Vibrating body and vibration wave motor

Abstract

To improve the drive performance.SOLUTION: A vibrating body 10 is a piezoelectric ceramic made of sodium niobate / potassium metal oxide, and includes an electromechanical conversion element 11 whose relative permittivity temperature characteristic is 500 [ppm / °C] or less in a temperature range of -40°C to 170°C, and a vibration wave is generated by the excitation of the electromechanical conversion element. A vibrating wave motor 1 includes the vibrating body, and a relative moving member 20 having a sliding surface that is in pressure contact with a driving surface 12a of the vibrating body and is relatively moved by the vibrating wave.SELECTED DRAWING: Figure 1

Description

[Technical field]

[0001] The present invention relates to a vibrating body and a vibration wave motor. [Background technology]

[0002] As shown in the following Patent Document 1, a vibration wave motor uses the expansion and contraction of a piezoelectric body to generate a traveling vibration wave (hereinafter, abbreviated as a traveling wave) on the driving surface of an elastic body, and this traveling wave causes an elliptical motion on the driving surface, and a moving element that is in pressure contact with the crest of the elliptical motion is driven. However, Patent Document 1 does not take into consideration the degradation of driving performance caused by the material of the piezoelectric body. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] Special Publication No. 1-17354 Summary of the Invention

[0004] The vibrating body of the first disclosed technology is a piezoelectric ceramic made of sodium potassium niobate metal oxide, and has an electromechanical conversion element whose relative dielectric constant temperature characteristic is 500 ppm / °C or less in absolute value in the temperature range of -40°C to 170°C. Vibration waves are generated by exciting the electromechanical conversion element. The electromechanical transducer element is made of a material having the following chemical formula: (1-C-E) (Li A (Na B K (1-B) ) (1―A) NbO 3 + C Ba(Zr D Ti (1―D) )O 3 + E BiFeO 3 however, 0 <A<0.2、0.4≦B≦0.6、0<C≦0.1、0<D<1.00、0<E<0.02

[0005] The vibrating body of the second disclosed technology is a piezoelectric ceramic made of sodium potassium niobate metal oxide, and has an electromechanical conversion element whose relative dielectric constant temperature characteristic is 390 ppm / ℃ or less in absolute value in the temperature range of 0℃ to 60℃. Vibration waves are generated by exciting the electromechanical conversion element. The electromechanical transducer element is made of a material having the following chemical formula: (1-C-E) (Li A (Na B K (1-B) ) (1―A) NbO 3 + C Ba(Zr D Ti (1―D) )O 3 + E BiFeO 3 however, 0 <A<0.2、0.4≦B≦0.6、0<C≦0.1、0<D<1.00、0<E<0.02 The vibrating body of the third disclosed technique is The piezoelectric ceramic is made of sodium and potassium niobate metal oxide and has an electromechanical conversion element whose relative dielectric constant temperature characteristic is 500 ppm / °C or less in absolute value in the temperature range of -40°C to 170°C, and a vibration wave is generated by exciting the electromechanical conversion element, and the electromechanical conversion element before being joined to the vibrating body has a change rate of capacitance of the electromechanical conversion element at -20°C compared to 60°C in the temperature range of -20°C to 60°C of 4 to 12%. The vibrating body of the fourth disclosed technique is The piezoelectric ceramic is made of sodium and potassium niobate metal oxide and has an electromechanical conversion element whose relative dielectric constant temperature characteristic is an absolute value of 390 ppm / °C or less in the temperature range of 0°C to 60°C, and a vibration wave is generated by exciting the electromechanical conversion element, and the electromechanical conversion element before being joined to the vibrating body has a change rate of capacitance of the electromechanical conversion element at -20°C compared to 60°C in the temperature range of -20°C to 60°C of 4 to 12%. The vibrating body of the fifth disclosed technique is The piezoelectric ceramic is made of sodium and potassium niobate metal oxide and has an electromechanical conversion element with a relative dielectric constant temperature characteristic of 500 ppm / °C or less in absolute value in the temperature range of -40°C to 170°C, and a vibration wave is generated by exciting the electromechanical conversion element, and the electromechanical conversion element before being joined to the vibrating body has a change rate of capacitance of 0°C to 60°C in the range of 0.5 to 3.9% in the temperature range of 0°C to 60°C. The vibrating body of the sixth disclosed technique is The piezoelectric ceramic is made of sodium and potassium niobate metal oxide and has an electromechanical conversion element whose relative dielectric constant temperature characteristic is an absolute value of 390 ppm / °C or less in the temperature range of 0°C to 60°C, and a vibration wave is generated by exciting the electromechanical conversion element, and the electromechanical conversion element before being joined to the vibrating body has a change rate of the electrostatic capacitance of the electromechanical conversion element at 0°C relative to that at 60°C in the temperature range of 0°C to 60°C of 0.5 to 3.9%. The vibrating body of the seventh disclosed technique is The piezoelectric ceramic is made of sodium and potassium niobate metal oxide and has an electromechanical conversion element whose relative dielectric constant temperature characteristic is 500 ppm / °C or less in absolute value in the temperature range of -40°C to 170°C, and a vibration wave is generated by exciting the electromechanical conversion element, and the electromechanical conversion element before being joined to the vibrating body has a change rate of the electrostatic capacitance of the electromechanical conversion element at 0°C relative to 25°C in the temperature range of 0°C to 25°C of -0.2 to 0.7%. The vibrating body of the eighth disclosed technique is The piezoelectric ceramic is made of sodium and potassium niobate metal oxide and has an electromechanical conversion element with a relative dielectric constant temperature characteristic of 390 ppm / °C or less in absolute value in the temperature range of 0°C to 60°C, and a vibration wave is generated by exciting the electromechanical conversion element, and the electromechanical conversion element before being joined to the vibrating body has a change rate of the electrostatic capacitance of the electromechanical conversion element at 0°C relative to 25°C in the temperature range of 0°C to 25°C of -0.2 to 0.7%. The vibrating body of the ninth disclosed technique is The piezoelectric ceramic is made of sodium and potassium niobate metal oxide, and has an electromechanical conversion element with a relative dielectric constant temperature characteristic of 500 ppm / °C or less in absolute value in the temperature range of -40°C to 170°C, whereby a vibration wave is generated by exciting the electromechanical conversion element, and the electromechanical conversion element joined to the vibrating body has a change rate of the electrostatic capacitance of the vibrating body at -20°C compared to 60°C in the temperature range of -20°C to 60°C of 15 to 22%. The vibrating body of the tenth disclosed technology is The piezoelectric ceramic is made of sodium and potassium niobate metal oxide and has an electromechanical conversion element whose relative dielectric constant temperature characteristic is an absolute value of 390 ppm / °C or less in the temperature range of 0°C to 60°C. Excitation of the electromechanical conversion element generates a vibration wave, and the electromechanical conversion element joined to the vibrating body has a change rate of the electrostatic capacitance of the vibrating body at -20°C compared to 60°C in the temperature range of -20°C to 60°C of 15 to 22%. The vibrating body of the eleventh disclosed technique is The piezoelectric ceramic is made of sodium and potassium niobate metal oxide, and has an electromechanical conversion element with a relative dielectric constant temperature characteristic of 500 ppm / °C or less in absolute value in the temperature range of -40°C to 170°C, whereby a vibration wave is generated by exciting the electromechanical conversion element, and the electromechanical conversion element joined to the vibrating body has a change rate of the electrostatic capacitance of the vibrating body at 0°C compared to 60°C in the temperature range of 0°C to 60°C of 6 to 11%. The vibrating body of the twelfth disclosed technique is The piezoelectric ceramic is made of sodium and potassium niobate metal oxide and has an electromechanical conversion element whose relative dielectric constant temperature characteristic is an absolute value of 390 ppm / °C or less in the temperature range of 0°C to 60°C. Excitation of the electromechanical conversion element generates a vibration wave, and the electromechanical conversion element joined to the vibrating body has a change rate of the electrostatic capacitance of the vibrating body at 0°C compared to 60°C in the temperature range of 0°C to 60°C of 6 to 11%. The vibrating body of the 13th disclosed technology is The piezoelectric ceramic is made of sodium and potassium niobate metal oxide, and has an electromechanical conversion element with a relative dielectric constant temperature characteristic of 500 ppm / °C or less in absolute value in the temperature range of -40°C to 170°C, whereby a vibration wave is generated by exciting the electromechanical conversion element, and the electromechanical conversion element joined to the vibrating body has a change rate of the electrostatic capacitance of the vibrating body at 0°C compared to 25°C in the temperature range of 0°C to 25°C of 3 to 7%. The vibrating body of the fourteenth disclosed technique is The piezoelectric ceramic is made of sodium and potassium niobate metal oxide, and has an electromechanical conversion element with a relative dielectric constant temperature characteristic of 390 ppm / °C or less in absolute value in the temperature range of 0°C to 60°C, whereby a vibration wave is generated by exciting the electromechanical conversion element, and the electromechanical conversion element joined to the vibrating body has a change rate of the electrostatic capacitance of the vibrating body at 0°C compared to 25°C in the temperature range of 0°C to 25°C of 3 to 7%.

