Use of high density paper substrate, coated high density substrate, and laminated packaging material and packaging container containing same

Abstract

The present invention relates to the use of a high density paper substrate (35a) made from cellulose fibers as a gas barrier material in a laminate packaging material (30) for packaging oxygen sensitive products, and further to a coated high density paper substrate (35) for enhancing the gas barrier properties. The present invention further relates to a laminate packaging material (30) comprising the high density paper substrate or the coated high density paper substrate, and a packaging container made from the laminate packaging material for packaging oxygen sensitive products.

Description

[Technical field]

[0001] The present invention relates to the use of a high density paper substrate made from cellulose fibers as a gas barrier material in a laminate packaging material for packaging oxygen sensitive goods such as oxygen sensitive foods, liquid, semi-liquid or viscous foods or water, and further to a coated high density paper substrate for enhancing the gas barrier properties.The present invention further relates to a laminate packaging material comprising a coated or uncoated high density paper substrate, and a packaging container comprising the laminate packaging material for packaging oxygen sensitive goods. [Background technology]

[0002] Single-use packages for liquid foods are often manufactured from paperboard or carton-based packaging laminates. One such commonly used package is sold under the trademark "Tetra Brik Aseptic" and is primarily employed for the aseptic packaging of liquid foods such as milk, fruit juices, etc., sold for long-term ambient storage. The packaging material of this known package is usually a laminate comprising a bulk or core layer of paper, paperboard or other cellulose-based material and a liquid-tight outer layer of thermoplastic. To make the package gas-tight, and in particular oxygen-tight, for the purposes of aseptic packaging or packaging of, for example, milk or fruit juice, these laminates usually comprise at least one additional layer, most commonly aluminum foil.

[0003] On the inside of the laminate, i.e. the side intended to face the filled food contents of the container produced from the laminate, there is an innermost layer applied onto the aluminum foil, which comprises one or more partial layers comprising adhesive polymers and / or heat-sealable thermoplastic polymers such as polyolefins, and, outside the bulk layer, there is an outermost heat-sealable polymer layer.

[0004] Packaging containers are generally produced by modern high-speed packaging machines of the type that form, fill and seal packages from webs of packaging material or prefabricated blanks. The packaging containers are produced by joining the longitudinal edges of a web of laminate packaging material together at overlap joints by welding together the inner and outer heat-sealable thermoplastic polymer layers, converting it into a tube. The tube is filled with the desired liquid food product and then divided into individual packages by repeatedly transversely sealing the tube at a predetermined distance from each other below the level of the contents in the tube. The packages are separated from the tube by scoring along the transverse seals and formed into the desired geometric shape, usually a parallelepiped shape, by creating creases in the packaging material along pre-prepared crease lines.

[0005] The main advantage of this continuous tube forming, filling and sealing packaging process concept is that the web can be continuously sterilized just before tube formation, offering the possibility of an aseptic packaging process, i.e. a process in which the liquid contents to be filled and the packaging material itself are reduced from bacteria and the filled packaging containers are produced under clean conditions so that they can be stored for long periods even at ambient temperature without risk of microbial growth in the filled product. Another important advantage of Tetra Brik® type packaging processes is that they allow continuous high speed packaging, which, as mentioned above, has a great impact on cost efficiency.

[0006] Packaging containers for sensitive liquid foods, such as milk and juice, can also be produced from sheet blanks or preassembled blanks of the laminate packaging material of the invention. Packages are produced from flat-folded tubular blanks of the packaging laminate by first assembling the blanks to form an open tubular container capsule, one open end of which is closed by folding and heat sealing an integral end panel. The container capsule thus closed is filled from the other open end with a food product, such as juice, and is then closed by further folding and heat sealing the corresponding integral end panel. Examples of packaging containers produced from sheet and tubular blanks are the conventional so-called gable top packages. Packages of this type can also be provided with a molded plastic top and / or a screw cap.

[0007] The aluminum foil layer of the packaging laminate provides gas barrier properties that are significantly superior to other gas barrier materials. At their performance levels, conventional aluminum foil-based packaging laminates for aseptic packaging of liquid foods are the most cost-effective packaging materials available on the market today.

[0008] Other materials that compete with foil-based materials need to be cost-effective in terms of raw materials, have comparable food preservation properties, and require relatively low complexity in converting the material into the finished packaging laminate.

[0009] Among the efforts to develop non-aluminum foil materials for liquid food carton packaging, there is also a general drive to develop prefabricated films or sheets with high or multiple barrier properties that can replace aluminum foil barrier materials in traditional laminate packaging materials, or combine multiple separate barrier layers in laminate materials and be compatible with traditional processes for lamination and manufacturing.

[0010] A preferred type of such alternative, more environmentally sustainable barrier material is a barrier coated paper substrate made by aqueous dispersion coating or vapor deposition coating onto a thin paper carrier substrate. There are various aqueous dispersion coating processes, vapor deposition coating processes and material recipes for such coatings, and there is a need for cost-effective barrier materials of the "non-foil" type, i.e., non-aluminum foil, with improved barrier properties, especially against gases such as oxygen gas, for use in packaging laminates for liquid food packaging.

[0011] Patent publication WO2011 / 003565A1 discloses a non-aluminium foil packaging material comprising a pre-coated metallized paper or cellulose-based substrate intended for induction heat sealing.

[0012] Patent publication WO2017 / 089508A1 discloses that improved barrier properties can be obtained in a similar manner from metallized paper in similar packaging laminates by selecting a paper substrate that provides optimal properties. Such metallized paper substrates not only provide improved barrier properties, but also exhibit better stability of the metallized layer for induction heat sealing purposes.

[0013] However, there remains a need to further improve the oxygen gas barrier properties of prior art gas barrier coated paper substrates, and there is also an increasing need to improve the recyclability and environmental sustainability properties of materials used in gas barrier coated paper substrates and laminated packaging materials containing same. Summary of the Invention [Problem to be solved by the invention]

[0014] It is therefore an object to use an improved paper substrate that contributes to good gas barrier properties of laminated packaging materials that include aluminum foil-free (non-foil) paper substrates for packaging oxygen-sensitive products.

[0015] It is also an object to provide an improved barrier coated paper substrate that contributes to the excellent gas barrier properties, as well as improved recyclability and environmental sustainability of such non-foil laminate packaging materials.

[0016] It is a further object to provide a non-foil laminate packaging material for oxygen sensitive products, such as aqueous liquid, semi-liquid or viscous foods, in a package that does not contain aluminum foil and provides good barrier and gas barrier properties.

[0017] The present invention aims to provide a cost-effective, foil-free, paper- or paperboard-based laminated packaging material that has superior gas and water vapour barrier properties, recyclability and environmental sustainability compared to aluminium foil barrier materials, for the manufacture of packages for long-term aseptic storage of liquid foods.

[0018] It is a further object of the present invention to provide a cost-effective, non-foil, paper or board based, mechanically robust, heat-sealable packaging laminate with good gas and water vapour barrier properties and good interlayer adhesion for the production of aseptic packaging containers for the long term storage of liquid foods with maintained nutritional quality under ambient conditions.

[0019] These objects can be achieved according to the present invention by the use of an improved paper substrate, a barrier coated paper substrate, a laminated packaging material comprising the improved paper substrate or the barrier coated paper substrate, and a packaging container made from the laminated packaging material, as defined in the appended claims. [Means for solving the problem]

[0020] According to a first aspect of the present invention, there is provided the use of a high density paper substrate made from cellulose fibers as a gas barrier material in a laminate packaging material for packaging oxygen sensitive products, such as oxygen sensitive foods, as well as liquid, semi-liquid or viscous foods or water. The high density paper substrate has a basis weight of 30 to 75 g / m2 measured according to ISO 536:2012. 2and has a density of 1000 kg / m3 measured according to ISO 534:2011 3 and the upper surface of the paper is impregnated with an impregnation composition comprising an impregnation polymer selected from the group consisting of polyvinyl alcohol, PVOH, ethylene vinyl alcohol, EVOH, starch, starch derivatives, carboxymethyl cellulose, nanocrystalline cellulose, NCC, and blends of two or more thereof, and the amount of the impregnation polymer is 0.3 to 4.0 g / m2 by dry weight. 2 , for example 0.5 to 4.0 g / m 2 , for example 0.5 to 3.0 g / m 2 It is.

[0021] Such a high density paper substrate can be obtained by impregnating at least the upper surface of the formed and dried paper with an aqueous impregnating composition comprising a water-soluble or water-dispersible polymer in a concentration of 5-20% by weight, for example 5-15% by weight, for example 7-13% by weight, for example 8-12% by weight, impregnated by a size press or film press operation or the like, thereafter calendering and drying the paper thus impregnated, so that the resulting density is 1000 kg / m 3 Such a high density is preferably obtained by supercalendering. Thus, the high density paper substrate of the present disclosure is preferably supercalendered. In one embodiment, the density is at least 1050 kg / m 3 , e.g., at least 1070 kg / m 3 A typical upper limit for density is 1300 kg / m 3 It could be.

[0022] In a further embodiment of the use of the first aspect, the upper surface of the high density paper has acquired a roughness lower than 100 ml / min Bendtsen by a calendering operation, such as a supercalendering operation.

[0023] By impregnating the top surface of the paper with an impregnation composition containing one or more of the listed polymers, the porous network of cellulose fibers, at least at the surface of the paper and below, may be filled and surrounded by the polymer when the paper is calendered, which binds and locks the fibrous material more tightly with fewer voids (due to the polymer being slightly more elastic than the cellulose fibers), thus avoiding the opening of inter-fiber channels through the material when the material is mechanically abused by folding and twisting. This is firstly due to the pore-filling effect of the polymer, which has a high affinity for cellulose, and secondly due to the polymer fixing the fibers together, which has a direct effect on gas and oxygen molecules trying to diffuse through the porous material. In addition, the pore-filling polymer has the correct effect of leveling the irregularities of the fibrous surface of the paper and preparing the surface to provide a non-porous and well-defined interface for further aqueous dispersion barrier coatings and polymer extrusion coatings, in improving the gas barrier properties of dense paper substrates. This eliminates air entrapment at the interface, which can cause coating defects and compromise the air tightness of the laminate.

[0024] According to a second aspect of the present invention there is provided a coated high density paper substrate for use as a gas barrier material in a laminate packaging material for oxygen sensitive products, such as oxygen sensitive foods, as well as liquid, semi-liquid or viscous foods or water, the upper surface of the high density paper substrate for use according to the first aspect having at least one coating of at least one gas barrier material having a total coating thickness of from 2 to 4000 nm, for example from 2 to 3500 nm.

[0025] In one embodiment, the top side of the paper substrate is coated with a gas barrier material comprising a polymer to a dry coating thickness of 100-5000 nm (0.1-5 μm), such as 100-4000 nm (0.1-4 μm), such as 300-3500 nm (0.3-3.5 μm), such as 300-2500 nm (0.3-2.5 μm), the polymer being a binder polymer or coating polymer selected from the group consisting of vinyl alcohol polymers and copolymers selected from the group consisting of polyvinyl alcohol, PVOH, ethylene vinyl alcohol, EVOH, starch and starch derivatives, nanofibril / microfibril cellulose, NFC, MFC, nanocrystalline cellulose, NNC, and blends of two or more thereof. The coating of the gas barrier material may be obtained by dispersion or solution coating of the aqueous gas barrier composition followed by drying.

[0026] According to another embodiment, the gas barrier material may be a water-dispersible polyamide or polyester, or polyvinylidene chloride. Preferably, such water-dispersible polyamide, polyester or polyvinylidene chloride is bio-based and / or can be applied in very small amounts of coating, i.e. less than 1 g / m 2 Only a very thin coating layer, such as less than 1.5 μm, can reinforce the oxygen gas barrier properties of the high density paper substrate.

[0027] In another embodiment, the upper surface of the paper substrate has a vapor-deposited coating of a gas barrier material selected from metals, metal oxides, inorganic oxides, and amorphous diamond-like carbon coatings.

