Method of treatment of a ceramic batch, ceramic pins and apparatus for treatment of a ceramic batch

Abstract

The invention relates to a method of treatment of a ceramic batch, to ceramic pins and to an apparatus for treatment of a ceramic batch. The method comprises the following steps: (a) providing a ceramic batch; (b) providing a tool for forming the ceramic batch, for example a forming tool (103) of an extruder (100); (c) forming the ceramic batch by means of the tool to give a bundle (400) of individual strands (401); and (d) drying, by means of a drying apparatus (200), at least one section of the bundle (400) in air, i.e. before it comes into contact with a solid body beneath – for example with a dish, a tablet or a belt conveyor (300), with the exception of another, already dried section of the bundle (400).

Description

[0001] Method for treating a ceramic offset, ceramic pins and

[0002] Device for treating a ceramic offset

[0003] Description

[0004] The invention relates to a method for treating a ceramic batch, ceramic pins and a device for treating a ceramic batch.

[0005] In the field of ceramics, a "ceramic batch" is understood to be a composition of one or more components from which a ceramic, i.e., a ceramic material, can be produced through firing, particularly sintering. A wide variety of ceramic raw materials are known as components of ceramic batches, for example, various silicate or oxide raw materials, such as raw materials based on the oxides aluminum oxide (Al2O3) or silicon oxide (SiO2). Ceramic batches are usually in the form of plastic, moldable masses.

[0006] Ceramics, i.e., ceramic materials, produced from such a ceramic batch are characterized by special properties. These properties can include, for example, high strength, high temperature resistance, and high open porosity.

[0007] It is known that ceramic materials can be made available in the form of ceramic pins, which find particular application due to their special properties. Due to their high strength, ceramic pins can be used, for example, as additives in building materials to positively influence the strength of building materials. Furthermore, due to their high temperature resistance, ceramic pins can be used, for example, for catalytic processes that take place at high temperatures. Another advantage is the large specific surface area of ​​ceramic pins resulting from their high open porosity. Due to this large specific surface area, ceramic pins can be used very effectively for catalytic processes. Either the ceramic material of the ceramic pin can be catalytically active, or the surface of the pores can be coated with catalytically active substances.

[0008] The mass production of such ceramic pins is problematic in the current state of the art. Mass production typically involves the manufacture of a bundle of individual strands of a ceramic batch from which the ceramic pins are to be fired. However, due to the nature of ceramic batches, the individual strands have a significant tendency to stick together. However, it is practically impossible to produce individual ceramic pins from such bonded strands of a ceramic batch. Rather, the bonded strands form a spatial network that remains intact even after firing. However, such a ceramic network does not exhibit the desired properties of individual ceramic pins. In particular, such a ceramic network is hardly suitable for use as an additive in building materials.Furthermore, the active surface, which can, for example, be catalytically active or serve as a carrier for catalytically active substances, is significantly limited.

[0009] The invention is based on the object of providing a method for treating a ceramic batch by means of which individual strands of the ceramic batch can be produced.

[0010] In particular, the invention is based on the object of providing such a method by which individual strands of the ceramic batch can be mass-produced.

[0011] In particular, the invention is based on the object of providing such a method by which such individual strands of the ceramic batch can be produced and made available in such a way that individual ceramic pins from these strands are combustible, in particular are suitable for mass production.

[0012] To achieve this object, the invention provides a method for treating a ceramic batch, comprising the following steps: providing a ceramic batch;

[0013] Providing a tool for forming the ceramic batch: forming the ceramic batch by the tool into a bundle of individual strands; and

[0014] Drying at least a portion of the bundle; wherein the step of drying the at least one portion of the bundle is performed such that the at least one portion of the bundle is dried before the at least one portion, after the forming step, is in contact with a solid body other than at least one of the following solid bodies: the tool, at least one other portion of the bundle.

