Electrolyte-containing liquid composition, method for producing electrolyte-containing liquid composition, and method for restoring capacity of non-aqueous electrolyte secondary battery

Abstract

To provide a composition that can easily supply a carrier ion contributing to charge and discharge, which is a main purpose.SOLUTION: In the present disclosure, the above-mentioned problem is solved by providing an electrolyte-containing liquid composition that is used to supply a carrier ion to a non-aqueous electrolyte secondary battery, the electrolyte-containing liquid composition including a liquid composition including a solvent and a solute, and an electrolyte, wherein the content of the electrolyte in the electrolyte-containing liquid composition is 30% by volume or more and 50% by volume or less, the solvent includes 1,2-dimethoxyethane, the solute includes an ion compound, the ion compound is composed of a radical anion of an aromatic compound and a metal cation, the aromatic compound is polyacene or polyphenyl, and the metal cation is an ion of the same type as the carrier ion.SELECTED DRAWING: Figure 4

Description

[Technical field]

[0001] The present disclosure relates to an electrolyte-containing liquid composition, a method for producing the electrolyte-containing liquid composition, and a method for restoring the capacity of a nonaqueous electrolyte secondary battery. [Background technology]

[0002] In general, in a non-aqueous electrolyte secondary battery, carrier ions move between a positive electrode and a negative electrode to charge and discharge the battery. For example, Patent Document 1 discloses that a mixed solvent of ethylene carbonate and 1,2-dimethoxyethane is used for the non-aqueous electrolyte of a non-aqueous electrolyte secondary battery. Patent Document 2 discloses that a mixed solvent of ethylene carbonate, 1,2-dimethoxyethane, and propylene carbonate is used for the non-aqueous electrolyte of a non-aqueous electrolyte secondary battery. Patent Document 3 discloses a third electrode that supplies lithium ions to the positive electrode.

[0003] In non-aqueous electrolyte secondary batteries, the electrolyte may be reduced and decomposed during use, forming a coating on the surface of the electrode. When a part of the carrier ions is taken up in the coating, the carrier ions contributing to charging and discharging are reduced, which is one of the causes of the reduction in the capacity of the non-aqueous electrolyte secondary battery. In Patent Document 3, in order to restore the capacity of a lithium ion secondary battery, a third electrode is provided in addition to a positive electrode and a negative electrode to supply carrier ions, and the third electrode and the positive electrode are externally short-circuited to move carrier ions (lithium ions) from the third electrode to the positive electrode, thereby supplying carrier ions only to the positive electrode. However, in Patent Document 3, the third electrode is provided, making the structure complicated. In addition, the operation of switching the connection of the electrodes is also complicated, and it is considered that there is room for improvement from the viewpoint of ease of operation. [Prior art documents] [Patent documents]

[0004] [Patent Document 1] Japanese Patent Application Publication No. 6-052888 [Patent Document 2] Japanese Patent Application Publication No. 6-176793 [Patent Document 3] JP 2016-076358 A Summary of the Invention [Problem to be solved by the invention]

[0005] The present disclosure has been made in consideration of the above-mentioned circumstances, and has as its main object to provide a composition that can easily replenish carrier ions that contribute to charging and discharging. [Means for solving the problem]

[0006] In order to solve the above problems, the present disclosure provides an electrolyte-containing liquid composition used for supplying carrier ions to a nonaqueous electrolyte secondary battery, the electrolyte-containing liquid composition comprising an electrolyte and a liquid composition containing a solvent and a solute, the content of the electrolyte in the electrolyte-containing liquid composition being 30 vol% or more and 50 vol% or less, the solvent comprising 1,2-dimethoxyethane, the solute comprising an ionic compound, the ionic compound comprising a radical anion of an aromatic compound and a metal cation, the aromatic compound being a polyacene or polyphenyl, and the metal cation being the same type of ion as the carrier ion.

[0007] According to the present disclosure, since a predetermined solvent and a predetermined amount of electrolyte are contained, it is possible to provide an electrolyte-containing liquid composition that can supply carrier ions that contribute to charging and discharging to a nonaqueous electrolyte secondary battery by a simple method.

[0008] In the above disclosure, the radical anion may include at least one selected from the group consisting of a naphthalene radical anion and a biphenyl radical anion, and the metal cation may include a lithium ion.

[0009] The present disclosure also provides a method for producing an electrolyte-containing liquid composition used to supply carrier ions to a nonaqueous electrolyte secondary battery, the method comprising: a precursor solution preparation step of preparing a precursor solution by dissolving an aromatic compound in a solvent; a liquid composition preparation step of preparing a liquid composition by dissolving a metal in the precursor solution; and an electrolyte-containing liquid composition preparation step of mixing the liquid composition and an electrolyte such that the content of the electrolyte in the electrolyte-containing liquid composition is 30 vol% or more and 50 vol% or less to prepare an electrolyte-containing liquid composition, wherein the solvent contains 1,2-dimethoxyethane, the aromatic compound is a polyacene or a polyphenyl, and a metal cation generated from the metal is the same type of ion as the carrier ion.

[0010] According to the present disclosure, it is possible to produce an electrolyte-containing liquid composition that can supply carrier ions that contribute to charging and discharging to a nonaqueous electrolyte secondary battery by a simple method.

