Surface modification of welding wire drive rolls

Abstract

To provide surface modification of welding wire driving rolls.SOLUTION: Welding wire driving rolls include an outer circumferential surface and a circumferential groove is projected from the outer circumferential surface to the radial inner side. The circumferential groove is formed by a first lateral wall having a first lateral surface, a second lateral wall having a second lateral wall surface and a groove base part extended between the first lateral wall and the second lateral wall. The first lateral wall surface includes a first surface finishing which contains a first ring of a crater laser-formed along the first lateral wall surface. The second lateral wall surface includes a second surface finishing which contains a second ring of a crater laser-formed along the second lateral wall surface.SELECTED DRAWING: Figure 2

Description

[Technical field]

[0001] CROSS-REFERENCE TO RELATED APPLICATIONS This application claims priority to U.S. Provisional Patent Application No. 62 / 902,085, filed September 18, 2019, the disclosures of which are incorporated herein by reference, and to U.S. Nonprovisional Patent Application No. 16 / 987,537, filed August 7, 2020, the disclosures of which are incorporated herein by reference.

[0002] The present invention relates to the surface finishing of welding wire drive rolls. [Background technology]

[0003] The drive roll of the welding wire electrode has a circumferential groove sized to the diameter of the wire being fed by the drive roll. The grooves of the drive roll designed to feed solid welding wire typically lack a surface finish such as knurling so that the solid welding wire can be tightly clamped between the drive rolls without deformation. However, cored welding wires (e.g., flux-cored welding wires and metal-cored welding wires) and solid wires made of soft metals such as aluminum and silicon bronze deform much more easily under high clamping pressures. The high clamping pressures required to reliably drive typical solid welding wires can be too great for cored or soft welding wires and can crush the wire. Wire deformation or crushing can result in feeding problems and poor performance during the welding arc. Typically, when a welding process uses cored or soft metal welding wires, the clamping pressure of the drive roll can be reduced by feeding the wire using a drive roll with knurling grooves. The knurling surface finish creates the friction necessary to drive the wire at low clamping pressures without cylindrical deformation or wire crushing. However, knurling tends to produce burrs on the outer surface of the wire. Burrs are undesirable because over time they wear away the liner of the welding torch through which the wire is fed. Additionally, knurling grooves on drive rolls requires special machining. It would be desirable to add a surface finish to the drive roll grooves that requires less machining than knurling, is less likely to produce burrs on the driven wire, and produces suitable friction for driving wire (e.g., cored or soft solid wire) with clamping pressures that do not deform the wire. Summary of the Invention [Means for solving the problem]

[0004] The following summary is provided in a simplified form to provide a basic understanding of some aspects of the devices, systems and / or methods discussed herein. This summary is not an extensive overview of the devices, systems and / or methods discussed herein. It is not intended to identify required elements or to delineate the scope of such devices, systems and / or methods. Its sole purpose is to present some concepts in a simplified form as a prelude to the more detailed description that is presented below.

[0005] According to one aspect of the present invention, there is provided a welding wire drive roll, the welding wire drive roll including an outer circumferential surface having a circumferential groove projecting radially inward from the outer circumferential surface. The circumferential groove is defined by a first sidewall having a first sidewall surface, a second sidewall having a second sidewall surface, and a groove base extending between the first sidewall and the second sidewall. The first sidewall surface includes a first surface finish including a first ring of laser formed craters along the first sidewall surface. The second sidewall surface includes a second surface finish including a second ring of laser formed craters along the second sidewall surface.

