum acceptable deflection value in the Z direction 210 of the composite bending beam 204 of between 12 inches (30.48 cm) and 16 inches (40.64 cm). In some illustrative examples, the composite bending beam 204 is configured to have a maximum acceptable deflection value in the Z direction 210 of the composite bending beam 204 of between 12 inches (30.48 cm) and 14 inches (35.56 cm). In some illustrative examples, the composite bending beam 204 is configured to have a maximum acceptable deflection value in the Z direction 210 of the composite bending beam 204 of between 14 inches (35.56 cm) and 16 inches (40.64 cm). Figure 3 The deflection of the composite bending beam 204 is depicted in FIG. The composite bending beam 204 is configured to accommodate angular deflections of up to 15 degrees.

[0100] As shown, the composite curved beam 204 is in a relaxed state 212. The radius 208 may be referred to as a relaxed radius.

[0101] Despite Figure 2 204 , but the composite curved beam 204 has through-thickness reinforcement in the form of through-thickness stitching. The composite curved beam 204 has through-thickness stitching (not shown) and curved surface 206 along the entire length of the composite curved beam 204 .

[0102] Now go to Figure 3 , an illustration of a front view of an aircraft with a composite bending beam in a deflected state is depicted in accordance with an illustrative embodiment. Figure 3 The view 300 of FIG. 2 is a view of the composite flex beam 204 in a deflected state 302. The composite flex beam 204 is in the deflected state 302 due to a load 303 placed on the composite flex beam 204 during landing of the aircraft 200. The composite flex beam 204 flattens between the relaxed state 212 and the deflected state 302. The composite flex beam 204 increases its radius between the relaxed state 212 and the deflected state 302. In the deflected state 302, the radius 304 of the composite flex beam 204 is greater than Figure 2 Radius 208. Radius 304 is referred to as the deflection radius. As shown, radius 304 is greater than 200 inches (508 cm).

[0103] When the composite bending beam 204 is bent, the curved surface 206 follows Figure 2 The composite curved beam 204 is "opened" by increasing the radius 208 of the composite curved beam 204 to the radius 304. When the curved surface 206 is "opened", radial forces appear in the composite curved beam 204. The through-thickness stitching (not shown) of the composite curved beam 204 provides out-of-plane strength. The through-thickness reinforcement (through-thickness stitching) (not shown) suppresses the inconsistency caused by radial forces in the composite curved beam 204.

[0104] Now go to Figure 4 , depicts an illustration of a cross-sectional view of an aircraft having a composite curved beam according to an illustrative embodiment. View 400 is Figures 2 to 3 FIG. 4 is a cross-sectional view of aircraft 200 of FIG. 400 . In view 400 , trunnion 402 and trunnion 404 are visible. In view 400 , trunnion 402 and trunnion 404 have circular cross-sections. Trunnion 402 is part of fitting 403. Trunnion 404 is part of fitting 405.

[0105] Fitting 403 and fitting 405 connect the composite curved beam 204 to a fuselage 406 of the aircraft 200. As shown, the central axis of the trunnion 402 and the central axis of the trunnion 404 are both offset relative to a neutral surface 407 of the composite curved beam 204. As shown, the central axis of the trunnion 402 and the central axis of the trunnion 404 are each offset from a top surface 408 of the composite curved beam 204 by at least 0.1 inches (0.254 cm). As shown, the offset 410 of the central axis of the trunnion 404 from the top surface 408 is greater than 0.1 inches (0.254 cm). An offset 412 of the central axis of the trunnion 402 from the neutral surface 407 is also depicted.

