MEW tissue scaffold

Abstract

Melt-electrowritten soft tissue scaffolds and methods for making same are provided. [Solution] The melt-electrowritten soft tissue scaffold of the present disclosure has a body having a first region including a first set of fibers and a second set of fibers, the first region being anisotropic, the first set of fibers being aligned substantially parallel to one another, each fiber of the first set of fibers having a serpentine structure with peaks and troughs, the first set of fibers having a first Young's modulus, the second set of fibers being aligned substantially parallel to one another, the second set of fibers being aligned transverse to the first set of fibers, each fiber of the second set of fibers having a serpentine structure with peaks and troughs, the second set of fibers having a second Young's modulus, and the first Young's modulus is not equal to the second Young's modulus.

Description

[Technical field]

[0001] The present disclosure relates generally to soft tissue scaffolds for use in tissue engineering, such as scaffolds used for heart valve regeneration. [Background technology]

[0002] Valvular heart disease (VHD) represents a significant health burden, responsible for one-third of cardiovascular disease cases, which cause over 5.8 million deaths worldwide each year. In developed countries, the prevalence of VHD is expected to rise due to the increasing aging population. For example, by 2020, approximately 20% of the European Union's population will be aged 65 years or older. Furthermore, valvular heart disease significantly affects children and young adults, with statistically 8 out of 1000 births affected by congenital valvular disease, which is expected to triple by 2050 in developing countries. The main treatment for diseased heart valves involves the surgical implantation of mechanical or bioprosthetic replacement valves. Although the adoption of replacement valves plays a pertinent role in enhancing the quality of life of elderly patients, their application is often accompanied by multiple limitations, and long-term survival rates are generally in the order of 60-70%.

[0003] Mechanical valves offer sufficient durability within the native hemodynamic environment, but their design does not resemble the native valve geometry and therefore requires anticoagulation to mitigate the risk of potential thromboembolism. Bioprosthetic replacement valves, on the other hand, are decellularized valves of porcine or ovine origin that mimic the physiological function of human heart valves to some extent. Although biological valves are significantly less thrombogenic, they do not function well under altered blood pressure due to hypertension. Biological valves are also prone to degradation and have a short lifespan, resulting in an average life expectancy of only 10-15 years. The choice between the two different replacement valves depends on the patient's medical condition and age group, with one of these options being more suitable for a particular group of patients. For patients suffering from congenital heart valve defects, small anatomical dimensions and rapid biological growth, combined with technology, further limit the range of replacement valves available. Specifically, the performance of biological and mechanical valves decreases at very small dimensions. Moreover, their inability to expand and remodel with the child's body growth necessitates multiple surgeries as the patient ages. Thus, in the past two decades, there has been increasing attention on heart valve tissue engineering (HVTE) for congenital valvular disease. HVTE aims to overcome the shortcomings of current treatments by providing biodegradable, yet mechanically stable three-dimensional (3D) constructs (scaffolds). HVTE allows tissue to grow, remodel, and repair before being resorbed by the body, subsequently giving a functionally fully regenerated heart valve in the indwelling state. Despite the advances in HVTE, current constructs still do not allow for the indwelling of a regenerated heart valve.

[0004] It will be understood that where a prior art publication is referenced herein, such reference is not an admission that the publication forms part of the general knowledge in the art in Australia or any other country. Summary of the Invention

[0005] In one aspect, the present invention provides a melt electrowritten anisotropic soft tissue scaffold comprising a first set of fibers arranged generally parallel to one another, each fiber of the first set of fibers having a serpentine structure formed with peaks and troughs, adjacent peaks for each fiber of the first set of fibers being separated by a first distance, and a second set of fibers arranged generally parallel to one another, the second set of fibers being arranged in a transverse direction to the first set of fibers, one or more fibers of the second set of fibers connecting adjacent fibers in the first set of fibers, each fiber of the second set of fibers having a serpentine structure formed with peaks and troughs, and a path length of the fibers of the first set of fibers over a first distance is not equal to a path length of the fibers of the second set of fibers over the same distance as the first distance.

[0006] The first set of fibers and the second set of fibers can be provided in a first region of the scaffold. In one aspect, the present invention provides a melt-electrowritten soft tissue scaffold comprising a body having a first region including a first set of fibers and a second set of fibers, the first region being anisotropic, the first set of fibers being aligned substantially parallel to one another, each fiber of the first set of fibers having a serpentine arrangement forming peaks and troughs, the first set of fibers having a first Young's modulus, the second set of fibers being aligned substantially parallel to one another, the second set of fibers being aligned transverse to the first set of fibers, each fiber of the second set of fibers having a serpentine structure forming peaks and troughs, the second set of fibers having a second Young's modulus, and the first Young's modulus is not equal to the second Young's modulus.

[0007] The second Young's modulus may also be at least twice as large as the Young's modulus of the first set of fibers. The path length of the fibers of the first set of fibers across the predefined distance may not be equal to the path length of the fibers of the second set of fibers across the predefined distance. By providing two sets of fibers with different path lengths, anisotropic scaffolds can be created that can mimic the mechanical properties of native tissue. For example, the scaffold can provide a structural analogue to collagen structure. Such analogues may be useful in improving the ability to regenerate tissues, such as heart valve tissue.

[0008] The path length of the fibers of the first fiber set across the first distance may be longer than the path length of the fibers of the second fiber set across the same linear distance as the first distance. In some embodiments, increasing the path length of the fibers of the first fiber set relative to the path length of the fibers of the second fiber set can increase the anisotropy ratio of the first fiber set to the second fiber set. This means that the first fiber set can be stretched more than the second fiber set when the first and second fiber sets are stretched to lengthen. This can be useful for providing a scaffold having first and second fiber sets with individual properties but connected to each other.

[0009] Adjacent fibers in the first set of fibers may be separated by a second distance. The second distance does not have to be equal to the first distance. Adjacent fibers in the first set of fibers may be connected in regions near their respective peaks to one or more fibers of the second set of fibers. In one aspect, the present invention provides a melt-electrowritten soft tissue scaffold comprising a first set of fibers arranged generally parallel to one another, each fiber of the first set of fibers having a serpentine structure formed with peaks and troughs, adjacent peaks for each fiber of the first set of fibers being separated by a first distance; and a second set of fibers arranged generally parallel to one another, the second set of fibers being arranged in a transverse direction to the first set of fibers, one or more fibers of the second set of fibers connecting adjacent fibers in the first set of fibers, each fiber of the second set of fibers having a serpentine structure formed with peaks and troughs, each fiber of the first set of fibers being separated by a second distance, the second distance not equal to the first distance.

[0010] The first and second sets of fibers can be provided in a first region of the scaffold. As used herein, the terms "transverse" and "transverse" should be broadly interpreted to mean that the angle formed between a first set of fibers and a second set of fibers ranges from about 1° to about 179°. The first and / or second fiber set can include regions having elongated straight fiber structures. Straight fiber structures can also be in addition to tortuous structures. Stated differently, the first and / or second fiber set can include a structure in which one or more fibers are not tortuous.

[0011] The second fiber set may be about 2 to 10 times stiffer than the first fiber set. For example, the second fiber set may be about 8 times stiffer than the first fiber set. Increasing the stiffness of the second fiber set compared to the first fiber set may be accomplished by decreasing the path length of the fibers in the second fiber set compared to the first fiber set. Additionally, the first fiber set of the disclosed scaffold can have a Young's modulus of about 0.1 MPa to 10 MPa. In one embodiment, the first fiber set can have a Young's modulus of about 1 MPa.

[0012] The second fiber set can have a Young's modulus of about 0.1 MPa to 10 MPa. In one embodiment, the second fiber set can have a Young's modulus of about 5 MPa. Increasing the first distance relative to the second distance can increase the anisotropy ratio between the first fiber set and the second fiber set. The anisotropy ratio is the ratio of the difference in mechanical properties between the first fiber set and the second fiber set. The degree of anisotropy can be varied by adjusting the fiber design, and the resulting construct can have a Young's modulus of 0.1 MPa to 10 MPa in each loading direction. The first distance can be about 1 to 10 times larger than the second distance, for example, 2 to 4 times larger. The first distance can be in the range of about 0.5 mm to about 2.5 mm, for example, about 1.0 mm to about 2.0 mm. The second distance can be in the range of about 0.1 mm to about 2.0 mm, for example, about 0.25 mm to about 0.50 mm. This spacing means that the spacing between adjacent fibers in the first set of fibers is about 0.1 mm to about 2.0 mm, for example, about 0.1 mm to about 0.5 mm. It should be understood that due to local variations, this spacing may be as large or small as about 0.1 mm to about 2.0 mm. This may be particularly true after the scaffold has been seeded with cells and / or further implanted in situ. The first and second distances may be selected such that the spacing, i.e., pore size, between adjacent fibers in the first set of fibers and / or the second set of fibers allows for cell proliferation. That is, a pore size of about 2.0 mm is often the upper limit for pore size, since pores larger than 2.0 mm tend to hinder cell proliferation through the scaffold and promote laminar growth rather than three-dimensional tissue growth. The increase in pore size is only to about 2.0 mm, so that over time, cells will fuse to all of the pore space, filling it with both cells and extracellular matrix. However, some applications may require pore sizes greater than 2.0 mm, and it should be understood that the above disclosure is not limited to a maximum pore size of 2.0 mm.

[0013] The first and second sets of fibers can be arranged to form a first layer of a layered structure. In some embodiments, the scaffold comprises multiple layers. The fiber arrangement or design can be different in each layer. The first and second distance can be different in each layer. In some embodiments of the disclosed scaffold, the fibers of the first fiber set can be interwoven with the fibers of the second fiber set. Alternatively or in addition to interwoven, the fibers of the first and / or second fiber set can be laminated to each other. Interwoven fibers can help to better connect the first and second fiber sets. For example, the first fiber set can be connected to the second fiber set by fusing the respective fibers. In some embodiments, a transition zone between the first and second fiber sets with a gradient in the transverse direction is provided to avoid delamination of the first and second fiber sets. The first and second fiber sets can be formed from medical grade biodegradable thermoplastics. The first and second fiber sets can be formed from different thermoplastics. The thermoplastics can be homopolymers or copolymers. In one aspect, the thermoplastic includes poly-e-caprolactone (PCL), poly(glycolide-co-trimethylene carbonate-co-caprolactone) thermopolymers, such as Strataprene® from Poly-Med Inc., (polycarbonate)urea, polyurethane and / or poly(ester urethane)urea. The thermoplastic may be biodegradable. The thermoplastic may be non-biodegradable. The melt electrowriting conditions (temperature, pressure, etc.) generally depend on the type of thermoplastic used to form the scaffold. The fibers of the first and second fiber sets can have diameters ranging from about 100 nm to about 100 μm. In some embodiments, the diameter is about 20 μm. The scaffold can further include a hydrogel. At least a portion of the first region can be embedded in the hydrogel.

[0014] The scaffold can include a planar region, such as a sheet of fabric. The scaffold can include a tubular region. The diameter of the tubular region can range from 0.5 to 50 mm. The tubular region is used in the construction of soft microactuators, typically as scaffolds for vascular regeneration and / or soft tissue in robotic devices. The scaffold can form part of the actuator. For example, melt electrowritten scaffolds for actuator components can be used. A combination of planar and tubular regions can be used. The scaffold can have three-dimensional features, such as protrusions that extend above the plane of the sheet or are formed in radially asymmetric portions. In some embodiments, the scaffold is a heart valve leaflet scaffold. In these embodiments, the first set of fibers can be generally oriented in the radial direction of the heart valve leaflet and the second set of fibers can be generally oriented in the circumferential direction of the heart valve leaflet.

[0015] In another aspect, the present invention provides a melt-electrowritten anisotropic soft tissue scaffold comprising a first set of fibers having a first Young's modulus and a second set of fibers having a second Young's modulus, the first Young's modulus unequal to the second Young's modulus, the first set of fibers being aligned in a transverse direction relative to the second set of fibers, the first and second sets of fibers being disposed in a first region of the scaffold.

[0016] A first Young's modulus is defined by a first set of fibers having a first curvature, and a second Young's modulus is defined by a second set of fibers having a second curvature. In some embodiments, straight fibers can impart specific mechanical properties and, consequently, Young's modulus to the first and / or second set of fibers. Changing the fiber diameter, pore size, and pattern arrangement (e.g., curvature) of the first and / or second set of fibers in different loading directions can change the Young's modulus of the first and / or second set of fibers, which in turn can change the anisotropic properties of the soft tissue scaffold.

[0017] One embodiment of the disclosed scaffold can further include a second region extending from the first region. The second region can support the first region, e.g., the second region can function as a support. The second region can be anisotropic or isotropic. The second region can be a soft tissue scaffold. The second region can be a mesh having fibers aligned in a first direction and a second direction. The first and second directions can be transverse to each other. The spacing between adjacent fibers in both the first and second directions can be the same. One embodiment can further include an intermediate region disposed at the interface between the first and second regions. The intermediate region can include a plurality of fibers. The intermediate region can reinforce the scaffold after it is implanted and sutured into tissue, e.g., help the scaffold withstand stresses applied thereto.

[0018] The first region can be semicircular. The second region can extend from the curved side of the first region, with the straight side of the first region forming the edge of the scaffold. In one embodiment, the first region can include a plurality of semicircular regions with the apexes of adjacent semicircles disposed adjacent to each other. The middle region can be disposed along the curved side. In one embodiment, the middle region can include a first set of concentric semicircular fibers arranged parallel to each other, and a second set of fibers connecting adjacent concentric semicircular fibers. The first region and the second region can be integral.

[0019] In another aspect, the present invention provides a method of fabricating an anisotropic soft tissue scaffold using melt electrowriting, comprising extruding a polymer melt through a nozzle to form fibers, depositing the fibers to form a first set of fibers arranged generally parallel to one another, each fiber of the first set of fibers having a serpentine structure with peaks and troughs, adjacent peaks in each fiber of the first set of fibers being spaced a first distance apart, and depositing the fibers to form a second set of fibers arranged generally parallel to one another, the second set of fibers being arranged in a transverse direction to the first set of fibers, one or more fibers of the second set of fibers connecting adjacent fibers in the first set of fibers, each fiber of the second set of fibers having a serpentine structure with peaks and troughs. In one aspect, the first set of fibers is deposited such that the first set of fibers has a first Young's modulus, and the second set of fibers is deposited such that the second set of fibers has a second Young's modulus. The first and second sets of fibers can form a first region of the scaffold.

[0020] In another embodiment, the present invention provides a method of fabricating an anisotropic soft tissue scaffold using melt electrowriting, comprising extruding a polymer melt through a nozzle to form fibers and depositing the fibers to form a body having a first region that is anisotropic, the first region comprising a first set of fibers arranged generally parallel to one another, each fiber of the first set of fibers having a serpentine structure formed with peaks and troughs, and a second set of fibers arranged generally parallel to one another, the second set of fibers being oriented in a transverse direction to the first set of fibers, each fiber of the second set of fibers having a serpentine structure formed with peaks and troughs, the first set of fibers being deposited such that the first set of fibers has a first Young's modulus, and the second set of fibers being deposited such that the second set of fibers has a second Young's modulus.

