Use of aluminosilicate polymers as an active ingredient against phytopathogenic microorganisms

Abstract

The invention relates to the use of aluminosilicate polymers having a local imogolite-type structure and their derivatives as active ingredients against phytopathogenic microorganisms, in particular Plasmopara viticola, responsible for downy mildew of grapevines. The invention also relates to a method for controlling the occurrence of diseases caused by phytopathogenic microorganisms in plants, comprising at least one step of applying to said plants a composition comprising at least one aluminosilicate polymer having a local imogolite-type structure and its derivatives as an active ingredient. Figure to be published: 1

Description

Title of the invention: Use of aluminosilicate polymers as active ingredient against phytopathogenic microorganisms

[0001] The present invention applies to the general field of phytosanitary products and the fight against phytopathogenic microorganisms. In particular, the invention relates to the use of aluminosilicate polymers of the imogolite or allophane type as active ingredient against phytopathogenic microorganisms, in particular phytopathogenic fungi such as pseudofungi of the Per-onosporaceae family of the Oomycetes class such as for example Plasmopara viticola responsible for mildew and phytopathogenic bacteria.The invention also relates to a method for combating the appearance of diseases caused by phytopathogenic microorganisms in plants comprising at least one step of applying, to said plants, a composition comprising at least one aluminosilicate polymer of imogolite or allophane type as active ingredient.

[0002] For a farmer, the diseases to which his plants are regularly exposed can have disastrous consequences on the yields, quality and survival of his crops. For example, soft rot, causing necrosis of plants, can lead to significant economic losses.

[0003] Phytosanitary products or pesticides used in agriculture help limit the development of organisms likely to affect crops and harvests. The aggressors are phytopathogenic microorganisms and include fungi and bacteria.

[0004] For example, mildew is a fungal disease affecting the leaves and bunches of vines in particular, but which is also found in other crops (potatoes, tomatoes, etc.). It is a disease that affects the entire French vineyard (to varying degrees depending on the wine-growing area), with parasitic pressure becoming high almost every other year. In addition, if no treatment is used, it can lead to: deformation of the shoots, an increase in the vulnerability of the vine, an alteration in the quality of the wine or even a drop in yield (which can reach up to 85%).

[0005] Currently, in the fight against downy mildew in vines, two methods are available to winegrowers: conventional control (prophylactic measures and pesticides) and biocontrol products. Prophylactic measures such as trellising, careful trimming or pruning require a lot of labor and have limited effectiveness. Pesticides for controlling downy mildew (folpel, mancozeb, fosetyl, etc.) are products derived from synthetic chemistry. These are the only effective means to today to prevent and / or stop diseases but their use is very controversial.

[0006] Since the end of the 19th century and the development of Bordeaux mixture, copper has been a major element in crop protection methods against various diseases (mildew, certain mycoses and most bacterial diseases), particularly in vines, fruit production and vegetable crops. While it remains widely used today in various forms of so-called "conventional" agriculture, alongside other pesticides, copper plays a crucial role in agrobiological systems, as it is currently the only active substance approved in organic farming with both a strong biocidal effect and a broad range of action. However, copper-based compounds accumulate in soils and are toxic to humans, microorganisms and the environment.Although most uses of copper are justified by its biological effectiveness, they pose ecotoxicological problems (proven risks for soil microbial populations, earthworms, certain aquatic organisms and crop auxiliaries). The highlighting of these environmental impacts of copper has led to regulatory restrictions on its use (capping of doses applicable per hectare and per year), and even its ban as a pesticide in certain European countries (Netherlands, Denmark), which generates distortions of competition between countries.

[0007] Biocontrol is a choice alternative for limiting the public health and environmental risks of crop treatments. Biocontrol products are "agents and products using natural mechanisms as part of the integrated fight against crop pests" (according to Article L253-6 of the Rural and Maritime Fishing Code). They cover macroorganisms (invertebrates, insects, mites or nematodes), micro-organisms (fungi, bacteria, viruses), chemical mediators such as sex pheromones and natural substances (substances of plant, animal or mineral origin). These products used at the beginning of the season, when pest pressures are low to medium, show good effectiveness.However, they are used in combination with more conventional plant protection products (copper for mildew and sulfur for another cryptogamic disease, powdery mildew) and thus make it possible to reduce the quantities used of these conventional pesticides. However, in the event of high pest pressure, at the time of flowering for example, biocontrol products are not effective.