[0006] According to another aspect of the present invention, there is provided a welding wire drive roll including an outer circumferential surface having a first circumferential groove and a second circumferential groove axially offset from the first circumferential groove, both of which project radially inward from the outer circumferential surface. The first circumferential groove is defined by a first sidewall having a first sidewall surface, a second sidewall having a second sidewall surface, and a first recessed groove base extending between the first sidewall and the second sidewall. The first sidewall surface includes a first plurality of laser formed craters arranged annularly along the first sidewall surface and includes first surface finishes each having a central recess recessed into the first sidewall surface and a peripheral portion elevated above the first sidewall surface. The second sidewall surface includes a second plurality of laser-formed craters arranged in an annular manner along the second sidewall surface and includes a second surface finish, each having a central recessed portion recessed into the second sidewall surface and a peripheral portion raised above the second sidewall surface. The second circumferential groove is defined by a third sidewall having a third sidewall surface, a fourth sidewall having a fourth sidewall surface, and a second recessed groove base extending between the third sidewall and the fourth sidewall. The third sidewall surface includes a third plurality of laser-formed craters arranged in an annular manner along the third sidewall surface and includes a third surface finish, each having a central recessed portion recessed into the third sidewall surface and a peripheral portion raised above the third sidewall surface. The fourth sidewall surface includes a fourth plurality of laser-formed craters arranged in an annular manner along the fourth sidewall surface and includes fourth surface finishes each having a central recess recessed into the fourth sidewall surface and a peripheral portion raised above the fourth sidewall surface.

[0007] According to another aspect of the present invention, there is provided a welding wire drive roll, the welding wire drive roll including an outer circumferential surface having a circumferential groove projecting radially inward from the outer circumferential surface, the circumferential groove being defined by a first sidewall, a second sidewall, and a groove base extending between the first sidewall and the second sidewall, and at least one of the first sidewall, the second sidewall, and the groove base including a surface finish including a ring of laser formed craters along a surface of at least one of the first sidewall, the second sidewall, and the groove base.

[0008] According to another aspect of the present invention, there is provided a method of surface finishing a welding wire drive roll, the method including the steps of providing a welding wire drive roll including an outer circumferential surface having a circumferential groove projecting radially inwardly from the outer circumferential surface, the circumferential groove being defined by a first sidewall having a first sidewall surface, a second sidewall having a second sidewall surface, and a groove base extending between the first sidewall and the second sidewall, the method further including rotating the welding wire drive roll while simultaneously irradiating the first sidewall with a pulsed laser beam to form a first ring of craters along the first sidewall surface.

[0009] These and other aspects of the present invention will become apparent to those skilled in the art to which the present invention pertains upon review of the following description and the accompanying drawings. [Brief description of the drawings]

[0010] [Figure 1] 1 illustrates an exemplary drive roll. [Diagram 2] FIG. 2 is a perspective view of an exemplary drive roll. [Diagram 3] 1 shows a cross-sectional view of a drive roll feeding a double wire. [Figure 4] 1 shows the surface finish of the drive roll grooves. [Diagram 5] 1 shows the surface finish of the drive roll grooves. [Figure 6] 1 shows a cross-sectional view of a drive roll feeding a single wire. [Figure 7] 1 shows a laser surface finish applied to a drive roll groove. [Figure 8] FIG. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0011] The present invention relates to a surface finish for welding wire drive rolls. The present invention will now be described with reference to the drawings, in which like reference numerals are used to refer to like elements in each drawing. It should be understood that the various drawings are not necessarily drawn to scale from one drawing to another or within a drawing, and in particular the dimensions of the components are arbitrarily drawn to facilitate comprehension of the drawings. In the following description, for purposes of explanation, numerous specific details are set forth to provide a thorough understanding of the invention. However, it will be apparent that the invention can be practiced without these specific details. Also, other embodiments of the invention are possible, and what is described herein can be practiced and carried out in other ways. The terms and phrases used in the description of the invention are employed for the purpose of facilitating understanding of the invention, and should not be construed as limiting the invention.

[0012] As used herein, "at least one," "one or more," and "and / or" are non-limiting expressions that are conjunctive and disjunctive. For example, each of the expressions "at least one of A, B, and C," "at least one of A, B, or C," "one or more of A, B, and C," "one or more of A, B, or C," and "A, B, and / or C" means A alone, B alone, C alone, both A and B, both A and C, both B and C, or all of A, B, and C. It should be understood that any disjunctive word or phrase expressing two or more alternative terms, whether described in the embodiments, claims, or drawings, considers the possibility of including one of the terms, either of the terms, or both terms. For example, the phrase "A or B" should be understood to include the possibility of "A" or "B" or "A and B."

