Method for producing a water-soluble unit dose article comprising a water-soluble fibrous structure

Abstract

1. A method for making fibrous water soluble unit doses (30), comprising the steps of: a. delivering a fibrous web material (16), wherein the fibrous web material is delivered in the form of a continuous band (24) of fibrous web material; and b. cutting the fibrous web material transversely to form a repeating, nested pattern of transversely and identically shaped fibrous water soluble unit doses (30), wherein the fibrous water soluble unit doses are nested to form a repeating, nested pattern of transversely and identically shaped fibrous water soluble unit doses.

Description

[Technical field]

[0001] A method is provided for making a household care composition for delivering an active agent onto a fabric in the form of a water-soluble unit dose article comprising a water-soluble fibrous structure and one or more particles, the method comprising the steps of delivering a fibrous structure and cutting the fibrous structure using a mosaic shape to form a repeating nested pattern of nearly identically shaped fibrous structures. [Background technology]

[0002] Water-soluble unit dose articles are desired by consumers because they provide a convenient, efficient and clean way to dispense fabric or hard surface treatment compositions. Water-soluble unit dose articles provide a metered dose of treatment composition, thereby avoiding over-dosing or under-dosing. Consumers are increasingly interested in fibrous water-soluble unit dose articles. The technology associated with such articles continues to evolve in terms of providing desired active agents with articles that allow consumers to perform the tasks they are trying to accomplish.

[0003] The process of making fibrous water-soluble unit doses requires cutting the doses from a larger web, a process that can generate a significant amount of scrap. Summary of the Invention [Problem to be solved by the invention]

[0004] Therefore, it is desirable to find a way to nest shapes that can be more easily adapted to high-speed manufacturing processes.Surprisingly, it has been found that by utilizing repeating asymmetric products that can be nested in fibrous webs, mosaic shapes with repeating patterns can be created while minimizing scrap.Furthermore, the mosaic shape pattern reduces unnecessary or undesirable fragments that are incorporated into the final product or that interfere with the production of water-soluble unit dose articles. [Means for solving the problem]

[0005] The objects and advantages of the invention will be set forth in part in the description which follows, or may be obvious from the description, or may be learned through practice of the invention.

[0006] The present invention provides an improved method for making fibrous water soluble unit doses, the method comprising the steps of delivering a fibrous web material delivered in the form of a continuous strip of fibrous web material, and cutting the absorbent web material transversely to form a repeating, nested pattern of transversely and substantially identically shaped fibrous water soluble unit doses, the fibrous water soluble unit doses being nested to form a repeating, transversely and identically shaped fibrous water soluble unit dose pattern.

[0007] The present invention further provides a method for making fibrous water soluble unit doses, the method comprising the steps of delivering a fibrous web material delivered in the form of a continuous strip of fibrous web material, and cutting the absorbent web material transversely to form a repeating, nested pattern of substantially identically shaped fibrous water soluble unit doses in the transverse direction, the fibrous water soluble unit doses being nested to form a repeating transverse pattern of generally identically shaped fibrous water soluble unit doses, the fibrous water soluble unit doses being asymmetric in the longitudinal direction along the strip of fibrous web from which they are cut.

[0008] The method is explained in more detail below with reference to specific embodiments thereof. [Brief description of the drawings]

[0009] [Figure 1] The process of creating plies of material. [Diagram 2] 1 is a band of fibrous material showing a mosaic pattern of fibrous single unit doses. [Diagram 3] 1 is a band of fibrous material showing an alternating mosaic pattern of fibrous single unit doses. [Figure 4] 1 is a band of fibrous material showing an alternating mosaic pattern of fibrous single unit doses. [Diagram 5] 1 is a band of fibrous material showing an alternating mosaic pattern of fibrous single unit doses. [Figure 6] 1 is a band of fibrous material showing an alternating mosaic pattern of fibrous single unit doses. [Figure 7] 1 is a band of fibrous material showing an alternating mosaic pattern of fibrous single unit doses. [Figure 8] FIG. 1 illustrates a fibrous single unit dose depicting a band of non-mosaic fibrous material. [Figure 9] FIG. 1 shows a perspective view of a container having a lid embodying the new design. [Figure 10] FIG. 1 shows a front view of a container having a lid embodying the new design. [Figure 11] FIG. 1 shows a side view of a container having a lid embodying the new design. [Figure 12] FIG. 1 shows a side view of a container having a lid embodying the new design. [Figure 13] FIG. 1 shows a rear view of a container having a lid embodying the new design. [Figure 14] FIG. 1 shows a top view of a container with a lid embodying the new design. [Figure 15] FIG. 13 shows a bottom view of a container with a lid embodying the new design. [Figure 16] FIG. 16 shows the container of FIGS. 9 to 15 with the lid open. [Figure 17] FIG. 17 shows the container of FIG. 16 filled with the fibrous water-soluble unit dose shown in FIG. 2. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0010] definition Features and advantages of the present invention will become apparent from the following description, including examples intended to give a broad expression of the invention. Various modifications will become apparent to those skilled in the art from the specification and practice of the invention. The scope is not intended to be limited to the particular forms disclosed, but rather the invention covers all modifications, equivalents, and alternatives falling within the spirit and scope of the invention as defined by the claims.

[0011] As used herein, the articles including "the," "a," and "an," when used in a claim or the specification, are understood to mean one or more of what is claimed or described.

[0012] As used herein, the terms "include", "includes" and "including" are meant to be open-ended.

[0013] As used herein, the terms "substantially free of" or "substantially free from" refer simply to either a complete absence or minimal amount of a component as an impurity or unintended by-product of another component. A composition that is "substantially free of" a component means that the composition contains less than about 0.5%, 0.25%, 0.1%, 0.05%, or 0.01%, or even 0%, by weight of the composition, of that component.

[0014] It should be understood that the term "comprising" also includes embodiments in which the term "comprising" means "consisting of" or "consisting essentially of".

[0015] As used herein, "sebum" refers to the oily secretion of the sebaceous gland and any artificial composition intended to replicate the oily secretion of the sebaceous gland. Representative sebum includes, but is not limited to, the artificial sebum described in EP 1482907, the artificial sebum described in EP 0142830, the artificial sebum according to D4265-14, and the artificial sebum sold as CFT PCS-132. CFT PCS-132 has an estimated composition of 18% free fatty acids, 32% beef tallow (stearic / oleic triglyceride), 4% fatty acid triglycerides, 12% hydrocarbon mixture, 18% lanolin (wax esters, C13-C24), 12% Cutina (wax and wax esters), and 4% cholesterol.

[0016] All cited patents and other publications are, in relevant part, incorporated by reference as if fully restated herein. The citation of any patent or other publication is not an admission that the cited patent or other publication is prior art to the present invention.

[0017] In this specification, all concentrations and percentages are by weight of the composition unless otherwise stated.

[0018] It should be understood that every maximum numerical limitation given throughout this specification includes every lower numerical limitation, as if such lower numerical limitations were expressly written herein. Every minimum numerical limitation given throughout this specification is intended to include every higher numerical limitation, as if such higher numerical limitations were expressly written herein. Every numerical range given throughout this specification will include every narrower numerical range that falls within such broader numerical range, as if such narrower numerical ranges were all expressly written herein.

[0019] The present invention provides an improved method for making fibrous water-soluble unit doses having a longitudinally asymmetric shape. The fibrous water-soluble unit doses are longitudinally asymmetric along the fibrous web from which they are cut. The method provides a technique for mass-producing such fibrous water-soluble unit doses from a continuous strip of fibrous web material in a manner that results in substantially zero waste of web material.

[0020] According to one embodiment of the method, the fibrous web material is delivered in a machine direction stream, for example from a supply roll, in the form of a continuous band or a series of adjacent bands. In other words, the parallel sides of the band of material are in the machine direction. The absorbent web material is cut transversely to form a repeating nested pattern of transversely and generally identically shaped fibrous water soluble unit doses. The fibrous water soluble unit doses are nested in that they form a repeating pattern along the cross section of the fibrous web. The fibrous water soluble unit doses are asymmetric along the length of the band of material or along the longitudinal centerline of each fibrous water soluble unit dose.

[0021] Adjacent fibrous water-soluble unit doses share a common defining cut line so that there is no waste of absorbent material between the fibrous water-soluble unit doses. Each pad is longitudinally asymmetrical with respect to the crotch and back. For example, in one particular embodiment, the rear portion of the pad includes ears that define the widest width of the pad, and a crotch region of smaller width extends longitudinally from the ears and rear portion.

[0022] The fibrous water soluble unit doses are defined across the band of fibrous web material such that each fibrous water soluble unit dose has a longitudinal length that is less than the transverse width of the web material, however, in this embodiment, nested pairs of fibrous water soluble unit doses have a combined nested longitudinal length that is equal to the transverse width of the fibrous web material.

[0023] The fibrous water-soluble unit dose comprises an upper ridge and a lower ridge. The upper ridge and the lower ridge serve one or more of a number of possible purposes, including altering the interaction between the fibrous water-soluble unit dose and the container that contains the fibrous water-soluble unit dose. The upper ridge, the lower ridge, or both can be utilized to pretreat the fabric.

[0024] The method is explained in more detail below with reference to specific embodiments thereof.

[0025] Fibrous water-soluble unit dose article As used herein, the phrases "water soluble unit dose article," "water soluble fibrous structure," and "water soluble fibrous element" mean that the unit dose article, fibrous structure, and fibrous element are miscible with water. In other words, the unit dose article, fibrous structure, or fibrous element can form a homogeneous solution with water at ambient conditions. As used herein, "ambient conditions" means 23°C ± 1.0°C and 50% ± 2% relative humidity. The water soluble unit dose article may contain insoluble materials that are dispersible at aqueous wash conditions with a suspended mean particle size of less than about 20 micrometers or less than about 50 micrometers.

[0026] The fibrous water soluble unit dose can include any of the disclosures found in U.S. patent application Ser. No. 15 / 880,594, filed Jan. 26, 2018, Ser. No. 15 / 880,599, filed Jan. 26, 2018, and Ser. No. 15 / 880,604, filed Jan. 26, 2018, which are incorporated by reference in their entireties.

[0027] These fibrous water-soluble unit dose articles can dissolve under various washing conditions, such as low temperature, low water volume and / or short wash cycles or cycles where the consumer overloads the washing machine, especially items with high water absorption capacity, while delivering sufficient active agent to exert the intended effect on the target consumer substrate (with performance similar to today's liquid products). Moreover, the water-soluble unit dose articles described herein can be economically manufactured by spinning fibers containing the active agent. The water-soluble unit dose articles described herein also have improved cleaning performance.

[0028] The surface of the fibrous water-soluble unit dose article may include a printed area. The printed area may cover from about 10% to about 100% of the surface of the article. The printed area may include ink, pigment, dye, bluing agent, or mixtures thereof. The printed area may be opaque, translucent, or transparent. The printed area may include a single color or multiple colors. The printed area may be on more than one side of the article and may include explanatory text and / or graphics. The surface of the water-soluble unit dose article may include an aversive agent, such as a bittering agent. Suitable bittering agents include, but are not limited to, naringin, sucrose octaacetate, quinine hydrochloride, denatonium benzoate, or mixtures thereof. Any suitable concentration of the aversive agent may be used. Suitable concentrations include, but are not limited to, 1 to 5000 ppm, or even 100 to 2500 ppm, or even 250 to 2000 ppm.

[0029] The water-soluble unit dose article disclosed herein comprises a water-soluble fibrous structure and one or more particles. The water-soluble fibrous structure may comprise a plurality of fibrous elements, e.g., a plurality of filaments. One or more particles, e.g., one or more active agent-containing particles, may be distributed throughout the structure. The water-soluble unit dose article may comprise a plurality of two or more and / or three or more fibrous elements that are intertwined or otherwise associated with each other to form a fibrous structure, and one or more particles may be distributed throughout the fibrous structure.

[0030] The fibrous water soluble unit dose article may exhibit a thickness, when measured by the Thickness Test Method described herein, of greater than 0.01 mm, and / or greater than 0.05 mm, and / or greater than 0.1 mm, and / or about 100 mm or less, and / or about 50 mm or less, and / or about 20 mm or less, and / or about 10 mm or less, and / or about 5 mm or less, and / or about 2 mm or less, and / or about 0.5 mm or less, and / or about 0.3 mm or less.

[0031] The fibrous water-soluble unit dose article has a basis weight of about 500 grams / m2 when measured according to the basis weight test method described herein. 2 ~ approx. 5,000 g / m 2 , or about 1,000 grams / m 2 ~ approx. 4,000g / m 2 , or about 1,500 grams / m 2 ~ approx. 3,500 g / m 2 , or about 2,000 grams / m 2 ~ approx. 3,000 g / m 2 The sheet may have a basis weight of 100 g.

