Improved reliability of novel WLCSP for package edges including package shielding

Abstract

To provide wafer level packaging architectures with active die regions that are surrounded by extended redistribution layer (RDL) structures.SOLUTION: An electronic package 100 includes a redistribution layer (RDL) 120 having a conductive layer 130 in a first dielectric layer 103, and a second dielectric layer 102 over the conductive layer and the first dielectric layer. The RDL has an extended RDL portion 121 having a first thickness T4 that vertically extends from a bottom surface of the first dielectric layer to a topmost surface of the second dielectric layer. The electronic package includes a die 110 on the RDL. The die has sidewall surfaces, a top surface, and a bottom surface that is opposite from the top surface, and also has an active region 111 on the bottom surface of the die. The first thickness is greater than a second thickness T3 of the RDL that vertically extends from the bottom surface of the first dielectric layer to the bottom surface of the die. The extended portion is over and around the sidewall surfaces.SELECTED DRAWING: Figure 1A

Description

[Technical field]

[0001] Embodiments of the present disclosure relate to semiconductor devices, and more particularly, to a wafer level packaging architecture with an active die area surrounded by an extended redistribution layer (RDL) structure. [Background technology]

[0002] The demand for smaller form factors and increased levels of integration for high performance are driving sophisticated packaging approaches in the semiconductor industry. One such approach is to enable small form factor miniaturization and high performance using wafer level packaging architectures. Such architectures typically rely on dicing processes to dice target dies on a wafer. For example, such dicing processes have been implemented to dice wafer level chip scale packages (WLCSPs), which are considered to be one of the smallest packages available in the existing industry. However, such wafer level packaging architectures also have their own integration challenges.

[0003] One challenge is that wafer level packages are highly susceptible to mechanical assembly and subsequent interconnect (BEOL) applications. This challenge is primarily due to the fact that wafer level packages have unprotected or exposed surfaces and areas. In particular, such wafer level packages have exposed active die areas (e.g., bottom and / or sidewall peripheral areas) that have silicon that is unprotected from the BEOL active areas and that are highly susceptible to assembly yield loss and reliability issues such as moisture and / or thermo-mechanical stress.

[0004] Another challenge is that wafer level packages suffer from micro-cracks in exposed active silicon areas that are typically created during the dicing process. However, in many cases, such micro-cracks go undetected during the manufacturing and assembly process. To reduce the propagation of micro-cracks, it has been proposed to implement crack stop structures within the wafer level package. Similarly, special dicing processes, such as a laser pre-cut process before the blade dicing process, have also been proposed to reduce the risk of generating severe micro-cracks.

[0005] Other wafer-level packaging technologies, such as Flip-Chip Chip Scale Package (FCCSP), perform subsequent assembly steps to cover critical active areas with underfill and / or molding materials. However, due to the additional processing and materials required, FCCSP also has its own integration challenges, such as longer assembly time, higher manufacturing costs, improved robustness, and larger substrate area. Other challenges, particularly for FCCSP, include thermo-mechanical stresses during on-board assembly and temperature / humidity issues in the field that force the propagation of microcracks.

[0006] Therefore, wafer level packaging structures and processes do not significantly reduce or avoid the propagation of such microcracks, ultimately resulting in end device failure, and therefore existing packaging techniques negate the advantages offered by wafer level packaging, making them an undesirable solution. [Brief description of the drawings]

[0007] [Figure 1A] 1 is a cross-sectional view of an electronic package including a die, a redistribution layer (RDL), and an extended RDL portion according to an embodiment.

[0008] [Figure 1B]1 is a cross-sectional view of an electronic package including a die, an RDL, and an extended RDL portion having conductive contacts according to an embodiment.

[0009] [Figure 2A] 1 is a cross-sectional view of an electronic package including a die, an RDL, and an extended RDL portion having conductive pillars according to an embodiment.

[0010] [Figure 2B] 1 is a cross-sectional view of an electronic package including a die, an RDL, and an extended RDL portion having conductive contacts and conductive pillars according to an embodiment.

[0011] [Figure 2C] FIG. 2 is an enlarged view of a portion of a cross-sectional view of an electronic package including a package substrate, an RDL, and an extended RDL portion having conductive pillars electrically coupled to the package substrate according to an embodiment.

[0012] [Figure 2D] FIG. 2 is a top view of an electronic package including a die, an RDL, and an extended RDL portion having a conductive ring according to an embodiment.

[0013] [Figure 2E] FIG. 2 is a top view of an electronic package including a die, an RDL, and an extended RDL portion having multiple conductive pillars according to an embodiment.

[0014] [Figure 3A] 1 is a cross-sectional view of an electronic package including a die, an RDL, and an extended RDL portion according to an embodiment.

[0015] [Figure 3B] 1 is a cross-sectional view of an electronic package including a die, an RDL, and an extended RDL portion having conductive traces according to an embodiment.

[0016] [Figure 3C]1 is a cross-sectional view of an electronic package including a die, an RDL, an extended RDL portion, and a conductive shield according to an embodiment.

[0017] [Figure 3D] 1 is a cross-sectional view of an electronic package including a die, an RDL, an extended RDL portion having conductive traces, and a conductive shield according to an embodiment.

[0018] [Figure 4A] 1 is a cross-sectional view of an electronic package including a die, an RDL, and an extended RDL portion according to an embodiment.

[0019] [Figure 4B] 1 is a cross-sectional view of an electronic package including a die, an RDL, and an extended RDL portion having conductive traces according to an embodiment.

[0020] [Figure 4C] 1 is a cross-sectional view of an electronic package including a die, an RDL, an extended RDL portion, and a conductive shield according to an embodiment.

[0021] [Figure 4D] 1 is a cross-sectional view of an electronic package including a die, an RDL, an extended RDL portion having conductive traces, and a conductive shield according to an embodiment.

[0022] [Figure 5A] 1A-1C are cross-sectional views illustrating a portion of a sequence for packaging one or more electronic packages having a die, an RDL, and an extended RDL portion having one or more conductive contacts in accordance with some embodiments. [Figure 5B] 1A-1C are cross-sectional views illustrating a portion of a sequence for packaging one or more electronic packages having a die, an RDL, and an extended RDL portion having one or more conductive contacts in accordance with some embodiments. [Figure 5C]1A-1C are cross-sectional views illustrating a portion of a sequence for packaging one or more electronic packages having a die, an RDL, and an extended RDL portion having one or more conductive contacts in accordance with some embodiments. [Figure 5D] 1A-1C are cross-sectional views illustrating a portion of a sequence for packaging one or more electronic packages having a die, an RDL, and an extended RDL portion having one or more conductive contacts in accordance with some embodiments. [Figure 5E] 1A-1C are cross-sectional views illustrating a portion of a sequence for packaging one or more electronic packages having a die, an RDL, and an extended RDL portion having one or more conductive contacts in accordance with some embodiments. [Figure 5F] 1A-1C are cross-sectional views illustrating a portion of a sequence for packaging one or more electronic packages having a die, an RDL, and an extended RDL portion having one or more conductive contacts in accordance with some embodiments.

[0023] [Figure 6A] 1A-1C are cross-sectional views illustrating a portion of a sequence for assembling one or more electronic packages having a die, an RDL, and an extended RDL portion having one or more conductive contacts and / or one or more conductive pillars in accordance with some embodiments. [Figure 6B] 1A-1C are cross-sectional views illustrating a portion of a sequence for assembling one or more electronic packages having a die, an RDL, and an extended RDL portion having one or more conductive contacts and / or one or more conductive pillars in accordance with some embodiments.

[0024] [Figure 7A] 1A-1C are cross-sectional views illustrating a portion of a sequence for assembling an electronic package having a die, an RDL, an extended RDL portion having one or more conductive contacts and / or conductive pillars, and a package substrate in accordance with some embodiments. [Figure 7B]1A-1C are cross-sectional views illustrating a portion of a sequence for assembling an electronic package having a die, an RDL, an extended RDL portion having one or more conductive contacts and / or conductive pillars, and a package substrate in accordance with some embodiments. [Figure 7C] 1A-1C are cross-sectional views illustrating a portion of a sequence for assembling an electronic package having a die, an RDL, an extended RDL portion having one or more conductive contacts and / or conductive pillars, and a package substrate in accordance with some embodiments. [Figure 7D] 1A-1C are cross-sectional views illustrating a portion of a sequence for assembling an electronic package having a die, an RDL, an extended RDL portion having one or more conductive contacts and / or conductive pillars, and a package substrate in accordance with some embodiments.

[0025] [Figure 8A] 1A-1C are cross-sectional views illustrating a portion of a sequence for packaging one or more electronic packages having a die, an RDL, and an extended RDL portion having one or more conductive traces in accordance with some embodiments. [Figure 8B] 1A-1C are cross-sectional views illustrating a portion of a sequence for packaging one or more electronic packages having a die, an RDL, and an extended RDL portion having one or more conductive traces in accordance with some embodiments. [Figure 8C] 1A-1C are cross-sectional views illustrating a portion of a sequence for packaging one or more electronic packages having a die, an RDL, and an extended RDL portion having one or more conductive traces in accordance with some embodiments. [Figure 8D] 1A-1C are cross-sectional views illustrating a portion of a sequence for packaging one or more electronic packages having a die, an RDL, and an extended RDL portion having one or more conductive traces in accordance with some embodiments.

[0026] [Figure 9]FIG. 1 is a schematic diagram of a computing device including an electronic package having a die, an RDL, and an extended RDL portion having conductive interconnects according to an embodiment. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0027] Described herein is an electronic package having an active die area protected by an extended redistribution layer (RDL) structure according to various embodiments. In the following description, various aspects of the exemplary embodiments are described using terms commonly used by those skilled in the art to convey the bulk of their work to others skilled in the art. However, it will be apparent to those skilled in the art that the present invention may be practiced with only some of the described aspects. For purposes of explanation, specific numbers, materials and configurations are set forth to provide a thorough understanding of the exemplary embodiments. However, it will be apparent to those skilled in the art that the present invention may be practiced without the specific details. In other instances, well-known features are omitted or simplified so as not to obscure the exemplary embodiments.

[0028] Although various operations are described as multiple separate operations, in an order that is most helpful in understanding the invention, the order of description should not be construed to imply that these operations are necessarily order dependent, and in particular, these operations do not have to be performed in the order that they are presented.

[0029] As mentioned above, current packaging solutions have begun to use wafer-level packaging architectures. However, existing wafer-level packaging architectures are not without problems. For example, such wafer-level packages suffer from low assembly yield and reliability. In particular, unprotected surfaces and exposed areas located around (and in the periphery of) the active die area are highly susceptible to thermo-mechanical stresses, humidity, mechanical assembly process issues, and other back-end interconnect (BEOL) applications. As such, additional complex assembly process steps have been proposed to add protective layers or screening and detection measurements (e.g., infrared (IR) inspection) to attempt to protect or identify manufacturing failures in such unprotected surfaces and / or areas. However, the inclusion of additional assembly steps, materials, and equipment leads to reduced yields, added costs, increased reliability studies and development time, and increased package substrate area. Thus, embodiments described herein include electronic packages that utilize an extended RDL structure to protect exposed active die areas and also provide shielding connections.

