New antibacterial breathable fabric and its manufacturing method

Abstract

The present invention relates to the technical field of nonwoven fabric manufacturing, in particular to a new antibacterial breathable fabric and its manufacturing method. The manufacturing method includes the following steps: S1, surface hot rolling treatment: a fiber web layer is subjected to surface hot rolling treatment, in which the lower surface of the fiber web layer is supported by a flexible belt, and its upper surface is contacted and hot rolled by a hot rolling member to produce a fiber web layer in which the upper surface fibers are thermally bonded and the lower surface fibers are fluffy; S2, spunlace processing treatment: a spunlace processing treatment is performed on the lower surface of the fiber mesh layer obtained in S1, and the flexible belt is made of a flexible material with high temperature resistance. This manufacturing method can realize the disposable processing molding of the new antibacterial breathable fabric. In addition, the finished fabric has excellent waterproof and antibacterial properties and good wearing comfort, and at the same time maintains good mechanical performance to extend the life and meet the usage requirements.

Description

[Technical field]

[0001] The present invention relates to the technical field of nonwoven fabric manufacturing, and in particular to a novel antibacterial breathable fabric and its manufacturing method. [Background technology]

[0002] Flashed polyethylene nonwoven material has excellent strength, tear resistance, puncture resistance and microbial barrier properties, making it the optimal choice for medical protective clothing fabrics.

[0003] However, the reinforcement method of conventional flash nonwoven fabrics generally adopts the methods of hot pressing and hot rolling. The fabrics made by these methods have a hard texture and are not suitable for direct use in the manufacture of protective clothing. To be used as protective clothing fabrics, they generally need to undergo a mechanical softening process. However, such treatment is not only complicated and tedious, but also damages the fibers in the fabric during the mechanical softening process, which ultimately affects the mechanical strength of the fabric and reduces the use performance of the fabric.

[0004] For example, the Chinese invention patent "System and process for softening high density polyethylene paper using a flush method" with publication number CN110528216A and publication date December 3, 2019 discloses a system for softening high density polyethylene paper using a flush method, including mechanical structures such as a pinch-down device with a driving device, a wrinkle device for producing lateral wrinkles, and a stretching device for eliminating wrinkle stretching. This solution requires producing high density polyethylene paper using a flush method and softening the fabric with mechanical force, which means that one-time molding is not possible, and at the same time, the size of the fabric changes when softened with mechanical force, which reduces the mechanical strength of the fabric, ultimately affecting the life of the fabric.

[0005] In addition, the invention "Composite Breathable Sheet" of the Chinese invention patent with publication number CN101137503A and publication date December 3, 2019, discloses a moisture-permeable composite sheet with a multi-layer material structure in which an absorbent fiber nonwoven layer is spunlaced, and mentions a preparation method in which a non-porous liquid-impermeable moisture-permeable film layer is formed on one side of the absorbent nonwoven layer by extrusion coating, and then a protective nonwoven layer of adhesive is laminated on the opposite side of the film to the absorbent nonwoven layer. The adhesive layer is located between the protective nonwoven layer and the film layer. As can be seen from the manufacturing process, the multi-layer material produced is made in individual steps that are the same for each layer, and after going through multiple steps, it becomes a material according to the purpose and is multi-layered composite. Due to the many processing steps, it cannot be molded at once. Summary of the Invention [Problem to be solved by the invention]

[0006] The problems with the prior art mentioned in the above Background Art are as follows: 1. Fabrics made from conventional flash nonwoven fabrics using hot pressing or hot rolling methods have a hard texture and generally require a mechanical softening process to be used as protective clothing fabrics. This manufacturing method is complicated and tedious, and affects the mechanical strength of the fabric. 2. In order to manufacture a finished fabric with good strength, waterproofness, antibacterial properties and wearing comfort, it is necessary to combine or bond materials made using multiple different technologies to form a composite structure of multi-layered materials to obtain the desired performance. This manufacturing method requires many processing steps and cannot be molded all at once. [Means for solving the problem]

[0007] In order to solve the above problems, the present invention provides a new method for manufacturing antibacterial breathable fabric, which includes the following steps:

[0008] S1, surface hot rolling treatment: the fiber web layer is subjected to surface hot rolling treatment, in which the lower surface of the fiber web layer is supported by a flexible belt and its upper surface is contacted with a hot rolling member and hot rolled, producing a fiber mesh layer in which the fibers on the upper surface are thermally bonded and the fibers on the lower surface are fluffy.

[0009] S2, spunlace processing: the underside of the fiber mesh layer obtained in S1 is subjected to spunlace processing, and the flexible belt is made of high-temperature resistant flexible material.

[0010] In one embodiment, the fiber mesh layer is subjected to a cold pressing process prior to the surface hot rolling process.

[0011] In one embodiment, a drying process is further included, in which the nonwoven fabric after S2 treatment is dried to remove moisture from the nonwoven fabric, thereby obtaining a new antibacterial and breathable fabric.

[0012] In one embodiment, during the drying step, the drying temperature is below the melting point of the fiber mesh layer.

[0013] In one embodiment, the flexible belt is made from a high temperature resistant blanket.

[0014] The present invention also employs a novel antibacterial breathable fabric, which has a first side and a second side, the first side being an antibacterial side and the second side being a spunlace side layer.

[0015] The upper surface of the fiber mesh layer is subjected to a surface hot rolling treatment to form an antibacterial surface on the upper surface, and in the surface hot rolling treatment, the lower surface of the fiber mesh layer is supported by a flexible belt and the upper surface is contacted and hot rolled by a hot rolling member.

[0016] The lower surface of the fiber mesh layer after the surface hot rolling treatment is subjected to a spunlace processing treatment to form a spunlace surface layer on the lower surface.

[0017] In one embodiment, the basis weight is 30 g to 90 g, and the thickness is 0.1 mm to 0.5 mm.

[0018] In one embodiment, the air permeability is 5 mm / s or more and 50 mm / s or less, and the moisture impermeability of the first surface is 5 kPa or more and 20 kPa or less.

[0019] In one embodiment, the breaking strength in the transverse and longitudinal directions is 150N / 5cm or more, the tear strength is 8N or more, the peel strength is 3N or more, and the drape coefficient is 50% or less.

