Solid metal component and method of manufacturing same

Abstract

A solid metal member having a core and an outer shell surrounding the core on all sides, A solid metal component, wherein the core and shell are constructed of different grades of steel, the core steel having a lower critical cooling rate for martensite and bainite than the shell steel.

Description

[Technical field]

[0001] The present invention relates generally to the field of manufacturing solid metal components.

[0002] The invention finds non-exclusive application in the manufacture of large dimension, thick metal components, such as those found in the lower sections of steam generators in nuclear power plants, known as "tube sheets." [Background technology]

[0003] The function of such steam generators is to transport calories from the nuclear power plant's reactor through thousands of U-tubes in contact with the feed water, to be output to a circuit (called the "secondary" circuit) that runs a turbine that drives the rotor of an alternator, producing electricity. After the calories are released to the steam generators, the water is returned to the reactor inlet.

[0004] The several thousand tubes are of great length and are held at regular heights by spacers welded to the tube plate, providing holes for the free inflow and outflow of water. At the bottom of the tube plate is a partition called a "water box" to separate the various circulating waters.

[0005] The tube plates of steam generators in pressurized hydroelectric power plants are thick (50-60 cm), large diameter forgings with thousands of holes for the replacement tubes. They are subjected to high mechanical stresses due to the pressure difference on both sides, and their stiffness is achieved by their thickness and by the mechanical properties of the material from which they are made, i.e. low alloy steels of the carbon-manganese class.

[0006] The extremely rigid nature of this component presents two major manufacturing challenges: - the metallurgical and chemical uniformity within the component is very poor, due to the low level of forging required by the required ingot size and final thickness, resulting in variations in mechanical properties throughout the mass; - The combination of the very large thickness of the steel used and the limited hardening effect does not allow for a strengthened bainite or martensite microstructure in the plate core after quality heat treatment, which guarantees the best compromise between resistance and toughness.

[0007] Typically, at the center of the component, the yield strength, tensile strength, and ductility bearing decrease, but the elastic change temperature increases by more than 50°C.

[0008] By improving these mediocre properties it is possible to design boards that are less solid and therefore easier to manufacture, or to provide a larger margin of safety.

[0009] In this context, increased lead times and greater flexibility in supply are also highly anticipated.

[0010] The basic functions required for this tubesheet are essentially: - bending resistance at different pressure loads; - mechanical stability during manufacture and operation to receive and maintain the tube bundle; -Welding capabilities in the ferrules and bowls of steam generators; -Ability to be clad by welding with stainless steel or nickel-based alloys It is.

[0011] Therefore, for simplicity, the compromise required concerns three characteristics: - Elastic limit and tensile strength; - Tenacity and elasticity; - Weldability.

[0012] Regarding this last property (weldability), it is noted that the carbon equivalent (C*) of the steel, calculated according to standard EN 10028-2, is approximately 0.52% (typical value) to 0.62% (steel "18MND5" optimized for heat treatment), which represents a target value that should not be exceeded by much, otherwise the preheating temperatures of the various welds may be reduced, with a particular risk of cold cracks. Summary of the Invention [Problem to be solved by the invention]

[0013] In the prior art of such production, ingot casting, lowering of segregation zones and plate forging show difficulties in achieving the first problem mentioned above (non-uniformity) and risk of scrap.

[0014] It has also been shown that there is no solution to the second problem (limited hardenability) except by changing the grade of steel, due to the necessary compromise between mechanical properties, hardenability and weldability.

[0015] The aim of the present invention is to overcome these drawbacks. [Means for solving the problem]

[0016] For this purpose, the present invention first provides A solid metal member having a core and an outer shell surrounding the core on all sides, The core and shell are solid metal components constructed of different grades of steel, the core steel having a lower critical cooling rate for martensite and bainite than the shell steel.

[0017] Thanks to these features of the invention, the components obtained have particularly uniform mechanical properties, this is especially the case with regard to hardness, while elasticity and toughness are high.

[0018] Another advantageous, non-limiting feature of the component is that the core is itself surrounded by at least one inner shell, which is surrounded by the outer shell, and the steel of the core has lower critical cooling rates for martensite and bainite than the steel of the inner shell, which are themselves lower than those of the outer shell.

[0019] The present invention also relates to a method for manufacturing such a component.

[0020] The method is characterized in that it comprises a step of depositing the steel on a prefabricated base by additive manufacturing or welding to simultaneously form the core and the remainder of the shell or shells, respectively.