[0006] The vibration wave motor of the third disclosed technology has a vibrating body of the first or second disclosed technology, and a relative moving member having a sliding surface that is in pressure contact with the driving surface of the vibrating body and is moved relatively by the vibration wave. [Brief description of the drawings]

[0007] [Figure 1] FIG. 1 is a cross-sectional view showing a vibration wave motor according to a first embodiment. [Diagram 2] FIG. 2 is a perspective view with a part of the vibrating body and the moving element cut away. [Diagram 3] FIG. 3 is a block diagram showing a driving device of the vibration wave motor according to the first embodiment. [Figure 4] FIG. 4 is an explanatory diagram showing the piezoelectric body according to the first embodiment. [Diagram 5] FIG. 5 is an explanatory diagram showing the vibrating body according to the first embodiment. [Figure 6] FIG. 6 is a table showing the constants (A to E) of chemical formula (1) for each of materials α to γ, and the temperature characteristics (−40 to 170° C., 0 to 60° C.) of the electromechanical coupling coefficient, the relative dielectric constant, the piezoelectric constant, and the relative dielectric constant. [Figure 7] FIG. 7 is a graph showing the temperature characteristics of the relative dielectric constant. [Figure 8A] FIG. 8A is a graph showing temperature characteristics of capacitance of materials α and β of the piezoelectric body according to the first embodiment. [Figure 8B] FIG. 8B is a graph showing the temperature characteristics of capacitance of the material γ of the piezoelectric body according to the first embodiment. [Figure 9A] FIG. 9A is a graph showing temperature characteristics of the capacitance of the vibrating body when materials α and β are used. [Figure 9B] FIG. 9B is a graph showing the temperature characteristics of the capacitance of the vibrating body when the material γ is used. [Figure 10] FIG. 10 is a graph showing the current consumption measured at each temperature for the oscillatory wave motor according to the first embodiment and an oscillatory wave motor equipped with a PZT. [Figure 11] FIG. 11 is an explanatory diagram showing an equivalent circuit of a vibrator of a vibration wave motor. [Figure 12] FIG. 12 is a table showing the minimum voltage of the drive signal capable of driving the vibration wave motor according to the first embodiment. [Figure 13] FIG. 13 is a cross-sectional view showing a lens barrel equipped with a vibration wave motor. [Figure 14] FIG. 14 is a cross-sectional view showing a lens barrel in which a circular ring-type oscillatory wave motor according to the second embodiment is mounted. [Figure 15] FIG. 15 is an explanatory diagram showing a vibrating body according to the third embodiment. [Figure 16] FIG. 16 is an explanatory diagram showing the driving principle of the vibrator according to the third embodiment. [Figure 17] FIG. 17 is an explanatory diagram illustrating an example of a dust prevention device according to the fourth embodiment. [Figure 18] FIG. 18 is a graph showing an example of temperature characteristics of capacitance of PZT (manufactured by Fuji Ceramics), which is a piezoelectric material produced for a vibration wave motor. [Figure 19] FIG. 19 is a graph showing an example of temperature characteristics of the electrostatic capacitance of the vibrator of the vibration wave motor when the PZT of FIG. 18 is used as the piezoelectric material. [Figure 20] FIG. 20 is a graph showing the measurement of the input current at each temperature for a vibration wave motor equipped with a PZT. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0008] Oscillatory wave motors use the expansion and contraction of a piezoelectric body to generate a traveling wave on the driving surface of an elastic body, which generates an elliptical motion on the driving surface, and the slider that is in pressure contact with the crest of the elliptical motion is driven. Oscillatory wave motors have the characteristic of having high torque even at low rotation, and when mounted on a driving device, it is possible to omit the gear of the driving device. Therefore, it is possible to achieve quieter operation by eliminating gear noise, and improve positioning accuracy.

[0009] The vibrating body of such a vibration wave motor is generally composed of an electromechanical conversion element (hereinafter referred to as a piezoelectric body) and an elastic body. The piezoelectric body is generally composed of a material such as lead zirconate titanate, commonly known as PZT.

[0010] Figure 18 is a graph showing an example of the temperature characteristic of the capacitance of PZT (manufactured by Fuji Ceramics), a piezoelectric material produced for a vibration wave motor. It can be seen that there is a gradient of about 4.4 pF / ℃ (≒2750 ppm / ℃) with respect to temperature.

[0011] Figure 19 is a graph showing an example of the temperature characteristic of the electrostatic capacitance of the vibrator of a vibration wave motor when the PZT of Figure 18 is used as the piezoelectric material. It can be seen that there is a gradient of about 6.2 pF / ℃ (≒4430 ppm / ℃) with respect to temperature. This gradient indicates, for example, that the lower the temperature, the lower the electrostatic capacitance of the piezoelectric body, and the higher the temperature, the higher the electrostatic capacitance of the piezoelectric body.

[0012] Figure 20 is a graph showing the current input to a vibration wave motor equipped with a PZT at each temperature. In each measurement, the drive voltage was set to 70 Vrms, and the current input to the vibration wave motor when driven at a specified rotation speed was measured. Compared to the current at room temperature, the input current decreases as the temperature decreases, but the input current increases as the temperature increases. This phenomenon coincides with the temperature characteristics of the capacitance value of the vibrating body shown in Figure 19.

[0013] The lower the temperature, the lower the capacitance of the vibrator, which increases the impedance and therefore the input current. However, the higher the temperature, the higher the capacitance of the vibrator, which increases the impedance and therefore the input current. Therefore, the higher the temperature, the higher the capacitance of the vibrator, which increases the impedance and therefore the input current. The oscillatory wave motor cannot be driven efficiently.

[0014] In a vibration wave motor, driving force is generated by a drive signal supplied from a drive device, and the desired driving performance is obtained when the drive signal is under certain conditions, for example, at an appropriate voltage value, but the voltage of the drive signal changes depending on the capacitance of the piezoelectric element.

[0015] Some driving devices are equipped with a matching circuit to match the impedance of the driving circuit that drives the piezoelectric motor with the impedance of the piezoelectric motor. As shown in Figure 18, PZT has a large temperature characteristic, so even if the voltage is adjusted to an appropriate level at room temperature in such a driving device, the driving voltage at low temperature and at high temperature will be significantly different. Therefore, the driving performance (driving efficiency and driving force) of the vibration wave motor cannot be fully demonstrated.