[0021] The path length of the fibers of the first fiber set over a first distance may not be equal to the path length of the fibers of the second fiber set over the same distance as the first distance. The first fiber set can be deposited such that adjacent peaks of each fiber of the first fiber set are separated by a first distance. The first fiber set can be deposited such that adjacent fibers in the first fiber set are separated by a second distance. The first and second fiber sets can be deposited such that the fibers of the first fiber set are interwoven with the fibers of the second fiber set. The first and second fiber sets can be deposited such that a portion of the first fiber set is fused to a portion of the second fiber set. The fusion of each fiber can be performed by depositing the fiber at a temperature above its melting point. For example, if the fiber is a PCL fiber, it can be deposited at a temperature above about 70° C. The method can further include annealing the scaffold to improve the fusion of each fiber.

[0022] The method can include depositing a plurality of fiber layers to form a layered structure. The first and second fiber sets can be deposited such that they form a layered structure. The method can further include depositing second and subsequent layered structures. The layered structures can be deposited such that each layered structure has a different anisotropy direction. Stated differently, the first fiber sets of each layered structure can be aligned to be oriented transverse to one another.

[0023] An embodiment may further include depositing the fibers to form a second region extending from the first region. The second region may be isotropic. The second region may include a mesh having fibers aligned in a first direction and a second direction. The first and second directions may be transverse to each other. In an embodiment, the first and second directions are perpendicular to each other. The spacing between adjacent fibers in both the first and second directions may be the same. An embodiment may further include depositing the fibers to form an intermediate region disposed at the interface between the first and second regions. The intermediate region may include a plurality of fibers. An embodiment may further include treating a surface of the scaffold to increase the hydrophilicity of the scaffold. The method may further include forming a hydrogel that at least partially embeds the first region.

[0024] The first and second fiber sets can be deposited on a stage. The stage can be a mold having planar, tubular, and / or three-dimensional features. Thus, the method can be used to prepare scaffolds having planar, tubular, and / or three-dimensional features. The method can further include depositing the first fiber set in a generally radial direction and depositing the second fiber set in a circumferential direction. The scaffold can be a heart valve leaflet scaffold.

[0025] Another embodiment provides a scaffold formed using the above method. In another aspect, the present invention provides a method of melt electrowriting to form a soft tissue scaffold, comprising rotating a conductive mandrel about a longitudinal axis of the mandrel, the mandrel having a radially asymmetric portion, extruding a polymer through a nozzle to form a fiber, and depositing the fiber onto the mandrel at a predetermined wrap angle relative to the longitudinal axis as the mandrel rotates to form the scaffold.

[0026] By radially asymmetric, it is meant that the radius of the mandrel is not constant relative to the longitudinal axis, but rather that there are one or more portions that extend differently along the radial direction, resulting in different radii. By radially extending, it is meant extending away from and / or towards the central axis of the mandrel. Such radial extension includes features such as protrusions that extend away from the central axis, and grooves and channels that are recessed towards the central axis. Channels can be formed by protrusions.

[0027] Melt electrowriting has generally only been able to produce flat and / or symmetrical structures, and typically only non-soft tissue scaffolds such as bone scaffolds. By incorporating radial asymmetric sections into the mandrel, it is now possible to use melt electrowriting to produce scaffolds with three-dimensional features that resemble native tissues, such as the sinuses of Valsalva.

[0028] By using melt electrowriting with medical-grade plastic to create radially asymmetric sections on a mandrel, patient-specific three-dimensional scaffold structures can be manufactured more easily and cheaply compared to other methods of creating three-dimensional scaffolds. A step of depositing fibers can be provided to form a first region of the scaffold. Depositing the fibers can include printing and / or wrapping the fibers on a mandrel. The method further includes moving the nozzle and the mandrel relative to one another. The mandrel can be moved transversely relative to the nozzle. The mandrel can be moved longitudinally relative to the nozzle. The nozzle can be moved in a direction perpendicular to the plane of movement of the mandrel along the transverse direction. Furthermore, in some aspects, the nozzle and the mandrel can move relative to one another with more than two degrees of freedom, for example six degrees of freedom. In some embodiments, the nozzle and the mandrel can move relative to one another with two, three, four, five or six degrees of freedom. By increasing the number of degrees of freedom of the nozzle's movement relative to the stage (e.g., mandrel) used in the method, complex printed patterns can be formed on the scaffold. This is also important to ensure consistency and accuracy of printing, as the electric field can be maintained stable by dynamically adjusting the position of the scaffold and the print head (e.g., nozzle).

[0029] The method further includes varying the wrap angle by adjusting the speed at which the mandrel and nozzle move relative to one another. The method also includes varying the wrap angle by adjusting the rotation speed of the mandrel. The mandrel can move relative to the nozzle at a translation speed of the outer surface of the mandrel in the range of about 10 mm / min to about 2000 mm / min, such as about 1000 mm / min. For a given translation speed, the actual number of revolutions per minute of the mandrel depends on the radius of the outer surface of the mandrel. The method further includes varying the fiber spacing between adjacent fibers for the fibers deposited on the mandrel by controlling the rotation of the mandrel and the nozzle and / or the relative motion of the mandrel and the nozzle. The fibers can be deposited on the mandrel at one or more wrap angles. The one or more angles are in the range of about 0 to 90 degrees, such as 30 to 60 degrees.

[0030] The fibers are deposited on the mandrel in one or more layers. Each layer has a structure. Multiple structures may be deposited on the mandrel. A first layer of fibers is deposited on the mandrel at a first temperature. A second and subsequent layer of fibers is deposited on the mandrel at a second temperature. The first temperature may be lower than the second temperature. Varying temperatures may aid in fusing the different layers. The fibers in each layer may be deposited on the mandrel at a different wrap angle. For example, one layer may have fibers deposited on the mandrel at 30° and another layer may have fibers deposited on the mandrel at 45°.

[0031] The method further includes forming a first configuration of scaffolds and then forming a second configuration of scaffolds on an exterior surface of the first configuration. The first configuration can be formed using melt electrowriting. The first configuration can be formed on a mandrel. The mandrel can include a first segment having a first composition and a second segment having a second composition. The first and second segments can be engaged with one another such that the second composition overlies a portion of the first composition. The first configuration can be formed by depositing fibers in the first composition. The second configuration can then be formed by depositing fibers in at least the second composition.

[0032] The method may be solvent-free. For example, the polymer may be extruded through a nozzle without the need for a solvent. In this case, the extruded polymer may be a melt. The polymer may be one that is approved for implantation. The polymer may be a medical grade polymer. The polymer may be poly-e-caprolactone (PCL). The fibers may be PCL fibers.

[0033] The method may further comprise subjecting the scaffold to a pre-treatment for subsequent functionalization. The pre-treatment for subsequent functionalization may comprise surface activation with plasma and / or embedding the scaffold in a hydrogel to form a fiber-reinforced hydrogel. The hydrogel may be biodegradable. The hydrogel may be biodegradable. The pre-treatment for subsequent functionalization may be performed after the scaffold is formed and before the scaffold is removed from the mandrel. That is, the pre-treatment may be performed while the scaffold portion is on the mandrel.

[0034] Another embodiment provides a soft tissue scaffold formed using the above method. Another embodiment provides a melt-electrowritten soft tissue scaffold comprising a first hollow segment that is radially symmetric and has a longitudinal axis and a second hollow segment that is radially asymmetric and correlates with the first hollow segment, the first hollow segment and the second hollow segment being formed from fibers oriented at one or more angles relative to the longitudinal axis.

[0035] The first hollow segment can have fibers arranged at a first angle relative to the longitudinal axis. The second hollow segment can have fibers arranged at a second angle relative to the longitudinal axis. The scaffold can further include two or more layers. Each layer has a different average fiber angle, diameter, and distance from each other. The angle or angles can be in the range of about 0-90°, for example 30-60°. The multiple layers can form a structure. The scaffold can have multiple structures. The multiple structures can be arranged radially and / or longitudinally relative to each other.

[0036] The fibers can have diameters ranging from about 10 nm to about 100 μm. The spacing between adjacent fibers can form pores. Thus, in some embodiments, the scaffold can include pores. The diameter of adjacent fibers and the spacing between adjacent fibers can determine the pore size. The pores can have sizes ranging from about 1 μm to about 5 mm, for example, from about 10 μm to about 100 μm. The pores can serve to allow cell growth in and around the scaffold. Thus, the size of the pores can be determined by the type of cells intended to be seeded on the scaffold and the tissue intended to be grown on the scaffold.

[0037] The scaffold can have mechanical properties similar to the native tissue that the scaffold is intended to regenerate. For example, the scaffold can have mechanical properties similar to soft tissue, such as the native aortic root. The scaffold can have mechanical properties such that when injected with cellular material, such as epithelial cells that can form the aortic root, the injected scaffold has mechanical properties similar to the native tissue. It is understood that the mechanical properties of a fresh scaffold, i.e., a scaffold that has not yet been implanted in a patient, will degrade in situ and change over time. The rate at which the scaffold degrades is determined by the polymer used to form the fibers, the patient, the type of tissue formed on the scaffold, and the forces applied to the scaffold and / or the regenerated tissue in situ.

[0038] The scaffold may be a scaffold for the aortic root. The second segment may include a radially extending bulge that forms a scaffold for the sinuses of Valsalva. The scaffold may further include a leaflet scaffold portion arranged within the cavity formed by the bulge. The location of the leaflet scaffold may be used as a scaffold for a valve in the aortic root. The scaffold may further comprise a hydrogel. The scaffold may be embedded in the scaffold or the hydrogel may be embedded in the scaffold. The hydrogel may be used in a method of introducing cells into the scaffold, and the combination of the hydrogel and the scaffold may each promote optimal cell-scaffold interactions and improve the mechanical properties to an improved integrity.

[0039] The scaffold can be in the range of about 1 mm to about 50 mm in diameter considering the aortic wall. The fibers can be made from polymers, copolymers, or composites such as aliphatic polyesters / polyethers including PCL, PLLA, PLGA, PDO, PMMA. In another aspect, the present invention provides a melt electrowriting system for forming a soft tissue scaffold, comprising: a stage; a conductive mandrel configured to be secured to the stage during use, the mandrel having a longitudinal axis and a radially asymmetric portion, the conductive mandrel being rotatable about the longitudinal axis, comprising a nozzle for extruding polymer fibers, and a power source for applying an electric potential between the nozzle and the conductive mandrel.

[0040] The mandrel can be formed from one or more metals, such as aluminum, stainless steel, copper, and / or a conductive polymer. The mandrel can be formed from a non-conductive material covered with a conductive material. The mandrel can have a conductive core, such as a metal rod. In one embodiment, the mandrel is a conductive plastic, such as conductive poly(lactic acid) with a metal core. The metal core can function as the shaft.

[0041] The mandrel can be formed from one or more segments that are engageable with one another. The mandrel can include a first segment that is engageable with a second segment. The first segment can have a first composition and the second segment can have a second composition. When the first and second segments are engaged with one another, the first composition can cover a portion of the second composition.

[0042] The stage and / or nozzle can move relative to one another. The stage and nozzle can move in the X, Y, and Z directions relative to one another. Increasing the degrees of freedom of the stage can facilitate more complex movements. The stage and nozzle may be movable relative to one another with more than two degrees of freedom, e.g., more than three degrees of freedom, six degrees of freedom, etc. Another aspect provides a scaffold prepared using the above system. The scaffold may be as described above. [Brief description of the drawings]

[0043] Embodiments are described hereinafter by way of example with reference to the accompanying drawings, in which however the embodiments are not limited thereto. [Figure 1] FIG. 1 shows an embodiment of a scaffold structure. [Diagram 2] FIG. 2 shows another embodiment of a scaffold structure. [Diagram 3] FIG. 3 shows another embodiment of a scaffold structure. [Figure 4] Figure 4 shows SEM images of embodiments of PCL melt electrospun scaffolds, (a) showing a pore with 0.5 mm circumferential and 2 mm radial dimensions formed with 20 layers of straight fibers, (b) a pore with 0.5 mm circumferential and 2 mm radial dimensions formed with 20 layers of helical patterned fibers, (c) a pore with 0.25 mm circumferential and 2 mm radial dimensions formed with 20 layers of helical patterned fibers, (d) cross-sectionally layered fibers, and (e) fusion of circumferential and radial fibers. [Diagram 5] Figure 5 shows a schematic diagram illustrating the deformation behavior of aortic valve leaflet collagen fibers and the origin of the J-shaped displacement of stress / strain. [Figure 6]Figure 6 shows the mechanical properties of melt-electrowritten scaffolds obtained by circumferential uniaxial tensile tests: (a) Stress / strain curves of representative scaffolds with different pore sizes and number of layers at strains up to 100%, (b) a continuous progression of fibers from tortuous to straight structures (scale bar = 2 mm), (c) representative stress / strain curves of 20-layer scaffolds with pore sizes of 0.5 and 0.25 at strains up to 30%, (d) comparison of representative stress / strain curves of 0.5 mm pore size scaffolds with 15, 20, and 30 layers, (e) tensile modulus of scaffolds with different pore sizes, and (f) comparison of tensile modulus of scaffolds with different number of layers. [Figure 7] Figure 7 shows the results of uniaxial tensile tests performed to determine the effect of curvature on the strain at maximum stress. (a) is a typical stress / strain curve, and (b) is the tensile modulus in different regions of the J-shaped curve. [Figure 8] Figure 8 shows the anisotropic properties of the optimized scaffold compared to native aortic valve leaflets: (a) Representative stress / strain curves in the circumferential (0.25 mm pores) and radial (1 and 2 mm pores) directions, (b) Anisotropy ratio of MEW scaffolds, and (c) Comparison of the elastic modulus of MEW scaffolds formed with PCL to that of porcine, ovine, and human aortic valve leaflets in the circumferential and radial test directions (native tissue properties are represented by dashed lines, while solid lines represent radial and circumferential values, respectively). [Figure 9] Figure 9 shows the characteristic stress relaxation response of the scaffolds obtained in uniaxial tensile tests. [Figure 10] FIG. 10 shows measured and predicted fatigue properties of an embodiment scaffold tested in (a) circumferential and (b) radial directions. [Figure 11] Figure 11 shows the characteristic hysteresis properties of the embodiment scaffolds: (b) a representative curve in the circumferential direction, (c) a representative curve in the radial direction, and (d) the effect of strain on the unloading / loading ratio. [Figure 12]FIG. 12 shows (a) overall appearance, (b) SEM images, and (c) live / dead staining of an embodiment scaffold statically cultured for 1 week and 2 weeks as a human / HUVSMC (human umbilical vein smooth muscle cell)-encapsulated fibrin complex. [Figure 13] FIG. 13 shows immunohistochemical analysis of the disclosed embodiment scaffolds for one and two weeks of static culture of human / HUVSMC (human umbilical vein smooth muscle cells)-encapsulated fibrin complex. Collagen synthesized during static culture is shown stained (green) for collagen type I (i, v) and (red) for collagen type III (iii, vi). Seeded cells stained positive for a-SMA (ii, vi). Scale bars are (b): 500 μm, (c): 200 μm, (d): i, ii, iii, v, vi, vii: 100 μm, and iv, viii: 200 μm. [Figure 14] 14 shows a silicone simulant of the aortic root with a scaffold according to an embodiment of the present disclosure sutured to three single leaflet valves (i) in a lateral view highlighting the suture path, (ii) in aortic view, and (iii) in ventricular view. [Figure 15] Figure 15 shows the opening and closing sequence of the valve in Figure 14. The scale bar is 5 mm. [Figure 16] FIG. 16 shows a graph plotting the performance of the valve of FIG. 14 under physiological aortic pressure and blood flow conditions. [Figure 17A] FIG. 17A shows an embodiment of a scaffold structure. [Figure 17B] FIG. 17B shows an embodiment of a scaffold structure. [Figure 17C] FIG. 17C shows an embodiment of a scaffold structure. [Figure 18] FIG. 18 shows an embodiment of a heart valve scaffold having two regions. [Figure 19] FIG. 19 shows a schematic of an embodiment of a scaffold having two regions. [Figure 20]FIG. 20 shows a schematic diagram of another embodiment of a scaffold having two regions and a middle region. [Figure 21] FIG. 21 shows an embodiment of a tubular heart valve scaffold having two regions. [Figure 22A] FIG. 22A shows a graph plotting the performance of the valve of FIG. 21 under physiological aortic and pulmonary artery pressure and flow conditions. [Figure 22B] FIG. 22B shows various stages of valve opening and closing under the aortic pressure and flow conditions of FIG. 22A. [Diagram 23] FIG. 23 illustrates an embodiment of a melt electrolighting system. [Figure 24A] FIG. 24A shows a side view of an embodiment of a mandrel used in the system of FIG. [Figure 24B] FIG. 24B shows a top view on an embodiment of a mandrel used in the system of FIG. [Figure 24C] FIG. 24C shows a perspective side view of an embodiment of a mandrel used in the system of FIG. [Diagram 25] FIG. 25 shows an embodiment of a two-piece mandrel for use in the system of FIGS. 22A and 22B. [Figure 26A] FIG. 26A illustrates an embodiment of a mandrel for use in the system of FIG. [Figure 26B] FIG. 26B shows an embodiment of a portion of a scaffold disposed on a segment of the mandrel from FIG. 26A. [Figure 26C] FIG. 26C shows an embodiment of a scaffold prepared using the mandrel of FIG. 25A. [Figure 27] FIG. 27 shows embodiments of scaffolds prepared with different fiber wrapping angles. [Figure 28] FIG. 28 shows microscopic images of tubular scaffolds with different wrapping angles. [Figure 29] FIG. 29 shows a multi-layered soft tissue scaffold. [Diagram 30] FIG. 30 shows multi-layered soft tissue scaffolds of various dimensions. [Diagram 31] Figure 31 shows the characteristics of the wrap angle and fiber diameter of the tubular melt electrowriting (MEW) scaffolds: (a) wrap angle on the wall and sinus; (b) fiber diameter on the wall and sinus; and (c) statistical comparison of wrap angle and fiber diameter between the wall and sinus. [Diagram 32] Figure 32 shows the viability of HUVSMCs directly seeded on MEW scaffolds with 0.5mm straight, 0.5mm serpentine, and 0.25mm serpentine pore sizes and cultured under static conditions for 1 and 2 weeks. a) Overall appearance; b) SEM images; and c) Live / Dead staining. Scale bars a: 2mm; b: 500μm; c: 200μm. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0044] FIG. 1 shows an embodiment of a melt electrowritten anisotropic soft tissue scaffold. The scaffold of FIG. 1 is in the form of a sheet 10. The sheet 10 has a first fiber set 12. The first fiber set 12 is made of a plurality of fibers (12a, 12b, . . . 12x) arranged approximately parallel to one another. Each fiber 12a-x has a serpentine structure that runs non-linearly with respect to the longitudinal direction represented by the dashed line 21. In the first fiber set 12, each fiber 12a-x has a peak formed as an upper portion 14 and a trough formed as a lower portion 16. Each upper portion 14 of each fiber 12a-x is separated by a first distance d1. The first distance d1 is common to the spacing between the apexes of adjacent peaks for all upper portions of the fibers 12a-x of the first fiber set 12. In the embodiment of FIG. 1, each fiber 12a-x is generally sinusoidal in shape. The spacing between the upper portions 12 is approximately the same as the spacing between the lower portions 16. Adjacent fibers of the first set of fibers (e.g., 12a and 12b) are separated by a second distance d2. In the embodiment of Figure 1, the first set of fibers 12 are provided as semicircles having a diameter of about 0.5 mm, where d1 is greater than the diameter. This helps to control and mimic the anisotropy of the sheet.

