Resist composition, method of forming resist pattern, fluorine-containing polymer compound, and compound

Abstract

To provide a resist composition achieving high sensitivity in formation of a resist pattern, having good lithography characteristics such as resolution and roughness, and having good defect characteristics after development, a method for forming a resist pattern using the resist composition, a fluorine-containing polymer compound used for the resist composition, and a compound usable for production of the fluorine-containing polymer compound.SOLUTION: The resist composition contains a resin ingredient (A1) whose solubility in a developing solution changes by the action of an acid and a fluorine-containing polymer compound (f0) having a structural unit (f0) derived from a compound represented by general formula (f0 - 1). In the formula, W1 is a polymerizable group-containing group. Lf00 is an organic group substituted with at least one hydroxy group. Lf02 is an l-valent linking group. Rf01 is a group containing a fluoroalcohol structure. [Chemical Formula 1] SELECTED DRAWING: None

Description

[Technical Field]

[0001] The present invention relates to a resist composition, a method of forming a resist pattern, a fluorine-containing polymeric compound, and a compound. [Background technology]

[0002] In recent years, advances in lithography technology have led to rapid advances in the miniaturization of patterns in the manufacturing of semiconductor devices and liquid crystal display devices. A common method for achieving this miniaturization is to shorten the wavelength (increase the energy) of the exposure light source.

[0003] Resist materials are required to have lithography properties such as sensitivity to these exposure light sources and resolution capable of reproducing patterns with minute dimensions. To satisfy these requirements, a chemically amplified resist composition has been used, which contains a base component whose solubility in a developer changes due to the action of acid, and an acid generator component that generates acid upon exposure.

[0004] Chemically amplified resist compositions generally use resins having specific structural units in order to improve lithography properties, etc. Furthermore, as patterns become increasingly finer, resist materials are required to not only improve various lithography properties but also suppress the occurrence of defects (surface imperfections).

[0005] For example, Patent Document 1 describes a resist composition that uses a resin component having a structural unit derived from hydroxystyrene and a structural unit containing an acid-decomposable group whose polarity increases under the action of acid, in combination with a fluororesin component having a structural unit containing a base-dissociable group. It is described that this resist composition can improve lithography properties and reduce the occurrence of defects. [Prior art documents] [Patent documents]

[0006] [Patent Document 1] Japanese Patent Application Publication No. 2018-022039 Summary of the Invention [Problem to be solved by the invention]

[0007] As resist patterns become finer, for example, in lithography using EUV (extreme ultraviolet) or EB (electron beam), the goal is to form fine patterns of several tens of nanometers. As resist patterns become finer, it has become a challenge to improve lithography properties such as roughness while maintaining good sensitivity. However, these lithography properties are in a trade-off relationship, and improving one property tends to deteriorate the other property. Resist compositions are required to improve both sensitivity and roughness without a trade-off between them. Furthermore, as resist patterns become finer, defects such as foreign matter appearing on the resist pattern after development have become an issue.

[0008] The present invention has been made in view of the above circumstances, and an object of the present invention is to provide a resist composition that enables high sensitivity in resist pattern formation, and that exhibits favorable lithography properties such as resolution and roughness, and also exhibits favorable defect characteristics after development; a method of forming a resist pattern that uses the resist composition; a fluorine-containing polymer compound that is used in the resist composition; and a compound that can be used for producing the fluorine-containing polymer compound. The objective is to provide the following. [Means for solving the problem]

[0009] In order to solve the above problems, the present invention employs the following configuration. That is, a first aspect of the present invention is a resist composition that generates acid upon exposure and whose solubility in a developer changes due to the action of the acid, the resist composition comprising: a resin component (A1) whose solubility in a developer changes due to the action of the acid; and a fluorine-containing polymeric compound (F0) that has a structural unit (f0) derived from a compound represented by the following general formula (f0-1):

[0010] [ka] [In the formula, W 1 is a polymerizable group-containing group. 00 is an organic group having at least one hydroxy group as a substituent. 02 is a (l+1)-valent linking group. 01 is a group represented by the following general formula (f0-r-1) or (f0-r-2), and l is an integer of 1 or greater, as long as the valence allows.

[0011] [ka] [In the formula, Rf 011 Rf is a fluorinated alkyl group having 1 to 12 carbon atoms. 012 represents a hydrogen atom or an organic group having 1 to 12 carbon atoms which may have a fluorine atom. Xf represents a cyclic group having 4 or more fluorine atoms as substituents. * Lf 02 represents a bond with .]

[0012] A second aspect of the present invention is a method of forming a resist pattern, comprising the steps of forming a resist film on a support using the resist composition according to the first aspect, exposing the resist film to light, and developing the exposed resist film to form a resist pattern.

[0013] A third aspect of the present invention is a fluorine-containing polymeric compound having a structural unit (f0) derived from a compound represented by the above general formula (f0-1).

[0014] A fourth aspect of the present invention is a compound represented by the general formula (f0-1). [Effects of the Invention]

[0015] According to the present invention, it is possible to provide a resist composition that enables high sensitivity in resist pattern formation, and that exhibits excellent lithography properties such as resolution and roughness, and also exhibits excellent defect characteristics after development; a method of forming a resist pattern that uses this resist composition; a fluorine-containing polymeric compound that is used in this resist composition; and a compound that can be used for producing the fluorine-containing polymeric compound. DETAILED DESCRIPTION OF THE INVENTION

[0016] In this specification and claims, the term "aliphatic" is defined as a relative concept to aromatic, and refers to groups, compounds, etc. that do not have aromaticity. Unless otherwise specified, the term "alkyl group" includes linear, branched, and cyclic monovalent saturated hydrocarbon groups. The same applies to alkyl groups in alkoxy groups. Unless otherwise specified, the term "alkylene group" includes linear, branched and cyclic divalent saturated hydrocarbon groups. The "halogen atom" includes a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom. The term "structural unit" refers to a monomer unit that constitutes a polymeric compound (resin, polymer, copolymer). The phrase "may have a substituent" includes both the case where a hydrogen atom (-H) is replaced with a monovalent group and the case where a methylene group (-CH2-) is replaced with a divalent group. The term "exposure" is a general concept that includes irradiation with radiation.

[0017] The term "acid-decomposable group" refers to a group having acid decomposability in which at least some of the bonds in the structure of the acid-decomposable group can be cleaved by the action of an acid. Examples of acid-decomposable groups whose polarity increases under the action of an acid include groups that decompose under the action of an acid to generate a polar group. Examples of polar groups include a carboxy group, a hydroxyl group, an amino group, and a sulfo group (-SO3H). More specific examples of the acid-decomposable group include groups in which the polar group is protected with an acid-dissociable group (for example, a group in which the hydrogen atom of an OH-containing polar group is protected with an acid-dissociable group).

[0018] The term "acid-dissociable group" refers to either (i) a group having acid dissociability such that the bond between the acid-dissociable group and an atom adjacent to the acid-dissociable group can be cleaved by the action of an acid, or (ii) a group in which a portion of the bond is cleaved by the action of an acid, and then a decarboxylation reaction occurs, thereby cleaving the bond between the acid-dissociable group and an atom adjacent to the acid-dissociable group. The acid-dissociable group constituting the acid-decomposable group must be a group with lower polarity than the polar group generated by dissociation of the acid-dissociable group. Therefore, when the acid-dissociable group dissociates due to the action of an acid, a polar group with higher polarity than the acid-dissociable group is generated, increasing the polarity. As a result, the polarity of the entire component (A1) increases. The increase in polarity relatively changes the solubility in the developer, increasing the solubility when the developer is an alkaline developer and decreasing the solubility when the developer is an organic developer.

[0019] A "base component" is an organic compound that has film-forming ability. Organic compounds used as base components are broadly divided into non-polymers and polymers. Non-polymers typically have a molecular weight of 500 or more and less than 4000. Hereinafter, the term "low molecular weight compound" refers to a non-polymer with a molecular weight of 500 or more and less than 4000. Polymers typically have a molecular weight of 1000 or more. Hereinafter, the terms "resin," "high molecular weight compound," or "polymer" refer to a polymer with a molecular weight of 1000 or more. The molecular weight of a polymer is determined by the weight average molecular weight converted into polystyrene by GPC (gel permeation chromatography).

[0020] The term "derived structural unit" refers to a structural unit formed by cleavage of a multiple bond between carbon atoms, such as an ethylenic double bond. In the "acrylate ester," the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent. αx ) is an atom or group other than a hydrogen atom. αx ) is substituted with a substituent containing an ester bond, or αx This also includes α-hydroxyacrylic esters in which the hydroxyl group is substituted with a hydroxyalkyl group or a group that modifies the hydroxyl group. Unless otherwise specified, the α-carbon atom of an acrylic ester refers to the carbon atom to which the carbonyl group of acrylic acid is bonded. Hereinafter, an acrylic ester in which the hydrogen atom bonded to the carbon atom at the α-position is substituted with a substituent may be referred to as an α-substituted acrylic ester.

[0021] The term "derivative" encompasses compounds in which the hydrogen atom at the α-position of the target compound is substituted with another substituent, such as an alkyl group or a halogenated alkyl group, as well as derivatives thereof. Examples of such derivatives include compounds in which the hydrogen atom of a hydroxyl group of a target compound, which may have the hydrogen atom at the α-position substituted with a substituent, is substituted with an organic group; and compounds in which a substituent other than a hydroxyl group is bonded to a target compound, which may have the hydrogen atom at the α-position substituted with a substituent. Unless otherwise specified, the α-position refers to the first carbon atom adjacent to the functional group. The substituents that replace the hydrogen atom at the α-position of hydroxystyrene include R αx The same can be mentioned.

[0022] In this specification and claims, some structures represented by chemical formulas may have asymmetric carbon atoms, and may exist as enantiomers or diastereomers. In such cases, a single chemical formula represents all isomers. These isomers may be used alone or as a mixture.

[0023] (Resist composition) The resist composition of this embodiment generates an acid upon exposure, and the solubility in a developer changes due to the action of the acid. This resist composition contains a base component (A) (hereinafter also referred to as "component (A)") whose solubility in a developer changes under the action of an acid, and a fluorine-containing polymeric compound (F0) (hereinafter also referred to as "component (F0)") having a structural unit (f0) derived from a compound represented by (f0-1) described below.

[0024] Furthermore, the resist composition of this embodiment may further contain other components in addition to the above-mentioned components (A) and (F0). Examples of other components include the following components (B), (D), (E), (F1), and (S).

[0025] In the resist composition of this embodiment, the component (A) may generate an acid upon exposure, or an additive component that is formulated separately from the component (A) may generate an acid upon exposure. Specifically, the resist composition of this embodiment may further contain: (1) an acid generator component (B) (hereinafter referred to as “component (B)”) that generates acid upon exposure; (2) the component (A) may be a component that generates acid upon exposure; or (3) the component (A) may be a component that generates acid upon exposure and may further contain component (B). That is, in the cases of (2) and (3) above, the component (A) is a "base component that generates acid upon exposure and whose solubility in a developer changes due to the action of the acid." When the component (A) is a base component that generates acid upon exposure and whose solubility in a developer changes due to the action of the acid, the component (A1) described below is preferably a resin that generates acid upon exposure and whose solubility in a developer changes due to the action of the acid. Such a resin can be a polymeric compound having a structural unit that generates acid upon exposure. The structural unit that generates acid upon exposure may be the structural unit (a5) described below.

[0026] When a resist film is formed using the resist composition of this embodiment and then subjected to selective exposure, an acid is generated from the component (B) in the exposed areas of the resist film, for example, and the action of the acid changes the solubility of the component (A) in a developer, whereas the solubility of the component (A) in the developer does not change in the unexposed areas of the resist film, resulting in a difference in solubility in a developer between the exposed and unexposed areas. Therefore, when the resist film is developed, if the resist composition is positive, the exposed areas of the resist film are dissolved and removed, forming a positive resist pattern, whereas if the resist composition is negative, the unexposed areas of the resist film are dissolved and removed, forming a negative resist pattern.

[0027] The resist composition of this embodiment may be a positive resist composition or a negative resist composition. Furthermore, the resist composition of this embodiment may be for an alkaline development process in which an alkaline developer is used in the development treatment during resist pattern formation, or may be for a solvent development process in which a developer containing an organic solvent (organic developer) is used in the development treatment.

[0028] <Base material component (A)> In the resist composition of this embodiment, the component (A) contains a resin component (A1) (hereinafter also referred to as "component (A1)") whose solubility in a developer changes under the action of acid. By using the component (A1), the polarity of the base component changes before and after exposure, making it possible to obtain good development contrast not only in alkaline development processes but also in solvent development processes. As the component (A), other polymeric compounds and / or low molecular weight compounds may be used in combination with the component (A1).

[0029] In the resist composition of this embodiment, the component (A) may use either a single type of compound, or a combination of two or more types of compounds.

[0030] About component (A1) The component (A1) is a resin component whose solubility in a developer changes under the action of an acid. The component (A1) preferably has a structural unit (a1) that includes an acid-decomposable group whose polarity increases upon the action of an acid. The component (A1) may contain other structural units in addition to the structural unit (a1), as necessary.

[0031] <Constituent unit (a1)> The structural unit (a1) is a structural unit that contains an acid-decomposable group whose polarity increases upon the action of an acid.

[0032] Examples of the acid-dissociable group include those that have been proposed as acid-dissociable groups for base resins used in chemically amplified resist compositions. Specific examples of acid-dissociable groups that have been proposed for use in base resins for chemically amplified resist compositions include the "acetal-type acid-dissociable groups," "tertiary alkyl ester-type acid-dissociable groups," "tertiary alkyloxycarbonyl acid-dissociable groups," and "secondary alkyloxycarbonyl acid-dissociable groups," which are explained below.

[0033] Acetal type acid dissociable group: Among the polar groups, examples of the acid-dissociable group that protects a carboxy group or a hydroxyl group include acid-dissociable groups represented by the following general formula (a1-r-1) (hereinafter sometimes referred to as "acetal-type acid-dissociable groups").

[0034] [ka] [In the formula, Ra' 1 , Ra' 2 is a hydrogen atom or an alkyl group. 3 is a hydrocarbon group, and Ra' 3 Ra' 1 , Ra' 2 may be bonded to any one of the following to form a ring.]

[0035] In formula (a1-r-1), Ra' 1 and Ra' 2 At least one of these is preferably a hydrogen atom, and both are more preferably hydrogen atoms. Ra' 1 or Ra' 2 When is an alkyl group, examples of the alkyl group include the same alkyl groups as those exemplified as the substituent that may be bonded to the carbon atom at the α-position in the description of the α-substituted acrylic acid ester above, and an alkyl group having 1 to 5 carbon atoms is preferred. Specific examples include linear or branched alkyl groups. More specific examples include methyl, ethyl, propyl, isopropyl, n-butyl, isobutyl, tert-butyl, pentyl, isopentyl, and neopentyl groups, with methyl and ethyl groups being more preferred, and methyl being particularly preferred.

[0036] In formula (a1-r-1), Ra' 3 Examples of the hydrocarbon group include a linear or branched alkyl group, and a cyclic hydrocarbon group. The linear alkyl group preferably has 1 to 5 carbon atoms, more preferably 1 to 4 carbon atoms, and even more preferably 1 or 2 carbon atoms. Specific examples include a methyl group, an ethyl group, an n-propyl group, an n-butyl group, and an n-pentyl group. Of these, a methyl group, an ethyl group, or an n-butyl group is preferred, and a methyl group or an ethyl group is more preferred.

[0037] The branched alkyl group preferably has 3 to 10 carbon atoms, and more preferably 3 to 5 carbon atoms. Specific examples include an isopropyl group, an isobutyl group, a tert-butyl group, an isopentyl group, a neopentyl group, a 1,1-diethylpropyl group, and a 2,2-dimethylbutyl group, with an isopropyl group being preferred.

[0038] Ra' 3 When is a cyclic hydrocarbon group, the hydrocarbon group may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group, and may be a polycyclic group or a monocyclic group. The monocyclic aliphatic hydrocarbon group is preferably a group in which one hydrogen atom has been removed from a monocycloalkane. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples include cyclopentane and cyclohexane. The aliphatic hydrocarbon group that is a polycyclic group is preferably a group in which one hydrogen atom has been removed from a polycycloalkane, and the polycycloalkane is preferably one having 7 to 12 carbon atoms, specifically adamantane, norbornane, isobornane, tricyclo[5.2.1.0] 2,6 ]decane, tetracyclododecane, and the like.

[0039] Ra' 3 When the cyclic hydrocarbon group is an aromatic hydrocarbon group, the aromatic hydrocarbon group is a hydrocarbon group having at least one aromatic ring. The aromatic ring is not particularly limited as long as it is a cyclic conjugated system having 4n+2 π electrons, and may be monocyclic or polycyclic. The aromatic ring preferably has 5 to 30 carbon atoms, more preferably 5 to 20 carbon atoms, further preferably 6 to 15 carbon atoms, and particularly preferably 6 to 12 carbon atoms. Specific examples of the aromatic ring include aromatic hydrocarbon rings such as benzene, naphthalene, anthracene, and phenanthrene; and aromatic heterocycles in which some of the carbon atoms constituting the aromatic hydrocarbon ring are substituted with heteroatoms. Examples of heteroatoms in the aromatic heterocycle include oxygen atoms, sulfur atoms, and nitrogen atoms. Specific examples of the aromatic heterocycle include pyridine rings and thiophene rings. Ra' 3Specific examples of the aromatic hydrocarbon group in the formula (I) include a group (aryl group or heteroaryl group) in which one hydrogen atom has been removed from the aromatic hydrocarbon ring or aromatic heterocycle; a group in which one hydrogen atom has been removed from an aromatic compound containing two or more aromatic rings (e.g., biphenyl, fluorene, etc.); and a group in which one hydrogen atom of the aromatic hydrocarbon ring or aromatic heterocycle has been substituted with an alkylene group (e.g., arylalkyl groups such as benzyl group, phenethyl group, 1-naphthylmethyl group, 2-naphthylmethyl group, 1-naphthylethyl group, and 2-naphthylethyl group). The alkylene group bonded to the aromatic hydrocarbon ring or aromatic heterocycle preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.

[0040] Ra' 3 The cyclic hydrocarbon group in may have a substituent. Examples of the substituent include -R P1 , -R P2 -OR P1 , -R P2 -CO-R P1 , -R P2 -CO-OR P1 , -R P2 -O-CO-R P1 , -R P2 -OH, -R P2 -CN or -R P2 -COOH (hereinafter these substituents are collectively referred to as "Ra x5 ") are also examples. where R P1 is a monovalent chain saturated hydrocarbon group having 1 to 10 carbon atoms, a monovalent alicyclic saturated hydrocarbon group having 3 to 20 carbon atoms, or a monovalent aromatic hydrocarbon group having 6 to 30 carbon atoms. P2 is a single bond, a divalent chain saturated hydrocarbon group having 1 to 10 carbon atoms, a divalent alicyclic saturated hydrocarbon group having 3 to 20 carbon atoms, or a divalent aromatic hydrocarbon group having 6 to 30 carbon atoms. P1 and R P2Some or all of the hydrogen atoms in the chain saturated hydrocarbon group, the alicyclic saturated hydrocarbon group, and the aromatic hydrocarbon group may be substituted with fluorine atoms. The alicyclic hydrocarbon group may have one or more of the above-mentioned substituents, or may have one or more of each of multiple types of the above-mentioned substituents. Examples of the monovalent chain saturated hydrocarbon group having 1 to 10 carbon atoms include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, and a decyl group. Examples of the monovalent aliphatic cyclic saturated hydrocarbon group having 3 to 20 carbon atoms include monocyclic aliphatic saturated hydrocarbon groups such as a cyclopropyl group, cyclobutyl group, cyclopentyl group, cyclohexyl group, cycloheptyl group, cyclooctyl group, cyclodecyl group, and cyclododecyl group; and polycyclic aliphatic saturated hydrocarbon groups such as a bicyclo[2.2.2]octanyl group, tricyclo[5.2.1.02,6]decanyl group, tricyclo[3.3.1.13,7]decanyl group, tetracyclo[6.2.1.13,6.02,7]dodecanyl group, and adamantyl group. Examples of the monovalent aromatic hydrocarbon group having 6 to 30 carbon atoms include groups in which one hydrogen atom has been removed from an aromatic hydrocarbon ring such as benzene, biphenyl, fluorene, naphthalene, anthracene, or phenanthrene.

[0041] Ra' 3 But Ra' 1 , Ra' 2 When the cyclic group is bonded to any of the above to form a ring, the cyclic group is preferably a 4- to 7-membered ring, and more preferably a 4- to 6-membered ring. Specific examples of the cyclic group include a tetrahydropyranyl group and a tetrahydrofuranyl group.

[0042] Tertiary alkyl ester-type acid-labile group: Among the polar groups, examples of the acid-dissociable group that protects the carboxy group include acid-dissociable groups represented by the following general formula (a1-r-2). Among the acid-dissociable groups represented by the following formula (a1-r-2), those constituted by an alkyl group may be referred to as "tertiary alkyl ester-type acid-dissociable groups" hereinafter for convenience.

[0043] [ka] [In the formula, Ra' 4 ~Ra' 6 are each a hydrocarbon group, and Ra' 5 , Ra' 6 may be bonded to each other to form a ring.

[0044] Ra' 4 Examples of the hydrocarbon group include a linear or branched alkyl group, a linear or cyclic alkenyl group, and a cyclic hydrocarbon group. Ra' 4 The linear or branched alkyl group and the cyclic hydrocarbon group (the monocyclic aliphatic hydrocarbon group, the polycyclic aliphatic hydrocarbon group, and the aromatic hydrocarbon group) in 3 The same can be mentioned. Ra' 4 The chain or cyclic alkenyl group in the formula (I) is preferably an alkenyl group having 2 to 10 carbon atoms. Ra' 5 , Ra' 6 The hydrocarbon group of Ra' 3 The same can be mentioned.

[0045] Ra' 5 and Ra' 6 and (a1-r2-3) are preferably substituted or unsubstituted by the alkyl group. On the other hand, Ra' 4 ~Ra' 6 When are not bonded to each other and are independent hydrocarbon groups, preferred examples include groups represented by the following general formula (a1-r2-4).

[0046] [ka] [In formula (a1-r2-1), Ra' 10 Ra' represents a linear or branched alkyl group having 1 to 12 carbon atoms, some of which may be substituted with a halogen atom or a heteroatom-containing group. 11 Ra' 10 represents a group that forms an aliphatic cyclic group together with the carbon atom to which Ya is bonded. In formula (a1-r2-2), Ya is a carbon atom. Xa is a group that forms a cyclic hydrocarbon group together with Ya. Some or all of the hydrogen atoms in this cyclic hydrocarbon group may be substituted. Ra 101 ~Ra 103 are each independently a hydrogen atom, a monovalent linear saturated hydrocarbon group having 1 to 10 carbon atoms, or a monovalent cyclic aliphatic saturated hydrocarbon group having 3 to 20 carbon atoms. Some or all of the hydrogen atoms in the linear saturated hydrocarbon group and the cyclic aliphatic saturated hydrocarbon group may be substituted. 101 ~Ra 103 Two or more of these may be bonded to each other to form a cyclic structure. In formula (a1-r2-3), Yaa is a carbon atom. Xaa is a group which forms an aliphatic cyclic group together with Yaa. Ra 104 In formula (a1-r2-4), Ra' is an aromatic hydrocarbon group which may have a substituent. 12 and Ra' 13 are each independently a monovalent chain saturated hydrocarbon group having 1 to 10 carbon atoms. Some or all of the hydrogen atoms in this chain saturated hydrocarbon group may be substituted. 14 is a hydrocarbon group which may have a substituent. * indicates a bond (the same applies hereinafter).

[0047] In the above formula (a1-r2-1), Ra' 10 is a linear or branched alkyl group having 1 to 12 carbon atoms, some of which may be substituted with a halogen atom or a heteroatom-containing group.

[0048] Ra' 10The linear alkyl group in the formula (I) has 1 to 12 carbon atoms, preferably 1 to 10 carbon atoms, and particularly preferably 1 to 5 carbon atoms. Ra' 10 In the formula (I), the branched alkyl group is the above-mentioned Ra' 3 The same can be mentioned.

[0049] Ra' 10 The alkyl group in may be partially substituted with a halogen atom or a heteroatom-containing group. For example, some of the hydrogen atoms constituting the alkyl group may be substituted with a halogen atom or a heteroatom-containing group. Furthermore, some of the carbon atoms (e.g., methylene groups) constituting the alkyl group may be substituted with a heteroatom-containing group. Examples of heteroatoms include oxygen, sulfur, and nitrogen atoms. Examples of heteroatom-containing groups include (-O-), -C(=O)-O-, -OC(=O)-, -C(=O)-, -OC(=O)-O-, -C(=O)-NH-, -NH-, -S-, -S(=O)2-, and -S(=O)2-O-.

[0050] In formula (a1-r2-1), Ra' 11 (Ra' 10 The aliphatic cyclic group formed together with the carbon atom to which the carbon atom is bonded is represented by Ra' in formula (a1-r-1). 3 Among these, monocyclic alicyclic hydrocarbon groups are preferred, and specifically, cyclopentyl and cyclohexyl groups are more preferred.

[0051] In the formula (a1-r2-2), the cyclic hydrocarbon group formed by Xa together with Ya includes Ra' in the formula (a1-r-1). 3 Examples of such groups include groups in which one or more hydrogen atoms have been further removed from the cyclic monovalent hydrocarbon group (aliphatic hydrocarbon group) shown above. The cyclic hydrocarbon group formed by Xa together with Ya may have a substituent. The substituent may be any of the above-mentioned Ra' 3Examples of the substituents include the same as those that the cyclic hydrocarbon group in the above may have. In formula (a1-r2-2), Ra 101 ~Ra 103 In the formula (I), examples of the monovalent chain saturated hydrocarbon group having 1 to 10 carbon atoms include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, and a decyl group. Ra 101 ~Ra 103 In the formula (I), examples of the monovalent aliphatic cyclic saturated hydrocarbon group having 3 to 20 carbon atoms include monocyclic aliphatic saturated hydrocarbon groups such as a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, a cycloheptyl group, a cyclooctyl group, a cyclodecyl group, and a cyclododecyl group; 2,6 ]decanyl group, tricyclo[3.3.1.1 3,7 ]decanyl group, tetracyclo[6.2.1.1 3,6 .0 2,7 ] Examples thereof include polycyclic aliphatic saturated hydrocarbon groups such as a dodecanyl group and an adamantyl group. Ra 101 ~Ra 103 Among these, from the viewpoint of ease of synthesis, a hydrogen atom or a monovalent chain saturated hydrocarbon group having 1 to 10 carbon atoms is preferred, and among these, a hydrogen atom, a methyl group, or an ethyl group is more preferred, with a hydrogen atom being particularly preferred.

[0052] The above Ra 101 ~Ra 103 Examples of the substituents that the chain saturated hydrocarbon group or the aliphatic cyclic saturated hydrocarbon group represented by the formula: x5 The same groups as those shown below can be mentioned.

[0053] Ra 101 ~Ra 103Examples of the group containing a carbon-carbon double bond formed by two or more of the above being bonded to each other to form a cyclic structure include a cyclopentenyl group, a cyclohexenyl group, a methylcyclopentenyl group, a methylcyclohexenyl group, a cyclopentylidene-ethenyl group, a cyclohexylidene-ethenyl group, etc. Among these, from the viewpoint of ease of synthesis, a cyclopentenyl group, a cyclohexenyl group, and a cyclopentylidene-ethenyl group are preferred.

