Dicing tape and dicing die bond film

Abstract

To provide a dicing tape, etc., that can break semiconductor wafers well in a low-temperature expansion process.SOLUTION: The dicing tape includes a base material layer and an adhesive layer with higher adhesiveness than the base material layer. The volume crystallinity calculated from a differential scanning calorimetry result of the base material layer is 20 J / cm3 or more and 120 J / cm3 or less, and the thickness of the base material layer is 80 μm or more.SELECTED DRAWING: Figure 1

Description

[Technical field]

[0001] The present invention relates to a dicing tape used, for example, when manufacturing a semiconductor integrated circuit, and a dicing die bond film provided with the dicing tape. [Background technology]

[0002] Conventionally, a dicing die bond film used in the manufacture of semiconductor integrated circuits has been known. This type of dicing die bond film includes, for example, a dicing tape and a die bond layer laminated on the dicing tape and adhered to a wafer. The dicing tape has a base layer and an adhesive layer in contact with the die bond layer. This type of dicing die bond film is used, for example, as follows in the manufacture of semiconductor integrated circuits.

[0003] A method for manufacturing semiconductor integrated circuits generally includes a front-end process of forming a circuit surface on one side of a wafer using highly integrated electronic circuits, and a back-end process of cutting chips out of the wafer with the circuit surface formed thereon and assembling them.

[0004] The post-processing includes, for example, a dicing process in which grooves are formed in the wafer to divide the wafer into small chips (dies), a mounting process in which the surface of the wafer opposite to the circuit surface is attached to a die-bonding layer and the wafer is fixed to a dicing tape, an expanding process in which the wafer with the grooves formed is divided together with the die-bonding layer to expand the space between the chips, a pick-up process in which the die-bonding layer is peeled off from the adhesive layer to take out the chip (die) with the die-bonding layer attached, and a die-bonding process in which the chip (die) with the die-bonding layer attached is attached to an adherend. A semiconductor integrated circuit is manufactured through these processes.

[0005] In the above manufacturing method, in the expanding step, for example, with a wafer placed on the die bond layer overlapping the dicing tape, the dicing tape is stretched in the radial direction at a low temperature such as below freezing, and then further stretched at room temperature to widen the gap (kerf) between adjacent chips (dies). Then, in order to maintain the gap (kerf), a part of the dicing tape that has been stretched and has reduced tension is heat-shrunk. Specifically, the dicing tape on the outer side of the part overlapping the cleaved chip (die) is heat-shrunk, thereby maintaining the gap (kerf).

[0006] However, in the expanding step performed under low-temperature conditions, the semiconductor wafer and the die bond layer may not be cleaved together in some cases. In order to prevent such problems, the dicing tape is required to have the performance to be able to cleave the semiconductor wafer well by the expanding step under low-temperature conditions.

[0007] In contrast, conventional dicing tapes are known that have an initial elastic modulus of 200 MPa or more and 380 MPa or less at -10°C and a Tan δ (loss elastic modulus / storage elastic modulus) of 0.080 or more and 0.3 or less at -10°C (Patent Document 1). According to the dicing tape described in Patent Document 1, when a semiconductor wafer is attached via a die bond layer, the semiconductor wafer and the die bond layer can be cleaved together by an expanding process carried out under low temperature conditions. [Prior art documents] [Patent documents]

[0008] [Patent Document 1] JP 2015-185591 A Summary of the Invention [Problem to be solved by the invention]

[0009] However, it cannot be said that sufficient research has been conducted yet on a dicing die bond film or dicing tape that can satisfactorily cleave a semiconductor wafer in a low-temperature expanding process.

[0010] Therefore, an object of the present invention is to provide a dicing tape and a dicing die bond film that can satisfactorily cleave a semiconductor wafer in a low-temperature expanding process. [Means for solving the problem]

[0011] In order to solve the above problems, the dicing tape according to the present invention includes a base layer and a pressure-sensitive adhesive layer having higher adhesion than the base layer, The volume crystallinity of the base layer calculated from the differential scanning calorimetry is 20 J / cm 3 More than 120J / cm 3 and the thickness of the base layer is 80 μm or more. The dicing tape having the above-described configuration can effectively cleave a semiconductor wafer in a low-temperature expanding process.

[0012] In the above dicing tape, it is preferable that a chart obtained by measuring the base layer by differential scanning calorimetry has an endothermic peak, and the temperature at the apex of the endothermic peak is 100° C. or higher. This has the advantage that the crystallinity of the base layer is higher, and therefore the mechanical energy caused by the expansion can be propagated more efficiently in the base layer.

[0013] The dicing die bond film according to the present invention comprises the above-mentioned dicing tape and a die bond layer bonded to the dicing tape. Effect of the Invention

[0014] According to the dicing tape and dicing die bond film of the present invention, the semiconductor wafer can be excellently cleaved in the low-temperature expanding step. [Brief description of the drawings]

[0015] [Figure 1] FIG. 2 is a cross-sectional view of the dicing die bond film of the present embodiment cut in the thickness direction. [Figure 2A] 1A to 1C are cross-sectional views each showing a schematic view of a half-cut process in a manufacturing method of a semiconductor integrated circuit. [Figure 2B] 1A to 1C are cross-sectional views each showing a schematic view of a half-cut process in a manufacturing method of a semiconductor integrated circuit. [Figure 2C] 1A to 1C are cross-sectional views each showing a schematic view of a half-cut process in a manufacturing method of a semiconductor integrated circuit. [Figure 2D] 1A to 1C are cross-sectional views each showing a schematic view of a half-cut process in a manufacturing method of a semiconductor integrated circuit. [Figure 3A] 1A to 1C are cross-sectional views each showing a schematic view of a mounting step in a manufacturing method of a semiconductor integrated circuit. [Figure 3B] 1A to 1C are cross-sectional views each showing a schematic view of a mounting step in a manufacturing method of a semiconductor integrated circuit. [Figure 4A] 1A to 1C are cross-sectional views each showing a schematic diagram of an expanding step performed at a low temperature in a method for manufacturing a semiconductor integrated circuit. [Figure 4B] 1A to 1C are cross-sectional views each showing a schematic diagram of an expanding step performed at a low temperature in a method for manufacturing a semiconductor integrated circuit. [Figure 4C] 1A to 1C are cross-sectional views each showing a schematic diagram of an expanding step performed at a low temperature in a method for manufacturing a semiconductor integrated circuit. [Figure 5A] 1A to 1C are cross-sectional views each showing a schematic diagram of an expanding step at room temperature in a method for manufacturing a semiconductor integrated circuit. [Figure 5B] 1A to 1C are cross-sectional views each showing a schematic diagram of an expanding step at room temperature in a method for manufacturing a semiconductor integrated circuit. [Figure 6] 1A to 1C are cross-sectional views illustrating a pickup step in a manufacturing method of a semiconductor integrated circuit. [Figure 7A] FIG. 1 is a first chart showing an example of differential scanning calorimetry (Example 1). [Figure 7B] FIG. 2 is a second chart showing an example of differential scanning calorimetry (Example 1). [Figure 8A]FIG. 1 is a first chart showing an example of differential scanning calorimetry (Comparative Example 1). [Figure 8B] FIG. 2 is a second chart showing an example of differential scanning calorimetry (Comparative Example 1). DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0016] Hereinafter, an embodiment of a dicing die bond film and a dicing tape according to the present invention will be described with reference to the drawings.

[0017] The dicing die bond film 1 of this embodiment includes a dicing tape 20 and a die bond layer 10 that is laminated on an adhesive layer 22 of the dicing tape 20 and adhered to a semiconductor wafer.

[0018] The dicing tape 20 of this embodiment is usually a long sheet and is stored in a rolled state until it is used. The dicing die bond film 1 of this embodiment is stretched on a circular frame having an inner diameter slightly larger than the silicon wafer to be cut, and is used after being cut.

[0019] The dicing tape 20 of this embodiment includes a base layer 21 and an adhesive layer 22 overlapping the base layer 21 .

[0020] In the dicing tape 20 of this embodiment, the volume crystallinity of the base layer 21 calculated from the results of differential scanning calorimetry is 20 J / cm 3 More than 120J / cm 3 or less, and the thickness of the base layer 21 is 80 μm or more. The dicing tape 20 of this embodiment has the above-mentioned configuration, and therefore can satisfactorily cleave the semiconductor wafer in the low-temperature expanding step.