[0028] When the impregnated surface of the paper is further coated with a conventional coating layer, the effect of improving the oxygen barrier property is further enhanced, and even very thin coatings can provide excellent barrier properties. The gas barrier action of thin coatings, such as coatings provided by dispersion or solution coating of gas barrier compositions, only a few micrometers thick, or coatings by deposition coating processes with nanometer thickness, such as PECVD, PVD, CVD and atmospheric plasma processes, is strengthened and protected by the effect of the impregnated and pore-filled paper substrate. In addition, the filled voids and the smoothing layer of the polymer reduce the surface roughness of the impregnated paper substrate, greatly improving the quality of the applied gas barrier coating, reducing pinholes and providing a uniform coating thickness. Thus, when a high-density paper substrate is used for laminated packaging materials or packages for oxygen barrier purposes, when further coated with a coating of gas barrier material, the combination of positive effects and mechanisms can provide even more significantly improved results.

[0029] According to a third aspect of the present invention, there is provided an improved laminate packaging material for packaging oxygen sensitive products such as oxygen sensitive foods, liquid, semi-liquid or viscous foods or water, comprising a high density paper substrate or further a gas barrier coated high density paper substrate. The laminate packaging material may further comprise a first outermost liquid-tight material layer and a second innermost liquid-tight material layer.

[0030] For the purpose of carton packaging of liquid or viscous food products, the laminate packaging material may further comprise a bulk layer of paper or paperboard or other cellulosic material, a first outermost liquid-tight material layer, a second innermost liquid-tight material layer, and a high density paper substrate or a gas barrier coated high density paper substrate disposed inside the bulk layer of paper or paperboard and between the bulk layer and the second innermost liquid-tight material layer, which may further be a heat sealable material layer.

[0031] According to a fourth aspect of the present invention, there is provided a packaging container for packaging oxygen-sensitive foods and oxygen-sensitive products such as liquid, semi-liquid or viscous foods or water, consisting of the laminate packaging material of the present invention, intended for packaging oxygen-sensitive products. In particular, a packaging container for packaging liquid, semi-solid or viscous foods is provided. According to one embodiment, the packaging container is at least partially manufactured from the laminate packaging material of the present invention, and according to a further embodiment, the packaging container is entirely manufactured from the laminate packaging material.

[0032] The use of a high-density paper substrate as described above, and further application of a gas barrier coating to such a high-density paper substrate, improves the gas barrier properties of the laminated packaging material and the packaging container using the same, and also improves water repellency and recyclability, i.e., sustainability.

[0033] Generally, the use of high density paper substrates in such laminate materials and packages results in a high percentage of fiber content that is renewable, i.e., of non-fossil origin, recyclable or biodegradable, allowing old materials to be recycled into the production of new materials. Furthermore, the use of such paper substrates as "facing layers in a sandwich construction" supports the use of bulk materials with lower bending stiffness, lower fiber quality and lower cost, or allows the use of bulk materials with lower density and lower fiber usage by laminating such facing layers on both sides of the bulk layer.

[0034] Additionally, the paper substrate for the gas barrier material coating of such materials and packages also improves the robustness of the pre-cut apertures that are laminated, i.e., pre-cut into the bulk layer, but then laminated with all other layers of the laminate, including the paper substrate.

[0035] (Detailed Description) The term "long-term storage" as used in the context of the present invention means that the packaging container is capable of preserving the quality, i.e. nutritional value, hygienic safety and taste, of the packaged food at ambient temperature conditions for at least 1 or 2 months, such as at least 3 months, preferably 6 months, such as 12 months or more.

[0036] The term "package integrity" generally refers to the tightness of the package, i.e., the resistance of the packaging container to leakage or breakage. The term encompasses the resistance of the package to the ingress of bacteria, dirt, and other microorganisms that may deteriorate the food contained therein and shorten the expected shelf life of the package.

[0037] One major contribution to the package integrity of laminate packaging materials is provided by good internal adhesion between adjacent layers of laminate material, which also contributes to the resistance of the material to defects such as pinholes, breaks, etc. in each layer, and also to the strength of the seal joints where the material is sealed when the package is formed. Thus, with respect to the integrity of the laminate packaging material itself, the focus is on the adhesion of each laminate layer to its adjacent layers, and the quality of each material layer. With respect to the sealing of the package, the integrity is mainly focused on the quality of the seal joints, which is ensured by a well-functioning and robust sealing operation in the filling machine, which is further ensured by the properly matched heat seal properties of the laminate packaging material.

[0038] The term "liquid or semi-liquid food" generally refers to food with a flowable content that may optionally contain food particles. Dairy and milk, soy, rice, grain and seed drinks, juice, nectar, soft drinks, water, flavored water, energy drinks, sports drinks, coffee or tea drinks, coconut water, wine, soup, jalapeno, tomato, sauces (such as pasta sauce), soy and olive oil are some non-limiting examples of foods that are contemplated.

[0039] Other examples of oxygen-sensitive foods that can be packaged and protected with the laminate packaging material of the present disclosure are, for example, dry foods and / or fatty foods. Examples of fatty foods include cheese, butter, spreads, etc. Such packaging can be, for example, flow-wrap packaging in bags or form, fill, seal (FFS) packaging. It can also be packaging in jars, trays, spread containers with lids, collapsible tubes, clamshell packages, sleeves, envelopes, or wrappers. Another application is as a packaging window. In these applications, the packaging material is usually subjected to folding or similar types of stress (e.g., creases, stretching), for which the high density paper-based packaging material of the present disclosure is particularly suitable.

[0040] The term "sterile" in relation to packaging materials and containers refers to a state in which microorganisms have been removed, inactivated, or killed. Examples of microorganisms include bacteria and spores. Generally, when a product is filled aseptically into a packaging container, an aseptic process is used. In order to maintain the sterility during the shelf life of the packaging container, the integrity properties of the package are very important. For the long-term storage of the filled food, and also to preserve the original taste and nutritional value, e.g., vitamin C content, it is important to have a barrier property against gases such as oxygen gas and vapors.

[0041] The term "bulk layer" usually refers to the thickest layer or layer containing the most material in a multi-layer laminate, i.e., the layer that contributes most to the mechanical properties and dimensional stability of the laminate and the packaging container folded from the laminate, e.g., paperboard, carton, etc. It can also refer to the layer that provides a larger thickness distance in a sandwich structure that further interacts with stabilizing facing layers having a higher Young's modulus on either side of the bulk layer to achieve sufficient mechanical properties of the formed packaging container.

[0042] Thickness measurements were performed by transmission electron microscopy using a Titan 80-300, FEI Instruments. Samples may be prepared by ultramicrotomy on a Leica EM UC6 Microtome.

[0043] OTR was measured using a coulometric sensor-based Oxtran 2 / 21 (Mocon) instrument according to ASTM F1927-14 and ASTM F1307-14. See further description of the OTR test method in connection with the examples.

[0044] Thus, there is provided the use of a high density paper substrate made from cellulose fibers as a gas barrier material in a laminate packaging material for packaging oxygen sensitive products such as oxygen sensitive foods, as well as liquid, semi-liquid or viscous foods or water, wherein the high density paper substrate has a basis weight of 30 to 75 g / m2, measured according to ISO 536:2012. 2 and has a density of 1000 kg / m3 measured according to ISO 534:2011 3 and on the upper surface of the paper substrate, the paper substrate is impregnated with an impregnation composition comprising an impregnation polymer selected from the group consisting of polyvinyl alcohol, PVOH, ethylene vinyl alcohol, EVOH, starch, starch derivatives, carboxymethyl cellulose, nanocrystalline cellulose, NCC, and blends of two or more thereof, and the amount of the impregnation polymer is 0.5 to 4.0 g / m2 in terms of dry weight. 2 , for example, 0.5 to 3.0 g / m 2 It is.

[0045] According to one embodiment, the impregnation composition comprises a majority, i.e., at least 50% by weight, of an impregnation polymer selected from PVOH, EVOH starch and starch derivatives, which materials are relatively easy to handle and relatively easy to prepare as low viscosity solutions suitable for impregnation, and are also relatively cost-effective. Impregnation compositions comprising a majority, i.e., at least 50% by weight, of an impregnation polymer selected from PVOH and EVOH are preferred, as they generally provide better oxygen barrier properties within this group.

[0046] The degree of hydrolysis of the PVOH may be 96% to 100%, such as 97% to 100%, for example 97% to 99%. PVOH with a high degree of hydrolysis is less sensitive to water and is preferred both during production and use. The weight average molecular weight (Mw) of the PVOH is preferably less than 100,000 g / mol, for example 10,000 to 90,000 g / mol, for example 30,000 to 80,000 g / mol. Such a relatively low Mw is preferred during impregnation, since it has a relatively low viscosity at a relatively high concentration. PVOH with a low Mw has a greater tendency to penetrate into the fiber web or paper substrate, rather than remaining on the surface of the paper.

[0047] The viscosity of the PVOH, measured according to DIN 53015, is preferably less than 20 mPa·s, for example from 5 to 16 mPa·s, for example from 6 to 13 mPa·s.

[0048] The degree of polymerization (DP) of PVOH is preferably less than 3000, for example, 1000 to 2000. The DP can be determined from the viscosity average degree of polymerization obtained from the viscosity in water. In this case, the viscosity is measured in a 4% aqueous solution at 20°C using a Brookfield synchronized-motor rotary type viscometer.

[0049] An example of a suitable PVOH is Kuraray's Poval 10 / 98, which has a viscosity of 10 mPa s, a degree of hydrolysis of 98%, a DP of about 1400, and a Mw of about 61,000 g / mol. Another suitable example is Kuraray's Poval 6 / 98, which has a viscosity of 6 mPa s and a degree of hydrolysis of 98%.

[0050] For some applications, it may be beneficial to choose EVOH as the impregnating polymer. EVOH has good moisture resistance and good oxygen barrier properties. An example of a suitable low viscosity formulation of EVOH is Kuraray's Exceval® AQ-4104.

[0051] As mentioned above, the impregnation composition may contain a significant amount of nanocrystalline cellulose, "NCC" (or "CNC"), or a blend of NCC with starch or PVOH, adjusted to a suitable viscosity for impregnation. NCC is attractive as a future barrier material in packaging because it is a cellulose and may provide good oxygen barrier properties, but may not currently be a cost-effective alternative for large-scale use.

[0052] Nanocrystalline cellulose (NCC) is a form of nanocellulose, but is distinct from microfibril cellulose (MFC) (CMF) and nanofibril cellulose (NFC) (CNF). The term "MFC" is commonly and sometimes incorrectly used for any type of fibrillated cellulose, but the more scientific view is that "MFC" refers to nanoscale cellulose particle fibers or fibrils or fibril aggregates with at least one dimension less than 100 nm.

[0053] Thus, MFC may include longer particles, so-called "fibrils", having a width of 10-100 nm and a length of at least 1 μm, such as up to 10 μm, for example a length of more than 10 μm.

[0054] Both MFC and NFC have aspect ratios of 50 or greater, while NCC is sometimes defined as having an aspect ratio of less than 50, for example, according to the TAPPI draft standard WI3021.

[0055] The term "NCC" is used for shorter particles and "rod-like" particles having a width of 3-50 nm and a length of 100-1000 nm, e.g. 100-900 nm, e.g. 100-500 nm, e.g. 100-200 nm. The preferred size of the NCC for the purpose of impregnating and filling the pores of the formed paper means that the majority of the NCC particles in the composition should have this size, and may have a length of 100-500 nm, e.g. 100-200 nm, and a small width of 3-50 nm.

[0056] In one embodiment, the amount of impregnating polymer is 1 to 2 g / m2 by dry weight. 2 The upper surface is at least 1.5 or 2 g / m 2 The impregnation composition may essentially comprise only water and the impregnation polymer.

[0057] Depending on the selection of the type of cellulose fiber on the back side, the back side may also be impregnated. The polymer impregnation may completely impregnate the cellulose voids throughout the thickness of the paper, or only a portion of the thickness, or only the center / middle of the thickness. It is considered desirable to impregnate as much polymer as possible to give the high density paper substrate optimal gas barrier properties. However, the amount of impregnated polymer needs to be balanced with the repulping properties of the paper so that the paper is useful in the recycling process after use. It may also be preferable to impregnate both sides of the paper to avoid curling of the dried paper substrate, which can cause problems in subsequent coating and lamination operations.

