To provide a versatile welding electrode that enables multiple resistance weld joints and long seam lengths between metal sheets. A welding electrode for resistance welding is comprised of a welding tool at least partially made of a first metal. The welding tool has a contact surface 1 that comes into contact with a workpiece 9 to be welded. The contact surface 1 is made of diamond doped with boron and / or phosphorus.

Description

[Technical field]

[0001] The present invention relates to a welding electrode for resistance welding as defined in the preamble of claim 1. The present invention further relates to a method for using such a welding electrode. [Background technology]

[0002] For example, from JF Key, TH Courtney: Refractory Metal Composite Tips for Resistance-Spot Welding of Galvanized Steel, Welding Research Supplement, 261-266, 1974, a welding electrode for resistance welding, in particular for resistance spot welding, is known.

[0003] Welding electrodes for resistance spot welding usually comprise a cap as a welding tool, which can be inserted into the electrode holder of a resistance spot welding device. For roll seam welding, a disk is used as a welding tool. When producing a welded joint between steel sheets, such welding electrodes are made of, for example, sintered CuAl2O3-based alloys, sintered CuCr-based alloys, sintered CuCrZr-based alloys, etc.

[0004] In recent years, there has been a demand, particularly in the automotive industry, for the production of welded joints between aluminum sheets. Conventional welding electrodes tend to stick to the aluminum sheets being welded, particularly when producing spot welded joints. [Prior art documents] [Non-patent literature]

[0005] [Non-Patent Document 1] JF Key, TH Courtney: Refractory Metal Composite Tips for Resistance-Spot Welding of Galvanized Steel, Welding Research Supplement, 261-266, 1974 Summary of the Invention [Problem to be solved by the invention]

[0006] The object of the present invention is to overcome the disadvantages of the prior art, in particular to provide a versatile welding electrode that allows multiple resistance weld joints and long seam lengths between metal sheets. Another object of the present invention is to provide a method for using the welding electrode. [Means for solving the problem]

[0007] This problem is solved by the features of claims 1 and 14. The dependent claims give practical embodiments of the invention.

[0008] The present invention proposes a welding electrode for resistance welding, the contact surface of which is made of diamond doped with boron and / or phosphorus. By using the proposed welding electrode, it is surprisingly possible to produce more than 1,400 welded joints, in particular spot welded joints, between metal sheets, in particular between aluminum sheets, without adhesion. Specifically, as far as is known at present, when producing a spot welded joint between two aluminum sheets, it is believed that the diamond layer according to the present invention mechanically breaks through at least a part of the passivation layer of Al2O3 formed on the surface of the aluminum sheets, so that the diamond layer comes into direct contact with the metallic aluminum. As a result, it is possible to significantly reduce the contact resistance between the welding electrode and the aluminum sheet. This prevents the aluminum sheet from melting in the region of the contact surface of the welding electrode, thereby preventing adhesion to the welding electrode.

[0009] In an advantageous embodiment, the diamond is doped with 500-20,000 ppm of boron, preferably 2,000-10,000 ppm of boron. Additionally or alternatively, the diamond may be doped with 500-20,000 ppm of phosphorus, thereby allowing the resistance welding process to be performed at a current of 30 kA / cm. 2 This corresponds to a current density about 30 times higher than that of conventional resistance welding methods for sheet metal welding (current densities used in conventional methods are usually 1 kA / cm 2 The current densities used can be very high, making it possible to achieve resistance welded joints at high speeds, in particular without undesirable heating of large areas of the workpiece to be welded.

[0010] In a further advantageous embodiment, the diamond is produced as a diamond layer in a CVD process, in which the diamond layer is deposited in-situ from the gas phase on the welding electrode, and it has been found that the diamond layer produced in this way exhibits surprisingly good durability even under the extreme conditions of resistance welding.

[0011] Advantageously, the thickness of the diamond layer is 0.5-50 μm, preferably 1-10 μm. Advantageously, the surface roughness of the diamond layer is an average roughness depth Rz>1 μm. A diamond coating having these parameters is characterized by an improved life of the welding electrode.