[0020] In one embodiment, the moisture permeability is 2500 g / (m 2 d) or higher, and the synthetic blood permeability of the first surface is level 2 or higher. Effect of the Invention

[0021] From the above, the new antibacterial breathable fabric manufacturing method provided by the present invention has the following beneficial effects compared to the conventional technology:

[0022] The new antibacterial and breathable fabric manufacturing method provided by the present invention makes it possible to realize disposable processing and molding of antibacterial and breathable fabrics, without the need for subsequent softening processing during the manufacturing process, and without the need for the finished fabric to be compounded or bonded with materials of different technologies. The finished fabric can have excellent waterproof and antibacterial properties and good wearing comfort, while maintaining good mechanical properties to extend its service life and meet the usage requirements.

[0023] Additional features and advantages of the invention will be set forth in the following description, and in part will be obvious from the description, or may be learned by the practice of the invention. The objectives and other advantageous advantages of the invention will be realized and obtained by the structure particularly pointed out in the description, claims, and drawings. [Brief description of the drawings]

[0024] In order to more clearly describe the technical scheme in the embodiments of the present invention or the prior art, the drawings used in the description of the embodiments or the prior art are briefly described below. It is obvious that the drawings in the following description are part of the embodiments of the present invention, and those skilled in the art can obtain other drawings from these drawings without creative work. The positional relationship described in the drawings in the following description is based on the direction shown by the assembly in the drawings, unless otherwise specified. [Figure 1] FIG. 1 is a process flow diagram of a method for producing a new antibacterial breathable fabric provided by the present invention. [Diagram 2] FIG. 1 is a structural diagram of a preferred embodiment of an antibacterial breathable fabric manufacturing device provided by the present invention. [Diagram 3] FIG. 2 is a structural diagram of a surface hot rolling unit in a preferred embodiment of the antibacterial breathable fabric manufacturing apparatus provided by the present invention. [Figure 4] FIG. 2 is a structural diagram of a flash spinning unit in a preferred embodiment of the antibacterial breathable fabric manufacturing apparatus provided by the present invention. [Diagram 5] FIG. 2 is a structural diagram of a spunlace fixing unit, which is a preferred embodiment of the antibacterial breathable fabric manufacturing apparatus provided by the present invention. [Figure 6] FIG. 2 is a structural diagram of the new antibacterial breathable fabric provided by the present invention. [Figure 7] This is a micrograph of the first side of the finished new antibacterial breathable fabric obtained in Example 1 provided by the present invention. [Figure 8] This is a micrograph of the second side of the finished new antibacterial breathable fabric obtained in Example 1 provided by the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0025] In order to make the purpose, technical scheme and advantages of the embodiments of the present invention clearer, the technical scheme in the embodiments of the present invention will be described below clearly and completely in conjunction with the drawings in the embodiments of the present invention. Obviously, the described embodiments are only some embodiments of the present invention, not all embodiments. The technical features designed in different embodiments of the present invention described below can be combined with each other as long as they do not conflict with each other. Based on the embodiments in the present invention, all other embodiments obtained by those skilled in the art without performing creative labor belong to the scope of protection of the present invention.

[0026] In the description of the present invention, it is necessary to explain that all terms used in the present invention (including technical and scientific terms) have the same meaning as those commonly understood by those skilled in the art to which the present invention belongs, and cannot be understood as limitations on the present invention. It is further understood that the terms used in the present invention should be understood to have a meaning consistent with the meaning of these terms in the context of the present specification and in the relevant field, and should not be understood in an idealized or overly formal sense unless expressly defined in the present invention.

[0027] Figure 1 is a process flow diagram of the manufacturing method of the new antibacterial breathable fabric provided by the present invention. Figures 2-5 are schematic diagrams used to assist in describing a preferred embodiment of the manufacturing apparatus used to implement the manufacturing method of the new antibacterial breathable fabric 700 of the present invention, which is composed of a flash spinning unit 100, a surface hot rolling unit 200, a spunlace fixing unit 300, a drying unit 400, and a winding unit 500 connected in sequence.

[0028] As shown in Figures 1 to 5, the preferred embodiment of the manufacturing method for the novel antibacterial breathable fabric 700 provided by the present invention is as follows:

[0029] This involves the following steps:

[0030] S1, surface hot rolling treatment: surface hot rolling treatment is performed on the fiber mesh layer 600. Here, the lower surface of the fiber mesh layer 600 is supported by the flexible belt 221, and its upper surface is contacted and hot rolled by the hot rolling member 211 to produce a fiber mesh layer 600 in which the fibers on the upper surface are thermally bonded and the fibers on the lower surface are fluffy.

[0031] S2, Spunlace processing: Spunlace processing is performed on the lower surface of the fiber mesh layer 600 obtained in S1. The flexible belt 221 is made of a flexible material that is resistant to high temperatures.

[0032] Specifically, in the manufacturing process, the upper surface of the fiber mesh layer 600 contacts the hot rolling member 211 to perform a surface hot rolling process, and the fibers on the upper surface of the fiber mesh layer 600 are heated and fused and strengthened to form a dense fiber layer with excellent waterproof and antibacterial properties. Meanwhile, the lower surface of the fiber mesh layer 600 contacts the flexible belt 221 and is supported by the flexible belt 221 during the surface hot rolling process. Since the flexible belt 221 is made of a flexible material with high temperature resistance, and the flexible belt 221 itself is soft and has a low temperature and does not melt and adhere, the lower surface of the fiber mesh layer 600 does not melt and adhere during the surface hot rolling process, and the fibers can maintain a fluffy state.

[0033] The fiber mesh layer 600 after hot rolling is subjected to a spunlace processing process, and high-pressure water needles formed by the spunlace head 32 act on the underside (i.e., the side with fluffy fibers) of the fiber mesh layer 600. The action of the high-pressure water needles causes the fluffy fibers to intertwine with each other, and the fiber mesh layer 600 forms a dense nonwoven fabric with a certain thickness.

