Hydrocarbon resin polymer, and production method of the same, and substrate structure

Abstract

To provide a fluorine substituent-containing hydrocarbon resin polymer having excellent electric performance, and production method of the same, and a substrate structure including a resin layer formed by cross-linking a resin composition including the hydrocarbon resin polymer.SOLUTION: A hydrocarbon resin polymer including a repeating unit (A) is derived from dicyclopentadiene (DCPD). The hydrocarbon resin polymer has a fluorine substituent where a content of the fluorine substituent is 100-4,500 ppm. A production method of the hydrocarbon resin polymer includes a step of polymerizing a mixture in the presence of a fluorine-containing compound, where the fluorine-containing compound is a boron trifluoride complex, and the mixture includes dicyclopentadiene. A substrate structure includes a resin layer, and a conductive layer disposed on the resin layer. The resin layer is formed from a resin composition including the hydrocarbon resin polymer using a cross-linking process.SELECTED DRAWING: Figure 2

Description

[Technical field]

[0001] CROSS-REFERENCE TO RELATED APPLICATIONS This application claims the benefit of U.S. Provisional Patent Application No. 63 / 585,037, filed September 25, 2023, and also claims the benefit of Taiwanese Patent Application No. 113,134,063, filed September 9, 2024, both of which are incorporated by reference in their entireties.

[0002] The present disclosure relates to resin polymers, methods for their manufacture, and substrate structures, and more particularly to hydrocarbon resin polymers, methods for their manufacture, and substrate structures. [Background technology]

[0003] The fifth generation mobile network technology (abbreviated as 5G mobile network) is the latest generation of mobile communication technology. 5G mobile communication technology has the characteristics of high-speed transmission, wide-ranging connectivity, and low latency. According to the frequency band used, 5G mobile communication technology can be divided into three types: high-frequency 5G, mid-frequency 5G, and low-frequency 5G. High-frequency 5G can achieve ultra-fast connection speeds.

[0004] However, in the process of signal transmission, the signal emission and reception quality of high frequency 5G may be affected by high frequency path loss, conductor loss, and dielectric loss. Therefore, it is necessary to develop a copper clad laminate (CCL) material with low dielectric loss to minimize the dielectric loss in the process of signal transmission in high frequency 5G and improve the signal emission and reception quality of high frequency 5G.

[0005] The reduction of dielectric loss can be achieved by reducing the dielectric properties (dielectric constant (Dk) and dissipation factor (Df)) of the copper clad laminate (CCL) material. Hydrocarbon resins or polyolefin materials, which consist of carbon and hydrogen atoms, have low dielectric loss properties due to the low number of polar functional groups. However, during manufacturing processing, hydrocarbons are easily oxidized by the heating process. The electrical performance of the oxidized hydrocarbon resins is reduced (i.e., the dielectric constant and dissipation factor increase).

[0006] Fluorine substituents are known to provide resins with two important properties: hydrophobicity and electron-withdrawing ability. These two properties greatly affect the dielectric properties of the resin. Specifically, fluorine substituents increase the hydrophobicity of the resin by reducing the surface energy. Hydrophobicity contributes to the resistance of the material to water and dirt, making the material suitable for use in electronic devices, and reducing the effect of moisture on the dielectric properties of the device. In addition, the electron-withdrawing ability of fluorine substituents reduces the polarizability of the material, thereby reducing the dielectric constant and dielectric loss of the material, making resins with fluorine substituents better for high frequency applications and helping to improve the speed and stability of signal transmission. Summary of the Invention [Problem to be solved by the invention]

[0007] In view of the above-mentioned problems, the present disclosure provides a hydrocarbon resin polymer having a fluorine substituent and a method for producing the same. The hydrocarbon resin polymer of the present disclosure has good electrical performance. The substrate structure with a resin layer formed by crosslinking the resin composition containing the hydrocarbon resin polymer of the present disclosure can also have good electrical performance.

[0008] In some embodiments, the present disclosure provides a hydrocarbon resin polymer comprising a repeat unit (A) derived from dicyclopentadiene (DCPD), the hydrocarbon resin polymer having a fluorine substituent, the fluorine substituent content being 100 to 4500 ppm based on the total weight of the hydrocarbon resin polymer.

[0009] In some embodiments, the present disclosure provides a method for producing a hydrocarbon resin polymer, the method comprising polymerizing a mixture in the presence of a fluorine-containing compound, the fluorine-containing compound being a boron trifluoride complex, and the mixture comprising dicyclopentadiene.

[0010] In some embodiments, the present disclosure provides a substrate structure. The substrate structure includes a resin layer and a conductive layer disposed on the resin layer. The resin layer is formed from a resin composition including a hydrocarbon resin polymer using a crosslinking process. The hydrocarbon resin polymer has a fluorine substituent and includes a repeat unit (A) derived from dicyclopentadiene (DCPD), and the fluorine substituent content is 100 to 4500 ppm based on the total weight of the hydrocarbon resin polymer. [Brief description of the drawings]

[0011] The embodiments, objects, features and advantages of the present disclosure can be best understood from the following detailed description taken in conjunction with the accompanying drawings. [Figure 1] FIG. 2 is a schematic diagram of a substrate structure according to an embodiment of the present disclosure. [Diagram 2] 1 is a 19F NMR spectrum of a hydrocarbon resin polymer according to one embodiment of the present disclosure. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0012] It is to be further understood that, as used herein, the terms "comprises," "comprising," "including," and / or "including" specify the presence of stated features, integers, steps, operations, elements, components, and / or groups thereof, but do not exclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and / or groups thereof. Unless the context clearly indicates otherwise, when used in the specification, the singular forms "a," "an," and "the" are intended to encompass the plural forms as well.

[0013] It should be understood that the terms "first," "second," etc. may be used herein to describe various elements, components, regions, layers, and / or locations, but these elements, components, regions, layers, and / or locations are not to be limited by these terms. These terms are used to distinguish one element, component, region, layer, or location from another element, component, region, layer, or location.

[0014] It should be understood that the terms "about", "approximately" and "approximately" as used herein generally indicate a given numerical value or range that varies within 20%, preferably within 10%, preferably within 5%, or within 3%, or within 2%, or within 1%, or within 0.5%. The given numerical value in this specification is an approximation, that is, even if "about", "approximately" or "approximately" is not explicitly stated, the meaning of "about", "approximately" or "approximately" may be included. Furthermore, it should be further understood that the numerical values ​​shown in this specification may include not only the numerical values ​​mentioned above, but also deviation values ​​within a deviation range that is acceptable to a person having ordinary skill in the art. It should be understood that the expression "a to b" used in this specification to indicate a specific numerical range is defined as "≧a and ≦b".

[0015] Unless otherwise defined, all terms (including technical and scientific terms) used in the specification have the same meaning as commonly understood by those skilled in the art to which the present invention belongs. Terms as defined in commonly used dictionaries should be understood to have a meaning consistent with the relevant technology and context or background of this disclosure, and should not be understood in an idealized or overly formal sense unless expressly defined in this specification. Descriptions of known functions and structures that may unnecessarily obscure the present disclosure are omitted below.

[0016] As used herein, the term "C 1-20 "Alkyl group" refers to a monovalent radical of a linear, branched, or cyclic aliphatic hydrocarbon having from 1 to 20 carbon atoms in the carbon chain. 1-20 Examples of alkyl groups include, but are not limited to, methyl, ethyl, propyl, iso-butyl, sec-butyl, tert-butyl, pentyl, iso-amyl, hexyl, decyl, dodecyl, cyclohexyl, cyclooctyl, and cyclododecyl groups, but the disclosure is not limited thereto.

[0017] Some embodiments of the present disclosure provide a hydrocarbon resin polymer. The hydrocarbon resin polymer comprises a repeating unit (A) derived from dicyclopentadiene (DCPD). The hydrocarbon resin polymer has a fluorine substituent, and the content of the fluorine substituent is 100 to 4500 ppm based on the total weight of the hydrocarbon resin polymer. When the content of the fluorine substituent in the hydrocarbon resin polymer is within the above range, the hydrocarbon resin polymer may have better electrical properties. In the present disclosure, the term "content of the fluorine substituent" refers to the amount of the fluorine substituent in the hydrocarbon resin polymer measured using trifluorotoluene (TFT) as an internal standard. 19 It is calculated based on the F NMR spectrum. Specifically, the "content of fluorine substituents" in the present disclosure is calculated using the following formula. Fluorine substituent content (ppm) = (trifluorotoluene (g)) / 146.11 × 19 × integral value of fluoride ions ÷ weight of hydrocarbon resin polymer (g) × 1,000,000 The integral value of the fluoride ion in the above formula is the integral value of the hydrocarbon resin polymer using trifluorotoluene (TFT) as the internal standard. 19 It is the sum of the areas of all peaks in the range from -125 ppm to -230 ppm in the F NMR spectrum.

