Hot water tank, its manufacturing method, and hot water heater

Abstract

The hot water storage tank comprises a main body, a first member, and a welded portion formed by welding the main body and the first member, and the main body is constructed using a corrosion-resistant material having corrosion resistance other than austenitic stainless steel.

Description

[Technical field]

[0001] The present disclosure relates to a hot water tank, a manufacturing method thereof, and a water heater including the hot water tank. [Background technology]

[0002] Conventionally, a material that has corrosion resistance and does not decrease even when welded has been desired as a material for hot water tanks that store water containing chlorides. For example, Patent Document 1 discloses austenitic stainless steel as a material for containers that come into contact with clean water, sewage, etc. In the component design of the austenitic stainless steel described in Patent Document 1, a weld is formed with a solidification structure in which the ferrite layer is unlikely to be dense. Therefore, the austenitic stainless steel described in Patent Document 1 is expected to prevent a decrease in corrosion resistance caused by a Cr-deficient layer and maintain excellent corrosion resistance even in the weld. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] JP 2003-64453 A Summary of the Invention [Problem to be solved by the invention]

[0004] However, from the viewpoint of the manufacturing cost of the hot water storage tank, it is sometimes desired to use a cheaper material. On the other hand, even if a cheaper material is used from the viewpoint of the manufacturing cost, the hot water storage tank of the water heater needs to have a certain level of corrosion resistance.

[0005] The present disclosure has been made against the background of the above-mentioned problems, and aims to provide a hot water storage tank and a manufacturing method thereof that can maintain the corrosion resistance of welds while reducing manufacturing costs, as well as a water heater equipped with such a hot water storage tank. [Means for solving the problem]

[0006] The hot water storage tank according to the present disclosure is a hot water storage tank for storing water, including tap water, and includes a main body, a first member, a welded portion formed by welding the main body and the first member, and a welded portion formed by welding the main body and the first member. Below Established in , to make the main body stand on its own The body has a leg portion, and the portion that may come into contact with water is made of a corrosion-resistant material, other than austenitic stainless steel, having a pitting potential of 0.3 V vs. Ag / AgCl or more, and the leg portion is Unlike the main body, It is made of ferritic stainless steel, austenitic stainless steel, or duplex stainless steel that is a mixture of ferritic stainless steel and austenitic stainless steel, and the pitting potential of the outer peripheral surface of the legs and main body that does not come into contact with water is less than 0.3 V vs. Ag / AgCl.

[0007] A manufacturing method of a hot water tank according to the present disclosure is a manufacturing method of a hot water tank for storing water including tap water, comprising: a main body member selection step of selecting a coil material of ferritic stainless steel or a coil material of duplex stainless steel mixed with ferritic stainless steel and austenitic stainless steel, each having a pitting potential of 0.3 V vs. Ag / AgCl or more; a step of forming a main body having a cylindrical barrel portion from the coil material selected in the main body member selection step, each having a pitting potential of 0.3 V vs. Ag / AgCl or more; a preparation step of preparing a piping connection part made of ferritic stainless steel, austenitic stainless steel, or a duplex stainless steel mixed with ferritic stainless steel and austenitic stainless steel, each having a pitting potential of 0.3 V vs. Ag / AgCl or more; and a step of welding the piping connection part prepared in the preparation step, each having a pitting potential of 0.3 V vs. Ag / AgCl or more, to the main body. a step of fixing a leg portion below the main body portion, the leg portion enabling the main body portion to stand on its own, the leg portion being made of ferritic stainless steel, austenitic stainless steel, or a duplex stainless steel which is a mixture of ferritic stainless steel and austenitic stainless steel, unlike the main body portion; Equipped with.

[0008] Furthermore, the water heater according to the present disclosure includes the above-mentioned hot water storage tank, a circulating water circuit through which water, which is a heat medium, circulates, and a tap water circuit through which tap water, which is a heat medium, circulates. Effect of the Invention

[0009] The hot water tank according to the present disclosure includes a welded portion formed by welding a main body and a first member. The main body is made of a corrosion-resistant material other than austenitic stainless steel. This makes it possible to maintain the corrosion resistance of the welded portion while suppressing the cost of manufacturing the hot water tank. [Brief description of the drawings]

[0010] [Figure 1] 1 is a schematic configuration diagram of a water heater according to a first embodiment. [Diagram 2] 1 is a schematic configuration diagram of a hot water storage tank according to a first embodiment. [Diagram 3] FIG. 1 is a diagram showing an example of measurement of pitting potential. [Figure 4] 4 is a flowchart showing a manufacturing process of the hot water storage tank according to the first embodiment. [Diagram 5] 1A is a diagram for explaining a gap between a main body and a pipe connection at a main body weld of a hot water storage tank in accordance with embodiment 1. FIG. [Figure 6] 11 is a diagram for explaining legs of a hot water storage tank according to embodiment 2. FIG. [Figure 7] 13 is a diagram for explaining another leg portion of the hot water storage tank according to the second embodiment. FIG. [Figure 8] FIG. 10 is a diagram for explaining still another leg portion of the hot water storage tank according to the second embodiment. [Figure 9] FIG. 10 is a diagram for explaining still another leg portion of the hot water storage tank according to the second embodiment. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0011] Hereinafter, the hot water storage tank, its manufacturing method, and hot water heater according to the present disclosure will be described with reference to the drawings. The present disclosure is not limited to the following embodiments, and can be modified in various ways without departing from the spirit of the present disclosure. The present disclosure also includes all combinations of possible configurations among the configurations shown in the following embodiments. In the following description, terms indicating directions (e.g., "up", "down", "right", "left", etc.) are used as appropriate to facilitate understanding, but these are for explanation and do not limit the present disclosure. In each drawing, the same reference numerals are assigned to the same or equivalent parts, and this is common throughout the entire specification. In each drawing, the relative dimensional relationship or shape of each component may differ from the actual one.

