Abstract

The present invention relates to methods, catalysts and materials for the low or zero carbon conversion of renewable electricity, air and water into fuels and chemicals by directly capturing carbon dioxide from the atmosphere and converting the carbon dioxide into fuels and chemicals using hydrogen produced by electrolysis of water.

Description

[Technical field]

[0001] The present invention relates to methods, catalysts and materials for low or zero carbon conversion of renewable electricity, air and water into fuels and chemicals by directly capturing carbon dioxide from the atmosphere and converting the carbon dioxide into fuels and chemicals using hydrogen produced by electrolysis of water. [Background technology]

[0002] Carbon dioxide is produced by many industrial and biological processes. Carbon dioxide is usually emitted into the atmosphere, and since the beginning of the Industrial Revolution, the carbon dioxide concentration in the Earth's atmosphere has been increasing. Carbon dioxide is recognized as a significant greenhouse gas that contributes to global climate change. In particular, reducing carbon dioxide at its source is difficult and generally unsuccessful. Carbon dioxide in the atmosphere continues to increase. A more preferable process to deal with carbon dioxide is to efficiently capture it from the atmospheric air and convert it into useful products that can replace fuels and chemicals produced from fossil resources, such as petroleum and natural gas, such as fuels (diesel fuel, kerosene, jet fuel, gasoline or gasoline blends, or other fuels) and chemicals (methanol, ammonia, solvents, wax, olefins, or other chemicals), resulting in low total net emissions of carbon dioxide into the atmosphere. This is what is meant by low carbon, ultra-low carbon, or zero carbon fuels and chemicals.

[0003] Carbon dioxide can be obtained from several sources. Industrial manufacturing plants that produce ammonia for fertilizer from natural gas or coal produce large amounts of carbon dioxide. Ethanol plants that convert corn or wheat into ethanol produce large amounts of carbon dioxide. Power plants that generate electricity from natural gas or coal produce large amounts of carbon dioxide. Natural gas deposits can also contain large amounts of carbon dioxide, so in some locations, natural gas processing plants must process much larger amounts of carbon dioxide. Capturing and utilizing CO2 often requires the separation of carbon dioxide from a flue gas stream or another stream where carbon dioxide is not the predominant component. Alkylamines are used to remove carbon dioxide from the flue gas steam. Alkylamines used in this process include monoethanolamine, diethanolamine, methyldiethanolamine, diisopropylamine, aminoethoxyethanol, or combinations thereof. Metal Organic Framework (MOF) materials have also been used as a means to separate and capture carbon dioxide from low concentration streams using chemisorption or physisorption. Other processes for obtaining high concentrations of carbon dioxide include chemical looping combustion, in which the carbon dioxide produced during the combustion process is captured in a circulating metal oxide material.

[0004] Carbon dioxide can also be captured from the atmosphere, called direct air capture (DAC). The challenge of capturing carbon dioxide from air is different than capturing it from exhaust gases or other sources, because the carbon dioxide concentration in air is fairly low, about 415 ppm. At such low concentrations, liquid alkylamines do not work well because the amine losses are often too high. MOF compounds are based on physical absorption of carbon dioxide and usually have too low uptake of carbon dioxide. The publication Sanz-Perez, et al, "Direct Capture of CO2 from Ambient Air", Chem. Rev. 2016, 116, 11840-11876 details the historical development of direct air capture of CO2. Numerous materials have been tried to capture carbon dioxide from low concentration air streams.

[0005] Two main types of materials and processes have developed as the most promising in the past decade. The first set of promising materials and processes is the use of amine-tethered solid sorbents. This takes advantage of the CO2 capture capabilities of amines (similar to the liquid amines mentioned above), but these types of materials are chemically tethered to a solid. Unlike the metal oxide-based chemical sorbents mentioned above, supported amine sorbents can operate in near-ambient conditions and ideally can be regenerated with a gentle temperature change. Choi et al, "Application of Amine-Tethered Solid Sorbents forDirect CO2Capture from Ambient Air", Environmental Science& Technology, 2011, 45, 2420-2427, describes these materials in detail. However, these chemical sorbents require a temperature change to release the carbon dioxide and an inert gas to flush it away. In the laboratory, nitrogen or argon or other inert gases are used. Commercially, however, separation of the inert gas from the carbon dioxide is almost as important a problem as the initial capture of the carbon dioxide. To overcome this inert gas problem, it has been shown that some of these supported adsorbents can be regenerated using water steam to release carbon dioxide. See Wen Li, et.Al "Steam Stripping for Regeneration of Supported Amine-Based CO2 Adsorbents", ChemSusChem 2010, 3, 899-903. The technology developed by Global Thermostat, as described in US9,555,365, falls into this general approach for DAC.

[0006] The second material and process uses aqueous metal hydroxides to react with CO2 from air to produce metal carbonates, which are then calcined to release the captured CO2 and make the metal hydroxides again. This cycle can be done in a series of continuous chemical reactors. This technology is developed by Carbon Engineering. Their process is described in detail in Keithet al, "A Process for the Capture of CO2 from theAtmosphere", Joule 2, 1573-1594, August 15, 2018. The resulting carbon dioxide from their process is cooled from 900°C and compressed to more than 100 atmospheres and either geologically sequestered or sent to a CO2 pipeline. Renewable hydrogen (H2) sources can be produced from water by electrolysis.

[0007] [ka]

[0008] The reaction uses electricity to split water into hydrogen and oxygen. An electrolyser consists of an anode and a cathode separated by an electrolyte. Electrolysers function differently in slightly different ways, mainly due to the type of electrolyte material required.

