Portion capsule for beverages

Abstract

The present invention relates to a portion capsule for beverages, so-called coffee capsules, with a cup-shaped casing having excellent barrier properties against gas ingress, water or humidity, and oxygen, comprising: i.) at least one layer of paper, ii.) at least one layer of a metallisation, iii.) at least one layer containing polylactic acid, and iv.) at least one sealing layer containing at least one thermoplastic material which is produced from glucose, lignin or cellulose.

Description

[0001] Portion capsule for drinks

[0002] Description

[0003] The present invention relates to a portion capsule for beverages, or beverage capsules, in particular coffee capsules, with a cup-shaped shell. Portion capsules for beverages, especially coffee, are known from the prior art. The cup-shaped shell is preferably frustoconical or cylindrical and has a base and a rim. It is manufactured, for example, from a deep-drawn plastic film or by injection molding. On a side opposite the base, a filling opening and a sealing rim surrounding the filling opening are provided, onto which a lid film or lid foil is applied or sealed after the portion capsule has been filled.

[0004] Capsules for brewing single portions of beverages like coffee or tea are widely used. The capsules consist of a cup-shaped body and a lid or cap film that tightly seals the body. The capsules are designed to be inserted into a compatible brewing machine with the lid film attached. To brew, the capsule with the lid film is pierced. Hot water, preferably under pressure, is then forced into the capsule by the machine. The hot beverage, e.g., brewed coffee, can then flow out through the pierced holes in the lid film.

[0005] There is a high demand for beverage capsules that have a high sealing capacity or excellent barrier properties and can also be disposed of sustainably.

[0006] The object of the present invention is to provide a portion capsule for beverages made from a biodegradable, compostable or home-compostable composite material that prevents gas ingress even better.

[0007] According to the invention, a portion capsule for beverages is provided, comprising a compostable or home compostable composite material which is made up of several layers and thus has complete sealing capability.

[0008] Therefore, the invention relates to a portion capsule for beverages comprising a composite material, from the outside in several layers, i.) at least one layer of paper, ii.) at least one layer of metallization, iii.) at least one layer containing polylactic acid, iv.) at least one sealing layer containing at least one thermoplastic

[0009] Plastic made from glucose, lignin, or cellulose.

[0010] In a preferred embodiment, the layers can be provided with a laminating adhesive at least between i.) and ii.). Preferably, the laminating adhesive has a weight of 2–6 g / m².

[0011] Furthermore, it is optionally provided that the composite material has at least one further layer of polyvinyl alcohol (ia.) to reinforce the barrier properties between layer i.) and ii.), preferably with a weight of 2 - 6 g / m², preferably one to three layers (ia - ic.) of polyvinyl alcohol, each with a weight of 2 - 6 g / m².

[0012] In a preferred embodiment, the layer i.) can have a basis weight of 75 g / m² to 200 g / m², in particular 130–170 g / m², and in particular 150 g / m². Paper within the meaning of this invention is a thin material made essentially from plant fibers.

[0013] In a further preferred embodiment, layer iii.) can contain at least one further aliphatic aromatic copolyester, in particular polybutylene adipate terephthalate (PBAT) (ecoflex® BASF), which is compostable according to EN 13432.

[0014] Particularly preferred are those from BASF with the trade name ecovio ® based on polylactic acid, which are compostable according to EN 13432.

[0015] Preferably, layer iii.) has a maximum modulus of elasticity of 100 to 300 MPa according to ISO 527. Furthermore, it is preferred that the maximum yield strength or tensile stress is 45 MPa, particularly 35 to 40 MPa according to ISO 527.

[0016] Furthermore, an MVR (190 degrees Celsius / 5 kg) of 8-12 cm is preferred. 3 / 10 min according to ISO 1133.

[0017] In a further preferred embodiment, layer iii) can consist of several such

[0018] consisting of layers, in particular two or three layers, each layer containing polylactic acid, or additionally containing at least one further aliphatic aromatic copolyester.

[0019] In layer iii.) additionally, besides polylactic acid (PLA), other biopolymers may be contained, such as modified polylactic acid, polylactic acid copolymers, polyhydroxyalkanoates (PHA), polycaprolactone (PCL).

[0020] Examples of PLA copolymers are copolymers with polyesters, e.g. aliphatic polyesters (CPLA).

[0021] Preferred are biodegradable polylactide-based plastics, such as modified polylactide, polylactide copolymers, alpha hydroxy acids such as poly(lactide-co-glycolide) (PLGA), polyanhydrides, aliphatic polyesters, copolyesters with aliphatic and aromatic blocks, polyesteramide, polyester urethane, a polyethylene oxide polymer, a polyglycol and copolymers thereof.