[0012] Embodiment 1 (Water heater configuration) Fig. 1 is a schematic configuration diagram of a water heater 100 according to embodiment 1. In Fig. 1, solid lines indicate a circulating water circuit 102, and dashed lines indicate a tap water circuit 103. Moreover, solid arrows in Fig. 1 indicate the flow direction of tap water flowing through the tap water circuit 103.

[0013] As shown in Fig. 1, the water heater 100 includes a hot water storage tank 101, a circulating water circuit 102, and a tap water circuit 103. The circulating water circuit 102 is configured by connecting an outdoor unit 140, a booster heater 151, a radiator 152, a strainer 153, a circulating water circuit pump 154, a flowmeter 155, an expansion vessel 156, a plate type heat exchanger 170, and a first three-way valve 159 with piping. The booster heater 151, the strainer 153, the circulating water circuit pump 154, the flowmeter 155, the expansion vessel 156, the plate type heat exchanger 170, and the first three-way valve 159 are provided inside the indoor unit 150.

[0014] Water circulates in the circulating water circuit 102 as a heat medium. A circulating water circuit pump 154 ​​circulates the water in the circulating water circuit 102. A refrigerant circuit (not shown) in which a refrigerant circulates is provided inside the outdoor unit 140. The water circulating in the circulating water circuit 102 is heated by exchanging heat with the refrigerant inside the outdoor unit 140. The water circulating in the circulating water circuit 102 is also heated by a booster heater 151. The refrigerant and the water heated by the booster heater 151 flow into a first three-way valve 159.

[0015] The first three-way valve 159 switches the flow path of the water circulating through the circulating water circuit 102. In detail, the first three-way valve 159 causes the water heated by the booster heater 151 to flow to at least one of the plate heat exchanger 170 or the radiator 152.

[0016] In the plate-type heat exchanger 170, heat is exchanged between the water flowing through the circulating water circuit 102 and the tap water flowing through the tap water circuit 103. The tap water flowing through the tap water circuit 103 is heated by the water flowing through the circulating water circuit 102 that has flowed into the plate-type heat exchanger 170 from the first three-way valve 159.

[0017] The radiator 152 is provided outside the indoor unit 150 in order to heat the indoor space. The water flowing through the circulating water circuit 102, which has flowed into the radiator 152 from the first three-way valve 159, dissipates heat to the indoor air in the radiator 152. Here, the device for heating the indoor space provided outside the indoor unit 150 does not have to be the radiator 152. For example, a floor heating system may be provided instead of the radiator 152.

[0018] The water circulating through the circulating water circuit 102 dissipates heat in the plate heat exchanger 170 or the radiator 152, and then flows into the strainer 153. In the circulating water circuit 102, iron rust particles and other foreign matter generated in the radiator 152 and other locations may flow into the first three-way valve 159 together with the circulating water. However, foreign matter such as iron rust particles may damage the first three-way valve 159. The strainer 153 removes foreign matter such as iron rust particles from the water circulating through the circulating water circuit 102.

[0019] The water that flows out of the strainer 153 passes through a flow meter 155 and flows into the outdoor unit 140. In addition, an expansion vessel 156 may be provided in the circulating water circuit 102 between the booster heater 151 and the first three-way valve 159. The expansion vessel 156 absorbs the expanding water that is generated.

[0020] The tap water circuit 103 is configured by connecting a hot water storage tank 101, a tap water circuit pump 164, a plate type heat exchanger 170, a scale removal device 160, and a second three-way valve 169 with piping. A pressure relief valve 50 may be provided in the hot water storage tank 101. The hot water storage tank 101, the tap water circuit pump 164, the plate type heat exchanger 170, and the scale removal device 160 are provided inside the indoor unit 150.

[0021] Tap water flows as a heat medium through the tap water circuit 103. Depending on the state of the second three-way valve 169, the tap water may circulate through the tap water circuit 103 or may flow out of the water heater 100.

[0022] As indicated by solid arrow A in Fig. 1, tap water flows into the tap water circuit 103 from the outside. The tap water that flows into the tap water circuit 103 flows into the hot water storage tank 101 from the lower part of the hot water storage tank 101. The tap water that flows into the hot water storage tank 101 exits from a lower part of the hot water storage tank 101 that is different from the position where the tap water flows into the hot water storage tank 101, and is sent to the plate heat exchanger 170 by the tap water circuit pump 164. The tap water that has been sent to the plate heat exchanger 170 and flows through the tap water circuit 103 is heated by heat exchange with the water flowing through the circulating water circuit 102.

[0023] The tap water flowing through the tap water circuit 103 heated by the plate heat exchanger 170 passes through the scale remover 160 and flows into the upper part of the hot water storage tank 101. The scale remover 160 removes scalant ions such as calcium ions, magnesium ions, and ionic silica contained in the tap water flowing through the tap water circuit 103. Scalant ions are more likely to precipitate when the temperature of the tap water rises. The tap water heated in the plate heat exchanger 170 passes through the scale remover 160, so that the scalant ions are more likely to be removed. In addition, if the scalant ions precipitate in the plate heat exchanger 170, the heat exchange performance is reduced and the flow passages in the plate heat exchanger 170 are blocked. However, the tap water that flows back into the hot water storage tank 101 after being heated by the plate heat exchanger 170 has had the scalant ions removed. Therefore, when the tap water returned to the hot water storage tank 101 is sent again to the plate heat exchanger 170 by the tap water circuit pump 164, it is possible to suppress deposition of scale-causing ions on the plate heat exchanger 170. Therefore, by removing the scale-causing ions with the scale remover 160, it is possible to protect the plate heat exchanger 170.