[0015] The invention is based in particular on the finding that strands formed from a ceramic batch stick together, in particular when these strands come into contact with a solid body after they have been formed. Through such contact with a solid body, the individual strands can be pressed against one another and thus stick together. Such a solid body can in particular be a body for receiving the shaped individual strands, for example a bowl, a tray or a belt for receiving the shaped strands. A fundamental idea of ​​the invention resulting from this finding is to treat the shaped strands in such a way that they do not stick together, or only stick to a reduced extent, when they come into contact with a solid body.After extensive testing, it was surprisingly found according to the invention that such sticking of the strands upon contact with a solid body can be prevented by drying the shaped strands after they have been shaped but before they come into contact with a solid body other than the mold. According to the invention, it was found that by drying the strands in this way, their surface can be modified in such a way that the strands no longer stick to one another after such at least superficial drying, or only stick to a significantly reduced extent. After the strands have been dried, they can therefore come into contact with a solid body, for example the surface of a receiving device for receiving the strands, since in this case the strands dried at least superficially according to the invention no longer stick to one another or only stick to a significantly reduced extent.The drying process step according to the invention is also based on these findings, in particular, according to which at least one section of the bundle is dried in such a way that this at least one section of the bundle is dried before this at least one section, after the forming step, comes into contact with a solid body other than at least one of the following solid bodies: with the tool, with at least one other section of the bundle. This dried section of the bundle was then dried according to the invention before it came into contact with a solid body that could have led to the strands of the section of this bundle sticking together; rather, during its drying, the section was at most still in contact with the tool by which it had previously been formed, or with another section of the bundle, which, however, does not cause the strands of this section to press against one another.The at least one other section of the bundle with which the section could possibly have been in contact before it was dried may in particular be one or both of the sections of the bundle adjacent to the section to be dried, with which the section to be dried is necessarily in contact.

[0016] According to the usual nomenclature, a “strand” is understood according to the invention to mean a long and thin extending object of a flexible material, in the present case in particular a flexible material in the form of a plastic ceramic batch.

[0017] Furthermore, according to the invention, the term “bundle” is understood to mean, in accordance with the usual nomenclature, a loosely combined quantity, in the present case a loosely combined quantity of the strands formed from the ceramic batch.

[0018] According to the invention, a “section” is understood to mean the entirety of the strands of the bundle between two spaced-apart cross-sections through the bundle, each of which runs normal to the longitudinal axis of the bundle.

[0019] The process according to the invention is preferably carried out continuously. Preferably, successive sections of the bundle are continuously dried according to the invention. The process according to the invention thus makes it possible to produce individual strands from a ceramic batch.

[0020] In particular, such individual strands can be mass-produced using the method according to the invention by continuously drying successive sections of the bundle according to the invention. This allows the production of an "endless" bundle of dried, individual strands, which can, in particular, be subjected to further treatment.

[0021] The individual strands produced by the process according to the invention can then be used to produce ceramic pins.

[0022] The inventive step of drying at least one section of the bundle of individual strands can be carried out in such a way that the individual strands are completely or only partially dried, in particular only superficially. According to the invention, it has been found that, to prevent the individual strands from sticking together, it is sufficient if they are only dried superficially. For process-economic reasons, it is therefore preferably provided that the step of drying at least one section of the bundle is carried out in such a way that the strands are dried superficially.

[0023] According to the invention, it has been found that even a very short drying time can be sufficient to dry at least one section of the bundle, in particular to dry it superficially, in such a way that subsequent sticking can be avoided. According to a preferred embodiment, the step of drying at least one section of the bundle can be carried out for a maximum of 10 seconds, in particular for a duration in the range of 1 to 10 seconds and particularly preferably for a duration in the range of 5 to 10 seconds. According to the invention, it has been found that such a drying time is advantageous for process-economic reasons, since the bundle of strands can be dried only for a very short time and then subjected to further treatment.Furthermore, it has been found according to the invention that such a short drying time can prevent deformation or uncontrolled tearing of the individual strands. Within the bundle, the individual strands can at least partially touch each other. However, the strands within the bundle preferably do not touch each other. This has the particular advantage that the strands within the section of the bundle that is dried according to the invention can be dried comprehensively.

[0024] The "other solid body" with which the at least one section of the bundle does not come into contact according to the invention until this region has been dried according to the invention can, in principle, be any solid body that does not represent the forming tool and / or at least one other section of the bundle. For example, this other solid body can be a device with which the region of the bundle of strands comes into contact after its forming and drying, for example, a device for receiving the formed strands dried according to the invention.