[0054] In formula (a1-r2-3), the aliphatic cyclic group formed by Xaa together with Yaa is Ra' in formula (a1-r-1). 3 The groups mentioned above as the aliphatic hydrocarbon group are preferably monocyclic or polycyclic groups. In formula (a1-r2-3), Ra 104 Examples of the aromatic hydrocarbon group in the formula include a group in which one or more hydrogen atoms have been removed from an aromatic hydrocarbon ring having 5 to 30 carbon atoms. 104 is preferably a group in which one or more hydrogen atoms have been removed from an aromatic hydrocarbon ring having 6 to 15 carbon atoms, more preferably a group in which one or more hydrogen atoms have been removed from benzene, naphthalene, anthracene or phenanthrene, still more preferably a group in which one or more hydrogen atoms have been removed from benzene, naphthalene or anthracene, particularly preferably a group in which one or more hydrogen atoms have been removed from benzene or naphthalene, and most preferably a group in which one or more hydrogen atoms have been removed from benzene.

[0055] Ra in formula (a1-r2-3) 104 Examples of the substituent that may be possessed by include a methyl group, an ethyl group, a propyl group, a hydroxy group, a carboxy group, a halogen atom, an alkoxy group (such as a methoxy group, an ethoxy group, a propoxy group, or a butoxy group), and an alkyloxycarbonyl group.

[0056] In formula (a1-r2-4), Ra' 12 and Ra' 13 are each independently a monovalent chain saturated hydrocarbon group having 1 to 10 carbon atoms. 12 and Ra' 13In the formula, the monovalent chain saturated hydrocarbon group having 1 to 10 carbon atoms includes the above-mentioned Ra 101 ~Ra 103 Examples include the same monovalent chain saturated hydrocarbon group having 1 to 10 carbon atoms as in the above. Some or all of the hydrogen atoms in this chain saturated hydrocarbon group may be substituted. Ra' 12 and Ra' 13 Among these, alkyl groups having 1 to 5 carbon atoms are preferred, alkyl groups having 1 to 5 carbon atoms are more preferred, methyl groups and ethyl groups are even more preferred, and methyl groups are particularly preferred. The above Ra' 12 and Ra' 13 When the chain saturated hydrocarbon group represented by the formula: is substituted, examples of the substituent include the above-mentioned Ra x5 The same groups as those shown below can be mentioned.

[0057] In formula (a1-r2-4), Ra' 14 Ra' is a hydrocarbon group which may have a substituent. 14 The hydrocarbon group in the formula (I) includes a linear or branched alkyl group, or a cyclic hydrocarbon group.

[0058] Ra' 14 The linear alkyl group in the formula (I) preferably has 1 to 5 carbon atoms, more preferably 1 to 4 carbon atoms, and even more preferably 1 or 2 carbon atoms. Specific examples include a methyl group, an ethyl group, an n-propyl group, an n-butyl group, an n-pentyl group, etc. Among these, a methyl group, an ethyl group, or an n-butyl group is preferred, and a methyl group or an ethyl group is more preferred.

[0059] Ra' 14 The branched alkyl group in the formula (I) preferably has 3 to 10 carbon atoms, more preferably 3 to 5. Specific examples include an isopropyl group, an isobutyl group, a tert-butyl group, an isopentyl group, a neopentyl group, a 1,1-diethylpropyl group, and a 2,2-dimethylbutyl group, with an isopropyl group being preferred.

[0060] Ra'14 When is a cyclic hydrocarbon group, the hydrocarbon group may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group, and may be a polycyclic group or a monocyclic group. The monocyclic aliphatic hydrocarbon group is preferably a group in which one hydrogen atom has been removed from a monocycloalkane. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples include cyclopentane and cyclohexane. The aliphatic hydrocarbon group that is a polycyclic group is preferably a group in which one hydrogen atom has been removed from a polycycloalkane, and the polycycloalkane is preferably one having 7 to 12 carbon atoms, specifically adamantane, norbornane, isobornane, tricyclo[5.2.1.0] 2,6 ]decane, tetracyclododecane, and the like.

[0061] Ra' 14 As the aromatic hydrocarbon group in 104 Among them, the aromatic hydrocarbon groups Ra' are the same as those in 14 is preferably a group in which one or more hydrogen atoms have been removed from an aromatic hydrocarbon ring having 6 to 15 carbon atoms, more preferably a group in which one or more hydrogen atoms have been removed from benzene, naphthalene, anthracene, or phenanthrene, still more preferably a group in which one or more hydrogen atoms have been removed from benzene, naphthalene, or anthracene, particularly preferably a group in which one or more hydrogen atoms have been removed from naphthalene or anthracene, and most preferably a group in which one or more hydrogen atoms have been removed from naphthalene. Ra' 14 Examples of the substituent that may be possessed by Ra include 104 Examples of the substituents include the same as those that may be possessed by the group.

[0062] Ra' in formula (a1-r2-4) 14 When is a naphthyl group, the position at which it is bonded to the tertiary carbon atom in the formula (a1-r2-4) may be either the 1st or 2nd position of the naphthyl group. Ra' in formula (a1-r2-4) 14When is an anthryl group, the position at which it is bonded to the tertiary carbon atom in the formula (a1-r2-4) may be any one of the 1st, 2nd, or 9th position of the anthryl group.

[0063] Specific examples of the group represented by the formula (a1-r2-1) are listed below.

[0064] [ka]

[0065] [ka]

[0066] [ka]

[0067] Specific examples of the group represented by the formula (a1-r2-2) are listed below.

[0068] [ka]

[0069] [ka]

[0070] [ka]

[0071] Specific examples of the group represented by the formula (a1-r2-3) are listed below.

[0072] [ka]

[0073] Specific examples of the group represented by the formula (a1-r2-4) are listed below.

[0074] [ka]

[0075] Tertiary alkyloxycarbonyl acid dissociating group: Among the polar groups, examples of the acid-dissociable group that protects the hydroxyl group include acid-dissociable groups represented by the following general formula (a1-r-3) (hereinafter, for convenience, may be referred to as "tertiary alkyloxycarbonyl acid-dissociable group").

[0076] [ka] [In the formula, Ra' 7 ~Ra' 9 are each alkyl groups.

[0077] In formula (a1-r-3), Ra' 7 ~Ra' 9 are each preferably an alkyl group having 1 to 5 carbon atoms, more preferably an alkyl group having 1 to 3 carbon atoms. The total number of carbon atoms in each alkyl group is preferably 3 to 7, more preferably 3 to 5, and most preferably 3 to 4.

[0078] Secondary alkyl ester-type acid-labile group: Among the polar groups, examples of the acid-dissociable group that protects the carboxy group include acid-dissociable groups represented by the following general formula (a1-r-4).

[0079] [ka] [In the formula, Ra' 10 is a hydrocarbon group. 11a and Ra' 11b are each independently a hydrogen atom, a halogen atom or an alkyl group. 12is a hydrogen atom or a hydrocarbon group. 10 and Ra' 11a or Ra' 11b and may be bonded to each other to form a ring. 11a or Ra' 11b and Ra' 12 may be bonded to each other to form a ring.

[0080] In the formula, Ra' 10 and Ra' 12 The hydrocarbon group in Ra' 3 The same can be mentioned. In the formula, Ra' 11a and Ra' 11b The alkyl group in Ra' is 1 The alkyl groups in the above formula (I) are the same as those in the above formula (I). In the formula, Ra' 10 and Ra' 12 The hydrocarbon group in 11a and Ra' 11b The alkyl group in may have a substituent. Examples of the substituent include the above-mentioned Ra x5 etc.

[0081] Ra' 10 and Ra' 11a or Ra' 11b may be bonded to each other to form a ring, which may be a polycyclic ring, a monocyclic ring, an alicyclic ring, or an aromatic ring. The alicyclic and aromatic rings may contain heteroatoms.

[0082] Ra' 10 and Ra' 11a or Ra' 11b Among the above, the ring formed by bonding together is preferably a monocycloalkene, a ring in which some of the carbon atoms of a monocycloalkene are substituted with heteroatoms (oxygen atoms, sulfur atoms, etc.), or a monocycloalkadiene, more preferably a cycloalkene having 3 to 6 carbon atoms, and more preferably cyclopentene or cyclohexene.

[0083] Ra' 10 and Ra' 11a or Ra' 11b The ring formed by bonding these may be a fused ring. Specific examples of such a fused ring include indan.

[0084] Ra' 10 and Ra' 11a or Ra' 11b The ring formed by bonding together may have a substituent. Examples of the substituent include the above-mentioned Ra x5 etc.

[0085] Ra' 11a or Ra' 11b and Ra' 12 and may be bonded to each other to form a ring, and the ring may include Ra' 10 and Ra' 11a or Ra' 11b and the ring formed by bonding with each other are exemplified.

[0086] Specific examples of the group represented by the formula (a1-r-4) are listed below.

[0087] [ka]

[0088] Examples of the structural unit (a1) include a structural unit derived from an acrylate ester in which the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent; a structural unit derived from acrylamide; a structural unit derived from hydroxystyrene or a hydroxystyrene derivative in which at least some of the hydrogen atoms in the hydroxyl groups are protected with a substituent containing the above-mentioned acid-decomposable group; and a structural unit derived from vinylbenzoic acid or a vinylbenzoic acid derivative in which at least some of the hydrogen atoms in -C(═O)-OH are protected with a substituent containing the above-mentioned acid-decomposable group.

[0089] Of the above, preferred structural units (a1) are structural units derived from acrylate esters in which the hydrogen atom bonded to the α-position carbon atom may be substituted with a substituent. Preferred specific examples of the structural unit (a1) include structural units represented by the following general formula (a1-1), (a1-2), or (a1-3).

[0090] [ka] [wherein R is a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms. 1 is a divalent hydrocarbon group which may have an ether bond. a1 is an integer between 0 and 2. 1 is an acid-dissociable group represented by the above general formula (a1-r-1), (a1-r-2) or (a1-r-4). 1 is n a2 + is a monovalent hydrocarbon group. n a2 is an integer between 1 and 3. 2 represents an acid-dissociable group represented by the above general formula (a1-r-1) or (a1-r-3). 001 represents a single bond or a divalent linking group. 01 is a single bond or a divalent linking group. 01 Rz is an acid-dissociable group represented by the above general formula (a1-r-1), (a1-r-2) or (a1-r-4). 01 is an alkyl group, a halogen atom, a halogenated alkyl group, a hydroxy group, or an alkoxy group. q is an integer of 0 to 3. n is an integer of 0 or more, provided that n≦q×2+4.

[0091] In the formulas (a1-1) to (a1-3), the alkyl group of 1 to 5 carbon atoms represented by R is preferably a linear or branched alkyl group of 1 to 5 carbon atoms, and specific examples thereof include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group, and a neopentyl group. The halogenated alkyl group of 1 to 5 carbon atoms is a group in which some or all of the hydrogen atoms of the alkyl group of 1 to 5 carbon atoms have been substituted with halogen atoms. As the halogen atom, a fluorine atom is particularly preferred. R is preferably a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a fluorinated alkyl group having 1 to 5 carbon atoms, and is most preferably a hydrogen atom or a methyl group from the viewpoint of industrial availability.

[0092] In the formula (a1-1), Va 1 The divalent hydrocarbon group in may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group.

[0093] Va 1 The aliphatic hydrocarbon group as the divalent hydrocarbon group in may be saturated or unsaturated, and is usually preferably saturated. More specifically, the aliphatic hydrocarbon group may be a straight-chain or branched-chain aliphatic hydrocarbon group, or an aliphatic hydrocarbon group containing a ring in its structure.

[0094] The linear aliphatic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 6 carbon atoms, even more preferably 1 to 4 carbon atoms, and most preferably 1 to 3 carbon atoms. As the straight-chain aliphatic hydrocarbon group, a straight-chain alkylene group is preferred, and specific examples include a methylene group [-CH2-], an ethylene group [-(CH2)2-], a trimethylene group [-(CH2)3-], a tetramethylene group [-(CH2)4-], and a pentamethylene group [-(CH2)5-]. The branched aliphatic hydrocarbon group preferably has 2 to 10 carbon atoms, more preferably 3 to 6 carbon atoms, even more preferably 3 or 4 carbon atoms, and most preferably 3 carbon atoms. The branched aliphatic hydrocarbon group is preferably a branched alkylene group, and specific examples thereof include alkyl alkylene groups such as alkylmethylene groups such as -CH(CH3)-, -CH(CH2CH3)-, -C(CH3)2-, -C(CH3)(CH2CH3)-, -C(CH3)(CH2CH2CH3)-, and -C(CH2CH3)2-; alkylethylene groups such as -CH(CH3)CH2-, -CH(CH3)CH(CH3)-, -C(CH3)2CH2-, -CH(CH2CH3)CH2-, and -C(CH2CH3)2-CH2-; alkyl trimethylene groups such as -CH(CH3)CH2CH2- and -CH2CH(CH3)CH2-; and alkyl tetramethylene groups such as -CH(CH3)CH2CH2CH2- and -CH2CH(CH3)CH2CH2-. The alkyl group in the alkylalkylene group is preferably a linear alkyl group having 1 to 5 carbon atoms.

[0095] Examples of the aliphatic hydrocarbon group containing a ring in its structure include an alicyclic hydrocarbon group (a group in which two hydrogen atoms have been removed from an aliphatic hydrocarbon ring), a group in which an alicyclic hydrocarbon group is bonded to the end of a straight-chain or branched-chain aliphatic hydrocarbon group, and a group in which an alicyclic hydrocarbon group is interposed in the middle of a straight-chain or branched-chain aliphatic hydrocarbon group. Examples of the straight-chain or branched-chain aliphatic hydrocarbon group include the same as the straight-chain aliphatic hydrocarbon group or the branched-chain aliphatic hydrocarbon group. The alicyclic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably has 3 to 12 carbon atoms. The alicyclic hydrocarbon group may be polycyclic or monocyclic. The monocyclic alicyclic hydrocarbon group is preferably a group in which two hydrogen atoms have been removed from a monocycloalkane. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane. The polycyclic alicyclic hydrocarbon group is preferably a group in which two hydrogen atoms have been removed from a polycycloalkane, and specific examples thereof include adamantane, norbornane, isobornane, and tricyclo[5.2.1.0]. 2,6 ]decane, tetracyclododecane, and the like.

[0096] Va 1 The aromatic hydrocarbon group as the divalent hydrocarbon group in the formula (I) is a hydrocarbon group having an aromatic ring. Such aromatic hydrocarbon groups preferably have 3 to 30 carbon atoms, more preferably 5 to 30, even more preferably 5 to 20, particularly preferably 6 to 15, and most preferably 6 to 12. However, this number of carbon atoms does not include the number of carbon atoms in the substituents. Specific examples of the aromatic ring contained in the aromatic hydrocarbon group include aromatic hydrocarbon rings such as benzene, biphenyl, fluorene, naphthalene, anthracene, and phenanthrene; and aromatic heterocycles in which some of the carbon atoms constituting the aromatic hydrocarbon ring are substituted with heteroatoms. Examples of the heteroatom in the aromatic heterocycle include an oxygen atom, a sulfur atom, and a nitrogen atom. Specific examples of the aromatic hydrocarbon group include a group in which two hydrogen atoms have been removed from the aromatic hydrocarbon ring (an arylene group); a group in which one hydrogen atom of a group in which one hydrogen atom has been removed from the aromatic hydrocarbon ring (an aryl group) has been substituted with an alkylene group (for example, a group in which one hydrogen atom has been further removed from the aryl group in an arylalkyl group, such as a benzyl group, a phenethyl group, a 1-naphthylmethyl group, a 2-naphthylmethyl group, a 1-naphthylethyl group, or a 2-naphthylethyl group). The number of carbon atoms in the alkylene group (the alkyl chain in the arylalkyl group) is preferably 1 to 4, more preferably 1 to 2, and particularly preferably 1.

[0097] In the formula (a1-1), Ra 1 is preferably an acid-dissociable group represented by the above general formula (a1-r-2) or (a1-r-4), and among these, a group represented by the general formula (a1-r2-1) or an acid-dissociable group represented by the general formula (a1-r-4) is more preferred.

[0098] In the formula (a1-2), Wa 1 n in a2 The monovalent hydrocarbon group may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group. The aliphatic hydrocarbon group refers to a hydrocarbon group that does not have aromaticity and may be saturated or unsaturated, but is usually preferably saturated. Examples of the aliphatic hydrocarbon group include linear or branched aliphatic hydrocarbon groups, aliphatic hydrocarbon groups containing a ring in their structure, and groups that combine linear or branched aliphatic hydrocarbon groups with aliphatic hydrocarbon groups containing a ring in their structure. The n a2 The +1 valence is preferably 2 to 4, more preferably 2 or 3. In the formula (a1-2), Ra 2 is preferably an acid-dissociable group represented by the above general formula (a1-r-1).

[0099] In the formula (a1-3), Ya 001 The divalent linking group in is not particularly limited, but suitable examples include a divalent hydrocarbon group which may have a substituent, and a divalent linking group containing a hetero atom. Ya 001 is preferably an ester bond [-C(=O)-O-, -OC(=O)-], an ether bond (-O-), a linear or branched alkylene group, an aromatic hydrocarbon group, or a combination thereof, or a single bond. The alkylene group preferably has 1 to 10 carbon atoms, more preferably 1 to 6 carbon atoms, still more preferably 1 to 4 carbon atoms, and particularly preferably 1 to 3 carbon atoms. Among these, Ya 001is more preferably a combination of an ester bond [-C(=O)-O-, -OC(=O)-] and a linear alkylene group, or a single bond, and even more preferably a single bond.

[0100] In the formula (a1-3), Ya 01 The divalent linking group in is not particularly limited, but suitable examples include a divalent hydrocarbon group which may have a substituent, and a divalent linking group containing a hetero atom. Ya 01 Among the above, Ya is preferably an ester bond [-C(=O)-O-, -OC(=O)-], an ether bond (-O-), a linear or branched alkylene group, an aromatic hydrocarbon group, or a combination thereof, or a single bond. 01 is more preferably a combination of an ester bond [-C(=O)-O-, -OC(=O)-] and a linear alkylene group, or a single bond, and even more preferably a single bond.

[0101] In the formula (a1-3), Rax 01 is preferably an acid-dissociable group represented by the above general formula (a1-r-2) or (a1-r-4), and among these, an acid-dissociable group represented by the general formula (a1-r-2) is more preferred, and a group represented by the general formula (a1-r2-1) is even more preferred.

[0102] In the formula (a1-3), Rz 01 The alkyl group, halogenated alkyl group, and alkoxy group in the formula (I) preferably have 1 to 10 carbon atoms, more preferably 1 to 5 carbon atoms, even more preferably 1 to 3 carbon atoms, and particularly preferably 1 or 2 carbon atoms. The alkyl group, halogenated alkyl group, and alkoxy group may be linear or branched. Rz 01 The halogen atom in Rz is preferably an iodine atom. 01 The halogen atom of the halogenated alkyl group in the formula (I) is preferably a fluorine atom, an iodine atom, or a bromine atom, and more preferably a fluorine atom. Rz01 As the alkyl group, an alkoxy group or a hydroxy group is preferred, and a hydroxy group is more preferred.

[0103] In the formula (a1-3), q is an integer of 0 to 3. When q is 0, the structure is a benzene structure; when q is 1, the structure is a naphthalene structure; when q is 2, the structure is an anthracene structure; and when q is 3, the structure is a tetracene structure. In the formula (a1-3), n is an integer of 0 or more, preferably 0 to 5, more preferably 0 to 3, and even more preferably 1 or 2. When n is an integer of 2 or more, Rz 01 may be the same as or different from each other. In the formula (a1-3), n≦q×2+4. For example, when q is 1 and the naphthalene structure is formed, all six hydrogen atoms of the naphthalene may be substituted with hydroxy groups. 001 , -Ya 01 -C(=O)-O-Ra 01 The substitution positions of the group and the hydroxy group are not particularly limited.

[0104] Specific examples of the structural unit (a1) are shown below. In each of the following formulas, R α represents a hydrogen atom, a methyl group, or a trifluoromethyl group.

[0105] [ka]

[0106] [ka]

[0107] [ka]

[0108] [ka]

[0109] [ka]

[0110] [ka]

[0111] [ka]

[0112] [ka]

[0113] [ka]

[0114] In each of the following formulas, R α represents a hydrogen atom, a methyl group, or a trifluoromethyl group. Rz represents a hydrogen atom, an alkyl group, a halogen atom, a halogenated alkyl group, a hydroxy group, or an alkoxy group.

[0115] [ka]

[0116] [ka]

[0117] [ka]

[0118] [ka]

[0119] [ka]

[0120] The structural unit (a1) contained in the component (A1) may be of one type, or may be of two or more types. As the structural unit (a1), a structural unit represented by the above formula (a1-1) or a structural unit represented by the above formula (a1-3) is more preferred, as these tend to further improve the properties (sensitivity, shape, etc.) in electron beam or EUV lithography. Among these, the acid-dissociable group (Ra 1 , Rax 01 ) are preferably acid-dissociable groups represented by the above general formula (a1-r2-1), (a1-r2-3), (a1-r2-4) or (a1-r-4), respectively, and among these, it is particularly preferable to select those which are cyclic groups.

[0121] Alternatively, the structural unit (a1) may include a structural unit represented by the following general formula (a1-1-1).

[0122] [ka] [In the formula, Ra 1 " is an acid-dissociable group represented by general formula (a1-r2-1), (a1-r2-3), (a1-r2-4) or (a1-r-4). * represents a bond.]

[0123] In the formula (a1-1-1), R, Va 1 and n a1 represents R and Va in the formula (a1-1). 1 and n a1 is the same as:

[0124] The acid-dissociable group represented by formula (a1-r2-1), (a1-r2-3), (a1-r2-4), or (a1-r-4) is as described above. Among these, it is preferable to select an acid-dissociable group that is a cyclic group, since this enhances reactivity and is suitable for use with EB or EUV.

[0125] The proportion of the structural unit (a1) in the component (A1) is preferably 5 to 80 mol %, more preferably 10 to 75 mol %, even more preferably 30 to 70 mol %, and particularly preferably 40 to 70 mol %, based on the total (100 mol %) of all structural units constituting the component (A1). By ensuring that the proportion of the structural unit (a1) is at least as large as the lower limit of the aforementioned preferred range, lithography properties such as sensitivity, resolution, and CDU improvement are improved. On the other hand, by ensuring that the proportion is at most the upper limit of the aforementioned preferred range, a balance with other structural units can be achieved, resulting in various favorable lithography properties.

[0126] Other structural units The component (A1) may contain other structural units in addition to the structural unit (a1) described above, as necessary. Examples of other structural units include a structural unit (a10) represented by general formula (a10-1) described below; a structural unit (a2) containing a lactone-containing cyclic group; a structural unit (a5) that generates acid upon exposure; a structural unit (a6) that has acid diffusion-controlling properties; and a structural unit (a8) derived from a compound represented by general formula (a8-1) described below.

[0127] Building block (a10): The structural unit (a10) is a structural unit represented by the following general formula (a10-1).

[0128] [ka] [In the formula, R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms.] x1 is a single bond or a divalent linking group. x1is an aromatic hydrocarbon group which may have a substituent. ax1 is an integer greater than or equal to 1.]

[0129] In the formula (a10-1), R is the same as R in the general formula (a1-1). R is preferably a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a fluorinated alkyl group having 1 to 5 carbon atoms, and from the viewpoint of industrial availability, a hydrogen atom or a methyl group is particularly preferred.

[0130] In the formula (a10-1), Ya x1 is a single bond or a divalent linking group. In the above chemical formula, Ya x1 The divalent linking group in is not particularly limited, but suitable examples include a divalent hydrocarbon group which may have a substituent, and a divalent linking group containing a hetero atom.

[0131] Optionally substituted divalent hydrocarbon groups: The divalent hydrocarbon group which may have a substituent may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group.

[0132] Aliphatic hydrocarbon groups The aliphatic hydrocarbon group refers to a hydrocarbon group that does not have aromaticity. The aliphatic hydrocarbon group may be saturated or unsaturated, and is usually preferably saturated. Examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, and an aliphatic hydrocarbon group containing a ring in its structure.

[0133] Linear or branched aliphatic hydrocarbon groups The linear aliphatic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 6 carbon atoms, even more preferably 1 to 4 carbon atoms, and most preferably 1 to 3 carbon atoms. As the straight-chain aliphatic hydrocarbon group, a straight-chain alkylene group is preferred, and specific examples include a methylene group [-CH2-], an ethylene group [-(CH2)2-], a trimethylene group [-(CH2)3-], a tetramethylene group [-(CH2)4-], and a pentamethylene group [-(CH2)5-]. The branched aliphatic hydrocarbon group preferably has 2 to 10 carbon atoms, more preferably 3 to 6 carbon atoms, even more preferably 3 or 4 carbon atoms, and most preferably 3 carbon atoms. The branched aliphatic hydrocarbon group is preferably a branched alkylene group, and specific examples thereof include alkyl alkylene groups such as alkylmethylene groups such as -CH(CH3)-, -CH(CH2CH3)-, -C(CH3)2-, -C(CH3)(CH2CH3)-, -C(CH3)(CH2CH2CH3)-, and -C(CH2CH3)2-; alkylethylene groups such as -CH(CH3)CH2-, -CH(CH3)CH(CH3)-, -C(CH3)2CH2-, -CH(CH2CH3)CH2-, and -C(CH2CH3)2-CH2-; alkyl trimethylene groups such as -CH(CH3)CH2CH2- and -CH2CH(CH3)CH2-; and alkyl tetramethylene groups such as -CH(CH3)CH2CH2CH2- and -CH2CH(CH3)CH2CH2-. The alkyl group in the alkylalkylene group is preferably a linear alkyl group having 1 to 5 carbon atoms.

[0134] The linear or branched aliphatic hydrocarbon group may or may not have a substituent, such as a fluorine atom, a fluorinated alkyl group having 1 to 5 carbon atoms and substituted with a fluorine atom, or a carbonyl group.

[0135] Aliphatic hydrocarbon groups containing rings in the structure Examples of the aliphatic hydrocarbon group containing a ring in its structure include a cyclic aliphatic hydrocarbon group (a group in which two hydrogen atoms have been removed from an aliphatic hydrocarbon ring) which may contain a substituent containing a heteroatom in the ring structure, a group in which the cyclic aliphatic hydrocarbon group is bonded to the end of a straight-chain or branched-chain aliphatic hydrocarbon group, and a group in which the cyclic aliphatic hydrocarbon group is interposed in the middle of a straight-chain or branched-chain aliphatic hydrocarbon group. Examples of the straight-chain or branched-chain aliphatic hydrocarbon group include the same as those described above. The cyclic aliphatic hydrocarbon group preferably has 3 to 20 carbon atoms, more preferably 3 to 12 carbon atoms. The cyclic aliphatic hydrocarbon group may be a polycyclic group or a monocyclic group. The monocyclic alicyclic hydrocarbon group is preferably a group in which two hydrogen atoms have been removed from a monocycloalkane. The monocycloalkane is preferably one having 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane. The polycyclic alicyclic hydrocarbon group is preferably a group in which two hydrogen atoms have been removed from a polycycloalkane, and specific examples thereof include adamantane, norbornane, isobornane, and tricyclo[5.2.1.0]. 2,6 ]decane, tetracyclododecane, and the like.

