Environmentally friendly construction material composition with improved early strength

Abstract

The present invention relates to a construction material composition containing up to 55% by dry weight of Portland cement, which has high early and long-term compressive strength. Other major components in cement are SCM, limestone, a sulfate source, and an accelerator.

Description

[Technical Field]

[0001] The present invention relates to a construction material composition comprising Portland cement clinker, a supplementary cementitious material, a calcium carbonate phase, a sulfate source, and a hardening accelerator A. Compared to conventional ordinary cement, the Portland cement clinker content is (significantly) reduced. [Background technology]

[0002] Cement systems are often monitored from the perspective of environmental aspects due to CO2 emissions. To address CO2 emissions, the cement industry is trending towards using more SCMs (auxiliary materials, usually slag, fly ash, and recently newly developed calcined clays) in ordinary Portland cement (OPC) (Scrivener et al., Cement and Concrete Research, 114, 2018).

[0003] A common drawback of using high amounts of SCM in cement is that it results in relatively low early strength. Systems incorporating calcined clay and limestone (so-called LC cements, which use about 50% OPC) 3 The performance of cement in OPC is comparable to that of OPC in many aspects, such as long-term strength (Antoni et al., Cement and Concrete Research, 42, 2012) and durability (Scrivener et al., Advances in Civil Engineering Materials, 8, 2019). However, the early strength is relatively lower compared to OPC due to the lower amount of C3S derived from OPC, which contributes to the early strength.

[0004] WO2010026155 relates to a seeding technique (CSH seeding) to enhance the early age reaction of tricalcium silicate (also known as 3CaO SiO2 or C3S) and therefore improve early strength (Thomas et al., The Journal of Physical Chemistry C, 113, 2009). This technique has been proven to work, and recent products such as X-Seed® have also been found to be effective.

[0005] WO2015150473 discloses a cement containing OPC, limestone, calcium sulfate and CSH. However, the strength after 28 days is not satisfactory. Summary of the Invention [Problem to be solved by the invention]

[0006] Therefore, there is a continuing need for improved environmentally friendly construction material compositions. Against this background, it was an object of the present invention to provide a construction material composition that exhibits improved mechanical properties in terms of early and / or long-term strength according to the EN 197-1:2011 standard, compared to ordinary Portland cement, while using a comparable amount of Portland cement clinker. In particular, it was an object of the present invention to provide a construction material composition that exhibits early and / or long-term strength equivalent to that of OPC containing a higher amount of Portland cement clinker, while using a reduced amount of Portland cement clinker. It was also an object of the present invention to provide a construction material composition that exhibits higher early and / or long-term strength with a clinker content approximately equivalent to that of cement classes CEM III, CEM IV, and CEM V according to EN 197-1:2011. It was also an object of the present invention to provide a construction material composition, including a mortar, that exhibits early and / or long-term strength equivalent to or even improved from those having a normal Portland cement content, even with a reduced amount of Portland cement clinker. Furthermore, it was an object of the present invention to provide a construction material composition that complies with the Globally Harmonized System (GHS) and contains only harmless ingredients, with an emphasis on avoiding ingredients classified as GHS08 (serious health hazard) or GHS06 (acute toxicity).Finally, it was an object of the present invention to provide a process for producing a construction material composition that contains a reduced amount of Portland cement clinker, yet still has the same or even improved early and / or long-term strength. [Means for solving the problem]

[0007] Surprisingly, it has been found that at least one of these objectives is achieved by the claimed construction material composition, which as defined herein below has been found to exhibit improved mechanical properties in terms of early and / or long-term strength compared to ordinary Portland cement according to the EN 197-1:2011 standard, with comparable amounts of Portland cement clinker and with an amount of Portland cement clinker in the OPC lower than 55% by weight.

[0008] Accordingly, in a first aspect, the present invention provides a construction material composition comprising: a) Portland cement clinker in an amount of 15 to 55% by dry weight based on the total dry weight of the construction material composition; b) supplemental cementitious materials in an amount of 20 to 75% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 5 to 40% by dry weight based on the total dry weight of the construction material composition; d) a sulfate source selected from the group consisting of gypsum, basanitite, anhydrite, and mixtures thereof, in an amount of greater than 2.2% to 8% by weight of SO3, based on the total dry weight of the construction material composition; e) a hardening accelerator A containing particles of calcium and silicon in a molar ratio Ca / Si of 0.1 to 2.2, in an amount of 0.1 to 5% by weight relative to the total weight of CaO and SiO2 of the hardening accelerator A, based on the total dry weight of the construction material composition; The present invention relates to a construction material composition comprising:

[0009] Preferred embodiments of the components of the construction material composition are described in more detail below, it being understood that each preferred embodiment is suitable both by itself and in combination with other preferred embodiments.

[0010] In a preferred embodiment A1 of the first aspect, the supplemental cementitious material is selected from the group consisting of slag, fly ash, natural pozzolana, calcined clay, silica fume and mixtures thereof.

[0011] In a preferred embodiment A2 of the first aspect, the calcium carbonate phase is selected from limestone, dolomite, calcite, aragonite, vaterite and mixtures thereof.

[0012] In a preferred embodiment A3 of the first aspect, the total SO3 content and the total Al2O3 content, as determined by elemental analysis, are present in a weight ratio of 1:10 to 5:1.

[0013] In a preferred embodiment A4 of the first aspect, the Portland cement clinker and the supplemental cementitious material are present in a weight ratio of 2:1 to 1:5.

[0014] In a preferred embodiment A5 of the first aspect, the Portland cement clinker and limestone are present in a weight ratio of 4:1 to 1:2.

[0015] In a preferred embodiment A6 of the first aspect, the curing accelerator A further comprises a water-soluble polymer in an amount of 0.1 wt % to 50 wt % relative to the dry weight of the curing accelerator A.

[0016] In a preferred embodiment A7 of the first aspect, the curing accelerator A has the following empirical formula: a CaO,SiO2,b Al2O3,c H2O,d X,e W (wherein X is an alkali metal, W is an alkaline earth metal; 0.5≦a≦2.5, preferably 0.66≦a≦2.0, 0≦b≦1, preferably 0≦b≦0.1, 1≦c≦6, preferably 1≦c≦6.0, 0≦d≦1, preferably 0≦d≦0.4 or 0.2, 0≦e≦2, preferably 0≦e≦0.1) The present invention relates to a method for producing calcium silicate hydrate.

[0017] In a preferred embodiment A8 of the first aspect, the construction material composition comprises: a) Portland cement clinker in an amount of 40-55% by dry weight based on the total dry weight of the construction material composition; b) supplementary cementitious materials in an amount of 30-45% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 15 to 30% by dry weight, based on the total dry weight of the construction material composition; d) a sulfate source in an amount of 2.5 to 7% by weight of SO3 based on the total dry weight of the construction material composition; e) Accelerator A in an amount of 0.1 to 5% by weight based on the total dry weight of the construction material composition and the combined weight of CaO and SiO2 of Accelerator A; Includes:

[0018] In a preferred embodiment A9 of the first aspect, the construction material composition comprises: a) Portland cement clinker in an amount of 30-40% by dry weight based on the total dry weight of the construction material composition; b) supplementary cementitious materials in an amount of 30-45% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 20-30% by dry weight based on the total dry weight of the construction material composition; d) a sulfate source in an amount of 2.5 to 7% by weight of SO3 based on the total dry weight of the construction material composition; e) Accelerator A in an amount of 0.5 to 5% by weight based on the total dry weight of the construction material composition and the combined weight of CaO and SiO2 of Accelerator A; Includes:

[0019] In a preferred embodiment A10 of the first aspect, the construction material composition comprises: a) Portland cement clinker in an amount of 20-30% by dry weight based on the total dry weight of the construction material composition; b) supplementary cementitious materials in an amount of 30-50% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 20 to 40% by dry weight, based on the total dry weight of the construction material composition; d) a sulfate source in an amount of 2.5 to 7% by weight of SO3 based on the total dry weight of the construction material composition; e) Accelerator A in an amount of 1.0 to 5% by weight based on the total dry weight of the construction material composition and the combined weight of CaO and SiO2 of Accelerator A; Includes:

[0020] In a preferred embodiment A11 of the first aspect, the building material composition comprises from greater than 30% to 75% by dry weight of the supplemental cementitious material, based on the total dry weight of the building material composition.

[0021] In a preferred embodiment A12 of the first aspect, the construction material composition comprises: a) Portland cement clinker in an amount of 15 to 47% by dry weight based on the total dry weight of the construction material composition; b) supplemental cementitious materials in an amount of greater than 30% to 70% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 5 to 20% by dry weight based on the total dry weight of the construction material composition; d) a sulfate source in an amount of 2.5 to 7% by weight of SO3 based on the total dry weight of the construction material composition; e) Accelerator A in an amount of 0.1 to 5% by weight based on the total dry weight of the construction material composition and the combined weight of CaO and SiO2 of Accelerator A; Preferably, the supplemental cementitious material comprises at least two different supplemental cementitious materials.

[0022] In a preferred embodiment A13 of the first aspect, the construction material composition further comprises at least one additive, preferably the at least one additive selected from the group consisting of inorganic carbonates, alkali metal sulfates, polymeric dispersants, set accelerators, set retarders, thickeners and stabilizers, or a mixture of two or more thereof.

[0023] In a preferred embodiment A14 of the first aspect, the construction material composition further comprises at least one polymeric dispersant, in particular a polycarboxylate ether, a phosphorylated polycondensate or a dispersant containing sulfonic acid and / or sulfonate groups.

[0024] In a preferred embodiment A15 of the first aspect, the construction material composition further comprises at least one polymeric dispersant which is a sulfonic acid and / or sulfonate group-containing dispersant selected from the group consisting of lignosulfonates, melamine-formaldehyde sulfonate condensates, beta-naphthalenesulfonic acid condensates, sulfonated ketone-formaldehyde condensates, and copolymers comprising sulfo- and / or sulfonate-group-containing units and carboxylic acid and / or carboxylate-group-containing units.

[0025] In a preferred embodiment A16 of the first aspect, the construction material composition further comprises at least one hardening accelerator B.

[0026] In a second aspect, the present invention relates to the use of a hardening accelerator A comprising particles of calcium and silicon in a molar ratio Ca / Si of 0.1 to 2.2 in a construction material composition comprising up to 55% by dry weight of Portland cement clinker, based on the total dry weight of the construction material composition, wherein the hardening accelerator A is present in the construction material composition in an amount of 0.1 to 5% by weight relative to the combined weight of CaO and SiO2 of the hardening accelerator A, based on the total dry weight of the construction material composition.

[0027] In a preferred embodiment B1 of the second aspect, the construction material composition is as claimed.

[0028] In a third aspect, the present invention relates to a mortar or concrete comprising a construction material composition as claimed.

[0029] In a fourth aspect, the present invention relates to a process for producing a construction material composition as claimed, wherein the calcium carbonate phase is provided as a powder and the accelerator A is provided as a suspension.

[0030] In a fifth aspect, the present invention relates to a process for producing a construction material composition as claimed, wherein the addition of the accelerator A is carried out during or after the blending of components a) to d). DETAILED DESCRIPTION OF THE INVENTION

[0031] Before describing exemplary embodiments of the present invention in detail, definitions important for understanding the present invention are provided.

[0032] As used in this specification and the appended claims, the singular forms "a" and "an" also include the respective plural forms unless the context clearly dictates otherwise. In the context of the present invention, the terms "about" and "approximately" refer to a range of accuracy that a person skilled in the art would recognize while still ensuring the technical effect of the feature in question. This term typically refers to a deviation of ±20%, preferably ±15%, more preferably ±10%, and even more preferably ±5% from the indicated numerical value. The term "comprising" should be understood to be open-ended. For the purposes of the present invention, the term "consisting of" is considered a preferred embodiment of "comprising." Hereinafter, when a group is defined as including at least a certain number of embodiments, this preferably also means that the group consists of only these embodiments. Furthermore, the terms "first," "second," "third," "(a)," "(b)," "(c)," "(d)," etc. in this specification and claims are used to distinguish between similar components and do not necessarily dictate a sequential or chronological order. Accordingly, it is to be understood that the terms so used are interchangeable under appropriate circumstances, and that the embodiments described herein can be performed in orders other than those described or illustrated herein. When terms such as "first," "second," "third," or "(a)," "(b)," "(c)," "(d)," "i," "ii," etc. refer to steps in a method, or use, or assay, unless otherwise specified in this application, as described herein above or below, there is no time gap or inconsistency between the steps, i.e., the steps may be performed simultaneously, or there may be time gaps of seconds, minutes, hours, days, months, weeks, or even years between such steps. While specific methodologies, procedures, reagents, etc. are described herein, it is to be understood that the invention is not limited thereto, as these may vary. It is also to be understood that the terminology used herein is used only for the purpose of describing specific embodiments and is not intended to limit the scope of the invention, which is limited only by the appended claims.Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art.

[0033] The terms "early strength" and "long-term strength" are interchangeable with the terms "early compressive strength" and "long-term compressive strength," respectively.

[0034] Preferred embodiments of the construction material composition and its use are described in detail below. It should be understood that the preferred embodiments of the present invention are preferred either alone or in combination with each other.

[0035] As indicated above, the present invention, in one embodiment, comprises: a) Portland cement clinker in an amount of 15 to 55% by dry weight based on the total dry weight of the construction material composition; b) supplemental cementitious materials in an amount of 20 to 75% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 5 to 40% by dry weight based on the total dry weight of the construction material composition; d) a sulfate source selected from the group consisting of gypsum, basanitite, anhydrite, and mixtures thereof, in an amount of greater than 2.2% to 8% by weight of SO3, based on the total dry weight of the construction material composition; e) a hardening accelerator A containing particles of calcium and silicon in a molar ratio Ca / Si of 0.1 to 2.2, in an amount of 0.1 to 5% by weight relative to the total weight of CaO and SiO2 of the hardening accelerator A, based on the total dry weight of the construction material composition; The present invention relates to a construction material composition comprising:

[0036] When referring to weight percentages of compositions and ingredients contained therein, it should be understood that in accordance with the present invention, the total amount of ingredients does not exceed 100% (±1% to account for rounding).

[0037] It should be further understood that, according to the present invention, the term "Portland cement clinker" refers to the entire clinker phase, excluding the calcium sulfate phase. Portland cement clinker phases include alite (C3S), belite (C2S), brownmillerite (C4AF) or C3A and mixtures thereof.

