Heatable windshield

Abstract

To provide a coated article.SOLUTION: A coated article includes a substrate, a first dielectric layer, a first metallic layer, a first primer layer, a second dielectric layer, a second metallic layer, a second primer layer, a third dielectric layer, a third primer layer, a third metallic layer, a fourth dielectric layer, a fourth metallic layer, a fourth primer layer, and a fifth dielectric layer. The total thickness of the metallic layers is at least 30 nanometers and at most 60 nanometers.SELECTED DRAWING: Figure 4a

Description

[Technical Field]

[0001] CROSS-REFERENCE TO RELATED APPLICATIONS This application claims priority to and claims priority to U.S. Provisional Application No. 62 / 976,645, filed February 14, 2020, and U.S. Provisional Application No. 62 / 825,326, filed March 28, 2019, the disclosures of which are incorporated by reference.

[0002] FIELD OF THE INVENTION The present invention relates generally to vehicle transparencies, such as vehicle windshields, and in one particular embodiment, to heatable vehicle windshields. [Background technology]

[0003] Technical considerations When an electric current is passed through the conductors on a laminated vehicle windshield, the temperature of the windshield increases. This is particularly useful in colder climates for windshield defogging and for melting ice and / or snow. In a wire heated windshield, an electrically conductive fine wire is placed between the windshield plies. The wire is connected to a power source, such as a conventional 14-volt vehicle alternator. The wire generates 5 to 7 watts per square decimeter (W / dm 2 ) of the windshield has a resistance low enough to provide a power density of 1000 W.

[0004] A problem with wire-heated windshields is that the wires can be visible to vehicle occupants, which is aesthetically undesirable and can impair visibility through the windshield. If the wire diameter is reduced to reduce wire visibility, the number of wires must increase to maintain a desired power density, which disadvantageously reduces the total solar energy transmitted (TSET) through the windshield. As the windshield height increases, the wires must be longer to maintain a desired power density. Longer wires are also undesirable from an aesthetic and / or transmittance perspective.

[0005] Some heated windshields use transparent conductive coatings rather than wires. However, these coatings have their own drawbacks. For example, conventional heated windshield coatings typically have a sheet resistance of 2 ohms per square (Ω / □) or greater. A conventional 14V (80 amp, 1,120 watt) alternator does not provide sufficient voltage to power conventional heated windshield coatings to temperatures sufficient for de-icing. Therefore, for vehicles with these coatings, the vehicle must be modified to increase the available voltage. For example, the alternator may be replaced with a 42V alternator, or a DC-DC converter may be added to increase the voltage from a 14V alternator. However, these solutions increase the cost and complexity of the vehicle's electrical system. [Prior art documents] [Patent documents]

[0006] [Patent Document 1] U.S. Patent No. 4,466,562 [Patent Document 2] U.S. Patent No. 4,671,155 [Patent Document 3] U.S. Patent No. 4,746,347 [Patent Document 4] U.S. Patent No. 4,792,536 [Patent Document 5] U.S. Patent No. 5,030,593 [Patent Document 6] U.S. Patent No. 5,030,594 [Patent Document 7] U.S. Patent No. 5,240,886 [Patent Document 8] U.S. Patent No. 5,385,872 [Patent Document 9] U.S. Patent No. 5,393,593 [Patent Document 10] U.S. Patent No. 4,287,107 [Patent Document 11] U.S. Patent No. 3,762,988 [Patent Document 12] U.S. Patent No. 5,796,055 [Patent Document 13] U.S. Patent No. 4,379,040 [Patent Document 14] U.S. Patent No. 4,861,669 [Patent Document 15] U.S. Patent No. 4,898,789 [Patent Document 16] U.S. Patent No. 4,898,790 [Patent Document 17] U.S. Patent No. 4,900,633 [Patent Document 18] U.S. Patent No. 4,920,006 [Patent Document 19] U.S. Patent No. 4,938,857 [Patent Document 20] U.S. Patent No. 5,328,768 [Patent Document 21] U.S. Patent No. 5,492,750 [Patent Document 22] U.S. Patent Application No. 10 / 007,382 [Patent Document 23] U.S. Patent Application No. 10 / 133,805 [Patent Document 24] U.S. Patent Application No. 10 / 397,001 [Patent Document 25] U.S. Patent Application Serial No. 10 / 422,094 [Patent Document 26] U.S. Patent Application Serial No. 10 / 422,095 [Patent Document 27] U.S. Patent Application Serial No. 10 / 422,096 Summary of the Invention [Problem to be solved by the invention]

[0007] It would therefore be desirable to provide a transparency that reduces or eliminates at least some of the problems associated with conventional heatable transparencies. [Means for solving the problem]

[0008] The present invention is directed to reducing the sheet resistance of coated transparencies by adding a metallic silver layer to the coating stack. Specifically, the total amount of silver in the coating stack is 30 nm to 60 nm; 35 to 47 nm; 35 to 43 nm; or 40 to 47 nm. As the silver thickness increases, the sheet resistance decreases. However, if the total thickness of the silver layer in the coating is too thick, the transmittance drops below 70%, which is unacceptable. Furthermore, if the total silver thickness is too thick, the glass appears reddish, which is undesirable. Therefore, the present invention is directed to a coating stack having a total silver thickness sufficient to provide a sheet resistance that allows de-icing with a 14V AC generator, and having a light transmittance of greater than 70%, preferably greater than 70.5%, and more preferably greater than 71%.

[0009] The present invention relates to a coated article comprising a substrate, the substrate being coated with at least one dielectric layer and at least one metal layer, the at least one metal layer having a total thickness of at least 30 nm and no more than 60 nm, at least 35 nm and no more than 47 nm, at least 35 nm and no more than 43 nm, or at least 40 nm and no more than 47 nm.

[0010] The present invention relates to a coated article. The coated article includes a substrate. A first dielectric layer is disposed on at least a portion of the substrate. A first metal layer is disposed on at least a portion of the first dielectric layer. A second dielectric layer is disposed on at least a portion of the first primer layer. A second metal layer is disposed on at least a portion of the second dielectric layer. A third dielectric layer is disposed on at least a portion of the second primer layer. A third metal layer is disposed on at least a portion of the third dielectric layer. A fourth dielectric layer is disposed on at least a portion of the third primer layer. The total thickness of the metal layers is at least 30 nm and not more than 60 nm. The present invention may optionally further include a fourth metal layer disposed on the fourth dielectric layer, and a fifth dielectric layer disposed on at least a portion of the fourth metal layer.

[0011] In another embodiment, the invention relates to a coated article. The coated article includes a substrate. A first dielectric layer is disposed on at least a portion of the substrate. A first metal layer is disposed on at least a portion of the first dielectric layer. A first primer layer is disposed on at least a portion of the first metal layer. A second dielectric layer is disposed on at least a portion of the first primer layer. A second metal layer is disposed on at least a portion of the second dielectric layer. A second primer layer is disposed on at least a portion of the second metal layer. A third dielectric layer is disposed on at least a portion of the second primer layer. A third metal layer is disposed on at least a portion of the third dielectric layer. A third primer layer is disposed on at least a portion of the third metal layer. A fourth dielectric layer is disposed on at least a portion of the third primer layer. The total thickness of the metal layers is at least 30 nm and no more than 60 nm. The present invention may optionally further include a fourth metal layer disposed on the fourth dielectric layer, a fourth primer layer disposed on the fourth metal layer, and a fifth dielectric layer disposed on at least a portion of the fourth primer layer.

[0012] In another embodiment, the present invention relates to a coated article. The coated article includes a substrate. A first dielectric layer is disposed on at least a portion of the substrate. A first metal layer is disposed on at least a portion of the first dielectric layer. A second dielectric layer is disposed on at least a portion of the first primer layer. A second metal layer is disposed on at least a portion of the second dielectric layer. A third dielectric layer is disposed on at least a portion of the second primer layer. A third metal layer is disposed on at least a portion of the third dielectric layer. A fourth dielectric layer is disposed on at least a portion of the third primer layer. The article has a sheet resistance of 0.850 ohms per square or less. The present invention may optionally further include a fourth metal layer disposed on the fourth dielectric layer, and a fifth dielectric layer disposed on at least a portion of the fourth metal layer.

[0013] In another embodiment, the invention relates to a coated article. The coated article includes a substrate. A first dielectric layer is disposed on at least a portion of the substrate. A first metal layer is disposed on at least a portion of the first dielectric layer. A first primer layer is disposed on at least a portion of the first metal layer. A second dielectric layer is disposed on at least a portion of the first primer layer. A second metal layer is disposed on at least a portion of the second dielectric layer. A second primer layer is disposed on at least a portion of the second metal layer. A third dielectric layer is disposed on at least a portion of the second primer layer. A third metal layer is disposed on at least a portion of the third dielectric layer. A third primer layer is disposed on at least a portion of the third metal layer. A fourth dielectric layer is disposed on at least a portion of the third primer layer. The article has a sheet resistance of 0.850 ohms per square or less. The present invention may optionally further include a fourth metal layer disposed on the fourth dielectric layer, a fourth primer layer disposed on the fourth metal layer, and a fifth dielectric layer disposed on at least a portion of the fourth primer layer.

[0014] In another embodiment, the present invention relates to a coated article. The coated article includes a first substrate having a first surface and a second surface. A second substrate including a third surface and a fourth surface is disposed on at least a portion of the first substrate. A coating is disposed on either the second surface or the third surface. The coating has a first dielectric layer disposed on at least a portion of the second surface or the third surface. A first metal layer is disposed on at least a portion of the first dielectric layer. A second dielectric layer is disposed on at least a portion of the first metal layer. A second metal layer is disposed on at least a portion of the second dielectric layer. A third dielectric layer is disposed on at least a portion of the second metal layer. A third metal layer is disposed on at least a portion of the third dielectric layer. The coated substrate has a visible light reflectance of 10% or less. The present invention may optionally further include a fourth metal layer disposed on the fourth dielectric layer, and a fifth dielectric layer disposed on at least a portion of the fourth metal layer.

[0015] In another embodiment, the invention relates to a coated article. The coated article includes a first substrate having a first surface and a second surface. A second substrate including a third surface and a fourth surface is disposed on at least a portion of the first substrate. A coating is disposed on either the second surface or the third surface. The coating has a first dielectric layer disposed on at least a portion of the second surface or the third surface. A first metal layer is disposed on at least a portion of the first dielectric layer. A first primer layer is disposed on at least a portion of the first metal layer. A second dielectric layer is disposed on at least a portion of the first primer layer. A second metal layer is disposed on at least a portion of the second dielectric layer. A second primer layer is disposed on at least a portion of the second metal layer. A third dielectric layer is disposed on at least a portion of the second primer layer. A third metal layer is disposed on at least a portion of the third dielectric layer. A third primer layer is disposed on at least a portion of the third metal layer. A fourth dielectric layer is disposed on at least a portion of the third primer layer. The coated substrate has a visible light reflectance of 10% or less. The present invention may optionally further include a fourth metal layer disposed on the fourth dielectric layer, a fourth primer layer disposed on the fourth metal layer, and a fifth dielectric layer disposed on at least a portion of the fourth primer layer.

[0016] In another embodiment, the invention relates to a coated article. The coated article includes a substrate. A first dielectric layer is disposed over at least a portion of the substrate. A first metal layer is disposed over at least a portion of the first dielectric layer. A second dielectric layer is disposed over at least a portion of the first metal layer. A second metal layer is disposed over at least a portion of the second dielectric layer. The total thickness of the metal layers is at least 38 nanometers and no more than 60 nanometers.

[0017] In another embodiment, the invention relates to a coated article. The coated article includes a substrate. A first dielectric layer is disposed on at least a portion of the substrate. A first metal layer is disposed on at least a portion of the first dielectric layer. A first primer layer is disposed on at least a portion of the first metal layer. A second dielectric layer is disposed on at least a portion of the first primer layer. A second metal layer is disposed on at least a portion of the second dielectric layer. A second primer layer is disposed on at least a portion of the second metal layer. The total thickness of the metal layers is at least 30 nm and no more than 60 nm.

[0018] The present invention will now be described with reference to the following drawings, in which like reference numerals refer to like parts throughout: [Brief explanation of the drawings]

[0019] [Figure 1a] FIG. 1a is a cross-sectional view (not to scale) of a non-limiting coating according to the present invention. [Figure 1b] FIG. 1b is a cross-sectional view (not to scale) of a non-limiting coating according to the present invention. [Figure 2a] FIG. 2a is a cross-sectional view (not to scale) of a non-limiting coating according to the present invention. [Figure 2b] FIG. 2b is a cross-sectional view (not to scale) of a non-limiting coating according to the present invention. [Figure 3a] FIG. 3a is a cross-sectional view (not to scale) of a non-limiting coating according to the present invention. [Figure 3b] FIG. 3b is a cross-sectional view (not to scale) of a non-limiting coating according to the present invention. [Figure 4a] FIG. 4a is a cross-sectional view (not to scale) of a non-limiting coating according to the present invention. [Figure 4b] FIG. 4b is a cross-sectional view (not to scale) of a non-limiting coating according to the present invention. [Figure 5a] FIG. 5a is a cross-sectional view (not to scale) of a non-limiting first dielectric layer embodiment according to the present invention. [Figure 5b] FIG. 5b is a cross-sectional view (not to scale) of a non-limiting first dielectric layer embodiment according to the present invention. [Figure 6a] FIG. 6a is a cross-sectional view (not to scale) of a non-limiting second dielectric layer according to the present invention. [Figure 6b] FIG. 6b is a cross-sectional view (not to scale) of a non-limiting second dielectric layer according to the present invention. [Figure 6c] FIG. 6c is a cross-sectional view (not to scale) of a non-limiting second dielectric layer according to the present invention. [Figure 6d] FIG. 6d is a cross-sectional view (not to scale) of a non-limiting second dielectric layer according to the present invention. [Figure 7a] FIG. 7a is a cross-sectional view (not to scale) of a non-limiting third dielectric layer according to the present invention. [Figure 7b] FIG. 7b is a cross-sectional view (not to scale) of a non-limiting third dielectric layer according to the present invention. [Figure 7c] FIG. 7c is a cross-sectional view (not to scale) of a non-limiting third dielectric layer according to the present invention. [Figure 7d] FIG. 7d is a cross-sectional view (not to scale) of a non-limiting third dielectric layer according to the present invention. [Figure 8a] FIG. 8a is a cross-sectional view (not to scale) of a fourth non-limiting dielectric layer embodiment according to the present invention. [Figure 8b] FIG. 8b is a cross-sectional view (not to scale) of a fourth non-limiting dielectric layer embodiment according to the present invention. [Figure 8c] FIG. 8c is a cross-sectional view (not to scale) of a fourth non-limiting dielectric layer embodiment according to the present invention. [Figure 8d] FIG. 8d is a cross-sectional view (not to scale) of a fourth non-limiting dielectric layer embodiment according to the present invention. [Figure 9a] FIG. 9a is a cross-sectional view (not to scale) of a fifth non-limiting dielectric layer embodiment according to the present invention. [Figure 9b] FIG. 9b is a cross-sectional view (not to scale) of a fifth non-limiting dielectric layer embodiment according to the present invention. [Figure 10]FIG. 10 is a schematic diagram (not to scale) of a windshield incorporating features of the present invention. [Figure 11] FIG. 11 is an enlarged view (not to scale) of the windshield taken along line II-II in FIG. [Figure 12] FIG. 12 is a schematic diagram (not to scale) of another windshield incorporating features of the present invention. [Figure 13] FIG. 13 shows the initial nucleation of film growth on a surface. [Figure 14A] FIG. 14A is a view of a windshield illustrating the ghosting effect that occurs when using a head-up display. [Figure 14B] FIG. 14B is a view of a windshield illustrating the ghosting effect that occurs when using a head-up display. [Figure 15] FIG. 15 shows a windshield having a coating arranged to reduce ghosting in a head-up display. [Figure 16] FIG. 16 shows an example of a coating according to the present invention that is useful in a head-up display. [Figure 17] FIG. 17 is a cross-sectional view (not to scale) of a non-limiting coating according to the present invention. [Figure 18] FIG. 18 shows an example of a coating according to the present invention that is useful in a head-up display. [Figure 19] FIG. 19 shows an example of a coating according to the present invention that is useful in a head-up display. [Figure 20] FIG. 20 shows an example of a coating according to the present invention that is useful in a head-up display. [Figure 21] FIG. 21 shows an example of a coating according to the present invention that is useful in a head-up display. [Figure 22] FIG. 22 shows an example of a coating according to the present invention that is useful in a head-up display. [Figure 23]FIG. 23 shows an example of a coating according to the present invention that is useful in a head-up display. [Figure 24] FIG. 24 shows an example of a coating according to the present invention having specific color and transmittance qualities. [Figure 25] FIG. 25 is a color chart of the exemplary coating from FIG. DETAILED DESCRIPTION OF THE INVENTION

