A kind of seaweed fiber electrostatic flocking fabric and its manufacturing method

Abstract

The invention discloses electrostatic flocking fabric made of alginate fibers. The electrostatic flocking fabric comprises a flock layer, an adhesive layer and a base cloth layer, wherein the flock layer is the alginate fibers; the base cloth layer is polyester 80 / 20 blended plain woven cloth; the middle adhesive layer is a polyacrylic acid flocking adhesive. The invention also discloses a preparation method of the electrostatic flocking fabric made of the alginate fibers. The preparation method comprises the following steps: cutting alginate fiber strands to prepare alginate fiber flock, and performing electric conduction and coloring treatment; pre-coating and mainly coating flocking base cloth with adhesives, wherein the total thickness of the adhesives is 0.2 to 0.25mm; in an electrostatic flocking room, orderly flocking the surface of the base cloth coated with the adhesives in a high-pressure alternating electrostatic field under the action of electric field force, and performing baking to firmly composite the flock with the base cloth so as to obtain the electrostatic flocking fabric. The electrostatic flocking fabric has a good flame resistance effect, has anti-bacterial and deodorization functions, is free from toxicity and harmless, can be naturally degraded, and is applied to interior decoration, functional seats and the like.

Description

technical field

[0001] The invention relates to a decorative electrostatic flocking fabric and a manufacturing method thereof, in particular to a seaweed fiber electrostatic flocking fabric and a manufacturing method thereof. . Background technique

[0002] The so-called flocking fabric, it uses all kinds of fabrics as the base fabric, the front is planted with nylon fluff or viscose fluff, and then processed by drying and washing. Most of the flocking fibers currently used are synthetic fiber materials, and natural fibers are used as planting materials. The fleece material is less, the environmental performance is poor, and it is easy to produce environmental pollution in the manufacturing process and later use. Simultaneously at present public place decoration fabrics such as hotel, hotel decoration fabrics, aircraft seat decoration fabrics etc. all require fabrics to have good flame-retardant properties, and the application of flocking fabrics aspect decoration fabrics i...

Examples

Embodiment 1

[0026] The fluff layer is a blended fiber of seaweed fiber and one or more of viscose, cotton and chemical fiber.

[0027] The manufacture method of above-mentioned a kind of seaweed fiber electrostatic flocking fabric, comprises the steps:

[0028] 1. Cut the seaweed fiber tow into fluff, and then conduct conductive treatment. The moisture content of the fluff is controlled at 8%, and the specific resistance is controlled at 3.6×10 8 Ω·㎝, made of seaweed fiber fluff with a length of 1 mm and a fineness of 1.8 denier.

[0029] 2. The flocking base fabric is made of polyester-cotton 80 / 20 blended plain weave fabric, and the base fabric is first coated with a layer of adhesive by scraping. The adhesive is polyacrylic acid plant produced by Shandong Lingchao New Material Co., Ltd. For velvet glue, the surface of the scraper is close to the surface of the base fabric, and then pre-baked, the temperature is 80-90°C, and the drying time is 1min. The surface of the fabric is beaut...

Embodiment 2

[0034] The fluff layer is a blended fiber of seaweed fiber and one or more of viscose, cotton and chemical fiber.

[0035] The manufacture method of above-mentioned a kind of seaweed fiber electrostatic flocking fabric, comprises the steps:

[0036] 1. Cut the seaweed fiber tow into fluff, and then conduct conductive treatment. The moisture content of the fluff is controlled at 10%, and the specific resistance is controlled at 3.6×10 9 Ω·cm, made into seaweed fiber fluff with a length of 1.2 mm and a fineness of 1.8 denier.

[0037] 2. The flocking base fabric is made of polyester-cotton 80 / 20 blended plain weave fabric, and the base fabric is first coated with a layer of adhesive by scraping. The adhesive is polyacrylic acid plant produced by Shandong Lingchao New Material Co., Ltd. Velvet glue, the surface of the scraper is close to the surface of the base cloth, and then pre-baked, the temperature is 80-90 ℃, and the drying time is 1.5 minutes. The surface of the fleece f...

Embodiment 3

[0042] The fluff layer is a blended fiber of seaweed fiber and one or more of viscose, cotton and chemical fiber.

[0043] The manufacture method of above-mentioned a kind of seaweed fiber electrostatic flocking fabric, comprises the steps:

[0044] 1. Cut the seaweed fiber tow into fluff, and then conduct conductive treatment. The moisture content of the fluff is controlled at 8%, and the specific resistance is controlled at 3.6×10 8 Ω·㎝, made of seaweed fiber fluff with a length of 1 mm and a fineness of 1.8 denier.