[0011] Furthermore, the present disclosure provides a capacity recovery method for a non-aqueous electrolyte secondary battery, the method including: an electrolyte-containing liquid composition preparation step of preparing the above-mentioned electrolyte-containing liquid composition; and a mixing step of mixing the electrolyte-containing liquid composition with an electrolyte of a non-aqueous electrolyte secondary battery that has been observed to have a specified battery capacity reduction.

[0012] According to the present disclosure, by using the above-mentioned electrolyte-containing liquid composition, carrier ions that contribute to charging and discharging can be replenished to a nonaqueous electrolyte secondary battery by a simple method, and the capacity of the nonaqueous electrolyte secondary battery can be restored.

[0013] The above disclosure does not need to include a constant-current, constant-voltage charging step of subjecting the nonaqueous electrolyte secondary battery to constant-current, constant-voltage charging after the electrolyte-containing liquid composition is mixed with the electrolyte of the nonaqueous electrolyte secondary battery. Effect of the Invention

[0014] The liquid composition according to the present disclosure has the effect of enabling carrier ions that contribute to charging and discharging to be easily replenished. [Brief description of the drawings]

[0015] [Figure 1] 2 is a photograph of the electrolyte-containing liquid composition and the battery electrodes in Example 1. [Diagram 2] 4 is a photograph of an electrolyte-containing liquid composition and a battery electrode in Comparative Example 2. [Diagram 3] 1 is a schematic flow chart of a method for producing an electrolyte-containing liquid composition according to the present disclosure. [Figure 4] 1 is a schematic flowchart of a capacity recovery method for a nonaqueous electrolyte secondary battery according to the present disclosure. [Diagram 5] 1 is a schematic flowchart of a conventional method for restoring capacity of a non-aqueous electrolyte secondary battery. [Figure 6] 1 is a graph showing the results of a cycle durability test. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0016] The electrolyte-containing liquid composition, the method for producing the electrolyte-containing liquid composition, and the capacity recovery method for a non-aqueous electrolyte secondary battery according to the present disclosure will be described in detail below.

[0017] A. Liquid composition containing electrolyte The electrolyte-containing liquid composition of the present disclosure is an electrolyte-containing liquid composition used for replenishing carrier ions to a nonaqueous electrolyte secondary battery, the electrolyte-containing liquid composition comprising a liquid composition containing a solvent and a solute, and an electrolyte, the content of the electrolyte in the electrolyte-containing liquid composition being 30 volume % or more and 50 volume % or less, the solvent comprising 1,2-dimethoxyethane, the solute comprising an ionic compound, the ionic compound comprising a radical anion of an aromatic compound and a metal cation, the aromatic compound being a polyacene or polyphenyl, and the metal cation being the same type of ion as the carrier ion.

[0018] According to the present disclosure, since a predetermined solvent and a predetermined amount of electrolyte are contained, it is possible to provide an electrolyte-containing liquid composition that can supply carrier ions that contribute to charging and discharging to a nonaqueous electrolyte secondary battery by a simple method.

[0019] As described above, the non-aqueous electrolyte secondary battery tends to decrease in carrier ions that contribute to charging and discharging with use, and the battery capacity gradually decreases. If the decreased carrier ions can be replenished, the battery life can be extended. Therefore, as a result of intensive research into the replenishment of carrier ions by a simple method, it has been found that the battery capacity can be restored by adding a liquid composition containing a specific ionic compound to a battery with a decreased battery capacity, and that the decrease in battery capacity due to charge and discharge cycles in subsequent use can be suppressed by performing constant current and constant voltage charging on the battery after the addition, that is, the cycle resistance, which is a property that makes it difficult for capacity to decrease due to charge and discharge cycles, can be improved.

[0020] As a result of further investigations, the inventors of the present invention have found that when an electrolyte-containing liquid composition containing 1,2-dimethoxyethane (DME) as a solvent for the liquid composition and further containing a predetermined amount of electrolyte is added to a battery in which a decrease in battery capacity is observed, the battery capacity can be restored, and the cycle resistance can be improved without constant current / constant voltage charging thereafter. By using the electrolyte-containing liquid composition, the cycle resistance of the battery can be improved by "simply adding" the composition, without constant current / constant voltage charging, which requires a long time. Therefore, the supply of carrier ions to the battery can be greatly simplified, which can greatly contribute to the extension of the battery life.

[0021] When DME was used as the solvent, the electrolyte was well mixed in the electrolyte-containing liquid composition (see FIG. 1(a)). On the other hand, when tetrahydrofuran (THF) was used as the solvent, phase separation occurred as shown in FIG. 2(a), so it is presumed that the electrolyte was not well mixed. In addition, when the electrodes of the batteries charged with each electrolyte-containing liquid composition were checked, when the solvent was DME, almost no charging unevenness was confirmed as shown in FIG. 1(b). On the other hand, when the solvent was THF, charging unevenness was confirmed as shown in FIG. 2(b). It is presumed that such a difference depending on the type of solvent used is one of the factors of the effect of the present disclosure described above. Note that the above-mentioned FIG. 1(a) is a photograph of the electrolyte-containing liquid composition of Example 1 described later, FIG. 1(b) is a photograph of the electrodes of the battery in Example 1 in a charged state, and FIG. 2 is a similar photograph in Comparative Example 2.

[0022] The electrolyte-containing liquid composition of the present disclosure includes a liquid composition containing a solvent and a solute, and an electrolyte. Each of these will be described below.