[0106] By offsetting the trunnions 402 and 404, movement of the trunnions 402 and 404 due to deflection of the composite bending beam 204 is controlled. The trunnions 402 are connected to the composite bending beam 204 through the base 417 of the fitting 403. The trunnions 404 are connected to the composite bending beam 204 through the base 415 of the fitting 405. The offset 412 of the trunnions 402 is set by the design of the base 417. The offset 410 of the trunnions 404 is set by the design of the base 415. The arrangement of the trunnions 402 and 404 (including the offsets 410 and 412, and the attachment points 414 of the base 415 of the fitting 405 and the attachment points 416 of the base 417 of the fitting 403) is selected to reduce strain on the surrounding aircraft structure caused by movement of the trunnions 402 and 404 when loads are applied to the composite bending beam 204. The arrangement of the attachment points 414 of the fitting 403 and the attachment points 416 of the fitting 405 along the length of the composite bending beam 204 is selected to reduce the strain on the surrounding aircraft structure caused by the movement of the trunnion 402 and the trunnion 404 when loads are applied to the composite bending beam 204. The arrangement of the attachment points 414 and the offsets 412 of the trunnion 402 is based on the design of the composite bending beam 204, including Figure 2 The arrangement of the attachment point 416 and offset 410 of the trunnion 404 is based on the design of the composite bending beam 204 (including the maximum deflection of the composite bending beam 204 and the expected loads of the aircraft 200). Figure 2 radius 208, the maximum deflection of the composite curved beam 204, and the expected loads on the aircraft 200).

[0107] Now go to Figure 5 , depicts an isometric view of a landing gear system of an aircraft having a composite curved beam according to an exemplary embodiment. The composite curved beam 500 is Figure 1 Physical realization of the composite bending beam 106.

[0108] As shown, the composite curved beam 500 is joined to the fuselage 502 by fittings 503 and 504. Fitting 503 includes a base 505 and a trunnion 506. Fitting 504 includes a base 507 and a trunnion 508. As shown, the trunnions 506 and 508 are positioned above the neutral surface of the composite curved beam 500. As shown, the trunnions 506 and 508 are at least 0.1 inches (0.254 cm) above the top surface of the composite curved beam 500.

[0109] View 509 is a simplified view of the connection between the composite curved beam 500 and a component of an aircraft. The fuselage 502 includes a frame 510, a frame 511, and a frame 512. The frame 510 is connected to the wing (not shown) and the strut (not shown) of the aircraft. The frame 511 is connected to the wing (not shown) and the composite curved beam 500 of the aircraft. The frame 512 is connected to the composite curved beam 500.

[0110] Now go to Figure 6 , depicts an illustration of a front view of a landing gear system with a composite curved beam for an aircraft, according to an exemplary embodiment. View 600 is a front view of a fuselage 502 and a composite curved beam 500. In view 600, additional components of the aircraft are depicted in dashed lines. For example, a wing 602 is depicted in dashed lines. The wing 602 is connected to a frame 510. The wing 602 is also connected to a strut 604, which is shown in dashed lines. The strut 604 is also connected to the frame 510.

[0111] Now go to Figure 7 , depicts an illustration of a front view of a flexure beam in a deflected state and a relaxed state for a landing gear system of an aircraft, according to an illustrative embodiment. View 700 depicts the movement of a composite flexure beam 702 when a load is applied to the composite flexure beam 702. In view 700, the composite flexure beam 702 is shown in a relaxed state 704 and a fully deflected state 706.

[0112] In the relaxed state 704, the composite bending beam 702 has a relaxed radius 708. In the fully deflected state 706, the composite bending beam 702 has a fully deflected radius 710. In the relaxed state 704, the load on the composite bending beam 702 is composed of the attached wheel assembly. In the fully deflected state 706, the load is greater than the reactive load due to the dynamic landing of the fully loaded aircraft.

[0113] As the composite bending beam 702 absorbs the landing load, the composite bending beam 702 changes from the relaxed radius 708 to a deflected radius, such as a fully deflected radius 710. As can be seen in view 700, as the composite bending beam 702 absorbs the load of the landing, the composite bending beam 702 flattens. As the composite bending beam 702 flattens, the distance between the attachment points of the composite bending beam 702 increases.

[0114] In view 700, a composite curved beam 702 has an attachment point 712 and an attachment point 714. Attachment point 712 and attachment point 714 each move outward between relaxed radius 708 and fully deflected radius 710. The distance between composite curved beams 702 increases by the sum of the distances that each of attachment points 712 and 714 moves outward.

