Plaster Treatment Compound

Abstract

A plaster treatment compound, particularly a water glass-containing waterproof plaster treatment compound, containing 20 to 69% by weight of an aqueous potassium silicate solution, 20 to 59.9% by weight of an aqueous lithium silicate solution, 10 to 20% by weight of octyltriethoxysilane, and 0.1 to 1% by weight of a water glass stabilizer.

Description

[Technical field]

[0001] The present invention relates to a compound for the treatment of plaster, in particular to a compound for enhancing waterproof plaster treatment, which contains waterglass. [Background technology]

[0002] From the current state of the art a wide range of means are known for improving the surface properties of plaster, which are related to the composition of the plaster and in particular to the type of its binder.

[0003] Acrylic plasters contain synthetic resin binders, which make the plasters hard, strong and water-repellent. Their main disadvantages are poor thermal stability, weak antifungal effect and especially poor vapor permeability, in addition to low resistance to dirt adhesion.

[0004] The binder of silicate plasters is made from potassium water glass, which is why they have good vapor permeability and can be used in all kinds of insulation systems. Their disadvantages include poor flexibility and water repellency.

[0005] In addition to these modern plasters, lime plasters are used in old and historical buildings. Their problem is their gradual degradation, which can be physical (moisture changes, mechanical influences) and biological (plant roots, microbial influences), but especially chemical, consisting of the decomposition of calcium carbonate as the main hardening product of lime mortars and plasters.

[0006] The strengthening of plaster can also be achieved by painting with water glass. The disadvantage of the known solutions using water glass is that after they have been used, the surface layer of the plaster often hardens and separates from the substrate.

[0007] From the Czech patent document CZ PV 1988-8934 a facade paint is known which is based on acrylates and styrene acrylates, methyl siloxanes and siloxides and water glass up to 10% by weight. The fillers are limestone and pigments. The paint does not have sufficient vapor permeability due to its organic base. The paint repels water, but is not suitable for repair treatment of old plaster.

[0008] From the further Czech patent document CZ PV 1991-1916, a paint for plaster based on limestone, potassium water glass, colloidal silicon dioxide, silicone, siloxane and pigments is known, which paint does not have good vapor permeability and is not suitable for repair treatment of old plaster.

[0009] From the Czech patent document CZ 279049, a coating material is known that consists of potassium water glass containing 5-15% by weight of silica, 5-15% by weight of 50% styrene acrylate dispersion, 20-30% by weight of limestone, dolomite, magnesite or mixtures thereof, 10-20% by weight of aluminum silicate, alkali metal, alkaline earth and magnesium silicate, 0.1-15% by weight of organic white and color pigments and 0.2-1% by weight of hydrophobizing additives based on silanes or polyorganosiloxanes. The disadvantage of this coating is that it forms a hard layer on the plaster, which can cause the destruction of the plaster. [Prior art documents] [Patent documents]

[0010] [Patent Document 1] Czech Republic Patent Application No. CZ PV 1988-8934 [Patent Document 2] Czech Republic Patent Application No. CZ PV 1991-1916 [Patent Document 3] Czech Republic Patent Application No. CZ 279049 Summary of the Invention [Problem to be solved by the invention]

[0011] From the above current technology, it is clear that the main drawback of the known current technology is that the known plaster surface treatment substances often cause destruction of the plaster surface.

[0012] It is an object of the present invention to provide a plaster treating compound which stabilises and improves the long-term surface properties of plaster. [Means for solving the problem]

[0013] The above mentioned disadvantages are largely eliminated and the object of the present invention is achieved by a plaster treatment compound, in particular a compound for the strengthening of waterproof plaster treatment containing water glass, characterized in that according to the invention it consists of 20-69% by weight of an aqueous potassium silicate solution, 20-59.9% by weight of an aqueous lithium silicate solution, 10-20% by weight of an octyltriethoxysilane solution and 0.1-1% by weight of a water glass stabilizer. The advantage of this compound is its high resistance to decomposition. The compound also has a good antifungal effect, is environmentally friendly, not harmful to health, reflects UV radiation well but does not emit organic toxic substances. To improve the hydrophobization effect, a solution of octyltriethoxysilane with a silane concentration of up to 30% by weight is added to the compound. The advantage is that there is no decrease in the vapor permeability, antifungal effect and thermal stability of the compound.