[0034] Specifically, the manufacturing method of this novel antibacterial breathable fabric 700 provided by the present invention includes at least the following design principles and inventive concepts:

[0035] The existing spunlace process is flexible and intertwined, and does not affect the original characteristics of the fiber and does not damage the fiber. The nonwoven fabric processed by this method can not only guarantee the mechanical performance, but also has an appearance closer to traditional woven fabrics than other nonwoven fabrics, and the fabric is soft and comfortable to wear. However, the spunlace method has requirements for the processed material, and the fibers on the surface of the material before spunlace processing must have a certain degree of cross-linking, and the fibers must remain relatively fluffy. In this way, the material will not break apart during spunlace processing, and at the same time, the fibers can be entangled by the action of water needles to ensure the spunlace effect on the surface of the fabric.

[0036] The important points of the present invention are as follows.

[0037] The two surfaces of the finished fabric produced by the present invention must have two properties: one side has the properties of flash polyethylene paper, with a smooth surface and dense thermally bonded fiber layer, and has excellent waterproof and antibacterial properties; the other side has the properties of spunlace nonwoven fabric, with the surface having the characteristics of conventional woven fabrics, excellent skin compatibility, while at the same time providing good overall material flexibility, excellent wearing comfort, and maintaining good mechanical properties.

[0038] To achieve this feature, the present invention innovatively introduces spunlace technology into the processing technology of flash nonwoven fabrics. In order to give the fabric the surface characteristics of spunlace nonwoven fabrics, it is necessary to keep the fibers of the fabric as fluffy as possible before spunlace processing.

[0039] Based on this, the present invention has found an important point to be controlled in the preparation method, namely, when the surface of the fiber mesh layer 600 is reinforced by heat bonding, the surface fibers on the side in contact with the hot-rolled member 211 are sufficiently heated and heat bonded to be fixed, and at the same time, the surface fibers on the side not in contact with the hot-rolled member 211 are maintained in a fluffy state, so that the surface fibers on the fluffy side of the fibers can be sufficiently entangled in the spunlace processing. In this way, the obtained material has excellent breathability and soft wearing comfort, and the waterproof and antibacterial properties of the heat-bonded side can be maintained. Unlike the conventional hot rolling process, in the surface hot rolling treatment of the present invention, the side not in contact with the hot-rolled member 211 is supported by the soft flexible belt 221 that is resistant to high temperatures, so that the fibers on this side can be maintained in a fluffy state, and a finished fabric with desired properties can be obtained by combining with the spunlace processing process.

[0040] From the above, we can see the following:

[0041] In the present invention, spunlace technology is innovatively applied to the manufacturing process of flash nonwoven fabric, and in order to ensure the spunlace effect, a high-temperature resistant soft flexible belt 221 is used instead of the conventional stainless steel roller or rubber roller, and the surface hot rolling technology is innovatively applied, in which the surface of the fiber web that contacts the heating roller is heated, and the heated fibers bond to each other to form a dense waterproof and antibacterial layer. Since the fibers on the opposite side are not in contact with the hot rolling member 211 but with the high-temperature resistant soft flexible belt 221, the surface fibers can be kept in a relatively fluffy state, which avoids the densification of the fibers on both sides by the conventional heating roller rolling method, and is advantageous for entangling with water needles during the subsequent spunlace processing.

[0042] The surface hot rolling technology and spunlace processing can be combined to obtain the desired material in one go, eliminating the need for conventional mechanical softening, and eliminating the need to compound or bond the finished fabric with materials from multiple different processes. The fabric obtained by this invention has good breathability, softness, and comfort, and maintains good mechanical performance while maintaining the waterproof and antibacterial properties of the thermally bonded surface.

[0043] Preferably, in the surface hot rolling process, the hot rolling temperature (i.e., the temperature of the hot rolling member 211) is (100-200)°C, and the tension of the flexible belt 221 is controlled to 0.5-6.0 MPa. In the spunlace processing process, the water pressure is (20-250) bar. With the appropriate hot rolling temperature and pressure, Hot rolling The fibers on the top surface of fiber mesh layer 600 that contact the surface of component 211 are heated and melted to bond and reinforce the fiber mesh layer, forming a dense fiber layer.

[0044] Preferably, the method further includes a step of producing a fiber mesh layer 600. In the step of producing the fiber mesh layer 600, a spinning solution is prepared using a polymer compound as a raw material, and the fiber mesh layer 600 is formed from the spinning solution by a flash spinning method.

[0045] Preferably, the fiber mesh layer 600 is subjected to a cold pressing process before the surface hot rolling process. After the fiber mesh layer 600 is prepared, before the surface hot rolling process, the fiber mesh layer 600 is cold pressed and pressed slightly to give the fiber mesh layer 600 a certain tensile force, so that the fiber mesh layer 600 can be easily transferred to the next process. More preferably, the fiber mesh layer is cold pressed using a cold pressing member 15, which is a hollow stainless steel roller. The light weight of the pressing roller prevents the fiber mesh layer 600 from being pressed too tightly, which makes it easier to form an upper surface with clearly fused fibers and a lower surface with fluffy fibers of the fiber mesh layer 600 after the surface hot rolling process.

[0046] Preferably, a drying process is further included. In the drying process, the nonwoven fabric after the S2 treatment is dried to remove the moisture of the nonwoven fabric, thereby obtaining a new antibacterial breathable fabric 700. More preferably, in the drying process, the drying temperature is lower than the melting point of the fiber mesh layer 600 (i.e., the melting point of the polymer compound in the spinning solution). The nonwoven fabric after spunlace is dried to completely remove the moisture on the surface of the nonwoven fabric, and since the polymer raw material is a thermoplastic material, when heated to a certain temperature, the fibers soften, and when further cooled, the fibers entangled with the spunlace are firmly attached, which is advantageous for improving the performance of the finished fabric. In addition, since the drying temperature does not exceed the melting point of the polymer, the fibers do not melt and the fabric does not harden, the nonwoven fabric after drying can maintain the soft characteristics of the spunlace nonwoven fabric.

[0047] Preferably, the flexible belt 221 is made of high temperature resistant blanket. The flexible belt 221 adopts high temperature resistant blanket material, which is not only easy to obtain raw materials, but also has soft fabric and high temperature resistance performance, and can meet the usage requirements. In addition, based on the above design concept, the flexible belt 221 can also adopt other high temperature resistant flexible materials that have a certain deflection, flexibility, and high temperature resistance. Materials with a temperature resistance of 240℃ or more are preferred.