[0021] The volume crystallinity is a value determined based on the results of differential scanning calorimetry (DSC measurement) performed on the base layer 21. Specifically, differential scanning calorimetry (DSC measurement) of the base layer 21 is carried out under the following measurement conditions. The volume crystallinity is calculated as follows from a chart obtained from one measurement. Specifically, about 10 mg of the measurement sample is weighed out using a commercially available DSC measurement device, and measurement is performed in a nitrogen gas atmosphere at a temperature increase rate of 5° C. / min from room temperature (about 20° C.) to 200° C. The measurement sample is prepared by cutting the base layer 21 in the thickness direction. The amount of endothermic heat is calculated from the area of ​​the endothermic peak that appears on the chart obtained by differential scanning calorimetry (DSC measurement). The area of ​​the endothermic peak is calculated by determining the area enclosed by the baseline that connects the low-temperature point where there is no change in the heat quantity at the peak and the high-temperature point, and the curve line that depicts the endothermic peak. The amount of endothermic heat is calculated based on the endothermic peak associated with melting. The calculated amount of endothermic heat is converted to a value per volume. Note that, when the base material layer 21 is composed of multiple layers of different materials, multiple endothermic peaks may appear on the measurement chart. When calculating the amount of endothermic heat, the amount of endothermic heat is calculated from the area of ​​each endothermic peak due to each layer, and the sum of the amounts of endothermic heat is divided by the total volume of the base material layer 21, and the value is adopted as the volume crystallinity of the base material layer 21. The area of ​​the endothermic peak appearing in the measurement chart is calculated using analysis software attached to the DSC measuring device. In addition, although an exothermic peak or a curve due to a glass transition point may appear in the measurement chart, these are not treated as endothermic peaks. In addition, the temperatures of the peak start point (hereinafter also simply referred to as Point A), the peak apex (hereinafter also simply referred to as Point C), and the peak end point (hereinafter also simply referred to as Point B) of the endothermic peak appearing in the measurement chart are measured using analysis software attached to the DSC measurement device. Most preferably, the area of ​​the endothermic peak, the peak onset, the peak apex, and the peak end point are determined by specific analysis software described later in the Examples based on the results of measurement using a specific DSC measurement device described later in the Examples.

[0022] The volume crystallinity above is 20 J / cm 3 If the volume crystallinity is less than 120 J / cm, the crystallinity of the base layer 21 is insufficient, and the breakability may be poor. 3 If it is larger than this, the crystallinity of the base material layer 21 will be too high, and there is a risk that the base material layer 21 will break during expansion. The volume crystallinity above is 25 J / cm 3 More than 26 J / cm is preferable. 3 More preferably, it is 30 J / cm or more. 3 This has the advantage that better cleavability is exhibited in the low-temperature expanding step. The volume crystallinity above is 100 J / cm 3 It is preferable that the concentration is less than 90 J / cm 3 More preferably, it is 82 J / cm or less. 3 It is more preferable that the thickness is not more than 100 mm. This has the advantage that breakage of the base material layer 21 during expansion is further suppressed.

[0023] For example, the volume crystallinity can be increased by forming the base layer 21 from a resin material having a higher degree of crystallinity, or by carrying out a slow cooling treatment or a stretching treatment when producing the base layer 21. On the other hand, the volume crystallinity can be decreased by forming the base layer 21 from a resin material having a lower degree of crystallinity, or by not carrying out a rapid cooling treatment or a stretching treatment when producing the base layer 21.

[0024] A chart obtained by measuring the base material layer 21 by differential scanning calorimetry (DSC) preferably has an endothermic peak having an apex (point C) in the range of 100° C. to 140° C. Such an endothermic peak is, for example, an endothermic peak that appears with the melting of a resin. The endothermic peak apex (point C) at 100°C or higher has the advantage that the material can be quickly solidified after the heat shrink is completed to maintain the kerf. It also has the advantage that better cleavability is exhibited. It is more preferable that the endothermic peak apex (point C) be at 105°C or higher. The endothermic peak apex (point C) being at 140° C. or lower has the advantage that sufficient heat shrinkage can be achieved during heat shrinking. The endothermic peak apex (point C) is more preferably at 135° C. or lower. In addition, when there are multiple endothermic peaks in the range of 100° C. to 140° C., it is preferable that at least one of these endothermic peaks satisfies the above condition (peak apex). Similarly, it is preferable that at least one of the endothermic peaks satisfies the following conditions (peak start point, peak end point, etc.).

[0025] For example, the apex (point C) of the endothermic peak can be shifted to a higher temperature by forming the base material layer 21 from a resin material having a higher melting point, constructing the base material layer 21 in a laminated structure using a layer of a resin material having a higher melting point, or blending (blending) a resin material having a higher melting point into the base material layer 21. On the other hand, the temperature of the apex (point C) of the endothermic peak can be shifted to a lower temperature by forming the base material layer 21 from a resin material having a lower melting point, constructing the base material layer 21 in a laminated structure using a layer of a resin material having a lower melting point, or blending (blending) a resin material having a lower melting point into the base material layer 21.

[0026] The temperature difference between the peak onset point (point A) and the peak apex (point C) in the endothermic peak is preferably 40° C. or less, more preferably 35° C. or less. By setting the temperature difference to 40° C. or less, the melting of the base material layer 21 can be completed with a smaller (narrower) temperature difference. Therefore, the base material layer 21 can be solidified and softened with a smaller temperature difference. Therefore, by thermally shrinking (heat shrinking) the base material layer 21 after expanding and quickly solidifying it after the heat shrinking is completed, the distance (kerf) between adjacent chips (dies) can be efficiently maintained. The temperature difference between the peak onset point (point A) and the peak apex (point C) of the endothermic peak may be 20° C. or more.

[0027] For example, by increasing the molecular weight dispersity of the resin (polymer) contained in the base layer 21, the temperature difference between the peak start point (point A) and the peak apex (point C) in the endothermic peak can be increased. For example, by decreasing the molecular weight dispersity of the resin (polymer) contained in the base layer 21, the temperature difference between the peak start point (point A) and the peak apex (point C) in the endothermic peak can be decreased.

[0028] In the above dicing tape, the temperature difference between the peak start point (point A) and the peak end point (point B) at the endothermic peak of the base material layer 21 is preferably 60° C. or less, and more preferably 50° C. or less. When the temperature difference is 60° C. or less, the temperature difference from the start of melting to the end of melting of the base material layer 21 becomes smaller, so that the base material layer 21 can be solidified and softened with a smaller temperature difference. This has the advantage that the above-mentioned thermal shrinkage performed after expanding can be efficiently performed. Such a temperature difference may be 30° C. or more.

[0029] For example, the temperature difference between the peak start point (point A) and the peak end point (point B) can be made smaller by decreasing the molecular weight dispersity of the resin (polymer) contained in the base layer 21. On the other hand, the temperature difference between the peak start point (point A) and the peak end point (point B) can be made larger by increasing the molecular weight dispersity of the resin (polymer) contained in the base layer 21.

[0030] In the above dicing tape, the temperature of the peak start point (point A) at the endothermic peak of the base material layer 21 is preferably 70°C or higher, more preferably 80°C or higher. The peak start point (point A) is an index of the temperature at which solidification of the base material layer 21 is completed, and when the temperature of the peak start point is 70°C or higher, the base material layer 21, once softened by the heater, starts to cool and completes solidification at a relatively high temperature. If the temperature is lower than 70°C, solidification of the base material layer 21 is completed, so that the above-mentioned thermal contraction after expansion can be sufficiently performed. Therefore, the kerf can be efficiently maintained in a good condition after expansion. The temperature at the peak onset point (point A) may be 110° C. or lower, or may be 100° C. or lower.

[0031] For example, the temperature of the peak onset point (point A) can be shifted to a higher temperature by forming the base material layer 21 with a resin material having a higher melting point, constructing the base material layer 21 in a laminated structure using a layer of a resin material having a higher melting point, or blending (blending) a resin material having a higher melting point into the base material layer 21. On the other hand, the temperature of the peak onset point (point A) can be shifted to a lower temperature by forming the base material layer 21 with a resin material having a lower melting point, constructing the base material layer 21 in a laminated structure using a layer of a resin material having a lower melting point, or blending (blending) a resin material having a lower melting point into the base material layer 21.

[0032] In the above dicing tape, the temperature of the peak end point (point B) of the endothermic peak of the base material layer 21 is preferably 150° C. or less, and more preferably 140° C. or less. The peak end point (point B) is an index of the temperature at which softening of the base material layer 21 is completed, and since the temperature of the peak end point is 150° C. or less, even if the heating temperature of the heater is somewhat low, the base material layer 21 is sufficiently softened as long as it is higher than 150° C. Therefore, even if the heating temperature for softening is somewhat low, the above-mentioned thermal shrinkage can be efficiently performed, and therefore the kerf can be efficiently maintained after expansion. The temperature at the peak end point (point B) may be 110° C. or higher, or 120° C. or higher.

[0033] For example, the temperature of the peak end point (point B) can be shifted to a lower temperature by forming the base material layer 21 with a resin material having a lower melting point, constructing the base material layer 21 in a laminated structure using a layer of a resin material having a lower melting point, or blending (blending) a resin material with a lower melting point into the base material layer 21. On the other hand, the temperature of the peak end point (point B) can be shifted to a higher temperature by forming the base material layer 21 with a resin material having a higher melting point, constructing the base material layer 21 in a laminated structure using a layer of a resin material having a higher melting point, or blending (blending) a resin material with a higher melting point into the base material layer 21.

