REACTIVE 2K COATING COMPOSITION

Description

[0001] The present invention relates to a two-component coating composition comprising a resin component (B) containing at least one epoxy resin as a curable component, and a hardener component (A) containing an amine hardener system as a curing agent for the epoxy resin of the resin component (B). The hardener component (A) of the two-component coating composition according to the invention further contains water and at least one cellulose derivative. The cellulose derivative contained in the hardener component (A) has a Brookfield viscosity, determined by means of a Brookfield rotational viscometer at 25°C, 60 rpm, spindle 2, on a 5% solution in water, of 2000 mPa s or less, and the weight ratio of water to the cellulose derivative in the hardener component (A) is 10:1 to 20:1. The present invention further relates to the use of the two-component coating composition as a floor coating. Background of the invention

[0002] US 2022 / 325106 describes a two-component coating composition comprising at least one water-dispersible polymer mixture (A) which has at least one mercapto-reactive group selected from the group of epoxides and Michael acceptors, and at least one water-emulsifiable thiol (B), comprising as forming components (Ba) at least one compound having at least two mercapto groups, (Bb) at least one compound having at least one mercapto-reactive group and at least one dispersing group, wherein the forming component (Ba) has a Hansch parameter of at least 2.0.

[0003] DE 10 2011 118507 relates to dyed cellulose containing finely divided particles coated and / or colored with a dye in the presence of a reactive binder comprising a polyfunctional and water-dispersible epoxy resin-amine binder, as a thermosetting or elastomeric layer in a physically and chemically durable form.

[0004] FR 2 861 737 describes thixotropic gels (I) consisting of aqueous emulsions or dispersions or water-dilutable compositions containing (a) at least one polymer or copolymer, (b) optionally a hardener having functions reactive with (a) and (c) at least one thickener which is soluble in water or aqueous solvents or miscible with water and which contains hydrophobic and hydrophilic functions.

[0005] CN 103 865 365 relates to a coating system consisting of a water-based base coat, a water-based intermediate coat and a solvent-based top coat, wherein the water-based base coat contains polyester resin, the water-based intermediate coat contains polyurethane resin and the solvent-based top coat contains polyester resin and isocyanate.

[0006] WO 02 / 062909 describes curable coating compositions, particularly for use in automotive refinishing, wherein a binder component of the two-component coating composition comprises an epoxy resin having at least one acetoacetic ester functionality and at least one epoxy group, and one or more reactive components having at least two acetoacetic ester functionalities. Suitable reactive components include structured reactive diluents, an acrylic polymer, a polyester, or a combination thereof. A crosslinking component of the coating composition comprises polyamine, a blocked polyamine, or a mixture thereof.

[0007] Two-component coating compositions comprising a resin component (B) containing at least one epoxy resin as a curable component, and a hardener component (A) containing an amine hardener system as a curing agent for the epoxy resin of resin component (B), as well as water, are known in the art. Such reactive plastic coatings are used, for example, as primers or as wear layers for protecting mineral substrates (e.g., concrete) in parking decks, garages, and other surfaces, for example, as an OS8 system. OS8 generally describes a surface protection system for concrete floor slabs as a driveable coating system. An OS 8 coating is a liquid-applied coating specifically designed for roadways, underground garages, ramps, etc.It is particularly suitable as a surface protection system for new buildings and the renovation of underground garages following damage or destruction to the old road surface caused by road salt. The OS 8 coating is applied as a protective system with minimum layer thicknesses of 1.00 mm to 5.00 mm, with a minimum thickness of 2.00 mm being recommended for roadway areas and 3.00 mm for ramp areas. The protective system includes: primer, scratch and leveling filler, a wearing course and a top coat. It ensures the protection of concrete in underground garages and parking garages in the following problem areas: Floor slabs in underground garages and parking garages and concrete floor slabs in underground garages and parking garages are exposed to heavy wear. Reinforcement corrosion due to cracking, penetrating moisture, chlorides from road salt, carbon dioxide (CO2) and temperature-induced deformation are the greatest risks.As a rule, quartz sand is added to create a non-slip surface to ensure the safety of people and vehicles.

[0008] When reacting the hardener component (A) with the resin component (B) of a 2-component composition, maintaining a desired stoichiometry, especially usually in the range of an (optimal) 1:1 stoichiometry, is of particular importance for network formation. The optimal, i.e., the maximum possible glass transition temperature T g of the resulting network is generally achieved at a molar ratio of the reactants of 1:1. If one of the two is present in excess, the T g is significantly lower. The T g influences the strength and resistance of the wear layer. However, the stoichiometry is influenced in an unpredictable way by the water in the hardener component (A). The degree of crosslinking is also influenced by the presence of water. The reason for this is the possibility that water, as a nucleophile, can attack the epoxy resin of the resin component (B) and react with it, i.e.Water competes with the amine hardener. The degree of crosslinking, and thus the strength and resistance, suffers as a result of this competitive reaction. However, the extent to which water competes with the amine hardener in this competitive reaction also depends on site-specific conditions that cannot be predicted precisely and reliably. Therefore, with such two-component coating compositions, it is difficult to reliably set the desired 1:1 stoichiometry in the factory. The ideal stoichiometry is always 1:1. However, the stoichiometry can vary slightly for specific customer requirements, e.g., 1:1.05. We always try to set a desired stoichiometry, but this should not change unexpectedly on site, which is difficult due to the water content in the hardener component (A).

[0009] A conventional OS8 coating is usually obtained by: 1. Apply a primer / levelling filler made of epoxy resin, 2. Sprinkle the fresh primer filler with quartz sand and sweep away the excess sand after the primer filler has hardened, and 3. Apply a top sealer with solvent-free 2-component epoxy resin.