[0012] In a further advantageous embodiment, more than 50% of the contact surface is composed of facets of diamond crystals, preferably co-grown diamond monocrystals, forming (111) or (001) planes. Advantageously, the growth area of ​​the diamond layer opposite to the contact surface is in contact with the intermediate layer on the cap side. In particular, the diamond monocrystal extends from the intermediate layer to the contact surface mainly in the

[0111] or

[0110] direction. That is, the diamond monocrystal extends from the intermediate layer to the contact surface with the grain boundaries mainly perpendicular to the contact surface. The diamond layer of the proposed structure is characterized by excellent electrical and thermal conductivity.

[0013] In a further advantageous embodiment, the intermediate layer is formed of a metal carbide and / or a metal nitride and / or a metal boride of the first metal, or a metal carbide and / or a metal nitride and / or a metal boride of a second metal different from the first metal. In particular, the first metal and / or the second metal form a carbide and / or a nitride and / or a boride that is stable up to a temperature of 800° C. The first metal and / or the second metal may in particular be composed of at least one of Cr, Ti, Nb, Mo, W and Ta. The intermediate layer may be formed directly in-situ in a CVD process or may be formed separately at a temperature between 600° C. and 1,050° C.

[0014] For example, the first metal may be W containing Cu as an alloy component. In this case, the intermediate layer may be formed directly in the CVD process for depositing the diamond layer. In this case, WC is formed as the intermediate layer. Also, for example, the first metal may be composed of W containing Fe as an alloy component. In this case, in the first CVD process, a TiN layer is deposited as an intermediate layer on the first metal. This layer may be doped with B. Next, in the second CVD process, the diamond layer is deposited on the intermediate layer.

[0015] Preferably, the first metal may contain Cu or Fe as an alloy component, or may contain Ag.

[0016] The welding tool may be partially formed of a third metal in addition to the first metal. The third metal may contain Cu as a main component. That is, the welding tool may have at least a part forming the contact surface formed of, for example, a W-based alloy, a Mo-based alloy, or the like. Alternatively, the welding tool may be made of another metal such as a Cu-based alloy. Such a welding tool can be manufactured relatively inexpensively.

[0017] The welding tool may be a cap which fits onto the electrode holder of a resistance spot welding device, but it may also be a disk of a roller seam welding device.

[0018] A further aspect of the invention proposes the use of a welding electrode according to the invention for producing a welded joint between workpieces made of a fourth metal having a passivation layer of a metal oxide.

[0019] The term "metal" in the sense of the present invention should be interpreted in a general way, i.e. it can also refer to alloys.

[0020] The "fourth metal" should be understood as a metal that spontaneously forms an oxide layer on its surface upon contact with air. Preferably, the fourth metal is selected from the group consisting of Al, Mg, Ni, Ti, Zn, Cr, Fe, Nb, Ta and Cu. Specifically, aluminum spontaneously forms a passivation layer of Al2O3 on its surface. Al2O3 exhibits electrical insulation and has a high hardness (Vickers hardness: about 2,000). The diamond layer provided on the welding electrode according to the present invention has a higher hardness, i.e., a Vickers hardness of 7,000 to 10,000. As a result, the welding electrode according to the present invention can break through a passivation layer formed on, for example, an aluminum plate, etc., so that a direct electrical contact is established between the diamond layer and the metallic conductive part below the passivation layer. As a result, the welding electrode according to the present invention can produce a welded joint without being deposited on the sheet metal to be welded. This effect also applies to other quaternary metals (e.g., Al, Mg, Ni, Ti, Zn, Cr, Fe, Nb, Ta, Cu, etc.) that form metal oxide passivation layers.

[0021] Advantageously, said weld joint is produced by resistance spot welding, however, by adapting the design of the welding electrode according to the invention, it is also conceivable to produce, for example, straight weld joints.

[0022] Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings. [Brief description of the drawings]

[0023] [Figure 1] FIG. [Diagram 2] 2 is a cross-sectional view of the welding cap taken along line AA' in FIG. 1; [Diagram 3] FIG. 2 is a bottom view of FIG. [Figure 4] 2 is a schematic cross-sectional view of a surface of a weld cap and a sheet metal to be welded; FIG. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0024] In figures 1 to 3 a welding electrode in the form of a cap or welding cap is shown. It has a contact surface 1 forming the free surface of a diamond layer 2. Reference number 3 denotes a part made, for example, of W, Mo or an alloy containing Mo or W as the main component. Reference number 4 denotes an intermediate layer. In this embodiment, the intermediate layer 4 is made substantially of WC or MoC. The intermediate layer 4 can be formed in-situ during the production of the diamond layer 2 by a CVD process.