[0024] The heated tap water that flows into the top of hot water storage tank 101 through scale removal device 160 flows out from the top of hot water storage tank 101 which is different from the inflow position. The heated tap water that flows out of hot water storage tank 101 flows out to the outside of water heater 100 through second three-way valve 169. The tap water that flows out to the outside of water heater 100 is supplied to a shower room, a washroom, a kitchen, etc.

[0025] The second three-way valve 169 switches the flow path of water circulating through the tap water circuit 103. In detail, the heated tap water flows out of the hot water storage tank 101, and then flows to at least one of the outside of the water heater 100 and the tap water circuit 103 by the second three-way valve 169.

[0026] When the tap water flow path does not communicate with the outside due to second three-way valve 169, the tap water flow path communicates with tap water circuit 103. In this case, tap water heated in hot water storage tank 101 circulates through tap water circuit 103. Therefore, after passing through second three-way valve 169, the tap water heated in hot water storage tank 101 merges with tap water flowing into tap water circuit 103 from the outside. Then, the tap water flowing in from the outside and the heated tap water flow into hot water storage tank 101 together.

[0027] (Hot water tank configuration) Next, a hot water storage tank 101 according to the present embodiment will be described with reference to Fig. 2. Fig. 2 is a schematic configuration diagram of the hot water storage tank 101 according to the embodiment 1. The hot water storage tank 101 includes a main body 1, a pipe connection 2, and a main body welded part 3 formed by welding the main body 1 and the pipe connection 2 together.

[0028] The main body 1 has a barrel 10 having a cylindrical shape and a head plate 20 provided to cover both ends of the barrel 10. The head plate 20 includes a first head plate 21 provided at one end of the barrel 10 and a second head plate 22 provided at the other end of the barrel 10. In the following description, the first head plate 21 and the second head plate 22 may be referred to as head plate 20 unless there is a need to particularly distinguish between them.

[0029] The body 10 and the head plate 20 are made of a corrosion-resistant material having different corrosion resistance from that of austenitic stainless steel. The corrosion-resistant material having different corrosion resistance from that of austenitic stainless steel is, for example, a ferritic stainless steel having a pitting potential of 0.3 V vs. Ag / AgCl or more, or a duplex stainless steel made by mixing ferritic stainless steel and austenitic stainless steel. In the following description, when there is no need to distinguish between ferritic stainless steel, austenitic stainless steel, and a duplex stainless steel made by mixing ferritic stainless steel and austenitic stainless steel, they may be referred to as stainless steel. Also, a duplex stainless steel made by mixing ferritic stainless steel and austenitic stainless steel may be referred to as duplex stainless steel.

[0030] The body 10 is formed into a cylindrical shape by welding a plate-shaped ferritic stainless steel or a plate-shaped duplex stainless steel having a pitting potential of 0.3 V vs. Ag / AgCl or more. In the body 10, the portion where the plate-shaped stainless steel is welded is the body weld 13. The body 10 and the first head plate 21, and the body 10 and the second head plate 22 are also welded. The portion where the body 10 and the first head plate 21 are welded is the first head plate weld 31, and the portion where the body 10 and the second head plate 22 are welded is the second head plate weld 32. The body weld 13 extends between the first head plate 21 and the second head plate 22, perpendicular to the circumferential direction of the cylindrical shape. The first head plate weld 31 and the second head plate weld 32 also extend in the circumferential direction of the cylindrical shape. The body 10, the first end plate 21, and the second end plate 22 may all be made of the same stainless steel, or one of them may be made of ferritic stainless steel and the others may be made of duplex stainless steel.

[0031] The pipe connection part 2 is made of ferritic stainless steel, austenitic stainless steel, or a duplex stainless steel made of a mixture of ferritic stainless steel and austenitic stainless steel, each having a pitting potential of 0.3 V vs. Ag / AgCl or more. The pipe connection part 2 is a part where a pipe through which tap water flows that constitutes the tap water circuit 103 (see FIG. 1) is connected to the hot water storage tank 101. The pipe connection part 2 may be a part of the pipe of the tap water circuit 103, or a joint to which the pipe of the tap water circuit 103 is connected. The pipe connection part 2 may be a part of a pipe other than the pipe of the tap water circuit 103. The joint as the pipe connection part 2 is, for example, a boss joint with a thread and a fastener joint. For example, a pressure relief valve 50 (see FIG. 1) may be connected to the joint as the pipe connection part 2. FIG. 2 shows an example in which five pipe connection parts 2 are provided, but the number of pipe connection parts 2 is not particularly limited. There may be one pipe connection part 2, or there may be five or more pipe connection parts. Furthermore, the pipe connection part 2 may be provided anywhere in the main body part 1. That is, the pipe connection part 2 may be provided in any part of the trunk part 10, the first end plate 21, and the second end plate 22. However, when the pipe connection part 2 is provided in a part made of ferritic stainless steel, the pipe connection part 2 is made of a material containing austenitic stainless steel. Here, the material containing austenitic stainless steel refers to austenitic stainless steel and duplex stainless steel which is a mixture of ferritic stainless steel and austenitic stainless steel.

[0032] The body weld portion 3 is a portion formed by welding the body portion 1 and the pipe connection portion 2. The body weld portion 3 will be described later.

[0033] (Pitting corrosion potential of hot water tank) Fig. 3 is a diagram showing an example of measurement of pitting potential. Fig. 3 shows an example of the current value flowing during voltage sweep. The horizontal axis of Fig. 3 is the swept potential, and the vertical axis is the common logarithm of the current value. In the measurement example shown in Fig. 3, silver and silver chloride (Ag / AgCl) were used as the reference electrode.

[0034] Pitting potential is a value that can be measured by electrochemical measurement of a metal material. The potential of the metal material is swept in the positive or negative direction to measure the potential dependence and reaction rate of the redox reaction that occurs on the electrode. In this case, the metal material is used as the electrode. Pitting potential can be measured with an electrochemical measuring device such as a potentiostat under test conditions that take into account the operating specifications of the water heater with a hot water storage tank and the water quality of the installation location, including "JIS G 0577:2014 Measurement method for pitting potential of stainless steel."