[0023] 1.Liquid composition (1) Solvent By dissolving a solute in a solvent, for example, it is expected that the stability of an ionic compound is improved. In the present disclosure, the solvent includes 1,2-dimethoxyethane (DME). The solvent may include only DME, or may include a solvent other than DME. The solvent other than DME may include, for example, a cyclic ether, a chain ether, etc., and specifically, may include at least one selected from the group consisting of tetrahydrofuran (THF), 1,3-dioxolane (DOL), 1,4-dioxane (DX), and 1,2-diethoxyethane (DEE).

[0024] The proportion of DME in the total solvent is, for example, 50% by volume or more, or may be 60% by volume or more, or 70% by volume or more, while the proportion may be, for example, 100% by volume, 95% by volume or less, 90% by volume or less, or 80% by volume or less.

[0025] (2) Solute The solute is dissolved in the solvent. The solute includes an ionic compound. The ionic compound contributes to the supply of carrier ions. The solute may include one type of ionic compound alone. The solute may include two or more types of ionic compounds.

[0026] In the present disclosure, the concentration of the solute in the liquid composition may be any concentration. The concentration of the solute may be determined, for example, by the balance between the dead space in the battery and the amount of carrier ions to be replenished. For example, if the concentration is too low, the volume of the liquid composition may become large, and it may not be possible to supply a sufficient amount to the battery. For example, if the concentration is too high, it may take a long time for the liquid composition to be mixed with the electrolyte.

[0027] The concentration of the solute in the liquid composition is, for example, 0.05 mol / L or more, may be 0.10 mol / L or more, or may be 0.50 mol / L or more. The concentration of the solute is 0.05 mol / L or more, and may promote the supply of carrier ions. On the other hand, the concentration is, for example, 1.1 mol / L or less, and may be 1.0 mol / L or less. The concentration of the solute is 1.1 mol / L or less, and may promote the supply of carrier ions.

[0028] (ionic compounds) The ionic compound is composed of a radical anion of an aromatic compound and a metal cation. The ionic compound may be dissociated or associated. The metal cation is the same type of ion as the carrier ion of the battery. For example, when the battery is a lithium ion battery, the carrier ion and the metal cation are both lithium (Li) ions. That is, the metal cation may include, for example, Li ions. For example, when the battery is a sodium ion battery, the carrier ion and the metal cation are both sodium (Na) ions. For example, when the battery is a magnesium ion battery, the carrier ion and the metal cation are both magnesium (Mg) ions.

[0029] The aromatic compound is a polyacene or a polyphenyl. A polyacene has a structure in which a plurality of aromatic rings are condensed. In the present disclosure, each aromatic ring of the polyacene may contain a heteroatom in the ring. The heteroatom may be, for example, nitrogen (N), oxygen (O), sulfur (S), etc. Each aromatic ring of the polyacene may have a substituent on the ring. A polyphenyl has a structure in which a plurality of phenyl groups are linked by single bonds. In the present disclosure, each aromatic ring of the polyphenyl may contain a heteroatom in the ring. Each aromatic ring of the polyphenyl may have a substituent on the ring.

[0030] In the present disclosure, an ionic compound in which the aromatic compound is a polyacene is referred to as a "first ionic compound." An ionic compound in which the aromatic compound is a polyphenyl is referred to as a "second ionic compound." The solute may include at least one selected from the group consisting of the first ionic compound and the second ionic compound.

[0031] (First ionic compound) The first ionic compound is represented by the following formula (1).

[0032] [ka]

[0033] In the above formula (1), n 1 is an integer from 1 to 4. 1 is any number. y+ represents a metal cation. y represents the valence of the metal cation. Each aromatic ring may contain a heteroatom in the ring. Each aromatic ring may have a substituent on the ring.

[0034] The first ionic compound includes a radical anion of a polyacene. The polyacene may be an aromatic hydrocarbon. The polyacene may be, for example, naphthalene, anthracene, tetracene, pentacene, etc. The polyacene may include a heteroatom in the ring. The polyacene may be, for example, quinoline, chromene, acridine, etc.

[0035] The first ionic compound may be, for example, lithium naphthalenide, which is composed of a naphthalene radical anion and a Li ion.

[0036] (Second ionic compound) The second ionic compound is represented by the following formula (2).

[0037] [ka]

[0038] In the above formula (2), n 2 is an integer from 1 to 4. 2 is any number. M y+ represents a metal cation. y represents the valence of the metal cation. Each aromatic ring may contain a heteroatom in the ring. Each aromatic ring may have a substituent on the ring.

[0039] The second ionic compound includes a radical anion of a polyphenyl. The polyphenyl may be a hydrocarbon. The polyphenyl may be, for example, biphenyl, o-terphenyl, m-terphenyl, p-terphenyl, p-quaterphenyl, p-quinquiphenyl, etc. The polyphenyl may include a heteroatom in the ring. The polyphenyl may be, for example, bipyridine, etc.

[0040] The second ionic compound may be, for example, lithium biphenylide, etc. Lithium biphenylide is composed of a biphenyl radical anion and a Li ion.

[0041] In the first ionic compound and the second ionic compound, examples of the substituents that can be introduced onto the ring include halogen atoms, alkyl groups, aryl groups, alkenyl groups, alkoxy groups, aryloxy groups, sulfonyl groups, amino groups, cyano groups, carbonyl groups, acyl groups, amide groups, and hydroxyl groups. The first ionic compound and the second ionic compound may each have one type of substituent alone. The first ionic compound and the second ionic compound may each have multiple substituents. Here, "multiple" refers to at least one of multiple and multiple types.