[0014] The plaster treatment compound further contains an aqueous colloidal silver solution at 0.1 to 1% by weight, most advantageously at a concentration of 100 ppm.The advantage is that it contains a solution of colloidal silver, which significantly improves fungal, viral and bacterial control.

[0015] The potassium silicate aqueous solution has a molar ratio of silica to potassium oxide in the range of 1.67 to 1.73 and a density of 1650 to 1670 kg / m 3The advantage of this composition is the excellent adhesion of the coating to the plaster and the optimization of the chemical bond of the compound with the plaster.

[0016] More advantageously, the aqueous lithium silicate solution has a molar silica to lithium oxide ratio in the range of 3.8 to 4.1 and a density of 1100 to 1300 kg / m 3 The range of. The advantage of this compound is its excellent water repellency. An additional advantage is that this compound reduces the viscosity and reduces the alkalinity, which helps this compound achieve deeper and more effective penetration into the plaster surface. Lithium water glass is water repellent, while covering the surface of the plaster, protecting it from the continuous intrusion of water, filling the pores that arise in the plaster, thereby preventing the transport of water and salts in the plaster.

[0017] Advantageously, the water glass stabilizer is a hydrophilic alkoxyalkyl-ammonium salt.

[0018] The main advantage of the plaster treatment compound according to the invention is that it simultaneously stabilizes the surface of the plaster in depth and significantly improves its properties. After hardening, the surface of the plaster resembles classical glass, but is strong, hard, wear-resistant and, in addition to water, is also resistant to salt solutions, oil and diesel oil. Another advantage is that the compound has an anti-corrosive effect on metal elements in contact with the plaster. The surface of the plaster is vapor-permeable, ensuring the release of water vapor that may remain in the plaster or enter it by rising from the masonry or ground. In addition, abrasion of the plaster is significantly eliminated. The plaster has a smooth, shiny and washable surface. The compound is environmentally protective and not harmful to health. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0019] Example 1

[0020] The reinforcing compound for waterproof plaster treatment contains 67% by weight of potassium silicate aqueous solution, 21% by weight of lithium silicate aqueous solution, 11% by weight of octyltriethoxysilane solution, 0.1% by weight of water glass stabilizer, and 0.9% by weight of colloidal silver aqueous solution with a concentration of 100 ppm.

[0021] The potassium silicate aqueous solution has a molar ratio of silica to potassium oxide of 1.7 and a density of 1660 kg / m 3 is within the range.

[0022] The lithium silicate solution has a molar mass ratio of silica to lithium oxide of 4.03 and a density of 1209 kg / m 3 It is.

[0023] The waterglass stabilizer is a hydrophilic alkoxyalkyl-ammonium salt in the form of a 98% aqueous solution of N,N,N',N'-tetrakis(2-hydroxypropyl)ethylenediamine.

[0024] Example 2

[0025] The reinforcing compound for waterproof plaster treatment contains 69% by weight of an aqueous potassium silicate solution, 20% by weight of an aqueous lithium silicate solution, 10% by weight of an octyltriethoxysilane solution and 1% by weight of a water glass stabilizer.

[0026] The potassium silicate aqueous solution has a molar ratio of silica to potassium oxide of 1.67 and a density of 1650 kg / m 3 is within the range.

[0027] The lithium silicate solution has a molar ratio of silica to lithium oxide of 3.8 and a density of 1100 kg / m 3 It is.

[0028] The waterglass stabilizer is a hydrophilic alkoxyalkyl-ammonium salt in the form of a 98% aqueous solution of N,N,N',N'-tetrakis(2-hydroxypropyl)ethylenediamine.

[0029] Example 3

[0030] The reinforcing compound for waterproof plaster treatment contains 68% by weight of potassium silicate aqueous solution, 20% by weight of lithium silicate aqueous solution, 10% by weight of octyltriethoxysilane solution, 1% by weight of water glass stabilizer, and 1% by weight of colloidal silver aqueous solution with a concentration of 100 ppm.

[0031] The potassium silicate aqueous solution has a molar ratio of silica to potassium oxide of 1.73 and a density of 1670 kg / m 3 is within the range.

