Phenylene ether oligomers and curable thermoset compositions containing phenylene ether oligomers - Patents.com

Abstract

The linear difunctional phenylene ether oligomers include repeat units derived from 2-methyl-6-cyclohexylphenol and have (meth)acrylate end groups. The linear difunctional phenylene ether oligomers can be particularly useful in curable compositions, thermoset compositions, and articles formed therefrom.

Description

[Technical field]

[0001] This disclosure relates to endcapped phenylene ether oligomers, methods for forming same, curable thermoset compositions containing same, and articles derived therefrom. [Background technology]

[0002] Thermosetting resins are materials that cure to form ultra-hard plastics. These materials can be used in a wide variety of consumer and industrial products. For example, thermosetting materials are used in protective coatings, adhesives, electronic laminates (such as those used in making computer circuit boards), flooring and paving applications, fiberglass reinforced pipes, and automotive parts (including leaf springs, pumps, and electrical components). Poly(arylene ether) copolymers generally have good dielectric properties. Due to their widespread use, especially in electronic applications, such as laminates for printed circuit boards, it is desirable to provide curable thermosetting compositions containing poly(arylene ether) copolymers that have lower viscosity while maintaining or improving dielectric constant, dissipation factor, heat resistance, and water absorption. Summary of the Invention [Problem to be solved by the invention]

[0003] Thus, there remains a need in the art for end-capped arylene ether polymers and oligomers that have a desirable set of properties for use in curable thermosetting compositions. It would be further advantageous if the capped arylene ether materials could provide curable thermosetting compositions with improved dielectric constants, dissipation factors, heat resistance, and water absorption. [Means for solving the problem]

[0004] Linear difunctional phenylene ether oligomers are provided that contain repeat units derived from 2-methyl-6-cyclohexylphenol and have (meth)acrylate end groups.

[0005] Also provided is a process for forming a linear difunctional phenylene ether oligomer, comprising the steps of oxidatively polymerizing 2-methyl-6-cyclohexylphenol in the presence of a catalyst to obtain a phenylene ether oligomer, and reacting the phenylene ether oligomer with a (meth)acrylate-containing compound to obtain the linear difunctional phenylene ether oligomer.

[0006] Additionally provided are curable thermoset compositions comprising the linear difunctional phenylene ether oligomers and articles derived from the curable thermoset compositions.

[0007] These and other features are illustrated in the following detailed description. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0008] The present inventors have conveniently discovered that phenylene ether oligomers derived from 2-methyl-6-cyclohexylphenol and end-capped with (meth)acrylate groups can be included in a curable thermosetting composition that achieves improved properties over thermosetting compositions that include phenylene ether oligomers that do not have repeat units derived from 2-methyl-6-cyclohexylphenol. For example, phenylene ether oligomers derived from 2-methyl-6-cyclohexylphenol can provide an improved combination of properties, such as solution viscosity, dissipation factor, resin flow, and dielectric constant.

[0009] Accordingly, an embodiment of the present disclosure is a linear difunctional phenylene ether oligomer comprising repeat units derived from 2-methyl-6-cyclohexylphenol, such that the phenylene ether oligomer comprises repeat units having the structure: [ka]

[0010] The oligomer may consist of the repeat units derived from 2-methyl-6-cyclohexylphenol, or may contain repeat units derived from a monohydric phenol other than 2-methyl-6-cyclohexylphenol. If the oligomer contains additional repeat units, the phenylene ether oligomer contains less than 30 weight percent (based on the total weight of the phenylene ether oligomer) of repeat units derived from a monohydric phenol having identical substituents at the 2- and 6-positions (e.g., 2,6-dimethylphenol, 2,3,6-dimethylphenol, etc., or combinations thereof). Preferably, the phenylene ether oligomer contains less than 20 weight percent, or less than 15 weight percent, or less than 10 weight percent, or less than 5 weight percent, or less than 2 weight percent, or less than 1 weight percent, or less than 0.5 weight percent, or less than 0.1 weight percent of repeat units derived from a monohydric phenol having identical substituents at the 2- and 6-positions. The oligomer may not contain repeat units derived from a monohydric phenol having identical substituents at the 2- and 6-positions. In one embodiment, the phenylene ether oligomers of the present disclosure exclude repeat units derived from 2-cyclohexylphenol.

[0011] The phenylene ether oligomer further comprises a (meth)acrylate end group. Thus, the phenylene ether oligomer has an end group having the structure: [ka] wherein R is hydrogen or methyl. In one embodiment, R is a methyl group and the phenylene ether oligomer comprises a methacrylate end group. In one embodiment, R is hydrogen and the phenylene ether oligomer comprises an acrylate end group.

[0012] The phenylene ether oligomer has a linear structure and is difunctional. "Difunctional" as used herein means that the phenylene ether oligomer has a functional group at both ends of the oligomer chain. Difunctional oligomers with functional groups at both ends of the oligomer chain are also called "telechelic" oligomers. Thus, the phenylene ether oligomer has, on average, two functional end groups (i.e., (meth)acrylate groups) per oligomer chain. For example, the difunctional oligomer has at least 1.5 to 2, or at least 1.70 to 2, or at least 1.8 to 2, or at least 1.9 to 2, or at least 1.95 to 2 (meth)acrylate groups / molecule, or up to 1.99 (meth)acrylate groups / molecule.

[0013] In one embodiment, the phenylene ether oligomer has the structure: [ka] In the formula, R 1 and R 2 are each independently halogen, unsubstituted or substituted C 1-12 Primary or secondary hydrocarbyl, C 1-12 Hydrocarbylthio, C 1-12 Hydrocarbyloxy, or C 2-12 halohydrocarbyloxy, where at least two carbon atoms separate the halogen and oxygen atoms, and R 3 and R 4 Each event is independently hydrogen, halogen, unsubstituted or substituted C 1-12 Primary or secondary hydrocarbyl, C 1-12 Hydrocarbylthio, C 1-12 Hydrocarbyloxy, or C 2-12halohydrocarbyloxy, where at least two carbon atoms separate the halogen and oxygen atoms, x and y are independently from 0 to 30, preferably from 0 to 20, more preferably from 0 to 15, even more preferably from 0 to 10, and even more preferably from 0 to 8, with the proviso that the sum of x and y is at least 2, preferably at least 3, and more preferably at least 4, and Y has a structure comprising: [ka] In the formula, R 7 Each event is independently hydrogen or C 1-12 is hydrocarbyl, R 8 and R 9 Each event is independently hydrogen, C 1-12 Hydrocarbyl, or C 1-6 is hydrocarbylene, R 8 and R 9 are collectively C 4-12 It forms an alkylene group, and z is 0 or 1.

[0014] In one embodiment, the phenylene ether oligomer has the structure: [ka] In the formula, R 1 -R 4 is as defined above.

[0015] In one embodiment, the phenylene ether oligomer has the structure: [ka] In the formula, R 1 -R 4 is as defined above.

[0016] In one embodiment, R 1 and R 2 Each event is methyl, and R 3 and R4 are hydrogen, z is 1, and Y is an isopropylidene group, and the phenylene ether oligomer has the structure: [ka]

[0017] In one embodiment, R 1 and R 2 Each event is methyl, and R 3 and R 4 are hydrogen, z is 1, and Y is an isopropylidene group, and the phenylene ether oligomer has the structure: [ka]

[0018] The phenylene ether oligomers of the present disclosure can be prepared by oxidatively polymerizing 2-methyl-6-cyclohexylphenol in the presence of a catalyst to provide a phenylene ether oligomer. The phenylene ether oligomers can be formed by polymerization of monomers including 2-methyl-6-phenylphenol and a dihydric phenol by the sequential addition of oxygen to a reaction mixture including the monomers, a solvent, and a polymerization catalyst.

[0019] Dihydric phenols have the structure: [ka] (4) In the formula, R 1 From R 4 , Y 1 , and z is as defined above.

[0020] For example, dihydric phenols include 1,1-bis(3,5-dimethyl-4-hydroxyphenyl)ethane, 1,1-bis(3-chloro-4-hydroxyphenyl)ethane, 1,1-bis(3-methyl-4-hydroxyphenyl)ethane, 1,2-bis(4-hydroxy-3,5-dimethylphenyl)-1,2-diphenylethane, 1,2-bis(3-methyl-4-hydroxyphenyl)-1,2-diphenylethane, 1,2-bis(3-methyl-4-hydroxyphenyl)ethane, 2,2'-binaphthol, 2,2'-biphenol, 2,2'-dihydro 2,2'-dihydroxy-4,4'-dimethoxybenzophenone, 2,2'-dihydroxy-4-methoxybenzophenone, 2,2'-dihydroxybenzophenone, 2,2-bis(3,5-dichloro-4-hydroxyphenyl)propane, 2,2-bis(3-bromo-4-hydroxyphenyl)propane, 2,2-bis(3-phenyl-4-hydroxyphenyl)propane, 2,2-bis(3-methyl-4-hydroxyphenyl)propane, 2,2-bis(3,5-dimethyl-4-hydroxyphenyl)propane, 1,1-bis(3,5-dimethyl-4-hydroxyphenyl)propane 1,1-bis(3-chloro-4-hydroxyphenyl)-1-phenylethane, 1,1-bis(3-methyl-4-hydroxyphenyl)-1-phenylethane, 2,2-bis(4-hydroxy-3,5-dimethylphenyl)-1-phenylpropane, 2,2-bis(4-hydroxy-3,5-dimethylphenyl)hexane, 2,2-bis(4-hydroxy-3,5-dimethylphenyl)pentane, 2,2-bis(3-methyl-4-hydroxynaphthyl)propane, 2,2-bis(3-methyl-4-hydroxyphenyl) -1-phenylpropane, 2,2-bis(3-methyl-4-hydroxyphenyl)hexane, 2,2-bis(3-methyl-4-hydroxyphenyl)pentane, 2,2'-methylenebis(4-methylphenol), 2,2'-methylenebis[4-methyl-6-(1-methylcyclohexyl)phenol], 3,3',5,5'-tetramethyl-4,4'-biphenol, 3,3'-dimethyl-4,4'-biphenol, bis(2-hydroxyphenyl)-methane, bis(4-hydroxy-2,6-dimethyl-3-methoxyphenyl)methane, bis(3,5-dimethyl-4-hydroxyphenyl)methane, bis(3-methyl-4-hydroxyphenyl)methane, bis-(4-hydroxy-3,5-dimethylphenyl)-cyclohexylmethane, bis(4-hydroxy-3,5-dimethylphenyl)phenylmethane, bis(3-methyl-4-hydroxyphenyl)cyclohexylmethane, bis(3-methyl-4-hydroxyphenyl)methane, bis(3,5-dimethyl-4-hydroxyphenyl)methane, bis(3-methyl-4-hydroxyphenyl)phenylmethane, 2,2',3,3',5,5'-hexamethyl-4,4'-biphenol, octafluoro-4,4'-biphenol, 2,3,3',5,5'-pentamethyl-4,4'-biphenol phenol, 1,1-bis(3,5-dibromo-4-hydroxyphenyl)cyclohexane, 1,1-bis(3,5-dimethyl-4-hydroxyphenyl)cyclohexane, bis(3-methyl-4-hydroxyphenyl)cyclohexane, tetrabromobisphenol, tetrabromobisphenol A, tetrabromobisphenol S, 2,2'-diallyl-4,4'-bisphenol A, 2,2'-diallyl-4,4'-bisphenol S, 3,3',5,5'-tetramethyl-4,4'-bisphenol sulfide, 3,3'-dimethyl bisphenol sulfide, 3,3',5,5'-tetramethyl-4,4'-bisphenol sulfone, or a combination thereof.

[0021] Molecular oxygen (O2) can be provided as air or pure oxygen. The polymerization catalyst is a metal complex containing a transition metal cation. The metal cation can include ions from Groups VIB, VIIB, VIIIB, or IB of the periodic table, or combinations thereof. Among these, chromium, manganese, cobalt, copper, and combinations comprising at least one of the foregoing ions can be used. In one embodiment, the metal ion is a copper ion (Cu + and Cu 2+). Metal salts that can serve as the metal cation source include cuprous chloride, cupric chloride, cuprous bromide, cupric bromide, cuprous iodide, cupric iodide, cuprous sulfate, cupric sulfate, cuprous tetraamine sulfate, cuprous acetate, cupric acetate, cuprous propionate, cupric butyrate, cupric laurate, cuprous palmitate, cuprous benzoate, and the corresponding manganese and cobalt salts. Instead of using any of the above-exemplified metal salts, it is also possible to add a metal or metal oxide and an inorganic acid, an organic acid, or an aqueous solution of such an acid to form the corresponding metal salt or hydrate in situ. For example, cuprous oxide and hydrobromic acid can be added to generate cuprous bromide in situ.

[0022] The polymerization catalyst further comprises at least one amine ligand. The amine ligand can be, for example, a monoamine, an alkylenediamine, or a combination comprising at least one of the foregoing. The monoamine comprises a dialkyl monoamine (e.g., di-n-butylamine, or DBA) and a trialkyl monoamine (e.g., N,N-dimethylbutylamine, or DMBA). The diamine comprises an alkylenediamine, for example, N,N'-di-tert-butylethylenediamine, or DBEDA. Suitable dialkyl monoamines include dimethylamine, di-n-propylamine, di-n-butylamine, di-sec-butylamine, di-tert-butylamine, dipentylamine, dihexylamine, dioctylamine, didecylamine, dibenzylamine, methylethylamine, methylbutylamine, dicyclohexylamine, N-phenylethanolamine, N-(p-methyl)phenylethanolamine, N-(2,6-dimethyl)phenylethanolamine, N-(p-chloro)phenylethanolamine, N-ethylaniline, N-butylaniline, N-methyl-2-methylaniline, N-methyl-2,6-dimethylaniline, diphenylamine, and the like, or combinations thereof. Suitable trialkyl monoamines include trimethylamine, triethylamine, tripropylamine, tributylamine, butyldimethylamine, phenyldiethylamine, and the like, or combinations thereof.