[0042] (3) Liquid composition The liquid composition of the present disclosure may further contain any component in addition to the above-mentioned components. For example, the liquid composition may contain a component that promotes dissociation of an ionic compound.

[0043] 2. Electrolyte The content of the electrolyte in the electrolyte-containing liquid composition is usually 30% by volume or more, may be 33% by volume or more, or may be 35% by volume or more. The content of the electrolyte is usually 50% by volume or less, may be 47% by volume or less, or may be 45% by volume or less.

[0044] The electrolyte may be any solution having electrical conductivity, for example, an electrolyte used in a non-aqueous electrolyte secondary battery. The composition of the electrolyte contained in the electrolyte-containing liquid composition may be the same as or different from the electrolyte used in the battery to which the electrolyte is to be added (carrier ions are to be supplied).

[0045] Such an electrolyte solution may be, for example, a mixture of an aprotic electrolyte solvent and LiPF 6 , LiBF 4 , LiN(FSO 2 ) 2 , and LiN(CF 3 SO 2 ) 2The electrolyte may have a solute such as ethylene carbonate (EC), propylene carbonate (PC), butylene carbonate (BC), vinylene carbonate (VC), vinyl ethylene carbonate (VEC), and fluoroethylene carbonate (FEC). Examples of the aprotic electrolyte solvent include cyclic carbonates such as ethylene carbonate (EC), propylene carbonate (PC), butylene carbonate (BC), vinylene carbonate (VC), vinyl ethylene carbonate (VEC), and fluoroethylene carbonate (FEC), and chain carbonates such as dimethyl carbonate (DMC), ethyl methyl carbonate (EMC), and diethyl carbonate (DEC). The aprotic electrolyte solvent may be used alone or in combination of two or more. The electrolyte may further contain additives in addition to the above components. The additives may include, for example, a film-forming agent, a flame retardant, and the like.

[0046] 3. Liquid composition containing electrolyte The electrolyte-containing liquid composition of the present disclosure is used to replenish carrier ions to a battery. Details of the battery will be described later. The replenishment of carrier ions can increase or restore the capacity of the battery. The electrolyte-containing liquid composition can be called, for example, a "carrier ion replenisher", a "capacity recovery agent", etc.

[0047] B. Method for producing electrolyte-containing liquid composition 3 is a schematic flow chart of the method for producing an electrolyte-containing liquid composition according to the present disclosure. The method for producing an electrolyte-containing liquid composition according to the present disclosure is used for supplying carrier ions to a non-aqueous electrolyte secondary battery, and includes a precursor solution preparation step of preparing a precursor solution by dissolving an aromatic compound in a solvent, a liquid composition preparation step of preparing a liquid composition by dissolving a metal in the precursor solution, and an electrolyte-containing liquid composition preparation step of mixing the liquid composition and an electrolyte so that the content of the electrolyte in the electrolyte-containing liquid composition is 30% by volume or more and 50% by volume or less to prepare an electrolyte-containing liquid composition, the solvent includes 1,2-dimethoxyethane, the aromatic compound is polyacene or polyphenyl, and the metal cation generated from the metal is the same type of ion as the carrier ion.

[0048] According to the present disclosure, it is possible to produce an electrolyte-containing liquid composition that can supply carrier ions that contribute to charging and discharging to a nonaqueous electrolyte secondary battery by a simple method.

[0049] 1. Precursor solution preparation process The precursor solution preparation step in the present disclosure is a step of preparing a precursor solution by dissolving an aromatic compound in a solvent.

[0050] The dissolving operation of the aromatic compound may be carried out, for example, in a low dew point environment. For example, the dissolving operation may be carried out under an argon (Ar) atmosphere. The low dew point environment may be, for example, an environment with a dew point of -20°C or less. The low dew point environment may be, for example, an environment with a dew point of -40°C or less. The low dew point environment may be, for example, an environment with a dew point of -60°C or less. The dissolving operation of the aromatic compound may be carried out, for example, in a room temperature environment. For example, a heating operation or the like may be carried out so as to promote the dissolution of the aromatic compound.

[0051] The aromatic compound is a precursor of the radical anion. For example, a powder of the aromatic compound may be prepared. The powder of the aromatic compound is put into a solvent. The mixture is stirred sufficiently so that the aromatic compound is substantially completely dissolved. This prepares a precursor solution. The aromatic compound and the solvent used in this step are the same as those described above in "A. Electrolyte-containing liquid composition, 1. Liquid composition", and therefore the description here is omitted.

[0052] 2. Liquid composition preparation process The liquid composition preparation step in the present disclosure is a step of preparing a liquid composition by dissolving a metal in the precursor solution.

[0053] The metal dissolving operation may also continue to be performed in a low dew point environment. The metal dissolving operation may be performed, for example, in a room temperature environment. For example, a heating operation or the like may be performed to promote the dissolution of the metal. The metal is a precursor of a metal cation. For example, the metal may be processed into a shape with a large surface area to promote the dissolution of the metal.

[0054] The metal is introduced into the precursor solution, the molar ratio of the metal to the aromatic compound may be, for example, 1 / 1 metal / aromatic compound, and the mixture is stirred sufficiently to substantially completely dissolve the metal.

[0055] When the aromatic compound is a polyacene, it is believed that the first ionic compound is produced, for example, by the reaction of the following formula (3).