[0030] Thus, the embodiments described herein include a die having an active area and an RDL having one or more extended RDL structures. In particular, the extended RDL structure may include an extended RDL portion, a conductive pillar and / or ring, and a conductive shield. The extended RDL portion is referred to as "extended" because the RDL has a seamless extension over and around the exposed peripheral area of ​​the active die. That is, the active die may be centered generally within the footprint of the RDL, resulting in unoccupied space on the RDL, and the extended portion may use such unoccupied space of the RDL. In embodiments herein, the electronic package may have an uninterrupted dielectric passivation layer over the critical BEOL active die area. For example, the exposed peripheral area may be a diced trench surface (or edge) disposed around the BEOL active die area. The surface may be part of a trench implemented by a grooving process (e.g., laser blade or lithographic grooving) that directly patterns an area on a sidewall surface of the active die, where the thickness of the grooved area is greater than the thickness of the active die area.

[0031] Thus, a seamless extended RDL portion may be placed directly over and around the exposed peripheral area resulting from the diced sidewall surface around the active die area. The extended RDL portion may be implemented using existing assembly processes with modified process flow sequences in combination with one or more RDL structures that are extended across the kerf area. The extended RDL portion provides one or more layers of protection to the wafer level packaging architecture to prevent microcracks and / or at least substantially slow down the propagation of microcracks for the lifetime of the device. Furthermore, in some embodiments, the extended RDL portion enables optimal electrical connection to any package shield by extending the conductive interconnects (e.g., pads or traces, etc.) to have one or more exposed surfaces at the side of the electronic package. Thus, embodiments enable greater robustness against thermo-mechanical stresses, humidity, and other mechanical assembly steps such as dicing, handling, testing, and on-board assembly. As such, the embodiments described herein enable higher yields and reliability, lower platform costs, denser product designs, and reduced packaging materials and reliable metrology.

[0032] Referring to FIG. 1A, a cross-sectional view of an electronic package 100 according to an embodiment is shown. In an embodiment, the electronic package 100 may be any type of wafer level package. For example, the electronic package 100 may be a WLCSP or a fan-in wafer level package (FI-WLP), etc. In an embodiment, the electronic package 100 may be combined with any other chip-scale packaging architecture (e.g., a flip-chip chip-scale package (FCCSP), etc.). Also, for simplicity, FIG. 1A shows a single extended RDL portion 121 on a single sidewall surface of the die 110, but it should be understood that any number of extended RDL portions 121 may be disposed on any of the sidewall surfaces of the die 110.

[0033] In some embodiments, the electronic package 100 may include a die 110 and an RDL 120. The die 110 may be disposed above the RDL 120. The die 110 may have sidewall surfaces, a top surface, and a bottom surface opposite the top surface. In an exemplary embodiment, the bottom surface of the die 110 may be disposed directly on the top surface of the RDL 120. Further, in such an exemplary embodiment, a plurality of solder balls 134 (or solder bumps) may be disposed on a bottom surface of the RDL 120 opposite the top surface of the RDL 120. For example, the solder balls 134 may electrically couple conductive pads of the RDL 120 to a package substrate (e.g., a printed circuit board (PCB)) or an interposer, or the like. Use of the RDL 120 to provide metallization interconnects (e.g., first level interconnects (FLI)) that electrically couple the solder balls 134 to active elements (e.g., transistors, etc.) on the bottom surface of the die 110 is described in more detail below.

[0034] In an embodiment, the die 110 may be any type of die. For example, the die 110 may be a semiconductor die, an electronic device (e.g., a wireless device), an integrated circuit (IC), a central processing unit (CPU), a graphics processing unit (GPU), a microprocessor (or processor), a platform controller hub (PCH), a memory (e.g., a high bandwidth memory (HBM)), or a field programmable gate array (FPGA), etc. In some embodiments, the die 110 may have an active area 111 and a crack stop component 112. In an embodiment, the active area and the crack stop component 111-112 may have a thickness T1.

[0035] In an embodiment, active area 111 may be located on a bottom surface of die 110. In an embodiment, active area 111 may have an active surface that is electrically coupled to RDL 120. In some embodiments, active area 111 may comprise any type of active element (in other embodiments, any type of active and / or passive element). For example, active area 111 may comprise circuitry, transistors, etc. suitable for processing signals. Active area 111 serves as a BEOL area for active elements that are stacked on top of each other.

[0036] In an exemplary embodiment, the crack stop component 112 may be located on a bottom surface of the die 110. In particular, in an embodiment, the crack stop component 112 may be located on a region of the bottom surface of the die 110 that is around the active area 111. In some embodiments, the crack stop component 112 may be located on a peripheral region of the bottom surface of the die 110. In an embodiment, the crack stop component 112 may be implemented as a picture-frame structure or the like that surrounds the active area 111. Thus, in some embodiments, the crack stop component 112 may be separated from the active area 111 by a portion of the die 110 (e.g., the silicon bulk, etc.).

[0037] As described above, the die 110 may have one or more trench-like regions 122. In an embodiment, the trench-like region 122 may be located on one or more of the sidewall surfaces of the die 110. In some embodiments, the trench region 122 (or a trench-shaped region) may be patterned directly on at least one or more bottom portions of the sidewall surfaces of the die 110. That is, the trench region 122 may be located around one or more peripheral regions (e.g., one or more corner edges of the bottom surface of the die 110) of the die 110. For example, a trench region 122 may be located on each of the four sidewall surfaces of the die 110. However, in an exemplary embodiment, a single trench region 122 is shown on the right sidewall surface of the die 110. However, it should be understood that an embodiment may include any number of trench regions 122, patterned on any of the sidewall surfaces of the die 110. Examples of multiple trench regions 122 are provided in more detail below.

[0038] As mentioned above, in some embodiments, trench region 122 may be a portion of a trench or groove, or the like, implemented by a grooving process or the like. For example, the grooving process may directly pattern a trench, which is then diced into trench region 122 on a sidewall surface of die 110, using a laser, a blade, or an etch (e.g., chemical wet etching), or the like. In some embodiments, trench region 122 may have a thickness T2. In an embodiment, thickness T2 of trench region 122 may be greater than thickness T1 of active area and crack stop components 111-112. Examples of grooving processes used to form trench region 122 are provided in more detail below.

[0039] In some embodiments, the RDL 120 may include one or more extended RDL portions 121, a plurality of vias 131, a conductive layer 130, and one or more dielectric layers 102-103. In an embodiment, the conductive layer 130 may be disposed within the dielectric layer 103. In an embodiment, the dielectric layer 102 may be disposed above the conductive layer 130 and the dielectric layer 103. In an embodiment, the RDL 120 may have a thickness T3. As shown in FIG. 1A, the thickness T3 may be defined from a bottom surface of the dielectric layer 103 to a bottom surface of the die 110. The vias 131 may extend through the dielectric layer 102. In an embodiment, the vias 131 may extend vertically from a top surface of the conductive layer 130 to a bottom surface of the die 110. In some embodiments, the vias 131 may electrically couple the solder balls 134 and the conductive layer 130 to the active area 111 of the die 110.

[0040] The conductive layer 130 may be any type of conductive interconnect. For example, the conductive layer 130 may comprise a copper pad, trace, line, or plane, etc. (e.g., conductive shield, pillar, ring, etc.) that may be electrically coupled to the solder balls 134 and the vias 131, etc. The vias 131 may be any type of via interconnect having any type of shape (e.g., through silicon vias (TSVs), lithographically defined vias, etc.). In the exemplary embodiment, a single conductive layer 130 having vias 131 is shown in the RDL 120. However, it should be understood that the RDL 120 may comprise any number of conductive layers 130 having any number of stacked vias 131. Also, in the exemplary embodiment, the vias 131 are shown as having a substantially vertical sidewall profile. Such an embodiment may be provided where the via opening is lithographically defined. However, it should be understood that the embodiment may comprise a via 131 having a tapered sidewall profile. Typically, such an embodiment is formed when the via opening is formed by a laser drilling process.

[0041] In some embodiments, the dielectric layers 102-103 may be a build-up film, a solder resist layer (e.g., solder mask), a photosensitive interlayer insulation (PID), an epoxy material, or any other dielectric material. In embodiments, the dielectric layers 102-103 may include the same dielectric material, while in other embodiments, the dielectric layers 102-103 may include different dielectric materials. For example, the dielectric layer 103 may be a solder resist layer and the dielectric layer 102 may be a build-up film. Also, in the exemplary embodiment, two dielectric layers 102-103 are shown in the RDL 120. However, it should be understood that an embodiment may include any number of dielectric layers 102-103 in the RDL 120 (e.g., a single dielectric layer or more than two dielectric layers).

[0042] As discussed above, the RDL 120 may comprise one or more extended RDL portions 121. In an exemplary embodiment, the one or more extended RDL portions 121 are shown above and around the trench region 122 of the die 110. In particular, the extended RDL portions 121 are shown extending laterally beyond a peripheral region of the bottom surface of the die 110 (i.e., the bottom corner edges of the die 110) and extending vertically to surround the bottom of the sidewall surfaces of the die 110. For example, the extended RDL portions 121 may extend vertically from a bottom surface of the dielectric layer 103 to a top surface of the dielectric layer 102 (i.e., the top surface of the trench region 122).

[0043] In the exemplary embodiment, the extended RDL portion 121 is shown having a semi-trench sidewall profile (or semi-grouping sidewall profile) at the upper end. However, it should be understood that embodiments may include an extended RDL portion 121 having a substantially sidewall profile, a tapered sidewall profile, or the like. Examples of multiple extended RDL portions 121 having such profiles are provided in more detail below.

[0044] In an exemplary embodiment, the extended RDL portion 121 may have a thickness T4 that overlaps with the thickness T1 of the active region 111. In an embodiment, the thickness T4 may be substantially greater than the thickness T1. In an embodiment, the thickness T4 may be approximately equal to the sum of the thickness T3 of the RDL 120 and the thickness T2 of the trench region 122. Meanwhile, in other embodiments, the extended RDL portion 121 may have a thickness that is greater than the sum of the thickness T3 of the RDL 120 and the thickness T2 of the trench region 122 (e.g., as shown in Figures 2A-2B below). Furthermore, the RDL 120 and the extended RDL portion 121 may have a combined footprint that is greater than the footprint of the bottom surface of the die 110. For example, the footprint of the bottom surface of the die 110 may be entirely within the combined footprint of the RDL 120 and the extended RDL portion 121.

[0045] Thus, because the extended RDL portion 121 is disposed directly on the trench region 122 and / or the sidewall surface of the die 110, the extended RDL portion 121 acts as a direct seamless extension of the RDL 120 that provides one or more additional protective barriers to the active area 111. That is, in an embodiment, the extended RDL portion 121 may use a portion of the dielectric layer 102 to generally surround the trench region 122 and the thickness T1 of the active area 111, thereby acting as an additional protective layer for the BEOL active area of ​​the die 110. For example, the extended RDL portion 121 increases the extent of the space (or width) between the outer sidewall surface of the active area 111 and the sidewall surface exposed to the exterior of the electronic package 100 without requiring additional protective layers, such as mold and underfill layers, that would adversely affect the wafer level packaging architecture.