[0038] In a preferred embodiment, the Portland cement clinker comprises primarily belite in an amount greater than 40% by weight, based on the total weight of the Portland cement clinker.

[0039] In one embodiment of the present invention, the Portland cement clinker according to component a) of the construction material composition is selected from clinker-containing materials comprising at least 65% by weight, preferably at least 80% by weight, more preferably at least 95% by weight of Portland cement clinker, based on the total weight of the clinker-containing materials used. In another preferred embodiment of the present invention, the Portland cement clinker according to component a) of the construction material composition is selected from clinker-containing materials comprising at least 65% by weight, preferably at least 80% by weight, more preferably at least 90% by weight, in particular at least 95% by weight of Portland cement clinker, based on the total weight of the clinker-containing materials. The clinker-containing material is ordinary Portland cement (OPC) according to DIN EN 197-1:2011-11. Preferred OPCs according to this standard are CEM I 42.5 N, CEM I 42.5 R, CEM I 52.5 N and CEM I 52.5 R or mixtures thereof in which at least 95% by weight is Portland cement clinker.

[0040] In one embodiment of the present invention, the construction material composition comprises Portland cement clinker in an amount of 15 to 55 dry weight %, preferably 20 to 55 dry weight % or 15 to 40 dry weight %, more preferably 15 to 47 dry weight %, or 25 to 50 dry weight %, or 40 to 55 dry weight %, or 30 to 40 dry weight %, or 20 to 30 dry weight %, based on the total dry weight of the construction material composition.

[0041] According to a preferred embodiment of the present invention, the construction material composition contains less than 40% by dry weight, preferably less than 35% by dry weight, more preferably less than 30% by dry weight, and especially less than 25% by dry weight of ingredients publicly known to be hazardous under GHS 08, based on the total dry weight of the construction material composition.More preferably, the construction material composition contains 0 to less than 40% by dry weight, preferably less than 0 to 35% by dry weight, more preferably less than 0 to 30% by dry weight, and especially less than 0 to 25% by dry weight of ingredients publicly known to be hazardous under GHS 08, based on the total dry weight of the construction material composition.

[0042] In this context, it is particularly preferred that the construction material composition comprises less than 40% by dry weight, preferably less than 35% by dry weight, more preferably less than 30% by dry weight, and in particular less than 25% by dry weight, of fine quartz (also known as powdered quartz), based on the total dry weight % of the construction material composition. Even more preferred, the construction material composition comprises 0 to less than 40% by dry weight, preferably less than 0 to 35% by dry weight, more preferably less than 0 to 30% by dry weight, and in particular less than 0 to 25% by dry weight, of fine quartz, based on the total dry weight % of the construction material composition.

[0043] The term "fine quartz" according to the present invention refers to fine quartz having a maximum grain size of up to 63 μm.

[0044] The construction material composition comprises the supplemental cementitious material in an amount of 20 to 75 dry weight %, preferably 20 to 55 dry weight %, more preferably 25 to 45 dry weight %, and even more preferably 30 to 45 dry weight %, based on the total dry weight of the construction material composition.

[0045] In another preferred embodiment of the present invention, the construction material composition comprises from more than 30% to 75% by dry weight, preferably from 35 to 72% by dry weight, more preferably from 45 to 71% by dry weight, even more preferably from 55 to 71% by dry weight, and especially from 65 to 70% by dry weight of the auxiliary cementitious material, based on the total dry weight of the construction material composition.

[0046] The supplemental cementitious material can be any suitable cementitious material. In one embodiment of the present invention, the supplemental cementitious material is selected from the group consisting of slag, fly ash, natural pozzolana, calcined clay, silica fume, and mixtures thereof.

[0047] Preferably, when the supplemental cementitious material is present in the construction material composition in an amount of more than 30% to 75% by dry weight, preferably 35 to 72% by dry weight, more preferably 45 to 71% by dry weight, even more preferably 55 to 71% by dry weight, and especially 65 to 70% by dry weight, based on the total dry weight of the construction material composition, at least two different supplemental cementitious materials are included. In this regard, preferably, the supplemental cementitious material comprises slag and a different supplemental cementitious material selected from the group consisting of fly ash, natural pozzolana, calcined clay, silica fume, and mixtures thereof. It is also preferred that the supplemental cementitious material comprises calcined clay and a different supplemental cementitious material selected from the group consisting of slag, fly ash, natural pozzolana, silica fume, and mixtures thereof. Preferably, the supplemental cementitious material comprises calcined clay and a different supplemental cementitious material selected from the group consisting of slag, fly ash, natural pozzolana, silica fume, and mixtures thereof.

[0048] When the supplemental cementitious material comprises at least two supplemental cementitious materials (i.e., SCM1 and SCM2), the weight ratio of SCM1 to SCM2 is preferably 3:1 to 1:3, more preferably 2:1 to 1:2, even more preferably 1.5:1 to 1:1.5, and in particular 1.2:1 to 1:1.2.

[0049] The slag can be industrial slag, i.e., waste from industrial processes, or synthetic slag. Since industrial slag is not always available in consistent quantities and quality, synthetic slag can be advantageous. Examples include blast furnace slag, electrolytic phosphorus slag, steel slag, and mixtures thereof.

[0050] Blast furnace slag (BFS) is a waste product of the steelmaking process. Other materials are granulated blast furnace slag (GBFS) and ground granulated blast furnace slag (GGBFS), which is finely ground granulated blast furnace slag. Ground granulated blast furnace slag varies in grinding degree and particle size distribution, which depends on the source and processing method, where grinding degree influences reactivity. The Blaine value is used as a parameter for grinding degree and is generally around 200-1000 m 2 kg -1 , preferably 300 to 600 m 2 kg -1 The finer the grinding, the higher the reactivity.

[0051] However, for purposes of this invention, the expression "blast furnace slag" is intended to include material obtained from all of the levels of processing, grinding, and quality mentioned (i.e., BFS, GBFS, and GGBFS). Blast furnace slag generally contains 30-45 wt.% CaO, about 4-17 wt.% MgO, about 30-45 wt.% SiO2, and about 5-15 wt.% Al2O3, typically about 40 wt.% CaO, about 10 wt.% MgO, about 35 wt.% SiO2, and about 12 wt.% Al2O3.

[0052] Electrothermal phosphorus slag is a waste product of electrothermal phosphorus production. It is less reactive than blast furnace slag and contains approximately 45-50% by weight CaO, approximately 0.5-3% by weight MgO, approximately 38-43% by weight SiO2, approximately 2-5% by weight Al2O3, and approximately 0.2-3% by weight Fe2O3, as well as fluorides and phosphates. Iron and steel slag is a waste product of various iron and steel manufacturing processes, with a highly variable composition.

[0053] The fly ash can be lignite fly ash and anthracite fly ash. Fly ash is produced, in particular, when burning coal in power plants. Class C fly ash (lignite fly ash) contains about 10% by weight of CaO according to WO 08 / 012438, while Class F fly ash (anthracite fly ash) contains less than 8% by weight, preferably less than 4% by weight, and generally about 2% by weight of CaO.

[0054] Natural pozzolans may be selected from tuff, tuff and volcanic ash, natural and synthetic zeolites and mixtures thereof.

[0055] Clay is the colloquial name for fine-grained earthy materials that become plastic when wetted with water. There are many types, most of which are composed of phyllosilicate minerals with varying amounts of water trapped within their mineral structure. Many types of clay minerals are known. Some of the more common types include kaolinite, illite, chlorite, vermiculite, and smectite, also known as montmorillonite, the latter two of which are notable for their ability to adsorb water.

[0056] Chemically, clays are typically hydrous aluminum silicates containing alkali metals, alkaline earth metals, and / or iron. Clay minerals consist of interlocking silicate sheets combined with secondary sheet-like aggregates of metal atoms, oxygen, and hydroxyls, forming 1:1 minerals such as kaolinite. Sometimes, the latter sheet-like structures are sandwiched between two silica sheets, forming 2:1 minerals such as vermiculite. Structurally, clay minerals consist of planes of cations arranged in sheets that can be tetrahedral or octahedral coordinated (with oxygen), which are then arranged in layers. These are often described as 2:1 when they contain units composed of two layers of tetrahedral sheets and one layer of octahedral sheets, and as 1:1 when they contain units of alternating tetrahedral and octahedral sheets. In addition, some 2:1 clay minerals have interlayer sites between consecutive 2:1 units that can be occupied by interlayer cations (often hydrated). Clay minerals are classified by layer type, and even within the same layer type, they are divided into groups based on the charge x per structural formula (Guggenheim S. et al., Clays and Clay Minerals, 54(6), 761-772, 2006). The charge x per structural formula is the net negative charge per layer and is expressed as a positive number. They are further subdivided into subgroups based on their dioctahedral or trioctahedral characteristics, and finally, by mineral species based on chemical composition, e.g., x≒0: pyrophyllite group, x≒0.2 to 0.6: smectite group, such as montmorillonite, nontronite, saponite or hectorite, x≒0.6~0.9: vermiculite group, x≒1.8~2: brittle micas, e.g., clintonite, anandite, kinoshitalite It is classified as follows.

[0057] In one embodiment, the supplemental cementitious material is a calcined clay (also referred to as a calcined clay). Calcined, as used herein, refers to heating to an elevated temperature in air or oxygen. The heat-treated clay material is a calcined clay produced at a temperature between 500°C and 900°C. According to another embodiment of the present invention, the heat-treated clay material is a calcined clay produced at a temperature between 500°C and 750°C. According to another embodiment of the present invention, the heat-treated clay material is produced by heat-treating the clay material, separate from the other components of the supplemental cementitious material, at a temperature sufficient to a) dehydroxylate the clay material to a crystallographically amorphous material, and b) prevent the formation of refractory aluminosilicate phases, such as mullite. It has been found preferable to use clays that have been calcined by heat-treating the clay at a temperature sufficient to a) dehydroxylate the clay to a crystallographically amorphous material, and b) prevent the formation of refractory crystalline aluminosilicate phases, such as mullite. The temperature that meets these requirements varies depending on the clay material, but is typically between 500 and 750°C if the clay is heated before mixing with the limestone.

[0058] Metakaolin is sometimes called calcined clay. Metakaolin is produced when kaolin is dehydrated. Kaolin releases physically bound water at 100-200°C, while dehydroxylation occurs at 500-800°C, causing the lattice structure to collapse and metakaolin (Al2SiO7) to form. Thus, pure metakaolin contains approximately 54% SiO2 and 46% Al2O3 by weight.

[0059] Fumed silica (i.e., silica fume) is produced by reacting chlorosilanes, such as silicon tetrachloride, in a hydrogen / oxygen flame. Fumed silica has a viscosity of 50-600 m 2 g -1 It is an amorphous SiO2 powder with a particle size of 5 to 50 nm and a specific surface area of ​​1000 nm.

[0060] A typical SCM is composed of an amorphous component and some mineral crystalline phases (as detected by XRD). Most of the reactive moieties are derived from the amorphous component. Chemically, SCM is primarily composed of Al2O3, SiO2, CaO, and alkali (Na2O and / or K2O). In this context, reactivity refers to the material's ability to react with HO alone or with Ca(OH)2 in the system, generating heat and developing strength.

[0061] The specific characteristics are listed in the table below (calorimetric reactivity is based on Li, X., et al. (2018), "Reactivity tests for supplementary cementitious materials: RILEM TC 267-TRM phase 1," Materials and Structures 51(6):151).

[0062] [Table 1]

[0063] The construction material composition comprises a calcium carbonate phase in an amount of 5 to 40 dry weight %, preferably 10 to 40 dry weight %, or 10 to 20 dry weight %, or 20 to 30 dry weight %, or 30 to 40 dry weight %, preferably 15 to 30 dry weight %, based on the total dry weight of the construction material composition. In another preferred embodiment of the present invention, the construction material composition comprises a calcium carbonate phase in an amount of 5 to 35 dry weight %, preferably 5 to 20 dry weight %, more preferably 5 to 10 dry weight % or 6 to 17 dry weight %, based on the total dry weight of the construction material composition.

[0064] The calcium carbonate phase may be any suitable calcium carbonate-containing phase. As used herein, the term "calcium carbonate phase" refers to a solid material that is at least 75% by weight, preferably at least 80% by weight, more preferably at least 85% by weight, and especially at least 90% by weight, composed of carbonate minerals such as calcite (CaC0), aragonite (CaC0), or vaterite (CaC0), or dolomite (CaMg(C0)) minerals.

[0065] In one embodiment of the present invention, the calcium carbonate phase is selected from the group consisting of limestone, dolomite, chalk and mixtures thereof.

[0066] In a preferred embodiment of the present invention, the calcium carbonate phase is selected from the group consisting of limestone, dolomite and mixtures thereof, in particular the calcium carbonate phase is limestone.

[0067] The calcium carbonate phase may be provided as a powder.

[0068] The construction material composition comprises a sulfate source in an amount of greater than 2.2% to 8% by weight of SO3, preferably in an amount of 2.5 to 7% by weight of SO3, based on the total dry weight of the construction material composition. The sulfate source according to the present invention is selected from the group consisting of gypsum, basanitite, anhydrite, and mixtures thereof.

[0069] It should be understood that the sulfate source according to the present invention refers to an additionally added sulfate source, and not to the calcium sulfate contained in the OPC. Thus, a construction material composition according to the present invention does not necessarily include an additionally added sulfate source.

[0070] Typically, gypsum rock is mined or quarried and then sent to a manufacturing facility. Manufacturers who receive the quarried gypsum crush larger pieces before further processing. The crushed rock is then ground into a fine powder and heated to 120–160°C in a process called "calcination," which drives off three-quarters of the chemically bound water, resulting in "calcined gypsum." Further heating of gypsum at temperatures slightly above 200°C produces anhydrite (CaSO4), which sets and hardens very slowly when mixed with water. Calcined gypsum (hemihydrate or anhydrite), CaSO4·1 / 2H2O, or CaSO4, is then used as the main component of gypsum plaster, plaster of Paris, gypsum board, and other gypsum products. Various calcination procedures produce alpha and beta hemihydrate gypsum. β-Calcium sulfate hemihydrate is produced by rapid heating in open-air equipment, resulting in the rapid evaporation of water and the formation of voids in the resulting anhydrite. Alpha hemihydrate is obtained by dehydrating gypsum in a sealed autoclave. The resulting crystals are dense, so the resulting inorganic binder requires less water for rehydration than beta hemihydrate.