[0020] As used herein, spatial or directional terms, such as "left," "right," "inside," "outside," "top," "bottom," and the like, refer to the present invention as shown in the drawings. However, it is understood that the present invention can assume various alternative orientations, and therefore, such terms are not to be considered limiting. Furthermore, as used herein, all numbers expressing dimensions, physical properties, processing parameters, quantities of ingredients, reaction conditions, and the like, used in the specification and claims, are understood to be modified in all instances by the term "about." Accordingly, unless indicated to the contrary, the numerical values ​​set forth in the following specification and claims may vary depending on the desired properties sought to be obtained by the present invention. At the very least, and without attempting to limit the application of the doctrine of equivalents to the scope of the claims, each numerical value should be construed in light of at least the number of reported significant digits and by applying ordinary rounding techniques. Furthermore, all ranges disclosed herein are understood to encompass the beginning and ending values ​​of the range, and any and all subranges subsumed within the range. For example, a stated range of "1 to 10" should be considered to include any and all subranges between (and including) the minimum value of 1 and the maximum value of 10, i.e., all subranges beginning with a minimum value of 1 or greater and ending with a maximum value of 10 or less, e.g., 1 to 3.3, 4.7 to 7.5, 5.5 to 10, etc. Furthermore, as used herein, the terms "formed on," "deposited on," or "provided on" mean formed, deposited, or provided on a surface, but not necessarily in contact with the surface. For example, a coating layer "formed on" a substrate does not exclude the presence of one or more other coating layers or films of the same or different composition located between the formed coating layer and the substrate. As used herein, the terms "polymer" or "macromolecule" include oligomers, homopolymers, copolymers, and terpolymers, e.g., polymers formed from two or more monomers or polymers. The terms "visible region" or "visible light" refer to electromagnetic radiation having wavelengths ranging from 380 nm to 800 nm. The terms "infrared region" or "infrared" refer to electromagnetic radiation having wavelengths ranging from greater than 800 nm to 100,000 nm.The terms "ultraviolet region" or "ultraviolet" refer to electromagnetic energy having wavelengths in the range of 300 nm to less than 380 nm. Additionally, all documents, including but not limited to, issued patents and patent applications, referenced herein are deemed "incorporated by reference" in their entirety. As used herein, the term "film" refers to a coating region of a desired or selected coating composition. A "layer" can include one or more "films," and a "coating" or "coating stack" can include one or more "layers." While silicon is not traditionally considered a metal, the terms "metal" and "metal oxide" include silicon and silica, respectively, as well as traditionally recognized metals and metal oxides. Unless otherwise indicated, thickness values ​​are geometric thickness values.

[0021] The discussion of the present invention may describe certain features as being "particularly" or "preferably" within certain limits (e.g., "preferably," "more preferably," or "most preferably" within certain limits). It is understood that the invention is not limited to these particular or preferred limits, but rather encompasses the full scope of the present disclosure.

[0022] A non-limiting heatable transparency 100 (e.g., an automobile windshield) incorporating features of the present invention is shown in Figures 10 and 11. The transparency 10 can have any desired visible, infrared, or ultraviolet transmission and reflectance. For example, the transparency 100 can have any desired amount of visible light transmission, such as from greater than 0% to 100%, e.g., greater than 70%. For windshield and front sidelight areas in the United States, visible light transmission is typically 70% or greater. For privacy areas such as rear seat sidelights and rear windows, visible light transmission can be lower than that for windshields, e.g., less than 70%.

[0023] As seen in FIG. 11 , the transparency 100 includes a first ply or first substrate 12 having a first major surface, i.e., outer major surface 14 (No. 1 surface), facing the vehicle exterior, and an opposite second or inner major surface 16 (No. 2 surface). The transparency 100 also includes a second ply or second substrate 110 having an outer (first) major surface 112 (No. 4 surface) and an inner (second) major surface 114 (No. 3 surface). This numbering of the ply surfaces reflects practice in the automotive industry. The first and second plies 12, 110 may be bonded together in any suitable manner, such as by a conventional interlayer 108. Although not required, a conventional edge sealant may be applied around the periphery of the laminated transparency 10 during and / or after lamination in any desired manner. A decorative band, such as an opaque, translucent, or colored shade band 102 (shown in FIG. 11 ), e.g., a ceramic band, can be provided on at least one surface of the plies 12, 110, e.g., around the inner major surface 16 of the first ply 12. An electrically conductive coating 10 is formed on at least a portion of the plies 12, 110, e.g., on the No. 2 surface 16 or the No. 3 surface 114. A bus bar assembly 120 (FIG. 10) is in electrical contact with the conductive coating 10. The bus bar assembly 120 is also connected to a power source 122 (FIG. 10 ), which will be discussed in more detail below. In one non-limiting embodiment of the present invention, the power source 122 can be a conventional vehicle alternator, for example, configured to provide approximately 14 volts. Thus, in the implementation of this non-limiting embodiment of the present invention, a DC-DC power converter is not present. In one non-limiting example, power supply 38 may be a 42 volt DC alternator, or a DC-DC converter may be added to step up the voltage from a 14 volt alternator to a sufficient level, for example, 42 volts DC.

[0024] In the broad implementation of the present invention, the plies 12, 110 of the transparency 100 can be of the same or different materials. The plies 12, 110 can comprise any desired material having any desired properties. For example, one or more of the plies 12, 110 can be transparent or translucent to visible light. "Transparent" means having a visible light transmittance of greater than 0% to 100%. Alternatively, one or more of the plies 12, 110 can be translucent. "Translucent" means allowing electromagnetic energy (e.g., visible light) to pass through rather than just diffusing it so that objects on the opposite side of the viewer are not clearly visible. Examples of suitable materials include, but are not limited to, plastic substrates (e.g., acrylic polymers such as polyacrylates; polyalkyl methacrylates such as polymethyl methacrylate, polyethyl methacrylate, polypropyl methacrylate; polyurethanes; polycarbonates; polyalkyl terephthalates such as polyethylene terephthalate (PET), polypropylene terephthalate, polybutylene terephthalate; polysiloxane-containing polymers; or copolymers of any monomers therefor, or any mixtures thereof); ceramic substrates; glass substrates; or mixtures or combinations of any of the above. For example, one or more of the plies 12, 110 can include conventional soda-lime silicate glass, borosilicate glass, or leaded glass. The glass may be clear glass. "Clear glass" means untinted or uncolored glass. Alternatively, the glass may be tinted or otherwise colored glass. The glass may be annealed glass or heat-treated glass. As used herein, the term "heat-treated" means tempered or at least partially tempered. The glass may be of any type, such as conventional float glass, and may be of any composition having any optical properties, for example, any values ​​of visible transmission, ultraviolet transmission, infrared transmission and / or total solar energy transmission."Float glass" means glass formed by the conventional float process in which molten glass is deposited onto a molten metal bath and controlled cooled to form a float glass ribbon. The ribbon is then cut and / or shaped and / or heat treated, if desired. Examples of float glass processes are disclosed in U.S. Patent Nos. 4,466,562 and 4,671,155. The first and second plies 12, 110 may each be, for example, clear float glass, or tinted or colored glass, or one ply 12, 110 may be clear glass and the other ply 12, 110 may be colored glass. Although not limiting to the present invention, examples of glass suitable for the first ply 12 and / or second ply 110 are described in U.S. Patent Nos. 4,746,347; 4,792,536; 5,030,593; 5,030,594; 5,240,886; 5,385,872; and 5,393,593. The first and second plies 12, 18 may be of any desired dimensions, such as length, width, shape, or thickness. In one exemplary automotive transparency, the first and second plies may each be 1 mm to 10 mm thick, e.g., 1 mm to 5 mm thick, or 1.5 mm to 2.5 mm, or 1.8 mm to 2.3 mm. In one non-limiting example, the first ply 12 and / or the second ply 110 may have a visible light transmittance of greater than 90%, e.g., greater than 91%, at a reference wavelength of 550 nm. The glass composition for the first ply 12 and / or the second ply 110 may have a total iron content in the range of greater than 0 wt% to 0.2 wt% and / or a redox ratio in the range of 0.3 to 0.6.

[0025] In one non-limiting example, one or both plies 12, 110 can have high visible light transmittance at a reference wavelength of 550 nanometers (nm). By "high visible light transmittance" is meant a visible light transmittance at 550 nm of 85% or more, e.g., 87% or more, e.g., 90% or more, e.g., 91% or more, e.g., 92% or more, at 5.5 mm equivalent thickness for glass having a sheet thickness of 2 mm to 25 mm. Glasses particularly useful in the practice of the present invention are disclosed in U.S. Patent Nos. 5,030,593 and 5,030,594.

[0026] The interlayer 108 may be of any desired material and may include one or more layers or plies. The interlayer 108 may be a polymeric or plastic material, such as a multilayer thermoplastic material including polyvinyl butyral, plasticized polyvinyl chloride, or polyethylene terephthalate. Suitable interlayer materials are disclosed, for example, but not limited to, U.S. Pat. Nos. 4,287,107 and 3,762,988. The interlayer 108 secures the first and second plies 12, 1101 together, provides energy absorption, reduces noise, and increases the strength of the laminate structure. The interlayer 108 may also be a sound-absorbing or sound-deadening material, for example, as described in U.S. Pat. No. 5,796,055. The interlayer 108 may have a solar control coating disposed thereon or incorporated therein, or may include a pigmented material that reduces solar energy transmission.

[0027] The coating 10 is an electrically conductive coating deposited on at least a portion of a major surface of one of the glass plies 12, 110, for example, the inner surface 16 of the outer glass ply 12 (FIG. 11) or the outer surface 112 of the inner glass ply 110. The conductive coating 10 may include three or four metal films disposed between dielectric layers applied sequentially over at least a portion of one of the glass plies 12, 110. The conductive coating 10 may be a heat and / or radiation reflective coating and may have one or more coating layers or films of the same or different composition and / or functionality. As used herein, the term "film" refers to a coating region of a desired or selected coating composition. A "layer" may include one or more "films," and a "coating" or "coating stack" may include one or more "layers." The conductive coating 30 may be a multilayer coating including three or four metal layers.

[0028] Non-limiting examples of suitable conductive coatings include one or more anti-reflective coating films, typically comprising a dielectric or anti-reflective material transparent to visible light, such as a metal oxide or an oxide of a metal alloy. The conductive coating 10 may also comprise three or four metal layers comprising a reflective metal, e.g., a noble metal such as gold, copper, or silver, or a combination or alloy thereof, and may further comprise a primer layer or barrier film, such as titanium or a titanium-aluminum alloy, as known in the art, located above and / or optionally below the metal reflective layer. The conductive coating 10 may have three or four metal layers; or may have at least three metal layers; or may have four or fewer metal layers. For example, the conductive coating 10 may consist of four metal layers; or may consist of three metal layers. In one non-limiting example, one or more of the metal layers may comprise silver.

[0029] The conductive coating 10 can be deposited by any conventional method, including, but not limited to, conventional chemical vapor deposition (CVD) and / or physical vapor deposition (PVD) methods. Examples of CVD methods include spray pyrolysis. Examples of PVD methods include electron beam evaporation and vacuum sputtering (e.g., magnetron sputter vapor deposition (MSVD)). Other coating methods, including, but not limited to, sol-gel deposition, can also be used. In one non-limiting example, the conductive coating 10 can be deposited by MSVD. Examples of MSVD coating devices and methods will be well understood by those skilled in the art and are described, for example, in U.S. Patent Nos. 4,379,040; 4,861,669; 4,898,789; 4,898,790; 4,900,633; 4,920,006; 4,938,857; 5,328,768; and 5,492,750.

[0030] A non-limiting coating suitable for the present invention is shown in FIGS. 1a and 1b. This coating includes one metal layer and one primer layer disposed between two dielectric layers. It includes a base layer or first dielectric layer 20 disposed on or in direct contact with at least a portion of a major surface of the substrate (e.g., No. 2 surface 16 of first ply 12 or No. 3 surface 114 of second ply 110). A first metal layer 28 is disposed on or in direct contact with at least a portion of first dielectric layer 20. A first primer layer 30 may be disposed on or in direct contact with at least a portion of first metal layer 28. A second dielectric layer 32 is disposed on or in direct contact with first primer layer 30. A protective layer 84 may be disposed on or in direct contact with second dielectric layer 32. An optional stress layer 82 may be disposed between second dielectric layer 32 and protective layer 84.

[0031] Another non-limiting coating suitable for the present invention is shown in Figures 2a and 2b. This coating includes two metal layers and two primer layers disposed between dielectric layers. It includes a base layer or first dielectric layer 20 disposed on or in direct contact with at least a portion of a major surface of the substrate (e.g., No. 2 surface 16 of first ply 12 or No. 3 surface 114 of second ply 110). A first metal layer 28 is disposed on or in direct contact with at least a portion of first dielectric layer 20. A first primer layer 30 may be disposed on or in direct contact with at least a portion of first metal layer 28. A second dielectric layer 32 is disposed on or in direct contact with first primer layer 30. A second metal layer 42 is disposed on or in direct contact with at least a portion of second dielectric layer 32. A second primer layer 44 may be disposed on or in direct contact with second metal layer 42. A third dielectric layer 46 is disposed on or in direct contact with the second primer layer 44. A protective layer 84 may be disposed on or in direct contact with the third dielectric layer 46. An optional stress layer 82 may be disposed between the third dielectric layer 46 and the protective layer 84.

[0032] A non-limiting exemplary coating suitable for the present invention is shown in Figures 3a and 3b. This exemplary coating includes three metal layers disposed between dielectric layers. It includes a base layer or first dielectric layer 20 disposed on or in direct contact with at least a portion of a major surface of the substrate (e.g., No. 2 surface 16 of first ply 12 or No. 3 surface 114 of second ply 110). A first metal layer 28 is disposed on or in direct contact with at least a portion of first dielectric layer 20. An optional first primer layer 30 may be disposed on or in direct contact with at least a portion of first metal layer 28. A second dielectric layer 32 is disposed on or in direct contact with first primer layer 44 or first metal layer 28. A second metal layer 42 is disposed on or in direct contact with at least a portion of second dielectric layer 32. An optional second primer layer 44 may be disposed on or in direct contact with the second metal layer 42. A third dielectric layer 46 may be disposed on or in direct contact with the second primer layer 44 or the second metal layer 42. A third metal layer 56 is disposed on the third dielectric layer 46. An optional third primer layer 58 may be disposed on or in direct contact with the third metal layer 56. A fourth dielectric layer 60 may be disposed on or in direct contact with the third primer layer or the third metal layer. A protective layer 84 may be disposed on or in direct contact with the fourth dielectric layer 60. An optional stress layer 82 may be disposed between the fourth dielectric layer 60 and the protective layer 84.

[0033] The first dielectric layer 20 can include one or more films of an antireflective material and / or a dielectric material, such as, but not limited to, a metal oxide, a metal alloy oxide, a nitride, an oxynitride, or a mixture thereof. The first dielectric layer 20 can be transparent to visible light. Examples of metal oxides suitable for the first dielectric layer 20 include oxides of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, silicon, gallium, and vanadium, and mixtures thereof. These metal oxides can contain small amounts of other materials, such as manganese in bismuth oxide or tin in indium oxide. Alternatively, oxides of metal alloys or metal mixtures can be used, such as oxides containing zinc and tin (e.g., zinc stannate); oxides of indium-tin alloys; silicon nitride; aluminum silicon nitride; or aluminum nitride. Additionally, doped metal oxides, such as antimony- or indium-doped tin oxide, or nickel- or boron-doped silicon oxide, can be used. In one non-limiting example, the first film 22 can be a zinc / tin alloy oxide. The zinc / tin alloy oxide can be obtained by magnetron sputtering vacuum deposition from a zinc and tin cathode, which can contain zinc and tin in proportions of 10 wt% to 90 wt% zinc and 90 wt% to 10 wt% tin. One suitable metal alloy oxide that can be present in the first film 42 is zinc stannate. "Zinc stannate" refers to Zn x Sn 1-x O 2-x (Formula 1) where "x" varies from greater than 0 to less than 1. For example, "x" can be greater than 0 and any fraction or decimal number from greater than 0 to less than 1. For example, when x=2 / 3, Formula 1 represents Zn 2 / 3 Sn 1 / 3 O 4 / 3 which is more commonly written as Zn2SnO4. Zinc stannate-containing films have a large amount of one or more of the forms of Formula 1 in the film.