[0009] However, each electrolysis technology has a theoretical minimum electrical energy input of 39.4 kWh / kgH2 (HHV of hydrogen) when water is fed to the system at normal pressure and temperature and all energy input is provided in the form of electricity. If adequate thermal energy is provided to the system, the required electrical energy input can be less than 39.4 kWh / kgH2. High temperature electrolysis, for example PEM steam electrolysis and especially solid oxide electrolysis, can have lower operating costs than an all-electric energy supply if the electrolyzer is co-located with a low-cost heat source or waste heat source. (Study on development of water electrolysis in the EU Final Report, E4tech Sari with Element Energy Ltd for the Fuel Cells and Hydrogen JointUndertaking, February 2014). Given the high energy required for electrolysis, the location of zero carbon fuel and chemical plants envisaged by the present invention needs to be located at or near cheap renewable electricity.

[0010] Besides electrolysis, current significant research is investigating the use of light energy and photocatalysis to split water into hydrogen and oxygen (Acar et al, Int. J. Energy Res. 2016; 40: 1449-1473).

[0011] Recent developments in Liquid Organic Hydrogen Carriers (LOHCs) indicate that it may be possible to react hydrogen with toluene at the site of electrolysis or water splitting to produce methylcyclohexane, which could then be transported as a liquid to another site for dehydrogenation, and the liquid toluene returned to the original site to continue the cycle. See Niermann et al, “Liquid Organic Hydrogen Carries (LOHC's) - Techno-Economic Analysis of LOHC's in a Defined Process Scheme”, EnergyEnviron. Sci. 2019, 12, 290. This development means that it may be possible to separate the site of electrolysis from the ultimate user of the renewable hydrogen.

[0012] One of the reactions that has been considered for the utilization of carbon dioxide is the reverse water gas shift (RWGS) reaction.

[0013] [ka]

[0014] This reaction converts carbon dioxide and hydrogen into carbon monoxide and water. The reaction is endothermic at room temperature and requires heat to proceed, and requires elevated temperatures and a good catalyst to convert carbon dioxide significantly.

[0015] Several catalysts have been disclosed for the RWGS reaction. The main catalysts previously investigated were Cu or Pt or Rh dispersed on metal oxide supports. (Daza & Kuhn, RSC Adv. 2016, 6, 49675-49691).

[0016] With CO (carbon monoxide) from the RWGS reaction and hydrogen from the electrolysis of water, it is possible to obtain useful products via catalytic hydrogenation of carbon monoxide to hydrocarbons. The mixture of H2 and CO is called synthesis gas or syngas. Syngas can be used as a feedstock to produce chemical products, including liquid fuels, alcohols, acetic acid, dimethyl ether, and many other chemical products. If we can produce H2 from water and CO from CO2, then we can have truly net zero carbon fuels and chemicals, with no CO2 or greenhouse gas emissions generated in the production of syngas and in the conversion of syngas to fuels and chemicals.

[0017] Catalytic hydrogenation of CO to produce heavier hydrocarbons (C) from methane in addition to oxygenated hydrocarbons. 100 The production of light gases, liquids and waxes from crude oils (up to 250°C or higher) is commonly referred to as Fischer-Tropsch (or FT) synthesis. In conventional low-temperature (<250°C) FT processes, the production of mainly high weight (or high wt%) FT waxes (C 25 These FT waxes are then hydrocracked and / or further processed to produce diesel, naphtha and other fractions. Light hydrocarbons are also produced during the hydrocracking process and may require further upgrading to produce usable products. The catalysts commonly used for FT are either cobalt (Co) or iron (Fe) based catalysts, which are also active in the water gas shift (WGS) reaction resulting in the conversion of the feed carbon monoxide to carbon dioxide. For more details on the state of the art of Fischer-Tropsch see (SS Ail, S. Dasappa / Renewable and Sustainable Energy Reviews 58(2016) 267-286). Summary of the Invention [Problem to be solved by the invention]

[0018] Despite the large amount of prior research on the subject and the global importance of successfully developing these technologies, successful methods, systems and catalysts have not been developed to date to capture atmospheric carbon dioxide and convert it into useful fuels and chemicals. Better methods, systems and catalysts are needed. [Means for solving the problem]

[0019] The present invention relates to methods, catalysts and materials for low or zero carbon conversion of renewable electricity, air and water into fuels and chemicals by capturing carbon dioxide directly from the atmosphere and converting it into fuels and chemicals using hydrogen produced by electrolysis of water. In this method, water is converted into hydrogen in an efficient electrolysis unit using renewable electricity as the energy source and, if necessary, the hydrogen is transported to a direct air capture (DAC) point via a LOHC system. The hydrogen is used in a beneficial way to improve the efficiency of the DAC system. Carbon dioxide and hydrogen are reacted into carbon monoxide and water in a RWGS reactor where renewable electricity provides the heat of reaction. The catalyst used in the RWGS reactor is a novel solid solution catalyst. The carbon monoxide produced and additional hydrogen are reacted into fuels and chemicals in a liquid fuel production reactor using a novel catalyst that directly produces fuels and chemicals. The net products produced are hydrocarbons of 4 to 24 carbon atoms in length. Other products may be produced from the syngas including methanol, wax, ammonia, solvents, other fuels and chemicals. [Brief description of the drawings]

[0020] [Figure 1] FIG. 1 shows the overall process for producing fuels and chemicals from renewable electricity, water and air, which can take place at two separate locations.

[0021] [Diagram 2]FIG. 2 shows two cycles for direct air capture (DAC) of CO2 using amine-based solid chemical sorbents.

[0022] [Diagram 3] FIG. 3 shows direct air capture (DAC) of CO2 using metal hydroxides / metal carbonates.