[0071] Common commercially available natural sources of gypsum often contain up to 20% or more clay minerals and other impurities, which reduce the amount of calcium sulfate accordingly.

[0072] The construction material composition comprises a hardening accelerator A containing particles of calcium and silicon in a molar ratio Ca / Si of 0.1 to 2.2 in an amount of 0.1 to 5 wt % relative to the total weight of CaO and SiO2 of the hardening accelerator A, based on the total dry weight of the construction material composition.

[0073] In one embodiment of the present invention, the curing accelerator A is included in an amount of 0.1 to 5%, or 0.5 to 5%, or 1.0 to 5.0% of the total weight of CaO and SiO2 of the curing accelerator A, based on the total dry weight of the construction material composition.

[0074] According to the present invention, the hardening accelerator A comprises particles of calcium and silicon in a molar ratio Ca / Si of 0.1 to 2.2, preferably 0.5 to 2.2, and particularly 1.5 to 2.2. In one embodiment of the present invention, the hardening accelerator A comprises particles of calcium and silicon in a molar ratio Ca / Si of 0.6 to 1.5 or 1.5 to 2.2.

[0075] In one embodiment of the present invention, the hardening accelerator A comprises particles of calcium and silicon in a molar ratio Ca / Si of 0.1 to 2.2 in an amount of 20 to 99.9% by weight, preferably 30 to 99.5% by weight, more preferably 40 to 90% by weight, and in particular 45 to 85% by weight, based on the dry weight of the hardening accelerator A.

[0076] It should be understood that the particles according to the present invention, in which calcium and silicon have a molar ratio Ca / Si of 0.1 to 2.2, do not include calcium salts selected from the group consisting of calcium chloride, calcium nitrate, calcium formate, calcium acetate, calcium bicarbonate, calcium bromide, calcium citrate, calcium chlorate, calcium gluconate, calcium hydroxide, calcium oxide, calcium hypochlorite, calcium iodate, calcium iodide, calcium lactate, calcium nitrite, calcium phosphate, calcium propionate, calcium sulfate, calcium sulfate hemihydrate, calcium sulfate dihydrate, calcium tartrate, calcium sulfamate, calcium maleate, calcium fumarate, calcium aluminate, calcium methanesulfonate, and do not include silicon dioxide in the form of microsilica, silica fume, or amorphous silica.

[0077] The particles according to the present invention, in which calcium and silicon have a molar ratio Ca / Si of 0.1 to 2.2, can be characterized, for example, by electron microscopy (TEM / SEM), and the molar ratio can be determined using EDX elemental analysis in an electron microscope such as a TEM or SEM.

[0078] In one embodiment of the present invention, the curing accelerator A further comprises a water-soluble polymer in an amount of 0.1 wt % to 50 wt % with respect to the dry weight of the curing accelerator A.

[0079] The water-soluble polymer may be a comb polymer.

[0080] In one embodiment of the present invention, the comb polymer comprises, as units having acid functionality, units of the general formula (Ia), (Ib), (Ic) and / or (Id): [ka] (In the formula, R 1 is H or an unbranched or branched C1-C4 alkyl group, CH2COOH or CH2CO-XR 2 , preferably H or CH3; X is NH-(C n H 2n ), O(C n H 2n ) (n=1, 2, 3 or 4, and a nitrogen atom or an oxygen atom is bonded to a CO group) or a chemical bond, preferably X is a chemical bond or O(C n H 2n ) and; R 2 is OM, PO3M2 or O-PO3M2, where R 2 is OM, then X is a chemical bond); [ka] (In the formula, R 3 is H or an unbranched or branched C1-C4 alkyl group, preferably H or CH3; n is 0, 1, 2, 3 or 4, preferably 0 or 1; R 4 is PO3M2 or O-PO3M2); [ka] (In the formula, R 5 is H or an unbranched or branched C1-C4 alkyl group, preferably H; Z is O or NR 7, preferably O; R 7 is H, (C n H 2n )-OH, (C n H 2n )-PO3M2, (C n H 2n )-OPO3M2, (C6H4)-PO3M2 or (C6H4)-OPO3M2, n is 1, 2, 3 or 4, preferably 1, 2 or 3; [ka] (In the formula, R 6 is H or an unbranched or branched C1-C4 alkyl group, preferably H; Q is NR 7 or O, preferably O; R 7 is H, (C n H 2n )-OH, (C n H 2n )-PO3M2, (C n H 2n )-OPO3M2, (C6H4)-PO3M2 or (C6H4)-OPO3M2, n is 1, 2, 3 or 4, preferably 1, 2 or 3; Each M is independently H or a cation equivalent. It contains at least one structural unit of the formula:

[0081] In one embodiment of the present invention, the comb polymer comprises, as units having polyether side chains, units of the general formula (IIa), (IIb), (IIc) and / or (IId): [ka] (In the formula, R 10 , R 11 and R 12 are, independently of each other, H or an unbranched or branched C1-C4 alkyl group; Z is O or S; E is an unbranched or branched C1-C6 alkylene group, a cyclohexylene group, CH2-C6H 10 , 1,2-phenylene, 1,3-phenylene or 1,4-phenylene; G is O, NH, or CO—NH; or E and G together form a chemical bond; A is C x H 2x (x=2, 3, 4 or 5, preferably 2 or 3) or CH2CH(C6H5); n is 0, 1, 2, 3, 4 or 5, preferably 0, 1 or 2; a is an integer of 2 to 350, preferably 5 to 150; R 13 is H, an unbranched or branched C1-C4 alkyl group, CO—NH2 and / or COCH3); [ka] (In the formula, R 16 , R 17 and R 18 are, independently of each other, H or unbranched or branched C1-C4 alkyl; E is an unbranched or branched C1-C6 alkylene group, a cycloalkylene group, CH2-C6H 10 , 1,2-phenylene, 1,3-phenylene, or 1,4-phenylene, or a chemical bond; A is C x H 2x (x=2, 3, 4 or 5, preferably 2 or 3) or CH2CH(C6H5); n is 0, 1, 2, 3, 4 and / or 5, preferably 0, 1 or 2; L is C x H 2x (x=2, 3, 4 or 5, preferably 2 or 3) or CH2-CH(C6H5); a is an integer of 2 to 350, preferably 5 to 150; d is an integer of 1 to 350, preferably 5 to 150; R 19 is H or an unbranched or branched C1-C4 alkyl group; R 20 is H or an unbranched C1-C4 alkyl group); [ka] (In the formula, R 21 , R 22 and R 23 are, independently of each other, H or unbranched or branched C1-C4 alkyl; W, O, NR 25 or N; Y is W=O or NR 25 1 if W=N, and 2 if W=N; A is C x H 2x (x=2, 3, 4 or 5, preferably 2 or 3) or CH2CH(C6H5); a is an integer of 2 to 350, preferably 5 to 150; R 24 is H or an unbranched or branched C1-C4 alkyl group; R 25 is H or an unbranched or branched C1-C4 alkyl group; [ka] (In the formula, R 6 is H or an unbranched or branched C1-C4 alkyl group; Q is NR 10 , N or O; Y is W=O or NR 10 1 if W=N, and 2 if W=N; R 10 is H or an unbranched or branched C1-C4 alkyl group; A is C x H 2x (x=2, 3, 4 or 5, preferably 2 or 3) or CH2C(C6H5)H; R 24 is H or an unbranched or branched C1-C4 alkyl group; M is H or a cation equivalent; and a is an integer of 2 to 350, preferably 5 to 150).

[0082] In one embodiment of the invention, the comb polymer comprises: (a) at least one amine compound represented by formula (IIa), 10 and R 12 is H and R 11 is H or CH3, E and G together form a chemical bond, and A is C x H 2x (x=2 and / or 3), a is 3 to 150, and R 13 is H or an unbranched or branched C1-C4 alkyl group; and / or (b) at least one amine compound represented by formula (IIb), wherein R 16 and R 18 is H and R 17 is H or CH3, E is a branched or unbranched C1-C6 alkylene group, A is C x H 2x (x=2 and / or 3), and L is C x H 2x (x=2 and / or 3), a is an integer of 2 to 150, d is an integer of 1 to 150, and R 19 is H or a branched or unbranched C1-C4 alkyl group, and R 20 is H or a branched or unbranched C1-C4 alkyl group; and / or (c) at least one amine compound represented by formula (IIc), wherein R 21 and R 23 is H and R 22 is H or CH3, and A is C x H 2x (x=2 and / or 3), a is an integer from 2 to 150, and R 24is H or a branched or unbranched C1-C4 alkyl group; and / or (d) at least one amine compound represented by formula (IId), wherein R 6 is H, Q is O, and R 7 is (C n H 2n )-O-(AO) a -R 9 and n is 2 and / or 3, and A is C x H 2x (x=2 and / or 3), a is an integer from 1 to 150, and R 9 is H or a branched or unbranched C1-C4 alkyl group) The polyether side chains include:

[0083] In one embodiment of the present invention, the comb polymer comprises at least one structural unit of formula (IIa) and / or (IIc).

[0084] In one embodiment of the present invention, the comb polymer comprises units of formula (I) and (II).

[0085] In one embodiment of the present invention, the comb polymer comprises structural units of formula (Ia) and (IIa).

[0086] In one embodiment of the present invention, the comb polymer comprises structural units of formula (Ia) and (IIc).

[0087] In one embodiment of the present invention, the comb polymer comprises structural units of formula (Ic) and (IIa).

[0088] In one embodiment of the present invention, the comb polymer comprises structural units of formulae (Ia), (Ic) and (IIa).

[0089] In one embodiment of the present invention, the comb polymer comprises (i) anionic or anion-forming structural units derived from acrylic acid, methacrylic acid, maleic acid, hydroxyethyl acrylate phosphate ester and / or hydroxyethyl methacrylate phosphate ester, hydroxyethyl acrylate phosphate diester and / or hydroxyethyl methacrylate phosphate diester, and (ii) C1-C4 alkyl-polyethylene glycol acrylate ester, polyethylene glycol acrylate ester, C1-C4 alkyl-polyethylene glycol methacrylate ester, polyethylene glycol methacrylate ester, C1-C4 alkyl-polyethylene glycol and polyether side chain structural units derived from ethylene glycol acrylate, polyethylene glycol acrylate, vinyloxy-C2-C4 alkylene-polyethylene glycol, vinyloxy-C2-C4 alkylene-polyethylene glycol C1-C4 alkyl ether, allyloxypolyethylene glycol, allyloxypolyethylene glycol C1-C4 alkyl ether, methallyloxypolyethylene glycol, methallyloxypolyethylene glycol C1-C4 alkyl ether, isoprenyloxypolyethylene glycol and / or isoprenyloxypolyethylene glycol C1-C4 alkyl ether.

[0090] In one embodiment of the invention, the comb polymer comprises: (i) hydroxyethyl acrylate phosphate ester and / or hydroxyethyl methacrylate phosphate ester, and (ii) C1-C4 alkyl-polyethylene glycol acrylate ester and / or C1-C4 alkyl-polyethylene glycol methacrylate ester; or (i) acrylic acid and / or methacrylic acid, and (ii) C1-C4 alkyl-polyethylene glycol acrylate and / or C1-C4 alkyl-polyethylene glycol methacrylate; or (i) acrylic acid, methacrylic acid, and / or maleic acid, and (ii) vinyloxy-C2-C4 alkylene-polyethylene glycol, allyloxy-polyethylene glycol, methallyloxy-polyethylene glycol, and / or isoprenyloxy-polyethylene glycol The compound includes structural units (i) and (ii) derived from

[0091] In this connection, the comb polymer preferably comprises (i) hydroxyethyl methacrylate phosphate ester, and (ii) C1-C4 alkyl-polyethylene glycol methacrylate ester or polyethylene glycol methacrylate ester; or (i) methacrylic acid, and (ii) a C1-C4 alkyl-polyethylene glycol methacrylate or a polyethylene glycol methacrylate; or (i) acrylic acid and maleic acid, and (ii) vinyloxy-C2-C4 alkylene-polyethylene glycol; or (i) acrylic acid and maleic acid, and (ii) isoprenyloxy-polyethylene glycol; or (i) acrylic acid, and (ii) vinyloxy-C2-C4 alkylene-polyethylene glycol; or (i) acrylic acid, and (ii) isoprenyloxy-polyethylene glycol; or (i) acrylic acid, and (ii) methallyloxy-polyethylene glycol; or (i) maleic acid, and (ii) isoprenyloxy-polyethylene glycol; or (i) maleic acid, and (ii) allyloxy-polyethylene glycol; or (i) maleic acid, and (ii) methallyloxy-polyethylene glycol The compound includes structural units (i) and (ii) derived from

[0092] In one embodiment of the present invention, the molar ratio of structural units (I):(II) is 1:4 to 15:1, more specifically 1:1 to 10:1.

[0093] In one embodiment of the present invention, the comb polymer comprises structural units (III) and (IV): [ka] (In the formula, T is a substituted or unsubstituted phenyl or naphthyl group, or a substituted or unsubstituted heteroaromatic group having 5 to 10 ring atoms, one or two of which are heteroatoms selected from N, O, and S; n is 1 or 2; B is N, NH, or O, with the proviso that n is 2 when B is N, and 1 when B is NH or O; A is unbranched or branched alkylene having 2 to 5 carbon atoms or CH2CH(C6H5); a is an integer from 1 to 300; R 25 is H, branched or unbranched C1-C 10 an alkyl group, a C5-C8 cycloalkyl group, an aryl group, or a heteroaryl group having 5 to 10 ring atoms, one or two of which are heteroatoms selected from N, O, and S; a phosphorylated polycondensate comprising: The structural unit (IV) is composed of the structural units (IVa) and (IVb): [ka] (In the formula, D is a substituted or unsubstituted phenyl or naphthyl group, or a substituted or unsubstituted heteroaromatic group having 5 to 10 ring atoms, one or two of which are heteroatoms selected from N, O, and S; E is N, NH, or O, with the proviso that m is 2 when E is N, and m is 1 when E is NH or O; A is unbranched or branched alkylene having 2 to 5 carbon atoms or CH2CH(C6H5); b is an integer from 0 to 300; M is, independently in each occurrence, H or a cation equivalent; [ka] (In the formula, V is a substituted or unsubstituted phenyl or naphthyl group, and R 8 , OH, OR 8 , (CO)R 8 , COOM, COOR 8 , SO3R 8 and NO2; R 7 is COOM, OCH2COOM, SO3M or OPO3M2; M is H or a cation equivalent; and R 8 is C1-C4 alkyl, phenyl, naphthyl, phenyl-C1-C4 alkyl or C1-C4 alkylphenyl) is selected from.