[0115] When the composite bending beam 702 is flattened, the top compression surface 716 shortens. When the composite bending beam 702 is loaded, the material in the composite bending beam 702 is strained. The top compression surface 716 shortens with the applied load. The bottom surface 718 lengthens with the applied load.

[0116] At the attachment point 712, the composite curved beam 702 is rotated as Figure 8 As a result of the rotation of the attachment point 712, the attached trunnion (not shown) will also move. It is desirable to offset the trunnion (not shown) above the composite curved beam 702 so that the movement toward the attachment point 714 has an acceptable value. The acceptable value is determined based on the design of the aircraft having the trunnion. The acceptable value takes into account the strain introduced into the aircraft design.

[0117] If the trunnion (not shown) is below the upper compression surface 716 of the composite bending beam 702, the movement of the trunnion during loading is in an undesirable direction. If the trunnion (not shown) is below the upper compression surface 716 of the composite bending beam 702, the movement of the trunnion during loading will add stress to the entire aircraft fuselage and landing gear assembly.

[0118] The attachment of the composite bending beam 702 to the fuselage (not shown) consists of a rotating support, including a trunnion (not shown), which is located above the composite bending beam 702 to eliminate the mismatch between the flattening of the composite beam and the compressive strain. By arranging the attachment points 712 and 714 at the desired locations and offsetting the trunnion (not shown) relative to the neutral surface of the composite bending beam 702, the mismatch between the flattening of the composite beam and the compressive strain will be eliminated. By arranging the attachment points 712 and 714 at the desired locations and offsetting the trunnion (not shown) relative to the neutral surface of the composite bending beam 702, the strain in the attachment, frame and aircraft structure is reduced.

[0119] Now go to Figure 8 , depicts an illustration of a front view of a portion of a flexure beam in a deflected state and a relaxed state for a landing gear system of an aircraft, according to an illustrative embodiment. View 800 depicts movement of a composite flexure beam 802 when a load is applied to the composite flexure beam 802. In view 800, a portion of the composite flexure beam 802 is shown in a relaxed state 804 and a fully deflected state 806.

[0120] The trunnion 808 is connected to the compound bending beam 802. For clarity and to see the movement of the trunnion 808, the connection between the trunnion 808 and the compound bending beam 802 is not shown. The trunnion 808 is connected to the compound bending beam 802 in any desired manner and using any desired mechanical connection. The trunnion 808 is connected to the attachment point 816 on the compound bending beam 802 by a mechanical connection (not shown). The mechanical connection creates an offset 810. The trunnion 808 has an offset 810 from an upper surface 811 of the compound bending beam 802. As shown, the offset 810 is approximately 2 inches (5.08 cm).

[0121] The composite bending beam 802 flattens as it bends between the relaxed state 804 and the fully deflected state 806. The composite bending beam 802 undergoes angular deflection when flattening. The composite bending beam 802 undergoes angular deflection 812 between the relaxed state 804 and the fully deflected state 806. As shown, the angular deflection 812 is approximately 9.3 degrees. The angular deflection 812 is only a non-limiting example of the value of the angular deflection of the composite bending beam 802 due to dynamic loading. The composite bending beam 802 is configured to accommodate angular deflections of up to 15 degrees. The amount of angular deflection experienced by the composite bending beam 802 is affected by the amount of load placed on the composite bending beam 802. Introducing a larger load increases the amount that the composite bending beam 802 bends, and also increases the amount of angular deflection of the composite bending beam 802. In some illustrative examples, the angular deflection of the composite bending beam 802 may also be referred to as the rotation of the composite bending beam 802.

[0122] As the composite curved beam 802 experiences angular deflection 812, the center of the trunnion 808 moves inwardly a distance 814. As shown, the distance 814 is less than the movement of the attachment point 816. As shown, the distance 814 is less than half an inch (1.27 cm). As shown, the movement of the attachment point 816 is greater than half an inch (1.27 cm). Due to the location of the trunnion 808 (including the offset 810 and the location of the attachment point 816), the displacement of the center of the trunnion 808 is an acceptable value and a desired direction.