[0010] Sprinkling quartz sand over the fresh primer filler in a separate step is traditionally necessary to create a slip-resistant structure close to the surface. It is not possible to add quartz sand or grit at the factory to conventional coating systems, as such components, with particle sizes in the millimeter range, are not dispersible and difficult to keep stably suspended without causing the coarse particles to settle quickly and become irremovable. Therefore, additional, time-consuming work steps are required on site. In addition to sprinkling quartz sand over a fresh primer filler, it is also necessary to wait for the primer filler to harden and then sweep away the excess sand in another separate step. Furthermore, sprinkling and sweeping up the quartz sand is not only time-consuming, but also costly and unsustainable.The swept sand is no longer clean and usually contains debris, meaning it cannot be easily reused. Most often, the swept sand is disposed of.

[0011] Floor coatings must also have a good flow. With the " Course " of the coating refers to the horizontal as well as the vertical course of the coating. "Horizontal gradient" means that the floor coating must have good and consistent mechanical properties, such as wear resistance, slip resistance or high strength and hardness, across the entire horizontal application surface. "Vertical gradient"means that a sufficiently solid base layer is formed at the bottom of the coating to anchor the floor coating to the mineral substrate, and that grain material, such as quartz sand or grit, is located relatively close to the surface to achieve an anti-slip structure (" Wear layer" ). However, the near-surface quartz sand / gravel must still be completely coated with sufficient binding agent to form a solid, hard (thermosetting), resistant wear layer. For this reason, conventional OS8 systems are usually applied as multi-layer coatings with a separate primer, a layer of grain material applied to the fresh primer, and a separate top sealer. This also requires additional, time-consuming work steps on site to apply several different layers.

[0012] The object of the present invention is to provide two-component coating compositions based on aqueous epoxy resins in which - regardless of the conditions encountered on the construction site - a desired stoichiometry, such as an optimal 1:1 stoichiometry, between the amine hardener system of the hardener component (A) and the epoxy resin of the resin component (B) can be reliably and safely adjusted in the factory.

[0013] In preferred embodiments, it is a further object of the present invention to provide two-component coating compositions which preferably already contain grain material at the factory.

[0014] In further preferred embodiments, it is a further object of the present invention to provide two-component coating compositions which preferably ensure both good anchoring to the substrate and, at the same time, a non-slip and durable surface, so that the application of a floor coating in one layer (single-layer coating) is possible. Summary of the invention

[0015] The present invention relates to a two-component coating composition comprising a resin component (B) containing at least one epoxy resin as a curable component, and a hardener component (A) containing an amine hardener system as a curing agent for the epoxy resin of the resin component (B), wherein the hardener component (A) further contains water and at least one cellulose derivative, and wherein the cellulose derivative has a Brookfield viscosity, determined by means of a Brookfield rotational viscometer at 25°C, 60 rpm, spindle 2, on a 5% solution in water, of 2000 mPa s or less, and the weight ratio of water to the cellulose derivative in the hardener component (A) is 10:1 to 20:1.

[0016] Furthermore, the invention relates to the use of the two-component coating composition according to the invention as a floor coating.

[0017] Further embodiments of the present invention are set forth in the following detailed description and the appended claims. Detailed description of the invention

[0018] As stated above, the present invention in its general form relates to a two-component coating composition comprising a resin component (B) containing at least one epoxy resin as a curable component and a hardener component (A) containing an amine hardener system as a curing agent for the epoxy resin of the resin component (B), wherein the hardener component (A) further contains water and at least one cellulose derivative, and wherein the cellulose derivative has a Brookfield viscosity, determined by means of a Brookfield rotational viscometer at 25°C, 60 rpm, spindle 2, on a 5% solution in water, of 2000 mPa s or less, and the weight ratio of water to the cellulose derivative in the hardener component (A) is 10:1 to 20:1. Low-viscosity cellulose derivative as a water retention agent

[0019] According to the present invention, the hardener component (A) of the two-component coating composition contains a low-viscosity cellulose derivative having a Brookfield viscosity of 2000 mPa s or less. Within the context of the present invention, data on the Brookfield viscosity of the cellulose derivative always refer to a measurement using a Brookfield rotational viscometer at 25°C, 60 rpm, spindle 2, on a 5% solution in water. In a preferred embodiment, the Brookfield viscosity of the cellulose derivative—measured using a Brookfield rotational viscometer at 25°C, 60 rpm, spindle 2, on a 5% solution in water—is 1000 mPa s or less, more preferably 500 mPa s or less. In a further embodiment, the Brookfield viscosity of the cellulose derivative is preferably 200 mPa s to 500 mPa s.

[0020] The type of low-viscosity cellulose derivative of the present invention is not particularly limited. In principle, all modified celluloses and cellulose derivatives are suitable. In a preferred embodiment, the cellulose derivative is selected from hydroxyethylcellulose (HEC), methylcellulose (MC), methylhydroxyethylcellulose (MHEC), ethylhydroxyethylcellulose (E-HEC), hydroxypropylcellulose (HPC), carboxymethylcellulose (CMC), or carboxymethylhydroxyethylcellulose (CMHEC). In a more preferred embodiment, the cellulose derivative is selected from hydroxyethylcelluloses (HEC).

[0021] The low-viscosity cellulose derivative is typically used in small amounts according to the invention. Typically, the cellulose derivative is present in the hardener component (A) in an amount of 0.4 to 4.0 wt.%, based on the total weight of the hardener component (A). In a preferred embodiment, the cellulose derivative is present in the hardener component (A) in an amount of 0.5 to 3.0 wt.%, preferably 0.5 to 2.0 wt.%, based in each case on the total weight of the hardener component (A).