[0058] Thus, "impregnated" means that the impregnation composition and impregnating polymer have penetrated the fibrous web to a substantial extent, i.e., have penetrated the cellulose fibers of the paper substrate to a substantial extent. However, it does not necessarily mean that the fibrous web is completely saturated with polymer throughout its thickness. As a result, the high density paper may contain unfilled pores, especially in the center. See also the explanation of FIG. 1f below. Thus, the SEM image of the cross section of the high density paper allows one to determine that the impregnating polymer has penetrated the fibrous web rather than forming a coating layer on the surface. In this way, the high density paper substrate and the fibrous web are impregnated with a polymer of 0.3 to 4.0 g / m 2 , for example 0.3 to 3.0 g / m 2 The coated substrate is impregnated with an impregnation composition comprising an impregnation polymer in an amount of 0.1 to 1.0 μg / g.

[0059] To facilitate application and impregnation of the polymer, it is water-soluble or water-dispersible.

[0060] The extent and depth of polymer impregnation throughout the thickness of the dense paper substrate can be examined by taking sliced ​​cross-sectional samples of the paper and examining them under a SEM microscope. Slicing can be done, for example, using a cryomicrotome.

[0061] The type of polymer used in the impregnation composition may be determined by FTIR spectroscopy or a combination of FTIR and other spectroscopic techniques.

[0062] The high density paper substrate for use in the present invention may be formed from cellulosic fibers comprising at least 50% by dry weight of a chemical pulp such as kraft pulp or sulfite pulp, for example at least 75% by dry weight of chemical pulp, for example at least 85% by dry weight of chemical pulp, for example at least 90% by dry weight of chemical pulp, for example at least 95% by dry weight of chemical pulp. The sulfate or sulfite pulp is used to provide a paper that is strong enough for downstream processes such as coating (sometimes at high speeds) and for final packaging processing and use.

[0063] Sulfate / kraft pulps may be preferred because they are widely produced in large quantities. However, sulfite pulps may be useful because they are generally easier to refine than sulfate pulps. Sulfite pulps have a higher degree of fiber swelling, which is a disadvantage from a drying standpoint (higher energy requirements during drying) but an advantage from a density standpoint (swelling improves fiber compliance, resulting in denser sheets). Kraft pulps are advantageous for improved repulping in recycling and for general dewatering of fibers. Sulfite fibers usually have a higher percentage of refined fibers, which may have a slightly adverse effect depending on the amount and degree of refinement. Therefore, according to one embodiment of the present invention, kraft pulps may be preferred.

[0064] The high density paper substrate may be formed from cellulose fibers containing 35-100%, such as 35-80%, such as 40-70%, softwood pulp, 0-65%, such as 20-65%, such as 30-60%, hardwood pulp, and optionally 0-15%, such as 0-10%, CTMP pulp, based on the dry weight of the pulp used to form the high density paper. Thus, the high density paper substrate may be formed from cellulose fibers containing 35-80%, such as 40-70%, softwood pulp, 20-65%, such as 30-60%, hardwood pulp, and optionally 0-15%, such as 0-10%, CTMP pulp, based on the dry weight of the pulp used to form the high density paper.

[0065] The advantage of including hardwood pulp is that it disintegrates relatively easily during refining, while allowing efficient dewatering in the wire section of the paper machine. The advantage of including softwood pulp is that it improves runnability on the paper machine and improves the strength / toughness properties of the resulting paper. The latter property may be improved by subjecting the softwood pulp to high consistency (HC) refining.

[0066] Such a pulp composition is advantageous for the general dewatering properties in the repulping and papermaking processes in recycling, as well as for the high quality of the regenerated fibers. When the proportion of softwood pulp is relatively high, for example at least 60%, for example at least 70%, it is advantageous for the pulp used in the manufacture of paper to have a Schopper-Riegler (SR) number, measured according to ISO 5267-1:1999, of 25 to 35. Such an SR number can promote a sufficiently high density without causing problems in dewatering and / or recycling, and may be obtained by adjusting the degree of low consistency (LC) refining.

[0067] If the SR number is greater than 35, it becomes difficult to dewater the diluted pulp fast enough in the forming section. If the SR number is less than 25, the final product generally has poor properties. If the consistency of the diluted pulp is greater than 0.9%, there is a risk that the paper will become too porous and the paper surface will be too rough to produce an impregnated high density paper base for use in the present application.

[0068] If the proportion of hardwood pulp contained in the furnish is relatively high, e.g., at least 65% by dry weight hardwood pulp, e.g., at least 75% by dry weight hardwood pulp, the Schopper-Riegler (SR) number, measured in accordance with ISO 5267-1:1999, may be between 33 and 45. Such SR numbers may facilitate sufficiently high densities without causing problems in dewatering and / or recycling, and may be obtained by adjusting the degree of low consistency (LC) refining.

[0069] The pulp may be diluted to a consistency of 0.1% to 0.5%, such as 0.1% to 0.4%, to reduce fiber clumping which reduces the porosity of the final paper.

[0070] Preferably, the softwood fibers used in the high density paper substrate are subjected to high consistency (HC) refining so that the fibers acquire some inherent ductility or stretchability in the high density paper substrate.

[0071] When softwood pulp is used, it may be high consistency (HC) refined, i.e. refined at a consistency of 20% to 40%, for example 25% to 38%, i.e. weight concentration of dry fiber in the pulp. The specific energy of the HC refining step may be at least 100 kWh / ton, for example at least 150 kWh / ton, for example 150 to 300 kWh / ton. The unit "ton" means ton of dry fiber.

[0072] The pulp may be bleached, which reduces the concentration of elements or compounds that cause contamination and / or odor in the final package.

[0073] Thus, the high density paper may be formed by providing a pulp comprising at least 50% by dry weight of a chemical pulp such as kraft pulp or sulfite pulp having a Shopper-Riegler of 25-50, e.g. 25-45, e.g. 25-35, diluting the pulp to a low consistency of 0.1-0.9%, forming a paper web from the diluted pulp in a forming section, and dewatering the formed paper web in a press section to obtain an intermediate dry matter content. The pulp may comprise less than 10% by dry weight, e.g. less than 5%, e.g. less than 3%, e.g. less than 1%, of pigments or inorganic fillers to further improve water repellency and dewaterability, or may be substantially free of pigments or inorganic fillers, e.g. less than 3% by dry weight, e.g. less than 1%. Silica or bentonite used as a retention agent is typically in an amount of less than 1 kg per tonne of dry pulp and is not considered an inorganic filler. Thus, the ash content of the pulp according to ISO 2144:2015 is preferably less than 5%, e.g. less than 3%, e.g. less than 1%.

[0074] The formed paper web may then be dried in a drying section to a low moisture content of 4-7% and then surface impregnated with an aqueous composition comprising a water-soluble or water-dispersible polymer, such as in a size press or film press operation. Reducing the moisture content prior to impregnation allows for the pores of the web to be filled.

[0075] The impregnation step may include adding an aqueous composition containing an impregnating polymer to each side of the paper substrate. The aqueous composition may have a viscosity measured at 60° C. of 55 to 90 mPa·s. Such a relatively low viscosity facilitates the penetration of the polymer into the fibrous web. The concentration of the impregnating polymer in the aqueous composition is preferably 7.0% to 13.0% (w / v), for example 8.0% to 12.0% (w / v).

[0076] Viscosity measurements at 60° C. are preferably made using a Brookfield rotational viscometer equipped with spindle No. 3 at 100 rpm.

[0077] To facilitate densification and impregnation, the impregnated paper is then dried, for example by heated cylinders or hot air, to a moisture content of 10-30%, for example 11-20%, before being subjected to a calendering in a calendering device consisting of at least two heated nips. The calendering may be carried out in at least one supercalender having 8-20 rolls, for example 9-19 rolls, for example 11-17 rolls of calendering rolls, and some moisture, such as to a moisture content of 11-20%, may be applied to the paper web again just before the calendering. The total nip impulse of the supercalendering process may be at least 600 kPa·s. The surface temperature of the heated calender rolls may be 120-160°C.

[0078] The moisture content of the paper web facilitates the calendering operation, thereby resulting in increased density, reduced porosity and improved surface properties in the final paper.

[0079] No calendaring is carried out prior to the impregnation operation.

[0080] During the calendering process the paper is dried. Extra drying can be achieved by carrying out additional drying immediately after the calendering (i.e. before reeling). For such additional drying an air dryer can be used. With this setup the moisture content can be reduced to below 4%, which is advantageous for subsequent coating operations such as vapor deposition coating.

[0081] To obtain a paper that forms an oxygen barrier, the number and size of the pores must be significantly reduced. Extensive refining of the pulp increases the degree of fiber bonding and reduces the porosity. Greaseproof paper produced by such extensive refining has a sufficiently low porosity to provide a grease barrier. It has therefore been thought that greaseproof paper could potentially be used as a substrate or carrier for gas barrier coatings. However, the resulting pulp has a high resistance to dewatering, requires long stock dewatering times, is costly in the manufacturing process, and is undesirable in the remanufacturing and recycling processes. Furthermore, further improvement in gas barrier properties is required. The same is true for parchment paper, which is produced by passing the fibers through a bath of sulfuric acid to gelatinize the fibers, but this gelation reduces the dewatering and water repellency of the fibers, and also makes the parchment paper undesirably brittle.

[0082] A different approach to filling the voids of fibrous cellulose materials is to use microfibrillated cellulose (MFC) as the main component of the cellulosic material of the sheet or film, which also has some oxygen barrier properties. However, this material is also highly resistant to dewatering, which can cause similar problems in both the manufacturing and recycling processes. Therefore, for the purposes of the present invention, it is not desirable to use high-density paper in which MFC or other types of nanocellulose are present in significant proportions in the pulp used to make the paper. Furthermore, MFC forms a gel in aqueous compositions rather than a solution or low-viscosity dispersion, making it unsuitable as an impregnation composition for molded and dried paper.

[0083] Thus, the high density paper of the present disclosure can be obtained without extensive low consistency (LC) refining, which increases the speed (and reduces the energy consumption) of the paper manufacturing process and facilitates recycling. Such relatively limited refining can be reflected by drainability measured after repulping.

[0084] The cellulose fibres of the high density paper substrate may exhibit a Canadian Standard Freeness (CSF) value of 200 ml or more, e.g. 200-500 ml, e.g. 220-450 ml, e.g. 300-450 ml, measured according to ISO 5267-2:2001, after repulping according to the Valmet repulping process carried out in a Valmet pulper of type HD400. The Valmet repulping process consists in repulping 0.5 kg of air-dried high density paper cut to 90 x 90 mm (0.09 x 0.09 m) with 15 litres of water in a Valmet pulper at 57°C and a rotation speed of 3000 rpm for 20 minutes. The CSF values ​​of the studied high density paper substrates are significantly different from the CSF values ​​of the best known papers of the prior art, which have a high content of refined fibres in order to provide a denser, i.e. less porous, fibre structure in the paper.

[0085] Expressed differently, as a drainage value, a high density paper substrate may provide, after repulping according to the standard method of ISO 5263-1:2004, a Shopper-Riegler (SR) number measured according to ISO 5267-1:1999 of 30-50, e.g. 33-50, e.g. 35-45. In this case, the SR numbers of the studied high density papers are significantly lower than the SR numbers of paper substrates used in the prior art.

[0086] Both the C SF value and the SR number measure the dewatering characteristics of the fibers within the cellulose fiber pulp and indicate how easy or difficult it is to repulp and recycle the fibers from the high density paper substrate and, in turn, from laminated packaging materials made of paper substrates.

[0087] High density paper substrates formed from cellulose fibers have an average fines content measured by L&W Fibretester+ (ABB, Lorentzen & Wettre, Sweden) of less than 40%, e.g., less than 35%, e.g., less than 32%, measured according to ISO 16065-2:2014 after repulping according to ISO 5263-1:2004, where fines are defined as fibrous particles shorter than 0.2 mm. For example, the fines content of greaseproof paper after repulping is usually higher, e.g., 40% or more, at least 35% or more, due to the paper manufacturing process using pulp with a high content of refined fibers. A typical lower limit of the average fines content is 15% or 20%.