[0045] The sheet 10 has a second set of fibers 18 arranged generally transversely to the first set of fibers 12. The term "transversely" should be broadly interpreted to mean that the first set of fibers 12 and the second set of fibers 18 are arranged at a predetermined angle between 0° and 90°, for example, about 30° to 90°, with respect to each other. Similar to the first set of fibers 12, the second set of fibers 18 is comprised of a plurality of fibers (18a-x), each having a peak formed as a left portion 20 and a trough formed as a right portion 22. The second set of fibers has a generally sinusoidal waveform. The second set of fibers 18 is connected to the first set of fibers 12. FIG. 1 shows that the connection point between the first and second set of fibers, for example, 13, is at the peak 14 of the first set of fibers 12 and the inflection point between the left portion 20 and the right portion 22 of the second set of fibers 18. In other words, the second set of fibers 18 is connected to a region adjacent the upper portion 14 of the first set of fibers 12. In some embodiments, the second set of fibers 18 is attached to a location other than the upper portion 14 of the first set of fibers 12, or to both the upper portion 14 and a location other than the upper portion 14, including locations adjacent or distant from the upper portion 14 and / or the left portion 20, or locations adjacent or distant from the upper portion 14 and / or the right portion 22.

[0046] It should be understood that the terms "peaks," "troughs," "upper portion," "lower portion," "left portion," and "right portion" are relative terms and do not limit the orientation of the sheet 10 to any particular direction. Stated differently, each fiber has a longitudinal direction (i.e., 21), and the fiber path lengths are arranged to extend from the longitudinal direction to either the left or right or above or below in an alternating manner to provide a meandering fiber path. As an example, when the sheet 10 is flipped from top to bottom, the peaks 14 are converted into troughs 16. Conversely, when the sheet 10 is flipped from left to right, the left portion 20 is converted into the right portion 22.

[0047] The path length of the first fiber set 12 for the first distance d1 is not equal to the path length of the fibers of the second fiber set for the same distance d1' as the first distance d1. For the embodiment of FIG. 1, the path length of the first fiber set 12 is greater than the path length of the second fiber set 18. The path length is the total length of the fibers when stretched longitudinally for the first distance, e.g., the total length of the fibers 12a between points 13 and 15. This longer path length of the first fiber set 12 is due in part to the higher curvature of the first fiber set 12 compared to the second fiber set 18. The longer path length allows the first fiber set 12 to be stretched from the serpentine state of FIG. 1 to a more straight state with a greater extension at a lower applied stress / strain compared to the second fiber set 18. When the first set of fibers 12 and / or the second set of fibers 18 are stretched to a straightened state (i.e., elongated), the initial linearly varying low stress / strain relationship transitions to a high (rapidly varying) stress / strain relationship until a certain ultimate tensile stress is reached. Thus, by imparting a higher curvature, the sheet 10 can stretch the first set of fibers 12 further in a general direction than the second set of fibers 18 before transitioning from low to high stress / strain. In other words, the sheet 10 has different elongation characteristics (i.e., different mechanical properties) in the X and Y directions.

[0048] Assuming that the path length of the first set of fibers 12 relative to the first distance d1 is greater than the path length of the second set of fibers 18, increasing the first distance d1 relative to the second distance d2 will also increase the anisotropy ratio of the first set of fibers 12 relative to the second set of fibers 18. The anisotropy ratio is the ratio of the elongation of the sheet 10 in the direction of the first fibers 12 to the elongation of the sheet 10 in the direction of the second set of fibers 18. In other words, the first set of fibers 12 can be stretched further than the second set of fibers 18 before reaching a certain ultimate tensile stress. In the embodiment of FIG. 1, the first set of fibers 12 has a high tensile modulus of about 1 Mpa and the second set of fibers 18 has a high tensile modulus of about 5 Mpa. Increasing the number of fibers comprising the first and / or second set of fibers increases the ultimate tensile stress of the set of fibers. For example, if the second distance d2 is decreased but the first distance d1 remains the same (i.e., the density of the first fiber set increases), the ultimate tensile stress of the sheet 10 increases in the direction of the first fibers 12, but the large elongation at low applied stress / strain remains the same. Increasing the density of the second fiber set 18 relative to the first fiber set 12 increases the ultimate tensile stress of the second fiber set 18. This means that by changing the first distance d1, the second distance d2, the path lengths of the first and second fiber sets, and the density of the first and / or second fiber sets, the specific mechanical properties of the sheet 10 can be tailored. However, by keeping the fiber path lengths of the first and second fiber sets different, the sheet 10 will have different mechanical properties along different directions, i.e., the directions of the first and second fibers, making the sheet anisotropic.

[0049] The first distance d1 in the embodiment of FIG. 1 is in the range of about 0.5 mm to about 2.5 mm, for example, about 1.0 to 2.0 mm. The second distance d2 is in the range of about 0.1 mm to about 0.5 mm. Reducing d2 increases the ultimate tensile strength of the first set of fibers. Since the sheet 10 functions as a scaffold for soft tissue, the size of the pores formed between adjacent fibers may be important. If the pore size is too small, cell infiltration into the scaffold is restricted.

[0050] Cell adhesion may also be affected. If the pore size is too large, proper cell infiltration may not occur and growth may be reduced. For example, if the pore size is too large, cells may first attach around the pore and then grow radially inward, but radial inward growth can only continue if the cells are supported unevenly. Therefore, the size of the pores formed by the first and second fibers should be about 1 μm to about 400 μm.

[0051] It should be understood that not all three-dimensional printing devices, such as melt electrowriting devices, are capable of providing sheets with such detail that the resolution of the fibers is often limited to about 200 μm. Such large fibers cannot provide a soft tissue scaffold that has anisotropic properties and can induce cell growth. In some embodiments, the diameter of the first and second set of fibers ranges from about 100 nm to about 100 μm, for example about 20 μm. In some embodiments, the fibers include PCL. In some embodiments, the fibers are PCL fibers. Other polymers that can be processed by melt electrowriting can also be used to form the fibers.

[0052] Scaffolds with anisotropic mechanical properties are useful for providing a structural analogue to collagen structure. This means that soft tissue scaffolds with mechanical properties similar to native tissues can be used to regenerate damaged and / or diseased tissues. For example, heart valve leaflets can be stretched further in the radial direction compared to the circumferential direction. Thus, soft tissue scaffolds with anisotropic mechanical properties can be useful as scaffolds for regenerating heart valve leaflets. In some embodiments, the first fiber set 12 (with higher curvature) is generally oriented in the radial direction, and the second fiber set 18 (with lower curvature) is generally oriented in the circumferential direction, thus providing a heart valve leaflet structure similar to the native collagen structure.

[0053] FIG. 1 illustrates an embodiment in which the first fiber set 12 and the second fiber set 18 have a generally sinusoidal waveform. Some embodiments can also have fibers with straight (i.e., elongated) regions, square waves, and / or zigzag waveforms. In some embodiments, fiber structures are used in combination. For example, the first fiber set can have a serpentine structure and the second fiber set can have a square wave. In the embodiment of FIG. 2, the sheet 40 has a serpentine first fiber set 42 arranged to have a zigzag structure. Each fiber of the first fiber set 21 has a peak formed in the shape of an upper portion peak 44 and a trough formed in the shape of a lower portion peak 46. Adjacent upper peaks 44 are separated by a first distance d1. Each fiber of the first fiber set 42 is separated by a second distance d2. The sheet 40 also has a second fiber set 48. Each fiber in the second set of fibers has a zigzag configuration with a peak formed in the shape of a left peak 52 and a trough formed in the shape of a right peak 50. The degree of curvature of the first set of fibers 42 is greater than the degree of curvature of the second set of fibers 48.

[0054] 3 illustrates an embodiment of a sheet 60 having a serpentine first set of fibers 62 having a square wave structure with peaks formed in the shape of the upper section 64 and troughs formed in the shape of the lower section 66. The central regions of adjacent upper sections 64 are spaced a first distance d1 apart. The fibers of the first set of fibers are arranged substantially parallel to one another and spaced a second distance d2 apart. The second set of fibers 68 has a square wave structure with peaks formed in the shape of the right section 70 and troughs formed in the shape of the left section 72. The first set of fibers 62 has a higher degree of curvature than the second set of fibers 68.

[0055] The term "serpentine" should be broadly interpreted to mean fibers that alternately meander on either side of the longitudinal direction. For example, in the embodiment of Figure 1, the longitudinal direction of the first set of fibers 12 is represented by dashed line 21. Each fiber of the first set of fibers alternates between meandering on either side of the longitudinal direction to form upper and lower sections 64 and 66.

[0056] In some embodiments, a plurality of first and / or second fiber sets are stacked on top of each other. For example, the first fiber set 12 has 10-30 layers of fibers, forming a laminate. In some embodiments, the first and / or second fiber sets are stacked on top of each other up to 2500 layers. In some embodiments, the number of layers ranges from 1 to 2500. A single layer has a thickness approximately equal to the diameter of the fiber. The 2500 layers can have a thickness (extending in the Z direction) of up to about 10 cm. In some embodiments, a plurality of sheets are combined to form a soft tissue scaffold. Each of the plurality of sheets may be a laminate. In these embodiments, each sheet may be the same, or a combination of different sheets may be used, for example a two-sheet scaffold having sheet 10 and sheet 60. The longitudinal directions of the first fiber sets for each sheet may be aligned parallel to each other and / or transverse to each other. In some embodiments, adjusting the longitudinal angle of the first set of fibers relative to each other for each sheet helps to control the anisotropic behavior of the resulting scaffold. If the scaffold has multiple layers, the fibers of each layer can be stacked separately, so that the resulting multi-layer scaffold has walls or the like that run from the outer layer to the inner layer (i.e., in the Z direction) with a serpentine structure. This means that in addition to having different mechanical properties in the X / Y directions, the soft tissue scaffold can have different mechanical properties in the Z direction.

[0057] To form the sheet 10, a melt electrowriting (MEW) device and / or system is used to melt the polymer and extrude it through a nozzle to form fibers. An embodiment of a MEW device is shown in FIG. 12. Fibers are deposited on the stage by applying an electric potential between the nozzle and the stage. A plurality of fibers are deposited approximately parallel to each other to form a first set of fibers 12. A second set of fibers 18 is also formed by depositing a plurality of approximately parallel fibers at an angle across the first set of fibers 12. In some embodiments, the first and second sets of fibers 12 / 18 are deposited such that the fibers of the first set of fibers 12 are interwoven with the fibers of the second set of fibers 18. Such a structure helps to improve the bonding of the first set of fibers 12 and the second set of fibers 18 at the contact points, e.g., 13. If the temperature of the deposited fiber is high enough, it will fuse to the already deposited fibers and form the contact points. To help ensure that the temperature of the deposited fiber is high enough, the temperature of the nozzle in some embodiments is higher than the temperature used to form the polymer melt prior to extrusion. For example, in some embodiments, when PCL is used to form the fibers, the nozzle is at about 85°C and the melt is at about 75°C.

[0058] In some embodiments, the first and second sets of fibers are deposited to form a laminate. In these embodiments, the method further includes depositing a second or subsequent laminate, e.g., a plurality of laminates. Each laminate can be formed by depositing a plurality of the first and / or second sets of fibers on top of one another. The longitudinal direction of the first set of fibers in one layer can be parallel and / or at an angle to the longitudinal direction of the first set of fibers in the second or subsequent layers.

