All-solid-state battery and method for producing same

Abstract

To provide an all-solid-state battery with a novel structure.SOLUTION: An all-solid-state battery of the present disclosure is an all-solid-state battery having at least one structural unit cell comprising a positive electrode collector layer, a positive electrode active material layer, a solid electrolyte layer, a negative electrode active material layer and a negative electrode collector layer stacked in this order. In the all-solid-state battery, a connecting conductor layer is laminated on the surface of the positive electrode collector layer side and / or the negative electrode collector layer side of the structural unit cell. Electrical resistivity of the connecting conductor layer is preferably lower than the electrical resistivity of the positive electrode collector layer or the negative electrode collector layer on which the connecting conductor layer is layered. The electrical resistivity of the connecting conductor layer is preferably 1×10-6 Ωm or lower.SELECTED DRAWING: Figure 3

Description

[Technical field]

[0001] The present invention relates to an all-solid-state battery and a manufacturing method thereof. [Background technology]

[0002] All-solid-state batteries are configured in such a way that the separator layer and electrolyte used in conventional liquid electrolyte lithium-ion batteries are replaced with a solid electrolyte. Due to the solid electrolyte's high flame retardancy, high pack energy density due to the absence of a cooling unit, and the ability to charge at high rates, all-solid-state batteries are expected to be put to practical use, particularly in automobiles.

[0003] Regarding the structure of an all-solid-state battery, Patent Document 1 discloses a structure in which unit cells each having a positive electrode layer formed on one side of a solid electrolyte and a negative electrode layer formed on the other side are stacked via a positive electrode current collector and a negative electrode current collector, the positive electrode current collectors are collectively connected to a positive terminal, and the negative electrode current collectors are collectively connected to a negative terminal, and the terminals are taken out to the outside of the battery. However, this structure has a problem in that the internal resistance of the battery increases due to the electrical resistance of the connection between the current collectors and the terminals.

[0004] In response to this, Patent Document 2 discloses a stacked all-solid-state battery structure in which a positive electrode current collector is folded and arranged so as to electrically connect the positive electrode layers of the electrode stack, and a negative electrode current collector is folded and arranged so as to electrically connect the negative electrode layers of the electrode stack. This makes it possible to reduce the electrical resistance of the connection between the positive electrode and negative electrode current collectors and the terminals in the conventional structure. However, such a structure has a problem in that the manufacturing process becomes complicated.

[0005] On the other hand, when the solid electrolyte contains sulfur and copper is used as a current collector, there is a problem that copper sulfide is generated and electrical resistance increases. Therefore, Patent Document 3 discloses an all-solid-state battery having a negative electrode current collector for an all-solid-state battery in which a nickel coating is formed on both sides of an electrolytic copper foil, a rolled copper foil, or a copper alloy foil, and a solid electrolyte containing sulfur, as an all-solid-state battery that suppresses the generation of copper sulfide and has excellent conductivity. However, in such a structure, since the laminate is all bonded, even if a part of the layer is defective, it is not possible to replace only the corresponding part, and there is a problem that the yield during production is low. [Prior art documents] [Patent documents]

[0006] [Patent Document 1] JP 2014-116156 A [Patent Document 2] JP 2020-113434 A [Patent Document 3] JP 2016-9526 A Summary of the Invention [Problem to be solved by the invention]

[0007] Therefore, an object of the present disclosure is to provide an all-solid-state battery having a novel configuration. [Means for solving the problem]

[0008] The configuration for solving the above problem is as follows: Aspect 1 An all-solid-state battery having at least one unit cell formed by laminating a positive electrode current collector layer, a positive electrode active material layer, a solid electrolyte layer, a negative electrode active material layer, and a negative electrode current collector layer in this order, a connecting conductor layer is laminated on a surface of the unit cell facing the positive electrode current collector layer and / or a surface of the unit cell facing the negative electrode current collector layer. Aspect 2 2. The all-solid-state battery of aspect 1, wherein the electrical resistivity of the connecting conductor layer is lower than the electrical resistivity of the positive electrode current collector layer or the negative electrode current collector layer on which the connecting conductor is laminated. Aspect 3 The electrical resistivity of the connecting conductor layer is 1×10 -6 3. The all-solid-state battery according to embodiment 1 or 2, wherein the resistance is Ωm or less. Aspect 4 The all-solid-state battery according to any one of Aspects 1 to 3, wherein the connecting conductor layer is made of copper and / or aluminum. Aspect 5 The all-solid-state battery according to any one of Aspects 1 to 4, wherein the negative electrode active material layer contains a sulfide-based solid electrolyte, and the negative electrode current collector layer is made of stainless steel or nickel. Aspect 6 A step of alternately stacking the structural unit cells and the connecting conductor layers, or stacking small units each including the structural unit cells and the connecting conductors, to form a laminate; A step of connecting a positive electrode terminal and a negative electrode terminal to the connection conductor layer of the obtained laminate; and A step of sealing the laminate with an exterior body; 6. The method for producing an all-solid-state battery according to any one of aspects 1 to 5, Effect of the Invention

[0009] According to the present disclosure, it is possible to provide an all-solid-state battery having a novel configuration. [Brief description of the drawings]

