Extraction and conversion method of phthalates contained in PVC plastics with alcohol

Abstract

The present invention relates to a method for obtaining dialkyl phthalates and recyclable target PVC plastics from a PVC feedstock containing at least one phthalate, comprising: a) solid-liquid extraction of a PVC feedstock in particulate form; n H 2n+1 (n is a positive integer less than 4 or greater than 8); producing a liquid phase rich in the phthalate and a solid phase comprising PVC plastic poor in the phthalate; (b) contacting the phthalate in the liquid phase with a solvent comprising a phthalate-rich, phthalate-poor PVC plastic; n H 2n+1 ) converting 2 to a dialkyl phthalate with said alcohol via transesterification; c) solid-liquid separation between said solid phase and said liquid phase; producing at least one solid stream comprising said phthalate-lean PVC plastic to obtain said target PVC plastic; d) liquid-liquid separation of a liquid phase; producing at least a first liquid effluent comprising said dialkyl phthalate and a second liquid effluent comprising said solvent.

Description

[Technical field]

[0001] The present invention relates to the field of recycling of plastics based on polyvinyl chlorides (PVC), in particular to a method for converting, by extraction and transesterification, the phthalates plasticizers present in the composition of PVC. More precisely, the present invention relates to a method for recovering dialkyl phthalate (DAP) and reusable target PVC plastics from a PVC feedstock containing at least one phthalate. [Background technology]

[0002] By definition, a plastic is a mixture of a base polymeric material and numerous additives, the assembly of which can be molded or shaped (generally under high temperature and / or pressure) to obtain semi-shaped articles or objects. According to the commonly accepted practice, said plastics are named by the name of the polymer of which they are composed. Thus, polyvinyl chloride (PVC) plastics correspond in fact to a combination of the polymer PVC, called "PVC resin" in the following description, and various additives chosen depending on the function required of said plastic. Said additives may be organic molecules or macromolecules, or also inorganic (nano)particles, used depending on the properties they give to the PVC resin: resistance to heat, light or mechanical stress (stabilizers), flexibility (plasticizers), processability (lubricants), coloring (dyes / pigments), etc.

[0003] Several methods exist for recycling PVC plastics: "conventional" methods with simple mechanical recycling of the plastics, methods that involve modification of their composition or even chemical transformation of the compounds of which they are composed.

[0004] Since the middle of the 20th century, chemical recycling of PVC plastics has been the subject of numerous studies directed towards dissolving the PVC resin with variable proportions of additives in a first step, followed by recovery of said resin in a second step using various chemical methods (precipitation, evaporation, etc.) in the presence of all or part of the soluble additives. For example, patent documents 1 to 3 are each directed towards recycling various PVC-based objects (flexible or rigid pipes, window frames, cables, etc.), in particular fibre-reinforced PVC-based objects (waterproofing fabrics, floor coverings, etc.). This recycling is carried out by a method comprising a first step of dissolving the PVC resin and soluble additives in an organic solvent, followed by a second step of precipitation with water steam, which makes it possible to recover the resin and most of the additives.

[0005] However, it is not always desirable to retain the additives thus recovered in the PVC in order to be recycled. For example, the change in additive regulations over time is a factor to be taken into account. Thus, some plasticizers belonging to the phthalate family, which were particularly widely used about 40 years ago to compound "flexible" PVC, have gradually become the subject of authorisation in Europe under the REACH Regulation and, since the end of 2006, have been directed towards establishing the safety of the production and use of chemicals in European industry, and have finally been gradually removed from the list of additives permitted for use. This is especially the case for the phthalates listed in the following exemplary list: dibutyl phthalate (DBP), dioctyl phthalate (DOP) or diethyl hexyl phthalate (DEHP), benzyl butyl phthalate (BBP), diisobutyl phthalate (DIBP), dipentyl phthalate (DPP), diisopentyl phthalate, n-pentylisopentyl phthalate, dihexyl phthalate, etc.

[0006] These new regulations are now moving towards banning the presence of such compounds in recycled raw materials (RRM). Considering that the useful life of PVC-based objects is often very long (several decades), PVC-based objects compounded before the end of 2006 and that have now reached the end of their useful life cannot be recycled via recovery methods aimed at the retention and management of these prohibited additives, whether these recovery methods are traditional methods, e.g. mechanical recycling methods or not (e.g. the example of the dissolution / precipitation method mentioned above).

[0007] Moreover, the phthalate plasticizers currently used in Europe (REACH-compliant phthalates) and in other parts of the world represent high-added-value additives, but they are not upgraded if they are retained in the PVC recycled raw materials, because they are expensive products, are present in the original PVC formulation in appreciable proportions (tens of percent), and cannot directly impart ad-hoc flexibility properties to the PVC RRM. Therefore, a supply of "fresh" plasticizers in appreciable quantities is essential for the reusability of recycled PVC materials.

[0008] Extraction of phthalate-type additives from PVC-based objects for removal or upgrading therefore represents a major challenge for optimized recyclability of PVC.

[0009] Several methods have been applied to enable this extraction, including a step of dissolving the PVC resin. For example, US Pat. No. 5,299,433 and US Pat. No. 5,299,452 both propose a first step of dissolving the PVC resin and at least phthalate type additives with a first organic solvent, followed by a second step of liquid-liquid extraction of the phthalates from the previously obtained solution through the use of a second organic solvent different from the first. US Pat. No. 5,299,433 discloses another example of possible implementation, which includes dissolving the PVC resin and at least phthalate type additives through the use of a solvent under supercritical conditions, and recovering the phthalates in this same solvent after the "breakdown" of the supercritical conditions.

[0010] The removal or upgrading of phthalate type additives from PVC plastics may be carried out without a preliminary step of dissolving said plastics and, in particular, without direct extraction of said phthalates from the solid polymer matrix with a suitable organic solvent, as fully illustrated in the publication of '1'. The challenge then consists in optimizing the extraction conditions (nature of the solvent, contact time, temperature, pressure, etc.) to achieve the best possible yield of extracted phthalates. This technique for removing phthalates from PVC plastics is often used, in particular, to detect and analytically quantify these particular additives in said plastics, but to the applicant's knowledge, no method for regenerating PVC-based objects includes this technique.

[0011] Although the extraction of phthalate type plasticizers is crucial to ensure efficient recycling of PVC plastics and to obtain reusable recycled PVC, it is insufficient to ensure the economic viability of a process for regenerating PVC-based objects. The main reason, which is often pointed out, is the difficulty in finding an economically viable balance between the costs of the individual operations carried out in the regeneration process and the resale costs of the obtained product (corresponding to the added value), which consists of phthalate-free PVC-based recycled material (naturally upgradeable) and the extracted phthalates (which themselves are slightly upgradeable). In particular, any regeneration process that includes a step of extracting phthalates from PVC-based objects leads to the recovery of a mixture of phthalates, which may contain phthalates that are not "REACH compliant". Upgrading of the REACH-non-compliant phthalates is naturally excluded, which would have to be treated as specific waste, resulting in additional costs. Although REACH-compliant phthalates are advantageous in themselves, upgrading of such phthalates is a practical challenge as it involves technically complex and expensive separation / purification steps. [Prior art documents] [Patent documents]

[0012] [Patent Document 1] European Patent No. 0945481 [Patent Document 2] European Patent No. 1268628 [Patent Document 3] European Patent No. 2276801 [Patent Document 4] European Patent No. 1311599 [Patent Document 5] JP 2007-191586 A [Patent Document 6] JP 2007-092035 A [Non-patent literature]

[0013] [Non-Patent Document 1] Uegduler et al., "Challenge and opportunities of solvent-based additive extraction methods for plastic recycling", Waste Management, 2020, Vol. 104, pp. 148-182 Summary of the Invention [Means for solving the problem]

[0014] (Summary of the invention) The present invention aims at at least partially to overcome the problems of the prior art, and is particularly directed towards providing a method for regenerating PVC-based objects. This method makes it possible to process any type of PVC feedstock containing phthalates and convert them into two interesting products that can be upgraded: specific dialkyl phthalates and phthalates, in particular recyclable PVC plastics that do not contain undesired phthalates, typically phthalates that are subject to authorization by the European REACH regulation. Another object of the present invention is to limit the number of individual steps traditionally associated with phthalate separation / purification operations during the recycling of phthalate-containing PVC, which makes it possible to limit processing costs.

[0015] Therefore, in order to achieve at least one of the above stated objectives, the present invention proposes, according to a first aspect, a method for recovering dialkyl phthalates and reusable target PVC plastics from a PVC feedstock containing at least one phthalate, comprising the following steps: a) solid-liquid extraction of said PVC feedstock in particulate form; the particles of the PVC feedstock are subjected to a solid-liquid extraction process according to formula C n H 2n+1 OH, where n is a positive integer less than 4 or greater than 8; resulting in a liquid phase rich in said phthalate and a solid phase comprising PVC plastic that is poor in said phthalate; b) of said phthalate in the liquid phase, of the formula C6H4(COOC n H 2n+1 ) chemical conversion of 2 to a dialkyl phthalate by transesterification with said alcohol; said liquid phase being enriched in said dialkyl phthalate; c) solid-liquid separation between said solid phase and said liquid phase; producing at least one solids stream comprising said phthalate-lean PVC plastic and recovering the target PVC plastic; d) liquid-liquid separation of the liquid phase to produce at least a first liquid effluent comprising the dialkyl phthalate and a second liquid effluent comprising the solvent.

[0016] One advantage of the present invention lies in the ability of the method to convert, by chemical transesterification, a mixture of phthalates initially trapped in the polymer matrix of various objects based on PVC plastics, into a single, REACH-compliant and upgradeable DAP-type phthalate product, regardless of the composition of said mixture (i.e., regardless of the nature and origin of the various phthalates) and despite the possible presence of numerous other additives. The generation of a single specific DAP product from a mixture of phthalates also makes it possible to limit the number of individual steps associated with separation / purification operations and therefore their costs.

