Lithium-ion rechargeable battery

Abstract

This lithium secondary battery comprises: a positive electrode in which lithium ions are occluded during discharging and lithium ions are discharged during charging; a negative electrode in which lithium metal is deposited during charging and lithium metal is dissolved during discharging; and a non-aqueous electrolyte having lithium ion conductivity. The surface of the negative electrode is covered with a protective layer. The protective layer contains a block polymer in which a first polymer portion having a repeating structure of a monomer unit A and a second polymer portion having a repeating structure of a monomer unit B are bonded.

Description

[Technical Field]

[0001] This disclosure relates to lithium secondary batteries. [Background technology]

[0002] Lithium-ion batteries are known as high-capacity non-aqueous electrolyte secondary batteries. Increasing the capacity of lithium-ion batteries can be achieved by using alloy active materials such as graphite and silicon compounds in combination as the negative electrode active material. However, the capacity of lithium-ion batteries is reaching its limits.

[0003] Lithium-ion batteries (lithium metal batteries) are promising as high-capacity non-aqueous electrolyte secondary batteries that surpass lithium-ion batteries. In lithium-ion batteries, lithium metal is deposited on the negative electrode during charging, and the lithium metal dissolves during discharge, releasing lithium ions into the non-aqueous electrolyte. During charging, lithium metal tends to deposit in a dendrite-like manner, resulting in a large expansion of the negative electrode during charging.

[0004] Patent Document 1 proposes preventing the growth of lithium dendrites using a lithium electrode comprising a porous metal current collector, an electrode composite containing lithium metal inserted into the pores formed in the metal current collector, and a lithium ion conductive protective film coated on at least one surface of the electrode composite. Examples of lithium ion conductive protective films include polyethylene oxide (PEO), polymethyl methacrylate (PMMA), and polyvinylidene fluoride (PVdF). [Prior art documents] [Patent Documents]

[0005] [Patent Document 1] Special Publication No. 2016-527679 [Overview of the project] [Problems that the invention aims to solve]

[0006] However, polyethylene oxide (PEO) and polymethyl methacrylate (PMMA), which are used as lithium-ion conductive protective films, are easily soluble in the electrolyte, and their protective function may decrease as the number of cycles increases. Furthermore, polyvinylidene fluoride (PVdF) may lack sufficient strength, and the protective layer may not be sufficiently effective. For this reason, even with the method described in Patent Document 1, it remains difficult to control the deposition morphology of lithium metal, and the suppression of dendrite formation is insufficient.

[0007] If the protective film is not strong enough, lithium metal dendrites may penetrate the protective film, come into contact with the non-aqueous electrolyte, and cause side reactions, which can degrade the cycle performance. [Means for solving the problem]

[0008] One aspect of the present disclosure relates to a lithium secondary battery comprising: a positive electrode that intercepts lithium ions during discharge and releases the lithium ions during charge; a negative electrode that deposits lithium metal during charge and dissolves the lithium metal during discharge; and a non-aqueous electrolyte having lithium ion conductivity, wherein the surface of the negative electrode is covered with a protective layer, and the protective layer comprises a block polymer in which a first polymer portion having a repeating structure of monomer units A and a second polymer portion having a repeating structure of monomer units B are bonded together. [Effects of the Invention]

[0009] According to this disclosure, the degradation of the cycle characteristics of lithium secondary batteries is suppressed. Novel features of the present invention are described in the appended claims, but the present invention, both in terms of structure and content, and in conjunction with other objects and features of the present invention, will be better understood by the following detailed description in conjunction with the drawings. [Brief explanation of the drawing]

[0010] [Figure 1]This is a schematic longitudinal cross-sectional view showing a lithium secondary battery according to one embodiment of the present disclosure. [Figure 2] This is a magnified view of a key part showing an example of the electrode group in Figure 1. [Figure 3] This is a close-up view of a key part showing another example of the electrode group in Figure 1. [Modes for carrying out the invention]

[0011] The lithium secondary battery according to this disclosure comprises a positive electrode that intercepts lithium ions during discharge and releases lithium ions during charge, a negative electrode in which lithium metal is deposited during charge and dissolves during discharge, and a non-aqueous electrolyte having lithium ion conductivity. The surface of the negative electrode is covered with a protective layer. The protective layer includes a block polymer in which a first polymer portion having a repeating structure of monomer unit A and a second polymer portion having a repeating structure of monomer unit B are bonded together.

[0012] Here, "monomer unit A(B)" refers to the unit formed in the polymer by polymerized monomer A(B). For example, when the vinyl group (-CH=CH2) of monomer A(B) having a vinyl group polymerizes, monomer unit A(B) has an ethane-1,1,2-triyl group (>CH-CH2-).

[0013] The negative electrode surface is covered with a protective layer. That is, the lithium metal deposited on the negative electrode is covered with a protective layer, suppressing contact between the lithium metal and the non-aqueous electrolyte. The protective layer also suppresses the growth of lithium metal dendrites. Therefore, side reactions caused by contact between lithium metal and the non-aqueous electrolyte are sufficiently suppressed, and the deterioration of cycle characteristics associated with these side reactions is suppressed.

[0014] By using a block polymer for the protective layer, the functions of the first polymer portion and the second polymer portion can be made compatible. Further, compared with the case where the first polymer portion and the second polymer are mixed and included in the protective layer, the respective disadvantages of the first polymer portion and the second polymer portion are reduced. Such an effect is a remarkable effect that cannot be obtained by simply copolymerizing monomer A and monomer B.

