Purification of electrolytic oxygen

Abstract

The present invention relates to a method for purifying an oxygen stream polluted by water, hydrogen and potentially nitrogen, said method comprising bringing the oxygen stream to be purified into contact with a zeolitic adsorbent material comprising at least one metal, in zero-valent metal form, or in oxidized form or in reduced form, and recovering purified oxygen streams. The invention also relates to the use of a zeolitic adsorbent material comprising at least one transition metal for the purification of oxygen, and to the use in industrial processes of oxygen thus purified.

Description

ELECTROLYTIC OXYGEN PURIFICATION

[0001] The invention relates to a method for purifying oxygen from an electrolyser and more specifically to a method for purifying oxygen containing water and hydrogen, as well as possibly traces of nitrogen and / or traces of residual electrolytes, such as for example potassium hydroxide.

[0002] The issue of oxygen purification is becoming a major challenge today. Indeed, while hydrogen has been obtained in large quantities by steam reforming until now, current ecological constraints linked to global warming have prompted scientists to reconsider water electrolysis to produce hydrogen.

[0003] In this electrolysis process, a water molecule is split to give one mole of hydrogen and half a mole of oxygen, according to the chemical equation H2O -> H2 + 1 / 2 O2. The electrolysis of water therefore generates a significant quantity of oxygen that must be purified in order to be able to recover it. Indeed, the oxygen produced by water electrolysis is often polluted by the co-produced hydrogen, in particular due to excessive permeation of hydrogen through the separating membrane(s) or solubilization of hydrogen in the electrolyte. As for the water present in the oxygen flow, this generally comes from gaseous entrainments, while the nitrogen comes, for example, from the inerting phases at the start of the electrolyzer and its solubilization in the cold and often pressurized water introduced into the electrolyzer.The contaminants to be removed from the oxygen flow are therefore hydrogen, nitrogen, water and possibly traces of electrolyte, for example KOH type.

[0004] Indeed, certain industrial applications and processes require oxygen, as pure as possible, with the highest possible purity, for example greater than 99%, in order to optimize the effectiveness of said oxygen in these processes or applications.

[0005] The prior art already provides numerous solutions for removing, in particular, hydrogen contained in a gas. For example, document EP0089183 describes a process for removing hydrogen from a gas which may also contain oxygen. This process comprises bringing said gas into contact at room temperature with a catalyst comprising a tin oxide and alumina support impregnated with 0.25% to 2.5% by weight of platinum and 0.25% to 2.5% by weight of palladium. The operation is carried out at room temperature. The hydrogen is oxidized to water but the water is not removed. The contents inlet hydrogen levels vary between 0.2% and 2% and outlet hydrogen levels vary between 0.04% and 0.09%.

[0006] Y. Jang et al. (“Effect of a modified 13X zeolite support in Pd-Based catalysts for hydrogen oxidation at room temperature”, RSC Adv, 11, (2021), 38047-38053) investigated the effect of a modified and palladium-doped 13X zeolite on the oxidation of hydrogen to water. Specifically, the authors demonstrated that when a 13X zeolite underwent acid treatment followed by specific calcination, the activity of the catalysts was significantly increased. In this paper, the zeolite is treated with acid, which leads to a degradation of the crystal structure. Therefore, it is not a zeolite that is involved in the oxidation of hydrogen to water.

[0007] The work of O. Yu. Golubeva et al. (“Catalytic hydrogen oxidation using zeolite RHO modified by silver nanoparticles”, Glass Physics and Chemistry, 38(5), (2012), 455-459) describes the catalytic activity of zeolite RHO modified by silver ions. It is shown that the incorporation of silver, in large quantities (greater than 17%, expressed as Ag2O) in the RHO structure, allows the oxidation of hydrogen in air (majority of nitrogen). This reaction is carried out at high temperature (around 200°C). However, no indication of the presence of water or water elimination is given.

[0008] The prior art currently does not provide any acceptable solution. However, it may be thought that nitrogen and water could be easily removed by passing them over a CaX type sieve and a 4A type sieve respectively, but in this case, the separation of hydrogen will be more difficult because this gas does not adsorb on the sieves. Therefore, there is currently no acceptable industrial solution for purifying a gas stream containing oxygen contaminated with hydrogen, water, nitrogen and possibly traces of residual electrolytes.

[0009] There therefore remains a need for an easily industrializable, less expensive and easy-to-implement oxygen purification process, in particular a less expensive and easier-to-implement hydrogen purification process than with the techniques known today. Thus, one of the objectives of the present invention is to provide an oxygen purification process which makes it possible to overcome the drawbacks encountered in the prior art, and in particular to purify oxygen more easily, and in particular to eliminate both the hydrogen and the water present as impurities in an oxygen stream.

[0010] Another objective of the present invention is to provide an oxygen purification method making it possible to eliminate both hydrogen and water present as impurities in an oxygen stream, but also nitrogen as well as other impurities such as traces residual electrolytes, such as potassium hydroxide, in particular for oxygen streams from an electrolyzer, also called electrolytic oxygen. Still other objectives will become apparent in light of the description of the present invention which follows.

[0011] The Applicant has now discovered that it is possible to meet in full or at least in part the objectives set out above and in particular to purify an oxygen flow, in particular an electrolytic oxygen flow, by eliminating, or at least significantly reducing, the hydrogen and water contents, as well as, where appropriate, the nitrogen contents and other traces of residual electrolytes, in a simple, effective and relatively inexpensive manner, and in particular by overcoming in full or in part the problems encountered in the prior art.

[0012] Unless otherwise indicated in the following description of the invention, all ranges of values, and in particular those identified by "between ... and ...." or "from .... to ....", are understood to include the limits. All percentages are mass percentages, unless otherwise indicated.

[0013] The present invention thus provides an "all-in-one" process for purifying and drying oxygen, by eliminating both hydrogen and water using a single zeolitic adsorbent material, the zeolite of which has undergone at least a partial cation exchange and / or impregnation with at least one transition metal.

[0014] More specifically, the present invention relates to a method for purifying an oxygen stream containing water, hydrogen and optionally nitrogen, comprising: - at least one step of bringing the oxygen flow to be purified into contact with a zeolitic adsorbent material comprising at least one metal, in zero-valent metallic form, or in oxidized form or in reduced form, and - at least one step of recovery of purified oxygen flow.