[0023] Suitable alkylenediamines include those having the formula: (R d )2N-R c -N(R d )2 In the formula, R c is a substituted or unsubstituted divalent residue, and each R d are independently hydrogen or C 1-8 In some examples of the above formula, two or three aliphatic carbon atoms form the nearest bond between the two diamine nitrogen atoms. Specific alkylenediamine ligands include R cR is dimethylene (-CH2CH2-) or trimethylene (-CH2CH2CH2-). d are independently hydrogen, methyl, propyl, isopropyl, butyl, or C 4-8 It may be an α-tertiary alkyl group. Examples of alkylenediamine ligands include N,N,N',N'-tetramethylethylenediamine (TMED), N,N'-di-tert-butylethylenediamine (DBEDA), N,N,N',N'-tetramethyl-1,3-diaminopropane (TMPD), N-methyl-1,3-diaminopropane, N,N'-dimethyl-1,3-diaminopropane, N,N,N'-dimethyl-1,3-diaminopropane, N-ethyl-1,3-diaminopropane, N-methyl-1,4-diaminobutane, N,N'-trimethyl-1,4-diaminobutane, N,N,N'-trimethyl-1,4-diaminobutane, N,N,N',N'-tetramethyl-1,4-diaminobutane, N,N,N',N'-tetramethyl-1,5-diaminopentane, or combinations thereof. In one embodiment, the amine ligand is di-n-butylamine (DBA), N,N-dimethylbutylamine (DMBA), N,N'-di-tert-butylethylenediamine (DBEDA), or a combination thereof. The catalyst can be prepared in situ by mixing a metal ion source (e.g., cuprous oxide and hydrobromic acid) with the amine ligand. In one embodiment, the polymerization catalyst includes copper ions, bromide ions, and N,N'-di-tert-butylethylenediamine.

[0024] The method of making a functionalized phenylene ether oligomer further includes reacting a phenylene ether oligomer (e.g., an "uncapped" hydroxyl-terminated phenylene ether oligomer) with a compound comprising a (meth)acrylate group to provide a functionalized phenylene ether oligomer. For example, the method can include reacting a hydroxyl-terminated phenylene ether oligomer with (meth)acryloyl chloride. The reaction between the phenylene ether oligomer and the compound comprising a (meth)acrylate group can be in a solvent. In some embodiments, the phenylene ether oligomer can be obtained as a powder, which is subsequently combined with the compound comprising a (meth)acrylate group and a solvent. In other embodiments, the uncapped phenylene ether oligomer can be obtained from the oxidative polymerization reaction as a solution without removing the solvent, and the uncapped phenylene ether oligomer is not isolated as a powder from the solvent solution. For example, a compound containing a (meth)acrylate group can be added directly to a solution of uncapped phenylene ether oligomers obtained directly from oxidative polymerization of 2-methyl-6-cyclohexylphenol and a dihydric phenol in a solvent, in which case the solvent is not removed from the reaction product before reacting with the compound containing a (meth)acrylate group. An exemplary synthesis is further described in the examples below. Suitable compounds containing a (meth)acrylate group and a group reactive with a hydroxyl-terminated phenylene ether oligomer can be easily determined by those skilled in the art.

[0025] The phenylene ether oligomers can have a number average molecular weight (Mn) of 600 to 5,000 grams / mole, for example, 600 to 3,500 grams / mole, or 1,000 to 5,000 grams / mole, or 1,000 to 3,500 grams / mole. The number average molecular weight can be determined, for example, by gel permeation chromatography against a polystyrene standard.

[0026] The phenylene ether oligomers of the present disclosure may have an intrinsic viscosity of less than 0.15 deciliters / gram, or from 0.02 to 0.15 deciliters / gram, or from 0.03 to 0.10 deciliters / gram, or from 0.035 to 0.075 deciliters / gram, as measured in chloroform at 25° C. using an Ubbelohde viscometer.

[0027] Also provided is a curable thermosetting composition comprising a linear difunctional phenylene ether oligomer having (meth)acrylate end groups. For example, the difunctional phenylene ether oligomer can be present in the curable thermosetting composition in an amount of 1 to 95 weight percent (wt%), or 5 to 95 wt%, or 10 to 85 wt%, or 20 to 80 wt%, or 30 to 70 wt%, or 5 to 30 wt%, or 5 to 15 wt%, based on the total weight of the curable thermosetting composition.

[0028] The curable thermosetting composition may further include one or more crosslinking agents, curing agents, curing catalysts, curing initiators, or combinations thereof. In some embodiments, the curable thermosetting composition may further include one or more flame retardants, fillers, coupling agents, or combinations thereof. For example, the curable thermosetting composition may include one or more crosslinking agents, curing agents, curing catalysts, curing initiators, or combinations thereof, and may further include one or more flame retardants, fillers, coupling agents, or combinations thereof.

[0029] There is considerable overlap between thermosetting resins, crosslinking agents, and coupling agents. As used herein, the term "crosslinking agent" includes compounds that can be used as thermosetting resins, crosslinking agents, coupling agents, or combinations thereof. For example, in some cases, a compound that is a thermosetting resin can also be used as a crosslinking agent, a coupling agent, or both.

[0030] The thermosetting resin is not particularly limited, and the thermosetting resin can be used alone or in combination of two or more thermosetting resins (e.g., including one or more auxiliary thermosetting resins). Exemplary thermosetting resins include epoxy resins, cyanate ester resins, (bis)maleimide resins, (poly)benzoxazine resins, vinyl resins (e.g., vinylbenzyl ether resins), phenolic resins, alkyd resins, unsaturated polyester resins, arylcyclobutene resins, perfluorovinyl ether resins, monomers, oligomers or polymers having curable unsaturation (e.g., vinyl functionality), and the like, or combinations thereof.

[0031] The epoxy resin can generally be any epoxy resin suitable for use in thermosetting resins. The term "epoxy resin" in this context refers to a curable composition of oxirane ring-containing compounds, for example, as described in CA May, Epoxy Resins, Second Supplementary Edition, (New York & Basle: Marcel Dekker Inc.), 1988. The epoxy resins may include bisphenol A type epoxy resins, such as those obtained from bisphenol A and those obtained by substituting at least one of the 2-, 3- and 5-positions of bisphenol A with a halogen atom, an alkyl group having 6 or less carbon atoms, or a phenyl group; bisphenol F type epoxy resins, such as those obtained from bisphenol F and those obtained by substituting at least one of the 2-, 3- and 5-positions of bisphenol F with a halogen atom, an alkyl group having 6 or less carbon atoms, or a phenyl group; glycidyl ether compounds derived from divalent or higher valent phenols, such as hydroquinone, resorcinol, tris-4-(hydroxyphenyl)methane, and 1,1,2,2-tetrakis(4-hydroxyphenyl)ethane; phenols, such as phenol and o-cresol, which are reaction products between formaldehyde; Novolac type epoxy resins derived from volac resins, such as bisphenol A novolac type epoxy resins and cresol novolac type epoxy resins, cycloaliphatic epoxy compounds, such as 2,2-bis(3,4-epoxycyclohexyl)propane, 2,2-bis[4-(2,3-epoxypropyl)cyclohexyl]propane, vinylcyclohexene dioxide, 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate, dicyclopentadiene-containing polyepoxides, aniline, p-aminophenol, m-aminophenol, 4-amino-m-cresol, 6-amino-m-cresol, 4,4'-diaminodiphenyl-ethane, 3,3'-diaminodiphenylmethane, 4,4'-diaminodiphenylether, 3,4'-diaminodiphenylether, 1,4-bis(4-aminophenoxy)benzene, 1,4-bis(3-aminophenoxy)-benzene, 1,Amine-type epoxy resins derived from 3-bis(4-aminophenoxy)-benzene, 1,3-bis(3-aminophenoxy)benzene, 2,2-bis(4-amino-phenoxyphenyl)propane, p-phenylenediamine, m-phenylenediamine, 2,4-toluenediamine, 2,6-toluenediamine, p-xylylene-diamine, m-xylylenediamine, 1,4-cyclohexane-bis(methylamine), 5-amino-1-(4'-aminophenyl)-1,3,3-trimethylindane, 6-amino-1-(4'-aminophenyl)-1,3,3-trimethyl-indane, etc., heterocyclic epoxy compounds, and glycidyl ester-type epoxy compounds, for example, those derived from glycidyl esters of aromatic carboxylic acids, for example, p-oxybenzoic acid, m-oxybenzoic acid, terephthalic acid, and isophthalic acid. "Epoxy resin" can also include the reaction product of a compound containing two or more epoxy groups and an aromatic dihydroxy compound, which can be optionally halogen-substituted and can be used alone or in combination of two or more.

[0032] The cyanate ester is not limited, and any resin made of cyanate ester monomers (polymerized to form a polymer containing multiple cyanate ester (-OCN) functional groups) can be used. Cyanate ester monomers, prepolymers (i.e., partially polymerized cyanate ester monomers or blends of cyanate ester monomers), homopolymers, and copolymers made with cyanate ester precursors, and combinations of these compounds. For example, cyanate esters can be prepared according to the methods disclosed in "Chemistry and Technology of Cyanate Ester Resins" by Ian Hamerton, Blackie Academic and Professional, U.S. Patent No. 3,553,244, and JP-A-7-53497. Exemplary cyanate ester resins include 2,2-bis(4-cyanatophenyl)-propane, bis(4-cyanatophenyl)ethane, bis(3,5-dimethyl-4-cyanatophenyl)methane, 2,2-bis(4-cyanatophenyl)-1,1,1,3,3,3-hexafluoropropane, α,α'-bis(4-cyanatophenyl)-m-diisopropyl-benzene, cyanate ester resins prepared from dicyclopentadiene-phenol copolymers, and prepolymers prepared from these monomers. An example of a prepolymer is PRIMASET BA-230S (Lonza). The cyanate ester prepolymers can be homopolymers or can be copolymers incorporating other monomers. Examples of such copolymers include BT resins available from Mitsubishi Gas Chemical, such as BT2160 and BT2170, which are prepolymers made with cyanate ester and bismaleimide monomers. Other cyanate ester polymers, monomers, prepolymers, and blends of cyanate ester monomers with other non-cyanate ester monomers are disclosed in US7393904, US7388057, US7276563, and US7192651.

[0033] Bismaleimide resins can be formed by reaction of a monomeric bismaleimide with a nucleophile such as a diamine, aminophenol, or aminobenzhydrazide, or by reaction of a bismaleimide with diallyl bisphenol A.Exemplary bismaleimide resins include 1,2-bismaleimidoethane, 1,6-bismaleimidohexane, 1,3-bismaleimidobenzene, 1,4-bismaleimido-benzene, 2,4-bismaleimidotoluene, 4,4'-bismaleimidodiphenylmethane, 4,4'-bismaleimido-diphenyl ether, 3,3'-bismaleimidodiphenyl sulfone, 4,4'-bismaleimido-diphenyl sulfone, 4,4'-bismaleimidodicyclohexylmethane, 3,5-bis(4-maleimidophenyl) Pyridine, 2,6-bismaleimido-pyridine, 1,3-bis(maleimidomethyl)cyclohexane, 1,3-bis(maleimidomethyl)benzene, 1,1-bis(4-maleimidophenyl)cyclohexane, 1,3-bis(dichloromaleimido)benzene, 4,4'-bis(citracon-imido)diphenylmethane, 2,2-bis(4-maleimidophenyl)propane, 1-phenyl-1,1-bis(4-maleimido-phenyl)ethane, N,N-bis(4-maleimidophenyl)toluene, 3,5-bismaleimido-pyridine, 1,3-bis(maleimidomethyl)cyclohexane, 1,3-bis(dichloromaleimido)benzene, 4,4'-bis(citracon-imido)diphenylmethane, 2,2-bis(4-maleimidophenyl)propane, 1-phenyl-1,1-bis(4-maleimido-phenyl)ethane, N,N-bis(4-maleimidophenyl)toluene, mido-1,2,4-triazole N,N'-ethylene bismaleimide, N,N'-hexamethylene bismaleimide, N,N'-m-phenylene bismaleimide, N,N'-p-phenylene bismaleimide, N,N'-4,4'-diphenylmethane bismaleimide, N,N'-4,4'-diphenylether bismaleimide, N,N'-4,4'-diphenylsufone bismaleimide, N,N'-4,4'-dicyclohexylmethane bismaleimide, Included are N,N'-α,α'-4,4'-dimethylenecyclohexane bismaleimide, N,N'-m-meta-xylene-bismaleimide, N,N'-4,4'-diphenylcyclohexane bismaleimide, and N,N'-methylene-bis(3-chloro-p-phenylene) bismaleimide, as well as those disclosed in US 3,562,223, US 4,211,860, and US 4,211,861, or prepared by the methods described, for example, in US 3,018,290.

[0034] Benzoxazine compounds have a benzoxazine ring in the molecule. Exemplary benzoxazine monomers can be prepared from the reaction of aldehydes, phenols, and primary amines with or without solvent. Phenolic compounds for forming benzoxazines include phenols and polyphenols. The use of polyphenols with two or more reactive hydroxyl groups in the formation of benzoxazines can result in branched, crosslinked, or combined branched crosslinked products. The group linking the phenolic group in the phenol can be a branch point or linking group in the polybenzoxazine.

[0035] Exemplary phenols for use in preparing the benzoxazine monomers include phenol, cresol, resorcinol, catechol, hydroquinone, 2-allylphenol, 3-allylphenol, 4-allylphenol, 2,6-dihydroxynaphthalene, 2,7-dihydroxynaphthalene, 2-(diphenyl-phosphoryl)hydroquinone, 2,2'-biphenol, 4,4-biphenol, 4,4'-isopropylidenediphenol, 4,4'-isopropylidenebis(2-methyl-phenol), 4,4'-isopropylidenebis(2-allylphenol), 4,4'(1,3-phenylenediisopropylidene)bisphenol (bisphenol M), 4,4'-isopropylidenebis(3-phenylenediisopropylidene)bisphenol, and the like. phenol), 4,4'-(1,4-phenylenediisopropylidene)-bisphenol, 4,4'-ethylidene diphenol, 4,4'-oxydiphenol, 4,4'-thiodiphenol, 4,4'-sulfonyldiphenol, 4,4'-sulfinyldiphenol, 4,4'-(hexafluoroisopropylidene)bisphenol, 4,4'(1-phenylethylidene)-bisphenol, bis(4-hydroxyphenyl)-2,2-dichloroethylene, bis(4-hydroxyphenyl)methane, 4,4'-(cyclopentylidene)diphenol, 4,4'-(cyclohexylidene)diphenol, 4,4'-(cyclododecylidene)diphenol, 4,4'-(bicyclo[2.2.1]heptylidene)diphenol, 4,4'-(9H-fluorene-9,9-diyl)diphenol, isopropylidene-bis(2-allylphenol), 3,3-bis(4-hydroxyphenyl)isobenzofuran-1(3H)-one, 1-(4-hydroxyphenyl)-3,3-dimethyl-2,3-dihydro-1H-inden-5-ol, 3,3,3',3'-tetramethyl-2,2',3,3'-tetrahydro-1,1'-spirobi-[indene]5,6'-diol, dihydroxa Examples of dibenzophenone include tris(4-hydroxyphenyl)methane, tris(4-hydroxy-phenyl)ethane, tris(4-hydroxyphenyl)propane, tris(4-hydroxyphenyl)butane, tris(3-methyl-4-hydroxyphenyl)methane, tetrakis(4-hydroxyphenyl)ethane, dicyclopentadienyl bis(2,6-dimethylphenol), dicyclopentadienyl bis(ortho-cresol), dicyclopentadienyl bisphenol, and the like.