[0016] In this embodiment, in order to address environmental issues, a lead-free material is used for the piezoelectric body, thereby improving the driving performance of the vibration wave motor. Hereinafter, the vibrator and the vibration wave motor of this embodiment will be described in embodiments 1 to 4.

[0017] [Embodiment 1] <Vibration wave motor> Fig. 1 is a cross-sectional view showing a vibration wave motor according to a first embodiment. Fig. 2 is a perspective view in which a part of a vibrating body 10 and a moving element 20 are cut away. In the first embodiment, the vibrating body 10 is fixed, and the moving element 20, which is an example of a relative moving member, is driven. The moving element 20 is made of a light metal such as aluminum. A sliding surface 20a of the moving element 20 is subjected to a surface treatment to improve wear resistance.

[0018] The vibrating body 10 is composed of an electromechanical conversion element (hereinafter referred to as a piezoelectric body) 11, such as a piezoelectric element or an electrostrictive element that converts electrical energy into mechanical energy, and an elastic body 12 to which the piezoelectric body 11 is bonded, and a traveling vibration wave is generated in the vibrating body 10.

[0019] The elastic body 12 is made of a metal material with high resonance sharpness and has a circular ring shape. The piezoelectric body 11 is bonded to one surface (bonding surface 12f) of the elastic body 12, and a groove 12b is cut on the side opposite to the bonding surface 12f. The tip of the protruding portion (a portion without the groove 12b) 12c becomes the driving surface 12a and is in pressure contact with the sliding surface 20a of the slider 20. The driving surface 12a is subjected to a lubricating surface treatment.

[0020] The portion of the elastic body 12 where the groove 12b is not cut is a base portion 12d, and a flange 12e extends from the base portion 12d toward the inner diameter side. The innermost diameter portion of the flange 12e is fixed to a fixing member 13. A sliding member such as a paint film or lubricating plating is applied to the protruding portion 12c of the elastic body 12 so as to cover the entirety.

[0021] The piezoelectric body 11, which will be described in detail later, is composed of a lead-free material whose main component is sodium potassium niobate. A flexible printed circuit board (FPC) 14 is bonded to the surface (opposite bonding surface) of the piezoelectric body 11 opposite to the bonding surface 12f with the elastic body 12, and extends to the circuit board. Electrodes are arranged on the opposite bonding surface, which has a two-group structure divided into two phases (phase A and phase B) along the circumferential direction. In each phase, the electrodes are alternately polarized every 1 / 2 wavelength, and the electrodes are arranged so that there is a 1 / 4 wavelength gap between phase A and phase B.

[0022] The output shaft 21 is connected to the slider 20 via a rubber member 22 and a stopper member 23 inserted so as to fit into the D-cut of the output shaft 21. The output shaft 21 and the stopper member 23 are fixed by an E-clip 24 so as to rotate integrally with the slider 20.

[0023] The rubber member 22 between the stopper member 23 and the moving element 20 is preferably made of butyl rubber or the like, which has a function of joining the moving element 20 and the stopper member 23 with the adhesiveness of the rubber and also has a function of absorbing vibration so as not to transmit vibration from the moving element 20 to the output shaft 21. The pressure member 25 is provided between the output gear 41 of the output shaft 21 and the bearing 27. With this structure, the moving element 20 is in pressure contact with the driving surface 12a of the elastic body 12.

[0024] <Vibration wave motor drive device> 3 is a block diagram showing a driving device 300 for the vibration wave motor 1 according to the embodiment 1. The driving device 300 includes a control unit 301, an oscillation unit 302, a phase shift unit 303, an amplification unit 304, the vibration wave motor 1, and a detection unit 305. The control unit 301 is electrically connected to a CPU 310 in the lens barrel 110 (see FIG. 13) or in the camera body.

[0025] The control unit 301 controls the driving of the vibration wave motor 1 based on a driving command from a CPU 310 in the lens barrel 110 or in the camera body. The control unit 301 receives a detection signal from a detection unit 305, obtains position information and speed information based on the value, and controls the frequency of the oscillation unit 302 so as to position the motor at a target position.

[0026] The oscillator 302 generates a drive signal of a desired frequency in response to a command from the controller 301. The phase shifter 303 divides the drive signal generated by the oscillator 302 into two drive signals with different phases. The amplifier 304 boosts each of the two drive signals divided by the phase shifter 303 to a desired voltage. The drive signal from the amplifier 304 is transmitted to the vibration wave motor 1, and application of this drive signal generates a traveling wave in the oscillator 10, driving the mover 20.

[0027] The detection unit 305 is configured with an optical encoder, a magnetic encoder, or the like, detects the position and speed of a driven object driven by driving the slider 20, and transmits the detected value to the control unit 301 as an electric signal.

[0028] Next, the operation of the vibration wave motor 1 will be described. When a drive command is issued from the control unit 301, the oscillator unit 302 generates a drive signal. The drive signal is divided by the phase shift unit 303 into two drive signals with a phase difference of 90 degrees, and is amplified to a desired voltage by the amplifier unit 304. The amplified drive signal is applied to the piezoelectric body 11 of the vibration wave motor 1, and the piezoelectric body 11 is excited (vibrated). The excitation of the piezoelectric body 11 generates a fourth-order bending vibration in the elastic body 12. The piezoelectric body 11 is divided into phase A and phase B, and the drive signals are applied to phase A and phase B, respectively.

[0029] The positional phase of the fourth-order bending vibration generated from phase A is shifted by 1 / 4 wavelength from that generated from phase B. In addition, because the phase A drive signal and the phase B drive signal are shifted in phase by 90 degrees, the two bending vibrations are combined to form four traveling waves.

[0030] An elliptical motion occurs at the crest of the traveling wave. Therefore, the moving element 20, which is in pressure contact with the driving surface 12a, is frictionally driven by this elliptical motion. An optical encoder serving as a detection unit 305 is disposed on the driving body driven by the driving of the moving element 20, and an electric pulse is generated from the optical encoder and transmitted to the control unit 301. The control unit 301 can obtain the current position and the current speed based on the signal of this electric pulse.

[0031] <Piezoelectric body 11> Fig. 4 is an explanatory diagram showing the piezoelectric body 11 according to the first embodiment. Fig. 4(a) is a diagram showing the front surface 11A of the piezoelectric body 11, and Fig. 4(b) is a diagram showing the back surface 11B of the piezoelectric body 11. Fig. 5 is an explanatory diagram showing the vibrating body 10 according to the first embodiment. Fig. 5(a) is a diagram showing the side surface of the vibrating body 10, and Fig. 5(b) is a diagram showing the vibrating body 10 viewed from the front surface 11A side of the piezoelectric body 11.

[0032] On the surface 11A, the electrode 16 is divided into two phases (phase A and phase B) along the circumferential direction. In each phase, the electrodes 16 are printed on the base material 18 of the piezoelectric body 11 with silver paste so that the electrodes are alternately polarized every 1 / 2 wavelength, and a 1 / 4 wavelength interval is provided between the phases A and B. The electrodes 16 may be plated with a metal such as NiP or gold. The base material 18 of the piezoelectric body 11 is made of a lead-free material whose main component is potassium sodium niobate.

[0033] On the back surface 11B, electrodes 19, which are not an electrode pattern like the electrodes 16, are printed with silver paste, and the base material 18 of the piezoelectric body 11 is exposed on both the outer and inner periphery sides. The electrodes 19 may be plated with a metal such as NiP or gold. The back surface 11B is bonded to the elastic body 12 with a room temperature curing adhesive.

[0034] In addition, the FPC 14 is joined to the front surface 11A in order to transmit a drive signal from the drive device 300, and is connected to the drive device 300. The GND line of the FPC 14 is joined to the ¼ wavelength electrode 16, and the ¼ wavelength electrode 16 and the metal part of the elastic body 12 are joined so as to straddle each other using conductive paint (not shown), and are adapted to be grounded to the metal part of the elastic body 12.