[0017] According to a first variant, steps a) and b) are carried out in the same individual operation.

[0018] According to a second variant, which is an alternative to the first variant, steps a) and b) form the object of two distinct and separate operations, step a) producing a stream comprising a liquid phase and a solid phase.

[0019] According to this second variant, step c) may be carried out between steps a) and b), and the stream comprising the liquid phase and said solid phase obtained from step a) may be sent to a solid-liquid separation step c) to give a stream comprising said phthalate-depleted PVC plastic and a first liquid stream comprising a liquid phase, which first liquid stream is sent to step b).

[0020] According to one or more embodiments, the method also comprises an additional step f1), which is carried out by condensing the unconverted and / or partially converted phthalates of formula C6H4(COOC) in step b). n H 2n+12) by transesterification with said alcohol to dialkyl phthalate, said step f1) being carried out between step c) and step d) by sending said liquid phase obtained at the end of all steps a), b) and c) to a first additional transesterification reactor, n H 2n+1 2) producing a second liquid stream enriched in said dialkyl phthalate, said second liquid stream being sent to step d).

[0021] According to one or more embodiments, the solvent is fed to a first additional transesterification reactor and / or at least a portion of the second liquid effluent from step d) comprising at least the solvent is recycled to the first additional transesterification reactor.

[0022] According to one or more embodiments, in step d), the first liquid effluent consists essentially of the dialkyl phthalate.

[0023] According to one or more embodiments, the liquid-liquid separation step d) also gives rise to a third effluent comprising the alcohol type by-products (AL) obtained during step b) and an optional fourth effluent comprising the phthalates partially converted and / or not converted in step b) and optionally other soluble impurities, said first liquid effluent consisting essentially of said dialkyl phthalates and said second effluent consisting essentially of said solvent.

[0024] According to one or more embodiments, the liquid-liquid separation step d) also gives rise to a third effluent comprising the alcohol type by-product (AL) obtained during step b), the first liquid effluent comprising the dialkyl phthalate, the phthalates partially and / or not converted in step b) and optionally soluble impurities, the second liquid effluent essentially consisting of the solvent, the process also comprising a step e) of purification of the first liquid effluent, giving rise to a liquid product essentially consisting of the dialkyl phthalate and a liquid residue comprising the phthalates partially and / or not converted in step b) and optionally soluble impurities.

[0025] According to one or more embodiments, the method also comprises an additional step f2), which is carried out by condensing the unconverted and / or partially converted phthalates of formula C6H4(COOC)2H2O3 in step b). n H 2n+1 )2 to dialkyl phthalates by transesterification with said alcohol, said step f2) being carried out by sending said liquid residue after step e) to a second additional transesterification reactor, n H 2n+1 ) producing a third liquid stream enriched in said dialkyl phthalate of step 2, said third liquid stream being returned to step d).

[0026] According to one or more embodiments, the solvent is fed to a second additional transesterification reactor and / or at least a portion of the second liquid effluent from step d) comprising at least the solvent is recycled to a second additional transesterification reactor.

[0027] According to one or more embodiments, the process also comprises recycling at least a portion of the liquid residue (17) to step b) and / or to an additional step f1), which comprises converting the phthalates of formula C6H4(COOC) that have not been converted and / or have been partially converted in step b) into phthalates of formula C6H4(COOC) n H 2n+12) Chemical conversion of dialkyl phthalates of formula C6H4(COOC)2 by transesterification with said alcohol, said step f1) being carried out between steps c) and d) by sending said liquid phase obtained at the end of all steps a), b) and c) to a first additional transesterification reactor, n H 2n+1 2) producing a second liquid stream enriched in said dialkyl phthalate, said second liquid stream being sent to step d).

[0028] According to one or more embodiments, the second liquid effluent comprising at least the solvent obtained from step d) is at least partially recycled to step a) and / or step b).

[0029] According to one or more embodiments, the solids stream comprising the phthalate-poor PVC plastic is at least partially recycled to step a).

[0030] According to one or more embodiments, the alcohol is selected from the list consisting of methanol, ethanol, n-propanol, i-propanol, preferably methanol, or from the list consisting of linear or branched nonanol, linear or branched decanol, linear or branched undecanol, linear or branched dodecanol, preferably nonanol or decanol.

[0031] According to one or more embodiments, the solvent also includes an organic co-solvent, preferably derived from the alcohol and having the formula R'COOC n H 2n+1 (n is the same as n of the alcohol, and R' is an alkyl group, preferably containing 1 to 3 carbon atoms), and an ether, and the organic co-solvent is added to the alcohol such that the mass ratio between the organic co-solvent and the alcohol is 0.01 to 4.

[0032] According to one or more embodiments, the organic co-solvent is selected from the group consisting of methyl acetate, methyl propanoate, and cyclopentyl methyl ether.

[0033] According to one or more embodiments, the alcohol is methanol, the dialkyl phthalate is dimethyl phthalate, and the solvent preferably comprises methyl propanoate added to methanol such that the mass ratio between the methyl propanoate and the alcohol is between 0.01 and 4.

[0034] According to one or more embodiments, the chemical conversion carried out by transesterification in step b) and optionally in steps f1) and / or f2) is carried out using a transesterification catalyst, preferably selected from the list consisting of inorganic or organic, basic or acidic, Brönsted homogeneous catalysts or Lewis acids, and heterogeneous catalysts formed by alkaline earth metal oxides, or alkali metal and / or alkaline earth metal carbonates or hydrogen carbonates, or alkali metals supported on alumina or zeolites, or zinc oxide and mixtures thereof with other oxides, or ion exchange resins.

[0035] According to one or more embodiments, the at least one phthalate of the PVC feedstock is a phthalate of empirical formula CH(COOR1)(COOR2), where an ester group is in the ortho position of the benzene nucleus, and R1 or R2 are independently selected from one of the members of the group consisting of a linear or branched or cyclic alkyl chain, a linear or branched alkoxyalkyl chain, or an aryl or alkylaryl chain, with R1 and / or R2 preferably comprising 1 to 20 carbon atoms, or even 1 to 15 carbon atoms.

[0036] According to one or more embodiments, the target PVC plastic is substantially free of said phthalates, and preferably contains less than 0.1% by weight total of phthalates selected from the list consisting of dibutyl phthalate, dioctyl or diethylhexyl phthalate, benzyl butyl phthalate, dibutyl phthalate, diisobutyl phthalate, dipentyl phthalate, diisopentyl phthalate, n-pentyl isopentyl phthalate, dihexyl phthalate, bis(2-methoxyethyl) phthalate, and mixtures thereof.

[0037] According to one or more embodiments, step b) and optional steps f1) and / or f2) are carried out at a temperature between room temperature and 200° C., preferably between 40° C. and 180° C., at a pressure between atmospheric pressure and 11.0 MPa, preferably between atmospheric pressure and 5.0 MPa, and for a duration ranging from 1 minute to 10 hours, preferably from 10 minutes to 4 hours.

[0038] According to one or more embodiments, step a) and / or step b) and optional steps f1) and / or f2) are carried out such that the molar ratio between the amount of alcohol of the solvent and the amount of said phthalate to be extracted or converted is between 2 and 250, preferably between 4 and 90.

[0039] According to a second aspect, the present invention relates to a method for recycling PVC-based objects containing at least one phthalate, the method comprising: - conditioning the PVC-based objects; including at least crushing or shredding the PVC-based objects; forming a PVC feedstock in particulate form; and - Recovery of dialkyl phthalates and recyclable target PVC plastics from said PVC feedstock in particulate form according to the present invention.

[0040] According to a third aspect, the present invention relates to a method for manufacturing a flexible PVC-based object, which object comprises recycled PVC plastic and / or dialkyl phthalate, obtained via the method for recovering dialkyl phthalate and reusable target PVC plastic according to the invention.

[0041] Other objects and advantages of the present invention will become apparent on reading the following description of examples of particular implementations of the invention, given by way of non-limiting examples, this description being made with reference to the accompanying drawings, in which: DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0042] (List of Drawings) FIG. 1 is a scheme of a method according to one embodiment of the invention, comprising steps a), b), c) and d).

[0043] FIG. 2 is a scheme of a process according to another embodiment, comprising steps a), b), c) and d), in which in step d) a separation takes place between DAP, the solvent, the by-products of alcohol type obtained in step b) and optionally the phthalates, partially converted and / or not converted in step b), optionally as a mixture with soluble impurities.

[0044] FIG. 3 is a scheme of the process according to the embodiment shown in FIG. 1 or FIG. 2, comprising steps a), b), c) and d), illustrating the implementation of the further optional step (f1) of transesterification and the recycling of the various streams.

[0045] FIG. 4 is a scheme of a process according to another embodiment of the invention, comprising steps a), b), c) and d) and also step e) of purification of the first effluent containing DAP obtained in step d).

[0046] FIG. 5 is a scheme of the process according to the embodiment shown in FIG. 4, illustrating the implementation of other optional transesterification steps (f1; f2) and recycling of the various streams.

[0047] FIG. 6 shows a scheme of a process according to a preferred embodiment of the invention, comprising steps a) and b) carried out in the same individual operation (first variant of the process according to the invention) and a step e) of purification of the first effluent comprising DAP, obtained in step d), and an additional step f2) of transesterification of the residue obtained from step e).

[0048] FIG. 7 is a scheme of a method according to another embodiment of the invention, comprising steps a), b), c) and d), in which steps a) and b) form the object of two distinct and separate operations (second variant of the method according to the invention) and in which step c) is carried out between steps a) and b).

[0049] FIG. 8 shows a scheme of a process as shown in FIG. 7 according to a preferred embodiment, comprising a step e) of purification of the first effluent containing DAP obtained in step d) and an additional step f2) of transesterification of the residue obtained in step e).