[0136] The cyclic aliphatic hydrocarbon group may or may not have a substituent, such as an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, or a carbonyl group. The alkyl group as the substituent is preferably an alkyl group having 1 to 5 carbon atoms, and more preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group. The alkoxy group as the substituent is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, or a tert-butoxy group, and still more preferably a methoxy group or an ethoxy group. The halogen atom as the substituent is preferably a fluorine atom. Examples of the halogenated alkyl group as the substituent include groups in which some or all of the hydrogen atoms of the alkyl group have been substituted with the halogen atoms. In the cyclic aliphatic hydrocarbon group, some of the carbon atoms constituting the ring structure may be substituted with a substituent containing a heteroatom, and the heteroatom-containing substituent is preferably -O-, -C(=O)-O-, -S-, -S(=O)2-, or -S(=O)2-O-.

[0137] Aromatic hydrocarbon groups The aromatic hydrocarbon group is a hydrocarbon group having at least one aromatic ring. The aromatic ring is not particularly limited as long as it is a cyclic conjugated system having 4n+2 π electrons, and may be monocyclic or polycyclic. The aromatic ring preferably has 5 to 30 carbon atoms, more preferably 5 to 20 carbon atoms, still more preferably 6 to 15 carbon atoms, and particularly preferably 6 to 12 carbon atoms. However, this number of carbon atoms does not include the number of carbon atoms in the substituent. Specific examples of the aromatic ring include aromatic hydrocarbon rings such as benzene, naphthalene, anthracene, and phenanthrene; and aromatic heterocycles in which some of the carbon atoms constituting the aromatic hydrocarbon ring are substituted with heteroatoms. Examples of heteroatoms in the aromatic heterocycle include oxygen atoms, sulfur atoms, and nitrogen atoms. Specific examples of the aromatic heterocycle include pyridine rings and thiophene rings. Specific examples of the aromatic hydrocarbon group include groups in which two hydrogen atoms have been removed from the aromatic hydrocarbon ring or aromatic heterocycle (arylene groups or heteroarylene groups); groups in which two hydrogen atoms have been removed from an aromatic compound containing two or more aromatic rings (e.g., biphenyl, fluorene, etc.); and groups in which one hydrogen atom of a group in which one hydrogen atom has been removed from the aromatic hydrocarbon ring or aromatic heterocycle (aryl group or heteroaryl group) has been substituted with an alkylene group (e.g., groups in which one hydrogen atom has been further removed from the aryl group in an arylalkyl group such as a benzyl group, phenethyl group, 1-naphthylmethyl group, 2-naphthylmethyl group, 1-naphthylethyl group, or 2-naphthylethyl group). The alkylene group bonded to the aryl group or heteroaryl group preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.

[0138] The aromatic hydrocarbon group may have a hydrogen atom substituted with a substituent. For example, a hydrogen atom bonded to an aromatic ring in the aromatic hydrocarbon group may be substituted with a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, and a hydroxyl group. The alkyl group as the substituent is preferably an alkyl group having 1 to 5 carbon atoms, and more preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group. Examples of the alkoxy group, halogen atom and halogenated alkyl group as the substituent include those exemplified as the substituent substituting the hydrogen atom of the cyclic aliphatic hydrocarbon group.

[0139] Divalent linking groups containing heteroatoms: Examples of the divalent linking group containing a hetero atom include -O-, -C(=O)-O-, -OC(=O)-, -C(=O)-, -OC(=O)-O-, -C(=O)-NH-, -NH-, -NH-C(=NH)- (H may be substituted with a substituent such as an alkyl group or an acyl group), -S-, -S(=O)2-, -S(=O)2-O-, and groups represented by the general formula -Y 21 -OY22 -, -Y 21 -O-, -Y 21 -C(=O)-O-, -C(=O)-OY 21 -, -[Y 21 -C(=O)-O] m” -Y 22 -, -Y 21 -OC(=O)-Y 22 -or- Y 21 -S(=O)2-OY 22 -, wherein Y 21 and Y 22 are each independently a divalent hydrocarbon group which may have a substituent, O is an oxygen atom, and m″ is an integer of 1 to 3. When the divalent linking group containing a hetero atom is -C(=O)-NH-, -C(=O)-NH-C(=O)-, -NH-, or -NH-C(=NH)-, the H may be substituted with a substituent such as an alkyl group, an acyl group, etc. The substituent (alkyl group, acyl group, etc.) preferably has 1 to 10 carbon atoms, more preferably 1 to 8, and particularly preferably 1 to 5 carbon atoms. General formula-Y 21 -OY 22 -, -Y 21 -O-, -Y 21 -C(=O)-O-, -C(=O)-OY 21 -, -[Y 21 -C(=O)-O] m” -Y 22 -, -Y 21 -OC(=O)-Y 22 -or- Y 21 -S(=O)2-OY 22 -Medium, Y 21 and Y 22 are each independently a divalent hydrocarbon group which may have a substituent. Examples of the divalent hydrocarbon group include the same as those described above. Y 21 As the alkyl group, a straight-chain aliphatic hydrocarbon group is preferred, a straight-chain alkylene group is more preferred, a straight-chain alkylene group having 1 to 5 carbon atoms is even more preferred, and a methylene group or ethylene group is particularly preferred. Y 22is preferably a linear or branched aliphatic hydrocarbon group, more preferably a methylene group, an ethylene group or an alkylmethylene group. The alkyl group in the alkylmethylene group is preferably a linear alkyl group having 1 to 5 carbon atoms, more preferably a linear alkyl group having 1 to 3 carbon atoms, and most preferably a methyl group. Formula − [Y 21 -C(=O)-O] m” -Y 22 In the group represented by -, m" is an integer of 1 to 3, preferably 1 or 2, and more preferably 1. That is, the group represented by the formula -[Y 21 -C(=O)-O] m” -Y 22 The group represented by - is a group represented by the formula -Y 21 -C(=O)-OY 22 Particularly preferred is a group represented by the formula -(CH2) a’ -C(=O)-O-(CH2) b’ In the formula, a' is an integer of 1 to 10, preferably an integer of 1 to 8, more preferably an integer of 1 to 5, even more preferably 1 or 2, and most preferably 1. b' is an integer of 1 to 10, preferably an integer of 1 to 8, more preferably an integer of 1 to 5, even more preferably 1 or 2, and most preferably 1.

[0140] Ya x1 is preferably a single bond, an ester bond [-C(=O)-O-, -OC(=O)-], an ether bond (-O-), a linear or branched alkylene group, or a combination thereof, and more preferably a single bond or an ester bond [-C(=O)-O-, -OC(=O)-].

[0141] In the formula (a10-1), Wa x1 is an aromatic hydrocarbon group which may have a substituent. Wa x1 The aromatic hydrocarbon group in the formula (n) is an aromatic ring which may have a substituent. ax1Examples of the aromatic ring include groups in which 4n+1) hydrogen atoms have been removed. The aromatic ring here is not particularly limited as long as it is a cyclic conjugated system having 4n+2 π electrons. The aromatic ring preferably has 5 to 30 carbon atoms, more preferably 5 to 20 carbon atoms, even more preferably 6 to 15 carbon atoms, and particularly preferably 6 to 12 carbon atoms. Specific examples of the aromatic ring include aromatic hydrocarbon rings such as benzene, naphthalene, anthracene, and phenanthrene; and aromatic heterocycles in which some of the carbon atoms constituting the aromatic hydrocarbon ring are substituted with heteroatoms. Examples of heteroatoms in aromatic heterocycles include oxygen atoms, sulfur atoms, and nitrogen atoms. Specific examples of aromatic heterocycles include pyridine rings and thiophene rings. Also, Wa x1 The aromatic hydrocarbon group in (n) is selected from aromatic compounds containing an aromatic ring which may have two or more substituents (for example, biphenyl, fluorene, etc.). ax1 +1) hydrogen atoms may also be removed. Among the above, Wa x1 As examples, benzene, naphthalene, anthracene, or biphenyl (n ax1 A group in which (n +1) hydrogen atoms have been removed from benzene or naphthalene is preferred. ax1 A group obtained by removing (n +1) hydrogen atoms from benzene is more preferred. ax1 A group in which +1) hydrogen atoms have been removed is more preferred.

[0142] Wa x1 The aromatic hydrocarbon group in may or may not have a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, and a halogenated alkyl group. Examples of the alkyl group, alkoxy group, halogen atom, and halogenated alkyl group as the substituent include Ya x1 Examples of the substituent include the same as those exemplified as the substituent of the cyclic aliphatic hydrocarbon group in Wa. The substituent is preferably a linear or branched alkyl group having 1 to 5 carbon atoms, more preferably a linear or branched alkyl group having 1 to 3 carbon atoms, further preferably an ethyl group or a methyl group, and particularly preferably a methyl group. x1The aromatic hydrocarbon group in the formula (I) preferably does not have a substituent.

[0143] In the formula (a10-1), n ax1 is an integer of 1 or more, preferably an integer of 1 to 10, more preferably an integer of 1 to 5, further preferably 1, 2 or 3, and particularly preferably 1 or 2.

[0144] Specific examples of the structural unit (a10) represented by the formula (a10-1) are shown below. In each of the following formulas, R α represents a hydrogen atom, a methyl group, or a trifluoromethyl group.

[0145] [ka]

[0146] [ka]

[0147] [ka]

[0148] The structural unit (a10) contained in the component (A1) may be of one type, or may be of two or more types. The component (A1) may or may not contain the structural unit (a10), although it is preferable for the component (A1) to contain the structural unit (a10). When the component (A1) contains the structural unit (a10), the proportion of the structural unit (a10) in the component (A1) is preferably 20 to 80 mol %, more preferably 25 to 70 mol %, even more preferably 30 to 60 mol %, and particularly preferably 30 to 50 mol %, based on the total (100 mol %) of all structural units constituting the component (A1). By ensuring that the proportion of the structural unit (a10) is at least as large as the lower limit of the above range, sensitivity can be further improved, while by ensuring that the proportion is at most the upper limit, it is easier to achieve a balance with other structural units.

[0149] Building block (a2): The component (A1) may or may not contain a structural unit (a2) that contains a lactone-containing cyclic group (provided that this does not fall under the category of structural unit (a1)). The lactone-containing cyclic group of the structural unit (a2) is effective in improving the adhesion of the resist film to the substrate when the component (A1) is used to form a resist film. Furthermore, the presence of the structural unit (a2) results in favorable lithography properties, for example, by appropriately adjusting the acid diffusion length, improving the adhesion of the resist film to the substrate, and appropriately adjusting the solubility during development.

[0150] A "lactone-containing cyclic group" refers to a cyclic group containing a ring (lactone ring) containing -OC(=O)- in its ring skeleton. The lactone ring is counted as the first ring, and a group consisting of only a lactone ring is called a monocyclic group. If a group further contains other ring structures, it is called a polycyclic group regardless of the structure. The lactone-containing cyclic group may be a monocyclic group or a polycyclic group. The lactone-containing cyclic group in the structural unit (a2) is not particularly limited and any suitable group can be used. Specific examples include groups represented by the following general formulae (a2-r-1) to (a2-r-7).

[0151] [ka] [In the formula, Ra' 21 are each independently a hydrogen atom, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, -COOR", -OC(=O)R", a hydroxyalkyl group, or a cyano group; R" is a hydrogen atom, an alkyl group, or a lactone-containing cyclic group; A" is an alkylene group having 1 to 5 carbon atoms which may contain an oxygen atom (-O-) or a sulfur atom (-S-), an oxygen atom, or a sulfur atom; n' is an integer of 0 to 2, and m' is 0 or 1. * represents a bond (the same applies hereinafter).

[0152] In the general formulas (a2-r-1) to (a2-r-7), Ra' 21The alkyl group in the formula (I) is preferably an alkyl group having 1 to 6 carbon atoms. The alkyl group is preferably linear or branched. Specific examples include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group, a neopentyl group, and a hexyl group. Among these, a methyl group or an ethyl group is preferred, and a methyl group is particularly preferred. Ra' 21 The alkoxy group in the formula (1) is preferably an alkoxy group having 1 to 6 carbon atoms. The alkoxy group is preferably linear or branched. Specifically, the alkoxy group in the formula (1) is preferably linear or branched. 21 Examples of the alkyl group include a group in which the alkyl groups mentioned above are linked to an oxygen atom (—O—). Ra' 21 The halogen atom in is preferably a fluorine atom. Ra' 21 The halogenated alkyl group in the formula Ra' is 21 Examples of the halogenated alkyl group include groups in which some or all of the hydrogen atoms of the alkyl group have been substituted with the halogen atoms. As the halogenated alkyl group, a fluorinated alkyl group is preferred, and a perfluoroalkyl group is particularly preferred.

[0153] Ra' 21 In the -COOR" and -OC(=O)R" groups, R" is a hydrogen atom, an alkyl group, or a lactone-containing cyclic group. The alkyl group in R'' may be linear, branched, or cyclic, and preferably has 1 to 15 carbon atoms. When R″ is a linear or branched alkyl group, it preferably has 1 to 10 carbon atoms, more preferably 1 to 5 carbon atoms, and is particularly preferably a methyl group or an ethyl group. When R" is a cyclic alkyl group, it preferably has 3 to 15 carbon atoms, more preferably 4 to 12 carbon atoms, and most preferably 5 to 10 carbon atoms. Specific examples include groups in which one or more hydrogen atoms have been removed from a monocycloalkane which may or may not be substituted with a fluorine atom or a fluorinated alkyl group; groups in which one or more hydrogen atoms have been removed from a polycycloalkane such as a bicycloalkane, a tricycloalkane, or a tetracycloalkane; and more specific examples include groups in which one or more hydrogen atoms have been removed from a monocycloalkane such as cyclopentane or cyclohexane; adamantane, norbornane, isobornane, or tricyclo[5.2.1.0 2,6 ] decane, tetracyclododecane, and other polycycloalkanes in which one or more hydrogen atoms have been removed. Examples of the lactone-containing cyclic group in R″ include the same groups as those represented by the general formulae (a2-r-1) to (a2-r-7) above. Ra' 21 The hydroxyalkyl group in the formula (I) preferably has 1 to 6 carbon atoms, and specifically, the hydroxyalkyl group in the formula (I) is preferably a hydroxyalkyl group having 1 to 6 carbon atoms. 21 and a group in which at least one hydrogen atom of the alkyl group is substituted with a hydroxyl group.

[0154] Ra' 21 Among the above, each of the groups is preferably independently a hydrogen atom or a cyano group.

[0155] In the general formulae (a2-r-2), (a2-r-3), and (a2-r-5), the alkylene group having 1 to 5 carbon atoms for A" is preferably a straight-chain or branched-chain alkylene group, and examples thereof include a methylene group, an ethylene group, an n-propylene group, and an isopropylene group. When the alkylene group contains an oxygen atom or a sulfur atom, specific examples thereof include groups in which -O- or -S- is present at the terminal or between carbon atoms of the alkylene group, such as -O-CH2-, -CH2-O-CH2-, -S-CH2-, and -CH2-S-CH2-. A" is preferably an alkylene group having 1 to 5 carbon atoms or -O-, more preferably an alkylene group having 1 to 5 carbon atoms, and most preferably a methylene group.

[0156] Specific examples of the groups represented by the general formulae (a2-r-1) to (a2-r-7) are listed below.

[0157] [ka]

[0158] [ka]

[0159] Of the structural units (a2), structural units derived from acrylate esters in which the hydrogen atom bonded to the α-position carbon atom may be substituted with a substituent are particularly preferred. Such a structural unit (a2) is preferably a structural unit represented by the following general formula (a2-1).

[0160] [ka] [In the formula, R represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms.] 21 is a single bond or a divalent linking group. 21is -O-, -COO-, -CON(R')-, -OCO-, -CONHCO- or -CONHCS-, where R' represents a hydrogen atom or a methyl group. 21 If -O-, Ya 21 does not become -CO-. Ra 21 is a lactone-containing cyclic group.

[0161] In the formula (a2-1), R is the same as defined above. R is preferably a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a fluorinated alkyl group having 1 to 5 carbon atoms, and from the viewpoint of industrial availability, a hydrogen atom or a methyl group is particularly preferred.

[0162] In the formula (a2-1), Ya 21 The divalent linking group in is not particularly limited, but suitable examples include a divalent hydrocarbon group which may have a substituent, and a divalent linking group containing a hetero atom. 21 As the divalent linking group in the general formula (a10-1), x1 Examples of the divalent linking group include the same as the divalent linking group in the above.

[0163] Ya 21 is preferably a single bond, an ester bond [—C(═O)—O—], an ether bond (—O—), a linear or branched alkylene group, or a combination thereof.

[0164] In the formula (a2-1), Ya 21 is a single bond, and La 21 is preferably —COO— or —OCO—.

[0165] In the above formula (a2-1), Ra 21 is a lactone-containing cyclic group. Ra 21 Suitable examples of the lactone-containing cyclic group in the formula (a2-r-1) include the groups represented by the general formulae (a2-r-1) to (a2-r-7) described above.

[0166] The structural unit (a2) contained in the component (A1) may be of one type, or may be of two or more types. The component (A1) may or may not contain the structural unit (a2). When the component (A1) contains the structural unit (a2), the proportion of the structural unit (a2) relative to the total (100 mol%) of all structural units constituting the component (A1) is preferably 1 to 20 mol%, more preferably 1 to 15 mol%, and even more preferably 1 to 10 mol%. When the proportion of the structural unit (a2) is at least as great as the preferred lower limit, the effects achieved by including the structural unit (a2) can be fully obtained due to the effects described above. When the proportion of the structural unit (a2) is at most the upper limit, a balance with other structural units can be achieved, and various lithography properties become favorable.

[0167] Building block (a5): The component (A1) may or may not include a structural unit (a5) that generates acid upon exposure. Known structural units can be used as the structural unit (a5). By including the structural unit (a5), the acid generated upon exposure tends to be more uniformly distributed within the resist film. Examples of the structural unit (a5) include structural units containing a structure described below for the component (B). Examples include structural units containing a structure represented by any of the general formulas (b-1) to (b-3) below. Suitable examples of the structural unit (a5) include structural units represented by general formula (a5-1) shown below.

[0168] [ka] [In the formula, R m is an alkyl group having 1 to 5 carbon atoms, a halogenated alkyl group having 1 to 5 carbon atoms, a halogen atom, or a hydrogen atom. 50 is a divalent linking group or a single bond. 50 is a divalent hydrocarbon group which may have a substituent. a5 is an integer between 0 and 2. 51 is a divalent linking group. 5is a divalent linking group which may have a heteroatom, or a single bond. 51 and Ra 52 are each independently a hydrogen atom, a fluorine atom or a fluorinated alkyl group, n5 is an integer of 1 to 4, m is an integer of 1 or more, and M' m+ is an m-valent onium cation.

[0169] {anion part} In the above formula (a5-1), R m is an alkyl group having 1 to 5 carbon atoms, a halogenated alkyl group having 1 to 5 carbon atoms, a halogen atom, or a hydrogen atom. R m The alkyl group having 1 to 5 carbon atoms is preferably a linear or branched alkyl group having 1 to 5 carbon atoms, and specific examples thereof include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group, and a neopentyl group. The halogenated alkyl group having 1 to 5 carbon atoms is a group in which some or all of the hydrogen atoms of the alkyl group having 1 to 5 carbon atoms have been substituted with halogen atoms. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, an iodine atom, etc. As the halogen atom in the halogenated alkyl group, a fluorine atom is particularly preferred. R m As the alkyl group, a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a fluorinated alkyl group having 1 to 5 carbon atoms is preferred, and from the viewpoint of industrial availability, a hydrogen atom or a methyl group is most preferred.

[0170] In the above formula (a5-1), La 50 is a divalent linking group or a single bond. La 50 The divalent linking group in the formula is not particularly limited, but suitable examples include a divalent hydrocarbon group which may have a substituent and a divalent linking group containing a hetero atom, and each of these groups is the same as those described above for Ya x1 The divalent linking group is the same as the optionally substituted divalent hydrocarbon group and the divalent linking group containing a hetero atom exemplified in the above. Among the above, La 50 is preferably an ester bond [-C(=O)-O-, -OC(=O)-], an ether bond (-O-), a linear or branched alkylene group, an aromatic hydrocarbon group, or a combination thereof, or a single bond. 5 is more preferably an ester bond [-C(=O)-O-, -OC(=O)-] or a single bond, and further preferably an ester bond [-C(=O)-O-, -OC(=O)-].

[0171] In the above formula (a5-1), Ra 50 is a divalent hydrocarbon group which may have a substituent. Ra 50 The divalent hydrocarbon group in may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group.

[0172] ··Ra 50 Aliphatic hydrocarbon groups in The aliphatic hydrocarbon group means a hydrocarbon group that does not have aromaticity. The aliphatic hydrocarbon group may be saturated or unsaturated, and is usually preferably saturated. Examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, and an aliphatic hydrocarbon group containing a ring in its structure.

[0173] Linear or branched aliphatic hydrocarbon groups The linear aliphatic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 6 carbon atoms, even more preferably 1 to 4 carbon atoms, and most preferably 1 to 3 carbon atoms. As the straight-chain aliphatic hydrocarbon group, a straight-chain alkylene group is preferred, and specific examples include a methylene group [-CH2-], an ethylene group [-(CH2)2-], a trimethylene group [-(CH2)3-], a tetramethylene group [-(CH2)4-], and a pentamethylene group [-(CH2)5-]. The branched aliphatic hydrocarbon group preferably has 2 to 10 carbon atoms, more preferably 3 to 6 carbon atoms, even more preferably 3 or 4 carbon atoms, and most preferably 3 carbon atoms. The branched aliphatic hydrocarbon group is preferably a branched alkylene group, and specific examples thereof include alkyl alkylene groups such as alkylmethylene groups such as -CH(CH3)-, -CH(CH2CH3)-, -C(CH3)2-, -C(CH3)(CH2CH3)-, -C(CH3)(CH2CH2CH3)-, and -C(CH2CH3)2-; alkylethylene groups such as -CH(CH3)CH2-, -CH(CH3)CH(CH3)-, -C(CH3)2CH2-, -CH(CH2CH3)CH2-, and -C(CH2CH3)2-CH2-; alkyl trimethylene groups such as -CH(CH3)CH2CH2- and -CH2CH(CH3)CH2-; and alkyl tetramethylene groups such as -CH(CH3)CH2CH2CH2- and -CH2CH(CH3)CH2CH2-. The alkyl group in the alkylalkylene group is preferably a linear alkyl group having 1 to 5 carbon atoms.

[0174] The linear or branched aliphatic hydrocarbon group may or may not have a substituent, such as a fluorine atom, a fluorinated alkyl group having 1 to 5 carbon atoms and substituted with a fluorine atom, or a carbonyl group.

[0175] Aliphatic hydrocarbon groups containing rings in the structure Examples of the aliphatic hydrocarbon group containing a ring in its structure include a cyclic aliphatic hydrocarbon group (a group obtained by removing two hydrogen atoms from an aliphatic hydrocarbon ring) which may contain a substituent containing a heteroatom in the ring structure, a group in which the cyclic aliphatic hydrocarbon group is bonded to the end of a straight-chain or branched-chain aliphatic hydrocarbon group, and a group in which the cyclic aliphatic hydrocarbon group is interposed in the middle of a straight-chain or branched-chain aliphatic hydrocarbon group. Examples of the straight-chain or branched-chain aliphatic hydrocarbon group include the same as those described above. The cyclic aliphatic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably has 3 to 12 carbon atoms. The cyclic aliphatic hydrocarbon group may be a polycyclic group or a monocyclic group. The monocyclic alicyclic hydrocarbon group is preferably a group in which two hydrogen atoms have been removed from a monocycloalkane. The monocycloalkane is preferably one having 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane. The polycyclic alicyclic hydrocarbon group is preferably a group in which two hydrogen atoms have been removed from a polycycloalkane, and specific examples thereof include adamantane, norbornane, isobornane, and tricyclo[5.2.1.0]. 2,6 ]decane, tetracyclododecane, and the like.

[0176] The cyclic aliphatic hydrocarbon group may or may not have a substituent, such as an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, or a carbonyl group. The alkyl group as the substituent is preferably an alkyl group having 1 to 5 carbon atoms, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group. The alkoxy group as the substituent is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, or a tert-butoxy group, and most preferably a methoxy group or an ethoxy group. Examples of the halogen atom as the substituent include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, with a fluorine atom being preferred. Examples of the halogenated alkyl group as the substituent include groups in which some or all of the hydrogen atoms of the alkyl group have been substituted with the halogen atoms. In the cyclic aliphatic hydrocarbon group, some of the carbon atoms constituting the ring structure may be substituted with a substituent containing a heteroatom, and the heteroatom-containing substituent is preferably -O-, -C(=O)-O-, -S-, -S(=O)2-, or -S(=O)2-O-.

[0177] ··Ra 50Aromatic hydrocarbon groups in The aromatic hydrocarbon group is a hydrocarbon group having at least one aromatic ring. The aromatic ring is not particularly limited as long as it is a cyclic conjugated system having 4n+2 π electrons, and may be monocyclic or polycyclic. The aromatic ring preferably has 5 to 30 carbon atoms, more preferably 5 to 20 carbon atoms, even more preferably 6 to 15 carbon atoms, and particularly preferably 6 to 12 carbon atoms. However, this number of carbon atoms does not include the number of carbon atoms in the substituents. Specific examples of the aromatic ring include aromatic hydrocarbon rings such as benzene, naphthalene, anthracene, and phenanthrene; and aromatic heterocycles in which some of the carbon atoms constituting the aromatic hydrocarbon ring are substituted with heteroatoms. Examples of heteroatoms in aromatic heterocycles include oxygen atoms, sulfur atoms, and nitrogen atoms. Specific examples of aromatic heterocycles include pyridine rings and thiophene rings. Specific examples of the aromatic hydrocarbon group include groups (arylene groups or heteroarylene groups) in which two hydrogen atoms have been removed from the aromatic hydrocarbon ring or aromatic heterocycle; groups in which two hydrogen atoms have been removed from an aromatic compound containing two or more aromatic rings (e.g., biphenyl, fluorene, etc.); and groups in which one hydrogen atom of a group (aryl group or heteroaryl group) in which one hydrogen atom has been removed from the aromatic hydrocarbon ring or aromatic heterocycle has been substituted with an alkylene group (e.g., groups in which one hydrogen atom has been further removed from the aryl group in an arylalkyl group such as a benzyl group, phenethyl group, 1-naphthylmethyl group, 2-naphthylmethyl group, 1-naphthylethyl group, or 2-naphthylethyl group). The alkylene group bonded to the aryl group or heteroaryl group preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.

[0178] The aromatic hydrocarbon group may have a hydrogen atom substituted with a substituent. For example, a hydrogen atom bonded to an aromatic ring in the aromatic hydrocarbon group may be substituted with a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, and a hydroxyl group. The alkyl group as the substituent is preferably an alkyl group having 1 to 5 carbon atoms, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group. Examples of the alkoxy group, halogen atom and halogenated alkyl group as the substituent include those exemplified as the substituent substituting the hydrogen atom of the cyclic aliphatic hydrocarbon group.

[0179] In the formula (a5-1), n a5 is an integer between 0 and 2. Among the above, Ra 50 is preferably an aliphatic hydrocarbon group containing a ring in its structure, more preferably a cyclic aliphatic hydrocarbon group which may contain a substituent containing a hetero atom in the ring structure, and even more preferably an alicyclic hydrocarbon group which is a polycyclic group or a monocyclic group and which may have a substituent. Or, among the above, Ra 50 is preferably an aromatic hydrocarbon group.

[0180] n a5 If is 2, then two Ra 50 may all be alicyclic hydrocarbon groups which may have a substituent, may all be aromatic hydrocarbon groups, or may be a combination of alicyclic hydrocarbon groups which may have a substituent and aromatic hydrocarbon groups.