[0059] The shape of the stage can determine the shape of the sheet 10 to some extent. For example, a planar stage results in a generally planar scaffold. However, if a tubular stage such as a mandrel is used, the scaffold will be tubular. Thus, the scaffold can take the form of many different shapes. For example, a vascular scaffold can have a polymeric structure as shown in FIG. 1. The stages in some embodiments also include three-dimensional features that result in a scaffold having the same three-dimensional characteristics. For example, a stage can have elements that form a mold for forming the leaflets of the aortic root. In these embodiments, the first set of fibers 12 is deposited radially to reflect the mechanical properties of the leaflets in the radial direction, and the second set of fibers 18 is deposited circumferentially to reflect the mechanical properties of the leaflets in the circumferential direction. Thus, depositing the first and / or second set of fibers 12 / 18 in specific directions can be used to form a soft tissue scaffold that acts as a structural analogue of the extracellular matrix support of natural collagen.

[0060] Typically, a working distance between the nozzle and stage of less than about 10 mm results in relatively fine features in the sheet 10 as a melt-electrowritten soft tissue scaffold, although a working distance of less than 4 mm typically provides the best deposition resolution and detail. Although the embodiments and examples have been directed to soft tissue scaffolds for heart valve leaflets, the present disclosure is not limited to scaffolds for heart valve leaflets, but can be broadly adapted to anisotropic soft tissue scaffolds for use in the regeneration of vascular, epidermal, tendon, ligament, breast, and other tissues that generally require the use of an anisotropic collagen extracellular matrix.

[0061] Another embodiment of a scaffold 80 is shown in FIG. 17A. The scaffold 80 is a tubular scaffold with two different regions formed as two different scaffold structures. One region of the scaffold 80 has a first structure 81 and another region of the scaffold has a second structure 82. The first structure 81 has a diamond type pattern, as represented diagrammatically as 81a. The second structure has a square mesh type pattern, as represented diagrammatically as 82a. A boundary region 83 is formed at the boundary where the first structure 81 changes into the second structure 82. The first structure 81 and the second structure 82 are integral in FIG. 17A. However, there are some embodiments in which the first structure 81 and the second structure 82 are not integral.

[0062] Another embodiment of the scaffold 84 is shown in FIG. 17B. The scaffold 84 is tubular and has a structure formed from a mesh with meandering fibers, as represented generally at 85. Another embodiment of the scaffold 86 is shown in FIG. 17C. The scaffold 86 is tubular and has a structure formed from a mesh with meandering fibers, as represented generally at 87. In some embodiments, the first structure 81 or the second structure 82 is replaced by the structure 85 and / or 87. The scaffolds 80, 84 and 86 are formed from PCL fibers having diameters in the range of about 10 nm to about 100 μm in one embodiment. The distance between adjacent fibers is in the range of about 0.1 mm to about 2.5 mm.

[0063] Another embodiment of a scaffold 200 is shown in FIG. 18. The scaffold 200 has a first region 202. The first region 202 is formed from a melt-electrowritten anisotropic soft tissue scaffold. In some embodiments, the anisotropic soft tissue scaffold of the first region is as described with reference to FIGS. 1-13. For example, the first region can have the structure of a sheet 10.

[0064] Extending from the first region 202 is a second region 204. The second region 204 is formed from a melt electrowritten material. The second region 204 serves as a support for suturing the scaffold 200 to tissue, such as the aortic root. The second region 202 may be a soft tissue scaffold. The structure of the second region 204 is selected to provide good suture retention properties. In some embodiments, the structure of the second region is selected to provide a pulsatile behavior that matches the aortic root during use. In some embodiments, the second region 204 is isotropic. For example, the second region 204 can have a polymer structure similar to 82a. In some embodiments, the second region 204 is anisotropic. The isotropy of the second region 204 can be adjusted by adjusting the relative angles between different sets of fibers. For example, an isotropic material can be formed when the first and second sets of fibers are aligned at approximately 90° to one another, but an anisotropic material can be formed when the first and second sets of fibers are aligned at an angle >90° to one another. The transition between the first region 202 and the second region 204 is defined by an interface 206. When the first region 202 and the second region 204 are integrated, the interface 206 is formed by changing the orientation of the fibers.

[0065] A schematic diagram of the tubular scaffold of FIG. 18 is shown in FIG. 19. The scaffold 200 shown in FIG. 19 is a planar projection of the tubular structure shown in FIG. 18. In some embodiments, the scaffold 200 is prepared as a flat sheet that is rolled and joined to form the tubular structure. For example, edge 216 and edge 218 can be joined together to form the tubular structure. However, in some embodiments, the scaffold 200 is prepared as a tube. In the embodiment of FIG. 19, the scaffold 200 has three first regions 202a, 202b, and 202c. The first regions 202a-202c are semicircular in shape. The second region 204 extends from the first regions 202a-202c. The interface 206 between each of the first regions 202 and the second region 204 is formed by the curved edge 207 of the first region 202.

[0066] The term "region" should be interpreted broadly to mean regions having similar polymer structures. For example, a first region has an anisotropic polymer structure and a second region has an isotropic structure. Generally, the structures of the first regions 202 are the same, but there may be some embodiments in which they are different. For purposes of illustrating embodiments of the present disclosure, the first and second regions shown in Figures 19 and 20 are represented by different hatching. It should be noted that the structures of the first and second regions are not limited to the hatched structures depicted.

[0067] The first regions 202a-202c form the three heart valve leaflets of the aortic root. The apexes 210 of adjacent first regions, e.g., 202b and 202c, are disposed proximate to each other. The apexes 210 are spaced apart from each other, with the second region 204 disposed partially between the apexes of adjacent first regions 202. However, there may be some embodiments in which the apexes of the first regions 202 touch and / or overlap each other. The scaffold 200 has opposing edges 212 and 210. The edge 212 is a downstream edge (e.g., aortic side) associated with the first regions 202a-202c. The edge 214 is an upstream edge (ventricular side) associated with the second region 204.

[0068] The scaffold 200 in some embodiments has an intermediate region in the form of a reinforced region 208. The reinforced region 208 has a series of concentric semicircular fibers 220 arranged parallel to one another and several connectors 222 connecting adjacent fibers 220. In use, the scaffold 200 is sutured into position around tissue. The reinforced region 208 helps dissipate and withstand forces applied to the scaffold 200 at the suture location. The reinforced region 208 also helps withstand differences in forces applied to the first region 202 and the second region 204. The reinforced region 208 is generally located at or overlapped on the interface 206. The reinforced region 208 may span the same area as the first region 202 and / or the second region 204.

[0069] The reinforcement regions 208 of each of the first regions 202a-b overlap near the edge 210. The intermediate region 208 extends from an initial first region, such as the apex of 202b, to the next first region, such as the apex of 202c. Generally, the stiffness of the scaffold increases in the reinforcement regions 208. At the overlap of the reinforcement regions 208, the stiffness of the scaffold can increase beyond a desired value. In some embodiments, the reinforcement regions 208 are tapered to control the stiffness of the reinforcement regions 208. For example, the number of fibers 220 and / or connectors 222 can be varied as the reinforcement region 208 extends from the apex 209 to the edge 212 of the terminal 211. In a tubular configuration, the terminals disposed between each of the first regions 202 form an angle between adjacent heart valve leaflets. Varying the structure of the reinforcement regions 208 can be used to tune the mechanical properties of the scaffold 200 and, as a result, the in-use properties. This can be used to tailor the mechanical properties of the scaffold 200. In one embodiment, the scaffold 200 is formed from PCL fibers having diameters ranging from about 10 nm to about 100 μm. The distance between adjacent fibers ranges from about 0.1 mm to about 2.5 mm.

[0070] An embodiment of a tubular scaffold 250 with a reinforced region is shown in FIG. 21. The scaffold 250 has a first region in the form of a semicircular heart valve leaflet 252 and a second region in the form of a tubular body 254. The second region 254 serves as a support for the first region 252. The scaffold 250 has three heart valve leaflets. The tubular body 254 extends from the heart valve leaflet 252. The reinforced region 256 is disposed between the heart valve leaflet 252 and the tubular body 254. The heart valve leaflets 252 have downstream edges (aortic side) 258. During use of the scaffold 250, when back pressure is applied to the scaffold 250, the edges 258 of the three heart valve leaflets 252 come together and engage with each other to close the valve (as best seen in FIG. 22B). The sutures 260 connect the apexes of adjacent heart valve leaflets such that an acute angle Q is formed between them. The angle Q is similar to the angle Q of a native aortic root heart valve. In one embodiment, the angle Q ranges from about 30° to about 50°. The angle Q depends on the distance from the pinch (suture) point to the apex 262 of the first region 252. Forming the angle Q helps ensure that the edges 258 contact each other during closure of the valve formed by the scaffold 250. In some embodiments, the sutures 260 are also used to attach the scaffold 250 to the surrounding tissue once the scaffold 250 is implanted. The scaffold 250 in one embodiment is formed from PCL fibers having a diameter in the range of about 10 nm to about 100 μm. The distance between adjacent fibers ranges from about 0.1 mm to about 2.5 mm. In the embodiment of FIG. 21, the second region 254 is provided as an isotropic soft tissue scaffold. However, there are some embodiments in which the second region 254 is anisotropic. In all embodiments, the second region 254 need not be a soft tissue scaffold.

[0071] Embedded within the scaffold 250 is a hydrogel. In some embodiments, the hydrogel is elastin-based. The hydrogel may help promote favorable tissue growth. The hydrogel may also help the scaffold withstand mechanical forces applied during use before tissue is formed, such as at the suture site. In one embodiment, the scaffold 250 is disposed in an annulus between the inner wall of a cylindrical outer component and the outer wall of an inner component. A hydrogel precursor is then injected into the annulus, causing the hydrogel to harden and embed into the scaffold. As used herein, the term "embedded" or similar phrases such as "embedded" should be broadly interpreted to mean that the hydrogel is in contact with the surface of the scaffold, the scaffold is completely contained within the hydrogel, the hydrogel is contained within the pores of the scaffold, or any combination thereof.

[0072] Hydrogels may be either biodegradable or non-biodegradable. Non-biodegradable hydrogels include polytetrafluoroethylene (PTFE) and expanded PTFE, polysiloxane (silicone, PDMS), thermoplastic polyurethane (TPU), thermoplastic polyurethane urea, polyhedral oligomeric silsesquioxane poly(carbonate-urea) urethane (POSS-PCUU), and / or polysiloxane urethane (urea) (PSU). Non-biodegradable hydrogels can allow the scaffold to function as a non-degradable replacement heart valve. If the hydrogel is non-biodegradable, the fibers used to form the scaffold are preferably non-biodegradable. If the hydrogel is biodegradable, the fibers used to form the scaffold are preferably biodegradable.

[0073] A graph plotting the performance of scaffold 250 under physiological aortic pressure and flow conditions is shown in Figure 22A. As can be seen, scaffold 250 exhibits little to no regurgitation and has regurgitation values ​​consistent with ISO 5840. The relative motion of the heart valve leaflets 252 of scaffold 250 during simulated physiological aortic pressure and flow conditions is shown in Figure 22B. During maximum flow, the downstream ends 258 of each leaflet 252 are furthest apart from each other, and during minimum flow, the downstream ends of each leaflet 252 contact each other to close the valve.

[0074] The figures have illustrated specific embodiments relating to aortic root valves, however the polymeric structures and scaffolds of the present disclosure may be applied to other valves, such as vascular valves, including venous valves, and to other tissues, such as tubular tissues. FIG. 23 shows an embodiment of a melt electrowriting system 100 for forming a tubular soft tissue scaffold. The system uses MEW to form the scaffold structure. The system 100 has a stage 112 on which a conductive mandrel 114 can be mounted. The mandrel 114 is conductive to allow an electric potential to be applied between a nozzle 116 and the mandrel 114. The nozzle 116 allows a polymer to be extruded to form a polymer fiber 118. In the embodiment of FIG. 23, the polymer extruded through the nozzle 116 to form the PCL fiber 118 is polycaprolactone (PCL). The mandrel 114 is horizontally movable around a plane defined by the base 199 of the stage, i.e., the mandrel 114 is movable in the XY direction. Since the nozzle 116 of the system 100 is fixed, the mandrel 114 is movable relative to the nozzle 116. However, in some embodiments, the mandrel 114 may be fixed and the nozzle 116 may move in the XY directions relative to the mandrel 114. Also, in some embodiments, the nozzle 116 and / or the mandrel 114 may be movable in the Z direction. In some embodiments, the nozzle is rotatable about one or more axes, meaning that in some embodiments the nozzle 116 and mandrel 114 are movable with more than three degrees of freedom, etc.

[0075] An embodiment of a mandrel is shown in Figures 24A, 24B, and 24C. The mandrel 150 has a central axis 151 extending along the longitudinal direction. A first segment formed in the shape of a tubular section 152 is radially symmetric. Extending from the tubular section 152 is a second segment formed in the shape of a bulbous region 154. The bulbous region 154 is radially asymmetric, which can be best seen in Figure 24B. The bulbous region 154 is formed of three radially extending hemispherical projections 156. In the embodiment of Figures 24A, 24B, and 24C, the bulbous region 154 is shaped to function as a trilobal form of the sinuses of Valsalva of the aortic root. In the embodiment of Figures 24A, 24B, and 24C, a central bore 156 extends along the longitudinal direction 151. The bore 156 allows the mandrel to be aligned coaxially with a shaft associated with the stage 112. It should be appreciated that the mandrel 150 is rotatable and thus the associated shaft and mandrel are in a fixed relationship to one another during use.

[0076] The mandrel 150 is electrically conductive. In some embodiments, the mandrel 150 is formed from a metal. However, in some embodiments, the mandrel may be formed from a non-conductive material and made conductive by applying a conductive coating to the outer fiber-receiving surface of the mandrel 150. For example, the mandrel may be prepared using a conventional three-dimensional printer to apply a layer of conductive material, such as copper, to the mandrel as shown in FIG. 24C. If the mandrel is to be coated with a metal to make it conductive, deposition, sputter coating, or the like may be used. In other embodiments, the mandrel 150 is formed from a three-dimensional printer using a conductive plastic, such as a conductive poly(lactic acid) / graphene composite.

[0077] The dimensions of the projections 156 and their relative size compared to the tubular region 152 depend on the size of the scaffold to be formed. For example, a three-dimensional model of the patient's aortic root, having the sinuses of Valsalva (i.e., projections 156), can be prepared according to the dimensions described by Thubrikar (European Journal of Cardio-Thoracic Surgery, 28(6), 850-855). This three-dimensional model can then be printed using a three-dimensional printer, resulting in a conductive structure even if not formed of conductive plastic. Using a three-dimensional printer to prepare the mandrel 150 allows for the formation of a patient-specific mandrel, and therefore the resulting scaffold, which is also patient-specific. Other methods of forming the mandrel 114, such as additive manufacturing methods, CNC, and casting, can be used to form the mandrel 114.

[0078] In the embodiment of Figures 24A, 24B, and 24C, the mandrel 150 is a one-piece construction. However, in some embodiments, it may be beneficial for the mandrel to be made of two or more segments. This may be useful to aid in removing the scaffold from the mandrel after it has been formed. It may also be useful to enable the feature of printing cavities in the walls of the scaffold. Figure 25 shows a two-part mandrel 160 having a first segment (i) and a second segment (ii). The first segment (i) has a first formation formed in the shape of a radially extending flap 162. The second segment (ii) has a second formation formed in the shape of an inwardly extending concave depression 164. The depression 164 terminates in a ridge 166. The ridges 166 are not continuous, so that there are gaps between each ridge.