[0048] The present invention provides a preferred embodiment of a manufacturing apparatus used to implement the manufacturing method of the above novel antibacterial breathable fabric 700, as shown in Figures 2-5, specifically as follows:

[0049] The manufacturing equipment of the novel antibacterial breathable fabric 700 includes a flash spinning unit 100, a surface hot rolling unit 200, a spunlace fixing unit 300 and a drying unit 400 connected in series.

[0050] Here, the flash spinning unit 100 is used to prepare a fiber mesh layer 600. The hot rolling unit 200 includes a conveyor belt member 22 and a rotary heating member 21. The conveyor belt member 22 includes a flexible belt 221 and at least two support members 222. The support members 222 are rotatably supported on the inner surface of the flexible belt 221. The outer surface of the flexible belt 221 is in contact with the outer periphery of the rotary heating member 21, and the rotary heating member 21 rotates to move to the outer periphery of the support member 222, and the fiber mesh layer 600 is introduced to the outer surface of the flexible belt 221, and then its lower surface is brought into contact with the flexible belt 221, and its upper surface is brought to the outer periphery of the rotary heating member 21 to perform a surface hot rolling treatment. The spunlace fixing unit 300 is used to perform a spunlace treatment on the lower surface of the fiber mesh layer 600 after the surface hot rolling treatment to obtain a nonwoven fabric after spunlace treatment. The drying unit 400 is used to dry the nonwoven fabric after spunlace to obtain an antibacterial and breathable fabric.

[0051] Regarding the flash spinning unit 100,

[0052] Preferably, the components of the flash spinning unit 100 include a nozzle head 11, a rotating splitter plate 12, an air amplifier 13, and a moving mesh curtain 14. Note that the nozzle head 11, the rotating splitter plate 12, the air amplifier 13, and the moving mesh curtain 14 are all existing components of the flash spinning unit 100, and their structures and connection relationships are also conventional technologies, so they will not be repeated here.

[0053] Preferably, the flash spinning unit 100 includes a cold press member 15 disposed above the moving mesh curtain 14. Preferably, the cold press member 15 uses a cold press roller, which is a hollow stainless steel roller. The cold press member 15 is provided to cold press the fiber mesh layer 600 on the moving mesh curtain 14.

[0054] Preferably, the flash spinning unit 100 is provided with a first vacuum suction device 16 for sucking the evaporated gaseous solvent through the first vacuum suction device 16, and the gaseous solvent can be condensed to liquid solvent and then reused.

[0055] In addition, according to the design concept of the present invention, the present invention can also employ the flash spinning unit 100 for manufacturing existing fiber mesh layers 600 of other structures, including but not limited to the embodiment of the flash spinning unit 100 provided in the above preferred form.

[0056] Regarding the surface hot rolling unit 200,

[0057] Preferably, the flexible belt 221 has a closed loop structure, and the flexible belt 221 rotates in a circular shape around the outer periphery of the support member 222 by the rotational drive of the rotary heating member 21. More preferably, a guide support roller is adopted for the support member 222. In use, the fiber mesh layer 600 is introduced into the flexible belt 221 through the support member 222 (guide support roller) and moves together with the flexible belt 221. The cooperation of the support member 222 and the circular flexible belt 221 not only saves the usage of the flexible belt 221, but also makes the rotation of the flexible belt 221 more convenient.

[0058] Preferably, the conveyor belt member 22 further includes a tension adjusting device 223 for adjusting the tension of the flexible belt 221. The tension adjusting device 223 can adjust the tension of the flexible belt 221 to adjust the interaction force (i.e., hot rolling pressure) between the outer surface of the flexible belt 221 and the outer periphery of the rotary heating member 21.

[0059] Preferably, the conveyor belt member 22 includes a first support member 2221, a second support member 2222, a third support member 2223, and a fourth support member 2224. The first support member 2221 and the second support member 2222 are provided on both sides of the rotary heating member 21, respectively, and the third support member 2223 and the fourth support member 2224 are provided below the rotary heating member 21. By setting in this manner, the working area of ​​the fusion treatment of the rotary heating member 21 to the upper surface of the fiber mesh layer 600 is increased, and production efficiency is improved. More preferably, the tension adjusting device 223 is provided on the outside of the flexible belt 221 and is disposed between the third support member 2223 and the fourth support member 2224, so that the flexible belt 221 is disposed in a "W" shape. By setting in this manner, the tension adjusting device 223 and the support member 222 cooperate to easily adjust the tension of the flexible belt 221.

[0060] Preferably, the rotary heating member 21 includes a hot rolling member 211 (hot rolling roller) and a transmission 212 for driving the hot rolling member 211 in rotation.

[0061] Regarding the spunlace fixing unit 300,

[0062] Preferably, the components of the spunlace fixing unit 300 include a drum 31, a spunlace head 32, a second vacuum suction device 33, and a guide roller 34. It should be noted that the above drum 31, the spunlace head 32, the second vacuum suction device 33, and the guide roller 34 are all existing components of the spunlace fixing unit 300, and their structures and connection relationships are also conventional technologies, and will not be repeated here. Based on the design concept of the present invention, the present invention can adopt other structures of the existing spunlace fixing unit 300, including but not limited to the embodiment of the spunlace fixing unit 300 provided in the above preferred form.

[0063] Regarding the drying unit 400, the drying unit 400 can be selected from existing drying equipment, for example, can be selected from a drum 31 dryer, can be selected from a grip-type dryer, etc., and is not specifically described in the present specification.

[0064] Regarding the winding unit 500,

[0065] Preferably, the manufacturing apparatus further includes a winding unit 500 for winding the nonwoven fabric (i.e., antibacterial breathable fabric) after drying. Note that the winding unit 500 can be selected from existing winding machines, and is not specifically described in the present specification.