[0035] Here, we will explain the material of the piezoelectric body 11. The material of the piezoelectric body 11 is a piezoelectric ceramic made of sodium potassium niobate metal oxide, and for example, the following material and manufacturing method are used. The material of the piezoelectric body 11 is as shown in the following chemical formula (1).

[0036] (1-C-E) (Li A (Na B K (1-B) ) (1―A) NbO3+ C Ba(Zr D Ti (1―D) )O3+ E BiFeO3 however, 0 <A<0.2、0.4≦B≦0.6、0<C≦0.1、0<D<1.00、0<E<0.02 (1)

[0037] The material of the piezoelectric body 11 has an extremely small temperature characteristic of the relative dielectric constant. Specifically, the rate of change of the relative dielectric constant in the range of -40°C to 170°C is 500 ppm / °C or less in absolute value, that is, in the range of -500 to +500 ppm / °C. Therefore, the temperature characteristic of the capacitance of the piezoelectric body 11 can be made extremely small.

[0038] When sodium carbonate and potassium carbonate are used as raw materials, the pH of the slurry becomes strongly alkaline during mixing and grinding. For this reason, in this embodiment, sodium niobate and potassium niobate with nano-sized particle size produced by hydrothermal synthesis are used as raw materials. This makes it possible to make the pH weakly alkaline.

[0039] Also, sodium niobate and potassium niobate may be used in which the composition ratio (x) of sodium to niobium and potassium to niobium is in the range of 1.00≦x≦1.01. In the manufacturing method described below, the range of (x) was changed to confirm the difference between when (x) is 1.00 and when it is 1.01.

[0040] The manufacturing method will be specifically described below. The composition of the niobium-based lead-free piezoelectric ceramic material is represented by the chemical formula (1-C-E) (Li A (Na B K (1-B) ) (1-A) Using NbO3 as the standard, A and B were varied within the following ranges.

[0041] 0.055≦A≦0.1 0.4≦B≦0.6

[0042] To this was added barium zirconate titanate and bismuth ferrite to create a composition.

[0043] (1-C-E) (Li A (Na B K (1-B) ) (1-A) NbO3+ C Ba(ZrD T i(1-D) )O3+ E B i F e O3 (0.055≦A≦0.1, 0.4≦B≦0.6, 0.05≦C≦0.1, 0.17≦D≦0.83, 0.005≦E≦0.01)

[0044] In the present embodiment, the lithium carbonate was mixed in the ratio of 0.055 to 0.1 mol, the barium carbonate in the ratio of 0.05 to 0.1 mol, the zirconium oxide in the ratio of 0.05 to 0.1 mol, the titanium oxide in the ratio of 0.05 to 0.1 mol, the bismuth oxide in the ratio of 0.005 to 0.01 mol, and the iron oxide in the ratio of 0.005 to 0.01 mol.

[0045] As a representative example, the composition and amounts of material α in FIG. 6, which is blended so that the total blend amount is 100 g scale, and a method for producing the material will be described.

[0046] Figure 6 is a table showing the constants (A to E) of chemical formula (1) for each material, as well as the temperature characteristics (rate of change) of the electromechanical coupling coefficient, dielectric constant, piezoelectric constant, and dielectric constant. The temperature characteristics of the dielectric constant were measured for two temperature ranges (-40 to 170°C, 0 to 60°C). The larger the electromechanical coupling coefficient, the more efficiently electrical energy is converted into mechanical energy. In addition to the main components, 0.1 wt% Cu is added to material γ. This improves the mechanical quality factor (described later in Figure 11).

[0047] In the composition of material α in Fig. 6 and its preparation method, lithium carbonate 0.057mol, barium carbonate 0.05mol, zirconium oxide 0.0415mol, titanium oxide 0.0085mol, bismuth oxide 0.005mol, and iron oxide 0.005mol were mixed and ground in 300ml of water for 24 hours using a ball mill to prepare a primary mixed ground liquid. In addition, the composition amounts of the other Nos. A to E are determined by different ratios relative to the composition amount of material α in Fig. 6.

[0048] The primary mixed and ground liquid was mixed with 0.444 mol of sodium niobate and 0.444 mol of potassium niobate, which were produced by a hydrothermal synthesis method in which solvothermal reaction was performed at 150°C to 300°C for 1 to 12 hours, to produce a mixture. The mixture was mixed and ground again in 300 ml of water at room temperature using a ball mill for 24 hours to produce a secondary mixed and ground liquid. The secondary mixed and ground liquid was then dried at 85°C for 48 hours while showing a weak alkalinity of pH 8.9 to pH 9.8, below pH 10, to produce a dried product.

[0049] Next, this dried material was pre-sintered twice at temperatures ranging from 700° C. to 800° C. The first pre-sintering was performed at 800° C. for 2 hours using an electric furnace, after which the pre-sintered powder was pulverized in 300 ml of water using a ball mill for 24 hours and dried at 85° C. for 48 hours using a thermostatic chamber to produce the primary pre-sintered pulverized dried powder, which was then pre-sintered again.

[0050] The second pre-sintering temperature range was 800°C, which was the same as the first pre-sintering temperature range, and the time was 2 hours. However, the first pre-sintering and the second pre-sintering may be performed under different firing temperatures. As for the sintering atmosphere, in this embodiment, the pre-sintering was performed in an air atmosphere, but it can also be performed in an atmosphere other than air. For example, it can be produced in an oxygen atmosphere.

[0051] The calcined powder was ground using a ball mill, bead mill, or other method, and the second calcined powder was ground in 300 ml of water using a ball mill for 24 hours so that the particle size of the secondary calcined, ground, and dried powder would be 1 μm or less. The powder was then dried at 85°C for 48 hours in a thermostatic chamber to produce the secondary calcined, ground, and dried powder.

[0052] The secondary calcined, pulverized, and dried powder was then mixed with 10 wt% of a binder, passed through a #40 mesh sieve, and dried at 110°C for 1 hour in a thermostatic chamber to produce a granular, sized powder.

[0053] After sieving, the sieved powder was placed in a φ15 mm mold and pressure was applied using a hydraulic press (200 ton press) until the molding density (ρ) reached approximately 2.3 g / cm. 3 from 2.6 g / cm 3 The thickness of the molded body was 1.5 mm. The time for applying pressure was 1 to 10 seconds. The molded density (ρ) was about 2.3 to 2.6 g / cm 3 The upper limit for molding is 2.6g / cm 3 , lower limit 2.3g / cm 3 The results were as follows: 3 was optimal.

[0054] After molding, degreasing is performed using an electric furnace at a temperature range of 700°C to 800°C, and in the embodiment, it is preferable to hold the material at 700°C for 4 hours and then sinter it at a sintering temperature range of 1100°C to 1250°C. In the embodiment, it was performed at 1200°C. The sintering was performed in air or the like.

[0055] After firing, the fired body was processed to a thickness of T = 0.5 mm using a polishing machine (6BN, HAMAI, #800 abrasive), and then silver paste (SR-2099, Namics Corporation) was applied to the surface of the processed element by screen printing, and silver electrodes were provided using an electric furnace at 800 ° C. The element with the silver electrodes was polarized by applying a voltage of 4.0 kV / mm for 10 minutes in insulating oil (silicon oil) at 50 ° C to produce niobium-based lead-free piezoelectric ceramics.

[0056] The measurement method for the niobium-based lead-free piezoelectric ceramic material was to leave it for 24 hours after polarization treatment and measure it by the resonance-antiresonance method using an impedance analyzer (Agilent 4294A). 33 The measurements were performed using a meter (ZJ-43, Institute of Phonetic Characters, Chinese Academy of Sciences).