[0022] The use of cellulose derivatives as rheology additives or thickeners is known in the prior art. For example, EP 1 937 891 describes interior and exterior wall paints containing cellulose derivatives as thickeners and rheology regulators. However, cellulose derivatives for such applications have significantly higher viscosities than the low-viscosity cellulose derivatives used in the invention.

[0023] In contrast, the viscosity of the resulting hardener component (A) according to the invention is not or hardly affected by the low-viscosity cellulose derivative. Rather, the low-viscosity cellulose derivative acts as a water retention agent in the present invention. The inventors of the present invention have found that the low-viscosity cellulose derivative binds the water present in the hardener component (A), so that it is not available for the undesirable side reaction with the epoxy resin of the resin component (B). As a result, according to the invention, a desired stoichiometry, in particular an optimal 1:1 stoichiometry, between the amine hardener system of the hardener component (A) and the epoxy resin of the resin component (B) can be safely and reliably adjusted in the factory, regardless of the unpredictable conditions encountered on the construction site.

[0024] As stated above, the hardener component (A) of the two-component coating composition according to the invention also contains water. This means that according to the invention, a two-component coating composition can be provided which is free of organic solvents. The weight ratio of water to the cellulose derivative in the hardener component (A) is 10:1 to 20:1. In this range, good water binding by the cellulose derivative is ensured, so that the water still contained in the hardener component (A) is not available for undesired side reactions with the epoxy resin of the resin component (B). In a preferred embodiment, the weight ratio of water to the cellulose derivative in the hardener component (A) is 12:1 to 18:1. In a further preferred embodiment, the weight ratio of water to the cellulose derivative is in the range of approximately 15:1.

[0025] During the preparation of the hardener component (A), the low-viscosity cellulose derivative is usually added as an aqueous solution or aqueous suspension. This is because, as explained above, only relatively small amounts of cellulose derivative are used and small amounts can be metered more effectively when an aqueous solution is used. Furthermore, this method allows for lump-free addition of the cellulose derivative. For example, the low-viscosity cellulose derivative is added to the hardener component (A) as a mixture of 80 parts water and 20 parts cellulose derivative. The water introduced into the hardener component (A) in this process is taken into account when setting the above-described total weight ratio of water to cellulose derivative in the resulting hardener component (A).

[0026] The total amount of water in the hardener component (A) is usually 10 to 30 wt.%, based on the total weight of the hardener component (A), preferably 12 to 25 wt.%, more preferably 15 to 22 wt.%.

[0027] The amine hardener system used in the hardener component (A) is not particularly limited according to the invention. For example, the amine hardener systems customary in the prior art can be used. Illustrative examples include, but are not limited to, aliphatic or cycloaliphatic amines, such as diethylenetriamine, 4,4'-methylenebis(cyclohexylamine), aminoethylpiperazine, 1,3-benzenedimethanamine (MXDA), isophoronediamine (IPDA), and / or polyetheramines. In one embodiment, an epoxy-polyamine adduct is used as the amine hardener system, preferably MXDA adducts or IPDA adducts, in particular isophoronediamine adduct with epoxy resin DGEBA.

[0028] The amine hardener system is typically present in the hardener component (A) in an amount of 2.5 to 18 wt.%, based on the total weight of the hardener component (A). In a preferred embodiment, the amine hardener system is present in the hardener component (A) in an amount of 2.5 to 13.5 wt.%, preferably 4.5 to 11.5 wt.%, more preferably 4.5 to 9 wt.%, in each case based on the total weight of the hardener component (A).

[0029] The epoxy resin used in resin component (B) is not particularly limited according to the invention. In principle, commercially available epoxy resins known in the art can be used. Illustrative examples thereof include, but are not limited to, diglycidyl ethers of bisphenol A, diglycidyl ethers of bisphenol F, or mixtures thereof. In a preferred embodiment, the epoxy resin in resin component (B) is a mixture of a diglycidyl ether of bisphenol A and a diglycidyl ether of bisphenol F.

[0030] Epoxy resins form the main part of resin component (B). Typically, resin component (B) contains 55 to 95 wt.%, such as 75 to 95 wt.%, of epoxy resins, based on the total weight of resin component (B). In one embodiment, resin component (B) contains 50 to 90 wt.% of diglycidyl ether of bisphenol A and 5 to 25 wt.% of diglycidyl ether of bisphenol F. In a preferred embodiment, resin component (B) contains 55 to 80 wt.%, more preferably 60 to 75 wt.% of diglycidyl ether of bisphenol A and 10 to 25 wt.%, more preferably 10 to 20 wt.% of diglycidyl ether of bisphenol F, each based on the total weight of resin component (B).

[0031] Further optional components of the two-component coating composition according to the invention are described below. Hardener component (A) preferably contains grain material

[0032] In a preferred embodiment of the present invention, the hardener component (A) further contains grain material. "Grain material" According to the invention, "granular aggregates" refers to all common silicate-based aggregates or artificial, granulated aggregates that have a grain size of at least 0.1 mm. Within the scope of the present invention, information on the grain size of the granular material refers to a measurement by sieve analysis in accordance with DIN 66165-1:2016-08. In a preferred embodiment, the grain size of the granular material is 0.1 mm to 4 mm, more preferably 0.2 mm to 3.0 mm. In a further preferred embodiment, the grain size distribution of the granular material is at least bimodal, such as bimodal, trimodal, etc.