[0050] In the figures, the same reference numbers indicate identical or similar components.

[0051] (Description of the embodiment) (term) Certain definitions are provided below, however further details regarding the subject matter defined below may be provided later in the specification.

[0052] The term "PVC-based object" means an object, generally a consumer object, that comprises, and preferably consists of, at least one PVC plastic.

[0053] The term "polyvinyl chloride plastic", also known as PVC plastic or simply PVC, refers to the combination of PVC polymer, also known as PVC resin, with various additives that are selected depending on the functionality required of the PVC plastic, which are themselves selected depending on the intended use.

[0054] The PVC polymers are derived from the radical polymerization of vinyl chloride (VCM), which itself is derived from chlorine and ethylene. Depending on the polymerization implementation, four families of PVC resins may be used: 1) suspension PVC or S-PVC resins (suspension polymerization of VCM), 2) emulsion PVC or PVC "paste" resins (emulsion polymerization), 3) bulk PVC or M-PVC resins (bulk polymerization) and 4) perchlorinated PVC or C-PVC resins obtained by perchlorination as a post-treatment on the preceding resin.

[0055] Said additives contained in the composition of PVC plastics can be organic or macromolecules or inorganic (nano)particles, and are used depending on the properties they impart to the PVC resin: resistance to heat, light or mechanical stress (stabilizers), flexibility (plasticizers), processability (lubricants), colorability (dyes / pigments), etc.

[0056] The term "phthalates" refers to a group of chemical products formed by dicarboxylic esters of o-phthalic acid. They consist of a benzene nucleus and two carboxylic ester groups placed in the ortho positions on the benzene nucleus. They have the following formula:

[0057] [ka]

[0058] or by the empirical formula CH(COOR)(COOR), where R and R are independently selected from one of the members of the group consisting of a linear, branched or cyclic alkyl chain, a linear or branched alkoxyalkyl chain, or an aryl or alkylaryl chain, said alkyl, alkoxyalkyl, aryl or alkylaryl chain typically containing 1 to 20 carbon atoms, or even 1 to 15 carbon atoms. For example, R and / or R may be selected from the groups ethyl, n-butyl, isobutyl, n-pentyl, iso-pentyl, n-hexyl, n-octyl, n-nonyl, n-decyl, isodecyl, methoxyethyl and benzyl.

[0059] Phthalates are commonly used as plasticizers for plastics, especially for PVC type plastics, to make them flexible, among other things.

[0060] As used herein, the term "dialkyl phthalate" (DAP) refers to at least one plasticizer of the phthalate type (in particular of the empirical formula C6H4(COOR1)(COOR2) above) present in a PVC-based object, and a dialkyl phthalate of the empirical formula C n H 2n+1 OH (n<4 or n>8) resulting from a transesterification reaction with alcohols of the empirical formula C6H4(COOC n H 2n+1 )2. Dimethyl phthalate is an example of DAP.

[0061] As used herein, empirical formula C n H 2n+1 The definition of the alcohol OH (n<4 or n>8) includes the empirical formula C n H 2n+1 O - The conjugate bases, where n<4 or n>8, may include cationic counterions, including those of metallic nature, which ensure the electronegativity of the conjugate base, as is well known to those skilled in the art. The conjugate bases are also known as "alkoxide" forms of the alcohol.

[0062] The term "alcohol type by-product(s)" (AL) refers to at least one plasticizer of the phthalate type present in the PVC-based object and to at least one by-product of the empirical formula C n H 2n+1 means one or more by-products of formula R1OH or R2OH resulting from a transesterification reaction between alcohols of formula ROH (n<4 or n>8), R1 and R2 being defined as R1 and R2 for phthalates. As mentioned above, the definition of said by-products of alcohol type of formula R1OH or R2OH includes those of empirical formula R1O - or R2O - and its conjugate base may also be included.

[0063] The term "intermediate alkyl phthalate" (IAP) or "partially converted phthalate" refers to the reaction of at least one plasticizer of the phthalate type (in particular of the above empirical formula C6H4(COOR1)(COOR2)) present in the PVC-based object with a compound of the empirical formula C n H 2n+1 OH (n<4 or n>8) resulting from an incomplete transesterification reaction with alcohols of the empirical formula C6H4(COOR1)(COOC n H 2n+1 ) or C6H4(COOR2)(COOC n H 2n+1 ) by-product. R1 and R2 are the same as R1 and R2 in phthalate.

[0064] The term "recyclable target PVC plastic" means "phthalate-free PVC", i.e. a solid containing at least one PVC resin supplemented with at least one of the additives originally present in the PVC plastic of the PVC feedstock treated according to the present invention, from which the phthalates have been extracted and converted according to the present invention into the form of at least one dialkyl phthalate. The term "phthalate-free" means in particular that the solid PVC obtained as product of the process according to the invention contains less than 0.1% by weight in total of phthalates subject to the authorization in Europe according to the REACH regulation (Annex XIV of Regulation (EC) Number 1907 / 2006 of the European Parliament and of the Council of 18 December 2006), in particular less than 0.1% by weight in total of phthalates selected from the list consisting of the following phthalates: dibutyl phthalate (DBP), dioctyl phthalate or diethylhexyl phthalate (DOP or DEHP), benzyl butyl phthalate (BBP), dibutyl phthalate (DBP), diisobutyl phthalate (DIBP), dipentyl phthalate (DPP), diisopentyl phthalate, n-pentyl isopentyl phthalate. , dihexyl phthalate, and bis(2-methoxyethyl) phthalate, which may be utilized alone or in mixtures.

[0065] As used herein, empirical formula C n H 2n+1 The alcohol of OH (n<4 or n>8), optionally supplemented with at least one organic co-solvent, is also referred to as the "solvent."

[0066] In this description, the term "greater than..." is understood to be strictly "greater than" and is symbolized by the symbol ">", and the term "less than..." is understood to be strictly "less than" and is symbolized by the symbol "<".

[0067] In this specification, the index "n" in the cited chemical formulae is a positive integer (i.e. strictly greater than 0). According to the present invention, n is less than 4 or greater than 8, preferably less than or equal to 20, or even less than or equal to 15.

[0068] As used herein, the term "room temperature" (rt) means a temperature, typically 20°C ± 5°C, and the term "atmospheric pressure" means a pressure of 0.101325 MPa.

[0069] As used herein, the term "comprise" is synonymous with (meaning the same thing as) the terms "include" and "contain" and is inclusive or open-ended and does not exclude other elements not specified. The term "comprise" is understood to encompass the exclusive and restrictive term "consist."

[0070] In this specification, the expression "between ... and ..." means that, unless otherwise specified, both limits of the interval are included in the stated range of values.

[0071] Herein, various ranges of parameters for a given process, such as pressure ranges and temperature ranges, may be used alone or in combination, for example, here a range of preferred pressure values ​​may be combined with a more preferred range of temperature values.

[0072] In the following text, specific embodiments of the present invention may be described, which may be implemented separately or in combination together, without any limitation of combination, where this is technically possible.

[0073] The following description of the process according to the invention refers to schemes in Figures 1 to 8, which show various implementations of the process according to the invention.

[0074] According to the present invention, the method for recovering DAP and recyclable target PVC plastic from a PVC feedstock containing at least one phthalate may comprise or consist of the following steps: a) solid-liquid extraction of said PVC feedstock (1) in particulate form; said particles of PVC feedstock are subjected to a solid-liquid extraction process according to formula C n H 2n+1 with a solvent (9) comprising at least one alcohol of n<4 or n>8; producing a liquid phase rich in said phthalate and a solid phase comprising said phthalate-poor PVC plastic; b) the phthalate of formula C6H4(COOC n H 2n+1 ) chemical conversion of 2 to a dialkyl phthalate by transesterification with said alcohol; enriching said liquid phase with said dialkyl phthalate; c) solid-liquid separation between said solid phase and said liquid phase; producing at least one solid stream (6) comprising said phthalate-lean PVC plastic and recovering said target PVC plastic; d) liquid-liquid separation of said liquid phase (4); producing at least a first liquid effluent ((5) or (14)) comprising said dialkyl phthalate and a second liquid effluent ((7) or (12)) comprising at least said solvent.

[0075] (Feed material) The process according to the invention is fed with a feedstock known as "PVC feedstock" (1) which contains at least one PVC plastic, which necessarily contains at least one phthalate as described in the present invention.

[0076] The PVC plastic may contain at least 0.1% by weight phthalate, or even at least 1% by weight phthalate, or alternatively at least 5% by weight phthalate. In general, the PVC plastic advantageously contains less than 60% by weight phthalate, typically less than 30% by weight phthalate.

[0077] Said PVC feedstock is advantageously a feedstock of PVC to be recycled of the "production scrap" type, i.e. waste resulting from processes for producing PVC polymers during their polymerization or for producing PVC plastics during their compounding / molding or for producing PVC-based objects during their manufacture, or of the "post-consumer waste" type, i.e. waste resulting after consumption by users of said PVC-based objects.

[0078] In particular, the PVC feedstock to be recycled may originate from any existing collection and sorting channel or network for production scrap and / or post-consumer waste, especially from collection and sorting channels or networks specific to plastic waste, which make it possible to isolate a stream based on at least one PVC plastic containing at least one phthalate.