[0034] The second film 24 can be a zinc-containing film, such as zinc oxide. Zinc oxide films can be deposited from zinc cathodes that include other materials to improve the sputtering properties of the cathode. For example, the zinc cathode can include a small amount of tin (e.g., less than 10 wt%, e.g., greater than 0-5 wt%) to improve sputtering. In this case, the resulting zinc oxide film would be considered to include a small percentage of tin oxide, e.g., 0-10 wt% or less tin oxide, e.g., 0-5 wt% tin oxide. An oxide layer sputtered from a zinc / tin cathode having 95 percent zinc and 5 percent tin is referred to herein as Zn. 0.95 S0 .5 O 1.05 and is referred to as a zinc oxide film. It is believed that a small amount of tin (e.g., less than 10 wt%) in the cathode forms a small amount of tin oxide in the second film 44, which contains primarily zinc oxide. In one non-limiting example, the first film 42 is zinc stannate and the second film 44 is zinc oxide (Zn 0.95 Sn 0.5 O 1.05). In an exemplary, non-limiting example, second film 24 is a film comprised of at least one of aluminum zinc oxide, gallium zinc oxide, indium zinc oxide, indium tin oxide, or vanadium zinc oxide. The aluminum zinc oxide, gallium zinc oxide, indium zinc oxide, indium tin oxide, or vanadium zinc oxide film is deposited from a zinc cathode that includes other materials to improve the sputtering characteristics of the cathode. For example, the aluminum zinc oxide, gallium zinc oxide, indium zinc oxide, indium tin oxide, or vanadium zinc oxide film may include an additional small amount (e.g., less than 10 wt%, e.g., greater than 0 to 5 wt%) of tin to improve sputtering. It is believed that the small amount of tin in the cathode (e.g., less than 10 wt%) forms a small amount of tin oxide in second film 24. In one non-limiting example, first film 22 comprises zinc stannate, and second film 24 comprises aluminum zinc oxide, gallium zinc oxide, indium zinc oxide, indium tin oxide, or vanadium zinc oxide. In one non-limiting example, first dielectric layer or second dielectric layer comprises a silicon nitride film. In some examples, such as FIG. 5b, first dielectric layer 20 includes only first film 22 and second film 24.

[0035] The first dielectric layer 20 may have a total thickness of 1,000 Å or less, such as 800 Å or less, such as 200 Å to 800 Å, 300 Å to 600 Å, such as 400 Å to 550 Å, such as 410 Å to 500 Å, or such as 420 Å to 470 Å, such as 422 Å to 463 Å.

[0036] As shown in FIG. 5a, a first seed film 26 may be disposed on or in direct contact with at least a portion of the second film of the first dielectric layer 20. The first seed film 26 may be adjacent to or in direct contact with the first metal layer 28, and may be between the first dielectric layer 20 and the first metal layer 28. The first seed film 26 is a film composed of at least one of aluminum, aluminum silver, aluminum zinc, zinc, zinc, zinc tin, germanium, nickel, magnesium, silicon carbide, aluminum nitride, indium zinc, vanadium zinc, gallium zinc, indium tin, niobium, zirconium, tantalum, molybdenum, aluminum-doped silver, silver, silver zinc, titanium aluminum, mixtures thereof, alloys thereof, oxides thereof, suboxides thereof, nitrides thereof, and subnitrides thereof. In one embodiment, the first seed film 26 includes aluminum zinc, vanadium zinc, zinc, silver zinc, metals thereof, alloys thereof, oxides thereof, or suboxides thereof. In another embodiment, first seed film 26 comprises gallium zinc, indium zinc, indium tin, a metal thereof, an alloy thereof, an oxide thereof, a nitride thereof, a subnitride thereof, or a suboxide thereof.

[0037] Non-limiting example compositions of the seed layer can be found in Table 1. In certain examples, a portion of the seed layer is formed in an O2 atmosphere with a specified flow rate to form an atmosphere of 1% to 70% O2 with the balance being argon. The flow rate is an approximation of the amount of O2 in the atmosphere, but one skilled in the art will recognize that additional O2 may enter the coating chamber because the coating chamber is not sealed from the outside environment. In one example, the seed layer is formed from vanadium zinc (V x Zn 1-x In another embodiment, the seed layer comprises silver oxide. In another embodiment, the seed layer comprises aluminum silver (Al x Ag 1-x). In one non-limiting example, the second film 44 of the first dielectric layer is a seed layer. In some examples, the first dielectric layer 40 includes the first film 42, the second film 44, and the seed layer. The seed layer can have a total thickness ranging from 0.5 nm to 10 nm, preferably from 0.75 nm to 8 nm, and more preferably from 0.9 nm to 6 nm. [Table 1]

[0038] A first metal layer 28 may be deposited on the first dielectric layer 20. The first metal layer 28 may comprise a reflective metal, such as, but not limited to, metallic gold, copper, silver, aluminum, or mixtures, alloys, or combinations thereof. In one embodiment, the first metal layer 28 comprises a metallic silver layer. The first metal layer 28 may have a thickness ranging from 50 Å to 200 Å, preferably from 75 Å to 150 Å, more preferably from 80 Å to 120 Å, and most preferably from 90 Å to 110 Å.

[0039] An optional first primer layer 30 may be deposited over the first metal layer 28. The first primer layer 30 may be an oxygen-scavenging material, such as titanium, that may be sacrificed during the deposition process to prevent decomposition or oxidation of the first metal layer 28 during the sputtering or subsequent heating step. The oxygen-scavenging material may be selected to oxidize before the material of the first metal layer 28. Non-limiting examples of materials suitable for the primer layer include titanium, cobalt, copper, silicon, zinc, aluminum, vanadium, tungsten, tantalum, niobium, zirconium, manganese, chromium, tin, nickel, germanium, magnesium, molybdenum, silver, silicon carbide, aluminum-doped silver, aluminum zinc, vanadium zinc, tungsten tantalum, titanium niobium, zirconium niobium, tungsten niobium, aluminum niobium, aluminum titanium, tungsten titanium, tantalum titanium, zinc titanium, aluminum silver, zinc tin, indium zinc, silver zinc, mixtures thereof, combinations thereof, and alloys thereof. The primer layer material may also take the form of a metal, oxide, suboxide, nitride, and / or subnitride of any of the materials that can be used as a primer layer, as listed above. At least a portion of the primer layer can be an oxide or nitride. In certain embodiments, a portion of the primer layer is a nitride.

[0040] For certain material compositions, the lower limit for one of the materials can be "greater than 0." When the lower limit is "greater than 0," this means that the weight percent (wt%) of the material is not equal to zero and can be any wt% between greater than 0 and the upper wt% limit. For some material compositions, the composition can change before and after the layer is heated. This is due to the material reacting with substances in the atmosphere, which changes the wt% distributed between the materials. Therefore, a particular material composition can have pre-heating ("before heating") and post-heating ("after heating") weight percentage measurements that account for this change. Non-limiting example compositions of primer layers can be found in Table 2. Some materials may only have pre-heating measurements or only post-heating measurements, depending on which measurement is more significant. [Table 2-1] [Table 2-2]

[0041] When titanium is used as the first primer layer 28, it is believed that the titanium will preferentially oxidize to titanium dioxide before oxidizing the underlying silver layer. In one embodiment, the first primer layer 28 has a thickness in the range of 5 Å to 50 Å, such as 10 Å to 35 Å, such as 15 Å to 35 Å, such as 10 Å to 20 Å, such as 10 Å to 30 Å, such as 20 Å to 30 Å, or such as 30 Å to 40 Å.

[0042] The second dielectric layer 32 can be deposited on the first metal layer 28 or the first primer layer 30 (if present). In the non-limiting illustrative example of FIGS. 6a-d, the second dielectric layer 32 includes a first film 34 deposited on the first metal layer 28 or the first primer layer 30. The first film 34 can include an oxide, nitride, oxynitride, or mixtures thereof of a metal selected from the group consisting of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, silicon, aluminum, gallium, vanadium, and mixtures thereof. In one example, the first film 34 includes zinc oxide. In another example, the first film 34 includes aluminum zinc oxide. In another example, the first film 34 includes indium zinc oxide. In another example, the first film 34 includes gallium zinc oxide. In another example, the first film 34 includes indium tin oxide. In another embodiment, the first film 34 comprises vanadium zinc oxide.

[0043] A second film 36 can be deposited on the first film 34. The second film 36 comprises an oxide, nitride, oxynitride, or mixtures thereof of a metal selected from the group consisting of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, silicon, aluminum, gallium, vanadium, and mixtures thereof. In one embodiment, the second film 36 comprises zinc stannate. In some embodiments, such as that of FIG. 6b, the first film 34 and the second film 36 are the only films in the second dielectric layer 32.

[0044] An optional third film 38 may be deposited on the second film 36 to form a multi-film second dielectric layer 32. The third film 38 comprises an oxide, nitride, oxynitride, or mixtures thereof of a metal selected from the group consisting of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, silicon, aluminum, gallium, vanadium, and mixtures thereof. In one example, the third film 38 comprises zinc oxide. In another example, the third film 38 comprises indium zinc oxide. In another example, the third film 38 comprises gallium zinc oxide. In another example, the third film 38 comprises indium tin oxide. In another example, the third film 38 comprises vanadium zinc oxide. In one non-limiting example, the first dielectric layer 20 or the second dielectric layer 32 comprises a silicon nitride film. 6a and 6c, the second dielectric layer 32 includes a first film 34, a second film 36, and a third film 38. In some embodiments, such as FIG. 6a, the second dielectric layer 32 includes only the first film 34, the second film 36, and the third film 38.

[0045] The second dielectric layer 32 may have a thickness in the range of 1,500 Å or less, such as 1,200 Å or less, such as 400 Å to 1,200 Å, 500 Å to 1,100 Å, such as 600 Å to 1,000 Å, such as 700 Å to 900 Å, or such as 775 Å to 850 Å.

[0046] The second seed film 40 may be adjacent to or in direct contact with the second metal layer 42, and may be between the second dielectric layer 32 and the first metal layer 42. The second seed film 40 is a film including at least one of aluminum, aluminum silver, aluminum zinc, zinc, zinc tin, germanium, nickel, magnesium, silicon carbide, aluminum nitride, indium zinc, vanadium zinc, gallium zinc, indium tin, niobium, zirconium, tantalum, molybdenum, aluminum-doped silver, silver, silver zinc, titanium aluminum, mixtures thereof, alloys thereof, oxides thereof, suboxides thereof, nitrides thereof, and subnitrides thereof. In one example, the second seed film 40 includes aluminum zinc, vanadium zinc, zinc, silver zinc, metals thereof, alloys thereof, oxides thereof, or suboxides thereof. The composition of the seed film can be found in Table 1, previously presented.

[0047] In one embodiment, the second seed film 40 is VxZn 1-x In another embodiment, the second seed film 40 comprises an Al oxide. x Zn 1-x In another embodiment, the second seed film 40 comprises a Ga oxide. x Zn 1-x In another embodiment, the second seed film 40 comprises an In oxide. x Zn 1-x In another embodiment, the second seed film 40 comprises a Sn oxide. x In 1-x In another embodiment, the second seed film 40 comprises Ag deposited in an oxygen / argon gas environment. In another embodiment, the second seed film 40 comprises Al x Ag 1-x 6c and 6d, the second dielectric layer 32 includes the first film 34, the second film 36, and the second seed film 40. In some embodiments, such as FIG. 6d, the second dielectric layer 32 includes only the first film 34, the second film 36, and the second seed film 40. In some embodiments, such as FIG. 6c, the second dielectric layer 32 includes the first film 34, the second film 36, the third film 38, and the second seed film 40.

[0048] A second metal layer 42 may be deposited over the second dielectric layer 32. The second metal layer 42 may include any one or more reflective materials described above with respect to the first metal layer 28. In one non-limiting example, the second metal layer 42 includes silver and / or copper. The second metal layer 42 may have a thickness ranging from 75 Å to 175 Å, preferably from 100 Å to 150 Å, more preferably from 110 Å to 130 Å, and most preferably from 119 Å to 129 Å. In another practical example, the second metal layer 42 may be thicker than the first and / or third metal layers.

[0049] A second primer layer 44 can be deposited on the second metal layer 42. The second primer layer 44 can be any of the materials previously described above for the first primer layer 30 and in Table 2. Examples of materials suitable for the primer layer include titanium, silicon, cobalt, zinc, aluminum, vanadium, tungsten, tantalum, niobium, zirconium, manganese, chromium, tin, nickel, gallium, indium, germanium, magnesium, molybdenum, silver, silicon carbide, aluminum-doped silver, aluminum zinc, vanadium zinc, tungsten tantalum, titanium niobium, zirconium niobium, tungsten niobium, aluminum niobium, aluminum titanium, tungsten titanium, tantalum titanium, zinc titanium, aluminum silver, zinc tin, indium zinc, silver zinc, mixtures thereof, and alloys thereof, where the primer can be deposited as a metal and subsequently oxidized. At least a portion of the primer layer is a nitride or oxide. When silver zinc, zinc, silver zinc oxide, aluminum zinc oxide, indium zinc oxide, gallium zinc oxide, or vanadium zinc oxide is used as the first primer layer 30, it is believed to preferentially oxidize before oxidation of the underlying silver layer.

[0050] In one embodiment, the second primer layer 44 includes zinc. In another embodiment, the second primer layer 44 includes Ag. x Zn 1-x In another embodiment, the second primer layer 44 comprises an Ag oxide. x Zn 1-xIn another embodiment, the second primer layer 44 comprises Al x Zn 1-x In another embodiment, the second primer layer 44 is an In oxide. x Zn 1-x In another embodiment, the second primer layer 44 comprises a Ga oxide. x Zn 1-x In another embodiment, the second primer layer 44 comprises a V oxide. x Zn 1-x In another embodiment, the second primer layer 44 comprises an Al oxide. x Ti 1-x In another embodiment, the second primer layer 44 comprises an Al oxide. x Nb 1-x In another embodiment, the second primer layer 44 comprises an Al oxide. x Nb 1-x In another embodiment, the second primer layer 44 comprises W. x Nb 1-x In another embodiment, the second primer layer 44 comprises W. x Ti 1-x In another embodiment, the second primer layer 44 comprises a Ti oxide. x Ta 1-x In another embodiment, the second primer layer 44 comprises a Ti oxide. x Nb 1-x In another embodiment, the second primer layer 44 comprises a Ti oxide. x Nb 1-x In another embodiment, the second primer layer 44 comprises Nb x Zr 1-x In another embodiment, the second primer layer 44 comprises Ta x W 1-x In another embodiment, the second primer layer 44 comprises a W oxide. x Nb 1-x In another embodiment, the second primer layer 44 comprises a Zn oxide. x Ti 1-xIn another embodiment, the second primer layer 44 comprises a titanium oxide. The second primer layer 44 may have a thickness in the range of about 5 Å to 50 Å, such as 10 Å to 35 Å, such as 15 Å to 35 Å, such as 10 Å to 20 Å, such as 10 Å to 30 Å, such as 20 Å to 30 Å, or such as 30 Å to 40 Å.

[0051] The third dielectric layer 46 may be deposited on the second metal layer 42 or the second primer layer 44 (if present). The third dielectric layer 46 may also include one or more materials discussed above with respect to the first and second dielectric layers 20, 32. In one non-limiting example, the third dielectric layer 46 may include a first film 48. The first film 48 includes an oxide, nitride, oxynitride, or mixtures thereof of a metal selected from the group consisting of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, silicon, aluminum, gallium, vanadium, and mixtures thereof. In one example, the first film 48 includes zinc oxide. In another example, the first film 48 includes aluminum zinc oxide. In another example, the first film 48 includes indium zinc oxide. In another example, the first film 48 includes gallium zinc oxide. In another example, the first film 48 includes indium tin oxide. In another embodiment, the first film 48 comprises vanadium zinc oxide.