[0025] Reference numeral 5 denotes a base of the weld cap. The base 5 may be made of a third metal different from the first metal forming the portion 3. A metal that is less expensive than the first metal used to form the portion 3 may be selected as the third metal for making the base 5. For example, the base 5 may be made of pure copper or a copper-based alloy (particularly a CuAl2O3-based alloy, a CuCr-based alloy or a CuCrZr-based alloy). Of course, the base 5 may be omitted and the cap may be made of the first metal forming the portion 3.

[0026] In a further embodiment, not shown, it is also possible to omit the part 3. The weld cap then consists, for example, of a copper-based alloy as is conventional. In this case, an intermediate layer 4 must be applied separately. The intermediate layer may be made of a carbide-forming metal. For example, the intermediate layer may contain Ti. The diamond layer 2 may then be deposited on such an intermediate layer 4 by a CVD process.

[0027] FIG. 4 shows a schematic diagram of a part 3 made of a W-based or Mo-based alloy. The alloy may have a grain boundary phase 6 at the grain boundaries (only a part of the grain boundaries is shown in the figure). The grain boundary phase 6 is composed of, for example, Fe, Ni, Co, or Cu. In the case of in-situ deposition, it is advantageous to superficially remove the grain boundary phase 6 by etching and / or particle blasting. This improves the bond strength between the diamond layer 2 and the intermediate layer 4.

[0028] The diamond crystals 7 extending from the intermediate layer 4 are more than 50% single crystal diamond. The facets of the diamond crystals 7, designated by reference numeral 8, consist of either (111) or (001) planes. Reference numeral P points to an arrow representing the direction of electric current in the diamond layer 2. The electric current flows parallel to the

[0111] direction and parallel to the

[0110] direction of the diamond crystals 7.

[0029] The contact surface 1 of the diamond layer 2 is formed by the entire facet 8. The contact surface 1 is provided facing a workpiece 9 to be welded, which is made of, for example, an aluminum-based alloy. The workpiece 9 has a metal oxide layer 10 on its surface.

[0030] Although not shown, the welding tool may be a disk instead of a cap. Such a disk is used in a roller seam welding device. In this case, the contact surface 1 is formed on the periphery of the disk. In the disk, the portion 3 and possibly also the base portion 5 are provided at the inner diameter side position in the same order as the cap shown in Figures 1 to 3.

[0031] To create a welded joint between the workpiece 9 and another workpiece (not shown), the diamond layer 2 is pressed against the metal oxide layer 10. 2 Within the range of 10 to 20 kA / cm 2 In this process, the workpiece 9 is welded to another workpiece (not shown) placed opposite and pressed against the workpiece 9 by an additional welding electrode (not shown) according to the invention.

[0032] The proposed welding electrode makes it possible to perform more than 1,000 spot welds, especially on aluminum plates, without any adhesion between the electrode and the aluminum plate. The present invention includes the following embodiments. [Aspect 1] A welding electrode for resistance welding, comprising a welding tool at least a portion of which is made of a first metal, the welding tool having a contact surface (1) that comes into contact with a workpiece (9) to be welded, 1. A welding electrode, characterized in that the contact surface (1) is made of diamond doped with boron and / or phosphorus. [Aspect 2] 2. The welding electrode according to claim 1, wherein the diamond is doped with 500 to 20,000 ppm of boron. [Aspect 3] 3. The welding electrode according to claim 1 or 2, wherein the diamond is prepared as a diamond layer (2) in a CVD process. [Aspect 4] The welding electrode according to any one of the first to third aspects, wherein the diamond layer (2) has a thickness of 0.5 to 50 μm, preferably 1 to 10 μm. [Aspect 5] 5. The welding electrode according to any one of the first to fourth aspects, wherein the diamond layer (2) has a surface roughness average roughness depth Rz>1 μm. [Aspect 6] 6. The welding electrode according to any one of the preceding claims, wherein more than 50% of the contact surface (1) is composed of facets forming a (111) or (001) plane of a diamond crystal, preferably a single diamond crystal. [Aspect 7] 7. The welding electrode according to any one of claims 1 to 6, wherein a growth region of the diamond layer (2) opposite the contact surface (1) is in contact with an intermediate layer (4). [Aspect 8] 8. The welding electrode according to any one of claims 1 to 7, wherein the diamond crystals (7) extend from the intermediate layer (4) to the contact surface (1) in a