[0079] The ridges generally extend from a common point 168 located near the longitudinal axis. In use, the second segment (ii) is attached to the stage 112 and the fibers 118 are arranged on the mandrel to form the scaffold. The recesses 164 form a mold for a valve associated with the sinuses of Valsalva of the aortic root. Once the fibers are deposited on the recesses 164 to form the valve scaffold, the first segment (i) is then connected to the second segment (ii) so that the flaps 162 sleeve the recesses coaxially arranged therein (not shown). The walls of the aortic root scaffold can then be formed by depositing the fibers 118 on the first segment (i) and the second segment (ii). The first segment (i) and the second segment (ii) can be engaged with each other to maintain a fixed relationship with each other. For example, an interference fit and / or bolts can be used to engage the first segment (i) and the second segment (ii) together.

[0080] The mandrel 160 is designed using a three-dimensional model of the aortic valve leaflets, including the sinuses of Valsalva, and the aortic root according to the patient's personalized anatomical features. This model is then separated into a two-piece model. The first component includes the sinuses of Valsalva and the aorta on the outflow side, and the second component includes the concave shape of the inflow leaflets (recess 164) and the aortic wall (left ventricle). The deposition of fibers during the formation of the scaffold with tubular MEW allows for easy attachment of the tubular scaffold to the leaflet scaffold with fused seams, interleaflet triangles, and annulus that mimic the native aortic valve.

[0081] An advantage of the mandrel 160 is that the valves and walls of the aortic root scaffold can be prepared using a single mandrel. Furthermore, because the mandrel 160 can be printed using a three-dimensional printer, the shape of the flap 162 (which acts as a mold for the sinuses of Valsalva) and the recess 164 (which acts as a mold for the valve) can be tailored specifically for the patient. This allows for the manufacture of custom soft tissue scaffolds. Furthermore, the use of melt electrowriting to form the scaffold means that simple and rapid manufacturing techniques can be employed.

[0082] Another embodiment of a two-part mandrel is shown in FIG. 26A. In this embodiment, the mandrel 170 has a first segment (i) and a second segment (ii) similar to the mandrel 160. The first segment (i) has a first formation formed in the shape of a radially extending flap 172. The second segment (ii) has a second formation formed in the shape of a semicircular cutout 174. To form an aortic root scaffold using the mandrel 170, a first component formed in the shape of a scaffold mesh 176 is wrapped around the cutout 174, as best seen in FIG. 26B. The first segment (i) of the mandrel 170 is then attached to the second segment (ii) of the mandrel while the mesh 76 is held in place. The assembled mandrel is then placed on the stage 112, and the walls and sinuses of the aortic scaffold are then formed on the mandrel 170 by depositing the fibers 118. A portion of the mesh 176 is embedded in the wall, fixing the mesh in place relative to the wall. An embodiment of a scaffold formed using a mandrel 170 is shown in Figures 26A, 26B, and 26C. Figure 26C(i) shows an embodiment of a scaffold 180 viewed along the longitudinal axis (e.g., 151) with the mesh 176 residing within the cavity formed by the wall 178 (Figure 26C(ii)) around the sinus of Valsalva 182. The use of a two-part mandrel aids in removing the scaffold from the mandrel after it has been created.

[0083] In some embodiments, a coil heater is placed within the bore 156 to heat the mesh 176 (i.e., the leaflets) to near its melting point and melt electrolight the wall (i.e., the root scaffold) to the upper portion of the mesh 176, providing a more secure connection between the mesh 76 and the wall 180. In other embodiments, a hydrogel system is incorporated into the seam to aid in better attachment of the base of the leaflets to the wall. This can be done in a post-processing step. In other embodiments, localized heating of the attachment point facilitates better fusion between the mesh 176 and the wall 180. This can be done by utilizing a low intensity laser to precisely position the fusion point at the desired location. It should be appreciated that in some embodiments, multiple configurations can be used that provide a more secure connection between the mesh 76 (i.e., the leaflets) and the wall 180 (i.e., the root scaffold).

[0084] To form a scaffold using the system 100, a fiber 118 is drawn from the nozzle 116 and deposited (e.g., printed) onto the mandrel 114. At the same time, the mandrel 114 is rotated and moved in the X direction (i.e., along the longitudinal axis of the mandrel) so that the fiber 118 is deposited to wrap around the mandrel 114 at a predetermined angle relative to the longitudinal direction 511. In some embodiments, the distance between the nozzle 116 and the outer surface of the mandrel 114 is adjusted by moving the stage 112 and / or the nozzle in the Z direction. The speed at which the mandrel 114 moves in the X direction determines the wrap angle. As the speed at which the mandrel moves in the X direction increases, the wrap angle of the fiber 118 decreases. Conversely, as the speed at which the mandrel moves in the X direction decreases, the wrap angle of the fiber 118 increases. In some embodiments, the speed at which the mandrel 114 rotates is also changed to adjust the wrap angle. Increasing the rotational speed of the mandrel 114 increases the wrap angle when a given motion on the mandrel 114 in the direction X is held constant, and decreasing the rotational speed of the mandrel 114 decreases the wrap angle. In some embodiments, the speed at which the mandrel 114 moves in the X direction and the speed at which the mandrel 114 rotates are adjusted to control the wrap angle. In some embodiments, the mandrel 114 is also moved in the Y direction (i.e., transverse to the longitudinal direction of the mandrel 114) in addition to the X direction. The movement of the mandrel 114 in the XY direction can be used to deposit (i.e., print) a specific fiber structure. Furthermore, the mandrel can be moved according to predefined coordinates to control the location at which the fibers are deposited (e.g., printed). In other words, the fibers can be printed as a three-dimensional conductive mandrel with a specific fiber structure, such as a serpentine structure, organic microstructures, etc. The mandrel 114 is rotated and moved back and forth along the X direction until the scaffold wall is formed. A single fiber may be used to form the wall of the scaffold, in which case the wall and wall-related features are unique to each other, or two or more fibers may be used to form the wall.For example, some embodiments use two or more nozzles that form two or more different fibers.

[0085] Varying the winding angle helps control the mechanical properties of the scaffold. The walls 178 around the sinuses of Valsalva 182 are generally formed with fibers deposited with a winding angle of greater than 45°, e.g., 60°, to help the scaffold 180 withstand radial and circumferential mechanical forces during use of the scaffold 180. The base 184 (i.e., the inflow side of the valve) and upper portion 186 (i.e., the outflow side of the valve) of the aortic root scaffold 180 are formed by winding fibers around the tubular section 152. The fiber angle of the base is generally less than 45°, e.g., 30°, to help the scaffold withstand forces acting along the longitudinal axis of the scaffold. Increasing the fiber density of the scaffold also helps to increase the mechanical strength of the scaffold. In general, the sinuses 182 of the scaffold are expected to be stiffer compared to the walls (184 / 186). For example, fibers can be deposited in the sinuses of Valsalva with small fiber spacing and in the aortic wall with large fiber spacing.

[0086] The particular wrapping angle, the transition between different wrapping angles, and the length of the region with a particular wrapping angle are determined by the size of the scaffold 180 and the structural requirements of the scaffold 180. For example, a scaffold for implantation in an adult patient will have different requirements to a scaffold for implantation in a pediatric patient. Examples of scaffolds with different dimensions and fiber angles are shown in FIG. 27. Scaffold 190 has a fiber angle of about 30° relative to the longitudinal direction, scaffold 192 has a fiber angle of about 45°, and scaffold 194 has a fiber angle of about 60°. Microscope images of tubular scaffold embodiments of scaffolds with fibers at 30° (scaffold 90) and 45° (scaffold 192) are shown more clearly in FIG. 28. The parameters used with the system 100 to manufacture one of the scaffolds shown in FIG. 27 are shown in Table 1. The higher the rotation speed of the mandrel, the higher the wrapping angle. In some embodiments, a base layer is first deposited (e.g., printed) on the mandrel 114. Subsequent layers of fibers 118 are then applied directly over the base layer. To help the layers bond together, the temperature at which the second or more layers are deposited on the mandrel 114 is higher than the temperature at which the base layer is deposited on the mandrel 114. For example, the first layer can be deposited at 81°C and the second layer can be deposited at 91°C. Using higher temperatures for the second and subsequent layers helps fuse the layers together. In some embodiments, the scaffold is annealed to help fuse the various layers together. The embodiments described herein are based on PCL-based fibers. However, PCL is just one example of a polymer that can be used in melt electrowriting to form soft tissue scaffolds as described herein.

[0087] [Table 1] The fiber diameter can also be adjusted by varying the rotation speed and wrap angle of the mandrel 114. Generally, as the wrap angle increases, the diameter of the fiber 118 decreases.

[0088] In some embodiments, the fibers 118 have a diameter ranging from about 10 nm to about 100 μm. One or more fiber diameters can be used to form the scaffold. The particular fiber diameter can depend on the type of cells seeded onto the scaffold and the tissue to be regenerated, as well as the requirements for the mechanical properties of the scaffold. It should be appreciated that layers of the scaffold can be formed by depositing multiple layers of fibers on a mandrel to form a structure. However, the scaffold can have multiple structures. For example, in some embodiments, multiple structures are deposited on the mandrel 114. The fibers of each structure can be aligned at a single angle or multiple angles. One embodiment of a three-layered scaffold is shown in FIG. 29. FIG. 29(a) shows a simulated model 1000 having an inner structure 1002, a middle structure 104, and an outer structure 106, each aligned coaxially with one another. The inner structure 1002 has fibers aligned at 50°, the middle structure has fibers aligned at 65°, and the outer structure has fibers aligned at 40°. This arrangement is similar to the collagen fiber orientation of the native aorta, where the inner structure 1002 serves as a scaffold for the intima, the middle structure 1004 serves as a scaffold for the media, and the outer structure 1006 serves as a scaffold for the adventitia. The scaffold 1000 in some embodiments has mechanical properties similar to the natural tissue that the scaffold is intended to regenerate. This means that the mechanical forces experienced in situ during the early stages of implantation, when the regenerated tissue is still immature to fully support itself, can be transferred to the scaffold. As cells proliferate and new tissue begins to grow, the scaffold using biodegradable fibers is replaced by the regenerated tissue and the scaffold degrades. During this transition from scaffold-supported tissue to regenerated tissue, the mechanical forces applied to the valve in situ are gradually transferred from the scaffold to the regenerated tissue.

[0089] An embodiment of a scaffold with this three-layer structure is shown in FIG. 29(b), showing a simulated model superimposed with an outer structure 1006. The dimensions and characteristics of the scaffold 1000 depend on the dimensions and characteristics of the mandrel on which the fibers are deposited and the requirements for a particular patient. FIG. 31 shows various three-layer melt electrospun scaffolds. Scaffold 1010 has an aortic wall with a diameter of about 10 mm, scaffold 1012 has an aortic wall with a diameter of about 15 mm, scaffold 1014 has an aortic wall with a diameter of about 20 mm, and scaffold 1016 has an aortic wall with a diameter of about 25 mm. The respective mandrels (110a, 112a, 114a, and 116a) are also shown.

[0090] Although the embodiments and examples have been directed to an aortic root scaffold, the present disclosure extends to tubular soft tissue scaffolds, such as blood vessels, generally, and is not limited to aortic root scaffolds. EXAMPLES

[0091] Exemplary embodiments are described by way of example only. EXAMPLES

[0092] 1.1 Materials and Methods 1.1.1 Rationality of material selection and scaffolding design PCL is selected as a candidate for this application due to its slow degradation profile, which allows the scaffold to secrete ECM proteins and provide the necessary time for tissue to develop before it degrades and loses mechanical integrity. The biocompatibility of this polymer and the relatively inexpensive manufacturing route provide a promising basis for HVTE applications. In addition to material properties, fiber alignment, porosity, fiber diameter, and hierarchical microstructure are factors that contribute to the anisotropic mechanical properties as well as the biological activities of the scaffold, such as cell adhesion, invasion, differentiation, and ECM generation. These factors need to be carefully considered in the design and fabrication of scaffolds for heart valve tissue engineering. Leveraging the capabilities of melt electrowriting (MEW), scaffolds with controlled and predefined structure, porosity, and fiber diameter can be designed and fabricated to the location of the aortic heart valve. To this end, biologically inspired electrospun fibers have been designed to mimic the biological architecture that allows for the deposition of extracellular matrix (ECM), recapitulating the composition, dimensions, and mechanical properties of native aortic valve leaflets, and mimicking the wavy orientation of collagen fibers found in the ventricular layer.

[0093] 1.1.2 Fabrication of biomimetic scaffolds Biologically inspired scaffolds are fabricated by indoor melt electrowriting (MEW) as shown diagrammatically in Figure 12. MEW is a new scaffold fabrication technique that allows the fabrication of solvent-free scaffolds by combining the principles of electrospinning and additive manufacturing. In this process, medical grade PCL pellets (Purasorb® PC12, Purac Biomaterials, The Netherlands) were heated to 75 and 85 °C in a plastic syringe (source information). An air pressure of 2.0 bar forces the melt polymer into a 23 G needle, and a high voltage of 6-6.5 kV attracts the fibers onto a laterally translating aluminum collector. The needle was initially kept at a distance of 7 mm from the collector, but this was shortened to 4 mm for samples tested under dynamic conditions. This is because melt electrowriting at a lower needle distance allows for a higher accuracy of deposition. When the needle was kept at 4 mm from the collector, the stage was moved at 280 mm / min. This is because electrowriting with a smaller gap and slower collection speed allows for greater deposition accuracy, in comparison to previous studies.All fiber networks (80 mm × 20 mm × 0.5 mm) were cut into (20 mm × 10 mm) samples using a laser cutting machine (ILS12.75, Universal Laser Systems, Inc., USA) at 80 W for mechanical characterization, imaging, and cell seeding.

[0094] 1.1.3 Morphological characterization by imaging techniques The morphological properties of the scaffolds were analyzed by scanning electron microscopy (SEM, JSM, 7001f, JEOL Ltd., Japan). The PCL melt-electrospun samples were gold sputter coated (JEOL Fine Sputter Coater) for 150 s at 10 mA before imaging, and the observations were performed under 32 mm working distance, 10 kV, and vacuum conditions. The overall appearance, fiber stacking, and melting point are considered in the imaging process, as they are determining factors of the printing quality. A stereomicroscope (Leica M125, Leica Microsystems, Germany) was used to evaluate the fiber diameter and fiber alignment throughout the process of printing optimization (n=20).

[0095] 1.1.3 Characterization of mechanical properties Uniaxial tensile tests were performed on all groups of scaffolds using an Instron Micro Tester equipped with a 500N load cell (5848, Instron, Australia). Samples (n=5) were circumferentially clamped with pneumatic clamps and suspended in air at room temperature. A tensile strain of 100% of the scaffold height was applied at a strain rate of 0.1mm / s and stress / strain curves were plotted to characterize the effects of pore seizure, number of layers, and degree of curvature. The linear modulus, tangent modulus, and high tensile modulus of all samples were calculated from the slope of the stress / strain curves at the initial linear region (0-5%), transition region (15-20%), and steepest region of the curve (20-30%), respectively. The maximum stress at the peak point was recorded and expressed as ultimate tensile stress (UTS) and compared to the maximum stress at failure of native aortic valve leaflets. The scaffolds that best represented the mechanical properties of native aortic valve leaflets were then selected for further mechanical testing. To measure the anisotropy ratio of the scaffolds, samples were laser cut (20 mm x 10 mm) in the radial direction (representative shown in Figure 5). The group that best mimicked the anisotropy of native leaflet tissue was plotted in a stress / strain curve and selected for thorough dynamic mechanical testing, including stepwise stress relaxation, fatigue, and hysteresis tests performed on samples submerged in phosphate-buffered saline (PBS) at physiological conditions (37 °C).

