Cellulose fiber materials and methods

Abstract

The present invention relates to a cellulose fibrous substrate comprising at least one top surface and at least one bottom surface, the cellulose fibrous substrate further comprising 60-90% by weight of cellulose fibers having a length of up to 10 mm, 0-10% of an acidic hardening catalyst, and 10-40% by weight of a binder selected from the group consisting of cellulose, hemicellulose, furan, lignin, and combinations thereof.

Description

[Technical Field]

[0001] The present invention relates to a cellulose fiber thermoset material and a method for producing said cellulose fiber thermoset material. [Background technology]

[0002] Given the growing awareness of the negative environmental impacts of global warming and marine and soil pollution, there is a need to replace pure fossil-based plastics, mineral-filled plastics and fiber-reinforced plastics (FRPs), glass fiber-reinforced plastics (GFRPs), and carbon fiber-reinforced plastics (CFRPs) with more environmentally friendly alternatives. FRP composites, such as GFRP and / or CFRP composites, exhibit high or very high strength-to-weight ratios and are extremely stiff due to the outstanding length and strength of their man-made, non-degradable fibers. These FRP composites are often used in a variety of applications, such as vehicles, protective sports equipment, buildings, and electrical housings, where flexural strength, impact resistance, and / or weather resistance are important. However, the environmental impact of these materials is high both in the production of raw materials such as glass or carbon fibers, the production of their intermediates, and their disposal and / or recycling. Attempts have been made to replace fossil-based polymers in GFRP and CFRP materials with more environmentally friendly alternatives, such as bio-based or bio-derived polymers. Additionally, attempts have been made to replace glass or carbon fibers with natural fibers such as flax, hemp, sisal, etc. However, the major challenge with both bio-based and / or bio-attributed and renewable and / or natural fiber alternatives for GFRP and CFRP composites is the high cost and lack of sufficient quantity and consistency of quality in supply to be competitive with fossil polymers and man-made fibers.

[0003] Natural fiber composites (NFCs) are classified into non-wood fiber-based composites and wood fiber and wood particle-based composites. Wood fibers are often shorter than other natural fibers, such as jute or flax. Because of the longer length of non-wood (natural) fibers, the application possibilities, driven, for example, by flexural strength, are greater than those of wood fibers and / or wood particles. These fibers often have a high cellulose content (>50%) and tend to be hydrophilic, creating challenges such as natural decay processes, dimensional instability, delamination, and other issues due to climate cycles (humidity and temperature). To address these issues, the NFC industry must infiltrate the composites with binders, often fossil-based, such as thermoplastics and thermosets; such systems are considered high in biocontent above 20%. In other words, these natural fibers are combined with fossil-based systems that are environmentally unfriendly and highly problematic to recycle or separate.

[0004] A large, stable, and renewable resource of cellulose fibers comes from forestry, where they are obtained from various tree species, such as conifers and eucalyptus, in the production of pulp and paper. Recently, many NFC materials have been manufactured by combining forest-derived cellulose fibers with polymers to create articles that not only reduce their environmental impact but are also more load-bearing. Such materials are typically manufactured by compounding pure wood fibers or fibers from pulp and paper manufacturing into particles for injection molding; therefore, the final article is not based on a layered sheet.

[0005] A known solution for creating load-bearing 3D single-curved or developable solutions based on cellulose fibers is wood veneer, which includes layers, where the long wood fibers of each layer are often oriented perpendicular to the wood fibers of the adjacent layer, and the layers are heat-pressed into a single-curved shape, such as a chair seat. For more complex 3D surfaces, such as double-curved or non-developable surfaces, specialized and expensive 3D veneers or plastics are the only option, as traditional veneers will splinter and break when trying to create a double-curved surface.

[0006] Another well-known example of using the short cellulose fibers found in paper is the use of high-pressure laminates, or HPL, consisting of several different layers of paper and facing material, and a polymeric or phenolic binder, to create flat load-bearing applications. Although some specialized and novel grades of HPL can be formed around single-curve edges by applying heat and restraint and using formable thermoplastic binders, HPL has never been used to produce articles with complex 3D non-developable surfaces involving single curvature, double curvature, and / or combinations of rotation and translation, such as load-bearing spherical shapes for helmets, cylindrical surfaces of revolution for vases, or complex surfaces for boat hulls.

[0007] In both of these examples, natural fibers are hydrophobic and / or decompose under UV light, so they are intended for indoor use. In the case of HPL, the outermost layer often has a special coating to enhance scratch resistance, UV resistance, and moisture resistance, as well as decorative appearance, such as imitation of marble or wood. Such materials can be used, for example, as countertops or laminate flooring stacks.

[0008] Another option for creating complex 3D load-bearing articles containing layers of fibers from renewable natural sources and possessing high tensile and flexural strength is to use long cellulose fibers such as hemp, flax, ramie, and sisal. Such fibers may be woven into flat but 2D flexible mats / fabrics impregnated with a binder. These materials are frequently used to create flat and 3D structures with advantageous mechanical properties. Here, fiber length is paramount, and each fiber is arranged on a complex 3D surface. This process is expensive, and sources of recovered fiber compete with the food and textile industries. Another challenge is that long natural fibers are hydrophilic and therefore absorb moisture, making them unsuitable for outdoor use and damp locations. Furthermore, the need for a polymer binder makes these natural fiber composites, like any composite containing polymers, difficult or impossible to recycle, thus disrupting the plastic recycling loop.

[0009] Finally, it is known to combine cellulose fibers with polymeric materials, such as thermoplastics, to produce particles for injection molding, extrusion, and blow molding and press molding. While thermoplastics can be biobased and biodegradable, such materials are significantly more expensive, and biobased solutions have inferior properties compared to fossil-based resin systems. Because NCFs and biobased polymers are based on field-grown crops, there is ongoing debate about whether they compete with agricultural land needed for food production. Furthermore, in some cases, the need for fertilizer and low yields mean that so-called bioplastics have a negative impact on the overall environment. Added to this is the uncertainty of weather, which can affect harvests and cause price fluctuations from year to year.