[0023] [Figure 4] FIG. 4 shows the LOHC process, in which hydrogen gas produced at location 1 is transported to location 2.

[0024] 5 and 6 show an integrated, highly efficient process for converting carbon dioxide, water and renewable electricity into renewable fuels and chemicals.

[0025] [Diagram 5] FIG. 5 illustrates the operation of the reverse water gas shift system and supporting unit.

[0026] [Figure 6] Figure 6 shows a portion of an overall process flow diagram for converting H2 and CO2 to fuels and chemicals. Specifically, Figure 6 shows a liquid fuel production system that reacts CO and H2 to produce longer chain hydrocarbons that can be used as fuels or chemicals. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0027] The present invention includes several subsystems. Figure 1 shows the overall process of producing fuels and chemicals from air, water and renewable electricity. The overall process starts with (1) generating renewable hydrogen from renewable or low carbon electricity and water by electrolysis, (2) the renewable hydrogen can be stored and transported to a second location via a liquid organic hydrogen carrier (LOHC) system if necessary, (3) direct air capture (DAC) to capture carbon dioxide from the atmosphere, and hydrogen from the electrolysis step is used to improve the efficiency of the DAC process, (4) producing CO from CO2 in a RWGS system, (5) converting syngas to hydrocarbons in a Liquid Fuel Production (LFP) reactor system, and (6) converting light hydrocarbons (C1-C5) generated in the Liquid Fuel Production (LFP) reactor to hydrogen and carbon monoxide (syngas) in an autothermal reformer (ATR) section to be recycled back to the LFP reactor.

[0028] Another aspect of the invention is to use the tail gas in a direct air capture process to fire a calciner, which would ideally use oxygen from the electrolyzer to condense the CO2 from the calciner so that it can be recycled back into the RWGS process.

[0029] From Figure 1, an electrolysis system produces renewable hydrogen. Water is fed to the electrolysis system. Renewable electricity is used to power the electrolysis system. Hydrogen can be produced by electrolysis of water.

[0030] [ka]

[0031] An electrolyzer consists of an anode and a cathode separated by an electrolyte. Slightly different methods result in different functions of the electrolyzer. Various electrolyzer designs can use a variety of electrolysis techniques, including alkaline electrolysis, membrane electrolysis, and high temperature electrolysis. Alkaline electrolysis is preferred because it is commercially possible to operate at large scales, exceeding 1 MW. Various electrolytes can be used, including KOH and NaOH liquids, with or without activating compounds. Activating compounds can be added to the electrolyte to improve electrolyte stability. Most ionic activators for hydrogen evolution reactions consist of ethylenediamine-based metal chloride complexes and Na2Mo4 or Na2WO4. Various electrocatalysts can be used on the electrodes, including many different combinations of metals and oxides, such as Raney-nickel-aluminum, and can be enhanced by adding cobalt or molybdenum to the alloy.

[0032] Several transition metal combinations, such as Pt2Mo, Hf2Fe, and TiPt, have been used as cathode materials and have shown significantly higher electrocatalytic activity than state-of-the-art electrodes.

[0033] Some electrolysers are designed to operate at high pressures, e.g., 30-50 bar, to produce hydrogen and oxygen. Pressurized electrolysers are preferred because they eliminate the energy-intensive step of compressing the syngas. Water at the cathode combines with electrons from the external circuit to form hydrogen gas and negatively charged oxygen ions. The oxygen ions pass through a solid ceramic membrane and react at the anode to form oxygen gas and generate electrons for the external circuit. In this way, both hydrogen and oxygen gases are produced in the electrolyser. In one embodiment, multiple electrolysers are operated in parallel. No electrolyser operates with 100% energy efficiency, and energy usage is critical to the economic operation of the facility. It is desirable for the energy usage in the electrolyser to be less than 200 megawatt hours (MWh) / metric ton (MT) of H2 produced, preferably less than 120 MWh / MT of H2 produced, and more preferably less than 60 MWh / MT of H2 produced. For alkaline electrolyser embodiments, power usage will be greater than 39.4 MWh / H2MT produced, however for high temperature electrolyser embodiments, power usage could potentially be less than 39.4 MWh / H2MT produced if waste heat is used to heat the electrolyser above ambient temperature.

[0034] Several different direct air capture (DAC) technologies can be used in the present invention. A first embodiment of the DAC technology is based on solid amine-based sorbents. Figure 2 shows one embodiment of the present invention. A supported amine sorbent based on primary, secondary or tertiary amines is loaded into the DAC reactor. The amine sorbent can chemically adsorb carbon dioxide in the air passing through the DAC reactor. As a result, a carbon dioxide depleted air stream exits the DAC reactor. This occurs at approximately ambient temperature and pressure. A blower can be used to draw air through the reactor. The loading of the solid amine sorbent in the DAC reactor and sizing of the amine sorbent optimize the pressure drop through the DAC reactor.