[0015] The polymer for forming the protective layer is desirably highly lithium-ion conductive. However, a polymer with high lithium-ion conductivity also has a high affinity for the electrolyte and may be easily dissolved in the electrolyte. Further, a high membrane strength may not be obtained, and in some cases, lithium metal dendrites may penetrate the protective layer, or the protective layer may be broken due to the tension accompanying the expansion and contraction of the wound body during charge and discharge. As a result, as the number of cycles increases, the membrane stability of the protective layer decreases, the growth of dendrites cannot be suppressed, and the cycle characteristics deteriorate. According to a lithium secondary battery according to an embodiment of the present disclosure, for example, by forming a protective layer with a block polymer in which a first polymer portion having high mechanical strength is terminated on a second polymer portion having high lithium conductivity, while obtaining high lithium-ion conductivity by the second polymer portion, the mechanical strength of the protective layer can be increased by the first polymer portion. Therefore, a protective layer having both high membrane stability and high lithium-ion conductivity can be obtained, and a lithium-ion battery having excellent cycle characteristics can be realized. The block polymer may be, for example, an ABA-type triblock copolymer in which the first polymer portion is bonded to both ends of the second polymer portion.

[0016] Block polymers can form a secondary structure in which they aggregate with each other. At this time, the secondary structure can be formed such that portions having the same monomer units within the block polymer are arranged in proximity to each other. That is, the secondary structure of the block polymer can be formed such that the first polymer portions of the individual block polymers aggregate and the second polymer portions aggregate. For example, it is considered possible to control the secondary structure of the block polymer such that the surface of the protective layer is covered with the first polymer portion having high film strength and the second polymer portion excellent in lithium ion conduction is disposed inside the protective layer. An ABA-type triblock copolymer can easily control the secondary structure of the block polymer by, for example, controlling the monomer units or the degree of polymerization (molecular weight) in the first polymer portion and the second polymer portion.

[0017] For the first polymer portion, for example, a polymer having high tensile strength and excellent mechanical strength can be used. The tensile strength of the first polymer portion may be higher than the tensile strength of the second polymer portion. Thereby, even when a polymer having low mechanical strength and / or easily soluble in an electrolyte is used for the second polymer portion, the mechanical strength can be increased by forming a block polymer bonded to the first polymer portion, and the film stability of the protective layer can be maintained at a high level.

[0018] For the second polymer portion, for example, a polymer having a higher degree of swelling in a non-aqueous electrolyte than the first polymer portion can be used. By using the second polymer portion having a high degree of swelling, high lithium ion conductivity can be obtained in the protective layer. On the other hand, as the degree of swelling increases, the film strength of the protective layer tends to decrease, but by forming a block polymer with the first polymer portion, the film strength of the protective layer can be maintained at a high value and high film stability can be maintained. Also, even when the degree of swelling of the second polymer portion is large and it would dissolve in a non-aqueous electrolyte alone, it can be used for the protective layer by forming a block polymer bonded to the first polymer portion.

[0019] The tensile strength and swelling degree of the first and second polymer portions are determined by disassembling a lithium secondary battery and analyzing the structure of the block polymer in the extracted protective layer. By analyzing the structure of the block polymer, the structures of the first and second polymer portions contained in the block polymer (types of monomer units A and B (i.e., monomers A and B), molecular weight, etc.) can be identified. If necessary, the first polymer, which is a homopolymer of the identified monomer A, and the second polymer, which is a homopolymer of monomer B, are synthesized separately, and their tensile strength and swelling degree are determined.

[0020] The tensile strength may be determined by forming a sample of a predetermined shape and following the procedures outlined in JIS K 7161, or it may be determined from a publicly known database.

[0021] The degree of swelling is defined as the percentage increase in polymer weight after immersing the first and second polymers in a non-aqueous electrolyte prepared using a non-aqueous electrolyte similar to the components obtained from the analysis, at a temperature of 40°C.

[0022] Whether a polymer is a block polymer, and if so, its structure (e.g., whether it is a triblock copolymer, a random copolymer, or a mixture of a first and second polymer), can be determined by end-group quantification using GPC (gel permeation chromatography)-NMR.

[0023] The first polymer portion includes, for example, at least one selected from the group consisting of polyimide (PI), polyamideimide (PAI), and polystyrene (PS). Among these, polystyrene (PS) is preferred because it is stable to non-aqueous electrolytes, has sufficient mechanical strength, and is inexpensive. That is, styrene is preferred as monomer A constituting monomer unit A. Note that 90 mol% or more of the monomer units constituting the first polymer portion may be monomer unit A. For example, monomer unit B constituting the second polymer portion may be included in the first polymer portion if it is 10 mol% or less.

[0024] The second polymer portion includes, for example, at least one selected from the group consisting of fluorine-containing polymers, polyacrylates, polyvinyl alcohol, polyacrylic acid, polymethacrylic acid, and polyethylene oxide (PEO). The fluorine-containing polymer may be at least one selected from the group consisting of polyvinylidene fluoride (PVdF), polytetrafluoroethylene (PTFE), copolymers of vinylidene fluoride (VdF) and hexafluoropropylene (HFP), and copolymers of VdF and tetrafluoroethylene (TFE). The acrylate may be polymethyl methacrylate (PMMA). Among these, polymethyl methacrylate (PMMA) is preferred. That is, methyl methacrylate is preferred as monomer B constituting monomer unit B. Note that monomer unit B may constitute 90 mol% or more of the monomer units constituting the second polymer portion. For example, monomer unit A constituting the first polymer portion may be included in the second polymer portion if it is 10 mol% or less.