[0025] In order to dry the at least one section of the bundle of individual strands according to the invention, any means which can be used for drying a ceramic batch can be used according to the invention, in particular also the means known from the prior art for drying ceramic batches. As explained above, the method and in particular also the drying are preferably carried out continuously, with preferably successive sections of the bundle being dried according to the invention. Preferably, the at least one, particularly preferably the successive sections, are actively dried. In particular, the drying takes place by subjecting the at least one or the successive sections to a heating or drying agent, in particular by actively subjecting them to a heating or drying agent.According to one embodiment, the at least one section of the bundle is dried by subjecting it to at least one of the following means: hot air, thermal radiation, or microwave radiation. According to the invention, it has been found that the bundle of strands can be dried particularly advantageously using one or more of these means to prevent them from sticking together. Thermal radiation can be provided, in particular, in the form of infrared radiation. Preferably, the bundle of individual strands is guided past such a means so that the agent can act on the bundle and dry it. Particularly preferably, the at least one section of the bundle is dried using hot air. Particularly preferably, the at least one section of the bundle is dried by subjecting it to hot air from a hot air blower.

[0026] According to the invention, it was discovered that this allows the strands to be dried particularly quickly and gently on their surfaces, preventing them from sticking together. In particular, exposure to hot air, particularly by a hot air blower, can be carried out for the aforementioned duration.

[0027] According to a preferred embodiment, it can be provided that the drying of at least one section of the bundle is carried out by hot air at a temperature in the range between 100°C and 700°C, in particular in the range between 350°C and 650°C. In particular, when drying by means of hot air in such a temperature range, it is possible to dry the individual strands superficially and gently in such a way that they subsequently no longer stick together.

[0028] According to a preferred embodiment, the step of drying at least one section of the bundle takes place immediately after the bundle has been formed. The step of drying at least one section of the bundle therefore takes place both temporally and in terms of the process technology immediately after the bundle has been formed. On the one hand, this has the process technology advantage that the strands of the bundle can be dried immediately after they have been formed and can thus be further treated immediately afterwards, which is particularly advantageous in terms of process economy. On the other hand, this also has the particular advantage that sticking of the strands can be particularly effectively suppressed, since the strands are not given time to stick together after they have been formed.

[0029] According to a preferred embodiment, the ceramic batch can be continuously formed into a bundle of strands by the process according to the invention. Such continuous forming is advantageous in terms of process economy and allows for particularly mass-produced individual strands. According to a particularly preferred embodiment, the ceramic batch can be formed by extrusion. This allows for a particularly simple continuous forming of a virtually "endless" bundle of individual strands.Such a continuously formed, quasi "endless" bundle can extend continuously from the tool on which it was formed, across a further region where it is dried according to the invention, to an adjoining region where the bundle can already be in contact with another solid body, for example in the form of a receiving device for the formed and dried bundle. In particular, if the forming is carried out by extrusion, according to a particularly preferred embodiment, the tool for forming the ceramic batch can be the forming tool or die of an extruder.

[0030] According to a preferred embodiment, the tool for molding the ceramic batch can comprise a plate with openings, wherein the molding step is carried out by pressing the ceramic batch through the openings. In particular, if the tool for molding the batch is the molding tool of an extruder, it can preferably be provided that the molding tool of the extruder comprises the aforementioned plate.

[0031] In principle, the openings in the plate can have any desired cross-sectional area. However, it can preferably be provided that the openings in such a plate have a circular cross-sectional area. According to the invention, it has been found that using such a tool in the form of a plate with openings, in particular where these openings have a circular cross-sectional area, a bundle of individual strands can be formed from the ceramic batch particularly easily and in a mass-producible manner, wherein the strands of the bundle formed in this way can be dried particularly effectively according to the invention in such a way that they do not stick together. In particular, where strands formed in this way are dried using hot air, the hot air can flow particularly effectively around strands formed by means of such circular openings in such a way that their surfaces are dried in such a way that they do not stick together.