[0079] Thus, the PVC feedstock, typically of the "production scrap" and / or "post-consumer waste" type, is generally obtained from the main fields of application where PVC plastics are used, such as, non-exhaustively, the building and construction sector, packaging, automotive, electrical and electronic equipment, sports, medical equipment, etc. Preferably, the PVC feedstock is obtained from the building and construction sector. More precisely, PVC-based objects are generally used in these fields as various rigid profiles (casings for windows, doors, sunshades, roller blinds), pipes and connections, and rigid bottles, plates and films, flexible films and sheets, flexible tubes and profiles, cables, flooring, coated fabrics, etc. Preferably, the PVC-based objects forming the PVC feedstock comprise at least one "flexible" PVC, i.e. PVC containing an additive of the plasticizer type, preferably of the phthalate type, such as, for example, the following PVC-based objects: flexible films and sheets, flexible tubes and profiles, cables, flooring, coated fabrics, etc.

[0080] Advantageously, the PVC feedstock comprises at least 50% by weight, preferably at least 70% by weight, preferably at least 90% by weight, even more preferably at least 95% by weight of PVC plastic comprising at least one phthalate.

[0081] Preferably, the PVC feedstock comprises "flexible" PVC, ie, PVC containing additives of the plasticizer type, preferably of the phthalate type.

[0082] Even more preferably, the PVC feedstock comprises primarily, or even exclusively, "flexible" PVC, ie PVC containing additives of the plasticizer type, preferably of the phthalate type.

[0083] The PVC feedstock treated in the method for recovering DAP and reusable target PVC plastics according to the invention is in particulate form. Thus, if the PVC feedstock is in an original form that is characteristic of manufacturing scrap or post-consumer waste, and especially in the latter case, in the original form of PVC-based objects, it may first undergo a conditioning step that at least includes crushing or shredding to form a PVC feedstock in particulate form. Depending on the channels and / or networks from which these manufacturing scraps and / or PVC-based objects at the end of their useful life originate, the PVC waste may be crushed and / or washed, and / or may undergo any other conditioning step described below, to form a PVC feedstock in particulate form suitable for the method according to the invention. For example, the PVC feedstock may advantageously be in the form of a crushed and possibly washed material, the largest dimension of which is less than 20 cm, preferably less than 10 cm, preferably less than 1 cm, even more preferably less than 5 mm. The PVC feedstock may advantageously be in the form of a finely divided solid, i.e. in the form of particles preferably having an average size of less than 1 mm, for example between 10 and 800 micrometers (μm), the average size advantageously corresponding to the average diameter of the spheres that the said particles are surrounded by.

[0084] The term "PVC feedstock in particulate form" therefore means particles of PVC plastic as already defined, typically having an average size of 10 μm to 20 cm, for example particles of crushed material type having an average size of 1 mm to 20 cm, preferably 1 mm to 10 cm, more preferentially 1 mm to 1 cm, even more preferentially 1 mm to 5 mm, or particles resulting from micronization (very fine grinding resulting in a powder) having an average size of less than 1 mm, preferably 10 μm to 800 μm.

[0085] Preferably, the PVC feedstock treated in the process according to the invention is in the form of particles of a comminuted material type, preferably particles having an average size of 1 mm to 5 mm, or particles resulting from micronization (very fine grinding resulting in a powder) having an average size of less than 1 mm.

[0086] PVC feedstock may also contain "macroscopic" impurities such as glass, metal, plastics other than PVC (e.g. PET, etc.), wood, paper, cardboard, inorganic components, etc. Advantageously, the PVC feedstock contains no more than 50% by weight of "macroscopic" impurities, preferably no more than 30% by weight, preferably no more than 10% by weight, even more preferably no more than 5% by weight.

[0087] Advantageously, the water content of the PVC feedstock in particulate form is less than or equal to 0.3% by weight, preferably less than or equal to 0.1% by weight.

[0088] The various steps of the method according to the invention leading to the DAP and to the target recyclable PVC plastic are detailed in the following paragraphs.

[0089] (Optional Preliminary Step to Condition PVC Feedstock) According to the invention, the method may comprise a preliminary step (not shown in the figures) of conditioning the PVC feedstock, which comprises at least one step of grinding or shredding the PVC feedstock to form a PVC feedstock in solid particulate form as defined above, which may be sent to a solid-liquid extraction step a). This preconditioning step may comprise one or more of the steps mentioned in the following non-exhaustive list: grinding by micronization, sorting, oversorting, washing, drying, etc. Depending on the nature of the PVC feedstock to be treated, the step or steps comprised in the preconditioning step, and their possible frequency and sequence, will be chosen, inter alia, by the person skilled in the art so as to limit the amount of macroscopic impurities and to reduce the size of the solid elements which originally constitute the PVC feedstock.

[0090] For example, the preconditioning step makes it possible to provide PVC feedstock in particulate form, e.g. ground and washed material having an average size of less than 5 mm, the macroscopic impurities content of which is preferably less than 10% by weight, more preferably less than 5% by weight. The preconditioned PVC feedstock may be in the form of finely divided solid particles, i.e. particulates having an average size of less than 1 mm, e.g. between 10 μm and 800 μm.

[0091] The step of preconditioning the PVC feedstock preferably comprises at least one step of drying the PVC feedstock, already in the form of solid particles of ad hoc size and macroscopic impurities content, so that the residual water content of said PVC feedstock is equal to or less than 0.3% by weight, preferably equal to or less than 0.1% by weight.

[0092] (Step a) of solid-liquid extraction of phthalates) The process according to the invention comprises treating a PVC feedstock (1) in particulate form with a granular mixture of PVC and propylene glycol according to the empirical formula C n H 2n+1 The method comprises a step a) of solid-liquid extraction of one or more phthalates from said feedstock (1) by placing it in contact with a solvent (9) comprising an alcohol of OH (n<4 or n>8) to obtain an effluent (2) comprising at least a liquid phase and a solid phase, said liquid phase being enriched in said one or more phthalates and said solid phase comprising PVC plastic being depleted in said one or more phthalates.

[0093] The particular choice of n for the solvent alcohol (excluding C4, C5, C6, C7 and C8 alcohols) makes it possible, during step b), to convert said phthalates by transesterification with said alcohol into at least one DAP as defined below, which DAP is not among the unwanted phthalates, e.g. those subject to authorisation by the aforementioned REACH regulation.

[0094] According to one or more embodiments, the alcohol has the empirical formula C n H 2n+1 and n<4, for example selected from the list consisting of methanol, ethanol, n-propanol, and i-propanol, and even more preferably n=1, where said alcohol is methanolCH3OH.

[0095] According to one or more embodiments, the alcohol has the empirical formula C n H 2n+1 OH, where n>8, for example selected from the list consisting of linear or branched nonanol, linear or branched decanol, linear or branched undecanol, linear or branched dodecanol, preferably nonanol or decanol.

[0096] According to one or more embodiments, the alcohol has the empirical formula C n H 2n+1 OH, where n>8 and n is 20 or less, or even where n is 15 or less.

[0097] According to one or more embodiments, the compound of empirical formula C n H 2n+1 The alcohol of formula OH (n<4 or n>8) may be, according to the present invention, in the form of its alkoxide, i.e., the empirical formula C n H 2n+1 O - The conjugate bases of the alcohols (n<4 or n>8) may be used in the form of cationic counterions, including those of metallic nature, ensuring that the electronegativity of the conjugate base is well known to those skilled in the art.

[0098] In addition to the alcohol, solvent (9) may contain an organic co-solvent to aid in the extraction of one or more phthalates from the PVC feedstock (1). In this case, the organic co-solvent may be an ester derived from the alcohol, the ester having the formula R'COOC n H 2n+1where n is the same as n of the alcohol from which the ester is derived (n<4 or n>8, e.g. n is 20 or less), R' is an alkyl group (linear, branched or cyclic, preferably linear) for example containing 1 to 3 carbon atoms, for example 1 or 2 carbon atoms, or alternatively the organic co-solvent may be an ether, for example cyclopentyl methyl ether (CPME), di-n-propyl ether or dioxane, preferably CPME, as illustrative examples.

[0099] The organic co-solvent is added to the alcohol such that the mass ratio of co-solvent relative to alcohol (co-solvent / solvent) is between 0 and 4, preferably between 0.01 and 4, more preferentially between 0.02 and 0.66, even more preferably between 0.05 and 0.66.

[0100] Said additional organic co-solvent, preferably when said alcohol is methanol, is advantageously selected from the group consisting of methyl acetate, methyl propanoate and CPME.

[0101] Preferably, step a) of solid-liquid extraction of one or more phthalates from a PVC feedstock (1) is carried out by placing said feedstock (1) in particulate form in contact with methanol supplemented with methyl propanoate, preferably such that the mass ratio between methyl propanoate and methanol is between 0 and 4, preferably between 0.01 and 4, more preferentially between 0.02 and 0.66, even more preferably between 0.05 and 0.66. In this case, the DAP resulting from this process is dimethyl phthalate (DMP).

[0102] Step a) of the solid-liquid extraction of the one or more phthalates of the PVC feedstock (1) is preferably carried out under the following operating conditions: temperature: room temperature to 200°C, preferably 40°C to 180°C, more preferably 60°C to 150°C, even more preferably 60°C to 145°C, pressure: atmospheric pressure to 11.0 MPa, preferably atmospheric pressure to 5.0 MPa, more preferably atmospheric pressure to 2.0 MPa, residence time: 1 minute to 10 hours, preferably 10 minutes to 4 hours, more preferably 10 minutes to 2 hours.

[0103] Preferably, step a) is carried out such that the molar ratio between the amount of alcohol of the solvent (9) and the amount of one or more phthalates to be extracted from the PVC feedstock (1) is between 2 and 250, preferably between 4 and 90, even more preferably between 4 and 30.

[0104] The reactor of step a) of the process according to the invention may advantageously be a reactor of the type stirred by a mechanical stirring system and / or a recirculation loop and / or fluidization, for example a discontinuous or continuous perfectly stirred reactor or a rotating drum type reactor.

[0105] In terms of implementation, the PVC feedstock (1) in particulate form and the solvent (9) comprising an alcohol, optionally supplemented with at least one organic co-solvent, are advantageously mixed.