[0015] In one embodiment of the invention, the oxygen to be purified comprises electrolytic oxygen, i.e. oxygen obtained by electrolysis of water. In a preferred embodiment, the oxygen to be purified comprises mainly oxygen, i.e. from 60 mol% to 99.99 mol% of pure oxygen, preferably from 80 mol% to 99.99 mol% of pure oxygen, more preferably from 90 mol% to 99.99 mol% of pure oxygen and more preferably from 95 mol% to 99.99 mol% of pure oxygen, typically from 96.50 mol% to 99.99 mol% of pure oxygen. As indicated above, the oxygen to be purified comprises at least water and hydrogen as impurities, as well as optionally nitrogen.

[0016] The zeolitic adsorbent material used in the present invention is a granular material comprising at least one zeolite exchanged and / or impregnated with one or more metals in zero-valent metallic form, or in oxidized form or in reduced form.

[0017] By "metal" is meant the metals of the Periodic Table of Elements, and in particular the metals of columns 3 to 15 of the Periodic Table of Elements, excluding metalloids and non-metals. Preferably the term "metal" is understood to mean the metals of columns 3 to 14 of the Periodic Table of Elements, excluding metalloids and non-metals, and more preferably by "metal" is meant the metals chosen from palladium, platinum, silver, titanium, tin, zinc, nickel, cobalt, iron and copper, and the lanthanides and actinides, alone or in mixtures of two or more of them.

[0018] More preferably, the metal is a metal selected from palladium (Pd), platinum (Pt), copper (Cu), iron (Fe), nickel (Ni), zinc (Zn), tin (Sn), cobalt (Co), and mixtures of two or more of them, in all proportions, and most preferably from palladium (Pd), platinum (Pt), copper (Cu), nickel (Ni), tin (Sn), iron (Fe), and mixtures of two or more of them, in all proportions. Among the mixtures of metals, mention may be made, as non-limiting examples, of the mixtures (or alloys) Pd / Ni, Pt / Ni, Pd / Pt / Ni, Sn / Pd, Sn / Pt, Sn / Pd / Pt, and Cu / Ag.

[0019] Other metals can of course be used, but the preferred metals and metal mixtures listed above have proven to be particularly effective and advantageous in terms of their efficiency / cost of supply ratio.

[0020] The zeolite adsorbent material usable in the process of the invention therefore comprises at least one zeolite adsorbent material and at least one metal, as set out above. Said at least one metal may be present in said zeolite adsorbent material in native form (or in metallic form, i.e. of zero valence, equal to 0) or oxidized form, or in reduced form, adsorbed totally or at least partially on said at least one zeolite. The metal may also be present in ionic form in the zeolite adsorbent material, and in this case it contributes totally or at least in part to the electronic neutrality of said zeolite adsorbent material.

[0021] The zeolitic adsorbent material usable in the process of the invention thus comprises at least one metal, as just defined, said at least one metal being able to be provided, that is to say deposited and / or impregnated and / or included by ion exchange in the structure of the zeolite, as explained below.

[0022] The supply is carried out according to conventional methods well known to those skilled in the art and is generally and advantageously carried out by means of one or more aqueous, organic or hydro-organic saline solutions, at least one of them comprising one or more metal salts, said saline solutions preferably being chosen from nitrates, acetates, sulfates, and others, of said metals.

[0023] The total mass quantity of metal introduced into the structure of the zeolite is generally and most often between 0.1% and 9% by mass, more generally between 0.1% and 7% by mass, preferably between 0.5% and 6% by mass, more preferably between 1% and 5% by mass, limits included, relative to the total weight of the zeolite adsorbent material used in the process of the present invention. This mass content is measured by X-ray fluorescence (FluoX) analysis, as indicated later in the description.

[0024] According to a preferred embodiment, in the case where the metal or metals are at least partially or totally deposited or impregnated on the zeolite crystals, the particle size of the metal particles is between 1 nm and 250 nm, preferably between 5 nm and 250 nm, more preferably between 5 nm and 100 nm, better still between 5 nm and 50 nm, for example approximately 15 nm to 20 nm. This particle size is measured by observation with a scanning electron microscope (SEM) equipped with a STEM detector (Scanning Transmission Electron Microscopy).

[0025] As indicated above, among the preferred metals, it is preferred to use copper and in this case the copper content in the zeolitic adsorbent material used in the process of the present invention is between 0.1% and 9% by mass, preferably, and most often, between 0.1% and 7% by mass, preferably between 0.5% and 6% by mass, more preferably between 1% and 5% by mass, limits included, relative to the total weight of said zeolitic adsorbent material. This content is in particular much lower than that encountered in zeolitic adsorbent materials containing copper, also called copper-doped zeolitic adsorbents, and known from the prior art.

[0026] According to a preferred embodiment, the method of the invention is implemented with a zeolitic adsorbent material containing copper and at least one other metal, and preferably at least one other metal chosen from zinc (Zn) and silver (Ag), to name only the most common mixtures, but also from palladium (Pd), platinum (Pt), iron (Fe), tin (Sn), cerium (Ce) and their mixtures in all proportions. The content of at least one other metal is generally lower than the copper content, and for example of the order of 20% by mass relative to the copper mass content, preferably of the order of 10% by mass relative to the copper mass content, and more generally between 0.1% and 20%, most often between 0.1% and 10% by mass relative to the copper mass content. The content of at least one other metal may, however, in certain cases and when desired, be equal to or greater than the copper content, in particular equal to or greater than 1% to 100%, advantageously 5% to 70%, better still equal to or greater than 10% to 70% by mass relative to the copper content.

[0027] According to another preferred embodiment, the method of the invention is implemented with a zeolitic adsorbent material containing palladium (Pd) and optionally at least one other metal chosen from zinc (Zn) and silver (Ag), tin (Sn) to name only the most common mixtures, but also from platinum (Pt), iron (Fe), cerium (Ce) and their mixtures in all proportions.

[0028] According to another preferred embodiment, the method of the invention is implemented with a zeolitic adsorbent material containing platinum (Pt) and optionally at least one other metal chosen from zinc (Zn) and silver (Ag), tin (Sn) to name only the most common mixtures, but also from palladium (Pd), iron (Fe), cerium (Ce) and their mixtures in all proportions.

[0029] Said at least one zeolite present in the zeolitic adsorbent material usable in the process of the present invention may be of any type well known to those skilled in the art and may be natural, artificial (modified natural zeolite) or synthetic (obtained by synthesis). Preferably, said at least one zeolite is chosen from LTA, FAU, RHO, MFI zeolites as well as mixtures of two or more of them. Particularly preferred are zeolites chosen from FAU type zeolites, MFI type zeolites, and mixtures thereof in all proportions and at all Si / AL ratios. Reference may advantageously be made to the work "Atlas of Zeolite Framework Types", Elsevier, 5 e edition, (2001), for information on the different types of zeolite listed above.