[0032] According to a preferred embodiment, the opening of the plate with a circular cross-sectional area can have a diameter in the range of 0.5 to 2 mm, particularly preferably a diameter in the range of 0.8 to 1.4 mm. According to the invention, it has been found that this allows strands to be formed with a diameter that, on the one hand, is sufficiently stable so that they do not tear during treatment, and, on the other hand, can be very effectively dried, at least superficially, so that they do not stick together.

[0033] According to a preferred embodiment, the circular openings of the plate with a circular cross-sectional area can be arranged in a grid pattern on the plate. According to a preferred embodiment, the openings can be spaced at a minimum distance in the range of 2 to 6 mm, more preferably in a range of 3 to 5 mm. According to the invention, it has been found that with such a spacing of the openings, the strands of the bundle formed by the openings can be dried particularly effectively.

[0034] According to a preferred embodiment, it can be provided that the openings of the plate have a maximum diameter of 3 mm.

[0035] According to a preferred embodiment, the plate, in particular the exit side of the plate, where the strands formed by the plate exit the plate, can be arranged vertically. This also makes it particularly effective to prevent the strands from sticking together immediately after they exit the plate.

[0036] According to a preferred embodiment, the strands can have a circular cross-sectional area. This cross-sectional area is the cross-sectional area of ​​the strands perpendicular to the longitudinal axis or longitudinal extension of the strands. According to the invention, it has been found that such strands with a circular cross-sectional area, on the one hand, have high green strength, making them stable and not prone to tearing, and, on the other hand, can be dried particularly effectively on the surface to prevent sticking.

[0037] According to a particularly preferred embodiment, the bundle can comprise strands having a diameter of less than 3 mm. This diameter is in turn the diameter transverse to the longitudinal axis or longitudinal extension of the strands. Particularly preferably, the bundle comprises strands having a diameter in the range from 0.5 to 2 mm and particularly preferably having a diameter in the range from 0.8 to 1.4 mm. As explained above, it has been found according to the invention that strands having such a diameter, on the one hand, have sufficient green strength and, on the other hand, can be dried particularly effectively.

[0038] The ceramic batch provided for the process according to the invention can, in principle, be any ceramic batch. A plastically deformable batch is preferably provided.

[0039] According to a particularly preferred embodiment, it can be provided that a non-basic batch is provided. As is known, a non-basic ceramic batch is one whose main oxides are not MgO and CaO and which therefore comprises these oxides, in particular, only in small proportions. According to a preferred embodiment, it can be provided that the ceramic batch provided for the process according to the invention has a chemical composition that comprises a total mass of the oxides MgO and CaO of less than 25 mass%, particularly preferably less than 15 mass%.

[0040] Preferably, the ceramic batch can be a non-basic ceramic batch whose main oxides are non-basic oxides, in particular one or more of the following oxides: Al2O3, SiO2, TiO2, V2O5, and WO3. According to a preferred embodiment, the ceramic batch can have a chemical composition comprising at least 75% by mass, more preferably at least 85% by mass, of one or more of the following oxides: Al2O3, SiO2, TiO2, V2O5, and WO3. According to a further development of this inventive concept, the oxides MgO and CaO can be present simultaneously in the above-described mass proportions.

[0041] The above-mentioned data in mass % are based on the total mass of the ceramic batch provided.

[0042] The chemical composition is determined according to DIN 51418-1:2008-08 and DIN 51418-2:2015-03.

[0043] The ceramic batch provided for the process according to the invention can preferably be a fine ceramic batch, i.e., a batch with a fine grain size. In particular, at least 90 mass% of the particles of the ceramic batch provided preferably have a grain size below 250 pm, determined by sieve analysis according to DIN 66165-1:2022-06 and DIN 66165-2:2016-08, provided only grain sizes above 20 pm are present; if grain sizes below this are also present, all grain sizes below 100 pm are determined by laser diffraction according to ISO 13320:2020-01.

[0044] According to the invention, it was found that such a fine ceramic batch can be treated particularly advantageously by the method according to the invention.

[0045] The ceramic batch treated by the method according to the invention can subsequently be further treated. In particular, the step of drying the bundle can be followed by a further treatment. In particular, after the bundle has been dried in one area according to the invention, it can then be picked up at this area on a receiving device. Such a receiving device can be, for example, a tray, a bowl, or a belt that receives the dried portion of the bundle for subsequent further treatment.