[0018] In some embodiments, the repeat unit (A) may have the following structure, although the disclosure is not limited thereto:

[0019] [ka]

[0020] In some embodiments, the repeat unit (A) may have a fluorine substituent (not shown).

[0021] The "*" in the above structure indicates the position of connection with other groups or units. Compared with the linear repeating unit, the repeating unit (A) derived from dicyclopentadiene (DCPD) has higher rigidity. Therefore, the glass transition temperature of the hydrocarbon resin polymer can be increased or the thermal properties of the hydrocarbon resin polymer can be improved.

[0022] In some embodiments, the number average molecular weight (Mn) of the hydrocarbon resin polymer may be in the range of 500 to 15,000 g / mol. If the number average molecular weight of the hydrocarbon resin polymer is too high, the solubility of the hydrocarbon resin polymer may be reduced. In some embodiments, the number average molecular weight of the hydrocarbon resin polymer may be 700 to 15,000 g / mol, 800 to 14,000 g / mol, or 900 to 13,000 g / mol.

[0023] The average number of fluorine substituents per molecule of the hydrocarbon resin polymer of the present disclosure can be calculated based on the content of fluorine substituents of the hydrocarbon resin polymer of the present disclosure and the number average molecular weight of the hydrocarbon resin polymer of the present disclosure. Specifically, the average number of fluorine substituents per molecule of the hydrocarbon resin polymer of the present disclosure is calculated using the following formula. Average number of fluorine substituents per molecule of hydrocarbon resin polymer = ((Fluorine substituent content (ppm) × 0.001) / 19) / (1000 / (Number average molecular weight of hydrocarbon resin polymer (g / mol))) According to the above formula, the hydrocarbon resin polymer of the present disclosure is calculated to have an average of 0.02 to 2 fluorine substituents per molecule. In some embodiments, the hydrocarbon resin polymer of the present disclosure has an average of 0.03 to 1.5 fluorine substituents per molecule, 0.03 to 1.0 fluorine substituents, 0.03 to 0.8 fluorine substituents, 0.03 to 0.5 fluorine substituents. When the hydrocarbon resin polymer of the present disclosure has an average of fluorine substituents per molecule within the above range, the electrical performance of the hydrocarbon resin polymer may be better.

[0024] In some embodiments, the hydrocarbon resin polymer may have a polymer dispersity index (PDI) of less than 22. A polymer dispersity index of less than 22 for the hydrocarbon resin polymer provides better processability for the hydrocarbon resin polymer. In some embodiments, the hydrocarbon resin polymer may have a polymer dispersity index of greater than 1.5. In some embodiments, the hydrocarbon resin polymer may have a polymer dispersity index of 1.5 to 20, 2 to 18, or 2.2 to 16.5.

[0025] In some embodiments, the hydrocarbon resin polymers of the present disclosure may include repeat units (B) derived from a monovinylaromatic compound and repeat units (C) derived from a divinylaromatic compound.

[0026] As used herein, a monovinyl aromatic compound is a compound that contains a carbocyclic aromatic structure and in which one hydrogen on a ring carbon atom of the carbocyclic aromatic structure is replaced with a vinyl group. In some embodiments, the vinyl group can be unsubstituted. In some embodiments, at least one hydrogen atom on the vinyl group is replaced with a C 1-20In some embodiments, the carbocyclic aromatic structure may be substituted with an alkyl group. In some embodiments, the carbocyclic aromatic structure may contain 6 to 60 or 6 to 20 ring carbon atoms. In some embodiments, the carbocyclic aromatic structure may be unsubstituted. In some embodiments, at least one hydrogen on a ring carbon atom in the carbocyclic aromatic structure is replaced by a C 1-20 It may be substituted with an alkyl group. Examples of monovinyl aromatic compounds may include, but are not limited to, styrene, methylstyrene, or ethylstyrene.

[0027] The repeat unit (B) derived from a monovinyl aromatic compound includes a carbocyclic aromatic structure derived from a monovinyl aromatic compound. For example, in some embodiments, the repeat unit (B) may have the following structure, but the disclosure is not limited thereto:

[0028] [ka]

[0029] The "*" in the above structure indicates the position of connection to other groups or units.

[0030] As used herein, a divinylaromatic compound is a compound that contains a carbocyclic aromatic structure and in which two hydrogens on the ring carbon atoms of the carbocyclic aromatic structure are replaced with vinyl groups. In some embodiments, the vinyl group can be unsubstituted. In some embodiments, at least one hydrogen atom on the vinyl group is replaced with a C 1-20 In some embodiments, the carbocyclic aromatic structure may be substituted with an alkyl group. In some embodiments, the carbocyclic aromatic structure may contain 6 to 60 or 6 to 20 ring carbon atoms. In some embodiments, the carbocyclic aromatic structure may be unsubstituted. In some embodiments, at least one hydrogen on a ring carbon atom of the carbocyclic aromatic structure is replaced by a C 1-20 It may be substituted with an alkyl group. Examples of divinylaromatic compounds may include, but are not limited to, divinylbenzene or diisopropenylbenzene (IPAMS).

[0031] The repeating unit (C) derived from a divinylaromatic compound comprises a carbocyclic aromatic structure derived from a divinylaromatic compound. In some embodiments, the repeating unit (C) may comprise a crosslinkable repeating unit (C1) and a crosslinked repeating unit (C2).

[0032] [ka]

[0033] R1, R2, R3, and R4 in the crosslinkable repeating unit (C1) and the crosslinked repeating unit (C2) are each independently H or C. 1-20 Ar1 and Ar2 may be alkyl groups, and Ar1 and Ar2 may be phenylene groups. "*" indicates the linking position of the crosslinkable repeating unit (C1) and / or the crosslinked repeating unit (C2) to other groups or units. In some embodiments, the crosslinkable repeating unit (C1) may include the structure shown below, but the disclosure is not limited thereto.

[0034] [ka]

[0035] In some embodiments, the crosslinked repeat unit (C2) may include the structure shown below, although the disclosure is not limited thereto.

[0036] [ka]

[0037] In some embodiments, the hydrocarbon resin polymer may contain 0.15 to 15 mol% of repeating unit (A), 14 to 95 mol% of repeating unit (B), and 4 to 85 mol% of repeating unit (C), where the sum of all units in the hydrocarbon resin polymer is 100 mol%. When the content of repeating unit (A) in the hydrocarbon resin polymer is within the ranges shown above, the thermal properties of the hydrocarbon resin polymer may be better and the manufacturing cost may be lower. When the content of repeating unit (B) and repeating unit (C) in the hydrocarbon resin polymer is within the ranges shown above, the hydrocarbon resin polymer may have better thermal properties and / or processability. In some embodiments, the hydrocarbon resin polymer may contain 0.15 to 10 mol% of repeating unit (A), 50 to 90 mol% of repeating unit (B), and 8 to 40 mol% of repeating unit (C), where the sum of all units in the hydrocarbon resin polymer is 100 mol%. In some embodiments, the hydrocarbon resin polymer may include 1 to 8 mol% of repeating units (A), 60 to 89 mol% of repeating units (B), and 10 to 30 mol% of repeating units (C), where the sum of all units in the hydrocarbon resin polymer is 100 mol%. In some embodiments, the hydrocarbon resin polymer may include 1 to 30 mol% of crosslinkable repeating units (C1), where the sum of all units in the hydrocarbon resin polymer is 100 mol%. When the content of crosslinkable repeating units (C1) in the hydrocarbon resin polymer is within the ranges shown above, the hydrocarbon resin polymer may have good thermal properties, electrical performance, and / or processability. In some embodiments, the hydrocarbon resin polymer may include 3 to 28 mol%, 5 to 25 mol%, or 6 to 22 mol% of crosslinkable repeating units (C1), where the sum of all units in the hydrocarbon resin polymer is 100 mol%.

[0038] The repeating unit (A) and the repeating unit (C) affect the thermal properties and thermal stability of the hydrocarbon resin polymer. In some embodiments, the total content of the repeating unit (A) and the repeating unit (C) in the hydrocarbon resin polymer is 13 mol% or more, where the total of all units in the hydrocarbon resin polymer is 100 mol%. When the total content of the repeating unit (A) and the repeating unit (C) is 13 mol% or more, the hydrocarbon resin polymer can be provided with excellent thermal properties and thermal stability. In some embodiments, the total content of the repeating unit (A) and the repeating unit (C) in the hydrocarbon resin polymer can be 15 mol%, 17 mol%, or 20 mol% or more, where the total of all units in the hydrocarbon resin polymer is 100 mol%. In some embodiments, the total content of the repeating unit (A) and the repeating unit (C) in the hydrocarbon resin polymer can be 45 mol%, 40 mol%, or 35 mol% or less, where the total of all units in the hydrocarbon resin polymer is 100 mol%.

[0039] In some embodiments, the hydrocarbon resin polymer may include a reactive double bond. In the present disclosure, a "reactive double bond" refers to a double bond in the repeat unit (A) or the repeat unit (C) that can react with other compounds or polymers. For example, in some embodiments, the reactive double bond includes a double bond in the repeat unit (A) shown below, or a double bond in a non-benzene ring of the repeat unit (C) shown below, but the present disclosure is not limited thereto.