[0013] Embodiments of the invention are described herein in the context of a welding system. Exemplary welding systems include gas metal arc welding (GMAW) systems, submerged arc welding (SAW) systems, flux-cored arc welding (FCAW) systems, metal-cored arc welding (MCAW) systems, and the like. Additionally, the wires described herein may be solid wires or cored wires (e.g., flux-cored electrodes and metal-cored electrodes). Embodiments of the invention may be used in manual, semi-automatic, and robotic welding operations. In addition to welding operations, embodiments of the invention may be used in weld-like processes, such as additive manufacturing and hardfacing processes. The wires described herein may be filler wires, for example, for use in gas tungsten arc welding (GTAW), plasma arc welding (PAW), or laser welding. Thus, the term "welding" should be interpreted to include welding and weld-like processes, and the term "welding wire" should be interpreted to include wire electrodes and filler wires.

[0014] An exemplary drive roll 100 is shown in Figures 1 and 2. The drive roll 100 has a central bore. The inner surface of the bore may include contoured recesses 102 for receiving protrusions of a wire feeder drive mechanism, such as a drive gear, that transmits drive torque to the drive roll 100. The drive roll 100 has an axis 104, shown in Figure 2, about which the drive roll 100 rotates during operation or during a surface finishing run. The drive roll 100 includes one or more annular or circumferential wire receiving grooves 106, 108. The circumferential wire receiving grooves 106, 108 are formed on the outer peripheral surface of the drive roll 100 and project radially inward toward the axis 104. The circumferential grooves 106, 108 are axially spaced apart or axially offset around the circumference of the drive roll 100.

[0015] In certain embodiments, the circumferential grooves 106, 108 are sized and shaped to receive and drive a single welding wire. In other embodiments, the circumferential grooves 106, 108 are designed and shaped to receive and drive two welding wires simultaneously. The two welding wires driven simultaneously may have the same diameter or different diameters. Exemplary standard welding wire diameters for use with the drive roll 100 include 0.030 inches, 0.035 inches, 0.040 inches, 0.045 inches, etc. The circumferential grooves 106, 108 may have the same width and depth as one another, or may have different widths and depths to accommodate different sizes or combinations of welding wires. If the circumferential grooves 106, 108 have the same width and depth as one another, the drive roll 100 can be reused when one groove wears by simply flipping the drive roll over and reinstalling it on the wire feeder.

[0016] FIG. 3 shows a partial cross-sectional view of an exemplary drive roll 100 when mounted on a wire feeder to feed a double welding wire. The drive rolls 100 are pressed against each other to apply a clamping force to the cored welding wires, e.g., the first E1 and the second E2 welding wires. Both welding wires E1, E2 are located in the annular or circumferential grooves of the upper and lower drive rolls 100. Due to the pressing or clamping force applied to the drive rolls 100, the welding wires E1, E2 are clamped in the circumferential groove against the upper and lower side walls 110 that form the groove and the adjacent welding wires. The welding wires E1, E2 are held stable in the circumferential groove through three points. The clamping system allows both wires E1, E2 to be fed uniformly through the wire feeder and the welding torch. The two welding wires E1, E2 frictionally support and pull each other while being fed out. The angular inner and outer sidewalls 110 of the circumferential groove apply both vertical and horizontal clamping forces to the welding wires E1, E2. The horizontal clamping force pushes the welding wires E1, E2 together into contact with one another. In certain embodiments, the welding wires E1, E2 are clamped within the circumferential groove such that they are radially offset from both of the groove bases 112. That is, each of the welding wires E1, E2 is secured between both of the angular sidewalls 110 of the groove such that there is a gap between the welding wires and the groove base 112. In FIG. 3, the drive roll 100 has a circumferential groove with straight, angular sidewalls 110 joined by a concavely curved or radiused groove base 112 extending between the sidewalls. In one exemplary embodiment, the angle between the sidewalls 110 and the outer circumferential surface of the drive roll 100 is approximately 150°, although other angles are possible and can be determined using sound engineering judgment. It should be understood that the sidewalls 110 need not be straight as shown, but may have curved sidewall surfaces, and the groove base 112 need not be concave as shown, but may be straight (e.g., to form a trapezoidal shaped circumferential groove). The circumferential grooves may have a variety of shapes. For example, if no horizontal clamping force is required, the circumferential grooves may be square, rectangular, or U-shaped. Additionally, the shapes of the circumferential grooves in the upper and lower drive rolls shown in FIG. 3 may differ from one another.