[0034] The base layer 21 may have a single-layer structure or a multilayer structure. Each layer of the base material layer 21 is, for example, a metal foil, a fiber sheet such as paper or cloth, a rubber sheet, or a resin film. Examples of the fiber sheet constituting the base layer 21 include paper, woven fabric, and nonwoven fabric. Examples of materials for the resin film include polyolefins such as polyethylene (PE), polypropylene (PP), and ethylene-propylene copolymers; ethylene copolymers such as ethylene-vinyl acetate copolymers (EVA), ionomer resins, ethylene-(meth)acrylic acid copolymers, and ethylene-(meth)acrylic acid ester (random, alternating) copolymers; polyesters such as polyethylene terephthalate (PET), polyethylene naphthalate (PEN), and polybutylene terephthalate (PBT); polyacrylates; polyvinyl chloride (PVC); polyurethanes; polycarbonates; polyphenylene sulfide (PPS); polyamides such as aliphatic polyamides and fully aromatic polyamides (aramids); polyether ether ketones (PEEK); polyimides; polyetherimides; polyvinylidene chloride; ABS (acrylonitrile-butadiene-styrene copolymers); cellulose or cellulose derivatives; silicone-containing polymers; and fluorine-containing polymers. These may be used alone or in combination of two or more.

[0035] The base layer 21 is preferably made of a polymeric material such as a resin film. When the base layer 21 has a resin film, the resin film may be subjected to a stretching process or the like to control the deformability such as elongation percentage. The surface of the base layer 21 may be subjected to a surface treatment in order to enhance adhesion with the pressure-sensitive adhesive layer 22. Examples of the surface treatment that can be used include oxidation treatment by chemical or physical methods such as chromate treatment, ozone exposure, flame exposure, high-voltage shock exposure, and ionizing radiation treatment. In addition, the base layer 21 may be subjected to a coating treatment using a coating agent such as an anchor coating agent, a primer, or an adhesive.

[0036] The base layer 21 is preferably composed of a plurality of layers, more preferably composed of at least three layers, and even more preferably composed of three layers. By having the base layer 21 have a laminated structure of multiple layers (e.g., a three-layer structure), it is possible to laminate a layer having a higher elastic modulus and a layer having a lower elastic modulus, which has the advantage that the elastic modulus of the base layer 21 can be controlled relatively easily. For example, in the case of a base layer having only a layer having a relatively high elastic modulus, the chip may lift or the base may break during the expanding process. Also, in the case of a base layer having only a layer having a relatively low elastic modulus, it may not be possible to transmit sufficient stress to the base layer to break it by expanding.

[0037] The three-layered base layer 21 preferably has two non-elastomer layers (X, X) made of a non-elastomer, and an elastomer layer (Y) disposed between the two non-elastomer layers and made of an elastomer (X layer / Y layer / X layer). The elastomer layer is a layer having an elastic modulus of 200 MPa or less at room temperature. The elastomer layer is usually formed of a polymer material that exhibits rubber elasticity at room temperature (23°C). On the other hand, the non-elastomer layer is a layer having an elastic modulus of more than 200 MPa at room temperature. Each layer of the elastomer having such a three-layer laminate structure is usually formed of a resin. The elastomer having a three-layer laminate structure is produced, for example, by coextrusion molding, and the three layers are integrated together.

[0038] In the base layer 21 having a three-layer structure, the ratio of the thickness of the inner layer to the thickness of one outer layer (Y thickness / X thickness) is preferably 5 or more and 15 or less.

[0039] The non-elastomer layer disposed on the outside has a melting point of, for example, 100° C. or more and 140° C. or less. In addition, the non-elastomer layer preferably has a molecular weight distribution dispersity (mass average molecular weight / number average molecular weight) of 3 or less when the constituent resin is measured by GPC.

[0040] The non-elastomer layer (X) may include low density polyethylene (LDPE), high density polyethylene (HDPE), polypropylene, etc. Examples of polypropylene include homopolymers (homopolypropylene) and copolymers such as random polypropylene and block polypropylene. The polypropylene may be metallocene polypropylene synthesized by a metallocene catalyst. The non-elastomer layer (X) preferably includes metallocene polypropylene.

[0041] On the other hand, the elastomer layer (Y) preferably contains an ethylene-vinyl acetate copolymer (EVA) or an α-olefin-based thermoplastic elastomer, and more preferably contains an ethylene-vinyl acetate copolymer (EVA). Examples of the α-olefin-based thermoplastic elastomer include an α-olefin homopolymer and a copolymer of two or more α-olefins. The ethylene-vinyl acetate copolymer resin (EVA) may contain 5% by mass or more and 35% by mass or less of vinyl acetate structural units.

[0042] The thickness (total thickness) of the base layer 21 is 80 μm or more. This thickness may be more than 100 μm. This thickness may be 150 μm or less. This value is the average value of measurements taken at least at three randomly selected locations. Hereinafter, the average value is also used for the thickness of the adhesive layer 22. If the thickness of the base material layer 21 is less than 80 μm, there is a risk that stress cannot be applied uniformly to the entire base material layer 21, and good cleavability may not be exhibited in the low-temperature expanding step.

[0043] The back side of the base material layer 21 (the side on which the adhesive layer 22 is not overlapped) may be subjected to a release treatment using a release agent (release agent) such as a silicone-based resin or a fluorine-based resin in order to impart releasability. The base layer 21 is preferably a light-transmitting (ultraviolet ray-transmitting) resin film or the like, since it allows active energy rays such as ultraviolet ray to be applied to the pressure-sensitive adhesive layer 22 from the back side.

[0044] The dicing tape 20 of this embodiment may include a release sheet that covers one surface of the adhesive layer 22 (the surface where the adhesive layer 22 does not overlap the base layer 21) before use. When the die bond layer 10, which has an area smaller than that of the adhesive layer 22, is arranged so as to be contained within the adhesive layer 22, the release sheet is arranged so as to cover both the adhesive layer 22 and the die bond layer 10. The release sheet is used to protect the adhesive layer 22, and is peeled off before the die bond layer 10 is attached to the adhesive layer 22.

[0045] As the release sheet, for example, a plastic film or paper that has been surface-treated with a release agent such as a silicone-based, long-chain alkyl-based, fluorine-based, or molybdenum sulfide-based release agent can be used. Furthermore, examples of the release sheet that can be used include films made of fluorine-based polymers such as polytetrafluoroethylene, polychlorotrifluoroethylene, polyvinyl fluoride, polyvinylidene fluoride, tetrafluoroethylene-hexafluoropropylene copolymer, and chlorofluoroethylene-vinylidene fluoride copolymer; films made of polyolefins such as polyethylene and polypropylene; and films made of polyesters such as polyethylene terephthalate (PET). As the release sheet, for example, a plastic film or paper whose surface is coated with a release agent such as a fluorine-based release agent or a long-chain alkyl acrylate-based release agent can be used. The release sheet can be used as a support material for supporting the adhesive layer 22. In particular, the release sheet is preferably used when the adhesive layer 22 is overlaid on the base layer 21. In detail, the adhesive layer 22 is overlaid on the base layer 21 in a state where the release sheet and the adhesive layer 22 are laminated, and after overlaying, the release sheet is peeled off (transferred), thereby overlaying the adhesive layer 22 on the base layer 21.

[0046] In this embodiment, the pressure-sensitive adhesive layer 22 contains, for example, an acrylic polymer, an isocyanate compound, and a polymerization initiator. The pressure-sensitive adhesive layer 22 preferably has a thickness of 5 μm or more and 40 μm or less. The shape and size of the pressure-sensitive adhesive layer 22 are usually the same as the shape and size of the base layer 21.

[0047] In the dicing tape 20 of this embodiment, the proportion of the thickness of the adhesive layer 22 to the total thickness of the dicing tape 20 may be 5% or more and 30% or less.

[0048] The acrylic polymer has at least an alkyl (meth)acrylate structural unit, a hydroxyl group-containing (meth)acrylate structural unit, and a polymerizable group-containing (meth)acrylate structural unit in the molecule. The structural units are units that constitute the main chain of the acrylic polymer. Each side chain in the acrylic polymer is included in each structural unit that constitutes the main chain. In this specification, the term "(meth)acrylate" refers to at least one of methacrylate (methacrylic acid ester) and acrylate (acrylic acid ester). Similarly, the term "(meth)acrylic acid" refers to at least one of methacrylic acid and acrylic acid.

[0049] In the acrylic polymer contained in the pressure-sensitive adhesive layer 22, the above-mentioned structural unit is 1 H-NMR, 13 This can be confirmed by NMR analysis such as C-NMR, pyrolysis GC / MS analysis, infrared spectroscopy, etc. The molar ratio of the above-mentioned structural units in the acrylic polymer is usually calculated from the blend amount (charge amount) when the acrylic polymer is polymerized.