[0056] [ka]

[0057] When the aromatic compound is polyphenyl, for example, the reaction of the following formula (4) is considered to proceed, thereby producing the second ionic compound.

[0058] [ka]

[0059] In this manner, the liquid composition of the present disclosure is prepared. After preparation of the liquid composition, the liquid composition may be diluted or concentrated so that the solute has a predetermined concentration. For example, the liquid composition may be diluted or concentrated so that the solute has a concentration of 0.05 mol / L to 1.1 mol / L. The metal used in this step is the same as that described above in "A. Electrolyte-containing liquid composition, 1. Liquid composition", and therefore will not be described here.

[0060] 3. Electrolyte-containing liquid composition preparation process The electrolyte-containing liquid composition preparation step in the present disclosure is a step of mixing the liquid composition and an electrolyte so that the content of the electrolyte in the electrolyte-containing liquid composition is 30 vol.% or more and 50 vol.% or less, to prepare an electrolyte-containing liquid composition.

[0061] The electrolyte solution can be mixed into the liquid composition by adding a predetermined amount of electrolyte solution to the liquid composition and then stirring the mixture with a rotor such as a stirrer. Note that the electrolyte solution and the amount of electrolyte solution mixed used in this step are the same as those described above in "A. Electrolyte-containing liquid composition, 2. Electrolyte solution" regarding the electrolyte solution and the content of the electrolyte solution, and therefore will not be described here.

[0062] C. Capacity recovery method for non-aqueous electrolyte secondary battery 4 is a schematic flow chart of the capacity recovery method for a nonaqueous electrolyte secondary battery according to the present disclosure. The capacity recovery method for a nonaqueous electrolyte secondary battery according to the present disclosure includes an electrolyte-containing liquid composition preparation step of preparing the above-mentioned electrolyte-containing liquid composition, and a mixing step of mixing the electrolyte-containing liquid composition with the electrolyte of a nonaqueous electrolyte secondary battery that has been found to have a specified battery capacity reduction.

[0063] According to the present disclosure, by using the above-mentioned electrolyte-containing liquid composition, carrier ions that contribute to charging and discharging can be supplied to a nonaqueous electrolyte secondary battery by a simple method, and the capacity of the nonaqueous electrolyte secondary battery can be restored. In the present disclosure, in addition to the electrolyte-containing liquid composition preparation step and the mixing step, other steps may be further included as necessary. Each step will be described below.

[0064] 1. Electrolyte-containing liquid composition preparation process The electrolyte-containing liquid composition preparation step in the present disclosure is a step of preparing the electrolyte-containing liquid composition described above. The electrolyte-containing liquid composition used in this step is the same as that described in "A. Electrolyte-containing liquid composition" above, and the method for preparing the electrolyte-containing liquid composition is the same as that described in "B. Method for producing electrolyte-containing liquid composition" above, so the description here is omitted.

[0065] 2.Mixing process The mixing step in the present disclosure is a step of mixing the electrolyte-containing liquid composition with an electrolyte of a nonaqueous electrolyte secondary battery in which a prescribed decrease in battery capacity is observed.

[0066] For example, the case of the battery is opened by a predetermined means. When the case is provided with a liquid inlet, the liquid inlet is opened. An electrolyte-containing liquid composition is poured into the battery through the liquid inlet. This allows the electrolyte-containing liquid composition and the electrolyte of the battery to be mixed in the battery. For example, the battery may be lightly shaken to promote mixing. After pouring, the mixture may be stirred using a rotor such as a stirrer. Furthermore, in order to suppress gelation after pouring, the electrolyte-containing liquid composition may be poured into the battery in multiple batches, thereby performing multi-stage mixing.

[0067] The amount of the electrolyte-containing liquid composition used can be determined, for example, from the concentration of the electrolyte-containing liquid composition and the amount of carrier ions to be replenished. The amount of carrier ions to be replenished can be calculated, for example, from the results of "3. Other steps, (3) First capacity measurement step" described later. For example, the amount of the capacity reduction (amount of electricity) can be converted into the number of moles of carrier ions to calculate the amount of carrier ions to be replenished. The amount of the electrolyte-containing liquid composition used can be an appropriate amount depending on the amount of carrier ions to be replenished. An example of an electrolyte-containing liquid composition used in an inappropriate amount is, for example, an excessively large amount. When the amount used is excessively large, the carrier ions are excessively supplied to the positive electrode, which may cause deterioration of the positive electrode active material.

[0068] After mixing the electrolyte-containing liquid composition with the electrolyte of the battery, the battery is left standing. This allows metal cations in the electrolyte-containing liquid composition to be supplied to the positive electrode. That is, carrier ions that contribute to charging and discharging can be replenished. For example, the battery may be left standing in a temperature environment of 0°C to 80°C. For example, the battery may be left standing in a room temperature environment. The standing time may be, for example, 1 hour to 48 hours. The standing time may be, for example, 6 hours to 24 hours.

[0069] The driving force of the reaction in the present disclosure is considered to be the potential difference between the electrolyte of the battery to which the electrolyte-containing liquid composition is mixed and the positive electrode. Therefore, for example, the higher the SOC of the battery, the more likely it is that the movement of metal cations will be promoted. This is because it is considered that the higher the SOC, the higher the potential of the positive electrode, and the larger the potential difference between the electrolyte and the positive electrode. However, if the SOC is excessively high, the material in the battery may be easily deteriorated when the battery is opened. When the electrolyte-containing liquid composition is mixed, the SOC of the battery may be, for example, 10% to 100%. When the electrolyte-containing liquid composition is mixed, the SOC of the battery may be, for example, 30% to 80%. When the electrolyte-containing liquid composition is mixed, the SOC of the battery may be, for example, 40% to 60%.