[0046] In the exemplary embodiment, the extended RDL portion 121 is shown as a stack of portions each comprising a dielectric layer 102, a dielectric layer 103, and a conductive layer 130. However, it should be understood that in some embodiments, the extended RDL portion 121 may comprise portions consisting only of the dielectric layer 102 and the conductive layer 130, while in other embodiments, it should be understood that the extended RDL portion 121 may comprise any number of portions made up of any number of the dielectric layers 102-103 and the conductive layer 130. Examples of multiple extended RDL portions 121 are provided in more detail below.

[0047] 1B, a cross-sectional view of an electronic package 101 according to a further embodiment is shown. In an embodiment, the electronic package 101 of FIG. 1B may be substantially similar to the electronic package 100 of FIG. 1A, except that one of the extended RDL portions 121 may include one or more conductive contacts 132. In some embodiments, the conductive contacts 132 may electrically couple the RDL 120 and / or the active area 111 of the die 110 to any other electrical components. For example, such electrical components may include conductive shields or interconnects, etc., as described in more detail below. In an embodiment, the conductive contacts 132 may be any type of conductive extension having an exposed sidewall surface. In an embodiment, the conductive contacts 132 may be conductive plugs, trenches, grooves, pillars, etc. Thus, in some embodiments, the conductive contacts 132 may have slanted (or tapered) surfaces, rounded surfaces, grooved surfaces (i.e., the surfaces of a portion of a trench), or substantially vertical surfaces, etc.

[0048] In some embodiments, the exposed sidewall surface of the conductive contacts 132 may have a thickness T5 that enhances the electrical connection to the RDL 120. For example, the thickness T5 may provide a larger exposed surface area for the conductive contacts 132 to have an optimal electrical connection with any type of conductive shield or interconnect, etc. In some embodiments, the conductive contacts 132 may be patterned directly in the RDL 120, thereby exposing one or more active edges that may enable optimal electrical connection to any type of package shielding architecture.

[0049] In an exemplary embodiment, the thickness T5 may be less than the thickness T3 of the RDL 120. However, in other embodiments, the thickness T5 may be approximately equal to or greater than the thickness T3 of the RDL 120. For example, the thickness T5 may be greater than the thickness of the sidewall surface of the die 110, which extends vertically from the bottom surface to the top surface of the die 110. Note that such examples of conductive contacts 132 (also referred to as conductive traces) are provided in more detail below. Also, in the exemplary embodiment, the extended RDL portion 121 is shown disposed in each of the trench regions 122 of the die 110, while the electrical contacts 132 are shown disposed on only one of the sidewall surfaces of the electronic package 101. However, it should be understood that an embodiment may include any number of extended RDL portions 121 with any number of electrical contacts 132 that may be disposed on either the sidewall surfaces of the die 110 and the electronic package 101.

[0050] 2A, a cross-sectional view of an electronic package 200 according to a further embodiment is shown. In an embodiment, the electronic package 200 of FIG. 2A may be substantially similar to the electronic packages 100-101 of FIGS. 1A-1B, except that one or more extended RDL portions 221 may include one or more conductive pillars 233. In some embodiments, the conductive pillars 233 may be coupled to a package substrate (or the like) to improve the reliability of the solder joints of the electronic package 200 without the need for any additional measures such as an underfill material. As described above, die 210 having active area 211, crack stop component 212 and trench region 222, and RDL 220 having conductive layer 230, via 231, dielectric layers 202-203, extended RDL portion 221 and solder ball 234 in FIG. 2A may be substantially similar to die 110 having active area 111, crack stop component 112 and trench region 122, and RDL 120 having conductive layer 130, via 131, dielectric layers 102-103, extended RDL portion 121 and solder ball 134 in FIG. 1A.

[0051] In some embodiments, the conductive pillars 233 may be electrically coupled to any type of substrate by a solder interconnect (e.g., solder paste). In particular, the conductive pillars 233 may be disposed at and coupled to a peripheral region of such a substrate. In embodiments, the conductive pillars 233 may be any type of conductive interconnect having substantially vertical sides. In some embodiments, the conductive pillars 233 may be located around the periphery of the RDL 220 to form a plurality of patterned structures, as shown in Figures 2C-2D below.

[0052] 2B, a cross-sectional view of an electronic package 201 according to a further embodiment is shown. In an embodiment, the electronic package 201 of FIG. 2B may be substantially similar to the electronic package 200 of FIG. 2A, except that one or more extended RDL portions 221 may include one or more conductive contacts 232 and one or more conductive pillars 233. In some embodiments, one or more extended RDL portions 221 may extend vertically from the upper ends of the conductive contacts 232 to the bottoms of the conductive pillars 233. Thus, such extended RDL portions 221 may have a thickness and exposed sidewall surfaces that enable improved solder joint reliability and larger electrical connections (and the like) to the package shielding architecture. Also, in the exemplary embodiment, the electrical contacts 232 and the conductive pillars 233 are shown as being disposed together on only one of the extended RDL portions 221. However, it should be understood that an embodiment may include electrical contacts 232 and conductive pillars 233 disposed on any number of extended RDL portions 221.

[0053] 2C, a cross-sectional view of a magnified portion of FIG. 2C is shown after the conductive pillars 233 of the extended RDL portion 221 according to an embodiment are electrically coupled to the package substrate 260. That is, in an exemplary embodiment, the conductive pillars 233 may be electrically coupled to the package substrate 260 (e.g., a PCB or an interposer) by solder bumps 236. Meanwhile, the conductive layer 230 of the RDL 220 may be electrically coupled to the package substrate 260 by solder balls 234. The conductive pillars 233 may have a width W. In an embodiment, the width W may be less than about 100 μm. In an embodiment, the width W may be equal to or less than about 50 μm.

[0054] 2D-2E, a series of bottom design views of electronic packages 250-251 according to further embodiments are shown. In some embodiments, electronic packages 250-251 of FIGS. 2D-2E may be substantially similar to at least one of electronic packages 200-201 of FIGS. 2A-2B, except that a conductive ring 233 is used in FIG. 2D and a plurality of conductive pillars 233 is used in FIG. 2E. Thus, the conductive rings and pillars 233 of FIGS. 2D-2E may be substantially similar to the conductive pillars 233 of FIGS. 2A-2B.

[0055] That is, in the embodiment of Figures 2A-2B, conductive pillars 233 may be patterned in the outer peripheral region of the RDL 220 (i.e., extended RDL portion 221) to form one or more conductive interconnects, such as the conductive ring shown in Figure 2D or the conductive pillars shown in Figure 2E. In the exemplary embodiment of Figure 2D, the conductive ring 233 may be a single continuous conductive interconnect that generally surrounds the dielectric 203 and the solder balls 234. Meanwhile, in the exemplary embodiment of Figure 2E, the conductive pillars 233 may be conductive interconnects spaced apart by gaps 235 that collectively surround the dielectric 203 and the solder balls 234.

[0056] Moreover, in some embodiments described herein, the conductive interconnects may be disposed in predetermined regions on the sidewall surface of the die, including conductive contacts, pillars, and / or traces, which may be spaced apart from one another by gap spacings (e.g., as shown with the conductive interconnects in FIG. 2D). Nevertheless, in other embodiments described herein, any of the conductive interconnects may be disposed on the sidewall surface of the die to surround the entire width / length of such sidewall surface of the die (e.g., as shown with the conductive interconnects in FIG. 2E). Thus, such conductive interconnects described herein in the extended RDL portion provide improved support to the electronic package, substantially reducing any thermo-mechanical pressures and pressures associated with coefficient of thermal expansion (CTE) mismatch between the electronic package and the board (or package substrate). For example, these conductive interconnects enable the electronic package to have improved reliability in harsh conditions (e.g., −40 / 125° C. and −55 / 125° C., etc.) typically experienced in the automotive industry and the like. Furthermore, such embodiments of the conductive interconnect may enable the electronic package to be made substantially smaller since supporting solder balls that are not essential (NC) for functionality (e.g., solder ball 234 in Figures 2D-2E) may not be required.

[0057] Referring to FIG. 3A, a cross-sectional view of an electronic package 300 according to a further embodiment is shown. In an embodiment, the electronic package 300 of FIG. 3A may be substantially similar to the electronic package 200 of FIG. 2A, except that the dielectric layer 302 in the extended RDL portion 321 extends vertically from the bottom surface of the dielectric layer 302 to the top surface of the die 310 without the need for a trench region. Thus, the die 310 with the active area 311 and the crack stop component 312, and the RDL 320 with the conductive layer 330, the via 331, the dielectric layers 302-303, the extended RDL portion 321, and the solder balls 334 in FIG. 3A may be substantially similar to the die 210 with the active area 211 and the crack stop component 212, and the RDL 220 with the conductive layer 230, the via 231, the dielectric layers 202-203, the extended RDL portion 221, and the solder balls 234 in FIG. 2A.

[0058] In an exemplary embodiment, the dielectric layer 302 in the extended RDL portion 321 may have a substantially vertical sidewall profile. However, it should be understood that the dielectric layer 302 in the extended RDL portion 321 may have a tapered sidewall profile or any other desired profile. As mentioned above, in an embodiment, the extended RDL portion 321 may have a top surface that is substantially flush with the top surface of the die 310. In some embodiments, the extended RDL portion 321 with the dielectric layer 302 may entirely cover each of the sidewall surfaces of the die 310, while in other embodiments, the extended RDL portion 321 with the dielectric layer 302 may partially cover each of the sidewall surfaces of the die 310.

[0059] 3B, a cross-sectional view of an electronic package 301 according to a further embodiment is shown. In an embodiment, the electronic package 301 of FIG. 3B may be substantially similar to the electronic package 301 of FIG. 3A, except that the conductive traces 332 in the extended RDL portion 321 extend vertically from the top surface of the conductive layer 330 to the top surface of the die 310 and surround the dielectric layer 302 in the extended RDL portion 321. For example, the conductive traces 332 and the dielectric layer 302 of the extended RDL portion 321 may both have top surfaces that are substantially coplanar with the top surface of the die 310. In some embodiments, the extended RDL portion 321 with the conductive traces 332 may entirely cover each of the sidewall surfaces of the dielectric layer 302 in the extended RDL portion 321. Meanwhile, in other embodiments, the extended RDL portion 321 with the conductive traces 332 may partially cover each of the sidewall surfaces of the dielectric layer 302 in the extended RDL portion 321. Also, in some embodiments, the conductive traces 332 may be disposed at predetermined locations on the sidewall surface of the die 310 (and spaced apart from one another at a predetermined gap interval (not shown)), while in other embodiments, the conductive traces 332 may extend the entire width / length of the sidewall surface of the die 310.