[0106] According to a first option, said mixing may be carried out before the introduction of the feedstock and the solvent into the reactor of the solid-liquid extraction step a), in which case said mixture may be formed in a mixer and then introduced into the reactor, said reactor being maintained at the desired pressure and temperature.

[0107] According to a second option, the PVC feedstock (1) in granular form and the solvent (9) comprising an alcohol, optionally supplemented with at least one organic cosolvent, may be introduced separately into the reactor of step a) of the process according to the invention. The solid PVC feedstock and the solvent are then preferably injected into the reactor via two separate lines, one line allowing the injection of the solvent (9) and the other line allowing the injection of the solid PVC feedstock (1) in granular form. In this case, a mixture of PVC feedstock and solvent is formed directly in the reactor.

[0108] According to the invention, said solid-liquid extraction step a) makes it possible to obtain at least one effluent (2) which comprises at least a liquid phase containing at least the extracted phthalates and at least a solid phase containing at least phthalate-poor, preferably phthalate-free, PVC plastic.

[0109] (Step b) of chemical conversion of the phthalate) The process according to the invention comprises the step of catalysing one or more phthalates of formula C6H4(COOC n H 2n+1 2) a step b) of chemical conversion of at least one DAP of the empirical formula C2, preferably in liquid phase, with said one or more phthalates in liquid phase obtained from step a) and n H 2n+1 OH (n<4 or n>8, preferably n<4, even more preferably n=1 (the alcohol is methanol CHOH)) is carried out by transesterification between the alcohol. When the alcohol is methanol, the transesterification is known as methanolysis.

[0110] The phthalate or phthalates present in the liquid phase at the end of step a) are of the formula C6H4(COOC n H 2n+1Step b) of the chemical conversion of 2 to DAP by transesterification is preferably carried out under the following operating conditions: temperature: room temperature to 200°C, preferably 40°C to 180°C, more preferably 60°C to 150°C, even more preferably 60°C to 145°C, pressure: atmospheric pressure to 11.0 MPa, preferably atmospheric pressure to 5.0 MPa, more preferably atmospheric pressure to 2.0 MPa, residence time: 1 minute to 10 hours, preferably 10 minutes to 4 hours, more preferably 10 minutes to 2 hours.

[0111] Preferably, step b) is carried out such that the molar ratio between the amount of alcohol of solvent (9) and the amount of phthalates to be converted in the liquid phase containing the one or more phthalates extracted at the end of step a) is between 2 and 250, preferably between 4 and 90, even more preferably between 4 and 30.

[0112] The alcohol used to carry out step b) is the same as the alcohol used to carry out step a).

[0113] Preferably, the one or more phthalates extracted in step a) have the formula C6H4(COOC n H 2n+1 Said step b) of the chemical conversion by transesterification of 2 to DAP is carried out in the presence of a transesterification catalyst, advantageously introduced into the reaction medium.

[0114] The transesterification catalyst thus used is, for example, selected from the following non-exhaustive list of catalysts well known to the person skilled in the art, preferably from the list consisting of: - homogeneous catalysts, for example basic catalysts (sodium or potassium hydroxide, sodium or potassium methoxide, sodium or potassium carbonate, etc.), inorganic Brønsted acid catalysts (hydrochloric acid, sulfuric acid, phosphoric acid, etc.), organic Brønsted acid catalysts (methanesulfonic acid, trifluoromethanesulfonic acid, trifluoroacetic acid, etc.), Lewis acid catalysts, especially boron compounds (BH3, BF3) and aluminum compounds (AlF3, AlCl3), and Lewis acid catalysts including organometallic compounds; Heterogeneous catalysts, such as alkaline earth metal oxides (CaO, BaO, etc.), alkali metal and / or alkaline earth metal carbonates or hydrogen carbonates (CaCO3, etc.), alkali metals supported on alumina or zeolites, zinc oxide and mixtures thereof with other oxides (for example zinc oxide and alumina), ion exchange resins (cationic or anionic), such as sulfonic resins, etc.

[0115] For example, the catalyst used according to the invention is a homogeneous catalyst, especially a homogeneous catalyst of the basic catalytic type, for example sodium methoxide.

[0116] Preferably, the amount of catalyst introduced is such that the mass ratio between the catalyst and the phthalate or phthalates to be converted is between 0.5% and 10% by weight, preferably between 1% and 8% by weight, even more preferably between 1% and 5% by weight.

[0117] The catalyst, whether homogeneous or heterogeneous, may be recycled and / or removed in the process by methods well known to those skilled in the art, and is preferably recycled: it is isolated, removed or preferably recycled to downstream steps of the process, for example to step c), step d) and / or step e) or to any other dedicated step for the transesterification reaction.

[0118] The reactor of step b) of the process according to the invention may advantageously be a reactor of the type stirred by a mechanical stirring system and / or by a recirculation loop and / or by fluidization, for example a perfectly stirred reactor of discontinuous or continuous type, or a reactor of the rotating drum type.

[0119] According to the invention, said step b) of conversion of phthalates results in the formation of phthalates of formula C6H4(COOC) obtained after transesterification. n H 2n+1It is then possible to obtain at least one liquid phase which contains at least two DAPs, i.e. at least one effluent which is formed at the end of step a) and which comprises a liquid phase enriched in DAP in step b).

[0120] Steps a) and b) of the method according to the invention may be carried out in one and the same individual operation or may be the subject of two separate successive individual operations, the individual operation of step a) always being carried out before the individual operation of step b).

[0121] In the embodiment presented in Figures 1 to 5, steps a) and b) are characterized in the form of separate "boxes", but they can either be carried out in the same individual operation or be the subject of two different successive individual operations. In the first case, the effluent (2) is present in the same reactor, which is for example used to carry out the two steps a) and b).

[0122] In the embodiment presented in FIG. 6, which is one of the preferred embodiments according to the invention, steps a) and b) are the subject of the same individual operation, which is this time characterized by the use of a single "box" (a+b).

[0123] In the embodiments shown in Figures 7 and 8, the embodiment of Figure 8 is one of the preferred embodiments according to the invention, in which steps a) and b) form the object of two distinct successive and separate operations, and which correspond to a scheme in which step c) is carried out between steps a) and b), as will be explained below.

[0124] (Solid-liquid separation step c) The process according to the invention comprises, on the one hand, reacting one or more phthalates of formula C6H4(COOC) obtained after the transesterification in step a) and / or n H 2n+12) the step of solid-liquid separation between a liquid phase containing the DAP and, on the other hand, a solid phase containing phthalate-poor, preferably phthalate-free, PVC plastic.

[0125] The physical separation of the liquid and solid phases may advantageously be carried out according to techniques known to the person skilled in the art, for example, non-exhaustively, by filtration, centrifugation, electrostatic precipitation or decantation, said techniques being used alone or in combination and in any order.

[0126] This step c) of solid-liquid separation thus makes it possible to obtain at least one solid stream (6) comprising one or more phthalate-poor PVC plastics extracted in step a), allowing to recover said reusable target PVC plastics.

[0127] The production of reusable target PVC as defined according to the present invention may require returning all or part of the solids stream (6) obtained in step c) to step a) for as many cycles as necessary to yield said target PVC plastic.

[0128] This possibility of recycling the solids stream is illustrated in Figures 2-8.

[0129] According to a first variant of the process according to the invention, said solid-liquid separation step c) is carried out after carrying out steps a) and b). This first variant is illustrated in figures 1 to 6. In this case, the liquid effluent (3) obtained from step b) is sent to a solid-liquid separation step c), leading to a separation between a liquid phase containing at least the DAP obtained after the transesterification in step b) and a solid phase containing one or more phthalate-poor PVC plastics. Advantageously, for this first variant of the process according to the invention, steps a) and b) are carried out together in the same individual operation, this particular implementation leading to a reduction in the number of individual operations required to carry out the process according to the invention, thus limiting the number of equipment, the amount of solvent used, the energy used, etc., and therefore leading to a reduction in costs. A preferred example of implementation according to this variant is illustrated in figure 6.

[0130] According to a second variant of the process according to the invention, a solid-liquid separation step c) is carried out after carrying out step a) and before carrying out step b). This second variant is in particular illustrated in figures 7 and 8. In this case, the liquid effluent (2) obtained from step a) is sent to a solid-liquid separation step c), leading to the separation of the liquid phase containing the extracted phthalates from the solid phase containing the PVC plastic depleted in one or more phthalates. As a result, for this second variant, steps a) and b) form the object of two distinct and separate operations. Step c) thus gives rise to a solid stream (6) comprising the PVC plastic depleted in one or more phthalates and a first liquid stream (18) containing the phthalate or phthalates extracted in step a) and which is then sent to step b) for the transformation of said phthalate or phthalates by transesterification. This second variant is particularly suitable in cases where the PVC feedstock to be treated would lead during step a) to the formation of solid phases which are unfavorable (in terms of chemical or rheological properties, etc.) for carrying out the transesterification chemistry.

[0131] For example, according to an embodiment according to this second variant of the method as shown in Figures 7 and 8, where step c) is carried out between steps a) and b), steps a) and c) according to the invention may be carried out continuously in the same discontinuous reactor, this discontinuous reactor having a device for filtering the liquid effluent (2) allowing several cycles of extraction of the phthalates from the solid phase and a device for withdrawing at least the solid phase (6) allowing the final recovery of the target PVC plastic.

[0132] For another example, step c) may be carried out by centrifugation of the liquid effluent (2) or (3) comprising a liquid phase containing at least the extracted phthalates and / or DAP and the solid phase obtained from step a), leading to the separation of solids (6) and advantageously to the return of said solids in whole or in part to step a), preferably placed in suspension beforehand, for example by feeding a solvent (9) (not shown in the figures), until the reusable target PVC plastic is produced.