[0123] The offset 810 reduces the movement of the trunnion 808. The movement of the trunnion 808 due to the angular deflection 812 of the composite bending beam 802 would be greater if the trunnion 808 was positioned at the attachment point 816. By reducing the movement of the trunnion 808, the strain introduced into the attached fuselage (not shown) is reduced.

[0124] Now go to Fig. 9 , depicts an illustration of a stitched cross-sectional view of a first end of a composite curved beam for an aircraft, according to an illustrative embodiment. View 900 is a cross-sectional view through a portion of a composite curved beam 902. Composite curved beam 902 is Figure 1900 is a cross-sectional view through a composite curved beam 902, for illustrative purposes only. There may be any desired number of layers in the fiber layers 904. The view 900 is a cross-sectional view through a composite material 908, which is formed from the fiber layers 904 that are infused with resin and cured. Cross-hatching is depicted in the composite material 908.

[0125] The through-thickness stitching 906 improves the out-of-plane strength of the composite curved beam 902. The stitching 906 suppresses inconsistencies in the composite curved beam 902 due to inter-laminar tensile stresses. The stitching 906 provides a mechanical connection between the layers of the composite curved beam 902 to reduce or eliminate out-of-tolerance inconsistencies. The stitching 906 prevents the layers of the composite curved beam 902 from being pulled apart when the composite curved beam 902 is bent. The stitching 906 can better resist inter-laminar stresses than using only resin alone. When the composite curved beam 902 is bent, the stitching 906 prevents the layers from moving relative to each other. In addition, the stitching 906 can prevent any delamination that forms between the layers of the composite curved beam 902.

[0126] Now go to Fig.10 , depicts an isometric illustration of the distribution of stitching in a composite curved beam for an aircraft, according to an illustrative embodiment. View 1000 is a view of a plurality of layers of reinforcement 1001. The plurality of layers of reinforcement 1001 are formed by applying stitching 1002 in fiber layers 1004. In view 1000, resin has not yet been injected into the plurality of layers of reinforcement 1001. The individual fiber layers in fiber layers 1004 are dry. Before stitching 1002 is added to form the plurality of layers of reinforcement 1001, the fiber layers 1004 have been formed into curved surface 1006.

[0127] Stitching 1002 extends across fiber layer 1004. As shown, stitching 1002 has a grid pattern 1008. The density 1010 of stitching 1002 increases near leading edge 1012. The density 1010 of stitching 1002 also increases near trailing edge 1014. The density 1010 of stitching 1002 is greater in areas that experience the greatest potential for delamination.

[0128] Grid pattern 1008 may have a cell size of up to 2 inches (5.08 cm). In some illustrative examples, grid pattern 1008 has a cell size in the range of 0.125 inches (0.3175 cm) to 0.5 inches (1.27 cm). Near leading edge 1012 and trailing edge 1014, cell size 1016 is smaller than cell size 1018 between leading edge 1012 and trailing edge 1014. Smaller cell sizes may provide greater strength against interlaminar shear stresses. Smaller cell sizes also provide greater delamination resistance.

[0129] Now go to Fig.11 , depicts an illustration of a flow chart of a method of forming a landing gear system for an aircraft, according to an exemplary embodiment. The method 1100 may be used to form Figure 1 The landing gear system 102 of FIG. The method 1100 may be used to form Figures 2 to 4 The composite curved beam 204 can be formed using the method 1100. Figures 5 and 6 The composite curved beam 500 can be formed using the method 1100. Figure 7 The composite curved beam 702 can be formed using the method 1100. Figure 8 The composite curved beam 802 can be formed using the method 1100. Fig. 9 The operations of method 1100 may be performed at Fig.10 This is implemented in application stitching 1002.