[0025] The molecular weights of the first polymer portion and the second polymer portion are not particularly limited, but it is preferable that the molecular weight of the first polymer portion is smaller than that of the second polymer portion in order to facilitate the preparation of the protective layer forming ink in which the block polymer is dissolved in the liquid component during the protective layer formation process described later. Here, the molecular weights of the first polymer portion and the second polymer portion refer to the number average molecular weight.

[0026] The molecular weight (number-average molecular weight) of the first polymer portion may be, for example, 1,000 or more and 100,000 or less. The molecular weight (number-average molecular weight) of the second polymer portion may be, for example, 10,000 or more and 1,000,000 or less. When the number-average molecular weight is within the above range, a protective layer with good flexibility is easily obtained. When the negative electrode is wound during the battery manufacturing process, it is easy to follow the negative electrode, and the coverage of the negative electrode surface by the protective layer is easily maintained.

[0027] From the viewpoint of suppressing contact between lithium metal and non-aqueous electrolyte and suppressing penetration of the protective layer by dendrites, the thickness of the protective layer may be 0.1 μm or more and 5 μm or less, or 0.5 μm or more and 2 μm or less. The thickness of the protective layer is determined by obtaining a cross-sectional image of the protective layer on the negative electrode surface using a scanning electron microscope (SEM), measuring the thickness of 10 arbitrary points on the protective layer using the said cross-sectional image, and calculating the average value of these measurements.

[0028] The protective layer contains the block polymer described above. The protective layer may also contain materials other than the block polymer. Examples of materials other than the block polymer include resin materials and inorganic particles. Examples of resin materials include the materials described above as the first or second polymer portion, as well as polyolefin resins, silicone resins, epoxy resins, and the like. The resin material may be used alone or in combination of two or more types.

[0029] Inorganic particles are particles containing inorganic materials (e.g., metal oxides, metal hydroxides, metal composite oxides, metal nitrides, metal carbides, metal fluorides, etc.). Within the protective layer, the mixing of block polymers (and resin materials) and inorganic particles facilitates good lithium-ion conductivity in the protective layer, allowing for smooth lithium-ion movement between the negative electrode and the non-aqueous electrolyte via the protective layer during charging and discharging. To enhance the strength of the protective layer, the density of inorganic particles is 6 g / cm³. 3 That's fine too.

[0030] Furthermore, the density of inorganic particles may be 3.5 times or more the density in areas within the protective layer that are not occupied by inorganic particles (i.e., areas occupied by block polymer or resin material). In this case, it is thought that when the protective layer is formed, the inorganic particles will be deposited thinly and densely, forming a film of uniform thickness. Therefore, uneven distribution due to aggregation of inorganic particles in the planar direction of the protective layer is suppressed, variations in strength in the planar direction of the protective layer are suppressed, and the reliability of the strength of the protective layer is improved.

[0031] Specific examples of inorganic materials that constitute inorganic particles include copper oxide, bismuth oxide, tungsten oxide, indium oxide, and silver oxide. Inorganic particles (inorganic materials) may be used individually or in combination of two or more types. In particular, it is preferable that the inorganic particles include at least one selected from the group consisting of copper oxide particles and bismuth oxide particles. In this case, the density of the inorganic particles should be 6 g / cm³. 3 It is easier to increase the size of the material, and it is also easier to adjust the density ratio of inorganic particles to resin material to 3.5 or higher. It is easier to uniformly disperse inorganic particles in the planar direction of the protective layer. In other words, it is easier to obtain a protective layer with high strength, and the reliability of the strength of the protective layer is also easily improved. Furthermore, it is easier to obtain a protective layer with good lithium ion conductivity.

[0032] If the protective layer contains resin materials other than block polymers, the proportion of block polymers to the total of block polymers and resin materials may be 80% or more, 90% or more, or 95% or more by mass.

[0033] If the protective layer contains inorganic particles, the mass percentage of inorganic particles in the protective layer may be 50% by mass or less, 35% by mass or less, 5% by mass or more, or 20% by mass or less. When the mass percentage of inorganic particles in the protective layer is within the above range, flexibility, strength, and lithium ion conductivity are sufficiently ensured in the protective layer.

[0034] The protective layer can be formed, for example, by applying a protective layer-forming ink to the surface of the negative electrode current collector and allowing it to dry. The application can be carried out using, for example, a bar coater, applicator, or gravure coater. The protective layer-forming ink can be prepared, for example, by adding and mixing a block polymer, a liquid component, and, if necessary, other resin materials and inorganic particles. The liquid component can be a component that disperses inorganic particles and dissolves resin materials, such as N-methyl-2-pyrrolidone (NMP), dimethyl ether (DME), or tetrahydrofuran (THF).

[0035] It is preferable to provide a space between the negative electrode and the positive electrode for the deposition of lithium metal. This space can be formed by providing a spacer between the negative electrode and the positive electrode. From the viewpoint of improving productivity, the same material as the protective layer may be used for the spacer. When forming the protective layer, the thickness of the protective layer may be partially increased, and the thicker portion may be used as a spacer. That is, the spacer may be integrated with the protective layer. For example, a protective layer may be formed by applying protective layer forming ink to the surface of the negative electrode current collector using a coater (e.g., a gravure coater), and then applying the same protective layer forming ink in a line on the protective layer using a dispenser to form a line-shaped protrusion (spacer). From the viewpoint of improving productivity, the drying of the protective layer and the protrusion may be performed simultaneously after the protrusion has been formed.