[0032] The lithium silicate solution has a molar ratio of silica to lithium oxide of 4.1 and a density of 1300 kg / m 3 It is.

[0033] The waterglass stabilizer is a hydrophilic alkoxyalkyl-ammonium salt in the form of a 98% aqueous solution of N,N,N',N'-tetrakis(2-hydroxypropyl)ethylenediamine.

[0034] Example 4

[0035] The reinforcing compound for waterproof plaster treatment contains 69% by weight of an aqueous potassium silicate solution, 20% by weight of an aqueous lithium silicate solution, 10% by weight of an octyltriethoxysilane solution and 1% by weight of a water glass stabilizer.

[0036] The potassium silicate solution has a molar ratio of silica to potassium oxide of 1.69 and a density of 1655 kg / m 3 is within the range.

[0037] The lithium silicate solution has a molar mass ratio of silica to lithium oxide of 4.05 and a density of 1250 kg / m 3 It is.

[0038] The waterglass stabilizer is a hydrophilic alkoxyalkyl-ammonium salt in the form of a 98% aqueous solution of N,N,N',N'-tetrakis(2-hydroxypropyl)ethylenediamine.

[0039] Example 5

[0040] The reinforcing compound for waterproof plaster treatment contains 20% by weight of potassium silicate aqueous solution, 59.8% by weight of lithium silicate aqueous solution, 20% by weight of octyltriethoxysilane solution, 0.1% by weight of water glass stabilizer, and 0.1% by weight of colloidal silver aqueous solution with a concentration of 100 ppm.

[0041] The potassium silicate solution has a molar ratio of silica to potassium oxide of 1.69 and a density of 1660 kg / m 3 is within the range.

[0042] The lithium silicate solution has a molar ratio of silica to lithium oxide of 4.01 and a density of 1150 kg / m 3 It is.

[0043] The waterglass stabilizer is a hydrophilic alkoxyalkyl-ammonium salt in the form of a 98% aqueous solution of N,N,N',N'-tetrakis(2-hydroxypropyl)ethylenediamine.

[0044] Example 6

[0045] The reinforcing compound for waterproof plaster treatment contains 20% by weight of an aqueous potassium silicate solution, 59.9% by weight of an aqueous lithium silicate solution, 20% by weight of an octyltriethoxysilane solution and 0.1% by weight of a water glass stabilizer.

[0046] The potassium silicate solution has a molar ratio of silica to potassium oxide of 1.68 and a density of 1662 kg / m 3 is within the range.

[0047] The lithium silicate solution has a molar mass ratio of silica to lithium oxide of 4.03 and a density of 1211 kg / m 3 It is.

[0048] The waterglass stabilizer is a hydrophilic alkoxyalkyl-ammonium salt in the form of a 98% aqueous solution of N,N,N',N'-tetrakis(2-hydroxypropyl)ethylenediamine. [Industrial Applicability]

[0049] The plaster treating compounds according to the invention can be used for the surface treatment of plaster, in particular for the renovation of old plaster and for the renovation of plaster on damp walls.

Claims

1. A 20 to 69% by weight aqueous solution of potassium silicate; 20 to 59.9% by weight of an aqueous solution of lithium silicate; 10 to 20% by weight of octyltriethoxysilane solution; 0.1 to 1% by weight of a water glass stabilizer; and a 0.1 to 1% by weight aqueous colloidal silver solution, The water glass stabilizer is a hydrophilic alkoxyalkyl ammonium salt, A plaster treatment compound characterized in that the concentration of said aqueous colloidal silver solution is 100 ppm.

2. 2. The plaster treatment compound according to claim 1, wherein the aqueous potassium silicate solution has a molar mass ratio of silica to potassium oxide in the range of 1.67 to 1.

73.

3. A plaster treatment compound according to claim 1 or 2, characterized in that the density of the aqueous potassium silicate solution is in the range of 1650 to 1670 kg / m3.

4. A plaster treatment compound according to any one of claims 1 to 3, characterized in that the aqueous lithium silicate solution has a molar mass ratio of silica to lithium oxide in the range of 3.8 to 4.

1.

5. A plaster treatment compound according to any one of claims 1 to 4, characterised in that the density of the aqueous lithium silicate solution is in the range of 1100 to 1300 kg / m3.