[0066] Combining the above-mentioned novel antibacterial breathable fabric 700 manufacturing method with the manufacturing equipment shown in Figures 2-5, the specific work process of realizing this manufacturing method using the preferred embodiment of the above-mentioned novel antibacterial breathable fabric 700 manufacturing equipment is as follows:

[0067] The polymer is added to the high-pressure reactor through a solute metering device and the associated solvent is added to the high-pressure reactor through a solvent metering device in a preset ratio. The high-pressure reactor is heated and pressurized to the preset reaction temperature and pressure state, and the polymer and solvent are sufficiently dissolved by the stirring action of the stirrer to form a homogeneous solution (i.e., spinning solution).

[0068] The homogeneous solution is sent to the nozzle head 11 through a high-pressure transport pipe, and the homogeneous solution is sprayed from the spinning holes of the nozzle head 11. The solvent in the solution evaporates from the high-temperature and high-pressure liquid and turns into gas. The polymer absorbs heat and cools rapidly, and at the same time, is rapidly stretched by the flashed solvent gas to form a fiber bundle containing a large amount of ultrafine fibers. The fiber bundle is refracted and diverged by the rotating splitter plate 12, and is amplified by the air amplifier 13 to form a fiber mesh with a mesh structure. The fiber mesh that continues to be formed is layered on the moving mesh curtain 14, and when the moving direction of the moving mesh curtain 14 and the falling direction of the fiber mesh are perpendicular to each other, the fiber mesh forms a continuous fiber mesh layer 600 with a certain basis weight and width on the moving mesh curtain 14, and the fiber mesh layer 600 is carried out from the moving mesh curtain 14.

[0069] Before entering the surface hot rolling unit 200, a cold press member 15 installed above the moving mesh curtain 14 is used to cold press the fiber mesh layer 600 on the moving mesh curtain 14. The solvent gas is collected by a first vacuum suction device 16 installed above, and condensed into liquid solvent for reuse.

[0070] The cold pressed fiber mesh layer 600 enters the surface hot rolling unit 200, where the fiber mesh layer 600 is introduced into the flexible belt 221 via the support member 222 (guide support roller). As the rotary heating member 21 rotates, Flexible Belt As the flexible belt 221 moves, the lower surface of the fiber mesh layer 600 comes into contact with the flexible belt 221. As the flexible belt 221 moves, the upper surface of the fiber mesh layer 600 is drawn into the outer periphery of the rotary heating member 21, and a surface hot rolling process is performed. The fibers on the upper surface of the fiber mesh layer 600 that contacts the surface of the rotary heating member 21 are heated and fused to be reinforced, forming a dense fiber layer. The lower surface of the fiber mesh layer 600 is not fused, and the fibers maintain a fluffy state.

[0071] When the fiber mesh layer 600 processed in the surface hot rolling unit 200 enters the spunlace bonding unit 300, a drum 31 is attached to the upper surface of the fiber mesh layer 600 (i.e., the surface bonded by hot rolling), and high-pressure water needles formed by the spunlace head 32 act on the lower surface of the fiber mesh layer 600 (i.e., the surface with fluffy fibers). The action of the high-pressure water needles causes the fluffy fibers to intertwine with each other, and the fiber mesh layer 600 forms a dense nonwoven fabric with a uniform thickness. The nonwoven fabric produced has excess moisture on the surface removed by the second vacuum suction device 33, and is then discharged by the guide roller 34.

[0072] The nonwoven fabric after spunlace enters the drying unit 400 to remove moisture from the surface of the nonwoven fabric. Finally, the dried finished product is wound up by the winding unit 500.

[0073] The present invention also provides the following examples and comparative examples.

[0074] The following examples and comparative examples are specifically set to demonstrate the effectiveness of the nonwoven fabric (i.e., antibacterial breathable fabric) produced by the novel antibacterial breathable fabric 700 manufacturing method of the present invention. Through test comparison of the relevant performance parameters of the manufactured products, the advantages of the novel antibacterial breathable fabric 700 manufacturing method provided by the present invention are demonstrated.

[0075] Example 1:

[0076] (1) Formation of fiber mesh layer 600 by flash spinning method:

[0077] A spinning solution is prepared using polymeric compounds as raw materials: 15% mass concentration polyethylene is sliced ​​and added to a high-pressure reactor together with an 85% mass concentration solvent (a mixture of 15% difluorochloromethane (R22) and 85% tetrafluorodichloroethane (R114)), and the temperature is raised to 180°C. After the temperature is raised, nitrogen gas is introduced to pressurize to 12 MPa while raising the temperature to 230°C, and stirring is performed for 2 hours at a stirring speed of 100 r / min. After the temperature is stabilized, a uniform spinning solution is formed in the high-pressure reactor.

[0078] The preferred embodiment of the new antibacterial breathable fabric 700 manufacturing equipment shown in Figure 2-5 is used to process the spinning solution, i.e., the spinning solution is flash-spun in the flash spinning unit 100 to form a 65g fiber mesh layer 600. Here, the spinning solution is sprayed from the nozzle head 11, and the speed of the spray air is 12000m / min. The spinning solution evaporates quickly, the polymer cools and solidifies into fiber bundles, and the fiber bundles sink into the moving mesh curtain 14, and the fibers aggregate into a mesh (i.e., fiber mesh layer 600), and the forward speed of the moving mesh curtain 14 is 50m / min.

[0079] (2) The fiber mesh layer 600 is subjected to a cold pressing process before the surface hot rolling process. The fiber mesh layer 600 is pressed by a cold pressing member 15 (cold pressing roller), which is a hollow stainless steel roller.

[0080] (3) Surface hot rolling treatment:

[0081] The obtained web layer 600 is introduced into the surface hot rolling unit 200 and subjected to a surface hot rolling process, whereby the fibers on one surface (upper surface) are thermally fused to form a dense fiber layer.

[0082] Here, the hot rolling temperature (the temperature of the hot rolling member 211 in the rotary heating member 21) is 140°C, and the rotation speed of the hot rolling member 211 is 52m / min. The flexible belt 221 adopts a high temperature resistant blanket. The tension of the flexible belt 211 is controlled to 1.65±0.15MPa.

[0083] (4) Spunlace processing:

[0084] The surface hot-rolled fiber mesh layer 600 is introduced into the spunlace bonding unit 300, which processes the other side (i.e., the bottom side) to form a dense material with different characteristics on both sides, i.e., a spunlaced nonwoven fabric.