[0008] Finally, oxygenated water or hydrogen peroxide has known bactericidal and fungicidal effects with high oxidizing power (PO) due to the 0-0 bond which is very reactive. It is a biocide authorized by the European Union and used in plant protection. However, its instability over time does not allow this to be used composed as a preventive product, particularly in viticulture.

[0009] There is therefore a need for new affordable products with an effectiveness comparable to that of copper products, usable throughout the season and having a low environmental impact.

[0010] Thus, the aim of the present invention is to overcome the drawbacks of the aforementioned prior art and to provide a solution making it possible to effectively combat phytopathogenic microorganisms and thus to prevent or delay the appearance of diseases caused by phytopathogenic microorganisms in plants.

[0011] The present invention thus has as its first object the use of at least one aluminosilicate polymer having a local structure of imogolite type as an active ingredient against phytopathogenic microorganisms.

[0012] According to the invention, a local structure of the imogolite type (or ILS, from the English expression "Imogolite Local Structure") is characterized by the association of aluminum and silicon atoms with an Al / Si ratio of 2:1. In the ideal structure, the aluminum atoms are in octahedral coordination linked together by edges. The silicon atoms are isolated and in tetrahedral coordination. They are connected to the dioctahedral layer of aluminum by three Si-O-Al bonds (see 3D representation in the attached [Fig.l]).

[0013] ILS type aluminosilicate polymers include imogolites, allophanes and proto-imogolites, their respective derivatives and their mixtures.

[0014] Imogolites are the tubular forms of these ILS-type aluminosilicate polymers. Imogolite is a mineral of the hydrated aluminosilicate family (clay mineral group), with the average chemical formula Al2SiO3(OH)4. It occurs naturally in volcanic ash and in certain soils. The atomic structure of imogolite was published in 1972 (CEO Cradwick et al., “Imogolite, a hydrated aluminium silicate of tubular structure,” Nature Physical Science, vol. 240, December 25, 1972, pp. 187-189). Imogolite has a well-defined nanotubular structure with a monodisperse outer diameter of about 2–3 nm and a polydisperse length of about 10–1000 nm (see the 3D representation of imogolite in the attached [Fig.2]).

[0015] According to a particular embodiment of the invention, the aluminosilicate polymers are chosen from imogolite nanotubes and nanotubes of imogolite derivatives.

[0016] Allophanes are aluminosilicate nanospheres with the average chemical formula Al2SiO3(OH)4. These nanospheres are generally 3 to 5 nm in diameter and also occur naturally in natural deposits. They are related to imogolites in that they share the same local ILS-type structure. A 3D representation of the structure of allophanes is given in [Fig.3] attached.

[0017] According to a particular embodiment of the invention, the aluminosilicate polymers are chosen from allophane nanospheres and nanospheres of allophane derivatives.

[0018] Proto-imogolites are curved, non-closed nanostructures of aluminosilicate with the average chemical formula Al2SiO3(OH)4 having a size between 1 and 6 nm which also exist naturally in natural deposits. They are related to imogolites in that they share the same local ILS-type structure. A 3D representation of the structure of proto-imogolites is given in the attached [Fig.4].

[0019] According to a particular embodiment of the invention, the aluminosilicate polymers are chosen from non-closed curved nanostructures of proto-imogolite type and nanostructures of proto-imogolite derivatives.

[0020] By derivatives is meant aluminosilicate polymers having a local ILS type structure, namely of the imogolite, allophane or proto-imogolite type, in which some of the constituent atoms have been replaced by atoms other than aluminum and silicon. For example, this includes:

[0021] - imogolites, allophanes or proto-imogolites in which the atoms aluminum have been partly replaced by other metal cations such as gallium, indium, iron, cobalt, nickel.