[0032] The fibrous water-soluble unit dose article may include a water-soluble fibrous structure and a plurality of particles distributed throughout the structure, the water-soluble fibrous structure including a plurality of fibrous elements that are identical or substantially identical from a compositional point of view. The water-soluble fibrous structure may include two or more different fibrous elements. Non-limiting examples of the differences between the fibrous elements may be physical differences such as different diameters, lengths, textures, shapes, stiffness, elasticity; chemical differences such as crosslinking levels, solubility, melting points, Tg, active agents, filament-forming materials, colors, active agent concentrations, basis weights, filament-forming materials concentrations, the presence of any coatings on the fibrous elements, biodegradable or not, hydrophobic or not, contact angles; differences in whether the fibrous elements lose their physical structure when exposed to intended conditions of use; differences in whether the morphology of the fibrous elements changes when exposed to intended conditions of use, and differences in the rate at which the fibrous elements release one or more of their active agents when exposed to intended conditions of use. Two or more fibrous elements in the fibrous structure may include different active agents. This may be the case when different active agents, such as anionic surfactants and cationic polymers, may be incompatible with one another. When using different fibrous elements, the resulting structures may exhibit different wetting, water absorption, and solubility characteristics.

[0033] The fibrous water soluble unit dose article may exhibit different regions, such as regions of different basis weight, density, caliper, and / or wetting characteristics. The fibrous water soluble unit dose article may be compressed at the end seal points. The fibrous water soluble unit dose article may include texture on one or more of its surfaces. The surface of the fibrous water soluble unit dose article may include a pattern, such as a non-random repeating pattern. The fibrous water soluble unit dose article may include openings. The fibrous water soluble unit dose article may include a fibrous structure having discrete regions of fibrous elements that are distinct from other regions of the fibrous elements in the structure. The fibrous water soluble unit dose article may be used as is or may be coated with one or more active agents.

[0034] The fibrous water-soluble unit dose article may include one or more plies. The fibrous water-soluble unit dose article may include at least two, and / or at least three, and / or at least four, and / or at least five plies. The fibrous plies may be fibrous structures. Each ply may include one or more layers, such as one or more fibrous element layers, one or more particle layers, and / or one or more fibrous element / particle mixture layers. The layers may be sealed. In particular, the particle layer and the fibrous element / particle mixture layer may be sealed to prevent particles from leaking out. The water-soluble unit dose article may include multiple plies, each ply including two layers, one layer being a fibrous element layer and one layer being a fibrous element / particle mixture layer, and the multiple plies are sealed together (e.g., at the edges). In addition to preventing particles from leaking out, the sealing may help the unit dose article maintain its original structure. However, when the water-soluble unit dose article is added to water, the unit dose article dissolves and releases particles into the washing liquid.

[0035] The fibrous elements and / or particles may be arranged within a water-soluble unit dose article, within a single ply, or within multiple plies to provide the article with two or more regions containing different active agents, for example, one region of the article may contain a bleaching agent and / or a surfactant, and another region of the article may contain a softener.

[0036] The water-soluble unit dose articles described herein may comprise a water-soluble fibrous structure and one or more rheology modifying particles comprising (a) about 10% to about 80% by weight of an alkyl alkoxylated sulfate and (b) about 0.5% to about 20% by weight of a rheology modifying agent. The particles described herein may comprise one or more additional active agents (in addition to the surfactants described above).

[0037] Rheology-modifying particles include: (a) about 10% to about 80% by weight of an alkyl alkoxylated sulfate; (b) about 0.5% to about 20% by weight of a rheology modifier selected from the group consisting of an alkoxylated amine, preferably an alkoxylated polyamine, more preferably a quaternized or non-quaternized alkoxylated polyethyleneimine, the alkoxylated polyalkyleneimine having a polyalkyleneimine core having one or more alkoxy side chains attached to at least one nitrogen atom in the polyalkyleneimine core, an ethylene oxide-propylene oxide-ethylene oxide (EOx1POyEOx2) triblock copolymer, where each of x1 and x2 ranges from about 2 to about 140, and y ranges from about 15 to about 70, and mixtures thereof.

[0038] As used herein, the term "rheology modifier" refers to a material that interacts with a concentrated surfactant, preferably a concentrated surfactant having a mesophase structure, to substantially reduce the viscosity and elasticity of the concentrated surfactant. Suitable rheology modifiers include, but are not limited to, sorbitol ethoxylates, glycerol ethoxylates, sorbitan esters, tallow alkyl ethoxylated alcohols, ethylene oxide-propylene oxide-ethylene oxide (EOx1POyEOx2) triblock copolymers, where each of x1 and x2 ranges from about 2 to about 140, and y ranges from about 15 to about 70, alkoxylated amines, alkoxylated polyamines, polyethyleneimine (PEI), alkoxylated variants of PEI, preferably ethoxylated PEI, and mixtures thereof. The rheology modifier may include one of the above polymers, for example, ethoxylated PEI, in combination with polyethylene glycol (PEG) having a weight average molecular weight of about 2,000 Daltons to about 8,000 Daltons.

[0039] As used herein, the term "functional rheology modifier" refers to a rheology modifier having additional detergent functionality. In some cases, the dispersant polymers described herein below may also function as functional rheology modifiers. The functional rheology modifiers may be present in the detergent particles of the present invention at a concentration of about 0.5% to about 20% by weight of the composition, preferably about 1% to about 15% by weight, more preferably about 2% to about 10% by weight.

[0040] Without being bound by theory, it is believed that functional rheology modifiers can interact with the molecular structure of mesophase surfactants, particularly alcohol-based anionic sulfate surfactants, and that the mesophase has more water than solid-phase surfactants and less water than the micellar phase characteristic of wash solutions. In other words, mesophase surfactants represent the transition state from solid to micellar phase that can be achieved in the successful use of fibrous water-soluble unit dose articles that include water-soluble fiber structures and particles, and if the rheology of this mesophase is too viscous or sticky, undesirable residues may be formed on fabrics under conditions of insufficient local dilution and / or insufficient shear. By substantially reducing the viscosity and elasticity of the mesophase, the rheology modifiers aid in dispersion, reducing the risk of residues forming on fabrics. Furthermore, for any residues that may form, such as clumpy gels, the rheology modifiers can reduce their persistence. The net effect is to reduce the occurrence of surfactant residues that remain on fabrics through washing.

[0041] Alkoxylated amines: The alkoxylated amines may be partially or fully protonated or unprotonated over the pH range of the concentrated surfactant mixture. Alternatively, the alkoxylated amines may be partially or fully quaternized. The alkoxylated amines may be unquaternized. The alkoxylated amines may contain ethoxylate (EO) groups.

[0042] The alkoxylated amines can be linear, branched, or a combination thereof, preferably branched.

[0043] Alkoxylated amines may contain two or more amine moieties, such as N,N,N',N'-tetra(2-hydroxyethyl)ethylenediamine (also described as a class of hydroxyalkylamines), which also function as chelating agents.

[0044] The alkoxylated amine may (or may be) an alkoxylated amine including an alkoxylated polyalkyleneimine. The alkoxylated polyalkyleneimine may be an alkoxylated polyethyleneimine (PEI).

[0045] Typically, the alkoxylated polyalkyleneimine polymer comprises a polyalkyleneimine backbone. The polyalkylimine may comprise a C2 alkyl group, a C3 alkyl group, or a mixture thereof, preferably a C2 alkyl group. The alkoxylated polyalkyleneimine polymer may have a polyethyleneimine ("PEI") backbone.

[0046] The alkoxylated PEI may comprise a polyethyleneimine backbone having a weight average molecular weight of about 400 to about 1000, or about 500 to about 750, or about 550 to about 650, or about 600, as measured before ethoxylation.

[0047] The PEI backbone of the polymers described herein, prior to alkoxylation, has the following general empirical formula:

[0048] [ka] It may have where B represents the continuation of this structure by branching. In some embodiments, n+m is 8, or 10, or 12, or 14, or 18, or 22 or more.

[0049] The alkoxylated polyalkylenimine polymer comprises an alkoxylated nitrogen group. The alkoxylated polyalkylenimine polymer may independently comprise an average of about 50 or less, or about 40 or less, or about 35 or less, or about 30 or less, or about 25 or less, or about 20 or less alkoxylate groups per alkoxylated nitrogen. The alkoxylated polyalkylenimine polymer may independently comprise an average of at least about 5, or at least about 10, or at least about 15, or at least about 20 alkoxylate groups per alkoxylated nitrogen.

[0050] The alkoxylated polyalkylenimine polymer, preferably the alkoxylated PEI, may contain an ethoxylate (EO) group, a propoxylate (PO) group, or a combination thereof. The alkoxylated polyalkylenimine polymer, preferably the alkoxylated PEI, may contain an ethoxylate (EO) group. The alkoxylated polyalkylenimine polymer, preferably the alkoxylated PEI, may not contain a propoxylate (PO) group.

[0051] The alkoxylated amine, preferably the alkoxylated polyalkylenimine polymer, more preferably the alkoxylated PEI, may contain, on average, about 1-50 ethoxylate (EO) groups and about 0-5 propoxylate (PO) groups per alkoxylated nitrogen. The alkoxylated polyalkylenimine polymer, preferably the alkoxylated PEI, may contain, on average, about 1-50 ethoxylate (EO) groups and no propoxylate (PO) groups per alkoxylated nitrogen. The alkoxylated polyalkylenimine polymer, preferably the alkoxylated PEI, may contain, on average, about 10-30 ethoxylate (EO) groups, preferably about 15-25 ethoxylate (EO) groups per alkoxylated nitrogen.

[0052] Suitable polyamines include low molecular weight, water-soluble, lightly alkoxylated ethoxylated / propoxylated polyalkyleneamine polymers. By "lightly alkoxylated," it is meant that the polymers of the present invention have an average of about 0.5 to about 20, or 0.5 to about 10, alkoxylations per nitrogen. The polyamines may be "substantially uncharged," meaning that there are no more than about 2 positive charges for every about 40 nitrogens present in the backbone of the polyalkyleneamine polymer at pH 10 or pH 7. However, it is recognized that the charge density of the polymer may vary with pH.

[0053] Suitable alkoxylated polyalkyleneimines, such as PEI600 EO20, are available from BASF (Ludwigshafen, Germany).

[0054] Ethylene oxide-propylene oxide-ethylene oxide (EOx1POyEOx2) triblock copolymer: In the ethylene oxide-propylene oxide-ethylene oxide (EOx1POyEOx2) triblock copolymer, each of x1 and x2 is in the range of about 2 to about 140, and y is in the range of about 15 to about 70. The ethylene oxide-propylene oxide-ethylene oxide (EOx1POyEOx2) triblock copolymer preferably has an average propylene oxide chain length of 20 to 70, preferably 30 to 60, more preferably 45 to 55 propylene oxide units.

[0055] Preferably, the ethylene oxide-propylene oxide-ethylene oxide (EOx1POyEOx2) triblock copolymer has a weight average molecular weight of about 1000 to about 10,000 daltons, preferably about 1500 to about 8000 daltons, more preferably about 2000 to about 7000 daltons, even more preferably about 2500 to about 5000 daltons, and most preferably about 3500 to about 3800 daltons.

[0056] Preferably, each ethylene oxide block or chain independently has an average chain length of from 2 to 90, preferably from 3 to 50, more preferably from 4 to 20 ethylene oxide units.

[0057] Preferably, the copolymer comprises 10% to 90%, preferably 15% to 50%, and most preferably 15% to 25% by weight of the copolymer of the combined ethylene oxide block. Most preferably, the total ethylene oxide content is divided equally between the two ethylene oxide blocks. By divided equally in this specification, it is meant that each ethylene oxide block contains on average 40% to 60%, preferably 45% to 55%, even more preferably 48% to 52%, and most preferably 50% of the total number of ethylene oxide units, with the % of both ethylene oxide blocks adding up to 100%. Some ethylene oxide-propylene oxide-ethylene oxide (EOx1POyEOx2) triblock copolymers, where each of x1 and x2 ranges from about 2 to about 140 and y ranges from about 15 to about 70, improve cleaning properties.

[0058] Preferably, the copolymer has a weight average molecular weight of about 3500 to about 3800 daltons, a propylene oxide content of 45 to 55 propylene oxide units, and an ethylene oxide content of 4 to 20 ethylene oxide units per ethylene oxide block.