[0046] According to one embodiment, it can therefore be provided that the step of drying the bundle at a region of the bundle is followed by receiving this region on a receiving device.

[0047] The area of ​​the bundle, for example picked up on a receiving device, can then be further dried until it has a desired residual moisture content in order to subsequently subject it to a firing, in particular a sintering firing.

[0048] According to one embodiment, it can be provided that the method according to the invention comprises the step of comminuting the bundle after the drying step. This comminution step can preferably be carried out after the bundle has been received on a receiving device and optionally further dried. By means of this comminution step, the dried strands can be comminuted, in particular, to a length desired for firing. The bundle is preferably comminuted in a particularly gentle manner, for example on a vibrating table, in a drum, by a roll crusher or by other gentle crushing units. According to one embodiment, it can be provided that the method according to the invention comprises the step of firing the strands after the drying step. This firing step can be carried out after the step of comminution of the strands.This firing is preferably carried out as a sintering firing, i.e., it is carried out in such a way that the ceramic batch from which the strands are made sinters into a ceramic in the form of ceramic pins. The firing temperature depends on the composition of the particular ceramic batch used. Firing is preferably carried out at a temperature of at least 450°C and particularly preferably at a temperature in the range of 550°C to 1,400°C. A holding time of 0.5 to 2 hours at maximum temperature has proven advantageous. The strands can preferably be held in a ceramic shell during firing, preferably a ceramic shell made of a non-oxide ceramic material, for example silicon carbide.

[0049] After firing, the strands are transformed into ceramic pins. These ceramic pins can be subjected to subsequent treatment or use.

[0050] According to one embodiment, it can be provided that the ceramic pins obtained are crushed, in particular to a desired length for their final use.

[0051] The invention also relates to ceramic pins comprising the following features: the pins are made of a non-basic, sintered ceramic; the pins have a thickness of less than 3 mm; the pins have a length:thickness ratio of more than 2.5.

[0052] The ceramic pins are preferably produced by the method according to the invention as set forth herein.

[0053] The non-basic ceramic of the pins preferably has the composition disclosed herein of the non-basic ceramic batch provided for the method according to the invention. The pins preferably have a thickness of less than 3 mm. The pins preferably have a circular cross-sectional area, with a cross-sectional area along the longitudinal axis or longitudinal extension of the pins. The pins with a circular cross-sectional area preferably have a diameter in the range of 0.5 to 2 mm, particularly preferably in the range of 0.7 to 1.2 mm.

[0054] The ceramic pins according to the invention have a length:thickness ratio of more than 2.5, preferably such a ratio in the range of 2.5 to 40 and particularly preferably in the range of 5 to 20.

[0055] According to the invention, it has been found that ceramic pins according to the invention with such dimensions are, on the one hand, particularly easy to handle and, on the other hand, have a particularly high surface-to-volume ratio. As a result, the ceramic pins according to the invention can be used particularly effectively for catalytic processes, for example, as carriers for catalytically active substances.

[0056] The invention also relates to the use of the ceramic pins according to the invention as an additive in building materials, in particular in ceramic building materials, particularly preferably in refractory ceramic building materials. In particular, the ceramic pins can be used in such building materials to influence the properties of the refractory ceramic building materials, in particular their physical properties, such as their thermal shock resistance, or their mechanical properties, in particular their elastic modulus.

[0057] The invention also relates to the use of the ceramic pins according to the invention for catalytic processes, in particular as a carrier material for catalytically active substances for catalytic processes.

[0058] The invention also relates to an apparatus for treating a ceramic batch, comprising the following features: a tool suitable for forming a ceramic batch into a bundle of individual strands; and a drying device suitable for drying at least a portion of the bundle such that the at least one portion of the bundle is dryable before the at least one portion, after forming with the tool, is in contact with a solid body other than at least one of the following solid bodies: with the tool, with at least one other portion of the bundle.

[0059] The device according to the invention can be used, in particular, to carry out the method according to the invention. The components of the device can therefore be particularly suitable for the method according to the invention, as disclosed herein.

