A light brushed comfortable yoga wear fabric

Abstract

The application provides a light-pilling comfortable yoga suit fabric, characterized in that: polyester and spandex are used for fabric weaving; the woven fabric is subjected to post-treatment, so that the water absorption performance of the inner side and the outer side of the fabric is different. The fabric has strong water absorption and quick drying effects.

Description

TECHNICAL FIELD

[0001] The present application relates to the field of knitting, in particular, to a light fleece comfortable yoga suit fabric. BACKGROUND

[0002] The current yoga suit fabric selection material is mostly nylon, pearl fiber and other fibers interwoven blended, and the functions of the fabric are mostly given by different yarns, and most of the functional yarns are high in cost.

[0003] Although there are some yoga suits on the market made of polyester or polyester + spandex, the price of the polyester yoga suit is lower than that of nylon, and the polyester has good strength and wear resistance, but the breathability of the yoga suit made of such fabric is particularly limited, the moisture absorption and sweat wicking ability is poor, and the quick drying performance required by yoga itself cannot be realized, which is not suitable for wearing yoga in hot summer. SUMMARY

[0004] The present application aims to overcome the above-mentioned defects, and provides a light fleece comfortable yoga suit fabric with strong water absorption and quick drying effect.

[0005] The present application provides a light fleece comfortable yoga suit fabric, characterized in that:

[0006] The fabric is woven by polyester and spandex;

[0007] The fabric is post-treated to make the water absorption performance of the inner and outer sides of the fabric different;

[0008] Among them, the water absorption performance of the outer surface of the fabric is stronger than that of the inner surface of the fabric.

[0009] Further, the present application provides a light fleece comfortable yoga suit fabric, characterized in that:

[0010] The specific weaving method of the fabric is:

[0011] The double-sided machine is selected;

[0012] The needle arrangement mode of the upper needle plate is AB, and the needle arrangement mode of the lower needle plate is BA.

[0013] Further, the present application provides a light fleece comfortable yoga suit fabric, characterized in that:

[0014] The threading mode is: the first 1.2 way is polyester + spandex;

[0015] Among them, the upper needle is full of spandex.

[0016] Further, the present application provides a light fleece comfortable yoga suit fabric, characterized in that:

[0017] The double-sided machine is a 34'' 32G double-sided machine.

[0018] Further, the light fuzzing comfortable yoga suit fabric provided by the present application is characterized in that:

[0019] The light fuzzing treatment is a carbon fuzzing process.

[0020] Further, the light fuzzing comfortable yoga suit fabric provided by the present application is characterized in that:

[0021] The post-treatment comprises a process of performing a fuzzing treatment on the outer surface of the fabric.

[0022] Further, the light fuzzing comfortable yoga suit fabric provided by the present application is characterized in that:

[0023] After the woven fabric is dyed, shaped and dried, the light fuzzing treatment is performed to make the fabric form short and dense nap.

[0024] Effects and advantages of the present application:

[0025] Considering the performance requirements of the yoga suit, the yoga fabric is currently made of nylon and other materials, and the dyeing of nylon requires higher equipment and technical requirements than the dyeing of polyester, and the same is true for the interweaving of nylon and other fibers.

[0026] In the scheme of the present application, by adjusting the weaving method and post-treatment process, only functional polyester and antibacterial spandex are used for weaving to realize a fabric suitable for yoga suits, which reduces the production risk and equipment and technical requirements, and is low in cost.

[0027] In the scheme of the present application, light fuzzing is performed on the surface of the fabric in the dyeing and finishing of the fabric to achieve the purpose of improving the water absorption and drying speed. BRIEF DESCRIPTION OF DRAWINGS

[0028] Figure 1 The embodiment provides a needle arrangement diagram of a light fuzzing comfortable yoga suit fabric.