[0070] 3.Other processes (1) Constant current / constant voltage charging process As described above, it is expected that the capacity of the battery will be restored by mixing the electrolyte-containing liquid composition with the electrolyte of the battery. Depending on the type of composition put into the battery, the capacity of the battery will be restored by mixing it into the battery, but the battery capacity may decrease due to the charge-discharge cycle in the subsequent use. In such a case, as shown in FIG. 5, after mixing the composition, constant current-constant voltage (CCCV) charging, in which constant current charging and constant voltage charging are performed in sequence, may be performed to the battery, and it may be expected that, for example, cycle resistance will be improved. FIG. 5 is a schematic flow chart of a capacity recovery method for a nonaqueous electrolyte secondary battery when a conventional carrier ion supplement is used, and is obtained by adding a "constant current constant voltage charging step" to the schematic flow chart of the capacity recovery method for a nonaqueous electrolyte secondary battery in the present disclosure of FIG. 4.

[0071] However, as is clear from the examples described below, when the above-mentioned electrolyte-containing liquid composition is used, a battery having good cycle resistance can be obtained without constant-current constant-voltage charging after mixing the electrolyte-containing liquid composition. Therefore, in the present disclosure, it is preferable not to include a constant-current constant-voltage charging step in which the electrolyte-containing liquid composition is mixed with the electrolyte of the nonaqueous electrolyte secondary battery and then the nonaqueous electrolyte secondary battery is charged with a constant current and a constant voltage. This allows the time required for the capacity of the battery to be restored to be significantly reduced.

[0072] (2) Battery collection process The method for restoring capacity of a battery according to the present disclosure may include collecting the battery. The battery may be collected by any method. For example, used batteries may be collected from the market. For example, used batteries may be collected during inspection of a vehicle or the like equipped with the battery.

[0073] (3) First capacitance measurement process The capacity recovery method for a battery according to the present disclosure may include calculating a first capacity loss rate by measuring the capacity of the recovered battery. The capacity measurement may be performed using a general charge / discharge device. The first capacity loss rate (unit: %) may be calculated by the following formula. In the above formula, C 0 indicates the initial capacity. C 1 indicates the capacity measured after recovery. For example, the rated capacity of a battery may be considered as the initial capacity. 1st capacity reduction rate={(C 0 -C 1 ) / C 0}×100

[0074] (4) First judgment step The capacity recovery method of the battery according to the present disclosure may include judging whether or not capacity recovery is necessary based on the first capacity reduction rate. For example, when the first capacity reduction rate is equal to or greater than a reference value, the process may proceed to the above-mentioned "2. Mixing step". That is, the electrolyte-containing liquid composition may be mixed with the electrolyte of a battery in which a specified battery capacity reduction is observed. The reference value may be set arbitrarily according to the application of the battery, the environment in which the battery is used, and the like. Note that, instead of the capacity, other characteristics may be measured. For example, resistance measurement or the like may be performed. The need for capacity recovery may be judged based on the result of the resistance measurement. The need for capacity recovery may be judged based on the result of the capacity measurement and the result of the resistance measurement.

[0075] (5) Battery reuse process In the above "(4) first determination step", for example, when the first capacity loss rate is less than a reference value, the battery may be reused as is. The battery may be reused for the purpose for which it was collected. The battery may be reused for a purpose different from the purpose for which it was collected.

[0076] (6)Second capacity measurement process The capacity recovery method of the present disclosure may include calculating a second capacity loss rate by measuring the capacity after mixing the electrolyte-containing liquid composition. The second capacity loss rate can be calculated in the same manner as the first capacity loss rate.

[0077] (7) Second judgment step The battery capacity recovery method according to the present disclosure may include determining whether or not material recycling is required based on the second capacity loss rate. For example, when the second capacity loss rate is equal to or greater than a reference value, the process may proceed to "(8) Material recycling process" described below. For example, when the second capacity loss rate is less than the reference value, the process may proceed to "(5) Battery reuse process" described above. In other words, the capacity may be considered to have been recovered to the extent that the battery can be reused.

[0078] (8) Material recycling process In the above "(7) second determination step", for example, when the second capacity loss rate is equal to or greater than a reference value, it may be deemed difficult to reuse the battery. By dismantling the battery, various materials (e.g., rare metals, etc.) may be recovered.

[0079] 4. Capacity recovery method for non-aqueous electrolyte secondary batteries In the present disclosure, a lithium ion battery is described as an example of a battery to be subjected to capacity recovery. However, the battery should not be limited to a lithium ion battery as long as it contains a non-aqueous electrolyte. The battery may be, for example, a sodium ion battery, a magnesium ion battery, etc. The structure of the battery may be the same as that of a general battery, for example, a battery including a positive electrode, a negative electrode, and an electrolyte, with a separator disposed between the positive electrode and the negative electrode.