[0050] The constituent unit of the alkyl (meth)acrylate is derived from an alkyl (meth)acrylate monomer. In other words, the molecular structure after the alkyl (meth)acrylate monomer is polymerized is the constituent unit of the alkyl (meth)acrylate. The term "alkyl" refers to the number of carbon atoms in the hydrocarbon portion ester-bonded to the (meth)acrylic acid. The hydrocarbon portion of the alkyl portion in the structural unit of the alkyl (meth)acrylate may be a saturated hydrocarbon or an unsaturated hydrocarbon. It is preferable that the alkyl portion does not contain a polar group containing oxygen (O) or nitrogen (N). This can prevent the polarity of the alkyl polymer from becoming extremely high. Therefore, the adhesive layer 22 is prevented from having excessive affinity for the die bond layer 10. Therefore, the dicing tape 20 can be more satisfactorily peeled off from the die bond layer 10. The number of carbon atoms in the alkyl portion may be 6 or more and 10 or less.

[0051] Examples of the alkyl (meth)acrylate structural unit include hexyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, nonyl (meth)acrylate, and decyl (meth)acrylate structural units.

[0052] The acrylic polymer has a hydroxyl group-containing (meth)acrylate structural unit, and the hydroxyl group of such a structural unit easily reacts with an isocyanate group. By allowing the acrylic polymer having a hydroxyl group-containing (meth)acrylate structural unit and the isocyanate compound to coexist in the adhesive layer 22, the adhesive layer 22 can be appropriately cured. Therefore, the acrylic polymer can be sufficiently gelled. Therefore, the adhesive layer 22 can exhibit adhesive performance while maintaining its shape.

[0053] The structural unit of the hydroxyl group-containing (meth)acrylate is preferably a structural unit of a hydroxyl group-containing C2-C4 alkyl (meth)acrylate. The term "C2-C4 alkyl" refers to the number of carbon atoms in the hydrocarbon moiety that is ester-bonded to the (meth)acrylic acid. In other words, the hydroxyl group-containing C2-C4 alkyl (meth)acrylate monomer refers to a monomer in which (meth)acrylic acid is ester-bonded to an alcohol having 2 to 4 carbon atoms (usually a dihydric alcohol). The hydrocarbon portion of the C2-C4 alkyl is usually a saturated hydrocarbon. For example, the hydrocarbon portion of the C2-C4 alkyl is a linear saturated hydrocarbon or a branched saturated hydrocarbon. It is preferable that the hydrocarbon portion of the C2-C4 alkyl does not contain a polar group containing oxygen (O), nitrogen (N), or the like.

[0054] Examples of the structural unit of the hydroxyl group-containing C2-C4 alkyl(meth)acrylate include structural units of hydroxybutyl(meth)acrylate such as hydroxyethyl(meth)acrylate, hydroxypropyl(meth)acrylate, hydroxyn-butyl(meth)acrylate, or hydroxyiso-butyl(meth)acrylate. In the structural unit of hydroxybutyl(meth)acrylate, the hydroxyl group (-OH group) may be bonded to the terminal carbon (C) of the hydrocarbon moiety, or may be bonded to a carbon (C) other than the terminal of the hydrocarbon moiety.

[0055] The acrylic polymer contains a structural unit of a polymerizable group-containing (meth)acrylate having a polymerizable unsaturated double bond in the side chain. Since the acrylic polymer contains a structural unit of a polymerizable group-containing (meth)acrylate, the adhesive layer 22 can be cured by irradiation with active energy rays (ultraviolet rays, etc.) before the pick-up step. In particular, the irradiation with active energy rays such as ultraviolet rays generates radicals from the photopolymerization initiator, and the acrylic polymers can be crosslinked by the action of these radicals. This makes it possible to reduce the adhesive strength of the adhesive layer 22 before irradiation. Then, the die bond layer 10 can be peeled off well from the adhesive layer 22. The active energy rays include ultraviolet rays, radioactive rays, and electron beams.

[0056] Specifically, the structural unit of the polymerizable group-containing (meth)acrylate may have a molecular structure in which an isocyanate group of an isocyanate group-containing (meth)acrylate monomer is bonded via urethane to a hydroxyl group in the structural unit of the above-mentioned hydroxyl group-containing (meth)acrylate.

[0057] The structural unit of the polymerizable group-containing (meth)acrylate having a polymerizable group can be prepared after polymerization of the acrylic polymer. For example, after copolymerization of an alkyl (meth)acrylate monomer and a hydroxyl group-containing (meth)acrylate monomer, the hydroxyl group in a part of the structural unit of the hydroxyl group-containing (meth)acrylate and the isocyanate group of the isocyanate group-containing polymerizable monomer are reacted to form a urethane reaction, thereby obtaining the structural unit of the polymerizable group-containing (meth)acrylate.

[0058] The isocyanate group-containing (meth)acrylate monomer preferably has one isocyanate group and one (meth)acryloyl group in the molecule. Examples of such monomers include 2-(meth)acryloyloxyethyl isocyanate (2-isocyanatoethyl (meth)acrylate).

[0059] The pressure-sensitive adhesive layer 22 of the dicing tape 20 in this embodiment further contains an isocyanate compound. A part of the isocyanate compound may be in a state after being reacted by a urethanization reaction or the like. The isocyanate compound has a plurality of isocyanate groups in the molecule. The isocyanate compound has a plurality of isocyanate groups in the molecule, which allows a crosslinking reaction between the acrylic polymers in the pressure-sensitive adhesive layer 22 to proceed. In detail, one isocyanate group of the isocyanate compound is reacted with a hydroxyl group of an acrylic polymer, and the other isocyanate group is reacted with a hydroxyl group of another acrylic polymer, whereby a crosslinking reaction via the isocyanate compound can proceed.

[0060] Examples of the isocyanate compound include diisocyanates such as aliphatic diisocyanates, alicyclic diisocyanates, and araliphatic diisocyanates.

[0061] Further, examples of the isocyanate compound include polymerized polyisocyanates such as dimers and trimers of diisocyanates, and polymethylene polyphenylene polyisocyanates.

[0062] In addition, the isocyanate compound may be, for example, a polyisocyanate obtained by reacting an excess amount of the above-mentioned isocyanate compound with an active hydrogen-containing compound. Examples of the active hydrogen-containing compound include an active hydrogen-containing low molecular weight compound and an active hydrogen-containing high molecular weight compound. As the isocyanate compound, allophanated polyisocyanate, biuretized polyisocyanate, etc. can also be used. The above isocyanate compounds can be used alone or in combination of two or more.

[0063] The isocyanate compound is preferably a reaction product of an aromatic diisocyanate and an active hydrogen-containing low molecular weight compound. The reaction rate of the isocyanate group in the reaction product of the aromatic diisocyanate is relatively slow, so that the pressure-sensitive adhesive layer 22 containing such a reaction product is prevented from being excessively hardened. The isocyanate compound is preferably one having three or more isocyanate groups in the molecule.

[0064] The polymerization initiator contained in the adhesive layer 22 is a compound that can initiate a polymerization reaction by the applied heat or light energy. By including a polymerization initiator in the adhesive layer 22, a crosslinking reaction between acrylic polymers can be promoted when heat energy or light energy is applied to the adhesive layer 22. In detail, a polymerization reaction between polymerizable groups between acrylic polymers having structural units of polymerizable group-containing (meth)acrylate can be initiated to harden the adhesive layer 22. This reduces the adhesive force of the adhesive layer 22, and in the pick-up process, the die bond layer 10 can be easily peeled off from the hardened adhesive layer 22. As the polymerization initiator, for example, a photopolymerization initiator or a thermal polymerization initiator is used. As the polymerization initiator, a general commercially available product can be used.

[0065] The pressure-sensitive adhesive layer 22 may further contain other components in addition to the above-mentioned components. Examples of the other components include tackifiers, plasticizers, fillers, antioxidants, antioxidants, UV absorbers, light stabilizers, heat stabilizers, antistatic agents, surfactants, and light release agents. The types and amounts of the other components may be appropriately selected depending on the purpose.

[0066] Next, the dicing die bond film 1 of the present embodiment will be described in detail.

[0067] The dicing die bond film 1 of this embodiment includes the above-mentioned dicing tape 20 and a die bond layer 10 laminated on the adhesive layer 22 of the dicing tape 20. The die bond layer 10 is to be adhered to a semiconductor wafer in the manufacture of a semiconductor integrated circuit.

[0068] The die bond layer 10 may contain at least one of a thermosetting resin and a thermoplastic resin. The die bond layer 10 preferably contains a thermosetting resin and a thermoplastic resin.