[0030] It should be understood that the zeolite adsorbent material usable in the process of the present invention may comprise one or more zeolite(s) of identical or different type(s), for example a zeolite chosen from zeolites of type X, type Y, type MFI, alone or in mixtures, for example a zeolite X, alone or with a zeolite of type MFI, or for example a zeolite Y, alone or with a zeolite of type MFI or a zeolite of type MFI alone or for example a zeolite X in a mixture with a zeolite Y, or for example a mixture of zeolite of type MFI with a zeolite X and a zeolite Y, to cite only simple illustrative examples and without any intention of limiting the scope of the present invention. It would therefore not be outside not within the scope of the invention if the zeolitic adsorbent material consisted of a mixture of structures with different Si / AL molar ratios

[0031] According to one embodiment of the invention, the Si / AI ratio of the zeolite or the apparent overall ratio of the mixture of zeolites, if there are several in the agglomerated zeolitic material, can take any value between 1 and 100. According to a preferred aspect, this Si / AI ratio is between 1 and 80, more preferably between 1 and 50, advantageously between 1 and 20. In a highly preferred manner, this Si / AI ratio is between 2 and 100, better still between 2 and 80, more preferably between 2 and 50, very advantageously between 2 and 20.

[0032] The zeolite adsorbent material usable in the process of the present invention may also comprise the hierarchical porosity homologues of the zeolites listed above. Zeolites with hierarchical porosity are well known to those skilled in the art and may, for example, be prepared according to the procedures described in applications WO2015019013 and WO2015028740, or else prepared by chemical, physical or physicochemical post-treatment of traditional zeolites, which are not zeolites with hierarchical porosity, also called non-mesoporous zeolites.

[0033] By zeolitic adsorbent material is meant zeolite crystals or mixtures of crystals of different zeolites, optionally agglomerated by one or more agglomeration binders well known to those skilled in the art, for example chosen from aluminas, silicas and clays. The agglomeration can be carried out before or after the operation(s) of adding metal or metals.

[0034] According to a preferred aspect, the zeolitic adsorbent material of the invention is in the form of an agglomerate, that is to say a material where the zeolite crystals are agglomerated using an agglomeration binder, as is now perfectly known to those skilled in the art. The agglomeration binder can be of any type, but for the purposes of the present invention, an agglomeration binder chosen from clays, aluminas, silicates, and mixtures of two or more of them in all proportions is preferred, and preferably the agglomeration binder is chosen from clays, and more preferably from kaolinic clays, such as kaolin, dickite, halloysite, kaolinite, nacrite, and others.

[0035] The binder content, i.e. the mass quantity of agglomeration binder relative to the total weight of the zeolitic adsorbent material, is within the ranges known to those skilled in the art, and is generally between 0.1% and 30%, preferably between 1% and 30%, more preferably between 5% and 30%, and advantageously between 10% and 30% by weight.

[0036] When agglomerating zeolite crystals with at least one agglomeration binder, it may also be advantageous or even desirable to add one or more additives or fillers well known to those skilled in the art, among which may be mentioned, by way of illustrative and non-limiting examples, additives well known to those skilled in the art, and in particular those chosen from shaping aid additives, pore-forming agents, silica, carboxymethylcellulose, and others and mixtures of them or several of them in all proportions to cite only the main additives commonly used during the agglomeration of zeolite crystals with an agglomeration binder.

[0037] When the binder is a zeolitizable binder, such as for example kaolin, kaolinite, and others, it can be zeolitized in whole or in part, that is to say transformed into zeolite, generally and most often under the action of a base, such as for example a sodium hydroxide solution, as is well known to those skilled in the art.

[0038] The zeolitic adsorbent materials suitable for use in the process of the present invention are generally and most often in the form of beads but can take any other form, for example needles, cylinders, hollow cylinders, discs, trilobed, quadrilobed, extruded, crushed and others.

[0039] The zeolite adsorbent material can be of any size and dimension, however, it is preferred and most often a zeolite adsorbent material whose volume average diameter is between 0.1 mm and 10 mm, preferably between 0.1 mm and 5 mm, more preferably between 0.5 mm and 5 mm, advantageously between 1 mm and 5 mm.

[0040] The zeolitic adsorbent material suitable for use in the process of the invention is commercially available or can be obtained according to conventional techniques well known to those skilled in the art, from operating methods known in the literature or the internet or even techniques easily adaptable from said known operating methods.

[0041] In one embodiment, the zeolitic adsorbent material can be easily prepared from zeolitic adsorbents, based on conventional zeolite(s) and / or based on zeolite(s) with hierarchical porosity, and comprising one or more alkali metal and / or alkaline earth metal cations, in particular lithium, sodium, potassium, calcium, strontium, barium, and an agglomeration binder which is optionally zeolitized in whole or at least in part, said zeolitic adsorbent being subjected to an impregnation and / or ion exchange treatment of at least one metal as defined above, generally in salt form, according to conventional techniques well known to those skilled in the art.

[0042] Alternatively, the step of impregnation and / or ion exchange of at least one metal as defined previously can be carried out directly on the zeolite crystals before agglomeration with a binder and shaping.

[0043] According to a preferred aspect, the process for preparing the zeolitic adsorbent material usable in the context of the present invention comprises at least the following steps: a) one or more cationic exchange(s) and / or impregnation(s) of zeolite crystals with one or more saline solutions of at least one metal chosen from the metals of columns 8 to 15 of the Periodic Table of Elements, excluding non-metals and metalloids, as defined above, b) agglomeration with at least one agglomeration binder, c) heat treatment for hardening (calcination) of said agglomeration binder(s), d) optionally at least partial zeolitization of said agglomeration binder(s), and e) recovery and optional activation, generally between 100°C and 550°C, of ​​said zeolitic adsorbent material usable in the context of the present invention.

[0044] In the method described above, step a) may be carried out one or more times before step b) and / or after step c) and / or d).

[0045] Generally, a cooking step is carried out, without this being in any way obligatory, preferably between step b) and step d), at a temperature generally between 400°C and 600°C. Alternatively, and when a cooking step is carried out, it may be possible to carry out step a) after this cooking step, and before step d), whether or not a step a) has already been carried out before step b).

[0046] According to a preferred embodiment of the process for preparing the zeolitic adsorbent material usable in the process of the present invention, a step of shaping said agglomerated material is carried out, according to any method well known to those skilled in the art. This shaping step can be carried out during or after step b) of agglomeration and can be followed by one or more step(s) a) of cationic exchange(s) and / or impregnation(s).