[0133] (Liquid-liquid separation step d)) The process according to the invention comprises the step of obtaining from the liquid phase obtained at the end of carrying out at least steps a), b) and c) a compound of formula C6H4(COOC n H 2n+1 ) a liquid-liquid separation step d) for extracting 2 DAP.

[0134] The liquid stream ((4), (13)) containing said liquid phase is advantageously fed to this liquid-liquid separation step d), thus making it possible to produce at least a first liquid effluent comprising DAP (stream (5) or (14) according to the diagram) and a second liquid effluent (stream (7) or (12) according to the diagram) at least comprising said solvent.

[0135] The liquid-liquid separation step d) may be carried out by methods well known to the person skilled in the art, such as, non-exhaustively, distillation, decantation, evaporation, liquid-liquid extraction, etc., carried out alone or in combination. The operating conditions (temperature, pressure, etc.) of this step are determined depending on the separation method chosen.

[0136] According to one or more embodiments, the first effluent (5) consists essentially of said DAP. In this case (these cases), the second liquid effluent (7), for example shown in FIG. 1 (or alternatively in FIG. 3), consists of the remaining liquid phase after extraction of the DAP, which contains at least the solvent, i.e. the alcohol, optionally supplemented with a co-solvent, the alcohol-type by-products (AL), intermediate alkyl phthalates (IAP) and one or more phthalates, which may not be converted, extracted at the end of step a) of the process according to the invention. The second liquid effluent (7) may be returned in whole or in part, preferably in whole, to step b) of the process according to the invention.

[0137] In this case (these cases), depending inter alia on the liquid-liquid separation method chosen, for example distillation with side draw or liquid-liquid extraction, it is also possible to separate from the liquid phase not only the solvent but also the AL and, highly advantageously, the IAP, possibly also the IAP with the unconverted phthalates extracted in step a). Such a separation is illustrated, for example, in FIG. 2 or FIG. 7 (and in FIG. 3 as an alternative to the production of stream (7)), where it can be seen that step d) gives rise, in addition to a first effluent (5) essentially consisting of the DAP and a second effluent (12) essentially consisting of the solvent, to a third effluent (10) comprising the AL obtained during the transesterification in step b), and a fourth effluent (11) comprising the (IAP) and / or one or more phthalates that have been partially converted in step b) and / or that have not been converted and possibly other soluble impurities. The fourth effluent (11) may advantageously be returned to step b) of the process according to the invention, in particular according to the first and second variants of the process according to the invention, in order to continue the chemical reaction leading to DAP and thereby improve the yield of this product.

[0138] According to one or more alternative embodiments, as shown in Figures 4 to 6 and 8, the first liquid effluent (14) containing DAP also contains other compounds, for example one or more phthalates partially converted (IAP) and / or not converted in step b) and possibly soluble impurities. As will be explained later, according to this or these embodiments, a step of purification of DAP of the first effluent is necessary. According to this or these embodiments, the liquid-liquid separation step d) therefore advantageously gives rise to said first liquid effluent (14) of impure DAP, a second liquid effluent (12) preferably consisting essentially of said solvent, and a third effluent (10) preferably containing AL obtained during the transesterification in step b). Isolation of AL and solvent is possible, inter alia, depending on the liquid-liquid separation method chosen, for example distillation with side draw or liquid-liquid extraction. When the second liquid effluent (12) essentially consists of said solvent thus recovered, the second liquid effluent (12) may advantageously be returned partially or entirely, preferably entirely, to step a) and / or step b) of the process according to the invention, in particular according to the first and second process variants according to the invention.

[0139] (Step e) of purification of DAP (optional) The process according to the invention may comprise an optional step e) of purification of the first effluent (14) containing the DAP obtained from the liquid-liquid separation step d) to improve its quality and therefore ultimately its upgrading. The embodiments shown in Figures 4, 5, 6 and 8 illustrate the implementation of such a purification step e).

[0140] In the case of carrying out said step e), the solvent is advantageously isolated during the implementation of step d).Furthermore, the IAP and optionally the phthalate(s) extracted at the end of step a) of the process according to the invention and not converted at the end of step b) can be isolated during step d) of the process according to the invention or alternatively during the implementation of said purification step e).

[0141] It is therefore possible to send the first effluent (14) comprising DAP, one or more phthalates partially and / or not converted in step b) and optionally soluble impurities to this purification step e) to form a liquid product (16) consisting essentially of said DAP and a liquid residue (17) comprising one or more phthalates partially and / or not converted in step b) and optionally soluble impurities.

[0142] The liquid residue (17) thus recovered may advantageously be returned to step b) of the method according to the invention, in particular according to the first and second variants of the method according to the invention, as illustrated in FIG. 4 or FIG. 5, to continue the chemical reaction leading to DAP.

[0143] Purification step e) may advantageously be carried out via methods well known to those skilled in the art, such as precipitation, crystallization or adsorption, optionally followed by filtration or centrifugation. Purification step e) may comprise the implementation of several of these methods in parallel or successively. For example, and without being exhaustive, purification step e) may comprise a step of precipitation and filtration followed by an adsorption step, or alternatively a step of adsorption and filtration followed by an optional precipitation step, or alternatively a step of crystallization and filtration. The operating conditions (temperature, pressure, etc.) of this step e) are determined depending on the purification method chosen.

[0144] (Additional steps f1) and / or f2) (optional) of chemical transformation by transesterification) In order to facilitate the production of DAP according to the invention, independently of step b) of chemical conversion of the one or more phthalates extracted in step a), it is possible to carry out an additional chemical conversion step allowing the conversion of the IAP and / or the one or more phthalates extracted which may not have been converted at the end of step b).

[0145] The method includes, as shown in FIG. 3 or FIG. 5, converting one or more phthalates not converted in step b) and / or at least one IAP of the formula C6H4(COOC) produced in step b). n H 2n+1 The process may thus comprise an additional step f1) using a solvent comprising an alcohol for the chemical conversion of 2 by transesterification to DAP. In these embodiments, step f1) is carried out between steps c) and d), advantageously after step b), by sending the liquid phase (4), advantageously obtained at the conclusion of all steps a), b) and c), to a first additional transesterification reactor, to give a second liquid stream (13) rich in DAP, said second liquid stream (13) being sent to step d). According to this embodiment, step c) is preferably carried out at the conclusion of step b).

[0146] The process further comprises the step of converting one or more phthalates of formula C6H4(COOC) which have not been converted in step b) and / or at least one IAP which has been produced in step b) or optionally in optional step f1). n H 2n+1 2) may comprise an additional step f2) of chemical conversion by transesterification with a solvent comprising an alcohol to DAP, which is carried out after step e) by sending the liquid residue (17) obtained from step e) to a second additional transesterification reactor to give a third liquid stream (15) enriched in DAP, said third liquid stream (15) being returned to step d).

[0147] The implementation of an additional step f1) and / or an additional step f2) of the chemical conversion by transesterification may be carried out according to the first variant (solid-liquid separation step c)) carried out after steps a) and b) or according to the second variant (solid-liquid separation step c)) between steps a) and b) of the process according to the invention.

[0148] Preferably, the process according to the invention comprises only one additional step of chemical conversion by transesterification, preferably step f2).

[0149] The implementation of steps f1) and / or f2) is as described for step b) of the method according to the invention. In particular, the relevant ranges of operating conditions for steps b) and f1) and / or f2) are similar, said ranges being chosen by the person skilled in the art to promote the production of DAP depending on the chemical nature of the stream to be treated at the inlet of said steps f1) and / or f2).

[0150] This also applies to the preferred use of a transesterification catalyst (8), as described in step b). The transesterification catalyst in steps f1) and / or f2) may be the same or different from that used in step b).

[0151] The stream (stream (4) or liquid residue (17)) sent to step f1) and / or step f2) is the liquid phase extracted in step a) and comprising the phthalate(s) optionally partially converted (IAP) and / or unconverted in step b), and optionally soluble impurities, which is then isolated either during the performance of the liquid-liquid separation step d) of the process according to the invention or, if this is advantageously carried out, during the performance of purification step e) of the process according to the invention.

[0152] Depending on the sequence of steps considered to include step f1) and / or step f2), the empirical formula C n H 2n+1It may be necessary to use an additional supply of solvent comprising an alcohol with OH (n<4 or n>8), possibly supplemented with at least one organic cosolvent, which can come from the supply of "fresh" solvent (9) or else from the recycling of said solvent stream (12), possibly isolated at the end of step d) of the process according to the invention. This additional supply in the first additional transesterification reactor carried out in step f1) and / or in the second additional transesterification reactor carried out in step f2) is by feeding fresh solvent (9) and / or recycling the second effluent (12) consisting of said solvent, and is illustrated in Figures 3, 5, 6 and 8.

[0153] If a purification step e) is performed, at least a portion of the liquid residue (17) generated in step e) may be recycled to step f1) as shown in FIG. 5 to continue the chemical reaction leading to DAP.

[0154] Figures 6 and 8 respectively represent preferred embodiments according to the first variant (solid-liquid separation step c)) after carrying out steps a) and b) of the method according to the invention and according to the second variant (solid-liquid separation step c)) between steps a) and b).

[0155] As can be seen in FIG. 6, according to a preferred embodiment of the invention according to a first variant, the process comprises the implementation in one and the same separate operation of steps a) and b), a solid-liquid separation step c) after steps a) and b), a liquid-liquid separation step d), a step e) of purification of the first effluent (14) obtained in step d) comprising the DAP and an additional step f2) of transesterification of the residue (17) advantageously obtained from step e).