[0069] Examples of the thermosetting resin include epoxy resin, phenol resin, amino resin, unsaturated polyester resin, polyurethane resin, silicone resin, and thermosetting polyimide resin. As the thermosetting resin, only one type or two or more types are adopted. As the thermosetting resin, epoxy resin is preferable in that it contains less ionic impurities that may cause corrosion of the semiconductor chip to be die-bonded. As the curing agent for epoxy resin, phenol resin is preferable.

[0070] Examples of the epoxy resin include bisphenol A type, bisphenol F type, bisphenol S type, brominated bisphenol A type, hydrogenated bisphenol A type, bisphenol AF type, biphenyl type, naphthalene type, fluorene type, phenol novolac type, orthocresol novolac type, trishydroxyphenylmethane type, tetraphenylolethane type, hydantoin type, trisglycidyl isocyanurate type, and glycidylamine type epoxy resins.

[0071] Phenol resins can act as curing agents for epoxy resins. Examples of phenol resins include novolac-type phenol resins, resol-type phenol resins, and polyoxystyrenes such as polyparaoxystyrene. Examples of novolac-type phenolic resins include phenol novolac resins, phenol aralkyl resins, cresol novolac resins, tert-butylphenol novolac resins, and nonylphenol novolac resins. As the phenolic resin, one kind or two or more kinds may be adopted.

[0072] In the die bond layer 10, the amount of the hydroxyl group of the phenol resin per equivalent of the epoxy group of the epoxy resin is preferably 0.5 equivalents or more and 2.0 equivalents or less, more preferably 0.7 equivalents or more and 1.5 equivalents or less, so that the curing reaction between the epoxy resin and the phenol resin can be sufficiently promoted.

[0073] When the die bond layer 10 contains a thermosetting resin, the content ratio of the thermosetting resin in the die bond layer 10 is preferably 5 mass % or more and 60 mass % or less, and more preferably 10 mass % or more and 50 mass % or less, relative to the total mass of the die bond layer 10. This allows the die bond layer 10 to appropriately exhibit its function as a thermosetting adhesive.

[0074] Examples of thermoplastic resins that can be included in the die bond layer 10 include natural rubber, butyl rubber, isoprene rubber, chloroprene rubber, ethylene-vinyl acetate copolymer, ethylene-acrylic acid copolymer, ethylene-acrylic acid ester copolymer, polybutadiene resin, polycarbonate resin, thermoplastic polyimide resin, polyamide resin such as 6-nylon and 6,6-nylon (trade name), phenoxy resin, acrylic resin, saturated polyester resin such as PET and PBT, polyamideimide resin, fluororesin, and the like. As the thermoplastic resin, an acrylic resin is preferable since it has a small amount of ionic impurities and a high heat resistance, and therefore the adhesiveness of the die bond layer 10 can be further ensured. As the thermoplastic resin, one kind or two or more kinds may be adopted.

[0075] The acrylic resin is preferably a polymer in which the constituent units in the molecule are primarily alkyl (meth)acrylates, for example, C2 to C4 alkyl (meth)acrylates. The acrylic resin may contain a structural unit derived from another monomer component copolymerizable with the alkyl (meth)acrylate monomer. Examples of the other monomer components include carboxy group-containing monomers, acid anhydride monomers, hydroxy group-containing monomers, glycidyl group-containing monomers, sulfonic acid group-containing monomers, phosphoric acid group-containing monomers, functional group-containing monomers such as acrylamide and acrylonitrile, and various other polyfunctional monomers. The acrylic resin is preferably a copolymer of an alkyl(meth)acrylate (particularly an alkyl(meth)acrylate having an alkyl portion with 4 or less carbon atoms), a carboxy group-containing monomer, a nitrogen atom-containing monomer, and a polyfunctional monomer (particularly a polyglycidyl-based polyfunctional monomer), in that it can exert a higher cohesive force in the die bond layer 10, and more preferably a copolymer of ethyl acrylate, butyl acrylate, acrylic acid, acrylonitrile, and polyglycidyl(meth)acrylate.

[0076] The glass transition temperature (Tg) of the acrylic resin is preferably −50° C. or higher and 50° C. or lower, and more preferably 10° C. or higher and 30° C. or lower, in that the elasticity and viscosity of the die bond layer 10 can be easily set within a desired range.

[0077] When the die bond layer 10 contains a thermosetting resin and a thermoplastic resin, the content of the thermoplastic resin in the die bond layer 10 is preferably 30% by mass or more and 70% by mass or less, more preferably 40% by mass or more and 60% by mass or less, and even more preferably 45% by mass or more and 55% by mass or less, based on the total mass of organic components excluding the filler (e.g., thermosetting resin, thermoplastic resin, curing catalyst, silane coupling agent, dye). Note that the elasticity and viscosity of the die bond layer 10 can be adjusted by changing the content of the thermosetting resin.

[0078] When the thermoplastic resin of the die bond layer 10 has a thermosetting functional group, for example, a thermosetting functional group-containing acrylic resin can be used as the thermoplastic resin. This thermosetting functional group-containing acrylic resin preferably contains a structural unit derived from an alkyl (meth)acrylate in the molecule in the largest mass ratio. Examples of the alkyl (meth)acrylate include the alkyl (meth)acrylates exemplified above. On the other hand, examples of the thermosetting functional group in the thermosetting functional group-containing acrylic resin include a glycidyl group, a carboxy group, a hydroxy group, and an isocyanate group. The die bond layer 10 preferably contains a thermosetting functional group-containing acrylic resin and a curing agent. When the thermosetting functional group in the thermosetting functional group-containing acrylic resin is a glycidyl group, it is preferable to use a compound having multiple phenol structures as the curing agent. For example, the above-mentioned various phenol resins can be used as the curing agent.

[0079] The die bond layer 10 preferably contains a filler. By changing the amount of the filler in the die bond layer 10, the elasticity and viscosity of the die bond layer 10 can be more easily adjusted. Furthermore, the physical properties of the die bond layer 10, such as electrical conductivity, thermal conductivity, and elastic modulus, can be adjusted. The filler may be an inorganic filler or an organic filler, and the inorganic filler is preferred. Examples of inorganic fillers include fillers containing aluminum hydroxide, magnesium hydroxide, calcium carbonate, magnesium carbonate, calcium silicate, magnesium silicate, calcium oxide, magnesium oxide, aluminum oxide, aluminum nitride, boron nitride, silica such as crystalline silica and amorphous silica, etc. Examples of materials for inorganic fillers include simple metals such as aluminum, gold, silver, copper, nickel, etc., and alloys. Fillers such as aluminum borate whiskers, amorphous carbon black, graphite, etc. The shape of the filler may be various shapes such as spherical, needle-like, and flake-like. As the filler, only one of the above types or two or more types are used.

[0080] The average particle size of the filler is preferably 0.005 μm or more and 10 μm or less, more preferably 0.005 μm or more and 1 μm or less. When the average particle size is 0.005 μm or more, the wettability and adhesiveness to an adherend such as a semiconductor wafer are further improved. When the average particle size is 10 μm or less, the characteristics of the added filler can be more fully exhibited, and the heat resistance of the die bond layer 10 can be further exhibited. The average particle size of the filler can be determined, for example, using a photometric particle size distribution meter (for example, product name "LA-910", manufactured by Horiba, Ltd.).

[0081] When the die bond layer 10 contains a filler, the content of the filler is preferably 30 mass% or more and 70 mass% or less, more preferably 40 mass% or more and 60 mass% or less, and even more preferably 42 mass% or more and 55 mass% or less, relative to the total mass of the die bond layer 10.

[0082] The die bond layer 10 may contain other components as necessary, such as a curing catalyst, a flame retardant, a silane coupling agent, an ion trapping agent, and a dye. Examples of the flame retardant include antimony trioxide, antimony pentoxide, and brominated epoxy resins. Examples of the silane coupling agent include β-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, γ-glycidoxypropyltrimethoxysilane, and γ-glycidoxypropylmethyldiethoxysilane. Examples of the ion trapping agent include hydrotalcites, bismuth hydroxide, and benzotriazole. As the other additives, one kind may be used alone, or two or more kinds may be used in combination.

[0083] The die bond layer 10 preferably contains a thermoplastic resin (particularly, an acrylic resin), a thermosetting resin, and a filler, in that the elasticity and viscosity can be easily adjusted.

[0084] The thickness of the die bond layer 10 is not particularly limited, but is, for example, 1 μm or more and 200 μm or less. The thickness may be 3 μm or more and 150 μm or less, or 5 μm or more and 100 μm or less. When the die bond layer 10 is a laminate, the above thickness is the total thickness of the laminate.

[0085] The glass transition temperature (Tg) of the die bond layer 10 is preferably 0° C. or higher, and more preferably 10° C. or higher. When the glass transition temperature is 0° C. or higher, the die bond layer 10 can be easily fractured by low-temperature expansion. The upper limit of the glass transition temperature of the die bond layer 10 is, for example, 100° C.