[0088] According to one embodiment, a high density paper substrate is used, which is impregnated from the top side and then calendered so that the surface roughness of the top side, measured for example according to SS-ISO 8791-2:2013, is lower than 100 ml / min Bendtsen, for example lower than 80 ml / min Bendtsen, for example 7-80 ml / min Bendtsen, for example 7-50 ml / min Bendtsen, for example 7-30 ml / min Bendtsen, for example 7-25 ml / min Bendtsen, for example 7-20 ml / min Bendtsen, a typical lower limit being 5 or 7 ml / min Bendtsen.

[0089] The lower the surface roughness, the more perfect the interface with the adjacent layers or coatings that are applied subsequently, with fewer defects such as pinholes and unevenness in the coating layer. As a result, the coating or further layers can be produced with higher quality and / or lower thickness. For the same thickness of gas barrier coating, the coating itself provides better oxygen barrier properties.

[0090] Another measure of surface roughness is the Parker Printsurf (PPS) roughness, which, when measured according to SS-ISO 8791-4:2013, exhibits a value of 1.0 to 2.0 μm, for example 1.2 to 1.8 μm.

[0091] Furthermore, the Gurley value according to ISO 5636-5:2013 of the high density paper substrate may be greater than 220 seconds, meaning that the surface of the high density paper substrate is closed, i.e., it does not trap air or oxygen between the surface fibers.

[0092] The impregnation step is preferably carried out by a size press or a film press. A film press is the most preferred device. If the film press is of the double-sided type, the backside impregnation of the paper web can also be carried out to further reduce the porosity of the finally provided high-density paper substrate and / or for curl control. The film press may use an OptiSizer film (Valmet) or a SpeedSizer (Voyt). After film pressing, the web is dried to a moisture content of 12% to 25%, preferably about 15%. This drying is preferably carried out by non-contact drying using hot air until the primer no longer adheres to the hot metal surface, followed by drying with a steam-heated cylinder. If the paper is impregnated with the impregnation composition only from one side, the paper may curl. Therefore, impregnation from both sides of the paper results in a flatter and more balanced high-density paper substrate.

[0093] Thus, the high density paper substrate may further be impregnated on the opposite, back surface of the paper with an impregnation composition comprising an impregnation polymer selected from the same group as for the top surface of the paper. In this way, the paper may be impregnated from the back and then calendered such that the roughness of the back surface is lower than 200 ml / min Bendtsen, for example lower than 150 ml / min Bendtsen, as measured according to SS-ISO 8791-2:2013.

[0094] Therefore, the amount of impregnated polymer on the upper surface of the high density paper is 0.3-4 g / m2 based on dry weight. 2 , for example, 0.3 to 3 g / m 2 , for example, 0.3 to 2 g / m 2 , e.g. 0.5-3g / m 2 , for example, 0.5 to 2 g / m 2 may be also possible.

[0095] The impregnation composition may comprise a water-soluble or water-dispersible impregnation polymer selected from polyvinyl alcohol, PVOH and ethylene vinyl alcohol, EVOH, and may optionally further comprise a crosslinker such as glyoxal in a weight ratio of 100:3 to 100:12. Preferably, the impregnation composition is an aqueous solution of a polymer having a low molecular weight and low viscosity. An example of a suitable formulation for PVOH is low viscosity grade of Poval® from Kuraray. An example of a low viscosity formulation of EVOH is Exeval® AQ-4104 from Kuraray. The degree of hydrolysis of PVOH is preferably as high as possible, such as 98% or 99%, and low molecular weight PVOH may be preferred as well to obtain the best impregnation effect. In a further embodiment, the impregnation polymer may be starch or a starch derivative such as chitosan in an aqueous solution. Anionic starch aqueous solutions are preferred as they have good affinity with cellulose.

[0096] In one embodiment, the impregnating polymer for the backside of the high density paper may be selected from polyvinyl alcohol, PVOH, and ethylene vinyl alcohol, EVOH, in an aqueous solution, optionally further comprising a crosslinker such as glyoxal, for example, the weight ratio of PVOH to glyoxal is 100:3 to 100:12, for example, 100:3 to 100:8.

[0097] In another embodiment, the impregnating polymer for the backside of the high density paper may instead be starch or a starch derivative such as chitosan in an aqueous solution to improve the resilience of the paper substrate. An additional advantage is that the paper substrate does not stick to the front and back sides when wound on a reel for transport and storage.

[0098] In addition to the impregnating polymer, the impregnating composition may further comprise a small amount of inorganic particles selected from the group consisting of clays such as bentonite, kaolin, or barite, and talcum, CaCO3, or silica particles. The particle size is preferably as small as possible for better impregnation properties, but together with the impregnating binder polymer of the impregnating composition, may support the filling of voids between the cellulose fibers.

[0099] The impregnation composition may completely or at least partially penetrate the thickness of the paper substrate web. Impregnation may occur from both the top and back side of the paper, partially or completely through to the center of the paper.

[0100] In one embodiment, the basis weight of the high-density paper substrate is 30 to 65 g / m 2 , e.g., 35 to 60 g / m 2 , for example 35-50g / m 2 , for example, 35 to 45 g / m 2 may be also possible.

[0101] The thickness of the high density paper substrate may be 35 to 65 μm, for example, 35 to 60 μm, for example, 35 to 50 μm, for example, 35 to 45 μm.

[0102] It has been found that in some applications, such as liquid-tight packaging of wet, liquid, or viscous products, it may be advantageous to use a dense paper substrate that is as thin as possible, as this may allow for less polymer to be required in the layers adjacent to the liquid-tight or heat-sealable layer.

[0103] According to certain embodiments, a high density paper substrate may be used with an upper and lower layer, i.e., a two-ply structure. Such a high density paper substrate allows its properties to be better tailored to its needs. In such a configuration, the properties of the upper layer may be tailored to accommodate another barrier layer, and the properties of the lower layer are tailored for strength / toughness. Alternatively, the upper layer may be tailored for printing, and the lower layer is coated with an additional layer. Hardwood pulp may provide an improved surface for printing or another barrier layer. Softwood pulp may improve runnability on the paper machine and provide beneficial strength / toughness properties to the resulting paper product.

[0104] For example, the top layer may be formed from at least 50% by dry weight hardwood pulp, such as at least 65% by dry weight hardwood pulp, for example at least 75% by dry weight hardwood pulp, to enable a denser and smoother top surface of the impregnated, calendered high density paper.

[0105] On the other hand, the bottom layer may be formed from at least 50% softwood pulp by dry weight, such as at least 65% softwood pulp by dry weight, such as at least 75% softwood pulp by dry weight. This may allow easier dewatering and repulping properties, or may simply make the paper cheaper to manufacture. If it is desired to impregnate such back surface as well, a larger amount of impregnation composition or impregnation polymer may be required.

[0106] The two-ply high density paper may include the method steps of using a first wire to form a first web, which is the top layer, and using a second wire to form a second web, which is the second layer, and bonding the first and second webs together.

[0107] The first web may be formed from a first furnish comprising at least 50% by dry weight hardwood pulp, such as at least 65% by dry weight hardwood pulp, for example at least 75% by dry weight hardwood pulp. The first furnish may have a headbox consistency of 0.12% to 0.60%, for example, 0.18% to 0.35%.

[0108] The Schopper-Riegler (SR) number, measured according to ISO 5267-1:1999, of the initial furnish in the headbox may be between 33 and 45. Such SR numbers can promote sufficiently high densities without causing dewatering and / or recycling problems and may be obtained by adjusting the degree of low consistency (LC) refining.

[0109] The second web may be formed from a second furnish comprising at least 50% softwood pulp by dry weight, such as at least 65% softwood pulp by dry weight, such as at least 75% softwood pulp by dry weight, which softwood pulp has preferably been subjected to high consistency (HC) refining (suitable specific energies as described above). The headbox consistency of the second furnish may be between 0.06% and 0.40%, for example between 0.10% and 0.25%.

[0110] In one embodiment, the headbox consistency of the second furnish is lower than the headbox consistency of the first furnish.

[0111] The Schopper-Riegler (SR) number, measured according to ISO 5267-1:1999, of the second furnish in the headbox may be between 25 and 35. Such an SR number can promote sufficiently high density without causing dewatering and / or recycling problems and may be obtained by adjusting the degree of low consistency (LC) refining.

[0112] Preferably, the furnish contains less than 2% by weight of inorganic filler, such as less than 1% by weight of inorganic filler on a dry basis, such as being substantially free of inorganic filler.

[0113] In the manufacture of two-ply papers, there may be an optional further adjacent coating or addition of starch or PVOH prior to laminating the top and bottom plies.

[0114] The density of the high-density paper base material is 1050-1500 kg / m 3 , for example, 1100-1400 kg / m 3 , for example, 1100-1300 kg / m 3 The impregnation composition, which includes a polymer in an aqueous solution, helps to fix the fibrous network in a locked position when it is subsequently calendered and dried. Paper densification provides direct and indirect gas barrier properties by using such paper substrates and is key to the success of the present invention.

[0115] The high density paper substrate has a tear resistance index of at least 4.1mNm measured in the machine direction (MD) according to ISO 1974:2012 2 / g, e.g., at least 4.4 mNm 2 / g.

[0116] In addition, the high density paper substrate has a tear resistance index, measured in the cross direction (CD) according to ISO 1974:2012, of at least 4.9 mNm 2 / g, e.g., at least 5.3 mNm 2 / g. Typical upper limits for MD and CD are 6.5 mNm 2 / g and 7.5mNm 2 In this way, the paper has higher tear resistance and also exhibits lower brittleness, which is advantageous not only for the general performance of the laminate packaging material, but also for the conversion and handling of the paper in the laminate.

[0117] The tensile stiffness index of the high density paper substrate may be 10-15 kNm / g in MD and 3-7 kNm / g in CD, so that the paper can efficiently contribute to the stiffness of the final package when used as a layer of the packaging material. In this disclosure, the tensile stiffness index is measured according to ISO 1924-3:2011.

[0118] The tensile strength index of the high density paper substrate may be at least 90 Nm / g in MD, such as at least 100 Nm / g, and at least 35 Nm / g in CD, such as 35 Nm / g~. In the present disclosure, the tensile strength index is measured according to ISO 1924-3:2005.

[0119] A higher tensile strength index may indicate a paper substrate that is useful for withstanding web handling forces during coating and lamination operations.

[0120] Preferably, beneficial barrier properties and recyclability are obtained without sacrificing strength, such as tensile strength and tear strength.

[0121] A coated high density paper substrate for gas barrier materials in laminate packaging materials for oxygen sensitive products may be provided by using any one of the above described embodiments of a high density paper substrate, the upper surface of which has at least one coating of at least one gas barrier material with a total coating thickness of 2-4000 nm, e.g., 2-3500 nm. Such thin coatings do not generate rejects or waste when recycling post-consumer laminate packaging materials containing such coatings in existing cellulose fiber recycling streams, and furthermore do not consume much material associated with the benefits such coatings provide.

[0122] According to one embodiment, the upper surface of the high density paper substrate may be coated with a gas barrier material to a dry coating thickness of 100-5000 nm (0.1-5 μm), such as 100-4000 nm (0.1-4 μm), such as 300-3500 nm (0.3-3.5 μm), such as 300-2500 nm (0.3-2.5 μm), the gas barrier material comprising a polymer selected from the group consisting of vinyl alcohol polymers and copolymers, such as a polymer selected from the group consisting of polyvinyl alcohol, PVOH, and ethylene vinyl alcohol, EVOH, furthermore a polymer selected from starch and starch derivatives, nanofibril cellulose / microfibril cellulose, NFC / MFC, nanocrystalline cellulose, NCC, and blends of two or more thereof. Such a thin coating is obtained by dispersion or solution coating of the gas barrier substance contained in the aqueous gas barrier composition and subsequent drying, as alternative methods such as extrusion coating cannot be applied to such a thin coating thickness. Although polymers and materials can also be applied as solutions or dispersions in organic solvents other than water, such methods are generally not relevant for providing environmentally sustainable packaging materials of the future.

[0123] In a preferred embodiment, the thickness is 0.5 to 3.5 g / m 2 , for example, 1 to 3 g / m 2 A coating of PVOH is applied to the top side of a high density paper substrate.

[0124] Furthermore, when the gas barrier material coating is formed by coating a dispersion or solution of the gas barrier composition and then drying, it further comprises a layered compound such as nano-dimensional layered clay, talcum or CaCO3.