[0010] In light of the challenges currently present in the art, it would be desirable to provide a cellulose fiber substrate containing natural and renewable components that has a low environmental impact while achieving mechanical properties comparable to fiber composites such as GFRP, fossil-based polymers, and even metals such as aluminum. It would also be desirable to provide materials and methods for obtaining such substrates. Similarly, it would be desirable to create a solution for large-scale production by: 1) using a stable, process-industry-based, large-scale, non-food-competitive biobased feedstock source; and 2) creating properties that enable a highly automated production process by reducing issues common with commercially available manual reinforced fiber composite solutions, such as wet, sticky solutions that are difficult to integrate into internal logistics, robotics systems, and the like. Summary of the Invention

[0011] In view of the above, the present invention aims to solve at least some of the problems / deficiencies of the prior art. To this end, the present invention provides a cellulose fiber material and a method for producing the same. The cellulose fiber material based on renewable natural resources comprises a surface, the surface having at least one developable and / or non-developable surface portion.

[0012] The cellulose fibrous substrate according to the present invention comprises at least one top surface and at least one bottom surface, and further comprises 60 to 90% by weight of cellulose fibers having a length of up to 10 mm, 0 to 10% of an acidic hardening catalyst, and 10 to 40% by weight of a binder selected from the group consisting of cellulose, hemicellulose, furan, lignin, and combinations thereof.

[0013] In one embodiment, a cellulose fibrous substrate is provided, wherein the binder is polyfurfuryl alcohol (PFA).

[0014] In one embodiment, a cellulose fibrous substrate is provided, wherein the cellulose fibers comprise 0-100% virgin cellulose fibers and 0-100% recycled cellulose fibers.

[0015] In one embodiment, a cellulose fibrous substrate is provided, wherein at least one top and / or bottom surface has at least one developable and / or non-developable surface portion.

[0016] In one embodiment, a cellulose fibrous substrate is provided, wherein the cellulose fibers in the substrate are arranged substantially parallel, or the cellulose fibers in the substrate are arranged substantially crosswise, or the cellulose fibers in the substrate are arranged substantially randomly, or a combination thereof.

[0017] In one embodiment, a cellulose fibrous substrate is provided, wherein the substrate comprises at least one cavity.

[0018] The load-bearing 3D article according to the present invention comprises a cellulose fiber substrate according to the present invention.

[0019] In one embodiment, a load-bearing 3D article is provided, the load-bearing article having a tensile strength of at least 40 MPa, preferably at least 50 MPa, more preferably at least 100 MPa.

[0020] In one embodiment, a load-bearing 3D article is provided, the load-bearing article having a thickness of at least 2.5 mm, preferably at least 5 mm, more preferably at least 10 mm.

[0021] The method for producing a cellulose fibrous substrate comprising at least one top surface and one bottom surface according to the present invention comprises the following steps: a) providing at least one sheet of cellulose fibers having a maximum length of 10 mm; b) impregnating at least one cellulose fiber sheet with a mixture of an acidic hardening catalyst and a binder selected from the group consisting of cellulose, hemicellulose, furan, lignin, and combinations thereof to obtain at least one impregnated cellulose fiber sheet; c) pre-curing at least one impregnated cellulose fiber sheet by applying heat in the range of 50 to 300°C, thereby obtaining a prepreg; d) placing one or more prepregs in a stack; e) At least 7 kg / cm 2 , preferably at least 25 kg / cm 2 , more preferably at least 30 kg / cm 2 and at a temperature of at least 60°C, preferably at least 140°C, more preferably at least 150°C, for at least 10 seconds, preferably at least 1 minute, more preferably at least 2 minutes, thereby obtaining a cellulose fibrous substrate having at least one top surface and one bottom surface; Includes.

[0022] In one embodiment, a method for producing a cellulosic fibrous substrate is provided, wherein the binder is polyfurfuryl alcohol (PFA).

[0023] In one embodiment, a method for producing a cellulose fibrous substrate is provided, wherein the cellulose fibers comprise a mixture of 0-100% virgin cellulose fibers and 0-100% recycled cellulose fibers.

[0024] In one embodiment, a method for producing a cellulose fibrous substrate is provided, wherein the cellulose fibers are provided in the form of paper.

[0025] In one embodiment, a method is provided for producing a cellulose fibrous substrate, wherein the top and / or bottom surface has at least one developable and / or non-developable surface portion.

[0026] In one embodiment, a method for producing a cellulosic fibrous substrate is provided, wherein the cellulosic fibrous substrate has an amount of bio-based carbon of at least 80%.

[0027] In one embodiment, there is provided a method for producing a cellulose fibrous substrate, wherein the cellulose fibrous substrate comprises 60 to 90 wt % of the cellulose fibers.

[0028] In one embodiment, a method for producing a cellulose fibrous substrate is provided, wherein the cellulose fibrous substrate comprises 10 to 40 wt % of the binder.

[0029] In one embodiment, there is provided a method for producing a cellulose fibrous substrate, wherein the cellulose fibrous substrate comprises 0 to 10 wt % of the acid catalyst.

[0030] In one embodiment, a method for manufacturing a cellulose fibrous substrate is provided, wherein the prepregs in a stack are oriented such that the grain directions within the prepregs are substantially parallel.

[0031] In one embodiment, a method of manufacturing a cellulose fibrous substrate is provided, wherein prepregs in a stack are oriented such that the angle of grain direction within a prepreg is in the range of 0 to 90 degrees relative to adjacent prepregs.

[0032] In one embodiment, there is provided a method for producing a cellulose fibrous substrate, further comprising the step of: f) cutting the prepreg and / or cellulose fibrous substrate into a predetermined shape.