[0052] The third dielectric layer 46 can include a second film 50 deposited on the first film 48. In one embodiment, the second film 50 includes an oxide, nitride, oxynitride, or mixtures thereof of a metal selected from the group consisting of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, silicon, aluminum, gallium, vanadium, and mixtures thereof. In one embodiment, the second film 50 includes zinc stannate. In some embodiments, such as that of FIG. 7b, the first film 48 and the second film 50 are the only films in the third dielectric layer 46.

[0053] The third dielectric layer 46 can include an optional third film 52. The third film 52 includes an oxide, nitride, oxynitride, or mixtures thereof of a metal selected from the group consisting of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, silicon, aluminum, gallium, vanadium, and mixtures thereof. In one embodiment, the third film 52 includes zinc oxide. In another embodiment, the third film 52 includes aluminum zinc oxide. In another embodiment, the third film 52 includes indium zinc oxide. In another embodiment, the third film 52 includes gallium zinc oxide. In another embodiment, the third film 52 includes indium tin oxide. In another embodiment, the third film 52 includes vanadium zinc oxide. In some embodiments, such as those shown in FIGS. 7a and 7c, the third dielectric layer 46 includes a first film 48, a second film 50, and a third film 52. In some embodiments, such as FIG. 7 a , the third dielectric layer 46 includes only a first film 48 , a second film 50 , and a third film 52 .

[0054] In one non-limiting embodiment of the present invention, the second dielectric layer 32 and the third dielectric layer 46 have thicknesses that are within 15% of each other, such as within 10%, for example, within 5% of each other. The third dielectric layer 46 can have a thickness of 1,500 Å or less, such as 1,200 Å or less, for example, 300 Å to 1,200 Å, 400 Å to 1,100 Å, for example, 500 Å to 1,000 Å, for example, 600 Å to 900 Å, for example, 700 Å to 825 Å, or for example, 730 Å to 760 Å.

[0055] The third seed film 54 may be adjacent to and / or in direct contact with the third metal layer 56, and may be between the third dielectric layer 46 and the third metal layer 56. The third seed film 54 is a film composed of at least one of aluminum, aluminum silver, aluminum zinc, zinc, zinc tin, germanium, nickel, magnesium, silicon carbide, aluminum nitride, indium zinc, vanadium zinc, gallium zinc, indium tin, niobium, zirconium, tantalum, molybdenum, aluminum-doped silver, silver, silver zinc, titanium aluminum, mixtures thereof, alloys thereof, oxides thereof, suboxides thereof, nitrides thereof, and subnitrides thereof. The composition of the seed film can be found in Table 1, previously presented. In one example, the third seed film 54 includes aluminum zinc, vanadium zinc, zinc, silver zinc, metals thereof, alloys thereof, oxides thereof, or suboxides thereof. In another embodiment, third seed film 54 is gallium zinc, indium zinc, indium tin, a metal thereof, an alloy thereof, an oxide thereof, a nitride thereof, a subnitride thereof, or a suboxide thereof.

[0056] In another embodiment, the third seed film 54 is VxZn 1-x In another embodiment, the third seed film 54 comprises an Al oxide. x Zn 1-x In another embodiment, the third seed film 54 comprises a Ga oxide. x Zn 1-x In another embodiment, the third seed film 54 comprises an In oxide. x Zn 1-x In another embodiment, the third seed film 54 comprises a Sn oxide. x In 1-x In another embodiment, the third seed film 54 comprises Ag deposited in an oxygen / argon gas environment. In another embodiment, the third seed film 54 comprises Al x Ag 1-x7c and 7d, the third dielectric layer 46 includes a first film 48, a second film 50, and a third seed film 54. In some embodiments, the second dielectric layer 46 includes a first film 48, a second film 50, a third film 52, and a third seed film 54. The third seed film 54 can have a total thickness ranging from 0.5 nm to 10 nm, preferably from 0.75 nm to 8 nm, and more preferably from 0.9 nm to 6 nm. The coating 10 can further include a third metal layer 56 deposited on the third dielectric layer 46. The third metal layer 56 can be any of the materials discussed above with respect to the first and second metal layers. In another non-limiting embodiment, the third metal layer 56 includes aluminum-doped silver. In one non-limiting embodiment, the third metal layer 56 includes silver and / or copper. The third metal layer 56 can have a thickness ranging from 75 Å to 175 Å, preferably from 100 Å to 150 Å, more preferably from 110 Å to 130 Å, and most preferably from 118 Å to 127 Å. In one non-limiting embodiment of the present invention, the first metal layer 28 is thinner than the third metal layer 56. In another non-limiting embodiment of the present invention, the second metal layer 42 is thinner than the third metal layer 56.

[0057] In one non-limiting example, the coated article includes only the first, second, and third metal layers 28, 42, 56. There are no additional metal layers in the coated article. The metal layers can include only silver, or only silver and copper, or greater than 80 wt% silver or silver and copper.

[0058] A third primer layer 58 can be deposited on the third metal layer 56. The third primer layer 58 can be any of the primer materials previously described above for the first or second primer layer 30, 44 and in Table 2. Examples of materials suitable for the primer layer include titanium, silicon, cobalt, zinc, aluminum, vanadium, tungsten, tantalum, niobium, zirconium, manganese, chromium, tin, nickel, gallium, indium, germanium, magnesium, molybdenum, silver, silicon carbide, aluminum-doped silver, aluminum zinc, vanadium zinc, tungsten tantalum, titanium niobium, zirconium niobium, tungsten niobium, aluminum niobium, aluminum titanium, tungsten titanium, tantalum titanium, zinc titanium, aluminum silver, zinc tin, indium zinc, silver zinc, mixtures thereof, and alloys thereof, where the primer can be deposited as a metal and subsequently oxidized. At least a portion of the primer layer is a nitride or oxide. When silver zinc, zinc, silver zinc oxide, aluminum zinc oxide, indium zinc oxide, gallium zinc oxide, or vanadium zinc oxide is used as the first primer layer 30, it is believed to preferentially oxidize before oxidation of the underlying silver layer.

[0059] In one embodiment, the third primer layer 58 includes zinc. In another embodiment, the third primer layer 58 includes Ag. x Zn 1-x In another embodiment, the third primer layer 58 comprises an Ag oxide. x Zn 1-x In another embodiment, the third primer layer 58 comprises Al x Zn 1-x In another embodiment, the third primer layer 58 comprises an In oxide. x Zn 1-x In another embodiment, the third primer layer 58 comprises a Ga oxide. x Zn 1-x In another embodiment, the third primer layer 58 comprises a V x Zn 1-x In another embodiment, the third primer layer 58 comprises an Al oxide. x Ti1-x In another embodiment, the third primer layer 58 comprises an Al oxide. x Nb 1-x In another embodiment, the third primer layer 58 comprises an Al oxide. x Nb 1-x In another embodiment, the third primer layer 58 comprises W. x Nb 1-x In another embodiment, the third primer layer 58 comprises W. x Ti 1-x In another embodiment, the third primer layer 58 comprises a Ti oxide. x Ta 1-x In another embodiment, the third primer layer 58 comprises a Ti oxide. x Nb 1-x In another embodiment, the third primer layer 58 comprises a Ti oxide. x Nb 1-x In another embodiment, the third primer layer 58 comprises Nb x Zr 1-x In another embodiment, the third primer layer 58 comprises a Ta oxide. x W 1-x In another embodiment, the third primer layer 58 comprises a W oxide. x Nb 1-x In another embodiment, the third primer layer 58 comprises a Zn oxide. x Ti 1-x Contains oxides.

[0060] In one non-limiting example, the third primer layer 58 has a thickness in the range of 5 Å to 50 Å, such as 10 Å to 35 Å, for example, 15 Å to 35 Å, for example, 10 Å to 20 Å, for example, 10 Å to 30 Å, for example, 20 Å to 30 Å, for example, 30 Å to 40 Å.

[0061] A fourth dielectric layer 60 may be deposited over the third metal layer 56 (e.g., over the third primer layer 58). The fourth dielectric layer 60 may be composed of one or more metal oxide or metal alloy oxide-containing layers, such as those discussed above with respect to the first, second, or third dielectric layers 20, 32, 46. Alternatively, the fourth dielectric layer may comprise silicon nitride or silicon oxynitride. In one non-limiting example, the fourth dielectric layer 60 includes a first film 62 deposited on the third metal layer 56 or the third primer layer 58 (if present), a second film 64 deposited on the first film 62, and an optional third film 66 deposited on the second film 64. The first film 62 includes an oxide, nitride, oxynitride, or mixtures thereof of a metal selected from the group consisting of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, silicon, gallium, vanadium, and mixtures thereof. In one embodiment, first film 62 comprises zinc oxide or zinc stannate. First film 62 may be composed of an oxide, nitride, oxynitride, or mixture of one or more metals selected from the group consisting of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, silicon, gallium, vanadium, and mixtures thereof. In one embodiment, first film 62 comprises zinc oxide or zinc stannate. In another embodiment, first film 62 comprises aluminum zinc oxide. In another embodiment, first film 62 comprises indium zinc oxide. In another embodiment, first film 62 comprises gallium zinc oxide. In another embodiment, first film 62 comprises indium tin oxide. In another embodiment, first film 62 comprises vanadium zinc oxide.

[0062] The fourth dielectric layer 60 may include a second film 64 deposited on the first film 62. In one example, the second film 64 includes an oxide, nitride, oxynitride, or mixtures thereof of a metal selected from the group consisting of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, silicon, gallium, vanadium, and mixtures thereof. In one example, the second film 64 includes zinc stannate, silicon nitride, or silicon oxynitride. In some examples, such as that of FIG. 8b, the first film 62 and the second film 64 are the only films in the fourth dielectric layer 60. The fourth dielectric layer 60 may include an optional third film 66 deposited on the second film 64. The third film 66 comprises an oxide, nitride, oxynitride, or mixtures thereof of a metal selected from the group consisting of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, silicon, gallium, vanadium, and mixtures thereof. In one embodiment, the third film 66 comprises zinc oxide, silicon oxynitride, or silicon nitride. In another embodiment, the third film 66 comprises zinc oxide. In another embodiment, the third film 66 comprises aluminum zinc oxide. In another embodiment, the third film 66 comprises indium zinc oxide. In another embodiment, the third film 66 comprises gallium zinc oxide. In another embodiment, the third film 66 comprises indium tin oxide. In another embodiment, the third film 66 comprises vanadium zinc oxide. In some embodiments, such as those shown in FIGS. 8a and 8c, the fourth dielectric layer 60 comprises a first film 62, a second film 64, and a third film 66. In some embodiments, such as FIG. 8 a , the fourth dielectric layer 60 includes only a first film 62 , a second film 64 , and a third film 66 .

[0063] In one non-limiting example, the first and third films 62, 66 of the fourth dielectric layer 60 may each have a thickness in the range of about 50 Å to 200 Å, such as 75 Å to 150 Å, e.g., 100 Å. The second film 78 may have a thickness in the range of 250 Å to 900 Å, e.g., 275 Å to 800 Å, e.g., 300 Å to 775 Å, e.g., 350 Å to 710 Å.

[0064] In embodiments where the fourth dielectric layer 60 is the top or outermost dielectric layer, the fourth dielectric layer may have a thickness of 1,000 Å or less, such as 600 Å or less, for example, in the range of 200 Å to 600 Å, 250 Å to 550 Å, for example, 300 Å to 500 Å, for example, 325 Å to 475 Å, or for example, 360 Å to 390 Å. In embodiments where the fourth dielectric layer 60 is the top dielectric layer, both the first dielectric layer 20 and the fourth dielectric layer 60 may be thinner than the second dielectric layer 32 and the third dielectric layer 46.

[0065] The fourth seed film 68 may be adjacent to or in direct contact with the fourth metal layer 70, and may be between the fourth dielectric layer 60 and the fourth metal layer 70. The fourth seed film 68 is a film composed of at least one of aluminum, aluminum silver, aluminum zinc, zinc, zinc tin, germanium, nickel, magnesium, silicon carbide, aluminum nitride, indium zinc, vanadium zinc, gallium zinc, indium tin, niobium, zirconium, tantalum, molybdenum, aluminum-doped silver, silver, silver zinc, titanium aluminum, mixtures thereof, alloys thereof, oxides thereof, suboxides thereof, nitrides thereof, and subnitrides thereof. In one embodiment, the fourth seed film 68 includes aluminum zinc, vanadium zinc, zinc, silver zinc, metals thereof, alloys thereof, oxides thereof, or suboxides thereof. In another embodiment, the fourth seed film 68 includes gallium zinc, indium zinc, indium tin, metals thereof, alloys thereof, oxides thereof, nitrides thereof, subnitrides thereof, or suboxides thereof. The composition of the seed film can be found in Table 1 provided above. In another embodiment, the fourth seed film 68 is V x Zn 1-x In another embodiment, the fourth seed film 68 comprises an Al oxide. x Zn 1-x In another embodiment, the fourth seed film 68 comprises a Ga x Zn 1-x In another embodiment, the fourth seed film 68 comprises an In oxide. x Zn 1-x In another embodiment, the fourth seed film 68 comprises a Sn oxide. x In 1-xIn another embodiment, the fourth seed film 68 comprises Ag deposited in an oxygen / argon gas environment. In another embodiment, the fourth seed film 68 comprises Al x Ag 1-x 8c and 8d, the fourth dielectric layer 60 includes a first film 62, a second film 64, and a fourth seed film 68. In some embodiments, such as FIG. 8d, the fourth dielectric layer 60 includes only the first film 62, the second film 64, and the fourth seed film 68. In some embodiments, such as FIG. 8c, the fourth dielectric layer 60 includes the first film 62, the second film 64, the third film 66, and the fourth seed film 68. The fourth seed film can have a total thickness ranging from 0.5 nm to 10 nm, preferably from 0.75 nm to 8 nm, and more preferably from 0.9 nm to 6 nm.

[0066] Another non-limiting exemplary coating 10 suitable for the present invention is shown in FIGS. 4a and 4b. The coating 10 may further include a fourth metal layer 70 disposed on or in direct contact with at least a portion of the fourth dielectric layer 60. The fourth metal layer 70 may be any of the materials discussed above with respect to the first, second, or third metal layers. In another non-limiting example, the fourth metal layer 70 comprises aluminum-doped silver. In one non-limiting example, the third metal layer 70 comprises silver and / or copper. The fourth metal layer 70 may have a thickness ranging from 50 Å to 175 Å, preferably from 75 Å to 150 Å, more preferably from 80 Å to 120 Å, and most preferably from 90 Å to 110 Å. In one non-limiting embodiment of the present invention, the first metal layer 28 and the fourth metal layer 70 have thicknesses within 20% of each other, such as within 15%, for example within 5% to 10% of each other.

[0067] In one non-limiting example, the coated article includes only the first, second, third, and fourth metal layers 28, 42, 56, 70. No additional metal layers are present in the coated article. The metal layers may include only silver, only silver and copper, or greater than 80 wt% silver or silver and copper. Each metal layer has a thickness. The sum of all metal layer thicknesses is at least 30 nm and at most 60 nm, e.g., at least 35 and at most 47 nm. In one non-limiting example, the total thickness of the metal layers is 50 nanometers or less, e.g., 47 nm or less, e.g., 43 nanometers or less. In another non-limiting example, the total thickness of the metal layers is at least 30 nm, at least 32 nm, at least 34 nm, at least 35 nm, at least 38 nm, or at least 40 nm.