[0017] 4 and 5 show exemplary surface finishes for the circumferential grooves 106, 108. The surface finish is applied to the surface of the sidewalls of the circumferential grooves 106, 108 to increase friction between the sidewalls and the welding wire so that the drive roll can feed the welding wire at low clamping pressures without slipping. In the embodiment of FIGS. 4 and 5, the surface finish is achieved by pulsed laser etching rather than knurling. Pulsed laser etching results in a less sharp or dull surface finish than knurling, and therefore reduces the likelihood of burrs on the drive wire that can wear the torch liner. Pulsed laser etching also requires less machining than knurling the grooves 106, 108.

[0018] To achieve a surface finish, a laser pulse is emitted to irradiate the sidewalls of the circumferential grooves 106, 108. The laser pulse creates craters 114 in the sidewalls of the grooves 106, 108. The laser pulse displaces material from the center of the crater 114 outward to the perimeter of the crater. Each crater 114 has a central recess 116 recessed into the sidewall surface of the groove and a peripheral portion 118 raised above the sidewall surface. The raised peripheral portion 118 of the crater 114 is formed by material displaced from the central recess 116 of each crater 114. Each laser pulse creates one crater in the sidewall of the groove.

[0019] The drive roll 100 can rotate while laser pulses are fired to form a ring of laser-formed craters along the sidewall surface of the circumferential groove. In FIGS. 4 and 5, each groove sidewall has a single ring of laser-formed craters. However, a sidewall can have multiple rings of laser-formed craters. Each crater 114 in the ring of laser-formed craters in FIGS. 4 and 5 is shown located at approximately the same radial distance from the central axis of the drive roll 100 (e.g., each central recess is at approximately the same radial location along the groove sidewall). However, the craters 114 do not have to be located at the same radial distance from the central axis of the drive roll 100. The craters 114 can be located anywhere along the sidewall surface of the grooves 106, 108 as appropriate. For example, some craters 114 can be higher along the groove sidewall surface closer to the outer periphery of the drive roll 100, while other craters can be lower along the groove sidewall surface closer to the groove base. The rings of laser-formed craters within the circumferential grooves 106, 108 or between different grooves on the drive roll 100 may be at approximately the same radial distance from the central axis of the drive roll or at different radial distances. For example, the ring of laser-formed craters on the outer sidewall of the circumferential groove may be at a different radial distance and location along the sidewall than the ring of laser-formed craters on the inner sidewall of the groove. Laser surface finishing may also be applied along the groove base if desired. Thus, the groove base may include one or more rings of laser-formed craters in addition to the craters on the sidewalls of the grooves 106, 108. In certain embodiments, such as a drive roll for a single wire having U-shaped circumferential grooves, the laser-formed craters are provided exclusively along the groove base and not along the sidewalls.

[0020] 4 and 5, adjacent craters 114 in each ring of laser-formed craters overlap one another. The diameter of each crater 114 is slightly greater than the spacing between the central recesses 116 of each crater. However, the craters 114 need not overlap, and each crater may be spaced from each adjacent crater as desired. The size, spacing, number, etc. of the craters on the groove sidewalls can be determined based on the characteristics of the wire electrode driven by the drive roll (e.g., compressive strength) and the characteristics of the drive roll (e.g., friction caused by the groove surface finish).