[0059] Preferably, the ethylene oxide-propylene oxide-ethylene oxide (EOx1POyEOx2) triblock copolymer has a weight average molecular weight of 1000 to 10,000 Daltons, preferably 1500 to 8000 Daltons, more preferably 2000 to 7500 Daltons. Preferably, the copolymer comprises 10% to 95%, preferably 12% to 90%, most preferably 15% to 85% by weight of the copolymer of multiple ethylene oxide blocks. Some ethylene oxide-propylene oxide-ethylene oxide (EOx1POyEOx2) triblock copolymers, where each of x1 and x2 ranges from about 2 to about 140 and y ranges from about 15 to about 70, improve dissolution.

[0060] Suitable ethylene oxide-propylene oxide-ethylene oxide triblock copolymers are commercially available from BASF as the Pluronic PE series or from Dow Chemical as the Tergitol L series. A particularly suitable material is Pluronic PE 9200.

[0061] Alkylalkoxylated sulfate: The alkylalkoxylated sulfate (AAS) is an alkylethoxylated sulfate (AES), preferably an ethoxylated C 2 alkoxylate having an average degree of ethoxylation of about 0.5 to about 3.0. 12 ~C 18 It may be an alkyl sulfate.

[0062] Typically, the weight ratio of alkyl alkoxylated sulfate to rheology modifier ranges from 4:1 to 40:1. The weight ratio of alkyl alkoxylated sulfate to rheology modifier may depend on the molecular weight of the alkyl alkoxylated sulfate alcohol precursor, the degree of alkoxylation, and the blend ratio of LAS / AES in the blended surfactant system. For example, for an ethoxylation degree of about 1.0 (e.g., NaAE1S), a NaLAS / NaAE1S blend ratio of about 1 / 3, and an AE1 alcohol precursor with a carbon chain length blend of 12 to 15, the functional rheology modifier / NaAE1S mass ratio may be at least about 4% to improve dissolution, such as 5% to 10%. For higher MW alcohol precursors with a carbon chain length blend of 14 to 15, the preferred functional rheology modifier / NaAE1S mass ratio may be at least about 9%, such as 9% to 20%. The concentration of the functional rheology modifier can be adjusted to maintain product dissolution over a wide range of possible anionic surfactant materials and blend ratios.

[0063] The mass of the rheology modifier (RM) relative to the mass of the NaAES surfactant can follow the relationship: RM / NaAES≧f(alc) / (a *(LAS / AES)+b), where f(alc) is a function of the structure and molecular weight of the alcohol used to make the AES surfactant, (LAS / AES) is the blend ratio of LAS to AES in the surfactant paste, a is ∼30, and b is ∼2. For a reference blend of predominantly C12-C15 linear alcohol ethoxylates (C25AE1), f(alc) is ∼1.0, and for a reference blend of predominantly C14-C15 linear alcohol ethoxylates (C45AE1), f(alc) is ∼1.2. The above guidelines are further dependent on the degree of ethoxylation and any branching structure of the ethoxylated alcohol precursors to the AES surfactant. The above guidelines can be expressed as a guidance ratio, where a value of ≥1 may indicate improved dissolution and a value of <1 may indicate worse dissolution. The guidance ratio is calculated as (RM / NaAES) / (f(alc) / (30 * (LAS / AES)+2).

[0064] The particles may comprise from about 15% to about 60%, or from 20% to 40% by weight of the alkyl alkoxylated sulfate, or from 30% to 80%, or even from 50% to 70% by weight of the alkyl alkoxylated sulfate.

[0065] The particles may include an alkylbenzene sulfonate, such as a linear alkylbenzene sulfonate (LAS). The particles may include 1% to 50% by weight of the alkylbenzene sulfonate, or 5% to 30% by weight of the alkylbenzene sulfonate.

[0066] The particles may have a particle size distribution such that D50 is greater than about 150 micrometers and less than about 1700 micrometers. The particles may have a particle size distribution such that D50 is greater than about 212 micrometers and less than about 1180 micrometers. The particles may have a particle size distribution such that D50 is greater than about 300 micrometers and less than about 850 micrometers. The particles may have a particle size distribution such that D50 is greater than about 350 micrometers and less than about 700 micrometers. The particles may have a particle size distribution such that D20 is greater than about 150 micrometers and D80 is less than about 1400 micrometers. The particles may have a particle size distribution such that D20 is greater than about 200 micrometers and D80 is less than about 1180 micrometers. The particles may have a particle size distribution such that D20 is greater than about 250 micrometers and D80 is less than about 1000 micrometers. The particles may have a particle size distribution such that D10 is greater than about 150 micrometers and D90 is less than about 1400 micrometers. The particles may have a particle size distribution such that D10 is greater than about 200 micrometers and D90 is less than about 1180 micrometers. The particles may have a particle size distribution such that D10 is greater than about 250 micrometers and D90 is less than about 1000 micrometers.

[0067] The particles may be used in bead-like detergents or derivatives thereof. The particles may have a particle size distribution such that D50 is greater than about 1 mm and less than about 4.75 mm. The particles may have a particle size distribution such that D50 is greater than about 1.7 mm and less than about 3.5 mm. The particles may have a particle size distribution such that D20 is greater than about 1 mm and D80 is less than about 4.75 mm. The particles may have a particle size distribution such that D20 is greater than about 1.7 mm and D80 is less than about 3.5 mm. The particles may have a particle size distribution such that D10 is greater than about 1 mm and D90 is less than about 4.75 mm. The particles may have a particle size distribution such that D10 is greater than about 1.7 mm and D90 is less than about 3.5 mm.

[0068] Particle size distribution is measured according to Applicants' Particle Size Distribution Test Method.

[0069] The particles may contain from about 10% to about 80% by weight, preferably from about 20% to about 60% by weight, and preferably from about 30% to about 50% by weight of detergent builder.

[0070] The particles may contain about 2% to about 40% by weight, preferably about 5% to about 30% by weight, and preferably about 10% to about 20% by weight of the buffering agent.

[0071] The particles may contain from about 2% to about 20% by weight, preferably from about 5% to about 10% by weight, of the chelating agent.

[0072] The particles may contain from about 2% to about 20% by weight, preferably from about 5% to about 10% by weight, of the dispersant polymer.

[0073] The particles may contain 0.5% to 15% by weight of soluble film or fiber structuring polymer. Examples of soluble film or fiber structuring polymers include, but are not limited to, polyvinyl alcohol, polyvinylpyrrolidone, polyethylene oxide, modified starch or cellulose polymers, and mixtures thereof. Such polymers may be present in product recycling streams that contain unit dose products that contain soluble fiber or film materials, such as pouch materials, in which case it is advantageous to incorporate the recycled materials into the particles.

[0074] The particles may have a density of less than 500 g / L. The particles may have a density of less than 450 g / L, such as 50 g / L to 450 g / L, 100 g / L to 400 g / L, 150 g / L to 350 g / L, 200 g / L to 400 g / L, 250 g / L to 400 g / L, or 300 g / L to 400 g / L.

[0075] The particles may have a density of 250 g / L to 400 g / L, but may have a particle size distribution such that D10 is greater than about 300 micrometers and D90 is less than about 1100 micrometers. The particles may have a particle size distribution such that D10 is between 300 and 500 micrometers.

[0076] Applicants have discovered that by using low density particles that fall within the desired size distribution, they can deliver similar levels of surfactant as denser particles while significantly increasing the dissolution rate and availability of the surfactant.

[0077] In addition, the use of low density high activity particles allows for the use of increased amounts of particles, thereby delivering higher levels of particle percentage as a function of total finished pad weight percentage.

[0078] Furthermore, as shown in Table 5, the LAS surfactant can be significantly increased to more than 20% of the total textile product, for example, 20% to 40%, by using low density particles.

[0079] The rheology modified particles may be coated or at least partially coated with a layer composition, for example as disclosed in US Patent Application Publication No. 2007 / 0196502. Preferably, the layer composition includes a non-surfactant active. More preferably, the non-surfactant active is selected from the group consisting of builders, buffers, and dispersant polymers. Even more preferably, the non-surfactant active is selected from the group consisting of zeolite A, sodium carbonate, sodium bicarbonate, and soluble polycarboxylate polymers. This is particularly advantageous when the active (AES as a non-limiting example) is suitable for cleaning under cold water and / or high hardness wash water conditions. The presence of the active in the layer promotes initial dissolution of the cold water and / or hardness resistant chemicals. Without being bound by theory, it is hypothesized that dissolution of cold water and hardness resistant chemicals in a faster order can protect more of the conventional cleaning actives (LAS surfactant as a non-limiting example), resulting in better overall cleaning performance.

[0080] Rheology-modifying particle fabrication process A concentrated aqueous paste containing a mixture of alkyl alkoxylated sulfate anionic detergent surfactant and a rheology modifier, preferably a functional rheology modifier, can be used to make rheology modified detergent particles according to a paste agglomeration process, which includes the steps of: (a) adding powdered raw materials into a mixer granulator, which may include one or more dry builders, buffers, dispersant polymers or chelating agents, necessary powder processing aids, and fines recycled from the agglomeration process; (b) adding a paste containing a premix of concentrated surfactant and functional rheology modifier; (c) running the mixer granulator to disperse the powders in the paste and provide a suitable mixing flow field to form agglomerates; and, optionally, (d) adding additional powdered ingredients to at least partially coat the agglomerates and remove any excess powder from the surface. (e) optionally drying the resulting agglomerates in a fluid bed dryer to remove excess water, (f) optionally cooling the agglomerates in a fluid bed cooler, (g) removing any excess fines from the particle size distribution of the agglomerates, preferably by elutriation from the fluid bed of steps e and / or f, and recycling the fines back to step a, (h) removing excess oversized particles from the particle size distribution of the agglomerates, preferably by sieve classification, and (i) grinding the oversized particles and recycling the ground particles to steps a, e, or f. The paste agglomeration process may be a batch or continuous process.

[0081] Variations of the above preferred embodiment may include adding additional LAS co-surfactant in a separate stream from the premixed surfactant paste in step (b). Process options include adding pre-neutralized LAS as a solid powder in step (a), adding neutralized or partially neutralized LAS paste as a supplementary material in step (b), or adding a liquid acid precursor (HLAS) as a supplementary material in step (b). In the latter case, sufficient free alkali must be present in the powder added in step (a) to effectively neutralize the HLAS during the aggregation process. Alternatively, neutralization of the HLAS may be performed in a separate pretreatment step, where the HLAS is first premixed with the alkaline buffer powder component and any other solid carriers to form a neutralized premix of LAS and alkaline buffer powder in powder form, which is then added in step (a) above.

[0082] As shown in the table below, it has surprisingly been found that by adding LAS in particulate form to a separate surfactant slurry during the particle aggregation process, particles can be created that have LAS to AES ratios greater than 1, e.g., 1.01-3.0, 1.05-2.5, 1.1-2.0, 1.2-1.8, etc. These particles can achieve lower densities while increasing the amount of readily available LAS. When combined with a web containing LAS, the total product LAS to AES ratio can be greater than 1.0, e.g., 1.01-3.0, 1.05-2.5, 1.1-2.0, 1.2-1.8, etc., as shown in the table below.

[0083] Alternatively, a concentrated aqueous paste containing a mixture of alkyl alkoxylated sulfate anionic detersive surfactant and rheology modifier may be used, extrusion processes being well known in the art.

[0084] Alternatively, the rheology modifier may be used as a binder in the aggregation process to make the rheology modified detergent particles.

[0085] Surprisingly, the rheology modified particles are finer and stronger than the same particles without the rheology modifier.

[0086] pH adjuster The single unit dose may include one or more basic pH adjusters that increase the pH of the irrigation solution to a pH greater than 8. Suitable basic pH adjusters include, but are not limited to, compounds that include sulfate ions, dihydrogen phosphate ions, fluoride ions, nitrite ions, acetate ions, bicarbonate ions, hydrogen sulfide ions, ammonia, carbonate ions, hydroxide ions, and combinations thereof. The inclusion of a basic pH adjuster does not exclude the inclusion of an acidic pH adjuster, such as citric acid. The single unit dose may include an acidic pH adjuster, provided that the final pH of the irrigation solution is greater than 8, such as, for example, 8.2, 8.4, 8.6, 8.8, 9, 9.2, 9.4, 9.6, 9.8, 10, 10.2, 10.4, 10.6, 10.8, 11, 11.2, 11.4, 11.6, 11.8, 12, 12.2, 12.4, 12.6, 12.8, or 13.