[0068] A fourth primer layer 72 may be disposed over or in direct contact with at least a portion of the fourth metal layer 70. The fourth primer layer 72 may be any of the primer materials listed above with respect to the first, second, or third primer layers 30, 44, 58 and in Table 2 previously presented. Examples of materials suitable for the primer layer include titanium, cobalt, silicon, zinc, aluminum, vanadium, tungsten, tantalum, niobium, zirconium, manganese, chromium, tin, nickel, gallium, indium, germanium, magnesium, molybdenum, silver, silicon carbide, aluminum-doped silver, aluminum zinc, vanadium zinc, tungsten tantalum, titanium niobium, zirconium niobium, tungsten niobium, aluminum niobium, aluminum titanium, tungsten titanium, tantalum titanium, zinc titanium, aluminum silver, zinc tin, indium zinc, silver zinc, mixtures thereof, and alloys thereof, where the primer may be deposited as a metal and subsequently oxidized. At least a portion of the primer layer is a nitride or an oxide. When silver zinc, zinc, silver zinc oxide, aluminum zinc oxide, indium zinc oxide, gallium zinc oxide, or vanadium zinc oxide is used as the first primer layer 30, it is believed to preferentially oxidize before the oxidation of the underlying silver layer.

[0069] In one embodiment, the fourth primer layer 72 includes zinc. In another embodiment, the fourth primer layer 72 includes Ag. x Zn 1-x In another embodiment, the fourth primer layer 72 comprises Ag. x Zn 1-x In another embodiment, the fourth primer layer 72 comprises Al x Zn 1-x In another embodiment, the fourth primer layer 72 is an In oxide. x Zn 1-x In another embodiment, the fourth primer layer 72 comprises a Ga oxide. x Zn 1-x In another embodiment, the fourth primer layer 72 comprises a V oxide. x Zn 1-x In another embodiment, the fourth primer layer 72 comprises an Al oxide. x Ti 1-x In another embodiment, the fourth primer layer 72 comprises an Al oxide. x Nb 1-x In another embodiment, the fourth primer layer 72 comprises an Al oxide. x Nb 1-x In another embodiment, the fourth primer layer 72 comprises W. x Nb 1-x In another embodiment, the fourth primer layer 72 comprises W. x Ti 1-x In another embodiment, the fourth primer layer 72 comprises a Ti oxide. x Ta 1-x In another embodiment, the fourth primer layer 72 comprises a Ti oxide. x Nb 1-x In another embodiment, the fourth primer layer 72 comprises a Ti oxide. x Nb 1-x In another embodiment, the fourth primer layer 72 comprises Nb x Zr 1-x In another embodiment, the fourth primer layer 72 comprises Ta x W 1-x In another embodiment, the fourth primer layer 72 comprises a W oxide. x Nb 1-xIn another embodiment, the fourth primer layer 72 comprises a Zn oxide. x Ti 1-x The fourth primer layer 72 may have a thickness in the range of 5 Å to 50 Å, such as 10 Å to 35 Å, such as 15 Å to 35 Å, such as 10 Å to 20 Å, such as 10 Å to 30 Å, such as 20 Å to 30 Å, or such as 30 Å to 40 Å.

[0070] The fifth dielectric layer 74 may be deposited on or in direct contact with the fourth metal layer 70 or the fourth primer layer 72 (if present). The fifth dielectric layer 74 may be composed of one or more metal oxide- or metal alloy oxide-containing layers, such as those discussed above with respect to the first, second, third, or fourth dielectric layers 20, 32, 46, 60. In one non-limiting example, the fifth dielectric layer 74 includes a first film 76 deposited on or in direct contact with the fourth metal layer 70 or the fourth primer layer 72. The first film 76 includes an oxide, nitride, oxynitride, or mixtures thereof of a metal selected from the group consisting of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, silicon, aluminum, gallium, vanadium, and mixtures thereof. In one example, the first film 76 includes zinc oxide or zinc stannate. In another example, the first film 76 includes aluminum zinc oxide. In another embodiment, first film 76 comprises indium zinc oxide. In another embodiment, first film 76 comprises gallium zinc oxide. In another embodiment, first film 76 comprises indium tin oxide. In another embodiment, first film 76 comprises vanadium zinc oxide.

[0071] The fifth dielectric layer 74 can include a second film 78 disposed over or in direct contact with at least a portion of the first film 76. In one embodiment, the second film 78 includes an oxide, nitride, oxynitride, or mixtures thereof of a metal selected from the group consisting of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, silicon, aluminum, gallium, vanadium, and mixtures thereof. In one embodiment, the second film 76 includes zinc stannate, silicon nitride, or silicon oxynitride. In some embodiments, such as FIG. 9b, the first film 76 and the second film 78 are the only films in the fifth dielectric layer 74.

[0072] The fifth dielectric layer 86 may include an optional third film 80 deposited on the second film 76. The third film 80 includes an oxide, nitride, oxynitride, or mixtures thereof of a metal selected from the group consisting of titanium, hafnium, zirconium, niobium, zinc, bismuth, lead, indium, tin, silicon, aluminum, gallium, vanadium, and mixtures thereof. In one embodiment, the third film 80 includes zinc oxide, silicon oxynitride, or silicon nitride. In another embodiment, the third film 80 includes silicon nitride. In another embodiment, the third film 80 includes zinc oxide. In another embodiment, the third film 80 includes aluminum zinc oxide. In another embodiment, the third film 80 includes indium zinc oxide. In another embodiment, the third film 80 includes gallium zinc oxide. In another embodiment, the third film 80 includes indium tin oxide. In another embodiment, the third film 80 includes vanadium zinc oxide. In some embodiments, such as FIG. 9 a , fifth dielectric layer 74 includes a first film 76 , a second film 78 and a third film 80 .

[0073] The fifth dielectric layer 74 may have a thickness in the range of 1,000 Å or less, such as 800 Å or less, such as 200 Å to 700 Å, 275 Å to 600 Å, such as 300 Å to 500 Å, such as 325 Å to 475 Å, or such as 350 Å to 460 Å.

[0074] In embodiments in which the article includes a fifth dielectric layer 74, the fourth dielectric layer 60 may have a thickness of 1,400 Å or less, such as 1,200 Å or less, such as in the range of 400 Å to 1,200 Å, 500 Å to 1,000 Å, such as 600 Å to 800 Å, such as 675 Å to 725 Å, or such as 690 Å to 710 Å. In embodiments in which the fifth dielectric layer 74 is the top dielectric layer, both the first dielectric layer 20 and the fifth dielectric layer 74 may be thinner than the second dielectric layer 32, the third dielectric layer 46, and the fourth dielectric layer 60.

[0075] Coating 10 may include an outermost protective layer 84, which, for example, in the non-limiting examples shown in FIGS. 1a-4b, is deposited on the topmost dielectric layer to help protect underlying layers, such as metal layers, from mechanical and chemical attack during processing. In one non-limiting example, protective layer 84 may be deposited on second dielectric layer 32, third dielectric layer 46, fourth dielectric layer 60, or fifth dielectric layer 74. In another non-limiting example, protective layer 84 may be disposed on, and optionally in direct contact with, metal layer 32, 56, or 70; or primer layer 44, 58, or 72. Protective layer 84 may be an oxygen barrier coating layer to prevent or reduce the migration of ambient oxygen to underlying layers of coating 10, such as during heating or bending. Protective layer 84 may be of any desired material or mixture of materials. In one exemplary embodiment, the protective layer 84 may include a layer having one or more metal oxide or nitride materials, such as, but not limited to, oxides and / or nitrides of aluminum, silicon, or mixtures thereof. For example, the protective coating 84 may include a layer having alumina in the range of 0 wt% to 100 wt% and / or silica in the range of 100 wt% to 0 wt%, such as 5 wt% to 95 wt% alumina and 95 wt% to 5 wt% silica, such as 10 wt% to 90 wt% alumina and 90 wt% to 10 wt% silica, such as 15 wt% to 90 wt% alumina and 85 wt% to 10 wt% silica, such as 50 wt% to 75 wt% alumina and 50 wt% to 25 wt% silica, such as 50 wt% to 70 wt% alumina and 50 wt% to 30 wt% silica, such as 35 wt% to 50 wt% silica. The coating layer may be a single coating layer comprising t% to 100 wt% alumina and 65 wt% to 0 wt% silica, for example, 70 wt% to 90 wt% alumina and 30 wt% to 10 wt% silica, for example, 75 wt% to 85 wt% alumina and 25 wt% to 15 wt% silica, for example, 88 wt% alumina and 12 wt% silica, for example, 65 wt% to 75 wt% alumina and 35 wt% to 25 wt% silica, for example, 70 wt% alumina and less than 30 wt% silica, for example, 60 wt% to 75 wt% alumina and more than 25 wt% to 40 wt% silica.Other materials, such as aluminum, chromium, hafnium, yttrium, nickel, boron, phosphorus, titanium, zirconium and / or oxides thereof, may also be present, for example, to adjust the refractive index of protective layer 84. In one non-limiting example, the refractive index of protective layer 84 may be in the range of 1 to 3, such as 1 to 2, such as 1.4 to 2, such as 1.4 to 1.8.

[0076] In one non-limiting example, protective layer 84 is a combination silica and alumina coating. Protective coating 84 can be sputtered from two cathodes (e.g., one silicon and one aluminum) or from a single cathode containing both silicon and aluminum. This silicon / aluminum oxide protective layer 84 is Si x Al 1-x O (1.5+x) / 2 where x can vary from greater than 0 to less than 1.

[0077] In another non-limiting example, the protective layers 80, 92 include a combination of titanium and alumina.

[0078] In one non-limiting example, protective layer 84 may be composed of silicon nitride (Si3N4), silicon oxynitride (SiON), silicon aluminum nitride (SiAlN), silicon aluminum oxynitride (SiAlON), mixtures thereof, and / or alloys thereof, which may increase the durability of metal functional layer 28, 42, 56, or 70. Protective layer 84 may be formed of silicon nitride deposited on another material with good electrical conductivity to improve silicon sputtering. For example, during deposition, the silicon cathode may include a small amount of aluminum (e.g., up to 20 wt%, up to 15 wt%, up to 10 wt%, or up to 5 wt%) to improve sputtering. In this case, the resulting silicon nitride protective layer would include a small percentage of aluminum, e.g., up to 15 wt% aluminum, e.g., up to 10 wt% aluminum, e.g., up to 5 wt% aluminum. Coating layers deposited from silicon cathodes having up to 10 wt% aluminum (added to increase the cathode's conductivity) are referred to herein as "silicon nitride" layers, although small amounts of aluminum may be present. Small amounts of aluminum in the cathode (e.g., 15 wt% or less, e.g., 10 wt% or less, e.g., 5 wt% or less) are believed to form aluminum nitride in a primarily silicon nitride protective layer 84. Protective layer 84 may be formed in a nitrogen atmosphere; however, it is understood that other gases, such as oxygen, may be present in the atmosphere during deposition of protective layer 84.

[0079] The protective layer may be of any desired thickness. The protective layer 84 may have a thickness in the range of 10 Å to 800 Å, such as 100 Å to 800 Å, such as 100 Å to 600 Å, such as 350 Å to 550 Å. In one non-limiting example, the protective coating 84 is a silicon / aluminum oxide coating (Si SiO 2 ) having a thickness in the range of 50 Å to 50,000 Å, such as 50 Å to 10,000 Å, such as 100 Å to 1,000 Å, such as 100 Å to 500 Å, such as 100 Å to 400 Å, such as 350 Å to 400 Å, such as 380 Å. x Al 1-x O (1.5+x) / 2). Protective layer 84 is the outermost layer of the coated article. Furthermore, protective layer 84 may be of non-uniform thickness. By "non-uniform thickness" it is meant that the thickness of protective layer 84 may vary over a given unit area; for example, protective layer 84 may have high and low points or regions.

[0080] In another non-limiting example, the protective coating 84 can be a multi-layer coating including a first film and a second film formed on the first film. The first film can include alumina, silica, titania, zirconia, tin oxide, or a mixture thereof. In one specific, non-limiting example, the first film can include alumina or a mixture or alloy including alumina and silica. For example, the first film can include more than 5 wt% alumina, e.g., more than 10 wt% alumina, e.g., more than 15 wt% alumina, e.g., more than 30 wt% alumina, e.g., more than 40 wt% alumina, e.g., 50 wt% to 70 wt% alumina, e.g., a silica / alumina mixture having a range of 60 wt% to 100 wt% alumina and a range of 40 wt% to 0 wt% silica, e.g., 60 wt% alumina and 40 wt% silica. In another example, the first layer can include zinc stannate. In another example, the first film can include zirconia. In one non-limiting example, the first film can have a thickness in the range of greater than 0 Å to 1 micron, e.g., 100 Å to 250 Å, e.g., 101 Å to 250 Å, e.g., 150 Å to 200 Å, e.g., 160 Å.

[0081] The second film of the protective layer 84 may include, for example, a metal oxide or a metal nitride. The second film may be titania, alumina, silica, zirconia, tin oxide, a mixture thereof, or an alloy thereof. For example, the second film may include a mixture of titania and alumina, a mixture of titania and silica, or zirconia. Examples of the second film may include a titania / alumina mixture having 40-60 wt% alumina and 60-40 wt% titania; 45-55 wt% alumina and 55-45 wt% titania; 48-52 wt% alumina and 52-48 wt% titania; 49-51 wt% alumina and 51-49 wt% titania; or 50 wt% alumina and 50 wt% titania. An example of the second film may include titanium aluminum oxide (TiAlO). Another example of the second film is a silica / alumina mixture having more than 40 wt% silica, such as more than 50 wt% silica, for example more than 60 wt% silica, for example more than 70 wt% silica, for example more than 80 wt% silica, for example, a silica / alumina mixture having silica in the range of 80 wt% to 90 wt% and alumina in the range of 10 wt% to 20 wt%, for example, 85 wt% silica and 15 wt% alumina. In one non-limiting example, the second film can have a thickness in the range of greater than 0 Å to 2 microns, for example, 50 Å to 5,000 Å, for example, 50 Å to 2,000 Å, for example, 100 Å to 1,000 Å, for example, 200 Å to 500 Å, for example, 220 Å to 350 Å, for example, 220 Å. Non-limiting examples of suitable protective layers are described, for example, in U.S. Patent Application Nos. 10 / 007,382; 10 / 133,805; 10 / 397,001; 10 / 422,094; 10 / 422,095; and 10 / 422,096.

[0082] In a non-limiting example, the protective layer 84 can include an additional third film formed on the second film. This third film can be any of the materials used to form the first or second film. The third film can include, for example, alumina, silica, titania, zirconia, tin oxide, or a mixture thereof. For example, the third film can include a mixture of silica and alumina. In another example, the third film includes zirconia. A stress layer 82 can be present between the upper dielectric layer and the protective layer 84, and on or in direct contact with at least a portion of the upper dielectric layer. The stress layer 82 is added below the protective layer 84 to reduce the sheet resistance of the coating. The stress layer 82 can have a thickness of 0.5 to 30 nm, preferably 1 to 25 nm, more preferably 1 to 20 nm, or most preferably 1 to 18 nm. In certain embodiments, stress layer 82 may include silicon, cobalt, titanium, niobium, zirconium, tantalum, oxygen, and / or titanium. In one embodiment, stress layer 82 includes silicon cobalt. In one embodiment, stress layer 82 includes Ti x Nb 1-x In another embodiment, the stress layer 82 comprises a Nb suboxide or oxide, where x is in the range of 1 to 100 wt % (BH and AH). x Zr 1-x In another embodiment, the stress layer 82 comprises a suboxide or oxide, where x is in the range of 1-12 wt% AH, preferably 1-11 wt% AH, more preferably 1-11 wt% AH, and most preferably 1-10 wt% AH. x Ta 1-x In another embodiment, the stress layer 82 comprises a suboxide or oxide, where x is in the range of 1-100 wt% AH, preferably 1-20 wt% AH or 30-100 wt% AH, more preferably 1-10 wt% AH or 500 wt% AH, and most preferably 1-4 wt% AH or 60-100 wt% AH. In another embodiment, the stress layer 82 comprises a Si x Co 1-x It comprises a suboxide or oxide, where x is in the range of 10 to 90 wt% AH, preferably 15 to 90 wt% AH, more preferably 18 to 90 wt% AH, and most preferably 20 to 90 wt% AH.