[0035] In FIG. 3, a point P1 shows a sudden rise in the current value. A passive film is formed on the surface of ferritic stainless steel, austenitic stainless steel, or a duplex stainless steel made of a mixture of ferritic stainless steel and austenitic stainless steel. This passive film is sound, but as the potential is increased, this passive film is locally destroyed and holes are formed. In other words, pitting corrosion grows. The lower limit potential at which this pitting corrosion occurs and grows is called the pitting corrosion potential. In FIG. 3, the pitting corrosion potential is shown as a pitting corrosion potential example PP. In this embodiment, the stainless steel constituting the main body 1 has a pitting corrosion potential of 0.3 V vs. Ag / AgCl or more before welding. In addition, it is desirable that the stainless steel constituting the pipe connection portion 2 has a pitting corrosion potential of 0.3 V vs. Ag / AgCl or more before welding.

[0036] The stainless steel constituting the main body 1 and the pipe connection 2 has high corrosion resistance due to the formation of a passive film on the metal surface, the main component of which is chromium (Cr). However, a large amount of heat is applied to the stainless steel during welding. This heat input history causes a phenomenon called sensitization of the stainless steel. Sensitization is a phenomenon in which the Cr concentration of chromium (Cr) in the stainless steel decreases along the grain boundaries in the metal, and the susceptibility to stress corrosion cracking increases. When sensitization occurs, the corrosion resistance decreases. In this embodiment, the main body welded portion 3, the trunk welded portion 13, the first head welded portion 31, and the second head welded portion 32 are each formed by welding. Therefore, even if the pitting potential before welding is 0.3 V vs. Ag / AgCl or more, the pitting potential after welding may be reduced. In this embodiment, it is desirable that the pitting potential of the main body welded portion 3, the trunk welded portion 13, the first head welded portion 31, and the second head welded portion 32 is 0.3 V vs. Ag / AgCl or more.

[0037] More specifically, it is desirable that the pitting potential of the main body welded portion 3, trunk welded portion 13, first head welded portion 31, and second head welded portion 32, which are in contact with the water stored in the main body 1, is 0.3 V vs. Ag / AgCl or more. Note that the pitting potential of the main body welded portion 3, trunk welded portion 13, first head welded portion 31, and second head welded portion 32, which are not in contact with water on the outer circumferential surface side of the main body 1, may be less than 0.3 V vs. Ag / AgCl. If the main body 1 and the piping connection 2 are made of stainless steel with a pitting potential of 0.3 V vs. Ag / AgCl or more, and the pitting potential of the water-contacting parts of the main body weld 3, the trunk weld 13, the first end plate weld 31, and the second end plate weld 32 is 0.3 V vs. Ag / AgCl or more, it will be possible to provide a hot water storage tank 101 that can maintain corrosion resistance, and a water heater 100 equipped with the hot water storage tank 101.

[0038] There is no particular limitation on the welding method used to form the main body weld 3, the trunk weld 13, the first head weld 31, and the second head weld 32. The welding method may be selected depending on the shape and conditions of the parts to be welded. For example, laser welding, TIG (Tungsten Inert Gas) welding, and CMT (Cold Metal Transfer) welding are selected as welding methods.

[0039] On the other hand, regardless of the welding method, oxides called oxide scale and weld burn may be generated on the surface of the welded portion depending on the conditions during welding. Therefore, after welding, the main body welded portion 3, the trunk welded portion 13, the first head welded portion 31, and the second head welded portion 32 each have a so-called temper color attached thereto. Such oxides cause a decrease in the corrosion resistance of the hot water storage tank 101. For this reason, in the trunk welded portion pickling step S16 to the main body welded portion pickling step S19 described below, pickling is performed to remove oxides from the welded portion. However, depending on the pickling conditions, the pitting potential of the welded portion may decrease. For example, when the pickling is performed for a long time or when the concentration of the acid used in the pickling is high, the pitting potential of the welded portion may decrease. For this reason, in this embodiment, it is desirable that the pitting potential of each of the main body welded portion 3, the trunk welded portion 13, the first head welded portion 31, and the second head welded portion 32 after pickling is 0.3 V vs. Ag / AgCl or more. More specifically, it is desirable that the pitting potential of the main body welded portion 3, trunk welded portion 13, first head welded portion 31, and second head welded portion 32 after pickling is 0.3 V vs. Ag / AgCl or more in the portions that come into contact with water stored inside the main body 1. Note that the pitting potential of the main body welded portion 3, trunk welded portion 13, first head welded portion 31, and second head welded portion 32 after pickling that does not come into contact with water on the outer peripheral surface side of the main body 1 may be less than 0.3 V vs. Ag / AgCl. Also, the outer peripheral surface of the main body 1 may or may not be pickled.

[0040] (Hot water tank manufacturing method) Next, a manufacturing method of the hot water storage tank 101 will be described with reference to Fig. 4. Fig. 4 is a flowchart showing the manufacturing steps of the hot water storage tank 101 according to the first embodiment. As shown in Fig. 4, the manufacturing method of the hot water storage tank 101 includes a body forming step S11, a body welding step S12, a pipe connection welding step S13, a first head plate welding step S14, a second head plate welding step S15, a body weld pickling step S16, a first head plate weld pickling step S17, a second head plate weld pickling step S18, and a main body weld pickling step S19.