[0156] According to this embodiment, as shown diagrammatically in FIG. 6, the PVC feedstock (1) in particulate form, optionally preconditioned, is introduced into a reactor combining the implementation of steps a) and b) of a chemical conversion by solid-liquid extraction and transesterification, respectively, preferably in the presence of a catalyst (8). The reactor is connected to a reactor having a reactor according to the empirical formula C n H 2n+1A fresh solvent stream (9) external to the process, containing at least one alcohol with OH (n<4 or n>8), preferably methanol, is also fed, supplemented with an optional co-solvent, preferably methyl propanoate, and optionally supplementing at least a portion of the solvent stream (12) separated in the liquid-liquid separation step d). The reaction effluent (3) contains a liquid phase containing at least DAP, preferably DMP, and a solid phase containing phthalate-poor, preferably phthalate-free, PVC plastic, which is sent to a solid-liquid separation step c), for example by carrying out centrifugation to produce a solid stream (6) containing the extracted phthalate-poor PVC plastic or plastics, to recover the reusable target PVC plastic, and to produce a liquid stream (4) containing at least DAP, preferably DMP, and at least solvent. The solid stream (6) may be partially recycled to step a). The liquid stream (4) obtained from step c) containing DAP, solvent, optionally one or more phthalates not converted or partially converted (IAP) and optionally AL is sent to a liquid-liquid separation step d), which makes it possible, on the one hand, to isolate the solvent as stream (12), but also, preferably, the AL as stream (10), and finally, a liquid effluent (14) containing DAP, preferably DMP, and optionally one or more phthalates not converted partially and / or not converted and optionally soluble impurities. The liquid effluent (14) is sent to a purification step e) to obtain purified DAP, preferably DMP. Since the residue (17) obtained from this purification step e) may still contain one or more phthalates not converted or partially converted (IAP), an additional chemical conversion step f2) of transesterification is preferably carried out. The residue (17) is therefore advantageously sent to a second transesterification reactor containing a suitable transesterification catalyst to carry out the transesterification of one or more unconverted or partially converted (IAP) phthalates with a solvent (9), which has the empirical formula Cn H 2n+1 The alcohol comprises OH (n<4 or n>8) and is supplemented with an optional co-solvent, preferably methyl propanoate. The solvent may be a fresh solvent feed or may originate from a stream (12) which is at least partially recycled to this step f2). This step f2) gives rise to a liquid stream (15) rich in said DAP, preferably DMP, which is returned to the liquid-liquid separation step d).

[0157] According to another preferred embodiment of the invention according to a second variant, as shown in FIG. 8, the process comprises the implementation of steps a) and b) in two distinct and separate operations, step c) being carried out between steps a) and b), followed by step d), also comprising a step e) of purification of the first effluent (14) obtained in step d) comprising DAP, and an additional step f2) of transesterification of the residue (17) obtained from step e).

[0158] According to this embodiment, as shown diagrammatically in Figure 8, the PVC feedstock (1) in particulate form, optionally preconditioned, is introduced into a reactor to carry out step a) of solid-liquid extraction of one or more phthalates from said PVC feedstock. The reactor is operated according to empirical formula C n H 2n+1The feedstock (1) is fed with fresh solvent (9) external to the process, comprising at least one alcohol, preferably methanol, of the formula (OH) (n is an integer n<4 or n>8, and optionally supplemented with a co-solvent, preferably methyl propanoate, and optionally with a solvent stream (12) isolated in a subsequent liquid-liquid separation step d). The effluent (2) resulting from step a) comprises at least a liquid phase containing at least one phthalate or phthalates extracted from the feedstock (1) and at least a solid phase containing PVC plastics depleted in phthalates, preferably free of extracted phthalates. The effluent (2) is fed to a solid-liquid separation step c), for example by carrying out a centrifugation to produce a solid stream (6) containing the PVC plastics depleted in one or more phthalates, to recover the reusable target PVC plastics, and to produce a liquid stream (18) containing at least one phthalate or phthalates and solvent extracted in step a). The liquid stream (18) is then sent to a reactor carrying out step b) of chemical transformation of the extracted phthalate(s) by transesterification, preferably in the presence of a catalyst (8). The transesterification reactor may be fed with a stream of fresh solvent (9) external to the process containing the same alcohol, preferably methanol, supplemented with an optional co-solvent, preferably methyl propanoate, and optionally with at least a portion of the solvent stream (12) isolated in the liquid-liquid separation step d). The reaction effluent (4), containing a liquid phase comprising at least DAP, preferably DMP, solvent and one or more phthalates that have not been converted or that have been partially converted (IAP), is sent to a liquid-liquid separation step d), which makes it possible, on the one hand, to isolate the solvent as stream (12), but also the AL as stream (10), and finally the liquid effluent (14) comprising DAP, preferably DMP and optionally the partially converted (IAP) and / or one or more phthalates that have not been converted and optionally soluble impurities. The liquid effluent (14) is preferably sent to a purification step e) to obtain purified DAP (16), preferably DMP.Since the residue (17) obtained from this purification step e) may still contain one or more unconverted or partially converted (IAP) phthalates, an additional transesterification chemical conversion step f2) is preferably carried out. The residue (17) is advantageously sent to a second transesterification reactor, preferably containing a suitable transesterification catalyst, to carry out the transesterification of the unconverted or partially converted (IAP) phthalates or phthalates according to empirical formula C. n H 2n+1 It is carried out using a solvent (9) containing an alcohol of the formula:OH (n is an integer n<4 or n>8), supplemented with an optional co-solvent, preferably methyl propanoate, which may be a fresh solvent feed or may originate from a stream (12) which is at least partially recycled to this step f2). This step f2) produces a liquid stream (15) enriched in said DAP, preferably DMP, which is returned to the liquid-liquid separation step d).

[0159] The present invention also relates to a method for recycling PVC-based objects containing at least one phthalate, said recycling method comprising: - conditioning the PVC-based object, which at least includes grinding or shredding the PVC-based object to form a PVC feedstock in particulate form; - recovery of DAP and recyclable target PVC plastic from said PVC feedstock in particulate form by the method for the recovery of DAP and recyclable target PVC plastic, as described in detail above.

[0160] The process of conditioning the PVC-based article may include the various steps detailed above for pre-conditioning the PVC feedstock before it is introduced into step a).

[0161] The present invention also relates to a method for producing flexible PVC-based objects comprising recycled PVC plastic and / or DAP obtained via the method for recovering DAP and reusable targeted PVC plastic as described in detail above.

[0162] Such manufacturing methods typically include recovering DAP and a recyclable target PVC plastic from a PVC feedstock as described above, followed by blending the recyclable target PVC plastic with additives or blending the recovered DAP with a PVC resin and then forming the blend.

[0163] (Example) This example illustrates the present invention without, however, limiting its scope, and in particular illustrates the extraction of phthalates contained in PVC plastic and their conversion to dimethyl phthalate by methanolysis in the presence of a catalyst.

[0164] 18.2 g of PVC plastic feedstock (obtained from PVC-based objects of the "medical tubing" type) are introduced into the reactor. The PVC plastic feedstock is in the form of extrudates with an average size of 2 mm and contains 4.4 g of didecyl phthalate (DIDP), the reactor being stirred by a paddle-type mechanical stirring system. 26.5 g of methanol and 17.7 g of methyl propanoate (organic cosolvent) are then added, resulting in a methyl propanoate / methanol mass ratio of 0.66 and a methanol / DIDP molar ratio of 84. 0.17 g of catalyst (NaOMe) is then added to this mixture, resulting in a NaOMe / DIDP mass percentage of 4%.

[0165] The reactor is closed gas-tight, purged with nitrogen and then heated to 100° C., bringing the autogenous pressure to the order of 1.2 MPa and maintaining it under these conditions for 4 hours with stirring at 1000 rpm. The reactor is then cooled.

[0166] After 4 hours, a solid and a liquid are obtained and analyzed.

[0167] Analysis of the liquid phase by gas chromatography with flame ionization detection (GC-FID) shows that it contains 1.89 g of dimethyl phthalate (DMP) from the conversion of DIDP and 0.05 g of decyl methyl phthalate from the partial conversion of DIDP. The liquid is also found to contain decanol (C 10 H 22 Identification was made possible by comparison of retention times with pure substance analytical standards, and quantification was carried out by determining the response factors resulting from the analysis of these same standards.

[0168] A preliminary fractionation of the solid obtained was carried out by preparative size exclusion chromatography (SEC) with dual optical detection (UV / visible) and refractive index measurement (RI). Analysis of the fractions obtained from the collection was carried out by high performance liquid chromatography (HPLC) with quantitative UV-visible type optical detection. The results show that DIDP is present in the target PVC plastics at a content of less than 1000 ppm, a content that complies with the European regulations in force.

[0169] These results show that a phthalate-free PVC is obtained, in accordance with the present invention, and that the DIDP is converted to 99.9%. In this example, the extraction of DIDP and its conversion are carried out in the same process. [Brief description of the drawings]

[0170] [Figure 1] 1 is a scheme of a method according to one embodiment of the present invention, comprising steps a), b), c) and d). [Diagram 2]FIG. 1 is a scheme of a process according to another embodiment, comprising steps a), b), c) and d), in which in step d) a separation is carried out between DAP, the solvent, the by-products of alcohol type obtained in step b) and optionally the phthalates, partially converted and / or not converted in step b), optionally as a mixture with soluble impurities. [Diagram 3] FIG. 3 is a scheme of the process according to the embodiment shown in FIG. 1 or FIG. 2, comprising steps a), b), c) and d), illustrating the implementation of the further optional step (f1) of transesterification and recycling of the various streams. [Figure 4] FIG. 1 is a scheme of a process according to another embodiment of the present invention, comprising steps a), b), c) and d) and also step e) of purification of the first effluent containing DAP obtained in step d). [Diagram 5] FIG. 5 is a scheme of the process according to the embodiment shown in FIG. 4, illustrating the implementation of further optional transesterification steps (f1; f2) and recycling of the various streams. [Figure 6] FIG. 1 is a scheme of a process according to a preferred embodiment of the invention, comprising steps a) and b) carried out in the same individual operation (first variant of the process according to the invention) and a step e) of purification of the first effluent comprising DAP, obtained in step d), and an additional step f2) of transesterification of the residue obtained from step e). [Figure 7] FIG. 1 is a scheme of a method according to another embodiment of the invention, comprising steps a), b), c) and d), in which steps a) and b) form the object of two distinct and separate operations (second variant of the method according to the invention) and in which step c) is carried out between steps a) and b). [Figure 8] FIG. 8 is a scheme of the process as shown in FIG. 7 according to a preferred embodiment, comprising a step e) of purification of the first effluent containing DAP obtained in step d) and an additional step f2) of transesterification of the residue obtained in step e).