[0086] The die bond layer 10 may have a single-layer structure, for example, as shown in Fig. 1. In this specification, a single layer means having only layers formed of the same composition. A form in which multiple layers formed of the same composition are laminated is also a single layer. On the other hand, the die bond layer 10 may have a multi-layer structure in which layers each formed of two or more different compositions are laminated.

[0087] In the dicing die bond film 1 of this embodiment, when used, the adhesive layer 22 is cured by irradiation with active energy rays (e.g., ultraviolet rays). In detail, in a state in which the die bond layer 10 having a semiconductor wafer bonded to one surface and the adhesive layer 22 bonded to the other surface of the die bond layer 10 are laminated, ultraviolet rays or the like are irradiated to at least the adhesive layer 22. For example, ultraviolet rays or the like are irradiated from the side where the base layer 21 is disposed, and the ultraviolet rays or the like reach the adhesive layer 22 after passing through the base layer 21. The adhesive layer 22 is cured by irradiation with ultraviolet rays or the like. Since the adhesive layer 22 hardens after irradiation, the adhesive strength of the adhesive layer 22 can be reduced, so that the die bond layer 10 (to which the semiconductor wafer is adhered) can be relatively easily peeled off from the adhesive layer 22 after irradiation.

[0088] The dicing die bond film 1 of this embodiment may be provided with a release sheet that covers one surface of the die bond layer 10 (the surface where the die bond layer 10 does not overlap with the adhesive layer 22) before use. The release sheet is used to protect the die bond layer 10, and is peeled off immediately before attaching an adherend (e.g., a semiconductor wafer) to the die bond layer 10. As this release sheet, the same release sheet as described above can be used. This release sheet can be used as a support material for supporting the die bond layer 10. The release sheet is preferably used when the die bond layer 10 is overlaid on the adhesive layer 22. In detail, the die bond layer 10 is overlaid on the adhesive layer 22 in a state in which the release sheet and the die bond layer 10 are laminated, and after overlaying, the release sheet is peeled off (transferred), so that the die bond layer 10 can be overlaid on the adhesive layer 22.

[0089] Since the dicing die bond film 1 of the present embodiment is configured as described above, it can favorably cleave the semiconductor wafer in the low-temperature expanding step described later.

[0090] Next, a method for manufacturing the dicing tape 20 and the dicing die bond film 1 of this embodiment will be described.

[0091] The manufacturing method of the dicing die bond film 1 of this embodiment is as follows: The method includes a step of producing a dicing tape 20 (a method of producing a dicing tape), and a step of producing a dicing die bond film 1 by overlaying a die bond layer 10 on the produced dicing tape 20.

[0092] The manufacturing method of the dicing tape (the process of manufacturing the dicing tape) is as follows: A synthesis step of synthesizing an acrylic polymer; a pressure-sensitive adhesive layer preparation step of preparing a pressure-sensitive adhesive layer 22 by volatilizing a solvent from a pressure-sensitive adhesive composition containing the above-mentioned acrylic polymer, an isocyanate compound, a polymerization initiator, a solvent, and other components appropriately added depending on the purpose; a base layer preparation step of preparing a base layer 21; The method further includes a lamination step of laminating the adhesive layer 22 and the base layer 21 together to laminate the base layer 21 and the adhesive layer 22 together.

[0093] In the synthesis step, for example, an acrylic polymer intermediate is synthesized by radically polymerizing a C9 to C11 alkyl (meth)acrylate monomer and a hydroxyl group-containing (meth)acrylate monomer. The radical polymerization can be carried out by a general method. For example, the above-mentioned monomers are dissolved in a solvent, stirred under heating, and a polymerization initiator is added to synthesize an acrylic polymer intermediate. In order to adjust the molecular weight of the acrylic polymer, the polymerization may be carried out in the presence of a chain transfer agent. Next, some of the hydroxyl groups of the structural units of the hydroxyl group-containing (meth)acrylate contained in the acrylic polymer intermediate are bonded to the isocyanate groups of the isocyanate group-containing polymerizable monomer by a urethane reaction, whereby some of the structural units of the hydroxyl group-containing (meth)acrylate become structural units of the polymerizable group-containing (meth)acrylate. The urethane reaction can be carried out by a general method. For example, the acrylic polymer intermediate and the isocyanate group-containing polymerizable monomer are stirred while being heated in the presence of a solvent and a urethane catalyst. This allows the isocyanate group of the isocyanate group-containing polymerizable monomer to be urethane-bonded to a part of the hydroxyl groups of the acrylic polymer intermediate.

[0094] In the pressure-sensitive adhesive layer preparation step, for example, an acrylic polymer, an isocyanate compound, and a polymerization initiator are dissolved in a solvent to prepare a pressure-sensitive adhesive composition. The viscosity of the composition can be adjusted by changing the amount of the solvent. Next, the pressure-sensitive adhesive composition is applied to a release sheet. As a coating method, for example, a general coating method such as roll coating, screen coating, or gravure coating is adopted. The applied composition is subjected to a solvent removal treatment, a solidification treatment, or the like to solidify the applied pressure-sensitive adhesive composition, thereby preparing the pressure-sensitive adhesive layer 22.

[0095] In the base layer preparation step, the base layer 21 can be prepared by film formation using a general method. Examples of the film formation method include a calendar film formation method, a casting method in an organic solvent, an inflation extrusion method in a closed system, a T-die extrusion method, and a dry lamination method. A co-extrusion molding method may also be used. Note that a commercially available film or the like may also be used as the base layer 21.

[0096] In the lamination step, the pressure-sensitive adhesive layer 22 overlapping the release sheet is laminated on the base layer 21. The release sheet may remain overlapping the pressure-sensitive adhesive layer 22 until use. In addition, in order to promote the reaction between the crosslinking agent and the acrylic polymer, and also between the crosslinking agent and the surface portion of the base layer 21, an aging treatment step may be carried out for 48 hours in an environment of 50°C after the lamination step.

[0097] Through these steps, the dicing tape 20 can be manufactured.

[0098] The manufacturing method of the dicing die bond film (the process of manufacturing the dicing die bond film) is as follows: A resin composition preparation step of preparing a resin composition for forming the die bond layer 10; a die bond layer preparation step of preparing a die bond layer 10 from a resin composition; and a bonding step of bonding the die bond layer 10 to the adhesive layer 22 of the dicing tape 20 manufactured as described above.

[0099] In the resin composition preparation step, for example, an epoxy resin, a curing catalyst for the epoxy resin, an acrylic resin, a phenolic resin, a solvent, etc. are mixed and each resin is dissolved in the solvent to prepare a resin composition. The viscosity of the composition can be adjusted by changing the amount of the solvent. Commercially available products can be used as these resins.

[0100] In the die-bonding layer preparation step, for example, the resin composition prepared as described above is applied to a release sheet. The application method is not particularly limited, and for example, a general application method such as roll coating, screen coating, gravure coating, etc. is adopted. Next, if necessary, the applied composition is solidified by a solvent removal treatment, a curing treatment, etc., to prepare the die-bonding layer 10.

[0101] In the bonding step, the release sheets are peeled off from the adhesive layer 22 of the dicing tape 20 and the die bond layer 10, respectively, and the die bond layer 10 and the adhesive layer 22 are bonded together so that they are in direct contact with each other. For example, they can be bonded together by pressure bonding. The temperature during bonding is not particularly limited, and is, for example, 30°C or higher and 50°C or lower, and preferably 35°C or higher and 45°C or lower. The linear pressure during bonding is not particularly limited, but is preferably 0.1kgf / cm or higher and 20kgf / cm or lower, and more preferably 1kgf / cm or higher and 10kgf / cm or lower.

[0102] The dicing die bond film 1 manufactured as described above is used, for example, as an auxiliary tool for manufacturing semiconductor integrated circuits. A specific example of its use will be described below.

[0103] A method for manufacturing a semiconductor integrated circuit generally includes a process of cutting out chips from a semiconductor wafer having a circuit surface formed thereon, and assembling the chips. This process includes, for example, a half-cut process in which a groove is formed in the semiconductor wafer to process the semiconductor wafer into chips (dies) by a fracturing process, and the semiconductor wafer is further ground to reduce its thickness, a mounting process in which one side (for example, the side opposite to the circuit side) of the half-cut semiconductor wafer is attached to the die bond layer 10 and the semiconductor wafer is fixed to the dicing tape 20, an expanding process in which the interval between the half-cut semiconductor chips is widened, a pick-up process in which the die bond layer 10 and the adhesive layer 22 are peeled off to take out the semiconductor chip (die) with the die bond layer 10 attached, and a die bonding process in which the semiconductor chip (die) with the die bond layer 10 attached is bonded to an adherend. When these processes are carried out, the dicing tape (dicing die bond film) of this embodiment is used as a manufacturing auxiliary tool.

