Loofah wood pulp cotton formula and preparation method thereof

Abstract

The invention provides a loofah wood pulp cotton formula and a preparation method thereof, and relates to the technical field of loofah wood pulp cotton, the loofah wood pulp cotton formula comprises loofah sponge fibers and wood pulp cotton, and the loofah wood pulp cotton formula comprises 40-60% of loofah sponge fibers and 40-60% of wood pulp cotton. The preparation method of the loofah wood pulp cotton formula comprises the specific steps of raw material pretreatment, mixing, forming and drying. The cleaning agent has the advantages of being good in cleaning effect, high in water absorption, high in obdurability, good in environmental protection performance and the like. When being used for cleaning various articles, the towel gourd wood pulp cotton can achieve a good cleaning effect on oil stains, dust and other stubborn stains. The loofah wood pulp cotton can quickly absorb a large amount of water and has excellent performance in cleaning scenes such as wiping water spots. The loofah wood pulp cotton is not easy to damage in the repeated use process, and the service life is greatly prolonged. The towel gourd wood pulp cotton can be naturally degraded after being discarded, does not cause pollution to the environment, and conforms to the modern environmental protection concept.

Description

Technical Field

[0001] The invention relates to the technical field of loofah wood pulp cotton, and in particular to a loofah wood pulp cotton formula and a preparation method thereof. Background Art

[0002] At present, common cleaning products on the market, such as sponges and ordinary wood pulp cotton, have problems such as poor cleaning effect, poor durability, and insufficient environmental performance. Sponges are prone to breeding bacteria during use, and have limited cleaning ability for stubborn stains; although ordinary wood pulp cotton has certain water absorption, it lacks toughness and is easily damaged after repeated use, and has a short service life. With the improvement of people's living standards and the enhancement of environmental awareness, higher requirements are placed on the performance and environmental protection of cleaning products, and a new type of loofah wood pulp cotton is needed. Summary of the Invention

[0003] The objective of the invention is to overcome the shortcomings in the prior art and to provide a loofah wood pulp cotton formula and a preparation method thereof. The technical solution adopted in the present invention is:

[0004] A loofah wood pulp cotton formula and a preparation method thereof include: the loofah wood pulp cotton formula comprises loofah fiber and wood pulp cotton, and the ratio of the loofah wood pulp cotton formula is: 40%-60% of loofah fiber and 40%-60% of wood pulp cotton.

[0005] A preparation method of a loofah wood pulp cotton formula. According to the above-mentioned loofah wood pulp cotton formula, the preparation method of the loofah wood pulp cotton formula specifically comprises the steps of raw material pretreatment, mixing, molding and drying.

[0006] As an improvement, the specific steps of the raw material pretreatment are: selecting mature loofah, removing the skin and seeds, cleaning the loofah and drying it naturally, and then crushing the dried loofah into fibers through a crushing device to obtain loofah fibers; screening the wood pulp cotton raw materials to remove impurities and unqualified parts and set aside.

[0007] As an improvement, the specific steps of mixing are: according to the mass ratio of 40%-60% of cucurbit fiber and 40%-60% of wood pulp cotton, the processed cucurbit fiber and wood pulp cotton are put into a mixing device, and they are fully stirred and mixed to make the two raw materials evenly mixed together.

[0008] As an improvement, the specific steps of forming are: passing the evenly mixed raw materials through a bonding forming device to form a loofah wood pulp cotton semi-finished product according to actual use requirements.

[0009] As an improvement, the drying step includes: placing the formed loofah wood pulp cotton semi-finished product into a drying device, drying it under suitable temperature and humidity conditions to remove excess moisture in the raw material and obtain finished loofah wood pulp cotton.

[0010] The beneficial effects of the present invention are:

[0011] The invention discloses a loofah wood pulp cotton formula and a preparation method thereof, which has the advantages of good cleaning effect, strong water absorption, high strength and toughness, good environmental protection performance, and the like. DETAILED DESCRIPTION

[0012] In order to make the contents of the present invention more clearly understood, the technical solutions in the embodiments of the present invention will be clearly and completely described below in combination with the embodiments of the present invention.

[0013] The loofah wood pulp cotton formula comprises loofah fiber and wood pulp cotton, and the proportion of the loofah wood pulp cotton formula is: 40%-60% of loofah fiber and 40%-60% of wood pulp cotton.

[0014] This application has the advantages of good cleaning effect, strong water absorption, high strength and toughness, and good environmental performance.