[0057] The lead-free niobium-based piezoelectric ceramic of the present embodiment was obtained by this manufacturing method. The electromechanical coupling coefficient, dielectric constant, piezoelectric constant, temperature characteristic of dielectric constant, and temperature characteristic of Curie point of the obtained lead-free niobium-based piezoelectric ceramic were measured by the following methods.

[0058] <Measuring device, measuring method> A method for measuring the temperature characteristic of the dielectric constant of the niobium-based lead-free piezoelectric ceramic material produced by the manufacturing method of this embodiment will be described.

[0059] The piezoelectric body 11 thus obtained, having a diameter of φ10 mm and a thickness of 0.5 mm, was left for 24 hours, and then a small ultra-low temperature incubator (MC-811, espec) was used to measure the capacitance at a frequency of 1 kHz and a voltage of 0.5 V from -40°C to 170°C and at 10°C intervals from 170°C to -40°C using an impedance analyzer (Agilent 4294A) to calculate the relative dielectric constant. The results are shown in FIG. 7.

[0060] Fig. 7 is a temperature characteristic diagram of the dielectric constant. Fig. 7 shows the change in the dielectric constant when the temperature is increased from -40°C to 170°C and decreased from 170°C to -40°C. In this embodiment, the difference between the dielectric constant measured at the time of increasing the temperature from the low temperature side of -40°C and the value measured at the time of decreasing the temperature from the high temperature side of 170°C is small at a maximum of 38, and the hysteresis value of the dielectric constant before and after the phase transition is within the range of 32 to 38.

[0061] It is generally known that the relative dielectric constant of a material such as quartz crystal hardly changes in the temperature range from -40° C. to 170° C. In this embodiment as well, as can be seen from FIG. 7, it is recognized that a material having sufficient practicality within this range has been provided.

[0062] <Temperature characteristics of capacitance of piezoelectric body 11> FIG. 8A is a graph showing the temperature characteristics of the capacitance of the materials α and β of the piezoelectric body 11 according to the first embodiment. FIG. 8B is a graph showing the temperature characteristics of the capacitance of the material γ of the piezoelectric body 11 according to the first embodiment. In FIG. 8A and FIG. 8B, for example, the low temperature range is greater than -20°C and less than 0°C, the normal temperature range is greater than 0°C and less than 25°C, and the high temperature range is greater than 25°C and less than 60°C. The change in capacitance of the materials α, β, and γ from the low temperature to the high temperature, when 60°C is used as the reference temperature, is about 2% at 0°C for the material α and about 10% at -20°C for the material β at 0°C and about 11% at -20°C for the material γ at 0°C and about 5% at -20°C for the material γ.

[0063] <Temperature Characteristics of Capacitance of Vibrating Body 10> FIG. 9A is a graph showing the temperature characteristic of the capacitance of the vibrating body 10 when materials α and β are used. FIG. 9B is a graph showing the temperature characteristic of the capacitance of the vibrating body 10 according to the first embodiment when material γ is used. When 60° C. is used as a reference, the change in capacitance of the vibrating body 10 from a low temperature to a high temperature is about 8% at 0° C. and about 18% at −20° C. for material α. For material β, the change is about 10% at 0° C. and about 20% at −20° C. For material γ, the change is about 6% at 0° C. and about 16% at −20° C. This is significantly smaller than the change rate of 25% at 0° C. and 31 to 33% at −20° C. when a PZT is installed.

[0064] <Current consumption measurement> FIG. 10 is a graph showing the measured current consumption at each temperature for the vibration wave motor 1 according to the first embodiment and a vibration wave motor equipped with a PZT. In each measurement, the driving voltage was set to 70 [Vrms], and the current input to the vibration wave motor when driven at a predetermined rotation speed was measured. It can be seen that the vibration wave motor 1 equipped with materials α, β, and γ has almost no temperature characteristic of the input current. Compared with the temperature characteristic of the input current of the PZT-equipped product shown in FIG. 19, it can be seen that it can be driven more efficiently than the PZT-equipped product, especially at high temperatures. This phenomenon is caused by the temperature characteristic of the capacitance of the vibrating body 10 as described above. This phenomenon will be explained with reference to FIG. 11.

[0065] 11 is an explanatory diagram showing an equivalent circuit of the vibrating body 10 of the vibration wave motor 1. The equivalent circuit 1100 of the vibrating body 10 is composed of the capacitance C of the piezoelectric body 11, an equivalent inductance L, an equivalent capacitance C, and a resonance resistance R. The current Ia of the vibrating body 10 is the sum of the current Ib (the following formula (2)) flowing to the capacitance C component of the piezoelectric body 11 and the current Ic (the following formula (3)) flowing to the LCR series side.

[0066]

number

[0067] Generally, a vibration wave motor is driven at a drive frequency that is slightly higher than the resonance frequency at which the impedance of the equivalent circuit 900 is minimized and the anti-resonance frequency at which the impedance of the equivalent circuit 900 is maximized. Under this drive frequency condition, the value of 1 / ωCd, which is the denominator of the current Ib, is much smaller than the value of R+(ωL-1 / ωC), which is the denominator of the current Ic, so that the current Ia input to the vibrating body 10 is approximately the same as the current Ib. In other words, the current consumption of the vibrating body 10 depends almost entirely on the value of the capacitance C of the piezoelectric body 11.

[0068] Therefore, when the capacitance of the vibrating body 10 changes due to temperature, the impedance also changes, causing a change in the input current. Since the components equipped with materials α, β, and γ hardly increase in capacitance even at high temperatures, there is also little increase in the input current.

[0069] In addition, a typical vibration wave motor is designed to match the impedance of the driving device with the impedance of the vibration wave motor. Therefore, if the capacitance Cd of the piezoelectric body 11 changes, the voltage of the drive signal (drive voltage E) changes. Therefore, if the capacitance Cd of the piezoelectric body 11 fluctuates due to the environmental temperature, the voltage of the drive signal also fluctuates.

[0070] Even if the vibration wave motor equipped with a PZT is adjusted to an appropriate voltage at room temperature, the driving voltage at low temperature and at high temperature will be significantly different. Specifically, a phenomenon occurs in which the voltage at low temperature is larger than that at room temperature and is smaller at high temperature. At low temperatures, the driving voltage is set higher than that which is actually required, and the driving efficiency of the driving circuit itself is impaired due to the high voltage. The vibration wave motor 1 according to the first embodiment has less change in capacitance at low and high temperatures compared to a product equipped with a PZT, so the fluctuation in the driving voltage can be significantly reduced, and the driving efficiency of the driving device 300 itself is improved.

[0071] In the following formula (4), Q is the mechanical quality factor. The values ​​of equivalent inductance L and equivalent capacitance C affect the resonance characteristics of the vibrating body 10. The mechanical quality factor Q is a measure of the resonance characteristics, and a larger value of the mechanical quality factor Q indicates better resonance characteristics. The mechanical quality factor Q increases as the Lm value increases. Compared to material β, material γ shown in FIG. 6 has a larger mechanical quality factor Q and improves resonance characteristics.

[0072]

number

[0073] It was also found that the oscillatory wave motor 1 according to the first embodiment has a small temperature characteristic of the drivable voltage.

[0074] 12 is a table showing the minimum voltage of the drive signal capable of driving the vibration wave motor 1 according to the first embodiment (hereinafter referred to as the drivable voltage). The vibration wave motor 1 cannot be driven with a drive voltage E lower than the drivable voltage. It can be seen that for all materials α, β, and γ, the drivable voltage remains almost unchanged in the temperature range of 0 to 50°C, where the capacitance remains almost unchanged. At -20°C, the drivable voltage is slightly higher, but the amount of variation is much smaller than when PZT is installed.

[0075] Experiments conducted by the inventors have revealed that the drivable voltage is correlated with the electrostatic capacitance of the vibrating body 10. The reason for this will be explained below. The electromechanical coupling coefficient Kvn of the vibrating body 10 is expressed by the following formula (5) as the amount of conversion from the electrical energy Ui stored in the vibrating body 10 to mechanical energy Ut, which is the distortion energy of vibration.