[0060] Further features of the invention emerge from the claims, the figures of the embodiment and the associated description of the figures.

[0061] All features of the invention can be combined with each other in any way, individually or in combination.

[0062] Embodiments of the invention are explained in more detail below.

[0063] To explain the embodiment, it is shown in

[0064] Figure 1 shows a schematic embodiment of a device according to the invention which serves to carry out the first and second embodiments of the method according to the invention; and

[0065] Figure 2 shows the tool for forming the ceramic offset of the device according to Figure 1.

[0066] First embodiment of a method according to the invention and a device according to the invention

[0067] For the first embodiment of the process according to the invention, a non-basic, plastically deformable batch based on the oxidic raw materials aluminum oxide and sepiolite was initially provided. These oxidic raw materials were mixed together with water and a conventional organic binder in the form of polyethylene oxide in a mixing and kneading unit until a plastically deformable batch was obtained. The batch had the following chemical composition, determined according to DIN 51418-1:2008-08 and DIN 51418-2:2015-03, each based on the total mass of the batch:

[0068] AI2O3: 90 mass%

[0069] SiO2: 7.95 mass%

[0070] Fe2O3: 0.15 mass%

[0071] TiO2: 0.95 mass%

[0072] CaO: 0.25 mass%

[0073] MgO: 0.25 mass%

[0074] Na2O + K2O: 0.45 mass%.

[0075] The batch was a fine ceramic batch, with 100 mass% of the batch particles having a grain size below 100 pm and 90 mass% of the batch particles having a grain size below 35 pm, each based on the total mass of the batch and determined by laser diffraction according to ISO 13320:2020-01.

[0076] This ceramic offset was subsequently treated by an embodiment of a device according to the invention as shown in Figure 1.

[0077] The device according to Figure 1 is designated in its entirety by reference numeral 1. The device 1 comprises a screw extruder 100, a drying device 200, and a receiving device 300.

[0078] The screw extruder 100 comprises a screw cylinder 101 in which an electric motor-driven extruder screw (not shown) is arranged. At one end of the screw cylinder 101, an input hopper 102 is arranged, through which a ceramic batch to be processed by the screw extruder 100 can be fed into the screw cylinder 101, indicated by the arrow P1. A ceramic batch fed into the screw extruder 100 through the input hopper 102 is conveyed in the screw cylinder 101 by the extruder screw to the end of the screw cylinder 101 opposite the input hopper 102, where the batch is pressed through a forming tool 103 by the rotational pressure of the extruder screw. The outlet side 104 of the forming tool 103 extends horizontally downward. Adjacent to the screw extruder 100, the drying device 200 in the form of a hot air blower is arranged.The drying device 200 is arranged in such a way that a ceramic batch pressed by the molding tool 103 can be subjected to hot air 201 immediately after it leaves the outlet side 104.

[0079] Finally, at a distance below the screw extruder 100 and the

[0080] The receiving device 300 in the form of a belt conveyor is arranged in the drying device 200. The receiving device 300 comprises a drive roller 301, a deflection roller 302, and a conveyor belt 303 running around the drive roller 301 and the deflection roller 302 and drivable by the drive roller 301. The receiving device 300 is arranged below the screw extruder 100 in such a way that a ceramic batch leaving the screw extruder 100 through the outlet side 104 comes to rest on the conveyor belt 303 due to gravity and can thus be conveyed by it, indicated by the arrow P2.

[0081] The molding tool 103 is shown in more detail in Figure 2. For clarity, the molding tool is shown "upside down" in the figure; in the use position, the molding tool 103, as shown in Figure 1, is arranged on the screw extruder 100 with its outlet side 104 facing downward.