[0041] In the body forming step S11, a portion that will become the body 10 is cut out from a roll of stainless steel, and a hole for connecting the pipe connection part 2 is formed. The ferritic stainless steel or duplex stainless steel that is a mixture of ferritic stainless steel and austenitic stainless steel that constitutes the body 10 is in a sheet form. This sheet-like stainless steel is in a coil shape wound into a roll and is called a coil material. The pitting potential of either the ferritic stainless steel or duplex stainless steel that constitutes the body 10 is 0.3 V vs. Ag / AgCl or more. In the body forming step S11, the coil material is cut to a predetermined length to form a rectangular stainless steel plate that forms the body 10. Next, a hole for welding the pipe connection part 2 is formed in the cut stainless steel plate. The hole is formed by cutting the stainless steel plate. The method for cutting the coil material is not particularly limited. For example, the coil material may be cut by a laser.

[0042] In the trunk welding step S12, the stainless steel plate in which the hole was formed in the trunk forming step S11 is roll-bent into a cylindrical shape with its longitudinal ends in contact with each other. The contacting ends of the cylindrical stainless steel plate are then welded to form a cylindrical trunk 10. The welded portion of the stainless steel plate is the trunk weld 13. It is desirable for the pitting potential of the trunk weld 13 to be 0.3 V vs. Ag / AgCl or higher.

[0043] In the pipe connection welding step S13, the hole in the body 10 formed in the body forming step S11 is widened by burring. Next, the pipe connection 2 is welded to the widened hole. The pipe connection 2 is made of ferritic stainless steel, austenitic stainless steel, or duplex stainless steel that is a mixture of ferritic stainless steel and austenitic stainless steel. The pitting potential of ferritic stainless steel, austenitic stainless steel, and duplex stainless steel is preferably 0.3 V vs. Ag / AgCl or more. In addition, when the body 10 is made of ferritic stainless steel, the pipe connection 2 made of austenitic stainless steel or duplex stainless steel is welded to the body 10. The portion where the pipe connection 2 is welded to the hole in the body 10 is the main body weld 3. The pitting potential of the main body weld 3 is preferably 0.3 V vs. Ag / AgCl or more.

[0044] In the first head welding process S14, the first head 21 is welded in the circumferential direction at one end of the cylindrical body 10. The first head 21 is made of ferritic stainless steel or a duplex stainless steel mixed with ferritic stainless steel and austenitic stainless steel, which has a pitting potential of 0.3 V vs. Ag / AgCl or more. The portion where the first head 21 and the body 10 are welded is the first head welded portion 31. The pitting potential of the first head welded portion 31 is preferably 0.3 V vs. Ag / AgCl or more. The body 10 and the first head 21 may be made of the same type of stainless steel, or one may be made of ferritic stainless steel and the other may be made of duplex stainless steel.

[0045] In the second head welding process S15, the second head 22 is welded in the circumferential direction at the other end of the cylindrical body 10. The second head 22 is made of ferritic stainless steel or a duplex stainless steel mixed with ferritic stainless steel and austenitic stainless steel, which has a pitting potential of 0.3 V vs. Ag / AgCl or more. The portion where the second head 22 and the body 10 are welded is the second head welded portion 32. The pitting potential of the second head welded portion 32 is preferably 0.3 V vs. Ag / AgCl or more. The body 10 and the second head 22 may be made of the same type of stainless steel, or one may be made of ferritic stainless steel and the other may be made of duplex stainless steel.

[0046] In the pickling process S16, the barrel weld 13 is pickled. After the pickling process, the temper color is removed from the barrel weld 13. It is desirable that the pitting potential of the barrel weld 13 after the pickling process is 0.3 V vs. Ag / AgCl or more.

[0047] In the first head welded portion pickling process S17, the first head welded portion 31 is pickled. After the pickling process, the temper color is removed from the first head welded portion 31. It is desirable that the pitting potential of the first head welded portion 31 after the pickling process is 0.3 V vs. Ag / AgCl or more.

[0048] In the second head welded portion pickling process S18, the second head welded portion 32 is pickled. After the pickling process, the temper color is removed from the second head welded portion 32. It is desirable that the pitting potential of the second head welded portion 32 after the pickling process is 0.3 V vs. Ag / AgCl or more.

[0049] In the main body weld pickling process S19, the main body weld 3 is pickled. After the pickling process, the temper color is removed from the main body weld 3. It is desirable that the pitting potential of the main body weld 3 after the pickling process is 0.3 V vs. Ag / AgCl or more.

[0050] The above-described steps do not include a step of connecting the pipe connection portion 2 to the first head plate 21 and the second head plate 22, but the pipe connection portion 2 may be welded to the first head plate 21 and the second head plate 22. The step of welding the pipe connection portion 2 to the first head plate 21 and the second head plate 22 is not particularly limited. In the first head plate welding step S14 and the second head plate welding step S15, the first head plate 21 and the second head plate 22 to which the pipe connection portion 2 has already been connected may be welded to the body portion 10. Also, in the first head plate welding step S14 and the second head plate welding step S15, the first head plate 21 and the second head plate 22 provided with holes to which the pipe connection portion 2 is connected may be welded to the body portion 10. In this case, in the first head plate welding step S14 and the second head plate welding step S15, the first head plate 21 and the second head plate 22 are welded to the body 10, and then the pipe connection portion 2 is welded to the first head plate 21 and the second head plate 22. In any case, in the body weld portion pickling step S19, all the body weld portions 3 are pickled. That is, not only the body weld portion 3 where the pipe connection portion 2 is welded to the body 10, but also the body weld portion 3 where the pipe connection portion 2 is welded to the first head plate 21 and the body weld portion 3 where the pipe connection portion 2 is welded to the second head plate 22 are pickled. Note that the order of the steps from the body weld portion pickling step S16 to the body weld portion pickling step S19 may be interchanged. Furthermore, the body weld portion pickling step S16 to the body weld portion pickling step S19 may not be individual steps, but may be one pickling step. That is, the trunk weld 13, the first head weld 31, the second head weld 32, and the main body weld 3 may be pickled all at once as a single pickling process. For example, by filling the hot water tank 101 with a pickling solution, pickling can be performed all at once.