[0083] 10 and 11 , a busbar assembly 120 is formed on the inner surface 16 of the outer ply 12 and includes a first or lower busbar 104 and a second or upper busbar 106 separated by a busbar distance D. The busbars 104, 106 are in electrical contact with the coating 10. The busbar assembly 120 also includes a first conductive lead or strip 116 connected to the first busbar 104 and a second conductive lead or strip 118 connected to the second busbar 106. Each of the leads 116, 118 is connected to a power source 122. The busbars 104, 106 and / or the conductive strips 116, 118 may be formed of a conductive metal foil or strip (such as, but not limited to, copper foil or tinned copper foil), or may be formed with a conductive coating (e.g., a ceramic coating), or a combination thereof. In one non-limiting embodiment of the present invention, bus bars 104 and 106 may be at least partially or completely disposed within decorative band 102 (as shown in FIG. 11).

[0084] Power supply 122 may be any conventional power source, however, in one non-limiting example, power supply 122 is a conventional automotive alternator configured to provide a voltage in the range of 13 to 15 volts, such as approximately 14 volts.

[0085] A further transparency 130 incorporating features of the present invention is shown in FIG. 12. The construction of transparency 130 is similar to that of transparency 100, except that coating 10 includes one or more "cutout" regions, e.g., cutouts 132 and 134. Cutouts 132 and 134 divide coating 10 into first main portion 136, second main portion 138, and central portion 140. Bus bar assembly 142 in this non-limiting example is a quad-feed assembly, i.e., has four connectors 144, 146, 148, and 150 connected to four bus bars 152, 154, 156, and 158, respectively. Bus bars 152 and 154 primarily supply power to first main portion 136, and bus bars 156 and 158 primarily supply power to second main region 138.

[0086] In one non-limiting embodiment of the present invention, the coating 30 provides electrical insulation of 2 to 10 watts per square decimeter (W / dm ) at a busbar-to-busbar distance D (see FIG. 10 ) ranging from 60 cm to 75 cm (24 inches to 30 inches) when the coating is in electrical contact with a conventional vehicle alternator, such as a conventional alternator producing 80 amps and 14 volts. 2 ), e.g. 4~8W / dm 2 , for example 5~6W / dm 2The transparency is configured or dimensioned to provide a power density of 1000 W or more. Such a power density is believed to be sufficient to melt ice in contact with the outer surface 14 of the substrate 12. For vision panels (e.g., windshields) in the United States, the transparency should also have a visible light transmittance of 70% or more, e.g., 71% or more. As one skilled in the art will recognize, providing a coating with sufficient conductivity and also sufficient transmittance requires balancing several different competing factors. For example, as the distance D between the busbars increases (i.e., the transparency becomes wider from top to bottom), the busbar-to-busbar resistance increases. As the busbar-to-busbar resistance increases, the power density decreases. To maintain power density, the resistivity of the coating must decrease as the busbar-to-busbar distance increases. One way to decrease the resistivity is by increasing the thickness of one or more of the silver layers and / or by increasing the number of silver layers. In one non-limiting embodiment of the present invention, the thickness and / or number of silver layers are configured to provide a total coating resistivity of 0.6 to 1.5 ohms per square (Ω / □), e.g., 0.6 to 1.0 ohms per square (Ω / □), e.g., 0.6 to 0.9 ohms per square (Ω / □). In one non-limiting embodiment of the present invention, the thickness and / or number of silver layers are configured to provide a total coating resistivity of 0.850 ohms per square (Ω / □) or less, e.g., 0.800 ohms per square (Ω / □) or less, e.g., 0.695 ohms per square (Ω / □) or less. However, as one skilled in the art will recognize, as the number or thickness of silver layers increases, visible light transmittance decreases. For a forward field of view of a vehicle, such as a windshield, the thickness and / or number of silver layers should not be increased to the point where the visible light transmittance of the field of view drops below about 70%.

[0087] In one non-limiting implementation of the present invention, the coating provides a visible light reflectance of 25% or less, such as 20% or less, such as 10% or less, such as 8% or less.

[0088] In one non-limiting implementation of the present invention, the coating 30 has an external reflectance a at an 8 degree angle in the range of 0 to -10, for example, -1 to -8, preferably -1.2 to -7.0, more preferably -1.5 to -6.8, and most preferably -1.7 to -6.5. * (Rg8a * ) is provided.

[0089] In one non-limiting implementation of the present invention, the coating 30 has an external reflectance b at an 8 degree angle in the range of 2 to -8, for example, 2.5 to -8.0, preferably 2.0 to -7.5, more preferably 1.8 to -7.3, and most preferably 1.5 to -7.0. * (Rg8b * ) is provided.

[0090] One embodiment of the present invention is a vehicle transparency having only three metal layers sandwiched between dielectric layers. Each metal layer has a thickness. The total thickness of all three metal layers is 30 nm to 60 nm; preferably 32 nm to 47 nm; more preferably 34 nm to 45 nm; and most preferably 35 nm to 43 nm. This vehicle transparency can have a coating according to Table 3. [Table 3-1] [Table 3-2] [Table 3-3]

[0091] One embodiment of the present invention is a vehicle transparency having only four metal layers sandwiched between dielectric layers. Each metal layer has a thickness. The total thickness of all four metal layers is 30 nm to 60 nm; preferably 35 nm to 50 nm; more preferably 39 nm to 48 nm; and most preferably 40 nm to 47 nm. This vehicle transparency may have a coating as shown in Table 4. [Table 4-1] [Table 4-2] [Table 4-3] [Table 4-4]

[0092] Figure 13 shows a diagram of the initial nucleation of film growth on a surface. Nucleation leads to a change in the Gibbs free energy of the system, including the volume and surface Gibbs free energies. To grow a 2D layer, the growth surface needs to have a high surface energy (i.e., high surface tension) for two-dimensional growth, and the change in Gibbs free energy needs to be large enough to create a denser film. Therefore, the material on which silver is grown (i.e., the seed film) and the material underneath which silver is coated (i.e., the primer layer) need to have a density favorable for two-dimensional silver growth and a high Gibbs free energy to avoid aggregation of silver. Several elements with high cohesive energy and high Gibbs energy relative to silver are listed in Table 5 below. These elements are some of the materials that have the potential to reduce aggregation of silver when used as either a seed film or a primer layer. [Table 5]

[0093] The objective of the present invention is to reduce the sheet resistance of the coated article while still maintaining at least 70% light transmission. To do this, various materials believed to provide the properties already mentioned were tested as replacements for standard materials known in the art for the primer layer, metal layer, seed film, and stress layer.

[0094] In another embodiment, the present invention is a coating useful for a windshield heads-up display (HUD). As shown in Figures 10, 11, 12, 14A, 14B, and 15, the windshield includes a first ply and a second ply. The first ply is the exterior or outer ply of the windshield. The second ply is the interior ply of the windshield. Between the two plies is an interlayer. The interlayer may be any standard interlayer used in the industry. One example of such an interlayer is a polyvinyl butyral (PVB) interlayer. Preferably, the interlayer has a wedge shape, with one side of the interlayer thicker than the other. The first ply has a No. 1 surface and a No. 2 surface. The No. 1 surface is the surface that faces the exterior of the vehicle when installed. The No. 2 surface faces the second ply. The second ply has a No. 3 surface and a No. 4 surface. The No. 3 surface faces the first ply and the No. 4 surface faces the interior of the vehicle when the windshield is installed on the vehicle. The coating can be disposed on the No. 2 or No. 3 surface, preferably the No. 2 surface. Non-limiting examples of coatings useful for windshield HUDs are provided in Figures 16-23.

[0095] For a HUD, the coating can be a triple metal coating or a quadruple metal coating. In embodiments where the coating is a triple metal coating, the coating has a first dielectric layer disposed over at least a portion of the substrate. A first metal layer is disposed over at least a portion of the first dielectric layer. Optionally, a primer is disposed over at least a portion of the first metal layer. A second dielectric layer is disposed over at least a portion of the first metal layer or the optional first primer. A second metal layer is disposed over at least a portion of the second dielectric layer. An optional second primer is disposed over at least a portion of the second metal layer. A third dielectric layer is disposed over at least a portion of the second metal layer or the optional second primer. A third metal layer is disposed over the third dielectric layer. An optional third primer layer is disposed over the third metal layer. A fourth dielectric layer is disposed over the third metal layer or the optional third primer layer. An overcoat is disposed over the fourth dielectric layer. The thickness of each layer is shown in Table 6 below. In cases where the primer layer includes aluminum and zinc, the total thickness of the metal layers of the tri-metal coating ranges from 10 nm to 65 nm, preferably from 15 nm to 55 nm, more preferably from 20 nm to 45 nm, and most preferably from 25 nm to 36 nm. Non-limiting examples of tri-metal coatings are provided in Figures 16-21 and 23. [Table 6-1] [Table 6-2]

[0096] In embodiments where the HUD coating includes a quaternary metal coating, the coating includes an additional layer above the fourth dielectric layer. That is, a fourth metal layer is disposed above the dielectric layer. An optional fourth primer layer is disposed above the fourth metal layer. A fifth dielectric layer is disposed above either the fourth metal layer or the optional fourth primer layer. An optional overcoat is disposed above the fifth dielectric layer. The thickness of each layer is shown in Table 7 below. In instances where the primer layer includes aluminum and zinc, the total thickness of the metal layers of the quaternary metal coating 34 ranges from 10 nm to 65 nm, preferably from 20 nm to 60 nm, more preferably from 40 nm to 55 nm, and most preferably from 35 nm to 45 nm.

[0097] A non-limiting example of a coating having four metal layers is provided in FIG. [Table 7-1] [Table 7-2]

[0098] In some non-limiting examples of HUD coatings, the coating further comprises a light absorbing agent. The light absorbing agent is selected from the group consisting of tinted glass, PVB, an absorbing layer, or a combination thereof. In the above examples, the additional absorbing layer can be disposed on top of the fourth or fifth dielectric layer such that the absorbing layer is disposed between the fourth or fifth dielectric layer and the optional overcoat, or is the outermost layer of the coating. Non-limiting examples of such embodiments are provided in Figures 20 and 21. The absorbing layer can be made of Ge, GeO x , NbN x , NbN x O y , Si a Al b , Si a Al b O x , Si a Co b , Si a Co b O x、Yes a What? b I will c 、Yes a What? b I will c ON x 、Yes a Cr b 、Yes a Cr b ON x 、Yes a Nor b 、SiNiO x 、SiO x 、SnN x 、SnO x 、SnO x N y 、TiN x ,You a Nb b N x ,You a Nb b ON x ,You a Nb b ON x N y 、TiO x N y 、WO x 、WO2、Zn:Co、ZnO:Fe、ZnO:Mn、ZnO:Ni、ZnO:V、ZnO:Cr、Zn a Sn b 、Zn a Sn b ON xor any combination thereof. In a non-limiting example, the light-absorbing compound can include cobalt silicon oxide. The absorbing layer can have a thickness of 1 nm to 40 nm, preferably 5 nm to 30 nm, more preferably 10 nm to 25 nm, and most preferably 15 nm to 20 nm. Alternatively, the absorbing layer can include a subcritical metal film. The metal of the subcritical metal layer can include silver, gold, alloys thereof, mixtures thereof, or combinations thereof. In a non-limiting example, the subcritical film includes silver. The subcritical metal film can have a thickness of 0.5 nm to 20 nm, preferably 1 nm to 10 nm, or more preferably 1.5 nm to 3.5 nm. The term "subcritical thickness" refers to a thickness below the critical thickness at which the coating material forms separate, unconnected regions of the coating material. The term "interspersed" refers to the coating material being deposited so as to form interspersed regions or islands of material rather than a continuous layer. An additional dielectric layer can be formed over at least a portion of the subcritical metal film. The additional dielectric layer formed on at least a portion of the subcritical metal film comprises a total thickness in the range of 25 nm to 33 nm, preferably 26 nm to 32 nm, more preferably 27 nm to 31 nm, and most preferably 28 nm to 30 nm, and may comprise any of the materials discussed above with respect to the first, second, third, fourth, and fifth dielectric layers.

[0099] In one non-limiting implementation of the coating for the HUD, the coating provides a visible light reflectance of 25% or less, e.g., 20% or less, e.g., 10% or less, e.g., 8% or less. In one non-limiting implementation of the invention, the coating provides an external reflectance at an angle of 8 degrees (°) in the range of 1 to -2, e.g., 1 to -1, preferably -0.5 to 0.5, more preferably -0.5 to 0, and most preferably 0. * (Rg8a * In one non-limiting embodiment, the coating provides an external reflectance b at 8° in the range of 1 to -2, for example, 1 to -1, preferably -0.5 to 0.5, more preferably -0.5 to 0, or most preferably 0. * (Rg8b * ) is provided.

[0100] In another embodiment, the present invention provides a method for producing a medicament having an RgL of at least 42, preferably at least 45, more preferably at least 46, and most preferably at least 50. * In another embodiment, the coating substrate has RgL * The value is at least 35 and not more than 55. In another embodiment, the RgL * is at least 42. In another embodiment, RgL * is 52 or less. In this example, there are two metal layers. The example includes a substrate and a coating on the substrate. The coating includes a first dielectric layer disposed on at least a portion of the substrate. A first metal layer is disposed on at least a portion of the first dielectric layer. Optionally, a primer is disposed on at least a portion of the first metal layer. A second dielectric layer is disposed on at least a portion of the first metal layer or the optional first primer. A second metal layer is disposed on at least a portion of the second dielectric layer. An optional second primer is disposed on at least a portion of the second metal layer. A third dielectric layer is disposed on at least a portion of the second metal layer or the optional second primer. An overcoat is disposed on the fourth dielectric layer. The thickness of each layer is shown in Table 8 below, and the results can be found in Figure 21. [Table 8-1] [Table 8-2]

[0101] The present invention also includes methods of making these various embodiments of coated articles, including providing a substrate and applying a coating over the substrate, the coating including a first dielectric layer applied over at least a portion of the substrate, an optional first seed film applied over at least a portion of the first dielectric layer, a first metal layer applied over at least a portion of the first dielectric layer or the optional first seed film, a first primer layer applied over at least a portion of the first metal layer, and a second dielectric layer applied over at least a portion of the first primer layer. The coating prepared by the above method may also optionally include a second seed film applied over at least a portion of the second dielectric layer, a second metal layer applied over at least a portion of the second dielectric layer or the second seed film, a second primer layer applied over at least a portion of the second metal layer, a third dielectric layer applied over at least a portion of the second primer layer, a third seed film applied over at least a portion of the third dielectric layer, a third metal layer applied over at least a portion of the third dielectric layer or the third seed film, a third primer layer applied over at least a portion of the third metal layer, a fourth dielectric layer applied over at least a portion of the third primer layer, a fourth seed film applied over at least a portion of the fourth dielectric layer, a fourth metal layer applied over at least a portion of the fourth dielectric layer or the fourth seed film, a fourth primer layer applied over at least a portion of the fourth metal layer, and / or a fifth dielectric layer applied over at least a portion of the fourth primer layer. The coating of the above method also optionally includes a protective layer over at least a portion of the top dielectric layer, and / or a stress layer applied over at least a portion of the top dielectric layer and between the top dielectric layer and the protective layer.

[0102] The present invention also includes methods of making these various embodiments of coated articles, including providing a substrate, applying a coating onto the substrate, heating the substrate including the coating, and bending the substrate including the coating into a desired shape, the coating including a first dielectric layer applied over at least a portion of the substrate, an optional first seed film applied over at least a portion of the first dielectric layer, a first metal layer applied over at least a portion of the first dielectric layer or the optional first seed film, a first primer layer applied over at least a portion of the first metal layer, and a second dielectric layer applied over at least a portion of the first primer layer. The coating prepared by the above method may also optionally include a second seed film applied over at least a portion of the second dielectric layer, a second metal layer applied over at least a portion of the second dielectric layer or the second seed film, a second primer layer applied over at least a portion of the second metal layer, a third dielectric layer applied over at least a portion of the second primer layer, a third seed film applied over at least a portion of the third dielectric layer, a third metal layer applied over at least a portion of the third dielectric layer or the third seed film, a third primer layer applied over at least a portion of the third metal layer, a fourth dielectric layer applied over at least a portion of the third primer layer, a fourth seed film applied over at least a portion of the fourth dielectric layer, a fourth metal layer applied over at least a portion of the fourth dielectric layer or the fourth seed film, a fourth primer layer applied over at least a portion of the fourth metal layer, and / or a fifth dielectric layer applied over at least a portion of the fourth primer layer. The coating of the above method may also optionally include a protective layer over at least a portion of the top dielectric layer, and / or a stress layer applied over at least a portion of the top dielectric layer and between the top dielectric layer and the protective layer.