[0040] [ka]

[0041] In some embodiments, the hydrogen content of the reactive double bonds in the hydrocarbon resin polymer may be less than 10%. If the hydrogen content of the reactive double bonds in the hydrocarbon resin polymer is too high, for example, greater than 10%, the hydrocarbon resin polymer is prone to oxidation during heat processing, which leads to poor electrical performance of the hydrocarbon resin polymer. In some embodiments, the hydrogen content of the reactive double bonds in the hydrocarbon resin polymer may be greater than 0.2%. If the hydrogen content of the reactive double bonds in the hydrocarbon resin polymer is too low, for example, less than 0.2%, the peel strength of the layer containing the hydrocarbon resin polymer may be excessively low. In some embodiments, the hydrogen content of the reactive double bonds in the hydrocarbon resin polymer may be 0.2% to 10%, 0.3% to 9%, 0.4% to 8%, or 0.5% to 7%. If the hydrogen content of the reactive double bonds in the hydrocarbon resin polymer is within the above range, the hydrocarbon resin polymer is less likely to oxidize in a high temperature environment (for example, above 150° C.), or tends to complete the crosslinking reaction before oxidation. Thus, the electrical performance of the hydrocarbon resin polymer may be improved.

[0042] In summary, the hydrocarbon resin polymers of the present disclosure can have good electrical performance (dielectric properties). In some embodiments, the hydrocarbon polymers of the present disclosure can also have good thermal properties or processability.

[0043] In some embodiments, the present disclosure provides a method for making a hydrocarbon resin polymer, the method comprising polymerizing a mixture in the presence of a fluorine-containing compound, the fluorine-containing compound being a boron trifluoride complex, and the mixture comprising dicyclopentadiene.

[0044] In some embodiments, the boron trifluoride complex may include boron trifluoride-tetrahydrofuran complex (BF3·THF), boron trifluoride-methanol complex (BF3·MeOH), boron trifluoride-hydrate (BF3·H2O), boron trifluoride-diethyl ether complex (BF3·OEt2), boron trifluoride-anisole complex (BF3·PhOMe), boron trifluoride-acetic acid complex (BF3·AcOH), or combinations thereof.

[0045] In some embodiments, the molar ratio of fluorine-containing compound:mixture can be 0.01 to 1:20. When the molar ratio of fluorine-containing compound:mixture is within the above range, the method for preparing the hydrocarbon resin polymer of the present disclosure has a better polymerization reaction rate, so that the hydrocarbon resin polymer has a suitable crosslinking degree and molecular weight, and the occurrence of gelation phenomenon can be avoided.In some embodiments, the molar ratio of fluorine-containing compound:mixture can be 0.05 to 1:20, 0.08 to 0.9:20, or 0.1 to 1:20.

[0046] The mixture may further include a monovinyl aromatic compound and / or a divinylaromatic compound, i.e., in some embodiments, the mixture may include dicyclopentadiene and a monovinyl aromatic compound, dicyclopentadiene and a divinylaromatic compound, or dicyclopentadiene and a monovinyl aromatic compound and a divinylaromatic compound.

[0047] In some embodiments, the mixture comprises 3 to 80 mol% dicyclopentadiene, 0 to 90 mol% monovinyl aromatic compounds, and 0 to 50 mol% divinylaromatic compounds, where the sum of all components in the mixture is 100 mol%. In some embodiments, the mixture comprises 3.5 to 70 mol% dicyclopentadiene, 20 to 88 mol% monovinyl aromatic compounds, and 0.05 to 35 mol% divinylaromatic compounds, where the sum of all components in the mixture is 100 mol%. In some embodiments, the mixture comprises 4 to 60 mol% dicyclopentadiene, 25 to 87 mol% monovinyl aromatic compounds, and 0.06 to 25 mol% divinylaromatic compounds, where the sum of all components in the mixture is 100 mol%. The definitions and examples of monovinyl aromatic compounds and divinylaromatic compounds are given above and will not be repeated here.

[0048] In some embodiments, the mixture may be polymerized at a polymerization temperature of 0 to 80° C. In some embodiments, the polymerization temperature may be 0 to 45° C., 0 to 40° C., 0 to 35° C., or 0 to 30° C. In some embodiments, the mixture may be polymerized for a reaction time of 1 to 8 hours. In some embodiments, the reaction time may be 2 to 7 hours.

[0049] The specific structure of the hydrocarbon resin polymer obtained by the method for producing the hydrocarbon resin polymer of the present disclosure is as described above, and will not be repeated here. The hydrocarbon resin polymer obtained by the method for producing the hydrocarbon resin polymer of the present disclosure can have good electrical performance (dielectric properties). In some embodiments, the hydrocarbon resin polymer obtained by the method for producing the hydrocarbon resin polymer of the present disclosure can also have good thermal properties or processability.

[0050] In some embodiments, the present disclosure provides a substrate structure. Figure 1 is a schematic diagram of a substrate structure according to an embodiment of the present disclosure. Referring to Figure 1, the substrate structure of the present disclosure includes a base layer 100, a conductive layer 103 disposed on the base layer 100, and a resin layer 101 disposed between the conductive layer 103 and the base layer 100. The resin layer 101 is formed from a resin composition including the above-mentioned hydrocarbon resin polymer using a crosslinking process.

[0051] In some embodiments, the base layer 100 may include, but is not limited to, polyimide (PI), polycarbonate (PC), polyethylene terephthalate (PET), glass, quartz, sapphire, ceramic, plastic, Ajinomoto Build-Up Film (ABF), fiberglass paper, cotton paper, or combinations thereof.

[0052] In some embodiments, the conductive layer 103 may include, but is not limited to, copper (Cu), aluminum (Al), molybdenum (Mo), tungsten (W), gold (Au), chromium (Cr), nickel (Ni), platinum (Pt), titanium (Ti), another suitable metallic material, or any combination thereof. In some embodiments, the conductive layer 103 may have a single layer structure or a multi-layer stack structure. For example, the conductive layer 103 may include a single layer of metallic copper.

[0053] The base layer 100 may have a first surface 100S1 and a second surface 100S2 opposite to the first surface 100S1. The conductive layer 103 may be disposed on the first surface 100S1 of the base layer 100, and the resin layer 101 may be disposed between the first surface 100S1 of the base layer 100 and the conductive layer 103.

[0054] In some embodiments, the substrate structure may further include another conductive layer 104 on the second surface 100S2 of the base layer 100, and the another resin layer 102 is disposed between the second surface 100S2 of the base layer 100 and the conductive layer 104. The another resin layer 102 may include the same material as the resin layer 101. The another conductive layer 104 may include copper (Cu), aluminum (Al), molybdenum (Mo), tungsten (W), gold (Au), chromium (Cr), nickel (Ni), platinum (Pt), titanium (Ti), another suitable metal material, or any combination thereof, but the present disclosure is not limited thereto. In some embodiments, the another conductive layer 104 may have a single layer structure or a multi-layer stack structure. The another conductive layer 104 may include the same or different material and the same or different structure as the conductive layer 103. For example, the conductive layer 104 may include a single layer of metallic copper.

[0055] Substrate structures having a resin layer comprising the hydrocarbon resin polymer of the present disclosure may have good electrical performance (dielectric properties). In some embodiments, substrate structures having a resin layer may also have good thermal properties, processability, and / or reliability.

[0056] One or more embodiments of the present disclosure will be described in more detail in the following examples, which are, however, used to illustrate the embodiments of the present disclosure and are not intended to limit the scope of the embodiments of the present disclosure.

[0057] [Preparation of Hydrocarbon Resin Polymers 1 to 27] Hydrocarbon resin polymer 1

[0058] Reaction process 6.61 g (5 mol%) of dicyclopentadiene (DCPD), 85.40 g (82 mol%) of styrene, 16.92 g (13 mol%) of divinylbenzene (DVB, 63% purity, the remaining 37% is ethylstyrene), and 289 g of toluene were added to a 1 L 4-neck vertical jacketed reactor under nitrogen atmosphere and stirred at 400 rpm using a four-wing flat blade to produce a mixture. 2.84 g of boron trifluoride-diethyl ether complex (BF3-OEt2) was injected using a syringe pump at a rate of 0.25 mL / min and a reaction temperature of 10 °C (the molar ratio of boron trifluoride-diethyl ether complex:mixture was 0.4:20). After 3 h of reaction time, the polymerization reaction was terminated by adding 9.32 g of isopropanol to obtain a polymer stock solution.

[0059] Refining Process First, the polymer stock solution was diluted with 100 g of toluene. The polymer stock solution was stirred with a mechanical stirrer at a rotation speed of 500 rpm. The polymer stock solution was slowly dripped into isopropanol through an addition funnel to obtain a white resin crude product. The weight of isopropanol was 5 times the weight of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a white solid. The white solid was washed with methanol to remove impurities and isopropanol, and heated at 60° C. under nitrogen atmosphere to remove the solvent, obtaining a white powder of hydrocarbon resin polymer as hydrocarbon resin polymer 1. The yield was about 45%.