[0033] Suitable granular materials according to the invention include, for example, silicate-based aggregates such as quartz, cristobalite, mica, feldspar, gneiss, or granite. Also suitable as granular materials are artificial, granulated aggregates such as artificial stone granules or glass. Furthermore, mixtures of silicate-based aggregates and artificial, granulated aggregates are suitable as granular materials according to the invention. In a preferred embodiment, the granular material is selected from quartz or granite. In a more preferred embodiment, the granular material contains both quartz and granite, such as quartz sand and granite chippings. In a particularly preferred embodiment, the granular material in the hardener component (A) is a mixture of quartz with a grain size of 0.2 mm to 2.2 mm and granite with a grain size of 1.0 mm to 2.0 mm.

[0034] The amount of grain material in the hardener component (A) is, for example, 45 to 80 wt.%, based on the total weight of the hardener component (A). In a preferred embodiment, the hardener component (A) contains 50 to 75 wt.%, preferably 55 to 70 wt.% of grain material, in each case based on the total weight of the hardener component (A).

[0035] In conventional coating systems from the prior art, it is not possible to add grain material directly at the factory because components with particle sizes in the millimeter range cannot be stably dispersed. Instead, the coarse particles settle quickly. This makes additional, separate work steps necessary on the construction site. However, the inventors of the present invention have found that the cellulose derivative contained as a water retention agent in the hardener component (A) simultaneously also has the property of dispersing larger particles, such as grain material, and stabilizing them in the hardener component (A), i.e. keeping them in suspension. This preferred embodiment therefore makes it possible to add sufficient grain material to the hardener component (A) of the two-component coating composition at the factory.This eliminates many work steps on the construction site, such as sanding, sweeping away excess sand after the primer / leveling filler has cured, etc., which represents a significant advantage for the construction site's workflow. This design also avoids the unwanted dust formation associated with sanding and sweeping. Hardener component (A) preferably contains filler

[0036] In a preferred embodiment of the present invention, the hardener component (A) further contains at least one filler. In contrast to the granular material described above, "Filler"Fine fillers with smaller particle sizes are understood. In one embodiment, the at least one filler has a median particle size D 50 of 1 µm to 100 µm. The median D 50 , also called the half-value grain size, indicates the average particle size of a filler, such that the proportion of particles larger than the D 50 value is equal to the proportion of particles smaller than the D 50 value. These values are preferably determined according to DIN ISO 9276-1:2004-09 (Presentation of the results of particle size analyses - Part 1: Graphic representation) and ISO 9276-2:2014-05 (Presentation of the results of particle size analyses - Part 2: Calculations of average particle sizes / diameters and moments from particle size distributions). A Mastersizer 3000 from Malvern Instruments Limited, for example, can be used for size determination.Typically, these values can also be easily obtained from a technical data sheet. In a preferred embodiment, the at least one filler has a median particle size D 50 of 1 µm to 50 µm, preferably 1 µm to 30 µm.

[0037] The type of the at least one filler is not particularly limited according to the invention. Preference is generally given to silicate fillers and / or sulfate fillers, as well as mixtures thereof. In one embodiment, the at least one filler is selected from quartz, cristobalite, phyllosilicates, talc, kaolin, mica, and alkaline earth sulfates. Due to their more difficult dispersibility, carbonate fillers are preferably not used according to the invention.

[0038] In a further embodiment, the at least one filler has an oil absorption value of 20 or less. In the context of the present invention, oil absorption values of the fillers are determined in accordance with DIN EN ISO 787-5. The oil absorption value of the fillers provides information about the morphology of the particles and corresponds to the amount of varnished linseed oil required to completely wet a filler sample under specified conditions. The oil absorption depends in particular on the surface / volume ratio and the morphology of the filler particles. The shape and size of the particles play a role here. While compact, round shapes have a positive effect on a low oil absorption, platelet- or rod-shaped filler particles lead to an increase in the oil absorption. According to the invention, fine fillers with a compact, round particle shape, i.e. an oil absorption value of 20 or less, are preferably used, as they decrease more quickly.Fine fillers with low oil numbers can also be packed into relatively dense spheres, which influences the elasticity and strength of the resulting coating film. In a preferred embodiment, the at least one filler has an oil number of 15 or less, preferably 10 or less.

[0039] Fillers within the meaning of the present invention, as stated above, are present in the hardener component (A) according to this embodiment in a total amount of preferably 2 to 15 wt.%, based on the total weight of the hardener component (A). In a preferred embodiment, filler is present in a total amount of 3 to 12 wt.%, more preferably 4 to 10 wt.%, in each case based on the total weight of the hardener component (A).

[0040] In one embodiment, a mixture of hard fillers (FH) and soft fillers (FW) is used, whereby the terms " hard " or " soft " refers to the Mohs hardness of the filler in question. Preferably, according to this embodiment, there are more soft fillers (FW) than hard fillers (FH) by weight, such as more than 50 wt.% of soft fillers (FW) and less than 50 wt.% of hard fillers (FH), based on the total weight of the fillers present in the hardener component (A). The Mohs hardness of the at least one soft filler (FW) is preferably 5 or less, more preferably 4 or less, such as 3.5 or less. The Mohs hardness of the at least one hard filler (FH) is more than 5, preferably 6 or more, more preferably 6.5 or more.

[0041] In a preferred embodiment, the hardener component (A) contains both a mixture of hard fillers (FH) and soft fillers (FW) as well as grain material, as described above. The function of the soft fillers (FW) according to this embodiment is a type of " Solid lubrication " between the larger particles of the grain material. The hard filler (FH) contributes to the mechanical strength of the coating according to this embodiment.