[0181] In the above formula (a5-1), La 51 is a divalent linking group. La 51 Examples of the divalent linking group in the formula (I) include non-hydrocarbon oxygen-atom-containing linking groups such as an oxygen atom (ether bond: -O-), an ester bond (-C(=O)-O-), an oxycarbonyl group (-O-C(=O)-), an amide bond (-C(=O)-NH-), a carbonyl group (-C(=O)-), and a carbonate bond (-O-C(=O)-O-); and combinations of such non-hydrocarbon oxygen-atom-containing linking groups with alkylene groups. A sulfonyl group (-SO2-) may be further linked to this combination. Examples of such divalent linking groups include linking groups represented by the following general formulae (L-al-1) to (L-al-8): In the following general formulae (L-al-1) to (L-al-8), Ra in the above formula (a5-1) 50 The bond to V' in the following general formulas (L-al-1) to (L-al-8) is 101 is.

[0182] [ka] [In the formula, V' 101 is a single bond or an alkylene group having 1 to 5 carbon atoms, and V' 102 is a divalent saturated hydrocarbon group having 1 to 30 carbon atoms.

[0183] V' 102 The divalent saturated hydrocarbon group in is preferably an alkylene group having 1 to 30 carbon atoms, more preferably an alkylene group having 1 to 10 carbon atoms, and even more preferably an alkylene group having 1 to 5 carbon atoms.

[0184] V' 101 and V' 102 The alkylene group in may be a straight-chain alkylene group or a branched-chain alkylene group, and is preferably a straight-chain alkylene group. V' 101 and V' 102Specific examples of the alkylene group in the formula (I) include a methylene group [-CH2-]; alkylmethylene groups such as -CH(CH3)-, -CH(CH2CH3)-, -C(CH3)2-, -C(CH3)(CH2CH3)-, -C(CH3)(CH2CH2CH3)-, and -C(CH2CH3)2-; an ethylene group [-CH2CH2-]; -CH(CH3)CH2-, -CH(CH3)CH(CH3)-, -C(CH3)2CH2-, and -CH(CH2CH3)CH2 -, etc.; a trimethylene group (n-propylene group) [-CH2CH2CH2-]; alkyl trimethylene groups such as -CH(CH3)CH2CH2- and -CH2CH(CH3)CH2-; a tetramethylene group [-CH2CH2CH2CH2-]; alkyl tetramethylene groups such as -CH(CH3)CH2CH2CH2- and -CH2CH(CH3)CH2CH2-; and a pentamethylene group [-CH2CH2CH2CH2CH2-]. Also, V' 101 or V' 102 In the formula (a1-r-1), some of the methylene groups in the alkylene group may be substituted with a divalent aliphatic cyclic group having 5 to 10 carbon atoms. The aliphatic cyclic group is represented by Ra' in the formula (a1-r-1). 3 A divalent group obtained by removing one more hydrogen atom from a cyclic aliphatic hydrocarbon group (a monocyclic aliphatic hydrocarbon group or a polycyclic aliphatic hydrocarbon group) of the above is preferred, and a cyclohexylene group, a 1,5-adamantylene group or a 2,6-adamantylene group is more preferred.

[0185] La 51 As for L-al-1, a divalent linking group containing an ester bond or a divalent linking group containing an ether bond is preferable, the linking groups represented by the above formulas (L-al-1) to (L-al-5) and (L-al-8) are more preferable, and the linking group represented by (L-al-3) or (L-al-8) is even more preferable.

[0186] In the formula (a5-1), Ya 5 is a divalent linking group which may have a heteroatom, or a single bond. Ya 5The divalent linking group in is not particularly limited, but suitable examples include a divalent hydrocarbon group which may have a substituent, and a divalent linking group containing a hetero atom. Ya 5 The divalent hydrocarbon group which may have a substituent and the divalent linking group which contains a hetero atom in x1 The divalent linking group is the same as the optionally substituted divalent hydrocarbon group and the divalent linking group containing a hetero atom exemplified in the above. Among the above, Ya 5 is preferably a linear or branched alkylene group or a single bond, and more preferably a single bond.

[0187] In the above formula (a5-1), Ra 51 and Ra 52 are each independently a hydrogen atom, a fluorine atom or a fluorinated alkyl group. Ra 51 and Ra 52 The fluorinated alkyl group in each of the above is preferably a linear or branched fluorinated alkyl group having 1 to 5 carbon atoms, more preferably a trifluoromethyl group. In the above formula (a5-1), SO3 - Ra bonded to the carbon atom adjacent to 51 and Ra 52 From the viewpoint of acid strength, it is preferable that at least one of the groups is a fluorine atom.

[0188] In the formula (a5-1), n5 represents an integer of 1 to 4, and 1, 2, or 3 is preferable.

[0189] {cation part} In the above formula (a5-1), M' m+ represents an m-valent onium cation. Among these, M' m+ is preferably a sulfonium cation or an iodonium cation, and m is an integer of 1 or more.

[0190] Preferred cationic moieties ((M' m+ ) 1 / m) includes organic cations represented by the following general formulas (ca-1) to (ca-3), respectively.

[0191] [ka] [In the formula, R 201 ~R 207 R each independently represents an aryl group which may have a substituent, an alkyl group which may have a substituent, or an alkenyl group which may have a substituent. 201 ~R 203 , R 206 ~R 207 may be bonded to each other to form a ring together with the sulfur atom in the formula. 208 ~R 209 R each independently represents a hydrogen atom or an alkyl group having 1 to 5 carbon atoms. 210 is an optionally substituted aryl group, an optionally substituted alkyl group, an optionally substituted alkenyl group, or an optionally substituted -SO2- containing cyclic group. 201 represents -C(=O)- or -C(=O)-O-.]

[0192] In the above general formulas (ca-1) to (ca-3), R 201 ~R 207 The aryl group in the formula (I) includes an unsubstituted aryl group having 6 to 20 carbon atoms, and a phenyl group or a naphthyl group is preferred. R 201 ~R 207 The alkyl group in the formula (I) is preferably a chain or cyclic alkyl group having 1 to 30 carbon atoms. R 201 ~R 207 The alkenyl group in the formula (I) preferably has 2 to 10 carbon atoms. R 201 ~R 207 , and R 210Examples of the substituent that may be possessed by the group include an alkyl group, a halogen atom, a halogenated alkyl group, a carbonyl group, a cyano group, an amino group, an aryl group, and groups represented by the following general formulae (ca-r-1) to (ca-r-7).

[0193] [ka] [In the formula, R' 201 are each independently a hydrogen atom, a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a chain alkenyl group which may have a substituent.

[0194] Optionally substituted cyclic groups: The cyclic group is preferably a cyclic hydrocarbon group, and the cyclic hydrocarbon group may be an aromatic hydrocarbon group or an aliphatic hydrocarbon group. An aliphatic hydrocarbon group means a hydrocarbon group that does not have aromaticity. Furthermore, the aliphatic hydrocarbon group may be saturated or unsaturated, and is usually preferably saturated.

[0195] R' 201 The aromatic hydrocarbon group in the formula (I) is a hydrocarbon group having an aromatic ring. The aromatic hydrocarbon group preferably has 3 to 30 carbon atoms, more preferably 5 to 30 carbon atoms, even more preferably 5 to 20 carbon atoms, particularly preferably 6 to 15 carbon atoms, and most preferably 6 to 10 carbon atoms. However, this number of carbon atoms does not include the number of carbon atoms in the substituent. R' 201 Specific examples of the aromatic ring contained in the aromatic hydrocarbon group in the above formula include benzene, fluorene, naphthalene, anthracene, phenanthrene, biphenyl, and aromatic heterocycles in which some of the carbon atoms constituting these aromatic rings are substituted with heteroatoms. Examples of the heteroatom in the aromatic heterocycle include an oxygen atom, a sulfur atom, and a nitrogen atom. R' 201Specific examples of the aromatic hydrocarbon group in include a group in which one hydrogen atom has been removed from the aromatic ring (aryl group: for example, phenyl group, naphthyl group, etc.), and a group in which one hydrogen atom of the aromatic ring has been substituted with an alkylene group (for example, arylalkyl groups such as benzyl group, phenethyl group, 1-naphthylmethyl group, 2-naphthylmethyl group, 1-naphthylethyl group, 2-naphthylethyl group, etc.). The alkylene group (the alkyl chain in the arylalkyl group) preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.

[0196] R' 201 The cyclic aliphatic hydrocarbon group in the formula (I) is an aliphatic hydrocarbon group containing a ring in the structure. Examples of aliphatic hydrocarbon groups that contain a ring in their structure include alicyclic hydrocarbon groups (groups in which one hydrogen atom has been removed from an aliphatic hydrocarbon ring), groups in which an alicyclic hydrocarbon group is bonded to the end of a straight-chain or branched-chain aliphatic hydrocarbon group, and groups in which an alicyclic hydrocarbon group is interposed in the middle of a straight-chain or branched-chain aliphatic hydrocarbon group. The alicyclic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms. The alicyclic hydrocarbon group may be a polycyclic group or a monocyclic group. The monocyclic alicyclic hydrocarbon group is preferably a group in which one or more hydrogen atoms have been removed from a monocycloalkane. The monocycloalkane is preferably one having 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane. The polycyclic alicyclic hydrocarbon group is preferably a group in which one or more hydrogen atoms have been removed from a polycycloalkane, and the polycycloalkane is preferably one having 7 to 30 carbon atoms. Among these, the polycycloalkane includes adamantane, norbornane, isobornane, tricyclo[5.2.1.0], and the like. 2,6 More preferred are polycycloalkanes having a polycyclic skeleton of a bridged ring system, such as decane and tetracyclododecane; and polycycloalkanes having a polycyclic skeleton of a condensed ring system, such as a cyclic group having a steroid skeleton.

[0197] Among them, R'201 The cyclic aliphatic hydrocarbon group in is preferably a group in which one or more hydrogen atoms have been removed from a monocycloalkane or a polycycloalkane, more preferably a group in which one hydrogen atom has been removed from a polycycloalkane, particularly preferably an adamantyl group or a norbornyl group, and most preferably an adamantyl group.

[0198] The linear or branched aliphatic hydrocarbon group which may be bonded to the alicyclic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 6 carbon atoms, still more preferably 1 to 4 carbon atoms, and particularly preferably 1 to 3 carbon atoms. As the straight-chain aliphatic hydrocarbon group, a straight-chain alkylene group is preferred, and specific examples include a methylene group [-CH2-], an ethylene group [-(CH2)2-], a trimethylene group [-(CH2)3-], a tetramethylene group [-(CH2)4-], and a pentamethylene group [-(CH2)5-]. The branched aliphatic hydrocarbon group is preferably a branched alkylene group, and specific examples thereof include alkyl alkylene groups such as alkylmethylene groups such as -CH(CH3)-, -CH(CH2CH3)-, -C(CH3)2-, -C(CH3)(CH2CH3)-, -C(CH3)(CH2CH2CH3)-, and -C(CH2CH3)2-; alkylethylene groups such as -CH(CH3)CH2-, -CH(CH3)CH(CH3)-, -C(CH3)2CH2-, -CH(CH2CH3)CH2-, and -C(CH2CH3)2-CH2-; alkyl trimethylene groups such as -CH(CH3)CH2CH2- and -CH2CH(CH3)CH2-; and alkyl tetramethylene groups such as -CH(CH3)CH2CH2CH2- and -CH2CH(CH3)CH2CH2-. The alkyl group in the alkylalkylene group is preferably a linear alkyl group having 1 to 5 carbon atoms.

[0199] Also, R' 201The cyclic hydrocarbon group in may contain a heteroatom, such as a heterocycle. Specific examples include lactone-containing cyclic groups represented by the above-mentioned general formulas (a2-r-1) to (a2-r-7), -SO2- containing cyclic groups represented by the below-mentioned general formulas (b5-r-1) to (b5-r-4), and other heterocyclic groups represented by the following chemical formulas (r-hr-1) to (r-hr-16), respectively.

[0200] [ka]

[0201] R' 201 Examples of the substituent in the cyclic group include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, a carbonyl group, and a nitro group. The alkyl group as a substituent is preferably an alkyl group having 1 to 5 carbon atoms, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group. The alkoxy group as a substituent is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, or a tert-butoxy group, and most preferably a methoxy group or an ethoxy group. As the halogen atom as a substituent, a fluorine atom is preferred. Examples of halogenated alkyl groups as substituents include alkyl groups having 1 to 5 carbon atoms, such as methyl, ethyl, propyl, n-butyl, and tert-butyl groups, in which some or all of the hydrogen atoms have been substituted with the above-mentioned halogen atoms. The carbonyl group as a substituent is a group that substitutes a methylene group (-CH2-) that constitutes a cyclic hydrocarbon group.

[0202] A chain alkyl group which may have a substituent: R' 201 The chain alkyl group may be either a straight chain or a branched chain. The linear alkyl group preferably has 1 to 20 carbon atoms, more preferably 1 to 15 carbon atoms, and most preferably 1 to 10 carbon atoms. The branched alkyl group preferably has 3 to 20 carbon atoms, more preferably 3 to 15 carbon atoms, and most preferably 3 to 10 carbon atoms. Specific examples include a 1-methylethyl group, a 1-methylpropyl group, a 2-methylpropyl group, a 1-methylbutyl group, a 2-methylbutyl group, a 3-methylbutyl group, a 1-ethylbutyl group, a 2-ethylbutyl group, a 1-methylpentyl group, a 2-methylpentyl group, a 3-methylpentyl group, and a 4-methylpentyl group.

[0203] An optionally substituted chain alkenyl group: R' 201 The chain alkenyl group may be either linear or branched, and preferably has 2 to 10 carbon atoms, more preferably 2 to 5 carbon atoms, even more preferably 2 to 4 carbon atoms, and particularly preferably 3 carbon atoms. Examples of the linear alkenyl group include a vinyl group, a propenyl group (allyl group), and a butenyl group. Examples of the branched alkenyl group include a 1-methylvinyl group, a 2-methylvinyl group, a 1-methylpropenyl group, and a 2-methylpropenyl group. Of the chain alkenyl groups mentioned above, linear alkenyl groups are preferred, vinyl groups and propenyl groups are more preferred, and vinyl groups are particularly preferred.

[0204] R' 201 Examples of the substituent in the chain alkyl or alkenyl group include an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, a carbonyl group, a nitro group, an amino group, the above-mentioned R' 201 Examples of the cyclic groups include the cyclic groups shown in the formula:

[0205] R' 201In addition to those mentioned above, the optionally substituted cyclic group, the optionally substituted chain alkyl group, or the optionally substituted chain alkenyl group also includes the same as the acid-dissociable group represented by formula (a1-r-2) above as the optionally substituted cyclic group or the optionally substituted chain alkyl group.

[0206] Among them, R' 201 is preferably a cyclic group which may have a substituent, and more preferably a cyclic hydrocarbon group which may have a substituent. More specifically, for example, a phenyl group, a naphthyl group, a group in which one or more hydrogen atoms have been removed from a polycycloalkane, a lactone-containing cyclic group represented by each of the general formulae (a2-r-1) to (a2-r-7) above, and an —SO2- containing cyclic group represented by each of the general formulae (b5-r-1) to (b5-r-4) described below are preferred.

[0207] In the above general formulas (ca-1) to (ca-3), R 201 ~R 203 , R 206 ~R 207 When they are bonded to each other to form a ring together with the sulfur atom in the formula, they may not contain a heteroatom such as a sulfur atom, an oxygen atom, or a nitrogen atom, or a carbonyl group, -SO-, -SO2-, -SO3-, -COO-, -CONH-, or -N(R N )-(applicable R N is an alkyl group having 1 to 5 carbon atoms.) The ring formed is preferably a 3- to 10-membered ring, including the sulfur atom, and particularly preferably a 5- to 7-membered ring, inclusive of the sulfur atom. Specific examples of the ring formed include a thiophene ring, a thiazole ring, a benzothiophene ring, a dibenzothiophene ring, a 9H-thioxanthene ring, a thioxanthone ring, a thianthrene ring, a phenoxathiin ring, a tetrahydrothiophenium ring, and a tetrahydrothiopyranium ring.

[0208] R 208 ~R 209each independently represents a hydrogen atom or an alkyl group having 1 to 5 carbon atoms, preferably a hydrogen atom or an alkyl group having 1 to 3 carbon atoms, and when they are alkyl groups, they may be bonded to each other to form a ring.

[0209] R 210 is an optionally substituted aryl group, an optionally substituted alkyl group, an optionally substituted alkenyl group, or an optionally substituted -SO2- containing cyclic group. R 210 The aryl group in the formula (I) includes an unsubstituted aryl group having 6 to 20 carbon atoms, and a phenyl group or a naphthyl group is preferred. R 210 The alkyl group in the formula (I) is preferably a chain or cyclic alkyl group having 1 to 30 carbon atoms. R 210 The alkenyl group in the formula (I) preferably has 2 to 10 carbon atoms. R 210 The -SO2- containing cyclic group in is not particularly limited and any group can be used. Specific examples include groups represented by the following general formulae (b5-r-1) to (b5-r-4), with "-SO2- containing polycyclic groups" being preferred and groups represented by general formula (b5-r-1) being more preferred.

[0210] [ka] [In the formula, Rb' 51 are each independently a hydrogen atom, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, -COOR", -OC(=O)R", a hydroxyalkyl group, or a cyano group; R" is a hydrogen atom, an alkyl group, a lactone-containing cyclic group, or an -SO2- containing cyclic group; B" is an alkylene group having 1 to 5 carbon atoms which may contain an oxygen atom or a sulfur atom, an oxygen atom, or a sulfur atom, and n' is an integer of 0 to 2. * represents a bond.

[0211] In the general formulae (b5-r-1) and (b5-r-2), B″ represents an alkylene group having 1 to 5 carbon atoms which may contain an oxygen atom or a sulfur atom, an oxygen atom, or a sulfur atom. B" is preferably an alkylene group having 1 to 5 carbon atoms or -O-, more preferably an alkylene group having 1 to 5 carbon atoms, and even more preferably a methylene group.

[0212] In the general formulae (b5-r-1) to (b5-r-4), Rb' 51 are each independently a hydrogen atom, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, -COOR", -OC(=O)R", a hydroxyalkyl group, or a cyano group, and among these, are preferably each independently a hydrogen atom or a cyano group.

[0213] Specific examples of the groups represented by general formulae (b5-r-1) to (b5-r-4) are listed below, in which "Ac" represents an acetyl group.

[0214] [ka]

[0215] [ka]

[0216] [ka]

[0217] Specific examples of suitable cations represented by the formula (ca-1) include cations represented by the following chemical formulas.

[0218] [ka]

[0219] [ka]

[0220] [ka] [In the formula, g1, g2, and g3 represent the number of repeating units, where g1 is an integer of 1 to 5, g2 is an integer of 0 to 20, and g3 is an integer of 0 to 20.]

[0221] [ka]

[0222] [ka]

[0223] [ka] [In the formula, R” 201 is a hydrogen atom or a substituent, and the substituent is the same as R 201 ~R 207 , and R 210 The substituents are the same as those exemplified as the substituents that may be possessed by the group

[0224] [ka]

[0225] Specific examples of suitable cations represented by the formula (ca-2) include diphenyliodonium cation, bis(4-tert-butylphenyl)iodonium cation, and the like.

[0226] Specific examples of suitable cations represented by the formula (ca-3) include cations represented by the following formulas (ca-3-1) to (ca-3-6).

[0227] [ka]

[0228] The cation moiety ((M') in the formula (a5-1) m+ ) 1 / m ) is preferably a sulfonium cation, more preferably a cation represented by each of the formulas (ca-1) to (ca-3), still more preferably a cation represented by the formula (ca-1), and particularly preferably a cation represented by each of the formulas (ca-1-1) to (ca-1-84). In particular, from the viewpoint of achieving high sensitivity, the preferred cation represented by the formula (ca-1) is one having an electron-withdrawing group such as a fluorine atom, a fluorinated alkyl group, or a sulfonyl group as a substituent, and for example, a cation selected from the group consisting of the cations represented by the above chemical formulas (ca-1-44), (ca-1-71) to (ca-1-84), respectively, is particularly preferred.

[0229] Specific preferred examples of the structural unit (a5) are shown below. In the following formula, R α represents a hydrogen atom, a methyl group, or a trifluoromethyl group. m+ represents m and M' in the above general formula (a5-1). m+ is the same as:

[0230] [ka]

[0231] [ka]

[0232] [ka]

[0233] The structural unit (a5) contained in the component (A1) may be of one type, or may be of two or more types. When the component (A1) contains the structural unit (a5), the proportion of the structural unit (a5) in the component (A1) is preferably 5 to 25 mol %, more preferably 10 to 20 mol %, and even more preferably 15 to 20 mol %, based on the total (100 mol %) of all structural units constituting the component (A1). When the proportion of the structural unit (a5) is at least as large as the lower limit of the above-mentioned preferred range, it becomes easier to achieve even higher sensitivity and improved resolution, while when it is at most the upper limit of the above-mentioned preferred range, it becomes easier to achieve a balance with other structural units.

[0234] Building block (a6): The structural unit (a6) is a structural unit that has acid diffusion controllability. The component (A1) may or may not have the structural unit (a6). Known structural units can be used as the structural unit (a6). Examples of the structural unit (a6) include structural units containing the structures described in the components (D1) and (D2) described below. Examples include structural units containing a structure represented by any of the general formulas (d1-1) to (d1-3) described below.

[0235] The structural unit (a6) contained in the component (A1) may be of one type, or may be of two or more types. When the component (A1) contains the structural unit (a6), the proportion of the structural unit (a6) in the component (A1) is preferably 1 to 20 mol %, more preferably 2 to 15 mol %, and even more preferably 3 to 10 mol %, based on the total (100 mol %) of all structural units constituting the component (A1). When the proportion of the structural unit (a6) is at least as large as the lower limit of the above-mentioned preferred range, even higher sensitivity can be easily achieved, while when it is at most the upper limit of the above-mentioned preferred range, it is easier to achieve a balance with other structural units.

[0236] Building block (a8): The structural unit (a8) is a structural unit derived from a compound represented by the following general formula (a8-1): The component (A1) may or may not contain the structural unit (a8).

[0237] [ka] [In the formula, W 2 is a polymerizable group-containing group. x2 is a single bond or (n ax2 +1)valent linking group. x2 and W 2 R may form a condensed ring. 1 R is a fluorinated alkyl group having 1 to 12 carbon atoms. 2 R is a hydrogen atom or an organic group having 1 to 12 carbon atoms which may have a fluorine atom. 2 and Ya x2 may be bonded to each other to form a ring structure. ax2 is an integer between 1 and 3.

[0238] W 2 The "polymerizable group" in the polymerizable group-containing group is a group that enables a compound having a polymerizable group to be polymerized by radical polymerization or the like, and refers to a group that contains a multiple bond between carbon atoms, such as an ethylenic double bond.

[0239] The polymerizable group-containing group may be a group consisting of only a polymerizable group, or may be a group consisting of a polymerizable group and a group other than the polymerizable group. Examples of the group other than the polymerizable group include a divalent hydrocarbon group which may have a substituent, and a divalent linking group containing a heteroatom. Examples of the polymerizable group-containing group include a group represented by the chemical formula: C(R X11 )(R X12 )=C(R X13 )-Ya x0 A group represented by the formula - is preferred. In this chemical formula, R X11 , R X12 and R X13 are each a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms, and Ya x0 is a single bond or a divalent linking group.

[0240] Ya x2 and W 2 The fused ring formed by W2 Polymerizable group of the site and Ya x2 and the fused ring formed by W 2 Other groups than the polymerizable group at the Ya site x2 and a fused ring formed by Ya x2 and W 2 The fused ring formed by these may have a substituent.

[0241] Specific examples of the structural unit (a8) are shown below. In the following formula, R α represents a hydrogen atom, a methyl group, or a trifluoromethyl group.

[0242] [ka]

[0243] Among the above examples, the structural unit (a8) is preferably at least one selected from the group consisting of structural units represented by chemical formulas (a8-1-01) to (a8-1-04), (a8-1-06), (a8-1-08), (a8-1-09), and (a8-1-10), and more preferably at least one selected from the group consisting of structural units represented by chemical formulas (a8-1-01) to (a8-1-04) and (a8-1-09).

[0244] The structural unit (a8) contained in the component (A1) may be of one type, or may be of two or more types. The component (A1) may or may not contain the structural unit (a8). The amount of the structural unit (a8) in the component (A1) relative to the total amount (100 mol %) of all structural units constituting the component (A1) is preferably within a range from 0 to 50 mol %, and more preferably from 0 to 30 mol %.

[0245] The component (A1) contained in the resist composition may use either a single type of compound, or a combination of two or more types of compounds.

[0246] Examples of the component (A1) include a polymeric compound having the structural unit (a1) and the structural unit (a10); a polymeric compound having the structural unit (a1), the structural unit (a10), and the structural unit (a0); a polymeric compound having the structural unit (a1), the structural unit (a10), and the structural unit (a2). Preferred examples of the component (A1) include a polymeric compound consisting of the structural unit (a1) and the structural unit (a10); a polymeric compound consisting of the structural unit (a1), the structural unit (a10), and the structural unit (a0); a polymeric compound consisting of the structural unit (a1), the structural unit (a10), and the structural unit (a2).

[0247] In a polymeric compound comprising the structural unit (a1) and the structural unit (a10), the proportion of the structural unit (a1) relative to the total (100 mol%) of all structural units constituting the polymeric compound is preferably 10 to 75 mol%, even more preferably 30 to 70 mol%, and even more preferably 40 to 70 mol%. The proportion of the structural unit (a10) in the polymer compound is preferably 25 to 90 mol %, more preferably 30 to 70 mol %, even more preferably 30 to 60 mol %, and particularly preferably 20 to 50 mol %, based on the total (100 mol %) of all structural units constituting the polymer compound.

[0248] In a polymeric compound composed of the structural unit (a1), the structural unit (a10), and the structural unit (a0), the proportion of the structural unit (a1) relative to the total (100 mol%) of all structural units constituting the polymeric compound is preferably 10 to 85 mol%, even more preferably 30 to 70 mol%, and even more preferably 40 to 70 mol%. The proportion of the structural unit (a10) in the polymer compound is preferably 10 to 85 mol %, more preferably 30 to 70 mol %, even more preferably 30 to 60 mol %, and particularly preferably 20 to 50 mol %, based on the total (100 mol %) of all structural units constituting the polymer compound. The proportion of the structural unit (a0) in the polymer compound is preferably 1 to 50 mol %, more preferably 3 to 30 mol %, even more preferably 5 to 20 mol %, and particularly preferably 5 to 15 mol %, relative to the total (100 mol %) of all structural units constituting the polymer compound.

[0249] In a polymeric compound composed of the structural unit (a1), the structural unit (a10), and the structural unit (a2), the proportion of the structural unit (a1) relative to the total (100 mol%) of all structural units constituting the polymeric compound is preferably 10 to 85 mol%, even more preferably 30 to 70 mol%, and even more preferably 40 to 70 mol%. The proportion of the structural unit (a10) in the polymer compound is preferably 10 to 85 mol %, more preferably 30 to 70 mol %, even more preferably 30 to 60 mol %, and particularly preferably 20 to 50 mol %, based on the total (100 mol %) of all structural units constituting the polymer compound. The proportion of the structural unit (a2) in the polymer compound is preferably 5 to 80 mol %, more preferably 10 to 60 mol %, even more preferably 10 to 40 mol %, and particularly preferably 10 to 30 mol %, relative to the total (100 mol %) of all structural units constituting the polymer compound.