[0060] Hydrocarbon Resin Polymer 2

[0061] Reaction process 15.23 g (11 mol%) of dicyclopentadiene, 80.39 g (74 mol%) of styrene, 19.5 g (15 mol%) of divinylbenzene (63% purity, the remaining 37% being ethylstyrene), and 149.82 g of toluene were added to a 1 L 4-neck vertical jacketed reactor under nitrogen atmosphere and stirred at 400 rpm using a four-wing flat blade to produce a mixture. 2.94 g of boron trifluoride-diethyl ether complex was injected using a syringe pump at a rate of 0.25 mL / min and a reaction temperature of 10 °C (the molar ratio of boron trifluoride-diethyl ether complex:mixture was 0.4:20). After 3 hours of reaction time, the polymerization reaction was terminated by adding 10.10 g of isopropanol to obtain a polymer stock solution.

[0062] Refining Process First, the polymer stock solution was diluted with 94 g of toluene. The polymer stock solution was stirred with a mechanical stirrer at a rotation speed of 500 rpm. The polymer stock solution was slowly dripped into isopropanol through an addition funnel to obtain a white resin crude product. The weight of isopropanol was 5 times the weight of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a white solid. The white solid was washed with methanol to remove impurities and isopropanol, and heated at 60° C. under nitrogen atmosphere to remove the solvent, obtaining a white powder of hydrocarbon resin polymer as hydrocarbon resin polymer 2. The yield was about 48%.

[0063] Hydrocarbon resin polymer 3

[0064] Reaction process 17.27 g (17 mol%) of dicyclopentadiene, 55.99 g (70 mol%) of styrene, 13 g (13 mol%) of divinylbenzene (63% purity, remaining 37% is ethylstyrene), and 110.99 g of toluene were added to a 1 L 4-neck vertical jacketed reactor under nitrogen atmosphere and stirred at 400 rpm using a four-wing flat blade to produce a mixture. 1.09 g of boron trifluoride-diethyl ether complex was injected using a syringe pump at a rate of 0.25 mL / min and a reaction temperature of 20 °C (the molar ratio of boron trifluoride-diethyl ether complex:mixture was 0.2:20). After 5.5 hours of reaction time, the polymerization reaction was terminated by adding 4.32 g of isopropanol to obtain a polymer stock solution.

[0065] Refining Process First, the polymer stock solution was diluted with 52 g of toluene. The polymer stock solution was stirred with a mechanical stirrer at a rotation speed of 500 rpm. The polymer stock solution was slowly dripped into isopropanol through an addition funnel to obtain a white resin crude product. The weight of isopropanol was 5 times the weight of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a white solid. The white solid was washed with methanol to remove impurities and isopropanol, and heated at 60° C. under nitrogen atmosphere to remove the solvent, obtaining a white powder of hydrocarbon resin polymer as hydrocarbon resin polymer 3. The yield was about 51%.

[0066] Hydrocarbon Resin Polymer 4

[0067] Reaction process 21.6 g (17 mol%) of dicyclopentadiene (95% purity), 70 g (70 mol%) of styrene (99.8% purity), 16.25 g (13 mol%) of divinylbenzene (63% purity, the remaining 37% being ethylstyrene), and 160 mL of toluene were added to a 1 L four-neck vertical jacketed reactor under nitrogen atmosphere and stirred at a stirring speed of 400 rpm using a one layer four-wing flat blade to produce a mixture. 2.73 g of boron trifluoride-diethyl ether complex was injected using a syringe pump at a rate of 0.25 mL / min and a reaction temperature of 10 °C (the molar ratio of boron trifluoride-diethyl ether complex:mixture was 0.4:20). After 2 hours of reaction time, the polymerization reaction was terminated by adding 8.1 g of isopropanol to obtain a colorless polymer stock solution.

[0068] Refining Process First, the polymer stock solution was filtered to remove impurities and insolubles. The polymer stock solution was stirred with a mechanical stirrer at a rotation speed of 500 rpm. The polymer stock solution was slowly dripped into isopropanol through an addition funnel to obtain a white resin crude product. The weight of isopropanol was 5 times that of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a white solid. The white solid was redissolved in toluene to make another stock solution, and a precipitation step was performed with isopropanol (weight ratio of stock solution to isopropanol was 1:5). After filtration, a white resin solid with higher purity was obtained. The white resin solid was washed with methanol to remove impurities and isopropanol, and then heated and stirred under vacuum to remove the solvent, obtaining a white powder of hydrocarbon resin polymer as hydrocarbon resin polymer 4.

[0069] Hydrocarbon Resin Polymer 5

[0070] Reaction process 34.53 g (17 mol%) of dicyclopentadiene (95% purity), 111.99 g (70 mol%) of styrene (99.8% purity), 26 g (13 mol%) of divinylbenzene (63% purity, the remaining 37% being ethylstyrene), and 166.48 g of toluene were added to a 1 L 4-neck vertical jacketed reactor under nitrogen atmosphere and stirred at 400 rpm using a four-wing flat blade to produce a mixture. 2.18 g of boron trifluoride-diethyl ether complex was injected using a syringe pump at a rate of 0.25 mL / min and a reaction temperature of 20 °C (the molar ratio of boron trifluoride-diethyl ether complex:mixture was 0.2:20). After 4.5 hours of reaction time, the polymerization reaction was terminated by adding 3.89 g of isopropanol to obtain a polymer stock solution.

[0071] Refining Process First, the polymer stock solution was diluted with 75 g of toluene. The polymer stock solution was stirred with a mechanical stirrer at a rotation speed of 500 rpm. The polymer stock solution was slowly dripped into isopropanol through an addition funnel to obtain a white resin crude product. The weight of isopropanol was 5 times the weight of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a white solid. The white solid was washed with methanol to remove impurities and isopropanol, and heated at 60° C. under nitrogen atmosphere to remove the solvent, obtaining a white powder of hydrocarbon resin polymer as hydrocarbon resin polymer 5.

[0072] Hydrocarbon resin polymers 6 and 7 Hydrocarbon resin polymers 6 and 7 were obtained by the same reaction and purification processes as those for hydrocarbon resin polymer 5, except that the reaction time was changed from 4.5 hours to 5.5 hours and 6.5 hours, respectively.

[0073] Hydrocarbon resin polymer 8

[0074] Reaction process 25.89 g (17 mol%) of dicyclopentadiene, 83.99 g (70 mol%) of styrene, 19.5 g (13 mol%) of divinylbenzene (63% purity, remaining 37% is ethylstyrene), and 66.60 g of toluene were added to a 1 L 4-neck vertical jacketed reactor under nitrogen atmosphere and stirred at 400 rpm using a four-wing flat blade to produce a mixture. 0.82 g of boron trifluoride-diethyl ether complex was injected using a syringe pump at a rate of 0.25 mL / min and a reaction temperature of 20 °C (the molar ratio of boron trifluoride-diethyl ether complex:mixture was 0.1:20). After 2 hours of reaction time, the polymerization reaction was terminated by adding 3.77 g of isopropanol to obtain a polymer stock solution.

[0075] Refining Process First, the polymer stock solution was diluted with 52 g of toluene. The polymer stock solution was stirred with a mechanical stirrer at a rotation speed of 500 rpm. The polymer stock solution was slowly dripped into isopropanol through an addition funnel to obtain a white resin crude product. The weight of isopropanol was 5 times the weight of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a white solid. The white solid was washed with methanol to remove impurities and isopropanol, and heated at 60° C. under nitrogen atmosphere to remove the solvent, obtaining a white powder of hydrocarbon resin polymer as hydrocarbon resin polymer 8.

[0076] Hydrocarbon Resin Polymer 9 to 12 Hydrocarbon resin polymers 9 to 12 were obtained by the same reaction and purification process as for hydrocarbon resin polymer 8, except that the reaction time was changed from 2 hours to 2.5 hours, 3 hours, 4 hours and 4.5 hours, respectively.

[0077] Hydrocarbon resin polymer 13

[0078] Reaction process 20.30 g (20 mol%) of dicyclopentadiene, 53.59 g (67 mol%) of styrene, and 110.976 g of toluene were added to a 400 mL five-neck vertical jacketed reactor under nitrogen atmosphere and stirred with a four-wing flat blade at a stirring speed of 400 rpm to produce a mixture. 4.36 g of boron trifluoride-diethyl ether complex was injected using a syringe pump at a rate of 0.25 mL / min and a reaction temperature of 20 °C (the molar ratio of boron trifluoride-diethyl ether complex:mixture was 0.8:20). After 0.5 hours, 13 g (13 mol%) of divinylbenzene (63% purity, the remaining 37% was ethylstyrene) was added. After 1.5 hours of reaction time, the polymerization reaction was terminated by adding 11.8 g of isopropanol to obtain a polymer stock solution.