[0035] There are at least three classes of solid supported amine sorbents that can be used. Class 1 sorbents consist of a polymeric or oxide support (typically silica) that is physically loaded with amines, including small molecules or small polymers. Class 2 sorbents are based on amine species covalently bonded to the surface of a solid support, for example, using organosilanes. For example, a Class 1 sorbent may be tetraethylenepantomine or diethanolamine impregnated onto MCM-41 silica. A typical Class 2 sorbent is MCM-41 grafted with triamines to enlarge the pores, which show good sorption at low partial pressures of carbon dioxide. Class 3 sorbents are amine-based solid sorbents described as hyperbranched aminosilica (HAS) materials that are synthesized by in situ ring-opening polymerization of aziridines off of a porous support. These sorbents typically have amine loadings of 2-10 mmol / g, pore sizes of 4-7 nm, and pore sizes of 40-600 m 2 The materials have a BET surface area of ​​0.01 to 0.8 cc / g and a pore volume of 0.1 to 0.8 cc / g. These materials work well with moist or dry air at atmospheric conditions, exhibiting a carbon dioxide adsorption of 0.5 to 4.0 mmol / g at a carbon dioxide concentration of about 400 ppm. Ideally, the DAC reactor is operated so that about 20 to 50% of the carbon dioxide in the air passing through it is removed. Removing more than 50% of the carbon dioxide is generally not preferred, as it significantly reduces the ability of the adsorbent to capture carbon dioxide. After the CO2 capture cycle is completed, the DAC reactor is switched to a regeneration cycle of the adsorbent to release CO2. In this cycle, the hydrogen produced in the electrolyzer is heated to about 90 to 120 °C by indirect heat exchange. As this hydrogen passes through the DAC reactor, the adsorbed carbon dioxide is released and mixed with the carbon dioxide gas. Typically, the amount of hydrogen gas used results in a hydrogen to carbon dioxide molar ratio of 2.0 and 3.0 mol / mol in the gas exiting the DAC reactor. This stream becomes the feed stream for the RWGS in Figure 5. This integration improves the efficiency of the DAC system in particular since no water vapor is required and no separation is required.

[0036] A second embodiment of the DAC technology is based on a different process chemistry. Figure 3 shows the embodiment. The process involves the recovery of carbon dioxide from air via the conversion of metal hydroxides to metal carbonates. Using a blower, air passes through an Air Contactor. The Air Contactor contacts the carbon dioxide carrying air with aqueous KOH. The KOH reacts with the carbon dioxide to produce aqueous K2CO3. The aqueous K2CO3 reacts with solid Ca(OH)2 in a pellet reactor. The K2CO3 is converted back to KOH and the Ca(OH)2 is converted to solid CaCO3. The calcium carbonate is fed to a calciner system, which converts the calcium carbonate to CaO. The calciner system is new as a circulating fluid bed and operates at over 50 psig. It is an oxygen blown circulating fluid bed system. Oxygen is used as the fluidizing gas with a superficial velocity between 0.25 and 2.5 m / s. Through a lance, natural gas or other combustible-containing gas is fed to the solid bed, where the oxygen reacts with the gas and the temperature is raised to 900 °C. This results in a conversion efficiency of CaCO3 to CaO + CO2 of over 90%. The solid CaO is separated from the gaseous CO2 in a cyclone system. The solid CaO is fed to a Slaker reactor, where it is converted to Ca(OH)2 and used in the pellet reactor. The hot CO2-containing gas is immediately mixed with the hydrogen produced in the electrolyzer. Typically, the amount of hydrogen gas mixed with the carbon dioxide results in a hydrogen to carbon dioxide molar ratio of 2.0 and 3.0 mol / mol in the gas leaving the DAC reactor system. This stream is the feed stream of the RWGS in Figure 5. This integration increases the efficiency of the DAC system, especially since no cooling or compression of the carbon dioxide is required. The heating requirements in this embodiment are also significantly reduced with respect to the feed of the RWGS since the mixed gases are already above 300°C.

[0037] FIG. 4 shows a LOHC system in one embodiment of the invention. It is possible for the electrolyzer and DAC system to be in the same physical location. However, it is possible that the DAC unit is at the source of the generated fuels and chemicals, while the electrolyzer may be in an area with abundant solar, wind or other renewable or low carbon resources that can be used to generate renewable electricity to produce hydrogen. In this case, the hydrogen produced in the electrolyzer needs to be transported to a second location. FIG. 4 shows how this can be achieved using a LOHC system. There are several different LOHC materials possible, but the most promising seems to be methylcyclohexane (MHC), which can be produced by reacting toluene with hydrogen. This is done in a hydrogenation reactor in FIG. 4. MHC is a liquid and can be easily transported to another location 2 from the electrolyzer location. The MHC can then be dehydrogenated at location 2 to produce hydrogen gas and toluene. The toluene is then sent back to location 1 to complete the cycle. The dehydrogenation is done in a catalytic reaction system. Numerous catalysts can be used, including S-Pt on alumina. The temperature of the dehydrogenation reaction is between 340-360°C with pressures between 1-30 bar. The MCH conversion is greater than 95% and the hydrogen yield is greater than 95%. The high temperature of the dehydrogenation reactor can be beneficially utilized in the metal hydroxide DAC process. The hydrogen produced in the dehydrogenation reactor is combined with the CO2 produced by the calciner, resulting in a gas stream with a temperature in excess of 400-500°C that can be used as an immediate feed (with some additional preheat) to the RWGS reaction system shown in Figure 5.

[0038] Figure 5 shows a RWGS system that produces CO from CO2. Zero carbon or very low carbon fuels and chemicals require that no fossil fuels are burned in the process of producing the fuels and chemicals. This means that heating the feed to the integrated process needs to be by indirect means (cross exchanger) or via electrical heating where the electricity comes from zero carbon or renewable sources such as wind, solar, geothermal or nuclear.

[0039] In Figure 5, hydrogen and carbon dioxide are in streams 1 and 2 forming a mixed gas (stream 3). The H2 / CO2 ratio is between 2.0-5.0 mol / mol, more preferably between 3.0-4.0 mol / mol. The mixed RWGS feed is heated to 900°F in unit 4 by indirect heat exchange. (482℃) It is important that this initial temperature increase be accomplished without using direct combustion of carbon-containing gases to provide the heat, as this would mean that CO2 is being produced, which would negate the effect of converting the CO2 into useful fuels and chemicals.