[0087] Concentrated Surfactant Paste The concentrated surfactant paste is an intermediate composition that can be combined with other ingredients to form rheology modifying particles. The concentrated surfactant composition may comprise, consist essentially of, or consist of the following ingredients: a surfactant system, which may include an alkyl alkoxylated sulfate surfactant; a rheology modifier as described herein; an organic solvent system, and water. These ingredients are described in more detail below.

[0088] The concentrated surfactant composition may comprise: a surfactant system at about 70% to about 90% by weight of the composition, the surfactant system comprising from about 50%, or from about 60%, or from about 70%, or from about 80% to about 100% of an alkyl alkoxylated sulfate surfactant; a rheology modifier at about 0.1% to about 25% by weight of the composition; an organic solvent system at less than about 5% by weight of the composition; and water. The surfactant system of the paste preferably comprises a LAS co-surfactant. When LAS is included in the surfactant system, the ratio of LAS:AES may be from about 0 to about 1, preferably from about 0.2 to about 0.7, more preferably from about 0.25 to about 0.35, and even more preferably from 0.3 to about 0.6.

[0089] Solid carrier: Suitable solid carriers include inorganic salts such as sodium carbonate, sodium sulfate, and mixtures thereof. Other preferred solid carriers include aluminosilicates such as zeolites, dry dispersant polymers in fine powder form, and absorbent grade fumed or precipitated silica (e.g., precipitated hydrophilic silica marketed under the trade name SN340 by Evonik Industries AG). Mixtures of solid carrier materials may also be used.

[0090] Fiber Structure The fibrous structure includes one or more fibrous elements. The fibrous elements can be associated with one another to form a structure. The fibrous structure can include particles within and / or on the structure. The fibrous structure can be homogenous, layered, single, zoned, or otherwise as desired, with different active agents defining various of the aforementioned portions.

[0091] The fibrous structure may include one or more layers, which together form a ply.

[0092] Textile elements The fibrous elements can be water soluble. The fibrous elements can include one or more filament-forming materials and / or one or more active agents, such as a surfactant. The one or more active agents can be releasable from the fibrous elements, such as when the fibrous elements and / or the fibrous structure including the fibrous elements are exposed to intended conditions of use.

[0093] Fibrous elements of the present invention can be spun from a filament-forming composition, also referred to as a fibrous element-forming composition, via a suitable spinning process operation (e.g., meltblowing, spunbonding, electrospinning, and / or rotary spinning, etc.).

[0094] As used herein, "filament-forming composition" and / or "fibrous element-forming composition" refer to a composition suitable for producing fibrous elements of the present invention, such as by meltblowing and / or spunbonding. The filament-forming composition includes one or more filament-forming materials that exhibit properties that make the material suitable for spinning into fibrous elements. The filament-forming materials may include polymers. In addition to the one or more filament-forming materials, the filament-forming composition may include one or more active agents, such as surfactants. Furthermore, the filament-forming composition may include one or more polar solvents (such as water) in which one or more, such as all of the filament-forming materials and / or one or more, such as all of the active agents, are dissolved and / or dispersed prior to spinning the fibrous elements (such as filaments derived from the filament-forming composition).

[0095] The filament-forming composition may include two or more different filament-forming materials. Thus, the fibrous elements may be monocomponent (one type of filament-forming material) and / or multicomponent, such as bicomponent. Two or more different filament-forming materials may be randomly combined to form the fibrous elements. Two or more different filament-forming materials may be regularly combined to form the fibrous elements, such as sheath-core bicomponent fibrous elements, which are not considered to be a random mixture of different filament-forming materials for the purposes of this disclosure. The bicomponent fibrous elements may be in any form, such as side-by-side, sheath-core, islands-in-the-sea, etc.

[0096] The fibrous elements may be substantially free of alkyl alkoxylated sulfate. Each fibrous element may contain about 0%, or about 0.1%, or about 5%, or about 10%, or about 15%, or about 20%, or about 25%, or about 30%, or about 35%, or about 40% to about 0.2%, or about 1%, or about 5%, or about 10%, or about 15%, or about 20%, or about 25%, or about 30%, or about 35%, or about 40%, or about 50% by weight of alkyl alkoxylated sulfate, based on the dry fibrous element. The amount of alkyl alkoxylated sulfate in each of the fibrous elements is small enough so as not to affect its processing stability and film solubility. Alkyl alkoxylated sulfates, when dissolved in water, can undergo a highly viscous hexagonal phase at certain concentration ranges, e.g., 30-60% by weight, resulting in a gel-like material. Thus, when incorporated in significant amounts into fiber elements, alkyl alkoxylated sulfates can significantly slow down the dissolution of water-soluble unit dose articles in water, or even worse, leave undissolved solids behind. Correspondingly, most of these surfactants are formulated into particles.

[0097] Each fibrous element may contain at least one filament-forming material and an active agent, preferably a surfactant. The surfactant may have a relatively low hydrophilicity because such surfactants are less likely to form a viscous gel-like hexagonal phase when diluted. The use of such surfactants in the formation of the filaments can effectively reduce gel formation during washing, which in turn can result in faster dissolution and less or no residue in washing. The surfactant can be selected, for example, from the group consisting of non-alkoxylated C6-C20 linear or branched alkyl sulfates (AS), C6-C20 linear alkyl benzene sulfonates (LAS), and combinations thereof. The surfactant may be a C6-C20 linear alkyl benzene sulfonate (LAS). LAS surfactants are well known in the art and can be readily obtained by sulfonating commercially available linear alkyl benzenes. Exemplary C6-C20 alkyl benzene sulfonates that can be used include: 20 Linear alkylbenzene sulfonates include C6-C 20 Alkali metal, alkaline earth metal, or ammonium salts of linear alkylbenzenesulfonic acid, e.g., C 11 ~C 18 Or C 11 ~C 14 Examples of the salts include sodium, potassium, magnesium, and / or ammonium salts of linear alkylbenzene sulfonic acid. 12 Sodium or potassium salts of linear alkylbenzene sulfonic acid, e.g., C 12 The sodium salt of linear alkylbenzene sulfonate, i.e., sodium dodecylbenzene sulfonate, may be used as the first surfactant.

[0098] the fibrous elements have at least about 5% by weight, and / or at least about 10% by weight, and / or at least about 15% by weight, and / or at least about 20% by weight, and / or less than about 80% by weight, and / or less than about 75% by weight, and / or less than about 65% by weight, and / or less than about 60% by weight, and / or less than about 55% by weight, and / or less than about 50% by weight, and / or less than about 45% by weight, and / or less than about 40% by weight, and / or less than about 35% by weight, and / or less than about 30% by weight, and / or less than about 25% by weight of filament-forming material, based on the dry fibrous elements and / or on the dry fibrous structure; The fibrous elements may comprise more than about 20% by weight, and / or at least about 35% by weight, and / or at least about 40% by weight, and / or at least about 45% by weight, and / or at least about 50% by weight, and / or at least about 55% by weight, and / or at least about 60% by weight, and / or at least about 65% by weight, and / or at least about 70% by weight, and / or less than about 95% by weight, and / or less than about 90% by weight, and / or less than about 85% by weight, and / or less than about 80% by weight, and / or less than about 75% by weight of an active agent, preferably a surfactant, based on the dry fibrous elements and / or on the dry fibrous structures. The fibrous elements may comprise more than about 80% by weight of a surfactant based on the dry fibrous elements and / or on the dry fibrous structures.

[0099] Preferably, each fibrous element can be characterized by a sufficiently high total surfactant content, for example, at least about 30% by weight, or at least about 40% by weight, or at least about 50% by weight, or at least about 60% by weight, or at least about 70% by weight of the first surfactant, based on the dry fibrous element and / or on the dry fibrous structure.

[0100] The total concentration of filament-forming materials present in the fibrous elements can be from about 5% to less than about 80% by weight based on the dry fibrous elements and / or the dry fibrous structure, and the total concentration of surfactants present in the fibrous elements can be from about 20% to about 95% by weight based on the dry fibrous elements and / or the dry fibrous structure.

[0101] One or more of the fibrous elements may include at least one additional surfactant selected from the group consisting of other anionic surfactants (i.e., other than AS and LAS), nonionic surfactants, zwitterionic surfactants, amphoteric surfactants, cationic surfactants, and combinations thereof.

[0102] Other suitable anionic surfactants include C6-C 20 Linear or branched alkyl sulfonates, C6-C 20 Linear or branched alkyl carboxylate, C6-C 20 Linear or branched alkyl phosphates, C6-C 20 Linear or branched alkyl phosphonates, C6-C 20 Alkyl N-methyl glucose amides, C6-C 20 methyl ester sulfonate (MES), and combinations thereof.

[0103] Suitable nonionic surfactants include alkoxylated fatty alcohols. The nonionic surfactants have the formula R(OC2H4) n OH ethoxylated alcohols and ethoxylated alkylphenols, where R is selected from the group consisting of aliphatic hydrocarbon radicals containing from about 8 to about 15 carbon atoms, and alkylphenyl radicals in which the alkyl group contains from about 8 to about 12 carbon atoms, and the average value of n is from about 5 to about 15. Non-limiting examples of nonionic surfactants useful herein include C8-C 18 Alkyl ethoxylates, such as NEODOL® nonionic surfactants from Shell, where the alkoxylate units can be ethyleneoxy units, propyleneoxy units, or mixtures thereof, C6-C 12 Alkylphenol alkoxylates, C 12 ~C 18 C6-C with alcohol and ethylene oxide / propylene oxide block polymer 12 Alkylphenol condensates (such as Pluronic® (BASF)); C 14 ~C 22Medium chain branched alcohols, BA, C 14 ~C 22 Medium Chain Branched Alkyl Alkoxylate (BAE x where x is 1 to 30); alkyl polysaccharides; specifically alkyl polyglycosides; polyhydroxy fatty acid amides, and ether-terminated poly(oxyalkylated) alcohol surfactants. Suitable nonionic detersive surfactants also include alkyl polyglucosides and alkyl alkoxylated alcohols. Suitable nonionic surfactants also include those sold by BASF under the trade name Lutensol®.

[0104] Non-limiting examples of cationic surfactants include quaternary ammonium surfactants, which may have up to 26 carbon atoms, including alkoxylate quaternary ammonium (AQA) surfactants; dimethylhydroxyethyl quaternary ammonium; dimethylhydroxyethyl lauryl ammonium chloride; polyamine cationic surfactants; cationic ester surfactants; and amino surfactants, such as amidopropyl dimethylamine (APA).Suitable cationic detersive surfactants also include alkyl pyridinium compounds, alkyl quaternary ammonium compounds, alkyl quaternary phosphonium compounds, alkyl tertiary sulfonium compounds, and mixtures thereof.

[0105] Suitable cationic detersive surfactants are quaternary ammonium compounds having the general formula: (R)(R1)(R2)(R3)N + X - In the formula, R is a linear or branched, substituted or unsubstituted C 6~18 R1 and R2 are independently selected from methyl or ethyl moieties, R3 is a hydroxyl, hydroxymethyl or hydroxyethyl moiety, and X is an anion that provides charge neutrality, suitable anions being, for example, halides such as chloride, sulfates, and sulfonates. Suitable cationic detersive surfactants include mono-C6~18 Alkyl mono-hydroxyethyl dimethyl quaternary ammonium chloride. A highly suitable cationic detersive surfactant is mono-C 8~10 Alkyl mono-hydroxyethyl dimethyl quaternary ammonium chloride, mono-C 10~12 Alkyl mono-hydroxyethyl dimethyl quaternary ammonium chloride, and mono-C 10 Alkyl mono-hydroxyethyl dimethyl quaternary ammonium chloride.

[0106] Suitable examples of zwitterionic surfactants include derivatives of secondary and tertiary amines, including derivatives of heterocyclic secondary and tertiary amines; derivatives of quaternary ammonium, quaternary phosphonium, or tertiary sulfonium compounds; betaines, including alkyl dimethyl betaines, cocodimethylamidopropyl betaines, and sulfo and hydroxy betaines; C8-C 18 (For example, C 12 ~C 18 ) amine oxide; N-alkyl-N,N-dimethylamino-1-propanesulfonate (alkyl groups are C8-C 18 (It may be possible).

[0107] Suitable amphoteric surfactants include aliphatic derivatives of secondary or tertiary amines, or aliphatic derivatives of heterocyclic secondary and tertiary amines, where the aliphatic group can be linear or branched, one of the aliphatic substituents contains at least about 8 carbon atoms or about 8 to about 18 carbon atoms, and at least one of the aliphatic substituents contains an anionic water-solubilizing group, such as carboxy, sulfonate, sulfate.Suitable amphoteric surfactants also include sarcosinates, glycinates, taurinates, and mixtures thereof.