[0079] Refining Process First, the polymer stock solution was diluted with 53 g of toluene. The polymer stock solution was stirred with a mechanical stirrer at a rotation speed of 500 rpm. The polymer stock solution was slowly dripped into isopropanol through an addition funnel to obtain a pale yellow resin crude product. The weight of isopropanol was 5 times the weight of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a pale yellow solid. The pale yellow solid was washed with methanol to remove impurities and isopropanol, and heated at 60° C. under nitrogen atmosphere to remove the solvent, obtaining a pale yellow powder of hydrocarbon resin polymer as hydrocarbon resin polymer 13. The yield was about 72%.

[0080] Hydrocarbon resin polymer 14

[0081] Reaction process 33.05 g (50 mol%) of dicyclopentadiene, 9.50 g (18.25 mol%) of styrene, 20.67 g (31.75 mol%) of divinylbenzene (63% purity, remaining 37% is ethylstyrene), 15.10 g of butyl acetate, and 29.26 g of toluene were added to a 400 mL five-neck vertical jacketed reactor under nitrogen atmosphere and stirred at 400 rpm using a four-wing flat blade to produce a mixture. 1.42 g of boron trifluoride-diethyl ether complex was injected using a syringe pump at a rate of 0.25 mL / min and a reaction temperature of 70 °C (the molar ratio of boron trifluoride-diethyl ether complex:mixture was 0.4:20). After 3 hours of reaction time, the polymerization reaction was terminated by adding 50 g of 5 wt% aqueous sodium bicarbonate solution to obtain a polymer stock solution.

[0082] Refining Process First, the polymer stock solution was diluted with 45 g of toluene. The polymer stock solution was stirred with a mechanical stirrer at a rotation speed of 500 rpm. The polymer stock solution was slowly dripped into isopropanol through an addition funnel to obtain a pale yellow resin crude product. The weight of isopropanol was 5 times the weight of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a pale yellow solid. 20 g of the crude product was dissolved in 40 g of toluene and stirred with a 50 mm stir bar at 200 rpm to obtain a polymer solution. The polymer solution was slowly dripped into isopropanol through an addition funnel to obtain a pale yellow resin crude product. The weight of isopropanol was 5 times the weight of the polymer solution. The solid-liquid phase was filtered by suction to obtain a pale yellow solid. The pale yellow solid was washed with methanol to remove impurities and isopropanol, and heated at 60° C. under nitrogen to remove the solvent to obtain a pale yellow powder of hydrocarbon resin polymer as hydrocarbon resin polymer 14.

[0083] Hydrocarbon Resin Polymer 15

[0084] Reaction process 50.67 g (20 mol%) of dicyclopentadiene (95% purity), 133.98 g (67 mol%) of styrene (99.8% purity), 32.5 g (13 mol%) of divinylbenzene (63% purity, the remaining 37% being ethylstyrene), and 320 mL of toluene were added to a 1 L 4-neck vertical jacketed reactor under nitrogen atmosphere and stirred at a stirring speed of 400 rpm using a one layer four-wing flat blade to produce a mixture. 5.45 g of boron trifluoride-diethyl ether complex was injected using a syringe pump at a rate of 0.25 mL / min and a reaction temperature of 10 °C (the molar ratio of boron trifluoride-diethyl ether complex:mixture was 0.4:20). After the addition of boron trifluoride-diethyl ether complex, the reaction temperature was adjusted to 15 °C and maintained for 2 h. The polymerization reaction was terminated by adding 16.2 g of isopropanol to obtain a colorless polymer stock solution.

[0085] Refining Process

[0086] First, the polymer stock solution was filtered to remove impurities and insolubles. The polymer stock solution was stirred with a mechanical stirrer at a rotation speed of 500 rpm. The polymer stock solution was slowly dripped into isopropanol through an addition funnel to obtain a white resin crude product. The weight of isopropanol was 5 times that of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a white solid. The white solid was redissolved in toluene to make another stock solution, and a precipitation step was performed with isopropanol (weight ratio of stock solution to isopropanol was 1:5). After filtration, a white resin solid with higher purity was obtained. The white resin solid was washed with methanol to remove impurities and isopropanol, and then heated and stirred under vacuum to remove the solvent, and a white powder of hydrocarbon resin polymer was obtained. The white powder of hydrocarbon resin polymer was redissolved in tetrahydrofuran to make another stock solution, and a precipitation step was performed with isopropanol (weight ratio of stock solution to isopropanol was 1:5). After filtration, a white resin solid with higher purity was obtained. The white resin solid was washed with methanol to remove impurities and isopropanol, then heated and stirred under vacuum to remove the solvent, yielding a white powder of hydrocarbon resin polymer as Hydrocarbon Resin Polymer 15.

[0087] Hydrocarbon Resin Polymer 16

[0088] Reaction process 21.6 g (17 mol%) of dicyclopentadiene (95% purity), 65.99 g (66 mol%) of styrene (99.8% purity), 21.25 g (17 mol%) of divinylbenzene (63% purity, the remaining 37% is ethylstyrene), and 160 mL of toluene were added to a 1 L 4-neck vertical jacketed reactor under nitrogen atmosphere and stirred at 400 rpm using a one layer four-wing flat blade to produce a mixture. 2.73 g of boron trifluoride-diethyl ether complex was injected using a syringe pump at a rate of 0.25 mL / min and a reaction temperature of 0°C (the molar ratio of boron trifluoride-diethyl ether complex:mixture was 0.4:20). After adding boron trifluoride-diethyl ether complex and waiting for 2 hours, 8.1 g of isopropanol was added to terminate the polymerization reaction, yielding a colorless polymer stock solution.

[0089] Refining Process First, the polymer stock solution was filtered to remove impurities and insolubles. The polymer stock solution was stirred with a mechanical stirrer at a rotation speed of 500 rpm. The polymer stock solution was slowly dripped into isopropanol through an addition funnel to obtain a white resin crude product. The weight of isopropanol was 5 times that of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a white solid. The white solid was redissolved in toluene to make another stock solution, and a precipitation step was performed with isopropanol (weight ratio of stock solution to isopropanol was 1:5). After filtration, a white resin solid with higher purity was obtained. The white resin solid was washed with methanol to remove impurities and isopropanol, and then heated and stirred under vacuum to remove the solvent, and a white powder of hydrocarbon resin polymer was obtained. The white powder of hydrocarbon resin polymer was redissolved in tetrahydrofuran to make another stock solution, and a precipitation step was performed with isopropanol (weight ratio of stock solution to isopropanol was 1:5). After filtration, a white resin solid with higher purity was obtained. The white resin solid was washed with methanol to remove impurities and isopropanol, then heated and stirred under vacuum to remove the solvent, yielding a white powder of hydrocarbon resin polymer as Hydrocarbon Resin Polymer 16.

[0090] Hydrocarbon Resin Polymer 17

[0091] Reaction process 43.15g (17mol%) of dicyclopentadiene (95% purity), 129.98g (65mol%) of styrene (99.8% purity), 44.99g (18mol%) of divinylbenzene (63% purity, the remaining 37% is ethylstyrene), and 320mL of toluene were added to a 1L 4-neck vertical jacketed reactor under nitrogen atmosphere and stirred at 400rpm using a one layer four-wing flat blade to produce a mixture. 5.45g of boron trifluoride-diethyl ether complex was injected using a syringe pump at a rate of 0.25mL / min and a reaction temperature of 0℃ (the molar ratio of boron trifluoride-diethyl ether complex:mixture was 0.4:20). After adding boron trifluoride-diethyl ether complex and waiting for 2 hours, 16.2g of isopropanol was added to terminate the polymerization reaction, yielding a colorless polymer stock solution.

[0092] Refining Process First, the polymer stock solution was filtered to remove impurities and insolubles. The polymer stock solution was stirred with a mechanical stirrer at a rotation speed of 500 rpm. The polymer stock solution was slowly dripped into isopropanol through an addition funnel to obtain a white resin crude product. The weight of isopropanol was 5 times that of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a white solid. The white solid was redissolved in toluene to make another stock solution, and a precipitation step was performed with isopropanol (weight ratio of stock solution to isopropanol was 1:5). After filtration, a white resin solid with higher purity was obtained. The white resin solid was washed with methanol to remove impurities and isopropanol, and then heated and stirred under vacuum to remove the solvent, and a white powder of hydrocarbon resin polymer was obtained. The white powder of hydrocarbon resin polymer was redissolved in tetrahydrofuran to make another stock solution, and a precipitation step was performed with isopropanol (weight ratio of stock solution to isopropanol was 1:5). After filtration, a white resin solid with higher purity was obtained. The white resin solid was washed with methanol to remove impurities and isopropanol, then heated and stirred under vacuum to remove the solvent, yielding a white powder of hydrocarbon resin polymer as Hydrocarbon Resin Polymer 17.