[0015] Good cleaning effect: The loofah fiber has a natural porous structure and rough surface, which can effectively absorb and remove stains on the surface of objects. Combined with the water absorption and cleaning ability of wood pulp cotton, the loofah wood pulp cotton can achieve good cleaning effect when cleaning various items, whether it is oil, dust or other stubborn stains.

[0016] Strong water absorption: Wood pulp cotton itself has excellent water absorption performance. After being mixed with melon fiber, the overall water absorption is further improved. It can quickly absorb a large amount of water and performs well in cleaning scenarios such as wiping water stains.

[0017] High strength and toughness: loofah fiber has high toughness and strength. After mixing with wood pulp cotton, it makes up for the defect of insufficient toughness of wood pulp cotton, making the prepared loofah wood pulp cotton not easy to be damaged during repeated use, greatly extending its service life.

[0018] Good environmental performance: Guarana fiber is a natural plant fiber, and wood pulp cotton has less pollution to the environment during the production process. Both can be naturally degraded after being discarded, and will not cause pollution to the environment, which is in line with modern environmental protection concepts.

[0019] During the preparation process, 10 kg of mature loofahs are selected, the skin and seeds are removed, the loofahs are soaked in clean water for 2 hours, then scrubbed clean with a brush, and placed in a well-ventilated place to dry naturally for 7 days. The dried loofahs are placed in a grinder and ground into fibers with a length of about 0.5-1 cm to obtain loofah fibers; 10 kg of high-quality wood pulp cotton raw materials are selected, screened through a sieve to remove impurities and fine particles therein, and set aside.

[0020] The obtained guar fiber and the screened wood pulp cotton were put into a blender at a mass ratio of 1:1, and stirred at a speed of 200 r / min for 15 minutes to fully mix the two raw materials.

[0021] The evenly mixed raw materials are placed in a mold of a flat vulcanizer and pressed for 10 minutes at a temperature of 80°C and a pressure of 5 MPa to produce a sheet-like loofah wood pulp cotton semi-finished product with a thickness of 1 cm and a size of 20 cm×30 cm.

[0022] The semi-finished loofah wood pulp cotton sheet is placed in a drying oven and dried at a temperature of 60° C. for 5 hours to remove moisture therein, thereby obtaining a finished loofah wood pulp cotton sheet.

[0023] The above are only preferred embodiments of the present invention and are not intended to limit the present invention. Any modifications, equivalent substitutions, and improvements made within the spirit and principles of the present invention shall be included in the scope of protection of the present invention.

Claims

1. A loofah wood pulp cotton formula, characterized in that, The loofah wood pulp cotton formula comprises loofah fiber and wood pulp cotton, and the proportion of the loofah wood pulp cotton formula is: 40%-60% of loofah fiber and 40%-60% of wood pulp cotton.

2. A method for preparing a loofah wood pulp cotton formula, the loofah wood pulp cotton formula according to claim 1, characterized in that, The preparation method of the loofah wood pulp cotton formula specifically comprises the following steps: raw material pretreatment, mixing, molding and drying.

3. The preparation method of a loofah wood pulp cotton formula according to claim 2, wherein The specific steps of the raw material pretreatment are: selecting mature loofah, removing the skin and seeds, cleaning the loofah and drying it naturally, and then crushing the dried loofah into fibers through a crushing device to obtain loofah fibers; screening the wood pulp cotton raw materials, removing impurities and unqualified parts, and setting aside.

4. A loofah wood pulp cotton formula and preparation method according to claim 2, characterized in that, The specific steps of mixing are: according to the mass ratio of 40%-60% of cucurbit fiber and 40%-60% of wood pulp cotton, the processed cucurbit fiber and wood pulp cotton are put into a mixing device, and the two raw materials are fully stirred and mixed to be evenly mixed together.

5. A loofah wood pulp cotton formula and preparation method thereof according to claim 2, characterized in that, The specific steps of forming are: passing the evenly mixed raw materials through bonding and forming equipment to form the loofah wood pulp cotton semi-finished product according to actual use requirements.

6. A loofah wood pulp cotton formula and preparation method thereof according to claim 2, characterized in that, The drying step includes: placing the formed semi-finished loofah wood pulp cotton product into a drying device, performing a drying process under suitable temperature and humidity conditions, removing excess water in the raw material, and obtaining a finished loofah wood pulp cotton product.