[0094] In this regard, in formula III, T is preferably a substituted or unsubstituted phenyl or naphthyl group, and A is C x H 2x (x=2 and / or 3), a is an integer from 1 to 150, and R 25 is H or branched or unbranched C1-C 10 It is an alkyl group.

[0095] In this regard, in formula IVa, D is preferably a substituted or unsubstituted phenyl or naphthyl group, E is NH or O, and A is C x H 2x (x=2 and / or 3), and b is an integer of 1 to 150.

[0096] In this context, T and / or D are preferably phenyl or naphthyl substituted with one or two C1-C4 alkyl, hydroxyl or two C1-C4 alkoxy groups.

[0097] In this context, V is preferably phenyl or naphthyl substituted with one or two C1-C4 alkyl, OH, OCH3 or COOM, and R 7 is COOM or OCH2COOM.

[0098] In this context, the polycondensate has the formula (V): [ka] (In the formula, R 5 and R 6 may be the same or different and are H, CH3, COOH, or a substituted or unsubstituted phenyl or naphthyl group, or a substituted or unsubstituted heteroaromatic group having 5 to 10 ring atoms, one or two of which are heteroatoms selected from N, O, and S. The further structural unit comprises:

[0099] In one embodiment of the present invention, R 5 and R 6 may be the same or different and are H, CH or COOH, more particularly H, or R 5 and R 6 One of the groups is H and the other is CH3.

[0100] In one embodiment of the present invention, the molar weight of the polyether side chains is ≧200 g / mol, preferably ≧300 g / mol and ≦6000 g / mol, preferably ≦5000 g / mol.

[0101] In one embodiment of the present invention, the molar weight of the polyether side chains is in the range of 200 to 6000 g / mol, more specifically in the range of 500 to 5000 g / mol, more preferably in the range of 1000 to 5000 g / mol.

[0102] In one embodiment of the present invention, the charge density of the comb polymer is in the range of 0.5 meq / g to 5 meq / g polymer, preferably in the range of 0.6 meq / g to 3 meq / g polymer.

[0103] In a further embodiment, the water-soluble polymer is a copolymer comprising sulfo- and / or sulfonate-group-containing units and carboxylic acid- and / or carboxylate-group-containing units. In an embodiment, the sulfo- or sulfonate-group-containing units are units derived from vinyl sulfonic acid, methallyl sulfonic acid, 4-vinylphenyl sulfonic acid, or units of the formula: [ka] (In the formula, R 1 represents hydrogen or methyl, R 2 , R 3 and R 4 are each independently H, a linear or branched C1-C6 alkyl, or a C6-C 14 represents aryl; M represents hydrogen, a metal cation, preferably a monovalent or divalent metal cation or an ammonium cation; a represents 1 or (1 / valence of cation), preferably 1 / 2 or 1. is a sulfonic acid-containing structural unit.

[0104] Preferred sulfo group-containing units are those derived from monomers selected from vinyl sulfonic acid, methallylsulfonic acid and 2-acrylamido-2-methylpropylsulfonic acid (AMPS), with AMPS being particularly preferred.

[0105] The carboxylic acid or carboxylate-containing units are preferably derived from monomers selected from acrylic acid, methacrylic acid, 2-ethylacrylic acid, vinylacetic acid, crotonic acid, maleic acid, fumaric acid, itaconic acid, citraconic acid, especially acrylic acid and methacrylic acid.

[0106] The sulfo-containing copolymers generally have a molecular weight M as determined by aqueous gel permeation chromatography. wis in the range of 1000 g / mol to 50,000 g / mol, preferably in the range of 1500 g / mol to 30,000 g / mol.

[0107] In one embodiment, the molar ratio of sulfo group-containing units to carboxylic acid-containing units is generally in the range of 5:1 to 1:5, preferably in the range of 4:1 to 1:4.

[0108] Preferably, the (co)polymer having carboxylic acid and / or carboxylate groups and sulfonic acid and / or sulfonate groups has a polymer backbone of carbon atoms, and the ratio of the sum of the number of carboxylic acid and / or carboxylate groups and sulfonic acid and / or sulfonate groups to the number of carbon atoms in the polymer backbone is in the range of 0.1 to 0.6, preferably in the range of 0.2 to 0.55. Preferably, the (co)polymer is obtainable by free radical (co)polymerization, and the carboxylic acid and / or carboxylate groups are derived from monocarboxylic acid monomers. Preferred (co)polymers are obtainable by free radical (co)polymerization, and the carboxylic acid and / or carboxylate groups are derived from the monomers acrylic acid and / or methacrylic acid, and the sulfonic acid and / or sulfonate groups are derived from 2-acrylamido-2-methylpropanesulfonic acid. Preferably, the weight average molecular weight M of the (co)polymer is w is 8,000 g / mol to 200,000 g / mol, preferably 10,000 to 50,000 g / mol. The weight ratio of the one or more (co)polymers to calcium silicate hydrate is preferably 1 / 100 to 4 / 1, more preferably 1 / 10 to 2 / 1, and most preferably 1 / 5 to 1 / 1.

[0109] In one embodiment of the invention, the water-soluble polymer is Copolymers comprising structural units of the formulae (Ia) and (IIa), in particular copolymers comprising structural units derived from acrylic and / or methacrylic acid and ethoxylated hydroxyalkyl vinyl ethers, such as ethoxylated hydroxybutyl vinyl ether; Copolymers comprising structural units of the formulae (Ia), (Id) and (IIa), in particular copolymers comprising structural units derived from acrylic acid and / or methacrylic acid, maleic acid and ethoxylated hydroxyalkyl vinyl ethers, such as ethoxylated hydroxybutyl vinyl ether; Copolymers comprising structural units of the formulae (Ia) and (IIc), in particular acrylic and / or methacrylic acid and copolymers of acrylic and / or methacrylic acid with C1-C 12 an ester of alkyl-terminated polyethylene glycol or a copolymer containing structural units derived from polyethylene glycol; Polycondensates comprising structural units of the formulae (III), (IVa) and (V), in particular condensates of ethoxylated phenol, phenoxy-C2-C6 alkanol phosphate and formaldehyde; homopolymers containing sulfo and / or sulfonate group-containing units or carbonate and / or carboxylate group-containing units; Copolymers containing sulfo and / or sulfonate group-containing units and carbonate and / or carboxylate group-containing units; and / or Polyacrylic acid; and These salts and combinations of two or more of these water-soluble polymers is selected from.

[0110] In one embodiment of the present invention, the hardening accelerator A comprises at least one further dispersant selected from the group consisting of lignosulfonates, melamine-formaldehyde sulfonate condensates, β-naphthalenesulfonic acid condensates, phenolsulfonic acid condensates and sulfonated ketone-formaldehyde condensates.

[0111] In one embodiment of the present invention, the accelerator A comprises particles of calcium silicate, preferably calcium silicate hydrate (also referred to as CSH). The calcium silicate hydrate may also contain foreign ions such as magnesium and aluminum. The calcium silicate hydrate can preferably be represented in terms of its composition by the following empirical formula: a CaO,SiO2,b Al2O3,c H2O,d X,e W (wherein X is an alkali metal, W is an alkaline earth metal; 0.5≦a≦2.5, preferably 0.66≦a≦2.0, 0≦b≦1, preferably 0≦b≦0.1, 1≦c≦6, preferably 1≦c≦6.0, 0≦d≦1, preferably 0≦d≦0.4 or 0.2, 0≦e≦2, preferably 0≦e≦0.1).

[0112] Calcium silicate hydrate (also called CSH) can be obtained by reacting a calcium compound with a silicate compound, preferably in the presence of a polycarboxylate ether (PCE). Products of this type containing calcium silicate hydrate are described, for example, in WO 2010 / 026155 A1, WO 2016097181, WO 2014 / 114784 or WO 2014 / 114782.

[0113] CSH can be provided, for example, as low-density CSH, CSH gel, or CSH seed crystals. Preferably, the size of the CSH seed crystals is small, and can be adjusted, for example, by grinding the CSH. CSH seed crystals having an average diameter of less than 10 μm, preferably less than 2 μm, and particularly less than 1 μm, as determined by laser diffraction and data analysis according to Mie theory in accordance with ISO 13320:2009, are preferred.

[0114] The moisture content of the powdered CSH-based accelerator A is preferably 0.1% to 5.5% by weight based on the total weight of the powder sample. The moisture content is measured by placing the sample in a drying chamber at 80°C until the sample weight becomes constant. The difference in the weight of the sample before and after drying is the weight of the water contained in the sample. The moisture content (%) is calculated by dividing the weight of the water contained in the sample by the weight of the sample.

[0115] The calcium silicate hydrate is preferably provided as an aqueous suspension. The water content of the aqueous suspension is preferably 10% to 95% by weight, preferably 40% to 90% by weight, more preferably 50% to 85% by weight, each expressed as a percentage of the total weight of the aqueous suspension sample. The water content is determined using a drying chamber in the same manner as described above.

[0116] Curing accelerator A can be provided in solid or liquid form. When provided as a solid, curing accelerator A is preferably in powder form. A suitable liquid form of curing accelerator A can be an aqueous solution or an aqueous suspension. The solid content of the liquid form ranges from 1 to 60% by weight, preferably 5 to 50% by weight, and more preferably 7 to 40% by weight, based on the total weight of the liquid form. The solid content of the liquid form can be determined by drying in a drying oven at 150°C until the weight becomes constant, and the difference in the determined weight is considered to be the proportion of water (including water bound to the solids in the suspension). When applied in liquid form, curing accelerator A is preferably an aqueous suspension.

[0117] Typically, a suspension containing calcium silicate hydrate in finely dispersed form is obtained by reacting a calcium compound with a silicate compound. This suspension effectively accelerates the hardening process of hydraulic binders, especially ordinary Portland cement. This suspension can be dried to a powder in a conventional manner, for example by spray drying or drum drying.

[0118] Typically, the calcium silicate hydrate is present in the composition in the form of foshagite, hillebrandite, xonotlite, cat stone, clinotobermorite, 9 Å-tobermorite (riversidelite), 11 Å-tobermorite, 14 Å-tobermorite (prombierite), djennite, metagenite, calcium chondrodite, afwillite, α-CSH, dell'aite, jaffeite, rosenhahnite, kilalaite and / or suornite. More preferably, the calcium silicate hydrate is present in the composition, preferably the aqueous accelerator suspension, in the form of xonotlite, 9 Å-tobermorite (riversidelite), 11 Å-tobermorite, 14 Å-tobermorite (prombierite), djennite, metagenite, afwillite and / or jaffeite.

[0119] In one embodiment of the invention, the particle size d(50) of the hardening accelerator A in liquid form is less than 5 μm, preferably less than 2 μm, more preferably less than 1 μm, in particular less than 500 nm, measured by light scattering using a MasterSizer® 3000 from Malvern in accordance with DIN ISO 13320:2009.

[0120] In a preferred embodiment of the invention, the particle size d(50) of the hardening accelerator A in liquid form is less than 2 μm, more preferably less than 1 μm, in particular less than 500 nm, measured by light scattering using a MasterSizer® 3000 from Malvern in accordance with DIN ISO 13320:2009.

[0121] In one embodiment of the present invention, the CSH is in the form of powder particles having a diameter of less than 150 μm, said powder particles comprising primary particles of calcium silicate hydrate having a diameter of less than 200 nm, or - Particle morphology with particle size distribution d(50) < 200 nm Available at.

[0122] Without wishing to be bound by any theory, it is believed that the small particle size of calcium silicate hydrate makes it particularly effective as a set accelerator.

[0123] In one embodiment of the present invention, the set accelerator A comprises calcium silicate hydrate, which is obtained in the form of a suspension by a process α) by reacting a water-soluble calcium compound with a water-soluble silicate compound, the reaction of which is carried out in the presence of an aqueous solution containing at least one polymeric dispersant comprising anionic and / or anion-forming groups and polyether side chains, preferably polyalkylene glycol side chains, or β) by reacting a calcium compound, preferably a calcium salt, most preferably a water-soluble calcium salt, with a silicon dioxide-containing component under alkaline conditions, the reaction being carried out in the presence of an aqueous solution of at least one polymeric dispersant comprising anionic and / or anion-forming groups and polyether side chains, preferably polyalkylene glycol side chains. In a further step, the suspension obtained by process α) or β) is dried in a conventional manner, for example by spray drying, to obtain the calcium silicate hydrate as a powder product.

[0124] Examples of processes α and β) are given in the international patent application published as WO 2010 / 026155 A1.

[0125] In one embodiment of the present invention, the set accelerator A comprises calcium silicate hydrate obtained in the form of a suspension by a process α-1) in which the water-soluble calcium compound is selected from calcium hydroxide and / or calcium oxide, and the water-soluble silicate compound is selected from alkali metal silicates having the formula mSiO₂·nMO (wherein M is Li, Na, K, or NH₄ or a mixture thereof, m and n are numbers of moles, and the m:n ratio is from about 2.0 to about 4), with the proviso that when the calcium silicate hydrate-based hydration accelerator in the set accelerator A is a powder product, the product in the form of a suspension obtained in the process α-1) is further dried in a step to obtain a powder product.

[0126] In general, calcium hydroxide can also be produced from calcium hydroxide-forming compounds, preferably calcium carbide, by contacting it with water to release acetylene and calcium hydroxide.

[0127] Examples of processes α), α-1) and β) are given in the international patent application published as WO 2010 / 026155 A1.

[0128] In one embodiment of the present invention, the hardening accelerator A comprises a low-order CSH having a crystallite size of less than 15 nm and at least one polymeric dispersant. This material is obtained, for example, by a process in which CSH produced under γ) hydrothermal conditions is wet-milled, the milling being carried out in the presence of a water-soluble dispersant.

[0129] Examples of compositions comprising low-order CSH and polymeric dispersants are given in the international patent application published as WO 2018 / 154012 A1.