[0021] FIG. 6 shows a partial cross section of an exemplary drive roll 111 having a U-shaped circumferential groove 113. The U-shaped groove 113 receives and drives the single-cored welding wire E1 of FIG. 6. The size (e.g., radius) of the two grooves 113 is closely matched to the diameter of the welding wire E1. The center or bottom of the circumferential groove 113 forms a groove base, and the side walls of the groove are recessed and extend from the groove base to the outer peripheral surface of the drive roll 111. The groove base and side walls may have the same radius or different radii. Surface finishes such as the laser-formed craters described above can be applied to one or more of the groove bases and each of the side walls. In one exemplary embodiment, a single ring of laser-formed craters is provided along the groove base at the bottom of each groove 113. The craters may overlap as shown in FIGS. 4 and 5, or may be spaced apart from one another.

[0022] FIG. 7 shows a schematic of the laser etching process performed on the side walls of the circumferential groove 108 of the drive roll 100. The surface finishing of the groove side walls can be completed in one revolution of the drive roll 100 or in multiple revolutions. Each groove side wall can receive a single surface finish (e.g., a single ring of laser-formed craters) or multiple surface finishes (e.g., multiple rings of laser-formed craters). Each groove side wall can be surface finished simultaneously by the same laser device 120 or by different laser devices. In certain embodiments, the same laser device 120 provides a surface finish to all four groove side walls and / or the groove base of the two circumferential grooves 106, 108 of the drive roll 100.

[0023] During a surface finishing operation, the drive roll 100 rotates at a given angular velocity while the laser device 120 pulses to irradiate portions of the circumferential grooves 106, 108 (e.g., sidewalls and / or groove base) with the laser beam 122. The energy of the laser beam pulses creates craters on the surfaces of the circumferential grooves 106, 108. The angular velocity of the drive roll 100 and the pulse frequency of the laser device 120 determine the number of craters in a given ring of craters on the sidewalls of the circumferential grooves 106, 108. The craters along the groove sidewalls or groove base can be created during one revolution of the drive roll 100 or during multiple revolutions of the drive roll. The laser device 120 can remain in a fixed position while performing the surface finishing on the groove sidewalls or can move to create craters at various radial distances along the sidewalls. The laser 120 need not be pulsed or can be pulsed intermittently during the surfacing operation to form ridges (e.g., stripes, corrugations, etc.) along the sidewalls or base of the groove. The size and depth of the craters, ridges, etc. formed by the laser 120 can be controlled or adjusted by adjusting the power or energy of the laser beam 122. The laser beam 122 may be directed perpendicular to the sidewalls or base of the circumferential groove to achieve surfacing, or at another angle relative to the sidewalls / base. The angle of the laser pulse relative to the groove walls may affect the shape of the crater. For example, a perpendicular laser pulse can be used to form a relatively uniform crater with a perimeter that is consistent in height. An oblique pulse can be used to form a crater with an uneven perimeter.

[0024] A drive roll 100 having two circumferential grooves 106, 108, and thus four sidewalls and / or two groove bases to be surfaced, can be laser etched relatively quickly, for example within a few seconds. If multiple laser devices 120 are used, various groove surfaces can be etched simultaneously. Alternatively, a single laser device 120 can sequentially surface finish each sidewall of the grooves 106, 108. The laser device 120 can also surface finish the groove bases, if necessary, by directing the laser beam 122 down to the bottom of the grooves.

[0025] In one exemplary embodiment, each crater or ring of craters in the surfacing has a diameter in the range of 0.020 to 0.050 inches, although other diameters are possible. If it is desired to overlap adjacent craters, the spacing between adjacent craters can be less than the diameter of the craters. If it is desired to space adjacent craters apart, the diameter of the craters should be less than the spacing between adjacent craters. The size of the craters is determined by the characteristics of the laser beam 122 (e.g., power and pulse duration), while the spacing between the craters is determined by the laser pulse frequency and the angular velocity of the drive roll 100 during the surfacing run.