[0085] Here, the water spouting pressure of the pre-wetting spunlace head 32 is 25 bar, the water spouting pressure of the main spunlace head 32 is 80 bar, the water spouting pressure of the spunlace head 32 for surface finishing is 52 bar, and the speed of the spunlace drum 31 is 54 m / min.

[0086] (5) The nonwoven fabric after spunlace is introduced into the drying unit 400 for drying / dehydration and low-temperature drying to obtain an antibacterial and breathable fabric.

[0087] Here, the drying temperature in the drying unit 400 is 105° C., the number of drying units 400 is 55 m / min, and the exhaust power of the drying unit 400 is set to 95%.

[0088] Example 2:

[0089] (1) Formation of fiber mesh layer 600 by flash spinning method:

[0090] A spinning solution is prepared using polymeric compounds as raw materials: 15% mass concentration polyethylene is sliced ​​and added to a high-pressure reactor together with an 85% mass concentration solvent (a mixture of 15% difluorochloromethane (R22) and 85% tetrafluorodichloroethane (R114)), and the temperature is raised to 180°C. After the temperature is raised, nitrogen gas is introduced to pressurize to 12 MPa while raising the temperature to 230°C, and stirring is performed for 2 hours at a stirring speed of 100 r / min. After the temperature is stabilized, a uniform spinning solution is formed in the high-pressure reactor.

[0091] The preferred embodiment of the new antibacterial breathable fabric 700 manufacturing equipment shown in Figure 2-5 is used to process the spinning solution, i.e., the spinning solution is flash-spun in the flash spinning unit 100 to form a 40g fiber mesh layer 600. Here, the spinning solution is sprayed from the nozzle head 11, and the speed of the spray air is 12000m / min. The spinning solution evaporates quickly, the polymer cools and solidifies into fiber bundles, and the fiber bundles sink into the moving mesh curtain 14, and the fibers aggregate into a mesh (i.e., fiber mesh layer 600), and the forward speed of the moving mesh curtain 14 is 80m / min.

[0092] (2) The fiber mesh layer 600 is subjected to a cold pressing process before the surface hot rolling process. The fiber mesh layer 600 is pressed by a cold pressing member 15 (cold pressing roller), which is a hollow stainless steel roller.

[0093] (3) Surface hot rolling treatment:

[0094] The obtained web layer 600 is introduced into the surface hot rolling unit 200 and subjected to a surface hot rolling process, whereby the fibers on one surface (upper surface) are thermally fused to form a dense fiber layer.

[0095] Here, the hot rolling temperature (the temperature of the hot rolling member 211 in the rotary heating member 21) is 135°C, and the rotation speed of the hot rolling member 211 is 83m / min. The flexible belt 221 adopts a high temperature resistant blanket. The tension of the flexible belt 211 is controlled to 1.1±0.1MPa.

[0096] (4) Spunlace processing:

[0097] The surface hot-rolled fiber mesh layer 600 is introduced into the spunlace bonding unit 300, which processes the other side (i.e., the bottom side) to form a dense material with different characteristics on both sides, i.e., a spunlaced nonwoven fabric.

[0098] Here, the water spouting pressure of the pre-wetting spunlace head 32 is 25 bar, the water spouting pressure of the main spunlace head 32 is 60 bar, the water spouting pressure of the surface finishing spunlace head 32 is 42 bar, and the speed of the spunlace drum 31 is 85 m / min.

[0099] (5) The nonwoven fabric after spunlace is introduced into the drying unit 400 for drying / dehydration and low-temperature drying to obtain an antibacterial and breathable fabric.

[0100] Here, the drying temperature in the drying unit 400 is 102° C., the number of drying units 400 is 86 m / min, and the exhaust power of the drying unit 400 is set to 95%.

[0101] Example 3:

[0102] (1) Formation of fiber mesh layer 600 by flash spinning method:

[0103] A spinning solution is prepared using polymeric compounds as raw materials: 15% mass concentration polyethylene is sliced ​​and added to a high-pressure reactor together with an 85% mass concentration solvent (a mixture of 15% difluorochloromethane (R22) and 85% tetrafluorodichloroethane (R114)), and the temperature is raised to 180°C. After the temperature is raised, nitrogen gas is introduced to pressurize to 12 MPa while raising the temperature to 230°C, and stirring is performed for 2 hours at a stirring speed of 100 r / min. After the temperature is stabilized, a uniform spinning solution is formed in the high-pressure reactor.

[0104] A preferred embodiment of the novel antimicrobial breathable fabric 700 manufacturing apparatus shown in FIG. 2-5 is used to process the spinning solution, i.e., the spinning solution is flash spun in a flash spinning unit 100 to form a 40 gram fiber mesh layer 600.

[0105] Here, the spinning solution is sprayed from the nozzle head 11, and the speed of the sprayed airflow is 12000 m / min. The spinning solution evaporates quickly, the polymer cools and solidifies to form a fiber bundle, and the fiber bundle sinks onto the moving mesh curtain 14, where the fibers aggregate to form a mesh. The forward speed of the moving mesh curtain 14 is 36 m / min.

[0106] (2) The fiber mesh layer 600 is subjected to a cold pressing process before the surface hot rolling process. The fiber mesh layer 600 is pressed by a cold pressing member 15 (cold pressing roller), which is a hollow stainless steel roller.

[0107] (3) Surface hot rolling treatment:

[0108] The obtained web layer 600 is introduced into the surface hot rolling unit 200 and subjected to a surface hot rolling process, whereby the fibers on one surface (upper surface) are thermally fused to form a dense fiber layer.

[0109] Here, the hot rolling temperature (the temperature of the hot rolling member 211 in the rotary heating member 21) is 145°C, and the rotation speed of the hot rolling member 211 is 37m / min. The flexible belt 221 adopts a high temperature resistant blanket. The tension of the flexible belt 211 is controlled to 2.6±0.2MPa.

[0110] (4) Spunlace processing:

[0111] The surface hot-rolled fiber mesh layer 600 is introduced into the spunlace bonding unit 300, which processes the other side (i.e., the bottom side) to form a dense material with different characteristics on both sides, i.e., a spunlaced nonwoven fabric.