[0047] The heat treatment steps described in the above process must not result in significant sintering of the metal atoms, which must remain as dispersed as possible in the zeolite(s). This point can easily be observed by scanning electron microscopy (SEM) or transmission electron microscopy (TEM). Sintering of the metal atoms is particularly easily avoided, and as this is well known, through careful and rigorous control of temperatures and durations of heat treatments.

[0048] Such methods for preparing zeolitic adsorbent materials exchanged and / or impregnated with / by one or more transition metals are well known to those skilled in the art, and reference may be made, for example and in a non-limiting manner, to document EP1125635 for a precise description of how to prepare the zeolitic adsorbent materials that can be used in the context of the method of the invention or to the document “Metal Sites in Zeolites: Synthesis, Characterization, and Catalysis”, Q. Zhang et al., Chem. Rev., (2023), 123(9), 6039-6106.

[0049] More particularly, the cationic exchanges can be carried out according to any methods well known to those skilled in the art, and for example by bringing a zeolitic adsorbent material into contact with one or more saline solutions, preferably aqueous, at least one of them comprising one or more metal salts, the cationic exchange being able to be single or multiple and when it is multiple, the successive exchanges can be carried out with identical or different saline solutions, each exchange step being able to be preceded and / or followed by at least one washing and / or heat treatment step, said heat treatment being able to be an oxidizing or reducing treatment.

[0050] The impregnation operation can also be easily carried out according to any methods well known to those skilled in the art, whether according to a wet or dry impregnation method. By wet impregnation is meant bringing a zeolitic adsorbent material in aqueous and / or organic suspension into contact with one or more saline solutions, preferably aqueous, at least one of them comprising one or more metal salts, the wet impregnation operation possibly being preceded and / or followed by at least one heat treatment step, said heat treatment possibly being an oxidizing or reducing treatment.Dry impregnation means bringing a zeolitic adsorbent material into contact with one or more saline solutions, preferably aqueous, at the correct volume, at least one of them comprising one or more metal salts, the dry impregnation operation possibly being preceded and / or followed by at least one heat treatment step, said heat treatment possibly being an oxidizing or reducing treatment.

[0051] The different steps listed above, cation exchange and / or impregnation, can be carried out one or more times and can be combined, for example a cation exchange operation can be followed by a wet or impregnation operation. dry, and include a washing step after cation exchange and possibly a heat treatment before the impregnation operation.

[0052] These various cationic exchange and impregnation operations lead to the presence, in the zeolite adsorbent material, of at least one metal in cationic form. Before use in the process of the present invention, and if this is necessary or desirable, a treatment using a reducing element, for example and advantageously under a stream of gaseous hydrogen, makes it possible to reduce the valence of the metal(s), possibly down to valence 0.

[0053] Non-limiting examples of zeolitic adsorbent materials that can be used in the process of the invention are the following: • zeolites of the sodium MFI type (MFI-Na) or of the protonated MFI type (MFI-H) with a Si / Al molar ratio of between 10 and 20, having a content of between 0.1% and 7% of at least one metal chosen from Pd, Pt, Ni, Ti, Co, Zn, Ce, Fe, Cu, Sn, Ag, alone or as a mixture of 2 or more of them. • zeolites of sodium FAll type (FAll-Na) or protonated FAll type (FAll-H) with a Si / Al molar ratio of between 1.25 and 20, having a content of between 0.1% and 7% of at least one metal chosen from Pd, Pt, Ni, Ti, Co, Zn, Ce, Fe, Cu, Zn, Sn, Ag, alone or as a mixture of 2 or more of them. • zeolites of sodium LTA type (LTA-Na) or protonated LTA type (LTA-H) with a Si / Al molar ratio equal to 1, having a content of between 0.1% and 7% of at least one metal chosen from Pd, Pt, Ni, Ti, Co, Zn, Ce, Fe, Cu, Zn, Sn, Ag, alone or as a mixture of 2 or more of them. • zeolites of sodium RHO type (RHO-Na) or protonated RHO type (RHO-H) with a Si / Al molar ratio of between 1 and 20, having a content of between 0.1% and 7% of at least one metal chosen from Pd, Pt, Ni, Ti, Co, Zn, Ce, Fe, Cu, Zn, Sn, Ag, alone or as a mixture of 2 or more of them.

[0054] According to a preferred embodiment, the zeolitic adsorbent material used in the present invention is a granular material comprising at least one zeolite exchanged or impregnated with one or more metals chosen from palladium, platinum, silver, titanium, tin, zinc, nickel, cobalt, iron and copper in zero-valent metallic form, or in oxidized form or in reduced form.

[0055] A particularly preferred embodiment of the method of the invention uses a zeolitic adsorbent material which is a granular material comprising at least one zeolite exchanged or impregnated with a metal chosen from copper, palladium, platinum, iron and zinc, alone or in mixtures of two or more of them in any proportions.

[0056] According to a further preferred embodiment, the method of the invention uses a zeolitic adsorbent material which is a granular material comprising at least one Faujasite (FAU) type zeolite, preferably a FAU type zeolite with a Si / Al ratio of between 1 and 100, for example a FAU-X type zeolite or a FAU-Y type zeolite and preferably a FAU-Y type zeolite, comprising sodium, and further comprising copper, or copper in a mixture or alloy with one or more metals chosen from palladium, platinum, tin, iron and zinc, the transition metal(s) being able to be exchanged or impregnated in said zeolitic adsorbent material.

[0057] According to another preferred embodiment, the method of the invention uses a zeolitic adsorbent material which is a granular material comprising at least one Faujasite (FAU) type zeolite, preferably a FAU type zeolite with a Si / Al ratio of between 2 and 100, for example a FAU-Y type zeolite, comprising sodium, and further comprising copper, or copper in a mixture or alloy with one or more metals chosen from palladium, platinum, iron, tin, and zinc, the metal(s) being able to be exchanged and / or impregnated in said zeolitic adsorbent material.

[0058] According to yet another preferred embodiment, the method of the invention uses a zeolitic adsorbent material which is a granular material comprising at least one MFI type zeolite, preferably an MFI type zeolite with a Si / Al ratio of between 10 and 100, comprising sodium, and further comprising copper, or copper in a mixture or alloy with one or more metals chosen from palladium, platinum, iron and zinc, the metal(s) being able to be exchanged or impregnated in said zeolitic adsorbent material.