[0060] 3C, a cross-sectional view of an electronic package 350 according to a further embodiment is shown. In an embodiment, the electronic package 350 of FIG. 3C may be substantially similar to the electronic package 300 of FIG. 3A, except that a conductive shield 360 is electrically coupled to an exposed sidewall surface of the conductive layer 330, and the conductive shield 360 embeds the extended RDL portion 321 and the die 310. For example, the conductive shield 360 may be disposed directly over and around the outer sidewall surface of the extended RDL portion 321. Additionally, in an embodiment, the conductive shield 360 may be disposed directly on the top surface of the extended RDL portion 321 and the die 310.

[0061] In some embodiments, the conductive shield 360 may be any type of packaging shield architecture. In embodiments, the conductive shield 360 may include any conductive material. For example, the conductive material may include copper, aluminum, gold, nickel, titanium, silver, stainless steel, or the like. Additionally, in other embodiments, the conductive shield 360 may include a stack of conductive layers stacked on top of each other. In embodiments, the conductive shield 360 may be implemented in a sputtering tool, or the like.

[0062] 3D, a cross-sectional view of an electronic package 351 according to further embodiments is shown. In an embodiment, the electronic package 351 of FIG. 3D may be substantially similar to the electronic package 350 of FIG. 3C, except that a conductive shield 360 is electrically coupled to the exposed sidewall surfaces of the conductive layer 330 and the conductive traces 332, and the conductive shield 360 embeds the extended RDL portion 321 and the die 310. For example, the conductive shield 360 may be disposed directly over and around the outer sidewall surfaces of the extended RDL portion 321. That is, as shown in the exemplary embodiment, the conductive shield 360 may be disposed directly on the dielectric layer 303 and the outer sidewall surfaces of the conductive layer 330 and the conductive traces 332. Furthermore, in some embodiments, the conductive shield 360 may be disposed directly on the top surface of the extended RDL portion 321 and the die 310. That is, as shown in the exemplary embodiment, the conductive shield may be disposed directly on the top surfaces of the conductive traces 332, the dielectric layer 302, and the die 310.

[0063] 4A, a cross-sectional view of an electronic package 400 according to a further embodiment is shown. In an embodiment, the electronic package 400 of FIG. 4A may be substantially similar to the electronic package 300 of FIG. 3A, except that the extended RDL portion 421 has a dielectric layer 404 disposed over and around the sidewall surfaces of the die 410, the dielectric layer 404 is also disposed over a peripheral region on the bottom surface of the die 110, and the dielectric layer 404 is directly bonded to the dielectric layer 402 in the RDL 420. Thus, die 410 having active area 411 and crack stop component 412, and RDL 420 having conductive layer 430, via 431, dielectric layers 402-404, extended RDL portion 421 and solder ball 434 in FIG. 4A may be substantially similar to die 310 having active area 311 and crack stop component 312, and RDL 320 having conductive layer 330, via 331, dielectric layers 302-203, extended RDL portion 321 and solder ball 334 in FIG. 3A.

[0064] In some embodiments, dielectric layer 404 may comprise a dielectric material that is the same as or different from the dielectric material of dielectric layer 402 (and / or, in some embodiments, dielectric layer 403). In embodiments, when dielectric layers 402 and 404 are composed of different dielectric materials, extended RDL portion 421 may comprise portions from dielectric layer 403, conductive layer 430, and dielectric layer 404.

[0065] In an exemplary embodiment, the dielectric layer 404 may extend vertically from a bottom surface of the dielectric layer 404 (and / or the dielectric layer 402) to a top surface of the die 410. In such an embodiment, the dielectric layer 404 may have a substantially vertical sidewall profile. However, it should be understood that the dielectric layer 404 may have a tapered sidewall profile or any other desired profile. As mentioned above, in an embodiment, the extended RDL portion 421 may have a top surface that is substantially flush with the top surface of the die 410. In some embodiments, the extended RDL portion 421 with the dielectric layer 404 may entirely cover each of the sidewall surfaces of the die 410, while in other embodiments, the extended RDL portion 421 with the dielectric layer 404 may partially cover each of the sidewall surfaces of the die 410.

[0066] 4B, a cross-sectional view of an electronic package 401 according to a further embodiment is shown. In an embodiment, the electronic package 401 of FIG. 4B may be substantially similar to the electronic package 401 of FIG. 4A, except that the conductive traces 432 in the extended RDL portion 421 extend vertically from the top surface of the conductive layer 430 to the top surface of the die 410 and surround the dielectric layer 404 in the extended RDL portion 421. For example, the conductive traces 432 and the dielectric layer 404 of the extended RDL portion 421 may both have top surfaces that are substantially coplanar with the top surface of the die 410. In some embodiments, the extended RDL portion 421 with the conductive traces 432 may entirely cover each of the sidewall surfaces of the dielectric layer 404 in the extended RDL portion 421. Meanwhile, in other embodiments, the extended RDL portion 421 with the conductive traces 432 may partially cover each of the sidewall surfaces of the dielectric layer 404 in the extended RDL portion 421.

[0067] Referring to FIG. 4C, a cross-sectional view of an electronic package 450 according to a further embodiment is shown. In an embodiment, the electronic package 450 of FIG. 4C may be substantially similar to the electronic package 400 of FIG. 4A, except that a conductive shield 460 is electrically coupled to an exposed sidewall surface of the conductive layer 430, and the conductive shield 460 embeds the extended RDL portion 421 and the die 410. In particular, for example, the conductive shield 460 may be disposed directly over and around the outer sidewall surfaces of the dielectric and conductive layers 403-404 and 430 of the extended RDL portion 421. Furthermore, in an embodiment, the conductive shield 460 may be disposed directly on the top surface of the dielectric layer 404 of the die 410 and the extended RDL portion 421. In an embodiment, the conductive shield 460 of FIG. 4C may be substantially similar to the conductive shield 360 of FIG. 3C.

[0068] 4D, a cross-sectional view of an electronic package 451 according to a further embodiment is shown. In an embodiment, the electronic package 451 of FIG. 4D may be substantially similar to the electronic package 450 of FIG. 4C, except that a conductive shield 460 is electrically coupled to exposed sidewall surfaces of the conductive layer 430 and conductive traces 432, and the conductive shield 460 embeds the extended RDL portion 421 and the die 410. For example, the conductive shield 460 may be disposed directly over and around the outer sidewall surfaces of the dielectric layer 403, conductive layer 430, and conductive traces 432 of the extended RDL portion 421. Additionally, in some embodiments, the conductive shield 460 may be disposed directly on the top surface of the die 410, as well as on the top surfaces of the conductive traces 432 and dielectric layer 404 of the extended RDL portion 421.

[0069] 5A-5F, a series of cross-sectional views are shown illustrating a process for patterning a wafer 590 to form one or more electronic packages 500-501 in accordance with some embodiments. The electronic packages 500-501 of FIGs. 5D-5E are substantially similar to those shown and described with respect to the electronic packages 100-101 of FIGs. 1A-1B. However, it should be understood that the substantially similar electronic packages 500-501 may be implemented using structures (e.g., extended RDL portions) similar to any of the structures described above with respect to FIGs. 2A-2E, 3A-3D, and 4A-4D.

[0070] 5A, a cross-sectional view of a wafer 590 is shown, according to an embodiment. In some embodiments, the wafer 590 may be any suitable type of wafer. For example, the wafer 590 may be a bulk silicon wafer, a silicon-on-insulator (SOI) wafer, an engineered substrate having one or more semiconductor materials (e.g., crystalline silicon, amorphous silicon, polysilicon, etc.), etc. In an embodiment, the wafer 590 may be polished to a predetermined thickness.

[0071] In some embodiments, wafer 590 may comprise die 510 and kerf region 540. In an exemplary embodiment, each of die 510 may be formed from one of the wafer die regions (shown in dashed lines) in wafer 590 that is spaced apart from the other wafer die regions by kerf region 540. In an embodiment, each of die 510 may comprise active region 511 and crack stop component 512. In an embodiment, kerf region 540 may comprise a process control monitor (PCM) region, or the like. In such an embodiment, active region 511, crack stop component 512, and PCM region are part of a BEOL region on the active side of wafer 590 that may be implemented with BEOL processing, or the like.

[0072] 5B, a cross-sectional view of wafer 590 is shown after trench opening 505 is formed according to an embodiment. In an embodiment, trench opening 505 may be patterned in kerf region 540 to form trench region 522 in a sidewall surface of die 510. In some embodiments, trench opening 505 may be implemented with a laser drilling process or a lithography process, or the like. In an embodiment, trench opening 505 may be patterned with a thickness that is greater than the thickness of the BEOL regions on the active side of wafer 590. In an embodiment, trench region 522 provides an exposed sidewall surface around the active side of die 510 that will be generally filled with a later-deposited dielectric layer to protect active area 511 of die 510 (as shown in FIG. 5C below).

[0073] 5C, a cross-sectional view of the wafer 590 is shown after a dielectric layer 502 has been disposed over and around the active area 511, the crack stop component 512, and the trench area 522, according to an embodiment. In an embodiment, the dielectric layer 502 may be a laminate layer or may be deposited by any other suitable process. The dielectric layer 502 may be a build-up film, a solder resist layer (e.g., solder mask), a PID, an epoxy material, or any other dielectric material. In an embodiment, the dielectric layer 502 is disposed over the active surface of the wafer 590 and the entire kerf area 540 with a predetermined thickness, and the dielectric layer 502 is disposed in the trench opening 505 to form a dielectric trench (or a dielectric filled trench) in the kerf area 540.

[0074] In some embodiments, the dielectric layer 502 may be patterned to form an opening 506 within the footprint of one or more kerf regions 540. In embodiments, the opening 506 may be located substantially within the footprint of an initial trench opening that was formed in the active surface of the wafer 590 (as shown in FIG. 5B). In embodiments, the opening 506 may be implemented with a laser drilling process or a lithography process, or the like. Note that the opening 506 may be omitted (if necessary) based on the desired packaging design.

[0075] 5D, a cross-sectional view of a wafer 590 is shown after an RDL 520 having an extended RDL portion 521 has been formed, according to an embodiment. In an embodiment, the RDL 520 may comprise a dielectric layer 503, a conductive layer 530, a via 531, and a conductive contact 532. In some embodiments, a conductive material may be disposed over the dielectric layer 502, a previously patterned opening (as shown in FIG. 5C), and a via opening (not shown) (e.g., using laser drilling) to form the conductive layer 530, the conductive contact 532, and the via 531, respectively. For example, the conductive material may be bare copper, etc. Although one conductive layer 530 is shown in FIG. 5D, it should be understood that an embodiment may include any number of conductive layers 530.

[0076] In embodiments, a dielectric layer 503 may be disposed over and around the conductive layer 530. In some embodiments, the dielectric layer 503 may be the same as or different from the dielectric layer 502. Solder balls 534 may be directly bonded to the conductive layer 530. As described herein, the RDL 520 has extended RDL portions 521 that may be mounted over and around trench regions 522 in the sidewall surfaces of the die 510. Furthermore, in some embodiments, one or more of the extended RDL portions 521 may include conductive contacts 532 having exposed sidewall surfaces after a subsequent dicing process (as shown in FIGS. 5E-5F).