[0125] According to another embodiment, the coated high density paper substrate has on its upper surface a vapor deposition coating of a gas barrier material selected from metals, metal oxides, inorganic oxides and amorphous diamond-like carbon coatings. More specifically, the vapor deposition coating may be selected from the group consisting of aluminum vapor deposition coatings and aluminum oxides (AlOx). Preferably, it is an aluminum vapor deposition coating.

[0126] In a further embodiment, the coated high density paper substrate further has on its upper surface a first coating of a gas barrier material formed by coating a dispersion or solution of a water gas barrier composition and subsequent drying, and a vapor deposition coating of a gas barrier material selected from metals, metal oxides, inorganic oxides and amorphous diamond-like carbon applied over the first coating.

[0127] The high density paper substrate, in which the gas barrier material is coated on the upper surface side of the paper substrate by vapor deposition coating, is applied to a thickness of 2 to 80 nm, for example, 2 to 50 nm, for example, 2 to 45 nm.

[0128] A coated high density paper substrate may further be provided, the back side of the paper substrate also being coated with at least one coating of at least one gas barrier material as defined in any of the above embodiments.

[0129] The vapor-deposited barrier coating that is ultimately applied to the top surface of the high density paper is applied by physical vapor deposition (PVD) or chemical vapor deposition (CVD), such as plasma enhanced chemical vapor deposition (PECVD).

[0130] Generally, below 5 nm the barrier properties may be too low to be useful, and above 200 nm, e.g. above 100 nm, e.g. above 50 nm, depending on the type of vapor deposition coating, the barrier coating may be less flexible and therefore more likely to crack when applied to flexible substrates and more costly.

[0131] Other examples of vapor-deposited coatings are aluminum oxide (AlOx, Al2O3) and silicon oxide (SiOx) coatings. Generally, PVD coatings of such oxides are brittle and not very suitable for incorporation into packaging materials by lamination, with the exception of metallized layers made by PVD, which have suitable mechanical properties for lamination materials.

[0132] Typically, aluminum metallization layers have a thin surface portion that essentially comprises aluminum oxide due to the nature of the metallization coating process used.

[0133] In one embodiment, such an aluminum vapor deposition layer is applied to have an optical density (OD) of 1.8 to 2.5, preferably 1.9 to 2.2. If the optical density is lower than 1.8, the barrier properties of the metallized film may be too low. On the other hand, if it exceeds 2.5, the metallized layer may become brittle and the heat resistance during the metallization process may be reduced due to the high thermal load when metallizing the substrate film for a long period of time. As a result, the quality and adhesion of the coating may be adversely affected.

[0134] Other coatings may be applied by plasma enhanced chemical vapor deposition (PECVD), which involves the deposition of vapors of compounds on a substrate in a more or less oxidizing environment. For example, silicon oxide coatings (SiOx) may be applied by PECVD processes and can provide very good barrier properties under certain coating conditions and gas recipes.

[0135] DLC defines a type of amorphous carbon material (diamond-like carbon) that exhibits some of the typical properties of diamond. Preferably, a hydrocarbon gas such as acetylene or methane is used as the process gas in the plasma to produce the coating of the amorphous hydrogenated carbon barrier layer, i.e. DLC, applied by PECVD vacuum process. The DLC coating applied by PECVD under vacuum provides good adhesion to adjacent polymer or adhesive layers in laminate packaging materials. In particular, polyolefins, especially polyethylene and polyethylene-based copolymers, provide good adhesion to adjacent polymer layers.

[0136] Thus, a laminated packaging material for packaging oxygen sensitive foods and oxygen sensitive products such as liquid, semi-liquid and viscous foods or water of a third aspect comprises a high density paper substrate as described in any one of the embodiments of the first aspect or a coated high density paper substrate as described in any one of the embodiments of the second aspect, and further comprises a first outermost layer of liquid-tight material and a second innermost layer of liquid-tight material, the second innermost layer may be a liquid-tight, heat-sealable material.

[0137] The laminate packaging material may further include a bulk layer of paper, paperboard or other cellulosic material, with a high density paper substrate or a coated high density paper substrate laminated between the bulk layer and the second, innermost layer.

[0138] When a vapor deposition coating is applied to a high density paper substrate, the coated paper typically also has additional water vapor barrier properties, eliminating the need for additional gas or water vapor barrier layers in the laminate structure.

[0139] When a first coating of a gas barrier material formed by applying a dispersion or solution of an aqueous gas barrier composition such as PVOH to the top surface of a high density paper substrate and then drying is applied, and then a vapor deposition coating of a gas barrier material selected from a metal, a metal oxide, an inorganic oxide, or an amorphous diamond-like carbon is applied, for example, by applying a vapor deposition coating of a gas barrier material selected from an inorganic oxide and an amorphous diamond-like carbon, such as an aluminum vapor deposition coating, on the first coating, a very good material is obtained, which may be used in place of a conventional aluminum foil of micrometer thickness (greater than 5 μm, for example 6 μm) as the sole oxygen barrier material in a laminate packaging material.

[0140] In a further embodiment, the high density paper substrate, or the coated high density paper substrate, is a binder selected from the group consisting of acrylic polymers and copolymers, starch, starch derivatives, cellulose derivatives, polymers and copolymers of vinyl acetate, copolymers of vinyl alcohol, and copolymers of styrene-acrylic or styrene-butadiene latex, with a density of 0.5 to 5 g / m 2 The intermediate bonding composition can be laminated to the bulk layer at a low level. Such low levels of intermediate bonding composition can only be applied by aqueous dispersion or solution coating of the polymer binder, and cannot be applied by extrusion coating or extrusion lamination of a polymer melt. Since both surfaces of the layers to be bonded are made of cellulose, such wet lamination is accomplished by imbibing an aqueous medium into each cellulose layer, forming a thin, dry adhesive layer at the interface of the two layers.

[0141] To improve the robustness of the mechanical properties of the laminated packaging material, the laminated packaging material may have a pre-manufactured polymer film laminated between the high density paper substrate or coated high density paper substrate and the second innermost layer of liquid-tight material. The pre-manufactured film has different mechanical properties than a simple extrusion coated or extrusion laminated layer of the same or corresponding polymer, because the polymers that compose it are more highly oriented. Thus, by incorporating such a film into the structure, the laminated material may have an overall increased strength and improved resistance to downstream tough processing of the material. It is preferable not to use such pre-manufactured films in the material, as they increase costs both from the material procurement point of view and from the lamination processing point of view. Pre-manufactured films may have different mechanical properties, ranging from a biaxially oriented tough film obtained by a simple extrusion cast film to a film produced by film blowing with inherent polymer orientation occurring in the process, or with subsequent additional orientation. However, it is preferable to use a simply extrusion coated or extrusion laminated polymer material.

[0142] The second, innermost layer of liquid-tight, heat-sealable material may be a polyolefin, preferably a blend of low density polyethylene (LDPE) and metallocene-catalyzed linear low density polyethylene (mLLDPE). This is the type of polymer currently most used for the innermost layer, as it provides the best balance of liquid-tightness and heat-sealability and maximizes package integrity of heat-sealed packaging containers. Careful selection of the composition of this layer allows for optimization of the amount of polymer in this layer to be as low as possible, while still producing a robust and reliable package filled with product.

[0143] In one embodiment, the second, innermost layer of liquid-tight, heat-sealable material may be or may include a pre-fabricated polymer film comprising a heat-sealable thermoplastic polymer material and, optionally, a further layer of material to provide improved robustness of the mechanical properties of the laminate packaging material.

[0144] In certain embodiments, the laminate packaging material may have a prefabricated polymeric film substrate laminated to the inside of a high density paper substrate or a coated high density paper substrate, i.e., on the side of the paper substrate opposite the side that is laminated to the bulk layer, the prefabricated polymeric film substrate having a vapor deposition coating of a gas barrier material selected from metals, metal oxides, inorganic oxides, and amorphous diamond-like carbon coatings.

[0145] According to different specific embodiments, the laminate packaging material may have a prefabricated polymer film substrate laminated to the inner side of a paper substrate or a coated high density paper substrate, i.e., the side of the paper substrate opposite to the side laminated to the bulk layer, and the prefabricated polymer film is filled with an inorganic layered compound to impart gas barrier and vapor barrier properties to the polymer film.

[0146] According to yet another specific embodiment, the laminate packaging material may have a pre-manufactured polymeric film substrate laminated to the inside of a high density paper substrate or a coated high density paper substrate, i.e., to the side of the high density paper substrate opposite the side that is laminated to the bulk layer. A previously manufactured polymer film is coated with a gas barrier material obtained from a dispersion or solution of the gas barrier material composition to a dry coating thickness of 100 to 4000 nm (0.1 to 4 μm), for example, 300 to 3500 nm (0.3 to 3.5 μm), for example, 300 to 2500 nm (0.3 to 2.5 μm), and then dried.

[0147] The purpose of any one of the specific embodiments listed above is to add complementary properties to the laminate packaging material when simply using a high density paper substrate as it is as a gas barrier material in the laminate structure, or when using such a coated high density paper substrate, or when the applied coating only provides some gas barrier properties, or when the coating only has a moisture-sensitive gas barrier material. By laminating the coated high density paper to a polymer film that also adds some moisture-resistant oxygen barrier properties, or at least water vapor barrier properties, at least two different gas barrier materials can interact to provide further enhanced overall barrier properties to the entire laminate structure. The necessary adhesive layer between the high density paper substrate and the additional barrier film ensures such enhanced barrier properties and may promote them to a synergistic level, since the adjacent adhesive layer acts as a "cushion" and additional "gas or vapor migration stopper" for the laminate structure.

[0148] The outermost and innermost liquid-tight layers, as well as the laminate layers within the laminate structure, do not usually provide a high barrier to migrating gas or small molecules. Their purpose is to directly barrier liquid water from penetrating the cellulosic bulk material and other paper layers. The liquid barrier layers also prevent water vapor migration to the extent that the cellulose would be wetted, but they cannot maintain the moisture content of the laminate structure at zero or at the low level of "dry" paper (i.e., about 7-8% at ambient temperature, i.e., 23°C and 50% RH). The moisture content in laminate packaging materials for liquid-filled packaging containers is usually quite high, and migration through the material will occur unless additional water vapor barriers are included, such as aluminum foil, vapor-deposited metallized layers, other vapor-deposited coatings, inorganic material layers, or other polymeric material layers.

[0149] In any of the above-listed embodiments including a prefabricated film, the prefabricated polymer film may comprise a polymer selected from any one of polypropylene, polyethylene, blends thereof, and copolymers of ethylene and propylene, and optionally additional comonomers. According to further embodiments, the prefabricated polymer film may comprise a polymer selected from high density polyethylene or linear low density polyethylene.

[0150] In any of the above-listed embodiments, the laminate packaging material may further include an additional high density paper substrate or a coated high density paper substrate laminated between the bulk layer and the first outermost layer.

[0151] In another embodiment, the laminate packaging material may instead further comprise a bulk layer of paper, paperboard or other cellulosic material, with a high density paper substrate or a coated high density paper substrate laminated between the bulk layer and the first outermost layer.

[0152] The upper surface of the high density paper substrate may be provided with a printable surface coating for printing purposes and may be oriented to be the first outermost layer in the laminate packaging material.

[0153] Alternatively, the upper surface of the high density paper substrate may be coated with an aluminum metallized coating and may be directed to the first outermost layer in a laminate packaging material.

[0154] At the same time, the high density paper substrate provides barrier properties, such as gas barrier properties, to the outside of the laminate packaging material, which are believed to be important to the functionality of the laminate packaging material and packaging containers for oxygen-sensitive products made from the laminate packaging material.

[0155] The paper or paperboard bulk layer used in the present invention typically has a thickness of about 100 μm to about 600 μm and a weight of about 100 to 500 g / m 2 , preferably about 200 to 300 g / m 2and may be conventional paper or paperboard of suitable packaging quality.

[0156] For low-cost, long-term, aseptic packaging of liquid foods, thinner packaging laminates with thinner paper core layers can be used. Packages made from such packaging laminates are not folded and resemble pillow-shaped flexible pouches. Papers suitable for such pouch packaging typically have a surface weight of about 50 to about 140 g / m2. 2 , preferably about 70 to about 120 g / m 2 , more preferably about 70 to about 110 g / m 2 The high density paper substrate used in the present invention may itself provide some stability to the laminate material and may therefore replace the paper layer that represents the "bulk" layer in such pouch materials.

