Sanitary napkin with marl moss

Abstract

The invention provides a sanitary napkin made of margarita and a making method of the sanitary napkin. The sanitary napkin has good air permeability and water absorption, can effectively reduce bacterium breeding, has an antibacterial effect, improves sanitary performance, and is simple in preparation method, low in cost and suitable for large-scale production. The method comprises the following steps: 1, collecting fresh marlidinum and cleaning; 2, steeping the marl moss in clear water, and uniformly stirring the marl moss and the clear water; 3, filtering to obtain marlidinum slurry; and 4, uniformly mixing and stirring 100 parts of marlidinum serous fluid, 1-3 parts of 35ml of water and a carboxymethyl cellulose adhesive. 5, pouring the mixture into a mold, and carrying out compression molding; and 6, drying at 60 DEG C, and cutting into a required size to obtain a sanitary towel finished product.

Description

1. Technical Field

[0001] The present invention relates to a preparation method of sanitary napkins, in particular to sanitary napkins made of Sphagnum moss. 2. Background Art

[0002] Traditional sanitary napkins are mainly made of chemical fibers and plastics, which have problems such as airtightness and easy allergy. Therefore, it is of great significance to develop a natural and environmentally friendly preparation method for sanitary napkins. 3. Summary of the Invention

[0003] The present invention provides a sanitary napkin made of Sphagnum moss, aiming to solve the deficiencies of traditional sanitary napkins. Sphagnum moss has the advantages of strong water absorption, good air permeability, antibacterial property, etc., and is suitable for the production of sanitary napkins.

[0004] 3.1 Preparation Method

[0005] (1) Collect Sphagnum moss and clean it thoroughly.

[0006] (2) Soak the Sphagnum moss in water and stir evenly.

[0007] (3) Filter to obtain Sphagnum moss slurry.

[0008] (4) Mix 100 grams of Sphagnum moss slurry with 35 milliliters of water and 1 - 3 parts of adhesive and stir evenly.

[0009] (5) Pour the mixture into a mold and press it into shape.

[0010] (6) Dry and cut to obtain the finished product of the sanitary napkin.

[0011] 3.2 Advantages

[0012] (1) The sanitary napkin made of Sphagnum moss by the present invention has good air permeability and water absorption, and can effectively reduce the growth of bacteria.

[0013] (2) Sphagnum moss has antibacterial effect, which can improve the sanitary performance of the sanitary napkin.

[0014] (3) The preparation method of the present invention is simple and low - cost, and is suitable for large - scale production. 4. Embodiments

[0016] The present invention will be described in detail below through specific embodiments.

[0017] Example 1.

[0018] (1) Collect fresh Sphagnum moss and clean it thoroughly.

[0019] (2) Soak the Sphagnum moss in clean water and stir evenly.

[0020] (3) Filter to obtain Sphagnum serosa;

[0021] (4) Mix the Sphagnum serosa and starch binder evenly by stirring;

[0022] (5) Pour the mixture into a mold and press it into shape;

[0023] (6) Dry at room temperature and cut into the required size to obtain the finished sanitary napkin product.

[0024] Example 2.

[0025] (1) Collect dry Sphagnum and grind it into powder;

[0026] (2) Soak the Sphagnum powder in warm water and stir evenly;

[0027] (3) Filter to obtain Sphagnum serosa;

[0028] (4) Mix 100 grams of Sphagnum serosa with 1 - 3 parts of 350 milliliters of water and carboxymethyl cellulose binder, and stir evenly;

[0029] (5) Pour the mixture into a mold and press it into shape;

[0030] (6) Dry at 60 °C and cut into the required size to obtain the finished sanitary napkin product.

Claims

1. A sanitary napkin made of marl moss, characterized in that: The sanitary napkin is formed by mixing and pressing the marl moss slurry and the adhesive.

2. The sanitary napkin according to claim 1, characterized in that The adhesive is a starch adhesive or a carboxymethyl cellulose adhesive.

3. The sanitary napkin according to claim 1 or 2, characterized in that: The thickness of the sanitary napkin is 0.5-2 mm.

4. A method for making sanitary napkins using marl moss, characterized in that: The following steps are involved: (1) Collect the marl moss and clean it; (2) Soak the marl moss in water and stir evenly; (3) filtering to obtain the marl moss liquid; (4) Mix 100 g of the marl moss slurry with 1-3 parts of 35 ml of water and the adhesive, and stir evenly; (5) pouring the mixture into a mold and pressing it into shape; (6) Drying and cutting to obtain the finished sanitary napkin.

5. The method according to claim 4, characterized in that The adhesive is a starch adhesive or a carboxymethyl cellulose adhesive.

6. The method according to claim 4 or 5, characterized in that: The drying temperature is room temperature or 60°C.