[0010] [Figure 1] FIG. 1 is a schematic diagram showing a unit cell 10A included in an all-solid-state battery 1A according to the first embodiment of the present disclosure. [Diagram 2] FIG. 2 is a schematic diagram of an all-solid-state battery 1A according to the first embodiment of the present disclosure. [Diagram 3] FIG. 3 is a plan view of the all-solid-state battery 1A according to the first embodiment of the present disclosure as viewed from the stacking direction. [Figure 4]FIG. 4 is a schematic diagram of an all-solid-state battery 1B according to the second embodiment of the present disclosure. [Diagram 5] FIG. 5 is a schematic diagram of an all-solid-state battery 1C according to the third embodiment of the present disclosure. [Figure 6] FIG. 6 is a schematic diagram of an all-solid-state battery 1D according to the fourth embodiment of the present disclosure. [Figure 7] FIG. 7 is a schematic diagram of an all-solid-state battery 1E according to the fifth embodiment of the present disclosure. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0011] 《All-solid-state battery》 The all-solid-state battery according to the present disclosure is an all-solid-state battery having a constituent unit cell formed by laminating a positive electrode current collector layer, a positive electrode active material layer, a solid electrolyte layer, a negative electrode active material layer, and a negative electrode current collector layer in this order, and is characterized in that a connecting conductor layer is laminated on a surface of the constituent unit cell facing the positive electrode current collector layer and / or a surface of the constituent unit cell facing the negative electrode current collector layer.

[0012] The all-solid-state battery according to the present disclosure may have a single layer structure having one constituent unit cell, or may have a layered structure in which a plurality of constituent unit cells and connecting conductor layers are alternately stacked.

[0013] By stacking a plurality of unit cells, the charge / discharge capacity per volume can be improved and the internal resistance of the battery can be reduced. In addition, in the all-solid-state battery according to the present disclosure, when a connecting conductor layer is disposed between each of the unit cells, the unit cells are not joined to each other. This is different from the configuration in which all the stacks are joined as disclosed in Patent Document 3, and when some of the unit cells are defective, only the corresponding unit cells can be replaced, thereby improving the yield during production.

[0014] Here, the series structure refers to a structure (bipolar structure) in which the constituent unit cells are arranged so that the positive electrode collector side of the constituent unit cells contacts one side of the connecting conductor and the negative electrode collector side of the constituent unit cells contacts the other side, and the polarities of the constituent unit cells are in the same direction, while the parallel structure refers to a structure (monopolar structure) in which the constituent unit cells are arranged so that the positive electrode collector side of the constituent unit cells contacts both sides of the positive connecting conductor and the negative electrode collector side of the constituent unit cells contacts both sides of the negative connecting conductor, and the polarities of the constituent unit cells are alternately stacked in the opposite directions. The series structure can increase the voltage of the battery. The parallel structure can also increase the charge / discharge capacity and reduce the internal resistance of the battery.

[0015] Fig. 1 is a schematic diagram showing a unit cell of an all-solid-state battery according to a first embodiment of the present disclosure. Note that Fig. 1 is not intended to limit the all-solid-state battery of the present disclosure.

[0016] As shown in FIG. 1, a unit cell 10A of an all-solid-state battery 1A according to the first embodiment of the present disclosure has a configuration in which a positive electrode collector layer 11, a positive electrode active material layer 12, a solid electrolyte layer 13, a negative electrode active material layer 14, and a negative electrode collector layer 15 are stacked in this order. When the unit cell 10A is viewed from the stacking direction, the positive electrode collector layer 11 and the positive electrode active material layer 12 are disposed inside the outer periphery of the solid electrolyte layer 13, the negative electrode active material layer 14, and the negative electrode collector layer 15. In addition, an insulator 16 is disposed so as to surround the outer periphery of the positive electrode collector layer 11 and the positive electrode active material layer 12. The insulator 16 has a frame-like shape that surrounds the outer periphery of the positive electrode collector layer 11 and the positive electrode active material layer 12.

[0017] By having the unit cell 10A have the insulator 16 as described above, it is possible to suppress a short circuit due to contact between the positive electrode collector layer 11 and / or the positive electrode active material layer 12 and the negative electrode active material layer 14 and / or the negative electrode collector layer 15.

[0018] 1, the insulator 16 is disposed at the ends of the positive electrode collector layer 11 and the positive electrode active material layer 12 so as to surround the entire outer periphery of the positive electrode collector layer 11 and the positive electrode active material layer 12 when viewed from the stacking direction of the structural unit cell 10A. Therefore, it is possible to fill a gap formed between the positive electrode collector layer 11 and / or the positive electrode active material layer 12 and the solid electrolyte layer 13 and / or the negative electrode active material layer 14. The insulator 16 may also be disposed so as to surround the entire outer periphery of the negative electrode active material layer 14 and the negative electrode collector layer 15 when viewed from the stacking direction.

[0019] Fig. 2 is a schematic diagram of an all-solid-state battery 1A according to the first embodiment of the present disclosure. Fig. 3 is a plan view of the all-solid-state battery 1A according to the first embodiment of the present disclosure when viewed from the stacking direction. Note that Figs. 2 and 3 are not intended to limit the all-solid-state battery of the present disclosure.

[0020] In the all-solid-state battery 1A shown in Fig. 2 and Fig. 3, a positive electrode connecting conductor layer 20a and a negative electrode connecting conductor layer 20b are laminated on the surface of the constituent unit cell 10A facing the positive electrode current collector layer 11 and the surface of the constituent unit cell 10A facing the negative electrode current collector layer 15, respectively. The constituent unit cell 10A and each connecting conductor layer 20a, 20b are both disposed within an exterior body 50. The positive electrode connecting conductor layer 20a is connected to a positive electrode terminal 30, and the negative electrode connecting conductor layer 20b is connected to a negative electrode terminal 40. The positive electrode terminal 30 and the negative electrode terminal 40 are each structured to be led out from the exterior body 50, and a current can be taken out therefrom.