[0059] In a preferred embodiment, examples of zeolitic adsorbent materials usable in the process of the invention are: Protonated FAU • protonated FAU type zeolites, with a Si / AI ratio of between 2 and 10, with a Pd content of between 0.1% and 1% by weight, • protonated FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a Pt content of between 0.1% and 1% by weight, • protonated FAU type zeolites, with a Si / AI ratio of between 2 and 10, with a Ni content of between 1% and 7% by weight, • protonated FAU type zeolites, with a Si / AI ratio of between 2 and 10, with a Ti content of between 4% and 7% by weight, protonated FAll type zeolites, with a Si / AI ratio of between 2 and 10, with a Co content of between 4% and 7% by weight, protonated FAll type zeolites, with a Si / AI ratio of between 2 and 10, with a Zn content of between 4% and 7% by weight, protonated FAll type zeolites, with a Si / AI ratio of between 2 and 10, with a Ce content of between 4% and 7% by weight, protonated FAll type zeolites, with a Si / AI ratio of between 2 and 10, with a Fe content of between 4% and 7% by weight, protonated FAll type zeolites, with a Si / AI ratio of between 2 and 10, with a Cu content of between 4% and 7% by weight, protonated FAll type zeolites, with a Si / AI ratio of between 2 and 10, with a Zn content of between 4% and 7% by weight, protonated FAll type zeolites, with a Si / AI ratio of between 2 and 10, with a Sn content of between 4% and 7% by weight, protonated FAll type zeolites, with a Si / AI ratio of between 2 and 10,with an Ag content of between 4% and 7% by weight, protonated FAll type zeolites, with a Si / Al ratio of between 2 and 10, with a Ti content of between 4% and 7% by weight, protonated FAll type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 2% and 4% by weight, and a palladium content of between 0.1% and 1% by weight, protonated FAll type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and a palladium content of between 0.1% and 1% by weight, protonated FAll type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and a palladium content of between 0.1% and 1% by weight, protonated FAll type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and a palladium content of between 0.1% and 1% by weight, platinum between 0.1% and 1% by weight, • protonated FAll type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and a nickel content of between 0.1% and 5% by weight, • protonated FAll type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and an iron content of between 0.1% and 5% by weight, • protonated FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and a cobalt content of between 0.1% and 1% by weight, • protonated FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and a zinc content of between 0.1% and 5% by weight, • protonated FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and a titanium content of between 0.1% and 5% by weight, • protonated FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and a tin content of between 0.1% and 5% by weight, Sadistic FAU • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a Pd content of between 0.1% and 1% by weight, • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a Pt content of between 0.1% and 1% by weight, • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a Ni content of between 1% and 7% by weight, • sodium FAU type zeolites, with a Si / AI ratio of between 2 and 10, with a Ti content of between 4% and 7% by weight, • sodium FAU type zeolites, with a Si / AI ratio of between 2 and 10, with a Co content of between 4% and 7% by weight, • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a Zn content of between 4% and 7% by weight, • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a Ce content of between 4% and 7% by weight, • sodium FAU type zeolites, with a Si / AI ratio of between 2 and 10, with an Fe content of between 4% and 7% by weight, • sodium FAU type zeolites, with a Si / AI ratio of between 2 and 10, with a Cu content of between 4% and 7% by weight, • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a Zn content of between 4% and 7% by weight, • sodium FAU type zeolites, with a Si / AI ratio of between 2 and 10, with a Sn content of between 4% and 7% by weight, • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with an Ag content of between 4% and 7% by weight, • sodium FAU type zeolites, with a Si / AI ratio of between 2 and 10, with a Ti content of between 4% and 7% by weight, • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 2% and 4% by weight, and a palladium content of between 0.1% and 1% by weight, • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and a palladium content of between 0.1% and 1% by weight, • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and a platinum content of between 0.1% and 1% by weight, • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and a nickel content of between 0.1% and 5% by weight, • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and an iron content of between 0.1% and 5% by weight, • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and a cobalt content of between 0.1% and 1% by weight, • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and a zinc content of between 0.1% and 5% by weight, • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and a titanium content of between 0.1% and 5% by weight, • sodium FAU type zeolites, with a Si / Al ratio of between 2 and 10, with a copper content of between 0.5% and 2% by weight, and a tin content of between 0.1% and 5% by weight, Protonated MFI • protonated MFI type zeolites, with a Si / AI ratio of between 10 and 20, with a Pd content of between 0.1% and 1% by weight, • protonated MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a Pt content of between 0.1% and 1% by weight, • protonated MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a Ni content of between 1% and 7% by weight, • protonated MFI type zeolites, with a Si / AI ratio of between 10 and 20, with a Ti content of between 4% and 7% by weight, • protonated MFI type zeolites, with a Si / AI ratio of between 10 and 20, with a Co content of between 4% and 7% by weight, • protonated MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a Zn content of between 4% and 7% by weight, • protonated MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a Ce content of between 4% and 7% by weight, • protonated MFI type zeolites, with a Si / AI ratio of between 10 and 20, with an Fe content of between 4% and 7% by weight, • protonated MFI type zeolites, with a Si / AI ratio of between 10 and 20, with a Cu content of between 4% and 7% by weight, • protonated MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a Zn content of between 4% and 7% by weight, • protonated MFI type zeolites, with a Si / AI ratio of between 10 and 20, with a Sn content of between 4% and 7% by weight, • protonated MFI type zeolites, with a Si / Al ratio of between 10 and 20, with an Ag content of between 4% and 7% by weight, • protonated MFI type zeolites, with a Si / AI ratio of between 10 and 20, with a Ti content of between 4% and 7% by weight, • protonated MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 2% and 4% by weight, and a palladium content of between 0.1% and 1% by weight, • protonated MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and a palladium content of between 0.1% and 1% by weight, • protonated MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and a platinum content of between 0.1% and 1% by weight, • protonated MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and a nickel content of between 0.1% and 5% by weight, • protonated MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and an iron content of between 0.1% and 5% by weight, • protonated MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and a cobalt content of between 0.1% and 1% by weight, • protonated MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and a zinc content of between 0.1% and 5% by weight, • protonated MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and a titanium content of between 0.1% and 5% by weight, • protonated MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and a tin content of between 0.1% and 5% by weight, MFI sodium zeolites of the MFI type, with a Si / AI ratio of between 10 and 20, with a Pd content of between 0.1% and 1% by weight, MFI sodium zeolites of the MFI type, with a Si / AI ratio of between 10 and 20, with a Pt content of between 0.1% and 1% by weight, MFI sodium zeolites of the MFI type, with a Si / AI ratio of between 10 and 20, with a Ni content of between 1% and 7% by weight, MFI sodium zeolites of the MFI type, with a Si / AI ratio of between 10 and 20, with a Ti content of between 4% and 7% by weight, MFI sodium zeolites of the MFI type, with a Si / AI ratio of between 10 and 20, with a Co content of between 4% and 7% by weight weight, sodium MFI type zeolites, with an Si / AI ratio of between 10 and 20, with a Zn content of between 4% and 7% by weight, sodium MFI type zeolites, with a Si / AI ratio of between 10 and 20, with a Ce content of between 4% and 7% by weight, sodium MFI type zeolites,with a Si / AI ratio between 10 and 20, with an Fe content between 4% and 7% by weight, sodium MFI type zeolites, with a Si / AI ratio of between 10 and 20, with a Cu content of between 4% and 7% by weight, sodium MFI type zeolites, with a Si / AI ratio of between 10 and 20, with a Zn content of between 4% and 7% by weight, sodium MFI type zeolites, with a Si / AI ratio of between 10 and 20, with a Sn content of between 4% and 7% by weight, sodium MFI type zeolites, with a Si / AI ratio of between 10 and 20, with an Ag content of between 4% and 7% by weight, sodium MFI type zeolites, with a Si / AI ratio of between 10 and 20, with a Ti content of between 4% and 7% by weight, • I sodium MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 2% and 4% by weight, and a palladium content of between 0.1% and 1% by weight, • sodium MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and a palladium content of between 0.1% and 1% by weight, • sodium MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and a platinum content of between 0.1% and 1% by weight, • sodium MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and a nickel content of between 0.1% and 5% by weight, • sodium MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and an iron content of between 0.1% and 5% by weight, • sodium MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and a cobalt content of between 0.1% and 1% by weight, • sodium MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and a zinc content of between 0.1% and 5% by weight, • sodium MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and a titanium content of between 0.1% and 5% by weight, • sodium MFI type zeolites, with a Si / Al ratio of between 10 and 20, with a copper content of between 0.5% and 2% by weight, and a tin content of between 0.1% and 5% by weight.