[0093] Hydrocarbon resin polymer 18

[0094] Reaction process 21.58 g (17 mol%) of dicyclopentadiene (95% purity), 56.99 g (57 mol%) of styrene (99.8% purity), 32.50 g (26 mol%) of divinylbenzene (63% purity, the remaining 37% is ethylstyrene), and 160 mL of toluene were added to a 1 L four-neck vertical jacketed reactor under nitrogen atmosphere and stirred at 400 rpm using a one layer four-wing flat blade to produce a mixture. 1.36 g of boron trifluoride-diethyl ether complex was injected using a syringe pump at a rate of 0.25 mL / min and low reaction temperature (0°C) (the molar ratio of boron trifluoride-diethyl ether complex:mixture was 0.2:20). After adding boron trifluoride-diethyl ether complex and waiting for 2 hours, 4.1 g of isopropanol was added to terminate the polymerization reaction, yielding a colorless polymer stock solution.

[0095] Refining Process First, the polymer stock solution was filtered to remove impurities and insolubles. The polymer stock solution was stirred with a mechanical stirrer at a rotation speed of 500 rpm. The polymer stock solution was slowly dripped into isopropanol through an addition funnel to obtain a white resin crude product. The weight of isopropanol was 5 times that of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a white solid. The white solid was redissolved in toluene to make another stock solution, and a precipitation step was performed with isopropanol (weight ratio of stock solution to isopropanol was 1:5). After filtration, a white resin solid with higher purity was obtained. The white resin solid was washed with methanol to remove impurities and isopropanol, and then heated and stirred under vacuum to remove the solvent, and a white powder of hydrocarbon resin polymer was obtained. The white powder of hydrocarbon resin polymer was redissolved in tetrahydrofuran to make another stock solution, and a precipitation step was performed with isopropanol (weight ratio of stock solution to isopropanol was 1:5). After filtration, a white resin solid with higher purity was obtained. The white resin solid was washed with methanol to remove impurities and isopropanol, then heated and stirred under vacuum to remove the solvent, yielding a white powder of hydrocarbon resin polymer as Hydrocarbon Resin Polymer 18.

[0096] Hydrocarbon resin polymer 19

[0097] Reaction process 20 g of dicyclopentadiene (100 mol%) and 10.93 g of toluene were added to a 100 mL three-neck reactor under nitrogen atmosphere and stirred with a stir bar at a stirring speed set at 400 rpm to produce a mixture. 0.43 g of boron trifluoride-diethyl ether complex was injected at once at a reaction temperature of 25°C (the molar ratio of boron trifluoride-diethyl ether complex:mixture was 0.4:20). The polymerization reaction was terminated after 4.5 hours of reaction time by adding 1.39 g of isopropanol to obtain a polymer stock solution.

[0098] Refining Process The polymer stock solution was stirred with a stir bar at a stirring speed set at 400 rpm and slowly dripped into isopropanol through an addition funnel to obtain a yellow crude resin product. The weight of isopropanol was 5 times the weight of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a yellow solid. The pale yellow solid was washed with methanol to remove impurities and isopropanol, and then heated at 60° C. under vacuum to remove the solvent, obtaining a yellow powder of hydrocarbon resin polymer as hydrocarbon resin polymer 19. The yield was about 6%.

[0099] Hydrocarbon Resin Polymer 20

[0100] Reaction process 20 g (55.6 mol%) of styrene (99.8% purity), 20 g (44.4 mol%) of divinylbenzene (63% purity, the remaining 37% is ethylstyrene), and 520.2 g of toluene were added to a 1000 mL 5-neck vertical jacketed reactor under nitrogen atmosphere and stirred at 400 rpm using a four-wing flat blade to produce a mixture. 2.185 g of boron trifluoride-diethyl ether complex was injected using a syringe pump at a rate of 0.25 mL / min and a reaction temperature of 20 °C (the molar ratio of boron trifluoride-diethyl ether complex:mixture was 0.88:20). After 3 hours of reaction time, the polymerization reaction was terminated by adding 11.8 g of isopropanol to obtain a polymer stock solution.

[0101] Refining Process First, the polymer stock solution was diluted with 260 g of toluene. The polymer stock solution was stirred with a mechanical stirrer at a rotation speed of 500 rpm. The polymer stock solution was slowly dripped into isopropanol through an addition funnel to obtain a pale yellow resin crude product. The weight of isopropanol was 5 times the weight of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a pale yellow solid. The pale yellow solid was washed with methanol to remove impurities and isopropanol, and heated at 60° C. under nitrogen atmosphere to remove the solvent, obtaining a yellow powder of hydrocarbon resin polymer as hydrocarbon resin polymer 20. The yield was about 40%.

[0102] Hydrocarbon Resin Polymer 21

[0103] Reaction process 15 g (100 mol%) of divinylbenzene (63% purity, the remaining 37% being ethylstyrene) and 30 g of toluene were added to a 250 mL round bottom flask at 25 °C under a nitrogen atmosphere to form a mixture. 1.0 g of boron trifluoride-diethyl ether complex was added at a reaction temperature of 10 °C (the molar ratio of boron trifluoride-diethyl ether complex:mixture is 0.12:20). At this time, the mixture immediately turned from colorless to yellow. The mixture was stirred at 10 °C for 20 minutes, and then 1 mL of isopropanol was added to terminate the polymerization reaction, obtaining a polymer stock solution.

[0104] Refining Process The pale yellow polymer solution was precipitated from isopropanol (500 mL) to give a white powder, which was then dried at 60° C. for 3 hours to give 9.8 g of hydrocarbon resin polymer 21. The yield was about 65%.

[0105] Hydrocarbon resin polymer 22

[0106] Reaction process 15 g (100 mol%) of styrene and 30 g of toluene were added to a 250 mL round bottom flask at 25°C under nitrogen atmosphere to form a mixture. 1.0 g of boron trifluoride-diethyl ether complex was added at a reaction temperature of 10°C (the molar ratio of boron trifluoride-diethyl ether complex:mixture is 0.2:20). At this time, the mixture immediately turned from colorless to yellow. The mixture was stirred at 10°C for 30 minutes, and then 1 mL of isopropanol was added to terminate the polymerization reaction and obtain a polymer stock solution.

[0107] Refining Process The pale yellow polymer solution was precipitated from isopropanol (500 mL) to give a white powder, which was then dried at 60° C. for 3 hours to give 8.3 g of hydrocarbon resin polymer 22. The yield was about 55%.

[0108] Hydrocarbon Resin Polymer 23

[0109] Reaction process 40 g (100 mol%) of dicyclopentadiene and 10 g of toluene were added to a 250 mL round bottom flask at 25 °C under nitrogen atmosphere to form a mixture. 0.42 g of boron trifluoride-diethyl ether complex was added (the molar ratio of boron trifluoride-diethyl ether complex:mixture is 0.2:20). The mixture immediately turned from colorless to brown. The mixture was stirred at 25 °C for 24 hours, and then 1 mL of isopropanol was added to terminate the polymerization reaction, yielding a polymer stock solution.

[0110] Refining Process

[0111] The brown polymer solution was precipitated from isopropanol (250 mL) to give a brown-orange powder, which was then dried at 60° C. for 3 hours to give 20.0 g of hydrocarbon resin polymer 23. The yield was about 50%.

[0112] Hydrocarbon Resin Polymer 24

[0113] Reaction process 19.2 g (60 mol%) of styrene, 3.6 g (40 mol%) of divinylbenzene (63% purity, the remaining 37% being ethylstyrene), and 30 g of toluene were added to a 250 mL round-bottom flask under nitrogen to form a mixture. 0.7 g of boron trifluoride-diethyl ether complex was added at a reaction temperature of 10 °C (the molar ratio of boron trifluoride-diethyl ether complex:mixture is 0.46:20). The mixture immediately turned from colorless to pale yellow. The mixture was stirred at 10 °C for 30 minutes, and then 1 mL of isopropanol was added to terminate the polymerization reaction, yielding a polymer stock solution.

[0114] Refining Process The pale yellow polymer solution was precipitated from isopropanol (500 mL) to give a white powder, which was then dried at 60° C. for 3 hours to give 14.8 g of hydrocarbon resin polymer 24. The yield was about 65%.

[0115] Hydrocarbon Resin Polymer 25

[0116] Reaction process A mixture was made by adding 8.4 g (20 mol%) dicyclopentadiene, 19.9 g (60 mol%) styrene, 10.1 g (20 mol%) diisopropenylbenzene (IPAMS), and 100 g toluene to a 250 mL round-bottom flask under nitrogen. 0.36 g boron trifluoride-diethyl etherate was added (the molar ratio of boron trifluoride-diethyl etherate:mixture was 0.16:20). The mixture immediately turned from colorless to yellow. The mixture was stirred at 20 °C for 3 h, and then 1 mL of isopropanol was added to terminate the polymerization reaction, yielding a polymer stock solution.