[0021] Fig. 4 is a schematic diagram of an all-solid-state battery 1B according to a second embodiment of the present disclosure. Note that Fig. 4 is not intended to limit the all-solid-state battery of the present disclosure.

[0022] The all-solid-state battery 1B according to the second embodiment of the present disclosure shown in Fig. 4 has a stacked structure (monopolar structure) in which three unit cells 10A are connected in parallel. The all-solid-state battery 1B has a stacked structure in which the negative electrode current collector layer 15 of the unit cell 10A is in contact with the negative electrode connecting conductor layer 20b, and the positive electrode current collector layer 11 is in contact with the positive electrode connecting conductor layer 20a. Here, the unit cells 10A are stacked alternately with their polarities inverted up and down.

[0023] 4, when a plurality of unit cells 10A are stacked, a plurality of positive electrode connecting conductor layers 20a and a plurality of negative electrode connecting conductor layers 20b are connected to a positive electrode terminal 30 and a negative electrode terminal 40, respectively. The connection method is the same as in the case of a single layer. These are sealed in an exterior body 50, and only a portion of the positive electrode terminal 30 and the negative electrode terminal 40 are led out from the exterior body 50.

[0024] Fig. 5 is a schematic diagram of an all-solid-state battery 1C according to a third embodiment of the present disclosure. Note that Fig. 5 is not intended to limit the all-solid-state battery of the present disclosure.

[0025] The all-solid-state battery 1C according to the third embodiment of the present disclosure shown in FIG. 5 has a stacked structure (bipolar structure) in which three unit cells 10A are connected in series. The stacked structure has a negative electrode current collector layer 15 of one unit cell 10A and a positive electrode current collector layer 11 of another unit cell 10A in contact with both sides of the connection conductor layer 20. At both ends of the stacked unit cells 10A in the stacking direction, a positive electrode connection conductor layer 20a is stacked on the surface on the positive electrode current collector layer 11 side, as in the case of a single layer, and a positive electrode terminal 30 is further connected. On the other hand, a negative electrode connection conductor layer 20b is stacked on the surface on the negative electrode current collector layer 15 side, and a negative electrode terminal 40 is connected. These are sealed with an exterior body 50, and only a part of the positive electrode terminal 30 and the negative electrode terminal 40 are led out from the exterior body 50.

[0026] In the all-solid-state battery 1C shown in Fig. 5, the materials constituting the connecting conductor layer 20, the positive electrode connecting conductor layer 20a, and the negative electrode connecting conductor layer 20b preferably have low electrical resistivity, and examples thereof include aluminum, copper, nickel, stainless steel (SUS), etc. Two or more of these may be used. Among these, aluminum or copper is preferred.

[0027] Fig. 6 is a schematic diagram of an all-solid-state battery 1D according to a fourth embodiment of the present disclosure. Note that Fig. 6 is not intended to limit the all-solid-state battery of the present disclosure.

[0028] An all-solid-state battery 1D according to a fourth embodiment of the present disclosure shown in Fig. 6 has a stacked structure in which a plurality of unit cells 10A are connected in series. Compared to the all-solid-state battery 1C in Fig. 5, the all-solid-state battery 1D according to the fourth embodiment has a bipolar structure in which no connecting conductor layer 20 is interposed between the unit cells 10A. By not having the connecting conductor layer 20, the battery volume can be reduced and the energy density of the battery can be improved.

[0029] Fig. 7 is a schematic diagram of an all-solid-state battery 1E according to a fifth embodiment of the present disclosure. Note that Fig. 7 is not intended to limit the all-solid-state battery of the present disclosure.

[0030] An all-solid-state battery 1E according to a fifth embodiment of the present disclosure shown in Fig. 7 has a stacked structure in which two constituent unit cells are connected in series. A constituent unit cell 10B (double-sided coating type) has a structure in which a negative electrode active material layer 14 and a solid electrolyte layer 13 are arranged in this order on one side of a current collector layer 17, and a positive electrode active material layer 12 is arranged on the other side, with an insulator 16 arranged around the positive electrode active material layer 12. The all-solid-state battery 1E has a bipolar structure in which two constituent unit cells 10B are stacked so that the solid electrolyte layer 13 and the positive electrode active material layer 12 are in contact with each other.

[0031] In FIG. 7, in the unit cell 10B, a laminate in which a positive electrode active material layer 12 is applied to one side of a positive electrode collector layer 11 and an insulator 16 is disposed on the outer periphery of the positive electrode collector layer 11 is disposed so that the positive electrode active material layer 12 is in contact with the laminate. In addition, a positive electrode connection conductor layer 20a connected to a positive electrode terminal 30 is in contact with the positive electrode collector layer 11. In addition, in the unit cell 10B, a laminate in which a negative electrode active material layer 14 and a solid electrolyte layer 13 are applied to one side of a negative electrode collector layer 15 in this order is disposed so that the solid electrolyte layer 13 is in contact with the laminate. In addition, a negative electrode connection conductor layer 20b connected to a negative electrode terminal 40 is in contact with the negative electrode collector layer 15. These are sealed with an exterior body 50, and only a part of the positive electrode terminal 30 and the negative electrode terminal 40 is led out from the exterior body.

[0032] <Unit Cell> The unit cell of the all-solid-state battery according to the present disclosure has a configuration in which a positive electrode current collector layer, a positive electrode active material layer, a solid electrolyte layer, a negative electrode active material layer, and a negative electrode current collector layer are laminated in this order.