[0060] As previously indicated, the process of the invention is an "all-in-one" process for purifying oxygen, by removing both hydrogen and water, present as impurities in an oxygen stream, more specifically an oxygen stream comprising or consisting of electrolytic oxygen.

[0061] By "all-in-one" process, it is meant that the passage over the zeolite adsorbent material allows the at least partial, or even total (content below the detection threshold) simultaneous (i.e. concomitant) elimination of hydrogen and water present in the oxygen flow in the same temperature range. However, it is well known to those skilled in the art that zeolites must operate at high temperature to eliminate hydrogen and that at high temperature zeolites adsorb little or no water, and on the contrary tend to desorb water. The "all-in-one" process of the present invention therefore has the great advantage of eliminating both hydrogen and water, and possibly other impurities, in the oxygen flow, while avoiding steps of changing temperature ranges, thus facilitating the industrial process in terms of time, energy expenditure, and productivity.It can thus be considered that the method of the present invention allows the purification of oxygen flows without external energy input, for example without external heating input.

[0062] As previously indicated, the present invention relates to the method for purifying an oxygen stream, in particular an electrolytic oxygen stream, containing, as impurities to be removed, hydrogen and water, and possibly nitrogen and possibly other impurities inherent in the oxygen synthesis process, in particular the electrolytic oxygen synthesis process.

[0063] Thus, the purification process of the present invention can be carried out according to any method well known to those skilled in the art of gas purification, and more specifically by adsorption of impurities on a zeolitic adsorbent material as defined above. For example, the adsorption process according to the present invention can be chosen from processes of the pressure and / or temperature modulated type, typically from PSA (Pressure Swing Adsorption), PVSA (Pressure Vacuum Swing Adsorption, with the use of desorption at subatmospheric pressure), TSA (Temperature Swing Adsorption), PTSA (Pressure Temperature Swing Adsorption, with the use of desorption at subatmospheric pressure), TSA (Temperature Swing Adsorption), PTSA (Pressure Temperature Swing Adsorption, with the use of desorption at subatmospheric pressure), TSA (Temperature Swing Adsorption), PTSA (Pressure Temperature Swing Adsorption), and PTSA (Pressure Temperature Swing Adsorption). in Temperature and Pressure), PVTSA (“Pressure Vacuum Temperature Swing Adsorption”, Adsorption Modulated in Temperature and Pressure, with use of desorption at sub-atmospheric pressure).

[0064] The fluid to be purified contains mainly oxygen, as indicated above, as well as water, hydrogen and possibly nitrogen. The water content is generally between 20 ppmv and 1.5 mol%, preferably 50 ppmv and 1.5 mol%, more preferably between 100 ppmv and 1.5 mol%, advantageously between 200 ppmv and 1.5 mol%. The hydrogen content in the flow is generally between 5 ppmv and 1 mol%, preferably between 5 ppmv and 5000 ppmv, more preferably between 5 ppmv and 3000 ppmv, better still between 5 ppmv and 1000 ppmv. The nitrogen content is between 0 and 1 mol%, generally between 10 ppmv and 1 mol%.

[0065] The method according to the present invention can be implemented according to any conventional gas separation method, and for example by passage through one or more column(s) (also called "adsorber(s)" or more simply "reactor(s)") comprising at least one bed of zeolitic adsorbent material as just defined. According to one embodiment, the method of the invention is implemented with at least two adsorbers, in particular when working in continuous flow, according to techniques well known to those skilled in the art.

[0066] Thus, the fluid to be purified is brought into contact with the zeolitic adsorbent material at a pressure generally between 0.5 MPa and 5 MPa, preferably between 0.9 MPa and 5 MPa, more preferably between 1.5 MPa and 5 MPa, and at a temperature between 10°C and 100°C, preferably between 15°C and 90°C, advantageously between 20°C and 60°C, typically between 25°C and 55°C.

[0067] In a preferred embodiment, after the adsorption phase, the bed of zeolitic adsorbent material is regenerated, i.e. desorbed either by reducing the pressure and countercurrent evacuation (PSA and VPSA processes), or by reducing the temperature (TSA process), possibly associated with reducing the pressure and countercurrent evacuation (PVTSA process).

[0068] In the case of PSA and VPSA processes, the desorption pressure is generally between 0.1 MPa and 1 MPa on the one hand and 500 Pa and 95 kPa respectively. As a general rule, and for obvious reasons of ease of implementation of the process and energy savings, the desorption temperature is close to the adsorption temperature, in other words, there is generally no intentional modification of the temperature.

[0069] According to a further preferred embodiment of the invention, a purge phase can be implemented at the end of the desorption phase, typically by countercurrent reintroduction of a fraction of the purified gas, typically less than 20% of the flow rate produced by an adsorber.