[0033] In one embodiment, there is provided a method for producing a cellulose fibrous substrate, further comprising the step of: g) creating cavities in the cellulose fibrous substrate.

[0034] Further features and advantages of the present invention will become apparent upon review of the appended claims and the following description. Those skilled in the art will appreciate that different features of the present invention can be combined to create embodiments other than those described below without departing from the scope of the invention.

[0035] These and other aspects of the invention will now be described in more detail with reference to the accompanying drawings, in which embodiments of the invention are shown. [Brief explanation of the drawings]

[0036] [Figure 1a] 1 shows an example of a surface of a cellulose fiber substrate according to the present invention. [Figure 1b] 1 shows an example of a surface of a cellulose fiber substrate according to the present invention. [Figure 1c] 1 shows an example of a surface of a cellulose fiber substrate according to the present invention. [Figure 2a] 2 shows another example of a surface of a cellulose fiber substrate according to the present invention. [Figure 2b] 2 shows another example of a surface of a cellulose fiber substrate according to the present invention. [Figure 2c] 2 shows another example of a surface of a cellulose fiber substrate according to the present invention. [Figure 2d] 2 shows another example of a surface of a cellulose fiber substrate according to the present invention. [Figure 2e] 2 shows another example of a surface of a cellulose fiber substrate according to the present invention. [Figure 3a] Three layers of prepreg material are shown. [Figure 3b] 1 shows a stiffened cellulose fibrous substrate molded into a curved surface. [Figure 4] Examples of cellulose fiber substrates of the present invention are shown below. [Figure 5] 1 shows a tensile strength test of a cellulose fiber substrate. [Figure 6] Figure 5 shows data comparing the tensile strength of the analyzed cellulose fiber substrates with that of other materials. [Figure 7] 1 shows a temperature diagram during the pressing process according to the invention. [Figure 8] 1 shows a cross section of a substrate according to the present invention. DETAILED DESCRIPTION OF THE INVENTION

[0037] The present invention will now be described with reference to the accompanying drawings, in which exemplary embodiments of the invention are shown. However, the present invention may be embodied in many different forms and should not be construed as limited to the embodiments of the invention set forth herein. Rather, these embodiments of the invention are provided as examples so that this disclosure will convey the scope of the invention to those skilled in the art. In the various figures, the same reference numerals, unless otherwise specified, indicate the same or similar components having the same or similar function.

[0038] As described above, the cellulose fiber substrate includes cellulose fibers having a length of up to 10 mm. The cellulose fibers are made using cellulose ethers or esters, which can be obtained from plant bark, wood, or leaves, or from other plant-based materials. The cellulose fibers can be obtained by converting wood into wood pulp. The length of each cellulose fiber in the composite material can be the same or different from the length of other cellulose fibers. In fact, it is believed that some of the cellulose fibers may have a length greater than 10 mm, but the amount of these fibers should be considered negligible. The term "negligible" is understood as an amount less than 0.01% by weight. The cellulose fibers may be provided in any suitable form, such as sheets, rolls, batting, etc.

[0039] The cellulose fibers that can be used to manufacture the cellulose fiber substrate according to the present invention may be recycled cellulose fibers, which offers the advantage of reducing the cost of the cellulose fiber substrate and contributing to a circular economy. Alternatively, the cellulose fibers may be virgin cellulose fibers, which provide increased tensile and / or flexural strength of the circuit board compared to when recycled cellulose fibers are used. Furthermore, the cellulose fibers may be a mixture of recycled and virgin cellulose fibers, ranging from 0 to 100% virgin cellulose fibers and 0 to 100% recycled cellulose fibers, respectively. The cellulose fibers may include paper, such as softwood kraft paper, hardwood kraft paper, sulfite fibers, organosolv fibers, nonwoven fabrics, or combinations thereof. It is contemplated that the cellulose fibers comprise 50 to 90% by weight of the kraft paper. The paper may be provided in sheet form and / or continuous sheet form, for example, in the form of a paper roll.

[0040] The cellulose fibrous substrate of the present invention may comprise 40-90% by weight of cellulose fibers and 10-40% by weight of a binder. The cellulose fibrous substrate may have at least 80%, preferably at least 90%, and more preferably at least 95% biobased carbon. Biobased carbon is derived entirely or partially from biomass resources. Biomass resources are renewable or reusable organic materials such as crop residues, wood residues, grasses, and aquatic plants. In contrast, non-biobased carbon is produced entirely from petrochemical sources. The amount of biobased carbon mentioned above is a measure of the amount of biobased carbon in a product compared to the total biobased carbon and petroleum-based carbon in the product. The term biobased carbon refers to non-fossil-derived carbon and relates to cellulose fibers and / or binders and / or additives.

[0041] The cellulosic fibrous substrate according to the present invention further comprises a binder selected from the group consisting of cellulose, hemicellulose, lignin, furan, preferably polyfurfuryl alcohol (PFA), and combinations thereof.

[0042] The cellulose fiber substrate may contain additives such as catalysts, UV agents, conductive compounds, pigments, hydrophobic materials, softeners, hardeners, and curing agents. The catalyst may be an acid catalyst, e.g., an inorganic acid or an organic acid. The catalyst may be added in the range of 0-10% by weight and may have a pH value of less than 5 and / or an acid value of less than 5 mg KOH / g. Additives may be added to increase chemical resistance, fire resistance, and abrasion resistance, and / or to increase the curing rate, thus maximizing production.