[0130] The method 1100 lays fiber layers 134 into a curved surface 110, each fiber layer having a corresponding fiber orientation (operation 1102). The method 1100 stitches through the fiber layers 134 along a length 148 of the curved surface 110 to form a plurality of reinforced layers 137, with a density 142 of stitches 108 being greater near a leading edge 143 and a trailing edge 144 of the curved surface 110 (operation 1104). The method 1100 injects resin 136 into the plurality of reinforced layers 137 to form a resin-infused curved structure (operation 1106). The method 1100 cures the resin-infused curved structure to form a composite curved beam 106 of the landing gear system 102 (operation 1108). Thereafter, the method 1100 terminates.

[0131] In some illustrative examples, stitching 108 includes stitching 108 through fiber layers 134 in a grid pattern 154 having a cell size 156 between 0.2 inches (0.508 cm) and 0.5 inches (1.27 cm) (operation 1110). In some illustrative examples, laying fiber layers 134 includes laying at least one layer having a non-traditional fiber orientation (operation 1112).

[0132] In some illustrative examples, method 1100 attaches composite curved beam 106 to aircraft 104 using trunnions 114 that are at least 0.1 inches (0.254 cm) above composite curved beam 106 (operation 1114 ). Offset 116 of trunnions 114 is designed to reduce stress introduced into components of aircraft 104 .

[0133] Now go to Fig.12 , an illustration of a flow chart of a method of operating an aircraft having a landing gear system with a composite bending beam is depicted in accordance with an illustrative embodiment. The method 1200 may be used Figure 1 The landing gear system 102. The method 1200 may be used Figures 2 to 4 The composite curved beam 204. The method 1200 may be used Figures 5 and 6 The composite curved beam 500. The method 1200 may be used Figure 7 The composite curved beam 702. The method 1200 may be used Figure 8 The composite curved beam 802. The method 1200 may be used Fig. 9 Composite curved beam 902.

[0134] The method 1200 flies the aircraft 104 (operation 1202). The method 1200 absorbs dynamic loads from the landing of the aircraft 104 in the composite curved beam 106 by flattening the composite curved beam 106, the composite curved beam 106 having a through-thickness stitching 108 and a curved surface 110 having a radius (112, 130) greater than 5 inches (12.7 cm) in a relaxed state (operation 1204). The composite curved beam 106 does not completely flatten when the composite curved beam 106 absorbs the dynamic loads. The amount of flattening of the composite curved beam 106 causes the composite curved beam 106 to deflect up to 12 inches (30.48 cm) in the Z direction of the composite curved beam 106. The amount of flattening of the composite curved beam 106 causes the composite curved beam 106 to experience an angular deflection of up to 15 degrees. Thereafter, the method 1200 terminates.

[0135] In some illustrative examples, trunnion 114 is coupled to composite curved beam 106 and offset 116 from neutral surface 118 of composite curved beam 106, and absorbing the dynamic load includes moving the center of trunnion 114 inward (operation 1206). Through-thickness stitching 108 prevents out-of-tolerance inconsistencies in composite curved beam 106 due to inter-laminar tensile stress. Method 1200 uses through-thickness stitching 108 to prevent delamination in composite curved beam 106 due to inter-laminar tensile stress (operation 1208).

[0136] As used herein, the phrase "at least one" when used with a list of items means that different combinations of one or more of the listed items can be used, and only one of the items in the list may be required. In other words, "at least one" means that any combination of items and numbers of items can be used from the list, but not all of the items in the list are required. The item may be a specific object, thing, or category.

[0137] For example, "at least one of item A, item B, or item C" may include, but is not limited to, item A, item A and item B, or item B. This example may also include item A, item B, and item C, or item B and item C. Of course, any combination of these items may exist. In other examples, "at least one" may be, for example, but not limited to, two of item A, one of item B, and ten of item C; four of item B and seven of item C; or other suitable combinations.

[0138] The flowcharts and block diagrams in the different depicted embodiments illustrate the architecture, functions and operations of some possible implementations of the devices and methods in the illustrative embodiments. In this regard, each box in the flowchart or block diagram may represent a module, segment, function and / or a part of an operation or step.