[0033] When the constituent unit cell is viewed from the stacking direction, the positive electrode collector layer and the positive electrode active material layer can be disposed inside the outer periphery of the solid electrolyte layer, the negative electrode active material layer, and the negative electrode collector layer. Also, when the constituent unit cell is viewed from the stacking direction, the outer periphery of the positive electrode collector layer and the positive electrode active material layer can coincide with that of the solid electrolyte layer, in which case the positive electrode collector layer, the positive electrode active material layer, and the solid electrolyte layer can be disposed inside the outer periphery of the negative electrode active material layer and the negative electrode collector layer.

[0034] This is because by reliably facing the positive electrode active material layer, particularly its end portion, to the solid electrolyte layer and the negative electrode active material layer, lithium ions that migrate from the positive electrode active material during charging can be easily inserted into the negative electrode active material, which makes it possible to suppress deposition of lithium metal on the surface of the positive electrode active material layer and on the interface between the positive electrode active material layer and the solid electrolyte layer, and thus makes it possible to suppress internal short circuits in the constituent unit cells.

[0035] In a configuration in which the positive electrode current collector layer and the positive electrode active material layer are disposed inside the outer periphery of the solid electrolyte layer, the negative electrode active material layer, and the negative electrode current collector layer, an insulator may be disposed so as to surround the outer periphery of the positive electrode current collector layer and the positive electrode active material layer. The insulator may have a frame-like shape surrounding the outer periphery of the positive electrode current collector layer and the positive electrode active material layer.

[0036] (Positive electrode current collector layer) The material constituting the positive electrode current collector layer is preferably one that does not react with the solid electrolyte or with charging and discharging at the positive electrode operating potential, and has low electrical resistivity. Examples include aluminum, stainless steel (SUS, austenitic, martensite, ferrite, austenitic-ferrite (two-phase)), nickel, etc. Two or more of these may be used. Among these, aluminum is particularly preferable.

[0037] In the all-solid-state battery of the present disclosure, the positive electrode current collector layer may be made of aluminum, stainless steel, or nickel, because these metals have low reactivity with the sulfide-based solid electrolyte.

[0038] (Cathode active material layer) The positive electrode active material layer is preferably composed mainly of a positive electrode active material and a solid electrolyte.

[0039] Examples of the positive electrode active material include LiCoO2, LiMnO2, LiNiO2, ternary lithium oxides of Ni, Co, and Mn, ternary lithium oxides of Ni, Co, and Al, and LiFePO4. Two or more of these may be used.

[0040] As the solid electrolyte, for example, Li2S-P2S5 (Li7P3S 11 ) and Li 10 GeP2S 12 Sulfide-based solid electrolytes such as Li6PS5Cl, Li6PS5I, etc., and Li 1.4 Al 0.4 Ti 1.6 (PO4)3, Li7La3Zr2O 12 , Li 1.5Al 0.5 Ge 1.5 Examples of the oxide-based solid electrolyte include (PO4)3. Two or more of these may be used. Among these, sulfide-based solid electrolytes are preferred. When using a sulfide-based solid electrolyte, it is preferred to coat the surface of the positive electrode active material with LiNbO3 in order to suppress the reaction of the positive electrode active material.

[0041] (solid electrolyte layer) The solid electrolyte layer is mainly composed of a solid electrolyte, such as those exemplified as the solid electrolyte constituting the positive electrode active material layer.

[0042] (Negative electrode active material layer) The negative electrode active material layer is preferably composed mainly of a negative electrode active material and a solid electrolyte.

[0043] Examples of the negative electrode active material include graphite, hard carbon, lithium titanate, titanium oxide, silicon, silicon oxide, etc. Two or more of these may be used.

[0044] As the solid electrolyte, there can be mentioned those exemplified as the solid electrolyte constituting the positive electrode active material layer.

[0045] (Negative electrode current collector layer) The material constituting the negative electrode current collector layer is preferably one that does not react with the solid electrolyte or with charging and discharging at the negative electrode operating potential, and has low electrical resistivity. Examples of the material include stainless steel (SUS), carbon, nickel, and copper. Two or more of these may be used.

[0046] Examples of materials constituting the insulator include resins such as polyethylene terephthalate (PET), polyimide (PI), polyphenylene sulfide (PPS), and ceramics such as alumina. Two or more of these may be used.

[0047] In the all-solid-state battery according to the present disclosure, when the negative electrode active material layer contains a sulfide-based solid electrolyte, the negative electrode current collector layer is preferably made of stainless steel or nickel, since these metals have low reactivity with the sulfide-based solid electrolyte.

[0048] <Connecting Conductor Layer> In the all-solid-state battery of the present disclosure, a connecting conductor layer is laminated on the surface of the constituent unit cell on the positive electrode current collector layer side and / or the surface on the negative electrode current collector layer side.

[0049] In the all-solid-state battery of the present disclosure, the positive electrode terminal and the negative electrode terminal are joined to the connecting conductor layer, so that the positive electrode terminal and the negative electrode terminal are not directly joined to the positive electrode current collector layer and the negative electrode current collector layer of the constituent unit cell, and the positive electrode current collector layer and the negative electrode current collector layer of the constituent unit cell are simply laminated without being bonded to the connecting conductor layer.

[0050] As a result, in the all-solid-state battery of the present disclosure, unlike a conventional all-solid-state battery in which a positive electrode current collector layer and a negative electrode current collector layer are joined to a positive electrode terminal and a negative electrode terminal, the constituent unit cells can be easily separated from the all-solid-state battery even in a state in which the all-solid-state battery is constructed. Therefore, for example, in the manufacturing process of an all-solid-state battery, if a part of the constituent unit cells is defective, only the constituent unit cell can be easily replaced with a non-defective constituent unit cell.