[0117] Refining Process The yellow polymer solution was precipitated from isopropanol (600 mL) to obtain a white powder, which was then dried at 60° C. for 3 hours to obtain 18.7 g of hydrocarbon resin polymer 25. The yield was about 48.58%.

[0118] Hydrocarbon Resin Polymer 26

[0119] Reaction process 25.38 g (20 mol%) of dicyclopentadiene, 68.07 g (60 mol%) of methylstyrene, 25 g (20 mol%) of divinylbenzene (63% purity, remaining 37% is ethylstyrene), and 320 mL of toluene were added to a 1 L 4-neck vertical jacketed reactor under nitrogen atmosphere and stirred at 400 rpm with a one layer four-wing flat blade to produce a mixture. 2.73 g of boron trifluoride-diethyl ether complex was injected using a syringe pump at a rate of 0.25 mL / min and a reaction temperature of 0°C (the molar ratio of boron trifluoride-diethyl ether complex:mixture was 0.4:20). After the addition of boron trifluoride-diethyl ether complex, the reaction temperature was adjusted to 23°C. After 3 hours of reaction time, the polymerization reaction was terminated by adding 8.1 g of isopropanol to obtain a colorless polymer stock solution.

[0120] Refining Process First, the polymer stock solution was filtered to remove impurities and insolubles. The polymer stock solution was stirred with a mechanical stirrer at a rotation speed of 500 rpm. The polymer stock solution was slowly dripped into isopropanol through an addition funnel to obtain a white resin crude product. The weight of isopropanol was 5 times that of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a white solid. The white solid was redissolved in toluene to make another stock solution, and a precipitation step was performed with isopropanol (weight ratio of stock solution to isopropanol was 1:5). After filtration, a white resin solid with higher purity was obtained. The white resin solid was washed with methanol to remove impurities and isopropanol, and then heated and stirred under vacuum to remove the solvent, obtaining a white powder of hydrocarbon resin polymer as hydrocarbon resin polymer 26.

[0121] Hydrocarbon Resin Polymer 27

[0122] Reaction process 9 g (44 mol%) of norbornene (NB), 9.93 g (43 mol%) of styrene, 3.73 g (13 mol%) of divinylbenzene (63% purity, the remaining 37% being ethylstyrene), and 30 mL of toluene were added to a 1 L three-neck vertical jacketed reactor under nitrogen atmosphere and stirred at a stirring speed of 400 rpm using a stir bar to produce a mixture. After the addition of boron trifluoride-diethyl ether complex, the reaction temperature was maintained at 0°C. After 2 hours of reaction time, the polymerization reaction was terminated by adding tetrahydrofuran to obtain a colorless polymer stock solution.

[0123] Refining Process First, the polymer stock solution was filtered to remove impurities and insolubles. The polymer stock solution was stirred with a mechanical stirrer at a rotation speed of 500 rpm. The polymer stock solution was slowly dripped into isopropanol through an addition funnel to obtain a white resin crude product. The weight of isopropanol was 5 times that of the polymer stock solution. The solid-liquid phase was filtered by suction to obtain a white solid. The white solid was redissolved in tetrahydrofuran to make another stock solution, and a precipitation step was performed with isopropanol (weight ratio of stock solution to isopropanol was 1:5). After filtration, a white resin solid with higher purity was obtained. The white resin solid was washed with methanol to remove impurities and isopropanol, and then heated and stirred under vacuum to remove the solvent, obtaining a white powder of hydrocarbon resin polymer as hydrocarbon resin polymer 27.

[0124] The materials and ratios (DCPD, monovinyl aromatics, and divinylaromatic compounds, or NB, monovinyl aromatics, and divinylaromatic compounds taken as 100 mol %) used to prepare the hydrocarbon resin polymers 1 to 27 are shown in Table 1 below. The polymerization time, polymerization temperature, and content of fluorine-containing compound (boron trifluoride-diethyl ether complex) are shown in Table 2 below.

[0125] [Table 1]

[0126] [Table 2]

[0127] The content of the fluorine-containing compound listed in Table 2 above is the molar ratio of the sum of the raw materials listed in Table 1 above to the fluorine-containing compound, with the sum of the raw materials listed in Table 1 above being 100 moles. For example, in Table 2, it can be seen that the content of the fluorine-containing compound in the hydrocarbon polymer 1 is 2, and the molar ratio of the sum of the DCPD, monovinyl aromatic compound, and divinyl aromatic compound listed in Table 1 to the fluorine-containing compound is 100:2.

[0128] [Structural analysis of hydrocarbon resin polymers 1 to 27]

[0129] The structural composition of the hydrocarbon resin polymers 1 to 27 was determined using nuclear magnetic resonance (NMR, JEOL, JNM-ECZ400S). 13 C-NMR and 1 The H-NMR analysis was performed. It should be understood that the hydrocarbon resin polymers 1 to 27 contain a repeat unit (A) derived from dicyclopentadiene, a repeat unit (B) derived from a monovinyl aromatic compound, and a repeat unit (C) derived from a divinylaromatic compound. Table 3 shows the repeat unit (A) content, repeat unit (B) content, repeat unit (C) content, and the sum of the repeat unit (A) and repeat unit (C) content of the hydrocarbon resin polymers 1 to 13 and 15 to 24, where the sum of the repeat unit (A), repeat unit (B), and repeat unit (C) is 100 mol %.

[0130] [Table 3]

[0131] [Measurement of physical / chemical properties of hydrocarbon resin polymers 1 to 27]

[0132] [Measurement of hydrogen content in reactive double bonds] Hydrocarbon resin polymers 1 to 27 were each dissolved in deuterated chloroform (CDCl3). The hydrogen content at the reactive double bonds in the hydrocarbon resin polymers 1 to 27 was measured by NMR (JEOL, JNM-ECZ400S / L1). Specifically, the hydrogen content at the reactive double bonds in the hydrocarbon resin polymers 1 to 27 was calculated by dividing the sum of the integral values ​​of hydrogen at the reactive double bonds by the sum of the integral values ​​of all hydrogen.

[0133] [Measurement of number average molecular weight (Mn) and polymer dispersity index (PDI)] Using polystyrene as a standard, the number average molecular weight (Mn) and polymer dispersity index (PDI) of the hydrocarbon resin polymers 1 to 27 were measured by gel permeation chromatography (GPC) (Waters APC, column: Waters Acquity XT 900).

[0134] Specifically, 5 mL of tetrahydrofuran (THF) was added to 0.01 g of hydrocarbon resin polymers 1 to 27, respectively, to prepare samples of hydrocarbon resin polymers 1 to 27. The samples of hydrocarbon resin polymers 1 to 27 were filtered through a 0.22 μm filter and analyzed by an instrument to obtain the number average molecular weight (Mn) and polymer dispersibility index (PDI) of hydrocarbon resin polymers 1 to 27.

[0135] [Measurement of the content of crosslinkable repeating units (C1)] The structures of the hydrocarbon resin polymers 1 to 27 were determined by NMR (JEOL, JNM-ECZ400S / L1) and GPC (Waters). CDCl3 was used as the solvent, and the resonance line of CDCl3 was used as the internal standard to obtain the content of crosslinkable repeating units (C1) in the hydrocarbon resin polymers 1 to 27.

[0136] The number average molecular weight (Mn), polymer dispersibility index (PDI), hydrogen content in reactive double bonds, and crosslinkable repeat unit (C1) content of the hydrocarbon resin polymers 1 to 27 are shown in Table 4 below.

[0137] [Table 4]

[0138] [Electrical performance test of hydrocarbon resin polymer] 20g of hydrocarbon resin polymer 1, 2, 4, 13, 15, 16, 17, and 20 were dissolved in 20g of toluene to make a mixture. The mixture was stirred until the hydrocarbon resin polymer was completely dissolved therein to make hydrocarbon resin polymer solutions 1, 2, 4, 13, 15, 16, 17, and 20. Glass fiber cloth (Asahi 2116, Dk / Df=3.3 / 0.0030@28GHz) was immersed in the hydrocarbon resin polymer solutions 1, 2, 4, 13, 15, 16, 17, and 20 for 16 hours and baked at 170°C for 10 minutes to make samples 1, 2, 4, 13, 15, 16, 17, and 20, respectively. The weights of the samples were measured using a network analyzer software (network analyzer Keysight, P5007A, SCR). The Dk / Df and RC% of the samples at 28GHz were measured and the results are shown in Table 5 below. Here, RC% represents the resin content. RC% = (weight after baking - weight of glass fiber cloth) / weight after baking x 100%

[0139] [Table 5]

[0140] [Measurement of fluorine substituent content] Preparation of internal standard solution: 2.9 mg of trifluorotoluene (TFT, internal standard) is dissolved in 7.9 mg of CDCl3 450 to prepare an internal standard solution (TFT content 0.0643%).

[0141] Sample preparation: 5 g of the hydrocarbon resin polymers 1 to 27 were added to about 1.1 g of the above internal standard solution, and ultrasonic shaking was performed for 10 minutes. After the hydrocarbon resin polymers 1 to 27 were dissolved, the samples were transferred to NMR tubes (JEOL / JNM-ECZ400S / L1) and analyzed in a test environment of 25°C. 19 F NMR spectra were obtained.