[0104] In the half-cut process, as shown in FIGS. 2A to 2D, a half-cut process is performed to cut the semiconductor integrated circuit into small pieces (dies). More specifically, a wafer processing tape T is attached to the surface of the semiconductor wafer W opposite to the circuit surface. A dicing ring R is also attached to the wafer processing tape T. With the wafer processing tape T attached, grooves for division are formed. A back-grind tape G is attached to the surface with the grooves formed, while the wafer processing tape T that was initially attached is peeled off. With the back-grind tape G attached, the semiconductor wafer W is ground until it reaches a predetermined thickness.

[0105] 3A and 3B, in the mounting step, a dicing ring R is attached to the adhesive layer 22 of the dicing tape 20, and a half-cut semiconductor wafer W is attached to the exposed surface of the die bond layer 10. Thereafter, the backgrind tape G is peeled off from the semiconductor wafer W.

[0106] In the expanding step, as shown in FIG. 4A to FIG. 4C, a dicing ring R is attached to the adhesive layer 22 of the dicing tape 20, and then fixed to a holder H of an expanding device. The dicing die bond film 1 is stretched so as to be expanded in the surface direction by pushing up a push-up member U provided in the expanding device from the lower side of the dicing die bond film 1. As a result, the half-cut processed semiconductor wafer W is cleaved under a specific temperature condition. The above temperature condition is, for example, −20 to 0° C., preferably −15 to 0° C., and more preferably −10 to −5° C. The expanded state is released by lowering the push-up member U (up to this point is the low-temperature expanding step). Furthermore, in the expanding step, as shown in FIG. 5A to FIG. 5B, the dicing tape 20 is stretched so as to expand the area under a higher temperature condition. As a result, the cleaved adjacent semiconductor chips are pulled apart in the surface direction of the film surface, and the kerf (gap) is further expanded (room-temperature expanding step).

[0107] 6, in the pick-up process, the semiconductor chip with the die bond layer 10 attached thereto is peeled off from the adhesive layer 22 of the dicing tape 20. In detail, the pin members P are raised to push up the semiconductor chip to be picked up through the dicing tape 20. The pushed-up semiconductor chip is held by the suction jig J. In the die bonding step, the semiconductor chip with the die bonding layer 10 attached thereto is bonded to an adherend.

[0108] As described above, the dicing die bond film 1 (dicing tape 20) of this embodiment is used in the above-mentioned process, and in the low-temperature expanding process, the dicing tape 20 is stretched at 0° C. or lower with the wafer bonded to the die bond layer 10, and the wafer is cleaved together with the die bond layer 10. Furthermore, in the expanding process at room temperature, the dicing tape 20 is stretched. The temperature in the low-temperature expanding step is usually 0° C. or lower, for example, from −15° C. to 0° C. The temperature in the expanding step at room temperature is, for example, from 10° C. to 25° C.

[0109] The matters disclosed in this specification include the following. (1) A base layer and a pressure-sensitive adhesive layer having higher adhesion than the base layer, The volume crystallinity of the base layer calculated from the differential scanning calorimetry is 20 J / cm 3 More than 120J / cm 3 and the thickness of the base layer is 80 μm or more. (2) The dicing tape according to (1) above, wherein a chart obtained by measuring the base layer by differential scanning calorimetry has an endothermic peak, and the temperature of the apex of the endothermic peak is 100° C. or higher. (3) The dicing tape according to (2) above, wherein the temperature difference between the peak start point (point A) and the peak apex (point C) of the endothermic peak is 40° C. or less. (4) The dicing tape according to (2) or (3) above, wherein the temperature difference between the peak start point (point A) and the peak end point (point B) at the endothermic peak is 30° C. or more and 60° C. or less. (5) The dicing tape according to any one of (2) to (4) above, wherein the temperature at the peak onset point (point A) in the endothermic peak is 70° C. or higher. (6) The dicing tape according to any one of (2) to (5) above, wherein the temperature at the endothermic peak end point (point B) is 150° C. or lower. (7) The dicing tape according to any one of (1) to (6) above, wherein the base layer has a single-layer structure or a multilayer structure. (8) The dicing tape according to any one of (1) to (7) above, wherein the base layer is composed of at least three layers. (9) The dicing tape according to (8) above, wherein the base layer includes a three-layer structure and has two non-elastomer layers (X, X) formed of a non-elastomer, and an elastomer layer (Y) disposed between the two non-elastomer layers and formed of an elastomer. (10) The dicing tape according to (9) above, wherein the base layer has a three-layer structure, and the ratio of the thickness of the inner layer to the thickness of one outer layer (Y thickness / X thickness) is 5 or more and 15 or less. (11) The dicing tape according to (9) or (10) above, wherein the non-elastomer layer (X) contains at least one selected from the group consisting of low density polyethylene (LDPE), high density polyethylene (HDPE), and polypropylene. (12) The dicing tape according to any one of (9) to (11) above, wherein the elastomer layer (Y) contains an ethylene-vinyl acetate copolymer (EVA). (13) The dicing tape according to any one of (1) to (11) above, wherein the thickness of the pressure-sensitive adhesive layer accounts for 5% to 30% of the total thickness of the dicing tape. (14) A dicing die bond film comprising the dicing tape according to any one of (1) to (13) above and a die bond layer bonded to the dicing tape. (15) The dicing die bond film according to (14) above, wherein the die bond layer contains at least one of a thermosetting resin and a thermoplastic resin. (16) The dicing die bond film according to (14) or (15) above, wherein the thickness of the die bond layer is 1 μm or more and 200 μm or less.

[0110] The dicing tape and dicing die bond film of this embodiment are as exemplified above, but the present invention is not limited to the dicing tape and dicing die bond film exemplified above. That is, various forms used in general dicing tapes and dicing die bond films can be adopted as long as they do not impair the effects of the present invention. EXAMPLES

[0111] The present invention will now be described in more detail with reference to experimental examples, but the present invention is not limited to these.

[0112] A dicing tape was produced as follows. The dicing tape was used to produce a dicing die bond film.

[0113] <Base material layer> The products shown below were used as raw materials to produce a three-layer laminated substrate layer or a single-layer substrate layer. Resin that makes up the inner layer Ingredient name: Ultrathene 626 Ethylene-vinyl acetate copolymer resin (EVA containing 15% vinyl acetate by mass) Tosoh Corporation Resin that makes up the inner layer Ingredient name: Ultrathene 633 Ethylene-vinyl acetate copolymer resin (EVA containing 20% ​​vinyl acetate by mass) Tosoh Corporation Resin that makes up the inner layer Raw material name: Evaflex V523 Ethylene-vinyl acetate copolymer resin (EVA containing 33% vinyl acetate by mass) Manufactured by Dow Mitsui Polychemicals Resin that makes up the inner layer Raw material name: Evaflex P1007 Ethylene-vinyl acetate copolymer resin (EVA containing 9% vinyl acetate by mass) Manufactured by Dow Mitsui Polychemicals Resin constituting the base layer of the comparative example Raw material name: Infuse9530 α-Olefin Block Copolymer Resin Dow Chemical Company Resin that makes up the outer layer Raw material name: WINTEC WFX4M Metallocene Polypropylene Japan Polypropylene Corporation

[0114] (Forming of base layer) The substrate layer was molded using an extrusion T-die molding machine. The extrusion temperature was 190°C. The substrate layers of the three-layer laminate type were integrated by co-extrusion molding from a T-die. After the integrated substrate layer (laminate) was sufficiently solidified, the substrate layer was wound into a roll and stored. The thickness ratio of each layer constituting the base material layer and the total thickness of the base material layer are as shown in Table 1.

[0115] <Adhesive layer> (Preparation of Adhesive Layer (Adhesive Composition)) The following raw materials were mixed to prepare a first resin composition. INA (isononyl acrylate) 173 parts by weight 54.5 parts by weight of HEA (hydroxyethyl acrylate) 0.46 parts by weight of AIBN (2,2'-azobisisobutyronitrile) 372 parts by weight of ethyl acetate Next, the first resin composition was placed in a round-bottom separable flask of a polymerization experimental apparatus equipped with a round-bottom separable flask (volume 1 L), a thermometer, a nitrogen inlet tube, and a stirring blade. While stirring the first resin composition, the liquid temperature of the first resin composition was adjusted to room temperature (23°C), and the inside of the round-bottom separable flask was replaced with nitrogen gas for 6 hours. Next, while nitrogen gas was flowing into the round-bottom separable flask, the first resin composition was stirred and the liquid temperature of the first resin composition was kept at 62°C for 3 hours. After that, the mixture was further kept at 75°C for 2 hours to carry out the polymerization reaction of the INA, HEA, and AIBN, and the second resin composition was prepared. Then, the flow of nitrogen gas into the round-bottom separable flask was stopped. After the second resin composition was cooled to room temperature, the following raw materials were added to the second resin composition. 2-Methacryloyloxyethyl isocyanate Compounds with polymerizable carbon-carbon double bonds Product name: Karenz MOI (Showa Denko Co., Ltd.) 52.5 parts by weight Dibutyltin dilaurate IV (Wako Pure Chemical Industries, Ltd.) 0.26 parts by weight The obtained third resin composition was stirred in the air at 50° C. for 24 hours. Finally, the following raw materials were added to 100 parts by mass of the polymer solid content of the third resin composition. 0.75 parts by weight of isocyanate compound (product name "Coronate L", manufactured by Tosoh Corporation) Photopolymerization initiator (product name "Omnirad127", manufactured by IGM Resins) 2 parts by weight Then, the third resin composition was diluted with ethyl acetate so that the solid content concentration was 20 mass %, thereby preparing a pressure-sensitive adhesive composition.