[0051] Therefore, other constituent unit cells and other parts constituting the all-solid-state battery can be used without being wasted, and the production yield of the all-solid-state battery can be improved.

[0052] In addition, an all-solid-state battery can be formed by alternately stacking the constituent unit cells and the connecting conductor layers (positive electrode connecting conductor layers and negative electrode connecting conductor layers). Therefore, the all-solid-state battery can be easily manufactured.

[0053] The positive electrode connecting conductor layer and the negative electrode connecting conductor layer are preferably in a shape that covers most or the entire positive electrode current collector layer and the negative electrode current collector layer, respectively. From the viewpoint of further reducing the electrical resistance per unit volume, a planar shape is preferable, but a lattice shape, mesh shape, etc. may also be used. The positive electrode connecting conductor layer and the negative electrode connecting conductor layer may be connected to a positive electrode terminal and a negative electrode terminal at a location that does not overlap with the positive electrode current collector layer and the negative electrode current collector layer, respectively. The connection method is preferably ultrasonic welding or spot welding from the viewpoint of further reducing the electrical resistance of the connection part.

[0054] The electrical resistivity of the positive electrode connecting conductor layer and the negative electrode connecting conductor layer is inversely proportional to the thickness. On the other hand, the smaller the thickness of the connecting conductor layer, the higher the energy density per battery volume, so the smaller the thickness of the positive electrode connecting conductor layer and the negative electrode connecting conductor layer is, the more preferable. Specifically, the thickness is preferably 100 μm or less, more preferably 50 μm or less, and even more preferably 20 μm or less.

[0055] The material constituting the positive electrode connecting conductor layer and the negative electrode connecting conductor layer preferably has low electrical resistance. Examples include aluminum, copper, nickel, and stainless steel (SUS). Two or more of these may be used. The electrical resistivity of the connecting conductor layer is preferably smaller than that of the positive electrode current collector layer or the negative electrode current collector layer in contact with it.

[0056] That is, it is preferable that the electrical resistivity of the positive electrode connecting conductor layer is smaller than that of the positive electrode current collector layer, and that the electrical resistivity of the negative electrode connecting conductor layer is smaller than that of the negative electrode current collector layer.

[0057] More specifically, the electrical resistivity of the connecting conductor layer is 1×10 -6 The electrical resistivity is preferably Ωm or less. The electrical resistivity is measured in accordance with JIS C2525:1999.

[0058] The electrical resistivity of the connecting conductor layer is 1×10 -6 Ωm or less, 5×10 -7 Ωm or less, 1×10 -7 Ωm or less, or 5×10 -8 It may be Ωm or less.

[0059] Methods for reducing the electrical resistance of the connecting conductor layer include, for example, using a metal material having a lower electrical resistivity than the material constituting the positive electrode connecting conductor layer or the negative electrode connecting conductor layer, and a method for increasing the thickness of the connecting conductor to increase its cross-sectional area.

[0060] In particular, the connecting conductor layer may be made of copper and / or aluminum.

[0061] When the all-solid-state battery of the present disclosure uses a sulfide-based solid electrolyte as the solid electrolyte, depending on the material of the negative electrode current collector layer used, the negative electrode current collector layer and the sulfide-based solid electrolyte may react with each other, and the internal resistance of the all-solid-state battery may increase. In such a case, it is possible to use, for example, a material that is less reactive with the sulfide-based solid electrolyte, such as stainless steel or nickel, as the material of the negative electrode current collector layer.

[0062] In addition, metals such as stainless steel and nickel generally have high electrical resistivity. For example, the electrical resistivity of stainless steel is more than 10 times that of copper. Therefore, if these metals are used as current collectors, the internal resistance of the entire solid-state battery will increase.

[0063] In this regard, when a sulfide-based solid electrolyte is used as the solid electrolyte, it is preferable to adopt a material having low reactivity with the sulfide-based solid electrolyte, such as stainless steel or nickel, for the current collector layer, and a material having low electrical resistivity, such as aluminum or copper, for the connecting conductor layer disposed on the current collector layer. With this configuration, the current collector layer uses a material having low reactivity with the sulfide-based solid electrolyte to suppress the reaction of the current collector layer with the sulfide-based solid electrolyte and suppress an increase in internal resistance, while the high electrical resistivity of the current collector layer can be offset by the connecting conductor layer having low electrical resistivity, and the internal resistance of the entire all-solid-state battery can be reduced.

[0064] Terminals Examples of materials constituting the positive electrode terminal and the negative electrode terminal include aluminum, copper, nickel, etc. Two or more of these may be used. A sealant film using a thermoplastic resin such as polypropylene may be disposed at the location in contact with the exterior body, which can strengthen the sealing by thermocompression bonding.

[0065] Exterior Body The exterior body is formed of, for example, a laminate film. In order to prevent the solid electrolyte in the constituent unit cell from reacting with moisture contained in the air and deteriorating, the exterior body preferably has gas barrier properties. The exterior body is preferably vacuum sealed, which can reduce the interface resistance of each layer.

[0066] <<Manufacturing method of all-solid-state batteries>> A method for producing an all-solid-state battery according to the present disclosure includes, in this order, a step of alternately stacking a plurality of constituent unit cells and connecting conductor layers, or alternately stacking the constituent unit cells and connecting conductor layers to form a laminate, a step of connecting a positive electrode terminal and a negative electrode terminal to the connecting conductor layers of the obtained laminate, and a step of sealing the laminate with an exterior body.