[0108] The fibrous elements may contain surfactant systems that contain only anionic surfactants, for example, either a single anionic surfactant or a combination of two or more different anionic surfactants. Alternatively, the fibrous elements may contain composite surfactant systems that contain, for example, a combination of one or more anionic surfactants with one or more nonionic surfactants, or a combination of one or more anionic surfactants with one or more zwitterionic surfactants, or a combination of one or more anionic surfactants with one or more amphoteric surfactants, or a combination of one or more anionic surfactants with one or more cationic surfactants, or a combination of all of the above types of surfactants (i.e., anionic, nonionic, amphoteric, and cationic).

[0109] Generally, fibrous elements are elongated particles whose length greatly exceeds their average diameter, e.g., the ratio of length to average diameter is at least about 10. Fibrous elements can be filaments or fibers. Filaments are relatively longer than fibers. Filaments can have lengths of about 2 inches or more, and / or about 3 inches or more, and / or about 4 inches or more, and / or about 6 inches or more. Fibers can have lengths less than about 2 inches, and / or less than about 1.5 inches, and / or less than about 1 inch.

[0110] The one or more filament-forming materials and active agents may be present in the fibrous elements in a weight ratio of the total concentration of filament-forming materials to active agent of about 2.0 or less, and / or about 1.85 or less, and / or less than about 1.7, and / or less than about 1.6, and / or less than about 1.5, and / or less than about 1.3, and / or less than about 1.2, and / or less than about 1, and / or less than about 0.7, and / or less than about 0.5, and / or less than about 0.4, and / or less than about 0.3, and / or greater than about 0.1, and / or greater than about 0.15, and / or greater than about 0.2. The one or more filament-forming materials and active agents may be present in the fibrous elements in a weight ratio of the total concentration of filament-forming materials to active agent of about 0.2 to about 0.7.

[0111] The fibrous elements may comprise from about 10% to less than about 80% by weight of a filament-forming material, such as a polyvinyl alcohol polymer, a starch polymer, and / or a carboxymethylcellulose polymer, based on the dry fibrous elements and / or the dry fibrous structure, and from about 20% to about 90% by weight of an active agent, such as a surfactant, based on the dry fibrous elements and / or the dry fibrous structure. The fibrous elements may further comprise a plasticizer (e.g., glycerin) and / or an additional pH adjuster (e.g., citric acid). The fibrous elements may have a weight ratio of filament-forming material to active agent of about 2.0 or less. The filament-forming material may be selected from the group consisting of polyvinyl alcohol, starch, carboxymethylcellulose, polyethylene oxide, and other suitable polymers, particularly hydroxyl-containing polymers and their derivatives. The filament-forming material may range in weight average molecular weight from about 100,000 g / mol to about 3,000,000 g / mol. In this range, it is believed that the filament forming material can provide an extensional rheology such that it is not so elastic that fiber attenuation is inhibited in the fiber production process.

[0112] The one or more active agents may be releasable and / or may be released when the fibrous elements and / or fibrous structures comprising the fibrous elements are exposed to intended conditions of use. The one or more active agents in the fibrous elements may be selected from the group consisting of surfactants, organic polymeric compounds, and mixtures thereof.

[0113] The fibrous elements may exhibit a diameter of less than about 300 μm, and / or less than about 75 μm, and / or less than about 50 μm, and / or less than about 25 μm, and / or less than about 10 μm, and / or less than about 5 μm, and / or less than about 1 μm, as measured according to the Diameter Test Method described herein. The fibrous elements may exhibit a diameter of greater than about 1 μm, as measured according to the Diameter Test Method described herein. The diameter of the fibrous elements may be used to control the release rate of one or more active agents present in the fibrous elements and / or the rate of degradation and / or change in the physical structure of the fibrous elements.

[0114] A fibrous element may include two or more different active agents that are compatible or incompatible with each other. A fibrous element may include an active agent within the fibrous element and an active agent on the exterior surface of the fibrous element, such as an active agent coating on the fibrous element. The active agent on the exterior surface of the fibrous element may be the same as or different from the active agent present within the fibrous element. If different, the active agents may be compatible or incompatible with each other. One or more active agents may be uniformly or substantially uniformly distributed throughout the fibrous element. One or more active agents may be distributed as discrete regions within the fibrous element.

[0115] Activator The water-soluble unit dose articles described herein may contain one or more active agents. The active agent may be present as a premix in the fiber element (as described above), in the particle (as described above), or in the article. The premix may be, for example, a slurry of the active agent combined with an aqueous absorbent. The active agent may be selected from the group consisting of surfactants, structurants, builders, organic polymeric compounds, enzymes, enzyme stabilizers, bleaching systems, brighteners, hueing agents, chelating agents, suds suppressors, conditioning agents, moisturizing agents, fragrances, fragrance microcapsules, fillers or carriers, alkalinity systems, pH control systems, buffers, alkanolamines, and mixtures thereof.

[0116] Surfactants The surfactant may be selected from the group consisting of anionic surfactants, nonionic surfactants, cationic surfactants, zwitterionic surfactants, amphoteric surfactants, ampholytic surfactants, and mixtures thereof, which are described in more detail above.

[0117] enzyme Examples of suitable enzymes include, but are not limited to, hemicellulases, peroxidases, proteases, cellulases, xylanases, lipases, phospholipases, esterases, cutinases, pectinases, mannanases, pectate lyases, keratinases, reductases, oxidases, phenoloxidases, lipoxygenases, ligninases, pullulanases, tannases, pentosanases, malanases, β-glucanases, arabinosidases, hyaluronidases, chondroitinases, laccases, and amylases, or mixtures thereof. A typical combination is an enzyme cocktail, which may include, for example, a protease and one or more non-protease enzymes, such as, for example, an amylase or a lipase in combination with any of those listed above.

[0118] When present in a detergent composition, the above additional enzymes may be present at an enzyme protein concentration of about 0.00001% to about 2%, about 0.0001% to about 1%, or even about 0.001% to about 0.5% by weight of the composition. The compositions disclosed herein may include about 0.001% to about 1% by weight of an enzyme (as an adjunct) which may be selected from the group consisting of lipase, amylase, protease, mannanase, cellulase, pectinase, and mixtures thereof.

[0119] Proteases Preferably, the enzyme composition comprises one or more proteases. Suitable proteases include metalloproteases and serine proteases, including neutral or alkaline microbial serine proteases, such as subtilisin (EC 3.4.21.62). Suitable proteases include those of animal, vegetable or microbial origin. In one aspect, such suitable proteases may be of microbial origin. Suitable proteases include chemically or genetically modified variants of the aforementioned suitable proteases. In one aspect, suitable proteases may be serine proteases, such as alkaline microbial proteases or / and trypsin-type proteases.

[0120] builder Suitable builders may be selected from the group consisting of aluminosilicates (e.g., zeolite builders such as zeolite A, zeolite P and zeolite MAP), silicates, phosphates, such as polyphosphates (e.g., sodium tri-polyphosphate), especially its sodium salt; carbonates, bicarbonates, sesquicarbonates, and carbonate minerals other than sodium carbonate or sesquicarbonates; organic mono-, di-, tri-, and tetracarboxylates, especially water-soluble non-surfactant carboxylates in the form of acid, sodium, potassium, or alkanolammonium salts, and oligomeric or water-soluble low molecular weight polymeric carboxylates, including aliphatic and aromatic types, and phytic acid. Additional suitable builders may be selected from citric acid, lactic acid, fatty acids, polycarboxylate builders, such as copolymers of acrylic acid, copolymers of acrylic acid and maleic acid, and copolymers of acrylic acid and / or maleic acid and other suitable ethylenic monomers with various types of additional functional groups. Alternatively, the composition may be substantially free of builders.

[0121] Polymer Dispersants Suitable polymers include, but are not limited to, polymeric carboxylates such as polyacrylates, polyacrylic acid-maleic acid copolymers, and sulfonated modifications thereof, e.g., hydrophobically modified sulfonated acrylic acid copolymers. The polymer may be a cellulosic polymer, polyester, polyterephthalate, polyethylene glycol, ethylene oxide-propylene oxide-ethylene oxide (EOx1POyEOx2) triblock copolymer, where each of x1 and x2 ranges from about 2 to about 140, and y ranges from about 15 to about 70, polyethyleneimine, any modified variants thereof, e.g., polyethylene glycol with grafted vinyl and / or alcohol moieties, and any combination thereof. In some cases, the dispersant polymer may also function as a rheology modifier, as described above.

[0122] Suitable polyethyleneimine polymers include propoxylated polyalkyleneimine (e.g., PEI) polymers. The propoxylated polyalkyleneimine (e.g., PEI) polymers may be ethoxylated. The propoxylated polyalkyleneimine (e.g., PEI) polymers may have an inner polyethylene oxide block and an outer polypropylene oxide block, with the degree of ethoxylation and the degree of propoxylation not being above or below certain limits. The ratio of polyethylene blocks to polypropylene blocks (n / p) may be from about 0.6, or from about 0.8, or from about 1, up to about 10, or up to about 5, or up to about 3. The n / p ratio may be about 2. The propoxylated polyalkyleneimine may have a PEI backbone with a weight average molecular weight (measured prior to alkoxylation) of about 200 g / mol to about 1200 g / mol, or about 400 g / mol to about 800 g / mol, or about 600 g / mol. The molecular weight of the propoxylated polyalkyleneimine may be about 8,000 to about 20,000 g / mol, or about 10,000 to about 15,000 g / mol, or about 12,000 g / mol.

[0123] Suitable propoxylated polyalkyleneimine polymers may include compounds of the following structure:

[0124] [ka] (where EO is an ethoxylate group and PO is a propoxylate group). The compound shown above is a PEI with a molar ratio of EO:PO of 10:5 (e.g., 2:1). Other similar suitable compounds may contain EO and PO groups present in a molar ratio of about 10:5 or about 24:16.

[0125] Stain Removal Polymer Suitable soil release polymers have a structure defined by one of the following structures (I), (II), or (III): (I) -[(OCHR 1 -CHR 2 ) a-O-OC-Ar-CO-] d (II) -[(OCHR 3 -CHR 4 ) b -O-OC-sAr-CO-] e (III) -[(OCHR 5 -CHR 6 ) c -OR 7 ] f (In the formula, a, b and c are each 1 to 200; d, e and f are each 1 to 50; Ar is 1,4-substituted phenylene; sAr is a 1,3-substituted phenylene substituted at the 5-position with SO3Me; Me is Li, K, Mg / 2, Ca / 2, Al / 3, ammonium, mono-, di-, tri-, or tetra-alkylammonium (alkyl groups are C1-C 18 Alkyl or C2-C 10 hydroxyalkyl), or mixtures thereof; R 1 , R 2 , R 3 , R 4 , R 5 , and R 6 are independently H or C1-C 18 n- or iso-alkyl; R 7 is linear or branched C1-C 18 Alkyl, or linear or branched C2-C 30 alkenyl, or a cycloalkyl group having 5 to 9 carbon atoms, or C8 to C 30 Aryl group or C6-C 30 It is an arylalkyl group.

[0126] Suitable soil release polymers are polyester soil release polymers such as Repel-o-tex polymers including Repel-o-tex SF, SF-2 and SRP6 supplied by Rhodia. Other suitable soil release polymers include Texcare polymers including Texcare SRA100, SRA300, SRN100, SRN170, SRN240, SRN300 and SRN325 supplied by Clariant. Other suitable soil release polymers are Marloquest polymers such as Marloquest SL supplied by Sasol.

[0127] Cellulosic Polymers Suitable cellulosic polymers include those selected from alkyl cellulose, alkyl alkoxy alkyl cellulose, carboxy alkyl cellulose, and alkyl carboxy alkyl cellulose. The cellulosic polymer may be selected from the group consisting of carboxymethyl cellulose, methyl cellulose, methyl hydroxyethyl cellulose, methyl carboxymethyl cellulose, and mixtures thereof. In one embodiment, the carboxymethyl cellulose has a degree of carboxymethyl substitution of 0.5 to 0.9 and a molecular weight of 100,000 Da to 300,000 Da.

[0128] Amine Non-limiting examples of amines can include, but are not limited to, polyetheramines, polyamines, oligoamines, triamines, diamines, pentamines, tetraamines, or combinations thereof. Specific examples of suitable additional amines include tetraethylenepentamine, triethylenetetraamine, diethylenetriamine, or mixtures thereof.

[0129] Bleach Suitable bleaching agents other than bleach catalysts include photobleaches, bleach activators, hydrogen peroxide, sources of hydrogen peroxide, preformed peracids, and mixtures thereof. Generally, when a bleaching agent is used, the detergent compositions of the present invention may comprise from about 0.1% to about 50%, or even from about 0.1% to about 25% of the bleaching agent, by weight of the detergent composition.