[0051] (Main body welded parts) Next, the main body welded portion 3 will be described with reference to Fig. 5. Fig. 5 is a diagram for explaining the gap SP between the main body 1 and the pipe connection portion 2 at the main body welded portion 3 of the hot water storage tank 101 according to embodiment 1. The portion indicated as Inside in Fig. 3 is the inside of the main body 1. The portion indicated as Outside in Fig. 3 is the outside of the main body 1.

[0052] As described in the above-mentioned pipe connection welding step S13, the pipe connection 2 is welded to the hole in the body 10 widened by burring. As in the case of the body 10, the pipe connection 2 is welded to the hole in the first end plate 21 and the second end plate 22 widened by burring. The body weld 3 is formed by inserting the pipe connection 2 into the hole in the body 1, i.e., the body 10, the first end plate 21, and the second end plate 22, and welding it. Here, when welding the pipe connection 2 inserted into the hole in the body 1 to the body 1, a gap SP as shown in FIG. 3 may be formed between the body 1 and the pipe connection 2. In this embodiment, the body 1 and the pipe connection 2 are welded so that the width W of the gap SP exceeds 100 μm. Here, the width W of the gap SP is the length in the left-right direction of the paper surface in FIG. 3. It is preferable that the width W of the gap SP does not exceed the thickness of the body 1. In addition, the width W of the gap SP does not become 10 mm or more. For example, the width W of the gap SP is greater than 100 μm but is equal to or smaller than 2 mm.

[0053] When the width W of the gap SP between the main body 1 and the pipe connection part 2 is 100 μm or less, the supply of dissolved oxygen in the gap SP is insufficient compared to the surrounding outside, and the oxygen concentration becomes low. In such a case, an oxygen concentration cell is formed due to the difference in oxygen concentration, and the corrosion reaction of the stainless steel progresses. As a result, holes may be formed in the main body 1 due to the gap corrosion of the main body welded part 3, and water may leak from the main body 1. Therefore, in this embodiment, the main body 1 and the pipe connection part 2 are welded so that the width W of the gap SP does not become 100 μm or less. Note that when the main body 1 and the pipe connection part 2 are welded, the stainless steel may melt and solidify in a shape spanning the main body 1 and the pipe connection part 2. In other words, the gap SP may be formed in the space that was the outside of the main body 1 before welding. In this embodiment, the main body 1 and the pipe connection part 2 are welded so that the width W of such a gap SP does not become 100 μm or less.

[0054] As described above, the hot water tank 101 according to this embodiment includes a main body 1, a pipe connection 2 as a first member, and a welded portion formed by welding the main body 1 and the pipe connection 2. The main body 1 is made of a corrosion-resistant material having corrosion resistance except for austenitic stainless steel. Therefore, the cost of manufacturing the hot water tank 101 can be suppressed while maintaining the corrosion resistance of the welded portion.

[0055] In addition, in hot water tank 101 according to this embodiment, the corrosion-resistant material is a material with a pitting potential of 0.3 V vs. Ag / AgCl or more, so hot water tank 101 can maintain its corrosion resistance.

[0056] Moreover, in the hot water tank 101 according to this embodiment, the first member is a pipe connection part 2 that connects the pipe to the main body part 1, and the weld part is a main body weld part 3 where the pipe connection part 2 and the main body part 1 are welded together. Moreover, the pipe connection part 2 is made of a corrosion-resistant material having corrosion resistance except for austenitic stainless steel. Therefore, the corrosion resistance of the main body weld part 3 can be maintained while suppressing the cost of manufacturing the hot water tank 101.

[0057] The hot water storage tank 101 according to this embodiment includes a main body 1, a pipe connection 2 that connects a pipe to the main body 1, and a main body weld 3 formed by welding the pipe connection 2 and the main body 1. At least one of the main body 1 and the pipe connection 2 is made of a material containing austenitic stainless steel. The main body 1 is made of ferritic stainless steel, or a duplex stainless steel that is a mixture of ferritic stainless steel and austenitic stainless steel. The pipe connection 2 is made of ferritic stainless steel, austenitic stainless steel, or a duplex stainless steel that is a mixture of ferritic stainless steel and austenitic stainless steel.

[0058] In this configuration, when the main body 1 is made of ferritic stainless steel, the pipe connection part 2 is made of a material containing austenitic stainless steel. The material containing austenitic stainless steel refers to austenitic stainless steel and duplex stainless steel, so when the main body 1 is made of ferritic stainless steel, the pipe connection part 2 is made of austenitic stainless steel or duplex stainless steel. On the other hand, when the main body 1 is made of duplex stainless steel, the pipe connection part 2 may be made of ferritic stainless steel. That is, when the main body 1 is made of duplex stainless steel, the pipe connection part 2 is made of ferritic stainless steel, austenitic stainless steel, or duplex stainless steel. In this way, since at least one of the main body 1 and the pipe connection part 2 of the hot water storage tank 101 is made of a material containing austenitic stainless steel, the corrosion resistance of the main body weld part 3 can be maintained.

[0059] Moreover, water heater 100 according to this embodiment includes hot water storage tank 101, a circulating water circuit 102 in which water, which is a heat medium, circulates, and a tap water circuit 103 in which tap water, which is a heat medium, circulates. Since water heater 100 includes hot water storage tank 101 that can maintain corrosion resistance, damage to hot water storage tank 101 is less likely to affect the performance and product life of water heater 100.

[0060] In the hot water storage tank 101 according to this embodiment, the body weld 3 has a pitting potential of 0.3 V vs. Ag / AgCl or more. Therefore, the corrosion resistance of the body weld 3, which is the portion where the pipe connection part 2 is welded to the body part 1, can be maintained.