[0077] 5E-5F, cross-sectional views of electronic packages 500-501 after the wafer has been diced are shown, according to some embodiments. That is, after RDL 520 has been implemented, the wafer may be diced in a dicing process (e.g., laser machining process, dicing process, etc.) that fully or partially removes the kerf region, thereby implementing diced electronic packages 500-501 having extended RDL portions 521. Thus, as described in the above embodiments, extended RDL portions 521 may thus be used to protect trench regions 522 and active areas 511 of die 510. Additionally, in other embodiments, extended RDL portions 521 may comprise vertically extending dielectric layers and / or conductive contacts, traces, pillars, and / or shields.

[0078] 6A-6B, a series of cross-sectional views are shown illustrating a process for patterning a wafer 690 to form one or more electronic packages 600-601 and 604 in accordance with some embodiments. Electronic packages 600-601 and 604 in FIG. 6B are similar to those shown and described with respect to electronic packages 500-501 in FIGS. 5E-5F.

[0079] In particular, in the following exemplary embodiment, beginning with Figure 6A, the structure of wafer 690 is similar to the structure of wafer 590 shown in Figure 5D, except that extended RDL portion 621 may further comprise conductive pillars 633. However, it should be understood that substantially similar electronic packages 600-601 and 604 may be implemented using structures similar to any of the structures described above with respect to Figures 1A-1B, 2A-2E, 3A-3D, and 4A-4D.

[0080] 6A, a cross-sectional view of a wafer 690 is shown after an RDL 620 with extended RDL portion 621 has been formed according to an embodiment. As mentioned above, the RDL 620 with extended RDL portion 621 disposed in the wafer 690 in FIG. 6A is substantially similar to the RDL 520 with extended RDL portion 521 disposed in the wafer 590 in FIG. 5D, except that one or more conductive plating processes may be performed to provide conductive pillars 633 on the conductive layer 630. Thus, die 610 having active area 611, crack stop component 612, and trench region 622, and RDL 620 having conductive layer 630, via 631, dielectric layers 602-603, and extended RDL portion 621 having conductive contact 632, kerf region 640, and solder ball 634 in FIG. 6A may be substantially similar to die 510 having active area 511, crack stop component 512, and trench region 522, and RDL 520 having extended RDL portion 521 having conductive layer 530, via 531, dielectric layers 502-503, and conductive contact 532, kerf region 540, and solder ball 534 in FIG. 5D.

[0081] In an embodiment, the extended RDL portion 621 may include both the conductive contacts and the pillars 632-633 and / or one of the conductive contacts and the pillars 632-633. In an embodiment, the conductive pillars 633 may be implemented in the same process, such as a lithography process, performed on the conductive layer 630 and the conductive contacts 632. In some embodiments, the conductive pillars 633 may have any thickness based on the desired packaging design. For example, the conductive pillars 633 may have a thickness that may substantially define a gap between a bottom surface of the conductive layer 630 and a top surface of a substrate (e.g., a PCB, an interposer, etc.) to which it is subsequently bonded.

[0082] 6B, cross-sectional views of electronic packages 600-601 and 604 after the wafer has been diced are shown, according to some embodiments. That is, after RDL 620 has been populated, the wafer may be diced in a dicing process that removes the kerf region completely or partially, thereby populating diced electronic packages 600-601 and 604 having respective extended RDL portions 621. Thus, electronic packages 600-601 and 604 of FIG. 6B are similar to electronic packages 500-501 of FIG. 5E-5F, except that extended RDL portions 621 include conductive contacts and / or pillars 632-633.

[0083] 7A-7D, a series of cross-sectional views are shown illustrating a process for patterning a wafer 790 to form an electronic package 700 according to some embodiments. The electronic package 700 of FIG. 7D is similar to that shown and described with respect to the electronic packages 100-101 of FIG. 1A-1B, except that the extended RDL portion 721 uses a conductive material (e.g., copper) to fill the trench region 722 of the die 710. That is, whereas in FIG. 1A-1B the extended RDL portion 121 used a dielectric layer 102 to fill the trench region 122 of the die 110, as shown in FIG. 7D below, the extended RDL portion 721 may use a conductive layer 730 to fill the trench region 722 of the die 710.

[0084] 7A-7D, wafer 790 and electronic package 700 include die 710 having active area 711 and trench region 722 similar to those shown and described above with respect to FIGS. 1A-1B, 2A-2E, 3A-3D, 4A-4D, 5A-5F, and 6A-6B, and RDL 720 having conductive layer 730, dielectric layers 702-703, extended RDL portion 721 having conductive contacts and pillars 732-733, kerf region 740, and solder balls 734.

[0085] 7A, a cross-sectional view of a wafer 790 is shown after a trench opening 705 has been formed, according to an embodiment. In an embodiment, the trench opening 705 may be patterned in a kerf region 740 to form a trench region 722 in a sidewall surface of a die 710.

[0086] 7B, a cross-sectional view of a wafer 790 is shown after a conductive layer 730 and a dielectric layer 702 have been disposed over and around an active area 711 and a trench area 722 according to an embodiment. In an embodiment, the conductive layer 730 is disposed directly on the bottom surface of the die 710 and the trench area 722. In an embodiment, the conductive layer 730 may be implemented by a lithography process or any other suitable plating process. In an embodiment, the conductive layer 730 is disposed over the active surface and kerf area 740 of the wafer 790 with a predetermined thickness. Although, in an exemplary embodiment, the initial trench opening may be partially filled by the predetermined thickness of the conductive layer 730.

[0087] Thereafter, in embodiments, an opening (not shown) may be patterned in the conductive layer 730 with any suitable patterning process. In some embodiments, the dielectric layer 702 is disposed in the patterned opening in the conductive layer 730 and disposed above the conductive layer 730 in the kerf region 740 to completely fill the initial trench opening. In embodiments, the dielectric layer 702 may have a surface that is substantially coplanar with a surface of the conductive layer 730.

[0088] Referring to FIG. 7C, a cross-sectional view of a wafer 790 is shown after an RDL 720 having an extended RDL portion 721 according to an embodiment has been formed. The structure of FIG. 7C may be similar to the structure shown in FIG. 6A, except that a conductive layer 730 is disposed directly on (and electrically coupled to) the active area 711 of the die 710 without the need for any vias (based on the desired packaging design), and the initial trench opening in the kerf region 740 is filled with the conductive layer 730, the dielectric layer 702, and the dielectric layer 703, respectively. In some embodiments, the extended RDL portion 721 may include portions of the conductive layer 730 and the conductive contacts and pillars 732-733 without the need for any dielectric material.

[0089] 7D, a cross-sectional view of an electronic package 700 electrically coupled to a package substrate 760 after the wafer has been diced according to an embodiment is shown. For example, after the RDL 720 is implemented, the wafer may be diced in a dicing process that removes the kerf region completely or partially, thereby implementing the diced electronic package 700 having the extended RDL portion 721. In an embodiment, the diced electronic package 700 may be electrically coupled to the package substrate 760 with solder bumps 736. In some embodiments, the package substrate 760 may be any type of packaging substrate. For example, the package substrate 760 may be a PCB, an interposer, or the like. Furthermore, as described above, the conductive pillars 733 may be disposed and positioned on and around the outer sidewall surface of the die 710 to form a conductive ring or one or more conductive pillars spaced apart from each other by a small gap (e.g., as shown in the embodiment in FIGS. 2D-2E).

[0090] 8A-8D, a series of cross-sectional views are shown illustrating a process for patterning a wafer 890 to form one or more electronic packages 800-801 and 804 in accordance with some embodiments. The structures of electronic packages 800-801 and 804 in FIG. 8D are similar to those shown and described with respect to electronic package 700 in FIG. 7D, except that extended RDL portion 821 has conductive traces 832 and portions of dielectric layer 802 that generally surround the sidewall surfaces of die 810. That is, as shown in FIG. 8D, extended RDL portion 821 is comprised of the portions of dielectric layer 802 that immediately surround the entire thickness of the sidewall surfaces of die 810 and the portions of conductive traces 832 that immediately surround the entire thickness of the outer sidewall surfaces of each portion of dielectric layer 802.

[0091] 8A-8D, wafer 890 and electronic packages 800-801 and 804 include die 810 having active area 811 similar to that shown and described above in connection with FIGS. 7A-7D, RDL 820 having conductive layer 830, dielectric layers 802-803, and extended RDL portion 821 having conductive traces 832, kerf area 840, and solder balls 834.

[0092] 8A, a cross-sectional view of a wafer 890 is shown after a trench opening 805 has been formed, according to an embodiment. In an embodiment, the trench opening 805 may be patterned in a kerf region 840 to expose an entire sidewall surface of a die 810.

[0093] 8B, a cross-sectional view of wafer 890 is shown after dielectric layer 802 and conductive layer 830 according to an embodiment have been disposed over and around active area 811 and trench area 822. In an embodiment, dielectric layer 802 is disposed directly on the bottom and sidewall surfaces of die 810. In an embodiment, dielectric layer 802 is disposed over active surface and kerf area 840 of wafer 890 at a predetermined thickness. Although, in an exemplary embodiment, the initial trench opening may be partially filled with the predetermined thickness of dielectric layer 802.

[0094] Thereafter, in embodiments, an opening (not shown) may be patterned in dielectric layer 802 with any suitable patterning process. In some embodiments, conductive layer 830 is disposed in the opening patterned in dielectric layer 802 and disposed above dielectric layer 802 on the active side and kerf region 840 of die 810 to completely fill the initial trench opening. In embodiments, conductive layer 830 may have an exposed and optionally polished bottom surface.

[0095] 8C, a cross-sectional view of a wafer 890 is shown after an RDL 820 having an extended RDL portion 821 has been formed according to an embodiment. The structure of FIG. 8C may be similar to the structure shown in FIG. 7C, except that the initial trench opening in kerf region 840 has been filled with dielectric layer 802 and conductive layer 830, respectively, and both dielectric layer 802 and conductive layer 830 generally surround the entire sidewall surface of die 810.

[0096] 8D , a cross-sectional view of one or more electronic packages 800-801 and 804 after the wafer has been diced is shown, according to an embodiment. For example, after RDL 820 has been implemented, the wafer may be diced in a dicing process that completely or partially removes the kerf region, thereby implementing diced electronic packages 800-801 and 804 having extended RDL portions 821. Thus, as shown in the exemplary embodiment, die 810 may have a top surface that is substantially coplanar with a top surface of the conductive traces 832 and portions of dielectric layer 802 of extended RDL portions 821.