[0130] Bleaching catalyst Suitable bleach catalysts include, but are not limited to, iminium cations and polyions, iminium zwitterions, modified amines, modified amine oxides, N-sulfonylimines, N-phosphonylimines, N-acylimines, thiadiazole dioxides, perfluoroimines, cyclic sugar ketones, and mixtures thereof.

[0131] Brightener Commercially available optical brighteners suitable for the present disclosure can be divided into subgroups including, but not limited to, derivatives of stilbenes, pyrazolines, coumarins, benzoxazoles, carboxylic acids, methinecyanines, dibenzothiophene-5,5-dioxides, azoles, 5- and 6-membered heterocycles, and various other materials.

[0132] The optical brightener may be selected from the group consisting of disodium 4,4'-bis{[4-anilino-6-morpholino-s-triazin-2-yl]-amino}-2,2'-stilbenedisulfonate (brightener 15, sold under the trade name Tinopal AMS-GX by BASF), disodium 4,4'-bis{[4-anilino-6-(N-2-bis-hydroxyethyl)-s-triazin-2-yl]-amino}-2,2'-stilbenedisulfonate (sold under the trade name Tinopal UNPA-GX by BASF), disodium 4,4'-bis{[4-anilino-6-(N-2-hydroxyethyl-N-methylamino)-s-triazin-2-yl]-amino}-2,2'-stilbenedisulfonate (sold under the trade name Tinopal 5 BM-GX by BASF). More preferably, the optical brightener is disodium 4,4'-bis{[4-anilino-6-morpholino-s-triazin-2-yl]-amino}-2,2'-stilbenedisulfonate.

[0133] The whitening agent may be added in particulate form or as a premix with a suitable solvent, e.g., non-ionic surfactant, propanediol.

[0134] Fabric color toning agent Fabric toning agents (sometimes also referred to as complementing agents, bluing agents, or whitening agents) typically impart a blue or purple hue to fabrics. Hueing agents can be used either alone or in combination to create a particular hue shade and / or tint different types of fabrics. This can be achieved, for example, by mixing red and green-blue dyes to produce a blue or purple shade. The hueing agent may be selected from any known chemical class of dyes, including, but not limited to, acridines, anthraquinones (including polycyclic quinones), azines, azos including premetallized azos (e.g., monoazos, diazos, trisazos, tetrakisazos, polyazos), benzodifuranes and benzodifuranones, carotenoids, coumarins, cyanines, diazahemicyanines, diphenylmethanes, formazans, hemicyanines, indigoids, methanes, naphthalimides, naphthoquinones, nitro and nitroso, oxazines, phthalocyanines, pyrazoles, stilbenes, styryls, triarylmethanes, triphenylmethanes, xanthenes, and mixtures thereof.

[0135] Suitable fabric hueing agents include dyes, dye-clay conjugates, and organic and inorganic pigments. Suitable dyes also include small molecule dyes and polymeric dyes. Suitable small molecule dyes include small molecule dyes selected from the group consisting of dyes classified in the Color Index (CI) classification of direct dyes, basic dyes, reactive dyes or hydrolyzed reactive dyes, solvent dyes, or disperse dyes, which are classified as, for example, blue, purple, red, green, or black, and either alone or in combination, produce the desired shade. Suitable polymeric dyes include polymeric dyes selected from the group consisting of polymers containing covalently attached (sometimes referred to as bonded) chromogens (dye-polymer conjugates), such as polymers with chromogens copolymerized in the polymer backbone, and mixtures thereof. Suitable polymeric dyes also include polymeric dyes selected from the group consisting of fabric substantive colorants sold under the name Liquitint® (Milliken, Spartanburg, South Carolina, USA), dye-polymer conjugates formed from at least one reactive dye and a polymer selected from the group consisting of polymers containing a moiety selected from the group consisting of hydroxyl moieties, primary amine moieties, secondary amine moieties, thiol moieties, and mixtures thereof.Suitable polymeric dyes also include polymeric dyes selected from the group consisting of Liquitint® Violet CT, carboxymethyl cellulose (CMC) covalently bonded to reactive blue, reactive violet, or reactive red dyes, such as CMC conjugated with CI Reactive Blue 19 sold under the trade name AZO-CM-CELLULOSE, product code S-ACMC by Megazyme (Wicklow, Ireland), alkoxylated triphenyl-methane polymeric colorants, alkoxylated thiophene polymeric colorants, and mixtures thereof.

[0136] The aforementioned fabric hueing agents may be used in combination (any mixture of fabric hueing agents may be used).

[0137] Encapsulating Agent The encapsulation may include a core and a shell having an inner surface and an outer surface, the shell encapsulating the core. The core may comprise any laundry care adjunct, but typically the core may comprise a material selected from the group consisting of: perfumes; whitening agents; color dyes; insect repellents; silicones; waxes; fragrances; vitamins; fabric softeners; skin care agents, in one aspect paraffin; enzymes; antimicrobial agents; bleaching agents; sensates; and mixtures thereof, and the shell may comprise a material selected from the group consisting of polyethylene; polyamides, polyvinyl alcohol, optionally containing other co-monomers; polystyrene; polyisoprene; polycarbonates; polyesters; polyacrylates; aminoplasts (in one aspect the aminoplasts may comprise polyureas, polyurethanes, and / or polyurea urethanes, and in one aspect the polyureas may comprise polyoxymethylene urea and / or melamine formaldehyde); polyolefins; polysaccharides, (in one aspect the polysaccharides may comprise alginates and / or chitosan); gelatin; shellac; epoxy resins; vinyl polymers; water insoluble inorganic materials; silicones; and mixtures thereof.

[0138] A preferred encapsulant comprises a fragrance. A preferred encapsulant comprises a shell that may comprise melamine formaldehyde and / or crosslinked melamine formaldehyde. Other preferred capsules comprise a polyacrylate-based shell. A preferred encapsulant is disclosed that comprises a core material and a shell at least partially surrounding the core material. At least 75%, 85%, or even 90% of the encapsulant may have a breaking strength of 0.2 MPa to 10 MPa and a benefit agent leakage rate of 0% to 20%, or even less than 10% or 5% of the total initial amount of encapsulated benefit agent. Preferably, at least 75%, 85%, or even 90% of the encapsulating agent may have a particle size (i) of 1 micrometer to 80 micrometers, 5 micrometers to 60 micrometers, 10 micrometers to 50 micrometers, or even 15 micrometers to 40 micrometers, and / or (ii) at least 75%, 85%, or even 90% of the encapsulating agent may have a particle wall thickness of 30 nm to 250 nm, 80 nm to 180 nm, or even 100 nm to 160 nm. A formaldehyde scavenger may be used with the encapsulating agent, for example in the capsule slurry, and / or may be added to the composition before, during, or after the encapsulating agent is added to the composition.

[0139] Suitable capsules can be made using known processes. Alternatively, suitable capsules can be purchased from Encapsys LLC (Appleton, Wisconsin USA). In a preferred embodiment, the composition may include a deposition aid, preferably in addition to the encapsulating agent. The preferred deposition aid is selected from the group consisting of cationic and non-ionic polymers. Suitable polymers include cationic starch, cationic hydroxyethyl cellulose, polyvinyl formaldehyde, locust bean gum, mannan, xyloglucan, tamarind gum, polyethylene terephthalate, and polymers containing dimethylaminoethyl methacrylate, optionally with one or more monomers selected from the group including acrylic acid and acrylamide.

[0140] fragrance Non-limiting examples of perfumes and perfume ingredients include, but are not limited to, aldehydes, ketones, esters, and the like. Other examples include various natural extracts and natural essences, which can include complex mixtures of ingredients such as orange oil, lemon oil, rose extract, lavender, musk, patchouli, balsam extract, sandalwood oil, pine oil, cedar, and the like. The final perfume can include very complex mixtures of such ingredients. The finished perfume can be included at a concentration ranging from about 0.01% to about 2% by weight of the detergent composition.

[0141] Dye transfer inhibitor Dye transfer inhibitors are effective in inhibiting the transfer of dye from one fabric to another during the washing process. In general, such dye transfer inhibitors can include polyvinylpyrrolidone polymers, polyamine N-oxide polymers, copolymers of N-vinylpyrrolidone and N-vinylimidazole, manganese phthalocyanine, peroxidase, and mixtures thereof. When used, these agents may be used at a concentration of about 0.0001% to about 10% by weight of the composition, in some examples, about 0.01% to about 5% by weight of the composition, and in other examples, about 0.05% to about 2% by weight of the composition.

[0142] Chelating Agents Suitable chelating agents include copper, iron, and / or manganese chelating agents, and mixtures thereof. Such chelating agents may be selected from the group consisting of phosphonates, aminocarboxylates, aminophosphonates, succinates, polyfunctionally substituted aromatic chelating agents, 2-pyridinol-N-oxide compounds, hydroxamic acids, carboxymethyl inulin, and mixtures thereof. The chelating agents may be present in the form of an acid or a salt, including alkali metal salts, ammonium salts, and substituted ammonium salts thereof, and mixtures thereof. Other chelating agents suitable for use herein are the commercially available DEQUEST series, as well as chelating agents from Monsanto, Akzo-Nobel, DuPont, Dow, Trilon® series from BASF and Nalco, copolymers of maleic acid and acrylic acid available from BASF, DOW, and Nippon Shokubai.

[0143] Foam suppressor Compounds for reducing or suppressing foam formation may be incorporated into the water-soluble unit dose article. Foam suppression may be particularly important in so-called "high concentration wash processes" and in front-loading washing machines. Examples of suds suppressors include monocarboxylic fatty acids and soluble salts thereof, high molecular weight hydrocarbons such as paraffin, fatty acid esters (e.g., fatty acid triglycerides), fatty acid esters of monohydric alcohols, aliphatic C 18 ~C 40 Included are ketones (eg, stearone), N-alkylated aminotriazines, waxy hydrocarbons preferably having a melting point below about 100° C., silicone suds suppressors, as well as secondary alcohols.

[0144] Further suitable antifoam agents are those derived from phenylpropylmethyl substituted polysiloxanes.

[0145] The detergent composition may comprise a suds suppressor selected from an organo-modified silicone polymer having aryl or alkylaryl substituents in combination with a primary filler which is a silicone resin and a modified silica. The detergent composition may comprise from about 0.001% to about 4.0%, by weight of the composition, of such suds suppressors.

[0146] The detergent composition may comprise a suds suppressor selected from a) a mixture of about 80 to about 92% ethylmethyl, methyl(2-phenylpropyl)siloxane, about 5 to about 14% MQ resin in octyl stearate, and about 3 to about 7% modified silica, b) a mixture of about 78 to about 92% ethylmethyl, methyl(2-phenylpropyl)siloxane, about 3 to about 10% MQ resin in octyl stearate, and about 4 to about 12% modified silica; or c) mixtures thereof, the percentages being by weight of the antifoam agent.

[0147] Foam booster If high foaming is desired, C 10 ~C 16 Foam boosters such as alkanolamides may be used. Some examples include C 10 ~C 14 Optionally, water soluble magnesium and / or calcium salts, such as MgCl2, MgSO4, CaCl2, CaSO4, etc., can also be added at a concentration of about 0.1% to about 2% by weight of the detergent composition to provide additional foam and enhance grease removal performance.

[0148] Conditioning Agent Suitable conditioning agents include high melting point fatty compounds.The high melting point fatty compounds useful herein have a melting point of 25°C or higher and are selected from the group consisting of fatty alcohols, fatty acids, fatty alcohol derivatives, fatty acid derivatives, and mixtures thereof.Suitable conditioning agents also include nonionic polymers and conditioning oils, such as hydrocarbon oils, polyolefins, and fatty acid esters.

[0149] Suitable conditioning agents include those characterized generally as silicones (e.g., silicone oils, polyoils, cationic silicones, silicone gums, high refractive index silicones, and silicone resins), organic conditioning oils (e.g., hydrocarbon oils, polyolefins, and fatty acid esters), or combinations thereof, or that otherwise form liquid dispersed particles in the aqueous surfactant matrix herein.

[0150] Fabric-reinforced polymer Suitable fabric reinforcing polymers are typically cationically charged and / or have a high molecular weight. The fabric reinforcing polymer may be a homopolymer or may be formed from two or more types of monomers. The monomer weight of the polymer generally ranges from 5,000 to 10,000,000, typically at least 10,000, preferably 100,000 to 2,000,000. Preferred fabric reinforcing polymers have a cationic charge density of at least about 0.2 meq / gm, preferably at least 0.25 meq / gm, more preferably at least 0.3 meq / gm, but also preferably less than 5 meq / gm, more preferably less than 3 meq / gm, most preferably less than 2 meq / gm, at the pH of the intended use of the composition (which generally ranges from pH 3 to pH 9, preferably pH 4 to pH 8). The fabric reinforcing polymer may be of natural or synthetic origin.