[0043] Surprisingly, the prepreg material of the present invention exhibits advantageous flotation properties during the curing process, most likely due to the combination of relatively short fibers and a binder with a specific viscosity. It is conceivable that alcohol, such as up to 20% ethanol or methanol, can be added to the process to further improve flotation capabilities. The term flotation is understood as the property of cellulose fibers that allows them to migrate and fill cracks and fractures that may appear during the production of cellulose fibrous substrates. The flotation property allows cellulose fibers to conform to the shape of a mold or tool during the manufacturing process. As shown in Figures 1-4, the flotation property enables the production of complex shapes, such as 3D shapes, as well as flat surfaces, and imparts control over the microsurface structure, thus enabling the tailored production of additional surface characteristics, such as smooth and blank or matte and rough surfaces. It is contemplated that shapes produced according to the present invention can be flat, single-curved, double-curved, spherical, composite, or have holes therein. Figures 3a and 3b show how a single sheet of prepreg is transformed into a single homogeneous material with a curved structure. Figure 8 shows a cross-section of a cellulose fiber substrate, but does not allow identification of the individual layers of cellulose fibers used during the manufacturing process. This is a property made possible by the surprising floating effect of short fibers in the manufacturing method according to the present invention. Figure 3a shows an embodiment in which the cellulose fiber substrate is made from three layers of prepreg. Each layer of prepreg contains cellulose fibers and a binder as described above. The layers have equal thickness.

[0044] As noted above, cellulose fibrous substrates include surfaces having at least one developable and / or non-developable surface portion. Figures 1a-1c show various examples of such surfaces. In particular, Figure 1a shows a developable, i.e., single-curved surface, while Figures 1b and 1c show non-developable, i.e., double-curved surfaces.

[0045] Figures 2a-2e show another example of a surface that includes developable and non-developable surface portions. Figure 2a is a perspective view of such a surface, while Figures 2b and 2c are front and top views, respectively. As can be seen in Figures 2d and 2e, the surface shown in Figure 2a includes non-developable portions A and B.

[0046] In the context of the present invention, a developable surface is a smooth surface with zero Gaussian curvature. Gaussian curvature is defined as the product of the two principal curvatures of a surface. In other words, a developable surface is a non-planar surface that can be flattened onto a plane without distortion, i.e., can be bent without stretching or compressing. Conversely, it is a surface that can be created by deforming a plane by folding, bending, rolling, cutting, and / or gluing. Examples of developable surfaces are cylinders and cones.

[0047] Conversely, a non-developable surface is a surface with a non-zero Gaussian curvature. Therefore, a non-developable surface is a non-planar surface that cannot be flattened onto a plane without distortion. The majority of surfaces are generally non-developable. Non-developable surfaces are sometimes called doubly curved surfaces. One of the most frequently used non-developable surfaces is the sphere.

[0048] Figure 4 shows a cellulose fiber substrate according to the present invention, where the cellulose fiber substrate is a chair seat. As can be seen in Figure 4, the chair seat comprises four sections C to F, which are described in more detail below.

[0049] Section C contains a complex, non-developable 3D surface with an edge having an arc and a transition from a doubly curved surface to a single curved surface. Section D contains a non-developable, complex 3D surface with an edge having an arc and a transition from an extreme doubly curved surface to an extreme single curved surface. Focusing on point E reveals a complex 3D edge with a larger radius that is doubly curved, i.e., non-developable, surface. Section F contains a complex 3D edge where a sharp edge radius (r<2mm) is maintained along all transitions between single and doubly curved surfaces.

[0050] The cellulose fibrous substrate of the present invention may have at least one portion that includes a radius of curvature of less than 10 cm, preferably less than 5 cm.

[0051] Cellulose fibers are made using cellulose ethers or esters, which can be obtained from plant bark, wood, or leaves, or from other plant-based materials. Cellulose fibers can be obtained by converting wood into wood pulp. The length of each cellulose fiber in the cellulose fiber substrate can be the same or different from the length of other cellulose fibers. In fact, it is believed that some cellulose fibers may have a length greater than 10 mm, but the amount of these fibers should be considered negligible. The term "negligible" is understood to mean an amount less than 0.01% by weight. The cellulose fibers may be provided in any suitable form, such as sheets or pellets.

[0052] The cellulose fibers may be randomly oriented or may be oriented so that the longitudinal extensions of the fibers are substantially parallel.

[0053] The cellulose fiber substrate of the present invention may comprise 40 to 90% by weight of cellulose fibers and 10 to 40% by weight of a binder. The cellulose fiber substrate of the present invention further comprises a binder selected from the group consisting of thermosetting resins, reactive thermoplastic resins, cellulose, hemicellulose, lignin, bio-based polymers, and combinations thereof. The thermosetting resin may be a substituted or unsubstituted furan, epoxy, polyurethane, or phenolic resin. The reactive thermoplastic resin may have similar performance to a thermosetting resin after curing and may be in liquid or powder form. Such binders are readily available, cost-effective, often biodegradable, and environmentally friendly. In particular, the binder is polyfurfuryl alcohol (PFA). Among bio-based polymers, mention may be made of polylactic acid, poly-L-lactide, polyhydroxybutyrate, polyhydroxyalkanoate (PHA), polyamide, polypropylene (PP), and polyethylene terephthalate.

[0054] As described above, it has been surprisingly discovered that, although the prepreg stack constituting the cellulose fibrous substrate of the present invention includes layers, the final cellulose fibrous substrate of the present invention can be recognized as being made from a homogeneous cellulose fibrous substrate, as shown in Figures 3b and 7. Without being bound by theory, it is believed that this effect is achieved by having cellulose fibers with lengths of less than 10 mm, preferably less than 4 mm. As described above, the short hydrophilic cellulose fibers are substantially completely impregnated with the binder. Furthermore, when high pressure is applied to the prepreg stack to form the cellulose fibrous substrate, cracks are rarely generated because the short fiber lengths allow the cellulose fibers to rearrange without breaking. Furthermore, even if a crack appears in one layer of the prepreg stack, the crack can be filled by cellulose fibers from at least one adjacent layer of the prepreg stack. Figure 8 shows a cross-section of a cellulose fibrous substrate, but the individual layers of cellulose fibers used during the manufacturing process cannot be identified. This property is made possible by the surprising floating effect of short fibers in the manufacturing method of the present invention.