[0080] In the present disclosure, the battery to be subjected to capacity recovery may be, for example, a used battery. The battery to be subjected to capacity recovery may be, for example, an unused battery. It is considered that the capacity of an unused battery is not substantially decreased. However, in general, a coating is formed on the negative electrode during the manufacturing process of the battery. Therefore, even in an unused battery, the carrier ions may be decreased from the initial amount. By mixing the above-mentioned electrolyte-containing liquid composition with the electrolyte of an unused battery, a battery with increased capacity can be obtained. The battery with increased capacity may have, for example, a capacity retention rate exceeding 100%. On the other hand, when a battery is used and the capacity is decreased, the capacity can be restored by mixing the electrolyte-containing liquid composition with the electrolyte of the battery.

[0081] D. Manufacturing method of non-aqueous electrolyte secondary battery The present disclosure can also provide a method for manufacturing a nonaqueous electrolyte secondary battery, which includes a capacity recovery step of performing the above-mentioned capacity recovery method for a nonaqueous electrolyte secondary battery on a battery with reduced capacity. The capacity recovery method for a nonaqueous electrolyte secondary battery is the same as that described in "C. Capacity recovery method for a nonaqueous electrolyte secondary battery" above, and therefore will not be described here.

[0082] The present disclosure is not limited to the above-described embodiments. The above-described embodiments are merely examples, and anything that has substantially the same configuration as the technical idea described in the claims of the present disclosure and exhibits similar effects is included in the technical scope of the present disclosure. EXAMPLES

[0083] [Example 1] <Preparation of Electrolyte-Containing Liquid Composition> Powdered naphthalene was prepared as an aromatic compound, 1,2-dimethoxyethane (DME) as a solvent, and Li as a metal cation source. Each material was placed in a glove box. An Ar atmosphere was present inside the glove box. A low dew point environment was created inside the glove box. A first mixture was prepared by adding naphthalene to DME. The first mixture was stirred to completely dissolve the naphthalene in the DME. This prepared a precursor solution. The amount of naphthalene added was adjusted so that the concentration in the liquid composition was 1.0 mol / L.

[0084] A second mixture was prepared by adding Li to the precursor solution. The second mixture was stirred to dissolve all of the Li. This resulted in the preparation of a liquid composition. The amount of Li added was adjusted so that the concentration in the liquid composition was 1.0 mol / L. It is believed that lithium naphthalenide was produced in the solution by the reaction of the following formula (5).

[0085] [ka]

[0086] The obtained liquid composition and an electrolyte were mixed so that the content of the electrolyte in the electrolyte-containing liquid composition was 50% by volume, to produce an electrolyte-containing liquid composition. The mixed electrolyte had the same composition as the electrolyte of the battery to be mixed with the electrolyte-containing liquid composition in the subsequent step and to be restored in capacity (capacity restoration target). The concentration of lithium naphthalenide was thought to be 1.0 mol / L.

[0087] <Capacity measurement of used batteries> The capacity of a used lithium-ion battery was measured using the following procedure. Two plates were prepared. A battery was sandwiched between the two plates. The two plates were fixed so that a specified load was applied to the battery. The battery in this state was stored in a thermostatic chamber for three hours. The temperature of the thermostatic chamber was set to room temperature.

[0088] After three hours of storage, the battery was connected to a charger / discharger. A charge / discharge cycle was performed once at a current rate of 0.5C in the range of 0% SOC to 100% SOC. The discharge capacity at this time was designated as the "capacity before use." The "capacity maintenance rate before use" was calculated by dividing the capacity before use by the initial capacity. The results are shown in Table 1 below. The capacity maintenance rate before use of the used battery was about 50%. In other words, the capacity of the used battery had decreased by about 50%.

[0089] <Mixing into batteries> The SOC of the battery was adjusted to 50%. The electrolyte-containing liquid composition was poured into the used battery. In the battery, the electrolyte-containing liquid composition and the battery electrolyte were mixed. The electrolyte of the battery was prepared by mixing ethylene carbonate (EC), dimethyl carbonate (DMC), and ethyl methyl carbonate (EMC) in a volume ratio of 3:4:3, and dissolving 1.1 M LiPF 6 A non-aqueous electrolyte solution containing the above was used.

[0090] [Example 2] An electrolyte-containing liquid composition was prepared in the same manner as in Example 1, except that the liquid composition and the electrolyte were mixed so that the content of the electrolyte in the electrolyte-containing liquid composition was 30 volume %. The electrolyte-containing liquid composition was then mixed with a used battery.

[0091] [Comparative Example 1] An electrolyte-containing liquid composition was prepared in the same manner as in Example 1, except that tetrahydrofuran (THF) was used as a solvent instead of DME, and mixed with a used battery. In this comparative example, after mixing of the electrolyte-containing liquid composition, the obtained battery was charged at a constant current and constant voltage for one week.

[0092] [Comparative Example 2] An electrolyte-containing liquid composition was prepared in the same manner as in Example 1, except that tetrahydrofuran (THF) was used as the solvent instead of DME, and mixed with a used battery.

[0093] [Comparative Example 3] An electrolyte-containing liquid composition was prepared in the same manner as in Example 1, except that the liquid composition and the electrolyte were mixed so that the content of the electrolyte in the electrolyte-containing liquid composition was 0 volume %, and then mixed into a used battery.

[0094] [Comparative Example 4] An electrolyte-containing liquid composition was prepared in the same manner as in Example 1, except that the liquid composition and the electrolyte were mixed so that the content of the electrolyte in the electrolyte-containing liquid composition was 20 volume %. The electrolyte-containing liquid composition was then mixed with a used battery.