[0036] The aldehyde used to form the benzoxazine can be any aldehyde, for example, an aldehyde having 1 to 10 carbon atoms. For example, the aldehyde can be formaldehyde. The amine used to form the benzoxazine can be an aromatic amine, an aliphatic amine, an alkyl-substituted aromatic, or an aromatic-substituted alkylamine. The amine can be, for example, a polyamine to prepare a multifunctional benzoxazine monomer for crosslinking.

[0037] The amines for forming the benzoxazines have from 1 to 40 carbon atoms if they do not contain aromatic rings, and thus they can have from 6 to 40 carbon atoms. Difunctional or polyfunctional amines can be branching points linking one polybenzoxazine to another.

[0038] In some embodiments, thermal polymerization at 150 to 300° C. can be used to polymerize the benzoxazine monomers. The polymerization can be carried out in bulk, from solution, or otherwise. A catalyst such as a carboxylic acid can be used to reduce the polymerization temperature or to accelerate the polymerization rate at the same temperature.

[0039] Vinylbenzyl ether resins can be prepared from the condensation of phenols with vinylbenzyl halides such as vinylbenzyl chloride. Bisphenol-A and trisphenols and polyphenols are commonly used to produce poly(vinylbenzyl ethers), which can be used to produce crosslinked thermosetting resins. Exemplary vinylbenzyl ethers are the condensation of vinylbenzyl halides with resorcinol, catechol, hydroquinone, 2,6-dihydroxynaphthalene, 2,7-dihydroxynaphthalene, 2-(diphenyl-phosphoryl)hydroquinone, bis(2,6-dimethylphenol), 2,2'-biphenol, 4,4-biphenol, 2,2',6,6'-tetramethylbiphenol, 2,2',3,3',6,6'-hexamethylbiphenol, 3,3',5,5'-tetrabromo -2,2'6,6'-tetramethylbiphenol, 3,3'-dibromo-2,2',6,6'-tetramethylbiphenol, 2,2',6,6'-tetramethyl-3,3'5-dibromobiphenol, 4,4'-isopropylidenediphenol, 4,4'-isopropylidenebis(2,6-dibromophenol), 4,4'-isopropylidenebis(2,6-dimethylphenol) (tetramethylbisphenol A), 4,4'-isopropylidenebis(2-methylphenol) phenol), 4,4'-isopropylidene bis(2-allylphenol), 4,4'(1,3-phenylenediisopropylidene)bisphenol, 4,4'-isopropylidenebis(3-phenylphenol), 4,4'-(1,4-phenylenediisopropylidene)bisphenol, 4,4'-ethylidene di-phenol, 4,4'-oxydiphenol, 4,4'-thiodiphenol, 4,4'-thiobisphenol (2,6-dimethylphenol), 4,4'-sulfonyldi-phenol, 4,4'-sulfonylbis(2,6-dimethylphenol) 4,4'-sulfinyl-diphenol, 4,4'-hexafluoroisopropylidenebisphenol, 4,4'(1-phenylethylidene)bisphenol, bis(4-hydroxyphenyl)-2,2-dichloro-ethylene, bis(4-hydroxyphenyl)methane, bis(2,6-dimethyl-4-hydroxyphenyl)methane, 4,4'-(cyclopentylidene)diphenol, 4,4'-(cyclohexylidene)diphenol, 4,4'-(cyclododecylidene)diphenol, 4,4'-(bicyclo[2.2.1]heptylidene)diphenol, 4,4'-(9H-fluorene-9,9-diyl)diphenol, 3,3-bis(4-hydroxyphenyl)-isobenzofuran-1(3H)-one, 1-(4-hydroxyphenyl)-3,3-dimethyl-2,3-dihydro-1H-inden-5-ol, 1-(4-hydroxy-3,5-dimethylphenyl)-1,3,3,4,6-pentamethyl-2,3-dihydro-1H-inden-5-ol, 3,3,3',3'-tetramethyl-2,2',3,3'-tetrahydro-1,1'-spirobi[indene]-5, These may include those vinyl benzyl ethers produced from reaction with 6'-diol, dihydroxybenzophenone, tris(4-hydroxyphenyl)methane, tris(4-hydroxyphenyl)ethane, tris(4-hydroxyphenyl)-propane, tris(4-hydroxyphenyl)butane, tris(3-methyl-4-hydroxyphenyl)methane, tris(3,5-dimethyl-4-hydroxy-phenyl)methane, tetrakis(4-hydroxyphenyl)ethane, tetrakis(3,5-dimethyl-4-hydroxyphenyl)-ethane, bis(4-hydroxyphenyl)phenylphosphine oxide, dicyclopentadienyl-bis(2,6-dimethylphenol), dicyclopentadienyl bisphenol, and the like.

[0040] Arylcyclobutenes include those derived from compounds of the structure: [ka] where B is an organic or inorganic radical of valence n (carbonyl, sulfonyl, sulfinyl, sulfide, oxy, alkylphosphonyl, arylphosphonyl, isoalkylidene, cycloalkylidene, arylalkylidene, diarylmethylidene, methylidenedialkylsilanyl, arylalkylsilanyl, diarylsilanyl and C 6-20(including phenolic compounds), each occurrence of X is independently hydroxy or C 1-24 hydrocarbyl (including linear and branched alkyl and cycloalkyl), and each occurrence of Z is independently hydrogen, halogen, or C 1-12 hydrocarbyl and n is 1 to 1000, or 1 to 8, or n is 2, 3, or 4. Other exemplary arylcyclobutenes and methods of synthesizing arylcyclobutenes can be found in US 4,743,399, US 4,540,763, US 4,642,329, US 4,661,193, US 4,724,260, and 5391,650.

[0041] Perfluorovinyl ethers are typically synthesized from phenol and bromotetrafluoroethane, followed by zinc-catalyzed reductive elimination to produce ZnFBr and the desired perfluorovinyl ether. By this route, bis-, tris-, and other polyphenols can be synthesized to produce bis-, tris-, and poly(perfluorovinyl ethers). Phenols useful in their synthesis include resorcinol, catechol, hydroquinone, 2,6-dihydroxynaphthalene, 2,7-dihydroxynapthalene, 2-(diphenyl-phosphoryl)hydroquinone, bis(2,6-dimethylphenol), 2,2'-biphenol, 4,4-biphenol, 2,2',6,6'-tetramethylbiphenol, 2,2',3,3',6,6'-hexamethylbiphenol, 3,3' ,5,5'-tetrabromo-2,2',6,6'-tetramethylbiphenol, 3,3'-dibromo-2,2',6,6'-tetramethylbiphenol, 2,2',6,6'-tetramethyl-3,3',5-dibromobiphenol, 4,4'-isopropylidenediphenol (bisphenol A), 4,4'-isopropylidenebis(2,6-dibromophenol), 4,4'-isopropylidenebis(2,6-dimethylphenol), 4,4'-isopropylidenebis(2,6-dimethylphenol), 4,4'-(1,4-phenylenediisopropylidene)-bisphenol, 4,4'-ethylidene diphenol, 4,4'-oxydiphenol, 4,4'-thiodiphenol, 4,4 'Thiobis(2,6-dimethylphenol), 4,4'-sulfonyldiphenol, 4,4'-sulfonylbis(2,6-dimethylphenol) 4,4'-sulfinyldiphenol, 4,4'-hexafluoroisopropylidene bisphenol, 4,4'(1-phenylethylidene)-bisphenol, bis(4-hydroxyphenyl)-2,2-dichloroethylene, bis(4-hydroxyphenyl)-methane, bis(2,6-Dimethyl-4-hydroxyphenyl)methane, 4,4'-(cyclopentylidene)diphenol, 4,4'-(cyclohexylidene)diphenol, 4,4'-(cyclododecylidene)diphenol, 4,4'-(bicyclo[2.2.1]heptylidene)-diphenol, 4,4'-(9H-fluorene-9,9-diyl)diphenol, 3,3-bis(4-hydroxyphenyl)isobenzofuran-1(3H)-one, 1-(4-hydroxyphenyl)-3,3-dimethyl-2,3-dihydro-1H-inden-5-ol, 1-(4-hydroxy-3,5-dimethylphenyl)-1,3,3,4,6-pentamethyl-2,3-dihydro-1H-inden-5-ol, 3,3,3',3'-tetramethyl-2,2',3,3'-tetrahydro-1,1'-spiro[4-hydroxyphenyl]isobenzofuran-1(3H)-one, Spirobiindene-5,6'-diol (spirobiindane), dihydroxybenzophenone, tris(4-hydroxyphenyl)methane, tris(4-hydroxyphenyl)ethane, tris(4-hydroxyphenyl)propane, tris(4-hydroxyphenyl)butane, tris(3-methyl-4-hydroxyphenyl)methane, tris(3,5-dimethyl-4-hydroxyphenyl)methane, tetrakis(4-hydroxyphenyl)ethane, tetrakis(3,5-dimethyl-4-hydroxyphenyl)ethane, bis(4-hydroxyphenyl)-phenylphosphine oxide, dicyclopentadienyl bis(2,6-dimethylphenol), dicyclopentadienyl bis(2-methylphenol), dicyclopentadienyl bisphenol, etc.

[0042] The crosslinking agent includes, but is not limited to, a co-crosslinking agent. The crosslinking agent can be used alone or in combination with two or more different crosslinking agents. Exemplary crosslinking agents and co-crosslinking agents include oligomers or polymers with curable vinyl functionality. Such materials include oligomers and polymers with crosslinkable unsaturation. Examples include styrene butadiene rubber (SBR), butadiene rubber (BR), and nitrile butadiene rubber (NBR) having unsaturated bonds based on butadiene, natural rubber (NR), isoprene rubber (IR), chloroprene rubber (CR), butyl rubber (IIR), and halogenated butyl rubber having unsaturated bonds based on isoprene, ethylene-α-olefin copolymer elastomers having unsaturated bonds based on dicyclopentadiene (DCPD), ethylidene norbornene (ENB), or 1,4-dihexadiene (1,4-HD) (e.g., ethylene-α-olefin copolymers obtained by copolymerizing ethylene, α-olefins, and dienes, such as ethylene-propylene-diene terpolymer (EPDM) and ethylene-butene-diene terpolymer (EBDM)). Examples also include hydrogenated nitrile rubber, fluorocarbon rubber, such as vinylidene fluoride-hexafluoropropene copolymer and vinylidene fluoride-pentafluoropropene copolymer, epichlorohydrin homopolymer (CO), copolymer rubber prepared from epichlorohydrin and ethylene oxide (ECO), epichlorohydrin allyl glycidyl copolymer, propylene oxide allyl glycidyl ether copolymer, propylene oxide epichlorohydrin allyl glycidyl ether terpolymer, acrylic rubber (ACM), urethane rubber (U), silicone rubber (Q), chlorosulfonated polyethylene rubber (CSM), polysulfide rubber (T) and ethylene acrylic rubber. Further examples include various liquid rubbers, such as several types of liquid butadiene rubber, and liquid atactic butadiene rubber, which is a butadiene polymer with 1,2-vinyl linkages prepared by anionic living polymerization.It is also possible to use liquid styrene butadiene rubber, liquid nitrile butadiene rubber (CTBN, VTBN, ATBN, etc., by Ube Industries, Ltd.), liquid chloroprene rubber, liquid polyisoprene, dicyclopentadiene-type hydrocarbon polymers, and polynorbornene (sold, for example, by Elf Atochem).

[0043] Polybutadiene resins containing high levels of 1,2 addition are desirable for the thermosetting matrix. Examples include functionalized polybutadienes and poly(butadiene-styrene) random copolymers sold under the trade names RICON, RICACRYL, and RICOBOND resins by Ricon Resins, Inc. These include butadienes containing both low vinyl content, e.g., RICON 130, 131, 134, 142, polybutadienes containing high vinyl content, e.g., RICON 150, 152, 153, 154, 156, 157, and P30D, random copolymers of styrene and butadiene, e.g., RICON 100, 181, 184, and maleic anhydride grafted polybutadienes and alcohol condensates derived therefrom, e.g., RICON 130MA8, RICON MA13, RICON 130MA20, RICON 131MAS, RICON 131MA10, RICON MA17, RICON MA20, RICON 184MA6, and RICON 156MA17. Also included are polybutadienes that can be used to improve adhesion, such as RICOBOND 1031, RICOBOND 1731, RICOBOND 2031, RICACRYL 3500, RICOBOND 1756, RICACRYL 3500, polybutadiene RICON 104 (25% polybutadiene in heptane), RICON 257 (35% polybutadiene in styrene), and RICON 257 (35% polybutadiene in styrene), (meth)acrylic-functionalized polybutadienes, such as polybutadiene diacrylate and polybutadiene dimethacrylate. These materials are sold under the trade names RICACRYL 3100, RICACRYL 3500, and RICACRYL 3801. Also included are powder dispersions of functional polybutadiene derivatives such as, for example, RICON 150D, 152D, 153D, 154D, P30D, RICOBOND 01731HS, and RICOBOND 1756HS.Further butadiene resins include poly(butadiene-isoprene) block and random copolymers, such as those having a molecular weight of 3,000 to 50,000 g / mol, and polybutadiene homopolymers having a molecular weight of 3,000 to 50,000 g / mol.Also included are polybutadienes, polyisoprenes, and polybutadiene-isoprene copolymers functionalized with maleic anhydride, 2-hydroxyethylmaleic acid, or hydroxylated functional groups.