[0096] Stepwise stress relaxation tests were performed to evaluate the behavior of selected PCL melt electrospun scaffolds under equilibrium conditions. Samples were subjected to 10% ramp tensile extension steps at a strain rate of 0.1 mm / s, held constant for 15 min between each step. Although stress relaxation behavior was observed beyond the 15 min relaxation period, a threshold value of 0.0001 N was initially defined to identify the relaxation period for the stress relaxation tests. The equilibrium modulus was calculated from the slope of the plotted stress / strain curve from the stress relaxation tests.

[0097] Mechanical fatigue is of great importance in the context of valve biomechanics due to the repetitive stresses applied during the systolic and diastolic cardiovascular cycle. Fatigue properties were investigated in a uniaxial tensile test setup where samples were subjected to a sinusoidal tensile strain of 10% amplitude and 1 Hertz frequency for 500 repeated cycles. The frequency and amplitude used for this fatigue test perfectly reproduce the cardiovascular loading conditions when a tensile force is applied at 70 beats / min (corresponding to 1 Hz) and the aortic valve leaflets stretch to 10% of their initial length. To measure the stiffness degradation of the scaffold under fatigue conditions, the stiffness of the scaffold was reported for the first cycle and every 100 cycles. Furthermore, to characterize the tendency of this electrospun scaffold to degrade, the stiffness of the scaffold was reported with respect to the number of force cycles applied to the scaffold.

[0098] Other important viscoelastic properties, hysteresis and recovery, were investigated by Anssari-Benam et al. 2 The viscoelastic properties are characterized to be compared to those of porcine aortic valve leaflets published by. Hysteresis tests are performed with 5% cycles of incremental loading and unloading up to 40% of the initial length. The sample is first loaded to 5% of its initial length at a strain rate of 0.1 mm / min and then returned to the starting point. This is then repeated by stretching the sample to 10%, and repeated continuously to identify the point where significant energy dissipation is observed and the scaffold is unable to fully recover its initial length.

[0099] 1.1.4 Clinical Biological Features 1.1.4.1 Cell isolation and culture Human umbilical vein smooth muscle cells (HUVSMCs) were isolated from umbilical cords kindly provided by the Department of Gynecology at the Aachen University Hospital, following human subjects approval from the ethical committee (EK2067). HUVSMCs were isolated by stripping the umbilical cord, removing any remaining adherent connective tissue, cutting into 1 mm tissue rings, and placing them in cell culture flasks. The growth of HUVSMCs from the tissue rings on tissue culture plastic (TCP) was observed after 1–2 weeks. HUVSMCs were cultured in Dulbecco's modified Eagle's medium (DMEM; Gibco) supplemented with 10% fetal calf serum (FCS; Gibco) at 5% CO2 and 95% humidity at 37 °C to a cell area coverage of 80% to 90% and then passaged. Cells between passages 5–7 were used for seeding MEW scaffolds. Before seeding, cell phenotype was verified by immunocytochemical staining for alpha-smooth muscle actin (a-SMA) and von Willebrand factor (vWF). Here, cells need to be positive for a-SMA and negative for vWF. For this, cells were seeded in 96-well plates, fixed with 3% methanol-free paraformaldehyde (PFA; Roth) in phosphate-buffered saline (PBS; Gibco) for 30 min, and rehydrated with PBS. Nonspecific epitopes were blocked and cell membranes were permeabilized with 5% normal goat serum (Dako) in 0.1% Triton-PBS for 1 h at room temperature. As primary antibodies, HUVSMCs were incubated with mouse anti-a-SMA (A2547; Sigma) diluted 1:400, or rabbit polyclonal anti-human vWf (A0082; Dako) diluted 1:200 for 1 h at 37 °C. Samples were then washed and incubated for 1 h at 37°C with the corresponding secondary antibodies: Alexa Fluor594 goat anti-mouse (A 1 1005; Invitrogen), or Alexa Fluor488 goat anti-rabbit (A 1 1008; Invitrogen), each diluted 1:400.

[0100] Counterstaining was performed with 4',6-diamidino-2-phenylindole (DAPI) nucleic acid stain (Molecular Probes). Stained cell-seeded MEW scaffolds were observed under an epi-illumination microscope (AxioObserver Z1; Carl Zeiss GmbH). Images were captured using a digital camera (AxioCam MRm; Carl Zeiss GmbH).

[0101] 1.1.4.2 Fibrin synthesis Lyophilized fibrinogen (Calbiochem) was dissolved in Milli-Q purified water and dialyzed overnight against Tris-buffered saline (TBS; pH 7.4) using a 6000-8000 molecular weight cut-off membrane (Novodirect). The resulting fibrinogen solution was filter sterilized and the concentration was determined by measuring the absorbance at 280 nm using an Infinite M200 spectrophotometer (Tecan Group Ltd). The fibrin gel component of this construct (5.0 mL total) consisted of 2.5 mL of fibrinogen solution (10 mg / mL) and 5 × 10 7 The culture consisted of 1.75 mL of TBS containing 100 mM umbilical artery SMC / FB cells or AD-MSCs, 0.375 mL of 50 mM CaCl-2 (Sigma) in TBS, and 0.375 mL of 40 U / mL thrombin (Sigma).

[0102] 1.1.4.3 Cell seeding experiments MEW scaffolds were sterilized by immersion in 80% ethanol followed by evaporation in a biosafety cabinet. After complete drying, MEW scaffolds were placed into custom-made silicone (M4641-A; B&G Faserverbundwerkstoffe GmbH) cell seeding molds. HUVSMCs were enzymatically detached from TCP by 0.25% trypsin / 0.02% EDTA solution (Gibco), collected in conical tubes (Sarstedt) and counted using a Neubauer chamber. Cells were centrifuged at 500 × g for 5 min and resuspended in cell culture medium at a concentration of 12.5 million cells / mL medium. Four spots (A = 4 cm) were seeded per scaffold. 2 ) were seeded with 1 million cells in a volume of 80 pL each (a total of 4 million cells per scaffold).

[0103] To embed the MEW scaffolds in fibrin gel, cells were resuspended in the polymerization initiator solution at a concentration of 20 million cells / mL. The mold was filled with the fibrin gel components. Rapid polymerization of fibrinogen ensured uniform cell distribution throughout the graft. The final cell concentration was 10 million cells / mL fibrin gel. The seeded and fibrin-embedded scaffolds were cultured in DMEM supplemented with 10% FCS, 1% antibiotic / antimycotic (ABM; Gibco) and 1 mM L-ascorbic acid 2-phosphate (Sigma) under static conditions at 37°C and 95% humidity for 1 and 2 weeks. The medium was changed every 2–3 days.

[0104] 1.1.4.4 Live / dead staining Cell viability in MEW scaffolds after 1 and 2 weeks was assessed by live-dead (LD) staining using calcein AM and propidium iodide. Calcein was used to stain viable HUVSMCs green, and propidium iodide was used to label dead cells red. Samples were stained for 10 min at 37 °C and then washed with PBS. Stained samples were subsequently observed under a microscope equipped for epi-illumination (AxioObserver Z1; Carl Zeiss GmbH). Images were acquired using a digital camera (AxioCam MRm; Carl Zeiss GmbH).

[0105] 1.1.4.5 Electron microscopy Scanning electron microscopy was performed after both culture periods to investigate cell adhesion and cell coverage and spreading on the MEW scaffolds. Cell-seeded MEW scaffolds were fixed in 3% glutaraldehyde in 0.1 M Sorenson's buffer (pH 7.4) for 1 h at room temperature. They were then washed in sodium phosphate buffer (0.2 M, pH 7.39, Merck) and dehydrated successively in 30%, 50%, 70%, 90% ethanol and three times for 10 min in 100% ethanol. Samples were critical point dried with CO2 and then sputter-coated (Leica EM SC D500) with a 20 nm gold-palladium layer. Images were acquired using an ESEM XL 30FEG microscope (FEI, Philips, Eindhoven, The Netherlands) at an accelerating voltage of 10 kV.

[0106] 1.1.4.6 Immunohistochemistry For immunohistochemical analysis of cell-seeded scaffolds, samples were fixed in 3% PFA without methanol in PBS for 1.5 h at room temperature and then washed with PBS. Fibrin-embedded samples were dehydrated, embedded in paraffin, and sectioned. Nonspecific epitopes were blocked and cell membranes were permeabilized with 5% normal goat serum (NGS; Dako) in 0.1% Triton-PBS for 1 h at room temperature. Seeded scaffolds were incubated with the following primary antibodies for 1 h at 37°C: mouse anti-human a-SMA (A 2547; Sigma) diluted 1:1000, rabbit anti-human collagen type I (R 1038, Acris) diluted 1:300, and rabbit anti-human collagen type III (R 1040, Acris) diluted 1:50. Samples were washed and incubated with the following secondary antibodies for 1 h at room temperature: Samples stained for a-SMA were incubated with Alexa Fluor594 goat anti-mouse (A 11005, Invitrogen) antibody, and samples stained for collagen type I were incubated with Alexa Fluor488 goat anti-rabbit (A 11008, Invitrogen) antibody, both diluted 1:400 for 1 h at 37 °C. Samples stained for collagen type III were incubated with rabbit immunoglobulin / biotinylated (E 0432, Dako) diluted 1:300 for 1 h at 37 °C, followed by streptavidin / TRITC (RA 021, Acris) diluted 1:1000 for 1 h at 37 °C. Native human umbilical cord served as a positive control. For negative controls, samples were incubated with diluent and secondary antibody only.

[0107] Actin staining was performed according to the manufacturer's instructions. PFA-fixed samples were washed with PBS, and cells were permeabilized with 0.1% Triton-PBS for 1 h at room temperature and incubated with 3.5 nM phalloidin in PBS for 1 h at room temperature. All samples were counterstained and images were taken as described above. 1.1.5 Statistical analysis The mechanical properties of all constructs were reported as mean standard deviation. Unpaired T-tests were used to compare scaffolds with variable pore sizes (n = 5), and one-way ANOVA with Tukey's multiple comparison component was utilized to investigate the effects of the number of layers and degree of curvature (n = 3) (GraphPad, Prism 7). Values of p < 0.05 were considered significant, and the levels of significance in all bar graphs were indicated using (p < 0.001****, 0.0001 < p < 0.001***, 0.001 < p < 0.01**, 0.01 < p < 0.05*).

[0108] 1.1.6 Setup of the valve function test Using a custom-made flow loop system, the valve function was evaluated under physiological aortic conditions (flow rate: 5.0 L / min, frequency: 70 bμm, mean aortic pressure: 100 mmHg, 120 - 80 mmHg), and the mean pressure gradient and effective orifice area (EOA) were examined. Pressures were measured using pressure transducers (DPT 6000, manufactured by pvd CODAN Critical Care GmbH) placed immediately adjacent to the inflow and outflow sides of the valve, and the instantaneous inflow to the valve was measured using a flowmeter (sonoTT, manufactured by em-tec GmbH). Next, a LabVIEW application was used as an interface to record the pressure and flow values measured by the pressure transducers and flowmeter. In accordance with the ISO5840-2 guidelines, the pressure difference between the ventricle and aorta and the square root of the mean of the inflow squared were calculated from 10 cycles to determine the mean pressure gradient and EOA.

[0109] 1.2 Results and discussion The structure of the scaffold mimics the collagen fibers found in the fibrous and ventricular layers of the aortic heart valve leaflets, with a 1 mm diameter helical pattern defined as a circumferential fiber laydown pattern (Figure 5, Figure 13). The helically patterned fibers are spaced 0.5 mm and 0.25 mm apart in the circumferential direction to quantify how fiber spacing affects the stiffness of the final construct. Collagen fibers are available at lower densities in combination with the highly crimped elastin fibers in the radial direction of the native leaflets, resulting in anisotropic behavior. Thus, 0.5 mm diameter semicircles are designed with larger spacing (2 and 1 mm) to control and mimic the anisotropy. Additionally, 10, 20, and 30 layers of fibers are stacked to characterize the effect of the number of layers on the tensile properties and their correlation with the native leaflet properties. The functional properties of the native aortic valve are related to the J-shaped stress / strain curve and the strain at which the maximum stress occurs. To reproduce this behavior and control the strain rate at which the stress rise occurs, we control the degree of curvature at which the fibers are deposited and fabricate the scaffold to find the optimal structure according to the properties of the native leaflet.

[0110] 1.2.1 Morphological and biologically inspired scaffold structures The morphology and printing quality of linearly and spirally patterned scaffolds with circumferential fiber spacing of 0.5 and 0.25 mm are illustrated in representative SEM images shown in Figure 4 . Regardless of the scaffold structure, the average fiber diameter was measured to be 19.76 ± 1.54 μm throughout the construct. This fiber diameter is orders of magnitude smaller than scaffolds produced by other melt extrusion techniques such as melt deposition modeling (FDM) and bioextrusion, where fiber diameters are generally greater than 200 μm. The fibers are precisely stacked throughout the stacked layers of all groups of scaffolds, regardless of the fiber structure, curved or straight (Figure 4a, c). Due to static charges accumulated during the MEW process, there are a few fibers that cross across the intended stacking structure in the case of 0.25 mm fiber spacing. In the scaffolds with straight fiber structure, the circumferential and radial fibers are aligned overlapping each other, rather than simply fused. Clear fusion behavior is observed in the case of scaffolds with a helical pattern at 0.5 mm fiber spacing. Proceeding to the dynamic mechanical characterization of the 0.25 mm-spaced helically patterned scaffolds, larger fibers (28.62 ± 0.87 µm) were observed due to the shorter needle-to-collector distance. As a result of this change in MEW parameters, better melt electrowriting quality and superior mechanical properties were achieved, as will be further described in the dynamic mechanical characterization subsection.

[0111] 1.2.2 Mechanical properties of scaffolds with different pore sizes, number of layers, and degree of curvature Scaffolds fabricated for heart valve tissue engineering applications must be able to withstand mechanical loading conditions as applied in cardiovascular blood flow regimes while simultaneously deforming to allow successful valve opening and closing. Heart valve leaflets are known to exhibit a J-shaped stress-strain curve that determines the optimal function of this soft tissue. Uniaxial tensile tests were performed and showed J-shaped stress / strain curves for all groups of scaffolds, as shown in Figure 6. The helical fibers were first transformed from a semicircular to a linear orientation (Figure 6), allowing for large extension at low applied stresses. This transformation profile results in a curvilinear transition from an initial linear low stress relationship to a steep stress / strain profile until a certain ultimate tensile stress is reached. This property is similar to that of native aortic valve tissue, where the wavy and interconnected collagen fibers throughout the tissue first unravel by twisting and bending, and then change from a helical pattern to straight fibers, resulting in a tangential increase in stiffness, as shown in Figure 6. Therefore, the tensile modulus calculated for a J-shaped stress / strain curve needs to be analyzed with respect to the specific strain levels identified during the course of the displacement.

[0112] Fiber spacing was found to have a significant effect on stiffness, with halving the pore dimensions of the scaffolds nearly doubling the UTS from 0.55 ± 0.040 MPa to 0.93 MPa ± 0.029. This significant increase was due to the high tensile modulus values ​​(E HTM、0.5mm = 3.07 ± 0.23 MPa, E HTM、0.25mm = 4.87 ± 0.094 MPa), but the increase in tangential and linear moduli was less significant. This behavior is explained by the identical curvature pattern used to fabricate both scaffolds, resulting in similar deformation behavior but different values ​​of high tensile and ultimate tensile moduli (Figure 7 and Figure 6d). On the other hand, when the effect of the scaffold yield strength was normalized by the increment in scaffold thickness, the number of layers stacked in the MEW process only had a small effect on the tensile modulus regardless of the pore dimensions (Figure 6a). However, as observed in the SEM images shown in Figure 4, the strain at which the maximum stress occurs is lowered by stacking more layers, since the PCL fibers are deposited with a smaller curvature in the higher layers.