[0022] - imogolites, allophanes or proto-imogolites in which the atoms of silicon have been replaced in whole or in part by other cations such as germanium, arsenic, phosphorus, carbon, aluminum, iron.

[0023] According to the invention, imogolites, allophanes, proto-imogolites and their derivatives can also be functionalized.

[0024] Thus, according to the invention, the imogolites, the allophanes, the proto-imogolites and their derivatives can be chosen from aluminosilicate polymers having a local structure of ILS type in which at least a portion of the surface hydroxyl groups have been functionalized by a group chosen from alkyl, alkene, alkyne, amino, thiol, halide, phenyl, silane groups and their mixtures.

[0025] According to a preferred embodiment of the invention, the aluminosilicate polymers are chosen from imogolite derivatives in the form of nanotubes having an external diameter ranging from 3 to 3.6 nm, preferably from 3.1 to 3.4 nm, said diameter being measured by small angle X-ray scattering (SAXS) for which part of the silicon atoms have been replaced by germanium atoms, part of the aluminum atoms have been replaced by iron atoms and part of the hydroxyl groups have been replaced by methyl groups.

[0026] The imogolite derivatives, also called “hybrid imogolites”, which can be used according to the present invention can be prepared according to the process described in international application WO2014 / 080370.

[0027] According to a preferred embodiment of the invention, the aluminosilicate polymers are chosen from allophane derivatives in the form of nanospheres having an external diameter ranging from 3 to 6 nm, said diameter being measured by SAXS.

[0028] The allophane derivatives, also called “hybrid allophanes”, which can be used according to the present invention can be prepared according to the process described in patent application FR3 023 181.

[0029] According to a preferred embodiment of the invention, the proto-imogolite derivatives are chosen from nanostructures having a size of between 1 and 6 nm, said size being measured by SAXS.

[0030] According to a particular and preferred embodiment of the invention, said aluminosilicate polymers are chosen from polymer mixtures consisting of approximately 5 to 90% by mass of imogolite and / or an imogolite derivative, approximately 5 to 90% by mass of allophane and / or an allophane derivative, and approximately 5 to 90% by mass of proto-imogolite and / or a proto-imogolite derivative, the sum of these individual percentages being equal to 100%. Among such mixtures, mixtures consisting of approximately 55% by mass of imogolite and / or an imogolite derivative, approximately 40% by mass of allophane and / or an allophane derivative and approximately 5% by mass of proto-imogolite and / or a proto-imogolite derivative are particularly preferred.

[0031] The use of these aluminosilicate polymers has no long-term impact on the environment because once incorporated into the soil, these polymers decompose into other clays already present (depending on the local geology). They also have an effectiveness comparable to that of the copper-based products usually used.

[0032] According to a particular and preferred embodiment of the invention, the aluminosilicate polymers are used in combination with hydrogen peroxide.

[0033] Indeed, as demonstrated in the examples illustrating the present invention, the joint use of at least one aluminosilicate polymer and hydrogen peroxide makes it possible to improve the effectiveness of the aluminosilicate polymers against the growth of phytopathogens and therefore to reduce the doses at which they can be used effectively (reduction of the minimum inhibitory concentration of the aluminosilicate polymers).

[0034] According to this particular embodiment of the invention, the optional use of hydrogen peroxide also has no environmental impact since its degradation products are water and oxygen.

[0035] Still according to this particular embodiment of the invention, the mass ratio of aluminosilicate polymers / hydrogen peroxide can vary from 1:0.01 to 1:0.8 approximately, and even more preferably from 1:0.1 to 1:0.4 approximately.

[0036] The phytopathogenic microorganisms against which the aluminosilicate polymers which can be used in accordance with the invention are effective may be phytopathogenic fungi or phytopathogenic bacteria.