[0130] In one embodiment of the present invention, the hardening accelerator A comprises calcium silicate hydrate in the form of a suspension or powder product, in which in case a) at least one polymeric dispersant having anionic and / or anion-forming groups and polyether side chains, preferably polyalkylene glycol side chains, is added to the product in suspension form obtained from process α), β), γ) or α-1) before the drying step to obtain the powder product, or in case b) at least one polymeric dispersant having anionic and / or anion-forming groups and polyether side chains, preferably polyalkylene glycol side chains, of formula (I): [ka] (In the formula, A 1 is NH2, NHMe, NMe2, N(CH2-CH2-OH)2, CH3, C2H5, CH2-CH2-OH, phenyl or p-CH3-phenyl, K n+ is an alkali metal cation or Ca 2+ , Mg 2+ , Sr 2+ , Ba 2+ , Zn 2+ , Fe 2+ , Fe 3+ , Al 3+ , Mn 2+ and Cu 2+ and n is the valence of the cation) At least one sulfonic acid compound of the formula (I) was added to the product in suspension form obtained from the process α), β), γ) or α-1). The valence of the cation is specifically the valence of the cationic charge, for example, K n+ Mg 2+ In this case, the valence of the magnesium ion is 2 (n=2).

[0131] Preferably, A 1 is NH2, CH3 and / or phenyl. Preferably, K n+ Ca 2+ is.

[0132] In case a), at least one polymeric dispersant having anionic and / or anion-forming groups and polyether side chains, preferably polyalkylene glycol side chains, serves as a drying aid that is added to the suspension obtained by process α), β) or α-1) before drying said suspension. An example of a) is given in the international patent application published under WO 2012 / 143205.

[0133] In case b), the sulfonic acid compound of formula (I) plays the role of a drying aid that is added to the suspension obtained by process α), β), γ) or α-1) before drying said suspension.

[0134] In a preferred embodiment, the polymeric dispersant used for preparing calcium silicate hydrate comprises at least one polymer (i.e., a water-soluble polymer) containing structural units comprising anionic and / or anion-forming groups and polyether side chains. More specifically, polymers can be used that contain relatively long side chains (in each case, the molecular weight is at least 200 g / mol, more preferably at least 400 g / mol) at various intervals on the main chain. The lengths of these side chains are often identical, but can also be quite different from each other (for example, when polyether macromonomers containing side chains of different lengths are copolymerized). Such polymers can be obtained, for example, by radical polymerization of acid monomers and polyether macromonomers. An alternative route to obtain this type of comb polymer is esterification and / or amidation by reacting similar (co)polymers, such as poly(meth)acrylic acid and acrylic acid / maleic acid copolymers, with suitable monohydroxy- or monoamino-functional polyalkylene glycols, preferably alkylpolyethylene glycols, respectively. Comb polymers obtainable by esterification and / or amidation of poly(meth)acrylic acid are described, for example, in EP 1 138 697 B1.

[0135] The average molecular weight Mw of the water-soluble polymer, as determined by gel permeation chromatography (GPC), is 5,000 g / mol to 200,000 g / mol, preferably 10,000 g / mol to 80,000 g / mol, and particularly 20,000 g / mol to 70,000 g / mol. The average molecular weight of the polymer was analyzed using GPC (column combination: OH-Pak SB-G, OH-Pak SB804HQ, and OH-Pak SB802.5HQ from Shodex, Japan; eluent: 80% by volume of aqueous HCO2NH4 (0.05 mol / L) and 20% by volume of acetonitrile; injection volume: 100 μl; flow rate: 0.5 ml / min). Calibration to determine the average molar mass was performed using linear poly(ethylene oxide) standards and polyethylene glycol standards.

[0136] The polymeric dispersant preferably meets the requirements of industry standard EN934-2 (February 2002).

[0137] In one embodiment, the construction material composition of the present invention comprises, as hardening accelerator A, a combination of calcium silicate hydrate and at least one calcium salt having a water solubility of at least 1 g in 1 liter of water at 23° C. Calcium chloride, calcium nitrate, calcium formate, calcium acetate, calcium bicarbonate, calcium bromide, calcium citrate, calcium chlorate, calcium gluconate, calcium hydroxide, calcium oxide, calcium hypochlorite, calcium iodate, calcium iodide, calcium lactate, calcium nitrite, calcium propionate, calcium sulfamate, calcium methanesulfonate, calcium sulfate, calcium sulfate hemihydrate, calcium sulfate dihydrate, and mixtures of two or more of these components, in particular calcium salts selected from the group comprising calcium nitrate, calcium acetate, calcium chloride, calcium hydroxide, calcium sulfamate, or calcium formate, or mixtures thereof, are preferred.

[0138] The amount of calcium silicate hydrate is preferably 0.1 to 4% by weight relative to the dry weight of accelerator A, based on the total dry weight of the construction material composition, and the amount of calcium salt having a water solubility of ≥ 1 g / l at 23°C is preferably 0.1 to 4% by weight relative to the dry weight of accelerator A, more preferably 0.5 to 2.5% by weight relative to the dry weight of accelerator A, based on the total dry weight of the construction material composition. The weight ratio of calcium silicate hydrate to calcium salt having a water solubility of ≥ 1 g / l at 23°C is in the range of 3:1 to 1:3.

[0139] Generally, the amount of the hardening accelerator A added further depends on the surface area of ​​the entire construction material composition.

[0140] Preferred construction material compositions provide an acceleration factor of accelerator A greater than 1.5, preferably greater than 2.0, and in particular greater than 2.5. To determine the acceleration factor (AF), two standard mortar compositions according to DIN EN 196-1 are prepared, one containing accelerator A in an amount of 2% by weight based on the amount of ordinary Portland cement, and the other containing no accelerator. The dry composition is then mixed with water (water / cement ratio = 0.4). The resulting cement pastes are then separately placed in an isothermal heat flow calorimeter (e.g., TamAir by TA Instruments) at 20°C. The heat flow of both samples is recorded. The heat of hydration (HoH) is then determined according to Equation 1:

number

[0141] In one embodiment of the present invention, the construction material composition further comprises at least one additional hardening accelerator B. The at least one additional hardening accelerator B is a calcium-containing compound different from anhydrous or hydrated calcium silicate, metal silicate hydrate, cement, or SCM. In this context, mention should be made of calcium aluminate, calcium hydroxide, calcium hydroxide nanoparticles, calcium oxide, calcium nitrate, calcium nitrite, calcium thiocyanate, calcium sulfate, calcium sulfate hemihydrate, calcium sulfate dihydrate, calcium acetate, calcium formate, calcium sulfamate, calcium methanesulfonate, and calcium chloride. In a specific embodiment of the present invention, the construction material composition further comprises additional hardening accelerators B, such as calcium sulfamate, calcium hydroxide, or calcium hydroxide nanoparticles. The construction material composition may comprise at least one additional hardening accelerator B in an amount of 0.1 to 5% by dry weight, preferably 1 to 5% by dry weight, and particularly 1.5 to 4% by dry weight, based on the total dry weight of the construction material composition.

[0142] In one embodiment, the set accelerator A, preferably calcium silicate hydrate, can be used in combination with at least one additional set accelerator B, preferably calcium hydroxide, calcium sulfamate or a mixture thereof. In this context, the weight ratio of CSH to Ca(OH)2 can preferably be 1:50 to 10:50, particularly preferably 1:20 to 5:20.

[0143] In one embodiment of the present invention, the total SO3 content and the total Al2O3 content, as determined by elemental analysis of the construction material composition, are present in a weight ratio of 1:10 to 5:1, preferably 1:10 to 3:1, more preferably 1:10 to 7:10, in particular 1:8 to 6:10.

[0144] In one embodiment of the invention, the Portland cement clinker and the supplemental cementitious material are present in a weight ratio of 2:1 to 1:5, preferably 2:1 to 1:2, more preferably 1.8:1 to 1:1.8, or 1.8:1 to 1.5:1, or 1.5:1 to 1:1, or 1:1 to 1:2. In another preferred embodiment of the invention, the Portland cement clinker and the supplemental cementitious material are present in a weight ratio of 1.5:1 to 1:4.5, more preferably 1:1 to 1:4, especially 1:2 to 1:3.8.

[0145] In one embodiment of the invention, the Portland cement clinker and limestone are present in a weight ratio of 4:1 to 1:2, preferably 3.5:1 to 1:1.5, or 3.5:1 to 3:1, or 1.5:1 to 1:1, or 1.3:1 to 1:1.5. In another embodiment of the invention, the Portland cement clinker and limestone are present in a weight ratio of 4:1 to 1:1, more preferably 3.5:1 to 1.5:1, especially 3:1 to 2:1.

[0146] In one embodiment of the invention, Portland cement clinker and a sulfate source selected from the group consisting of gypsum, bassanilite, anhydrite, and mixtures thereof are present in a weight ratio of 60:1 to 2:1, preferably 55:1 to 5:1, more preferably 55:1 to 20:1, or 40:1 to 10:1, or 20:1 to 5:1. In another preferred embodiment of the invention, Portland cement clinker and a sulfate source selected from the group consisting of gypsum, bassanilite, anhydrite, and mixtures thereof are present in a weight ratio of 40:1 to 2:1, more preferably 20:1 to 1:2, especially 10:1 to 3:1.

[0147] In one embodiment of the present invention, Portland cement clinker and accelerator A are present in a weight ratio of 40:1 to 5:1, preferably 35:1 to 10:1, or 25:1 to 5:1, or 20:1 to 15:1.

[0148] In one embodiment of the invention, the supplemental cementitious material and limestone are present in a weight ratio of 10:1 to 1:2, preferably 4:1 to 1:2, more preferably 3:1 to 1:1.8. In another embodiment of the invention, the supplemental cementitious material and limestone are present in a weight ratio of 10:1 to 2:1, more preferably 10:1 to 3:1.

[0149] In one embodiment of the present invention, the supplemental cementitious material and the sulfate source are present in a weight ratio of from 40:1 to 1:1, preferably from 30:1 to 4:1.

[0150] In one embodiment of the present invention, the construction material composition is free of alkanolamines. In another embodiment of the present invention, the construction material composition is free of carbohydrates. In yet another embodiment of the present invention, the construction material composition is free of alkanolamines and carbohydrates.

[0151] In a preferred embodiment of the present invention, the construction material composition comprises: a) Portland cement clinker in an amount of 20 to 55% by dry weight based on the total dry weight of the construction material composition; b) supplementary cementitious materials in an amount of 20-50% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 10 to 40% by dry weight, based on the total dry weight of the construction material composition; d) a sulfate source selected from the group consisting of gypsum, basanitite, anhydrite, and mixtures thereof, in an amount of greater than 2.2% to 8% by weight of SO3, based on the total dry weight of the construction material composition; e) a hardening accelerator A containing particles of calcium and silicon in a molar ratio Ca / Si of 0.1 to 2.2, in an amount of 0.1 to 5% by weight relative to the total weight of CaO and SiO2 of the hardening accelerator A, based on the total dry weight of the construction material composition; Includes:

[0152] In a preferred embodiment of the present invention, the construction material composition comprises: a) Portland cement clinker in an amount of 40-55% by dry weight based on the total dry weight of the construction material composition; b) supplementary cementitious materials in an amount of 30-45% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 15 to 30% by dry weight, based on the total dry weight of the construction material composition; d) a sulfate source in an amount of 2.5 to 7% by weight of SO3 based on the total dry weight of the construction material composition; e) Accelerator A in an amount of 0.1 to 5% by weight based on the total dry weight of the construction material composition and the combined weight of CaO and SiO2 of Accelerator A; Contains or a) Portland cement clinker in an amount of 30-40% by dry weight based on the total dry weight of the construction material composition; b) supplementary cementitious materials in an amount of 30-45% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 20-30% by dry weight based on the total dry weight of the construction material composition; d) a sulfate source in an amount of 2.5 to 7% by weight of SO3 based on the total dry weight of the construction material composition; e) Accelerator A in an amount of 0.5 to 5% by weight based on the total dry weight of the construction material composition and the combined weight of CaO and SiO2 of Accelerator A; contains, or a) Portland cement clinker in an amount of 20-30% by dry weight based on the total dry weight of the construction material composition; b) supplementary cementitious materials in an amount of 30-50% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 20 to 40% by dry weight, based on the total dry weight of the construction material composition; d) a sulfate source in an amount of 2.5 to 7% by weight of SO3 based on the total dry weight of the construction material composition; e) Accelerator A in an amount of 1.0 to 5% by weight based on the total dry weight of the construction material composition and the combined weight of CaO and SiO2 of Accelerator A; Includes:

[0153] In a preferred embodiment of the present invention, the construction material composition comprises from more than 30% to 75% by dry weight, more preferably from 38 to 72% by dry weight, even more preferably from 45 to 71% by dry weight, and especially from more than 50% to 70% by dry weight of the auxiliary cementitious material, based on the total dry weight of the construction material composition.

[0154] In a preferred embodiment of the present invention, the construction material composition comprises: a) Portland cement clinker in an amount of 15 to 47% by dry weight based on the total dry weight of the construction material composition; b) supplemental cementitious materials in an amount of greater than 30% to 70% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 5 to 20% by dry weight based on the total dry weight of the construction material composition; d) a sulfate source in an amount of 2.5 to 7% by weight of SO3 based on the total dry weight of the construction material composition; e) Accelerator A in an amount of 0.1 to 5% by weight based on the total dry weight of the construction material composition and the combined weight of CaO and SiO2 of Accelerator A; and preferably the supplemental cementitious material comprises at least two different supplemental cementitious materials.

[0155] In a preferred embodiment of the present invention, the construction material composition comprises: a) Portland cement clinker in an amount of 15 to 30% by dry weight based on the total dry weight of the construction material composition; b) supplemental cementitious materials in an amount of greater than 50% to 70% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 5 to 20% by dry weight based on the total dry weight of the construction material composition; d) a sulfate source in an amount of 2.5 to 7% by weight of SO3 based on the total dry weight of the construction material composition; e) Accelerator A in an amount of 0.1 to 5% by weight based on the total dry weight of the construction material composition and the combined weight of CaO and SiO2 of Accelerator A; and preferably the supplemental cementitious material comprises at least two different supplemental cementitious materials.

[0156] In one embodiment of the present invention, the construction material composition further comprises at least one additive. The weight ratio of the construction material composition to the additive is generally in the range of 10,000:1 to 1:10,000, preferably in the range of 5,000:1 to 1:5,000, and in particular in the range of 1,000:1 to 1:1,000.

[0157] In one embodiment of the present invention, the construction material composition further comprises at least one additive, preferably selected from the group consisting of inorganic carbonates, alkali metal sulfates, polymeric dispersants, set accelerators, set retarders, thickeners and stabilizers, or a mixture of two or more thereof.

[0158] Preferably, the additive is selected from at least one of the additives detailed below.