[0113] To mimic the J-shaped stress / strain behavior of native aortic valve leaflets, it is important to tune the value of the strain exerting the ultimate tensile stress (strain to UTS). Increasing the curvature of the designed helical pattern by 0.1 mm increases the strain exerting the UTS from 23% to 47% of the initial specimen length. Such a two-fold increase was also observed by doubling the scaffold length by adding 0.1 mm to increase the curvature while maintaining the J-shaped behavior. This behavior is consistent with the fact that scaffolds with higher curvature require more elongation compared to the control group to straighten initially curved like scaffold constructs. Furthermore, a notable decrease in tangent modulus for the more curved patterns was observed, supporting the change in the curvilinear transition from straight to high tensile modulus caused by the degree of curvature (Figure 7). Although fabricated with similar MEW parameters, a slight decrease in UTS is also observed for the highly curved scaffolds due to the reduced fiber diameter of the highly curved fibers.

[0114] In addition to the J-shaped stress / strain behavior of the aortic valve leaflets, the anisotropy enhances stretchability in the radial direction rather than the circumferential direction. Therefore, larger pore dimensions have been designed in the radial (1 and 2 mm) direction of the scaffold to adjust the anisotropy ratio. A pore size of 1 mm results in greater elasticity with a UTS of 2.56 ± 0.15 times and a yield strength 9.06 ± 0.73 times smaller in the radial direction than 0.25 of the circumferential pore size. Increasing the radial pore size to 2 mm doubles this ratio. The anisotropy ratio can be modified depending on the level of anisotropy required for all heart valve leaflets, regardless of their location.

[0115] To mimic the mechanical properties of this highly complex tissue, the optimal structure, pore dimensions, scaffold thickness, and degree of curvature must be selected for the scaffold. For this purpose, fiber spacings of 0.25 mm and 2 mm were selected in the circumferential and radial directions, respectively. As shown in Figure 11c, the J-shaped stress / strain behavior exhibited by this melt electrospun soft tissue scaffold resembles that of native valve leaflets of different sources. Importantly, the high tensile modulus values ​​of porcine and ovine leaflets were fully mimicked by our scaffolds, even more so than in bioreactor conditioning (Figure 8(d)). The mechanical properties of the melt electrospun scaffolds were almost comparable to those of human aortic valve leaflets when compared to the results published by Missirlis. 3 It is still expected that upon cell seeding and dynamic conditioning of this scaffold, an increase in tensile modulus may be observed as a result of ECM protein deposition throughout the construct, as reported in other studies.

[0116] To fully mimic the mechanical properties of this highly complex tissue, the scaffold requires the selection of optimal architecture, pore size, scaffold thickness, degree of curvature, and pore size. 1.2.3 Stress relaxation Stress relaxation is noted as a key property regulating cell-ECM interactions for mechanosensitive cell types that should be considered when fabricating scaffolds as cell culture platforms. Altering the viscoelastic behavior of biomaterials has been shown to affect cell behavior independent of stiffness, as cells sense a decrease in substrate stiffness. Therefore, stress relaxation tests were performed to evaluate the viscoelastic behavior by stretching the scaffolds at 10% of the tensile strain ramp and allowing the scaffolds to relax for 15 min at each cycle (Figure 9). The melt electrospun scaffolds exhibited stress relaxation properties where the relaxation behavior was more pronounced at higher strain rates. A rapid relaxation was observed initially, followed by a slower rate of relaxation at all strain levels. When the scaffolds were stretched by 10%, a relaxation of 30% was observed, which increased to 44% with increasing strain values ​​of stretching. The mechanical response of the melt electrospun scaffolds was similar to the relaxation behavior of native aortic valve leaflets, reported by Stella et al. to be 27.5 ± 0.77% in a biaxial setup. The stress relaxation values ​​reported for native valve leaflets correlate with the stress relaxation behavior of melt electrospun scaffolds at a strain rate of 10%, which is how much aortic valve leaflets stretch at physiological blood pressure. This similarity in stress relaxation provides a native-like environment for seeded cells, facilitating mechanical stimulation over an appropriate set of loading conditions.

[0117] 1.2.4 Fatigue Mechanical fatigue plays an important role in valve biomechanics, as the valve is subjected to a combination of shear, flexure, and extension loading conditions. The aortic heart valve is located in a very demanding physiological condition where repetitive cyclic stresses are applied during its function. Despite the importance of fatigue properties, there is very limited information on the fatigue behavior of native heart valves as well as fabricated scaffolds for the purpose of heart valve tissue engineering. Cyclic uniaxial tensile tests were performed on the fabricated MEW scaffolds, subject to cardiovascular loading conditions in both circumferential and radial directions. A J-shaped stress / strain behavior was observed in both test directions similar to the native aortic valve leaflets, with the circumferential direction being 8 times stiffer than the radial direction, further confirming the anisotropic nature of the melt electrospun scaffolds (Figure 10). When a force is repeatedly applied to the scaffold for 500 cycles, the stiffness decreases by 19% in the circumferential direction and 20% in the radial direction, and the rate of this decrease decreases after approximately 70 cycles of conditioning.

[0118] A logarithmic equation was then fitted to this graph to predict the fatigue properties of the scaffold after 60 million cycles, which corresponds to 2 years of valve function. It is calculated that the stiffness of the scaffold will decrease by 47% and 62% when tested in the circumferential and radial directions, respectively. Most importantly, the stiffness of the scaffold after 2 years of function, 41.1 kPa, is far greater than the transvalvular pressure applied to the aortic heart valve leaflets (80 mmHg, which corresponds to 10.7 kPa).

[0119] 1.2.5 Hysteresis and recovery Viscous effects in aortic valve leaflets and their correlation with elasticity remain largely unknown for both tissue and tissue engineered heart valves, despite their importance to the functional properties of the valve. To further characterize the viscoelastic properties of the melt electrospun scaffold, hysteresis tests were performed by loading and unloading the scaffold in both circumferential and radial directions, and the elasticity of this construct was characterized by measuring the energy dissipation at various strain levels. The area under the stress / strain hysteresis loading curve up to a given strain level is essentially the energy used to stretch the scaffold to a specified extent.

[0120] Similarly, the area under the unloading curve represents the recovery of its stored energy by returning the scaffold to its original length. The difference between these two values ​​is the dissipation of this strain energy, which, if large, has previously been shown to irreversibly stretch the specimen. As shown in Figure 11, J-shaped stress / strain curves were observed in both test directions, with all strain levels further highlighting the J-shaped behavior of the fabricated scaffolds. However, linear deformation behavior was identified starting from the fourth cycle in the circumferential direction (15%) and the fifth cycle in the radial direction of the test (20%), which was previously shown as an indication of plastic deformation. The linear stress / strain behavior was associated with a sudden decrease in the unloading / loading scaffold area at the same strain levels, further highlighting the onset of plastic deformation at these strain levels. A similar phenomenon was observed by Ansar-Benam et al. for aortic valve leaflet tissue. 2 reported that the natural valve leaflets behave mechanically and quantitatively similarly.

[0121] 1.2.6 Evaluation of the biological activity of the scaffolds Since PCL MEW scaffolds are hydrophobic after fabrication, we first plasma treated the scaffolds with O2 / Ar2 plasma to render the surface hydrophilic. We then evaluated the ability of the scaffolds to support human umbilical vein smooth muscle cell (HUVSMC) growth, proliferation, and extracellular matrix deposition. HUVSMCs were selected because they have been shown to be appropriate for cardiovascular tissue engineering and clinically relevant for a pediatric population that may greatly benefit from tissue engineered heart valves by avoiding repeated surgeries to accommodate somatic cell growth. HUVSMCs were seeded in two different configurations: i) directly seeded on the surface of the scaffold and ii) encapsulated in fibrin and synthesized in a molding process, completely embedding the scaffold in the fibrin gel containing the cells. In both cases, the constructs were maintained in static culture for 1 and 2 weeks.

[0122] Figure 32 shows the results of the direct seeding approach. The high cell viability shown by the live / dead staining assay (Figure 32c) indicates the suitability of the PCL melt-electrowritten scaffolds for cells to colonize. After one week of culture, a small number of pores were filled by cells in the meandering patterned scaffolds, but not in the straight fiber scaffolds. This may be due to the larger surface area provided by the curved fibers, which promotes cell attachment and further colonization. Over the following week, the pores in all scaffold configurations were completely filled (Figure 32b), and the number of dead cells remained low (Figure 32c). Immunohistochemical analysis revealed the synthesis of collagen types I and III, two major components of native heart valve leaflets.

[0123] Next, MEW scaffolds were embedded in HUVSMC-laden fibrin gels to generate hybrid constructs taking advantage of both the mechanical properties provided by the fiber phase and the biomimetic microstructure, resulting in the increased extracellular matrix typically observed for cell-laden fibrin. The embedding process resulted in homogeneously embedded MEW scaffolds without exposure of PCL fibers (Figures 12a and 12b) or negative effects on HUVSMC viability (Figure 12c). Collagen I and III extracellular matrix deposition was confirmed by immunohistochemistry (Figure 12d). Remodeling of the hybrid constructs during 2 weeks of culture did not result in tissue contraction due to the mechanical support provided by the fibers, whereas the control fibrin gels contracted significantly already within the first week (Figures 12aii and 12aiv). Cell-mediated tissue contraction leads to insufficient valve closure, resulting in leaflet shortening. This well-known phenomenon is a major drawback that threatens the entire concept of engineering functional tissues both in vitro and in vivo.

[0124] 1.2.7 Valve Function Finally, as a proof of principle, we investigated the suitability of the MEW scaffold to be molded into a trileaflet valve and its potential to withstand the harsh hemodynamic conditions in the aortic position in a custom-made flow loop system. Another major issue is the insufficient mechanical properties of tissue engineered heart valves, as most valves are implanted in a low pressure circulation as pulmonary prostheses. MEW scaffolds were embedded in fibrin and sutured as single leaflets to a 2.2 cm diameter silicone model of the aortic root featuring the sinuses of Valsalva (Figure 14), resulting in valves with a diameter of 2.2 cm. These valves were tested in a mock circulatory system under physiological aortic pressure and flow conditions as indicated by ISO5840, demonstrating a mean transvalvular pressure drop of 2.45 ± 0.36 mmHg and a mean transvalvular pressure drop of 3.3 cm. 2 It showed good hydrodynamic performance with an EOA of ±0.26, which meets the ISO requirements for a 2.2 cm diameter valve (see Figure 16). This indicates that the scaffold has sufficient strength to withstand systemic conditions and at the same time has sufficient bending stiffness to avoid stenotic behavior. How to determine the bending stiffness is tentatively developed or reported along with the protocol based on standards for fiber characterization but subject to technical or conceptual limitations. Thus, in this study the influence of layers on the bending behavior of the scaffold was qualitatively shown to evaluate the proper bending behavior of the valve in a custom-made flow loop. Frames extracted from the high-speed video display full closure and unobstructed opening of the valve leaflets during a simulated cardiac cycle (Figure 15). The hydrodynamic evaluation also demonstrated that the suture retention properties and the valve were not dependent on any rigid stent structure to withstand physiological loads. It is important to note that the performance of the proof-of-principle valve was achieved with an acellular fibrin layer and dynamic stimulation of the cell-laden construct is expected to further improve the mechanical properties of the fibrin. Due to the slow degradation rate of PCL, it is expected that during the first in vivo phase (18 months), the MEW scaffold will support in situ tissue formation to ensure its further development into a functional and mechanically adequate valve upon subsequent scaffold degradation. EXAMPLES

[0125] 2.1 Materials and Methods 2.1.1 3D printing of the aortic root model To facilitate the manufacturing process of the personalized scaffold, instead of physically fabricating the mandrel from a conductive metal, rapid prototyping using a fused deposition modeling (FDM) 3D printer is chosen to create a mold (mandrel) that is subsequently electrospun. The mold of the aortic root was fabricated by depositing PLA fibers (Bilby 3d, Australia) from a 0.2 mm nozzle on a translating collector (1000 mm / min) kept at 90 degrees to allow good mounting of the model (Wombat Drafter, Australia). The obtained model was of high quality with a smooth surface and the dimensions were in harmony with the modeled part. However, the electrical conductivity of the collector is a fundamental requirement in the process of melt electrowriting, an element that is missing in materials commonly used for FDM 3D printing. Therefore, a conductive layer of copper was deposited on the surface of the model by physical vapor deposition sputtering (PVDS). PVDS coating was performed by placing the model in a vacuum chamber (5.1 E-7 Torr) for 2000 seconds at a theoretical rate of 8.946 A and 200 Watts per second, and this coating protocol resulted in the model being completely coated (Figure 23c). An alternative to PVDS coating is to use a conductive polymer filament that can be used to print the desired model in 3D. A conductive PLA / graphene composite (Proto pasta) was used to fabricate the model (Makerbot, Replicator2×, Australia). The nominal volume resistivity of this composite is reported to be 15 ohm-cm throughout the layer. The filament was melted at 210°C and deposited on a translating collector moving at 1000 mm / min, yielding a smooth aortic root mold including the sinuses of Valsalva. The latter approach was found to be more suitable for this application, as it eliminates the need for post-treatment coatings and expedites the process one step further. The model is used as a mandrel for MEW to form a 3D scaffold.

[0126] 2.1.2 MEW of personalized tubular scaffolds replicating the macroscopic geometry of the aortic root A custom-made MEW tubular collector was used to fabricate melt-electrowritten scaffolds replicating the macroscopic geometry of the aortic root, including the sinuses of Valsalva. In this process, medical-grade PCL pellets (Purasorb® PC12, Purac Biomaterials, The Netherlands) are heated to 80 °C or 92 °C in a plastic syringe. Air pressure of 2.0 bar forces the molten polymer into a 23 G needle, and a high voltage of 10.5-11.0 kV pulls the fiber down into a rotating mandrel collector while the mandrel is moved transversely in the x-axis. The needle was kept 10.5 mm from the mandrel wall and positioned 7.5 mm from the highest point of the sinus while other MEW parameters were held constant. A symmetric aluminum tube 1 In the case of , different combinations of rotational and translational speeds can be utilized to achieve the desired wrapping angle. However, there is no literature study on MEW on asymmetric models made of polymers. Furthermore, MEW was performed on a new mandrel-collector assembly where the established parameters did not comply with this construct. Although similar principles were used to establish the relationship between rotational and translational speed combinations and wrapping angle for this new collector, the MEW parameters had to be optimized to comply with the new collector setup, geometry, and conductivity values ​​for the polymer.

[0127] First, the programmed rotational speed of the motor is not equal to the effective rotational speed of the mandrel collector due to losses caused by the pulley system, so the effective rotational speed of the motor was measured experimentally. As expected, a linear relationship is found between the set spindle speed and the mandrel rotational speed. This ratio is used to calculate the tangential speed, which is related to the diameter of the 3D printed model across the wall and sinus of Valsalva. The fiber wrap angle is controlled by maintaining a constant translation speed (1000 mm / min) while varying the rotational speed of the mandrel. Another important factor to consider is the effect of the polymer jet lag on the actual deposition length, as opposed to the programmed tube length. This ratio is used to identify the effective collector translation, which directly affects the actual fiber wrap angle, which was previously established in our group. The fiber wrap angle is controlled by maintaining a constant effective translation speed (1000 mm / min) while varying the rotational speed of the mandrel (Table 1). The fibers in the aortic root are programmed to align at 30°, 45°, and 60° to the axis of the mandrel. At the sinus of Valsalva, higher wrapping angles are expected to be achieved due to the increased tangential velocity in this region. The voltage applied between the needle and the rotating mandrel was slightly increased (0.2 kV) for the 45° and 60° scaffolds due to the additional pulling force exerted by the increased rotational speed of the mandrel.