[0061] In the hot water storage tank 101 according to this embodiment, the main body 1 has a cylindrical body 10, a first end plate 21 provided at one end of the body 10, and a second end plate 22 provided at the other end of the body 10. The body 10 is welded between one end and the other end at a body weld 13 extending perpendicularly to the circumferential direction of the cylindrical shape, the body 10 and the first end plate 21 are welded at a first end plate weld 31, and the body 10 and the second end plate 22 are welded at a second end plate weld 32. The body weld 13, the first end plate weld 31, and the second end plate weld 32 each have a pitting potential of 0.3 V vs. Ag / AgCl or more.

[0062] In this configuration, the pitting potential of the welded portion of the main body 1 is 0.3 V vs. Ag / AgCl or more, so that the corrosion resistance of the welded portion can be maintained.

[0063] Furthermore, in the hot water storage tank 101 according to this embodiment, the main body welded portion 3, the trunk welded portion 13, the first head welded portion 31, and the second head welded portion 32 are each pickled with acid, and have a pitting potential of 0.3 V vs. Ag / AgCl or higher. Therefore, the corrosion resistance of the welded portions can be maintained after pickling with acid.

[0064] Furthermore, in the body welded portion 3 of the hot water storage tank 101 according to this embodiment, a gap SP exceeding 100 μm is provided between the body portion 1 and the pipe connection portion 2. This makes it possible to suppress the occurrence of crevice corrosion, and to maintain the corrosion resistance of the body welded portion 3.

[0065] The manufacturing method of the hot water tank 101 according to the present embodiment includes a step S11 of forming the main body 1 having a cylindrical barrel 10 with a coil material of ferritic stainless steel or a coil material of duplex stainless steel which is a mixture of ferritic stainless steel and austenitic stainless steel, each having a pitting potential of 0.3 V vs. Ag / AgCl or more. Also includes a step S13 of welding the piping connection part 2 made of ferritic stainless steel, austenitic stainless steel, or a duplex stainless steel which is a mixture of ferritic stainless steel and austenitic stainless steel, each having a pitting potential of 0.3 V vs. Ag / AgCl or more, to the main body 1.

[0066] With this configuration, the hot water tank 101 is manufactured from stainless steel with a pitting potential of 0.3 V vs. Ag / AgCl or higher, so that the hot water tank 101 having high corrosion resistance can be manufactured even if production variations occur in welding conditions, etc.

[0067] The manufacturing method of the hot water storage tank 101 according to the present embodiment also includes a step S16 of pickling the body welded portion 13 of the body 10, which is formed by welding the coil material and has a pitting potential of 0.3 V vs. Ag / AgCl or more. It also includes a step S17 of pickling the first head welded portion 31, which is a welded portion between the body 10 and the first head 21 provided at one end of the body 10 and has a pitting potential of 0.3 V vs. Ag / AgCl or more. It also includes a step S18 of pickling the second head welded portion 32, which is a welded portion between the body 10 and the second head 22 provided at the other end of the body 10 and has a pitting potential of 0.3 V vs. Ag / AgCl or more.

[0068] In this configuration, the body welded portion 13, the first head welded portion 31, and the second head welded portion 32, which have a pitting potential of 0.3 V vs. Ag / AgCl or more after welding, are pickled with acid. Since the pitting potential before pickling is 0.3 V vs. Ag / AgCl or more, the corrosion resistance of the body welded portion 13, the first head welded portion 31, and the second head welded portion 32 after pickling can be maintained. Therefore, a hot water storage tank 101 with high corrosion resistance can be manufactured.

[0069] Embodiment 2 In this embodiment, the differences from embodiment 1 will be mainly described. The present embodiment differs from embodiment 1 in that hot water tank 101 includes legs 40 provided on main body 1. Other configurations are the same as embodiment 1, and therefore description thereof will be omitted.

[0070] The leg portion 40 according to the present embodiment will be described with reference to Figs. 6 to 9. Fig. 6 is a diagram for explaining the leg portion 40 of the hot water storage tank 101 according to the second embodiment. Fig. 7 is a diagram for explaining another leg portion 40 of the hot water storage tank 101 according to the second embodiment. Fig. 8 is a diagram for explaining yet another leg portion 40 of the hot water storage tank 101 according to the second embodiment. Fig. 9 is a diagram for explaining yet another leg portion 40 of the hot water storage tank 101 according to the second embodiment.

[0071] As shown in Figs. 6 to 9, the hot water tank 101 includes a leg 40 provided on the main body 1. The leg 40 is made of ferritic stainless steel, austenitic stainless steel, or a duplex stainless steel made of a mixture of ferritic stainless steel and austenitic stainless steel. The leg 40 is provided to make the main body 1 self-supporting. For this reason, the leg 40 is provided on the head plate 20, which is disposed at the lower part in the direction of gravity, of the first head plate 21 or the second head plate 22. The method of fixing the leg 40 to the head plate 20 is not particularly limited as long as the leg 40 is fixed to the head plate 20. However, it is preferable that the leg 40 is fixed to the head plate 20 by welding. In addition, when the leg 40 and the head plate 20 are welded, it is preferable that at least one of the head plate 20 or the leg 40 is made of stainless steel including austenitic stainless steel. By including the austenitic stainless steel in either the head plate 20 or the leg 40, the leg 40 can be provided on the main body 1 without impairing the corrosion resistance of the hot water tank 101. The pitting potential of the legs 40 may be less than 0.3 V vs. Ag / AgCl. However, when the portion to which the legs 40 are welded is exposed to the inner circumferential surface side of the main body 1 and comes into contact with stored water, it is desirable that the pitting potential of the portion to which the legs 40 are welded be 0.3 V vs. Ag / AgCl or more.