[0139] In some alternative implementations of the illustrative embodiments, the functions marked in the blocks may not occur in the order marked in the figure. For example, in some cases, two blocks shown in succession may be executed substantially simultaneously, or the blocks may sometimes be executed in the reverse order, depending on the functions involved. Moreover, in a flow chart or block diagram, other blocks may be added in addition to the illustrated blocks. Some blocks may be optional. For example, Fig.11 Operations 1110 to 1114 may be optional. As another example, Fig.12 Operations 1206 to 1208 may be optional.

[0140] You can Fig.13 Aircraft manufacturing and service method 1300 is shown and Fig.14 Exemplary embodiments of the present disclosure are described in the context of aircraft 1400 as shown. Fig.13 , a diagram of an aircraft manufacturing and service method is depicted according to an illustrative embodiment. During pre-production, aircraft manufacturing and service method 1300 may include Fig.14 Specification and design 1302 of the aircraft 1400 and material procurement 1304 .

[0141] During production, component and subassembly manufacturing 1306 and system integration 1308 of the aircraft 1400 occurs. Thereafter, the aircraft 1400 may undergo certification and delivery 1310 to be placed into service 1312. While in service 1312 by a customer, the aircraft 1400 is scheduled for routine maintenance and overhaul 1314, which may include modification, reconfiguration, refurbishment, or other maintenance and overhaul.

[0142] Each of the processes of the aircraft manufacturing and service method 1300 may be performed or carried out by a system integrator, a third party, and / or an operator. In these examples, the operator may be a customer. For purposes of this description, a system integrator may include, but is not limited to, any number of aircraft manufacturers and major system subcontractors; a third party may include, but is not limited to, any number of contractors, subcontractors, and suppliers; and an operator may be an airline, a leasing company, a military entity, a service organization, etc.

[0143] Now refer to Fig.14 , depicts a diagram of an aircraft in which an illustrative embodiment may be implemented. In this example, aircraft 1400 is Fig.13 14. Aircraft manufacturing and service method 1300 is produced and may include fuselage 1402 having multiple systems 1404 and interior 1406. Examples of systems 1404 include one or more of propulsion system 1408, electrical system 1410, hydraulic system 1412, and environmental system 1414. Any number of other systems may be included. Although an aviation example is shown, different illustrative embodiments may be applied to other industries, such as the automotive industry.

[0144] Apparatus and methods embodied herein may be employed during at least one of the stages of aircraft manufacturing and service method 1300. Fig.13 One or more illustrative embodiments are used during at least one of component and subassembly manufacturing 1306, system integration 1308, or maintenance and overhaul 1314 of the landing gear system 102. For example, the illustrative embodiments are used during component and subassembly manufacturing 1306 to form a composite curved beam 106 of the landing gear system 102. As an example, the method 1100 can be used during component and subassembly manufacturing 1306 to form the composite curved beam 106. The landing gear system 102 is a portion of a fuselage 1402 of an aircraft 1400. The method 1100 can be used to manufacture a portion of the aircraft 1400, such as the fuselage 1402.

[0145] The illustrative example shows a landing gear system having a composite flex beam. The composite flex beam is formed from layers of fibers that are stitched and infused with resin.

[0146] Stitching improves out-of-plane strength and reduces interlaminar tension. Stitching reduces or prevents delamination in composite flex beams. Resin infusion is a manufacturing method used to make composite flex beams with out-of-plane stitching.

[0147] An illustrative example provides a landing gear system configured to provide desired strength and deflection at a lower weight than a metal landing gear system. An illustrative example provides a landing gear system configured to provide desired strength and deflection at a lower cost than an oil hydraulic strut. An illustrative example provides a composite bending beam configured to have a desired strength to carry the loads of an aircraft landing. The composite bending beam is configured to bend a specified amount without causing inconsistency. In the landing gear system, the deflection absorbs the loads of an aircraft landing using the composite bending beam. Through-thickness stitching in the composite bending beam provides off-plane strength. The offset of the trunnion in the landing gear system reduces stress in the attached aircraft structure.