[0250] The component (A1) can be produced by dissolving the monomers that derive each structural unit in a polymerization solvent, and then adding a radical polymerization initiator such as azobisisobutyronitrile (AIBN) or dimethyl azobisisobutyrate (e.g., V-601) to the solution and polymerizing the resulting mixture. Examples of monomers that derive each structural unit include monomers that derive the structural unit (a10), monomers that derive the structural unit (a1), and monomers that derive any other structural unit (for example, the structural unit (a4), the structural unit (st), etc.). These monomers (for example, the monomers that derive the structural unit (a10)) may have protected hydroxyl groups, etc., as necessary. In this case, the component (A1) can be produced by carrying out a deprotection reaction after carrying out the polymerization reaction as described above. During polymerization, a chain transfer agent such as HS-CH2-CH2-CH2-C(CF3)2-OH may be used in combination to introduce a -C(CF3)2-OH group to the terminal. Copolymers incorporating hydroxyalkyl groups, in which some of the alkyl group's hydrogen atoms are substituted with fluorine atoms, are effective in reducing development defects and LER (line edge roughness: unevenness on the line sidewalls).

[0251] The weight average molecular weight (Mw) of the component (A1) (based on polystyrene standards measured by gel permeation chromatography (GPC)) is not particularly limited, but is preferably 1,000 to 50,000, more preferably 5,000 to 40,000, and even more preferably 5,000 to 30,000. When the Mw of the component (A1) is less than or equal to the preferred upper limit of this range, the compound has sufficient solubility in a resist solvent for use as a resist, and when it is at least the preferred lower limit of this range, the compound exhibits good dry etching resistance and the cross-sectional shape of the resist pattern. The dispersity (Mw / Mn) of the component (A1) is not particularly limited, but is preferably from 1.0 to 4.0, more preferably from 1.0 to 3.0, and particularly preferably from 1.0 to 2.0, where Mn represents the number average molecular weight.

[0252] About ingredient (A2) The resist composition of this embodiment may also use, as the component (A), a base component (hereafter referred to as “component (A2)”) that does not fall under the category of the component (A1) and whose solubility in a developer changes upon the action of an acid. There are no particular restrictions on the component (A2), and it can be selected from the many conventional base components for chemically amplified resist compositions. The component (A2) may be a high molecular weight compound or a low molecular weight compound, and may be used alone or in combination of two or more types.

[0253] The proportion of the component (A1) within the component (A), relative to the total mass of the component (A), is preferably 25 mass% or more, more preferably 50 mass% or more, even more preferably 75 mass% or more, and may even be 100 mass%. When this proportion is 25 mass% or more, sensitivity is likely to be improved, and a resist pattern that is excellent in various lithography properties such as resolution and roughness is likely to be formed.

[0254] The amount of the component (A) in the resist composition of this embodiment may be adjusted depending on factors such as the thickness of the resist film to be formed.

[0255] <Acid generator component (B)> The resist composition of this embodiment may contain an acid generator component (B) that generates an acid upon exposure. There are no particular restrictions on the component (B), and any of the acid generators that have been proposed as acid generators for chemically amplified resist compositions can be used. Examples of such acid generators include onium salt-based acid generators such as iodonium salts and sulfonium salts, oxime sulfonate-based acid generators, diazomethane-based acid generators such as bisalkyl or bisarylsulfonyldiazomethanes and poly(bissulfonyl)diazomethanes, nitrobenzyl sulfonate-based acid generators, iminosulfonate-based acid generators, and disulfone-based acid generators. Component (B) may be contained in the form of a compound, or in the form of a compound incorporated into component (A1) as the structural unit (a5), or in both of these forms.

[0256] Examples of the onium salt acid generator include a compound represented by the following general formula (b-1) (hereinafter also referred to as "component (b-1)"), a compound represented by general formula (b-2) (hereinafter also referred to as "component (b-2)"), or a compound represented by general formula (b-3) (hereinafter also referred to as "component (b-3)").

[0257] [ka] [In the formula, R 101 and R 104 ~R108 R each independently represents a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a chain alkenyl group which may have a substituent. 104 and R 105 R may be bonded to each other to form a ring structure. 102 is a fluorine atom or a fluorinated alkyl group having 1 to 5 carbon atoms. 101 is a divalent linking group containing an oxygen atom or a single bond. 101 ~V 103 are each independently a single bond, an alkylene group, or a fluorinated alkylene group, provided that Y 101 and V 101 cannot be a single bond at the same time. 101 ~L 102 are each independently a single bond or an oxygen atom. 103 ~L 105 are each independently a single bond, —CO— or —SO2—; m is an integer of 1 or more; and M' m+ is an m-valent onium cation.

[0258] {anion part} Anion in component (b-1) In formula (b-1), R 101 represents a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a chain alkenyl group which may have a substituent.

[0259] Optionally substituted cyclic groups: The cyclic group is preferably a cyclic hydrocarbon group, and the cyclic hydrocarbon group may be an aromatic hydrocarbon group or an aliphatic hydrocarbon group. An aliphatic hydrocarbon group means a hydrocarbon group that does not have aromaticity. Furthermore, the aliphatic hydrocarbon group is preferably saturated.

[0260] R 101The aromatic hydrocarbon group in the formula (I) is a hydrocarbon group having an aromatic ring. The number of carbon atoms in the aromatic hydrocarbon group is preferably 3 to 30, more preferably 5 to 30, even more preferably 5 to 20, particularly preferably 6 to 15, and most preferably 6 to 10. However, the number of carbon atoms does not include the number of carbon atoms in the substituent. R 101 Specific examples of the aromatic ring contained in the aromatic hydrocarbon group in the above formula include benzene, fluorene, naphthalene, anthracene, phenanthrene, biphenyl, and aromatic heterocycles in which some of the carbon atoms constituting these aromatic rings are substituted with heteroatoms. Examples of the heteroatom in the aromatic heterocycle include an oxygen atom, a sulfur atom, and a nitrogen atom. R 101 Specific examples of the aromatic hydrocarbon group in the formula (I) include a group in which one hydrogen atom has been removed from the aromatic ring (aryl group: for example, phenyl group, naphthyl group, etc.), and a group in which one hydrogen atom of the aromatic ring has been substituted with an alkylene group (for example, benzyl group, phenethyl group, 1-naphthylmethyl group, etc.). The number of carbon atoms in the alkylene group (alkyl chain in the arylalkyl group) is preferably 1 to 4, more preferably 1 to 2, and particularly preferably 1.

[0261] R 101 The cyclic aliphatic hydrocarbon group in the formula (I) is an aliphatic hydrocarbon group containing a ring in the structure. Examples of aliphatic hydrocarbon groups that contain a ring in their structure include alicyclic hydrocarbon groups (groups in which one hydrogen atom has been removed from an aliphatic hydrocarbon ring), groups in which an alicyclic hydrocarbon group is bonded to the end of a straight-chain or branched-chain aliphatic hydrocarbon group, and groups in which an alicyclic hydrocarbon group is interposed in the middle of a straight-chain or branched-chain aliphatic hydrocarbon group. The alicyclic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms. The alicyclic hydrocarbon group may be a polycyclic group or a monocyclic group. The monocyclic alicyclic hydrocarbon group is preferably a group in which one or more hydrogen atoms have been removed from a monocycloalkane. The monocycloalkane is preferably one having 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane. The polycyclic alicyclic hydrocarbon group is preferably a group in which one or more hydrogen atoms have been removed from a polycycloalkane, and the polycycloalkane is preferably one having 7 to 30 carbon atoms. Among these, the polycycloalkane includes adamantane, norbornane, isobornane, tricyclo[5.2.1.0], and the like. 2,6 More preferred are polycycloalkanes having a polycyclic skeleton of a bridged ring system, such as decane and tetracyclododecane; and polycycloalkanes having a polycyclic skeleton of a condensed ring system, such as a cyclic group having a steroid skeleton.

[0262] Among them, R 101 The cyclic aliphatic hydrocarbon group in is preferably a group in which one or more hydrogen atoms have been removed from a monocycloalkane or a polycycloalkane, more preferably a group in which one hydrogen atom has been removed from a polycycloalkane, further preferably an adamantyl group or a norbornyl group, and particularly preferably an adamantyl group.

[0263] The linear aliphatic hydrocarbon group which may be bonded to the alicyclic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 6, even more preferably 1 to 4, and most preferably 1 to 3. The linear aliphatic hydrocarbon group is preferably a linear alkylene group, and specific examples thereof include a methylene group [-CH2-], an ethylene group [-(CH2)2-], a trimethylene group [-(CH2)3-], a tetramethylene group [-(CH2)4-], and a pentamethylene group [-(CH2)5-]. The branched aliphatic hydrocarbon group which may be bonded to the alicyclic hydrocarbon group preferably has 2 to 10 carbon atoms, more preferably 3 to 6 carbon atoms, even more preferably 3 or 4 carbon atoms, and most preferably 3 carbon atoms. The branched aliphatic hydrocarbon group is preferably a branched alkylene group, and specific examples thereof include alkyl alkylene groups such as alkylmethylene groups such as -CH(CH3)-, -CH(CH2CH3)-, -C(CH3)2-, -C(CH3)(CH2CH3)-, -C(CH3)(CH2CH2CH3)-, and -C(CH2CH3)2-; alkylethylene groups such as -CH(CH3)CH2-, -CH(CH3)CH(CH3)-, -C(CH3)2CH2-, -CH(CH2CH3)CH2-, and -C(CH2CH3)2-CH2-; alkyl trimethylene groups such as -CH(CH3)CH2CH2- and -CH2CH(CH3)CH2-; and alkyl tetramethylene groups such as -CH(CH3)CH2CH2CH2- and -CH2CH(CH3)CH2CH2-. The alkyl group in the alkylalkylene group is preferably a linear alkyl group having 1 to 5 carbon atoms.

[0264] Also, R 101 The cyclic hydrocarbon group in may contain a heteroatom, such as a heterocycle, etc. Specific examples include the lactone-containing cyclic groups represented by the general formulae (a2-r-1) to (a2-r-7) above, the —SO—-containing cyclic groups represented by the general formulae (b5-r-1) to (b5-r-4) above, and other heterocyclic groups represented by the chemical formulae (r-hr-1) to (r-hr-16) above.

[0265] R 101 Examples of the substituent in the cyclic group include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, a carbonyl group, and a nitro group. The alkyl group as a substituent is preferably an alkyl group having 1 to 5 carbon atoms. The alkoxy group as a substituent is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, or a tert-butoxy group, and most preferably a methoxy group or an ethoxy group. As the halogen atom as a substituent, a fluorine atom, a bromine atom, or an iodine atom is preferred. Examples of halogenated alkyl groups as substituents include alkyl groups having 1 to 5 carbon atoms, such as methyl, ethyl, propyl, n-butyl, and tert-butyl groups, in which some or all of the hydrogen atoms have been substituted with the above-mentioned halogen atoms. The carbonyl group as a substituent is a group that substitutes a methylene group (-CH2-) that constitutes a cyclic hydrocarbon group.

[0266] R 101 The cyclic hydrocarbon group in may be a fused ring group containing a fused ring in which an aliphatic hydrocarbon ring and an aromatic ring are fused. Examples of the fused ring include a polycycloalkane having a polycyclic skeleton of a bridged ring system to which one or more aromatic rings are fused. Specific examples of the bridged ring system polycycloalkane include bicycloalkanes such as bicyclo[2.2.1]heptane (norbornane) and bicyclo[2.2.2]octane. The fused ring group is preferably a group containing a fused ring in which two or three aromatic rings are fused to a bicycloalkane, and more preferably a group containing a fused ring in which two or three aromatic rings are fused to a bicyclo[2.2.2]octane. 101 Specific examples of the fused cyclic group in the formula (b-1) include groups represented by the following formulas (r-br-1) to (r-br-2). In the formulas, * represents Y in formula (b-1). 101 represents a bond bonded to

[0267] [ka]

[0268] R 101Examples of the substituent that the fused cyclic group in the formula (I) may have include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, a carbonyl group, a nitro group, an aromatic hydrocarbon group, and an alicyclic hydrocarbon group. The alkyl group, alkoxy group, halogen atom, and halogenated alkyl group as the substituent of the fused cyclic group are the same as those described above in R 101 Examples of the substituents for the cyclic group in the formula (I) include the same as those listed above. Examples of the aromatic hydrocarbon group as the substituent of the fused ring group include a group in which one hydrogen atom has been removed from an aromatic ring (aryl group: for example, a phenyl group, a naphthyl group, etc.), a group in which one hydrogen atom of the aromatic ring has been substituted with an alkylene group (for example, an arylalkyl group such as a benzyl group, a phenethyl group, a 1-naphthylmethyl group, a 2-naphthylmethyl group, a 1-naphthylethyl group, a 2-naphthylethyl group, etc.), and heterocyclic groups represented by the above formulas (r-hr-1) to (r-hr-6). Examples of the alicyclic hydrocarbon group as a substituent of the fused ring group include groups in which one hydrogen atom has been removed from a monocycloalkane such as cyclopentane or cyclohexane; 2,6 ] groups in which one hydrogen atom has been removed from a polycycloalkane such as decane, tetracyclododecane, or tetracyclododecane; lactone-containing cyclic groups represented by the general formulae (a2-r-1) to (a2-r-7) above; —SO2- containing cyclic groups represented by the general formulae (b5-r-1) to (b5-r-4) above; and heterocyclic groups represented by the formulae (r-hr-7) to (r-hr-16) above.

[0269] A chain alkyl group which may have a substituent: R 101 The chain alkyl group may be either a straight chain or a branched chain. The linear alkyl group preferably has 1 to 20 carbon atoms, more preferably 1 to 15 carbon atoms, and most preferably 1 to 10 carbon atoms. The branched alkyl group preferably has 3 to 20 carbon atoms, more preferably 3 to 15 carbon atoms, and most preferably 3 to 10. Specific examples include a 1-methylethyl group, a 1-methylpropyl group, a 2-methylpropyl group, a 1-methylbutyl group, a 2-methylbutyl group, a 3-methylbutyl group, a 1-ethylbutyl group, a 2-ethylbutyl group, a 1-methylpentyl group, a 2-methylpentyl group, a 3-methylpentyl group, and a 4-methylpentyl group.

[0270] An optionally substituted chain alkenyl group: R 101 The chain alkenyl group may be either linear or branched, and preferably has 2 to 10 carbon atoms, more preferably 2 to 5, even more preferably 2 to 4, and particularly preferably 3. Examples of the linear alkenyl group include a vinyl group, a propenyl group (allyl group), and a butenyl group. Examples of the branched alkenyl group include a 1-methylvinyl group, a 2-methylvinyl group, a 1-methylpropenyl group, and a 2-methylpropenyl group. Of the chain alkenyl groups mentioned above, linear alkenyl groups are preferred, vinyl groups and propenyl groups are more preferred, and vinyl groups are particularly preferred.

[0271] R 101 Examples of the substituent in the chain alkyl or alkenyl group include an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, a carbonyl group, a nitro group, an amino group, and the above-mentioned R 101 Examples of the cyclic groups include the cyclic groups shown in the formula:

[0272] In formula (b-1), Y 101 is a single bond or a divalent linking group containing an oxygen atom. Y 101 is a divalent linking group containing an oxygen atom, 101 may contain atoms other than oxygen atoms. Examples of atoms other than oxygen atoms include carbon atoms, hydrogen atoms, sulfur atoms, and nitrogen atoms. Examples of the divalent linking group containing an oxygen atom include the linking groups represented by the above general formulas (L-al-1) to (L-al-8). In the following general formulas (L-al-1) to (L-al-8), R in the above formula (b-1) 101 The bond to V' in the following general formulas (L-al-1) to (L-al-8) is 101 is.

[0273] In formula (b-1), V 101 is a single bond, an alkylene group, or a fluorinated alkylene group. 101 is preferably a single bond or a linear fluorinated alkylene group having 1 to 4 carbon atoms.

[0274] In formula (b-1), R 102 is a fluorine atom or a fluorinated alkyl group having 1 to 5 carbon atoms. 102 is preferably a fluorine atom or a perfluoroalkyl group having 1 to 5 carbon atoms, and more preferably a fluorine atom.

[0275] Specific examples of the anion moiety represented by the formula (b-1) include, for example, Y 101 When Y is a single bond, examples of the anion include a fluorinated alkylsulfonate anion such as a trifluoromethanesulfonate anion or a perfluorobutanesulfonate anion; 101 When is a divalent linking group containing an oxygen atom, examples of the anions include those represented by any of the following formulae (an-1) to (an-3).

[0276] [ka] [In the formula, R” 101 R" is an aliphatic cyclic group which may have a substituent, a monovalent heterocyclic group represented by the above chemical formulas (r-hr-1) to (r-hr-16), a fused cyclic group represented by the above formula (r-br-1) or (r-br-2), a chain alkyl group which may have a substituent, or an aromatic cyclic group which may have a substituent. 102R" is an aliphatic cyclic group which may have a substituent, a fused cyclic group represented by the formula (r-br-1) or (r-br-2) above, a lactone-containing cyclic group represented by each of the general formulae (a2-r-1), (a2-r-3) to (a2-r-7) above, or an -SO2- containing cyclic group represented by each of the general formulae (b5-r-1) to (b5-r-4) above. 103 V" is an aromatic cyclic group which may have a substituent, an aliphatic cyclic group which may have a substituent, or a chain alkenyl group which may have a substituent. 101 is a single bond, an alkylene group having 1 to 4 carbon atoms, or a fluorinated alkylene group having 1 to 4 carbon atoms. 102 is a fluorine atom or a fluorinated alkyl group having 1 to 5 carbon atoms; each v" is independently an integer of 0 to 3, each q" is independently an integer of 0 to 20, and n" is 0 or 1.

[0277] R” 101 , R” 102 and R” 103 The aliphatic cyclic group which may have a substituent is represented by R 101 The substituent is preferably a group exemplified as the cyclic aliphatic hydrocarbon group in the formula (b-1). 101 Examples of the substituents that may be substituted on the cyclic aliphatic hydrocarbon group in the above formula (1) include the same as those that may be substituted on the cyclic aliphatic hydrocarbon group in the above formula (1).

[0278] R” 101 and R” 103 The aromatic cyclic group which may have a substituent in the formula (b-1) is R 101 The substituent is preferably a group exemplified as the aromatic hydrocarbon group in the cyclic hydrocarbon group in the formula (b-1). 101 Examples of the substituents that may substitute the aromatic hydrocarbon group in the above formula (1) include the same as those in the above formula (1).

[0279] R” 101 The chain alkyl group which may have a substituent in the formula (b-1) is R 101 The alkyl group is preferably one of the groups exemplified as the chain alkyl group in the above formula. R” 103 The chain alkenyl group which may have a substituent is R 101 Preferably, it is a group exemplified as the chain alkenyl group in the above formula.

[0280] Anion in component (b-2) In formula (b-2), R 104 , R 105 are each independently a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a chain alkenyl group which may have a substituent, and each is represented by R 101 However, R 104 , R 105 may be bonded to each other to form a ring. R 104 , R 105 is preferably a chain alkyl group which may have a substituent, more preferably a linear or branched alkyl group, or a linear or branched fluorinated alkyl group. The chain alkyl group preferably has 1 to 10 carbon atoms, more preferably 1 to 7 carbon atoms, and even more preferably 1 to 3 carbon atoms. 104 , R 105 The number of carbon atoms in the chain alkyl group of R is preferably as small as possible within the above range of carbon atoms, for reasons such as good solubility in resist solvents. 104 , R 105 In the chain alkyl group, the greater the number of hydrogen atoms substituted with fluorine atoms, the stronger the acid strength and the improved transparency to high-energy light of 250 nm or less and electron beams, which is preferable. The proportion of fluorine atoms in the chain alkyl group, i.e., the fluorination rate, is preferably 70 to 100%, more preferably 90 to 100%, and most preferably a perfluoroalkyl group in which all hydrogen atoms are substituted with fluorine atoms. In formula (b-2), V 102 , V 103 are each independently a single bond, an alkylene group, or a fluorinated alkylene group, and each represents V in formula (b-1).101 The same can be mentioned. In formula (b-2), L 101 , L 102 are each independently a single bond or an oxygen atom.

[0281] Anion in component (b-3) In formula (b-3), R 106 ~R 108 are each independently a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a chain alkenyl group which may have a substituent, and each is represented by R 101 The same can be mentioned. In formula (b-3), L 103 ~L 105 are each independently a single bond, —CO— or —SO2—.

[0282] Among the above, the anion moiety of the component (B) is preferably the anion in the component (b-1), and more preferably the anion represented by the above formula (an-1).

[0283] {cation part} In the formula (b-1), formula (b-2), and formula (b-3), M' m+ represents an m-valent onium cation. Among these, sulfonium cation and iodonium cation are preferred. m is an integer of 1 or more.

[0284] The cation moiety of component (B) is preferably a sulfonium cation, more preferably a cation represented by each of the formulas (ca-1) to (ca-3), still more preferably a cation represented by the formula (ca-1), and particularly preferably a cation represented by each of the formulas (ca-1-1) to (ca-1-84).

[0285] In the resist composition of this embodiment, as the component (B), one type of compound may be used alone, or two or more types may be used in combination. When the resist composition contains the component (B), the amount of the component (B) in the resist composition is preferably less than 50 parts by mass, more preferably 5 to 45 parts by mass, and even more preferably 10 to 43 parts by mass, per 100 parts by mass of the component (A). By ensuring that the amount of component (B) falls within this preferred range, it becomes easier to obtain a homogeneous solution when the individual components of the resist composition are dissolved in an organic solvent, and the storage stability of the resist composition becomes excellent, which is advantageous.

[0286] <Base component (D)> The resist composition of this embodiment may contain, in addition to the component (A), a base component (component (D)) that traps the acid generated upon exposure (i.e., controls the diffusion of the acid). The component (D) functions as a quencher (acid diffusion controller) that traps the acid generated in the resist composition upon exposure. Examples of the component (D) include a photodegradable base (D1) (hereinafter referred to as "component (D1)") that decomposes upon exposure and loses its acid diffusion controllability, and a nitrogen-containing organic compound (D2) (hereinafter referred to as "component (D2)") that does not fall under the category of component (D1). Among these, the photodegradable base (component (D1)) is preferred because it is likely to enhance all of the properties of high sensitivity, reduced roughness, and suppressed occurrence of coating defects. The components (D1) and (D2) may be contained in the form of a compound, or may be incorporated into the component (A1) as the structural unit (a6), or may be in both of these forms. The compounds exemplified below as the component (D1) may be used as the acid generator component (component (B)) in combination with other compounds.

[0287] Regarding component (D1) The component (D1) is not particularly limited as long as it decomposes upon exposure to light and loses its acid diffusion controllability, and is preferably one or more compounds selected from the group consisting of a compound represented by the following general formula (d1-1) (hereinafter referred to as "component (d1-1)"), a compound represented by the following general formula (d1-2) (hereinafter referred to as "component (d1-2)"), and a compound represented by the following general formula (d1-3) (hereinafter referred to as "component (d1-3)"): The components (d1-1) to (d1-3) do not act as quenchers in the exposed areas of the resist film because they decompose and lose their acid diffusion control properties (basicity), but act as quenchers in the unexposed areas of the resist film.

[0288] [ka] [In the formula, Rd 1 ~Rd 4 is a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a chain alkenyl group which may have a substituent. 2 In this case, no fluorine atom is bonded to the carbon atom adjacent to the S atom. 1 is a single bond or a divalent linking group; m is an integer of 1 or more; M m+ are each independently an m-valent organic cation.

[0289] {(d1-1) component} Anion part In formula (d1-1), Rd 1 is a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a chain alkenyl group which may have a substituent, and each of the R' 201 The same can be mentioned. Among these, Rd 1is preferably an aromatic hydrocarbon group which may have a substituent, an aliphatic cyclic group which may have a substituent, or a chain-like alkyl group which may have a substituent. Examples of the substituent which these groups may have include a hydroxyl group, an oxo group, an alkyl group, an aryl group, a fluorine atom, a fluorinated alkyl group, a lactone-containing cyclic group represented by the above general formulas (a2-r-1) to (a2-r-7), an ether bond, an ester bond, or a combination thereof. When an ether bond or an ester bond is contained as a substituent, it may be via an alkylene group, and in this case, the substituent is preferably a linking group represented by the above formulas (L-al-1) to (L-al-5). Note that Rd 1 In the case where the aromatic hydrocarbon group, the aliphatic cyclic group, or the chain alkyl group has a linking group represented by the above general formulas (L-al-1) to (L-al-8) as a substituent, in the above general formulas (L-al-1) to (L-al-8), Rd in formula (d1-1) 1 The carbon atom constituting the aromatic hydrocarbon group, the aliphatic cyclic group, or the chain alkyl group in the formula (L-al-1) to (L-al-8) is bonded to V' 101 is. Suitable examples of the aromatic hydrocarbon group include a phenyl group, a naphthyl group, and a polycyclic structure containing a bicyclooctane skeleton (a polycyclic structure consisting of a bicyclooctane skeleton and another ring structure). Examples of the aliphatic cyclic group include adamantane, norbornane, isobornane, tricyclo[5.2.1.0 2,6 It is more preferable that the cycloalkane is a group in which one or more hydrogen atoms have been removed from a polycycloalkane such as decane or tetracyclododecane. The chain alkyl group preferably has 1 to 10 carbon atoms, and specific examples thereof include straight-chain alkyl groups such as a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, a nonyl group, and a decyl group; and branched-chain alkyl groups such as a 1-methylethyl group, a 1-methylpropyl group, a 2-methylpropyl group, a 1-methylbutyl group, a 2-methylbutyl group, a 3-methylbutyl group, a 1-ethylbutyl group, a 2-ethylbutyl group, a 1-methylpentyl group, a 2-methylpentyl group, a 3-methylpentyl group, and a 4-methylpentyl group.

[0290] When the chain-like alkyl group is a fluorinated alkyl group having a fluorine atom or a fluorinated alkyl group as a substituent, the number of carbon atoms in the fluorinated alkyl group is preferably 1 to 11, more preferably 1 to 8, and even more preferably 1 to 4. The fluorinated alkyl group may contain atoms other than fluorine atoms. Examples of atoms other than fluorine atoms include oxygen atoms, sulfur atoms, and nitrogen atoms.

[0291] Preferred examples of the anion moiety of the component (d1-1) are shown below.

[0292] [ka]

[0293] Cation part In formula (d1-1), M m+ is an m-valent organic cation. M m+ Suitable organic cations include those similar to those represented by the general formulae (ca-1) to (ca-3), with the cation represented by the general formula (ca-1) being more preferred, and the cations represented by the general formulae (ca-1-1) to (ca-1-84) being even more preferred. The component (d1-1) may be used alone or in combination of two or more.

[0294] {(d1-2) component} Anion part In formula (d1-2), Rd 2 is a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a chain alkenyl group which may have a substituent, and R' 201 The same can be mentioned. However, Rd 2 In this case, the carbon atom adjacent to the S atom is not bonded to a fluorine atom (is not fluorinated), which makes the anion of component (d1-2) an appropriately weak acid anion, thereby improving the quenching ability of component (D). Road 2 The alkyl group is preferably a chain alkyl group which may have a substituent or an aliphatic cyclic group which may have a substituent, and more preferably an aliphatic cyclic group which may have a substituent.

[0295] The chain alkyl group preferably has 1 to 10 carbon atoms, and more preferably 3 to 10 carbon atoms. Examples of the aliphatic cyclic group include adamantane, norbornane, isobornane, tricyclo[5.2.1.0 2,6 ] a group (which may have a substituent) in which one or more hydrogen atoms have been removed from decane, tetracyclododecane, or the like; and a group in which one or more hydrogen atoms have been removed from camphor is more preferred.