[0044] Further examples of curable vinyl-functional oligomers and polymers include unsaturated polyester resins based on maleic anhydride, fumaric acid, itaconic acid and citraconic acid, unsaturated epoxy (meth)acrylate resins containing acryloyl or methacryloyl groups, unsaturated epoxy resins containing vinyl or allyl groups, urethane (meth)acrylate resins, polyether (meth)acrylate resins, polyalcohol (meth)acrylate resins, alkyd acrylate resins, polyester acrylate resins, spiroacetal acrylate resins, diallyl phthalate resins, diallyl tetrabromophthalate resins, diethylene glycol bisallyl carbonate resins, and polyethylene polythiol resins. For example, crosslinking agents. Other exemplary crosslinking agents further include multifunctional crosslinking monomers, for example (meth)acrylate monomers having two or more (meth)acrylate moieties per monomer molecule. Exemplary multifunctional monomers include di(meth)acrylates, such as 1,6-hexanediol di(meth)acrylate, 1,4-cyclohexanediol di(meth)acrylate, tripropylene glycol di(meth)acrylate, neopentyl glycol di(meth)acrylate, neopentyl glycol propoxylate di(meth)acrylate, neopentyl glycol ethoxylate di(meth)acrylate, neopentyl glycol propoxylate di(meth)acrylate, neopentyl glycol ethoxylate di(meth)acrylate, polyethylene glycol di(meth)acrylate, glycerol di(meth)acrylate, and the like; tri(meth)acrylates, such as trimethylolpropane tri(meth)acrylate, 1,2,4-butanetriol tri(meth)acrylate, trimethylolpropane ethoxylate tri(meth)acrylate, etc.; tri(meth)allyl, for example, tri(meth)allyl cyanurate, tri(meth)allyl isocyanurate, tri(meth)allyl ester of citric acid, tri(meth)allyl ester of phosphoric acid, pentaerythritol tri(meth)acrylate, tris(hydroxyethyl)isocyanurate tri(meth)acrylate, etc.; tetra(meth)acrylate, for example, pentaerythritol tetra(meth)acrylate, etc.; penta(meth)acrylates, such as dipentaerythritol penta(meth)acrylate, hexa(meth)acrylates, such as dipentaerythritol hexa(meth)acrylate, sorbitol hexa(meth)acrylate, glycidyl compounds, such as glycidyl(meth)acrylate, (meth)allyl glycidyl ether, 1-chloro-2,3-epoxypropyl(meth)acrylate, 2-bromo-3,4-epoxybutyl(meth)acrylate, 2-(epoxyethyloxy)-ethyl(meth)acrylate, 2-(3,4-epoxybutyloxy)-ethyl (meth)acrylate, etc.; polythiol compounds, for example, trimethylolpropane tris(mercaptopropionate), pentaerythritol tetrakis(3-mercaptopropionate), etc.; silanes, for example, tetramethoxysilane, tetraethoxysilane, tetrapropoxysilane, tetra-n-butoxysilane, vinyltris(methylethyloxyimino)silane, vinyltris-(acetoxime)silane, methyltris(methylethyloxyimino)silane, methyltris(acetoxime) ) silane, vinyltrimethoxysilane, methyltrimethoxysilane, vinyltris(isopropenoxy)silane, tetraacetoxysilane, methyltriacetoxysilane, ethyltriacetoxysilane, vinyltriacetoxysilane, di-t-butoxy-diacetoxysilane, methyltris(ethyllactate)silane, vinyltris(ethyllactate)silane, etc., carbodiimides, such as N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride, dicyclohexylcarbodiimide, etc., or combinations thereof. The curable thermosetting composition can optionally include a crosslinking catalyst, such as a carboxylate.

[0045] When the curable thermosetting composition includes a crosslinking agent, the crosslinking agent can be included in an amount of 1 to 60 wt%, or 5 to 45 wt%, or 10 to 30 wt%, based on the total weight of the curable thermosetting composition.

[0046] Curable thermosetting compositions can include one or more curing agents. As used herein, the term "curing agent" includes compounds variously referred to as curing agents, hardeners, etc., or both.

[0047] Exemplary curing agents and hardeners include amines, alcohols, phenols, carboxylic acids, acid anhydrides, etc. For example, phenolic hardeners include novolac-type phenolic resins, resole-type phenolic resins, cresol novolac resins, aralkyl-type phenolic resins, phenol aralkyl resins, cresol aralkyl resins, naphthol aralkyl resins, dicyclopentadiene-type phenolic resins, terpene-modified phenolic resins, biphenyl-type phenolic resins, biphenyl-modified phenol aralkyl resins, bisphenols, triphenylmethane-type phenolic resins, tetraphenylol ethane resins, naphthol novolac resins, naphthol-phenol co-condensed novolac resins, naphthol-cresol co-condensed novolac resins, aminotriazine-modified phenolic resins, or combinations thereof. Examples of anhydride hardeners include methylhexahydrophthalic anhydride (MHHPA), methyltetrahydrophthalic anhydride, styrene-maleic anhydride copolymer (SMA), and olefin-maleic anhydride copolymers, such as maleic anhydride grafted polyethylene, maleic anhydride grafted polypropylene, or combinations thereof. Other hardeners and hardeners include compounds such as dicyandiamide, polyamides, amidoamines, phenalkamines, Mannich bases, anhydrides, phenol-formaldehyde resins, amine-formaldehyde resins, phenol-formaldehyde resins, carboxylic acid functional polyesters, polysulfides, polymercaptans, isocyanates, cyanate ester compounds, or any combination thereof. Other exemplary hardeners include tertiary amines, Lewis acids, and oligomers or polymers with unsaturation.

[0048] When the curable thermosetting composition includes a curing agent, the curing agent can be included in an amount of 0.01 to 50 wt%, or 0.1 to 30 wt%, or 0.1 to 20 wt%, based on the total weight of the curable thermosetting composition.

[0049] Curable thermosetting compositions can include a curing catalyst. As used herein, the term "curing catalyst" includes compounds variously referred to as cure accelerators, cure promoters, cure catalysts, and cure cocatalysts.

[0050] Exemplary cure accelerators include, for example, substituted or unsubstituted C 3-6Heterocyclic accelerators include those that contain a heterocycle, where each heteroatom is independently the same or different and is nitrogen, oxygen, phosphorus, silicon, or sulfur. Heterocyclic accelerators include benzotriazoles, triazines, piperazines such as aminoethylpiperazine, N-(3-aminopropyl)piperazine, etc., imidazoles such as 1-methylimidazole, 2-methylimidazole, 3-methylimidazole, 4-methylimidazole, 5-methylimidazole, 1-ethylimidazole, 2-ethylimidazole, 3-ethylimidazole, 4-ethylimidazole, 5-ethylimidazole, 1-n-propylimidazole, 2-n-propylimidazole, 1-isopropylimidazole, 2-isopropylimidazole, 1-n-butylimidazole, 2-n-butylimidazole, 1-isobutylimidazole, 2-isobutylimidazole, 2-undecyl-1H-imidazole, 2-heptadecyl-1H-imidazole, 1,2-dimethylimidazole, 1,3-dimethylimidazole, 2,4-dimethylimidazole, 2-ethyl-4-methylimidazole Midazole, 1-phenylimidazole, 2-phenyl-1H-imidazole, 4-methyl-2-phenyl-1H-imidazole, 2-phenyl-4-methylimidazole, 1-benzyl-2-methylimidazole, 1-benzyl-2-phenylimidazole, 1-cyanoethyl-2-methylimidazole, 1-cyanoethyl-2-ethyl-4-methylimidazole, 1-cyanoethyl-2-undecylimidazole, 1-cyanoethyl-2-phenylimidazole, 2-phenyl-4,5-dihydroxymethylimidazole, 2-phenyl-4-methyl-5-hydroxymethylimidazole, 1-cyanoethyl-2-phenyl-4,5-di(2-cyanoethoxy)methylimidazole, cyclic amidines such as 4-diazabicyclo(2,2,2)octane, diazabicycloundecene, 2-phenylimidazoline, etc., N,N-dimethylaminopyridine, sulfamidate, or combinations thereof.

[0051] Amine cure accelerators include: isophorone diamine, triethylenetetraamine, diethylenetriamine, 1,2- and 1,3-diaminopropane, 2,2-dimethylpropylenediamine, 1,4-diaminobutane, 1,6-diaminohexane, 1,7-diaminoheptane, 1,8-diaminooctane, 1,9-diaminononane, 1,12-diaminododecane, 4-azaheptamethylenediamine, N,N'-bis(3-aminopropyl)butane-1,4-diamine, dicyanamide, diaminodiphenylmethane ... Phenylsulfonic acid (amine adduct), 4,4'-methylenedianiline, diethyltoluenediamine, m-phenylenediamine, p-phenylenediamine, melamine formaldehyde resin, urea formaldehyde resin, tetraethylenepentamine, 3-diethylaminopropylamine, 3,3'-iminobispropylamine, 2,4-bis(p-aminobenzyl)aniline, tetraethylenepentamine, 3-diethylaminopropylamine, 2,2,4- and 2,4,4-trimethylhexamethylenediamine, 1,2- and 1,3-diamine diaminocyclohexane, 1,4-diamino-3,6-diethylcyclohexane, 1,2-diamino-4-ethylcyclohexane, 1,4-diamino-3,6-diethylcyclohexane, 1-cyclohexyl-3,4-diaminocyclohexane, 4,4'-diaminodicyclohexylmethane, 4,4'-diaminodicyclohexylpropane, 2,2-bis(4-aminocyclohexyl)propane, 3,3'-dimethyl-4,4'-diaminodicyclohexyl Cyclohexylmethane, 3-amino-1-cyclohexaneaminopropane, 1,3- and 1,4-bis(aminomethyl)cyclohexane, m- and p-xylylenediamine, or diethyltoluenediamine, or tertiary amine cure accelerators, such as triethylamine, tributylamine, dimethylaniline, diethylaniline, benzyldimethylamine (BDMA), α-methylbenzyldimethylamine, N,N-dimethylaminopyridine, N,N-dimethylaminoethanol, N,N-dimethylaminocresol, or tri(N,N-dimethylaminomethyl)phenol, or a combination thereof.

[0052] The cure accelerator can be a latent cationic cure catalyst, such as, for example, diaryliodonium salts, phosphonate esters, sulfonate esters, carboxylate esters, phosphonylidenes, triarylsulfonium salts, benzylsulfonium salts, aryldiazonium salts, benzylpyridinium salts, benzylammonium salts, isoxazolium salts, and the like, or combinations thereof. Diaryliodonium salts are those having the structure [(R 10 )(R 11 )I] + X - wherein R 10 and R 11 are each independently optionally 1-20 Alkyl, C 1-20 C substituted with one to four monovalent radicals selected from alkoxy, nitro, and chloro; 6-14 is a monovalent aromatic hydrocarbon radical, and X- is an anion. Additional cure accelerators have the structure [(R 10 )(R 11 )I] + SbF6 - wherein R 10 and R 11 each independently represents, optionally, 1 to 4 C 1-20 Alkyl, C 1-20 Alkoxy, nitro, or chloro substituted C 6-14 It is a monovalent aromatic hydrocarbon, for example, 4-octyloxyphenylphenyliodonium hexafluoroantimonate.

[0053] The cure accelerator can be a metal salt complex, such as a copper(II), aluminum(III), zinc, cobalt, tin salt of an aliphatic or aromatic carboxylic acid selected from copper(II), tin(II), and aluminum(III) salts of acetate, stearate, gluconate, citric acid, benzoate, and mixtures thereof. For example, the cure accelerator can be a copper(II) or aluminum(III) salt of a β-diketonate, a copper(II), iron(II), iron(III), cobalt(II), cobalt(III), or aluminum(III) salt of an acetylacetonate, a zinc(II), chromium(II), or manganese(II) salt of an octoate, or a combination thereof.

[0054] When the curable thermosetting composition includes a curing catalyst, the curing catalyst can be included in an amount of 0.01 to 5 wt%, or 0.05 to 5 wt%, or 0.1 to 5 wt%, based on the total weight of the curable thermosetting composition.

[0055] The curable thermosetting composition may optionally include a cure initiator, such as a peroxide compound. Exemplary peroxide cure initiators include benzoyl peroxide, dicumyl peroxide, methyl ethyl ketone peroxide, lauryl peroxide, cyclohexanone peroxide, t-butyl hydroperoxide, t-butyl benzene hydroperoxide, t-butyl peroctoate, t-butyl peroxybenzoate, t-butyl peroxy 2-ethylhexyl carbonate, 2,4-dichlorobenzoyl peroxide, 2,5-dimethylhexane-2,5-dihydroperoxide, butyl-4,4-bis(tert-butyldioxy)valerate, 2,5-dimethyl-2,5-di(t-butylperoxy)-hex-3-yne, di-t-butylperoxy ... oxide, t-butylcumyl peroxide, α,α'-bis(t-butylperoxy-m-isopropyl)benzene, 2,5-dimethyl-2,5-di(t-butylperoxy)hexane, dicumyl peroxide, di(t-butylperoxy)isophthalate, t-butylperoxybenzoate, 2,2-bis(t-butylperoxy)butane, 2,2-bis(t-butylperoxy)octane, 2,5-dimethyl-2,5-di(benzoylperoxy)hexane, 1,1-di-(tert-butylperoxy)-3,3,5-trimethylcyclohexane, di(trimethylsilyl)peroxide, trimethylsilylphenyltriphenylsilylperoxide, and the like, or combinations thereof.

[0056] When the curable thermosetting composition includes a curing initiator, the curing initiator can be included in an amount of 0.1 to 5 wt%, or 0.5 to 5 wt%, or 1 to 5 wt%, based on the total weight of the curable thermosetting composition.

[0057] Flame retardants include, for example, organic compounds containing phosphorus, bromine, or chlorine. Non-brominated and non-chlorinated phosphorus-containing flame retardants may be preferred for regulatory reasons in certain applications, such as organic phosphates and organic compounds containing phosphorus-nitrogen bonds.