[0157] The high density paper substrate may be bonded to the bulk layer by an intermediate adhesive or thermoplastic polymeric bonding layer, thereby bonding the uncoated surface of the barrier coated paper to the bulk layer. According to one embodiment, the bonding layer is a polyolefin layer, for example, a layer of a polyethylene-based polyolefin copolymer or blend, especially one containing a majority of ethylene monomer units. The bonding layer may bond the bulk layer to the barrier coated cellulose-based substrate by melt extrusion laminating the bonding polymer layer between the web of the bulk layer and the cellulose-based substrate web, and simultaneously pressing the three layers together while advancing through a laminating roller nip, providing a laminate structure by extrusion lamination.

[0158] In another embodiment, the barrier coated substrate web may be bonded to the bulk layer by wet applying an aqueous dispersion of an adhesive composition containing an adhesive polymer binder to one of the web surfaces to be laminated and pressing the two paper webs together while advancing through a laminating roller nip to provide a wet laminate structure. The water of the aqueous adhesive composition is absorbed into the fibrous cellulose network of the two paper layers and partially evaporates over time during the subsequent lamination process. Thus, no forced drying process is required. The adhesive polymer binder is selected from the group consisting of acrylic polymers and copolymers, starch, cellulose and polysaccharide derivatives, vinyl acetate and vinyl alcohol polymers and copolymers. To achieve the best environmental and sustainability profile, adhesive binders derived from plants or non-fossil sources are preferred.

[0159] Suitable thermoplastics for the outermost and innermost layers may be polyolefins such as homopolymers or copolymers of polyethylene and polypropylene, preferably polyethylene, more preferably polyethylene selected from the group consisting of low density polyethylene (LDPE), linear LDPE (LLDPE), metallocene catalyzed linear low density polyethylene (mLLDPE) and blends or copolymers thereof. According to one embodiment, the outermost liquid-tight layer is LDPE and the innermost liquid-tight heat-sealable layer is a blend composition of mLLDPE and LDPE for optimal lamination and heat-sealing properties.

[0160] The same thermoplastic polyolefin-based materials, especially polyethylene, listed for the outermost and innermost layers are also suitable for the adhesive layer inside the laminate material, i.e. between a bulk or core layer, such as paper or paperboard, and a further barrier film or sheet. In one embodiment, the thermoplastic adhesive layer may be a simpler or more conventional polyethylene layer, such as a low density polyethylene (LDPE) layer.

[0161] Although polyethylene-based polymers have been used and optimized for a very long time in the field of liquid carton packaging materials, other thermoplastic polymer materials, such as other polyolefins, such as other polyethylenes or polypropylenes, or other liquid-tight materials, such as polyesters, to further impart heat sealability and thermal processability, are considered within the scope of the present invention. Thus, any kind of bio-based such thermoplastic materials are considered within the scope of the present invention, insofar as a separate gas barrier property must still be provided through the use of the present invention, the high density paper substrate, and the materials described in relation to the barrier-coated high density paper substrate.

[0162] In a further embodiment, the second innermost layer of liquid-tight, heat-sealable polyolefin is a pre-manufactured film containing the same or similar polyolefin as described above to improve the robustness of the mechanical properties of the packaging material. Due to the manufacturing process in film blowing and film casting operations, and any subsequent film orientation operation steps, the polymer of such a film acquires properties different from those obtained from the (co)extrusion coated polyolefin layer. Such pre-manufactured polymer films contribute to the mechanical robustness of the laminate packaging material, and to the mechanical strength and package integrity of the packaging container formed and filled from the laminate packaging material.

[0163] According to further embodiments, suitable bonding or joining layers in the interior of the laminate material, for example between the bulk or core layer and the barrier-coated high density paper substrate, or between the outer heat-sealable layer and the barrier-coated high density paper substrate, may also be so-called adhesive thermoplastic polymers, such as modified polyolefins, mainly based on LDPE or LLDPE copolymers or monomer units containing functional groups such as carboxylic acid or glycidyl functional groups, i.e. graft copolymers, such as (meth)acrylic acid monomers or maleic anhydride (MAH) monomers, i.e. ethylene acrylic acid copolymer (EAA) or ethylene methacrylic acid copolymer (EMAA), ethylene-glycidyl (meth)acrylate copolymer (EG(M)A) or MAH-grafted polyethylene (MAH-g-PE). Another example of such modified or adhesive polymers are so-called ionomers or ionomeric polymers. Preferably, the modified polyolefins are ethylene acrylic acid copolymers (EAA) or ethylene methacrylic acid copolymers (EMAA).

[0164] The laminate packaging material produced as described above provides good integrity when converted into a filled packaging container due to good adhesion between adjacent layers in the laminate structure, and the good qualities of each and every barrier coating and barrier pre-coating. In particular, for packaging liquids and moist foods, it is important that the interlayer adhesion within the laminate packaging material is maintained, as well as the oxygen gas barrier properties, even under moist packaging conditions.

[0165] According to further embodiments, a packaging container formed from the laminated packaging material can be partially sealed, filled with a liquid or semi-liquid food product, and then sealed by sealing the packaging material to itself, optionally in combination with a plastic opening or top of the package.

[0166] In conclusion, due to the improved properties offered by the high density paper substrate itself, a robust and reliable package for shelf-stable liquid food packaging can be obtained by using a high density paper substrate further coated with a barrier layer or laminated to a further barrier material layer in the laminate packaging material defined by the present invention. The laminate packaging material structure works better for forming into a folded and formed package, both due to the improved interaction and adhesion between the high density paper substrate and the gas barrier material coating, and the improved contribution of the paper substrate itself to the gas barrier properties.

[0167] ( Examples and Description of the Preferred Embodiments ) Hereinafter, preferred embodiments of the present invention will be described with reference to the drawings. [Brief description of the drawings]

[0168] [Figure 1a] FIG. 1 shows a schematic cross-sectional view of an embodiment of a high density paper substrate for use in the present invention. [Figure 1b] FIG. 1 shows a schematic cross-sectional view of an embodiment of a high density paper substrate for use in the present invention. [Figure 1c] These are SEM images of the surface and cross section of high density paper. [Figure 1d] These are SEM images of the surface and cross section of high density paper. [Figure 1e] These are SEM images of the surface and cross section of high density paper. [Figure 1f] These are SEM images of the surface and cross section of high density paper. [Figure 2a] FIG. 1 is a schematic cross-sectional view of a barrier coated high density paper substrate according to the present invention; [Figure 2b] FIG. 1 is a schematic cross-sectional view of a barrier coated high density paper substrate according to the present invention; [Figure 2c] FIG. 1 is a schematic cross-sectional view of a barrier coated high density paper substrate according to the present invention; [Diagram 3] FIG. 2 shows a laminated packaging material according to the present invention comprising an embodiment of the barrier coated high density paper substrate of FIG. 2a or FIG. 2c. [Figure 4] FIG. 2b shows a laminated packaging material according to the present invention comprising an embodiment of the barrier coated high density paper substrate of FIG. 1a or FIG. 1b. [Diagram 5] FIG. 2c shows a further alternative laminated packaging material comprising a barrier coated high density paper substrate as shown diagrammatically in FIG. 2c. [Figure 6a] FIG. 1 is a schematic diagram showing a method of dispersion coating a base layer or barrier precoat composition onto a cellulosic substrate. [Figure 6b] FIG. 1 is a schematic diagram illustrating a method for melt (co)extrusion coating a coating layer of a thermoplastic heat-sealable, liquid-tight polymer onto a web substrate to form the innermost and outermost layers of the packaging laminate of the present invention. [Figure 7a] FIG. 1 is a perspective view of a plant for carrying out physical vapor deposition (PVD) coatings on paper substrates or films using solid metal evaporation pieces; [Figure 7b] FIG. 1 is a schematic diagram of a plant for plasma enhanced chemical vapor deposition (PECVD) coating of paper substrates or films by magnetron plasma. [Figure 8a] FIG. 2 is a diagram showing a representative example of a packaging container made from a laminate packaging material according to the present invention. [Figure 8b] FIG. 2 is a diagram showing a representative example of a packaging container made from a laminate packaging material according to the present invention. [Figure 8c] FIG. 2 is a diagram showing a representative example of a packaging container made from a laminate packaging material according to the present invention. [Figure 8d] FIG. 2 is a diagram showing a representative example of a packaging container made from a laminate packaging material according to the present invention. [Figure 9] FIG. 1 illustrates the principle by which packaging containers are manufactured from a packaging laminate in a continuous roll-fed, form, fill and seal process. [Figure 10]FIG. 1 shows significantly different oxygen transmission rates for two comparative laminate packaging materials using gas barrier coated high density paper substrates as the barrier material, with the only difference being the high density paper substrate chosen. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0169] Working Example Example 1 1A: Manufacturing of paper base material (2-ply paper) Two pulps were provided: i) ECF bleached kraft pulp from softwoods (mixture of pine and spruce) and ii) ECF bleached kraft pulp from hardwoods (e.g. birch).

[0170] The softwood pulp was refined using high consistency (HC) refining with a specific energy of 225 kWh / ton (net energy input per ton of dry fiber). The HC refined pulp was then mixed in a mixing chest with broken pulp, which contained a blend of bleached softwood and hardwood pulps (the majority of the broken pulp was from the same paper mill). The broken content of this softwood-based mixture was 30%. This softwood-based mixture was subjected to low consistency (LC) refining with a specific energy of 75 kWh / ton. The LC refining resulted in a Shopper-Riegler (SR) according to ISO 5267-1:1999 of ~30°SR.

[0171] Hardwood pulp was mixed separately with homogeneous broken wood and refined at low consistency with a specific energy of 85 kWh / ton. The proportion of broken wood in the hardwood-based mixture was 20%. The LC refined hardwood-based mixture had a Shopper-Riegler (SR) value of ~38°SR.

[0172] Papermaking chemicals were added to each of the two fibre streams (4 kg / tonne cationic starch, 0.2 kg / tonne silica, 0.4 kg / tonne AKD). The softwood-based mix was pumped into the lower headbox of a two-ply Fourdrinier papermaking machine, while the hardwood-based mix was pumped into the upper headbox of the same fourply papermaking machine. The dry mass flow rates through each headbox were the same, with a total pre-coating basis weight of 60 g / m 2 (i.e., 30 g / m per layer) 2 ). The vertical slice lip was 34 mm at the lower headbox and 16 mm at the upper headbox, reflecting relatively low headbox consistencies (approximately 0.12% at the lower layer and 0.25% at the upper layer). The wire speed was 600 m / min. On paper machines specifically adapted for this product, wire speeds can be significantly increased.

[0173] The two layers formed on the Fourdrinier were coupled at a dryness of ~10% and further dewatered to a dryness of ~20% using a vacuum foil box, and then wet pressed in a press section with two single felt press nips.

[0174] After wet pressing, the web was dried in a conventional multi-cylinder dryer to form a paper substrate with a moisture content of ~5%. Prior to winding, the paper substrate was calendered in a soft nip with a line load of 20 kNm. The properties of the paper substrate are shown below (Table 1).

[0175] The SEM image of the surface portion of the formed paper is shown in Figure 1c.

[0176] 1B: Impregnation A 1A paper substrate was off-line impregnated on both sides with an aqueous polyvinyl alcohol (PVOH) composition in a conventional film press. The type of PVOH was Poval 10 / 98 from Kuraray and its concentration in the composition was 10% (in separate tests the concentration was instead 8%, which also gave good results). The composition further contained glyoxal (Cartabond TSI) in an amount of 6 wt% relative to the amount of PVOH. The glyoxal acted as a crosslinking agent. The viscosity of the composition was 74 mPa s (measured at 60 °C). The applied amount of PVOH was 1 g / m2 on the top surface. 2 , back / bottom surface is 2g / m 2 The reason for using more PVOH on the back / bottom surface was that the pulp used to form the bottom layer had a lower SR number (hence the back / bottom surface had a lower surface density compared to the top surface). The PVOH impregnated paper substrate was dried with hot air to a moisture content of 8%. The properties of the dried PVOH impregnated paper substrate are shown below (Table 1).