[0103] The invention is further described in the following numbered paragraphs:

[0104] Item 1. A coated article comprising: a substrate; a first dielectric layer over at least a portion of the substrate; a first metal layer over at least a portion of the first dielectric layer; a first primer layer over at least a portion of the first metal layer; a second dielectric layer over at least a portion of the first primer layer; a second metal layer over at least a portion of the second dielectric layer; a second primer layer over at least a portion of the second metal layer; a third dielectric layer over at least a portion of the second primer layer; a third metal layer over at least a portion of the third dielectric layer; a third primer layer over at least a portion of the third metal layer; and a fourth dielectric layer over at least a portion of the third primer layer, wherein the total thickness of the metal layers is at least 30 nanometers and no more than 60 nanometers.

[0105] Item 2. A coated article according to Item 1, wherein the first metal layer is selected from the group consisting of silver, copper, gold, aluminum, mixtures thereof, and alloys thereof, the second metal layer is selected from the group consisting of silver, copper, gold, aluminum, mixtures thereof, and alloys thereof, and / or the third metal layer is selected from the group consisting of silver, copper, gold, aluminum, mixtures thereof, and alloys thereof.

[0106] Item 3. The coated article according to item 1, wherein the first metal layer comprises silver, the second metal layer comprises silver, and the third metal layer comprises silver.

[0107] Item 4. A coated article according to any of the preceding items, wherein the first metal layer has a thickness of at least 90 Å and at most 140 Å, the second metal layer has a thickness of at least 110 Å and at most 140 Å, and / or the third metal layer has a thickness of at least 90 Å and at most 150 Å.

[0108] Item 5. A coated article according to any of the preceding items, wherein the first metal layer has a first metal layer thickness and the third metal layer has a third metal layer thickness, and the first metal layer thickness is at least 10% thicker or thinner than the third metal layer thickness.

[0109] Item 6. A coated article according to any of the preceding items, wherein the first metal layer has a first metal layer thickness and the second metal layer has a second metal layer thickness, the first metal layer thickness being less than the second metal layer thickness.

[0110] Item 7. A coated article according to any of the preceding items, wherein the third metal layer has a third metal layer thickness and the second metal layer has a second metal layer thickness, the third metal layer thickness being less than the second metal layer thickness.

[0111] Item 8. A coated article according to any of the preceding items, further comprising: a fourth metal layer over at least a portion of the fourth dielectric layer; a fourth primer layer over at least a portion of the fourth metal layer; and a fifth dielectric layer over at least a portion of the fourth primer layer.

[0112] Item 9. The coated article according to Item 8, wherein the first metal layer is selected from the group consisting of silver, copper, gold, palladium, aluminum, mixtures thereof, or alloys thereof, the second metal layer is selected from the group consisting of silver, copper, gold, palladium, aluminum, mixtures thereof, or alloys thereof, the third metal layer is selected from the group consisting of silver, copper, gold, palladium, aluminum, mixtures thereof, or alloys thereof, and / or the fourth metal layer is selected from the group consisting of silver, copper, gold, palladium, aluminum, mixtures thereof, or alloys thereof.

[0113] Item 10. The coated article according to item 8 or 9, wherein the first metal layer comprises silver, the second metal layer comprises silver, the third metal layer comprises silver, and the fourth metal layer comprises silver.

[0114] Item 11. A coated article according to any one of Items 8 to 10, wherein the first metal layer has a thickness of at least 90 Å and at most 100 Å, the second metal layer has a thickness of at least 110 Å and at most 130 Å, the third metal layer has a thickness of at least 110 Å and at most 130 Å, and the fourth metal layer has a thickness of at least 90 Å and at most 110 Å.

[0115] Item 12. The coated article according to any one of Items 8 to 11, wherein the first metal layer has a first metal layer thickness, the fourth metal layer has a fourth metal layer thickness, and the first metal layer thickness is 10% thicker or thinner than the fourth metal layer thickness.

[0116] Item 13. The coated article according to any one of Items 8 to 12, wherein the second metal layer has a second metal layer thickness, the third metal layer has a third metal layer thickness, and the second metal layer thickness is 10% thicker or thinner than the third metal layer thickness.

[0117] Item 14. A coated article according to any one of Items 8 to 13, wherein the first metal layer has a first metal layer thickness, the second metal layer has a second metal layer thickness, and the first metal layer thickness is thinner than the second metal layer thickness.

[0118] Item 15. A coated article according to any one of Items 8 to 14, wherein the fourth metal layer has a fourth metal layer thickness, the third metal layer has a third metal layer thickness, and the fourth metal layer thickness is thinner than the third metal layer thickness.

[0119] Item 16. A coated article according to any of the preceding items, wherein the total thickness of all metal layers is 47 nm or less and / or at least 35 nm.

[0120] Item 17. The coated article according to Item 16, wherein the total thickness of all metal layers is 43 nanometers or less and / or at least 35 nanometers.

[0121] Item 18. The coated article according to Item 1, wherein at least one of the metal layers comprises at least one of silver, copper, gold, palladium, aluminum, mixtures thereof, or alloys thereof.

[0122] Item 19. A coated article according to any of the preceding items, wherein the first dielectric layer comprises a zinc stannate film and a zinc oxide film over at least a portion of the zinc stannate film.

[0123] Item 20. A coated article according to any of the preceding items, wherein the second dielectric layer and / or the third dielectric layer comprises a first zinc oxide film, an optional zinc stannate film on at least a portion of the first zinc oxide film, and a second film on at least a portion of the zinc stannate film, wherein the second film comprises zinc oxide, silicon nitride, silicon oxynitride, or a combination thereof.

[0124] Item 21. A coated article according to any of the preceding items, wherein the fourth dielectric layer comprises a zinc oxide film and a zinc stannate film on at least a portion of the zinc oxide film.

[0125] Item 22. A coated article according to any of the preceding items, wherein at least one dielectric layer comprises a silicon nitride film.

[0126] Item 23. A coated article according to any of the preceding items, further comprising an outermost protective coating comprising a protective layer, the protective layer comprising at least one of Si3N4, SiAlN, SiAlON, SiAlO, titania, alumina, silica, zirconia, alloys thereof, or mixtures thereof.

[0127] Item 24. A coated article according to Item 23, wherein the outermost protective layer comprises Si3N4, SiAlO, SiAlN, SiAlON, or a mixture thereof.

[0128] Item 25. The coated article according to Item 23, wherein the outermost protective layer comprises titania.

[0129] Item 26. A coated article according to any of the preceding items, wherein at least one of the first primer layer, the second primer layer, and / or the third primer layer is selected from titanium, cobalt, silicon, zinc, aluminum, vanadium, tungsten, tantalum, niobium, zirconium, manganese, chromium, tin, nickel, gallium, indium, germanium, magnesium, molybdenum, silver, silicon carbide, aluminum-doped silver, aluminum zinc, vanadium zinc, tungsten tantalum, titanium niobium, zirconium niobium, tungsten niobium, aluminum niobium, aluminum titanium, tungsten titanium, tantalum titanium, zinc titanium, aluminum silver, zinc tin, indium zinc, silver zinc, mixtures thereof, and alloys thereof, and wherein the primer may be deposited as a metal and subsequently oxidized.

[0130] Item 27. The coated article according to Item 26, wherein at least one of the first primer layer, the second primer layer, and / or the third primer layer comprises titanium or a nickel-chromium alloy, and the primer is deposited as a metal and subsequently oxidized.

[0131] Item 28. A coated article according to Item 26, wherein the first primer layer, the second primer layer, and / or the third primer layer is a metal oxide comprising a metal selected from titanium, cobalt, silicon, zinc, aluminum, vanadium, tungsten, tantalum, niobium, zirconium, manganese, chromium, tin, nickel, gallium, indium, germanium, magnesium, molybdenum, silver, silicon carbide, aluminum-doped silver, aluminum zinc, vanadium zinc, tungsten tantalum, titanium niobium, zirconium niobium, tungsten niobium, aluminum niobium, aluminum titanium, tungsten titanium, tantalum titanium, zinc titanium, aluminum silver, zinc tin, indium zinc, silver zinc, mixtures thereof, and alloys thereof, and the primer can be deposited as a metal and subsequently oxidized.

[0132] Item 29. The article according to item 28, wherein at least one of the first primer layer, the second primer layer, and / or the third primer layer is a metal oxide comprising a metal including titanium, a titanium-aluminum alloy, nickel, or a nickel-chromium alloy.

[0133] Item 30. A coated article according to any of the preceding items having a visible light transmittance of at least 70%.

[0134] Item 31. A coated article comprising: a substrate; a first dielectric layer over at least a portion of the substrate; a first metal layer over at least a portion of the first dielectric layer; a first primer layer over at least a portion of the first metal layer; a second dielectric layer over at least a portion of the first primer layer; a second metal layer over at least a portion of the second dielectric layer; a second primer layer over at least a portion of the second metal layer; a third dielectric layer over at least a portion of the second primer layer; a third metal layer over at least a portion of the third dielectric layer; a third primer layer over at least a portion of the third metal layer; and a fourth dielectric layer over at least a portion of the third primer layer; the coated article having a sheet resistance of 0.85 Ω / □ or less.

[0135] Item 32. A coated article according to Item 31, having a sheet resistance of 0.8 Ω / □ or less.

[0136] Item 33. A coated article according to Item 31 or 32, having a sheet resistance of 0.7 Ω / □ or less.

[0137] Item 34. A coated article according to any one of Items 31 to 33, having a visible light transmittance of at least 70%.

[0138] Item 35. A coated article according to any one of Items 31 to 34, wherein at least one of the metal layers comprises at least one of silver, copper, gold, palladium, aluminum, mixtures thereof, or alloys thereof.

[0139] Item 36. A coated article according to any one of Items 31 to 35, wherein at least one of the dielectric layers comprises at least one of a zinc stannate film, a zinc oxide film, a silicon nitride film, or a mixture thereof.

[0140] Item 37. A coated article according to any of Items 31 to 36, wherein at least one of the primer layers is selected from titanium, cobalt, silicon, zinc, aluminum, vanadium, tungsten, tantalum, niobium, zirconium, manganese, chromium, tin, nickel, gallium, indium, germanium, magnesium, molybdenum, silver, silicon carbide, aluminum-doped silver, aluminum zinc, vanadium zinc, tungsten tantalum, titanium niobium, zirconium niobium, tungsten niobium, aluminum niobium, aluminum titanium, tungsten titanium, tantalum titanium, zinc titanium, aluminum silver, zinc tin, indium zinc, silver zinc, mixtures thereof, and alloys thereof, and the primer is deposited as a metal and subsequently oxidized.

[0141] Item 38. A coated article according to any of the preceding items, wherein the first primer layer comprises titanium, aluminum, nickel, or chromium, and the primer is deposited as a metal and subsequently oxidized.

[0142] Item 39. An article according to any of the preceding items, wherein the second primer layer comprises titanium, aluminum, nickel, or chromium, and the primer is deposited as a metal and subsequently oxidized.

[0143] Item 40. An article according to any of the preceding items, wherein the third primer layer comprises titanium, aluminum, nickel, or chromium, and the primer is deposited as a metal and subsequently oxidized.

[0144] Item 41. A coated article comprising: a substrate; a first dielectric layer over at least a portion of the substrate; a first metal layer over at least a portion of the first dielectric layer; a first primer layer over at least a portion of the first metal layer; a second dielectric layer over at least a portion of the first primer layer; a second metal layer over at least a portion of the second dielectric layer; and a second primer layer over at least a portion of the second metal layer, wherein the total thickness of the metal layers is at least 30 nanometers and no more than 60 nanometers.

[0145] Item 42. A coated article according to Item 41, wherein the first metal layer is selected from the group consisting of silver, copper, gold, aluminum, mixtures thereof, or alloys thereof, and the second metal layer is selected from the group consisting of silver, copper, gold, aluminum, mixtures thereof, or alloys thereof.

[0146] Item 43. A coated article according to Item 41 or 42, wherein the first metal layer comprises silver and the second metal layer comprises silver.

[0147] Item 44. A coated article according to any one of Items 41 to 43, wherein the first metal layer has a thickness of at least 90 nm and at most 140 nm, and the second metal layer has a thickness of at least 110 nm and at most 140 nm.

[0148] Item 45. A coated article according to any one of Items 41 to 44, wherein the first metal layer has a first metal layer thickness, the second metal layer has a second metal layer thickness, and the first metal layer thickness is 10% thicker or thinner than the first metal layer thickness.

[0149] Item 46. A coated article according to any one of Items 41 to 45, wherein the first metal layer has a first metal layer thickness, the second metal layer has a second metal layer thickness, and the first metal layer thickness is thinner than the second metal layer thickness.

[0150] Item 47. A coated article according to any of Items 41 to 46, further comprising a third metal layer disposed on at least a portion of the third dielectric layer, a third primer layer on at least a portion of the third metal layer, and a fourth dielectric layer on at least a portion of the third primer layer.

[0151] Item 48. A coated article according to Item 47, wherein the first metal layer is selected from the group consisting of silver, copper, gold, palladium, aluminum, mixtures thereof, or alloys thereof, the second metal layer is selected from the group consisting of silver, copper, gold, palladium, aluminum, mixtures thereof, or alloys thereof, and the third metal layer is selected from the group consisting of silver, copper, gold, palladium, aluminum, mixtures thereof, or alloys thereof.

[0152] Item 49. A coated article according to Item 47 or 48, wherein the first metal layer comprises silver, the second metal layer comprises silver, and the third metal layer comprises silver.

[0153] Item 50. A coated article according to any one of Items 47 to 49, wherein the first metal layer has a thickness of at least 110 Å and at most 140 Å, the second metal layer has a thickness of at least 130 Å and at most 140 Å, and the third metal layer has a thickness of at least 110 Å and at most 150 Å.

[0154] Item 51. The coated article according to any of Items 47 to 50, wherein the first metal layer has a first metal layer thickness, the third metal layer has a third metal layer thickness, and the first metal layer thickness is 10% thicker or thinner than the third metal layer thickness.

[0155] Item 52. A coated article according to any one of Items 47 to 51, wherein the first metal layer has a first metal layer thickness, the second metal layer has a second metal layer thickness, and the first metal layer thickness is thinner than the second metal layer thickness.

[0156] Item 53. A coated article according to any one of Items 47 to 52, wherein the third metal layer has a third metal layer thickness, the second metal layer has a second metal layer thickness, and the third metal layer thickness is thinner than the second metal layer thickness.

[0157] Item 54. A coated article according to any of items 47 to 53, further comprising: a fourth metal layer over at least a portion of the fourth dielectric layer; a fourth primer layer over at least a portion of the fourth metal layer; and a fifth dielectric layer over at least a portion of the fourth primer layer.

[0158] Item 55. A coated article according to Item 54, wherein the first metal layer is selected from the group consisting of silver, copper, gold, palladium, aluminum, mixtures thereof, or alloys thereof, the second metal layer is selected from the group consisting of silver, copper, gold, palladium, aluminum, mixtures thereof, or alloys thereof, the third metal layer is selected from the group consisting of silver, copper, gold, aluminum, mixtures thereof, or alloys thereof, and the fourth metal layer is selected from the group consisting of silver, copper, gold, palladium, aluminum, mixtures thereof, or alloys thereof.

[0159] Item 56. A coated article according to Item 54 or 55, wherein the first metal layer comprises silver, the second metal layer comprises silver, the third metal layer comprises silver, and the fourth metal layer comprises silver.

[0160] Item 57. A coated article according to any one of Items 54 to 56, wherein the first metal layer has a thickness of at least 90 Å and at most 100 Å, the second metal layer has a thickness of at least 110 Å and at most 130 Å, the third metal layer has a thickness of at least 110 Å and at most 130 Å, and the fourth metal layer has a thickness of at least 90 Å and at most 110 Å.

[0161] Item 58. A coated article according to any of Items 54 to 57, wherein the first metal layer has a first metal layer thickness, the fourth metal layer has a fourth metal layer thickness, and the first metal layer thickness is 10% thicker or thinner than the fourth metal layer thickness.

[0162] Item 59. A coated article according to any one of Items 54 to 58, wherein the fourth metal layer has a fourth metal layer thickness, the third metal layer has a third metal layer thickness, and the fourth metal layer thickness is thinner than the third metal layer thickness.