[0070] It should also be understood that the process of the present invention may also comprise one or more pressure equalization phases between the possible different adsorbers. The pressure equalization phase(s) may advantageously be carried out between the adsorption and desorption phases, according to techniques also well known to those skilled in the art. The advantage of providing one or more pressure equalization phases is in particular to minimize as much as possible the losses of oxygen but also of hydrogen in the entire process. Similarly, it may be envisaged to recycle the gas collected at desorption, as is customary to do with hydrogen PSA processes.

[0071] In the case of the TSA and PVTSA processes, a fraction of the purified gas (typically less than 20% of the flow produced by the adsorber) is heated to a temperature between 40°C and 250°C, then injected countercurrently onto the adsorber, possibly at a reduced pressure compared to the adsorption phase (PVTSA), i.e. between 1 kPa and 3 MPa. As for PSA and VPSA, different pressure equalization and purge configurations can be considered.

[0072] In the process of the present invention, the adsorption and desorption phases follow one another cyclically. The process may optionally include a cooling system integrated into the adsorber, the aim of which is to avoid or at least minimize excessive heating of the adsorbent bed, which would inhibit the adsorption of water by the zeolitic adsorbent granular material, as indicated above. The process may also include a step of drying the gas stream, before and / or after passing over the zeolitic adsorbent material comprising at least one metal according to the invention.

[0073] Being able to dry, i.e. adsorb the water present or formed on the same material, will simplify the processes downstream of the electrolysers while producing a flow of high-purity oxygen, particularly of the quality required in many areas of application.

[0074] The method of the invention thus has numerous advantages, and in particular that of being able to both reduce the hydrogen dissolved in the oxygen flow and adsorb the water possibly already present in the hydrogen flow as well as the water formed by the reduction of the dissolved oxygen. The method of the invention thus makes it possible to easily obtain, on an industrial level, high purity oxygen flows, and in particular oxygen flows of purity greater than 99%, and more particularly electrolytic oxygen flows of purity greater than 99% and comprising less than 5 ppmv of hydrogen, and less than 1 ppmv of water, these quantities of impurities are determined according to conventional techniques well known to those skilled in the art and for example using an ionization mass spectrometer.

[0075] According to another aspect of the invention, it relates to a flow of purified oxygen obtained according to the method previously described, and its use as an industrial product or reagent, in various fields, such as for example the fields of metallurgy or even the medical field, to name only a few known applications. It should be noted that one of the main interests is to be able to have oxygen free or almost free of hydrogen, for obvious safety reasons.

[0076] According to another aspect, the invention relates to the use of the zeolitic adsorbent material as defined above for the purification of an oxygen stream, and in particular for the purification of electrolytic oxygen.

[0077] According to yet another aspect, the invention relates to a process for preparing high purity oxygen comprising at least the following steps: 1) electrolysis of an aqueous solution comprising mainly hydrogen oxide to generate a flow of hydrogen and a flow of oxygen, 2) recovery of the oxygen flow from step 1) of electrolysis, 3) purification of the oxygen stream recovered in step 2) by passage over a zeolitic adsorbent material, as defined previously, and 4) high purity oxygen recovery.

[0078] It should be understood that the process for preparing high-purity oxygen according to the invention comprises a step 1) of electrolysis which can be carried out in a conventional manner well known to those skilled in the art.

[0079] This process thus makes it possible to obtain very high purity oxygen efficiently and economically, and in particular more economically than the synthesis processes known today for preparing oxygen by electrolysis of water. Analytical techniques Si / Al molar ratio and exchange rate

[0080] The measurement of the Si / Al molar ratio and the exchange rate is carried out by any analytical chemical analysis techniques known to those skilled in the art. Among these techniques, mention may be made of the chemical analysis technique by X-ray fluorescence. as described in standard NF EN ISO 12677: 2011 on a wavelength dispersive spectrometer (WDXRF), for example Tiger S8 from Bruker.

[0081] X-ray fluorescence is a spectral technique that exploits the photoluminescence of atoms in the X-ray range to establish the elemental composition of a sample. The excitation of atoms, generally by an X-ray beam or by bombardment with electrons, generates specific radiation after returning to the ground state of the atom. The X-ray fluorescence spectrum has the advantage of depending very little on the chemical combination of the element, which offers a precise determination, both quantitative and qualitative. A measurement uncertainty of less than 0.4% by weight is typically obtained after calibration for each oxide.

[0082] These elementary chemical analyses make it possible to verify the Si / Al molar ratio of the starting zeolite, the content of metal or metals deposited, as well as to verify the quality of the ion exchange. In the description of the present invention, the measurement uncertainty of the Si / Al molar ratio is ± 5%. The quality of the ion exchange is linked to the number of moles of sodium oxide, Na2O, remaining in the agglomerated zeolite adsorbent after exchange. It should be noted that the contents of different oxides are given as a percentage by weight relative to the total weight of anhydrous zeolite adsorbent material.

[0083] The Si / Al molar ratio of the zeolite present in the zeolitic adsorbent material is measured by solid-state Nuclear Magnetic Resonance (NMR) spectroscopy of silicon. In the description of the present invention, the measurement uncertainty of the Si / Al molar ratio is ± 5%. Metal content

[0084] The amount of metal present in the zeolite adsorbent material is also obtained from X-ray fluorescence analysis, as indicated above, and is expressed in % by mass of metal. Granulometry of metal particles

[0085] The estimation of the number-average diameter of the metal particles contained in the zeolite adsorbent material is carried out by observation under a scanning electron microscope (SEM).

[0086] To estimate the size of the metal particles in the samples, a set of images is taken at a magnification of at least 5000. The diameter of at least 200 particles is then measured using dedicated software, for example Smile View software from the publisher LoGraMi. The accuracy is around 3%. The measurement of the histogram constituted from the said diameter measurements allows at the same time the determination of the standard deviation o of its distribution. Particle size of zeolite adsorbents:

[0087] The determination of the volume average diameter of zeolite adsorbents is carried out by analyzing the particle size distribution of an agglomerate sample by imaging according to ISO 13322-2:2006, using a conveyor belt allowing the sample to pass in front of the camera lens.

[0088] The volume mean diameter is then calculated from the particle size distribution by applying ISO 9276-2:2001. In this document, the term "volume mean diameter" or "size" is used for zeolite agglomerates. The accuracy is of the order of 0.01 mm for the agglomerate size range of the invention. Qualitative analysis by X-ray diffraction

[0089] The purity of zeolites in zeolite adsorbent materials is assessed by X-ray diffraction analysis, known to those skilled in the art by the acronym DRX. This identification is carried out on a Bruker DRX device.