[0037] Among the phytopathogenic fungi, we can in particular mention the pseudofungi of the Peronosporaceae family of the Oomycetes class such as for example Plasmopara viticola responsible for downy mildew of the vine or those of the Pythiaceae family such as for example Phytophthora infestans responsible for downy mildew of the potato and the tomato,Ascomycete fungi responsible for scab on fruit trees, such as Venturia inaequalis, which causes apple scab, or those belonging to the order Erysiphales and the family Erysiphaceae, which cause powdery mildew, such as Erysiphe necator, which causes powdery mildew on grapevines, or those belonging to the family Helotiaceae, such as Pseudopezicula tracheiphila, which causes parasitic red blotch on grapevines (Brenner), or those from the family Venturiaceae, such as Spilocaea oleaginea, which causes cycloconium (peacock eye disease) on olive trees, or fungi from the family Sclerotiniaceae and the genus Monilinia, including Monilinia fructigena, which mainly attacks pome fruits, and Monilinia laxa, which mainly attacks stone fruits.responsible for brown rot or those of the order Taphrinales and the family Taphrinaceae such as for example Taphrina deformons responsible for peach leaf curl or those of the family Bo-tryosphaeriaceae such as for example Guignardia bidwellii responsible for black rot or the necrotrophic fungi botrytis of the family Sclerotiniaceae such as for example botrytis cinerea responsible for gray mold (Botrytis) or those of the family Pleosporaceae such as for example Al-ternaria solani responsible for Alternaria blight (altemariose) in tomatoes and potatoes, the Phoma fungi of the family Sphaerioidaceae of the class Cœlomycetes such as for example Phomopsis viticola responsible for excoriose.

[0038] Among the phytobacteria, we can particularly mention Ralstonia solanacearum of the Burkholderiaceae family responsible for brown rot of potatoes, proteobacteria of the Comamonadaceae family such as, for example, Xylophilus ampelinus responsible for bacterial necrosis of vines or those of the Pseudomonadaceae family such as, for example, Pseudomonas savastanoi responsible for bacteriosis of olive trees or those of the Xanthomonadaceae family such as, for example, Xanthomonas campestris pv. Vesicatoria responsible for spots bacterial in tomatoes or those of the Pseudomonadaceae family such as Pseudomonas syringae pv. Lachrymans responsible for angular leaf spot in cucumbers.

[0039] According to a particularly preferred embodiment, the aluminosilicate polymers according to the invention are used as fungicides, and very particularly against pseudofungi of the Peronosporaceae family of the Oomycetes class, most preferably against Plasmopara viticola.

[0040] The invention also has as a second object a method for combating the appearance of diseases caused by phytopathogenic microorganisms in plants, said method comprising at least one step of applying, to said plants, a composition comprising, as active ingredient against said phytopathogenic microorganisms, at least one aluminosilicate polymer having a local structure of the ILS type.

[0041] The aluminosilicate polymers with a local structure of the ILS type are preferably chosen from imogolites, allophanes, proto-imogolites, their respective derivatives and their mixtures.

[0042] According to this second object, the aluminosilicate polymers are as defined according to the first object of the invention.

[0043] In the same way, the phytopathogenic microorganisms targeted by the method according to the invention are those listed above according to the first subject of the invention.

[0044] Thus, the method according to the present invention makes it possible to combat plant diseases caused by phytopathogenic fungi or phytopathogenic bacteria.

[0045] According to a particular and preferred embodiment of the invention, the method is a method for combating plant diseases caused by pseudofungi of the Peronosporaceae family of the Oomycetes class, most preferably against Plasmopara viticola. According to this particular embodiment, the method is applied to the treatment of vines, potato plants or tomato plants, most preferably vines.

[0046] According to a preferred embodiment of the invention, the composition is a liquid composition comprising said at least one aluminosilicate polymer and water.

[0047] The concentration of aluminosilicate polymer within said composition generally varies from approximately 0.1 to 100 g / L, preferably from approximately 0.2 to 50 g / L and even more preferably from approximately 0.5 to 30 g / L.

[0048] The composition which can be used according to the process in accordance with the invention can also be in the form of a concentrated composition to be diluted, a powder or granules to be dispersed at the time of use at the desired concentration.