[0022] The layer iii.) can have a thickness of 10 - 50 pm, in particular 10 - 30 pm.

[0023] In a further preferred embodiment, according to layer ii.) the metal can be selected from boron, aluminium or silicon, in particular boron oxide, aluminium oxide or silicon oxide.

[0024] In a further preferred embodiment, layer ii.) can have a thickness of 20–50 nm, in particular 30–40 nm. Metallization is carried out by vapor deposition onto layer iii.).

[0025] In a further preferred embodiment, layer iii) can additionally contain a coating, in particular made of acrylate.

[0026] In a further preferred embodiment, the acrylate coating can have an additional thickness of 20–40 nm on top of layer iii). The coating provides advantageous protection and fixation of the metallization in layer ii).

[0027] At least one acrylate may be selected from the group consisting of polyurethane, polyester, epoxy, and polyether acrylates or methaacrylates, in particular oligomers, and / or monomers selected from the group consisting of mono-, di-, tri-, tetra-, and hexafunctional acrylates or methaacrylates. Furthermore, it is preferred that the metallization layer (ii.) on layer (iii.) has a weight of 0.1 to 0.15 g / m² and / or that the acrylate has a weight of 0.04 to 0.06 g / m².

[0028] In a further preferred embodiment, the sealing layer iv.) can contain at least one thermoplastic polymer made from glucose, lignin, or cellulose, preferably compostable according to EN 13432. Furthermore, the sealing layer iv.) can contain biopolymers, such as, but not limited to, polyhydroxyalkanoates (PHA), polycaprolactone (PCL), polyester (PET), starch, polylactic acid (PLA), polyolefins (PE), and polyamides (PA).

[0029] Preferably, the sealing layer iv.) has a maximum modulus of elasticity of 3000 or 4000 to 4500 MPa according to ISO 527 (measurement of the modulus of elasticity at a test speed of 1 mm / min). Furthermore, it is preferred that the maximum yield strength or tensile stress is 40 to 60 MPa, in particular 55 or 54 MPa according to ISO 527.

[0030] Furthermore, an MVR (190 degrees Celsius / 2.16 kg) of 3-5 cm is preferred. 3 / 10 min according to ISO 1133.

[0031] In one embodiment, a sealing layer iv.) is preferably made of a polymer mixture, namely comprising a.) 70-95 wt. % of at least one thermoplastic polymer made of glucose,

[0032] a.) is made from lignin or cellulose, having a modulus of elasticity of 4000 - 4400 MPa and a yield strength or tensile strength of 50 - 60 MPa according to ISO 527, and b.) 5 - 30 wt. % of at least one thermoplastic polymer made from glucose,

[0033] is made from lignin or cellulose, having a modulus of elasticity of 200 - 400 MPa and a yield strength or tensile stress of 10 - 20 MPa according to ISO 527

[0034] Furthermore, a polymer mixture of a.) / b.) of 85 wt. % : 15 wt. % is preferred.

[0035] Furthermore, it is preferred that a.) an MVR (190 degrees Celsius / 2.16 kg) of 3 cm 3 / 10 min according to ISO 1133 and b.) has an MVR (190 degrees Celsius / 2.16 kg) of 6 cm 3 / 10 min according to ISO 1133. In addition, a.) and b.) may contain biopolymers such as polyhydroxyalkanoates (PHA), polycaprolactone (PCL), polyester (PET), starch, polylactic acid (PLA), polyolefins (PE), polyamides (PA).

[0036] Such polymer blends are available from the company Tecnaro, Ilsfeld, Germany. For example, Abroblend®.

[0037] In particular, the sealing layer allows for advantageous mechanical strength of the beverage capsule with optimal internal pressure.

[0038] In a further preferred embodiment, the sealing layer iv.) can consist of several such layers, in particular two or three layers, each layer containing at least one further thermoplastic polymer made from glucose, lignin or cellulose that is compostable according to EN 13432.

[0039] The sealing layer iv.) can have a thickness of 5 - 15 pm, in particular 10 pm.

[0040] Therefore, the invention also relates to a beverage capsule or a portion capsule for beverages, wherein the beverage capsule contains at least one composite material according to the invention.

[0041] Overall, the present invention realizes a compostable or home-compostable beverage capsule in accordance with European Standard (EN) 13432.

[0042] Furthermore, it is preferred that the beverage capsule has a lid film or lid foil, as described, for example, in EP 24 186 396.8 of the applicant.

[0043] The layer of paper according to i.) forms the outer layer of the beverage capsule according to the invention.

[0044] To protect the contents of the container, the layers according to the invention, in their selected arrangement, exhibit optimal barrier properties against oxygen and water vapor and therefore achieve excellent sealing properties. The barrier layers according to the invention have a suitable barrier effect against oxygen and water vapor.