[0042] In a further embodiment, the filler or filler mixture at least partially contains at least one filler which has a bulk density of at least 3.5 g / cm 3<. Information on the bulk density of a filler in the context of the present invention refers to a determination in accordance with DIN EN ISO 787-10: 1995. Preferably, the predominant proportion of the fillers present in the resin component (A) as a whole, such as more than 50% by weight, based on the total weight of the fillers in the resin component (A), has a bulk density of at least 3.5 g / cm 3<. In a preferred embodiment, the filler at least partially contains at least one filler which has a bulk density of at least 4.0 g / cm 3<, preferably at least 4.2 g / cm 3<. In a further preferred embodiment, the filler contains at least barium sulfate.

[0043] In a preferred embodiment, the present invention relates to a two-component coating composition comprising a resin component (B) containing, as a curable component, at least one epoxy resin described above, and a hardener component (A) containing an amine hardener system described above as a curing agent for the epoxy resin of the resin component (B), wherein the hardener component (A) further comprises water, at least one cellulose derivative described above, at least one grain material described above, and a mixture of at least one soft filler (FW) and at least one hard filler (FH) described above, wherein the cellulose derivative has a Brookfield viscosity, determined by means of a Brookfield rotational viscometer at 25°C, 60 rpm, spindle 2, on a 5% solution in water, of 2000 mPa s or less,the weight ratio of water to the cellulose derivative in the hardener component (A) is 10:1 to 20:1, the grain material has a grain size, determined by sieve analysis according to DIN 66165-1:2016-08, of at least 0.1 mm, the at least one soft filler (FW) has a Mohs hardness of 5 or less, preferably 4 or less, the at least one hard filler (FH) has a Mohs hardness of more than 5, preferably 6 or more, and both the at least one soft filler (FW) and the at least one hard filler (FH) have a median particle size D 50 , determined according to DIN ISO 9276-1:2004-09, of 1 µm to 100 µm. In a more preferred embodiment, the present invention further relates to a two-component coating composition comprising a resin component (B) containing at least one epoxy resin as a curable component, and a hardener component (A),which contains an amine hardener system as a curing agent for the epoxy resin of the resin component (B), wherein the hardener component (A) further contains water, at least one cellulose derivative, at least one grain material, and a mixture of at least one soft filler (FW) and at least one hard filler (FH), wherein the cellulose derivative has a Brookfield viscosity, determined by means of a Brookfield rotational viscometer at 25°C, 60 rpm, spindle 2, on a 5% solution in water, of 2000 mPa s or less, the weight ratio of water to the cellulose derivative in the hardener component (A) is 10:1 to 20:1, the grain material has a grain size, determined by sieve analysis according to DIN 66165-1:2016-08, of at least 0.1 mm, the at least one soft filler (FW) has a Mohs hardness of 5 or less, preferably 4 or less, the at least one hard filler (FH) has a Mohs hardness of more than 5, preferably 6 or more,both the at least one soft filler (FW) and the at least one hard filler (FH) have a median particle size D 50 , determined according to DIN ISO 9276-1:2004-09 and ISO 9276-2:2014-05, of 1 µm to 100 µm, and the at least one soft filler (FW) has a bulk density of at least 3.5 g / cm 3<.,

[0044] According to the latter embodiments, the soft filler (FW) is preferably barium sulfate (barite, BaSO 4 ) and the hard filler (FH) is selected from quartz and / or cristobalite, with barium sulfate preferably being present in more than 50 wt.%, based on the total weight of all fillers in the hardener component (A). Quartz and cristobalite are characterized by high hardness and a low oil absorption. Barium sulfate is heavy, i.e. it has a high bulk density (bulk density of 4.5 g / cm 3< ), soft and generally also has a low oil absorption. Barium sulfate also has the advantage that there are not as many OH groups on its surface as in quartz, cristobalite or granite, i.e. BaSO 4 is less polar and interacts less well with the cellulose derivative used according to the invention. As a result, fine fillers with a high bulk density, such as BaSO 4 , can collect close to the ground under the force of gravity and form a base layer there.In one embodiment, BaSO 4 with a median particle size D 50 of 10 µm or less (e.g. 1 to 10 µm) is used.

[0045] According to the latter embodiments of the present invention, it is possible to provide a coating composition that already contains sufficient grain material at the factory, achieves good horizontal and vertical flow, and offers both good anchoring to the substrate and, at the same time, high surface slip resistance and high mechanical resistance. This makes it possible for the first time to provide a coating composition, such as an OS8 coating, that can be applied in a single step as a single-layer coating, with consistent or even improved results compared to the multi-layer process established in the prior art. In this way, work steps and working time can be significantly reduced on the construction site. Other optional components

[0046] The resin component (B) of the present invention consists predominantly of the epoxy resins described above. Optionally, the resin component (B) may also contain reactive diluents. Suitable reactive diluents are known in the art. Illustrative examples include, but are not limited to, glycidyl-functionalized alcohols, such as C 12 -C 14 aliphatic glycidyl ethers or diglycidyl ethers of butanediol, hexanediol, neopentyl glycol, and polypropylene glycol. Propylene carbonate is also suitable as a complementary reactive diluent to the glycidyl-functionalized alcohols.

[0047] In one embodiment, the resin component (B) contains 5 to 25 wt.%, preferably 10 to 25 wt.%, more preferably 10 to 20 wt.% of reactive diluent, based on the total weight of the resin component (B).

[0048] According to the invention, the resin component (B) is generally free of organic solvents.

[0049] Essential and preferred components of the hardener component (A) according to the present invention are described further above. Furthermore, the hardener component (A) may also contain further optional components.