[0049] According to a preferred embodiment of the invention, said composition contains hydrogen peroxide. In this case, the amount of hydrogen peroxide generally varies from 0.05 to 50 g / L, preferably from approximately 0.1 to 25 g / L and even more preferably from approximately 0.25 to 15 g / L.

[0050] Still according to this embodiment, the mass ratio of aluminosilicate polymers / hydrogen peroxide preferably varies from 1:0.01 to 1:0.8 approximately, and even more preferably from 1:0.1 to 1:0.4 approximately.

[0051] The composition used according to the process in accordance with the invention may also contain one or more adjuvants conventionally used in phytosanitary products such as spraying agents, anti-foam agents, wetting agents, thixotropic agents, compatibilizing agents, pH stabilizing agents, etc.

[0052] The application step may consist of a step of spreading or spraying said composition on the aerial parts of the plant to be treated.

[0053] The amount of composition applied to the plants may vary depending on the concentration of aluminosilicate polymers in said composition.

[0054] Thus the quantity of composition applied to the plants will be adapted so that the dose of aluminosilicate polymers is between approximately 100 g and 5 kg per hectare and preferably between approximately 500 g and 3 kg per hectare.

[0055] The method according to the invention may comprise several application steps over time depending on the species of plant to be treated, the weather conditions and the forecast occurrence of phytopathogenic microorganisms. For example, when the method is implemented to combat mildew, particularly in vines, the number of applications of said composition preferably varies from 5 to 15 applications per year on average, with a first application in spring, for example in April, then subsequent applications every 4 days to every 2 to 3 weeks depending on the weather conditions.

[0056] Other characteristics, variants and advantages of the method according to the invention will become more apparent on reading the following exemplary embodiments, given by way of illustration and not limitation of the invention, as well as the appended figures in which:

[0057] - [Fig.l] is a 3D schematic representation of the local structure of type THEY. In this figure, the aluminum octahedra are shown in white and shades of gray, the silicon tetrahedron is in black, and the spheres correspond to the oxygen atoms. Hydrogen atoms are not shown;

[0058] - [Fig.2] is a 3D schematic representation of the structure of imogolite. In this figure, aluminum octahedra are shown in white and shades of gray, silicon tetrahedra in black, and spheres correspond to oxygen atoms. Hydrogen atoms are not shown;

[0059] - [Fig.3] is a 3D schematic representation of the structure of allophane. In this figure, aluminum octahedra are shown in white and shades of gray, silicon tetrahedra in black, and spheres correspond to oxygen atoms. Hydrogen atoms are not shown;

[0060] - [Fig.4] is a 3D schematic representation of the structure of the proto- imogolite. In this figure, aluminum octahedra are shown in white and shades of gray, silicon tetrahedra in black, and spheres correspond to oxygen atoms. Hydrogen atoms are not shown;

[0061] - [Fig.5] is a cryo-transmission electron microscopy photograph (cryo-MET) of the predominantly (> 90% by mass) aluminosilicate polymer of imogolite type prepared in example 1;

[0062] - [Fig.6] is a cryo-transmission electron microscopy photograph (cryo-MET) of the predominantly (> 90% by mass) allophane-type aluminosilicate polymer prepared in Example 2;

[0063] - [Fig.7] is a cryo-transmission electron microscopy photograph (cryo-MET) of a mixture of aluminosilicate polymers of imogolite, allophane and proto-imogolite type prepared in Example 3;

[0064] - [Fig.8] represents the percentage of inhibition of growth in vitro on vine leaf discs of the fungus Plasmopara viticola of a composition comprising predominantly (> 90% by mass) an imogolite-type aluminosilicate polymer and hydrogen peroxide (formulation 1) depending on the dose tested (in g / L);

[0065] - [Fig.9] represents the percentage of inhibition of growth in vitro on vine leaf discs of the fungus Plasmopara viticola of a composition comprising predominantly (> 90% by mass) an imogolite-type aluminosilicate polymer (formulation 2) depending on the dose tested (in g / L);

[0066] - [Fig. 10] represents the percentage of inhibition of growth in vitro on vine leaf discs of the fungus Plasmopara viticola of a composition comprising predominantly (> 90% by mass) an allophane-type aluminosilicate polymer and hydrogen peroxide (formulation 3) depending on the dose tested (in g / L);