[0111] or

[0110] direction. [Aspect 9] 9. The welding electrode according to any one of the preceding claims, wherein the intermediate layer (4) is formed of a carbide compound and / or a nitride compound and / or a boride compound of the first metal, or a carbide compound and / or a nitride compound and / or a boride compound of a second metal different from the first metal. [Aspect 10] 10. The welding electrode of any one of claims 1 to 9, wherein the first metal and / or the second metal form carbide and / or nitride and / or boride compounds that are stable up to temperatures of 800° C. [Aspect 11] 11. The welding electrode of any one of claims 1-10, wherein the first metal and / or the second metal is comprised of at least one of the elements Cr, Ti, Nb, Mo, W, and Ta. [Aspect 12] 12. The welding electrode of any one of claims 1-11, wherein a portion of the welding tool is formed from a third metal. [Aspect 13] 13. The welding electrode of any one of the preceding claims, wherein the third metal comprises Cu as a major component. [Aspect 14] 14. Use of the welding electrode according to any one of the preceding claims for producing a resistance welded joint between workpieces (9) made of a fourth metal having a metal oxide passivation layer (10). [Aspect 15] 15. The method of claim 14, wherein the resistance welded joint is made by resistance spot welding, resistance projection welding, or resistance seam welding. [Aspect 16] 16. The use according to any one of claims 14 to 15, wherein the fourth metal is selected from the group consisting of Al, Mg, Ni, Ti, Zn, Cr, Fe, Nb, Ta and Cu. [Explanation of symbols]

[0033] 1 Contact surface 2 Diamond layer 3 parts 4. Middle Tier 5 base 6 Grain boundary phase 7 Diamond Crystal 8. Facets 9 Work 10 Metal oxide layer P Arrow

Claims

1. A welding electrode for resistance welding, comprising a welding tool at least a portion of which is made of a first metal, the welding tool having a contact surface (1) that comes into contact with a workpiece (9) to be welded, the contact surface (1) being made of diamond doped with boron and / or phosphorus; The diamond is provided as a diamond layer (2), The thickness of the diamond layer (2) is 0.5 to 50 μm; The surface roughness of the diamond layer (2) is an average roughness depth Rz>1 μm; 1. A welding electrode, characterized in that more than 50% of said contact surface (1) is composed of facets forming the (111) or (001) planes of a diamond crystal.

2. 10. The welding electrode of claim 1, wherein the diamond is doped with 500 to 20,000 ppm of boron.

3. 3. The welding electrode according to claim 1 or 2, wherein the diamond layer (2) is a chemical vapour deposition (CVD) diamond layer (2).

4. 4. The welding electrode according to claim 1, wherein a growth area of ​​the diamond layer (2) opposite the contact surface (1) is in contact with an intermediate layer (4) located between the welding tool and the diamond layer (2).

5. 5. The welding electrode according to claim 4, wherein the diamond crystals (7) extend from the intermediate layer (4) to the contact surface (1) in a [111] or [110] direction.

6. 6. The welding electrode according to claim 4 or 5, wherein the intermediate layer (4) is formed of a carbide and / or nitride and / or boride compound of the first metal or a carbide and / or nitride and / or boride compound of a second metal different from the first metal.

7. 7. The welding electrode according to claim 6, wherein the carbide and / or nitride and / or boride compounds of the first metal and / or the second metal are stable up to a temperature of 800°C.

8. 8. The welding electrode according to claim 1, wherein the first metal and / or the second metal is composed of at least one of the elements Cr, Ti, Nb, Mo, W and Ta.

9. 9. The welding electrode according to claim 1, wherein another part of the welding tool is formed of a third metal.

10. The welding electrode according to claim 9, wherein the third metal contains Cu as a major component.

11. 11. Use of a welding electrode according to any one of claims 1 to 10 for producing a resistance welded joint between workpieces (9) made of a fourth metal having a passivation layer (10) of metal oxide.

12. 12. The method of claim 11, wherein the resistance welded joint is made by resistance spot welding, resistance projection welding, or resistance seam welding.

13. 13. The use according to claim 11 or 12, wherein the fourth metal is selected from the group consisting of Al, Mg, Ni, Ti, Zn, Cr, Fe, Nb, Ta and Cu.