[0050] In one embodiment, the hardener component (A) optionally also contains one or more pigments. Suitable pigments are generally known in the prior art. Illustrative examples include, but are not limited to, inorganic white pigments such as titanium dioxide, zinc white, zinc sulfide, lithopone, and / or ettringite; inorganic black pigments such as iron oxide black, iron manganese black, spinel black, and / or carbon black; and / or inorganic colored pigments such as chromium oxide, hydrated chromium oxide green, chrome green, cobalt green, ultramarine green, cobalt blue, ultramarine blue, manganese blue, ultramarine violet, cobalt and manganese violet, iron oxide red, cerium sulfide, molybdate red, ultramarine red, iron oxide brown, mixed brown, spinel and corundum phases, chromium titanium yellow, tin zinc titanate, chrome orange, iron oxide yellow, nickel titanium yellow, chrome yellow, and / or bismuth vanadate. Among the pigments mentioned, the following are often used:Titanium dioxide, zinc sulfide, zinc oxide, iron oxide, chromium oxide, cobalt blue, spinel pigment, nickel titanate, chromium titanate, and any mixtures thereof. In one embodiment, pigments with a bulk density of 4 g / cm3 or more are used.

[0051] In one embodiment, the hardener component (A) contains 0 to 12 wt.%, such as 1 to 12 wt.%, preferably 1 to 10 wt.%, more preferably 2 to 8 wt.% of pigments, based on the total weight of the hardener component (A).

[0052] In a further embodiment, the hardener component (A) optionally also contains one or more rheology additives. Rheology additives (thickeners) can be used to fine-tune the viscosity. Suitable rheology additives are known in the art. Illustrative examples include, but are not limited to, polymer-based rheology additives, such as synthetic polymers and copolymers based on methacrylic, acrylic, vinyl, and polyurethane. Less suitable according to the present invention, however, are organic, modified materials based on guar, alginate, pectin, xanthan gum, tragacanth gum, and starch, as well as inorganic thickeners such as bentonite. In one embodiment of the invention, polymeric acrylate thickeners or polyurethane thickeners are used as rheology additives.

[0053] In one embodiment, the hardener component (A) contains 0 to 0.1 wt.%, such as 0.01 to 0.1 wt.%, preferably 0.01-0.06 wt.%, more preferably 0.01-0.04 wt.% of rheology additive, based on the total weight of the hardener component (A).

[0054] The hardener component (A) may also contain further additives. These include all additives known to the person skilled in the art, such as additives for deaeration or defoaming (preferably siloxanes), surface modification (matting, lubricity, scratch resistance - e.g., silicones, waxes, silicas), flow modifiers (e.g., silicones, surfactants, solvents), light stabilizers, UV absorbers, flame retardants, antistatic agents, anti-skinning agents, corrosion inhibitors, stabilizers, catalysts, etc. In one embodiment, such further additives are present in the hardener component (A) in a total amount of, if appropriate, 0 to 2.0 wt.%, preferably 0.1 to 2.0 wt.%, more preferably 0.1 to 1.5 wt.%, even more preferably 0.1 to 1.0 wt.%, based on the total weight of the hardener component (A).

[0055] Preferably, no further wetting and dispersing agents are used according to the invention. This means that conventional dispersants, such as polycarboxylates, especially salts of polyacrylic acids, polyphosphates, polycarboxylic acid polymers, fatty alcohol derivatives, or amine compounds as dispersants, are preferably not present in the two-component coating composition of the present invention.

[0056] According to the invention, the hardener component (A) is generally free of organic solvents. Coating composition and use

[0057] In one embodiment, the hardener component (A) comprises, based on the total weight of the hardener component (A): 2.5 to 18 wt.%, preferably 2.5 to 13.5 wt.%, more preferably 4.5 to 11.5 wt.%, even more preferably 4.5 to 9 wt.% of amine hardener system, 0.4 to 4.0 wt.%, preferably 0.5 to 3.0 wt.%, more preferably 0.5 to 2.0 wt.% of cellulose derivative, 10 to 30 wt.%, preferably 12 to 25 wt.%, more preferably 15 to 22 wt.% of water, optionally 45 to 80 wt.%, preferably 50 to 75 wt.%, more preferably 55 to 70 wt.% of grain material, optionally 2 to 15 wt.%, preferably 3 to 12 wt.%, more preferably 4 to 10 wt.% of filler, optionally 0 to 12 wt.%, preferably 1 to 10 wt.%, more preferably 2 to 8 wt.% of pigment, optionally 0 to 0.1 wt.%, preferably 0.01 to 0.06 wt.%, more preferably 0.01 to 0.04 wt.% of rheology additive, and optionally 0 to 2.0 wt.%, preferably 0.1 to 2.0 wt.%, more preferably 0.1 to 1.5 wt.%, even more preferably 0.1 to 1.0 wt.% of further additives.

[0058] In one embodiment, the hardener component (A) consists essentially of the components mentioned immediately above in the amounts mentioned immediately above or in preferred amounts. In another embodiment, the hardener component (A) consists of the components mentioned immediately above in the amounts mentioned immediately above or in preferred amounts.

[0059] In one embodiment, the resin component (B) comprises, based on the total weight of the resin component (B): 50 to 90 wt.%, preferably 55 to 80 wt.%, more preferably 60 to 75 wt.% of diglycidyl ether of bisphenol A, 5 to 25 wt.%, preferably 10 to 25 wt.%, more preferably 10 to 20 wt.% of diglycidyl ether of bisphenol F, and optionally 5 to 25 wt.%, 10 to 25 wt.%, more preferably 10 to 20 wt.% of reactive diluent.

[0060] In one embodiment, the resin component (B) consists essentially of the components mentioned immediately above in the amounts mentioned immediately above or in preferred amounts. In another embodiment, the resin component (B) consists of the components mentioned immediately above in the amounts mentioned immediately above or in preferred amounts.