[0026] In one exemplary embodiment, the drive roll 100 has a diameter of about 1-3 / 4 inches. The drive roll 100 can rotate for about 3 seconds while pulsing the laser at 20-60 Hz to form a ring of laser-formed craters along the sidewalls of the groove having between about 60 and 180 craters. The process can be repeated for each sidewall, resulting in a relatively quick surface finish of all four sidewalls of two circumferential grooves in about 12 seconds or less. Of course, other drive roll angular velocities and laser pulse frequencies are possible and are considered within the scope of the present invention.

[0027] In Figures 4 and 5, the crater 114 and each ring of craters are shown as being substantially centered along the sidewall of each circumferential groove 106, 108. However, it should be understood that the crater 114 need not be centered along the sidewall of the groove 106, 108, but may be located closer to the outer periphery of the drive roll 100 or closer to the groove base, if desired. The crater diameter in Figures 4 and 5 is greater than 50% of the width of the sidewall of the circumferential groove 106, 108. However, the crater 114 may have a smaller diameter, such as less than 50% of the width of the sidewall of the circumferential groove 106, 108. The diameter of the crater 114 can be controlled by the energy level of the laser pulse applied to the sidewall of the groove 106, 108.

[0028] FIG. 8 is a flow diagram of an exemplary method of surface finishing a welding wire drive roll. In step 200, a drive roll is provided as described above. The drive roll is rotated (e.g., one or more revolutions) while simultaneously irradiating a first sidewall of the first circumferential groove with a pulsed laser beam as described above (step 202). The drive roll is further rotated while simultaneously irradiating a second sidewall of the first circumferential groove with the pulsed laser beam (step 204). The drive roll is further rotated while simultaneously irradiating a first sidewall of the second circumferential groove with the pulsed laser beam (step 206). The drive roll is further rotated while simultaneously irradiating a second sidewall of the second circumferential groove with the pulsed laser beam (step 208). The surface finish forms at least one ring of craters on each sidewall of the circumferential wire drive groove.

[0029] A laser etching surface finishing process for the welding wire drive roll is discussed above. However, other surface finishing processes may be employed in addition to or in place of the laser etching process discussed above. For example, a thermal spray process may be used to apply powder to the surface of the drive roll. Thermal spray processes include laser powder, plasma spray powder, HVOF (high velocity oxygen fuel), or twin wire arc spray. The particle size of the powder can be controlled so that the surface adequately drives the welding wire while minimizing wire marking and deformation to alleviate feeding issues.

[0030] Another surface finishing process for welding wire drive rolls is hard particle embedded electroplating. Electroplating is used to create a coated surface with embedded hard particles such as tungsten carbide or diamond. Common electroplating substrates are nickel or chrome. The size of the embedded particles can be controlled to minimize surface damage to the driven wire.

[0031] Another surface finishing process for welding wire drive rolls involves applying a hard coating to the surface of the soft drive roll.

[0032] It will be apparent that the present disclosure is illustrative and that various modifications may be made by adding, modifying or removing details without departing from the fair scope of the subject matter contained herein. The invention is therefore not limited to the particular details of this disclosure except to the extent that the following claims are necessarily so limited. [Explanation of symbols]

[0033] 100 Driving Roll 102 Recess 104 Axis 106, 108 Circumferential groove 110 Side wall 111 Driving Roll 112 Groove base 113 Groove 114 Crater 116 Central recess 118 Outer area 120 Laser Device 122 Laser Beam E1,E2 Wire

Claims

1. In a welding wire drive roll including an outer circumferential surface and a circumferential groove protruding radially inward from the outer circumferential surface, the circumferential groove is a first sidewall having a first sidewall surface; a second sidewall having a second sidewall surface; formed from a groove base extending between the first sidewall and the second sidewall; the first sidewall surface includes a first surface finish including a first ring of laser-formed craters along the first sidewall surface formed by irradiating the first sidewall with at least one pulsed laser beam; the second sidewall surface includes a second surface finish including a second ring of laser-formed craters along the second sidewall surface formed by irradiating the second sidewall with at least one pulsed laser beam; a welding wire drive roll, wherein the first ring of laser formed craters has a first laser formed crater diameter in the range of 0.020 to 0.050 inches (0.0508 to 0.127 cm) and the second ring of laser formed craters has a second laser formed crater diameter in the range of 0.020 to 0.050 inches (0.0508 to 0.127 cm).