[0058] Examples of phosphorus-based flame retardants include phosphates, phosphazenes, phosphites, phosphines, phosphinates, polyphosphates, and phosphonium salts. Phosphates include triphenyl phosphate, tricresyl phosphate, isopropylated triphenyl phosphate, phenyl bis(dodecyl)phosphate, phenyl bis(neopentyl)phosphate, phenyl bis(3,5,5'-trimethylhexyl)phosphate, ethyl diphenyl phosphate, 2-ethylhexyl di(p-tolyl)phosphate, bis(2-ethylhexyl)p-tolylphosphate, tritolyl phosphate, bis(2-ethylhexyl)phenyl phosphate, tri(nonylphenyl)phosphate, bis(dodecyl)p-tolylphosphate, dibutylphenyl phosphate, 2-chloroethyl diphenyl phosphate, p-tolyl bis(2,5,5'-trimethylhexyl)phosphate, 2-ethylhexyl diphenyl phosphate, xylenyl-diphenyl phosphate, cresyl-diphenyl phosphate, 1,3-phenylene bis(di-2,6-xylenyl phosphate), 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO), tetraphenyl diphosphate (RDP), condensed phosphate compounds, such as aromatic condensed phosphate compounds, as well as cyclic phosphate compounds, bis(diphenyl)phosphate of hydroquinone, bis(diphenyl)phosphate of bisphenol A, and the like, or their oligomeric or polymeric counterparts, or combinations thereof.

[0059] Examples of phosphazene compounds include cyclic and linear phosphazene compounds. Cyclic phosphazene compounds (cyclophosphazenes) have a cyclic structure and a phosphorus-nitrogen double bond is present in the molecule. Examples of phosphinate compounds include aluminum dialkylphosphinate, aluminum tris-(diethylphosphinate), aluminum tris-(methylethylphosphinate), aluminum tris-(diphenylphosphinate), zinc bis-(diethylphosphinate), zinc bis-(methylphosphinate), zinc bis-(diphenylphosphinate), titanyl bis-(diethylphosphinate), titanyl bis-(methylethylphosphinate), and titanyl bis-(diphenylphosphinate). Examples of polyphosphate compounds include melamine polyphosphate, melam polyphosphate, and melem polyphosphate. Examples of phosphonium salt compounds include tetraphenylphosphonium tetraphenylborate. Examples of phosphite compounds include trimethyl phosphite and triethyl phosphite. Flame retardant compounds containing phosphorus-nitrogen bonds include phosphonitrilic chloride, phosphorus ester amides, phosphoric acid amides, phosphonic acid amides, phosphinic acid amides, and tris(aziridinyl)phosphine oxide.

[0060] Halogenated materials can also be used as flame retardants, such as bisphenols, such as 2,2-bis-(3,5-dichlorophenyl)-propane, bis-(2-chlorophenyl)-methane, bis(2,6-dibromophenyl)-methane, 1,1-bis-(4-iodophenyl)-ethane, 1,2-bis-(2,6-dichlorophenyl)-ethane, 1,1-bis-(2-chloro-4-iodophenyl)ethane, 1,1-bis-(2-chloro-4-methylphenyl)-ethane, 1,1-bis-(3,5-dichlorophenyl)-ethane, 2,2-bis-(3-phenyl-4-bromophenyl)-ethane, 2,6-bis-(4,6-dichloronaphthyl)-propane, as well as 2,2-bis-(3,5-dichloro-4-hydroxyphenyl)-propane 2,2 bis-(3-bromo-4-hydroxyphenyl)-propane. Other halogenated materials include 1,3-dichlorobenzene, 1,4-dibromobenzene, 1,3-dichloro-4-hydroxybenzene, and biphenyls such as 2,2'-dichlorobiphenyl, polybrominated 1,4-diphenoxybenzene, 2,4'-dibromobiphenyl, and 2,4'-dichlorobiphenyl as well as decabromodiphenyl ether, decabromodiphenylethane, and oligomeric and polymeric halogenated aromatic compounds such as brominated styrene, 4,4-dibromobiphenyl, ethylene-bis(tetrabromophthalimide), or copolycarbonates and carbonate precursors of bisphenol A and tetrabromobisphenol A, such as phosgene. Metal synergists such as antimony oxide can also be used with the flame retardants.

[0061] Inorganic flame retardants, e.g., C 1-16Alkyl sulfonates such as potassium perfluorobutanesulfonate (Rimar salt), potassium perfluorooctane sulfonate, tetraethylammonium perfluorohexanesulfonate, and potassium diphenylsulfonesulfonate, salts of Na2CO3, K2CO3, MgCO3, CaCO3, and BaCO3, or fluoro-anion complexes such as Li3AlF6, BaSiF6, KBF4, K3AlF6, KAlF4, K2SiF6, or Na3AlF6 can also be used.

[0062] When the curable thermosetting composition includes a flame retardant, the flame retardant can be included in an amount greater than 1 wt%, or from 1 to 20 wt%, or from 5 to 20 wt%, based on the total weight of the curable thermosetting composition.

[0063] The curable thermosetting composition can further include inorganic or organic fillers, such as particulate fillers, fibrous fillers, and the like, or combinations thereof. Any inorganic and organic fillers can be used, including those known in the art, without limitation.

[0064] Exemplary fillers include, for example, clay, talc, kaolin, wollastonite, mica, calcium carbonate, magnesium carbonate, alumina, thiourea, glass powder, B or Sn based fillers such as zinc borate, zinc stannate and zinc hydroxystannate, metal oxides such as zinc oxide and tin oxide, alumina, silica (including fused quartz, fumed silica, spherical silica, and crystalline silica), boron nitride (including spherical boron nitride), aluminum nitride, silicon nitride, magnesia, magnesium silicate, antimony trioxide, glass fibers (chopped, milled, or cloth), glass mat, glass spheres, hollow glass microspheres, aramid fibers, quartz, and the like, or combinations thereof. Other exemplary inorganic fillers include powdered titanium ceramics, such as any one of the titanates of barium, lead, strontium, calcium, bismuth, magnesium, and the like. Inorganic fillers also include hydrates such as aluminum hydroxide, magnesium hydroxide, zeolites, and hydrotalcites. In some embodiments, the fillers can be treated with the coupling agents disclosed herein.

[0065] Glass fibers include those based on E, A, C, ECR, R, S, D, and NE glasses, as well as quartz. The glass fibers can have any suitable diameter, for example, 2 to 30 micrometers (μm), or 5 to 25 μm, or 5 to 15 μm. The length of the glass fibers before compounding is not limited and can be 2 to 7 millimeters (mm), or 1.5 to 5 mm. Alternatively, longer glass fibers or continuous glass fibers can be used. Suitable glass fibers are commercially available from sources such as Owens Corning, Nippon Electric Glass, PPG, and Johns Manville.

[0066] The organic filler can be, for example, polytetrafluoroethylene powder, polyphenylene sulfide powder, and poly(ether sulfone) powder, poly(phenylene ether) powder, polystyrene, divinylbenzene resin, and the like, or combinations thereof.

[0067] Fillers can be selected based on the coefficient of thermal expansion (CTE) and thermal conductivity requirements. For example, Al2O3, BN, AlN, or combinations thereof can be used for electronics modules with high thermal conductivity. For example, MgO can be used for increased thermal conductivity and increased CTE. For example, SiO2 (e.g., amorphous SiO2) can be used for lightweight modules with low CTE and small dielectric constant.

[0068] When the curable thermosetting composition includes a filler, the filler can be included in an amount of greater than 1 wt%, or from 1 to 50 wt%, or from 1 to 30 wt%, or from 10 to 30 wt%, based on the total weight of the curable thermosetting composition.

[0069] Coupling agents, also called adhesion promoters, include chromium complexes, silanes, titanates, zircon-aluminates, olefin-maleic anhydride copolymers, reactive cellulose esters, etc. Exemplary olefin-maleic anhydride copolymers include: maleic anhydride grafted polyethylene, maleic anhydride grafted polypropylene, or combinations thereof. Exemplary silanes include: epoxy silane compounds, amino silane compounds, methacryloxy silane compounds, vinyl silane compounds, or combinations thereof.

[0070] Examples of aminosilane coupling agents are γ-aminopropyltrimethoxy-silane, γ-aminopropyltriethoxysilane, N-β(aminoethyl)γ-aminopropylmethyl-dimethoxysilane, N-β(aminoethyl)γ-aminopropyltrimethoxysilane, and N-β(aminoethyl)γ-aminopropyltriethoxysilane. Exemplary epoxysilane coupling agents include: γ-glycidoxypropylmethyldiethoxysilane, γ-glycidoxypropyltrimethoxysilane, and γ-glycidoxypropyltriethoxysilane. Examples of methacryloxysilane coupling agents include: γ-methacryloxypropylmethyldimethoxysilane, γ-methacryloxypropyltrimethoxysilane, γ-methacryloxypropyldiethoxysilane, and γ-methacryloxypropyltriethoxysilane.

[0071] Other exemplary silane coupling agents include bis(3-triethoxysilylpropyl) tetrasulfide, bis(3-triethoxysilylpropyl) trisulfide, bis(3-triethoxysilylpropyl) disulfide, bis(2-triethoxysilylethyl) tetrasulfide, bis(3-trimethoxysilylpropyl) tetrasulfide, bis(2-trimethoxysilylethyl) tetrasulfide, 3-mercaptopropyl trimethoxysilane, 3-mercaptopropyl triethoxysilane, 2-mercaptoethyl trimethoxysilane, 2-mercaptoethyl tri-ethoxysilane, 3-trimethoxysilylpropyl-N,N-dimethylthiocarbamoyl tetrasulfide, 3-triethoxysilylpropyl Silane coupling agents include silane coupling agents such as silane coupling agents, ...

[0072] When the curable thermosetting composition includes a coupling agent, the coupling agent can be included in an amount of 0.01 to 5 wt%, or 0.05 to 5 wt%, or 0.1 to 5 wt%, based on the total weight of the curable thermosetting composition.

[0073] The curable thermosetting composition can optionally include a solvent. The solvent can be, for example, C 3-8 Ketone, C 3-8 N,N-Dialkylamides, C 4-16 Dialkyl ether, C 6-12 Aromatic Hydrocarbons, C 1-3 Chlorinated hydrocarbons, C 3-6 Alkyl alkanoates, C 2-6 Specific ketone solvents include, for example, acetone, methyl ethyl ketone, methyl isobutyl ketone, or combinations thereof. 4-8 N,N-dialkylamide solvents include, for example, dimethylformamide, dimethylacetamide, N-methyl-2-pyrrolidone, or combinations thereof. Specific dialkyl ether solvents include, for example, tetrahydrofuran, ethylene glycol monomethyl ether, dioxane, or combinations thereof. Specific aromatic hydrocarbon solvents include, for example, benzene, toluene, xylene, styrene, divinylbenzene, or combinations thereof. The aromatic hydrocarbon solvent can be non-halogenated. Specific C 3-6 Alkyl alkanoates include, for example, methyl acetate, ethyl acetate, methyl propionate, ethyl propionate, or combinations thereof. 2-6 Alkyl cyanides include, for example, acetonitrile, propionitrile, butyronitrile, or combinations thereof. 2-6The alkyl cyanide can be, for example, acetonitrile, propionitrile, butyronitrile, or a combination thereof. For example, the solvent can be N,N-dimethylformamide, N,N-dimethylacetamide, N,N-diethylacetamide, N,N-dimethylmethoxyacetamide, N-methyl-2-pyrrolidone, N-cyclohexylpyrrolidinone, N-methylcaprolactam, 1,3-dimethyl-2-imidazolidone, 1,2-dimethoxyethane, 1,3-dioxane, 1,4-dioxane, tetrahydrofuran, γ-butyrolactone, γ-caprolactone, dimethylsulfoxide, benzophenone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexyl ketone, methyl ethyl ... xanone, diglyme, triglyme, tetraglyme, N,N-dimethylethyleneurea, N,N-dimethylpropyleneurea, tetramethylurea, propylene glycol phenyl ether, anisole, veratrole, o-dichlorobenzene, chlorobenzene, trichloroethane, methylene chloride, chloroform, pyridine, picoline, ethyl lactate, n-butyl acetate, butyl cellosolve acetate, butyl carbitol acetate, ethyl cellosolve acetate, ethyl carbitol acetate, propylene carbonate, sulfolane, ionic liquids, or combinations thereof.

[0074] If a solvent is used, the curable thermosetting composition can include 2 to 99 wt% of the solvent based on the total weight of the curable thermosetting composition. For example, the amount of solvent can be 5 to 80 wt%, or 10 to 60 wt%, or 20 to 50 wt%, based on the total weight of the curable thermosetting composition. The solvent can be selected, in part, to adjust the viscosity of the curable thermosetting composition. Thus, the amount of solvent can depend on variables including the type and amount of capped poly(arylene ether) copolymer, the type and amount of other ingredients such as curing additives, the type and amount of any supplemental thermosetting resin(s), and the processing temperature used for any subsequent processing of the curable thermosetting composition, such as impregnation of a reinforcing structure with the curable thermosetting composition for preparation of a composite. The solvent can be anhydrous. For example, the solvent can include less than 100 parts per million (ppm), or less than 50 ppm, or less than 10 ppm of water based on the total weight of the solvent.

[0075] The curable thermosetting composition can further include a curable unsaturated monomer composition, and the monomer composition can include, for example, a monofunctional styrenic compound (e.g., styrene), a monofunctional (meth)acrylic compound, and the like, or a combination thereof. For example, the curable unsaturated monomer composition can be an alkene-containing monomer or an alkyne-containing monomer. Exemplary alkenes and alkyne-containing monomers include those described in U.S. Pat. No. 6,627,704 to Yeager et al., and (meth)acrylates, (meth)acrylamides, N-vinylpyrrolidones, and vinylazalactones disclosed in U.S. Pat. No. 4,304,705 to Heilman et al. Exemplary monofunctional monomers include: mono(meth)acrylates, such as methyl (meth)acrylate, ethyl (meth)acrylate, isopropyl (meth)acrylate, isooctyl (meth)acrylate, isobornyl (meth)acrylate, (meth)acrylic acid, n-hexyl (meth)acrylate, tetrahydrofurfuryl (meth)acrylate, N-vinylcaprolactam, N-vinylpyrrolidone, (meth)acrylonitrile, and the like, or combinations thereof.

[0076] The curable thermosetting composition can optionally further include one or more additional additives, such as, for example, dyes, pigments, colorants, antioxidants, heat stabilizers, light stabilizers, plasticizers, defoamers, lubricants, dispersants, flow modifiers, drip retardants, antiblocking agents, antistatic agents, flow promoters, processing aids, base adhesives, mold release agents, toughening agents, low shrinkage additives, stress relief additives, and the like, or combinations thereof. When present, the additional additives can be included in any effective amount, such as, for example, 0.01 to 20 wt%, or 0.01 to 10 wt%, or 0.01 to 5 wt%, or 0.01 to 1 wt%, based on the total weight of the curable thermosetting composition.