[0045] 2. The flocking base fabric is made of polyester-cotton 80 / 20 blended plain weave fabric, and the base fabric is first coated with a layer of adhesive by scraping. The adhesive is polyacrylic acid plant produced by Shandong Lingchao New Material Co., Ltd. For velvet glue, the surface of the scraper is close to the surface of the base fabric, and then pre-baked, the temperature is 80-90°C, and the drying time is 1min. The surface of the fabric is beaut...

technical field

[0001] The invention relates to a decorative electrostatic flocking fabric and a manufacturing method thereof, in particular to a seaweed fiber electrostatic flocking fabric and a manufacturing method thereof. . Background technique

[0002] The so-called flocking fabric, it uses all kinds of fabrics as the base fabric, the front is planted with nylon fluff or viscose fluff, and then processed by drying and washing. Most of the flocking fibers currently used are synthetic fiber materials, and natural fibers are used as planting materials. The fleece material is less, the environmental performance is poor, and it is easy to produce environmental pollution in the manufacturing process and later use. Simultaneously at present public place decoration fabrics such as hotel, hotel decoration fabrics, aircraft seat decoration fabrics etc. all require fabrics to have good flame-retardant properties, and the application of flocking fabrics aspect decoration fabrics i...

Examples

Embodiment 1

[0026] The fluff layer is a blended fiber of seaweed fiber and one or more of viscose, cotton and chemical fiber.

[0027] The manufacture method of above-mentioned a kind of seaweed fiber electrostatic flocking fabric, comprises the steps:

[0028] 1. Cut the seaweed fiber tow into fluff, and then conduct conductive treatment. The moisture content of the fluff is controlled at 8%, and the specific resistance is controlled at 3.6×10 8 Ω·㎝, made of seaweed fiber fluff with a length of 1 mm and a fineness of 1.8 denier.

[0029] 2. The flocking base fabric is made of polyester-cotton 80 / 20 blended plain weave fabric, and the base fabric is first coated with a layer of adhesive by scraping. The adhesive is polyacrylic acid plant produced by Shandong Lingchao New Material Co., Ltd. For velvet glue, the surface of the scraper is close to the surface of the base fabric, and then pre-baked, the temperature is 80-90°C, and the drying time is 1min. The surface of the fabric is beaut...

Embodiment 2

[0034] The fluff layer is a blended fiber of seaweed fiber and one or more of viscose, cotton and chemical fiber.

[0035] The manufacture method of above-mentioned a kind of seaweed fiber electrostatic flocking fabric, comprises the steps:

[0036] 1. Cut the seaweed fiber tow into fluff, and then conduct conductive treatment. The moisture content of the fluff is controlled at 10%, and the specific resistance is controlled at 3.6×10 9 Ω·cm, made into seaweed fiber fluff with a length of 1.2 mm and a fineness of 1.8 denier.

[0037] 2. The flocking base fabric is made of polyester-cotton 80 / 20 blended plain weave fabric, and the base fabric is first coated with a layer of adhesive by scraping. The adhesive is polyacrylic acid plant produced by Shandong Lingchao New Material Co., Ltd. Velvet glue, the surface of the scraper is close to the surface of the base cloth, and then pre-baked, the temperature is 80-90 ℃, and the drying time is 1.5 minutes. The surface of the fleece f...

Embodiment 3

[0042] The fluff layer is a blended fiber of seaweed fiber and one or more of viscose, cotton and chemical fiber.

[0043] The manufacture method of above-mentioned a kind of seaweed fiber electrostatic flocking fabric, comprises the steps:

[0044] 1. Cut the seaweed fiber tow into fluff, and then conduct conductive treatment. The moisture content of the fluff is controlled at 8%, and the specific resistance is controlled at 3.6×10 8 Ω·㎝, made of seaweed fiber fluff with a length of 1 mm and a fineness of 1.8 denier.

[0045] 2. The flocking base fabric is made of polyester-cotton 80 / 20 blended plain weave fabric, and the base fabric is first coated with a layer of adhesive by scraping. The adhesive is polyacrylic acid plant produced by Shandong Lingchao New Material Co., Ltd. For velvet glue, the surface of the scraper is close to the surface of the base fabric, and then pre-baked, the temperature is 80-90°C, and the drying time is 1min. The surface of the fabric is beaut...