[0095] [evaluation] <Measurement of battery capacity after insertion> After the electrolyte-containing liquid composition was poured in, the battery was left for 12 hours. After the 12 hours, the discharge capacity was measured using the same procedure as above. The discharge capacity at this time was taken as the "capacity after pouring". The "capacity maintenance rate after pouring" was calculated by dividing the capacity after pouring by the initial capacity. The "ratio of capacity maintenance rates before and after pouring" was calculated by dividing the capacity maintenance rate after pouring by the capacity maintenance rate before pouring. The results are shown in Table 1 below. A ratio of the capacity maintenance rates before and after pouring exceeding 1 indicates that the capacity has increased before and after pouring.

[0096] <Cycle durability test> A cycle durability test was conducted on the battery after the above-mentioned storage. The test consisted of 100 cycles of charge and discharge under the conditions of temperature: 25°C, constant current charge: 0.5C, constant current discharge: 0.5C, and SOC: 0% to 100%. The results are shown in Figure 6. After the cycle durability test was completed, the capacity of the battery was measured. From this, the "capacity retention rate after cycling" was calculated. The "capacity retention rate after cycling" is shown in Table 1 below.

[0097] [Table 1]

[0098] In Examples 1 and 2, which use DME as a solvent and contain a predetermined amount of electrolyte, the capacity increased by mixing the electrolyte-containing liquid composition with the electrolyte of the battery. This result is believed to be due to the Li ions of lithium naphthalenide being electrochemically inserted only into the positive electrode. On the other hand, in Comparative Examples 3 and 4, which use DME as a solvent but contain a small amount of electrolyte, the capacity of the battery dramatically decreased after the electrolyte-containing liquid composition was added. It is presumed that the content ratio of electrolyte in the electrolyte-containing liquid composition has a large effect on the recovery of battery capacity.

[0099] In Comparative Examples 1 and 2, in which THF was used as the solvent, the capacity increased by mixing the electrolyte-containing liquid composition with the electrolyte of the battery. The cycle resistance was high in Comparative Example 1, in which constant current and constant voltage charging was performed after mixing, but in Comparative Example 2, in which constant current and constant voltage charging was not performed, the capacity dropped rapidly after a certain period of time. On the other hand, in Examples 1 and 2, in which DME was used as the solvent and a predetermined amount of electrolyte was included, it was confirmed that the battery showed high cycle resistance, similar to Comparative Example 1, although constant current and constant voltage charging was not performed after mixing.

Claims

1. An electrolyte-containing liquid composition used to supply carrier ions to a non-aqueous electrolyte secondary battery, comprising: The electrolyte-containing liquid composition comprises a liquid composition comprising a solvent and a solute, and an electrolyte; The content of the electrolyte in the electrolyte-containing liquid composition is 30% by volume or more and 50% by volume or less, the solvent is 1,2-dimethoxyethane; the solute is an ionic compound; The ionic compound comprises a radical anion of an aromatic compound and a metal cation, the aromatic compound is a polyacene or a polyphenyl; the metal cation is an ion of the same type as the carrier ion, The electrolyte solution is The electrolyte contains at least one solvent selected from ethylene carbonate (EC), propylene carbonate (PC), butylene carbonate (BC), vinylene carbonate (VC), vinylethylene carbonate (VEC), fluoroethylene carbonate (FEC), dimethyl carbonate (DMC), ethyl methyl carbonate (EMC), and diethyl carbonate (DEC), The electrolyte solution contains at least one solute selected from LiPF 6 , LiBF 4 , LiN(FSO 2 ) 2 , and LiN(CF 3 SO 2 ) 2 ; Liquid composition containing electrolyte.

2. The radical anion includes at least one selected from the group consisting of a naphthalene radical anion and a biphenyl radical anion, The electrolyte-containing liquid composition according to claim 1 , wherein the metal cation comprises a lithium ion.

3. A method for producing an electrolyte-containing liquid composition used to supply carrier ions to a nonaqueous electrolyte secondary battery, comprising the steps of: A precursor solution preparation step of preparing a precursor solution by dissolving an aromatic compound in a solvent; a liquid composition preparation step of preparing a liquid composition by dissolving a metal in the precursor solution; an electrolyte-containing liquid composition preparation step of mixing the liquid composition and an electrolyte solution such that the content of the electrolyte solution in the electrolyte-containing liquid composition is 30% by volume or more and 50% by volume or less to prepare an electrolyte-containing liquid composition; Including, the solvent comprises 1,2-dimethoxyethane; the aromatic compound is a polyacene or a polyphenyl; A method for producing an electrolyte-containing liquid composition, wherein the metal cation generated from the metal is the same type of ion as the carrier ion.

4. An electrolyte-containing liquid composition preparation step of preparing the electrolyte-containing liquid composition according to claim 1 or 2; a mixing step of mixing the electrolyte solution-containing liquid composition with an electrolyte solution of a nonaqueous electrolyte secondary battery in which a prescribed decrease in battery capacity has been observed.

5. 5. The capacity recovery method for a nonaqueous electrolyte secondary battery according to claim 4, which does not include a constant-current, constant-voltage charging step of subjecting the nonaqueous electrolyte secondary battery to constant-current, constant-voltage charging after the electrolyte-containing liquid composition is mixed with the electrolyte of the nonaqueous electrolyte secondary battery.