[0097] FIG. 9 illustrates a computing device 900 according to one example of an embodiment described herein. FIG. 9 illustrates an example of the computing device 900. The computing device 900 houses a motherboard 902. The motherboard 902 may include multiple components, including but not limited to a processor 904, a device package 910 (or electronic package), and at least one communication chip 906. The processor 904 is physically and electrically coupled to the motherboard 902. For some embodiments, the at least one communication chip 906 is also physically and electrically coupled to the motherboard 902. For other embodiments, the at least one communication chip 906 is part of the processor 904.

[0098] Depending on its application, computing device 900 may include other components that may or may not be physically and electrically coupled to motherboard 902. These other components include, but are not limited to, volatile memory (e.g., DRAM), non-volatile memory (e.g., ROM), flash memory, graphics processors, digital signal processors, crypto-processors, chipsets, antennas, displays, touch screen displays, touch screen controllers, batteries, audio codecs, video codecs, power amplifiers, Global Positioning System (GPS) devices, compasses, accelerometers, gyroscopes, speakers, cameras, and mass storage devices (e.g., hard disk drives, compact discs (CDs), digital versatile discs (DVDs)).

[0099] At least one communications chip 906 enables wireless communication for the transmission of data between computing devices 900. The term "wireless" and its derivatives may be used to describe circuits, devices, systems, methods, techniques, communications channels, etc. that may communicate data through the use of modulated electromagnetic radiation through a non-solid medium. The term is not intended to imply that the associated devices are completely wire-free, although in some embodiments this may not be the case. At least one communications chip 906 may implement any of a number of wireless standards or protocols, including but not limited to Wi-Fi (IEEE 802.11 family), WiMAX (IEEE 802.112 family), IEEE 802.20, Long Term Evolution (LTE), Ev-DO, HSPA+, HSDPA+, HSUPA+, EDGE, GSM, GPRS, CDMA, TDMA, DECT, Bluetooth, derivatives thereof, and any other wireless protocols designated as 3G, 4G, 5G and beyond. Computing device 900 may include multiple communications chips 906. For example, the first communications chip 906 may be dedicated to short-range wireless communications, such as Wi-Fi® and Bluetooth®, and the second communications chip 906 may be dedicated to long-range wireless communications, such as GPS, EDGE, GPRS, CDMA, WiMAX®, LTE, Ev-DO, and others.

[0100] The processor 904 of the computing device 900 includes an integrated circuit die packaged within the processor 904. The term "processor" may refer to any device or part of a device that processes electronic data from registers and / or memory and converts the electronic data into other electronic data that may be stored in registers and / or memory. The device package 910 may be an electronic package, such as a wafer level package. In an embodiment, the device package 910 may be substantially similar to any of the electronic packages described and shown in Figures 1A-1B, 2A-2E, 3A-3D, 4A-4D, 5A-5F. Thus, the device package 910 may include any of the extended RDL portion structures described and shown herein or any other components from the figures described herein.

[0101] It is noted that any device package 910 may be a single component / device, a subset of components, and / or an entire system, as the materials, features, and components may be limited to the device package 910 and / or any other components of the computing device 900 that may require any of the extended RDL portion structures described herein (e.g., the motherboard 902, the processor 904, the communications chip 906, and / or other components of the computing device 900 that may require the embodiments described herein).

[0102] At least one communications chip 906 also includes an integrated circuit die packaged within the communications chip 906. For some embodiments, the integrated circuit die of the communications chip 906 may be packaged with one or more devices on an electronic package having an extended RDL portion, as described herein.

[0103] In the foregoing specification, the embodiments have been described with reference to specific exemplary embodiments thereof. However, it should be noted that all of these and similar terms are to be associated with the appropriate physical quantities and are merely convenient labels applied to these quantities. It is apparent that various modifications may be made thereto without departing from the broader spirit and scope. The specification and drawings should therefore be interpreted in an illustrative rather than a restrictive sense.

[0104] The following examples relate to further embodiments. The various features of the different embodiments can be combined in various ways, with some features included and other features excluded, to suit a variety of different applications.

[0105] The following examples relate to further embodiments.

[0106] Example 1: An electronic package comprising: an RDL over a package substrate, the RDL having a conductive layer in a first dielectric layer and a second dielectric layer over the conductive layer and the first dielectric layer; an extended portion of the RDL having a first thickness, the first thickness extending vertically from a bottom surface of the first dielectric layer to a top surface of the second dielectric layer; and a die over the RDL, the die having a plurality of sidewall surfaces, a top surface, and a bottom surface opposite the top surface, the die having an active area over the bottom surface of the die, the first thickness being greater than a second thickness of the RDL that extends vertically from the bottom surface of the first dielectric layer to the bottom surface of the die, the extended portion being above and around a first region of the bottom surface and a second region of the sidewall surfaces, the active area having a top surface disposed below the top surface of the second dielectric layer.

[0107] Example 2: The electronic package of Example 1, further comprising a plurality of vias in the RDL, the plurality of vias electrically coupling the conductive layer to the active area.

[0108] Example 3: The electronic package of Examples 1-2, wherein the extended portion has a first dielectric layer, a conductive layer, and a portion of the second dielectric layer.

[0109] Example 4: The electronic package of Examples 1-3, wherein the second region is a trench-shaped region on a plurality of sidewall surfaces of the die, the trench-shaped region directly couples with the first region on the bottom surface of the die, and the trench-shaped region on each of the plurality of sidewall surfaces is directly surrounded by an extended portion of the RDL.

[0110] Example 5: The electronic package of Examples 1-4, wherein the trench-shaped region is immediately surrounded by a portion of the second dielectric layer in the extended portion, the portion of the conductive layer having an exposed sidewall surface, and the portion of the second dielectric layer having an exposed sidewall surface that is substantially coplanar with a plurality of sidewall surfaces of the die and the exposed sidewall surface of the portion of the conductive layer.

[0111] Example 6: The electronic package of Examples 1-5, further comprising a crack stop structure on a bottom surface of the die, the active area being surrounded by the crack stop structure, and a plurality of solder balls electrically coupling the RDL to a package substrate.

[0112] Example 7: The electronic package of Examples 1 to 6, wherein the first dielectric layer has one or more first dielectric materials and the second dielectric layer has one or more second dielectric materials, and the one or more first dielectric materials are the same as or different from the one or more second dielectric materials.

[0113] Example 8: The electronic package of Examples 1 to 7, wherein the trench-shaped region has a thickness greater than a thickness of the active region, and the top surface of the second dielectric layer of the extended portion is directly coupled to the top surface of the trench-shaped region.

[0114] Example 9: The electronic package of Examples 1-8, further comprising one or more conductive contacts on the extended portion of the RDL, the one or more conductive contacts being directly on the portion of the conductive layer, each conductive contact having an exposed sidewall surface that is substantially coplanar with an exposed sidewall surface of the portion of the conductive layer.

[0115] Example 10: forming a plurality of trench openings in a first side of a substrate; disposing a first dielectric layer over the trench openings and the first side of the substrate; disposing a conductive layer over the first dielectric layer; and disposing a second dielectric layer over the conductive layer and the first dielectric layer to form an RDL, the RDL having the conductive layer and the first dielectric layer; and removing regions of the substrate disposed over the trench openings to dicing the substrate into a plurality of electronic packages, each of the regions extending perpendicularly from a surface of the RDL to a second side of the substrate opposite the first side, each of the diced electronic packages having a first thickness. 1. A method of forming an electronic package comprising: an extended portion of the RDL, the extended portion of the RDL having a first thickness extending vertically from a bottom surface of the second dielectric layer to a top surface of the first dielectric layer; and a die over the RDL and the extended portion, the die having a plurality of sidewall surfaces, a top surface, and a bottom surface opposite the top surface, the die having an active area on the bottom surface of the die, the first thickness being greater than a second thickness of the RDL that extends vertically from the bottom surface of the second dielectric layer to the bottom surface of the die, the extended portion being above and around the first region of the bottom surface and the second region of the sidewall surfaces, and the active area having a top surface disposed below the top surface of the first dielectric layer.

[0116] Example 11: The method of Example 10, further comprising disposing a plurality of vias in the first dielectric layer of the RDL, the plurality of vias electrically coupling the conductive layer to the active area.

[0117] Example 12: The method of Examples 10-11, wherein the extended portion comprises a first dielectric layer, a conductive layer, and a portion of the second dielectric layer.

[0118] Example 13: The method of Examples 10-12, wherein the second region is a trench-shaped region on a sidewall surface of the die, the trench-shaped region directly interfaces with the first region on the bottom surface of the die, and the trench-shaped region on each of the sidewall surfaces is directly surrounded by an extended portion of the RDL.

[0119] Example 14: The electronic package of Examples 10 to 13, wherein the trench-shaped region is immediately surrounded by a portion of the first dielectric layer in the extended portion, the portion of the conductive layer having an exposed sidewall surface, and the portion of the first dielectric layer having an exposed sidewall surface that is substantially coplanar with the sidewall surface of the die and the exposed sidewall surface of the portion of the conductive layer.

[0120] Example 15: The electronic package of Examples 10 to 14, further comprising the steps of: disposing a crack stop structure on a bottom surface of the die, the active area being surrounded by the crack stop structure; and electrically coupling the RDL to a package substrate by a plurality of solder balls.

[0121] Example 16: The method of Examples 10-15, wherein the first dielectric layer has one or more first dielectric materials and the second dielectric layer has one or more second dielectric materials, and the one or more first dielectric materials are the same as or different from the one or more second dielectric materials.

[0122] Example 17: The method of Examples 10 to 16, wherein the trench-shaped region has a thickness greater than a thickness of the active region, and a top surface of the first dielectric layer of the extended portion is directly bonded to a top surface of the trench-shaped region.

[0123] Example 18: The method of Examples 10-17, further comprising one or more conductive contacts on the extended portion of the RDL, the one or more conductive contacts being directly on the portion of the conductive layer, each conductive contact having an exposed sidewall surface that is substantially coplanar with an exposed sidewall surface of the portion of the conductive layer.

[0124] Example 19: A package substrate, a redistribution layer (RDL) electrically coupled to the package substrate, and a die electrically coupled to the package substrate by the RDL, the die having a plurality of sidewall surfaces, a top surface, and a bottom surface opposite the top surface, the die having an active area on the bottom surface of the die, the RDL including a conductive layer in a first dielectric layer, a second dielectric layer above the conductive layer and the first dielectric layer, a plurality of vias in the second dielectric layer electrically coupling the conductive layer to the active area, and an extended portion of the RDL having a first thickness, the first thickness extending from the bottom surface of the first dielectric layer to a top surface of the second dielectric layer. an extended portion of the RDL, the extended portion being above and around an area of ​​the bottom surface and a trench-shaped area of ​​the sidewall surface; the active area having a top surface disposed below a top surface of the second dielectric layer; the extended portion having a first dielectric layer, a conductive layer, and a portion of the second dielectric layer, the portion of the conductive layer having an exposed sidewall surface; and a conductive contact directly overlying the portion of the conductive layer in the extended portion, each conductive contact having an exposed sidewall surface that is substantially coplanar with the exposed sidewall surface of the portion of the conductive layer. 1. An electronic package comprising:

[0125] Example 20: The electronic package of example 19, wherein the trench-shaped region directly couples with the region on the bottom surface of the die and the trench-shaped region on each of the sidewall surfaces is directly surrounded by the extended portion of the RDL.