[0076] Kvn = (Ut / Ui) 0.5 (5)

[0077] Most of the electrical energy Ui stored in the vibrating body 10 is stored in the piezoelectric body 11. On the other hand, the energy Pf stored in the piezoelectric body 11 is as shown in the following formula (6).

[0078] Pf = E × ω × Cdv (6)

[0079] E is the drive voltage, ω is the angular frequency, and Cdv is the capacitance of the vibrating body 10. The oscillatory wave motor 1 can be driven when the strain energy is equal to or greater than a certain threshold. If the electromechanical coupling coefficient Kvn and ω are constant, the strain energy at a certain threshold depends on the capacitance Cdv of the vibrating body 10 and the applied voltage. However, in a product equipped with a PZT, the capacitance Cdv of the vibrating body 10 fluctuates with temperature, and it is thought that the drivable voltage changes accordingly.

[0080] When driven by a constant voltage drive signal, the drive voltage E of a PZT-equipped product is set based on the drivable voltage at -20°C, where the drivable voltage is largest. However, because the difference between the drive voltage E and the drivable voltage at room temperature and high temperature is large, a current greater than the current actually required is input. On the other hand, the vibration wave motor 1 according to the first embodiment has a small temperature characteristic of the drivable voltage, and the difference between the drive voltage and the drivable voltage at each temperature does not change much, so that approximately the required current is input at each temperature.

[0081] <Lens barrel> 13 is a cross-sectional view showing a lens barrel 110 equipped with a vibration wave motor 1. The lens barrel 110 has an outer fixed barrel 31, an inner fixed barrel 32, and the vibration wave motor 1. The outer fixed barrel 31 is, for example, cylindrical, and covers the outer periphery of the lens barrel 110. The outer fixed barrel 31 has a protruding piece 31a protruding from its inner circumferential surface toward the optical axis OA. The protruding piece 31a supports the inner fixed barrel 32. The inner fixed barrel 32 is, for example, cylindrical, and is provided on the inner circumferential side of the outer fixed barrel 31. The vibration wave motor 1 is provided between the outer fixed barrel 31 and the inner fixed barrel 32.

[0082] In the inner fixed barrel 32, a first lens group L1, a second lens group L2, a third lens group L3, and a fourth lens group L4 are arranged on the same optical axis OA from the subject side. The third lens group L3 is an AF lens held by a circular AF (Auto Focus) ring 119. The first lens group L1, the second lens group L2, and the fourth lens group L4 are fixed to the inner fixed barrel 32. The third lens group L3 is configured to be movable in the direction of the optical axis OA (hereinafter, optical axis direction) relative to the inner fixed barrel 32 by the movement of the AF ring 119.

[0083] The vibration wave motor 1 is attached to a gear unit module 113. The gear unit module 113 is attached to the inner fixed cylinder 32 of the lens barrel 110. The rotational motion of the output gear 41 of the vibration wave motor 1 is transmitted to a cam ring 116 via a reduction gear 115 of the gear unit module 113, and the cam ring 116 is driven to rotate.

[0084] The cam ring 116 has a key groove 117 cut obliquely relative to the circumferential direction. The AF ring 119 has a fixed pin 118. The fixed pin 118 is inserted into the key groove 117. When the cam ring 116 is rotationally driven with the fixed pin 118 inserted into the key groove 117, the AF ring 119 is driven in a straight line in the direction of the optical axis OA, so that it can be stopped at a desired position. The driving device 300 shown in FIG. 2 is provided between the outer fixed cylinder 31 and the inner fixed cylinder 32 of the lens barrel 110, and drives, controls, detects the number of rotations, etc. of the vibration wave motor 1 described above.

[0085] Thus, according to the oscillatory wave motor 1 of the first embodiment, the temperature characteristic of the current consumption can be made smaller than that of a PZT-equipped product. Also, since the change in the capacitance Cdv of the oscillator 10 at low and high temperatures is smaller than that of a PZT-equipped product, the fluctuation in the drive voltage E can be made significantly smaller, improving the drive efficiency of the drive device 300 itself. Furthermore, since the capacitance Cdv of the oscillator 10 is less likely to vary with the environmental temperature than that of a PZT-equipped product, the temperature change in the drivable voltage of the oscillatory wave motor 210 can also be made smaller.

[0086] [Embodiment 2] The second embodiment is an example in which the vibration wave motor 1 of the first embodiment is replaced with a circular vibration wave motor. The same components as those of the first embodiment are given the same reference numerals, and the description thereof will be omitted.

[0087] 14 is a cross-sectional view showing a lens barrel equipped with a circular vibration wave motor according to the second embodiment. The lens barrel 200 has an outer fixed barrel 31 and an inner fixed barrel 32, and a motor unit having a circular vibration wave motor 210 is fixed to the outer fixed barrel 31 and the inner fixed barrel 32. The driving device 300 is provided between the outer fixed barrel 31 and the inner fixed barrel 32 of the lens barrel 200, and drives, controls, detects the number of rotations, etc. of the vibration wave motor 210. The driving device 300 is adapted to match the impedance of the driving device 300 with that of the vibration wave motor.

[0088] Next, the configuration of the vibration wave motor 210 will be described. The vibration body 211 is composed of a piezoelectric body 11 made of sodium potassium niobate metal oxide, the same as in the first embodiment, and an elastic body 214 to which the piezoelectric body 11 is bonded. The vibration body 211 is designed to generate traveling waves, and in the second embodiment, nine traveling waves will be described as an example.

[0089] The elastic body 214 is made of a metal material with high resonance sharpness. The shape of the elastic body 214 is annular. A groove is cut on the surface of the elastic body 214 opposite to the surface to which the piezoelectric body 11 is joined. The reason for cutting the groove is to bring the neutral plane of the traveling wave as close as possible to the piezoelectric body 11 side, thereby amplifying the amplitude of the traveling wave of the driving surface 216a. The surface where the groove is not provided becomes the driving surface 216a, and is brought into pressure contact with the slider 220. A lubricating coating film is applied to the surface of the driving surface 216a of the elastic body 214 to ensure driving performance and improve durability.

[0090] As in the first embodiment, the piezoelectric body 11 is divided into two phases (phase A and phase B) along the circumferential direction, and in each phase, elements with alternating polarization at 1 / 2 wavelength intervals are arranged, with a 1 / 4 wavelength interval between phase A and phase B. The material of the piezoelectric body 11 is the same as in the first embodiment, and is made of a material with an extremely small temperature characteristic of the relative dielectric constant, that is, a material with a small temperature characteristic of the capacitance C.

[0091] A nonwoven fabric 252 and a pressure member 250 are disposed below the piezoelectric body 11. The nonwoven fabric 252 is, for example, made of felt, and is disposed below the piezoelectric body 11 so as not to transmit the vibration of the vibrating body 211 to the pressure member 250.

[0092] The pressure member 250 is disposed under a pressure plate (not shown) and generates a pressure force. In the second embodiment, the pressure member 250 is a disc spring. However, it may be a coil spring or a wave spring instead of a disc spring. The pressure member 250 is held by fixing a pressing ring 251 to a fixing member 223.

[0093] The slider 220 is made of a light metal such as aluminum, and a sliding material is provided on the sliding surface to improve wear resistance. A vibration absorbing member 243 such as rubber is disposed on the slider 220 to absorb vertical vibrations of the slider 220, and an output transmission member 242 is disposed on the vibration absorbing member 243.

[0094] The output transmission member 242 is regulated in the pressure direction and radial direction by a bearing 253 provided in the fixed member 223, thereby regulating the pressure direction and radial direction of the moving element 220. The output transmission member 242 has a protrusion 241, from which a fork connected to a cam ring 315 is engaged, and the cam ring 315 rotates together with the rotation of the output transmission member 242.