[0036] The following provides a more detailed explanation of each component of a lithium-ion secondary battery. [Negative electrode] The negative electrode is equipped with a negative electrode current collector. In a lithium secondary battery, lithium metal is deposited on the surface of the negative electrode during charging. More specifically, lithium ions contained in the non-aqueous electrolyte accept electrons on the negative electrode during charging, becoming lithium metal, and depositing on the surface of the negative electrode. The lithium metal deposited on the surface of the negative electrode dissolves as lithium ions in the non-aqueous electrolyte during discharge. The lithium ions contained in the non-aqueous electrolyte may originate from lithium salts added to the non-aqueous electrolyte, or they may be supplied from the positive electrode active material during charging, or both. The protective layer covers the surface of the negative electrode current collector if no lithium metal is deposited on its surface, and covers the surface of the lithium metal if lithium metal is deposited on its surface.

[0037] The negative electrode may include a lithium ion storage layer supported on the negative electrode current collector (a layer that exhibits capacity through the absorption and release of lithium ions by the negative electrode active material (such as graphite)). In this case, the open-circuit potential of the negative electrode when fully charged may be 70 mV or less relative to the lithium metal (lithium dissolution potential). When the open-circuit potential of the negative electrode when fully charged is 70 mV or less relative to the lithium metal, lithium metal is present on the surface of the lithium ion storage layer when fully charged. That is, the negative electrode exhibits capacity through the deposition and dissolution of lithium metal. The protective layer covers the surface of the lithium ion storage layer if no lithium metal is deposited on its surface, and covers the surface of the lithium metal if lithium metal is deposited on its surface.

[0038] Here, "fully charged" refers to the state in which the battery has been charged to a charge level of, for example, 0.98 × C or higher, where C is the rated capacity of the battery. The open-circuit potential of the negative electrode at full charge can be measured by disassembling the fully charged battery under an argon atmosphere, removing the negative electrode, and assembling a cell with lithium metal as the counter electrode. The non-aqueous electrolyte of the cell may have the same composition as the non-aqueous electrolyte in the disassembled battery.

[0039] The lithium-ion storage layer is formed by creating layers of a negative electrode composite material containing a negative electrode active material. In addition to the negative electrode active material, the negative electrode composite material may also contain binders, thickeners, conductive agents, etc.

[0040] Examples of negative electrode active materials include carbonaceous materials, Si-containing materials, and Sn-containing materials. The negative electrode may contain one type of negative electrode active material, or a combination of two or more types. Examples of carbonaceous materials include graphite, easily graphitizable carbon (soft carbon), and difficult-to-graphitize carbon (hard carbon).

[0041] Conductive materials include, for example, carbon materials. Examples of carbon materials include carbon black, acetylene black, Ketjenblack, carbon nanotubes, and graphite.

[0042] Examples of binders include fluororesins, polyacrylonitrile, polyimide resins, acrylic resins, polyolefin resins, and rubbery polymers. Examples of fluororesins include polytetrafluoroethylene and polyvinylidene fluoride.

[0043] The negative electrode current collector can be any conductive sheet. Examples of conductive sheets include foil and film.

[0044] The material of the negative electrode current collector (conductive sheet) may be any conductive material other than lithium metal and lithium alloys. The conductive material may be a metallic material such as a metal or alloy. It is preferable that the conductive material is one that does not react with lithium. More specifically, it is preferable that the conductive material does not form any alloys or intermetallic compounds with lithium. Examples of such conductive materials include copper (Cu), nickel (Ni), iron (Fe), and alloys containing these metallic elements, or graphite in which the basal surface is preferentially exposed. Examples of alloys include copper alloys and stainless steel (SUS). Among these, copper and / or copper alloys with high conductivity are preferred.

[0045] The thickness of the negative electrode current collector is not particularly limited, but can be, for example, 5 μm or more and 300 μm or less.

[0046] [Positive electrode] The positive electrode comprises, for example, a positive electrode current collector and a positive electrode composite layer supported by the positive electrode current collector. The positive electrode composite layer includes, for example, a positive electrode active material, a conductive material, and a binder. The positive electrode composite layer may be formed on only one side of the positive electrode current collector or on both sides. The positive electrode can be obtained, for example, by applying a positive electrode composite slurry containing the positive electrode active material, a conductive material, and a binder to both sides of the positive electrode current collector, drying the coating, and then rolling it.

[0047] The positive electrode active material is a material that intercepts and releases lithium ions. Examples of positive electrode active materials include lithium-containing transition metal oxides, transition metal fluorides, polyanions, fluorinated polyanions, and transition metal sulfides. Among these, lithium-containing transition metal oxides are preferred because they have low manufacturing costs and a high average discharge voltage.

[0048] During charging, lithium contained in lithium-containing transition metal oxides is released from the positive electrode as lithium ions and deposited as lithium metal on the negative electrode or negative electrode current collector. During discharge, the lithium metal dissolves from the negative electrode, releasing lithium ions, which are then absorbed into the composite oxide of the positive electrode. In other words, the lithium ions involved in charging and discharging generally originate from the solute in the non-aqueous electrolyte and the positive electrode active material.