[0159] The construction material composition may contain at least one alkali metal carbonate or alkaline earth metal carbonate, particularly sodium carbonate, potassium carbonate, magnesium carbonate, calcium carbonate, and / or mixed calcium-magnesium carbonate (CaMg(CO3)2). In particular, the alkaline earth metal carbonate may be present in an X-ray amorphous form. The carbonate is generally present in an amount ranging from about 1 to about 20% by weight, based on the weight of the inorganic binder.

[0160] Preferably, the composition comprises at least one dispersant for the inorganic binder. In one embodiment, the dispersant is a polymeric dispersant having anionic and / or anion-forming groups and polyether side chains (preferably containing polyalkylene glycol side chains). The anionic and / or anion-forming groups and polyether side chains are preferably attached to the backbone of the polymeric dispersant.

[0161] In this case, the dispersant is more preferably selected from the group consisting of polycarboxylate ethers (PCE) and phosphorylated polycondensates, and in the case of PCE, the anionic groups are carboxyl groups and / or carboxylate groups. Polycarboxylate ethers (PCE) are most preferred.

[0162] The PCE is preferably produced by radical copolymerization of a polyether macromonomer and an acid monomer such that at least 45 mol %, preferably at least 80 mol %, of the total structural units of the copolymer are formed by copolymerization of the polyether macromonomer and the acid monomer. The term acid monomer particularly refers to a monomer containing an anionic and / or anion-forming group. The term polyether macromonomer particularly refers to a monomer containing at least two ether groups, preferably at least two alkylene glycol groups.

[0163] The polymeric dispersant preferably has, as anionic and / or anion-forming groups, the general formula (Ia), (Ib), (Ic) and / or (Id): [ka] (In the formula, R 1 is H or a branched or unbranched C1-C4 alkyl group, CH2COOH or CH2CO-XR 3 and; X is NH-(C n H 2n ) or O-(C n H 2n ) (n=1, 2, 3 or 4, and a nitrogen atom or an oxygen atom is bonded to a CO group) or a chemical bond; R 2 is OM, PO3M2 or O-PO3M2, where R 2 is OM, then X is a chemical bond; R 3 is PO3M2 or O-PO3M2); [ka] (In the formula, R 3 is H or an unbranched or branched C1-C4 alkyl group; n is 0, 1, 2, 3 or 4; R 4 is PO3M2 or O-PO3M2); [ka] (In the formula, R 5 is H or an unbranched or branched C1-C4 alkyl group; Z is O or NR 7 and; R 7 is H, (C n H 2n )-OH, (C n H 2n )-PO3M2, (C n H 2n )-OPO3M2, (C6H4)-PO3M2 or (C6H4)-OPO3M2, n is 1, 2, 3 or 4); [ka] (In the formula, R 6 is H or an unbranched or branched C1-C4 alkyl group; Q is NR 7 or O; R 7 is H, (C n H 2n )-OH, (C n H 2n )-PO3M2, (C n H 2n )-OPO3M2, (C6H4)-PO3M2 or (C6H4)-OPO3M2, n is 1, 2, 3 or 4; Each M in the above formula is independently H or a cation equivalent. It contains at least one structural unit of the formula:

[0164] Preferred are compositions in which the polymeric dispersant comprises, as a polyether side chain, at least one structural unit of the general formulae (IIa), (IIb), (IIc) and / or (IId): [ka] (In the formula, R 10 , R 11 and R 12 are, independently of each other, H or unbranched or branched C1-C4 alkyl; Z is O or S; E is an unbranched or branched C2-C6 alkylene group, a cyclohexylene group, CH2-C6H 10 , 1,2-phenylene, 1,3-phenylene or 1,4-phenylene; G is O, NH, or CO—NH; or E and G together form a chemical bond; A is unbranched or branched alkylene having 2, 3, 4 or 5 carbon atoms or CH2CH(C6H5); n is 0, 1, 2, 3, 4 or 5; a is an integer from 2 to 350; R 13 is H, an unbranched or branched C1-C4 alkyl group, CO—NH2 or COCH3); [ka] (In the formula, R 16 , R 17 and R 18 are, independently of each other, H or unbranched or branched C1-C4 alkyl; E is an unbranched or branched C1-C6 alkylene group, a cyclohexylene group, CH2-C6H 10 , 1,2-phenylene, 1,3-phenylene, or 1,4-phenylene, or a chemical bond; A is unbranched or branched alkylene having 2, 3, 4 or 5 carbon atoms or CH2CH(C6H5); n is 0, 1, 2, 3, 4 and / or 5; L is C x H 2x (x=2, 3, 4, or 5) or CH2CH(C6H5); a is an integer from 2 to 350; d is an integer from 1 to 350; R 19 is H or an unbranched or branched C1-C4 alkyl group; R 20 is H or an unbranched C1-C4 alkyl group; n is 0, 1, 2, 3, 4 or 5; [ka] (In the formula, R 21 , R 22 and R 23 are, independently of each other, H or unbranched or branched C1-C4 alkyl; W, O, NR 25 or N; V is W=O or NR 25 1 if W=N, and 2 if W=N; A is unbranched or branched alkylene having 2 to 5 carbon atoms or CH2CH(C6H5); a is an integer from 2 to 350; R 24 is H or an unbranched or branched C1-C4 alkyl group; R 25 is H or an unbranched or branched C1-C4 alkyl group; [ka] (In the formula, R 6 is H or an unbranched or branched C1-C4 alkyl group; Q is NR 10 , N or O; V is W=O or NR 10 1 if W=N, and 2 if W=N; R 10 is H or an unbranched or branched C1-C4 alkyl group; A is unbranched or branched alkylene having 2 to 5 carbon atoms or CH2CH(C6H5); and a is an integer from 2 to 350.

[0165] In one embodiment, the polymeric dispersant comprises structural units (III) and (IV): [ka] (In the formula, T is a substituted or unsubstituted phenyl or naphthyl group, or a substituted or unsubstituted heteroaromatic group having 5 to 10 ring atoms, one or two of which are heteroatoms selected from N, O, and S; n is 1 or 2; B is N, NH, or O, with the proviso that n is 2 when B is N, and 1 when B is NH or O; A is unbranched or branched alkylene having 2 to 5 carbon atoms or CH2CH(C6H5); a is an integer from 1 to 300; R 25 is H, branched or unbranched C1-C 10 an alkyl group, a C5-C8 cycloalkyl group, an aryl group, or a heteroaryl group having 5 to 10 ring atoms, one or two of which are heteroatoms selected from N, O, and S. a phosphorylated polycondensate comprising: The structural unit (IV) is selected from the structural units (IVa) and (IVb): [ka] (In the formula, D is a substituted or unsubstituted phenyl or naphthyl group, or a substituted or unsubstituted heteroaromatic group having 5 to 10 ring atoms, one or two of which are heteroatoms selected from N, O, and S; E is N, NH, or O, with the proviso that m is 2 when E is N, and m is 1 when E is NH or O; A is unbranched or branched alkylene having 2 to 5 carbon atoms or CH2CH(C6H5); b is an integer from 0 to 300; M is, independently in each occurrence, H or a cation equivalent; [ka] (In the formula, V is a substituted or unsubstituted phenyl or naphthyl group, and R 8 , OH, OR 8 , (CO)R 8 , COOM, COOR 8 , SO3R 8 and NO2; R 7 is COOM, OCH2COOM, SO3M or OPO3M2; M is H or a cation equivalent; and R 8 is C1-C4 alkyl, phenyl, naphthyl, phenyl-C1-C4 alkyl or C1-C4 alkylphenyl).

[0166] The polymeric dispersants comprising structural units (I) and (II) can be prepared by conventional methods, for example, by free radical polymerization. The preparation of the dispersants is described, for example, in EP-A-0894811, EP-A-1851256, EP-A-2463314 and EP-A-0753488.

[0167] In a preferred embodiment, the dispersant is a polymer containing sulfonic acid and / or sulfonate groups. In one embodiment, the polymeric dispersant contains sulfonic acid and / or sulfonate and is selected from the group consisting of lignosulfonate (LGS), melamine formaldehyde sulfonate condensates (MFS), β-naphthalene sulfonic acid condensates (BNS), sulfonated ketone-formaldehyde condensates, and copolymers containing sulfo- and / or sulfonate-containing units and carboxylic acid and / or carboxylate-containing units.

[0168] Lignosulfonates, which are used as sulfonated polymeric dispersants, are products obtained as by-products of the paper industry. Products of this type are described in Ullmann's Encyclopedia of Industrial Chemistry, 5th Ed., Vol. A8, pages 586 and 587. They are represented by the highly simplified and idealized formula: [ka] (wherein n is usually 5 to 500) units. Typically, the molecular weight of lignosulfonates is between 2,000 and 100,000 g / mol. They are generally present in the form of their sodium, calcium and / or magnesium salts. Suitable lignosulfonates are, for example, products sold under the trade name Borresperse by Borregaard LignoTech, Norway.

[0169] Melamine-formaldehyde-sulfonate condensates (also referred to as MFS resins) and their preparation are described, for example, in Canadian Patent No. 2,172,004 A1, German Patent Application No. 4,411,797 A1, U.S. Pat. No. 4,430,469, U.S. Pat. No. 6,555,683, and Swiss Patent No. 686,186, as well as in Ullmann's Encyclopedia of Industrial Chemistry, 5th Ed., vol. A2, page 131 and Concrete Admixtures Handbook - Properties, Science and Technology, 2nd Ed., pages 411, 412. Preferred melamine-formaldehyde-sulfonate condensates have the formula: [ka] (wherein n is typically a number from 10 to 300) (highly simplified and idealized) units. The molecular weight is preferably in the range of 2,500 to 80,000 g / mol. Examples of melamine-formaldehyde-sulfonate condensates include products sold under the trade name Melment (registered trademark) by BASF Construction Additives GmbH.

[0170] In addition to the sulfonated melamine units, additional monomers can be co-condensed. Urea is particularly preferred. Furthermore, aromatic building blocks such as gallic acid, aminobenzenesulfonic acid, sulfanilic acid, phenolsulfonic acid, aniline, ammonium benzoate, dialkoxybenzenesulfonic acid, dialkoxybenzoic acid, pyridine, pyridinemonosulfonic acid, pyridinedisulfonic acid, pyridinecarboxylic acid, and pyridinedicarboxylic acid can be co-condensed with the melamine-formaldehyde-sulfonate condensate.

[0171] Sulfonated ketone-formaldehyde is a product in which a mono- or diketone is used as the ketone component. Preferably, acetone, butanone, pentanone, hexanone, or cyclohexanone is incorporated into the polymer. This type of condensation product is known and is described, for example, in WO 2009 / 103579. Sulfonated acetone-formaldehyde condensates are preferred. These are typically represented by the formula (according to J. Plank et al., J. Appl. Poly. Sci. 2009, 2018-2024): [ka] (wherein m and n are typically integers of 10 to 250, and M is an alkali metal ion, for example, Na + and the ratio of m:n is generally in the range of about 3:1 to about 1:3, particularly in the range of about 1.2:1 to about 1:1.2. Suitable acetone-formaldehyde condensates include, for example, products sold under the trade name Melcret® K1L by BASF Construction Solutions GmbH.

[0172] Additionally, aromatic building blocks such as gallic acid, aminobenzenesulfonic acid, sulfanilic acid, phenolsulfonic acid, aniline, ammonium benzoate, dialkoxybenzenesulfonic acid, dialkoxybenzoic acid, pyridine, pyridinemonosulfonic acid, pyridinedisulfonic acid, pyridinecarboxylic acid, and pyridinedicarboxylic acid can be co-condensed.

[0173] β-Naphthalene-formaldehyde condensates (BNS) are products obtained by sulfonating naphthalene and then polycondensing it with formaldehyde. Products of this type are described, inter alia, in "Concrete Admixtures Handbook - Properties, Science and Technology, 2nd Ed., pages 411-413" and "Ullmann's Encyclopedia of Industrial Chemistry, 5th Ed., Vol. A8, pages 587, 588". They are compounds of the formula [ka] Includes units of.

[0174] Typically, the molecular weight (M w ) is 1,000 to 50,000 g / mol.

[0175] Suitable β-naphthalene-formaldehyde condensates are, for example, the products sold under the trade name Melcret® 500L by BASF Construction Additives GmbH.

[0176] Additionally, aromatic building blocks such as gallic acid, aminobenzenesulfonic acid, sulfanilic acid, phenolsulfonic acid, aniline, ammonium benzoate, dialkoxybenzenesulfonic acid, dialkoxybenzoic acid, pyridine, pyridinemonosulfonic acid, pyridinedisulfonic acid, pyridinecarboxylic acid, and pyridinedicarboxylic acid can be co-condensed.

[0177] In a further embodiment, the dispersant is a copolymer comprising sulfo and / or sulfonate group-containing units and carboxylic acid and / or carboxylate group-containing units. In one embodiment, the sulfo or sulfonate group-containing units are units derived from vinyl sulfonic acid, methallyl sulfonic acid, 4-vinylphenyl sulfonic acid, or units of the formula: [ka] (In the formula, R 1 represents hydrogen or methyl, R 2 , R 3 and R 4 are each independently H, a linear or branched C1-C6 alkyl, or a C6-C 14 represents aryl; M represents hydrogen, a metal cation, preferably a monovalent or divalent metal cation or an ammonium cation; a represents 1 or (1 / valence of cation), preferably 1 / 2 or 1. is a sulfonic acid-containing structural unit.

[0178] Preferred sulfo group-containing units are those derived from monomers selected from vinyl sulfonic acid, methallylsulfonic acid and 2-acrylamido-2-methylpropylsulfonic acid (AMPS), with AMPS being particularly preferred.

[0179] The carboxylic acid or carboxylate-containing units are preferably derived from monomers selected from acrylic acid, methacrylic acid, 2-ethylacrylic acid, vinylacetic acid, crotonic acid, maleic acid, fumaric acid, itaconic acid, citraconic acid, especially acrylic acid and methacrylic acid.

[0180] The molecular weight Mw of the sulfo group-containing copolymer determined by aqueous gel permeation chromatography is generally in the range of 1000 g / mol to 50,000 g / mol, preferably in the range of 1500 g / mol to 30,000 g / mol.

[0181] In one embodiment, the molar ratio of sulfo group-containing units to carboxylic acid-containing units is generally in the range of 5:1 to 1:5, preferably in the range of 4:1 to 1:4.