[0095] A key groove 317 is cut obliquely in the circumferential direction in the cam ring 315, and a fixing pin 318 provided on the AF ring 319 fits into the key groove 317. When the cam ring 315 is driven to rotate, the AF ring 319 is driven in a straight line in the optical axis direction, so that it can be stopped at a desired position.

[0096] The retaining ring 251 is attached to the fixed member 223 by means of a screw, and by attaching this, the output transmission member 242, the moving element 220, the vibrating body 211, and the pressure member 250 can be configured as one motor unit.

[0097] The vibration wave motor 210 using the vibrating body 211 according to the second embodiment has a significantly smaller temperature characteristic of current consumption compared to a PZT-equipped product, as in the first embodiment. Also, the impedance of the driving device 300 and the impedance of the vibration wave motor 210 are matched. In the vibration wave motor 210 according to the second embodiment, the change in the capacitance Cdv of the vibrating body 10 at low and high temperatures is smaller compared to a PZT-equipped product, so that the fluctuation in the driving voltage E can be significantly reduced, and the driving efficiency of the driving device 300 itself is improved. Furthermore, the capacitance Cdv of the vibrating body 10 is less likely to vary depending on the environmental temperature, so the temperature change in the drivable voltage of the vibration wave motor 210 is also small, as in the first embodiment.

[0098] [Embodiment 3] The vibration wave motor of the third embodiment is a type in which the vibrator is composed only of a piezoelectric body 11, and a drive rail, which is a relative moving member, is driven linearly. The same components as those of the first and second embodiments are given the same reference numerals, and the description thereof will be omitted.

[0099] Fig. 15 is an explanatory diagram showing a vibrating body according to embodiment 3. Fig. 15(A) is a front view and a rear view of the vibrating body 1500, Fig. 15(B) is a schematic perspective view of the vibrating body 1500, and Fig. 15(C) is an explanatory diagram showing an implementation example of the vibrating body 1500.

[0100] The oscillatory wave motor 1 according to the third embodiment is a type in which a vibrating body 1500 is composed only of a piezoelectric body 11, and is linearly driven by a drive rail 1550, which is a relative moving member. The vibrating body 1500 is composed of a piezoelectric body 11 made of sodium potassium niobate metal oxide, the same as in the first embodiment, and a sliding member 1560 installed at the end.

[0101] The vibrating body 1500 is pressed against the drive rail 1550 by a pressure spring 1525. A linear guide 1527 is provided between the fixed member 1513 and the drive rail 1550, with a linear guide fixed portion 1527a fixed to the fixed member 1513 and a movable portion 1527b coupled to the drive rail 1550 so that the drive rail 1550 can only move left and right in the drawing. An elliptical motion is generated at the position of the sliding member 1560 of the vibrating body 1500, and the drive rail 1550 is driven linearly.

[0102] The vibrating body 1500 has a two-layer structure, and in the first layer, one electrode 1510 is provided on a first surface 1501, and one electrode 1520 of the same shape is provided on the opposite second surface 1502. An A-phase drive signal is input to the electrode 1510 on the first surface 1501 side, and the electrode 1520 on the second surface 1502 is GND. The input of the A-phase drive signal generates a standing wave of longitudinal primary mode vibration in the vibrating body 1500.

[0103] Four divided electrodes 1531-1534 are provided on the third surface 1503 of the second layer, and the polarization directions of the four electrodes 1531-1534 are alternated. One electrode 1540 having the same shape as the first layer is also provided on the opposite fourth surface 1504. A B-phase drive signal is input to the electrodes 1531-1534 on the third surface 1503 side, and the electrode 1540 on the fourth surface 1504 side is GND. The input of the B-phase drive signal generates a standing wave of bending secondary mode vibration in the vibrating body 1500.

[0104] The first and second layers are connected to a common GND by joining a second surface 1502, which is the GND of the first layer, and a fourth surface 1504, which is the GND of the second layer. A groove 1505 is provided in the center of the vibrating body 1500, and a pressure spring 1525 fits into this groove to prevent the pressure position from shifting and to support the driving rail 1550 in the longitudinal direction.

[0105] The sliding member 1560 is made of an engineering plastic material with good wear resistance, and is provided at the location shown in the figure where the amplitude of the standing wave of the primary longitudinal mode vibration is maximized and the amplitude of the standing wave of the secondary bending mode vibration is maximized.

[0106] <Operation principle of vibrating body 1500> Fig. 16 is an explanatory diagram showing the driving principle of the vibrating body 1500 according to the embodiment 3. Below, a chronological explanation will be given in the order of (a) to (e) in Fig. 16. In the graphs on the left side of (a) to (e) in Fig. 16, t is time, the vertical axis is voltage, and the horizontal axis is time.

[0107] t=1: The voltage of phase A is 0 and the voltage of phase B is negative. At this time, the displacement of the primary longitudinal vibration is zero, and a secondary bending vibration occurs in which point C is displaced in the negative direction and point D is displaced in the positive direction.

[0108] t=2: The voltage of phase A is positive, and the voltage of phase B is 0. At this time, a primary longitudinal vibration occurs with a displacement in the positive direction, and the displacement of the secondary bending vibration becomes zero.

[0109] t=3: The voltage of phase A is 0 and the voltage of phase B is positive. At this time, the displacement of the primary longitudinal vibration is zero, and a secondary bending vibration occurs in which point C is displaced in the positive direction and point D is displaced in the negative direction.

[0110] t=4: The voltage of phase A is positive, and the voltage of phase B is 0. At this time, the primary longitudinal vibration occurs, which causes displacement in the negative direction, and the displacement of the secondary bending vibration becomes zero.

[0111] t=5: Return to the case of t=1. When vibration is generated in this manner, elliptical motion occurs at points C and D where sliding member 1560 is attached, as shown at the right end of Fig. 16. When a slider is brought into pressure contact with this sliding member 1560, the slider receives a frictional force due to the elliptical motion and is driven. In the third embodiment, the piezoelectric body 11 is made of the same material as in the first embodiment, and thus the same effects as in the first embodiment can be obtained.

[0112] [Embodiment 4] The fourth embodiment shows an example in which the vibration wave motor 1 is applied to a dustproof device provided in a camera. The same components as those in the first embodiment are given the same reference numerals, and the description thereof will be omitted.

[0113] 17 is an explanatory diagram showing an example of a dust prevention device according to the fourth embodiment. The dust prevention device 1700 is installed near an imaging element 1701, and removes dust particles adhering to the optical filter 1702 by vibrating an optical filter 1702 using the vibration of a piezoelectric body 11. The dust prevention device 1700 according to the fourth embodiment is also composed of a piezoelectric body 11 and a driving device 300. The problem that the voltage of the driving vibration from the driving device 300 varies depending on the value of the capacitance Cd of the piezoelectric body 11 is the same as that of the vibrating body 10 of the vibration wave motor 1. In the fourth embodiment, the piezoelectric body 11 is made of the same material as in the first embodiment, and thus the same effect as in the first embodiment can be obtained.