[0067] Examples of a method for producing the all-solid-state battery 1A shown in FIGS. 2 and 3 include a method for producing a laminate by forming a laminate by the steps of: integrating a laminate of a positive electrode collector layer 11 and a positive electrode active material layer 12, a solid electrolyte layer 13, and a laminate of a negative electrode active material layer 14 and a negative electrode collector layer 15, and arranging an insulator 16 to produce a structural unit cell 10A; connecting a positive electrode connection conductor layer 20a to a positive electrode terminal 30; connecting a negative electrode connection conductor layer 20b to a negative electrode terminal 40; stacking the structural unit cell 10A on the negative electrode connection conductor layer 20b so that the negative electrode collector layer 15 side is in contact with the negative electrode connection conductor layer 20b, and stacking the positive electrode connection conductor layer 20a on the positive electrode collector layer 11 side of the structural unit cell 10A; and then sealing the laminate with an exterior body 50, leaving a part of the positive electrode terminal 30 and the negative electrode terminal 40 exposed.

[0068] Another example is a method that includes, in this order, a step of fixing the positive electrode connecting conductor layer 20a to which the positive electrode terminal 30 is connected in advance and the negative electrode connecting conductor layer 20b to which the negative electrode terminal 40 is connected to the outer casing 50, a step of sandwiching the constituent unit cell 10A between the positive electrode connecting conductor layer 20a and the negative electrode connecting conductor layer 20b, and then a step of sealing the outer casing 50.

[0069] The former method is preferred since stacking in sequence in the same direction makes manufacturing easier.

[0070] The manufacturing method of the all-solid-state battery 1B shown in FIG. 4 may include, for example, a step of integrating a laminate of a positive electrode collector layer 11 and a positive electrode active material layer 12, a solid electrolyte layer 13, and a laminate of a negative electrode active material layer 14 and a negative electrode collector layer 15, and arranging an insulator 16 to prepare a structural unit cell 10A; a step of stacking the structural unit cells 10A so that the negative electrode collector layer 15 is in contact with the negative electrode connecting conductor layer 20b, and stacking the positive electrode connecting conductor layer 20a on the positive electrode collector layer 11 side of the structural unit cell 10A; a step of alternately stacking the constituent unit cells 10A with the positive electrode connecting conductor layers 20a and the negative electrode connecting conductor layers 20b; a step of connecting the multiple positive electrode connecting conductor layers 20a to the positive electrode terminal 30 outside the stacking range of the constituent unit cells 10A; a step of connecting the multiple negative electrode connecting conductor layers 20b to the negative electrode terminal 40 outside the stacking range of the constituent unit cells 10A; and a step of sealing the stacked structure with an exterior body 50, leaving parts of the positive electrode terminal 30 and the negative electrode terminal 40 exposed. Examples of the step of alternately stacking the constituent unit cell 10A with the positive electrode connecting conductor layer 20a and the negative electrode connecting conductor layer 20b include a method having, in this order, a step of stacking another constituent unit cell 10A on the opposite side of the positive electrode connecting conductor layer 20a so that the positive electrode current collector layer 11 side of the other constituent unit cell 10A is in contact with the positive electrode current collector layer 11 side of the other constituent unit cell 10A, and stacking the negative electrode connecting conductor layer 20b on the negative electrode current collector layer 15 side of the constituent unit cell 10A in a similar manner.

[0071] 5 may be produced in the same manner as in the production method of the all-solid-state battery 1B shown in FIG. 4, by, for example, producing a constituent unit cell 10A, connecting the positive electrode connection conductor layer 20a to the positive electrode terminal 30, connecting the negative electrode connection conductor layer 20b to the negative electrode terminal 40, alternately stacking the constituent unit cells 10A and the connection conductor layers 20 to obtain a stacked structure, and sandwiching the stacked structure between the positive electrode connection conductor layer 20a and the negative electrode connection conductor layer 20b, and sealing the stacked structure with an exterior body 50 while leaving parts of the positive electrode terminal 30 and the negative electrode terminal 40 exposed.

[0072] Here, in the all-solid-state battery 1C shown in FIG. 5, examples of the process of alternately stacking the constituent unit cells 10A and the connection conductor layers 20 include a process of stacking the constituent unit cells 10A on the negative electrode connection conductor layer 20b so that the negative electrode current collector layer 15 side is in contact, and stacking the connection conductor layer 20 on the positive electrode current collector layer 11 side of the constituent unit cell 10A, a process of stacking another constituent unit cell 10A on the opposite side of the connection conductor layer 20 so that the negative electrode current collector layer 15 side is in contact, and stacking the connection conductor layer 20 on the positive electrode current collector layer 11 side of the other constituent unit cell 10A, a process of stacking the constituent unit cells 10A and the connection conductor layer 20 in a similar manner, and a process of stacking the last constituent unit cell 10A and then stacking the positive electrode connection conductor layer 20a on the positive electrode current collector layer 11 of the last constituent unit cell 10A, in this order.

[0073] A method for manufacturing the all-solid-state battery 1D shown in FIG. 6 may be similar to the method for manufacturing the all-solid-state battery 1C shown in FIG. 5, except that the connecting conductor layer 20 is not disposed between adjacent unit cells 10A.