[0126] Example 21: The electronic package of Examples 19 to 20, wherein the trench-shaped region is immediately surrounded by a portion of the second dielectric layer of the extended portion, the portion of the second dielectric layer having an exposed sidewall surface that is substantially coplanar with the sidewall surface of the die and the exposed sidewall surface of the portion of the conductive layer.

[0127] Example 22: The electronic package of Examples 19 to 21, further comprising: a crack stop structure on the bottom surface of the die, the active area being surrounded by the crack stop structure; a plurality of solder balls electrically coupling the RDL to a first region on the top surface of the package substrate; and a conductive interconnect electrically coupling a portion of the conductive layer to a second region on the top surface of the package substrate, the conductive interconnect having an exposed sidewall surface that is substantially coplanar with the exposed sidewall surface of the portion of the conductive layer, the first region being generally within the footprint of the second region, and the conductive region having a conductive ring and a plurality of conductive pillars.

[0128] Example 23: An electronic package of Examples 19 to 22, wherein the first dielectric layer has one or more first dielectric materials and the second dielectric layer has one or more second dielectric materials, and the one or more first dielectric materials are the same as or different from the one or more second dielectric materials.

[0129] Example 24: The electronic package of Examples 19 to 23, wherein the trench-shaped region has a thickness greater than a thickness of the active region, and the top surface of the second dielectric layer of the extended portion is directly bonded to the top surface of the trench-shaped region.

[0130] Example 25: The electronic package of Examples 19 to 24, further comprising a conductive shield electrically coupled to one or more of the exposed surfaces of the conductive layer portions or the exposed surfaces of the conductive contacts, the conductive shield being above and around the top and sidewall surfaces of the die.

[0131] The above description of illustrated embodiments of the invention, including what is described in the Abstract, is not intended to be exhaustive or to limit the invention to the precise form disclosed. While specific embodiments of, and examples for, the invention are described herein for illustrative purposes, various equivalent modifications are possible within the scope of the invention, as those skilled in the art will recognize.

[0132] These modifications can be made to the invention in light of the above teachings. The terms used in the following claims should not be construed to limit the invention to the specific embodiments disclosed in the specification and the claims. Rather, the scope of the invention should be determined entirely by the following claims and should be construed in accordance with established doctrines of claim interpretation.

[0133] In the foregoing specification, the method and apparatus have been described with reference to specific exemplary embodiments thereof. It will be apparent that various modifications may be made thereto without departing from the broader spirit and scope. The specification and drawings are therefore to be regarded in an illustrative rather than a restrictive sense. [Other possible items] [Item 1] a redistribution layer (RDL) above a package substrate, a conductive layer within the first dielectric layer; a second dielectric layer overlying the conductive layer and the first dielectric layer; an extended portion of the RDL having a first thickness, the first thickness extending vertically from a bottom surface of the first dielectric layer to a top surface of the second dielectric layer; and a die on the RDL, the die having a plurality of sidewall surfaces, a top surface, and a bottom surface opposite the top surface, the die having an active area disposed on the bottom surface of the die, the RDL electrically coupling the active area to the package substrate, the first thickness being greater than a second thickness of the RDL that extends perpendicularly from the bottom surface of the first dielectric layer to the bottom surface of the die, and the extended portion being above and around a first region of the bottom surface of the die and a second region of the plurality of sidewall surfaces of the die. 1. An electronic package comprising: [Item 2] 2. The electronic package of claim 1, further comprising a plurality of vias in the second dielectric layer, the plurality of vias electrically coupling the conductive layer to the active area. [Item 3] 2. The electronic package of claim 1, wherein the active area has an upper surface disposed below the top surface of the first dielectric layer, and the extended portion includes portions of the first dielectric layer, the conductive layer, and the second dielectric layer. [Item 4] 4. The electronic package of claim 3, wherein the second region is a trench-shaped region on the sidewall surfaces of the die, the trench-shaped region directly coupling with the first region on the bottom surface of the die, the first region being a peripheral region on the bottom surface of the die, and the trench-shaped region on each of the sidewall surfaces is directly surrounded by the extended portion of the RDL. [Item 5] 5. The electronic package of claim 4, wherein the trench-shaped region is immediately surrounded by the portion of the second dielectric layer of the extended portion, the portion of the conductive layer having an exposed sidewall surface, and the portion of the second dielectric layer having an exposed sidewall surface that is substantially coplanar with the multiple sidewall surfaces of the die and the exposed sidewall surface of the portion of the conductive layer. [Item 6] a crack stop structure on the bottom surface of the die, the active area being surrounded by the crack stop structure; a plurality of solder balls electrically coupling the RDL to the package substrate; Item 1. The electronic package of item 1, further comprising: [Item 7] 2. The electronic package of claim 1, wherein the first dielectric layer has one or more first dielectric materials and the second dielectric layer has one or more second dielectric materials, the one or more first dielectric materials being the same as or different from the one or more second dielectric materials. [Item 8] 6. The electronic package of claim 5, wherein the trench-shaped region has a thickness greater than a thickness of the active region, and the top surface of the second dielectric layer of the extended portion directly bonds to a top surface of the trench-shaped region. [Item 9] 6. The electronic package of claim 5, further comprising one or more conductive contacts on the extended portion of the RDL, the one or more conductive contacts directly overlying the portion of the conductive layer, each conductive contact having an exposed sidewall surface that is substantially coplanar with the exposed sidewall surface of the portion of the conductive layer. [Item 10] forming a plurality of trench openings in an active surface of a substrate, the substrate having a plurality of die regions and a plurality of kerf regions, each die region having an active area disposed on the active surface; disposing a first dielectric layer over the active surface and in the plurality of trench openings to form trenches, the trenches having a thickness greater than a thickness of the active area; disposing a conductive layer over the first dielectric layer, the conductive layer being disposed over the active area and the trench; disposing a second dielectric layer over the conductive layer and the first dielectric layer, the conductive layer, the first dielectric layer, the second dielectric layer, and the trench being part of a first redistribution layer (RDL) patterned directly on the active surface of the substrate; removing the kerf regions from the substrate and dicing the die regions, the first RDL, and the trench to form one or more electronic packages, each electronic package having a die disposed on a second RDL having an extended portion, the die having a plurality of sidewall surfaces, a top surface, and a bottom surface opposite the top surface, each sidewall surface having a trench-shaped region formed from one of the diced trenches, the extended portion being above and around an area on the bottom surface of the die and the trench-shaped region on the sidewall surfaces of the die; 16. A method of forming an electronic package comprising: [Item 11] Item 12. The method of item 11, wherein the die is formed from one of the diced die areas, the second RDL is a portion of the diced first RDL, the extended portion is a portion of the diced first RDL and the diced trench, the trench shaped area is entirely filled with the first dielectric layer that was part of the diced trench, and the extended portion has a first thickness extending vertically from a bottom surface of the second dielectric layer to a top surface of the first dielectric layer, the first thickness being thicker than a second thickness of the second RDL extending vertically from the bottom surface of the second dielectric layer to the bottom surface of the die. [Item 12] 12. The method of claim 11, wherein the active area has a top surface disposed below the top surface of the first dielectric layer, and the extended portion includes portions of the first dielectric layer, the conductive layer, and the second dielectric layer. [Item 13] Item 13. The method of item 12, wherein the trench-shaped region directly couples with the region on the bottom surface of the die, the region being a peripheral region on the bottom surface of the die, and the trench-shaped region on each sidewall surface is directly surrounded by the extended portion of the second RDL. [Item 14] Item 14. The method of item 13, wherein removing the kerf regions exposes a sidewall surface of the portion of the conductive layer and a sidewall surface of the portion of the first dielectric layer, the exposed sidewall surface of the portion of the first dielectric layer being substantially coplanar with the sidewall surface of the die and the exposed sidewall surface of the portion of the conductive layer. [Item 15] prior to removing the plurality of kerf regions from the substrate; disposing a plurality of vias in the first dielectric layer, the plurality of vias electrically coupling the conductive layer to the active area; disposing crack stop structures on the bottom surface of the die areas, each active area being surrounded by one of the crack stop structures; electrically coupling the first RDL to a package substrate by a plurality of solder balls; Item 11. The method of item 10, further comprising: [Item 16] Item 11. The method of item 10, wherein the first dielectric layer comprises one or more first dielectric materials and the second dielectric layer comprises one or more second dielectric materials, the one or more first dielectric materials being the same as or different from the one or more second dielectric materials. [Item 17] Item 11. The method of item 10, wherein the trench-shaped region has a thickness greater than the thickness of the active region, and the top surface of the first dielectric layer of the extended portion directly bonds to a top surface of the trench-shaped region. [Item 18] prior to removing the plurality of kerf regions from the substrate; Item 15. The method of item 14, further comprising disposing one or more conductive contacts on the extended portion, the one or more conductive contacts directly overlying the portion of the conductive layer, the one or more conductive contacts having exposed sidewall surfaces that are substantially coplanar with the exposed sidewall surfaces of the portion of the conductive layer. [Item 19] A package substrate; a redistribution layer (RDL) electrically coupled to the package substrate; a die electrically coupled to the package substrate by the RDL; the die having a plurality of sidewall surfaces, a top surface, and a bottom surface opposite the top surface, the die having an active area on the bottom surface of the die, and the RDL comprising: a conductive layer within the first dielectric layer; a second dielectric layer overlying the conductive layer and the first dielectric layer; a plurality of vias in the second dielectric layer electrically coupling the conductive layer to the active area; an extended portion of the RDL having a first thickness, the first thickness extending vertically from a bottom surface of the first dielectric layer to a top surface of the second dielectric layer, the first thickness being greater than a second thickness of the RDL extending vertically from the bottom surface of the first dielectric layer to the bottom surface of the die, the extended portion being over and around an area at the bottom surface of the die and a trench-shaped area at the sidewall surfaces, the active area having a top surface disposed below the top surface of the second dielectric layer, the extended portion having one or more conductive contacts and one or more portions of the first dielectric layer, the conductive layer, and the second dielectric layer, the one or more conductive contacts being directly over the portion of the conductive layer, the one or more conductive contacts having exposed sidewall surfaces that are substantially coplanar with exposed sidewall surfaces of the portion of the conductive layer; 1. An electronic package comprising: [Item 20] 20. The electronic package of claim 19, wherein the trench-shaped region directly couples with the region on the bottom surface of the die, the region being a peripheral region on the bottom surface of the die, and the trench-shaped region on each of the sidewall surfaces is directly surrounded by the extended portion of the RDL. [Item 21] 20. The electronic package of claim 19, wherein the trench-shaped region is immediately surrounded by the portion of the second dielectric layer of the extended portion, the portion of the second dielectric layer having an exposed sidewall surface that is substantially coplanar with the sidewall surface of the die, the exposed sidewall surface of the one or more conductive contacts, and the exposed sidewall surface of the portion of the conductive layer. [Item 22] a crack stop structure on the bottom surface of the die, the active area being surrounded by the crack stop structure; a plurality of solder balls electrically coupling the RDL to a first region disposed on an upper surface of the package substrate; a conductive interconnect electrically coupling the extended portion to a second region disposed on the top surface of the package substrate, the conductive interconnect having one or more exposed sidewall surfaces that are substantially coplanar with the exposed sidewall surfaces of the portion of the conductive layer, the first region being generally within a footprint of the second region, the conductive interconnect having a conductive ring and a plurality of conductive pillars; 20. The electronic package of claim 19, further comprising: [Item 23] 20. The electronic package of claim 19, wherein the first dielectric layer has one or more first dielectric materials and the second dielectric layer has one or more second dielectric materials, the one or more first dielectric materials being the same as or different from the one or more second dielectric materials. [Item 24] 20. The electronic package of claim 19, wherein the trench-shaped region has a thickness greater than a thickness of the active region, and the top surface of the second dielectric layer of the extended portion directly bonds to a top surface of the trench-shaped region. [Item 25] 23. The electronic package of claim 22, further comprising a conductive shield electrically coupled to two or more of the exposed sidewall surfaces of the portion of the conductive layer or the exposed sidewall surfaces of the one or more conductive contacts, the conductive shield being above and around the top and sidewall surfaces of the die.