[0082] The molding tool 103 has a substantially tabular structure and comprises a plate 105 with openings 106 arranged in a grid. The openings 106 each have a circular cross-sectional area with a diameter of 1.1 mm. The thickness of the plate 105 is 10 mm, which also corresponds to the length of the openings 106. The openings 106 are arranged such that they are each located at the intersection points of a rectangular grid with 10 x 10 intersection points, so that the plate 105 has a total of one hundred openings 106. The screw extruder 100 is configured such that a ceramic batch can be pressed through the openings 106 of the plate 105 at extrusion pressures in the range of 25 to 60 bar, thereby forming a bundle 400 of individual strands 401 from the ceramic batch.The exit side 104 of the plate 105 is arranged, as explained above, facing horizontally downwards, so that the individual strands 401 of the bundle 400, after exiting the openings 106, leave them hanging vertically downwards. Overall, a single strand can be formed through each of the openings 106, so that a bundle of 100 individual strands 401 can be formed from the ceramic batch through the plate 105.

[0083] The above-mentioned ceramic mass of the first embodiment was treated by the device 1 as follows.

[0084] First, the ceramic mass was fed into the screw extruder 100 via the feed hopper 102 as indicated by arrow P1, and there it was conveyed through the extruder screw in the screw cylinder 101 to the forming tool 103. At the forming tool 103, the ceramic batch was pressed through the openings 106 with an extrusion pressure within the range specified above, so that a bundle 400 of individual strands 401 was formed from the ceramic batch, which exited the openings 106 hanging vertically downwards. The formed strands 401 each had a circular cross-sectional area with a diameter slightly less than the diameter of the openings 3 and amounted to approximately 1.0 mm.

[0085] Immediately after leaving the forming tool 103, the bundle 400 was exposed to the hot air 201 of the drying device 200 and thereby dried. In this case, a section 402 of the bundle 400 was dried by the hot air 201 before this section 402, after its formation, came into contact with a solid body other than the forming tool 103 and the section 403 of the bundle 400 adjacent to the section 402. Hot air 201 with a temperature of approximately 500°C and a duration of approximately 7 seconds was blown onto the section 402 by the drying device 200, so that the strands 401 of this section 402 of the bundle 400 were superficially dried by the hot air 201.

[0086] The correspondingly surface-dried strands 401 were then placed on the conveyor belt 303 of the receiving device 300 according to arrow P2 and transported further by the conveyor belt 303 in order to subject the dried strands 401 to further treatment.

[0087] The treatment of the ceramic batch by the device 100 was carried out as a continuous process, whereby an “endless” bundle 400 of strands 401 was continuously formed and successive sections 402 were continuously dried by the drying device 200 by continuously passing the bundle 400 past the hot air 201.

[0088] The further treatment of the dried strands 402 deposited on the conveyor belt 303 is not shown in Figure 1 and was as follows:

[0089] The dried strands 401 were subjected to a further drying step, which completely dried them. This further drying took place at a temperature of 25°C for a duration of 48 hours.

[0090] The strands 401 finally dried were then gently broken in a grinding drum so that the strands 401 predominantly had a length of less than 20 mm.

[0091] The broken strands 401 were finally subjected to a ceramic firing. The ceramic firing was carried out in an electrically heated furnace, maintaining a maximum temperature of 1,400°C for approximately 2 hours.

[0092] During the ceramic firing, the strands 401 rested in a ceramic shell made of silicon carbide.

[0093] After firing, 401 ceramic pins were obtained from the strands. These pins consisted of a non-basic, sintered ceramic with the oxide composition described above. The pins had a diameter of approximately 0.88 mm. Furthermore, the ceramic pins had lengths ranging from approximately 5 to 15 mm, thus having a length-to-thickness ratio in the range of approximately 5.7 to 17.0.

[0094] The ceramic pins were then used as an additive in a refractory ceramic building material to increase its thermal shock resistance. Second embodiment of a method according to the invention

[0095] The second embodiment corresponded to the first embodiment described above with the differences as described below.

[0096] For the process, a non-basic, ceramic batch was provided which contained the following components in the following mass proportions, based on the total mass of the batch:

[0097] TiO2-based raw material: 81.5 mass%

[0098] Bentonite: 6% by mass

[0099] Ammonium metavanadate: 2.5% by mass

[0100] Glass fiber: 10% by mass.

[0101] The TiO2-based raw material included not only TiO2 but also chemical components of WO3.