[0177] Figure 1d is an SEM image of the surface area of ​​the PVOH-impregnated paper substrate. As shown in Figure 1d, the PVOH does not form a film on the surface area. Instead, the PVOH permeates the fiber network.

[0178] In another test, the amount of PVOH applied was 1 g / m2 on the top surface. 2 , back side / bottom side 2g / m 2 Instead of 1.5g / m2 per side 2 It was decided.

[0179] 1C: Super Calendar The 1B impregnated paper was remoistened to 15%. The remoistened paper was fed to an offline multi-nip calender (12 nips) also called supercalender. Supercalendering was performed using a thermo roll surface temperature of 140°C obtained by an external induction heater to obtain a high density paper. The line load at each nip was 450 kNm. The total supercalendering nip impulse was ~800 kPa·s (nip x line load / web speed). The high density paper was dried by the heat from the thermo roll. The moisture content at winding was 8%. The properties of the high density paper are shown below (Table 1).

[0180] An SEM image of the surface portion of the high density paper is shown in Figure 1e. Additionally, an SEM image of the cross section 10f of the high density paper is shown in Figure 1f. The dark grey areas 15 are PVOH and the light grey areas 16 are fibers. There are also unfilled pores 17. As a result, the high density paper is not saturated with PVOH. However, Figure 1f shows that most of the PVOH is within the fiber web. A small portion of PVOH is present on the surface.

[0181] 1D: See the First Super Calendar For reference, the paper base produced according to 1A above was supercalendered (but not impregnated) as in 1C above, with only softwood kraft pulp and broked pulp in both layers. The obtained properties are shown below (Table 1).

[0182] 1E: See the Second Super Calendar As a reference, a machine glazed (MG) paper made from a mixture of hardwood and softwood (40:60 dry weight) pulps was supercalendered as in 1C above, but the total nip impulse of the supercalendering step was about 10% lower. The resulting properties are shown below (Table 1).

[0183] 2A: Paper base material (single layer paper) Although the purpose was different, a single-ply paper with similar properties was provided, manufactured by a similar process. The single-ply paper was made from a mixture of Kraft softwood and Kraft hardwood pulps with a small amount of CTMP pulp in a mixing ratio of 45:45:10. The single-ply paper was impregnated from the top with polyvinyl alcohol and then dried at about 1050 kg / m2. 3 The resulting basis weight is 45 g / m 2 The surface roughness of the upper surface was about 25 ml / min Bendtsen.

[0184] 2B: Paper base material (single layer paper) A single-ply paper of the same composition as the paper base 2A was provided. This single-ply paper was impregnated with polyvinyl alcohol from the top surface and had a strength of about 1100 kg / m 3 , 57g / m 2 The smoothness of the upper surface was less than 15 ml / min Bendtsen.

[0185] Resulting properties For (Table 1), the following applies: Basis weight is measured according to ISO 536:2012 and is in g / m 2 Thickness was measured according to ISO 534:2011. Density was measured according to ISO 534:2011 and is expressed in kg / m 3 Roughness means Bendtsen roughness and is measured according to ISO 8791-2:2013 and has the unit of ml / min. Tensile strength index is measured in MD and CD according to ISO 1924-3:2005 and has the unit of Nm / g. Tear strength index is measured in MD and CD according to ISO 1974:2012 and has the unit of mNm 2 / g. Tensile stiffness index was measured according to ISO 1924-3:2005. SR was measured according to ISO 5267-1:1999 after repulping according to ISO 5263-1:2004. Canadian Standard Freeness "CSF" was measured in ml according to ISO 5267-2:2001 after repulping according to Valmet's repulping method using a Valmet HD400 pulper. Valmet's repulping method is detailed below. Somerville residue, quantified as weight percent, measures the residue retained in a Somerville shive with a slot plate width of 0.15 mm and a flake content analyzer. The Somerville method is detailed below. SV residue content was calculated as the dry weight percent of the dry material that had been introduced (to the repulper). Dry means that the moisture content in the test material is 0%, dried in an oven before weighing. Fines content was measured with L&W Fibretester (ABB, Lorentzen&Wettre, Sweden) ISO 16065-2 after repulping according to ISO 5263-1:2004. Fines refers to all objects with a particle length of less than 0.2 mm as confirmed by an image-based fiber analyzer. Oxygen transmission rate (OTR) was measured using a 20 g / m2 fiber filter on the top surface of the paper. 2 After lamination with LDPE, measured according to ASTM F1927-14, units are cm / m 3 / 24 hours at 0.2 atm (21%) oxygen. Super Perga 1 and 2 are commercially available greaseproof papers. Super Perga 1 was used as the paper substrate in WO2017 / 089508.

[0186] [Table 1]

[0187] § According to supplier datasheet ※ 1.5g / m per side 2Tested on high density paper impregnated with PVOH * The basis weight is 32g / m 2 Instead, it is 38g / m 2 It became ** After supercalendering according to Example 1C (no PVOH impregnation)

[0188] As shown above (Table 1), supercalendering (densification) or PVOH impregnation alone does not result in very low OTR values. For example, supercalendering had almost no effect on the OTR value of non-impregnated paper Super Perga 2. In contrast, when the PVOH-impregnated paper substrate of Example 1B was supercalendered, the OTR value (50% RH) decreased by about 70%, and the OTR value (50% RH) decreased by about 10 cm. 3 / m 2 / 24 hours).

[0189] Valmet's repulping process was carried out as follows: The paper was repulped using a Valmet HD400 pulper, used for stock preparation, i.e. fiber grinding. Agitation was achieved using an impeller with three radial sawtooth blades measuring 30 x 40 mm rotating at a speed of 3000 rpm. The paper was cut into pieces of 90 x 90 mm. 0.5 kg of air-dried paper pieces were mixed with 10 liters of water, i.e. to a 5% consistency, and repulped at a temperature of 57°C for 2.5 minutes. Then, 5 liters of water was added to give a consistency of 3.3%. Repulping was continued for a further 17.5 minutes at 57°C. The total repulping time was 20 minutes.

[0190] For quantification of Somerville residues retained on a Somerville sieve with a slot plate width of 0.15 mm and a flake content analyzer, the pulp obtained from the Valmet repulping process described above was diluted to a consistency of less than 1% and then analyzed on the Somerville analyzer to obtain the percentage of flake residues as a weight percentage calculated relative to the oven-dried material (i.e., 0% moisture content) initially introduced into the repulping operation.

[0191] Measurement of Canadian Standard Freeness of Pulp: The pulp obtained from the Valmet repulping process described above was diluted to about 0.3% and tested for Canadian Standard Freeness according to ISO 5267-2:2001.

[0192] The impregnated but uncoated paper, when further coated with a layer of LDPE, exhibits a lower OTR than the unimpregnated paper used in the prior art. These properties decrease with increasing moisture content (80% RH) because the impregnating polymers used are sensitive to humidity.

[0193] Example 2 The impregnated high density paper substrate 2B of Example 1 is included, and 1 g / m 2 The laminate packaging material was provided with two coatings of PVOH and dried after each coating. The oxygen transmission rate of the laminate was measured by a fluorescence method using an oxygen probe PSt9 from PreSens GmbH, Germany. In this method, the flat sample to be analyzed is placed on a cell flushed with dry nitrogen, in which the probe is also placed. The area of ​​the circular cell is 68 cm 2 (0.0068m 2 ) The surface of the specimen not facing the cell is exposed to ambient air at 23°C and 50% RH, i.e. 0.21% oxygen. The oxygen concentration reading from the probe is used to calculate the oxygen transmission rate according to ASTM F3136-15. The units are ml / specimen.

[0194] The comparative test was carried out on a paper made of mostly softwood sulfate (kraft) pulp fibres, refined to achieve low porosity but not as refined as conventional grease blotting paper, with a basis weight of 39 g / m 2 , density 974kg / m 3 The comparative paper was supercalendered and had a top surface smoothness of about 33 ml / min Bendtsen.

[0195] The laminate packaging material had the following layer structure: / LDPE12g / m2 / 80mN Liquid Paperboard / LDPE20g / m 2 / Paper base material containing 2x PVOH 1g / m 2 / Adh EAA Copolymer 6g / m 2 / Blend LDPE+mL LDPE 19g / m 2 /

[0196] This oxygen permeability measurement method allows us to examine the oxygen barrier properties of flat materials before and after folding. The folding angle is 165 degrees, so that the barrier layer is on the outside of the fold. The measured values ​​are the average values ​​of five samples.

[0197] The results are shown in the graph of Figure 10, which demonstrates that folding of a laminated packaging material containing a PVOH-coated reference paper substrate that is not impregnated but has otherwise similar properties in terms of density and surface roughness and exhibits some inherent oxygen barrier properties results in a loss of its oxygen barrier properties, whereas the oxygen transmission rate of a laminated packaging material containing an impregnated high density paper does not change substantially after one folding operation. 2 When coated with LDPE, the oxygen permeability is approximately 34cc / m 2 / day / 0.2atm, 23°C, 50%RH, the sample paper, i.e. Paper 2B of Example 1, was measured with a corresponding OTR value of 9.3. The reference paper only has a low level of oxygen barrier, so the main loss comes mainly from the coating of PVOH polymer. On the other hand, in the case of Paper 2B, the damage of the PVOH coating may be compensated by the impregnated paper substrate. This may be due to the combined effect of the additional inclusion of PVOH with its inherent gas barrier properties in the cellulose material, and the complete filling of the voids or pores of the cellulose material by the impregnated polymer, so that oxygen molecules cannot diffuse through the paper material between the fibers, but encounter some resistance, i.e. "barrier".

[0198] Example 3 The saturated high density paper according to 1C and 2A of Example 1 was dispersion coated two more times with intermediate and subsequent drying operations to obtain 3 g / m PVOH. 2 It was fed and metallized to an optical density of about 2. A laminate packaging material was then produced according to the following layer structure: / LDPE12g / m 2 / Paperboard 80mN / LDPE 20g / m 2 / Paper base material + PVOH + met / Adhesive EAA copolymer 6g / m 2 +29g / m 2 Blend LDPE+mLLDPE /

[0199] The packages were produced on a Tetra Pak® E3 / CompactFlex filling machine. This type of filling machine has the capacity to fill portion packages at a speed of 9000 packages per hour and has the flexibility to quickly change between different package formats. The packages were Tetra Brik® packaging containers and had a capacity of 200 ml.

[0200] During testing, no major issues were identified with package integrity (tightness of the package against the surrounding environment) and seal performance and were therefore considered successful.

[0201] The oxygen transmission rate of flat packaging materials was measured using a coulometric detector according to the ASTM F1927-14 standard. The moisture level was 50% or 80% relative humidity and the unit is cm 3 / m 2 / 24h, the oxygen pressure can be selected to be 0.2 atm or 1 atm. To make the OTR value measured at 1 atm comparable to the OTR value measured at 0.2 atm, the former value can be multiplied by 0.2.

[0202] The oxygen transmission rate of packaging materials (filled, empty, dry) was measured at 0.2 atm (ambient air containing 21% oxygen) according to ASTM F1307-14. The unit is cm 3 / package / 24h.

[0203] The package is mounted in a special holder and the inside of the package is purged with nitrogen. As oxygen permeates through the package into the nitrogen carrier gas, it is carried to a coulometric sensor. The sensor reads the amount of oxygen that leaks into the nitrogen gas inside the package.

[0204] The comparative examples have a basis weight of 32 g / m 2 (Example 3) and 38 g / m 2 A greaseproof paper from Nordic Paper called "Super Perga® WS Parchment" (Example 4) was used.

[0205] [Table 2]

[0206] * / LDPE12g / m 2 / Paperboard 260mN / LDPE 20g / m 2 / Paper base material+PVOH+met / LDPE20g / m 2 / LDPE+mLLDPE20gm 2 / ** / LDPE12g / m 2 / Paperboard 80mN / LDPE 20g / m 2 / Paper base material+PVOH+met / LDPE40g / m 2 / *** / LDPE12g / m 2 / Paperboard 80mN / LDPE 20g / m 2 / HD paper base + PVOH + met / adhesive EAA copolymer 6g / m 2 +29g / m 2 Blend LDPE+mLLDPE /

[0207] The difference between the comparative example and the example according to the invention is the amount of polyethylene in the layer facing the inside of the package, i.e. 40 g / m 2 and 35 g / m 2Although there is a difference in the amount of oxygen permeability, polyethylene has a low oxygen permeability relative to HD paper and applied coatings, so this has no practical effect on the comparison of oxygen permeability. A typical oxygen permeability of 40 μm thick LDPE is 600-900 cm at 23 °C. 3 / m 2 / 24h / 0.2atm.