[0040] The RWGS feed gas, which contains mixed H2 and CO2, is heated at least partially to 1,400°F in a preheater outside the main reactor vessel. (760℃) A higher inlet temperature (stream 5) or preferably 1,500° F. (816℃) to a higher inlet temperature to produce a heated feed gas.

[0041] Figure 5 shows a gas turbine that uses electrical heating to raise the temperature of the feed gas to 1,400°F by indirect heat exchange. (760℃) to temperatures above 1,500°F (816℃) to temperatures above 1,600°F. (871℃)1 shows the preheater as unit 4 which raises the temperature of the feed gas to a temperature higher than that of the feed gas. There are many ways to achieve electrical heating of the feed gas. One way is by electrical heating in an electrically heated radiant furnace. In this embodiment, at least a portion of the feed gas passes through heating coils in the furnace. The heating coils are surrounded by radiant electric heating elements in the furnace. The radiant electric heating elements can be made from a number of materials. The heating elements may be nickel chromium alloys. The elements may be wound in strip or wire form or cast in a zigzag shape. The elements are supported by an insulated steel shell, typically using ceramic fiber for insulation. The radiant elements may be divided into multiple sections to control the pattern of heating. Multiple coils and multiple sections may be required to provide heat to the feed gas and generate the heated feed gas. Radiant furnaces require proper design of heating elements and fluid coils to ensure good view factors and good heat transfer. In another embodiment of the invention, the gas passes directly over the heating elements, whereby the gas is heated by convective heat transfer. It is desirable for the power usage by the radiant furnace to be as low as possible. The power usage by the radiant furnace is less than 0.5 MWh (megawatt-hour) of power / metric ton (MT) of CO2 in the feed gas, more preferably less than 0.40 MWh / MT of CO2, and even more preferably less than 0.20 MWh / MT of CO2.

[0042] The heated RWGS feed gas is then fed into the RWGS main reactor (unit 6). There are two possible embodiments of the RWGS main reactor. In a first embodiment, the RWGS main reactor is adiabatic or nearly adiabatic and designed to minimize heat loss, but no heat is added to the main reactor, and the temperature in the main reactor decreases from the inlet to the outlet of the reactor. In a second embodiment, the RWGS main reactor is designed similarly, but additional heat is added to the vessel to maintain an isothermal or nearly isothermal temperature distribution in the vessel. Heat may be added to the vessel by internal or external heaters or by other means.

[0043] The RWGS main reactor vessel (unit 6) is a reactor with a length greater than its diameter. The inlet of the main reactor vessel is smaller than the overall diameter of the vessel. The main reactor vessel is a steel vessel. The steel vessel is internally insulated to limit heat loss. Various insulation materials may be used to limit heat loss to the environment, including poured or castable refractory lining or insulating bricks (see Harbison-Walker Handbook of Refractory Practices, 2005, https: / / mha-net.org / docs / Harbison%20Walker%202005%20Handbook.pdf).

[0044] Inside the main reactor vessel is a bed of catalyst. The catalyst can be in the form of granules, pellets, spheres, trilobes, quadra-lobes, monoliths or any other designed shape to minimize the pressure drop across the reactor. Ideally, the shape and size of the catalyst particles are controlled to ensure that the pressure drop across the reactor is less than 50 pounds per square inch (psi) [345 kPa], more preferably less than 20 psi [138 kPaJ]. The size of the catalyst form can have a characteristic dimension between 1 mm and 10 mm. The catalyst particles can be as small as 40 mm or larger. 2 / g, and more preferably 80 m 2 / g, preferably with an internal surface area of ​​100 m 2 The structured material is a porous material with a surface area of ​​10 ...

[0045] The RWGS catalyst used in the present process is a versatile, high performance solid solution-based catalyst capable of efficiently carrying out the RWGS reaction. This robust solid solution catalyst has high thermal stability up to 1,100°C, does not form carbon (coking), and has good tolerance to contaminants that may be present in the captured CO2 stream.

[0046] The catalyst exhibits high activity at low metal concentrations (0.5-20 wt%) compared to other catalysts that require at least 30 wt% transition and other metal loadings. Moreover, no expensive precious metals are required to improve catalyst performance. The manufacturing process for the RWGS catalyst is also important in that it produces a catalyst that forms a unique solid solution phase, a bimetallic crystalline phase, that does not segregate the metal phase. This unique chemical structure improves resistance to coking compared to conventional metal supported catalysts. Resistance to poisons such as sulfur and ammonia is also improved. Furthermore, the catalyst exhibits improved catalytic activity at a low surface area compared to monometallic atomically segregated catalyst phases. The catalyst does not require alkali promotion to suppress carbon deposition. The conversion of CO2 to CO per pass in the RWGS main reactor is typically 60-90%, more preferably 70-90%. When an adiabatic reactor embodiment is used, the temperature in the RWGS main reactor decreases from the inlet to the outlet. The outlet temperature of the RWGS main reactor is 100°C higher than the inlet temperature of the main reactor. °F(56℃) ~200°F (111℃) and more preferably 105° C. lower than the inlet temperature of the main reactor. °F(58℃) ~160°F (89℃) The weight hourly space velocity (WHSV) for the RWGS, calculated by dividing the mass flow rate of the RWGS reactants (H2+CO2) per hour by the mass of catalyst in the bed of the RWGS main reactor, is between 1,000 hr -1 ~60,000hr -1 More preferably, it is between 5,000 hours -1 ~30,000hr -1 It is between.