[0296] Road 2 The hydrocarbon group may have a substituent, and the substituent may be Rd 1 Examples of the substituents include the same as those that may be contained in the hydrocarbon group (aromatic hydrocarbon group, aliphatic cyclic group, chain alkyl group) in the above.

[0297] Preferred examples of the anion moiety of the component (d1-2) are shown below.

[0298] [ka]

[0299] Cation part In formula (d1-2), M m+ is an m-valent organic cation, and M in the formula (d1-1) m+ is the same as: The component (d1-2) may be used alone or in combination of two or more.

[0300] {(d1-3) component} Anion part In formula (d1-3), Rd 3 is a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a chain alkenyl group which may have a substituent, and 201 The Rd is preferably a fluorine atom-containing cyclic group, a chain alkyl group, or a chain alkenyl group. Among these, a fluorinated alkyl group is preferred, and the Rd 1 The same fluorinated alkyl groups as those mentioned above are more preferred.

[0301] In formula (d1-3), Rd 4 is a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a chain alkenyl group which may have a substituent, and R' 201 The same can be mentioned. Among these, alkyl groups, alkoxy groups, alkenyl groups and cyclic groups which may have a substituent are preferred. Road 4 The alkyl group in Rd is preferably a linear or branched alkyl group having 1 to 5 carbon atoms, and specific examples thereof include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group, and a neopentyl group. 4 A portion of the hydrogen atoms of the alkyl group may be substituted with a hydroxyl group, a cyano group, or the like. Road 4The alkoxy group in is preferably an alkoxy group having 1 to 5 carbon atoms, and specific examples of the alkoxy group having 1 to 5 carbon atoms include a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, and a tert-butoxy group. Of these, a methoxy group and an ethoxy group are preferred.

[0302] Road 4 The alkenyl group in R' 201 Examples include the same alkenyl groups as those in the above, and vinyl, propenyl (allyl), 1-methylpropenyl, and 2-methylpropenyl groups are preferred. These groups may further have an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms as a substituent.

[0303] Road 4 The cyclic group in the formula (I) is the same as the R' 201 Examples of the cyclic groups include cyclopentane, cyclohexane, adamantane, norbornane, isobornane, tricyclo[5.2.1.0 2,6 ] An alicyclic group in which one or more hydrogen atoms have been removed from a cycloalkane such as decane or tetracyclododecane, or an aromatic group such as a phenyl group or naphthyl group is preferred. 4 When Rd is an alicyclic group, the resist composition dissolves well in an organic solvent, resulting in excellent lithography properties. 4 When is an aromatic group, in lithography using EUV or the like as an exposure light source, the resist composition exhibits excellent light absorption efficiency, and exhibits favorable sensitivity and lithography properties.

[0304] In formula (d1-3), Yd 1 is a single bond or a divalent linking group. Yd 1 The divalent linking group in is not particularly limited, but examples thereof include a divalent hydrocarbon group (aliphatic hydrocarbon group, aromatic hydrocarbon group) which may have a substituent, and a divalent linking group containing a hetero atom. 21Examples of the divalent linking group include the same divalent hydrocarbon groups which may have a substituent and divalent linking groups containing a hetero atom as those mentioned in the description of the divalent linking group in the above. Yd 1 is preferably a carbonyl group, an ester bond, an amide bond, an alkylene group, or a combination thereof. The alkylene group is more preferably a linear or branched alkylene group, and further preferably a methylene group or an ethylene group.

[0305] Preferred examples of the anion moiety of the component (d1-3) are shown below.

[0306] [ka]

[0307] [ka]

[0308] Cation part In formula (d1-3), M m+ is an m-valent organic cation, and M in the formula (d1-1) m+ is the same as: The component (d1-3) may be used alone or in combination of two or more.

[0309] The component (D1) may be any one of the components (d1-1) to (d1-3) above, or a combination of two or more of them. When the resist composition contains the component (D1), the amount of the component (D1) within the resist composition is preferably 0.5 to 15 parts by mass, more preferably 1 to 15 parts by mass, and even more preferably 2 to 15 parts by mass, relative to 100 parts by mass of the component (A).

[0310] The component (D1) preferably contains the component (d1-1) above. The content of the component (d1-1) in the entire component (D1) is preferably 50% by mass or more, more preferably 70% by mass or more, and even more preferably 90% by mass or more. The component (D1) may consist solely of the compound component (d1-1).

[0311] Manufacturing method of component (D1): The method for producing the components (d1-1) and (d1-2) is not particularly limited, and they can be produced by known methods. The method for producing component (d1-3) is not particularly limited, and it can be produced, for example, in a manner similar to that described in US2012-0149916. The compound of component (D1) has been shown as an example of a base component (component (D)) that traps acid generated by exposure, but the compound of component (D1) may also be used as component (B). For example, in the resist composition of this embodiment, a compound of component (D1) may be used as the component (B), and a compound that generates an acid with a lower acidity than the acid generated by the compound of component (D1) upon exposure may be used as the component (D). Alternatively, in the resist composition of this embodiment, a compound of component (D1) may be used as the component (B), and a component (D2) described below may be used as the component (D).

[0312] Regarding component (D2) The component (D) may contain a nitrogen-containing organic compound component (hereinafter referred to as "component (D2)") that does not fall under the category of the component (D1) described above. The component (D2) is not particularly limited as long as it acts as an acid diffusion controller and does not fall under the category of component (D1), and any known component may be used. Among these, aliphatic amines are preferred, and among these, secondary aliphatic amines and tertiary aliphatic amines are particularly preferred. An aliphatic amine is an amine having one or more aliphatic groups, and the aliphatic groups preferably have 1 to 12 carbon atoms. Examples of aliphatic amines include amines in which at least one hydrogen atom of ammonia NH3 has been substituted with an alkyl group or hydroxyalkyl group having 12 or less carbon atoms (alkylamines or alkyl alcohol amines), and cyclic amines. Specific examples of alkylamines and alkyl alcoholamines include monoalkylamines such as n-hexylamine, n-heptylamine, n-octylamine, n-nonylamine, and n-decylamine; dialkylamines such as diethylamine, di-n-propylamine, di-n-heptylamine, di-n-octylamine, and dicyclohexylamine; trialkylamines such as trimethylamine, triethylamine, tri-n-propylamine, tri-n-butylamine, tri-n-pentylamine, tri-n-hexylamine, tri-n-heptylamine, tri-n-octylamine, tri-n-nonylamine, tri-n-decylamine, and tri-n-dodecylamine; and alkyl alcoholamines such as diethanolamine, triethanolamine, diisopropanolamine, triisopropanolamine, di-n-octanolamine, and tri-n-octanolamine. Among these, trialkylamines having 6 to 30 carbon atoms are more preferred, and tri-n-pentylamine or tri-n-octylamine is particularly preferred.

[0313] Examples of cyclic amines include heterocyclic compounds containing a nitrogen atom as a heteroatom. The heterocyclic compounds may be monocyclic (aliphatic monocyclic amines) or polycyclic (aliphatic polycyclic amines). Specific examples of the aliphatic monocyclic amine include piperidine and piperazine. The aliphatic polycyclic amine is preferably one having 6 to 10 carbon atoms, and specific examples thereof include 1,5-diazabicyclo[4.3.0]-5-nonene, 1,8-diazabicyclo[5.4.0]-7-undecene, hexamethylenetetramine, and 1,4-diazabicyclo[2.2.2]octane.

[0314] Other aliphatic amines include tris(2-methoxymethoxyethyl)amine, tris{2-(2-methoxyethoxy)ethyl}amine, tris{2-(2-methoxyethoxymethoxy)ethyl}amine, tris{2-(1-methoxyethoxy)ethyl}amine, tris{2-(1-ethoxyethoxy)ethyl}amine, tris{2-(1-ethoxypropoxy)ethyl}amine, tris[2-{2-(2-hydroxyethoxy)ethoxy}ethyl]amine, and triethanolamine triacetate, with triethanolamine triacetate being preferred.

[0315] Furthermore, an aromatic amine may be used as the component (D2). Examples of aromatic amines include 4-dimethylaminopyridine, pyrrole, indole, pyrazole, imidazole or derivatives thereof, tribenzylamine, 2,6-diisopropylaniline, N-tert-butoxycarbonylpyrrolidine, and 2,6-di-tert-butylpyridine.

[0316] The component (D2) may be used alone or in combination of two or more. When the resist composition contains the component (D2), the amount of the component (D2) within the resist composition is typically within a range from 0.01 to 5 parts by mass per 100 parts by mass of the component (A). By ensuring this range, the resist pattern shape and stability over time during storage can be improved.

[0317] <At least one compound (E) selected from the group consisting of organic carboxylic acids, phosphorus oxoacids and derivatives thereof> The resist composition of this embodiment may contain, as an optional component, at least one compound (E) selected from the group consisting of organic carboxylic acids, and phosphorus oxo acids and derivatives thereof (hereafter referred to as "component (E)") for the purposes of preventing sensitivity degradation and improving the resist pattern shape and stability over time after exposure. Specific examples of organic carboxylic acids include acetic acid, malonic acid, citric acid, malic acid, succinic acid, benzoic acid, and salicylic acid, with salicylic acid being preferred. Examples of phosphorus oxoacids include phosphoric acid, phosphonic acid, and phosphinic acid, with phosphonic acid being particularly preferred.

[0318] In the resist composition of this embodiment, the component (E) may be used either as a single type, or in combination of two or more types. When the resist composition contains the component (E), the amount of the component (E) per 100 parts by mass of the component (A) is preferably 0.01 to 5 parts by mass, and more preferably 0.05 to 3 parts by mass. By setting the amount within this range, lithography properties are further improved.

[0319] <Fluorine additive component (F)> The resist composition of this embodiment contains a fluorine additive component (hereafter referred to as "component (F)") as a hydrophobic resin. Component (F) is used to impart water repellency to the resist film, and when used as a resin separate from component (A), it can improve lithography properties.

[0320] ≪Fluorine-containing polymer compound (F0)≫ In this embodiment, the component (F) contains a fluorine-containing polymer compound (F0) (hereinafter also referred to as "component (F0)") having a structural unit (f0) derived from a compound represented by the following general formula (f0-1) (hereinafter also referred to as "compound (f0-1)").

[0321] <Constituent unit (f0)> The structural unit (f0) is a structural unit derived from a compound represented by the following general formula (f0-1).

[0322] [ka] [In the formula, W 1 is a polymerizable group-containing group. 00is an organic group having at least one hydroxy group as a substituent. 02 is a (l+1)-valent linking group. 01 is a group represented by the following general formula (f0-r-1) or (f0-r-2), and l is an integer of 1 or greater, as long as the valence allows.

[0323] [ka] [In the formula, Rf 011 Rf is a fluorinated alkyl group having 1 to 12 carbon atoms. 012 represents a hydrogen atom or an organic group having 1 to 12 carbon atoms which may have a fluorine atom. Xf represents a cyclic group having 4 or more fluorine atoms as substituents. * Lf 02 represents a bond with .]

[0324] In the general formula (f0-1), W 1 represents a polymerizable group-containing group. The "polymerizable group" is a group that enables a compound having a polymerizable group to be polymerized by radical polymerization or the like, and refers to a group that contains a multiple bond between carbon atoms, such as an ethylenic double bond. Examples of the polymerizable group include a vinyl group, an allyl group, an acryloyl group, a methacryloyl group, a fluorovinyl group, a difluorovinyl group, a trifluorovinyl group, a difluorotrifluoromethylvinyl group, a trifluoroallyl group, a perfluoroallyl group, a trifluoromethylacryloyl group, a nonylfluorobutylacryloyl group, a vinyl ether group, a fluorine-containing vinyl ether group, an allyl ether group, a fluorine-containing allyl ether group, a styryl group, a vinyl naphthyl group, a fluorine-containing styryl group, a fluorine-containing vinyl naphthyl group, a norbornyl group, a fluorine-containing norbornyl group, and a silyl group.

[0325] The polymerizable group-containing group may be a group composed only of a polymerizable group, or may be a group composed of a polymerizable group and a group other than the polymerizable group. Examples of the group other than the polymerizable group include a divalent hydrocarbon group which may have a substituent, and a divalent linking group containing a hetero atom. Examples of the polymerizable group-containing group include a group represented by the formula: C(R X11 )(R X12 )=C(R X13 )-Ya x0 In the above formula, R X11 , R X12 and R X13 each independently represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms; x0 represents a single bond or a divalent linking group. x0 Examples of the divalent linking group in the formula (Ya) include a divalent hydrocarbon group which may have a substituent, and a divalent linking group containing a hetero atom. x0 Examples of the divalent linking group in the formula include an ester bond (-C(=O)-O-), an oxycarbonyl group (-OC(=O)-), an ether bond (-O-), a linear or branched alkylene group, or a combination thereof. x0 is preferably a single bond, an ester bond (-C(=O)-O-), or an oxycarbonyl group (-OC(=O)-).

[0326] In the formula (f0-1), Lf 00 The organic group in is not particularly limited as long as it has at least one hydroxy group as a substituent, but examples thereof include divalent hydrocarbon groups which may have a substituent. From the viewpoint of increasing sensitivity and improving LWR, Lf 00 is preferably an organic group having at least one hydroxy group and at least one iodine atom as substituents. Lf 00 The number of hydroxy groups in the organic group is not particularly limited, but is preferably 1 or 2.

[0327] Optionally substituted divalent hydrocarbon groups: The divalent hydrocarbon group which may have a substituent may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group.

[0328] Aliphatic hydrocarbon groups The aliphatic hydrocarbon group refers to a hydrocarbon group that does not have aromaticity. The aliphatic hydrocarbon group may be saturated or unsaturated, and is usually preferably saturated. Examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, and an aliphatic hydrocarbon group containing a ring in its structure.

[0329] Linear or branched aliphatic hydrocarbon groups The linear aliphatic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 6 carbon atoms, even more preferably 1 to 4 carbon atoms, and most preferably 1 to 3 carbon atoms. As the straight-chain aliphatic hydrocarbon group, a straight-chain alkylene group is preferred, and specific examples include a methylene group [-CH2-], an ethylene group [-(CH2)2-], a trimethylene group [-(CH2)3-], a tetramethylene group [-(CH2)4-], and a pentamethylene group [-(CH2)5-]. The branched aliphatic hydrocarbon group preferably has 2 to 10 carbon atoms, more preferably 3 to 6 carbon atoms, even more preferably 3 or 4 carbon atoms, and most preferably 3 carbon atoms. The branched aliphatic hydrocarbon group is preferably a branched alkylene group, and specific examples thereof include alkyl alkylene groups such as alkylmethylene groups such as -CH(CH3)-, -CH(CH2CH3)-, -C(CH3)2-, -C(CH3)(CH2CH3)-, -C(CH3)(CH2CH2CH3)-, and -C(CH2CH3)2-; alkylethylene groups such as -CH(CH3)CH2-, -CH(CH3)CH(CH3)-, -C(CH3)2CH2-, -CH(CH2CH3)CH2-, and -C(CH2CH3)2-CH2-; alkyl trimethylene groups such as -CH(CH3)CH2CH2- and -CH2CH(CH3)CH2-; and alkyl tetramethylene groups such as -CH(CH3)CH2CH2CH2- and -CH2CH(CH3)CH2CH2-. The alkyl group in the alkylalkylene group is preferably a linear alkyl group having 1 to 5 carbon atoms.

[0330] The linear or branched aliphatic hydrocarbon group may or may not have a substituent, such as a hydroxy group, a fluorine atom, a fluorinated alkyl group having 1 to 5 carbon atoms and substituted with a fluorine atom, or a carbonyl group.

[0331] Aliphatic hydrocarbon groups containing rings in the structure Examples of the aliphatic hydrocarbon group containing a ring in its structure include a cyclic aliphatic hydrocarbon group (a group in which two hydrogen atoms have been removed from an aliphatic hydrocarbon ring) which may contain a substituent containing a heteroatom in the ring structure, a group in which the cyclic aliphatic hydrocarbon group is bonded to the end of a straight-chain or branched-chain aliphatic hydrocarbon group, and a group in which the cyclic aliphatic hydrocarbon group is interposed in the middle of a straight-chain or branched-chain aliphatic hydrocarbon group. Examples of the straight-chain or branched-chain aliphatic hydrocarbon group include the same as those described above. The cyclic aliphatic hydrocarbon group preferably has 3 to 20 carbon atoms, more preferably 3 to 12 carbon atoms. The cyclic aliphatic hydrocarbon group may be a polycyclic group or a monocyclic group. The monocyclic alicyclic hydrocarbon group is preferably a group in which two hydrogen atoms have been removed from a monocycloalkane. The monocycloalkane is preferably one having 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane. The polycyclic alicyclic hydrocarbon group is preferably a group in which two hydrogen atoms have been removed from a polycycloalkane, and specific examples thereof include adamantane, norbornane, isobornane, and tricyclo[5.2.1.0]. 2,6 ]decane, tetracyclododecane, and the like.

[0332] The cyclic aliphatic hydrocarbon group may or may not have a substituent, such as an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, or a carbonyl group. The alkyl group as the substituent is preferably an alkyl group having 1 to 5 carbon atoms, and more preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group. The alkoxy group as the substituent is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, or a tert-butoxy group, and still more preferably a methoxy group or an ethoxy group. The halogen atom as the substituent is preferably a fluorine atom. Examples of the halogenated alkyl group as the substituent include groups in which some or all of the hydrogen atoms of the alkyl group have been substituted with the halogen atoms. In the cyclic aliphatic hydrocarbon group, some of the carbon atoms constituting the ring structure may be substituted with a substituent containing a heteroatom, and the heteroatom-containing substituent is preferably -O-, -C(=O)-O-, -S-, -S(=O)2-, or -S(=O)2-O-.

[0333] Aromatic hydrocarbon groups The aromatic hydrocarbon group is a hydrocarbon group having at least one aromatic ring. The aromatic ring is not particularly limited as long as it is a cyclic conjugated system having 4n+2 π electrons, and may be monocyclic or polycyclic. The aromatic ring preferably has 5 to 30 carbon atoms, more preferably 5 to 20 carbon atoms, still more preferably 6 to 15 carbon atoms, and particularly preferably 6 to 12 carbon atoms. However, this number of carbon atoms does not include the number of carbon atoms in the substituent. Specific examples of the aromatic ring include aromatic hydrocarbon rings such as benzene, naphthalene, anthracene, and phenanthrene; and aromatic heterocycles in which some of the carbon atoms constituting the aromatic hydrocarbon ring are substituted with heteroatoms. Examples of heteroatoms in the aromatic heterocycle include oxygen atoms, sulfur atoms, and nitrogen atoms. Specific examples of the aromatic heterocycle include pyridine rings and thiophene rings. Specific examples of the aromatic hydrocarbon group include groups in which two hydrogen atoms have been removed from the aromatic hydrocarbon ring or aromatic heterocycle (arylene groups or heteroarylene groups); groups in which two hydrogen atoms have been removed from an aromatic compound containing two or more aromatic rings (e.g., biphenyl, fluorene, etc.); and groups in which one hydrogen atom of a group in which one hydrogen atom has been removed from the aromatic hydrocarbon ring or aromatic heterocycle (aryl group or heteroaryl group) has been substituted with an alkylene group (e.g., groups in which one hydrogen atom has been further removed from the aryl group in an arylalkyl group such as a benzyl group, phenethyl group, 1-naphthylmethyl group, 2-naphthylmethyl group, 1-naphthylethyl group, or 2-naphthylethyl group). The alkylene group bonded to the aryl group or heteroaryl group preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.

[0334] The aromatic hydrocarbon group may have a hydrogen atom substituted with a substituent. For example, a hydrogen atom bonded to an aromatic ring in the aromatic hydrocarbon group may be substituted with a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, and a hydroxy group. The alkyl group as the substituent is preferably an alkyl group having 1 to 5 carbon atoms, and more preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group. Examples of the alkoxy group, halogen atom and halogenated alkyl group as the substituent include those exemplified as the substituent substituting the hydrogen atom of the cyclic aliphatic hydrocarbon group.

[0335] Among them, Lf 00 As the aromatic group, an aromatic group having at least one hydroxy group as a substituent is preferred, and an aromatic group having at least one hydroxy group and at least one iodine atom as a substituent is more preferred.

[0336] In the formula (f0-1), Lf 02The (l+1)-valent linking group in the formula (Lf) is not particularly limited, but is preferably an organic group containing a carbonyloxy group, and 02 -01) is more preferred.

[0337] [ka] [In the formula, *1 represents Lf in the formula (f0-1) 00 Lf is the bond that bonds with 21 *2 represents a hydrocarbon group which may have a substituent. 01 ) l n1 is an integer equal to or greater than 1, as long as valence allows.

[0338] The formula (Lf 02 -01)Medium, Lf 21 The hydrocarbon group which may have a substituent in the formula (I) may be a linear hydrocarbon group, a branched hydrocarbon group, a cyclic hydrocarbon group, or a combination thereof. The formula (Lf 02 -01), n1 is preferably an integer of 1 to 3, and more preferably 1 or 2.

[0339] The formula (Lf 02 As the group represented by the general formula (Lf 02 -01-1)~(Lf 02 -01-3) is preferred.

[0340] [ka] [In the formula, *1 represents Lf in the formula (f0-1) 00 RLf is a bond that bonds to 2 is a linear or branched alkyl group or a cycloalkyl group. Z is an aliphatic ring. *2 is the (Rf 01 ) l n1 is an integer equal to or greater than 1, as long as valence allows.

[0341] The formula (Lf 02 -01-1) Medium, RLf 2 The linear or branched alkyl group in is preferably a linear alkyl group having 1 to 5 carbon atoms or a branched alkyl group having 2 to 5 carbon atoms, more preferably a methyl group or an isobutyl group. The formula (Lf 02 -01-2) and (Lf 02 In -01-3), the aliphatic ring in Z is preferably a norbornene ring or a cyclohexane ring.

[0342] In the formula (f0-1), Rf 01 is a group represented by the general formula (f0-r-1) or (f0-r-2).

[0343] In the formula (f0-r-1), Rf 011 The fluorinated alkyl group having 1 to 12 carbon atoms is a group in which some or all of the hydrogen atoms of an alkyl group having 1 to 12 carbon atoms have been substituted with fluorine atoms. The alkyl group may be linear or branched. Specific examples of linear fluorinated alkyl groups having 1 to 12 carbon atoms include methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, and dodecyl groups in which some or all of the hydrogen atoms have been substituted with fluorine atoms. Specific examples of branched fluorinated alkyl groups having 1 to 12 carbon atoms include 1-methylethyl, 1,1-dimethylethyl, 1-methylpropyl, 2-methylpropyl, 1-methylbutyl, 2-methylbutyl, 3-methylbutyl, 1-ethylbutyl, 2-ethylbutyl, 1-methylpentyl, 2-methylpentyl, 3-methylpentyl, and 4-methylpentyl groups in which some or all of the hydrogen atoms have been substituted with fluorine atoms.

[0344] Rf 011 Of the above, the fluorinated alkyl group having 1 to 12 carbon atoms is more preferably a fluorinated alkyl group having 1 to 5 carbon atoms, and specifically, a trifluoromethyl group is particularly preferred.

[0345] In the formula (f0-r-1), Rf 012 In the above, examples of the organic group having 1 to 12 carbon atoms which may have a fluorine atom include monovalent hydrocarbon groups having 1 to 12 carbon atoms which may have a fluorine atom. Examples of the hydrocarbon group include a linear or branched alkyl group, and a cyclic hydrocarbon group. Specific examples of the linear alkyl group include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, an undecyl group, and a dodecyl group. Specific examples of the branched alkyl group include a 1-methylethyl group, a 1,1-dimethylethyl group, a 1-methylpropyl group, a 2-methylpropyl group, a 1-methylbutyl group, a 2-methylbutyl group, a 3-methylbutyl group, a 1-ethylbutyl group, a 2-ethylbutyl group, a 1-methylpentyl group, a 2-methylpentyl group, a 3-methylpentyl group, and a 4-methylpentyl group.

[0346] Rf 012 When is a cyclic hydrocarbon group, the hydrocarbon group may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group, and may be a polycyclic group or a monocyclic group. The monocyclic aliphatic hydrocarbon group is preferably a group in which one hydrogen atom has been removed from a monocycloalkane. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples include cyclopentane and cyclohexane. The aliphatic hydrocarbon group that is a polycyclic group is preferably a group in which one hydrogen atom has been removed from a polycycloalkane, and the polycycloalkane preferably has 7 to 12 carbon atoms, and specific examples thereof include adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane.

[0347] Rf 012When the cyclic hydrocarbon group is an aromatic hydrocarbon group, the aromatic hydrocarbon group is a hydrocarbon group having at least one aromatic ring. Specific examples of the aromatic hydrocarbon group include groups in which one hydrogen atom has been removed from an aromatic hydrocarbon ring such as benzene, naphthalene, anthracene, phenanthrene, biphenyl, and fluorene.

[0348] Rf 012 The organic group having 1 to 12 carbon atoms may have a substituent other than a fluorine atom, such as a hydroxy group, a carboxy group, a halogen atom (such as a chlorine atom or a bromine atom), an alkoxy group (such as a methoxy group, an ethoxy group, a propoxy group or a butoxy group), or an alkyloxycarbonyl group.

[0349] Rf 012 is preferably a fluorinated alkyl group having 1 to 12 carbon atoms, more preferably a fluorinated alkyl group having 1 to 5 carbon atoms, and even more preferably a trifluoromethyl group.

[0350] In the formula (f0-r-2), Xf is a cyclic group having four or more fluorine atoms as a substituent. The cyclic group may be an aliphatic ring or an aromatic ring, and may be polycyclic or monocyclic. The monocyclic aliphatic ring is preferably a group in which two hydrogen atoms have been removed from a monocycloalkane. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples include cyclopentane and cyclohexane. The polycyclic aliphatic ring is preferably a group in which two hydrogen atoms have been removed from a polycycloalkane, and the polycycloalkane preferably has 7 to 12 carbon atoms, and specific examples thereof include adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane.

[0351] Examples of the aromatic ring in Xf include a benzene ring, a naphthalene ring, an anthracene ring, a phenanthrene ring, a biphenyl ring, and a fluorene ring.

[0352] The cyclic group in Xf is preferably an aromatic ring, more preferably a benzene ring.

[0353] The substituent of the cyclic group in Xf includes a fluorine atom, a fluorinated alkyl group, etc. 02 The substituents on the cyclic group in the formula (I) contain a total of four or more fluorine atoms. For example, Rf 02 The cyclic group in may have four or more fluorine atoms as substituents, may have two or more fluorinated alkyl groups containing two or more fluorine atoms as substituents, or may have both fluorine atoms and fluorinated alkyl groups as substituents, and the number of fluorine atoms contained in the substituents may be four or more.

[0354] The substituent on the cyclic group in Xf is preferably a fluorine atom or a trifluoromethyl group, more preferably a fluorine atom.

[0355] In the formula (f0-1), l is preferably an integer of 1 to 3, and more preferably 1 or 2.

[0356] The structural unit (f0) is preferably a structural unit derived from a compound represented by the following general formula (f0-1-1).