[0074] A method for manufacturing the all-solid-state battery 1E shown in FIG. 7 may include, for example, the steps of: producing a structural unit cell 10B in which a negative electrode active material layer 14 and a solid electrolyte layer 13 are laminated in this order on one side of a current collector layer 17, a positive electrode active material layer 12 is disposed on the opposite side of the current collector layer 17, and an insulator 16 is disposed around the positive electrode active material layer 12; connecting a positive electrode connecting conductor layer 20a to a positive electrode terminal 30; connecting a negative electrode connecting conductor layer 20b to a negative electrode terminal 40; a step of stacking a structure in which the positive electrode active material layer 14 and the solid electrolyte layer 13 are stacked in this order, a step of stacking the positive electrode active material layer 12 side of the constituent unit cell 10B on the solid electrolyte layer 13 side, a step of stacking the constituent unit cells 10B in the same manner, and a step of stacking the positive electrode active material layer 12 on the positive electrode current collector layer 11 and the insulator 16 on the solid electrolyte layer 13 side of the last constituent unit cell 10B so that the positive electrode active material layer 12 side is in contact with the positive electrode current collector layer 11. Another example is a method in which, of the constituent unit cells 10A, laminates not having the positive electrode current collector layer 11 or the negative electrode current collector layer 15 are stacked on top of each other, and finally sandwiched between the positive electrode connecting conductor layer 20a and the negative electrode connecting conductor layer 20b.

[0075] When stacking the constituent unit cells, in order to prevent misalignment of the stacking, an adhesive or the like can be applied to and fixed to parts of the constituent unit cells, the insulator, the positive electrode connecting conductor layer, the negative electrode connecting conductor layer, the connecting conductor layer, etc.

[0076] 4 to 7, even after the stacking step is completed, the stacked structure can be disassembled and the constituent unit cells 10A, 10B, etc. can be easily removed. Therefore, for example, if it is found that a part of the constituent unit cells 10A, 10B is defective after the stacking step is completed, only that part can be easily replaced with a non-defective part, thereby improving the yield of battery production.

[0077] Furthermore, in conventional stacked-type all-solid-state batteries, in order to strongly bond each layer of a structure in which multiple constituent unit cells are stacked, and thereby reduce interface resistance, it is necessary to perform a batch pressing of the stack, but because the sizes, materials, thicknesses, elastic moduli, etc. of each layer are different, parts of the structure are prone to damage and short circuits due to pressure concentration, etc., which was an issue. In the above-mentioned manufacturing method of all-solid-state batteries shown in Figures 4 to 7, the constituent unit cells can be pressed before stacking, and the constituent unit cells are in contact with each other as metal layers, which reduces interface resistance, and therefore it is possible to produce a battery without performing a batch pressing.

[0078] In the manufacturing method of the all-solid-state batteries 1B to 1E according to the present embodiment in Fig. 4 to 7, the positive electrode connecting conductor layer 20a and the negative electrode connecting conductor layer 20b, the connecting conductor layer 20, the constituent unit cells 10A and 10B, and the insulator 16 may be laminated in any order as long as the final laminated arrangement is as shown in the drawings. For example, in Fig. 4, it is also possible to integrate the negative electrode current collector layers 15 of the two constituent unit cells 10A on both sides of the negative electrode connecting conductor layer 20b, and then alternately stack them with the positive electrode connecting conductor layers 20a to produce a laminate. EXAMPLES

[0079] Examples 1 and 2, and Comparative Example 1 The following examples are given for explanation, but the present invention is not limited thereto. First, the evaluation methods used in the examples and comparative examples are described.

[0080] <Electrical resistivity measurement> The electrical resistivity of the current collector layer and the connecting conductor layer used in each of the examples and comparative examples was measured in accordance with JIS C2525:1999.

[0081] <Evaluation of battery internal resistance> For the all-solid-state batteries produced in each Example and Comparative Example, a charge-discharge test was performed at 25°C and 0.1C rate while both sides were sandwiched between flat plates and pressure was applied, and the charge capacity and discharge capacity were measured to evaluate the internal resistance of the battery. Note that, for the C rate, 1C is the current value that charges the battery to its full capacity in 1 hour, and 0.1C is the current value that charges the battery to its full capacity in 10 hours.

[0082] Thereafter, the battery was charged at 60° C. at a rate of 2 C, and the charge capacity was measured. After that, the battery was discharged at a rate of 0.1 C, and the charge capacity was measured at a rate of 6 C, and the internal resistance of the battery was evaluated.

[0083] Example 1 (Positive electrode active material layer and positive electrode current collector layer) Aluminum foil (electrical resistivity 2.7×10) was used as the positive electrode current collector layer. -8 A positive electrode active material layer was formed on the positive electrode current collector layer by applying a positive electrode active material slurry made of a mixture of a ternary lithium oxide of Ni, Co, and Mn coated with LiNbO3 (positive electrode active material), an argyrodite-type sulfide-based solid electrolyte, carbon nanofiber “VGCF” (registered trademark)-H (conductive additive), and an organic binder, using a positive electrode current collector (20 Ω·m, thickness 20 μm).

[0084] (Negative Electrode Active Material Layer and Negative Electrode Current Collector Layer) The negative electrode current collector layer was made of stainless steel foil (electrical resistivity 5.4×10 -7 A negative electrode active material layer was formed on the negative electrode current collector layer by coating a negative electrode active material slurry made of a mixture of graphite (negative electrode active material), an argyrodite-type sulfide solid electrolyte, and an organic binder using a negative electrode current collector layer (1000 Ω·m, thickness 10 μm).

[0085] (solid electrolyte layer) A mixture of an argyrodite-type sulfide-based solid electrolyte and an organic binder was applied to a stainless steel foil to form a solid electrolyte layer.

[0086] (Unit cell) The positive electrode active material layer, the solid electrolyte layer, and the negative electrode active material layer were integrated to obtain a unit cell. Note that the stainless steel foil of the solid electrolyte layer was peeled off during the integration.