[0049] Examples of transition metal elements included in lithium-containing transition metal oxides include Sc, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Y, Zr, and W. Lithium-containing transition metal oxides may contain one or more transition metal elements. The transition metal elements may be Co, Ni, and / or Mn. Lithium-containing transition metal oxides may optionally contain one or more main group elements. Examples of main group elements include Mg, Al, Ca, Zn, Ga, Ge, Sn, Sb, Pb, and Bi. The main group elements may also be Al, etc.

[0050] Among lithium-containing transition metal oxides, composite oxides containing Co, Ni, and / or Mn as transition metal elements, and possibly containing Al as an optional component, and having a layered rock salt-type crystalline structure, are preferred for obtaining high capacity. In this case, in a lithium secondary battery, the molar ratio of the total amount of lithium (mLi) in the positive and negative electrodes to the amount of metal M other than lithium in the positive electrode (mM), : mLi / mM, is set to, for example, 1.1 or less.

[0051] For example, the binders and conductive agents exemplified for the negative electrode can be used. The shape and thickness of the positive electrode current collector can be selected from the shape and range of the positive electrode current collector.

[0052] Examples of materials for the positive electrode current collector (conductive sheet) include metallic materials containing Al, Ti, Fe, etc. The metallic material may be Al, Al alloy, Ti, Ti alloy, Fe alloy, etc. The Fe alloy may be stainless steel (SUS).

[0053] The thickness of the positive electrode current collector is not particularly limited, but can be, for example, 5 μm or more and 300 μm or less.

[0054] [Separator] A porous sheet having ion permeability and insulating properties is used as the separator. Examples of porous sheets include thin films, woven fabrics, and nonwoven fabrics with microporous properties. The material of the separator is not particularly limited, but it may be a polymer material. Examples of polymer materials include olefin resins, polyamide resins, and cellulose. Examples of olefin resins include polyethylene, polypropylene, and copolymers of ethylene and propylene. The separator may contain additives as needed. Examples of additives include inorganic fillers.

[0055] The thickness of the separator is not particularly limited, but is, for example, 5 μm or more and 20 μm or less, and preferably 10 μm or more and 20 μm or less.

[0056] [Non-aqueous electrolytes] A non-aqueous electrolyte having lithium ion conductivity contains, for example, a non-aqueous solvent, lithium ions dissolved in the non-aqueous solvent, and anions. The non-aqueous electrolyte may be liquid or gel-like.

[0057] The liquid non-aqueous electrolyte is prepared by dissolving a lithium salt in a non-aqueous solvent. When the lithium salt dissolves in the non-aqueous solvent, lithium ions and anions are generated.

[0058] The gel-like non-aqueous electrolyte contains a lithium salt and a matrix polymer, or a lithium salt, a non-aqueous solvent, and a matrix polymer. As the matrix polymer, for example, a polymer material that absorbs the non-aqueous solvent and gels is used. Examples of the polymer material include fluororesin, acrylic resin, polyether resin, and the like.

[0059] As the lithium salt or anion, known ones used in the non-aqueous electrolyte of a lithium secondary battery can be used. Specifically, BF4 - , ClO4 - , PF6 - , CF3SO3 - , CF3CO2 - , anions of imides, anions of oxalate complexes, and the like can be mentioned. As the anions of imides, N(SO2CF3)2 - , N(C m F 2m+1 SO2) x (C n F 2n+1 SO2)y - (m and n are each independently an integer of 0 or 1 or more, x and y are each independently 0, 1, or 2, and x + y = 2 is satisfied.) and the like can be mentioned. The anion of the oxalate complex may contain boron and / or phosphorus. As the anion of the oxalate complex, bisoxalate borate anion, difluorooxalate borate anion: BF2(C2O4) - , PF4(C2O4) - , PF2(C2O4)2 -Examples include these. Non-aqueous electrolytes may contain these anions individually or in combination of two or more.

[0060] From the viewpoint of suppressing the dendritic deposition of lithium metal, the non-aqueous electrolyte preferably contains at least an oxalate complex anion, and among them, BF2(C2O4) - It is desirable to include fluorine-containing oxalate complex anions such as PF6. The interaction between the fluorine-containing oxalate complex anion and lithium makes it easier for lithium metal to precipitate uniformly in fine particulate form. Therefore, it is easier to suppress localized deposition of lithium metal. By controlling the deposition morphology of lithium metal to some extent using oxalate complex anions, the function of suppressing contact between the lithium metal and non-aqueous electrolyte in the protective layer is more effectively exerted. Fluorine-containing oxalate complex anions may be combined with other anions. Other anions include PF6. - And / or imide anions.

[0061] Examples of non-aqueous solvents include esters, ethers, nitriles, amides, or halogen-substituted compounds thereof. The non-aqueous electrolyte may contain one of these non-aqueous solvents or two or more of them. Examples of halogen-substituted compounds include fluorides.

[0062] Examples of esters include carbonate esters and carboxylic acid esters. Examples of cyclic carbonate esters include ethylene carbonate, propylene carbonate, and fluoroethylene carbonate (FEC). Examples of linear carbonate esters include dimethyl carbonate (DMC), ethyl methyl carbonate (EMC), and diethyl carbonate. Examples of cyclic carboxylic acid esters include γ-butyrolactone and γ-valerolactone. Examples of linear carboxylic acid esters include ethyl acetate, methyl propionate, and methyl fluoropropionate.

[0063] Examples of ethers include cyclic ethers and linear ethers. Examples of cyclic ethers include 1,3-dioxolane, 4-methyl-1,3-dioxolane, tetrahydrofuran, and 2-methyltetrahydrofuran. Examples of linear ethers include 1,2-dimethoxyethane, diethyl ether, ethyl vinyl ether, methylphenyl ether, benzyl ethyl ether, diphenyl ether, dibenzyl ether, 1,2-diethoxyethane, and diethylene glycol dimethyl ether.