[0357] [ka] [In the formula, W 1 is a polymerizable group-containing group. Ar1 and Ar2 are each independently an aromatic group. Lf 01 is a divalent linking group. 02 is a (l+1)-valent linking group. k is 0 or 1. p and q are each independently an integer of 0 or greater, as far as valence allows, provided that p+q≧1. m and n are each independently an integer of 0 or greater, as far as valence allows. Rf 01 is a group represented by the following general formula (f0-r-1) or (f0-r-2), and l is an integer of 1 or greater, as long as the valence allows.

[0358] [ka] [In the formula, Rf 011 Rf is a fluorinated alkyl group having 1 to 12 carbon atoms. 012 represents a hydrogen atom or an organic group having 1 to 12 carbon atoms which may have a fluorine atom. Xf represents a cyclic group having 4 or more fluorine atoms as substituents. * Lf 02 represents a bond with .]

[0359] In the formula (f0-1-1), W 1 The polymerizable group-containing group in the formula (f0-1) is W 1 The polymerizable group-containing group is the same as that in W. 1 As the above formula C(R X11 )(R X12 )=C(R X13 )-C(=O)-O-, a group represented by the above formula C(R X14 )(R X15 )=C(R X16 )-Ar x11 a group represented by —C(═O)—O—, X17 )(R X18 )=C(R X19 )-, or a group represented by the above formula C(R X20 )(R X21 )=C(R X22 )-C(=O)-OC(Rf x11 )(Rf x12 )- is preferred, and the group represented by the above formula C(R X11 )(R X12 )=C(R X13 )-C(=O)-O-, a group represented by the above formula C(R X14 )(R X15 )=C(R X16 )-Ar x11 a group represented by —C(═O)—O—, or the above formula C(R X17 )(R X18 )=C(R X19 )- is more preferred. In the above formula, R X11 ~R X22are each independently a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms. x11 and Rf x12 are each independently a fluorinated alkyl group having 1 to 5 carbon atoms.

[0360] In the formula (f0-1-1), Lf 02 , Rf 01 and l is Lf in the formula (f0-1). 02 , Rf 01 and l.

[0361] In the formula (f0-1-1), examples of the aromatic groups in Ar1 and Ar2 include aromatic hydrocarbon rings such as benzene, naphthalene, anthracene, and phenanthrene; and aromatic heterocycles in which some of the carbon atoms constituting the aromatic hydrocarbon ring are substituted with heteroatoms. Examples of heteroatoms in the aromatic heterocycles include oxygen atoms, sulfur atoms, and nitrogen atoms. Specific examples of aromatic heterocycles include pyridine rings and thiophene rings. Specific examples of the aromatic hydrocarbon group include groups in which two hydrogen atoms have been removed from the aromatic hydrocarbon ring or aromatic heterocycle (arylene groups or heteroarylene groups); groups in which two hydrogen atoms have been removed from an aromatic compound containing two or more aromatic rings (e.g., biphenyl, fluorene, etc.); and groups in which one hydrogen atom of a group in which one hydrogen atom has been removed from the aromatic hydrocarbon ring or aromatic heterocycle (aryl group or heteroaryl group) has been substituted with an alkylene group (e.g., groups in which one hydrogen atom has been further removed from the aryl group in an arylalkyl group such as a benzyl group, phenethyl group, 1-naphthylmethyl group, 2-naphthylmethyl group, 1-naphthylethyl group, or 2-naphthylethyl group). The alkylene group bonded to the aryl group or heteroaryl group preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.

[0362] In the aromatic groups of Ar1 and Ar2, a hydrogen atom of the aromatic hydrocarbon group may be substituted with a substituent. For example, a hydrogen atom bonded to an aromatic ring in the aromatic hydrocarbon group may be substituted with a substituent. Examples of the substituent include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, and a hydroxy group. As the substituent that the aromatic group in Ar1 and Ar2 may have, from the viewpoint of increasing sensitivity, a halogen atom is preferred, and an iodine atom is more preferred.

[0363] In the formula (f0-1-1), Lf 01 As the divalent linking group in L 01 -, -NR L 01 Examples of the alkyl group include -C(=O)-, -C(=O)-O-, -OC(=O)-, -O-, -C(=O)-, -NH-, -SONH-, a linear or branched aliphatic hydrocarbon group, or a combination thereof. L 01 is a hydrogen atom or an alkyl group having 1 to 5 carbon atoms. Among them, Lf 01 As the divalent linking group in *1 -C(=O)-O- *2 or *1 -O-Lf 011 -C(=O)- *2 In the formula, *1 is a bond bonding to Ar1 in formula (f0-1-1), and *2 is a bond bonding to Ar2 in formula (f0-1-1). 011 is an alkylene group having 1 to 5 carbon atoms, preferably a methylene group.

[0364] In the formula (f0-1-1), p+q is preferably 1 or 2. In the formula (f0-1-1), m+n≧1 is preferable, m+n is more preferably an integer of 1 to 4, and m+n is still more preferably an integer of 2 to 4.

[0365] From the viewpoint of the balance of hydrophilicity and hydrophobicity, in the formula (f0-1-1), k is 0, Ar2 is a benzene ring, n, q, and l are 1, Lf 02 but *1 -C(=O)-O- *2 , Rf 01 is preferably a group represented by the general formula (f0-r-1).

[0366] Specific examples of the compound (f0-1) are shown below.

[0367] [ka]

[0368] [ka]

[0369] [ka]

[0370] [ka]

[0371] [ka]

[0372] [ka]

[0373] [ka]

[0374] [ka]

[0375] [ka]

[0376] [ka]

[0377] [ka]

[0378] The structural unit (f0) contained in the component (F0) may be of one type, or may be of two or more types. Within the component (F0), the proportion of the structural unit (f0) relative to the total (100 mol%) of all structural units constituting the component (F0) is preferably 40 to 95 mol%, more preferably 45 to 90 mol%, and even more preferably 50 to 85 mol%. From the viewpoint of defect characteristics after development, the proportion of the structural unit (f0) is preferably 70 mol % or more. By ensuring that the proportion of the structural unit (f0) is at least as large as the lower limit of the above-mentioned preferred range, it is easy to increase sensitivity, improve fine resolution, and reduce LWR. On the other hand, by ensuring that the proportion of the structural unit (f0) is at most the upper limit of the above-mentioned preferred range, it is easy to improve the solubility of the resist composition in a developer and form a pattern with good defect characteristics after development.

[0379] The component (F0) may contain other structural units in addition to the structural unit (f0) described above, as necessary. Examples of other structural units include a structural unit (f1) containing an acid-decomposable group whose polarity increases when acted upon by an acid; a structural unit (f2) containing a lactone-containing cyclic group; and a structural unit (f10) represented by the general formula (a10-1) above.

[0380] Building block (f1): The structural unit (f1) is a structural unit containing an acid-decomposable group whose polarity increases when acted upon by an acid, and is the same as the structural unit (a1) within the component (A1) described above. Of these, the structural unit (f1) is preferably a structural unit represented by the general formula (a1-1), (a1-2), or (a1-3).

[0381] The structural unit (f1) contained in the component (F0) may be of one type, or may be of two or more types. The component (F0) may or may not contain the structural unit (f1), although it is preferable for the component (F0) to contain the structural unit (f1). When the component (F0) contains the structural unit (f1), the proportion of the structural unit (f1) in the component (F0) is preferably 1 to 40 mol %, more preferably 5 to 35 mol %, and even more preferably 10 to 30 mol %, relative to the total (100 mol %) of all structural units constituting the component (F0). By ensuring that the proportion of the structural unit (f1) is at least as large as the lower limit of the aforementioned preferred range, lithography properties such as sensitivity, resolution, and roughness can be improved. On the other hand, by ensuring that the proportion of the structural unit (f1) is at most the upper limit of the aforementioned preferred range, a balance with other structural units can be achieved, and various lithography properties can be improved.

[0382] Building block (f2): The structural unit (f2) is a structural unit that contains a lactone-containing cyclic group, and is the same as the structural unit (a2) within the component (A1). Of these, the structural unit (f2) is preferably a structural unit represented by the general formula (a2-1) shown above.

[0383] The structural unit (f2) contained in the component (F0) may be of one type, or may be of two or more types. The component (F0) may or may not contain the structural unit (f2), although it is preferable for the component (F0) to contain the structural unit (f2). When the component (F0) contains the structural unit (f2), the proportion of the structural unit (f2) in the component (F0) is preferably 1 to 60 mol %, more preferably 5 to 55 mol %, and even more preferably 10 to 50 mol %, relative to the total (100 mol %) of all structural units constituting the component (F0). By ensuring that the proportion of the structural unit (f2) is at least as large as the lower limit of the above-mentioned preferred range, the solubility of the resist composition in a developer is likely to be improved. On the other hand, by ensuring that the proportion of the structural unit (f2) is no greater than the upper limit of the above-mentioned preferred range, a balance with other structural units can be achieved, and various lithography properties are likely to be excellent.

[0384] Unit (f10): The structural unit (f10) is a structural unit represented by the aforementioned general formula (a10-1), and is the same as the structural unit (a10) within the aforementioned component (A1).

[0385] The structural unit (f10) contained in the component (F0) may be of one type, or may be of two or more types. The component (F0) may or may not contain the structural unit (f10), although it is preferable for the component (F0) to contain the structural unit (f10). When the component (F0) contains the structural unit (f10), the proportion of the structural unit (f10) in the component (F0) is preferably 1 to 60 mol %, more preferably 3 to 55 mol %, and even more preferably 5 to 50 mol %, based on the total (100 mol %) of all structural units constituting the component (F0). By ensuring that the proportion of the structural unit (f10) is at least as large as the lower limit of the aforementioned preferred range, sensitivity is likely to be further improved. On the other hand, by ensuring that the proportion of the structural unit (f10) is no greater than the upper limit of the aforementioned preferred range, it is easier to achieve a balance with other structural units.

[0386] Examples of the component (F0) include polymeric compounds that include a repeating structure of the structural unit (f0) and the structural unit (f2), polymeric compounds that include a repeating structure of the structural unit (f0) and the structural unit (f1), polymeric compounds that include a repeating structure of the structural unit (f0) and the structural unit (f10), polymeric compounds that include a repeating structure of the structural unit (f0), the structural unit (f2), and the structural unit (f10), and polymeric compounds that include a repeating structure of the structural unit (f0), the structural unit (f1), and the structural unit (f10).

[0387] The component (F0) can be produced by dissolving the monomers that derive each structural unit in a polymerization solvent, and then adding a radical polymerization initiator such as azobisisobutyronitrile (AIBN) or dimethyl azobisisobutyrate (e.g., V-601) to the solution and polymerizing the resulting mixture. Alternatively, the (F0) component can be produced by dissolving a monomer that derives the structural unit (f0) and a monomer that derives any structural unit (for example, the structural unit (f10)) in a polymerization solvent, adding a radical polymerization initiator such as those described above to polymerize, and then carrying out a deprotection reaction.

[0388] The weight average molecular weight (Mw) of the component (F0) (based on polystyrene standards measured by gel permeation chromatography (GPC)) is not particularly limited, but is preferably 1,000 to 50,000, more preferably 4,000 to 35,000, and even more preferably 4,000 to 20,000. From the viewpoint of defect characteristics after development, the weight average molecular weight (Mw) of the component (F0) is preferably 7,000 to 15,000, more preferably 8,000 to 14,000, and even more preferably 9,000 to 12,000. The dispersity (Mw / Mn) of the component (F0) is not particularly limited, but is preferably from 1.0 to 4.0, more preferably from 1.0 to 3.0, and particularly preferably from 1.0 to 2.0, where Mn represents the number average molecular weight.

[0389] The resist composition of this embodiment may also contain, as the component (F), a fluorine additive component that is decomposable in an alkaline developer and does not fall under the category of the component (F0). The proportion of the component (F0) in the component (F) is preferably 25% by mass or more, more preferably 50% by mass or more, and even more preferably 75% by mass or more, relative to the total mass of the component (F), and may even be 100% by mass.

[0390] In the resist composition of this embodiment, the component (F) may be used alone, or in combination of two or more different compounds. In the resist composition of this embodiment, the amount of the component (F0) relative to 100 parts by mass of the component (A) is preferably 0.1 to 30 parts by mass, more preferably 0.3 to 25 parts by mass, even more preferably 0.5 to 20 parts by mass, and particularly preferably 0.9 to 17 parts by mass. From the viewpoint of defect characteristics after development, the amount of the component (F0) relative to 100 parts by mass of the component (A) is preferably 1 to 14 parts by mass, more preferably 3 to 13 parts by mass, and even more preferably 4 to 12 parts by mass. When the content of the component (F0) is at least as large as the lower limit of the above-mentioned range, it is easy to increase sensitivity and reduce LWR. On the other hand, when the content of the component (F0) is at most the upper limit of the above-mentioned preferred range, it is easy to improve the solubility of the resist composition in a developer and to form a pattern with good defect characteristics after development.

[0391] <Organic solvent component (S)> The resist composition of this embodiment can be produced by dissolving the resist materials in an organic solvent component (hereafter referred to as “component (S)”). In the resist composition of this embodiment, the component (S) may be used alone or as a mixed solvent of two or more types, with propylene glycol monomethyl ether acetate (PGMEA), propylene glycol monomethyl ether (PGME), γ-butyrolactone, ethyl lactate (EL), and cyclohexanone being preferred.

[0392] Furthermore, a mixed solvent of PGMEA and a polar solvent is also preferred as component (S), and the blending ratio (mass ratio) may be appropriately determined taking into consideration the compatibility between PGMEA and the polar solvent, etc. The component (S) is also preferably a mixed solvent of at least one selected from PGMEA and EL with γ-butyrolactone, in which case the mass ratio of the former to the latter is preferably 70:30 to 95:5. There are no particular restrictions on the amount of component (S) used, and it is set appropriately depending on the coating film thickness so as to provide a concentration that allows application to a substrate, etc. Generally, the component (S) is used so that the solids concentration of the resist composition falls within the range of 0.1 to 20 mass %, and preferably 0.2 to 15 mass %.

[0393] The resist composition of this embodiment may be prepared by dissolving the resist material in component (S) and then removing impurities using a polyimide porous film, a polyamideimide porous film, or the like. For example, the resist composition may be filtered using a filter made of a polyimide porous film, a filter made of a polyamideimide porous film, or a filter made of a polyimide porous film and a polyamideimide porous film. Examples of such polyimide porous films and polyamideimide porous films include those described in JP 2016-155121 A.

[0394] The resist composition of this embodiment described above contains a resin component (A1) and a fluorine-containing polymeric compound (F0). The component (F0) has a structural unit (f0) derived from a compound represented by general formula (f0-1). The structural unit (f0) is an organic group Lf having at least one hydroxy group as a substituent. 00 and fluorine alcohol structure (Rf 01 This improves the hydrophilicity of the resist composition and improves its solubility in the developer, which is thought to result in higher sensitivity and contribute to improvements in fine resolution, LWR, and development defect characteristics. The structural unit (f0) is an organic group Lf 00 The structural unit (f0) may have an iodine atom as a substituent therein. The iodine atom has a high absorption of EUV light with a wavelength of 13.5 nm. Therefore, when the structural unit (f0) is an organic group Lf 00 When the structural unit (f0) has an iodine atom as a substituent, secondary electrons are likely to be generated during exposure. 00 It is thought that secondary electrons generated from iodine atoms present in the component (A1) promote decomposition of the cation moieties of components that generate acid upon exposure, such as structural unit (a5) in component (A1) and component (B), thereby achieving higher sensitivity and improving resolution. Generally, when a component containing an iodine atom is introduced into a resist composition, the hydrophobicity of the resist composition increases, and the solubility in a developer tends to decrease. However, the structural unit (f0) is a compound containing an iodine atom. 00The structural unit (f0) has a hydroxy group therein and also contains a fluorine alcohol structure. Therefore, even when the structural unit (f0) has an iodine atom as a substituent, the hydrophilicity of the resist composition is improved and the solubility in a developer is improved, which is presumably responsible for improving LWR and development defect characteristics. It is presumed that the combined effects described above enable the resist composition of this embodiment to achieve high sensitivity, improved fine resolution, reduced LWR, and capable of forming a resist pattern with favorable defect characteristics after development.

[0395] (Method for forming a resist pattern) A method for forming a resist pattern according to a second aspect of the present invention is a method comprising the steps of forming a resist film on a support using the resist composition according to the first aspect of the present invention, exposing the resist film to light, and developing the exposed resist film to form a resist pattern. One embodiment of the resist pattern forming method is, for example, a resist pattern forming method carried out as follows.

[0396] First, the resist composition of the above-described embodiment is applied onto a support using a spinner or the like, and then baked (post-apply bake (PAB)) at a temperature of, for example, 80 to 150°C for 40 to 120 seconds, preferably 60 to 90 seconds, to form a resist film. Next, the resist film is selectively exposed using an exposure device such as an electron beam lithography device or an ArF exposure device, either through a mask (mask pattern) on which a predetermined pattern has been formed, or by direct irradiation with an electron beam without using a mask pattern, and then baked (post-exposure bake (PEB)) for 40 to 120 seconds, preferably 60 to 90 seconds, at a temperature of 80 to 150°C. Next, the resist film is developed using an alkaline developer in the case of an alkaline development process, or a developer containing an organic solvent (organic developer) in the case of a solvent development process.

[0397] After the development process, a rinse process is preferably carried out. In the case of an alkaline development process, the rinse process is preferably a water rinse using pure water, and in the case of a solvent development process, it is preferable to use a rinse solution containing an organic solvent. In the case of a solvent development process, the developing treatment or rinsing treatment may be followed by a treatment of removing the developing solution or rinsing solution adhering to the pattern using a supercritical fluid. After the development treatment or rinsing treatment, the film is dried. In some cases, a baking treatment (post-baking) may be performed after the development treatment.

[0398] The support is not particularly limited, and conventionally known supports can be used, such as substrates for electronic components and those on which a predetermined wiring pattern is formed. More specifically, examples include silicon wafers, substrates made of metals such as copper, chromium, iron, and aluminum, and glass substrates. Materials that can be used for the wiring pattern include copper, aluminum, nickel, and gold.

[0399] The wavelength used for exposure is not particularly limited, and radiation such as ArF excimer laser, KrF excimer laser, F2 excimer laser, EUV (extreme ultraviolet), VUV (vacuum ultraviolet), EB (electron beam), X-rays, and soft X-rays can be used. The method for forming a resist pattern of this embodiment is particularly useful for a method in which the resist film is exposed to EUV (extreme ultraviolet) or EB (electron beam) in the step of exposing the resist film.

[0400] The exposure method for the resist film may be a normal exposure (dry exposure) carried out in air or an inert gas such as nitrogen, or may be liquid immersion lithography. Immersion exposure is an exposure method in which the space between the resist film and the lowest lens of the exposure device is filled with a solvent (immersion medium) that has a refractive index greater than that of air, and then exposure (immersion exposure) is performed in that state. The immersion medium is preferably a solvent having a refractive index greater than that of air and less than that of the resist film to be exposed, such as water, a fluorine-based inert liquid, a silicon-based solvent, or a hydrocarbon-based solvent. As the immersion medium, water is preferably used.

[0401] An example of an alkaline developer used in the development treatment in the alkaline development process is a 0.1 to 10 mass % aqueous solution of tetramethylammonium hydroxide (TMAH). The organic solvent contained in the organic developer used in the development treatment in the solvent development process may be any organic solvent capable of dissolving component (A) (component (A) before exposure), and may be appropriately selected from known organic solvents. Specific examples include polar solvents such as ketone solvents, ester solvents, alcohol solvents, nitrile solvents, amide solvents, and ether solvents, as well as hydrocarbon solvents.

[0402] Examples of ester-based solvents include methyl acetate, butyl acetate, ethyl acetate, isopropyl acetate, pentyl acetate, isopentyl acetate, amyl acetate, propylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol monobutyl ether acetate, diethylene glycol monoethyl ether acetate, ethyl-3-ethoxypropionate, 3-methoxybutyl acetate, 3-methyl-3-methoxybutyl acetate, methyl formate, ethyl formate, butyl formate, propyl formate, ethyl lactate, butyl lactate, propyl lactate, butyl butanoate, methyl 2-hydroxyisobutyrate, isoamyl acetate, isobutyl isobutyrate, and butyl propionate.

[0403] Examples of nitrile solvents include acetonitrile, propionitrile, valeronitrile, and butyronitrile.

[0404] The organic developer may contain known additives as needed. Examples of such additives include surfactants. The surfactants are not particularly limited, but may include, for example, ionic or nonionic fluorine-based and / or silicon-based surfactants.

[0405] The development process can be carried out by a known development method, such as a method of immersing the support in a developer for a certain period of time (dip method), a method of piling up the developer on the surface of the support by surface tension and leaving it standing for a certain period of time (puddle method), a method of spraying the developer onto the surface of the support (spray method), or a method of continuously applying the developer while scanning a developer application nozzle at a constant speed onto a support rotating at a constant speed (dynamic dispense method).

[0406] The organic solvent contained in the rinse solution used in the rinsing treatment after development in the solvent development process can be selected appropriately from the organic solvents listed above as organic solvents used in the organic developer, so long as it does not easily dissolve the resist pattern. Typically, at least one solvent selected from hydrocarbon solvents, ketone solvents, ester solvents, alcohol solvents, amide solvents, and ether solvents is used. These organic solvents may be used alone or in combination of two or more, and may be used in combination with other organic solvents or water.

[0407] The rinse treatment (cleaning treatment) using a rinse solution can be carried out by a known rinse method, such as a method of continuously applying the rinse solution onto a support rotating at a constant speed (spin coating method), a method of immersing the support in the rinse solution for a certain period of time (dipping method), or a method of spraying the rinse solution onto the surface of the support (spray method).

[0408] According to the method of forming a resist pattern of the present embodiment as described above, the resist composition described above is used, thereby enabling the formation of a resist pattern which has high sensitivity, is excellent in lithography properties such as resolution and roughness, and has reduced pattern defects after development.

[0409] The resist composition of the above-described embodiment and the various materials used in the pattern formation method of the above-described embodiment (e.g., resist solvent, developer, rinse, anti-reflective coating composition, top coat composition, etc.) preferably do not contain impurities such as metals, halogen-containing metal salts, acids, alkalis, or components containing sulfur or phosphorus atoms. Examples of metal-containing impurities include Na, K, Ca, Fe, Cu, Mn, Mg, Al, Cr, Ni, Zn, Ag, Sn, Pb, Li, and salts thereof. The content of impurities contained in these materials is preferably 200 ppb or less, more preferably 1 ppb or less, even more preferably 100 ppt (parts per trillion) or less, particularly preferably 10 ppt or less, and most preferably substantially free (below the detection limit of the measuring device).

[0410] (Fluorine-containing polymer compound) The fluorine-containing polymer compound of this embodiment has a structural unit (f0) derived from a compound represented by the following general formula (f0-1).

[0411] [ka] [In the formula, W 1 is a polymerizable group-containing group. 00 is an organic group having at least one hydroxy group as a substituent. 02 is a (l+1)-valent linking group. 01 is a group represented by the following general formula (f0-r-1) or (f0-r-2), and l is an integer of 1 or greater, as long as the valence allows.

[0412] [ka] [In the formula, Rf 011 Rf is a fluorinated alkyl group having 1 to 12 carbon atoms. 012represents a hydrogen atom or an organic group having 1 to 12 carbon atoms which may have a fluorine atom. Xf represents a cyclic group having 4 or more fluorine atoms as substituents. * Lf 02 represents a bond with .]

[0413] The fluorine-containing polymeric compound of this embodiment is the same as the component (F0) of the resist composition according to the first aspect. The fluorine-containing polymeric compound of this embodiment is useful as a fluorine additive component used in a resist composition.

[0414] (compound) The compound of this embodiment is represented by the following general formula (f0-1).

[0415] [ka] [In the formula, W 1 is a polymerizable group-containing group. 00 is an organic group having at least one hydroxy group as a substituent. 02 is a (l+1)-valent linking group. 01 is a group represented by the following general formula (f0-r-1) or (f0-r-2), and l is an integer of 1 or greater, as long as the valence allows.

[0416] [ka] [In the formula, Rf 011 Rf is a fluorinated alkyl group having 1 to 12 carbon atoms. 012 represents a hydrogen atom or an organic group having 1 to 12 carbon atoms which may have a fluorine atom. Xf represents a cyclic group having 4 or more fluorine atoms as substituents. * Lf 02 represents a bond with .]

[0417] The fluorine-containing polymeric compound of this embodiment is the same as the compound (f0-1) that derives the structural unit (f0) contained in the component (F0) of the resist composition according to the first aspect.

[0418] (Method of producing the compound) The method for producing the compound according to this embodiment is not particularly limited, and the compound can be produced by appropriately combining known methods, as in the <Synthesis Examples of Compounds> shown in the [Examples] below.

[0419] The compound of this embodiment is useful for producing a fluorine-containing polymer compound having the structural unit (f0) (the fluorine-containing polymer compound (F0) in the first aspect). [Example]

[0420] The present invention will be described in more detail below with reference to examples, but the present invention is not limited to these examples.

[0421] <Examples of compound synthesis> (Intermediate Synthesis Example 1: Synthesis of Intermediate (H3)) 2,6-Diiodo-4-vinylphenol (11.1 g, 30.0 mmol) was dissolved in 30 g of N,N-dimethylformamide (DMF). Potassium carbonate (5.1 g, 37.0 mmol) was added to the solution, followed by the dropwise addition of a 20 g DMF solution of ethyl bromoacetate (5.5 g, 33.0 mmol). After stirring at room temperature for 3 hours, 100 g of methyl tert-butyl ether (TBME) was added and the mixture was washed with 100 g of ultrapure water. After distilling off the solvent, the resulting concentrate was dissolved in 50 g of acetonitrile, 35 g of 5% aqueous sodium hydroxide was added, and the mixture was stirred at room temperature for 16 hours. 210 g of 5% aqueous citric acid was then added dropwise over 30 minutes. The precipitate was collected by filtration, washed with 100 g of ultrapure water, and dried under reduced pressure to obtain intermediate (H3) (11.0 g, yield = 85.0%).

[0422] [ka]

[0423] (Intermediate Synthesis Examples 2 and 3: Synthesis of Intermediate (H1) and Intermediate (H2)) Intermediate (H1) and intermediate (H2) were obtained in the same manner as in the synthesis example of intermediate (H3), except that 2,6-diiodo-4-vinylphenol was changed to equimolar phenols (PH-01) and (PH-02).

[0424] [ka]

[0425] (Intermediate Synthesis Example 4: Synthesis of Carboxylic Acid (CA1)) Compound (AC-01) (14.5 g, 75.0 mmol), triethylamine (8.5 g, 77.5 mmol), and acetonitrile (150 g) were added to a 500 mL three-neck flask and cooled to 5°C. Methacrylic acid chloride (38.5 g, 80.0 mmol) dissolved in acetonitrile (150 g) was added dropwise over 30 minutes and allowed to react for 1 hour. A 1% NH3 aqueous solution (150 g) and dichloromethane (150 g) were then added and stirred for 30 minutes. The organic layer was recovered and washed with ultrapure water (100 g). Trifluoroacetic acid (13.6 g, 120 mmol) was then added and stirred for 15 hours. The precipitate was collected by filtration, washed with 100 g of ultrapure water, and dried under reduced pressure to obtain carboxylic acid (CA1) (9.8 g, yield = 58.8%).

[0426] [ka]

[0427] (Intermediate Synthesis Examples 5 and 6: Synthesis of Intermediate (AC2) and Intermediate (AC3)) Carboxylic acid (CA2) and carboxylic acid (CA3) were obtained in the same manner as in the synthesis example of carboxylic acid (CA1), except that compound (AC-01) was changed to compounds (AC-02) and (AC-03).