[0112] Here, the water spouting pressure of the pre-wetting spunlace head 32 is 25 bar, the water spouting pressure of the main spunlace head 32 is 100 bar, the water spouting pressure of the spunlace head 32 for surface finishing is 55 bar, and the speed of the spunlace drum 31 is 38 m / min.

[0113] (5) The nonwoven fabric after spunlace is introduced into the drying unit 400 for drying / dehydration and low-temperature drying to obtain an antibacterial and breathable fabric.

[0114] Here, the drying temperature in the drying unit 400 is 108° C., the number of drying units 400 is 38 m / min, and the exhaust power of the drying unit 400 is set to 95%.

[0115] Comparative Example 1

[0116] (1) Using the same spinning solution as in Example 1, a 65 gram fiber mesh layer 600 is formed by flash spinning. The manufacturing process and manufacturing method of the fiber mesh layer 600 are the same as those of Example 1.

[0117] (2) The resulting fiber mesh layer 600 is subjected to conventional flash paper post-processing techniques by directly hot rolling the fiber mesh layer 600 with stainless steel rollers to form a dense, stiff, paper-like nonwoven fabric with the fibers thermally bonded on both sides.

[0118] Here, the hot rolling process of the stainless steel roller is as follows: hot rolling temperature is 150° C., pressing pressure is 3.0 MPa, and rotation speed is 55 m / min.

[0119] (3) The fiber mesh layer 600 is treated after hot rolling in the process described in Patent CN110528216A "System and process for softening high density polyethylene paper using the flash method" to obtain a soft material.

[0120] In addition, in the embodiment, the novel antibacterial breathable fabric 700 is manufactured using a manufacturing device as shown in the preferred embodiment in Figure 2-5. Specifically, the manufacturing method of the novel antibacterial breathable fabric 700 in the embodiment adopts a set of a flash spinning unit 100, a set of a surface hot rolling unit 200, and a set of a spunlace fixing unit 300, and the spunlace fixing unit 300 uses a combination of one drum 31 and three spunlace heads 32. Here, along the moving direction of the fiber mesh layer 600, the three spunlace heads 32 are in the order of the pre-wetting spunlace head 32, the main spunlace head 32, and the spunlace head 32 with surface arrangement function.

[0121] The finished products produced in the examples and comparative examples were subjected to relevant performance index tests, and the test results are shown in Table 1 below.

[0122] [Table 1]

[0123] In Table 1, the degree of drape refers to the degree to which the free boundary of the fabric sags under the action of its own weight, and is expressed as the drape coefficient F, i.e., the ratio of the projected area of ​​the sagging part of the sample to its original area. The smaller the percentage of the drape coefficient F, the better the degree of drape of the fabric and the better the flexibility of the fabric. The higher the level of synthetic blood permeability, the better.

[0124] In Table 1, the test standards or test methods for each performance are as follows: Basis weight test refers to national standard GB / T24218.1-2009; Thickness test refers to national standard GB / T24218.2-2009; Air permeability test refers to national standard GB / T5453-1997; Moisture permeability test refers to national standard GB / T12704-1991; Breaking strength test refers to national standard GB / T24218.3-2010; Tear strength test refers to national standard GB / T3917.3-2009; Peel strength test refers to standard ASTM D2724; Hydrostatic pressure test refers to national standard GB / T4744-1997; Anti-synthetic blood permeability test refers to national standard GB19082-2009.

[0125] Figure 6 is a schematic structural diagram of the new antibacterial breathable fabric 700 produced by the present invention, which has a first side 71 and a second side 72. The finished fabric produced by the present invention is directly spun from flash spinning, and is not composite. The first side 71 and the second side 72 in Table 1 and Figure 6 are only to show that the two sides of the material have different characteristics. Among them, the first side 71 is the antibacterial side (the top side mentioned above), and the second side 72 is the spunlace surface layer (the bottom side mentioned above), which is the side that contacts the skin of the body when used.

[0126] The results of the examples and comparative examples are analyzed.

[0127] As is clear from Figures 7-8, in the finished fabric produced in Example 1, the micrograph of the first side 71 of the finished fabric in Figure 7 shows that the surface fibers are completely bonded, the surface is dense, and there are micropores between the fibers. The micrograph of the second side 72 of the finished fabric in Figure 8 shows that the surface fibers are not bonded, and there are many micropores between the fibers. In addition, by combining the contents of Table 1, it can be seen that the antibacterial and breathable fabrics produced in Examples 1 to 3 have good mechanical strength, good drape and good flexibility, good breathability, good wearing comfort, and can maintain the waterproof and antibacterial properties of the thermal bonding surface, which meets the use needs of the fabric. In other words, the produced products have the two characteristics of high strength and high waterproof and antibacterial properties of flash method nonwoven fabrics, and excellent wearing comfort.

[0128] The manufacturing method of the present invention can realize disposable processing of nonwoven finished products, and can give the finished products two characteristics without compounding or bonding materials from multiple different processes or adding a separate softening process: the finished products have soft wearing comfort and excellent waterproof and antibacterial properties, while at the same time maintaining the mechanical strength of the material, which can extend the life of the material.

[0129] In Comparative Example 1, not only was the flexibility reduced compared to Example 1, but the usability of the finished product was also reduced, and the breathability, mechanical strength, and water-blocking performance were also significantly reduced, making it difficult to achieve both comfortable wearability and excellent waterproof and antibacterial properties, as in the product manufactured according to the present invention. Also, in Comparative Example 1, the processing process for the finished fabric product involves many steps, making the technology complicated.

[0130] From the above, the present invention has the following beneficial effects.

[0131] According to the manufacturing method of the new antibacterial breathable fabric 700 provided in the present invention, the antibacterial breathable fabric can be processed and shaped in one go, and the finished product can have two characteristics of excellent waterproof and antibacterial properties and good wearing comfort without the need for compounding or bonding materials from multiple different processes or adding processes such as softening treatment, and the finished nonwoven fabric can maintain good mechanical properties to extend its life and meet its usage requirements.