2. 2. The welding wire drive roll of claim 1, wherein adjacent craters of the first ring of laser-formed craters overlap and adjacent craters of the second ring of laser-formed craters overlap.

3. 2. The welding wire drive roll of claim 1, wherein the first ring of laser-formed craters and the second ring of laser-formed craters are located approximately the same radial distance from a central axis of the welding wire drive roll.

4. 2. The welding wire drive roll of claim 1, wherein a first ring of laser-formed craters is substantially centered along the first sidewall and a second ring of laser-formed craters is substantially centered along the second sidewall.

5. 2. The welding wire drive roll of claim 1, wherein each crater diameter of the first ring of laser-formed craters and the second ring of laser-formed craters is at least 50% of a width of the first sidewall and the second sidewall.

6. The welding wire drive roll of claim 1 , wherein the groove base is concave.

7. 2. The welding wire drive roll of claim 1 , wherein each crater in the first ring of laser-formed craters includes a central recess recessed into the first sidewall surface and a peripheral portion raised above the first sidewall surface.

8. 8. The welding wire drive roll of claim 7, wherein the outer periphery portion is formed from material displaced from the central recess.

9. The outer circumferential surface has a second circumferential groove protruding radially inward from the outer circumferential surface, and the second circumferential groove is a third sidewall having a third sidewall surface; a fourth sidewall having a fourth sidewall surface; formed from a second groove base extending between the third sidewall and the fourth sidewall; the third sidewall surface includes a third surface finish including a third ring of laser-formed craters along the third sidewall surface; 2. The welding wire drive roll of claim 1, wherein the fourth sidewall surface includes a fourth surface finish including a fourth ring of laser formed craters along the fourth sidewall surface.

10. 10. The welding wire drive roll of claim 9, wherein the first ring of laser-formed craters, the second ring of laser-formed craters, the third ring of laser-formed craters, and the fourth ring of laser-formed craters are located at substantially the same radial distance from a central axis of the welding wire drive roll.

11. A welding wire drive roll including an outer circumferential surface having a first circumferential groove and a second circumferential groove axially offset from the first circumferential groove, the first circumferential groove and the second circumferential groove both protruding radially inward from the outer circumferential surface, the first circumferential groove being: a first sidewall having a first sidewall surface; a second sidewall having a second sidewall surface; a first groove base extending between the first sidewall and the second sidewall; the first sidewall surface includes a first plurality of laser-formed craters arranged in an annular fashion along the first sidewall surface formed by irradiating the first sidewall with at least one pulsed laser beam, the first surface finishes each having a central recess recessed into the first sidewall surface and a peripheral portion elevated above the first sidewall surface; the second sidewall surface includes a second plurality of laser-formed craters arranged in an annular fashion along the second sidewall surface formed by irradiating the second sidewall with at least one pulsed laser beam, and each second surface finish has a central recess recessed into the second sidewall surface and a peripheral portion elevated above the second sidewall surface; The second circumferential groove is a third sidewall having a third sidewall surface; a fourth sidewall having a fourth sidewall surface; a second groove base extending between the third sidewall and the fourth sidewall; the third sidewall surface includes a third plurality of laser-formed craters arranged in an annular fashion along the third sidewall surface formed by irradiating the third sidewall with at least one pulsed laser beam, the third surface finishes each having a central recess recessed into the third sidewall surface and a peripheral portion elevated above the third sidewall surface; the fourth sidewall surface includes a fourth plurality of laser-formed craters arranged in an annular fashion along the fourth sidewall surface formed by irradiating the fourth sidewall surface with at least one pulsed laser beam, the fourth surface finishes each having a central recess recessed into the fourth sidewall surface and a peripheral portion elevated above the fourth sidewall surface; at least one of the first plurality of laser-formed craters has a first crater diameter in a range of 0.020 to 0.050 inches (0.0508 to 0.127 cm), at least one of the second plurality of laser-formed craters has a second crater diameter in a range of 0.020 to 0.050 inches (0.0508 to 0.127 cm), at least one of the third plurality of laser-formed craters has a third crater diameter in a range of 0.020 to 0.050 inches (0.0508 to 0.127 cm), and at least one of the fourth plurality of laser-formed craters has a fourth crater diameter in a range of 0.020 to 0.050 inches (0.0508 to 0.127 cm).