[0428] [ka]

[0429] (Intermediate Synthesis Example 7: Synthesis of Carboxylic Acid (CA4)) Intermediate (H1) (13.4 g, 75.0 mmol), compound (AC-01) (15.5 g, 80.0 mmol), and dimethylaminopyridine (DMAP) (1.0 g, 8.0 mmol) were dissolved in 150 g of dichloromethane, and diisopropylcarbodiimide (DIC) (12.5 g, 100 mmol) was added to the solution. After stirring at room temperature for 16 hours, insoluble matter was removed by filtration. Trifluoroacetic acid (68.4 g, 600 mmol) was added to the collected filtrate, and the mixture was stirred for 15 hours. The precipitate was collected by filtration, washed with 100 g of ultrapure water, and then dried under reduced pressure to obtain carboxylic acid (CA4) (17.6 g, yield = 75.0%).

[0430] [ka]

[0431] (Intermediate Synthesis Examples 8 to 12: Synthesis of Intermediates (CA5) to (CA9)) Carboxylic acids (CA5), (CA6), (CA7), (CA8), and (CA9) were obtained in the same manner as in the synthesis example of carboxylic acid (CA4), except that compound (AC-01) was replaced with compounds (AC-02) and (AC-03), and intermediate (H1) was replaced with intermediates (H2) and (H3). Carboxylic acid (CA10) is a known compound.

[0432] [ka]

[0433] (Monomer Synthesis Example 1: Synthesis of Monomer (m0-01)) Compound (OH-1) (5.7 g, 25.0 mmol), 4-vinylsalicylic acid (4.1 g, 25.0 mmol), and dimethylaminopyridine (DMAP) (0.4 g, 3.2 mmol) were dissolved in 150 g of dichloromethane, and diisopropylcarbodiimide (DIC) (3.8 g, 30 mmol) was added to the solution. After stirring at room temperature for 16 hours, insoluble materials were removed by filtration. After distilling off the solvent, the resulting mixture was purified by column chromatography to obtain monomer (m0-01) (7.9 g, yield = 85.0%).

[0434] [ka]

[0435] (Monomer Synthesis Examples 2 to 4: Synthesis of Monomers (m0-02), (m0-05), and (m0-07)) Monomers (m0-02), (m0-05), and (m0-07) were obtained in the same manner as in the synthesis example for monomer (m0-01), except that compound (OH-1) was replaced with equimolar amounts of compounds (OH-2), (OH-3), and (OH-4).

[0436] [ka]

[0437] (Monomer Synthesis Examples 5 to 18: Synthesis of Monomers (m0-09), (m0-17), (m0-25), (m0-26), (m0-29), (m0-31), (m0-33), (m0-41), (m0-49), (m0-65), (m0-73), (m0-79), (m0-105), and (m0-121)) Monomers (m0-09), (m0-17), (m0-25), (m0-26), (m0-29), (m0-31), (m0-33), (m0-41), (m0-49), (m0-65), (m0-73), (m0-79), (m0-105), and (m0-121) were obtained in the same manner as in the synthesis example for monomer (m0-01), except that 4-vinylsalicylic acid was changed to the corresponding carboxylic acid and compound (OH-1) was changed to compound (OH-2), (OH-3), or (OH-4) in an equimolar amount.

[0438] [ka]

[0439] [ka]

[0440] NMR measurements were carried out on each of the obtained monomers, and their structures were identified based on the following results.

[0441] (Monomer (m0-01)) 1 H-NMR (DMSO-d6,400MHz): δ(ppm)=10.75(s,Ar-OH,1H),8.20(s,OH,1H),7.78(d,ArH,1H),7.70(d,ArH,1H),6.95(d,ArH,1H),6 .56-6.63(dd,CH=CH2,1H),5.80-5.84(d,CH=CH2,1H),5.23-5.25(d,CH=CH2,1H),4.32-4.36(m,CH2,2H),2.31-2.35(m,CH2,2H)

[0442] (Monomer (m0-02)) 1H-NMR(DMSO-d6,400MHz):δ(ppm)=10.75(s,Ar-OH,1H),8.20(s,OH,1H),7.78(d,ArH,1H),7.70(d,ArH,1H),6.95(d,ArH,1H),6.56-6.63(dd,CH=CH2,1H),5.80-5.84(d,CH=CH2,1H),5.23-5.25(d,CH=CH2,1H),5.18-5.22(m,CH,1H),2.31-2.39(m,CH2,1H),2.10-2.15(m,CH2,1H),1.28(d,CH3,3H)

[0443] (モノマー(m0-05)) 1 H-NMR(DMSO-d6,400MHz):δ(ppm)=10.75(s,Ar-OH,1H),8.05(s,OH,2H),7.78(d,ArH,1H),7.70(d,ArH,1H),6.95(d,ArH,1H),6.56-6.63(dd,CH=CH2,1H),5.80-5.84(d,CH=CH2,1H),5.21-2.25(m,CH+CH=CH2,2H),2.08-2.42(m,CH2+CH,5H),1.62-1.68(m,CH2,1H),1.30-1.40(m,CH2,2H)

[0444] (モノマー(m0-07)) 1 H-NMR(DMSO-d6,400MHz):δ(ppm)=10.75(s,Ar-OH,1H),10.30(s,Ar-OH,1H),7.78(d,ArH,1H),7.70(d,ArH,1H),6.95(d,ArH,1H),6.56-6.63(dd,CH=CH2,1H),5.80-5.84(d,CH=CH2,1H),5.23-5.25(d,CH=CH2,1H)

[0445] (モノマー(m0-09)) 1H-NMR(DMSO-d6,400MHz):δ(ppm)=10.97(s,Ar-OH,1H),8.20(s,OH,1H),7.71(d,ArH,1H),6.93(d,ArH,1H),6.42(d,ArH,1H),6.02(d,C=CH2,1H),5.64-5.68(d,C=CH2,1H),4.32-4.36(m,CH2,2H),2.31-2.35(m,CH2,2H),1.75(s,CH3,3H)

[0446] (モノマー(m0-17)) 1 H-NMR(DMSO-d6,400MHz):δ(ppm)=10.97(s,Ar-OH,1H),8.20(s,OH,1H),7.88-7.92(m,ArH,2H),7.71(d,ArH,1H),7.58-7.62(m,ArH,2H),6.93(d,ArH,1H),6.42(d,ArH,1H),6.56-6.63(dd,CH=CH2,1H),5.80-5.84(d,CH=CH2,1H),5.23-5.25(d,CH=CH2,1H),4.42(s,CH2,2H),4.32-4.36(m,CH2,2H),2.31-2.35(m,CH2,2H)

[0447] (モノマー(m0-25)) 1 H-NMR(DMSO-d6,400MHz):δ(ppm)=11.30(s,Ar-OH,1H),8.20(d,OH+I-ArH,2H),7.88(d,I-ArH,1H),6.56-6.63(dd,CH=CH2,1H),5.80-5.84(d,CH=CH2,1H),5.23-5.25(d,CH=CH2,1H),4.32-4.36(m,CH2,2H),2.31-2.35(m,CH2,2H)

[0448] (モノマー(m0-26)) 1H-NMR(DMSO-d6,400MHz):δ(ppm)=11.30(s,Ar-OH,1H),8.20(d,OH+I-ArH,2H),7.88(d,I-ArH,1H),6.56-6.63(dd,CH=CH2,1H),5.80-5.84(d,CH=CH2,1H),5.23-5.25(d,CH=CH2,1H),5.18-5.22(m,CH,1H),2.31-2.39(m,CH2,1H),2.10-2.15(m,CH2,1H),1.28(d,CH3,3H)

[0449] (モノマー(m0-29)) 1 H-NMR(DMSO-d6,400MHz):δ(ppm)=11.30(s,Ar-OH,1H),8.20(d,I-ArH,1H),8.05(s,OH,2H),7.88(d,I-ArH,1H),6.56-6.63(dd,CH=CH2,1H),5.80-5.84(d,CH=CH2,1H),5.21-2.25(m,CH+CH=CH2,2H),2.08-2.42(m,CH2+CH,5H),1.62-1.68(m,CH2,1H),1.30-1.40(m,CH2,2H)

[0450] (モノマー(m0-31)) 1 H-NMR(DMSO-d6,400MHz):δ(ppm)=11.30(s,Ar-OH,1H),10.30(s,Ar-OH,1H),8.20(d,I-ArH,1H),7.88(d,I-ArH,1H),6.56-6.63(dd,CH=CH2,1H),5.80-5.84(d,CH=CH2,1H),5.23-5.25(d,CH=CH2,1H)

[0451] (モノマー(m0-33)) 1H-NMR(DMSO-d6,400MHz):δ(ppm)=10.97(s,Ar-OH,1H),8.20(s,OH,1H),8.05(d,I-ArH,1H),6.42(d,I-ArH,1H),6.02(d,C=CH2,1H),5.64-5.68(d,C=CH2,1H),4.32-4.36(m,CH2,2H),2.31-2.35(m,CH2,2H),1.75(s,CH3,3H)

[0452] (モノマー(m0-41)) 1 H-NMR(DMSO-d6,400MHz):δ(ppm)=10.97(s,Ar-OH,1H),8.20(s,OH,1H),8.05(d,I-ArH,1H),7.81-7.83(dd,ArH,2H),7.58-7.60(dd,ArH-2H),6.56-6.63(dd,CH=CH2,1H),6.42(d,I-ArH,1H),5.80-5.84(d,CH=CH2,1H),5.23-5.25(d,CH=CH2,1H),4.32-4.36(m,CH2,2H),2.31-2.35(m,CH2,2H)

[0453] (モノマー(m0-49)) 1 H-NMR(DMSO-d6,400MHz):δ(ppm)=10.97(s,Ar-OH,1H),8.20(s,OH,1H),7.84(d,I-ArH,1H),7.71(d,ArH,1H),7.30(d,I-ArH,1H),6.93(d,ArH,1H),6.91(d,I-ArH,1H),6.56-6.63(dd,CH=CH2,1H),6.42(d,I-ArH,1H),5.80-5.84(d,CH=CH2,1H),5.23-5.25(d,CH=CH2,1H),4.42(s,CH2,2H),4.32-4.36(m,CH2,2H),2.31-2.35(m,CH2,2H)

[0454] (モノマー(m0-65)) 1H-NMR(DMSO-d6,400MHz):δ(ppm)=10.97(s,Ar-OH,1H),8.20(s,OH,1H),8.05(d,I-ArH,1H),7.84(d,I-ArH,1H),7.30(d,I-ArH,1H),6.91(d,I-ArH,1H),6.56-6.63(dd,CH=CH2,1H),6.42(d,I-ArH,1H),5.80-5.84(d,CH=CH2,1H),5.23-5.25(d,CH=CH2,1H),4.42(s,CH2,2H),4.32-4.36(m,CH2,2H),2.31-2.35(m,CH2,2H)

[0455] (モノマー(m0-73)) 1 H-NMR(DMSO-d6,400MHz):δ(ppm)=11.30(s,Ar-OH,1H),8.20(s,OH,1H),8.05(d,I-ArH,1H),6.02(d,C=CH2,1H),5.64-5.68(d,C=CH2,1H),4.32-4.36(m,CH2,2H),2.31-2.35(m,CH2,2H),1.75(s,CH3,3H)

[0456] (モノマー(m0-79)) 1 H-NMR(DMSO-d6,400MHz):δ(ppm)=11.30(s,Ar-OH,1H),10.30(s,Ar-OH,1H),8.05(d,I-ArH,1H),6.02(d,C=CH2,1H),5.64-5.68(d,C=CH2,1H),1.75(s,CH3,3H)

[0457] (モノマー(m0-105)) 1H-NMR (DMSO-d6,400MHz):10.97(s,Ar-OH,1H),8.20(s,OH,1H),8.05(d,I-ArH,1H),8.02(d,I-ArH,2H),6.56-6.63(dd,CH=CH2,1H),6. 42(d,I-ArH,1H),5.80-5.84(d,CH=CH2,1H),5.23-5.25(d,CH=CH2,1H),4.42(s,CH2,2H),4.32-4.36(m,CH2,2H),2.31-2.35(m,CH2,2H)

[0458] (Monomer (m0-121)) 1 H-NMR (DMSO-d6,400MHz):11.30(s,Ar-OH,1H),8.20(s,OH,1H),8.05(d,I-ArH,1H),8.02(d,I-ArH,2H),6.56-6.63(dd,CH=CH 2,1H),5.80-5.84(d,CH=CH2,1H),5.23-5.25(d,CH=CH2,1H),4.42(s,CH2,2H),4.32-4.36(m,CH2,2H),2.31-2.35(m,CH2,2H)

[0459] <Examples of polymer compound production> The fluorine-containing polymer compounds (F0-1) to (F0-50) were each obtained by radical polymerization of monomers that derive the structural units constituting each polymer compound in a predetermined molar ratio, followed by a deprotection reaction as necessary. The weight average molecular weight (Mw) and molecular weight dispersity (Mw / Mn) of each of the obtained polymer compounds were determined by GPC measurement (converted to standard polystyrene). The results are shown in Tables 1 and 2. Furthermore, the copolymerization composition ratio (the proportion (molar ratio) of each structural unit in the structural formula) of each obtained polymer compound was determined by carbon-13 nuclear magnetic resonance spectroscopy (600 MHz, C-NMR). The results are shown in Tables 1 and 2.

[0460] [Table 1]

[0461] [Table 2]

[0462] [ka]

[0463] [ka]

[0464] [ka]

[0465] <Preparation of Resist Composition> (Examples 1 to 60, Comparative Examples 1 to 4) The components shown in Tables 3 to 5 were mixed and dissolved to prepare the resist compositions of each example.

[0466] [Table 3]

[0467] [Table 4]

[0468] [Table 5]

[0469] In Tables 3 to 5, the abbreviations have the following meanings: The numbers in brackets [ ] are the blend amounts (parts by mass). (A1)-1: The following polymer compound (A1-1): The weight average molecular weight (Mw) calculated in terms of standard polystyrene by GPC measurement was 5,800, and the molecular weight dispersity (Mw / Mn) was 1.54. 13The copolymer composition ratio (the ratio (molar ratio) of each structural unit in the structural formula) determined by C-NMR was l / m = 50 / 50. (A1)-2: The following polymer compound (A1-2): The weight average molecular weight (Mw) calculated in terms of standard polystyrene by GPC measurement was 6,000, and the molecular weight dispersity (Mw / Mn) was 1.55. 13 The copolymer composition ratio (the ratio (molar ratio) of each structural unit in the structural formula) determined by C-NMR was l / m = 50 / 50. (A1)-3: The following polymer compound (A1-3): The weight average molecular weight (Mw) calculated in terms of standard polystyrene by GPC measurement was 5,900, and the molecular weight dispersity (Mw / Mn) was 1.54. 13 The copolymer composition ratio (the ratio (molar ratio) of each structural unit in the structural formula) determined by C-NMR was l / m = 50 / 50. (A1)-4: The following polymer compound (A1-4): The weight average molecular weight (Mw) calculated in terms of standard polystyrene by GPC measurement was 5,700, and the molecular weight dispersity (Mw / Mn) was 1.52. 13 The copolymer composition ratio (proportion (molar ratio) of each structural unit in the structural formula) determined by C-NMR was l / m / n = 35 / 50 / 15. (A1)-5: The following polymer compound (A1-5): The weight average molecular weight (Mw) calculated in terms of standard polystyrene by GPC measurement was 5,900, and the molecular weight dispersity (Mw / Mn) was 1.54. 13 The copolymer composition ratio (the ratio (molar ratio) of each structural unit in the structural formula) determined by C-NMR was l / m / o = 45 / 50 / 5. (A1)-6: The following polymer compound (A1-6): The weight average molecular weight (Mw) calculated in terms of standard polystyrene by GPC measurement was 5,800, and the molecular weight dispersity (Mw / Mn) was 1.53. 13 The copolymer composition ratio (the proportion (molar ratio) of each structural unit in the structural formula) determined by C-NMR was l / m / n / o = 30 / 50 / 15 / 5.

[0470] [ka]

[0471] (B1)-1: An acid generator comprising the following compound (B1-1). (D1)-1: An acid diffusion controller comprising the following compound (D1-1):

[0472] [ka]

[0473] (F0)-1 to (F0)-50: the fluorine-containing polymer compounds (F0-1) to (F0-50) (F1)-1: The following fluorine-containing polymer compound (F1-1), having a weight average molecular weight (Mw) of 12,000 and a molecular weight dispersity (Mw / Mn) of 1.50, calculated in terms of standard polystyrene, as determined by GPC. 13 The copolymer composition ratio (the ratio (molar ratio) of each structural unit in the structural formula) determined by C-NMR was l / m = 25 / 75. (F1)-2: The following fluorine-containing polymer (F1-2): The weight average molecular weight (Mw) calculated in terms of standard polystyrene as determined by GPC measurement was 12,200, and the molecular weight dispersity (Mw / Mn) was 1.49. 13 The copolymer composition ratio (the ratio (molar ratio) of each structural unit in the structural formula) determined by C-NMR was l / m = 25 / 75. (F1)-3: The following fluorine-containing polymer (F1-3): The weight average molecular weight (Mw) calculated in terms of standard polystyrene as determined by GPC measurement was 12,100, and the molecular weight dispersity (Mw / Mn) was 1.50. 13 The copolymer composition ratio (the ratio (molar ratio) of each structural unit in the structural formula) determined by C-NMR was l / m = 25 / 75. (F1)-4: The following fluorine-containing polymer compound (F1-4). The weight average molecular weight (Mw) calculated in terms of standard polystyrene by GPC measurement was 12,100, and the molecular weight dispersity (Mw / Mn) was 1.51. 13 The copolymer composition ratio (the ratio (molar ratio) of each structural unit in the structural formula) determined by C-NMR was l / m = 25 / 75.

[0474] [ka]

[0475] (S)-1: A mixed solvent of propylene glycol monomethyl ether acetate / propylene glycol monomethyl ether=60 / 40 (mass ratio).

[0476] <Formation of resist pattern> Each resist composition of each example was applied using a spinner onto an 8-inch silicon substrate that had been treated with hexamethyldisilazane (HMDS), and then pre-baked (PAB) on a hot plate at 110°C for 60 seconds, followed by drying to form a resist film with a thickness of 50 nm. Next, the resist film was subjected to exposure using an electron beam lithography system JEOL-JBX-9300FS (manufactured by JEOL Ltd.) at an acceleration voltage of 100 kV to form a 1:1 line and space pattern (hereinafter referred to as "LS pattern") with a target size of 25 nm line width. This was followed by a post-exposure bake (PEB) treatment at 110°C for 60 seconds. Subsequently, alkaline development was performed for 60 seconds at 23°C using a 2.38% by mass tetramethylammonium hydroxide (TMAH) aqueous solution "NMD-3" (trade name, manufactured by Tokyo Ohka Kogyo Co., Ltd.). After that, the substrate was rinsed with pure water for 15 seconds, resulting in the formation of a 1:1 LS pattern with a pitch of 50 nm and a line width of 25 nm.

[0477] [Evaluation of optimal exposure (Eop)] The optimum exposure dose Eop (μC / cm) for forming a target size LS pattern by the above <Formation of resist pattern> 2 This is called "Eop (μC / cm 2 )" are shown in Tables 6 to 8.

[0478] [Evaluation of LWR (Line Width Roughness)] For the LS patterns formed in the above <Formation of Resist Pattern>, 3σ, which is a measure of LWR, was determined. This is shown in Tables 6 to 8 as "LWR (nm)". "3σ" indicates three times the standard deviation (σ) (unit: nm) obtained from the measurement results of measuring 400 line positions in the longitudinal direction of the line using a scanning electron microscope (accelerating voltage 800 V, product name: S-9380, manufactured by Hitachi High-Technologies Corporation). The smaller the 3σ value, the less rough the line sidewalls are, meaning that an LS pattern with a more uniform width is obtained.

[0479] <Evaluation of fine resolution> The limiting resolution at the optimum exposure dose (Eop) at which the LS pattern is formed, specifically, the space size (nm) of the resolved pattern when the exposure dose is gradually reduced from the optimum exposure dose (Eop) to form the LS pattern, was determined using a scanning electron microscope S-9380 (Hitachi High-Technologies Corporation). The results are shown in Tables 6 to 8 as "limiting resolution (nm)."

[0480] <Defect evaluation after development> The total number of defects in the wafer (total number of defects) was measured for the LS pattern using a surface defect observation device (product name: KLA2905, manufactured by KLA-Tencor Corporation). Defect targets were limited to those 1 um or larger in size, and measurements were taken 10 times per sample. The average evaluation result was taken as the "number of defects." When the number of foreign particles / defects on the coating film surface of Comparative Example 1 was set to 1.0, evaluation was performed according to the following evaluation criteria. The evaluation results are shown in Tables 6 to 8. (Evaluation criteria) ○: 0.5 or less △: 0.5~1.0 ×: 1.0 or more

[0481] [Table 6]

[0482] [Table 7]

[0483] [Table 8]

[0484] As shown in Tables 6 to 8, the resist compositions of the examples were superior in sensitivity, LWR, fine feature resolution, and defects compared to the resist compositions of the comparative examples.

Claims

1. A resist composition that generates an acid upon exposure and whose solubility in a developer changes due to the action of the acid, a resin component (A1) whose solubility in a developer changes under the action of an acid; a fluorine-containing polymer compound (F0) having a structural unit (f0) derived from a compound represented by the following general formula (f0-1); A resist composition comprising: 【Chemistry 1】 [In the formula, W １ is a polymerizable group-containing group. ００ is an organic group having at least one hydroxy group as a substituent. ０２ is a (l+1)-valent linking group. ０１ is a group represented by the following general formula (f0-r-1) or (f0-r-2), and l is an integer of 1 or greater, as long as the valence allows. 【Chemistry 2】 [wherein, Rf ０１１ is a fluorinated alkyl group having 1 to 12 carbon atoms. ０１２ represents a hydrogen atom or an organic group having 1 to 12 carbon atoms which may have a fluorine atom, and Xf represents a cyclic group having four or more fluorine atoms as substituents. ＊ is Lf ０２ represents a bond with .]

2. In the general formula (f0-1), Lf ００ 2. The resist composition according to claim 1, wherein is an organic group having at least one hydroxy group and at least one iodine atom as substituents.

3. 2. The resist composition according to claim 1, wherein the structural unit (f0) is a structural unit derived from a compound represented by the following general formula (f0-1-1): 【Transformation 3】 [In the formula, W １ is a polymerizable group-containing group. Ar1 and Ar2 each independently represent an aromatic group. Lf ０１ is a divalent linking group. ０２ is a (l+1)-valent linking group. k is 0 or 1. p and q are each independently an integer of 0 or greater, as long as the valence allows, provided that p+q≧1. m and n are each independently an integer of 0 or greater, as long as the valence allows. Rf ０１ is a group represented by the following general formula (f0-r-1) or (f0-r-2), and l is an integer of 1 or greater, as long as the valence allows. 【Chemistry 4】 [wherein, Rf ０１１ is a fluorinated alkyl group having 1 to 12 carbon atoms. ０１２ represents a hydrogen atom or an organic group having 1 to 12 carbon atoms which may have a fluorine atom, and Xf represents a cyclic group having four or more fluorine atoms as substituents. ＊ is Lf ０２ represents a bond with .]

4. 4. The resist composition according to claim 3, wherein in general formula (f0-1-1), m+n≧1.

5. 10. A method for forming a resist pattern, comprising the steps of: forming a resist film on a support using the resist composition according to claim 1; exposing the resist film; and developing the exposed resist film to form a resist pattern.

6. A fluorine-containing polymeric compound having a structural unit (f0) derived from a compound represented by the following general formula (f0-1): 【Transformation 5】 [In the formula, W １ is a polymerizable group-containing group. ００ is an organic group having at least one hydroxy group as a substituent. ０２ is a (l+1)-valent linking group. ０１ is a group represented by the following general formula (f0-r-1) or (f0-r-2), and l is an integer of 1 or greater, as long as the valence allows. 【Transformation 6】 [wherein, Rf ０１１ is a fluorinated alkyl group having 1 to 12 carbon atoms. ０１２ represents a hydrogen atom or an organic group having 1 to 12 carbon atoms which may have a fluorine atom, and Xf represents a cyclic group having four or more fluorine atoms as substituents. ＊ is Lf ０２ represents a bond with .]

7. In the general formula (f0-1), Lf ００ The fluorine-containing polymer compound according to claim 6 , wherein is an organic group having at least one hydroxy group and at least one iodine atom as substituents.

8. 7. The fluorine-containing polymer compound according to claim 6, wherein the structural unit (f0) is a structural unit derived from a compound represented by the following general formula (f0-1-1): 【Transformation 7】 [In the formula, W １ is a polymerizable group-containing group. Ar1 and Ar2 each independently represent an aromatic group. Lf ０１ is a divalent linking group. ０２ is a (l+1)-valent linking group. k is 0 or 1. p and q are each independently an integer of 0 or greater, as long as the valence allows, provided that p+q≧1. m and n are each independently an integer of 0 or greater, as long as the valence allows. Rf ０１ is a group represented by the following general formula (f0-r-1) or (f0-r-2), and l is an integer of 1 or greater, as long as the valence allows. 【Transformation 8】 [wherein, Rf ０１１ is a fluorinated alkyl group having 1 to 12 carbon atoms. ０１２ represents a hydrogen atom or an organic group having 1 to 12 carbon atoms which may have a fluorine atom, and Xf represents a cyclic group having four or more fluorine atoms as substituents. ＊ is Lf ０２ represents a bond with .]

9. 9. The fluorine-containing polymer compound according to claim 8, wherein, in general formula (f0-1-1), m+n≧1.

10. A compound represented by the following general formula (f0-1): 【Chemistry 9】 [In the formula, W １ is a polymerizable group-containing group. ００ is an organic group having at least one hydroxy group as a substituent. ０２ is a (l+1)-valent linking group. ０１ is a group represented by the following general formula (f0-r-1) or (f0-r-2), and l is an integer of 1 or greater, as long as the valence allows. 【Chemistry 10】 [wherein, Rf ０１１ is a fluorinated alkyl group having 1 to 12 carbon atoms. ０１２ represents a hydrogen atom or an organic group having 1 to 12 carbon atoms which may have a fluorine atom, and Xf represents a cyclic group having four or more fluorine atoms as substituents. ＊ is Lf ０２ represents a bond with .]

11. In the general formula (f0-1), Lf ００ The compound according to claim 10, wherein is an organic group having at least one hydroxy group and at least one iodine atom as substituents.

12. The compound according to claim 10, represented by the following general formula (f0-1-1): 【Chemistry 11】 [In the formula, W １ is a polymerizable group-containing group. Ar1 and Ar2 each independently represent an aromatic group. Lf ０１ is a divalent linking group. ０２ is a (l+1)-valent linking group. k is 0 or 1. p and q are each independently an integer of 0 or greater, as long as the valence allows, provided that p+q≧1. m and n are each independently an integer of 0 or greater, as long as the valence allows. Rf ０１ is a group represented by the following general formula (f0-r-1) or (f0-r-2), and l is an integer of 1 or greater, as long as the valence allows. 【Chemistry 12】 [wherein, Rf ０１１ is a fluorinated alkyl group having 1 to 12 carbon atoms. ０１２ represents a hydrogen atom or an organic group having 1 to 12 carbon atoms which may have a fluorine atom, and Xf represents a cyclic group having four or more fluorine atoms as substituents. ＊ is Lf ０２ represents a bond with .]

13. The compound according to claim 12, wherein, in general formula (f0-1-1), m+n≧1.

Images