[0055] The cellulose fiber substrate according to the present invention has a tensile strength and / or flexural strength of at least 40 MPa, preferably at least 50 MPa, and more preferably at least 100 MPa. Those skilled in the art will readily appreciate that such tensile strength and / or flexural strength is extremely surprising for an article comprising a cellulose fiber substrate based on short cellulose fibers. Such high tensile strength and / or flexural strength exceeds the tensile strength and / or flexural strength of articles comprising wood- and plastic-based cellulose fiber substrates and is comparable to the tensile strength and / or flexural strength achieved when using certain cellulose fiber substrates.

[0056] The mechanical properties of the substrate according to the invention were measured and the results were as follows: [Table 1]

[0057] Figure 5 shows the results of the tensile strength test according to ISO 527. Six different specimens with different thicknesses were tested. As can be seen from the table shown in Figure 5, the average tensile strength was measured to be 166 MPa, which clearly exceeds the tensile strength of wood and wood-based materials and is comparable to porous ceramics and composites such as GFRP (Figure 6).

[0058] One of the reasons for the high tensile and / or bending strength of the cellulose fibrous substrate of the present invention is believed to be the good adhesion between the fibers and the binder, which contributes to the internal mechanical cross-linking of the fibers to each other so that the fibers are trapped and fixed together, thus contributing to the tensile and / or bending strength of the cellulose fibrous substrate.

[0059] Another reason for the high tensile and / or flexural strength of cellulose fiber substrates is the possibility to determine the fiber orientation in 3D articles during manufacturing.

[0060] The cellulose fibers may be randomly oriented or may be oriented so that the longitudinal extension of the fibers is substantially parallel or substantially intersecting. To this end, the fibers may be arranged so that the longitudinal extension (grain direction) of the majority of the fibers is aligned in the same direction. This can be achieved by arranging one or more prepregs in a specific direction in the stack. In particular, at least one prepreg may be oriented so that the grain direction of the cellulose fibers in at least one prepreg is substantially parallel to the grain direction of the cellulose fibers in the other prepreg. It has been shown that the tensile strength and / or flexural strength in a direction parallel to the grain direction is significantly higher, for example, by a factor of two, compared to the tensile strength and / or flexural strength in a direction perpendicular to the grain direction. Therefore, it is possible to design a cellulose fiber substrate so that the tensile strength and / or flexural strength are tailored to the intended application.

[0061] The cellulose fibers of each of the at least one prepreg may also be oriented so that the cellulose fibers are arranged in a cross shape. The at least one prepreg may then be arranged so that the grain direction of the cellulose fibers of one of the at least one prepreg is perpendicular to the grain direction of the cellulose fibers of another of the at least one prepreg. The at least one prepreg may also be arranged so that the grain direction of the cellulose fibers of one of the at least one prepreg forms an angle of 0 to 90° with respect to the grain direction of the cellulose fibers of another of the at least one prepreg, thereby achieving a cross shape with an angle ranging from 0 to 90°.

[0062] It is known that cellulose fiber substrates containing long cellulose fibers, such as hemp, flax, ramie, and sisal, can exhibit significantly higher tensile and / or bending strength. Surprisingly, it has been found that 3D articles of the present invention containing cellulose fiber substrates containing short cellulose fibers, i.e., cellulose fibers having a length of up to 10 mm, preferably up to 4 mm, exhibit tensile and / or bending strength comparable to natural fibrous cellulose fiber substrates containing long cellulose fibers. At the same time, due to the fact that the short cellulose fibers are impregnated with a binder, articles containing short cellulose fibers are water-repellent to a greater extent than articles containing long cellulose fibers. The term "water-repellent" refers to being hydrophobic and / or having a density that prevents water from penetrating the material. Because short cellulose fibers are easily mobile within a cellulose fiber substrate during manufacturing, the fibers can "float" and fill cracks and crevices that may appear during the manufacturing of cellulose fiber substrates with complex surface structures, allowing layers to fuse together. According to the present invention, it is possible to manufacture cellulose fiber substrates with a small radius of curvature, a known challenge in the field of creating complex 3D structures.

[0063] The cellulose fiber substrates according to the present invention exhibit high moisture resistance, possibly due to the nature of the binder in combination with the manufacturing process. Furthermore, the cellulose fiber substrates according to the present invention have been found to be self-extinguishing when using PFA.

[0064] Furthermore, the cellulose fiber substrate according to the present invention has been found to be flammable and self-extinguishing. According to a glow-wire test performed in accordance with IEC 60695-2-12:2021, the cellulose fiber substrate according to the present invention passed temperature tests at 650°C and 850°C when cured using PFA as a binder. The cellulose fiber substrate according to the present invention is fire-resistant according to STD 104-0001 / ISO 3795, UV-resistant according to STD 423-0061, scratch-resistant according to STD 423-0030, heat-resistant according to Volvo STD 423-0055, impact-resistant according to EN 13087, and VOC-free as tested in accordance with Volvo STD 429-0003. The density of the cellulose fiber substrate according to the present invention is 134 g / cm according to ISO 11183. 3 The glass transition temperature Tg was measured to be 145°C according to ISO11358, and the Charpy impact strength was 8.6kJ / m according to ISO179. 2 A life cycle analysis calculation performed on a cellulose fiber substrate according to the present invention resulted in 0.65 kg CO2 equivalents.

[0065] Examples of the cellulose fiber substrate of the present invention are sports equipment such as helmets and skateboards, furniture such as chairs and tables, and vehicle parts such as dashboards, door handles and interior parts. Furthermore, the cellulose fiber substrate can be used in buildings and structures, home appliances, large appliances, etc.