[0067] - [Fig.l 1] represents the percentage of inhibition of growth in vitro on vine leaf discs of the fungus Plasmopara viticola of a composition comprising predominantly (> 90% by mass) an allophane-type aluminosilicate polymer (formulation 4) depending on the dose tested (in g / L);

[0068] - [Fig. 12] represents the percentage of inhibition of growth in vitro on vine leaf discs of the fungus Plasmopara viticola of a composition comprising a mixture of aluminosilicate polymers with a local structure of the ILS type, said mixture consisting of 55% by mass of imogolite, 40% by mass of allophane and 5% by mass of proto-imogolite (formulation 5) depending on the dose tested (in g / L),

[0069] - [Fig. 13] represents the histogram of the doses inhibiting the growth of the fungus Plasmopara viticola (IC50), as well as the minimum inhibitory concentration (MIC) for each of the formulations 1 to 5 tested. EXAMPLES

[0070] Reagents and materials used in the examples:

[0071] - Aluminum chloride hexahydrate (A1C13.6(H2O)), 99% pure, Sigma-Aldrich,

[0072] - Nona hydrated aluminum perchlorate (A1(C1O4)3.9(H2O)), 99% pure, Sigma- Aldrich,

[0073] - Sodium hydroxide (NaOH), 98% pure, Sigma-Aldrich,

[0074] - Tetraethoxysilane (Si(OCH2CH3)4), 99% pure, Sigma-Aldrich,

[0075] - Deionized water,

[0076] - Tangential ultrafiltration membrane (retention threshold of 300 kDa) in po- lysulfone, sold under the trade name UF20M3, by the company Polymem,

[0077] - Dialysis membrane having a retention threshold of 6 - 8 kDa, sold under the name Commercial Spectra / Por™ 16-8 kD mination by Spectrum™ Labs,

[0078] - Hydrogen peroxide at 110 volumes (H2O2 30% by mass), Thermo Scientific,

[0079] - Sporangia of Plasmopara viticola (Strain Pv2543_l, Hungary collected in 2013).

[0080] EXAMPLE 1: Synthesis of an aluminosilicate polymer predominantly (> 90% by mass) of the imogolite type (Clay 1)

[0081] To a deionized water solution containing 2 mM Al(C104)3«9(H20) was added, with stirring, tetraethoxysilane until a Si / Al molar ratio of 0.55 was reached. After 30 minutes of stirring, a 0.1 M NaOH solution was added until a NaOH / Al molar ratio of 2 was reached, still with stirring. The solution was then left stirring for 4 hours and then heated to 90°C for 7 days. Once cooled, the solution was then concentrated by tangential ultrafiltration with a 300 kDa polysulfone membrane until a concentration factor of 100 was reached. The concentrated solution thus obtained was then dialyzed in a dialysis tube consisting of a Spectra / Por™ membrane with a retention threshold of 6 - 8 kDa against deionized water, until the conductivity of the dialysis water was less than 2 pS / cm. [Fig.5] attached is a cryo-transmission electron microscopy (cryo-TEM) photograph of Clay 1 thus obtained.

[0082] EXAMPLE 2: Synthesis of an aluminosilicate polymer predominantly (> 90% by mass) of the allophane type (Clay 2)

[0083] To a solution of deionized water containing 200 mM AlCl3«6(H2O) was added, with stirring, tetraethoxysilane until a Si / Al molar ratio equal to 0.55 was reached. After 30 minutes of stirring, a 0.1 M NaOH solution was added until a NaOH / Al molar ratio of 2 was reached, still under stirring. The solution was then left stirring for 4 hours and then heated at 90°C for 7 days. Once cooled, the solution was then dialyzed in a dialysis tube made of a Spectra / Por™ membrane with a retention threshold of 6 - 8 kDa against deionized water until the conductivity of the dialysis water was less than 2 pS / cm. The attached [Fig.6] is a cryo-transmission electron microscopy (cryo-TEM) photograph of Clay 2 thus obtained.