[0148] In addition, this disclosure includes examples according to the following clauses:

[0149] Item 1. A landing gear system for an aircraft, the landing gear system comprising: a composite curved beam having through-thickness stitching and a curved surface having a radius greater than 5 inches (12.7 centimeters (cm)); and an ear shaft connected to the composite curved beam and offset from a neutral surface of the composite curved beam.

[0150] Clause 2. The landing gear system of clause 1, wherein the composite bending beam is configured to have a maximum acceptable deflection value in the Z direction of the composite bending beam between 12 inches (30.48 cm) and 14 inches (35.56 cm).

[0151] Clause 3. A landing gear system according to clause 1 or 2, wherein the composite bending beam is configured to accommodate angular deflections of up to 15 degrees.

[0152] Clause 4. A landing gear system according to any one of clauses 1 to 3, wherein the density of the stitching is greater near the leading and trailing edges of the composite bending beam.

[0153] Clause 5. A landing gear system as recited in any one of Clauses 1 to 4, wherein the stitching is in a grid pattern having a cell size between 0.2 inches (0.508 cm) and 0.5 inches (1.27 cm).

[0154] Clause 6. A landing gear system according to any one of clauses 1 to 5, wherein the trunnion is offset from the top surface of the composite bending beam by between 0.1 inches (0.254 cm) and 10 inches (25.4 cm) so that movement of the trunnion has an acceptable value, wherein the maximum acceptable value of movement of the trunnion is based on the design of the aircraft having the trunnion.

[0155] Clause 7. A landing gear system according to Clause 6, wherein the maximum acceptable value of trunnion movement is such that, based on the design of the aircraft, when a load is applied to the composite bending beam, the strain induced on the surrounding aircraft structure due to the movement of the trunnion is acceptable.

[0156] Clause 8. A landing gear system according to any one of clauses 1 to 7, wherein the curved surface extends across the entire composite curved beam.

[0157] Clause 9. The landing gear system of any one of Clauses 1 to 8, wherein the through-thickness stitching extends across the entire composite curved beam.

[0158] Clause 10. A landing gear system according to any one of Clauses 1 to 9, wherein the through-thickness stitching has more than one wire diameter.

[0159] Clause 11. A landing gear system for an aircraft, the landing gear system comprising: a composite curved beam having through-thickness stitching and a curved surface along the entire length of the composite curved beam, the density of the stitching being greater near the leading edge and the trailing edge of the composite curved beam.

[0160] Clause 12. The landing gear system of clause 11, wherein the composite bending beam is configured to have a maximum acceptable deflection value in the Z direction of the composite bending beam between 12 inches (30.48 cm) and 14 inches (35.56 cm).

[0161] Clause 13. The landing gear system of Clause 11, wherein the composite bending beam is configured to accommodate angular deflections of up to 15 degrees.

[0162] Clause 14. A landing gear system according to any one of clauses 1 to 13, wherein the stitching is in a grid pattern.

[0163] Clause 15. The landing gear system of Clause 14, wherein the grid pattern has a cell size between 0.2 inches (0.508 cm) and 0.5 inches (1.27 cm).

[0164] Clause 16. A landing gear system according to any one of clauses 1 to 15, wherein the curved surface is a varying curved surface.

[0165] Clause 17. The landing gear system of any one of clauses 1 to 16, wherein a width of the composite bending beam narrows moving toward the first and second ends of the composite bending beam.

[0166] Clause 18. The landing gear system of any one of Clauses 1 to 17, wherein a width of the composite curved beam is greater near a fuselage of the aircraft.

[0167] Clause 19. The landing gear system of any of Clauses 1 to 18, further comprising: a trunnion positioned at least 0.1 inches (0.254 cm) above a top surface of the composite bending beam.

[0168] Item 20. A method of forming a landing gear system for an aircraft, the method comprising the steps of: laying fiber layers into a curved surface, each fiber layer having a corresponding fiber orientation; stitching through the fiber layers along the length of the curved surface to form a plurality of reinforced layers, the density of the stitching being greater near the leading edge and the trailing edge of the curved surface; injecting resin into the plurality of reinforced layers to form a resin-injected curved structure; and curing the resin-injected curved structure to form a composite curved beam of the landing gear system.