[0021] In another non-limiting significant feature of the method, the grade of the remaining steel of said outer shell is the same as the grade of said base; the grade of steel of the remainder of said outer shell is different from said base grade, and these two grades exhibit equal or nearly equal critical cooling rates of martensite and bainite; said base being manufactured by forging or rolling; said base is manufactured by additive manufacturing or welding;

[0022] Other features and advantages of the invention will become apparent from the following description, taken in conjunction with the accompanying drawings, which represent, by way of example and not by way of limitation, various possible embodiments of the invention, in which: [Brief description of the drawings]

[0023] [Figure 1] 1 is a schematic view along a vertical section of a component according to the invention; [Diagram 2] 2A-2D are schematic diagrams illustrating steps in the manufacture of the component of FIG. 1. [Diagram 3] 3 is a schematic diagram showing a manufacturing process of a member at a step subsequent to the step shown in FIG. 2. [Figure 4] FIG. 2 is a diagram showing the hardness change at the center of a component according to the invention after quenching and tempering treatment using the materials shown in Table I, which is referred to hereinafter. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0024] As will become apparent from the following description, the invention is based on the combination of carefully structured materials and a manufacturing process which, after quality processing, provides uniform high mechanical properties throughout the thickness of the component thus produced.

[0025] Throughout this description, including the claims, the term "member" is understood to mean both a plate, i.e. an object whose thickness is smaller than its length and width, and any other three-dimensional object whose thickness is greater than its other dimension, e.g. a parallelepiped or cylindrical object.

[0026] The present invention includes a disk-shaped solid metal plate 1 as shown in FIG.

[0027] It is shown to be arranged in a thickness 2 of stainless steel or an alloy known as Inconel (trademark). Unlike the one shown in figures 2 and 3, this thickness is preferably associated with the plate 1 after manufacture.

[0028] If the plate is the bottom plate of a steam generator (as described above), thickness 2 will be in contact with the primary water and therefore form a corrosion barrier for the remainder of plate 1 .

[0029] The plate 1 has a core 5 and an outer shell 3, which surrounds said core 5 on all sides. The core 5 and the shell 3 are made of different grades of steel.

[0030] More precisely, in the example shown, the core 5 is itself surrounded by an inner shell 4 , which is surrounded by said outer shell 3 .

[0031] In embodiments not shown, it may include a single outer shell 3 in direct contact with the core, but conversely it may include two or more shells.

[0032] In any case, in the present invention, the steel of the core 5 and the steel of each shell 3 and 4 are of different grades, the steel of said core 5 having a lower critical cooling rate for martensite and bainite than the steel of the shell 4 that surrounds it, and similarly for each shell that surrounds the previous shell.

[0033] Thus, in the case of FIG. 1, the velocity of the inner shell 4 is lower than that of the outer shell 3 .

[0034] This plate 1 can be manufactured according to the method detailed below.

[0035] First, a plate or base 30 is forged or rolled, having a typical thickness, usually between 10 and 15 cm. At such a thickness, very good metallurgical quality, free of macrosegregations, is ensured. If necessary, this plate 30 can be manufactured in the same manner as described below.

[0036] The remaining parts of the plate 1 are said to be "deposited" and are obtained by additive manufacturing or welding, which means that the total thickness of the plate 1 is gradually increased.

[0037] Referring to FIG. 2, this means that after the base 30 is formed, not only the lower portion of the shell 4 but also the side walls 31 of the shell 3 (the latter being formed at the ends of the assembly of the base 30 and the side walls 31) are simultaneously formed.

[0038] This operation is preferably carried out by one or a combination of the following methods: -Gas Metal Arc Welding (GMAW) or Metal Inert Gas / Active Inert Gas (MIG / MAG); -Submerged arc welding (SAW) or submerged arc welding with strips of solid flux (ASF) or other wires or fluxes; -Electroslag welding (ESW) or vertical slag welding.

[0039] In these deposition methods, the variations included are preferably the following metal depositions with typical high deposition rates (kg / h): -Tandem (two wires or strips with their own power supply); - Multi-wire (several wires with a magnetic core power supply); -Twin (two wires or strips in the same power supply); -Co-buildup without power supply; - combination of the aforementioned technologies; -High temperature (i.e. preheated) metal build-up.

[0040] To prevent cold cracking at the lowest possible preheat temperature, the build-up material is preferably selected to have a carbon equivalent of less than 0.65%, typically less than 0.62%, and exhibit very low diffusible hydrogen levels.

[0041] The fluxes used in the SAW and ESW processes are preferably basic fluxes which allow for better fusion zone properties.

[0042] The concept of steel grade selection with respect to plate dimensions and heat treatability is to select the more "hardenable" (i.e. suitable for hardening) grades closer to the center of the final part.

[0043] The gradient of quench sensitivity thus produced is intended to compensate for the decrease in cooling rate during quenching between the shell and the core.

[0044] For this purpose, the final properties obtained after quenching and tempering for various chemical analyses and local cooling rates are considered. Metallurgical transformation models in conjunction with the estimation of local cooling rates can be advantageously used to achieve this in a predictable way.

[0045] For the current steam generator tubesheets, the grades should be selected as follows: -Base 30 grade is a heat treat optimized version of the current specification ideal of 18MND 5. Typical analysis by mass percent is C 0.2, Mn 1.3, Mo 0.5, Ni 0.65. - The grade of metal deposited to make up the remainder of plate 1 must have a lower critical cooling rate for martensite and bainite than the previous layers further out, with a carbon equivalent not exceeding 0.65% and a pearlitic ferrite content as low as possible (<10%) to maintain a predominantly bainitic microstructure.