[0151] Pearlizing Agent Non-limiting examples of pearlescent agents include: mica, titanium dioxide coated mica, bismuth oxychloride, fish scales, mono- and diesters of alkylene glycols. The pearlescent agent may be ethylene glycol distearate (EGDS).

[0152] Hygiene and odors Suitable hygiene and malodour actives include zinc ricinoleate, thymol, quaternary ammonium salts such as Bardac®, polyethyleneimine (such as Lupasol® from BASF) and its zinc complexes, silver and silver compounds, especially Ag + or those designed to slowly release nanosilver dispersions.

[0153] buffer system The water-soluble unit dose articles described herein can be formulated so that during use in aqueous cleaning operations, the wash water has a pH of about 7.0 to about 12, and in some examples, about 7.0 to about 11. Techniques for controlling pH at recommended use concentrations include the use of buffers, alkalis, or acids, which are known to those skilled in the art. These techniques include, but are not limited to, the use of sodium carbonate, citric acid or sodium citrate, lactic acid or lactate salts, monoethanolamine or other amines, boric acid or borate salts, and other pH adjusting compounds known in the art.

[0154] The detergent compositions herein may include a dynamic in-wash pH profile, in which the wax-covered citric acid particles may be used in conjunction with other pH control agents such that (i) the wash liquor pH is greater than 10 after about 3 minutes of contact with water, (ii) the wash liquor pH is less than 9.5 after about 10 minutes of contact with water, (iii) the wash liquor pH is less than 9.0 after about 20 minutes of contact with water, and (iv) the equilibrium pH of the wash liquor is in the range of about 7.0 to about 8.5, if desired.

[0155] Method of preparation As illustrated in FIG. 1, a solution of a filament-forming composition 35 is provided. The filament-forming composition may include one or more filament-forming materials and, optionally, one or more active agents. The filament-forming composition 35 passes through one or more die block assemblies 40 including a plurality of spinnerets 45 to form a plurality of fiber elements 30 including one or more filament-forming materials and, optionally, one or more active agents. The plurality of die block assemblies 40 can be used to spin different layers of fiber elements 30, the fiber elements 30 of the different layers having different compositions from each other or being the same as each other. Two or more die block assemblies arranged in series can be provided to form three, four, or any other integer number of layers in a given ply. The fiber elements 30 can be deposited on a belt 50 moving in the machine direction MD to form a first ply 10.

[0156] Particles can be introduced into the flow of fiber elements 30 between the die block assembly 40 and the belt 50. The particles can be fed from a particle receiver to a belt feeder 41 or, optionally, a screw feeder. The belt feeder 41 can be configured and controlled to deliver the desired particle mass to the process. The belt feeder can provide an air knife 42 that suspends and directs the particles in an air stream into the fiber elements 30 to form a particle-fiber layer of intermingled fiber elements 30 and particles that are then deposited on the belt 50.

[0157] To form the water-soluble product, a first ply 10 can be provided. A second ply 15 can be provided separately from the first ply 10. The first ply 10 and the second ply 15 are superimposed on one another. Superimposed means one is disposed above or below the other, with the proviso that additional plies or other materials, such as active agents, may be disposed between the superimposed plies. A portion of the first ply 10 can be joined to a portion of the second ply 15 to form the water-soluble product 5. Each ply may include one or more layers.

[0158] Particle-fiber layer The particle-fiber layer may be arranged in several ways. Clusters of particles may be distributed in pockets distributed within the layer, and such pockets may be formed between layers of fiber elements, with the contact network and porosity within each cluster of particles being governed by traditional particle packing physics, but the clusters being substantially extended within the layer. The particles may be relatively homogeneously distributed throughout the fiber structure, substantially free of localized particle clusters, and the packing is substantially extended on the scale of individual particles, with less interparticle contact and larger interparticle pores. Without being bound by theory, it is believed that a water-soluble unit dose article comprising a layer containing fiber elements and particles, when a sticky surfactant such as AES is sequestered in particles with an extended structure, improves the dispersion and dissolution of the unit dose article by both rapid absorption of water into the extended structure and reduced contact between particles with the sticky surfactant.

[0159] Pouches. The single unit dose may be in the form of a pouch. The composition may be provided either in the form of a unit dose, in the form of a tablet, or in the form of a liquid / solid (optionally granular) / gel / paste, preferably held within a water-soluble film (known as a pouch or pod). The composition may be enclosed in a single compartment pouch or a multi-compartment pouch. Multi-compartment pouches are described in more detail in EP 2133410(A). Shaded or non-shaded dyes or pigments, or other cosmetic agents, may also be used in one or more compartments.

[0160] Suitable films for forming the pouch are soluble or dispersible in water, preferably having a water solubility / dispersibility of at least 50%, preferably at least 75%, or even at least 95%, as measured by the methods set out herein after using a glass filter having a maximum pore size of 20 micrometers: A pre-weighed 400 ml beaker is charged with 50 grams ± 0.1 grams of pouch material and 245 mL ± 1 mL of distilled water is added. This is vigorously stirred for 30 minutes with a magnetic stirrer set at 600 rpm. The mixture is then filtered through a pleated qualitative sintered glass filter with the pore size defined above (maximum 20 micrometers). The water is dried from the collected filtrate by any conventional method and the weight of the remaining material is determined (this is the dissolved or dispersed fraction). The percentage of solubility or dispersion can then be calculated. A preferred film material is a polymeric material. The film material can be obtained, for example, by casting, blowing, extruding or blow-extruding a polymeric material as known in the art. Preferred polymers, copolymers or derivatives thereof suitable for use as pouch materials are selected from polyvinyl alcohol, polyvinylpyrrolidone, polyalkylene oxides, acrylamide, acrylic acid, cellulose, cellulose ethers, cellulose esters, cellulose amides, polyvinyl acetates, polycarboxylic acids and salts, polyamino acids or peptides, polyamides, polyacrylamides, maleic acid / acrylic acid copolymers, polysaccharides including starch and gelatin, natural gums such as xanthan and cara gum. More preferred polymers are selected from polyacrylates and water-soluble acrylate copolymers, methylcellulose, sodium carboxymethylcellulose, dextrin, ethylcellulose, hydroxyethylcellulose, hydroxypropylmethylcellulose, maltodextrin, polymethacrylates, and most preferably polyvinyl alcohol, polyvinyl alcohol copolymers and hydroxypropylmethylcellulose (HPMC), and combinations thereof. Preferably, the concentration of the polymer, e.g., PVA polymer, in the pouch material is at least 60%. The polymer may have any weight average molecular weight, preferably from about 1000 to 1,000,000, more preferably from about 10,000 to 300,000, and even more preferably from about 20,000 to 150,000. Mixtures of polymers may also be used as the pouch material.This may be beneficial to control the mechanical and / or dissolution properties of the compartment or pouch depending on the application and required requirements. Suitable mixtures include, for example, mixtures in which one polymer has a higher water solubility than another polymer and / or one polymer has a higher mechanical strength than another polymer. Also suitable are mixtures of polymers with different weight average molecular weights, for example a mixture of PVA or its copolymers with a weight average molecular weight of about 10,000-40,000, preferably around 20,000, and PVA or its copolymers with a weight average molecular weight of about 100,000-300,000, preferably around 150,000. Also suitable herein are polymer blend compositions comprising hydrolytically degradable water-soluble polymer blends, such as, for example, a polymer blend of polylactide and polyvinyl alcohol obtained by mixing polylactide and polyvinyl alcohol, typically comprising about 1-35% by weight of polylactide and about 65-99% by weight of polyvinyl alcohol. Preferred for use herein are polymers that are from about 60% to about 98% hydrolyzed, preferably from about 80% to about 90% hydrolyzed, to improve the solubility characteristics of the material.

[0161] Of course, different film materials and / or films of different thicknesses may be used in making the compartments of the present invention. An advantage of selecting different films is that the resulting compartments may exhibit different solubility or release characteristics.

[0162] The most preferred film materials are the PVA films known as MonoSol Reference Nos. M8630, M8900, H8779 (described in Applicant's co-pending application Reference Nos. 44528 and 11599), the PVA films described in U.S. Pat. Nos. 6,166,117 and 6,787,512, and PVA films having comparable solubility and deformation characteristics.

[0163] The film material herein may also include one or more additive-containing components. For example, it may be beneficial to add plasticizers such as glycerol, ethylene glycol, diethylene glycol, propylene glycol, sorbitol and mixtures thereof. Other additives include functional detergent additives delivered to the wash water, such as organic polymer dispersants.

[0164] Bittering agents may be incorporated into the pouch or pod by being incorporated into the composition inside the pouch and / or by being coated onto the film.

[0165] Washing Instructions The present invention also encompasses a washing method using the article according to the present invention, comprising the steps of placing at least one article according to the present invention in a washing machine together with the laundry to be washed, and performing a washing or cleaning operation. Specifically, the method may comprise the steps of obtaining a fabric having sebum attached thereto, and treating the fabric with a washing step, the washing step comprising contacting the fabric with a washing liquid. The washing liquid is prepared by diluting the water-soluble unit dose and detergent in water 300-800 times, preferably 400-700 times, and the washing liquid comprises a pH of 8 or more.

[0166] Any suitable washing machine may be used, examples include an automatic washing machine, a manual washing operation, or a mixture thereof, preferably an automatic washing machine.

[0167] Those skilled in the art will recognize suitable machines for the relevant washing operations. The articles of the present invention may be used in conjunction with other compositions such as fabric additives, fabric softeners, rinse aids, and the like.

[0168] The washing temperature may be between 5° C. and 90° C., for example below 30° C. The washing process may include at least one washing cycle having a duration between 5 and 50 minutes. The automatic washing machine may include a rotating drum, and during at least one washing cycle, the drum has a rotation speed between 15 and 40 rpm, preferably between 20 and 35 rpm.

[0169] The fabric may be cotton, polyester, a cotton / polyester blend, or mixtures thereof, preferably cotton.

[0170] A water-soluble unit dose article comprising a water-soluble fibrous structure and one or more rheology-modifying particles dispersed throughout the structure may remove one or more types of stains, such as, for example, butter, beef, grass, tea, spaghetti, sebum, wine, and any other type of stain that may be imparted to fabric.

[0171] Method of preparation The method of making the fibrous water-soluble unit dose will now be described in detail with reference to its specific embodiment. The embodiment is provided for the purpose of illustrating the invention and is not meant to limit the invention. For example, features described or illustrated as part of one embodiment may be used in another embodiment to produce further embodiments. The present invention is intended to include these and other modifications and variations that fall within the scope and spirit of the invention.

[0172] The method is particularly suitable for producing fibrous water-soluble unit dose structures from a web of fibrous material, and the fibrous water-soluble unit doses are intended for use in various cleaning operations, such as personal cleansing, dishware, and laundry.The present invention is not limited to any particular type or composition of fibrous web material, and may be implemented with any suitable fibrous web material known to those skilled in the art, in addition to those mentioned above.The fibrous web material may include any structure and combination of fibers and particles combined within the fibrous web.The fibrous structure and particle composition are described in detail in the previous sections of this document.

[0173] The fibrous water-soluble unit dose material may be formed into a web structure by using a variety of conventional methods and techniques. For example, the absorbent web may be formed by dry-forming techniques, air-laying techniques, wet-forming techniques, foam-forming techniques, and the like, as well as combinations thereof. Methods and equipment for carrying out such techniques are well known in the art.

[0174] An embodiment of the method includes delivering a fibrous web material or a supply of fiber elements. As shown in FIG. 1, a first spin beam is used to spin a first layer of fiber elements and collect them on a forming belt. The forming belt with the first layer of fibers is then passed under a second spin beam modified with a particle addition system. The particle addition system can substantially inject particles from the second spin beam toward a landing zone on the forming belt directly below the fiber elements. A suitable particle addition system can be assembled from a particle feeder such as a vibration, belt or screw feeder, and an injection system such as an air knife or other fluidized conveying system. To aid in consistent distribution of particles in the transverse direction, the particles are preferably fed across approximately the same width as the spinning die to ensure that the particles are delivered across the entire width of the composite structure. Preferably, the particle feeder is completely enclosed except for the exit to minimize breakage of the particle feed material. The co-impingement of the particles and fiber elements on the forming belt under the second spin beam expands the particle packing and creates a composite structure in which the fibers substantially penetrate the inter-particle pores.