[0066] Thus, the cellulose fiber substrate of the present invention can replace currently available cellulose fiber substrates, including more expensive and environmentally unfriendly materials such as plastics and GFRP, without compromising tensile and flexural strength, and with even improved tensile and flexural strength compared to plastics and wood.

[0067] The cellulose fiber substrate of the present invention has high moisture resistance, which is very beneficial when the cellulose fiber substrate is intended for outdoor use or for use in a wet environment, such as a bathroom or a humid climate. Furthermore, the surface finish of the cellulose fiber substrate of the present invention is highly decorative and aesthetically appealing and can be further tailored to the desired application. In particular, the surface of the cellulose fiber substrate may be glossy or matte. The cellulose fiber substrate may have a glossy-satin finish, a matte finish, a textured surface, a patterned surface, or a surface with letters or pictures. The cellulose fiber substrate of the present invention and the 3D article produced therefrom may have a variable thickness throughout the entire detail, or may have the same thickness throughout the entire detail.

[0068] The cellulose fiber substrates according to the present invention and 3D articles produced therefrom may have a thickness of at least 1.5 mm, preferably at least 2.5 mm, preferably at least 5 mm, more preferably at least 10 mm. As is clear from the above, the cellulose fiber substrates according to the present invention exhibit unprecedented strength despite their relatively thinness. Thus, the cellulose fiber substrates combine a lightweight and slim structure with excellent impact strength. The cellulose fiber substrates according to the present invention and 3D articles produced therefrom may also have significantly greater thicknesses, such as thicknesses of at least 20 mm, preferably at least 40 mm, more preferably at least 50 mm. Furthermore, the total surface area of the cellulose fiber substrate is at least 0.1 m 2 In particular, the total surface area of the cellulose fiber substrate may be 0.3 m 2 ~100m 2 In other words, cellulose fiber substrates can be quite large and still exhibit unprecedented strength, which allows such articles to be used in impact absorbing applications.

[0069] The cellulose fiber substrate of the present invention may be rigid. The term "rigid" in the context of the present invention is intended to mean lacking or lacking flexibility. The cellulose fibers in the cellulose fiber substrate may be provided in the form of a sheet.

[0070] The cellulose fiber material from which the 3D articles of the present invention are produced may be in the form of at least one layer of cellulose fibers impregnated with a binder. Furthermore, the cellulose fiber substrate from which the 3D articles of the present invention are produced may be a prepreg stack comprising at least two layers, preferably at least three layers. The term "prepreg stack" is understood to mean a product produced by laminating, i.e., by combining one or more superimposed layers of material. In practice, the prepreg stack may comprise more than three layers, for example, at least four, preferably at least five, and more preferably at least six layers. Each layer preferably comprises cellulose fibers and a binder as described above.

[0071] Surprisingly, it has been found that although the stack of prepregs constituting the cellulose fiber substrate of the present invention includes layers, the final cellulose fiber substrate of the present invention is recognized as being made from a homogeneous cellulose fiber substrate. Without being bound by theory, it is believed that this effect is achieved by having the cellulose fibers have a length of less than 10 mm, preferably less than 4 mm. As described above, the short hydrophilic cellulose fibers are substantially completely impregnated with the binder. Furthermore, when the prepreg stack is subjected to high pressure and high temperature to form the cellulose fiber substrate, the short fiber length allows the cellulose fibers to rearrange without breaking, so that cracks are hardly generated. The pressure should be at least 20 kg / cm. 2 , preferably at least 25 kg / cm 2 , more preferably 30 kg / cm 2The temperature may be at least 60°C, preferably at least 140°C, more preferably at least 150°C. In particular, the temperature may be 148°C to 152°C. Furthermore, even if a crack appears in one of the layers of the prepreg stack, the crack can be filled by cellulose fibers from at least one of the adjacent layers of the prepreg stack during the manufacturing process.

[0072] When a stack of prepregs is used, each layer of the stack of prepregs may be positioned relative to the other layers such that the longitudinal extension of the fibers is adapted to the intended use of the resulting cellulosic fiber substrate.

[0073] Each layer of the prepreg stack may have a thickness of 0.01 mm to 10 mm. In practice, the thickness of each layer depends on the total thickness of the cellulose fiber substrate as described above. Thus, if the cellulose fiber substrate includes only one layer of cellulose fiber substrate, the thickness of the layer is substantially equal to the thickness of the cellulose fiber substrate. If multiple layers are present, the thickness of each layer may be the same as or different from the thickness of the other layers in the prepreg stack. The term "multiple" in the context of the present invention means at least two.

[0074] The prepreg stack disclosed above may be a high pressure stack of prepregs (HPL), which is produced by impregnating multiple layers of kraft paper containing cellulose fibers with a binder.

[0075] The cellulose fiber substrate according to the present invention may include at least one surface layer. In the context of the present invention, the term "surface layer" is understood to mean a layer disposed on the surface of the cellulose fiber substrate. Such a surface layer may be disposed to provide scratch resistance, UV resistance, food compatibility, aesthetic appearance, antibacterial properties, color, surface structure, friction, or any other desired functionality.

[0076] The method for producing a cellulose fiber substrate by hot and pressure molding comprises the following steps: a) providing at least one sheet of cellulose fibers having a maximum length of 10 mm; b) impregnating at least one cellulose fiber sheet with a mixture of an acidic hardening catalyst and a binder selected from the group consisting of cellulose, hemicellulose, furan, lignin, and combinations thereof to obtain at least one impregnated cellulose fiber sheet; c) pre-curing at least one impregnated cellulose fiber sheet by applying heat in the range of 50 to 300°C, thereby obtaining a prepreg; d) placing one or more prepregs in a stack; e) At least 7 kg / cm 2 , preferably at least 25 kg / cm 2 , more preferably at least 30 kg / cm 2 and at a temperature of at least 60°C, preferably at least 140°C, more preferably at least 150°C, for at least 10 seconds, preferably at least 1 minute, more preferably at least 2 minutes, thereby obtaining a cellulose fibrous substrate having at least one top surface and one bottom surface; Includes.