[0084] EXAMPLE 3: Synthesis of a mixture of aluminosilicate polymers of imogolite, allophane and proto-imogolite type (Clay 3)

[0085] To a deionized water solution containing 2 mM AlCl3«6(H2O) was added, with stirring, tetraethoxysilane until a Si / Al molar ratio of 0.55 was reached. After 30 minutes of stirring, a 0.1 M NaOH solution was added until a NaOH / Al molar ratio of 2 was reached, still with stirring. The solution was then left stirring for 4 hours and then heated to 90°C for 7 days. Once cooled, the solution was then concentrated by tangential ultrafiltration with a 300 kDa polysulfone membrane until a concentration factor of 100 was reached. The concentrated solution thus obtained was then dialyzed in a dialysis tube made of a Spectra / Por™ membrane with a retention threshold of 6 - 8 kDa against deionized water, until the conductivity of the dialysis water was less than 2 pS / cm.A mixture of aluminosilicate polymers consisting of about 55% by mass of imogolite, about 40% by mass of allophane and about 5% by mass of proto-imogolite (Clay 3) was obtained. The attached [Fig.7] is a cryo-transmission electron microscopy (cryo-TEM) photograph of the Clay 3 thus obtained.

[0086] EXAMPLE 4: Demonstration of the effectiveness of 5 formulations based on aluminosilicate polymers against the agent responsible for vine downy mildew, Plasmopara viticola, in vitro

[0087] The objective of this example is to demonstrate the effectiveness of different liquid formulations based on aluminosilicate polymers as prepared above in Examples 1 to 3, respectively Clays 1 to 3, optionally in the presence of hydrogen peroxide, against the agent responsible for vine mildew.

[0088] 4.1 Characteristics of the formulations tested

[0089] Different liquid formulations based on deionized water, clays and possibly hydrogen peroxide were prepared. The characteristics of the different liquid formulations tested are detailed in Table 1 below:

[0090] [Tables 1] Formulations Prepared volume Composition Clay concentration H2O2 concentration Fl 20 mL Clay 1 + H2O2 30% m. 5 g / L 2.5 g / L F2 20 mL Clay 1 5 g / L - F3 20 mL Clay 2 + H2O2 30% m. 5 g / L 2.5 g / L F4 20 mL Clay 2 5 g / L - F5 20 mL Clay 3 5 g / L -

[0091] 4.2 Efficacy test protocol

[0092] Discs with a diameter of 18 mm were cut from vine leaves and placed in Petri dishes, with the upper surface in contact with Whatman paper.

[0093] Each of the formulations 1 to 5 above was tested at different doses and as detailed in Table 2 below:

[0094] [Tables2] Doses tested Clay concentrations (g / L) DI 0.25 D2 0.50 D3 0.75 D4 1.00 D5 1.50 D6 3.00 D7 5.00

[0095] The different doses tested were obtained by corresponding dilution of each of the formulations 1 to 5 with deionized water.

[0096] For each of the formulations 1 to 5, each of the doses tested was applied using a microdiffuser to the vine leaves at a rate of 1 mL of formulation tested per Petri dish, and at a rate of 6 to 8 leaf discs per concentration tested.

[0097] The vine leaf discs were then dried before inoculating with the phytopathogenic agent (extemporaneous tests).

[0098] Inoculation was carried out using a suspension in sterile water of sporangia of the fungus Plasmopara viticola at a concentration of between 40,000 and 50,000 sporangia / mL at a rate of 3 drops of 15 qL per leaf disc of vine. Pathogen development was assessed after 7 days of incubation at 22°C as a percentage of growth. These data were then transformed into the average percentage of fungal growth inhibition in the treated modalities compared to the control modality (sprayed with sterile water), according to the following equation 1:

[0099] [Equation 1]:

[0100] % inhibition = 100.x F1 - 1 % growth control j

[0101] For each of the formulations tested, it is then possible to plot a curve representing the evolution of the percentage of inhibition as a function of the clay concentration (in g / L) and thus to determine a value corresponding to the dose inhibiting the growth of the fungus by 50% (IC50), as well as the minimum inhibitory concentration (MIC). The results obtained for each of the formulations 1 to 5 tested are given in the attached figures 8 to 12 corresponding respectively to the % of inhibition of the growth of the fungus calculated for the different doses tested of formulations 1 to 5 (in g / L).