Claims

1. 1. A method for recovering dialkyl phthalates and recyclable target PVC plastic from a PVC feedstock containing at least one phthalate, comprising the steps of: a) solid-liquid extraction of said PVC feedstock (1) in particulate form; said particles of PVC feedstock are subjected to a solid-liquid extraction process according to formula C ｎ H ２ｎ＋１ OH (n is a positive integer less than 4 or greater than 8); resulting in a liquid phase rich in said phthalate and a solid phase comprising said phthalate-poor PVC plastic; b) of said phthalate in said liquid phase, ６ H ４ (COOC ｎ H ２ｎ＋１ ) ２ to a dialkyl phthalate by transesterification with said alcohol; enriching said liquid phase with said dialkyl phthalate; c) solid-liquid separation between said solid phase and said liquid phase; producing at least one solid stream (6) comprising said phthalate-lean PVC plastic and recovering said target PVC plastic; d) liquid-liquid separation of said liquid phases to produce at least a first liquid effluent ((5), (14)) comprising said dialkyl phthalate and a second liquid effluent ((7), (12)) comprising at least said solvent.

2. 2. The method of claim 1, wherein steps a) and b) are carried out in the same individual operation.

3. 2. The method according to claim 1, wherein steps a) and b) form the object of two distinct and separate operations, step a) generating a stream (2) comprising said liquid phase and said solid phase.

4. 4. The method according to claim 3, wherein step c) is carried out between steps a) and b), and wherein the stream (2) comprising the liquid and solid phases obtained from step a) is sent to a solid-liquid separation step c) to obtain the stream (6) comprising the phthalate-lean PVC plastic and a first liquid stream (18) comprising the liquid phase, and the first liquid stream (18) is sent to step b).

5. Additional step f of chemical transformation １ ) and the step f １ ) of the unconverted and / or partially converted phthalate of step b) of formula C ６ H ４ (COOC ｎ H ２ｎ＋１ ) ２ and by transesterification of the dialkyl phthalate of step f with the alcohol. １ ) is carried out between steps c) and d) by sending the liquid phase obtained at the end of all steps a), b) and c) to a first additional transesterification reactor, ６ H ４ (COOC ｎ H ２ｎ＋１ ) ２ and sending said second liquid stream (13) to step d).

6. 6. The process according to claim 5, wherein the solvent (9) is fed to a first further transesterification reactor and / or at least a portion of the second liquid effluent ((7), (12)) obtained from step d) and comprising at least the solvent is recycled to the first further transesterification reactor.

7. 2. The method of claim 1, wherein in step d), the first liquid effluent (5) consists essentially of the dialkyl phthalate.

8. 2. The process according to claim 1, wherein the liquid-liquid separation step d) results in a third effluent (10) comprising alcohol type by-products obtained during step b) and optionally also a fourth effluent (11) comprising the phthalates partially converted and / or not converted in step b) and optionally other soluble impurities, said first liquid effluent (5) consisting essentially of said dialkyl phthalates and said second liquid effluent (12) consisting essentially of said solvent.

9. 2. The method of claim 1 , The liquid-liquid separation step d) also results in a third effluent (10) comprising alcohol type by-products obtained during step b), said first liquid effluent (14) comprising said dialkyl phthalates, phthalates partially converted and / or not converted in step b) and possibly soluble impurities, and said second liquid effluent (12) essentially consisting of said solvent, said process also comprising the following step e): e) also comprising a step of purification of said first liquid effluent (14) to produce a liquid product (16) consisting essentially of said dialkyl phthalates and a liquid residue (17) containing said phthalates partially converted and / or unconverted in step b) and optionally said soluble impurities.

10. Additional step f of chemical transformation ２ ), which is also included in step b) by the conversion of said phthalates of formula C ６ H ４ (COOC ｎ H ２ｎ＋１ ) ２ and the step f is carried out by transesterification with the alcohol to the dialkyl phthalate of ２ ) is carried out after step e) by sending the liquid residue (17) to a second additional transesterification reactor, ６ H ４ (COOC ｎ H ２ｎ＋１ ) ２ and returning said third liquid stream (15) to step d).

11. 11. The process according to claim 10, wherein the solvent (9) is fed to a second additional transesterification reactor and / or at least a portion of the second liquid effluent (12) obtained from step d) and comprising at least the solvent is recycled to the second additional transesterification reactor.

12. of at least a portion of said liquid residue (17), step b) and / or additional step f) １ ) and additional process f １ ) is a phthalate of formula C which has not been converted and / or has been partially converted in step b). ６ H ４ (COOC ｎ H ２ｎ＋１ ) ２ to a dialkyl phthalate by transesterification with said alcohol, １ ) is carried out between steps c) and d) by sending the liquid phase obtained at the end of all steps a), b) and c) to a first additional transesterification reactor, ６ H ４ (COOC ｎ H ２ｎ＋１ ) ２ and sending said second liquid stream (13) to step d).

13. 2. The process according to claim 1, wherein the second liquid effluent ((7), (12)) obtained from step d) and at least comprising the solvent is at least partially recycled to step a) and / or step b).

14. 2. The method according to claim 1, wherein the solids stream (6) comprising phthalate-poor PVC plastic is at least partially recycled to step a).

15. 2. The method according to claim 1, wherein the alcohol is selected from the list consisting of methanol, ethanol, n-propanol, i-propanol, preferably from methanol, or from the list consisting of linear or branched nonanol, linear or branched decanol, linear or branched undecanol, linear or branched dodecanol, preferably from nonanol or decanol.

16. The solvent also includes an organic co-solvent, preferably an organic co-solvent derived from the alcohol and having the formula R'COOC ｎ H ２ｎ＋１ 2. The method of claim 1, wherein R′ is an alkyl group preferably containing 1 to 3 carbon atoms, and the organic co-solvent is added to the alcohol in a mass ratio between the organic co-solvent and the alcohol of 0.01 to 4.

17. 17. The method of claim 16, wherein the organic co-solvent is selected from the group consisting of methyl acetate, methyl propanoate, and cyclopentyl methyl ether.

18. 2. The method of claim 1, wherein the alcohol is methanol, the dialkyl phthalate is dimethyl phthalate, and the solvent preferably comprises methyl propanoate, such that the mass ratio between the methyl propanoate and the alcohol is between 0.01 and 4.

19. In step b), optionally step f １ ) and / or f ２ 2. The process according to claim 1, wherein the chemical conversion carried out by transesterification in step (a) is carried out in the presence of a transesterification catalyst, preferably selected from the list consisting of inorganic or organic, basic or acidic, Bronsted homogeneous catalysts, or Lewis acids, and heterogeneous catalysts formed from alkaline earth metal oxides, or alkali metal and / or alkaline earth metal carbonates or hydrogen carbonates, or alkali metals supported on alumina or zeolites, or zinc oxide and mixtures thereof with other oxides, or ion exchange resins.

20. The at least one phthalate of the PVC feedstock has the empirical formula C ６ H ４ (COOR １ ) (COOR ２ ) phthalates, where the ester group is in the ortho position to the benzene nucleus, R １ Or R ２ is independently selected from one of the members of the group consisting of a linear or branched or cyclic alkyl chain, a linear or branched alkoxyalkyl chain, or an aryl or alkylaryl chain; R １ and / or R ２ The method of claim 1, wherein preferably comprises 1 to 20 carbon atoms, or even 1 to 15 carbon atoms.

21. 2. The method of claim 1, wherein the target PVC plastic is substantially free of said phthalates, preferably containing less than 0.1% by weight total of phthalates selected from the list consisting of dibutyl phthalate, dioctyl or diethylhexyl phthalate, benzyl butyl phthalate, dibutyl phthalate, diisobutyl phthalate, dipentyl phthalate, diisopentyl phthalate, n-pentyl isopentyl phthalate, dihexyl phthalate, bis(2-methoxyethyl) phthalate, and mixtures thereof.

22. Step b), and optionally step f. １ ) and / or f ２ 2. The method according to claim 1, wherein said step (a) is carried out at a temperature between room temperature and 200° C., preferably between 40° C. and 180° C., at a pressure between atmospheric pressure and 11.0 MPa, preferably between atmospheric pressure and 5.0 MPa, for a period of 1 minute to 10 hours, preferably 10 minutes to 4 hours.

23. Step a) and / or step b) and optionally step f. １ ) and / or f ２ 2. The process according to claim 1, wherein said step (a) is carried out in such a way that the molar ratio between the amount of alcohol of the solvent (9) and the amount of the phthalate to be extracted or converted is between 2 and 250, preferably between 4 and 90.

24. 1. A method for recycling PVC-based objects containing at least one phthalate, the method comprising: - conditioning the PVC-based objects, the conditioning comprising at least grinding or shredding the PVC-based objects to form a PVC feedstock in particulate form; - Recovery of dialkyl phthalates and recyclable target PVC plastic from said PVC feedstock in particulate form according to any one of claims 1 to 23.

25. 24. A method for manufacturing a flexible PVC-based object, the object comprising recycled PVC plastic and / or dialkyl phthalates, which are obtained via the method according to any one of claims 1 to 23.