[0077] The above method may further comprise the steps of: f) cutting the edges of the cellulose fibrous substrate; and h) creating cavities in the cellulose fibrous substrate.

[0078] In summary, the present invention provides a cellulose fiber substrate comprising cellulose fibers, which are natural, readily available, highly recyclable, and therefore environmentally friendly and cost-effective. A surprising and unexpected advantage of the present invention is that not only are the mechanical properties, such as flexural strength and tensile strength, of the cellulose fiber substrate of the present invention comparable to the tensile strength and / or flexural strength of 3D articles made from GFRP, but the present invention is also made from short cellulose fibers combined with a bio-based binder, which provides design freedom for creating complex 3D surfaces, particularly those containing non-developable parts. Another advantage of the present invention is that by-products from the food and agricultural industries are used as binders, which contributes to a circular economy and is environmentally friendly.

[0079] While the invention has been illustrated in the accompanying drawings and in the foregoing description, such illustrations are to be considered illustrative or exemplary and not restrictive. The invention is not limited to the disclosed embodiments. Other variations to the disclosed embodiments can be understood and effected by those skilled in the art in practicing the claimed invention, from a study of the drawings, the disclosure, and the appended claims. In the appended claims, the word "comprising" does not exclude other elements or steps, and the indefinite article "a" or "an" does not exclude a plurality. The mere fact that certain measures are recited in mutually different dependent claims does not indicate that a combination of these measures cannot be used to advantage. Any reference signs in the claims are not to be construed as limiting the scope. Examples of embodiments of the present invention are listed in the following items [Aspect 1] to [Aspect 22]. [Aspect 1] A cellulose fiber substrate, at least one top surface; at least one bottom surface; Including, The cellulose fiber substrate is 60 to 90% by weight of cellulose fibers having a length of up to 10 mm; 0-10% acid curing catalyst; 10 to 40 wt. % of a binder selected from the group consisting of cellulose, hemicellulose, furan, lignin, and combinations thereof; Further comprising: Cellulose fiber substrate. [Aspect 2] 2. The cellulose fibrous substrate of claim 1, wherein the binder is polyfurfuryl alcohol (PFA). [Aspect 3] 3. The cellulose fiber substrate according to aspect 1 or 2, wherein the cellulose fibers comprise 0 to 100% virgin cellulose fibers and 0 to 100% recycled cellulose fibers. [Aspect 4] Aspect 4. The cellulose fibrous substrate of any one of aspects 1 to 3, wherein the at least one top surface and / or bottom surface has at least one developable and / or non-developable surface portion. [Aspect 5] 5. The cellulose fiber substrate of any one of aspects 1 to 4, wherein the cellulose fibers in the substrate are arranged substantially parallel, or the cellulose fibers in the substrate are arranged substantially crosswise, or the cellulose fibers in the substrate are arranged substantially randomly, or a combination thereof. [Aspect 6] Aspect 6. The cellulose fibrous substrate of any one of aspects 1 to 5, wherein the substrate comprises at least one cavity. [Aspect 7] A load-bearing 3D article comprising the cellulose fibrous substrate of any one of embodiments 1 to 6. [Aspect 8] 11. The load-bearing 3D article according to aspect 10, wherein said load-bearing article has a tensile strength of at least 40 MPa, preferably at least 50 MPa, more preferably at least 100 MPa. [Aspect 9] 9. The load-bearing 3D article according to aspect 10 or 8, wherein said load-bearing article has a thickness of at least 2.5 mm, preferably at least 5 mm, more preferably at least 10 mm. [Aspect 10] 1. A method for producing a cellulose fibrous substrate comprising at least one top surface and a bottom surface, the method comprising: a) providing at least one sheet of cellulose fibers having a maximum length of 10 mm; b) impregnating said at least one cellulose fiber sheet with a mixture of an acidic hardening catalyst and a binder selected from the group consisting of cellulose, hemicellulose, furan, lignin and combinations thereof to obtain at least one impregnated cellulose fiber sheet; c) pre-curing said at least one impregnated cellulose fiber sheet by applying heat in the range of 50 to 300°C, thereby obtaining a prepreg; d) placing one or more of said prepregs in a stack; e) At least 7 kg / cm 2 , preferably at least 25 kg / cm 2 , more preferably at least 30 kg / cm 2 and at a temperature of at least 60°C, preferably at least 140°C, more preferably at least 150°C, for at least 10 seconds, preferably at least 1 minute, more preferably at least 2 minutes, thereby obtaining a cellulose fibrous substrate having at least one top surface and one bottom surface; A method comprising: [Aspect 11] 11. The method for producing a cellulose fibrous substrate of embodiment 10, wherein the binder is polyfurfuryl alcohol (PFA). [Aspect 12] 12. The method for producing a cellulose fibrous substrate according to claim 10 or 11, wherein the cellulose fibers comprise a mixture of 0-100% virgin cellulose fibers and 0-100% recycled cellulose fibers. [Aspect 13] 13. The method for producing a cellulose fibrous substrate according to any one of aspects 10 to 12, wherein the cellulose fibers are provided in the form of paper. [Aspect 14] 14. The method for producing a cellulose fibrous substrate of any one of aspects 10 to 13, wherein the top surface and / or the bottom surface has at least one developable and / or non-developable surface portion. [Aspect 15] 15. The method for producing a cellulose fibrous substrate according to any one of aspects 10 to 14, wherein the cellulose fibrous substrate has a bio-based carbon content of at least 80%. [Aspect 16] 16. The method for producing a cellulose fibrous substrate according to any one of aspects 10 to 15, wherein the cellulose fibrous substrate comprises 60 to 90 wt % of the cellulose fibers. [Aspect 17] 17. The method for producing a cellulose fibrous substrate according to any one of aspects 10 to 16, wherein the cellulose fibrous substrate comprises 10 to 40 wt. % of the binder. [Aspect 18] 18. The method for producing a cellulose fibrous substrate according to any one of aspects 10 to 17, wherein the cellulose fibrous substrate comprises 0 to 10 wt. % of the acid catalyst. [Aspect 19] 19. The method for producing a cellulose fibrous substrate of any one of aspects 10 to 18, wherein the prepregs in the stack are oriented such that grain directions in the prepregs are substantially parallel. [Aspect 20] 20. The method for producing a cellulose fibrous substrate of any one of aspects 10 to 19, wherein the prepregs in the stack are oriented such that the angle of grain direction within a prepreg is in the range of 0 to 90 degrees relative to an adjacent prepreg. [Aspect 21] A method for producing a cellulose fiber substrate according to any one of aspects 10 to 20, further comprising the step of: f) cutting the prepreg and / or the cellulose fiber substrate into a predetermined shape. [Aspect 22] 22. The method for producing a cellulose fibrous substrate according to any one of aspects 10 to 21, further comprising the step of: g) creating cavities in the cellulose fibrous substrate.