[0047] The gas exiting the RWGS main reactor is the RWGS product gas (Stream 7). The RWGS product gas contains carbon monoxide (CO), hydrogen (H2), unreacted carbon dioxide (CO2), and water (H2O). In addition, the RWGS product gas may contain small amounts of methane (CH4) produced in the main reactor by side reactions.

[0048] At this point in the process, the product gas of the RWGS can be used in a variety of ways. It can be cooled, compressed, and used downstream to produce fuels and chemicals. The product gas of the RWGS can also be cooled, compressed (in unit 8), sent back to the preheater, and fed back to the main reactor.

[0049] As shown in units 9 and 10, the product gas of the RWGS may also be reheated in a second electric preheater and sent to a second reactor vessel for additional conversion of CO to CO. Unit 11 shows optional compression of the syngas before sending it to the synthesis step for liquid fuel production.

[0050] FIG. 6 shows a Liquid Fuel Production (LFP) reactor system. This is also known as the hydrocarbon synthesis step. The LFP reactor converts CO and H2 into long chain hydrocarbons that can be used as liquid fuels and chemicals. Syngas (stream 12) is combined with recycled syngas to produce the feed to the LFP reactor, stream 13, and optionally the product (stream 21) from the ATR (unit 19), described below. The combined gases fed to the LFP reactor are shown as stream 14. The feed to the LFP reactor includes H2 and CO. Ideally, the ratio of H2 to CO in this stream is between 1.9 and 2.2 mol / mol.

[0051] The LFP reactor (unit 15) is a multi-tubular fixed bed reactor system. Each tube of the LFP reactor can have a diameter between 13 mm and 26 mm. The length of the reactor tube is generally greater than 6 m, more preferably greater than 10 m. The LFP reactor is generally oriented vertically, such that the feed to the LFP reactor enters the top of the LFP reactor. However, in some circumstances the reactor can be oriented horizontally, and in situations where height is limited it may be advantageous to install the reactor at an incline.

[0052] The majority of the length of the LFP reactor tubes is filled with the LFP catalyst. The LFP catalyst may also be mixed with a diluent, such as silica or alumina, to aid in distributing the feed to the LFP reactor within the LFP reactor tubes. The chemical reactions that occur within the LFP reactor produce hydrocarbons with lengths between 4 and 24 carbons (C4-C 24 An LFP product gas is produced that includes LFP (hydrocarbon) products and water. It is important that the LFP reactor does not generate significant amounts of CO2. It is desirable that less than 2% of the CO in the feed to the LFP reactor is converted to CO2 in the LFP reactor. It is important that only limited amounts of carbon monoxide in the feed to the LFP reactor are also converted to hydrocarbons with carbon numbers greater than 24. It is preferred that less than 10% by weight of the hydrocarbon fraction of the LFP product have a carbon number greater than 24. More preferably, it is desirable that less than 4% by weight of the hydrocarbon fraction of the LFP product have a carbon number greater than 24.

[0053] As mentioned above, the Fischer-Tropsch (FT) process generally produces products in the wax range (C 24+ ), with a majority in the FT process having chain lengths of 1 to 100 carbon atoms. However, the LFP catalysts used in embodiments of this invention do not produce heavier hydrocarbons in the same yields as other catalysts used in conventional FT processes.

[0054] In some embodiments of the invention, the LFP catalyst has limited activity for conversion of CO to CO2 via the water gas shift reaction. In some embodiments of the invention, the water gas shift conversion of CO to CO2 is less than 5% of the CO in the feed. In some embodiments, the LFP catalyst comprises nickel as the active metal. In some embodiments, the LFP catalyst comprises cobalt as the active metal. In some embodiments, the LFP catalyst comprises cobalt and nickel as the active metals. The LFP catalyst is supported on a metal oxide support selected from the group of alumina, silica, titania, activated carbon, carbon nanotubes, zeolites, or other support materials or mixtures thereof, having sufficient size, shape, pore size, surface area, crush strength, effective pellet radius.

[0055] The catalyst can have lobed supports of various shapes, with either three, four or five lobes, with two or more lobes longer than the other two shorter lobes, and the longer lobes being symmetrical together. The distance from the mid-point of the support or from the mid-point of each lobe is called the effective pellet radius, and ranges from C4 to C5. 24 It is an important parameter for achieving the desired selectivity to hydrocarbons. The promoter of the LFP catalyst may include one of cerium, ruthenium, lanthanum, platinum, rhenium, gold, nickel or rhodium. The promoter of the LFP catalyst is less than 1 wt. % of the total catalyst, preferably less than 0.5 wt. %, and even more preferably less than 0.1 wt. %.

[0056] The LFP catalyst support has a pore size greater than 8 nanometers (nm), an average effective pellet radius less than 60 micrometers (μm), a crush strength greater than 3 lb / mm, and a particle size less than 125 m. 2 / g. After metal impregnation, the catalyst has a metal dispersion of about 4%. 24Several types of supports have been found to maximize the yield of hydrocarbons, including alumina, alumina / silica combinations, activated carbon, carbon nanotubes, and / or zeolite-based supports.

[0057] LFP fixed bed reactors are used for C4-C 24 Operate to maximize hydrocarbon yield.

[0058] Alternatively, the LFP fixed bed reactor uses a conventional FT catalyst that produces mostly wax. In one embodiment, the LFP reactor is operated at a pressure between 150 and 450 psi. The reactor is operated at 350° F. (177℃) to 460°F (238℃) and typically about 410° F. (210℃) The FT reaction is exothermic. The reactor tube bundle is placed into a heat exchanger where the reactor temperature is maintained inside the LFP reactor tubes by boiling steam on the outside of the LFP reactor tubes. Since the steam temperature is lower than the LFP reaction temperature, heat flows from the LFP reactor tubes to the cooler steam. The steam temperature is maintained by maintaining the steam pressure. The steam is generally saturated steam.