[0116] <Dicing tape manufacturing> The adhesive composition was applied to one surface of the base layer using an applicator so as to have a thickness of 10 μm after drying. The base layer after the adhesive composition application was heated and dried at 110° C. for 3 minutes to form an adhesive layer, thereby producing a dicing tape.

[0117] <Preparation of dicing die bond film> (Creation of die bond layer) The following raw materials were added to methyl ethyl ketone and mixed to obtain a composition for a die bond layer having a solid content concentration of 20 mass %. Acrylic resin (product name "SG-P3", Nagase ChemteX Corporation, glass transition temperature 12°C) 100 parts by weight Epoxy resin (product name "JER1001", manufactured by Mitsubishi Chemical Corporation) 46 parts by weight Phenolic resin (product name "MEH-7851ss", manufactured by Meiwa Kasei Co., Ltd.) 51 parts by weight Spherical silica (product name "SO-25R", manufactured by Admatechs Co., Ltd.) 191 parts by weight 0.6 parts by weight of curing catalyst (product name "Curesol PHZ", manufactured by Shikoku Chemical Industry Co., Ltd.) Next, a release liner was prepared by silicone-treating a PET separator (thickness 50 μm). A die-bonding layer composition was applied to the treated surface of the release liner with an applicator so that the thickness after drying was 10 μm. The solvent was evaporated from the die-bonding layer composition by drying at 130° C. for 2 minutes, and a die-bonding sheet was obtained in which a die-bonding layer was laminated on the release liner. (Laminating the die bond layer and dicing tape) Next, the adhesive layer of the dicing tape was attached to the die bond layer (the side on which the release sheet was not laminated) of the die bond sheet. After that, the release liner was peeled off from the die bond layer to prepare a dicing die bond film provided with the die bond layer.

[0118] As described above, the dicing tape and the dicing die bond film of the examples and the comparative examples were manufactured according to the above-mentioned method. The configuration of each dicing tape is shown in Table 1.

[0119] [Table 1]

[0120] The volume crystallinity was calculated as follows. The amount of heat absorbed by the inner layer was multiplied by the thickness ratio occupied by the inner layer, and then multiplied by the specific gravity of the inner layer to calculate the volume crystallinity of the inner layer. Similarly, the volume crystallinity of the outer layer was calculated. These calculated values ​​were then summed up. The sum was used as the volume crystallinity.

[0121] <Differential scanning calorimetry (DSC) measurement> Measurement samples were taken out from the dicing tape of each of the Examples and Comparative Examples. The measurement samples were taken out from the base layer by cutting the base layer in the thickness direction. Using a commercially available DSC measuring device, about 10 mg of the measurement sample was weighed out, and the measurement was carried out in a nitrogen gas atmosphere at a temperature increase rate of 5°C / min from room temperature (about 20°C) to 200°C. The area of ​​the endothermic peak appearing in the measurement chart, and the temperatures of the peak start point, peak apex, and peak end point of the endothermic peak were measured using analysis software attached to the device. When multiple peaks appeared in the measurement chart, the above-mentioned temperatures and other parameters were measured for each peak. Details of the DSC measuring device and analysis software are as follows. Measurement equipment: TA Instruments Japan Co., Ltd. Device name DSC Q-2000 Analysis software: TA Instruments Universal Analysis 2000 version 4.5A The charts obtained by performing differential scanning calorimetry (DSC measurement) on the base layer of Example 1 are shown in Figures 7A and 7B. Figures 7A and 7B each show the same measurement results in a different display format. In Figure 7A, the diagonal line in the chart represents the temperature. Similarly, charts obtained by carrying out differential scanning calorimetry (DSC measurement) on the base layer of Comparative Example 1 are shown in FIGS. 8A and 8B.

[0122] <Performance evaluation (evaluation of breakability)> The dicing die bond films produced in each of the Examples and Comparative Examples were used to perform performance evaluation as follows. After a wafer processing tape (trade name "V-12SR2", manufactured by Nitto Denko Corporation) was attached to one side of a bare wafer (diameter 300 mm), the bare wafer was fixed to a dicing ring via the wafer processing tape, and a dicing device (manufactured by DISCO, model number 6361) was used to form a lattice-shaped groove (25 μm wide, 100 μm deep) on the side opposite to the side where the wafer processing tape was attached, so that the chips would be 2 mm x 2 mm square. Next, the wafer processing tape (trade name "V-12SR2", manufactured by Nitto Denko Corporation) was peeled off from the wafer, a back grinding tape was attached to the side where the grooves were formed, and the bare wafer was ground to a thickness of 30 μm (0.030 mm) using a back grinder (manufactured by DISCO, model number DGP8760). The ground wafer with the back grind tape was bonded to the die bond film surface of the dicing die bond tape at a temperature of 60°C. Next, the ground wafer and the dicing die bond film bonded thereto were bonded to a ring and fixed, and then the back grind tape was peeled off. Then, the die bond layer was cleaved in a cool expander unit under the conditions of an expansion temperature of -5°C, an expansion speed of 100mm / sec, and an expansion amount of 14mm. Next, room temperature expansion was performed under the conditions of room temperature, an expansion speed of 1mm / sec, and an expansion amount of 10mm. Then, while maintaining the expanded state, the outer periphery of the dicing die bond film was thermally shrunk under the conditions of a heat temperature of 200°C, a heat distance of 18mm, and a rotation speed of 5° / sec. In the dicing die bond film after heat shrinkage, the fracture of the die bond layer was confirmed using a microscope. A fracture rate of 90% or more was evaluated as ◯, a fracture rate of less than 90% and 80% or more was evaluated as △, and a fracture rate of less than 80% was evaluated as ×.

[0123] Table 1 shows the results of differential scanning calorimetry (DSC) measurements of the base layer of the dicing tape of each of the Examples and Comparative Examples, and the results of performance evaluation (evaluation of breakability).

[0124] As can be seen from the above evaluation results, the dicing die bond films of the examples were able to cleave the semiconductor wafer better in the low-temperature expanding process than the dicing die bond films of the comparative examples.

[0125] In the dicing tape of the embodiment, the volume crystallinity calculated from the DSC measurement chart of the base layer is 20 J / cm 3 More than 120J / cm 3 and the thickness of the base layer is 80 μm or more. The volume crystallinity above is 20 J / cm 3 Since the crystallinity in the base layer is relatively large, the semiconductor wafer can be favorably cleaved in the low-temperature expanding step. 3Since the crystallinity in the base material layer is not greater than necessary, the base material layer 21 is prevented from breaking during expansion. By using a dicing tape (dicing die bond film) of the embodiment having a base layer with such physical properties in the manufacture of semiconductor integrated circuits, the semiconductor wafer can be successfully cut in the low-temperature expansion process while preventing breakage of the base layer 21. [Industrial Applicability]

[0126] The dicing tape and dicing die bond film of the present invention are suitably used, for example, as auxiliary tools for producing semiconductor integrated circuits. [Explanation of symbols]

[0127] 1: Dicing die bond film, 10: die bond layer, 20: dicing tape, 21: Base material layer, 22: Adhesive layer.

Claims

1. A base layer and a pressure-sensitive adhesive layer having higher adhesion than the base layer, The substrate layer has two non-elastomer layers formed of a non-elastomer, and an elastomer layer disposed between the two non-elastomer layers and formed of an elastomer, each of the two non-elastomeric layers comprises a metallocene polypropylene; The amount of heat absorption was calculated from the area of ​​the endothermic peak that appeared in the chart obtained by differential scanning calorimetry of the base layer, and the volume crystallinity obtained by converting the calculated amount of heat absorption into a value per volume was 25 J / cm ３ More than 90J / cm ３ and the thickness of the base layer is 80 μm or more and 150 μm or less.

2. 2. The dicing tape according to claim 1, wherein a chart obtained by measuring the base layer by differential scanning calorimetry has an endothermic peak, and the temperature of the apex of the endothermic peak is 105° C. or higher and 135° C. or lower.

3. A dicing die bond film comprising the dicing tape according to claim 1 or 2 and a die bond layer attached to the dicing tape.

Images