Claims

1. a redistribution layer (RDL) above a package substrate, said RDL comprising: a conductive layer within the first dielectric layer; a second dielectric layer overlying the conductive layer and the first dielectric layer; an extended portion of the RDL having a first thickness, the first thickness extending vertically from a bottom surface of the first dielectric layer to a top surface of the second dielectric layer; and a die on the RDL, the die having a plurality of sidewall surfaces, a top surface, and a bottom surface opposite the top surface, the die having an active area disposed on the bottom surface of the die, the RDL electrically coupling the active area to the package substrate, the first thickness being greater than a second thickness of the RDL that extends vertically from the bottom surface of the first dielectric layer to the bottom surface of the die; 1. An electronic package comprising:

2. The electronic package of claim 1 , further comprising a plurality of vias in said second dielectric layer, said plurality of vias electrically coupling said conductive layer to said active area.

3. 3. The electronic package of claim 1, wherein the active area has a top surface disposed below the top surface of the second dielectric layer, and the extended portion includes the first dielectric layer, the conductive layer, and portions of the second dielectric layer.

4. the extended portion is above and around a first region of the bottom surface of the die and a second region of the plurality of sidewall surfaces of the die; 3. The electronic package of claim 1, wherein the second region is a trench-shaped region on the sidewall surfaces of the die, the trench-shaped region directly coupling with the first region on the bottom surface of the die, the first region being a peripheral region on the bottom surface of the die, and the trench-shaped region on each of the sidewall surfaces is directly surrounded by the extended portion of the RDL.

5. 5. The electronic package of claim 4, wherein the trench-shaped region is immediately surrounded by the portion of the second dielectric layer of the expanded portion, the portion of the conductive layer having an exposed sidewall surface, and the portion of the second dielectric layer having an exposed sidewall surface that is substantially coplanar with the multiple sidewall surfaces of the die and the exposed sidewall surface of the portion of the conductive layer.

6. a crack stop structure on the bottom surface of the die, the active area being surrounded by the crack stop structure; a plurality of solder balls electrically coupling the RDL to the package substrate; The electronic package of claim 1 or 2, further comprising:

7. 3. The electronic package of claim 1, wherein the first dielectric layer comprises one or more first dielectric materials and the second dielectric layer comprises one or more second dielectric materials, the one or more first dielectric materials being the same as or different from the one or more second dielectric materials.

8. 6. The electronic package of claim 5, wherein the trench-shaped region has a thickness greater than a thickness of the active area, and the top surface of the second dielectric layer of the extended portion directly bonds to a top surface of the trench-shaped region.

9. 3. The electronic package of claim 1, further comprising one or more conductive contacts on the extended portion of the RDL, the one or more conductive contacts directly overlying the portion of the conductive layer, each conductive contact having an exposed sidewall surface that is substantially coplanar with an exposed sidewall surface of the portion of the conductive layer.

10. forming a plurality of trench openings in an active surface of a substrate, the substrate having a plurality of die regions and a plurality of kerf regions, each die region having an active area disposed on the active surface; disposing a first dielectric layer over the active surface and in the plurality of trench openings to form trenches, the trenches having a thickness greater than a thickness of the active area; disposing a conductive layer over the first dielectric layer, the conductive layer being disposed over the active area and the trench; disposing a second dielectric layer over the conductive layer and the first dielectric layer, the conductive layer, the first dielectric layer, the second dielectric layer, and the trench being part of a first redistribution layer (RDL) patterned directly on the active surface of the substrate; removing the kerf regions from the substrate and dicing the die regions, the first RDL, and the trench to form one or more electronic packages, each electronic package having a die disposed on a second RDL having an extended portion, the die having a plurality of sidewall surfaces, a top surface, and a bottom surface opposite the top surface, each sidewall surface having a trench-shaped region formed from one of the diced trenches, the extended portion being above and around an area on the bottom surface of the die and the trench-shaped region on the sidewall surfaces of the die; 16. A method of forming an electronic package comprising:

11. 11. The method of claim 10, wherein the die is formed from one of the diced die areas, the second RDL is part of the diced first RDL, the extended portion is part of the diced first RDL and the diced trench, the trench shaped area is entirely filled with the first dielectric layer that was part of the diced trench, and the extended portion has a first thickness extending vertically from a bottom surface of the second dielectric layer to a top surface of the first dielectric layer, the first thickness being thicker than a second thickness of the second RDL extending vertically from the bottom surface of the second dielectric layer to the bottom surface of the die.

12. 12. The method of claim 11 , wherein the active area has a top surface disposed below the top surface of the second dielectric layer, and the extended portion comprises portions of the first dielectric layer, the conductive layer, and the second dielectric layer.

13. 12. The method of claim 10 or 11, wherein the trench-shaped region directly couples with the region on the bottom surface of the die, the region on the bottom surface of the die being a peripheral region on the bottom surface of the die, and the trench-shaped region on each sidewall surface is directly surrounded by the extended portion of the second RDL.

14. 12. The method of claim 10 or 11, wherein removing the plurality of kerf regions exposes a sidewall surface of the portion of the conductive layer and a sidewall surface of the portion of the first dielectric layer, the exposed sidewall surface of the portion of the first dielectric layer being substantially coplanar with the sidewall surface of the die and the exposed sidewall surface of the portion of the conductive layer.

15. prior to removing the plurality of kerf regions from the substrate; disposing a plurality of vias in the first dielectric layer, the plurality of vias electrically coupling the conductive layer to the active area; disposing crack stop structures on the bottom surface of the plurality of die areas, each active area being surrounded by one of the crack stop structures; electrically coupling the first RDL to a package substrate by a plurality of solder balls; The method of claim 10 or 11, further comprising:

16. 12. The method of claim 10 or 11, wherein the first dielectric layer comprises one or more first dielectric materials and the second dielectric layer comprises one or more second dielectric materials, the one or more first dielectric materials being the same as or different from the one or more second dielectric materials.

17. 12. The method of claim 11, wherein the trench-shaped region has a thickness greater than the thickness of the active region, and the top surface of the first dielectric layer in the extended portion directly bonds to a top surface of the trench-shaped region.

18. prior to removing the plurality of kerf regions from the substrate; 12. The method of claim 10 or 11, further comprising disposing one or more conductive contacts on the extended portion, the one or more conductive contacts directly overlying the portion of the conductive layer, the one or more conductive contacts having exposed sidewall surfaces that are substantially coplanar with exposed sidewall surfaces of the portion of the conductive layer.

19. A package substrate; a redistribution layer (RDL) electrically coupled to the package substrate; a die electrically coupled to the package substrate by the RDL; the die having a plurality of sidewall surfaces, a top surface, and a bottom surface opposite the top surface, the die having an active area on the bottom surface of the die, and the RDL comprising: a conductive layer within the first dielectric layer; a second dielectric layer overlying the conductive layer and the first dielectric layer; a plurality of vias in the second dielectric layer electrically coupling the conductive layer to the active area; an extended portion of the RDL having a first thickness, the first thickness extending vertically from a bottom surface of the first dielectric layer to a top surface of the second dielectric layer, the first thickness being greater than a second thickness of the RDL extending vertically from the bottom surface of the first dielectric layer to the bottom surface of the die, the extended portion being over and around an area at the bottom surface of the die and a trench-shaped area at the sidewall surfaces, the active area having a top surface disposed below the top surface of the second dielectric layer, the extended portion having one or more conductive contacts and one or more portions of the first dielectric layer, the conductive layer, and the second dielectric layer, the one or more conductive contacts being directly over the portion of the conductive layer, the one or more conductive contacts having exposed sidewall surfaces that are substantially coplanar with exposed sidewall surfaces of the portion of the conductive layer; 1. An electronic package comprising:

20. 20. The electronic package of claim 19, wherein the trench-shaped region directly couples with the region on the bottom surface of the die, the region on the bottom surface of the die being a peripheral region on the bottom surface of the die, and the trench-shaped region on each of the plurality of sidewall surfaces is directly surrounded by the extended portion of the RDL.

21. 21. The electronic package of claim 19 or 20, wherein the trench-shaped region is immediately surrounded by the portion of the second dielectric layer of the expanded portion, the portion of the second dielectric layer having an exposed sidewall surface that is substantially coplanar with the sidewall surface of the die, the exposed sidewall surfaces of the one or more conductive contacts, and the exposed sidewall surface of the portion of the conductive layer.

22. a crack stop structure on the bottom surface of the die, the active area being surrounded by the crack stop structure; a plurality of solder balls electrically coupling the RDL to a first region disposed on a top surface of the package substrate; a conductive interconnect electrically coupling the extended portion to a second region disposed on the top surface of the package substrate, the conductive interconnect having one or more exposed sidewall surfaces that are substantially coplanar with the exposed sidewall surfaces of the portion of the conductive layer, the first region being generally within a footprint of the second region, the conductive interconnect having a conductive ring and a plurality of conductive pillars; 21. The electronic package of claim 19 or 20, further comprising:

23. 21. The electronic package of claim 19 or 20, wherein the first dielectric layer comprises one or more first dielectric materials and the second dielectric layer comprises one or more second dielectric materials, the one or more first dielectric materials being the same as or different from the one or more second dielectric materials.

24. 21. The electronic package of claim 19 or 20, wherein the trench-shaped region has a thickness greater than a thickness of the active area, and the top surface of the second dielectric layer of the extended portion is directly coupled to a top surface of the trench-shaped region.

25. 23. The electronic package of claim 22, further comprising a conductive shield electrically coupled to the two or more of the exposed sidewall surfaces of the portions of the conductive layer or the exposed sidewall surfaces of the one or more conductive contacts, the conductive shield over and around the top and sidewall surfaces of the die.