[0077] The curable thermosetting compositions can be prepared by combining the difunctional phenylene ether oligomers and other optional ingredients disclosed herein using any suitable method.

[0078] Cured thermosetting compositions are also provided, including the cured product of the curable thermosetting composition. There is no particular restriction on the manner in which the curable thermosetting composition can be cured. The curable composition can be, for example, thermally cured or can be cured by using irradiation techniques, such as UV irradiation or electron beam irradiation. For example, the cured product can be obtained by heating the curable thermosetting composition as defined herein for a time and temperature sufficient to evaporate the solvent and achieve curing. If thermal curing is used, the temperature can be 30 to 400°C, or 50 to 250°C, or 100 to 250°C. Heating can be between 1 minute and 24 hours, or 1 minute and 6 hours, or 3 hours and 5 hours. Curing can be carried out to produce a partially cured, often tack-free, resin, which is then fully cured by heating for a longer period of time or at a temperature within the aforementioned ranges. As used herein, the term "cured" encompasses partially cured or fully cured products.

[0079] The cured thermoset composition can have one or more desirable properties. For example, the thermoset composition can have a glass transition temperature of 165° C. or more, preferably 170° C. or more, more preferably 165 to 180° C. The thermoset composition can also advantageously exhibit a low dielectric constant (Dk), a low dissipation factor (Df), and reduced moisture absorption. For example, the thermoset composition can have a dielectric constant of less than 3.0, preferably less than 2.75, more preferably less than 2.6 at a frequency of 10 GHz. The thermoset composition can have a dissipation factor of less than 0.01, or less than 0.005 at a frequency of 10 GHz. Thus, the thermoset composition comprising the phenylene ether oligomer of the present disclosure can be particularly well suited for use in electronics applications.

[0080] The curable thermosetting composition and the cured thermosetting composition can be used in a variety of applications and uses, including any application where a conventional thermosetting composition is used. For example, useful articles comprising the curable thermosetting composition or the cured thermosetting composition can be in the form of a composite, foam, fiber, layer, coating, encapsulant, adhesive, sealant, molded part, prepreg, casing, laminate, metal clad laminate, electronic composite, structural composite, or combinations thereof. Exemplary uses and applications include coatings, such as protective coatings, sealants, weather resistant coatings, scratch resistant coatings, and electrically insulating coatings, adhesives, binders, bonding agents, composites, such as those using carbon fiber and glass fiber reinforcement. When used as a coating, the disclosed compounds and compositions can be deposited on the surface of various underlying substrates. For example, the compositions can be deposited on the surface of metal, plastic, glass, fiber siding, ceramic, stone, wood, or any combination thereof. The disclosed compositions can be used as coatings on the surface of metal containers (e.g., aluminum or steel), such as those commonly used for packaging and containment in the paint and surface coating industries. The curable thermoset compositions and cured thermoset compositions derived therefrom can also be particularly well suited for use in forming electrical and computer components.

[0081] The method of forming the composite can include impregnating a reinforcing structure with a curable thermosetting composition, partially curing the curable thermosetting composition to form a prepreg, and stacking a plurality of prepregs. The reinforcing structure can be a porous base material, such as a fiber preform or substrate, or other porous material including ceramic, polymer, glass, carbon, or combinations thereof. For example, the porous base material can be a woven or nonwoven glass cloth, woven glass fiber, or carbon fiber. When the article includes a fiber preform, the method of making the article can include forming the article from the curable thermosetting composition by coating or impregnating the preform with the curable composition. The impregnated fibrous preform can be optionally molded before or after removing the solvent. In some aspects, the curable thermosetting composition layer can further include a woven or nonwoven glass cloth. For example, the curable layer can be prepared by impregnating a glass cloth with the curable composition and removing the solvent from the impregnated glass cloth. Exemplary reinforcing structures are described, for example, in Anonymous (Hexcel Corporation), "Prepreg Technology," March 2005, Publication No. FGU 017b, Anonymous (Hexcel Corporation), "Advanced Fibre Reinforced Matrix Products for Direct Processes," June 2005, Publication No. ITA272, and Bob Griffiths, "Farnborough Airshow Report 2006," CompositesWorld.com, September 2006. The weight and thickness of the reinforcing structure will be selected according to the intended use of the composite, using criteria well known to those skilled in the art of producing fiber reinforced resin composites. The reinforcing structure can include a variety of finishes suitable for the thermosetting component of the curable thermosetting composition.

[0082] A method of making an article from a curable thermosetting composition can include partially curing the curable thermosetting composition to form a prepreg or fully curing the curable thermosetting composition to form a composite article. References herein to the property of a "cured composition" refer to a substantially fully cured composition. For example, the resin in a laminate formed from a prepreg is typically substantially fully cured. Those skilled in the art of thermosetting can determine whether a sample is partially cured or substantially fully cured without undue experimentation. Curing can be before or after removal of the solvent from the curable composition. Additionally, the article can be further shaped, for example by thermoforming, before or after removal of the solvent, before curing, after partial curing, or after full curing. In one embodiment, the article is formed and the solvent is removed, the article is partially cured (B-staged), optionally shaped, and then further cured.

[0083] Commercial-scale methods of forming composites are known in the art, and the curable thermosetting compositions described herein are easily adaptable to existing processes and equipment. For example, prepregs are often produced on a processor. The main components of a processor include a feeder roller, a resin impregnation tank, a processor oven, and a receiving roller. The reinforcing structure (e.g., E-glass) is usually wound into a large spool. The spool is then attached to a feeder roller, which rotates and gradually pays out the reinforcing structure. The reinforcing structure then travels through a resin impregnation tank containing a curable thermosetting composition. The curable composition impregnates the reinforcing structure. After exiting the tank, the coated reinforcing structure travels upward through a vertical processor oven, which is typically at a temperature of 175 to 200° C. and the solvent is evaporated. The resin begins to polymerize at this point. When the composite emerges from the tower, it is fully cured so that the web is not wet and is not tacky. However, the curing process is stopped short of completion so that additional curing can occur when the laminate is produced. The web then rolls the prepreg onto a receiving roller.

[0084] Electrical and electronic articles comprising or derived from the curable thermosetting composition are also provided. Articles include those comprising printed circuits used in the medical or aerospace industries. Still other articles include antennas and similar articles. Articles such as printed circuit boards are used, for example, in lighting, solar energy, displays, cameras, audio and video equipment, personal computers, mobile phones, electronic organizers, and similar devices, or office automation equipment. For example, electrical components can be mounted on printed circuit boards, including laminates. Other exemplary articles prepared from the curable composition for various applications include copper clad laminates (CCLs), such as metal core copper clad laminates (MCCCLs), composite articles, and coated articles, such as multi-layer articles.

[0085] The dielectric layer can be prepared from a curable thermosetting composition and can be useful in circuit assemblies, for example, metal clad laminates, such as copper clad laminates. For example, the laminate can include a dielectric layer, a conductive metal circuit layer disposed on the dielectric layer, and optionally, a heat dissipating metal matrix layer disposed on the dielectric layer, opposite the conductive metal layer. The dielectric layer can optionally include a fiber preform (e.g., a woven layer). For example, the dielectric layer can further include a glass cloth layer.

[0086] The conductive metal layer can be in the form of a circuit and can be copper, zinc, tin, brass, chromium, molybdenum, nickel, cobalt, aluminum, stainless steel, iron, gold, silver, platinum, titanium, etc., or combinations thereof. Other metals include copper-molybdenum alloys, nickel-cobalt-iron alloys, such as KOVAR available from Carpenter Technology Corporation, nickel-iron alloys, such as INVAR available from National Electronic Alloys, Inc., bimetals, trimetals, trimetals derived from two layers of copper and one layer of Invar, and trimetals derived from two layers of copper and one layer of molybdenum. Exemplary metal layers include copper or copper alloys. Alternatively, wrought copper foil can be used. The conductive metal layer can have a thickness of 2 to 200 micrometers (μm), or 5 to 50 μm, or 5 to 40 μm.

[0087] The heat dissipating metal matrix layer can be a thermally conductive metal, such as aluminum, boron nitride, aluminum nitride, copper, iron, steel, or the like, or a combination thereof. Thermally conductive, electrically conductive metals can be used, provided that the metal is electrically insulated from the metal circuit layer. A preferred supporting metal matrix layer can have a thickness of 0.1 to 20 millimeters (mm), or 0.5 to 10 mm, or 0.8 to 2 mm.

[0088] The conductive metal layer and the supporting metal matrix layer can be pretreated to have a high surface roughness for enhanced adhesion to the dielectric layer. Treatment methods include, for example, cleaning, flame treatment, plasma discharge, corona discharge, etc., to enhance adhesion of the metal layer. The dielectric layer can be firmly adhered to the conductive metal layer or heat spreader layer without the use of adhesives, or adhesives can be used to improve adhesion of the dielectric layer to the conductive metal layer or heat spreader layer. Exemplary adhesives used to bond the composite sheet to the metal include polyimide adhesives, acrylic adhesives, epoxies, etc., or combinations thereof.

[0089] Copper clad laminates can be produced by thermal lamination under pressure of one or more dielectric layers, one or more conductive metal layers, and a supporting metal matrix layer without the use of a thermosetting adhesive. The dielectric layer can be prepared from a curable thermosetting composition and can be prepared by a solution casting process to form the layers before the thermal lamination step. For example, the dielectric layer, the conductive metal layer, and the heat dissipation layer can be thermally laminated together under pressure by an adhesive-free process to form a laminate. The conductive metal layer can optionally be in the form of a circuit before lamination, or the conductive metal layer can optionally be etched to form an electrical circuit after lamination. The lamination can be performed by hot pressing or roll calendaring, for example, a roll-to-roll process. The conductive metal layer in the copper clad laminate can be further patterned to provide a printed circuit board. Furthermore, the copper clad laminate can be shaped to provide a circuit board having the shape of a sheet, tube, or rod.

[0090] Alternatively, laminates for circuit assemblies can be manufactured by a solution casting process, where the curable thermosetting composition is cast directly onto a conductive metal layer and then laminated to a heat-spreading metal matrix layer. For example, the curable thermosetting composition can be cast directly onto a heat-spreading metal matrix layer and then laminated to a conductive metal layer.

[0091] Multi-layer laminates containing additional layers can also be produced by thermal lamination in one step or in two or more successive steps by processes such as hot pressing or roll calendering. For example, up to seven layers, or up to 16 layers, can be present in the laminate. In one embodiment, the laminate can be formed in one step or in two or more successive steps with a cloth-thermoset resin-metal-thermoset resin-cloth-thermoset resin-metal foil sequence or a subcombination thereof with fewer layers, so that the laminate includes a layer of thermoset film between any layer of metal foil and any layer of cloth. In another embodiment, a first laminate can be formed in one step or in two or more successive steps with a layer of cloth between two layers of thermoset resin, for example, a layer of woven glass cloth between two layers of thermoset resin. A second laminate can then be prepared by laminating a metal foil to the thermoset side of the first laminate.

[0092] The printed circuit board prepared from the curable thermosetting composition can have a total thickness of 0.1 to 20 mm, specifically 0.5 to 10 mm, where the total thickness refers to the assembly including each of the layers, the dielectric layer, the conductive metal layer, and the supporting metal matrix layer. The circuit assembly can have a total thickness of 0.5 to 2 mm, specifically 0.5 to 1.5. There is no particular limit to the thickness of the dielectric layer, and it can be 5 to 1500 μm, or 5 to 750 μm, or 10 to 150 μm, or 10 to 100 μm. For example, the printed circuit board can be a metal core printed circuit board (MCPCB) for use in light emitting diode (LED) applications.

[0093] The curable thermosetting composition can be used, for example, as a coating in the preparation of multi-layer articles. A method of making a coating can include combining the curable thermosetting composition and, optionally, a fluoropolymer, and forming a coating on a substrate. For example, a multilayer article can be made by forming a layer comprising a curable thermosetting composition, removing solvent from the layer, and optionally curing to provide a primer layer, forming a second layer over the primer layer comprising a ceramic (e.g., Al2O3, TiO2, ZrO2, Cr2O3, SiO2, MgO, BeO, YO3, Al2O3-SiO2, MgO-ZrO2, SiC, WC, B4C, TiC, Si3N4, TiN, BN, AlN, TiB, ZrB2, etc.), a thermoplastic polymer, a fluoropolymer (e.g., polytetrafluoroethylene, tetrafluoroethylene-perfluoroalkyl vinyl ether copolymer, tetrafluoroethylene-hexafluoropropylene copolymer, polychlorotrifluoroethylene, tetrafluoroethylene-ethylene copolymer, polyvinylidene fluoride, etc.), or a combination thereof, providing a multilayer article, and optionally heat treating the multilayer article to cure the curable thermosetting composition. In some embodiments, the second layer can further comprise a curable thermosetting composition.

[0094] Additional uses for the curable thermosetting compositions include, for example, acid bath vessels, neutralization tanks, aircraft components, bridge girders, bridge decks, electrolytic cells, exhaust stacks, scrubbers, sporting goods, stairs, walkways, automotive exterior panels, e.g., hoods and trunk lids, floor pans, air intakes, pipes and ducts, e.g., heater ducts, industrial fans, fan housings, and blowers, industrial mixers, boat hulls and decks, marine terminal fenders, tiles and coatings, siding, business machine housings, trays, e.g., cable trays, concrete modifiers, Dishwasher and refrigerator parts, electrical seals, electrical panels, tanks such as electrorefining tanks, water softener tanks, fuel tanks, and various filament wound tanks and tank linings, furniture, garage doors, grates, protective gear, luggage, outdoor motor vehicles, pressurized tanks, optical waveguides, radomes, handrails, railway parts such as tank cars, hopper car covers, car doors, truck bed liners, satellite television dishes, signage, solar energy panels, telephone switchgear housings, tractor parts, transformer covers, truck parts such as fenders, hoods, bodies , cabs, and loading platforms, insulation for rotating machinery, e.g., ground insulation, turn insulation, and phase isolation insulation, commutators, core insulation and cord and lacing tape, drive shaft couplings, propeller blades, missile components, rocket motor cases, airfoil sections, sucker rods, fuselage sections, wing skins and flares, engine nacelles, cargo hatches, tennis racquets, golf club shafts, fishing rods, skis and ski poles, bicycle components, lateral leaf springs, pumps, e.g., automotive smog pumps, electrical components, implants, and tools, e.g., electrical cable couplings. , windings and high density multi-element assemblies, sealing of electromechanical devices, battery cases, resistors, fuses and thermal cutoff devices, coatings for printed wiring boards, cast items such as capacitors, transformers, crankcase heaters, small molded electronic components such as coils, capacitors, resistors, and semiconductors, as a replacement for steel in chemical processing, pulp and paper, power generation, and wastewater treatment, scrub towers, pultruded parts for structural applications such as structural members, grates, and guardrails, swimming pools, swimming pool slides, hot tubs,and saunas, drive shafts for under hood applications, dry toner resins for copiers, marine tooling and composites, heat shields, submarine hulls, prototype generation, development of experimental models, laminate trim, drilling fixtures, bonding fixtures, inspection fixtures, industrial metal forming dies, aircraft stretch block and hammer forms, vacuum forming molds, flooring, e.g. flooring for generation and assembly areas, clean rooms, machine shops, control rooms, laboratories, parking structures, freezers, coolers, and outdoor loading docks, conductive compositions for antistatic applications, for decorative flooring, expansion joints for bridging, injectable mortars for patching and repairing cracks in structural concrete, grouting for tiles, machine rails, metal dowels, bolts and posts, repair of oil and fuel storage tanks, and many other uses.