[0090] This analysis makes it possible to identify the different zeolites present in the adsorbent material since each zeolite structure has a unique diffractogram defined by the positioning of the diffraction peaks and by their relative intensities.

[0091] Prior to measurement, the zeolite materials are crushed then spread and smoothed on a sample holder by simple mechanical compression.

[0092] The conditions for acquiring the diffractogram produced on the Bruker D5000 device are as follows: • Cu tube used at 40 kV - 30 mA; • slit size (diverging, diffusion and analysis) = 0.6 mm; • filter: Ni; • rotating sample device: 15 rpm 1 ; • measuring range: 3° < 20 < 50°; • step: 0.02°; • counting time per step: 2 seconds.

[0093] The interpretation of the diffractogram obtained is carried out with the EVA software with identification of the zeolites using the ICDD PDF-2 base, release 2011. Dubinin volume microcrystallinity

[0094] The volume of Dubinin (or microporous V m i) is determined in a conventional manner well known to those skilled in the art, in particular from the measurement of the isotherm adsorption of a gas at its liquefaction temperature, for example nitrogen, argon, oxygen, and others. Preferably, nitrogen is used. Prior to this adsorption measurement, the zeolite crystals of the invention are degassed between 300°C and 450°C for a period ranging from 9 hours to 16 hours, under vacuum (Pressure < 6.7.10 -4Pa). For example, for a zeolite with a FAll or MFI structure, the measurement of the nitrogen adsorption isotherm at 77K is then carried out on a Micromeritics ASAP 2020 type device, taking at least 35 measurement points at relative pressures with a P / PO ratio between 0.002 and 1. The micropore volume is determined according to the Dubinin and Raduskevitch equation from the isotherm obtained, applying the ISO 15901-3:2007 standard. The micropore volume thus evaluated is expressed in cm 3 of liquid adsorbent per gram of anhydrous adsorbent. The measurement uncertainty is ± 0.003 cm 3 g -1 . Example according to the invention

[0095] An oxygen stream is recovered from an electrolyzer at a temperature of 50°C. The oxygen stream is pressurized to 0.8 MPa. The oxygen stream contains 3000 ppmv of hydrogen and 1000 ppmv of water.

[0096] The electrolytic oxygen stream to be purified is introduced into a column containing 1 liter of zeolitic adsorbent material. The contact time between the stream and said zeolitic adsorbent material is set at 10 seconds. The zeolitic adsorbent material consists of 1 mm diameter beads obtained by agglomeration, with 20% by weight of binder, of H-MFI zeolite crystals (protonated MFI), with a Si / Al ratio equal to 12.5, with a Pd content of 0.3% by weight.

[0097] The purified oxygen stream recovered from the column outlet is analyzed using an ionization mass spectrometer. The residual water content is confirmed using a hygrometer probe from Panametrics. The purified oxygen contains 0.3 ppmv of water and the residual hydrogen content is below the detection limit.

Claims

CLAIMS 1. Method for purifying an oxygen stream containing water, hydrogen and optionally nitrogen, comprising: - at least one step of bringing the oxygen flow to be purified into contact with a zeolitic adsorbent material comprising at least one metal, in zero-valent metallic form, or in oxidized form or in reduced form, and - at least one step of recovery of purified oxygen flow.

2. The method of claim 1, wherein the oxygen to be purified comprises electrolytic oxygen.

3. Method according to claim 1 or claim 2, wherein the oxygen to be purified comprises from 60 mol% to 99.99 mol% of pure oxygen, preferably from 80 mol% to 99.99 mol% of pure oxygen, more preferably from 90 mol% to 99.99 mol% of pure oxygen and more preferably from 95 mol% to 99.99 mol% of pure oxygen, typically from 96.50 mol% to 99.99 mol% of pure oxygen, and comprises at least water and hydrogen as impurities, as well as optionally nitrogen.

4. A method according to any one of the preceding claims, wherein said at least one transition metal is selected from the metals of columns 3 to 15 of the Periodic Table of Elements, excluding metalloids and non-metals, preferably from the metals of columns 3 to 14 of the Periodic Table of Elements, excluding metalloids and non-metals, and more preferably from palladium, platinum, silver, titanium, tin, zinc, nickel, cobalt, iron and copper, and alone or in mixtures of two or more of them.

5. Method according to any one of the preceding claims, in which the zeolitic adsorbent material comprises at least one zeolite chosen from LTA, FAll, RHO, MFI zeolites as well as mixtures of two or more of them, and preferably chosen from FAll type zeolites, MFI type zeolites, and their mixtures in all proportions and at all Si / AL ratios.

6. Method according to any one of the preceding claims, in which the zeolitic adsorbent material comprises at least one zeolite chosen from zeolites of type FAll, of type MFI, and their mixtures and at least one metal, in metallic form of zero valence, or in oxidized form or in reduced form, chosen from copper, palladium, platinum, tin, iron and zinc, and their mixtures, the metal(s) being able to be exchanged or impregnated in said zeolitic adsorbent material.

7. Method according to any one of the preceding claims, in which the oxygen stream to be purified is brought into contact with the zeolitic adsorbent material at a pressure of between 0.5 MPa and 5 MPa, preferably between 0.9 MPa and 5 MPa, more preferably between 1.5 MPa and 5 MPa, and at a temperature of between 10°C and 100°C, preferably between 15°C and 90°C, advantageously between 20°C and 60°C, typically between 25°C and 55°C.

8. Use of a zeolitic adsorbent material comprising at least one metal, in zero-valent metallic form, or in oxidized form or in reduced form, in which said at least one metal is chosen from the metals of columns 3 to 15 of the Periodic Table of Elements, excluding metalloids and non-metals, preferably from the metals of columns 3 to 14 of the Periodic Table of Elements, excluding metalloids and non-metals, and more preferably chosen from palladium, platinum, silver, titanium, tin, zinc, nickel, cobalt, iron and copper, alone or in mixtures of two or more of them, for the purification of an oxygen stream, and in particular for the purification of electrolytic oxygen.

9. Use of a purified oxygen stream obtained according to the process of any one of claims 1 to 7, as an industrial product or reagent.

10. Process for the preparation of high purity oxygen comprising at least the following steps: 1) electrolysis of an aqueous solution comprising mainly hydrogen oxide to generate a flow of hydrogen and a flow of oxygen, 2) recovery of the oxygen flow from step 1) of electrolysis, 3) purification of the oxygen flow recovered in step 2) by passage over a zeolitic adsorbent material according to the method of any one of claims 1 to 7, and 4) high purity oxygen recovery.