12. 12. The welding wire drive roll of claim 11, wherein the first plurality of laser-formed craters, the second plurality of laser-formed craters, the third plurality of laser-formed craters, and the fourth plurality of laser-formed craters are located at substantially the same radial distance from a central axis of the welding wire drive roll.

13. The welding wire drive roll of claim 12 , wherein adjacent craters in each annular array overlap.

14. the first plurality of laser-formed craters arranged in an annular pattern along the first sidewall surface are substantially centered along the first sidewall; the second plurality of laser-formed craters arranged in an annular pattern along the second sidewall surface are substantially centered along the second sidewall; the third plurality of laser-formed craters arranged in an annular pattern along the third sidewall surface are substantially centered along the third sidewall; 13. The welding wire drive roll of claim 12, wherein the fourth plurality of laser-formed craters arranged annularly along the fourth sidewall surface are substantially centered along the fourth sidewall.

15. 12. The welding wire drive roll of claim 11, wherein a crater diameter of the first plurality of laser-formed craters is at least 50% of a width of the first sidewall, a crater diameter of the second plurality of laser-formed craters is at least 50% of a width of the second sidewall, a crater diameter of the third plurality of laser-formed craters is at least 50% of a width of the third sidewall, and a crater diameter of the fourth plurality of laser-formed craters is at least 50% of a width of the fourth sidewall.

16. In a welding wire drive roll including an outer circumferential surface and a circumferential groove protruding radially inward from the outer circumferential surface, the circumferential groove is A first sidewall; and A second sidewall; and a groove base extending between the first sidewall and the second sidewall; at least one of the first sidewall, the second sidewall, and the groove base includes a surface finish including a ring of laser-formed craters along a surface of the at least one of the first sidewall, the second sidewall, and the groove base formed by irradiating the first sidewall, the second sidewall, or the groove base with at least one pulsed laser beam, a laser-formed first crater of the laser-formed craters having a diameter in the range of 0.020 to 0.050 inches (0.0508 to 0.127 cm).

17. 1. A method for finishing a welding wire drive roll, comprising the steps of: providing a welding wire drive roll, the welding wire drive roll including an outer circumferential surface having a circumferential groove projecting radially inwardly from the outer circumferential surface, the circumferential groove being defined by a first sidewall having a first sidewall surface, a second sidewall having a second sidewall surface, and a groove base extending between the first sidewall and the second sidewall; and rotating the welding wire drive roll while simultaneously irradiating the first sidewall with a pulsed laser beam to form a first ring of craters along the first sidewall surface, each of the craters having a diameter in the range of 0.020 to 0.050 inches (0.0508 to 0.127 cm) and at least 50% of a width of the first sidewall.

18. 18. The method of claim 17, wherein each crater in the first ring of craters includes a central recess recessed into the first sidewall surface and a peripheral portion raised above the first sidewall surface, the peripheral portion being formed by material displaced from the central recess.

19. 20. The method of claim 17, further comprising the step of forming a second ring of craters along the second sidewall surface by simultaneously rotating the welding wire drive roll while irradiating the second sidewall with a pulsed laser beam.

20. 20. The method of claim 19, wherein the first ring of craters and the second ring of craters are located at substantially the same radial distance from a central axis of the welding wire drive roll.

21. 21. The method of claim 20, wherein adjacent craters in the first ring of craters overlap and adjacent craters in the second ring of craters overlap.

Images