[0072] As long as the main body 1 can be supported so as to stand on its own, the shape and number of the legs 40 are not particularly limited. As shown in FIG. 6, the legs 40 may be plate-shaped and arranged so that the flat surface is placed on the ground. FIG. 6 shows an example in which one plate-shaped leg 40 is fixed to the center of the mirror plate 20. As shown in FIG. 7, the surface of the leg 40 fixed to the mirror plate 20 may have a shape that follows the curved surface of the mirror plate 20. As shown in FIG. 8 and FIG. 9, the legs 40 may not be singular, but may be multiple. FIG. 8 shows an example in which two legs 40 having an L-shape in side view are fixed to the mirror plate 20. FIG. 9 shows an example in which three legs 40 are fixed to the mirror plate 20. As shown in FIG. 9, it is not necessary that all of the multiple legs 40 have the same shape and size. The legs 40 may be made of a material other than ferritic stainless steel, austenitic stainless steel, and duplex stainless steel. [Explanation of symbols]

[0073] 1 main body, 2 piping connection, 3 main body weld, 10 body, 13 body weld, 20 head plate, 21 first head plate, 22 second head plate, 31 first head plate weld, 32 second head plate weld, 40 legs, 50 pressure relief valve, 100 water heater, 101 hot water storage tank, 102 circulating water circuit, 103 tap water circuit, 140 outdoor unit, 150 indoor unit, 151 booster heater, 152 radiator, 153 strainer, 154 circulating water circuit pump, 155 flow meter, 156 expansion vessel, 159 first three-way valve, 160 scale removal device, 164 tap water circuit pump, 169 second three-way valve, 170 plate heat exchanger, P1 point, PP pitting potential example, SP gap, W width.

Claims

1. A hot water storage tank for storing water, including tap water, comprising: A main body portion, A first member; a welded portion formed by welding the main body portion and the first member; Equipped with The main body is made of a corrosion-resistant material, other than austenitic stainless steel, having a pitting potential of 0.3 V vs. Ag / AgCl or more. Hot water tank.

2. the first member is a pipe connection portion that connects a pipe to the main body portion, The weld portion is a body weld portion formed by welding the pipe connection portion and the body portion, The pipe connection portion is made of the corrosion-resistant material. The hot water storage tank according to claim 1.

3. The body weld has a pitting potential of 0.3 V vs. Ag / AgCl or more. The hot water storage tank according to claim 2.

4. A hot water storage tank for storing water, including tap water, comprising: A main body portion, A pipe connection portion for connecting a pipe to the main body portion; a main body weld portion formed by welding the piping connection portion and the main body portion; Equipped with At least one of the main body and the pipe connection portion is made of a material containing austenitic stainless steel, The main body is made of ferritic stainless steel or a duplex stainless steel made of a mixture of ferritic stainless steel and austenitic stainless steel, The pipe connection part is made of ferritic stainless steel, austenitic stainless steel, or a duplex stainless steel made of a mixture of ferritic stainless steel and austenitic stainless steel, The body weld has a pitting potential of 0.3 V vs. Ag / AgCl or more. Hot water tank.

5. The body weld is pickled and has a pitting potential of 0.3 V vs. Ag / AgCl or more. The hot water storage tank according to any one of claims 2 to 4.

6. The main body portion is A body portion having a cylindrical shape; A first end plate provided at one end of the body portion; a second end plate provided at the other end of the body; having The body portion is welded between the one end portion and the other end portion at a body portion weld portion extending perpendicularly to a circumferential direction of the cylindrical shape, The body portion and the first head are welded to each other at a first head weld portion, The body portion and the second head are welded to each other at a second head weld portion, Each of the body welded portion, the first head welded portion, and the second head welded portion has a pitting potential of 0.3 V vs. Ag / AgCl or more. The hot water storage tank according to any one of claims 2 to 4.

7. the body welded portion, the first head welded portion, and the second head welded portion are pickled; Each of the body welded portion, the first head welded portion, and the second head welded portion has a pitting potential of 0.3 V vs. Ag / AgCl or more. The hot water storage tank according to claim 6.

8. At the body welded portion, a gap exceeding 100 μm is provided between the body portion and the pipe connection portion. The hot water storage tank according to any one of claims 2 to 4.

9. The device further includes a leg portion provided on the main body portion, The legs are made of ferritic stainless steel, austenitic stainless steel, or a duplex stainless steel made of a mixture of ferritic stainless steel and austenitic stainless steel. The hot water storage tank according to any one of claims 2 to 4.

10. A method for manufacturing a hot water tank for storing water, including tap water, comprising the steps of: A step of forming a main body having a cylindrical body portion from a coil material of ferritic stainless steel or a coil material of duplex stainless steel which is a mixture of ferritic stainless steel and austenitic stainless steel, the pitting potential of which is 0.3 V vs. Ag / AgCl or more; a step of welding a pipe connection part made of ferritic stainless steel, austenitic stainless steel, or a duplex stainless steel made of a mixture of ferritic stainless steel and austenitic stainless steel, the duplex stainless steel having a pitting corrosion potential of 0.3 V vs. Ag / AgCl or more, to the main body part; A method for manufacturing a hot water tank comprising:

11. A step of pickling a welded portion of the body of the body, to which the coil material is welded, and having a pitting potential of 0.3 V vs. Ag / AgCl or more; A step of pickling a first head welded portion, which is a welded portion between the body portion and a first head provided at one end of the body portion and has a pitting potential of 0.3 V vs. Ag / AgCl or more; a step of pickling a second head welded portion, which is a welded portion between the body portion and a second head provided at the other end portion of the body portion and has a pitting potential of 0.3 V vs. Ag / AgCl or more; Equipped A method for manufacturing the hot water tank according to claim 10.

12. A hot water storage tank according to any one of claims 1 to 4, a circulating water circuit in which water, which is a heat medium, circulates; A tap water circuit in which tap water circulates as a heat medium. A water heater equipped with.