[0142] The resulting hydrocarbon resin polymer19 Based on the F NMR spectrum, the fluorine substituent content of the hydrocarbon resin polymers 1 to 27 is calculated using the following formula: Fluorine substituent content (ppm) = (trifluorotoluene (g)) / 146.11 × 19 × fluoride ion integral value ÷ weight of hydrocarbon resin polymer (g) × 1,000,000 The integral value of the fluoride ion in the above equation is obtained 19 It is the sum of the areas of all peaks in the range from -125 ppm to -230 ppm in the F NMR spectrum.

[0143] For example, FIG. 2 shows the structure of the hydrocarbon resin polymer 15. 19 The fluorine substituent content of the hydrocarbon polymer 15 is shown in FIG. 19 The F NMR spectrum was calculated based on the integral of the fluoride ion calculated by summing the areas of all peaks in the range of −125 ppm to −230 ppm, according to the above formula.

[0144] The average number of fluorine substituents of the hydrocarbon resin polymers 1 to 19 was calculated based on the fluorine substituent content of the hydrocarbon resin polymers 1 to 19 and the number average molecular weight of the hydrocarbon resin polymers 1 to 19. Specifically, the average number of fluorine substituents per molecule of the hydrocarbon resin polymer of the present disclosure is calculated using the following formula. Average number of fluorine substituents per molecule of hydrocarbon resin polymer = ((Fluorine substituent content (ppm) × 0.001) / 19) / (1000 / (Number average molecular weight of hydrocarbon resin polymer (g / mol)))

[0145] The fluorine substituent content of the hydrocarbon polymers 1 to 19 calculated above, and the average number of fluorine substituents per molecule of the hydrocarbon polymers are listed in Table 6 below.

[0146] [Table 6]

[0147] According to Table 6 above, the hydrocarbon resin polymers 20, 21, 22, and 24 have no fluorine substituents. Furthermore, the hydrocarbon resin polymer 27, which is polymerized from norbornene instead of dicyclopentadiene, has no fluorine substituents. It is clear that dicyclopentadiene and fluorine-containing compounds are necessary to prepare the hydrocarbon resin polymers with fluorine substituents.

[0148] According to Tables 5 and 6, the hydrocarbon resin polymers with fluorine substituents have a lower loss factor (Df). It is clear that the hydrocarbon resin polymers with fluorine substituents have better electrical performance.

[0149] Furthermore, according to Table 4, the hydrocarbon resin polymers 1 to 19, 23, 25, and 26 all have a polymer dispersibility index (PDI) of less than 22, a number average molecular weight (Mn) of 2,500 to 15,000 g / mol, and a hydrogen content of reactive bonds greater than 0.2%. The hydrocarbon resin polymers 1 to 19, 25, and 26 all have a hydrogen content of reactive bonds less than 10%. It is clear that in some embodiments, the hydrocarbon resin polymers of the present disclosure may have good thermal properties or processability in addition to having better electrical performance. The resin composition including the hydrocarbon resin polymer of the present disclosure may form a resin layer with good peel strength. The substrate structure including the resin layer may have good electrical performance (dielectric properties). In some embodiments, the substrate structure including the resin layer may also have good thermal performance, processability, and / or reliability.

[0150] While the present invention has been described by way of example and in terms of a preferred embodiment, it is to be understood that the invention is not limited to the disclosed embodiment. On the contrary, it is intended to cover various modifications and similar arrangements (as would be apparent to those skilled in the art). Thus, the scope of the appended claims should be accorded the broadest interpretation so as to encompass all such modifications and similar arrangements.

Claims

1. 1. A hydrocarbon resin polymer comprising: Contains a repeating unit (A) derived from dicyclopentadiene (DCPD), The hydrocarbon resin polymer has a fluorine substituent, and the content of the fluorine substituent is from 100 to 4500 ppm based on the total weight of the hydrocarbon resin polymer.

2. 2. The hydrocarbon resin polymer of claim 1, wherein said hydrocarbon resin polymer has an average of 0.02 to 2 fluorine substituents per molecule.

3. 2. The hydrocarbon resin polymer of claim 1, wherein the number average molecular weight (Mn) of the hydrocarbon resin polymer is in the range of 500 to 15,000 g / mol.

4. 2. The hydrocarbon resin polymer of claim 1, wherein said hydrocarbon resin polymer has a polymer dispersibility index (PDI) of less than 22.

5. 2. The hydrocarbon resin polymer of claim 1, wherein the content of hydrogen atoms in reactive double bonds of said hydrocarbon resin polymer is less than 10%.

6. A repeating unit (B) derived from a monovinyl aromatic compound; A repeating unit (C) derived from a divinyl aromatic compound; The hydrocarbon resin polymer of claim 1 further comprising:

7. 7. The hydrocarbon resin polymer of claim 6, wherein the hydrocarbon resin polymer comprises 0.15 to 15 mol % of the repeating unit (A), 14 to 95 mol % of the repeating unit (B), and 4 to 85 mol % of the repeating unit (C), where the sum of all units in the hydrocarbon resin polymer is 100 mol %.

8. 8. The hydrocarbon resin polymer according to claim 7, wherein the sum of the repeating units (A) and (C) is 13 mol % or more, based on 100 mol % of the total of all units in the hydrocarbon resin polymer.

9. The repeating unit (C) comprises a crosslinkable repeating unit (C1) and a crosslinked repeating unit (C2), 【Chemistry 1】 (wherein R1, R2, R3, and R4 are each independently H or C 1-20 Ar1 and Ar2 are alkyl groups, and Ar1 and Ar2 are phenylene groups. * indicates the position where the crosslinkable repeating unit (C1) and the crosslinked repeating unit (C2) are linked to other groups or units.

7. The hydrocarbon resin polymer according to claim 6, wherein the content of the crosslinkable repeating unit (C1) is from 1 to 30 mol %, with the sum of all units in the hydrocarbon resin polymer being 100 mol %.

10. The hydrocarbon resin polymer 19 7. The hydrocarbon resin polymer of claim 6, wherein the F NMR spectrum has a peak in the range of -125 ppm to -230 ppm.

11. 1. A method for producing a hydrocarbon resin polymer, comprising the steps of: polymerizing the mixture in the presence of a fluorine-containing compound, the fluorine-containing compound being a boron trifluoride complex and the mixture comprising dicyclopentadiene; A method for producing a hydrocarbon resin polymer.

12. The boron trifluoride complex includes boron trifluoride-tetrahydrofuran complex (BF 3 ・THF), boron trifluoride-methanol complex (BF 3 .MeOH), boron trifluoride hydrate (BF 3 ・H 2 O), boron trifluoride-diethyl ether complex (BF 3 ・OEt 2 ), boron trifluoride-anisole complex (BF 3 PhOMe), boron trifluoride-acetic acid complex (BF 3 12. The method of claim 11, wherein the hydrocarbon resin polymer comprises a tertiary amine, ...

13. 12. The method of claim 11, wherein the molar ratio of said fluorine-containing compound: said mixture is from 0.01 to 1:

20.

14. The mixture further comprises a monovinylaromatic compound and / or a divinylaromatic compound. A method for producing the hydrocarbon resin polymer of claim 11.

15. 15. The method of claim 14, wherein said mixture comprises from 3 to 80 mol% dicyclopentadiene, from 0 to 90 mol% said monovinyl aromatic compound, and from 0 to 50 mol% said divinylaromatic compound, where the sum of all components in said mixture is 100 mol%.

16. A substrate structure, comprising: A resin layer; a conductive layer disposed on the resin layer; Including, The resin layer is formed from a resin composition using a crosslinking process, the resin composition includes a hydrocarbon resin polymer, the hydrocarbon resin polymer has a fluorine substituent and includes a repeat unit (A) derived from dicyclopentadiene (DCPD); A substrate structure, wherein the content of said fluorine substituents is from 100 to 4500 ppm based on the total weight of said hydrocarbon resin polymer.

17. 17. The substrate structure of claim 16, wherein said hydrocarbon resin polymer has an average of 0.02 to 2 fluorine substituents per molecule.

18. The hydrocarbon resin polymer A repeating unit (B) derived from a monovinyl aromatic compound; A repeating unit (C) derived from a divinyl aromatic compound; The substrate structure of claim 16 further comprising:

19. 20. The substrate structure of claim 18, wherein the hydrocarbon resin polymer comprises 0.15 to 15 mol % of the repeating unit (A), 14 to 95 mol % of the repeating unit (B), and 4 to 85 mol % of the repeating unit (C), where the sum of all units in the hydrocarbon resin polymer is 100 mol %.

20. 20. The substrate structure according to claim 19, wherein the sum of the repeating units (A) and (C) is 13 mol % or more, with the sum of all units in the hydrocarbon resin polymer being 100 mol %.