[0132] The finished fabric produced by the present invention is itself formed by direct spinning using flash spinning, and is not a composite. Here, the finished fabric produced has a first side 71 and a second side 72, the first side 71 being an antibacterial side, and the second side 72 being a spunlace surface layer (i.e., the side that comes into contact with the skin of the body during use). The finished fabric can achieve the following performance: its basis weight is 30-90 grams, its thickness is 0.1mm-0.5mm, its air permeability is 5-50mm / s, and its moisture permeability is 2500g / (m 2 d) or more, the transverse and longitudinal breaking strength is 150N / 5cm or more, the tear strength is 8N or more (tear strength in the transverse and longitudinal directions are both 8N or more), the peel strength is 3N or more, and the drape coefficient is less than 50%. At the same time, the moisture permeability of the first surface 71 reaches 5-20kPa, and the synthetic blood permeability is greater than level 2.

[0133] What needs to be explained is the following:

[0134] In the text, "grammage" refers to the weight per unit area (m 2 ) refers to the weight of material per unit.

[0135] In this document, "~" is used to represent a range of values, with both endpoints included within the range.

[0136] In the examples and comparative examples, the polymer solute used in the spinning solution is polyethylene. Based on the above design concept, the polymer may be a single existing polyolefin or a composition of multiple existing polyolefins, for example, a conventional flash spinning polymer such as linear high density polyethylene, linear polyethylene, low density polyethylene, polypropylene, etc., including but not limited to the polyethylene provided in the examples.

[0137] In addition, in the actual control, those skilled in the art will adjust the process parameters of the surface hot rolling treatment and spunlace processing treatment steps based on the applicability of the basis weight of the fiber mesh layer 600 to ensure the product performance. Specifically, the specific process parameters are determined by the material and basis weight of the product. The high and low melting point and basis weight changes of the material of the fiber mesh layer 600 need to adjust the process parameters to achieve the desired product effect. When the melting point of the material is high, the hot rolling temperature of the surface hot rolling treatment needs to be increased accordingly to achieve the desired hot bonding effect. When the basis weight of the material of the fiber mesh layer 600 increases, the number of fibers that need to be thermally bonded increases, and the hot rolling temperature and the tension of the flexible belt 221 in the surface hot rolling treatment need to be increased. As the basis weight of the material increases, the number of fibers required for spunlacing also increases, and the pressure of the main spunlace head head 32 needs to be increased.

[0138] It should be noted that those skilled in the art will understand that although there are many problems in the prior art, each embodiment or technical scheme of the present invention can only improve in one or more aspects without simultaneously solving all of the technical problems described in the prior art or background art. Those skilled in the art should understand that the contents not described in the claims should not be considered as limitations on the claims.

[0139] Here, many terms such as surface hot rolling, spunlace processing, and cold pressing are used, but the possibility of using other terms is not excluded. These terms are used only to more simply describe and explain the essence of the present invention. It is contrary to the spirit of the present invention to interpret them as any additional restrictions. Terms such as "first", "second" and the like (if any) in the description of the embodiments of the present invention and the claims and the above drawings are used to distinguish similar objects and are not necessarily used to describe a specific order or priority.

[0140] Finally, the above examples are for illustrating the technical scheme of the present invention, and are not intended to limit it. The present invention is described in detail with reference to the above examples, but those skilled in the art will understand that modifications of the technical scheme described in the above examples, or equivalent replacement of part or all of the technical features thereof, can be made. These modifications or replacements do not deviate from the essence of the corresponding technical scheme from the scope of the technical scheme of each embodiment of the present invention.

[0141] It should be noted that those skilled in the art will understand that although there are many problems in the prior art, each embodiment or technical scheme of the present invention can only improve in one or more aspects without simultaneously solving all of the technical problems described in the prior art or background art. Those skilled in the art should understand that the contents not described in the claims should not be considered as limitations on the claims. [Explanation of symbols]

[0142] 100 Flash Spinning Unit 200 Surface hot rolling unit 300 Spunlace Fixing Unit 400 Drying Unit 500 Winding unit 600 fiber mesh layer 11 Nozzle head 12 Rotating splitter plate 13 Air Amplifier 14 Mobile Mesh Curtain 15 Cold press parts 16 First vacuum suction device 111 Spinneret 21 Rotating heating element 22 Conveyor belt components 211 Hot-rolled parts 212 Transmission 221 Flexible Belt 222 Support member 223 Tension adjustment device 2224 Fourth support member 2221 First support member 2222 Second support member 2223 Third support member 31 Drums 32 Spunlace Head 33 Second vacuum suction device 34 Guide roller 700 New antibacterial breathable fabric 71 Front page 72 Second side

Claims

1. A method for producing a new antibacterial breathable fabric, comprising: Surface hot rolling treatment: performing surface hot rolling treatment on the fiber mesh layer to produce a fiber mesh layer in which the fibers on the upper surface are thermally bonded and the fibers on the lower surface are fluffy; Spunlace processing: performing a spunlace processing on the lower surface of the fiber mesh layer obtained by the surface hot rolling treatment; The surface hot rolling process is carried out using a surface hot rolling unit having a rotating heating member, a flexible belt, and at least two rotatable support members; the flexible belt being a closed loop made of a high temperature resistant flexible material; the flexible belt is disposed such that a front surface of the flexible belt contacts the rotary heating member and a back surface of the flexible belt is supported by the at least two support members; The fiber mesh layer subjected to the surface hot rolling treatment is supported on the lower surface by the flexible belt and hot-rolled on the upper surface by contacting the rotating heating member. This is a new method for manufacturing an antibacterial, breathable fabric.

2. The manufacturing method of the novel antibacterial breathable fabric as claimed in claim 1, characterized in that the fiber mesh layer is subjected to a cold pressing treatment before the surface hot rolling treatment.

3. A drying process is also included. The method for producing the new antibacterial and breathable fabric described in claim 1, characterized in that in the drying process, the nonwoven fabric after the spunlace processing is dried to remove moisture from the nonwoven fabric, thereby obtaining a new antibacterial and breathable fabric.

4. The manufacturing method of the novel antibacterial breathable fabric as claimed in claim 3, characterized in that in the drying process, the drying temperature is lower than the melting point of the fiber mesh layer.

5. The manufacturing method of the new antibacterial breathable fabric as claimed in claim 1, characterized in that the flexible belt is made of high temperature resistant blanket.