[0064] The concentration of lithium salt in the non-aqueous electrolyte is, for example, between 0.5 mol / L and 3.5 mol / L. The concentration of anion in the non-aqueous electrolyte may also be between 0.5 mol / L and 3.5 mol / L. Furthermore, the concentration of anion of the oxalate complex in the non-aqueous electrolyte may be between 0.05 mol / L and 1 mol / L.

[0065] The non-aqueous electrolyte may contain additives. The additives may form a film on the negative electrode. The formation of a film derived from the additive on the negative electrode makes it easier to suppress dendrite formation. Examples of such additives include vinylene carbonate, FEC, vinyl ethyl carbonate (VEC), and the like.

[0066] [Lithium-ion rechargeable battery] The configuration of the lithium secondary battery according to this disclosure will be described below with reference to the drawings, using a cylindrical battery equipped with a wound electrode group as an example. Figure 1 is a longitudinal cross-sectional view of a lithium secondary battery 10, which is an example of this embodiment.

[0067] The lithium secondary battery 10 is a cylindrical battery comprising a cylindrical battery case, a wound electrode group 14 housed within the battery case, and a non-aqueous electrolyte (not shown). The battery case consists of a case body 15, which is a bottomed cylindrical metal container, and a sealing body 16 that seals the opening of the case body 15. The case body 15 has an annular stepped portion 21 formed by partially pressing the side wall from the outside near the opening. The sealing body 16 is supported by the opening-side surface of the stepped portion 21. A gasket 27 is placed between the case body 15 and the sealing body 16, thereby ensuring the airtightness of the battery case. Inside the case body 15, insulating plates 17 and 18 are placed at both ends of the electrode group 14 in the direction of the winding axis, respectively.

[0068] The sealing body 16 comprises a filter 22, a lower valve body 23, an insulating member 24, an upper valve body 25, and a cap 26. The cap 26 is located on the outside of the case body 15, and the filter 22 is located on the inside of the case body 15. The lower valve body 23 and the upper valve body 25 are connected to each other at their respective centers, with the insulating member 24 interposed between their respective peripheries. The filter 22 and the lower valve body 23 are connected to each other at their respective peripheries. The upper valve body 25 and the cap 26 are connected to each other at their respective peripheries. A ventilation hole is formed in the lower valve body 23. When the internal pressure of the battery case rises due to abnormal heat generation or the like, the upper valve body 25 bulges towards the cap 26 and separates from the lower valve body 23. This disconnects the electrical connection between the lower valve body 23 and the upper valve body 25. If the internal pressure rises further, the upper valve body 25 ruptures, and gas is discharged from the opening formed in the cap 26.

[0069] The electrode group 14 consists of a positive electrode 11, a negative electrode (negative electrode current collector) 12, and a separator 13. The positive electrode 11, the negative electrode 12, and the separator 13 interposed between them are all strip-shaped and are wound in a spiral pattern such that their respective width directions are parallel to the winding axis. Insulating plates 17 and 18 are positioned at both ends of the electrode group 14 in the axial direction, respectively.

[0070] Here, Figure 2 is a magnified view of a key part showing an example of the electrode group in Figure 1. Figure 2 is a schematic magnified view of region X enclosed by the dashed line in Figure 1, showing a state in which lithium metal has not been deposited on the surface of the negative electrode current collector.

[0071] As shown in Figure 2, the positive electrode 11 comprises a positive electrode current collector and a positive electrode composite layer. The positive electrode 11 is electrically connected to a cap 26, which also serves as a positive electrode terminal, via a positive electrode lead 19. One end of the positive electrode lead 19 is connected, for example, to the vicinity of the longitudinal center of the positive electrode 11 (the exposed portion of the positive electrode current collector). The other end of the positive electrode lead 19 extending from the positive electrode 11 is welded to the inner surface of the filter 22 through a through hole formed in the insulating plate 17.

[0072] The negative electrode 12 includes a negative electrode current collector 32, the surface of which is covered with a protective layer 40. The protective layer 40 is a layer containing the block polymer described above. The negative electrode 12 is electrically connected to the case body 15, which also serves as the negative electrode terminal, via a negative electrode lead 20. One end of the negative electrode lead 20 is connected, for example, to the longitudinal end of the negative electrode 12 (the exposed portion of the negative electrode current collector 32), and the other end is welded to the inner bottom surface of the case body 15. During charging, lithium metal is deposited on the surface of the negative electrode current collector 32, and the surface of the lithium metal is covered with the protective layer 40.

[0073] Here, Figure 3 is a magnified view of a key part showing another example of the electrode group in Figure 1. Figure 3 is a schematic magnified view of region X enclosed by the dashed line in Figure 1, showing a state in which lithium metal is not deposited on the surface of the negative electrode current collector. Components identical to those in Figure 2 are denoted by the same reference numerals and their explanations are omitted.