[0059] The conversion of CO in the LFP reactor is maintained at between 30 and 80 mole % CO conversion per pass. The CO can be recycled for additional conversion or sent downstream to additional LFP reactors. Carbon selectivity to CO2 is minimized to less than 4% of the converted CO, more preferably less than 1%. C4-C 24 The carbon selectivity to hydrocarbons is between 60 and 90%. The product gas of the LFP reactor is the desired C4-C 24 Hydrocarbons, as well as unreacted carbon monoxide, hydrogen, water, small amounts of C1-C5 hydrocarbons and small amounts of C 24+ The desired products are separated from the stream by distillation or other acceptable means. Carbon Selectivity is defined as:

[0060]

number

[0061] where n CO Converted is the molar flow rate of CO converted in the LFP reactor, and n i is the molar flow rate of hydrocarbon of carbon number i produced in the LFP reactor. Carbon selectivity to carbon dioxide is defined as:

[0062]

number

[0063] where n CO2 is the molar flow rate of CO2 produced in the LFP reactor, which is highly desirable for zero-carbon fuel and chemical production processes that start with carbon dioxide as a feedstock.

[0064] The product emerges from the bottom of the reactor. Heavy hydrocarbons (C 24+), which can be removed at the reactor outlet. If the LFP reactor is operated under suitable conditions with a catalyst, there will be very few heavy hydrocarbons. The main product of the LFP is stream 16, which is cooled and condensed in unit 17. Unreacted carbon monoxide, hydrogen, and C1-C5 hydrocarbons or tail gas (unit 18) are part of the feed to the auto-thermal reformer (ATR). Figure 6 also shows the auto-thermal reformer (ATR) (unit 19) portion of the process. In the auto-thermal reformer (ATR), the hydrocarbon feed to the ATR includes carbon monoxide, hydrogen, and C1-C5 hydrocarbons. Auto-thermal reforming of methane (C1)-based natural gas to carbon monoxide and hydrogen has been attempted commercially for many years. See K. Aasberg-Petersen et al. / Journal of Natural Gas Science and Engineering 3(2011) 423-459.

[0065] The ATR used in this invention is not necessarily conventional in that it is desired to produce a product that is rich in CO, with a ratio of H2 to CO produced between 1.9 and 2.2 mol / mol, and less than 10 mol% CO2 in the product gas. The oxidant feed to the ATR includes water vapor and O2, where the O2 is produced at least in part by electrolysis of H2O (stream 29). The oxidant feed to the ATR and the hydrocarbon feed to the ATR are preheated and then reacted in the ATR burner where the oxidant and hydrocarbons are partially oxidized at temperatures in the range of 950-1,050°C. The ATR reactor can be divided into three sections, the combustion section (or burner) completely combusting at least a portion of the hydrocarbon feed to the ATR to H2O and CO2.

[0066] In the thermal section, further conversion takes place through homogeneous gas-phase reactions. These reactions are slower than combustion reactions, such as the oxidation of CO, or pyrolysis reactions involving higher hydrocarbons. The main overall reaction in the thermal section is the homogeneous gas-phase steam reforming and shift reactions of hydrocarbons. In the catalytic section, the final conversion of hydrocarbons takes place through heterogeneous catalytic reactions, including steam reforming of methane and water-gas shift reactions. As a result, the ATR product gas has a composition close to the predicted thermodynamic equilibrium composition. The actual ATR product gas composition is the same as the thermodynamic equilibrium composition, with a difference of less than 70°C. This is the so-called equilibrium approach temperature.

[0067] To keep the amount of CO2 produced in the ATR to a minimum, the amount of water vapor in the oxidant feed to the ATR should be kept as low as possible while still resulting in an ATR product gas that is closer to the expected equilibrium composition and less soot. Typically, the ratio of total water vapor to carbon (mol / mol) in the combined (oxidant + hydrocarbon) feed to the ATR is desired to be between 0.4 and 1.0, and optimally about 0.6.

[0068] The ATR product leaves the ATR catalytic section at a temperature greater than 800° C. The ATR product is cooled to a lower temperature through a waste heat boiler (unit 22) where heat is transferred to generate steam that can be used to generate electricity, similar to the low pressure steam produced by the LFP reactor.

[0069] ATR catalysts suitable for the reaction in the catalytic zone are typically nickel-based. RWGS catalysts can be used as ATR catalysts. Other suitable ATR catalysts are nickel on alpha-alumina or magnesium alumina spinels (MgAl2O4) with or without precious metal promoters, including gold, platinum, rhenium, or ruthenium. Spinels have higher melting points, higher thermal strength, and stability than alumina-based catalysts.

[0070] The ATR product can be combined with the RWGS product and used as feed to the LFP reactor. This allows for a C4-C 24 This results in high utilization of the hydrocarbon products.

[0071] In some embodiments, the LFP product gas is not suitable as a direct feed to the ATR and must be pre-reformed. In these cases, the LFP product gas contains unreacted carbon monoxide, hydrogen, and C1-C5 hydrocarbons, and comprises the hydrocarbon feed gas to a pre-reformer. Typically, the higher hydrocarbons and carbon oxides in this stream require the use of a pre-reformer instead of being used directly as the hydrocarbon feed to the ATR. The pre-reformer is typically an adiabatic reactor. The adiabatic pre-reformer converts the higher hydrocarbons in the pre-reformer feed to a mixture of methane, steam, carbon oxides, and hydrogen, making them suitable as a subsequent hydrocarbon feed to the ATR. One advantage of using a pre-reformer is that the higher hydrocarbon feed to the ATR can be pre-heated, reducing the oxygen used in the ATR. As a result, the integrated process as described above can convert carbon dioxide into C4-C suitable for use as fuels or chemicals. 24 This results in high conversion to hydrocarbon products (Stream 24).