[0175] As illustrated in FIG. 1, a solution of a filament-forming composition 35 is provided. The filament-forming composition may include one or more filament-forming materials and, optionally, one or more active agents. The filament-forming composition 35 passes through one or more die block assemblies 40 including a plurality of spinnerets 45 to form a plurality of fiber elements 30 including one or more filament-forming materials and, optionally, one or more active agents. The plurality of die block assemblies 40 can be used to spin different layers of fiber elements 30, the fiber elements 30 of the different layers having different compositions from each other or being the same as each other. Two or more die block assemblies arranged in series can be provided to form three, four, or any other integer number of layers in a given ply. The fiber elements 30 can be deposited on a belt 50 moving in the machine direction MD to form a first ply 10.

[0176] Particles can be introduced into the flow of fiber elements 30 between the die block assembly 40 and the belt 50. The particles can be fed from a particle receiver to a belt feeder 41 or, optionally, a screw feeder. The belt feeder 41 can be configured and controlled to deliver the desired particle mass to the process. The belt feeder can provide an air knife 42 that suspends and directs the particles in an air stream into the fiber elements 30 to form a particle-fiber layer of intermingled fiber elements 30 and particles that are then deposited on the belt 50.

[0177] To form the water-soluble product, a first ply 10 can be provided. A second ply 15 can be provided separately from the first ply 10. The first ply 10 and the second ply 15 are superimposed on one another. Superimposed means one is disposed above or below the other, with the proviso that additional plies or other materials, such as active agents, may be disposed between the superimposed plies. A portion of the first ply 10 can be joined to a portion of the second ply 15 to form the water-soluble product 5. Each ply may include one or more layers.

[0178] To make the fiber elements, an aqueous solution, preferably having a solids content of about 45% to 60%, is processed through one or more spinning beams as shown in FIG.

[0179] A suitable spin beam includes a capillary die having an attenuating air stream and a drying air stream suitable for substantially drying the attenuated fibers prior to impingement on the forming belt.

[0180] Referring to FIG. 2, the fibrous web material 16 is provided in the form of a ribbon or strip 24. As mentioned above, the fibrous web material 16 may be provided from a roll or directly from an in-line manufacturing operation. The strip of fibrous web material 24 is conveyed in a machine direction 18 and has a machine direction side 20 defined by the opposing parallel sides of the strip 24. The strip of web material 24 also has a transverse dimension 22 that may be considered the "width" of the strip 24. Although FIG. 2 shows a single strip of web material 24, it should be understood that the absorbent web material may be provided in the form of multiple adjacent strips 24. After the fibrous water soluble unit doses 30 are defined into a strip in accordance with the present invention, the multiple fibrous water soluble unit doses may be separated for subsequent individual packaging.

[0181] 2, the bands 24 of fibrous web material are cut in the transverse direction 22 to form a repeating nested pattern of fibrous water soluble unit doses 30. The fibrous water soluble unit doses 30 are oriented to be symmetrical along a centerline axis 32 of each fibrous water soluble unit dose 30 that lies along an angle relative to the longitudinal axis 22 of the band 24 and the machine direction 18. The fibrous water soluble unit doses have a longitudinal centerline 34 that is parallel to the longitudinal edge of the band along the machine direction 18. The fibrous water soluble unit doses are asymmetrical along the longitudinal centerline 34 of the fibrous water soluble unit dose. The fibrous water soluble unit doses may also be asymmetrical along the transverse centerline of the fibrous water soluble unit dose, the transverse axis being parallel to the transverse axis of the band of material. The fibrous water soluble unit doses 30 may be symmetrical along an axis that is not parallel to either the longitudinal axis or the transverse axis of the band along which the fibrous water soluble unit doses are cut, such as the individual centerline axis 32 of each fibrous water soluble unit dose 30. The fibrous water soluble unit dose includes upper ridges 36 and lower ridges 38. The upper ridges 36 and lower ridges 38 serve one or more of several purposes. During the manufacturing process, the upper ridges 36 and lower ridges 38 function to form a nested mosaic pattern. The upper ridges 36, the lower ridges 38, or both, may be integral to the shape of the water soluble unit dose and are delineated by one or more perforations 42.

[0182] Referring to FIG. 2, a process of cutting the band 24 of fibrous web material with transverse cuts to define individual fibrous water-soluble unit doses 30 is shown, which may be performed by a conventional, generally shown, rotary knife or roll having blades defined in a pattern corresponding to the nesting shape of the fibrous water-soluble unit doses 30. In this regard, it should be understood that any suitable cutter mechanism may be utilized, including methods and devices developed in the future. Conventional cutter mechanisms and devices are well known in the art and may include rotary knives, die cutters, water cutters, laser cutters, and the like, as well as combinations thereof. The method according to the present invention is not limited by any particular cutting method or device.

[0183] Referring again to FIG. 2, it can be seen that adjacent nested fibrous water soluble unit doses 30 share a common defined cut line 44 such that waste of absorbent material between the nested fibrous water soluble unit doses 30 is minimized. In the embodiment of FIG. 2, there is minimal or no material waste. In conventional nesting patterns, there is typically about 5% to about 35% material waste between adjacent unit doses. The present invention encompasses nesting configurations with minimal waste, desirably less than about 20%, and more desirably zero waste. The ability to mass produce longitudinally asymmetric fibrous water soluble unit doses without wasting web material is an important feature.

[0184] It should be understood that a vast number of shapes and configurations are possible for defining the laterally nested fibrous water soluble unit doses 30 according to the present invention, particularly the longitudinally asymmetric fibrous water soluble unit doses as described herein. The fibrous water soluble unit doses 30 generally have the same shape and are asymmetric with respect to the longitudinal axis 34 of the band of fibrous material. The mosaic shapes of the fibrous water soluble unit doses alternate, with alternating fibrous water soluble unit doses sharing a common defining break or cord, so that there is substantially no waste of fibrous material between adjacent fibrous water soluble unit doses. Particular embodiments of fibrous water soluble unit dose configurations within the scope of the present invention are illustrated in Figures 2-7. However, it should be understood that such embodiments are for illustrative purposes only, and the present invention is not limited to any particular configuration.

[0185] 3-7 depict alternative patterns of nested fibrous water soluble unit doses 30. As shown in FIG.

[0186] It should be understood that the present invention encompasses various other embodiments, modifications, and equivalents to the embodiments of the present invention described herein, which may be suggested to persons skilled in the art after reading the description of the invention set forth herein, without departing from the scope and spirit of the present invention.

[0187] As shown in Figure 8, the use of a non-tesselated design results in a significant increase in waste and space 46 between unit doses 30. This is evidenced by the gaps between the single unit doses found at each corner of adjacent unit doses.

[0188] 9-15 show an embodiment of a container having a lid embodying the new design.

[0189] FIG. 9 shows a perspective view of a container having a lid embodying the new design.

[0190] FIG. 10 shows a front view of a container having a lid embodying the new design.

[0191] FIG. 11 shows a side view of a container having a lid embodying the new design.

[0192] FIG. 12 shows a side view of a container having a lid embodying the new design.

[0193] FIG. 13 shows a rear view of a container with a lid embodying the new design.

[0194] FIG. 14 shows a top view of a container with a lid embodying the new design.

[0195] FIG. 15 shows a bottom view of a container with a lid embodying the new design.

[0196] FIG. 16 shows the container of FIGS. 9-15 with the lid open.

[0197] FIG. 17 shows the container of FIG. 16 filled with the fibrous water-soluble unit doses shown in FIG.

[0198] The fibrous water-soluble unit dose may be housed in the container of Figs. 9-17. Surprisingly, it has been found that by having an asymmetric shape along the longitudinal centerline exhibiting upper and lower ridges, the fibrous water-soluble unit dose is less likely to move within the package. In other words, the upper and lower ridges help lock the fibrous water-soluble unit dose by simultaneously applying pressure to both sides of the package tray. Furthermore, due to their structure, the upper and lower ridges allow for compression and absorption of potential shock from impact without affecting the overall shape of the fibrous unit dose. Furthermore, the use of the upper and lower ridges may allow for the creation of a gap between the bottom corner of the fibrous water-soluble unit dose and the bottom of the tray. This gap may protect the fibrous water-soluble unit dose if the package becomes wet.

[0199] Each of the upper or lower ridges may be perforated to facilitate removal. Alternatively, the upper and lower ridges may be cut from the fibrous water-soluble unit dose by the user. The ridges may be used to pretreat spots on fabric. The upper and lower ridges may be attached during pretreatment or may be separated from the fibrous water-soluble unit dose for pretreatment purposes. In addition, the upper ridges facilitate removal from the package by providing a pinch point for the user.

[0200] A. A method for making a fibrous water soluble unit dose comprising: a. delivering a fibrous web material, the fibrous web material being delivered in the form of a continuous strip of fibrous web material; b. cutting the absorbent web material transversely to form a repeating, nested pattern of transversely and generally identically shaped fibrous water soluble unit doses; A method for making fibrous water soluble unit doses, wherein the fibrous water soluble unit doses are nested to form a repeating pattern of laterally and generally identically shaped fibrous water soluble unit doses. B. The method of paragraph A, wherein the fibrous water soluble unit doses are not symmetrical along a centerline of each fibrous water soluble unit dose parallel to the longitudinal edge of the band of fibrous web material. C. The method of paragraphs A or B, wherein the fibrous water soluble unit doses are asymmetric longitudinally along the strip of the fibrous web into which they are cut. D. The method of any one of paragraphs A-C, wherein the fibrous web material is delivered from a supply roll. E. The method of any one of paragraphs A-D, wherein the fibrous water soluble unit doses are nested to form a repeating pattern along the cross-section of the fibrous web, while not being symmetrical along the centerline of each fibrous water soluble unit dose parallel to the longitudinal edge of the band of fibrous material. F. The method of any one of paragraphs A-E, wherein each fibrous water soluble unit dose is symmetrical along a centerline axis of each fibrous water soluble unit dose that lies along an angle relative to the longitudinal axis of the band of fibrous web material. G. The method of any one of paragraphs A-F, wherein adjacent fibrous water soluble unit doses share a common defining cut line. H. The method of any one of paragraphs A-G, wherein the fibrous water soluble unit dose comprises an upper ridge and a lower ridge. I. The method of any one of paragraphs A-H, wherein the fibrous water soluble unit dose comprises one or more protuberances. J. The method of paragraph I, wherein the one or more protuberances are integral to the shape of the water soluble unit dose and are delineated by one or more perforations.

[0201] Dimensions and values ​​disclosed herein should not be understood as being strictly limited to the exact numerical values ​​recited. Instead, unless otherwise indicated, each such dimension is intended to mean both the recited value and a functionally equivalent range surrounding that value. For example, a dimension disclosed as "40 mm" is intended to mean "about 40 mm."

[0202] For purposes of clarity, the total "wt. %" values ​​do not exceed 100 wt.

[0203] All documents cited herein, including cross-referenced documents or related patents or applications, are incorporated herein by reference in their entirety unless expressly excluded or specifically limited. The citation of any document shall not be deemed to be prior art to any invention disclosed or claimed herein, or to teach, suggest or disclose such invention, either alone or in combination with any other reference(s). Furthermore, to the extent that any meaning or definition of a term in this document conflicts with any meaning or definition of the same term in a document incorporated by reference, the meaning or definition assigned to that term in this document shall apply.

[0204] While particular examples and / or embodiments of the present invention have been illustrated and described, it would be obvious to those skilled in the art that various other changes and modifications can be made without departing from the spirit and scope of the invention. It is therefore intended to cover in the appended claims all such changes and modifications that are within the scope of this invention.

Claims

[Claim 1] 1. A method for making a fibrous water soluble unit dose comprising: a. delivering a fibrous web material, said fibrous web material being delivered in the form of a continuous strip of fibrous web material; b. cutting the fibrous web material transversely to form a repeating mosaic pattern of transversely and identically shaped fibrous water soluble unit doses; said fibrous water soluble unit doses are tessellated to form a repeating pattern of lateral and shaped fibrous water soluble unit doses; the fibrous water soluble unit doses are not symmetrical along a centerline of each fibrous water soluble unit dose parallel to a longitudinal edge of the band of fibrous web material; The fibrous water-soluble unit dose comprises a first protrusion formed at one longitudinal end and a second protrusion formed at an opposite longitudinal end, the fibrous water soluble unit doses are symmetrical along an axis that is not parallel to either the longitudinal or transverse axis of the strip into which the fibrous water soluble unit doses are cut; A method for making a fibrous water-soluble unit dose.