[0046] (Example) An example based on a commercially available product is provided below in Table 1 (referred to as "Table 1"), which includes typical chemical analyses, carbon equivalent values, and martensite (VcM) and bainite (VcB) critical cooling rates.

[0047] These latter values ​​have to be compared with the low cooling rates obtained because of the extremely large thickness of the plate: the cooling rates Vr700 (K / h) at 700°C are 5400, 3300, 1700, 770 and 475 for depths of 0, 5, 12, 20 and 25 cm, respectively.

[0048] [Table 1] Figure 3 shows the hardness results calculated through the centre of the plate after quenching in 865°C water and tempering at 635°C using the grades shown in Table 1. The segments shown in the figure have the reference numerical value of the part of plate 1 to which they relate.

[0049] The hardness is found to be quite uniform.

[0050] Also, the pearlite-ferrite contents remained below 10% in all deposited metals, implying high elasticity and toughness of these C-Mn-Ni steels.

[0051] In fact, while the actual quality criterion of the microstructure is the relative amounts of bainite and martensite, emphasis is also placed on the amounts of ferrite and pearlite. A microstructure exhibiting good mechanical properties preferably contains more than 90% bainite + martensite and therefore less than 10% ferrite + pearlite.

[0052] As a result, the transformation rate to exactly 10% ferrite + pearlite (abbreviated as "V10FP" (unit: K / h)) is also important.

[0053] Thus, the above table can be completed as follows: -For base 30, V10FP=1900; -For inner shell 4, V10FP=590; -For core 5, V10FP=335; -For part 31 of shell 3, V10FP=640.

[0054] In the above examples, three to four different chemical compositions are used. It can be conveniently reduced to only two different grades. These alternatives are suitable to accommodate the progression of the hardenability of the shell increasing towards the core.

[0055] Due to the circular geometry of the plate 1, the deposit is easily constructed with, but not limited to, a welding head which is only radially movable and welds circumferentially.

[0056] This avoids the more expensive use of robots with this manufacturing dimension.

[0057] For example, to form outer and inner passes, or simply to reduce manufacturing time, Several welding heads can advantageously be used simultaneously or sequentially.

[0058] Temperature control devices are advantageously used to compensate for preheat (above 150°C), interpass, and post-weld (24 hours, above 250°C) temperatures.

[0059] For a better manufacturing strategy, this can be done as follows: a) Although not necessary, it is beneficial to start with a forged base that is fixed before welding to the turning tool. b) A peripheral strip can be used to limit the thickness to be machined after welding. c) The construction is done additively, layer by layer, from bottom to top. d) Intermediate heat treatments may be carried out to reduce deformation and residual stresses (stress relief treatments above 550°C), to reduce the risk of hydrogen (preventive treatments) and to restore the properties of the underlying material. e) Intermediate forging operations can be carried out to further improve the final properties. Similarly, final forging can be easily carried out. f) Stress relieving treatment / first austenitizing / air cooling. g) Machining of blank types. h) Qualification by austenitizing at low temperature (AC3+40°C), water quenching and tempering depending on the grade used (approximately 635°C in the example given). AC3 is the conventional designation for the end of the alpha / gamma transformation on heating.

[0060] The method according to the invention has the following advantages: (Main Effects) - Elimination of macrosegregations, - uniformity of mechanical properties throughout the plate thickness, -Excellent overall mechanical properties, especially an excellent resistance / toughness balance.

[0061] (Secondary Benefits) -There is greater freedom in supplier selection and the company no longer requires extremely large ingot casting capacities. -Potential to reduce overall production time -Possibility of local repairs during manufacturing -Possibility of intermediate heat treatment -Possibility of intermediate and final forging -More economical installation than large forges.

[0062] Potential users of such technology include steam generator manufacturers, solid component forgers, boiler builders, forgers, and manufacturers of welding equipment and products.

Claims

1. A solid metal member having a core and an outer shell surrounding the core on all sides, the core and outer shell being constructed of different grades of steel, the steel of the core having a lower critical cooling rate for martensite and bainite than the steel of the outer shell; the core is itself surrounded by at least one inner shell, the inner shell being surrounded by the outer shell; A solid metal component in which the steel of the core exhibits lower critical cooling rates for martensite and bainite than the steel of the inner shell, which are themselves lower than those of the outer shell.

2. (1) forming a base that becomes a part of the outer shell and the inner shell; (2) depositing steel for the core, the inner shell, and the outer shell onto the base by additive manufacturing or welding to simultaneously form the core and the remaining portions of the outer shell and the inner shell, respectively; The method for producing the member according to claim 1, comprising the steps of:

3. The method of claim 2, wherein in step (2), the grade of steel for the outer shell is the same as that of the base.

4. The method described in claim 2, wherein in step (2), the grade of steel for the outer shell is different from the grade of the base, and the two grades exhibit equal or nearly equal critical cooling rates of martensite and bainite.

5. The method according to any one of claims 2 to 4, wherein the base is formed by forging or rolling.

6. The method of any one of claims 2 to 4, wherein the base is formed by additive manufacturing or welding.