[0114] The above-described embodiment is not limited to the above, and may be any combination of the above. In addition, other aspects that are conceivable within the scope of the technical ideas of the above-described embodiment are also included in the scope of the above. [Explanation of symbols]

[0115] 1 vibration wave motor, 10 vibration body, 11 piezoelectric body, 12 elastic body, 12a driving surface, 12f joint surface, 20 moving element, 20a sliding surface, 30 driving device, 110 lens barrel, 200 lens barrel, 210 vibration wave motor, 211 vibration body, 214 elastic body, 216a driving surface, 220 moving element, 1400 vibration body, 1700 dustproof device

Claims

1. The piezoelectric ceramic is made of sodium potassium niobate metal oxide, and the electromechanical transducer has a temperature characteristic of a relative dielectric constant of 500 ppm / °C or less in absolute value in the temperature range of -40°C to 170°C. A vibration wave is generated by exciting the electromechanical transducer, The electromechanical transducer element is made of the following chemical formula: Vibrating body. (1-C-E) (Li A (Na B K (1-B)) (1-A) NbO 3 + C Ba (Zr D Ti (1-D)) O 3 + E BiFeO 3 however, 0<A<0.2, 0.4≦B≦0.6, 0<C≦0.1, 0<D<1.00, 0<E<0.02

2. The piezoelectric ceramic is made of sodium potassium niobate metal oxide, and the electromechanical transducer has a temperature characteristic of a relative dielectric constant of 390 ppm / °C or less in absolute value in the temperature range of 0°C to 60°C. A vibration wave is generated by exciting the electromechanical transducer, The electromechanical transducer element is made of the following chemical formula: Vibrating body. (1-C-E) (Li A (Na B K (1-B)) (1-A) NbO 3 + C Ba (Zr D Ti (1-D)) O 3 + E BiFeO 3 however, 0<A<0.2, 0.4≦B≦0.6, 0<C≦0.1, 0<D<1.00, 0<E<0.02

3. A vibrating body according to claim 1 or 2, The electromechanical transducer element contains copper. Vibrating body.

4. An electromechanical transducer element made of a piezoelectric ceramic made of sodium potassium niobate metal oxide, the temperature characteristic of the relative dielectric constant being 500 ppm / °C or less in absolute value in the temperature range of -40°C to 170°C, A vibration wave is generated by exciting the electromechanical transducer, The electromechanical transducer element before being joined to the vibrating body has a change rate of the capacitance of the electromechanical transducer element at −20° C. to that at 60° C. in a temperature range of −20° C. to 60° C. in a range of 4 to 12%. Vibrating body.

5. A piezoelectric ceramic made of sodium potassium niobate metal oxide, the piezoelectric ceramic having an electromechanical transducer element having a temperature characteristic of a relative dielectric constant of 390 ppm / °C or less in absolute value in the temperature range of 0°C to 60°C, A vibration wave is generated by exciting the electromechanical transducer, The electromechanical transducer element before being joined to the vibrating body has a change rate of the capacitance of the electromechanical transducer element at −20° C. to that at 60° C. in a temperature range of −20° C. to 60° C. in a range of 4 to 12%. Vibrating body.

6. An electromechanical transducer element made of a piezoelectric ceramic made of sodium potassium niobate metal oxide, the temperature characteristic of the relative dielectric constant being 500 ppm / °C or less in absolute value in the temperature range of -40°C to 170°C, A vibration wave is generated by exciting the electromechanical transducer, The electromechanical transducer element before being joined to the vibrating body has a change rate of the capacitance of the electromechanical transducer element at 0°C to 60°C of 0.5 to 3.9% in a temperature range from 0°C to 60°C. Vibrating body.

7. An electromechanical transducer element comprising a piezoelectric ceramic made of sodium potassium niobate metal oxide, the electromechanical transducer element having a temperature characteristic of a relative dielectric constant of 390 ppm / °C or less in absolute value in a temperature range of 0°C to 60°C, A vibration wave is generated by exciting the electromechanical transducer, The electromechanical transducer element before being joined to the vibrating body has a change rate of the capacitance of the electromechanical transducer element at 0°C to 60°C of 0.5 to 3.9% in a temperature range from 0°C to 60°C. Vibrating body.

8. An electromechanical transducer element made of a piezoelectric ceramic made of sodium potassium niobate metal oxide, the temperature characteristic of the relative dielectric constant being 500 ppm / °C or less in absolute value in the temperature range of -40°C to 170°C, A vibration wave is generated by exciting the electromechanical transducer, The electromechanical transducer element before being joined to the vibrating body has a change rate of the capacitance of the electromechanical transducer element at 0°C to 25°C in a range of -0.2 to 0.7% in a temperature range from 0°C to 25°C. Vibrating body.

9. An electromechanical transducer element comprising a piezoelectric ceramic made of sodium potassium niobate metal oxide, the electromechanical transducer element having a temperature characteristic of a relative dielectric constant of 390 ppm / °C or less in absolute value in a temperature range of 0°C to 60°C, A vibration wave is generated by exciting the electromechanical transducer, The electromechanical transducer element before being joined to the vibrating body has a change rate of the capacitance of the electromechanical transducer element at 0°C to 25°C in a range of -0.2 to 0.7% in a temperature range from 0°C to 25°C. Vibrating body.

10. An electromechanical transducer element made of a piezoelectric ceramic made of sodium potassium niobate metal oxide, the temperature characteristic of the relative dielectric constant being 500 ppm / °C or less in absolute value in the temperature range of -40°C to 170°C, A vibration wave is generated by exciting the electromechanical transducer, The electromechanical transducer joined to the vibrating body has a change rate of the electrostatic capacitance of the vibrating body at −20° C. to that at 60° C. in a temperature range of −20° C. to 60° C. of 15 to 22%. Vibrating body.

11. An electromechanical transducer element comprising a piezoelectric ceramic made of sodium potassium niobate metal oxide, the temperature characteristic of the relative dielectric constant being 390 ppm / °C or less in absolute value in the temperature range of 0°C to 60°C, A vibration wave is generated by exciting the electromechanical transducer, The electromechanical transducer joined to the vibrating body has a change rate of the electrostatic capacitance of the vibrating body at −20° C. to that at 60° C. in a temperature range of −20° C. to 60° C. of 15 to 22%. Vibrating body.

12. An electromechanical transducer element made of a piezoelectric ceramic made of sodium potassium niobate metal oxide, the temperature characteristic of the relative dielectric constant being 500 ppm / °C or less in absolute value in the temperature range of -40°C to 170°C, A vibration wave is generated by exciting the electromechanical transducer, The electromechanical transducer joined to the vibrating body has a change rate of the electrostatic capacitance of the vibrating body at 0°C to 60°C of 6 to 11% in a temperature range from 0°C to 60°C. Vibrating body.

13. An electromechanical transducer element comprising a piezoelectric ceramic made of sodium potassium niobate metal oxide, the temperature characteristic of the relative dielectric constant being 390 ppm / °C or less in absolute value in the temperature range of 0°C to 60°C, A vibration wave is generated by exciting the electromechanical transducer, The electromechanical transducer joined to the vibrating body has a change rate of the electrostatic capacitance of the vibrating body at 0°C to 60°C of 6 to 11% in a temperature range from 0°C to 60°C. Vibrating body.

14. An electromechanical transducer element made of a piezoelectric ceramic made of sodium potassium niobate metal oxide, the temperature characteristic of the relative dielectric constant being 500 ppm / °C or less in absolute value in the temperature range of -40°C to 170°C, A vibration wave is generated by exciting the electromechanical transducer, The electromechanical transducer joined to the vibrating body has a change rate of the electrostatic capacitance of the vibrating body at 0°C to 25°C of 3 to 7% in a temperature range from 0°C to 25°C. Vibrating body.

15. An electromechanical transducer element comprising a piezoelectric ceramic made of sodium potassium niobate metal oxide, the temperature characteristic of the relative dielectric constant being 390 ppm / °C or less in absolute value in the temperature range of 0°C to 60°C, A vibration wave is generated by exciting the electromechanical transducer, The electromechanical transducer joined to the vibrating body has a change rate of the electrostatic capacitance of the vibrating body at 0°C to 25°C of 3 to 7% in a temperature range from 0°C to 25°C. Vibrating body.

16. A vibrating body according to any one of claims 1 to 15, a relative motion member having a sliding surface that is in pressure contact with the driving surface of the vibrator and that is moved relatively by the vibration wave; An oscillatory wave motor having the above structure.

Images