[0045] To manufacture the beverage capsule, each layer is laminated using a preferably biodegradable laminating adhesive. A food-grade, biodegradable laminating adhesive is preferably used. Examples include aqueous solutions of polyvinyl alcohol (PVOH) based on starch, protein adhesives, or polyurethane (Morchem, Munich, Germany).

[0046] Another suitable biodegradable laminating adhesive is the water-based adhesive Epotal® Eco from BASF.

[0047] Capsules for beverages made from biodegradable plastic can be manufactured using the methods commonly used in plastics engineering.

[0048] It should be noted that features described in connection with one exemplary embodiment or exemplary object can be combined with any other exemplary embodiment or exemplary object.

[0049] When a term is referred to with an indefinite or definite article, such as "ein" in the singular, this also includes the term in the plural and vice versa, unless the context clearly indicates otherwise.

[0050] The term "encompass", as used here, not only includes the meaning of "contain", but can also mean "consisting of" and "essentially consisting of".

[0051] ISO 527 specifies the mechanical behavior of plastics under tensile stress. This standard defines the test methods for determining the tensile properties of plastics.

[0052] ISO 1133 describes the method for determining the MVR (Melt Volume Rate) and the MFR (Melt Flow Rate), which indicate the mass of plastic extruded through the die in grams per 10 minutes (g / 10 min). The MVR indicates how much volume of plastic is extruded through a defined die in a specific time period under specified conditions. The MVR is expressed in cubic centimeters per 10 minutes (cm³). 3 / 10 min).

Claims

Patent claims:

1. Portion capsule for beverages comprising, from the outside in, several layers, i.) at least one layer of paper, ii.) at least one layer of metallization, iii.) at least one layer containing polylactic acid, iv.) at least one sealing layer containing at least one thermoplastic Plastic made from glucose, lignin, or cellulose.

2. Portion capsule for beverages according to claim 1 comprising at least one laminating adhesive between i.) and ii.) with a weight of 2-6 g / sq m.

3. Portion capsule for beverages according to claim 1 or claim 2, wherein layer iii.) contains at least one further aliphatic aromatic copolyester, in particular polybutylene adipate terephthalate (PBAT), which is compostable according to EN 13432.

4. Portion capsule for beverages according to one of the preceding claims, wherein the sealing layer iv.) contains at least one further thermoplastic material made from glucose, lignin or cellulose, which is compostable according to EN 13432.

5. Portion capsule for beverages according to one of the preceding claims, wherein i.) have a gram weight of 75 g / m² to 200 g / m², in particular 130 - 170 g / m², in particular 150 g / m².

6. Portion capsule for beverages according to one of the preceding claims, wherein according to layer ii.) the metal is selected from boron, aluminium or silicon, in particular boron oxide, aluminium oxide or silicon oxide.

7. Portion capsule for beverages according to one of the preceding claims, wherein layer ii.) has a thickness of 20 - 50 nm.

8. Portion capsule for beverages according to one of the preceding claims, wherein ii.) additionally includes a coating, in particular made of acrylate.

9. Portion capsule for beverages according to claim 8, wherein at least one acrylate is selected from the group consisting of polyurethane, polyester, epoxy and polyether acrylates or methaacrylates, in particular oligomers, and / or monomers selected from the group consisting of mono-, di-, tri-, tetra- and hexafunctional acrylates or methaacrylates.

10. Portion capsule for beverages according to one of claims 8 or 9, wherein the acrylate coating has a thickness of 20 - 40 nm.

11. Portion capsule for beverages according to any one of claims 1 to 10, wherein the metallization layer ii.) has a weight of 0.1 to 0.15 g / m² and / or the acrylate according to any one of claims 8 or 9 has a weight of 0.04 to 0.06 g / m².

12. Portion capsule for beverages according to one of claims 1 to 11, wherein at least one further layer of polyvinyl alcohol is contained between layer i.) and ii.), in particular having a weight of 2 - 6 g / sqm.

13. Portion capsule for beverages according to any one of claims 1 to 12, wherein layer iii.) has a maximum modulus of elasticity of 100 to 300 MPa according to ISO 527 and / or the maximum yield strength or tensile stress is 45 MPa, in particular 35 to 40 MPa according to ISO 527 and / or the MVR (190 degrees Celsius / 5 kg) is 8-12 cm 3 / 10 min according to ISO 1133.

14. Portion capsule for beverages according to any one of claims 1 to 12, wherein the sealing layer iv.) has a maximum modulus of elasticity up to 4500 MPa according to ISO 527, and / or the maximum tensile strength or yield strength of 40 - 60 MPa according to ISO 527, and / or the MVR (190 degrees Celsius / 2.16 kg) of 3-5 cm 3 / 10 min according to ISO 1133.