[0169] Clause 21. The method according to clause 20, further comprising the step of attaching the composite bending beam to the aircraft using an ear shaft, wherein the ear shaft is located at least 0.1 inches (0.254 cm) above the composite bending beam so as to reduce the movement of the ear shaft caused by the bending of the composite bending beam.

[0170] Clause 22. The method of clause 20 or 21, wherein the stitching comprises stitching through the fiber layer in a grid pattern, the grid pattern having a cell size between 0.2 inches (0.508 cm) and 0.5 inches (1.27 cm).

[0171] Clause 23. The method of any of Clauses 20 to 22, wherein laying down the fiber layers comprises laying down at least one layer having a non-conventional fiber orientation.

[0172] Clause 24. A method of operating an aircraft having a landing gear system with a composite flex beam, the method comprising the steps of: causing the aircraft to fly; and absorbing dynamic loads from landing of the aircraft in the composite flex beam by flattening the composite flex beam, the composite flex beam having through-thickness stitching and a curved surface having a radius greater than 5 inches (12.7 cm) in a relaxed state.

[0173] Clause 25. A method of operating an aircraft having a landing gear system according to any one of Clauses 1 to 19 with a composite bending beam, the method comprising the steps of: causing the aircraft to fly; and absorbing dynamic loads from landing of the aircraft in the composite bending beam by flattening the composite bending beam, wherein the radius in a relaxed state is greater than 5 inches (12.7 cm).

[0174] Clause 26. The method of clause 24 or 25, wherein a trunnion is connected to the composite bending beam and is offset relative to a neutral surface of the composite bending beam, wherein absorbing the dynamic load comprises moving a center of the trunnion inwardly.

[0175] Clause 27. The method of any of Clauses 24 to 26, using the through-thickness stitching to prevent delamination in the composite bending beam due to interlaminar tensile stresses.

[0176] Descriptions of different illustrative embodiments have been presented for purposes of illustration and description, and are not intended to be exhaustive or limited to the embodiments of the disclosed forms. Many modifications and variations will be apparent to those of ordinary skill in the art. In addition, different illustrative embodiments may provide different features compared to other illustrative embodiments. The selected embodiments are selected and described in order to best explain the principles of the embodiments, practical applications, and to enable others of ordinary skill in the art to understand the disclosure of various embodiments with various modifications suitable for the specific purposes contemplated.

Claims

1. A landing gear system for an aircraft, the landing gear system comprising: A composite curvature beam having through-thickness stitching and a curved surface along the entire length of the composite curvature beam, the density of the stitching being greater near the leading and trailing edges of the composite curvature beam.

2. The landing gear system according to claim 1, wherein: The stitching is in a grid pattern.

3. The landing gear system according to claim 2, wherein: The grid pattern has a cell size between 0.2 inches (0.508 cm) and 0.5 inches (1.27 cm).

4. The landing gear system according to claim 1, wherein: The curved surface is a changing curved surface.

5. The landing gear system according to claim 1, wherein: The width of the composite bending beam narrows moving toward the first end and the second end of the composite bending beam.

6. The landing gear system according to claim 1, wherein: The width of the composite curved beam is greater near the fuselage of the aircraft.

7. The landing gear system according to claim 1, further comprising: A trunnion is positioned at least 0.1 inches (0.254 cm) above a top surface of the composite curved beam.

8. A method of operating an aircraft having a landing gear system with a composite bending beam, the method comprising the steps of: causing the aircraft to fly; and absorbing dynamic loads from the landing of the aircraft in the composite curved beam by flattening the composite curved beam, the composite curved beam having through-thickness stitching and a curved surface having a radius greater than 5 inches (12.7 cm) in a relaxed state.

9. The method according to claim 8, wherein: A trunnion is connected to the composite bending beam and is offset relative to a neutral surface of the composite bending beam, wherein absorbing the dynamic load includes moving a center of the trunnion inwardly.

10. The method of claim 8, using the through-thickness stitching to prevent delamination in the composite bending beam due to interlaminar tensile stresses.