[0072] The present disclosure includes the following. (1) 1. An integrated process for converting a feed stream comprising air, electricity, and water into a product stream comprising a hydrocarbon, the process comprising: a. an electrolysis step for converting an electrolyzer feed stream comprising water into an electrolyzer product stream comprising hydrogen and oxygen, wherein at least a portion of the electricity used is from a renewable resource; b. direct air recovery by contacting the air with an adsorbent to remove carbon dioxide from the air stream; c. a reverse water gas shift step in which at least a portion of the hydrogen from the electrolyzer product stream is reacted with a carbon dioxide comprising stream from the direct air recovery step to produce a reverse water gas shift product stream comprising carbon monoxide; d. a hydrocarbon synthesis step of reacting at least a portion of the hydrogen from the electrolyzer product stream with a stream comprising at least a portion of the reverse water gas shift product stream to produce a hydrocarbon synthesis product stream; e. an autothermal reforming step in which at least a portion of the oxygen produced by electrolysis is reacted with one or more streams containing unreacted reactants from the hydrocarbon synthesis step; The method includes: (2) The method described in (1) above, wherein the direct air capture uses a solid supported amine adsorbent. (3) The process of claim 2, wherein the solid supported amine sorbent is regenerated using a hydrogen-containing stream produced in the electrolytic cell. (4) The method described in (1) above, wherein the direct air capture uses aqueous KOH to remove carbon dioxide from air. (5) The method described in (1) above, wherein the electrolyzer is at location 1, the direct air recovery is at location 2, and hydrogen from the electrolyzer is transported from location 1 to location 2 by means of LOHC. (6) The method of claim 1, wherein the reverse water gas shift reactor feed is heated to at least 1,500°F (816°C) in an electric radiant furnace, the reactor vessel is an adiabatic reactor, and the reactor outlet temperature is at least 100°F (56°C) lower than the reactor inlet temperature. (7) The feed to the reverse water gas shift reactor has a hydrogen to carbon dioxide molar ratio (H 2 (mol) / CO 2 (mol)) is 2.5 to 4.0. (8) The feedstock for the hydrocarbon synthesis has a hydrogen to carbon monoxide molar ratio between 1.90 and 2.20, 4 ~C 24 Selectivity is 70% or more, and C 24 2. The process of claim 1, wherein the amount of carbon monoxide converted to heavier products is less than 10%. (9) The method according to (1) above, wherein the autothermal reforming step includes steam as a feed, and the steam to carbon ratio is between 0.40 and 1.00. (10) The method according to (9) above, wherein the autothermal reforming (ATR) catalyst comprises a solid solution catalyst.

Claims

1. 1. An integrated process for converting a feed stream comprising air, electricity, and water into a product stream comprising a hydrocarbon, the process comprising: a. an electrolysis step for converting an electrolyzer feed stream comprising water into an electrolyzer product stream comprising hydrogen and oxygen, wherein at least a portion of the electricity used is from a renewable resource; b. direct air recovery, removing carbon dioxide from the air stream by contacting the air with an adsorbent; c. a reverse water gas shift step in which at least a portion of the hydrogen from the electrolyzer product stream is reacted with a carbon dioxide comprising stream from the direct air recovery step in a reverse water gas shift reactor to produce a reverse water gas shift product stream comprising carbon monoxide; d. A hydrocarbon synthesis step, reacting at least a portion of the hydrogen from the electrolyzer product stream with a stream comprising at least a portion of the reverse water gas shift product stream to produce a hydrocarbon synthesis product stream; e. an autothermal reforming step in which at least a portion of the oxygen produced by electrolysis is reacted with a stream or streams containing unreacted reactants from the hydrocarbon synthesis step; The feed to the reverse water gas shift reactor has a hydrogen to carbon dioxide molar ratio (H ２ (mol) / CO ２ (mol)) is 2.0 to 5.0 and the stream is heated to a temperature greater than 1,400° F. (760° C.).

2. 10. The method of claim 1, wherein the direct air capture uses a solid supported amine adsorbent.

3. 3. The method of claim 2, wherein a stream comprising hydrogen produced in the electrolytic cell is used to regenerate the solid supported amine sorbent.

4. 10. The method of claim 1, wherein the direct air capture uses aqueous KOH to remove carbon dioxide from the air.

5. 2. The method of claim 1, wherein the electrolyzer is at location 1 and the direct air recovery is at location 2, and hydrogen from the electrolyzer is transported from location 1 to location 2 by a LOHC process.

6. 2. The process of claim 1, wherein the reverse water gas shift reactor feed is heated in an electric radiant furnace to at least 1,500°F (816°C) as the reactor feed, the reactor vessel is an adiabatic reactor, and the reactor outlet temperature is at least 100°F (56°C) lower than the reactor inlet temperature.

7. The feed to the reverse water gas shift reactor has a molar ratio of hydrogen to carbon dioxide (H ２ (mol) / CO ２ 2. The method of claim 1, wherein the composition is such that (mol) is 2.5 to 4.

0.

8. 10. The method of claim 1, wherein the autothermal reforming step includes steam as a feed, and the steam to carbon ratio is between 0.40 and 1.

00.

9. 9. The method of claim 8, wherein the catalyst for the autothermal reforming step comprises a solid solution catalyst.