[0095] Useful processes for preparing articles and materials include those generally known in the art for the processing of thermosetting resins. Such processes are described in the literature, for example, Engineered Materials Handbook, Volume 1, Composites, ASM International Metals Park, Ohio, copyright 1987 Cyril A. Dostal Senior Ed, pp. 105-168 and 497-533, and "Polyesters and Their Applications" by Bjorksten Research Laboratories, Johan Bjorksten (pres.) Henry Tovey (Ch. Lit. Ass.), Betty Harker (Ad. Ass.), James Henning (Ad. Ass.), Reinhold Publishing Corporation, New York, 1956. Processing techniques include resin transfer molding, sheet molding, bulk molding, pultrusion, injection molding, such as reaction injection molding (RIM), atmospheric pressure molding (APM), casting, such as centrifugal and static casting, open mold casting, lamination, such as wet or dry lay-up and spray lay-up, also include contact molding, such as cylindrical contact molding, compression molding, such as vacuum assisted resin transfer molding and chemically assisted resin transfer molding, matched tool molding, autoclave curing, heat curing in air, vacuum bagging, pultrusion, Seeman's Composite Resin Infusion Manufacturing Processing (SCRIMP), open molding, continuous combination of resin and glass, and filament winding, such as cylindrical filament winding. For example, an article can be prepared by a resin transfer molding process.

[0096] Also provided are articles derived from the curable thermosetting compositions, the articles being composites, foams, fibers, layers, coatings, encapsulants, adhesives, sealants, molded parts, prepregs, casings, castings, laminates, or combinations thereof, or the articles being metal clad laminates, electronic composites, structural composites, or combinations thereof. The articles can be manufactured, for example, by casting, molding, extrusion, etc., as disclosed herein, and removing the solvent from the formed article. In some aspects, the article can be a layer, formed by casting the curable composition onto a substrate and forming a cast layer. The solvent can be removed by various means, for example, by heating the cast layer, heating the cast layer under heat and pressure, for example, by laminating the cast layer to another substrate. In some aspects, the articles prepared by the above methods can include adhesives, packaging materials, capacitor films, or circuit board layers. In some aspects, the articles prepared from the curable compositions can be dielectric layers, or coatings disposed on a substrate, such as wire or cable coatings. For example, the article can be a circuit material, such as a dielectric layer in a printed circuit board, for example, used in lighting or communication applications. Another exemplary article prepared from the curable composition can be one or more coating layers. The curable composition can be used to prepare articles disclosed herein for other curable thermosetting compositions. EXAMPLES

[0097] This disclosure is further illustrated by the following non-limiting examples.

[0098] The materials used for the examples below are listed in Table 1.

[0099] [Table 1]

[0100] Oxidative coupling polymerization reactions were carried out in a 500 ml jacketed glass reactor equipped with a bubbling reactor, overhead stirrer, thermocouple, nitrogen pad, and a dip tube for oxygen bubbling. Derivatization or endcapping reactions were carried out in a 500 ml glass reactor equipped with a heating mantle, Dean-Stark condenser, thermocouple, and addition funnel.

[0101] Casting of the hardenable compositions for subsequent curing was carried out using a Specac manual hydraulic press.

[0102] PPE-CMP oligomer was synthesized according to the following procedure: Toluene (42.45 grams), CMP (42.3 grams), TMBPA (5.76 grams), DMBA (4.32 grams), DBA (0.28 grams), and a mixture of DBEDA (0.075 grams), PTC-1 (0.04 grams), and toluene (0.13 grams) were placed in a 500 ml bubbling polymerization vessel and stirred under nitrogen. Catalyst solution (0.02 grams of Cu2O and 0.33 grams of 48% HBr) was added to the above reaction mixture. After the addition of the catalyst solution, oxygen flow was started. The temperature was ramped from 25°C to 32°C in 15 minutes and increased to 49°C in 115 minutes. The oxygen flow was maintained for 1500 minutes, at which point the flow was stopped and 0.46 grams of NTA and 5.68 grams of water were added to the reaction mixture. The resulting mixture was stirred at 60°C for 2 hours. The layers were separated by centrifugation and the light phase was isolated by removal of the toluene. The oligomer was obtained after drying overnight under nitrogen in a vacuum oven at 110°C.

[0103] The PPE-CMP-2MA oligomer was synthesized according to the following procedure: PPE-CMP oligomer (36 grams) was dissolved in toluene (75 grams) in a 500 ml three-neck round bottom flask equipped with a heating mantle, Dean-Stark condenser, stirrer and thermocouple. The solution was heated to 120° C. and water was removed by azeotropic distillation. After water removal, the reaction mixture was cooled to 85° C. and DMAP (0.36 grams) was added. After complete dissolution of DMAP, MAA (6.63 grams) was added using an addition funnel over 20 minutes. The reaction temperature was increased to 110° C. and the reaction was stirred for 4 hours. PPE-CMP-2MA was isolated by precipitation into methanol. The powder was further dried overnight at 110° C. under vacuum and nitrogen.

[0104] Curable compositions were prepared by dissolving PPE-CMP-2MA in chloroform. The chloroform was removed under vacuum and nitrogen until a dry powder was obtained. The dry powder was used for chemorheology and further cured for performance evaluation. Cured castings were prepared by partially curing the composition (e.g., until gel time). The partially cured composition was transferred to a 40 millimeter diameter die and the die was placed in a hot die press. The sample was cured by increasing the temperature to 150° C. under pressure (1 ton). Once the temperature reached 150° C., the sample was then allowed to cool to 70° C., the die was transferred to an oven, and the sample was cured at 200° C. for 120 minutes under vacuum.

[0105] The compositions were characterized using the following test procedures.

[0106] Nuclear Magnetic Resonance (NMR) Spectroscopic Analysis: The chemical structures and compositions of the oligomers were determined by NMR analysis. 1 H NMR spectra were acquired on a Varian Mercury Plus400 instrument operating at an observation frequency of 400.14 MHz.

[0107] Gel permeation chromatography was performed against polystyrene standards and used to determine the number average molecular weight (Mn) and weight average molecular weight (Mw).

[0108] Solution Viscosity Measurements: A DV2+ pro Brookfield viscometer fitted with a UL adapter for low viscosity materials was used. Measurements were performed to determine the solution viscosity of 50 wt% oligomer in MEK using spindle 00 at 25° C. controlled by a water jacket.

[0109] Differential Scanning Calorimetry (DSC): The glass transition temperatures (Tg) of the oligomers were measured using a TA Instruments Differential Scanning Calorimeter with a 20°C / min temperature ramp from 25°C to 300°C. Analyses were performed under nitrogen. All sample weights were in the range of 8 to 11 milligrams. T-zero pans were used.

[0110] The heat of exotherm and degree of cure were also determined using DSC with a temperature ramp from 25° C. to 300° C. at a 10° C. / min temperature ramp. All sample weights were in the range of 8 to 11 milligrams. The degree of cure was determined by the ratio of the heat of exotherm from the uncured and partially cured (B-stage) compositions.

[0111] Gel times were measured using a TA Instruments Ares G2 rheometer under nitrogen atmosphere using 25 mm parallel plates with a target gap of 1 mm. An oscillatory temperature ramp with a starting temperature of 80° C. and a ramp rate of 5° C. / min, constant strain of 30%, and angular frequency of 10 Rad / s was used.

[0112] Viscosity measurements (referred to as "Resin Flow" in the tables below) were performed using a TA Instruments Ares G2 rheometer under nitrogen atmosphere using 25 mm parallel plates with a target gap of 1 mm. An oscillatory temperature ramp was used with a starting temperature of 80° C. and a ramp rate of 3° C. / min, a constant strain of 1%, and an angular frequency of 10 Rad / s.

[0113] Thermogravimetric analysis (TGA) was performed to characterize the decomposition of the cured samples, starting at 25°C and ramping up to 800°C using a temperature ramp rate of 10°C / min.

[0114] Dielectric measurements were performed using an Agilent Technologies E5071C network analyzer equipped with a split-post dielectric resonator (SPDR) fixture for measurements of dielectric constant (Dk) and dissipation factor (Df) at 10 GHz.

[0115] Moisture absorption was characterized by placing the castings in a water bath at 50° C. The samples were removed from the bath, allowed to dry and weighed every 24 hours.

[0116] <Example 1> PPE-CMP-2MA was prepared according to the synthesis described above. The structure of PPE-CMP-2MA was confirmed by solution NMR spectroscopy. 1 1 H NMR spectroscopy also confirmed that the end groups of the oligomer were methacrylate units, resulting in a difunctional oligomer with an average functionality of 2.

[0117] Table 2 shows some of the properties of the PPE-CMP-2MA oligomer of Example 1.

[0118] [Table 2]

[0119] Curable compositions were prepared according to Table 3. The rheology and cure behavior of the formulations were measured after solvent removal. The performance of the cured materials is also shown in Table 3. The performance of the compositions containing the oligomer of Example 1 was compared to a difunctional PPE-methacrylate oligomer containing repeat units derived from 2,6-dimethylphenol (shown as Comparative Example 1).

[0120] [Table 3]

[0121] [Table 4]

[0122] As shown in Table 3, the PPE-CMP-2MA oligomer exhibited improved dielectric performance. Thus, it is believed that the materials described herein are well suited for use in electronic materials, particularly prepreg laminates and metal clad laminates for printed circuit boards.

[0123] <Comparative Example 2> A CP-PPE oligomer was synthesized to compare with the CMP-PPE oligomer described above according to the following procedure. A mixture of toluene (168 grams), CP (49 grams), TMBPA (6.40 grams), DMBA (1.68 grams), DBA (0.56 grams), and 0.088 grams of DBEDA, 0.047 grams of PTC-1, and 0.15 grams of toluene was placed in a 500 milliliter bubbling polymerization vessel and stirred under nitrogen. Catalyst solution (0.42 grams, 0.03 grams of Cu2O, and 0.39 grams of (48%) HBr) was added to the reaction mixture. After the addition of the catalyst solution, oxygen flow was started. The temperature was ramped from 25°C to 39.4°C in 15 minutes and increased to 48.9°C in 70 minutes. The oxygen flow was maintained for 130 minutes, at which point it was stopped and 1.0 grams of NTA and 6.0 grams of water were added to the reaction mixture. The resulting mixture was stirred at 60° C. for 2 hours. The layers were separated by centrifugation and the light phase was isolated by precipitation into methanol. The precipitated particles were filtered and dried overnight under nitrogen in a vacuum oven at 110° C. prior to analysis.

[0124] CP-PPE oligomer 1 H and 31 All were characterized by P NMR spectroscopy. 1H NMR spectra were acquired on an Agilent DD2 600 instrument operating at an acquisition frequency of 599.90 MHz. Spectra for all samples were collected under quantitative conditions. Approximately 30 mg of 2-cycloheylphenol final ppt sample was added to 1 milliliter of 1,1,2,2-tetrachloroethane-d2. Spectral parameters included 9615 Hz spectral width, 1.7 s acquisition time (16K data points), 4.20 μs pulse width (45° flip angle), and 15 s pulse delay. An s2pul pulse sequence was used. Typically, 32 acquisitions were sufficient to achieve a good signal-to-noise ratio. Data processing was performed using NetNMR software with 0.25 Hz line broadening and polynomial baseline correction routines.

[0125] 31 P-NMR spectroscopy was used to identify and quantify phenolic functionality in various polymer samples. The technique involves derivatization of polymer phenolic residues with 2-chloro-1,3,2-dioxaphospholane. This reaction produces a variety of structurally similar 2-aryloxy-1,3,2-dioxaphospholanes that differ only in the aromatic ring substitution. 31 Due to the sensitivity of the P-nucleus to its electronic environment, various phenol end groups are 31 The P-chemical shifts can be used to identify the end groups. In addition to the phenol end groups, this method can also quantify alcohol and acid functionality in many resins. The use of an internal standard, 2,4-dibromophenol, allows the quantification of the hydroxyl end group functionality of polymer resins to be determined.

[0126] All spectra, 31The data were acquired on an Agilent DD2 600 spectrometer operating at 242.84 MHz for P. The instrument was fitted with a 5 mm OneNMR™ PFG probe. Approximately 80 mg of sample was dissolved in 4.0 ml of chloroform-d containing 0.95 mg / ml 2,4-dibromophenol (internal standard) and 15 mg / ml Cr(acac)3 (a T1 relaxation enhancing reagent to reduce data acquisition time). In addition, pyridine is added as an acid scavenger at 1 ml pyridine / 100 ml CDCl3 internal standard stock solution. Sample and internal standard weights are recorded to 4 decimal places. A decoupler was gated off during the pulse delay to eliminate NOE and ensure complete relaxation of the phosphorus nucleus between scans. Acquisition parameters included a 3 s pulse delay and a 45° flip angle. Also, a 23.6 kHz spectral width (100 to 200 ppm region) and 32K data points resulted in a 1.39 s acquisition time. Typically, 1024 scans were required for sufficient signal-to-noise ratio. Broadband proton decoupling was performed using a Waltz-16 pulse sequence. The internal standard, 2,4-dibromo-phenol signal, was used as the chemical shift reference (δ=130.24 ppm). The resulting spectra were processed using 1 Hz exponential apodization and baseline corrected using a polynomial fit routine. All data processing was performed using NetNMR software.