[0102] The attached [Fig. 13] represents the histogram of the IC50 and MIC for each of the formulations 1 to 5 tested.

[0103] The CL® and MIC values ​​for each of the formulations 1 to 5 tested (F1 to F5) are also presented in Table 3 below:

[0104] [Tables3] Fl F2 F3 F4 F5 IC5o (g / L) 0.73 0.29 0.57 0.71 0.01 MIC (g / L) 3.66 6.23 2.64 3.01 1.75

[0105] All of these results demonstrate that, although not necessary, the addition of hydrogen peroxide allows the significant increase in the effectiveness of formulation 1 of approximately 50% (MIC = 3.66 g / L for formulation 1 comprising Clay 1 and hydrogen peroxide compared to 6.23 g / L for formulation 2 comprising only Clay 1). This conclusion also applies to the results obtained with Clay 2 (2.64 g / L for formulation 3 comprising Clay 2 and hydrogen peroxide compared to 3.01 g / L for formulation 4 comprising only Clay 2).

[0106] Finally, according to the MIC results, formulation 5 prepared based on Clay 3 only (without hydrogen peroxide) is the most effective against the growth of vine mildew (MIC = 1.75 g / L).

Claims

Claims

1. Use of at least one aluminosilicate polymer having a local imogolite-type structure as an active ingredient against phytopathogenic microorganisms.

2. Use according to claim 1, characterized in that the aluminosilicate polymers are chosen from imogolites, allophanes and proto-imogolites, their respective derivatives and their mixtures.

3. Use according to claim 1 or 2, characterized in that the aluminosilicate polymers are chosen from polymer mixtures consisting of 5 to 90% by mass of imogolite and / or an imogolite derivative, 5 to 90% by mass of allophane and / or an allophane derivative, and 5 to 90% by mass of proto-imogolite and / or a proto-imogolite derivative, the sum of these individual percentages being equal to 100%.

4. Use according to any one of claims 1 to 3, characterized in that the aluminosilicate polymers are used in combination with hydrogen peroxide.

5. Use according to claim 4, characterized in that the mass ratio of aluminosilicate polymers / hydrogen peroxide varies from 1:0.01 to 1:0.

8.

6. Use according to any one of the preceding claims, characterized in that the phytopathogenic microorganisms are phytopathogenic fungi or phytopathogenic bacteria.

7. Use according to any one of the preceding claims, characterized in that the phytopathogenic microorganisms are pseudofungi of the Peronosporaceae family of the Oomycetes class.

8. Method for combating the occurrence of diseases caused by phytopathogenic microorganisms in plants, said method comprising at least one step of applying, to said plants, a composition comprising, as active ingredient against said phytopathogenic microorganisms, at least one aluminosilicate polymer having a local imogolite-type structure.

9. Method according to claim 8, characterized in that it is applied to the treatment of vines, potato plants or tomato plants.

10. Method according to claim 8 or 9, characterized in that the concentration of aluminosilicate polymers within said composition varies from 0.1 to 100 g / L.

11. Method according to any one of claims 8 to 10, characterized in that said composition contains hydrogen peroxide.

12. Method according to claim 11, characterized in that the mass ratio of aluminosilicate polymers / hydrogen peroxide varies from 1:0.01 to 1:0.

8.

13. Method according to any one of claims 8 to 12, characterized in that the application step consists of a step of spreading or spraying said composition on the aerial parts of the plant to be treated.

14. Method according to any one of claims 8 to 13, characterized in that a dose of aluminosilicate polymers of between 100 g and 5 kg per hectare is applied.

15. Method according to any one of claims 8 to 14, characterized in that said method is implemented to combat mildew, and in that the number of applications of said composition varies from 5 to 15 applications per year on average.