[0074] As shown in Figure 3, a spacer 50 is provided between the negative electrode 12, which has a protective layer 40 on its surface, and the separator 13. The spacer 50 is formed by linear protrusions provided along the longitudinal direction of the separator 13. The height of the spacer 50 (linear protrusions) based on the protective layer 40 is, for example, 10 μm or more and 100 μm or less. The width of the spacer 50 (linear protrusions) is 200 μm or more and 2000 μm or less. The spacer 50 may be made of the same material as the protective layer 40 and may be integrated with the protective layer 40. Multiple linear protrusions may be provided parallel to each other at predetermined intervals. As shown in Figure 3, if lithium metal is not deposited on the surface of the negative electrode current collector 32, a space 51 is formed between the negative electrode 12 and the separator 13. During charging, the lithium metal deposited on the surface of the negative electrode current collector 32 is contained in the space 51 between the negative electrode 12 and the separator 13 while being subjected to the pressing force of the separator 13.

[0075] Since the lithium metal is contained in the space 51 between the negative electrode 12 and the separator 13, the apparent volume change of the electrode group due to the deposition of lithium metal during the charge-discharge cycle is reduced. Therefore, the stress applied to the negative electrode current collector 32 is also suppressed. Furthermore, since pressure is applied from the separator 13 to the lithium metal contained between the negative electrode 12 and the separator 13, the deposition state of the lithium metal is controlled, making it less likely for the lithium metal to become isolated, and suppressing a decrease in charge-discharge efficiency.

[0076] In the illustrated example, the cross-sectional shape of the spacer 50 is rectangular. However, embodiments of the present disclosure are not limited thereto, and the spacer may be, for example, trapezoidal, rectangular with a curve at least one corner, elliptical, or part of an ellipse. In the illustrated example, the spacer 50 is provided between the negative electrode 12 and the separator 13. However, embodiments of the present disclosure are not limited thereto, and the spacer may be provided between the positive electrode and the separator, or between the positive electrode and the negative electrode and the separator, respectively.

[0077] The illustrated example describes a cylindrical lithium secondary battery equipped with a wound electrode group, but the shape of the lithium secondary battery is not limited to this, and can be appropriately selected from various shapes such as cylindrical, coin-type, prismatic, sheet-type, and flat-type depending on its application. The form of the electrode group is also not particularly limited and may be stacked. Furthermore, known components other than the electrode group and non-aqueous electrolyte of the lithium secondary battery can be used without particular restriction.

[0078] [Examples] The lithium secondary batteries relating to this disclosure will be described in more detail below based on examples and comparative examples. However, this disclosure is not limited to the following examples.

[0079] Example 1 (Fabrication of the positive electrode) A layered rock salt type lithium-containing transition metal oxide (NCA: positive electrode active material) containing Li, Ni, Co, and Al (with a molar ratio of Li to the total of Ni, Co, and Al being 1.0), acetylene black (AB: conductive material), and polyvinylidene fluoride (PVdF: binder) were mixed in a mass ratio of NCA:AB:PVdF = 95:2.5:2.5. An appropriate amount of N-methyl-2-pyrrolidone (NMP) was then added and the mixture was stirred to prepare a positive electrode mixture slurry.

[0080] The obtained positive electrode mixture slurry was applied to both sides of an Al foil (positive electrode current collector), dried, and then rolled out using a roller to create the coating of the positive electrode mixture. Finally, the resulting laminate of the positive electrode current collector and the positive electrode mixture was cut to a predetermined electrode size to obtain a positive electrode having positive electrode mixture layers on both sides of the positive electrode current collector.

[0081] (Fabrication of a negative electrode with a protective layer on its surface) A strip of electrolytic copper foil (15 μm thick) was prepared as the negative electrode current collector, and a 25 μm Li foil was attached to the negative electrode current collector. A protective layer forming ink was prepared by mixing a block polymer with NMP, which is a dispersion medium. The protective layer forming ink was applied to both sides of the negative electrode and dried to form a protective layer (2 μm thick).

[0082] The block polymer used was a synthesized ABA-type triblock copolymer in which both ends of the second polymer portion, polymethyl methacrylate (PMMA) (number average molecular weight 19,000), were terminated with the first polymer portion, polystyrene (PS) (number average molecular weight 9,000).

[0083] (Preparation of non-aqueous electrolytes) Ethylene carbonate (EC) and dimethyl carbonate (DMC) were mixed in a volume ratio of EC:DMC = 30:70. LiPF6 was dissolved at a concentration of 1 mol / L and LiBF2(C2O4) at a concentration of 0.1 mol / L in the resulting mixed solvent to prepare a liquid non-aqueous electrolyte.

[0084] (Battery assembly) One end of an aluminum positive electrode lead was welded to the positive electrode current collector. One end of a nickel negative electrode lead was welded to the negative electrode obtained above. In an inert gas atmosphere, the positive and negative electrodes were wound in a spiral shape with a polyethylene separator (microporous membrane) between them to create an electrode group.

[0085] The electrode group was housed in a bag-shaped outer casing made of a laminate sheet with an Al layer, the non-aqueous electrolyte was injected, and then the outer casing was sealed to fabricate lithium secondary battery A1. When housing the electrode group in the outer casing, the other ends of the positive electrode lead and the other end of the negative electrode lead were left exposed to the outside of the outer casing.

[0086] [evaluation] A charge-discharge cycle test was performed on battery A1. In the charge-discharge cycle test, the battery was charged in a constant temperature chamber at 25°C under the following conditions, then paused for 20 minutes, and then discharged under the following conditions. This cycle was repeated 150 times.

[0087] (charging) Constant current charging was performed at a current of 10mA per unit area (square centimeter) of the electrodes until the battery voltage reached 4.3V. Then, constant voltage charging was performed at a voltage of 4.3V until the current value per unit area of ​​the electrodes reached 1mA.