[0127] Cyclohexylphenol and tetramethylbisphenol A copolymer (CP-PPE) was synthesized by oxidative coupling polymerization as described above. The material was precipitated to remove unreacted monomer for better structural analysis. NMR spectroscopy was used to determine the chemical structure. The remaining amount of monomer was 31 The branching at the unsubstituted 6-position was determined by P NMR. 1 This was confirmed by 1 H NMR spectroscopy based on the number of protons in the aromatic rings. If a linear polymer was obtained, the number of protons should be 3, but it was determined to be 2.5. Thus, the CP-PPE oligomers exhibited a branched structure.

[0128] The disclosure further includes the following aspects.

[0129] Embodiment 1: A linear difunctional phenylene ether oligomer comprising repeat units derived from 2-methyl-6-cyclohexylphenol and having (meth)acrylate end groups.

[0130] Embodiment 2: The difunctional phenylene ether oligomer of embodiment 1, wherein the phenylene ether oligomer contains less than 30 weight percent of repeat units derived from a monohydric phenol having identical substituents at the 2- and 6-positions.

[0131] Embodiment 3: The phenylene ether oligomer of embodiment 1 or 2, wherein the repeat unit derived from 2-methyl-6-cyclohexylphenol has the structure: [ka]

[0132] Embodiment 4: The phenylene ether oligomer of any of embodiments 1 through 3, wherein the phenylene ether oligomer has the structure: [ka] wherein R is methyl or hydrogen; x and y are independently 0 to 30, provided that the sum of x and y is at least 2; R 1 , R 2 、 R 3 , and R 4 Each event is independently hydrogen, halogen, unsubstituted or substituted C 1-12 Primary or secondary hydrocarbyl, C 1-12 Hydrocarbylthio, C 1-12 Hydrocarbyloxy, or C 2-12 halohydrocarbyloxy, where at least two carbon atoms separate the halogen and oxygen atoms, z is 0 or 1, and Y has a structure including: [ka] In the formula, R 7 Each event is independently hydrogen and C 1-12 Contains hydrocarbyl, R 8 and R 9 Each event is independently hydrogen, C 1-12 Hydrocarbyl, or C 1-6 is hydrocarbylene, R 8 and R 9 are collectively C 4-12 Forms an alkylene group, preferably R 1 and R 2 Each event is methyl, and R 3 and R 4 is hydrogen, z is 1, and Y is an isopropylidene group.

[0133] Embodiment 5: A method for producing the linear difunctional phenylene ether oligomer of any of embodiments 1 to 4, comprising oxidatively polymerizing 2-methyl-6-cyclohexylphenol in the presence of a catalyst to obtain a phenylene ether oligomer, and reacting the phenylene ether oligomer with a (meth)acrylate-containing compound to obtain the linear difunctional phenylene ether oligomer.

[0134] Embodiment 6: The method of embodiment 5, wherein the oxidatively polymerizing step is further in the presence of a bisphenol, preferably tetramethylbisphenol A.

[0135]

[0023] Embodiment 7: A curable thermosetting composition comprising the linear difunctional phenylene ether oligomer of any of embodiments 1 to 4.

[0136]

[0023] Example 8: The curable thermosetting composition of Example 7, further comprising one or more crosslinkers, curing agents, curing catalysts, curing initiators, or combinations thereof.

[0137]

[0036] Example 9: The curable thermosetting composition of example 7 or 8, further comprising one or more flame retardants, fillers, coupling agents, or combinations thereof.

[0138] Embodiment 10: A cured thermoset composition comprising a cured product of any one or more of the curable thermoset compositions of embodiments 7-9, wherein preferably the thermoset composition has a glass transition temperature of 165° C. or more, preferably 170° C. or more, more preferably 165 to 180° C., as determined using differential scanning calorimetry; the thermoset composition has a dielectric constant of less than 3.0, preferably less than 2.75, more preferably less than 2.6 at a frequency of 10 GHz; and the thermoset composition has a dielectric loss tangent of less than 0.01, or less than 0.005 at a frequency of 10 GHz.

[0139] Embodiment 11: A method for the production of the cured thermoset composition of embodiment 10, comprising curing the curable thermoset composition at a temperature preferably from 50 to 250° C.

[0140] Example 12: An article comprising the cured thermoset composition of Example 10, preferably the article is a composite, a foam, a fiber, a layer, a coating, an encapsulant, an adhesive, a sealant, a molded part, a prepreg, a casing, a casting, a laminate, or a combination thereof, or the article is a metal clad laminate, an electronic composite, a structural composite, or a combination thereof.

[0141] Embodiment 13: A varnish composition comprising the curable thermosetting composition of any one of embodiments 7 to 9, and a solvent.

[0142] Example 14: An article made from the varnish composition of Example 13, preferably a fiber, a layer, a coating, a casting, a prepreg, a composite, a laminate, or a metal clad laminate.

[0143] Embodiment 15: A method for producing the article of embodiment 14, comprising the steps of impregnating the varnish composition into a substrate to form a prepreg, and curing the varnish composition.

[0144] The compositions, methods, and articles may alternatively comprise, consist of, or consist essentially of any suitable materials, steps, or ingredients disclosed herein. The compositions, methods, and articles may additionally, or alternatively, be designed to be devoid of, or substantially free of, any materials (or species), steps, or ingredients that are not otherwise required for the function or achievement of the purpose of the compositions, methods, and articles.

[0145] All ranges disclosed herein are inclusive of the endpoints, and the endpoints are independently combinable with each other. "Combinations" include blends, mixtures, alloys, reaction products, and the like. The terms "first," "second," and the like do not denote an order, quantity, or importance, but rather are used to distinguish one element from another. The terms "a," "an," or "the" do not denote a limitation of quantity, and should be construed to encompass both the singular and the plural, unless otherwise stated herein or clearly contradicted by context. "Or" means "and / or," unless expressly stated otherwise. Throughout the specification, reference to "an embodiment" means that a particular element described in connection with an embodiment is included in at least one embodiment described herein, and may or may not be present in other embodiments. The term "combinations thereof," as used herein, includes and is not limited to one or more of the listed elements, allowing for the presence of one or more similar, unnamed elements. In addition, it should be understood that the described elements can be combined in any suitable manner in the various embodiments.

[0146] Unless specified to the contrary herein, all test standards are the latest standards in effect as of the filing date of this application or, if priority is claimed, the filing date of the earliest priority application in which the test standard appears.

[0147] Unless otherwise specified, technical and scientific terms used herein have the same meaning as commonly understood by those skilled in the art to which this application belongs. All cited patents, patent applications, and other references are incorporated herein by reference in their entirety. However, if a term in this application contradicts or conflicts with a term in the incorporated reference, the term in this application shall take precedence over the conflicting term in the incorporated reference.

[0148] Compounds are described using standard nomenclature. For example, any position that is not substituted by any indicated group is understood to have its valence filled by the indicated bond or hydrogen atom. A dash ("-") that is not between two letters or symbols is used to indicate the point of attachment for a substituent. For example, -CHO is attached through the carbon of a carbonyl group.

[0149] As used herein, the term "hydrocarbyl", whether used by itself or as a prefix, subscript, or fragment of another term, refers to a residue containing only carbon and hydrogen. The residue can be aliphatic or aromatic, straight-chain, cyclic, bicyclic, branched, saturated, or unsaturated. It can also contain a combination of aliphatic, aromatic, straight-chain, cyclic, bicyclic, branched, saturated, and unsaturated hydrocarbon moieties. However, when a hydrocarbyl residue is described as substituted, it may optionally contain heteroatoms in addition to the carbon and hydrogen members of the substituted residue. Thus, when specifically described as substituted, the hydrocarbyl residue can also contain one or more carbonyl groups, amino groups, hydroxyl groups, etc., or can contain heteroatoms within the backbone of the hydrocarbyl residue. The term "alkyl" refers to branched or straight-chain, saturated aliphatic hydrocarbon groups, such as methyl, ethyl, n-propyl, i-propyl, n-butyl, s-butyl, t-butyl, n-pentyl, s-pentyl, and n- and s-hexyl. "Alkenyl" means a straight or branched chain, monovalent hydrocarbon group having at least one carbon-carbon double bond, such as ethenyl (-HC=CH2). "Alkoxy" means an alkyl group linked through an oxygen (i.e., alkyl-O-), such as methoxy, ethoxy, and sec-butyloxy groups. "Alkylene" means a straight or branched chain, saturated, divalent aliphatic hydrocarbon group, such as methylene (-CH2-) or propylene (-(CH2)3-). "Cycloalkylene" means a divalent cyclic alkylene group, -C n H 2n-xwhere x is the number of hydrogens replaced by the cyclization(s). "Cycloalkenyl" means a monovalent group having one or more rings and one or more carbon-carbon double bonds within the rings, all ring members being carbon (e.g., cyclopentyl and cyclohexyl). "Aryl" means an aromatic hydrocarbon group containing the specified number of carbon atoms, e.g., phenyl, tropone, indanyl, or naphthyl. "Arylene" means a divalent aryl group. "Alkylarylene" means an arylene group substituted with an alkyl group. "Arylalkylene" means an alkylene group substituted with an aryl group (e.g., benzyl). The prefix "halo" means a group or compound containing one or more fluoro, chloro, bromo, or iodo substituents. A combination of different halo atoms (e.g., bromo and fluoro) or only chloro atoms can be present. The prefix "hetero" means that the compound or group contains at least one ring member that is a heteroatom (e.g., 1, 2, or 3 heteroatoms), where the heteroatom(s) are each independently N, O, S, Si, or P. "Substituted" means that the compound or group contains, each independently, C, H, or C, in place of a hydrogen. 1-9 Alkoxy, C 1-9 Haloalkoxy, nitro (-NO2), cyano (-CN), C 1-6 Alkylsulfonyl (-S(=O)2-alkyl), C 6-12 Arylsulfonyl (-S(=O)2-aryl), thiol (-SH), thiocyano (-SCN), tosyl (CH3C6H4SO2-), C 3-12 Cycloalkyl, C 2-12 Alkenyl, C 5-12 Cycloalkenyl, C 6-12 Aryl, C 7-13 Aryl alkylene, C 4-12 Heterocycloalkyl, and C 3-12 It means substituted with at least one (e.g., 1, 2, 3, or 4) substituents, which may be heteroaryl, provided that the standard valence of the substituted atom is not exceeded. The number of carbon atoms indicated in the group excludes any substituents. For example, -CH2CH2CN is a C2 alkyl group substituted with a nitrile.

[0150] While particular embodiments have been described, presently unanticipated or unforeseen alternatives, modifications, variations, improvements, and substantial equivalents may occur to the applicant or those skilled in the art, and it is therefore intended that the appended claims, as filed and as they may be amended, shall cover all such alternatives, modifications, variations, improvements, and substantial equivalents.

Claims

1. A linear difunctional phenylene ether oligomer containing repeat units derived from 2-methyl-6-cyclohexylphenol and having (meth)acrylate end groups.

2. 10. The difunctional phenylene ether oligomer of claim 1, wherein said phenylene ether oligomer comprises less than 30 weight percent of repeat units derived from a monohydric phenol having identical substituents at the 2- and 6-positions.

3. The phenylene ether oligomer according to claim 1 or 2, wherein the repeating unit derived from 2-methyl-6-cyclohexylphenol has the following structure: 【Chemistry 1】

4. The phenylene ether oligomer has the structure: 【Chemistry 2】 During the ceremony, R is methyl or hydrogen; x and y are independently 0 to 30, provided that the sum of x and y is at least 2; R １ , R ２ , R ３ , and R ４ Each event is independently hydrogen, halogen, unsubstituted or substituted C １－１２ Primary or secondary hydrocarbyl, C １－１２ Hydrocarbylthio, C １－１２ Hydrocarbyloxy, or C ２－１２ halohydrocarbyloxy, wherein at least two carbon atoms separate the halogen and oxygen atoms; z is 0 or 1; Y has a structure including: 【Chemistry 3】 In the formula, R ７ Each event is independently hydrogen and C １－１２ Contains hydrocarbyl, R ８ and R ９ Each event is independently hydrogen, C １－１２ Hydrocarbyl, or C １－６ is hydrocarbylene, R ８ and R ９ are collectively C ４－１２ Forming an alkylene group, Preferably, R １ and R ２ Each event of R is methyl; ３ and R ４ The phenylene ether oligomer of claim 1 or 2, wherein each occurrence of is hydrogen, z is 1, and Y is an isopropylidene group.

5. A method for producing the linear difunctional phenylene ether oligomer according to claim 1 or 2, comprising the steps of: oxidatively polymerizing 2-methyl-6-cyclohexylphenol in the presence of a catalyst to obtain a phenylene ether oligomer; and reacting the phenylene ether oligomer with a (meth)acrylate-containing compound to obtain the linear difunctional phenylene ether oligomer; The method includes:

6. 6. The method of claim 5, wherein the oxidative polymerizing step is further in the presence of a bisphenol, preferably tetramethylbisphenol A.

7. A curable thermosetting composition comprising the linear difunctional phenylene ether oligomer of claim 1 or 2.

8. 8. The curable thermosetting composition of claim 7, further comprising one or more crosslinkers, curing agents, curing catalysts, curing initiators, or combinations thereof.

9. 8. The curable thermosetting composition of claim 7, further comprising one or more flame retardants, fillers, coupling agents, or combinations thereof.

10. A cured thermoset composition comprising the cured product of the curable thermoset composition of claim 7.

11. 11. A method for the preparation of a cured thermoset composition according to claim 10, comprising the step of curing the curable thermoset composition, preferably at a temperature of from 50 to 250°C.

12. 11. An article comprising the cured thermoset composition of claim 10, Preferably, the article is a composite, a foam, a fiber, a layer, a coating, an encapsulant, an adhesive, a sealant, a molded part, a prepreg, a casing, a casting, a laminate, or a combination thereof; or The article is a metal clad laminate, an electronic composite, a structural composite, or a combination thereof.

13. A curable thermosetting composition according to claim 7, and solvent A varnish composition comprising:

14. 14. An article made from the varnish composition of claim 13, preferably said article being a fiber, a layer, a coating, a casting, a prepreg, a composite, a laminate, or a metal clad laminate.

15. 15. A method for the manufacture of the article of claim 14, comprising the steps of impregnating a substrate with the varnish composition to form a prepreg, and curing the varnish composition.