[0128] 2.1.3 Morphological characterization The morphological properties of the tubular MEW scaffolds were analyzed to evaluate the effectiveness of this process in producing scaffolds with different wrapping angles and fiber diameters. The specimens were divided into eight sections and random points on three replicates of each segment were imaged under an optical microscope (Axio Lab A1, ZEISS) to examine the effect of varying the collector to needle distance on the images (Figure 27). The segments were named accordingly where the ascending aorta is essentially the top part of the scaffold and the left ventricle is referred to as the bottom of the scaffold. Each sample was placed between two microscope glass slides to flatten the scaffold pieces and allow for more consistency across the entire section. In total, 81 images were obtained for all independent scaffold wrapping angles and the images were exported into image analysis software (Image J) to measure fiber diameter and wrapping angle. The data obtained was then statistically analyzed and plotted using Minitab18 to quantitatively evaluate the consistency of printing across all samples while comparing wrapping angles and fiber diameters between different groups.

[0129] 2.2 Results and Discussion Scaffolds were successfully fabricated with good qualitative finish, with consistent surface thickness throughout the construct. Microscopic images shown in Figure 27 show the difference in winding angles in pre-programmed scaffolds of 30, 45, and 60°, as well as visually highlighting the sinuses for individual scaffolds. Clearly discernible variations in fiber winding angle directly generate anisotropic properties, as reported for tubular melt-electrowritten scaffolds [Biointerphases 7, 1-16 (2012)].

[0130] The illustrated qualitative analysis was obtained by measuring and statistically evaluating the fiber wrap angles across all samples and replicates for the aortic root and sinuses, as shown in Figure 31a. The deposited melt electrowritten fiber wrap angles across all scaffold groups are nearly the same for the preprogrammed 30, 45 and 60° configuration angles. These have been calculated using the formulas listed in the experimental protocol. All calculations were performed to predict and predefine the fiber wrap angles across the aortic wall. For the 30, 45 and 60° configurations, the fibers were wrapped at 29.25 ± 3.08°, 45.22 ± 4.96° and 56.55 ± 2.14°, validating the effectiveness of this method of predefining the fiber wrap angles. As all printing parameters were kept constant throughout the melt electrowriting process, higher wrap angles were observed across the sinuses for all groups of scaffolds (Figure 31b). The fiber wrap angle across the sinus was consistently 4.5 degrees greater than the angle measured at the wall for all configurations. One-way ANOVA and post-hoc Tukey multiple comparison statistical tests were performed across all of the scaffold configurations to ensure statistical significance of the aforementioned relationship. As shown in Figure 31, the wrap angles across the wall and sinus for all groups of scaffolds are significantly different according to the multiple comparison tests performed. The smaller the needle-to-collector distance, the higher the effective tangential velocity at the sinus and the greater the fiber wrap angle in this region. In fact, the established relationship between tangential velocity and fiber wrap angle allowed for prediction of fiber wrap angle across the height gradient seen in the sinuses of Valsalva. These data correlate well with the mechanical properties of native aortic valve sinuses, as studies have found that the sinuses of the aortic root are more mechanically robust compared to aortic wall tissue.

[0131] In addition to the wrapping angle, fiber diameter was measured across the walls and sinuses of all three scaffold configurations. The inverse relationship between fiber diameter and the configured wrapping angle is clearly shown in Figure 31b. The higher mandrel rotation speed of the 60° scaffold produces a greater stretching effect on the deposited fibers compared to the 30° and 45° scaffolds. This phenomenon leads to a decrease in fiber diameter from 20.24 ± 1.59 mm for the 30° scaffold to 18.03 ± 1.38 mm and 14.84 ± 1.63 mm for the 45° and 60° scaffolds, respectively. Furthermore, Figure 31c confirms the effect of variable needle-to-collector distance on the jet pulse. Fibers deposited on the sinuses were shown to be clearly larger in diameter by an average of 4.3 μm compared to the corresponding scaffold walls. Tukey's multiple comparison statistical test authenticated the statistical difference between fiber diameters across the walls and sinuses for all three groups of scaffolds.

[0132] Finally, a hierarchical tri-layered and multi-scale scaffold was successfully fabricated with ideal surface finish, as shown in Figure 28. Further mechanical and morphological characterization is performed on the tri-layered scaffold to evaluate the mechanical effectiveness of this construct for the aortic root location. The design and manufacturing methodology utilized was successful in producing a scaffold that resembled the geometric dimensions of the aortic root. This exemplary embodiment aimed to control the wrapping angle of the PCL fibers while conforming to a prefabricated mold (i.e., mandrel) that replicates the shape of the aortic valve, including the sinuses of Valsalva.

[0133] The mathematical relationship between the fiber wrapping angle and the combination of the collector translation speed and the mandrel rotation speed was verified by fabricating melt-electrowritten scaffolds on a 3D printed conductive mold according to Eqs. 1–4. Formulas 1~4: TIFF0007628307000002.tif65137

[0134] In the sinus of Valsalva, higher wrapping angles and fiber diameters were achieved due to the shorter needle-to-collector distance in this region. Furthermore, higher wrapping angles were found to decrease fiber diameter because a higher mandrel rotation speed must be used to achieve that wrapping angle. Anisotropic mechanical properties are expected for this tubular MEW scaffold, as a smaller wrapping angle is hypothesized to be associated with higher axial stiffness. On the other hand, a larger wrapping angle is expected to result in higher circumferential compliance.

[0135] The heart valve leaflets and aortic root melt-electrospun scaffolds are integrated to fabricate the entire valve conduit. The mechanical and morphological properties of the flat tubular personalized scaffolds are optimized towards those of the aortic heart valve leaflets and aortic root, respectively. However, these scaffolds are fabricated by different collector (i.e., mandrel) settings, so it is not possible to fabricate both scaffolds in one step. To fabricate a scaffold for the aortic heart valve location while mimicking the valve dimensions and design, the flat scaffold can be incorporated into a tubular aortic root scaffold. Alternatively, a multi-step design and manufacturing framework can be used to incorporate the leaflet scaffold into the tubular aortic root scaffold (e.g., Figure 25).

[0136] The pre-established optimal flat melt electrospun scaffold is laser cut (laser cutting device) to the dimensions of the valve leaflets and wrapped around the 3D printed model. Localized heating of the scaffold at the commissure points creates three fusion points that conform the scaffold to a concave profile, allowing for the coaptation found in native aortic valve leaflets (Figure 25b). An aluminum mandrel collector was then used to hold these two mandrels together for the tubular MEW fabrication process. The sinuses of Valsalva act as a shielding mandrel to block fiber deposition from the electrowinding step that forms the valve leaflet scaffold.

[0137] Tubular melt electrospun scaffolds were successfully fabricated in a two-piece model with a flat leaflet scaffold within a tube. The leaflets were seamlessly attached inside the tubular scaffold mainly at the aortic root seam and inter-leaflet triangle regions. However, the attachment points seem to be weak as they were limited only to the top layer of the flat part and the first layer of the tubular scaffold. To improve the fusion points, the tubular scaffold was fabricated at a higher temperature (92 °C) and rotation speed where the attachment seemed relatively stronger compared to previous MEW parameters. Reinforcement techniques may be required to ensure the functionality of the aortic valve scaffold under cardiovascular conditions. Reinforcement of these attachment points can be done through the MEW fabrication process or as a post-processing step after the completion of tubular melt electrospun.

[0138] In the following claims and the foregoing description, unless the context requires otherwise, either by express wording or necessary implication, the word "comprise" or variations such as "comprises" or "comprising" are used in an inclusive sense, i.e., to specify the presence of stated features, but not to exclude the presence or addition of further features in various embodiments of the scaffolds and methods.

[0139] It will be apparent to those skilled in the art that many modifications can be made without departing from the spirit and scope of the disclosure.

Claims

1. a body having a first region comprising a first set of fibers and a second set of fibers; the first region is anisotropic; the first set of fibers are aligned substantially parallel to one another; each fiber of the first set of fibers has a serpentine structure with peaks and troughs formed therein; the first set of fibers has a first Young's modulus; the second set of fibers are aligned substantially parallel to one another; the second set of fibers is aligned transversely to the first set of fibers; each fiber of the second set of fibers has a serpentine structure with peaks and troughs formed therein; the second set of fibers has a second Young's modulus; in the first region, one or more fibers of the second set of fibers connect adjacent fibers of the first set of fibers; The first Young's modulus is not equal to the second Young's modulus. A melt-electrowritten soft tissue scaffold for cardiovascular tissue, comprising:

2. the second Young's modulus is at least twice the Young's modulus of the first set of fibers; 2. The scaffolding of claim 1.

3. a path length of the fibers of the first set of fibers over a predefined distance is not equal to a path length of the fibers of the second set of fibers over the predefined distance; 3. A scaffold according to claim 1 or 2.

4. Increasing the path length of the fibers of the first fiber set relative to the path length of the fibers of the second fiber set increases the anisotropy ratio of the first fiber set to the second fiber set.

4. The scaffolding of claim 3.

5. the fibers of the first set of fibers are spaced a first distance apart; each fiber in the second set of fibers is spaced a second distance apart; A scaffold according to any one of claims 1 to 4.

6. the first distance is in the range of about 0.1 mm to about 2.5 mm; 6. A scaffolding as claimed in claim 5.

7. the second distance is not equal to the first distance; 7. A scaffold according to claim 5 or 6.

8. the first distance being about 1 to 10 times the second distance; A scaffold according to any one of claims 5 to 7.

9. the first set of fibers has a Young's modulus in the range of about 1 kPa to about 10 MPa, e.g., 1 MPa; A scaffold according to any one of claims 1 to 8.

10. the second set of fibers has a Young's modulus in the range of about 1 kPa to about 10 MPa, e.g., 5 MPa; A scaffold according to any one of claims 1 to 9.

11. the second set of fibers being about 5 to 10 times stiffer than the first set of fibers; A scaffold according to any one of claims 1 to 10.

12. the first fiber set and the second fiber set form a first layered structure; A scaffold according to any one of claims 1 to 11.

13. Containing a plurality of layered structures, 13. A scaffolding as claimed in claim 12.

14. the fibers of the first fiber set are interwoven with the fibers of the second fiber set; A scaffold according to any one of claims 1 to 13.

15. the body includes a second region extending from the first region; the second region supports the first region; A scaffold according to any one of claims 1 to 14.

16. the second region is a mesh having fibers aligned in a first direction and a second direction; the first and second directions are transverse to each other; 16. The scaffolding of claim 15.

17. Further comprising an intermediate region located at a boundary between the first region and the second region, the intermediate region comprising a plurality of fibers; 17. A scaffold according to claim 15 or 16.

18. the first region is semicircular; the second region extends from a curved side of the first region, the straight side of the first region forming an edge of the scaffold; A scaffold according to any one of claims 15 to 17.

19. the first region includes a plurality of semicircular regions; The vertices of adjacent semicircles are spaced close to each other, 20. The scaffolding of claim 18.

20. The intermediate region is disposed along the curved side.

20. A scaffolding according to claim 18 or 19 when according to claim 17.

21. the intermediate region includes a first set of concentric semicircular fibers arranged parallel to one another and a second set of fibers connecting adjacent concentric semicircular fibers; 21. The scaffolding of claim 20.

22. The first region and the second region are integrated. A scaffold according to any one of claims 15 to 21.

23. the first and second sets of fibers from the first region are formed from polycaprolactone; 23. A scaffold according to any one of claims 1 to 22.

24. the fibers of the first and / or second fiber sets in the first region have diameters in the range of about 100 nm to about 100 μm; 24. A scaffold according to any one of claims 1 to 23.

25. the first region forms a portion of a heart valve leaflet scaffold; the first set of fibers being generally oriented in a radial direction of the heart valve leaflets; the second set of fibers being generally oriented circumferentially about the heart valve leaflets.

25. A scaffold according to any one of claims 1 to 24.

26. Further, the composition includes a hydrogel. At least a portion of the first region is embedded in the hydrogel.

26. A scaffold according to any one of claims 1 to 25.

27. comprising a planar region and / or a tubular region; 27. A scaffold according to any one of claims 1 to 26.

28. The cardiovascular tissue is a heart valve.

28. A scaffold according to any one of claims 1 to 27.

29. extruding a polymer melt through a nozzle to form a fiber; depositing the fibers to form a body having a first region that is anisotropic; the first region includes a first set of fibers aligned substantially parallel to one another; each fiber of the first set of fibers has a serpentine structure formed with peaks and troughs; a second set of fibers aligned substantially parallel to one another; the second set of fibers is aligned transversely to the first set of fibers; each fiber of the second set of fibers has a serpentine structure formed with peaks and troughs; in the first region, one or more fibers of the second set of fibers connect adjacent fibers of the first set of fibers; the first set of fibers is deposited such that the first set of fibers has a first Young's modulus; The second set of fibers is deposited such that the second set of fibers has a second Young's modulus. A method for fabricating anisotropic soft tissue scaffolds for cardiovascular tissue using melt electrowriting.

30. the first region is formed such that a path length of fibers of the first set of fibers over a predefined distance is not equal to a path length of fibers of the second set of fibers over the predefined distance; 30. The method of claim 29.

31. the first region, wherein each fiber of the first set of fibers is spaced a first distance apart; the fibers of the second set of fibers being formed to be spaced a second distance apart; 31. The method of claim 29 or 30.

32. the first distance is in the range of about 0.1 mm to about 2.5 mm; 32. The method of claim 31 .

33. the second distance is not equal to the first distance; 33. The method of claim 31 or 32.

34. the first distance being about 1 to 10 times greater than the second distance; The method according to any one of claims 31 to 33.

35. the first and second fiber sets are deposited such that fibers of the first fiber set are interwoven with fibers of the second fiber set; 35. The method according to any one of claims 29 to 34.

36. the first and second sets of fibers are deposited such that they form a layered structure; 36. The method according to any one of claims 29 to 35.

37. depositing fibers to form a second region extending from the first region; the second region includes a mesh having fibers aligned in a first direction and a second direction; the first and second directions are transverse to each other; 37. The method according to any one of claims 29 to 36.

38. depositing fibers to form an intermediate region disposed at an interface between the first region and the second region; the intermediate region comprising a plurality of fibers; 38. The method of claim 37.

39. the first and second sets of fibers of the first region are deposited on a stage; The stage is planar, tubular and / or of a type having three-dimensional features; 39. The method according to any one of claims 29 to 38.

40. the first region is a heart valve leaflet scaffold; the first set of fibers is generally oriented in a radial direction of the heart valve leaflet; the second set of fibers is generally oriented circumferentially about the heart valve leaflets.

40. The method according to any one of claims 29 to 39.

41. the polymer melt comprises polycaprolactone; 41. The method according to any one of claims 29 to 40.

42. forming a hydrogel at least partially embedding the first region.

42. The method according to any one of claims 29 to 41.

43. The cardiovascular tissue is a heart valve.

43. The method according to any one of claims 29 to 42.

Images