[0102] This composition was mixed with water and an organic binder in the form of

[0103] Polyethylene oxide was mixed and kneaded in an aggregate. The batch subsequently had the following chemical composition, based on the total mass of the batch, determined according to DIN 51418-1:2008-08 and DIN 51418-2:2015-03:

[0104] SiO2: 8.8 mass%

[0105] AI2O3: 2.9 mass%

[0106] Fe2O3: 0.25 mass%

[0107] TiO2: 74.70 mass%

[0108] CaO + MgO: 2.7 mass%

[0109] Na2O + K2O: 0.2 mass%

[0110] V2O5: 2.0 mass%

[0111] WO3: 8.45 mass%.

[0112] The TiO2 raw material had a grain size of 100 mass% of the particles below 100 pm and 85 mass% of the particles below 2.5 pm, each based on the total mass of the TiO2 raw material and determined by laser diffraction according to ISO 13320:2020-01. The bentonite had a grain size of 100 mass% of the particles below 100 pm, based on the total mass of the bentonite and determined by laser diffraction according to ISO 13320:2020-01.

[0113] The glass fibers had a diameter of 5 pm and a length of 4.5 mm.

[0114] The batch was formed according to the first embodiment, dried, and then deposited on a receiving device. The strands were then broken by shaking on a vibrating plate.

[0115] The ceramic firing took place at a maximum temperature of 580°C with a holding time of 4 hours. The ceramic bond was achieved via the glass fibers, whose glass transition temperature was approximately 525°C.

[0116] The resulting ceramic pins had a diameter of 0.93 mm and a length ranging from approximately 10 to 20 mm. Thus, the pins had a length-to-thickness ratio in the range of approximately 10.8 to 21.5.

[0117] The ceramic pins were subsequently used as active catalytic material in a catalytic process.

Claims

Patent claims 1. A method for treating a ceramic batch, comprising the following steps: A. provision of a ceramic backfill; B. Provision of a tool for forming the ceramic offset: C. Forming the ceramic batch by the tool into a bundle of individual strands; and D. drying at least a portion of the bundle; wherein E. the step of drying the at least one portion of the bundle is carried out such that the at least one portion of the bundle is dried before the at least one portion is in contact with a solid body other than at least one of the following solid bodies: the tool, at least one other portion of the bundle after the forming step.

2. The method according to claim 1, wherein the drying is carried out by exposure to at least one of the following means: hot air, heat radiation or microwave radiation.

3. A method according to at least one of the preceding claims, wherein the drying takes place immediately after the forming of the bundle.

4. A method according to at least one of the preceding claims, wherein the tool is a plate with openings and wherein the forming step is carried out by pressing the ceramic batch through the openings.

5. The method of claim 4, wherein the openings have a circular cross-sectional area.

6. The method according to at least one of claims 4 to 5, wherein the openings have a maximum diameter of 3 mm.

7. The method according to at least one of the preceding claims, wherein the tool is the molding tool of an extruder.

8. The method according to at least one of the preceding claims, wherein the ceramic batch is a non-basic ceramic batch.

9. A method according to at least one of the preceding claims, wherein the bundle comprises strands having a diameter of less than 3 mm.

10. The method according to at least one of the preceding claims, wherein the bundle comprises strands having a circular cross-sectional area.

11. A method according to at least one of the preceding claims, wherein the dried portion of the bundle is deposited on a solid body after drying.

12. A method according to at least one of the preceding claims, comprising the step of comminuting the strands after the drying step.

13. A method according to at least one of the preceding claims, comprising the step of firing the strands after the drying step.

14. Ceramic pins comprising the following features: 14.1 the pins are made of a non-basic, sintered ceramic; 14.2 the pins have a thickness of less than 3 mm; 14.3 the pins have a length:thickness ratio of more than 2.

5.

15. Apparatus for treating a ceramic batch, comprising the following features: 15.1 a tool (103) suitable for forming a ceramic batch into a bundle (400) of individual strands (401); and 15.2 a drying device (200) suitable for drying at least one portion (402) of the bundle (400) such that the at least one portion (402) of the bundle (400) is dryable before the at least one portion (402) is in contact with a solid body other than at least one of the following solid bodies after forming with the tool (103): with the tool (103), with at least one other portion (403) of the bundle (400).