[0163] Item 60. A coated article according to any one of Items 41 to 59, having a visible light transmittance of at least 70%.

[0164] Item 61. The coated article according to Item 41, wherein at least one of the metal layers comprises at least one of silver, copper, gold, palladium, aluminum, mixtures thereof, or alloys thereof.

[0165] Item 62. A coated article according to any of Items 41 to 61, wherein at least one of the dielectric layers comprises at least one of a zinc stannate layer, a zinc oxide layer, a silicon nitride layer, or a mixture thereof.

[0166] Item 63. A coated article according to any one of Items 41 to 62, further comprising an outermost protective coating including a protective layer, the protective layer comprising at least one of Si3N4, SiAlN, SiAlON, titania, alumina, silica, zirconia, alloys thereof, or mixtures thereof.

[0167] Item 64. A coated article according to any of Items 41 to 63, wherein at least one primer layer is selected from titanium, cobalt, silicon, zinc, aluminum, vanadium, tungsten, tantalum, niobium, zirconium, manganese, chromium, tin, nickel, gallium, indium, germanium, magnesium, molybdenum, silver, silicon carbide, aluminum-doped silver, aluminum zinc, vanadium zinc, tungsten tantalum, titanium niobium, zirconium niobium, tungsten niobium, aluminum niobium, aluminum titanium, tungsten titanium, tantalum titanium, zinc titanium, aluminum silver, zinc tin, indium zinc, silver zinc, mixtures thereof, and alloys thereof, and the primer is deposited as a metal and subsequently oxidized.

[0168] Item 65. A coated article comprising: a first substrate including a first surface and a second surface; a second substrate including a third surface and a fourth surface disposed on at least a portion of the first substrate, the second surface being disposed facing the third surface, and the second and third surfaces being separated by an intermediate layer; and a functional coating disposed on either the second or third surface, the functional coating comprising: a first dielectric layer on at least a portion of the surface; a first metal layer on at least a portion of the first dielectric layer; and a fourth metal layer on at least a portion of the first metal layer. a second dielectric layer over at least a portion of the first primer layer; a second metal layer over at least a portion of the second dielectric layer; a second primer layer over at least a portion of the second metal layer; a third dielectric layer over at least a portion of the second primer layer; a third metal layer over at least a portion of the third dielectric layer; a third primer layer over at least a portion of the third metal layer; and a fourth dielectric layer over at least a portion of the third primer layer, wherein the coated substrate has a visible light reflectance of 10% or less.

[0169] Item 66. The coated article according to Item 65, further comprising: a fourth metal layer over at least a portion of the fourth dielectric layer; a fourth primer layer over at least a portion of the fourth metal layer; and a fifth dielectric layer over at least a portion of the fourth primer layer.

[0170] Item 67. A coated article according to Item 65 or 66, wherein the coated substrate has a visible light reflectance of 8% or less.

[0171] Item 68. A coated article according to any one of Items 65 to 67, having a visible light transmittance of at least 70%.

[0172] Item 69. A coated article according to any one of Items 65 to 68, wherein at least one of the metal layers comprises at least one of silver, copper, gold, aluminum, mixtures thereof, or alloys thereof.

[0173] Item 70. A coated article according to any of Items 65 to 69, wherein at least one of the dielectric layers comprises at least one of a zinc stannate layer, a zinc oxide layer, a silicon nitride layer, or a mixture thereof.

[0174] Item 71. A coated article according to any of Items 65 to 70, further comprising an outermost protective coating comprising a protective layer, the protective layer comprising at least one of Si3N4, SiAlN, SiAlON, titania, alumina, silica, zirconia, alloys thereof, or mixtures thereof.

[0175] Item 72. A coated article according to any of Items 65 to 71, wherein at least one of the primer layers is selected from titanium, cobalt, silicon, zinc, aluminum, vanadium, tungsten, tantalum, niobium, zirconium, manganese, chromium, tin, nickel, gallium, indium, germanium, magnesium, molybdenum, silver, silicon carbide, aluminum-doped silver, aluminum zinc, vanadium zinc, tungsten tantalum, titanium niobium, zirconium niobium, tungsten niobium, aluminum niobium, aluminum titanium, tungsten titanium, tantalum titanium, zinc titanium, aluminum silver, zinc tin, indium zinc, silver zinc, mixtures thereof, and alloys thereof, and the primer is deposited as a metal and subsequently oxidized.

[0176] The following examples illustrate various embodiments of the present invention, however, it is understood that the invention is not limited to these particular examples. [Example]

[0177] "Example 1" As already mentioned, the sheet resistance of the coating can be reduced by using new materials in the individual layers. The sheet resistance is also expected to be reduced by adding new layers all together. In Table 9, Ti 78 Nb 22was integrated into the stack in place of the Ti primer layer. Ag deposited by oxygen was also included as a seed film under the silver metal layer. The substrate was a clear glass substrate. ZT stands for zinc tin, also known as zinc stannate. Zn90 is tin-doped zinc oxide deposited in the presence of oxygen from a cathode containing 10 wt% tin and 90 wt% zinc (i.e., ZnO90 / 10). Ag stands for silver. PPO is the protective layer or coating discussed above. Before integrating these layers, each layer was optimized to have the lowest sheet resistance. The best samples for different combinations are listed in the table below. [Table 9]

[0178] As already discussed, Ti is used as the stress layer under the protective layer. 78 Nb 22 O x An additional coating stack was also tested, inserting a total of three layers, varying from the baseline to the final coating stack, and the sheet resistance values ​​can be seen in Table 10. [Table 10]

[0179] Table 11 replaces the Ti primer layer or Ti78Nb22 primer layer with Ti3Nb97Nx or titanium niobium nitride. [Table 11]

[0180] Table 12 shows an experiment with a coating stack having aluminum zinc primer and aluminum zinc oxide above and below the silver layer as part of the dielectric layer. The sheet resistance drops from 3.75 to 3.21 Ω / □ for the single silver stack. [Table 12]

[0181] Table 13 shows the results of a coating stack run with aluminum zinc primer and aluminum zinc oxide above and below the silver layer. 90 Sn 10 The resistance drops from 1 to 0.73 Ω / □ for the triple silver stack with AZ primer and Ag oxygen deposited seed film between O and O. [Table 13]

[0182] The addition of a stress layer below the protective layer can further reduce the sheet resistance of the coating stack. A variety of additional materials have been tested for use as stress layers. Some of these materials are listed in Table 14, which demonstrates the reduction in sheet resistance due to the inclusion of these materials as stress layers. [Table 14]

[0183] Experiments were conducted by replacing the dielectric layer film surrounding the metal layer with VZnO (vanadium zinc oxide). The top dielectric layer film immediately below the metal layer was replaced, and the bottom dielectric layer film immediately above the metal layer was replaced. These were paired with both Ti and zinc metal primer layers. The results of these experiments are shown in Table 15 below. [Table 15]

[0184] "Example 2" Tables 16 and 17 show exemplary coatings of the present invention. The reported thicknesses are geometric thicknesses in angstroms (Å). The substrate is a clear glass substrate having a thickness of 2.1 mm. ZS means zinc stannate deposited in the presence of oxygen from a cathode having 52 wt% zinc and 48 wt% tin. TZO means tin-doped zinc oxide deposited in the presence of oxygen from a cathode containing 10 wt% tin and 90 wt% zinc (i.e., ZnO90 / 10). Ag means silver. TiO x refers to a titanium primer layer that is deposited as a metal and oxidized during processing. [Table 16] [Table 17]

[0185] Tables 18-22 show the spectral characteristics for the samples in Tables 5 and 6. [Table 18] [Table 19] [Table 20] [Table 21] [Table 22]

[0186] Those skilled in the art will readily recognize that modifications can be made to the present invention without departing from the concepts disclosed in the foregoing description. Accordingly, the specific embodiments detailed herein are illustrative only and do not limit the scope of the invention, which is set forth in the full breadth of the appended claims and any and all equivalents thereof.

Claims

1. a substrate; a first dielectric layer on at least a portion of the substrate, the first dielectric layer comprising a total thickness of 42 nm to 47 nm, the first dielectric layer consisting of a first film on at least a portion of the substrate and a second film on at least a portion of the first film, the first film comprising zinc stannate or tin oxide; a first metal layer over at least a portion of the first dielectric layer, the first metal layer having a thickness of at least 90 Å and at most 100 Å; a first primer layer comprising titanium on at least a portion of the first metal layer, the first primer layer having a thickness of 20 Å to 40 Å; a second dielectric layer on at least a portion of the first primer layer, the second dielectric layer having a total thickness of 78 nm to 85 nm, the second dielectric layer consisting of a first film on at least a portion of the first primer layer, a second film on at least a portion of the first film, and a third film on at least a portion of the second film, the second film comprising zinc stannate; a second metal layer on at least a portion of the second dielectric layer, the second metal layer having a thickness of at least 110 Å and at most 130 Å; a second primer layer comprising titanium on at least a portion of the second metal layer, the second primer layer having a thickness of 20 Å to 40 Å; a third dielectric layer on at least a portion of the second primer layer, the third dielectric layer comprising a total thickness of 70 nm to 82.5 nm, the third dielectric layer consisting of a first film on at least a portion of the second primer layer, a second film on at least a portion of the first film, and a third film on at least a portion of the second film, the second film comprising zinc stannate; a third metal layer on at least a portion of the third dielectric layer, the third metal layer having a thickness of at least 110 Å and at most 130 Å; a third primer layer comprising titanium on at least a portion of the third metal layer, the third primer layer having a thickness of 20 Å to 40 Å; a fourth dielectric layer on at least a portion of the third primer layer, the fourth dielectric layer having a total thickness of 55 nm to 70 nm, the fourth dielectric layer consisting of a first film on at least a portion of the third primer layer, a second film on at least a portion of the first film, and a third film on at least a portion of the second film, the second film comprising zinc stannate; a fourth metal layer on at least a portion of the fourth dielectric layer, the fourth metal layer having a thickness of at least 90 Å and at most 110 Å; a fourth primer layer comprising titanium on at least a portion of the fourth metal layer, the fourth primer layer having a thickness of 20 Å to 40 Å; a fifth dielectric layer on at least a portion of the fourth primer layer, the fifth dielectric layer having a total thickness of 42.5 nm to 47.5 nm, the fifth dielectric layer consisting of a first film on at least a portion of the fourth primer layer and a second film on at least a portion of the first film, the second film comprising zinc stannate or tin oxide; A coated article comprising: The coated article comprises four metal layers, the total thickness of the four metal layers is at least 40 nanometers and no more than 47 nanometers; the coated article has a sheet resistance of 0.85 Ω / □ or less; A coated article, wherein the coated article has a visible light transmittance of greater than 70%.

2. The coated article of claim 1 , wherein at least one of the metal layers comprises at least one of silver, copper, gold, aluminum, mixtures thereof, or alloys thereof.

3. A coated article as described in claim 1 or 2, wherein the coated article further comprises an outermost protective coating, the outermost protective coating having a total thickness in the range of 20 nm to 120 nm.

4. 4. The coated article of claim 1, wherein the first primer layer, the second primer layer, the third primer layer, and / or the fourth primer layer are deposited as metals and subsequently oxidized.

5. a first substrate comprising a first surface and a second surface; a second substrate over at least a portion of the first substrate, the second substrate including a third surface and a fourth surface; the second surface is disposed facing the third surface; a second substrate, the second and third surfaces separated by an intermediate layer; a functional coating disposed on either the second or third surface; 1. A vehicle transparency comprising: a first dielectric layer on at least a portion of the second surface or the third surface, the first dielectric layer comprising a total thickness of 42 nm to 47 nm, the first dielectric layer consisting of a first film on at least a portion of the substrate and a second film on at least a portion of the first film, the first film comprising zinc stannate or tin oxide; a first metal layer over at least a portion of the first dielectric layer, the first metal layer having a thickness of at least 90 Å and at most 100 Å; a first primer layer comprising titanium on at least a portion of the first metal layer, the first primer layer having a thickness of 20 Å to 40 Å; a second dielectric layer on at least a portion of the first primer layer, the second dielectric layer having a total thickness of 78 nm to 85 nm, the second dielectric layer consisting of a first film on at least a portion of the first primer layer, a second film on at least a portion of the first film, and a third film on at least a portion of the second film, the second film comprising zinc stannate; a second metal layer on at least a portion of the second dielectric layer, the second metal layer having a thickness of at least 110 Å and at most 130 Å; a second primer layer comprising titanium on at least a portion of the second metal layer, the second primer layer having a thickness of 20 Å to 40 Å; a third dielectric layer on at least a portion of the second primer layer, the third dielectric layer comprising a total thickness of 70 nm to 82.5 nm, the third dielectric layer consisting of a first film on at least a portion of the second primer layer, a second film on at least a portion of the first film, and a third film on at least a portion of the second film, the second film comprising zinc stannate; a third metal layer on at least a portion of the third dielectric layer, the third metal layer having a thickness of at least 110 Å and at most 130 Å; a third primer layer comprising titanium on at least a portion of the third metal layer; a fourth dielectric layer on at least a portion of the third primer layer, the fourth dielectric layer having a total thickness of 55 nm to 70 nm, the fourth dielectric layer consisting of a first film on at least a portion of the third primer layer, a second film on at least a portion of the first film, and a third film on at least a portion of the second film, the second film comprising zinc stannate; a fourth metal layer on at least a portion of the fourth dielectric layer, the fourth metal layer having a thickness of at least 90 Å and at most 110 Å; a fourth primer layer comprising titanium on at least a portion of the fourth metal layer, the fourth primer layer having a thickness of 20 Å to 40 Å; a fifth dielectric layer on at least a portion of the fourth primer layer, the fifth dielectric layer having a total thickness of 42.5 nm to 47.5 nm, the fifth dielectric layer consisting of a first film on at least a portion of the fourth primer layer and a second film on at least a portion of the first film, the second film comprising zinc stannate or tin oxide; Including, The functional coating consists of four metal layers, the total thickness of the four metal layers is at least 40 nanometers and no more than 47 nanometers; the functional coating has a sheet resistance of 0.85 Ω / □ or less; A vehicle transparency wherein the functional coating has a visible light transmittance of greater than 70%.

6. 6. The vehicle transparency of claim 5, wherein said vehicle transparency has a visible light reflectance of 20% or less.

7. A vehicle transparency material as described in claim 5 or 6, wherein at least one of the metal layers comprises at least one of silver, copper, gold, aluminum, mixtures thereof or alloys thereof.

8. A vehicle transparency material as described in any one of claims 5 to 7, wherein the first primer layer, the second primer layer, the third primer layer, and / or the fourth primer layer are deposited as metals and subsequently oxidized.

9. A vehicle transparency as described in any one of claims 5 to 8, wherein the vehicle transparency further comprises an outermost protective coating, the outermost protective coating having a total thickness in the range of 20 nm to 120 nm.

10. A vehicle transparency material as described in claim 9, wherein the outermost protective coating comprises a first film and a second film formed on the second film, the first film comprising alumina, silica, titania, zirconia, tin oxide, or a mixture thereof, and the second film comprising titania, alumina, silica, zirconia, tin oxide, a mixture thereof, or an alloy thereof.

11. A vehicle transparency material described in any one of claims 5 to 10, wherein the vehicle transparency material has a visible light transmittance of 71% or more.

12. A vehicle transparency material as described in any one of claims 5 to 11, wherein the vehicle transparency material is a vehicle windshield.

13. A coated article described in any one of claims 1 to 4, wherein the first metal layer is thinner than the second metal layer.

14. A coated article described in any one of claims 1 to 4 and claim 13, wherein the third metal layer is thinner than the second metal layer.

15. A coated article described in any one of claims 1 to 4, wherein the first metal layer is thinner than the second metal layer, and the third metal layer is thinner than the second metal layer.

16. The coated article of claim 3, wherein the outermost protective coating comprises a first film and a second film formed on the second film, the first film comprising alumina, silica, titania, zirconia, tin oxide, or a mixture thereof, and the second film comprising titania, alumina, silica, zirconia, tin oxide, a mixture thereof, or an alloy thereof.

17. A coated article described in any one of claims 1 to 4 and claims 13 to 16, wherein the coated article has a visible light transmittance of 71% or more.