[0087] An all-solid-state battery consisting of one unit cell was fabricated as follows. Stainless steel foil (electrical resistivity 5.4×10) was used as the positive electrode connecting conductor layer. -7An aluminum positive electrode terminal was connected by ultrasonic welding to a stainless steel sheet (electrical resistivity 2.7×10 Ω·m, thickness 10 μm) used as the negative electrode connecting conductor layer. Similarly, stainless steel foil was used as the negative electrode connecting conductor layer, and a negative electrode terminal made of nickel-coated copper was connected by ultrasonic welding. The negative electrode collector layer side of the constituent unit cell was overlaid on the negative electrode connecting conductor layer, and an insulating film was placed on the end face of the positive electrode active material layer of the constituent unit cell, with the inside of the insulating film cut out to the same size as the positive electrode active material layer. Aluminum foil (electrical resistivity 2.7×10 6) with a lead already connected was attached to the positive electrode collector layer side of the constituent unit cell. -8 A connecting conductor layer (resistance 100 Ω·m, thickness 20 μm) was placed on top. The above laminated structure was vacuum sealed in the exterior laminate film.

[0088] Example 2 Aluminum foil was used as the positive electrode connecting conductor layer, and copper foil (electrical resistivity 1.7×10 -8 An all-solid-state battery was fabricated in the same manner as in Example 1, except that a SiO2 nanotube was used (resistance: 1.0 Ω·m, thickness: 17 μm).

[0089] Comparative Example 1 A unit cell was produced using a positive electrode current collector layer made of aluminum foil with one side larger than that of the positive electrode active material layer, and a negative electrode current collector layer made of copper foil with one side larger than that of the negative electrode active material layer, without using a positive electrode connecting conductor layer and a negative electrode connecting conductor layer, and a positive electrode terminal and a negative electrode terminal were connected by ultrasonic welding outside the lamination range of the positive electrode current collector layer and the negative electrode current collector layer, respectively, in the same manner as in Example 1, except that the unit cell was produced using a positive electrode connecting conductor layer and a negative electrode connecting conductor layer.

[0090] The evaluation results of Examples 1 and 2 and Comparative Example 1 are shown in Table 1.

[0091] [Table 1]

[0092] Examples 1 and 2, which used stainless steel foil as the negative electrode current collector layer and a connecting conductor layer, showed improved discharge capacity and charge capacity compared to Comparative Example 1. Example 2, which used aluminum foil as the positive electrode connecting conductor and copper foil as the negative electrode connecting conductor, showed a further improved charge capacity at a 6C rate.

[0093] Examples 3 and 4, and Comparative Example 2 Example 3 An all-solid-state battery of Example 3 was produced in the same manner as in Example 1. However, the produced all-solid-state battery of Example 1 and the all-solid-state battery of Example 3 had slightly different weights of the positive electrode active material layer and the negative electrode active material layer.

[0094] Example 4 Ten unit cells prepared in Example 3 were stacked in parallel connection and vacuum sealed with a laminate film as an exterior body to obtain a stacked type all-solid-state battery of Example 4.

[0095] Comparative Example 2 Ten unit cells prepared in the same manner as in Comparative Example 1, except that an aluminum foil was used for the positive electrode current collector layer and a stainless steel foil was used for the negative electrode current collector layer, were stacked in parallel and vacuum sealed with a laminate film for an exterior body, to obtain a stacked-type all-solid-state battery of Comparative Example 2.

[0096] Battery evaluation The all-solid-state battery of Example 3 and the stacked type all-solid-state batteries of Example 4 and Comparative Example 2 were charged and discharged, and the charge capacity and discharge capacity were measured. The measurement results are shown in Table 2.

[0097] [Table 2]

[0098] As shown in Table 2, the stacked all-solid-state battery of Example 4 had a charge capacity and a discharge capacity that were about 10 times larger than those of the all-solid-state battery of Example 3.

[0099] On the other hand, the stacked type all-solid-state battery of Comparative Example 2 was damaged during stacking, resulting in a short circuit. [Explanation of symbols]

[0100] 1A, 1B, 1C, 1D, and 1E solid-state batteries 10A, 10B Unit Cell 11 Positive electrode current collector layer 12 Cathode active material layer 13 Solid electrolyte layer 14 Negative electrode active material layer 15 Negative electrode current collector layer 16 Insulators 17 Current collector layer 20 Connecting conductor layer 20a Positive electrode connecting conductor layer 20b Negative electrode connecting conductor layer 30 Positive terminal 40 Negative terminal 50 Exterior body

Claims

1. An all-solid-state battery having at least one unit cell formed by laminating a positive electrode current collector layer, a positive electrode active material layer, a solid electrolyte layer, a negative electrode active material layer, and a negative electrode current collector layer in this order, a connecting conductor layer is laminated on a surface of the unit cell facing the positive electrode current collector layer and / or a surface of the unit cell facing the negative electrode current collector layer, a frame-shaped insulator is disposed so as to surround the outer periphery of the positive electrode current collector layer and the positive electrode active material layer; All-solid-state battery.

2. The all-solid-state battery according to claim 1 , wherein the electrical resistivity of the connecting conductor layer is lower than the electrical resistivity of the positive electrode current collector layer or the negative electrode current collector layer on which the connecting conductor layer is laminated.

3. The electrical resistivity of the connecting conductor layer is 1×10 －６ The all-solid-state battery according to claim 1 or 2, having a resistance of Ωm or less.

4. The all-solid-state battery according to any one of claims 1 to 3, wherein the connecting conductor layer is made of copper and / or aluminum.

5. The all-solid-state battery according to any one of claims 1 to 4, wherein the negative electrode active material layer contains a sulfide-based solid electrolyte, and the negative electrode current collector layer is made of stainless steel or nickel.

Images