[0182] Preferably, the (co)polymer having carboxylic acid and / or carboxylate groups and sulfonic acid and / or sulfonate groups has a polymer backbone of carbon atoms, and the ratio of the sum of the number of carboxylic acid and / or carboxylate groups and sulfonic acid and / or sulfonate groups to the number of carbon atoms in the polymer backbone is in the range of 0.1 to 0.6, preferably 0.2 to 0.55. Preferably, the (co)polymer is obtainable by free radical (co)polymerization, and the carboxylic acid and / or carboxylate groups are derived from monocarboxylic acid monomers. Preferred (co)polymers are obtainable by free radical (co)polymerization, and the carboxylic acid and / or carboxylate groups are derived from the monomers acrylic acid and / or methacrylic acid, and the sulfonic acid and / or sulfonate groups are derived from 2-acrylamido-2-methylpropanesulfonic acid. Preferably, the weight average molecular weight M of the (co)polymer is w is 8,000 g / mol to 200,000 g / mol, preferably 10,000 to 50,000 g / mol. The weight ratio of the one or more (co)polymers to calcium silicate hydrate is preferably 1 / 100 to 4 / 1, more preferably 1 / 10 to 2 / 1, and most preferably 1 / 5 to 1 / 1.

[0183] It is also possible to use mixtures of the aforementioned dispersants, such as lignosulfonates (LGS), melamine formaldehyde sulfonate condensates (MFS), β-naphthalene sulfonic acid condensates (BNS), copolymers comprising sulfo- and / or sulfonate-containing units and carboxylic acid and / or carboxylate-containing units, sulfonated ketone-formaldehyde condensates, polycarboxylate ethers (PCE) and / or phosphorylated polycondensates. Preferred mixtures include copolymers comprising sulfo- and / or sulfonate-containing units and carboxylic acid and / or carboxylate-containing units and / or phosphorylated polycondensates.

[0184] In one embodiment, the dispersant is a) a non-ionic copolymer for improving the workability of a construction material composition in the form of a paste (cement mixture), comprising at least the following monomers: Component A, an ethylenically unsaturated carboxylic acid ester monomer containing a moiety that is hydrolyzable in the cement mixture, the hydrolyzed monomer residue containing an active binding site for the components of the cement mixture; and At least one type of C with 1 to 350 units 2~4 Component B comprising an ethylenically unsaturated carboxylic acid ester or alkenyl ether monomer containing an oxyalkylene pendant group or b) a non-ionic copolymer comprising residues of the formula: R-(OA) n -N-[CH2-PO(OM2)2]2 (In the formula, R is H or a saturated or unsaturated hydrocarbon group, preferably C1-C 15 It is the basis, A are the same or different and independently represent alkylene having 2 to 18 carbon atoms, preferably ethylene and / or propylene, most preferably ethylene; N is an integer of 5 to 500, preferably 10 to 200, and most preferably 10 to 100; M is H, alkali metal, 1 / 2 alkaline earth metal and / or amine is a phosphonate-containing polymer of the formula:

[0185] In one embodiment of the present invention, the construction material composition further comprised at least one polymeric dispersant, in particular a polycarboxylate ether, a phosphorylated polycondensate or a dispersant containing sulfonic acid and / or sulfonate groups.

[0186] In one embodiment of the present invention, the construction material composition further comprises at least one polymeric dispersant which is a sulfonic acid and / or sulfonate group-containing dispersant selected from the group consisting of lignosulfonates, melamine-formaldehyde sulfonate condensates, beta-naphthalene sulfonic acid condensates, sulfonated ketone-formaldehyde condensates, and copolymers comprising sulfo- and / or sulfonate-group-containing units and carboxylic acid and / or carboxylate-group-containing units.

[0187] As indicated above, in one embodiment, the present invention further relates to the use of a hardening accelerator A comprising particles of calcium and silicon in a molar ratio Ca / Si of 0.1 to 2.2 in a construction material composition comprising up to 55% by dry weight of Portland cement clinker, based on the total dry weight of the construction material composition, wherein the hardening accelerator A is present in the construction material composition in an amount of 0.1 to 5% by weight relative to the combined weight of CaO and SiO2 of the hardening accelerator A, based on the total dry weight of the construction material composition.

[0188] The present invention also relates to the use of the construction material composition of the present invention as an inorganic binder for inorganic binder-containing construction material formulations and / or for producing building materials, in particular concrete, such as in-place concrete, finished concrete elements, precast concrete elements, concrete products, natural stone concrete, concrete blocks, cast-in-place concrete, shotcrete, ready-mix concrete, pneumatically pumped concrete, and the like.

[0189] The present invention also relates to the use of the construction material composition of the present invention as an inorganic binder for inorganic binder-containing construction material formulations and / or for producing building materials, in particular dry mortars, such as concrete repair systems, repair mortars, industrial cement flooring, one- and two-component waterproofing slurries, screeds, filling and self-leveling compositions, such as joint sealants or self-leveling underlayments, adhesives, such as building or construction adhesives, adhesives for exterior or interior thermal insulation composite systems (ETICS), tile adhesives, grouts, such as joint grouts, non-shrink grouts, tile grouts, windmill grouts, anchor grouts, flowable or self-leveling grouts, EIFS grouts (exterior thermal insulation and finishing systems), screeds or waterproofing layers.

[0190] The present invention also relates to the use of the construction material composition of the present invention as an inorganic binder for inorganic binder-containing construction material formulations and / or for producing building materials, in particular processed products such as foamed cement, cement boards, autoclaved aerated concrete, fiber-reinforced cement boards or cement tiles.

[0191] According to a preferred embodiment of the present invention, the construction material composition contains less than 40% by dry weight, preferably less than 35% by dry weight, more preferably less than 30% by dry weight, and especially less than 25% by dry weight of ingredients publicly known to be hazardous under GHS 08, based on the total dry weight of the construction material composition.More preferably, the construction material composition contains 0 to less than 40% by dry weight, preferably less than 0 to 35% by dry weight, more preferably less than 0 to 30% by dry weight, and especially less than 0 to 25% by dry weight of ingredients publicly known to be hazardous under GHS 08, based on the total dry weight of the construction material composition.

[0192] In this context, it is particularly preferred that the construction material composition comprises less than 40% by dry weight, preferably less than 35% by dry weight, more preferably less than 30% by dry weight, and in particular less than 25% by dry weight, of fine quartz (also known as powdered quartz), based on the total dry weight % of the construction material composition. Even more preferred, the construction material composition comprises 0 to less than 40% by dry weight, preferably less than 0 to 35% by dry weight, more preferably less than 0 to 30% by dry weight, and in particular less than 0 to 25% by dry weight, of fine quartz, based on the total dry weight % of the construction material composition.

[0193] The term "fine quartz" according to the present invention refers to fine quartz having a maximum particle size of up to 63 μm.

[0194] In one embodiment of the present invention, the building material composition is as described in more detail above.

[0195] In one embodiment of the present invention, the building material composition is as claimed.

[0196] As indicated above, the present invention also relates in one embodiment to a mortar or concrete comprising the claimed construction material composition. Further details regarding the construction material composition are given in the description above. In this context, mention should be made of mortars, such as dry mortars, sagging-resistant, flowable or self-leveling mortars, drainage mortars or repair mortars and concretes, such as in-place concrete, finished concrete elements, precast concrete elements, concrete products, natural stone concrete, concrete blocks, cast-in-place concrete, shotcrete, ready-mixed concrete, pneumatically pumped concrete, concrete repair systems.

[0197] In certain embodiments of the present invention, the mortar comprises a dispersant. Suitable dispersants are as described in more detail above.

[0198] In one embodiment of the present invention, the mortar comprises at least one polymeric dispersant, in particular a polycarboxylate ether, a phosphorylated polycondensate or a dispersant containing sulfonic acid and / or sulfonate groups.

[0199] In one embodiment of the present invention, the mortar comprises at least one polymeric dispersant which is a sulfonic acid and / or sulfonate group-containing dispersant selected from the group consisting of lignosulfonates, melamine formaldehyde sulfonate condensates, beta-naphthalene sulfonic acid condensates, sulfonated ketone-formaldehyde condensates, and copolymers comprising sulfo group-containing units and / or sulfonate group-containing units and carboxylic acid and / or carboxylate group-containing units.

[0200] As indicated above, the present invention, in one embodiment, further relates to a process for producing the claimed construction material composition. Further details regarding the construction material composition can be found from the description above.

[0201] In one embodiment of the invention, calcium carbonate is provided as a powder. In one embodiment of the invention, accelerator A is provided as a suspension. Preferably, the calcium carbonate phase is provided as a powder and accelerator A is provided as a suspension.

[0202] In a preferred embodiment, the process comprises mixing calcium carbonate with accelerator A.

[0203] In one embodiment, the present invention relates to a process for producing the claimed construction material composition, wherein the accelerator A is added during or after the blending of components a) to d). The blending can be carried out by simultaneously grinding all of components a) to e). The blending can further be carried out in several steps, for example, in step 1, component a) is simultaneously ground with component d), and in step 2, components b) and c) are blended with the mixture of a) and d), and component e) is added during or after step 1 or step 2.

[0204] Preferably, component e) is added after components a) to d) have been combined.

[0205] Particularly preferably, the addition of component e) is carried out at a temperature below 150°C if component e) is in suspension form, or below 120°C, more preferably below 100°C, if component e) is in powder form.

[0206] The present invention further relates to the following embodiments: It should be understood that each preferred embodiment is preferred both by itself and in combination with the other preferred embodiments.

[0207] In a preferred embodiment, the present invention provides a) Portland cement clinker in an amount of 20 to 55% by dry weight based on the total dry weight of the construction material composition; b) supplementary cementitious materials in an amount of 20-50% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 10 to 40% by dry weight, based on the total dry weight of the construction material composition; d) a sulfate source selected from the group consisting of gypsum, basanitite, anhydrite, and mixtures thereof, in an amount of greater than 2.2% to 8% by weight of SO3, based on the total dry weight of the construction material composition; e) a hardening accelerator A containing particles of calcium and silicon in a molar ratio Ca / Si of 0.1 to 2.2, in an amount of 0.1 to 5% by weight relative to the total weight of CaO and SiO2 of the hardening accelerator A, based on the total dry weight of the construction material composition; The present invention relates to a construction material composition comprising:

[0208] In a preferred embodiment, the present invention relates to a construction material composition according to the preceding embodiment, wherein the supplemental cementitious material is selected from the group consisting of slag, fly ash, natural pozzolana, calcined clay, silica fume, and mixtures thereof.

[0209] In a preferred embodiment, the present invention relates to a construction material composition according to any one of the preceding embodiments, wherein the calcium carbonate phase is selected from limestone, dolomite, calcite, aragonite, vaterite, and mixtures thereof.

[0210] In a preferred embodiment, the present invention relates to a construction material composition according to any one of the preceding embodiments, wherein the total SO3 content and the total Al2O3 content, as determined by elemental analysis, are present in a weight ratio of 1:10 to 5:1.

[0211] In a preferred embodiment, the invention relates to a construction material composition according to any one of the preceding embodiments, wherein the Portland cement clinker and the supplemental cementitious material are present in a weight ratio of 2:1 to 1:2.

[0212] In a preferred embodiment, the present invention relates to a construction material composition according to any one of the preceding embodiments, wherein the Portland cement clinker and limestone are present in a weight ratio of 4:1 to 1:2.

[0213] In a preferred embodiment, the present invention relates to the construction material composition according to any one of the preceding embodiments, wherein the hardening accelerator A further comprises a water-soluble polymer in an amount of 0.1 wt.% to 50 wt.%, relative to the dry weight of the hardening accelerator A.

[0214] In a preferred embodiment, the present invention relates to a construction material composition according to any one of the preceding embodiments, wherein the hardening accelerator A has the following empirical formula: a CaO,SiO2,b Al2O3,c H2O,d X,e W (wherein X is an alkali metal, W is an alkaline earth metal; 0.5≦a≦2.5, preferably 0.66≦a≦2.0, 0≦b≦1, preferably 0≦b≦0.1, 1≦c≦6, preferably 1≦c≦6.0, 0≦d≦1, preferably 0≦d≦0.4 or 0.2, 0≦e≦2, preferably 0≦e≦0.1) The present invention relates to a construction material composition comprising particles of calcium silicate hydrate of the formula (I).

[0215] In a preferred embodiment, the present invention provides a construction material composition according to any one of the preceding embodiments, comprising: a) Portland cement clinker in an amount of 40-55% by dry weight based on the total dry weight of the construction material composition; b) supplementary cementitious materials in an amount of 30-45% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 15 to 30% by dry weight, based on the total dry weight of the construction material composition; d) a sulfate source in an amount of 2.5 to 7% by weight of SO3 based on the total dry weight of the construction material composition; e) Accelerator A in an amount of 0.1 to 5% by weight based on the total dry weight of the construction material composition and the combined weight of CaO and SiO2 of Accelerator A; The present invention relates to a construction material composition comprising:

[0216] In a preferred embodiment, the present invention provides a construction material composition according to any one of the preceding embodiments, comprising: a) Portland cement clinker in an amount of 30-40% by dry weight based on the total dry weight of the construction material composition; b) supplementary cementitious materials in an amount of 30-45% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 20-30% by dry weight based on the total dry weight of the construction material composition; d) a sulfate source in an amount of 2.5 to 7% by weight of SO3 based on the total dry weight of the construction material composition; e) Accelerator A in an amount of 0.5 to 5% by weight based on the total dry weight of the construction material composition and the combined weight of CaO and SiO2 of Accelerator A; The present invention relates to a construction material composition comprising:

[0217] In a preferred embodiment, the present invention provides a construction material composition according to any one of the preceding embodiments, comprising: a) Portland cement clinker in an amount of 20-30% by dry weight based on the total dry weight of the construction material composition; b) supplementary cementitious materials in an amount of 30-50% by dry weight based on the total dry weight of the construction material composition; c) a calcium carbonate phase in an amount of 20 to 40% by dry weight, based on the total dry weight of the construction material composition; d) a sulfate source in an amount of 2.5 to 7% by weight of SO3 based on the total dry weight of the construction material composition; e) Accelerator A in an amount of 1.0 to 5% by weight based on the total dry weight of the construction material composition and the combined weight of CaO and SiO2 of Accelerator A; The present invention relates to a construction material composition comprising:

[0218] In a preferred embodiment, the present invention relates to a construction material composition according to any one of the preceding embodiments, further comprising at least one additive, preferably the at least one additive selected from the group consisting of inorganic carbonates, alkali metal sulfates, polymeric dispersants, set accelerators, set retarders, thickeners and stabilizers, or a mixture of two or more thereof.