Claims

1. A cellulose fiber substrate, at least one top surface; at least one bottom surface; Including, The cellulose fiber substrate is 60 to 90% by weight of cellulose fibers having a length of up to 10 mm; 0-10% acidic curing catalyst; 10 to 40 wt. % of a binder selected from the group consisting of cellulose, hemicellulose, furan, lignin, and combinations thereof; Further comprising: Cellulose fiber substrate.

2. 2. The cellulose fibrous substrate of claim 1, wherein the binder is polyfurfuryl alcohol (PFA).

3. The cellulose fiber substrate according to claim 1 or 2, wherein the cellulose fibers comprise 0 to 100% virgin cellulose fibers and 0 to 100% recycled cellulose fibers.

4. 3. The cellulose fibrous substrate of claim 1 or 2, wherein the at least one top and / or bottom surface has at least one developable and / or non-developable surface portion.

5. 3. The cellulose fiber substrate according to claim 1 or 2, wherein the cellulose fibers in the substrate are arranged substantially parallel, or the cellulose fibers in the substrate are arranged substantially crosswise, or the cellulose fibers in the substrate are arranged substantially randomly, or a combination thereof.

6. The cellulose fibrous substrate of claim 1 or 2, wherein the substrate comprises at least one cavity.

7. A load-bearing 3D article comprising the cellulose fiber substrate of claim 1 or 2.

8. 8. The load-bearing 3D article of claim 7, wherein said load-bearing 3D article has a tensile strength of at least 40 MPa.

9. 8. The load-bearing 3D article of claim 7, wherein said load-bearing 3D article has a thickness of at least 2.5 mm.

10. 1. A method for manufacturing a cellulose fibrous substrate comprising at least one top surface and a bottom surface, the method comprising: a) providing at least one cellulose fiber sheet having a maximum length of 10 mm; b) impregnating said at least one cellulose fiber sheet with a mixture of an acidic curing catalyst and a binder selected from the group consisting of cellulose, hemicellulose, furan, lignin and combinations thereof to obtain at least one impregnated cellulose fiber sheet; c) pre-curing said at least one impregnated cellulose fiber sheet by applying heat in the range of 50 to 300°C, thereby obtaining a prepreg; d) placing one or more of said prepregs in a stack; e) pressing the stack in a press tool at a pressure of at least 7 kg / cm2 and at a temperature of at least 60°C for at least 10 seconds, thereby obtaining a cellulose fibrous substrate having at least one top surface and one bottom surface; A method comprising:

11. 11. The method for producing a cellulose fibrous substrate according to claim 10, wherein the binder is polyfurfuryl alcohol (PFA).

12. 12. The method for producing a cellulose fibrous substrate according to claim 10 or 11, wherein the cellulose fibers comprise a mixture of 0 to 100% virgin cellulose fibers and 0 to 100% recycled cellulose fibers.

13. 12. The method for producing a cellulose fibrous substrate according to claim 10 or 11, wherein the cellulose fibers are provided in the form of paper.

14. 12. A method for producing a cellulose fibrous substrate according to claim 10 or 11, wherein the top surface and / or the bottom surface have at least one developable and / or non-developable surface portion.

15. 12. The method for producing a cellulose fibrous substrate according to claim 10 or 11, wherein the cellulose fibrous substrate has an amount of bio-based carbon of at least 80%.

16. 12. The method for producing a cellulose fibrous substrate according to claim 10 or 11, wherein the cellulose fibrous substrate comprises 60 to 90% by weight of the cellulose fibers.

17. 12. The method for producing a cellulose fibrous substrate according to claim 10 or 11, wherein the cellulose fibrous substrate comprises 10 to 40% by weight of the binder.

18. 12. The method for producing a cellulose fibrous substrate according to claim 10 or 11, wherein the cellulose fibrous substrate comprises up to 10% by weight of the acidic curing catalyst.

19. 12. The method for producing a cellulose fibrous substrate according to claim 10 or 11, wherein the prepregs in the stack are oriented so that grain directions in the prepregs are substantially parallel.

20. 12. The method for producing a cellulose fibrous substrate according to claim 10 or 11, wherein the prepregs in the stack are oriented such that the angle of the grain direction in a prepreg is in the range of 0 to 90 degrees relative to adjacent prepregs.

21. 12. The method for producing a cellulose fiber substrate according to claim 10 or 11, further comprising the step of: f) cutting the prepreg and / or the cellulose fiber substrate into a predetermined shape.

22. 12. The method for producing a cellulose fibrous substrate according to claim 10 or 11, further comprising the step of: g) creating cavities in the cellulose fibrous substrate.