[0061] The two-component coating composition of the present invention is generally free of organic solvents.

[0062] In the two-component coating composition according to the present invention, the hardener component (A) and the resin component (B) are arranged in separate containers. The weight ratio of the total weight of the hardener component (A) to the total weight of the resin component (B) depends on the respective concentrations of the reactive constituents. For example, the weight ratio of the total weight of the hardener component (A) to the total weight of the resin component (B) depends on the selected amine hardener system in the hardener component (A) (e.g., amine concentration, etc.). A person skilled in the art is able to determine the reactive amount or stoichiometry of the amine hardener system in the hardener component (A) and of the epoxy resins in the resin component (B), and then adjust the stoichiometry in the two-component coating composition, i.e., the ratio of hardener component (A) to resin component (B), as desired.Amines in the hardener component (A) can be used stoichiometrically with respect to the epoxy resins in the resin component (B). One advantage of the present invention is that a desired stoichiometry, for example an optimal 1:1 stoichiometry, between the amines in the amine hardener system of the hardener component (A) and the epoxy resins in the resin component (B) can be reliably and safely adjusted in the factory, regardless of the conditions encountered on the construction site. In one embodiment, the weight ratio of the total weight of the hardener component (A) to the total weight of the resin component (B) is 100:5 to 100:15, for example, approximately 100:8. In embodiments of the invention that already contain grain material in the factory, a relatively short open time or pot life of approximately 20-30 minutes can also be adjusted, since subsequent sanding of the coating is no longer necessary.

[0063] The present invention also relates to the use of the above-described two-component coating composition as a floor coating. The invention can be used in all floor coatings (e.g., industrial floors or in parking garages), for example, as a primer and / or as a wear layer, for example for the protection of mineral substrates (e.g., concrete) in the area of parking decks, garages, and other surfaces. In one embodiment, the two-component coating composition is used both as a primer and simultaneously as a wear layer (single-layer coating), for example, as an OS8 coating.

[0064] The coating composition according to the invention is applied (e.g., by hand application) to a substrate (e.g., a mineral substrate) immediately after mixing the hardener component (A) and the resin component (B) and then allowed to cure. If necessary, the coating can be rolled with a nap roller after application to create a more homogeneous surface. The coating exhibits very good adhesion to mineral substrates and to polyurethane / epoxy coatings, very good abrasion resistance, very good wear resistance, and better UV resistance than conventional epoxy coatings. Example and comparison example

[0065] A two-component coating composition was prepared with the ingredients and weight proportions shown in Table 1 below: Table 1: Raw materials Wt.[%] Component A: Epoxy-polyamine adduct 6,0 Polydimethylsiloxane 0,02 Polysiloxane 0,02 hydrophobic silica 0,03 Barite (BaSO 4 ) 4,1 Pigment mixture 5,0 Quartz flour 3,2 Water 18,35 Polymeric rheology additive 0,03 Hydroxyethylcellulose 1,25 Quartz sand (0.2-2.2 mm) 41 Granite chippings (1.0-2.0 mm) 21 Component B: Epoxy resin (bisphenol A) 70,4 Epoxy resin (bisphenol F) 14,8 Epoxy reactive thinner 14,8

[0066] A commercially available epoxy-polyamine adduct with an amine content of 125-200 mg KOH / g (ASTM D 2073-92) was used. The epoxy-polyamine adduct was used with a water content of 55 wt.%. The quantities given in Table 1 refer to the epoxy-polyamine adduct without water content. The water content of the epoxy-polyamine adduct used is taken into account in Table 1 in the total water content of component A.

[0067] The hydroxyethylcellulose used in the working example is a mixture of 80 parts water and 20 parts hydroxyethylcellulose. The quantities given in Table 1 above refer to hydroxyethylcellulose without water. The water content in the aqueous solution of the hydroxyethylcellulose used is taken into account in Table 1 in the total water quantity in Component A.

[0068] The mixing ratio of component A to component B is approximately 100:8 by weight. The open time or pot life is approximately 20-30 minutes. The Brookfield viscosity, determined using a Brookfield rotational viscometer at 25°C, 60 rpm, spindle 2, on a 5% water solution of the hydroxyethylcellulose used here, is 300 mPa•s.

[0069] As a comparative example, a formulation with the components and proportions shown in Table 1 was used, but the low-viscosity hydroxyethylcellulose was simply omitted from component A.

[0070] The results obtained were as shown in Table 2 below: Working example Comparison example Abrasion loss [g] 1000 revolutions 1,692 2,520 Glass transition temperature [°C] 72 59 Wear resistance against rolling stress (BCA) AR1 AR2

[0071] The abrasion resistance (abrasion loss) was determined according to DIN EN ISO 5470-1:09-1999 with the following test parameters: ∘ Testing device: Taber Abraser according to ASTM D 4060 ∘ Friction roller: H 22 according to DIN EN 18026 ∘ Contact weight: 1000 g

Claims

1. A two-component coating composition with a resin component (B), which contains at least one epoxy resin as a hardenable component, and a hardener component (A), which contains an amine hardener system as the hardening agent for the epoxy resin of the resin component (B), wherein the hardener component (A) furthermore contains water and at least one cellulose derivative, and wherein the cellulose derivative has a Brookfield viscosity, determined by means of a Brookfield rotation viscometer at 25 °C, 60 rpm, spindle 2, on a 5 % solution in water, of 2000 mPa·s or less, and the ratio by weight of water to the cellulose derivative in the hardener component (A) is 10:1 to 20:1.