[0088] (discharge) A constant current discharge was performed at a current of 10mA per unit area (square centimeter) of the electrodes until the battery voltage reached 3V.

[0089] The ratio of the discharge capacity C2 at cycle 150 to the discharge capacity C1 at cycle 1 (C2 / C1 × 100) was calculated as the capacity retention rate (%) at cycle 150.

[0090] Example 2 As the block polymer, an ABA-type triblock copolymer was synthesized and used, in which both ends of the second polymer portion, polyethylene oxide (PEO) (number average molecular weight 20,000), were terminated with the first polymer portion, polystyrene (PS) (number average molecular weight 9,000). Aside from this, lithium secondary battery A2 was fabricated and evaluated using the same method as in Example 1.

[0091] Comparative Example 1 Lithium secondary battery B1 was fabricated and evaluated using the same method as in Example 1, except that a protective layer was not formed on the surface of the negative electrode current collector.

[0092] Comparative Example 2 A protective layer-forming ink was prepared by mixing polymethyl methacrylate (PMMA) (number average molecular weight 19,000) with NMP as a dispersion medium. The protective layer-forming ink was applied to the surface of the negative electrode current collector and dried to form a protective layer (thickness 2 μm) composed of PMMA layers. Lithium secondary battery B2 was fabricated and evaluated using the same method as in Example 1.

[0093] Comparative Example 3 A protective layer-forming ink was prepared by mixing polystyrene (PS) (number average molecular weight 9,000) with NMP, a dispersion medium. The protective layer-forming ink was applied to the surface of the negative electrode current collector and dried to form a protective layer (thickness 2 μm) composed of PS layers. Lithium secondary battery B3 was fabricated and evaluated using the same method as in Example 1.

[0094] Comparative Example 4 A protective layer-forming ink was prepared by mixing 51 parts by mass of polymethyl methacrylate (PMMA) (number average molecular weight 19,000), 49 parts by mass of polystyrene (PS) (number average molecular weight 9,000), and NMP as a dispersion medium. The protective layer-forming ink was applied to the surface of the negative electrode current collector and dried to form a protective layer (thickness 2 μm) composed of a mixed layer of PMMA and PS. Lithium secondary battery B4 was fabricated and evaluated using the same method as in Example 1.

[0095] Table 1 shows the evaluation results for batteries A1-A2 and B1-B4.

[0096] In battery B1, the capacity retention rate decreased because no protective layer was provided. In batteries B2 and B3, the protective layer contained either the first polymer or the second polymer individually, but the capacity retention rate did not improve. In battery B4, the protective layer contained a mixture of the first polymer and the second polymer, but the capacity retention rate did not improve.

[0097] In contrast, batteries A1 to A2, which incorporated a block polymer in which the first polymer portion and the second polymer portion were bonded into a protective layer, showed a significantly higher capacity retention rate compared to batteries B1 to B4.

[0098] [Table 1] [Industrial applicability]

[0099] The lithium secondary battery of this disclosure can be used in electronic devices such as mobile phones, smartphones, and tablet devices, electric vehicles including hybrid and plug-in hybrid vehicles, and home battery storage systems combined with solar cells.

[0100] Although the present invention has been described in relation to preferred embodiments at present, such disclosure should not be interpreted restrictively. Various modifications and alterations will undoubtedly become apparent to those skilled in the art in the field to which the invention pertains by reading the above disclosure. Accordingly, the appended claims should be interpreted as encompassing all modifications and alterations without departing from the true spirit and scope of the invention. [Explanation of Symbols]

[0101] 10 Lithium-ion rechargeable batteries 11 Positive electrode 12 Negative electrode 13 Separator 14 electrode group 15 Case body 16 Sealing body 17, 18 Insulating board 19 Positive lead 20 Negative lead 21 Stepped section 22 filters 23 Lower valve body 24 Insulating material 25 Upper valve body 26 caps 27 Gasket 32 Negative electrode current collector 40 protective layer 50 Spacers 51 Space

Claims

1. A positive electrode that absorbs lithium ions during discharge and releases the lithium ions during charging, A negative electrode in which lithium metal is deposited during charging and the lithium metal dissolves during discharge, A non-aqueous electrolyte having lithium ion conductivity, Equipped with, The surface of the negative electrode is covered with a protective layer. The protective layer comprises a block polymer in which a first polymer portion having a repeating structure of monomer unit A and a second polymer portion having a repeating structure of monomer unit B are bonded together. The block polymer is an ABA-type triblock copolymer in which the first polymer portion is bonded to both ends of the second polymer portion. The tensile strength of the first polymer portion is greater than the tensile strength of the second polymer portion. The degree of swelling of the second polymer portion relative to the non-aqueous electrolyte is greater than the degree of swelling of the first polymer portion relative to the non-aqueous electrolyte. The monomer unit B is a methyl methacrylate unit, A lithium secondary battery wherein the molecular weight of the first polymer portion is smaller than the molecular weight of the second polymer portion.

2. The lithium secondary battery according to claim 1, wherein the monomer unit A is a styrene unit.

3. The lithium secondary battery according to claim 1 or 2, wherein the molecular weight of the first polymer portion is 1,000 or more and 100,000 or less.

4. The lithium secondary battery according to any one of claims 1 to 3, wherein the molecular weight of the second polymer portion is 10,000 or more and 1,000,000 or less.

5. The lithium secondary battery according to any one of claims 1 to 4, wherein the thickness of the protective layer is 0.1 μm or more and 5 μm or less.

Images