[0029] Figure 2 The embodiment provides a triangle diagram of a light fuzzing comfortable yoga suit fabric. DETAILED DESCRIPTION

[0030] The fabric production process is weaving-dyeing-shaping-surface light fuzzing-shaping-finished product.

[0031] The weaving process is as follows:

[0032] Yarn selection: 50D / 72F DTY functional polyester (cooling), 40D spandex (antibacterial spandex)

[0033] Needle arrangement is as follows Figure 1 The needle arrangement of the upper needle disc is AB, and the needle arrangement of the lower needle disc is BA.

[0034] Triangle arrangement is as follows Figure 2 ; the upper needle and the lower needle share one loop-forming-float-loop-forming-float, and the upper needle needs to be fully lined with spandex.

[0035] Yarn threading method: the first 1.2 is 50D / 72F functional polyester + 40D spandex, and the upper needle is fully lined with spandex, and the length of the two yarns is 11.4 cm*3 cm / 50N.

[0036] The above dyeing: conventional polyester dyeing is adopted;

[0037] The above light sanding: carbon sanding is adopted to make the outer surface of the fabric have short and dense nap, and enhance the water absorption and quick drying property.

[0038] The specific performance is as follows:

[0039] Moisture absorption is tested according to GB / T21655.1-2008, and the test results are as follows: before washing, the air permeability and moisture conductivity is <1s, the water absorption rate is 276%, the wicking height is 168mm straight and 156.0mm transversely, the evaporation rate is 0.23g / h, and the moisture permeability is 1.00*10 4 g / (m 2 24h);

[0040] After washing, the air permeability and moisture conductivity is <1s, the water absorption rate is 265%, the wicking height is 167mm straight and 157.0mm transversely, the evaporation rate is 0.22g / h, and the moisture permeability is 1.01*10 4 g / (m 2 24h).

[0041] Comparative example:

[0042] Common polyester fabric for yoga clothes on the market

[0043] Moisture absorption is tested according to GB / T21655.1-2008, and the test results are as follows: the air permeability and moisture conductivity is <3s, the water absorption rate is 246%, the wicking height is 155mm straight and 146.0mm transversely, the evaporation rate is 0.19g / h, and the moisture permeability is 1.00*10 4 g / (m 2 24h)

[0044] From the comparison of the two groups of data, it can be found that although the comparative product can also meet the standard test indicators, its water absorption and drying performance is obviously poorer than that of the product of the embodiment.

[0045] In the scheme of the embodiment, due to the special weaving process, light brushing is performed on the surface of the fabric, so that the water absorption performance of the inner and outer sides of the fabric is different, which enables the sweat on the skin surface to be transmitted from the inside to the outside more quickly, thereby enhancing the wearing comfort of the garment.

Claims

1. A light brushed comfortable yoga wear fabric, characterized in that: polyester and spandex are used for fabric weaving; the woven fabric is post-processed to make the water absorption performance of the inner and outer sides of the fabric different; wherein the water absorption performance of the outer surface of the fabric is stronger than that of the inner surface of the fabric; the post-processing includes a process of light brushing treatment on the outer surface of the fabric.

2. A light brushed comfort yoga wear fabric as claimed in claim 1, wherein: The light brushing treatment is a carbon brushing process.

3. A light brushed comfort yoga wear fabric as claimed in claim 1, wherein: The specific weaving method of the fabric is: selecting a double face machine; the needle arrangement mode of the upper needle disc is AB, and the needle arrangement mode of the lower needle disc is BA.

4. A light brushed comfort yoga garment fabric as claimed in claim 3, wherein: The threading mode is: the first 1.2 way is polyester + spandex; wherein the upper needle is full of spandex.

5. A light brushed comfort yoga garment fabric as claimed in claim 3, wherein: The double face machine is a 34" 32G double face machine.

6. The light brushed comfortable yoga wear fabric of claim 1, characterized in that: after the woven fabric is dyed, shaped and dried, light brushing treatment is performed to make the fabric form short and dense pile.