2. The two-component coating composition as claimed in claim 1, wherein the cellulose derivative is selected from hydroxyethylcellulose (HEC), methylcellulose (MC), methylhydroxyethylcellulose (MHEC), ethylhydroxyethylcellulose (E-HEC), hydroxypropylcellulose (HPC), carboxymethylcellulose (CMC), carboxymethylhydroxyethylcellulose (CMHEC), and wherein the cellulose derivative is preferably selected from hydroxyethylcelluloses (HEC).

3. The two-component coating composition as claimed in claim 1 or claim 2, wherein the cellulose derivative has a Brookfield viscosity of 1000 mPa·s or less, preferably 500 mPa·s or less, more preferably 200 mPa·s to 500 mPa·s.

4. The two-component coating composition as claimed in one of claims 1-3 wherein, in the hardener component (A), the ratio by weight of water to the cellulose derivative is 12:1 to 18:1, and preferably in the region of approximately 15:1.

5. The two-component coating composition as claimed in one of claims 1-4, wherein the hardener component (A) furthermore contains at least one granular material with a grain size, determined by means of sieving analysis in accordance with DIN 66165-1:2016-08, of at least 0.1 mm, preferably 0.1 mm to 4 mm, more preferably 0.2 mm to 3.0 mm, and wherein the grain size distribution of the granular material is preferably at least bimodal.

6. The two-component coating composition as claimed in claim 5, wherein the granular material is selected from silicate-based rock aggregates, preferably quartz, cristobalite, mica, feldspar, gneiss, or granite, or granulated artificial aggregates, preferably granular artificial stone or glass, as well as mixtures of these materials, wherein preferably, the granular material is selected from quartz or granite, more preferably quartz and granite, and wherein particularly preferably, the granular material is a mixture of quartz with a grain size of 0.2 mm to 2.2 mm and granite with a grain size of 1.0 mm to 2.0 mm.

7. The two-component coating composition as claimed in one of claims 1-6, wherein furthermore, the hardener component (A) contains at least one filler, and wherein the at least one filler preferably has a median particle size value D50, determined in accordance with DIN ISO 9276-1:2004-09 and ISO 9276-2:2014-05, of 1 µm to 100 µm, more preferably 1 µm to 50 µm, yet more preferably 1 µm to 30 µm.

8. The two-component coating composition as claimed in claim 7, wherein the at least one filler is selected from silicate and / or sulphate fillers as well as mixtures thereof, preferably quartz, cristobalite, sheet silicates, talc, kaolin, mica and alkaline earth sulphates, in particular barium sulphate.

9. The two-component coating composition as claimed in claim 7 or claim 8, wherein the filler contains at least one filler which has a bulk density of at least 3.5 g / cm3, preferably at least 4.0 g / cm3, more preferably at least 4.2 g / cm3, and / or the at least one filler has an oil absorption value, determined in accordance with DIN EN ISO 787-5, of 20 or less, preferably 15 or less, more preferably 10 or less.

10. The two-component coating composition as claimed in one of claims 7 to 9, wherein the filler is a mixture of (i) at least one soft filler (FW) with a Mohs hardness of 5 or less, preferably 4 or less, more preferably 3 or less, and (ii) at least one hard filler (FH) with a Mohs hardness of more than 5, preferably 6 or more, more preferably 6.5 or more.

11. The two-component coating composition as claimed in one of claims 1-10, wherein the hardener component (A) furthermore contains at least one pigment, at least one rheological additive and / or at least one further additive.

12. The two-component coating composition as claimed in one of claims 1-11, wherein the at least one epoxy resin in the resin component (B) is selected from a diglycidyl ether of bisphenol A, a diglycidyl ether of bisphenol F and mixtures thereof, and wherein the epoxy resin in the resin component (B) is preferably a mixture of a diglycidyl ether of bisphenol A and a diglycidyl ether of bisphenol F.

13. The two-component coating composition as claimed in one of claims 1-12, wherein the resin component (B) furthermore contains a reactive diluent.

14. The two-component coating composition as claimed in one of claims 1-13, wherein the hardener component (A) comprises, respectively with respect to the total weight of the hardener component (A): 2.5-18 % by weight, preferably 2.5-13.5 % by weight, more preferably 4.5-11.5 % by weight, yet more preferably 4.5-9 % by weight, of an amine hardener system, 0.4 to 4.0 % by weight, preferably 0.5 to 3.0 % by weight, more preferably 0.5 to 2.0 % by weight, of cellulose derivative, 10-30 % by weight, preferably 12-25 % by weight, more preferably 15-22 % by weight, of water, 45-80 % by weight, preferably 50-75 % by weight, more preferably 55-70 % by weight, of granular material, 2-15 % by weight, preferably 3-12 % by weight, more preferably 4-10 % by weight, of filler, if appropriate, 0-12 % by weight, preferably 1-10 % by weight, more preferably 2-8 % by weight, of pigment, if appropriate, 0-0.1 % by weight, preferably 0.01-0.06 % by weight, more preferably 0.01-0.04 % by weight, of rheological additive, and / or if appropriate, 0-2.0 % by weight, preferably 0.1-2.0 % by weight, more preferably 0.1-1.5 % by weight, yet more preferably 0.1-1.0 % by weight, of further additives, and / or the resin component (B) comprises, respectively with respect to the total weight of the resin component (B) : 50-90 % by weight, preferably 55 to 80 % by weight, more preferably 60 to 75 % by weight, of diglycidyl ether of bisphenol A, 5-25 % by weight, preferably 10 to 25 % by weight, more preferably 10 to 20 % by weight, of diglycidyl ether of bisphenol F, and / or 5-25 % by weight, preferably 10 to 25 % by weight, more preferably 10 to 20 % by weight, of reactive diluent.

15. Use of the two-component coating composition as claimed in one of claims 1-14, as a floor coating.