[0219] In a preferred embodiment, the present invention relates to a construction material composition according to any one of the preceding embodiments, further comprising at least one polymeric dispersant, in particular a polycarboxylate ether, a phosphorylated polycondensate or a sulfonic acid and / or sulfonate group-containing dispersant.

[0220] In a preferred embodiment, the present invention relates to a construction material composition according to any one of the preceding embodiments, further comprising at least one polymeric dispersant which is a sulfonic acid and / or sulfonate group-containing dispersant selected from the group consisting of lignosulfonates, melamine-formaldehyde sulfonate condensates, beta-naphthalenesulfonic acid condensates, sulfonated ketone-formaldehyde condensates, and copolymers comprising sulfo- and / or sulfonate-group-containing units and carboxylic acid and / or carboxylate-group-containing units.

[0221] In a preferred embodiment, the present invention relates to a construction material composition according to any one of the preceding embodiments, further comprising at least one hardening accelerator B.

[0222] In a preferred embodiment, the present invention relates to the use of a hardening accelerator A comprising particles of calcium and silicon in a molar ratio Ca / Si of 0.1 to 2.2 in a construction material composition comprising up to 55% by dry weight of Portland cement clinker, based on the total dry weight of the construction material composition, wherein the hardening accelerator A is present in the construction material composition in an amount of 0.1 to 5% by weight relative to the combined weight of CaO and SiO2 of the hardening accelerator A, based on the total dry weight of the construction material composition.

[0223] In a preferred embodiment, the present invention relates to the use according to any one of the preceding embodiments, wherein the construction material composition is as defined in any one of the preceding embodiments.

[0224] In a preferred embodiment, the present invention relates to a mortar or concrete comprising the construction material composition according to any one of the preceding embodiments.

[0225] In a preferred embodiment, the present invention relates to a process for producing a construction material composition according to any one of the preceding embodiments, wherein the calcium carbonate phase is provided as a powder and the accelerator A is provided as a suspension.

[0226] The present invention is further illustrated by the following examples. [Example]

[0227] As the OPC, Milke CEM I 52.5 R (d 50 = 5.1 μm) and a Portland cement clinker content of 90 wt% based on the total amount of OPC. 50 = 19.44 μm) was used.

[0228] Limestone was purchased from Omya. It was Omyacarb 15 AL (d 50 =15).

[0229] Anhydrite (CAB 30) was calcium sulfate purchased from LANXESS Deutschland GmbH.

[0230] Hardening accelerator A (referred to as CSH) was prepared in two steps: Step 1 - A suspension of CSH was prepared according to Example Suspension S11 in Table 4 of WO 2018 / 154012 A1. In Step 2, the resulting suspension was further dried according to Example TH1-q in Table 4 of WO 2014 / 114784 A1, except that the suspension from Step 1 was used instead of Suspension H1. The final Ca / Si molar ratio of the particles contained in Hardening Accelerator A, in which calcium and silicon are present in a Ca / Si molar ratio of 0.1 to 2.2, was 1.85.

[0231] The fired clay was purchased from Tara Society, India (d 50 =12.0 μm).

[0232] Slag (Moerdijk 4500) was purchased from Ecocem (d 50 =10.0 μm).

[0233] Class F fly ash was purchased from Powerment HKV (d 50 =14.5μm).

[0234] Microsilica RW Q1-Filler was purchased from RW Silicium GmbH (d 50 =0.1~0.3μm).

[0235] Powdered quartz M8 was purchased from Sibelco (d50 = 27 μm, Blaine value = 3200 cm 2 / g).

[0236] Additives: Superplasticizer Glenium ACE 30 from BASF Schweiz AG, a polycarboxylate ether-based superplasticizer with a solids content of 30.0 wt.%. Vinapor DF 9010 F, a defoamer from BASF Construction Additives GmbH. Starvis 3040 F, a stabilizer from BASF Construction Additives GmbH.

[0237] Strength was measured using a standard mortar test according to DIN EN 196-1:2005. The total amount of water per mix was 225 g. This amount of water corresponds to a water / cement ratio of 0.5 when pure cement is used (Comparative Example 0 in Table 1). To compare different mortars with equal slump flows, a superplasticizer was used to equalize the slump flow to 17 cm ± 1 cm. The comparative mortars used an amount of 1.5 g per 1800 g of mortar. The samples according to the invention with CSH did not require the addition of additional superplasticizer to achieve the target slump flow.

[0238] Each mortar mix contained 0.5 g of antifoaming agent to adjust the air content, and 0.5 g of stabilizer was added to prevent separation of the mortar.

[0239] Limestone-burned clay cement (LC 3 Standard mortar tests were carried out on the ) system. Accelerator A (designated CSH) was tested at dosages of 1.5 and 3 wt. % (see Table 1) based on the dry weight of the accelerator.

[0240] Standard design LC containing 50 wt% cement 3 The test was carried out with a mix of LC designed with the cement in the system changed to 35 and 25 wt%. 3 The mix was also tested, and the results are shown in Table 2.

[0241] When CSH was added at 3 wt%, not only the early strength but also the long-term strength of the calcined clay system was improved compared to the reference. On the other hand, the standard LC containing 50 wt% cement 3 In this system, the use of 3 wt% CSH was able to achieve strength equivalent to that of pure OPC. Further optimization of the mix design, along with the CSH loading, could provide a solution to obtain performance equivalent to OPC while limiting the use of OPC in the mix (i.e., 40% OPC).

[0242] The raw materials were mixed in amounts according to Table 1, and strengths were measured according to EN 196-1 after 8 hours, 24 hours, 7 days, and 28 days. The strengths are shown in Tables 2 (8h, 24h, 7d, and 28d) and 3 (28d). Examples 0 to 12 contain CEM I 52.5 R cement.

[0243] [Table 2]

[0244] [Table 3]

[0245] [Table 4]

[0246] As can be seen from the examples, the inventive system comprising at least Portland cement clinker, a supplemental cementitious material, a calcium carbonate phase and accelerator A not only provides high early strength, but also has improved or comparable long term strength.

[0247] Additionally, tests were also carried out on cement containing CEM I 42.5 N. The raw materials were mixed in the percentage ratios shown in Tables 4 to 6, 8, 9 and 10. The strength according to EN 196-1 for each was measured after 24 hours, 2 days, 7 days and 28 days (as shown in Tables 4, 5, 7, 8, 9 and 11).

[0248] [Table 5]

[0249] [Table 6]

[0250] [Table 7]

[0251] [Table 8]

[0252] [Table 9]

[0253] [Table 10]

[0254] [Table 11]

[0255] [Table 12]

[0256] As can be seen from Examples 0-86, the systems of the present invention, which include at least Portland cement clinker, a supplemental cementitious material, a calcium carbonate phase, and accelerator A, not only provide high early strength, but also have improved or comparable long-term strength.

[0257] It should be noted that although the compressive strength of Example 67 is comparable to that of Example 22, Example 67 contains powdered quartz, i.e., Example 67 does not avoid non-hazardous ingredients that fall under GHS08. On the other hand, Example 22 contains limestone instead of powdered quartz, which is preferable from a safety perspective.

[0258] Therefore, the present invention provides, among other things, environmentally friendly compositions. For example, a comparison of Comparative Examples 20 and 23 with Inventive Example 26 reveals that the Inventive Example has not only excellent early strength but also excellent long-term strength. All of these compositions provide compositions with low amounts of OPC and somewhat high amounts of limestone, and are therefore particularly environmentally friendly.

Claims

1. A construction material composition comprising: a) Portland cement clinker in an amount of 15 to 55 dry weight percent based on the total dry weight of the building material composition; b) a supplemental cementitious material in an amount of greater than 30% to 75% by dry weight, based on the total dry weight of the building material composition, the supplemental cementitious material comprising calcined clay; c) a calcium carbonate phase that is limestone in an amount of 5 to 40% by dry weight, based on the total dry weight of the construction material composition; d) greater than 2.2 wt. % to 8 wt. % SO , based on the total dry weight of the construction material composition. ３ a sulfate source selected from the group consisting of gypsum, basanitite, anhydrite and mixtures thereof; e) A hardening accelerator A containing particles of calcium and silicon in a molar ratio Ca / Si of 0.1 to 2.2, wherein the CaO and SiO of the hardening accelerator A are ２ and a curing accelerator A in an amount of 0.1 to 5% by weight based on the total weight of the A construction material composition comprising:

2. A construction material composition as described in claim 1, wherein the supplemental cementitious material further comprises a different supplemental cementitious material selected from the group consisting of slag, fly ash, natural pozzolan, silica fume and mixtures thereof.

3. Total SO determined by elemental analysis ３ Content and total Al ２ O ３ The construction material composition according to claim 1 or 2, wherein the content is in a weight ratio of 1:10 to 5:

1.

4. 4. The construction material composition according to any one of claims 1 to 3, wherein the Portland cement clinker and the supplemental cementitious material are present in a weight ratio of from 2:1 to 1:

5.

5. 5. The construction material composition according to claim 1, wherein the Portland cement clinker and the calcium carbonate phase are present in a weight ratio of from 4:1 to 1:

2.

6. The construction material composition according to any one of claims 1 to 5, wherein the hardening accelerator A further comprises a water-soluble polymer in an amount of 0.1 wt% to 50 wt% based on the dry weight of the hardening accelerator A.

7. The curing accelerator A has the following empirical formula: CaO, SiO ２ ,b All ２ O ３ ,cH ２ O, D, W wherein X is an alkali metal; W is an alkaline earth metal; 0.5≦a≦2.5, preferably 0.66≦a≦2.0, 0≦b≦1, preferably 0≦b≦0.1, 1≦c≦6, preferably 1≦c≦6.0, 0≦d≦1, preferably 0≦d≦0.4 or 0.2; 0≦e≦2, preferably 0≦e≦0.1) 7. The construction material composition according to claim 1, comprising particles of calcium silicate hydrate of formula (I).

8. a) the Portland cement clinker in an amount of 40 to 55 dry weight percent based on the total dry weight of the construction material composition; b) the supplemental cementitious material in an amount of greater than 30% to 45% by dry weight, based on the total dry weight of the building material composition; c) the calcium carbonate phase in an amount of 15 to 30% by dry weight, based on the total dry weight of the construction material composition; d) 2.5 to 7 wt. % SO , based on the total dry weight of the construction material composition. ３ the sulfate source in an amount of e) the CaO and SiO of the hardening accelerator A based on the total dry weight of the construction material composition ２ and the curing accelerator A in an amount of 0.1 to 5% by weight based on the total weight of the The construction material composition according to any one of claims 1 to 7, comprising:

9. a) the Portland cement clinker in an amount of 30 to 40 dry weight percent based on the total dry weight of the construction material composition; b) the supplemental cementitious material in an amount of greater than 30% to 45% by dry weight, based on the total dry weight of the building material composition; c) the calcium carbonate phase in an amount of 20-30% by dry weight based on the total dry weight of the construction material composition; d) 2.5 to 7 wt. % SO , based on the total dry weight of the construction material composition. ３ the sulfate source in an amount of e) the CaO and SiO of the hardening accelerator A based on the total dry weight of the construction material composition ２ and the curing accelerator A in an amount of 0.5 to 5% by weight based on the total weight of the curing accelerator A and the curing accelerator A. The construction material composition according to any one of claims 1 to 7, comprising:

10. a) Portland cement clinker in an amount of 20-30% by dry weight based on the total dry weight of the construction material composition; b) the supplemental cementitious material in an amount of greater than 30% to 50% by dry weight, based on the total dry weight of the building material composition; c) the calcium carbonate phase in an amount of 20 to 40% by dry weight, based on the total dry weight of the construction material composition; d) 2.5 to 7 wt. % SO , based on the total dry weight of the construction material composition. ３ an amount of said sulfate source; e) the CaO and SiO of the hardening accelerator A based on the total dry weight of the construction material composition ２ and the curing accelerator A in an amount of 1.0 to 5% by weight based on the total weight of the The construction material composition according to any one of claims 1 to 7, comprising:

11. a) the Portland cement clinker in an amount of 15 to 47 dry weight percent based on the total dry weight of the building material composition; b) the supplemental cementitious material in an amount of greater than 30% to 70% by dry weight, based on the total dry weight of the building material composition; c) the calcium carbonate phase in an amount of 5 to 20% by dry weight, based on the total dry weight of the construction material composition; d) 2.5 to 7 wt. % SO , based on the total dry weight of the construction material composition. ３ an amount of said sulfate source; e) the CaO and SiO of the hardening accelerator A based on the total dry weight of the construction material composition ２ and the curing accelerator A in an amount of 0.1 to 5% by weight based on the total weight of the and preferably the supplemental cementitious material comprises at least two different supplemental cementitious materials.

12. and / or further comprising at least one additive, said at least one additive being preferably selected from the group consisting of inorganic carbonates, alkali metal sulfates, polymeric dispersants, set accelerators, set retarders, thickeners and stabilizers or mixtures of two or more thereof; and / or further comprising at least one polymeric dispersant, in particular a polycarboxylate ether, a phosphorylated polycondensate or a dispersant containing sulfonic acid and / or sulfonate groups; and / or at least one polymeric dispersant which is a sulfonic acid and / or sulfonate group-containing dispersant selected from the group consisting of lignosulfonates, melamine formaldehyde sulfonate condensates, beta-naphthalene sulfonic acid condensates, sulfonated ketone-formaldehyde condensates, and copolymers comprising sulfo group-containing units and / or sulfonate group-containing units and carboxylic acid and / or carboxylate group-containing units; The construction material composition according to any one of claims 1 to 11, further comprising at least one curing accelerator B.

13. 1. Use of a hardening accelerator A containing particles of calcium and silicon in a molar ratio of Ca / Si of 0.1 to 2.2 in a construction material composition comprising up to 55% by dry weight of Portland cement clinker based on the total dry weight of the construction material composition, wherein the hardening accelerator A is used in the construction material composition to reduce the CaO and SiO of the hardening accelerator A to 0.1 to 2.2 based on the total dry weight of the construction material composition. ２ and the construction material composition is as claimed in any one of claims 1 to 12.

14. A mortar or concrete comprising the construction material composition according to any one of claims 1 to 12.

15. 13. A process for producing a construction material composition according to any one of claims 1 to 12, wherein the calcium carbonate phase is provided as a powder and the accelerator A is provided as a suspension.

Images