[0208] Example 4 [Table 3]

[0209] ※ / LDPE 12g / m2 / Paperboard 80mN / LDPE 20g / m2 / Aluminum foil 6.3μm / Adhesive EAA copolymer 6g / m 2 +19g / m 2 Blend LDPE+mLLDPE / ※※ / LDPE12g / m2 / Paperboard80mN / LDPE20g / m 2 / Paper base material + PVOH + met / Adhesive EAA copolymer 6g / m 2 +19g / m 2 Blend LDPE+mLLDPE /

[0210] The coarse rejects, i.e. the non-fibrous recyclable parts of the laminate material (polymer, aluminum foil and part of the non-peelable fibers), were measured after repulping in a Valmet pulper. The repulping was carried out in the same way as for the determination of CSF and Somerville residue values ​​by repulping of a single paper substrate in Example 1 above, except that the laminate packaging material to be repulped and analyzed was first cut into pieces of 30 x 90 mm. The coarse rejects were sieved off with a 10 mm diameter hole plate, dried to 0% moisture and calculated as the weight percentage of the dry material introduced into the pulper (0% moisture content).

[0211] A coarse reject, determined by a contractor contracted to a global industrial supplier of textile processing and recycling equipment, was produced in a similar manner, except that 20 g of laminate material was mixed in 2 liters of water and allowed to disintegrate for 18 minutes to a consistency of approximately 1% instead of 3.3%. The water temperature was also kept at 57°C in this repulping test.

[0212] It has been confirmed above that the previously discussed paper substrates for oxygen barrier coatings can produce relatively high oxygen barrier levels in the laminate packaging materials and the packages filled and sealed therefrom, but do not result in a reduction in the amount of reject material in existing recycling processes, such as the recycling of used beverage cartons. Although aluminum foil as a raw material can be avoided, the amount of material discarded or incinerated from the recycling of materials (gross rejects) would be similarly high, as seen in Comparative Examples 4C2 and 4C1, as tested by the recycling company mentioned above.

[0213] A comparative evaluation of the paper-based barrier laminates of the prior art has not yet been carried out with the Valmet pulper and the repulping method described above, but based on the results of Comparative Examples 4C2 and 4C1, it is expected that the Valmet method will also produce a high percentage of coarse rejects, similar to the tested reference aluminum foil material. On the other hand, the laminate material according to the present invention shows a significantly lower percentage of rejects, such as less than 20 wt% coarse rejects. The laminate material comprising the paper substrate 1C of Example 1, as shown in Examples 3A and 4A, seems to require a slightly longer repulping time of the laminate material compared to the laminate material according to Example 4B, but in any case, it is similarly disintegrated after a long repulping time, such as 50 minutes in this case, resulting in a similarly low percentage of coarse rejects. The laminate material tested for repulping in Example 4B comprises a paper substrate with a similar composition to that of Example 3B, but with a higher basis weight. Thus, the laminate packaging material of the present invention, Example 3B, is expected to produce a similarly low amount of coarse rejects.

[0214] conclusion A filled 200 ml package made from a standard laminate of the coated paper of the present invention had a water vapor density of 0.03 cc / m2 at 23° C. and 50% RH. 2 This shows a very low level of oxygen transmission rate of 0.2 atm / day. Furthermore, this value does not appear to deteriorate significantly in an environment of 23°C and 80% RH. OTR testing was performed 2-3 weeks after manufacturing of the filled and sealed packages. The oxygen transmission rate of 0.03 for the 200ml package provides approximately 2-3 times the shelf life for oxygen sensitive products compared to the oxygen transmission rate of approximately 0.075 for Comparative Example 3C2.

[0215] The OTR of the laminate material of the present invention is at least as good as that of similar paper-based barrier laminates of the prior art. However, the loss of oxygen barrier properties due to deformation of the laminate material to filled, formed, and heat-sealed packages is not to the same extent. This difference is not due to the higher amount of PVOH coated compared to the comparative example, as described above. The difference may improve the oxygen barrier properties of the flat laminate material, but cannot explain the improvement in oxygen barrier properties in filled and sealed packages beyond a minor level of improvement.

[0216] In general, package integrity has proven to be better with the paper-based barrier of the present invention. Furthermore, the lower the basis weight of the paper substrate, e.g., 30-65 g / m 2 , for example, 35 to 60 g / m 2 , for example, 35 to 50 g / m 2It has been found that the integrity of the package is improved. The thickness of the paper substrate is preferably 35-60 μm, e.g., 35-50 μm, e.g., 35-45 μm. If the coated paper substrate was thicker, more polymer was needed to create a tight and durable seal when transforming the laminated material into a filled and sealed rectangular shaped package. This is very important because packaging materials will need to fit into recycling streams with very high fiber content in the future, so that the material can be recycled and used again rather than becoming waste.

[0217] Furthermore, the impregnated high density paper substrate of the present invention provides a laminated material with improved recycling and repulping properties compared to both aluminum foil-based and non-aluminum foil gas barrier-based laminated packaging materials. This improvement further supports the development of more sustainable packaging materials. It also allows the fiber-based content to be increased in laminated packaging materials for packaging highly oxygen-sensitive products, such as fruit juices and fruit and vegetable-based foods containing natural vitamin C.

[0218] Further, with reference to the accompanying drawings: In Figure 1a, one embodiment of a high density paper substrate 10a of the present invention is shown in cross section. The paper substrate 10a has a single layer structure, and the upper surface 12a is impregnated with polyvinyl alcohol 11a having a high degree of hydrolysis. The dry weight of the impregnated PVOH is about 1 to 1.5 g / m 2 The paper base material has a thickness of about 1 to 2 g / m on the back surface 14a. 2 The PVOH or oxidized starch may be impregnated 13a.

[0219] Figure 1b shows in cross section an embodiment of a high density paper substrate 10b of the present invention. The paper substrate 10b has a two-layer structure, and the top layer 11b on the top side of the paper substrate is impregnated at its top surface 12b with polyvinyl alcohol having a high degree of hydrolysis. The dry weight of the impregnated PVOH is about 1 g / m 2The lower layer 13b of the paper base material is also about 2 g / m 2 In the manufacture of two-ply paper, optionally a further intermediate coating or addition 15b of starch or PVOH may be applied before laminating the top layer to the bottom layer.

[0220] Figure 1c shows an SEM image of the surface area of ​​the paper that was wet pressed and dried without impregnation and calendering to obtain the final properties and high density.

[0221] Figure 1d is an SEM image of the surface area of ​​the PVOH-impregnated paper substrate. As shown in Figure 1d, the PVOH does not form a film on the surface area. Instead, the PVOH penetrates into the fiber web.

[0222] Figure 1e is an SEM image of the surface of high-density paper obtained by subjecting the impregnated paper of Figure 1d to a supercalendering treatment.

[0223] Figure 1f is an SEM image of a cross section 10f of the high density paper. The dark grey areas 15 are PVOH and the light grey areas 16 are fibers. There are also unfilled pores 17. As a result, the high density paper is not saturated with PVOH. However, Figure 1f shows that most of the PVOH is present within the fiber web. Only a small amount of PVOH is present on the surface of the paper.

[0224] In Figure 2a, one embodiment of a gas barrier coated high density paper substrate 20a of the present invention is shown in cross section. The high density paper substrate 21a shown in Figure 1a or 1b is first coated with a water gas barrier composition consisting of PVOH in two coating steps with an intermediate step and a subsequent drying step, to a dry weight of 1.5 g / m 2 That is, twice the thickness, or 3 g / m 2 A layer 22a of is applied.

[0225] Thus, the PVOH coated high density paper substrate 23a (i.e., comprising 21a and 22a) further has a vapor deposition coating of an aluminum metallized layer 24a over the PVOH coating 22a. This coating configuration in combination with the high density paper substrate provides a preferred non-foil laminate packaging material that provides high and durable gas barrier properties in packaging containers that are folded, filled and heat sealed from such non-foil packaging material.

[0226] Figure 2b shows a gas barrier coated high density paper substrate 20b of the present invention, which corresponds to the PVOH coated high density paper substrate 23a of Figure 2a. The high density paper substrate 21b shown in Figure 1a or 1b was thus coated with a water gas barrier composition consisting of PVOH in a two-coating process with an intermediate process and a subsequent drying process, to a dry weight of 1.5 g / m 2 That is, twice the thickness, or 3 g / m 2 This is another variation of the paper-based gas barrier material, which can be combined with additional complementary barrier materials in a laminate packaging material, such as a vapor-deposited barrier coating on a polymeric film substrate. Such non-foil laminate packaging materials similarly provide a durable gas barrier to folded, formed, filled, and heat-sealed packaging materials.

[0227] FIG. 2c shows an alternative gas barrier coated high density paper substrate 20c. The high density paper substrate 21c shown in FIG. 1a or FIG. 1b is coated with an aluminum metallized layer 24c on the upper side of the high density paper substrate 21c by vapor deposition coating. When designing the internal gas barrier property of the impregnated high density paper substrate as high as possible, it may be sufficient to directly coat the paper substrate by vapor deposition coating to further enhance the total gas barrier performance of the high density paper substrate. The coated high density paper substrate 20c also provides high and durable gas barrier properties as the only barrier material or in combination with additional complementary barrier materials in packaging containers that are folded, filled and heat sealed from non-foil laminate packaging materials.

[0228] In FIG. 3, a laminate packaging material 30 for liquid carton packaging is shown, which has a bending force of 80 mN and a compressibility of about 200 g / m 2 The packaging laminate includes a bulk layer 31 of paperboard having a basis weight of about 100 g / m2, and further includes a liquid-tight, heat-sealable outer layer 32 of polyolefin applied to the outside of the bulk layer 31, which outer layer is directed toward the outside of the package produced from the packaging laminate. The outer layer 32 is transparent to allow a printed decorative pattern 37 applied to the bulk layer of paper or paperboard to be visible on the outside, thereby informing the contents of the package, the package brand, and other information targeted to consumers in retail establishments and food stores. The polyolefin of the outer layer 32 is a conventional low density polyethylene (LDPE) of heat-sealable quality, but may also include more similar polymers, including LLDPE. The application weight is about 12 g / m2. 2A liquid-tight, heat-sealable innermost layer 33 is placed on the opposite side of the bulk layer 31, this layer being directed towards the inside of a packaging container manufactured from the packaging laminate. Such heat-sealable innermost layer 33, which will form a strong transverse heat seal of a liquid packaging container manufactured from the laminate packaging material, may comprise one or a combination of two or more polyethylenes selected from the group consisting of LDPE, linear low density polyethylene (LLDPE) and LLDPE manufactured by polymerizing ethylene monomers having α-olefin alkylene monomers of C4 to C8, more preferably C6 to C8, in the presence of a metallocene catalyst, so-called metallocene-LLDPE (mLLDPE). The coating weight is about 29 g / m 2 It is.

[0229] The bulk layer 31 is laminated to the uncoated side of the barrier coated paper substrate 20a from Figure 2a, i.e. 35, by an intermediate bonding layer 36 of low density polyethylene (LDPE). The intermediate bonding layer 36 is formed by melt extrusion as a thin molten curtain of polymer between the two paper webs, so that it laminates the bulk layer and the barrier coated paper substrate to each other as all three layers pass through the chilled press roller nip. The thickness of the intermediate bonding layer 36 is 12-18 μm, e.g. 12-15 μm.

[0230] The heat-sealable innermost layer 33 may consist of one layer or alternatively may comprise two or more partial layers of the same or different types of LDPE or LLDPE or blends thereof, and is well adhered to the metallized barrier deposition coated surface 24a, i.e. 20a, of the barrier coated high density paper substrate 33. The heat-sealable innermost layer 33 is bonded to the barrier coated high density paper substrate 20a by applying the tie layer 38 and the innermost layer 33 together in a single melt coextrusion coating process, for example by an intermediate coextrusion tie layer 38 of ethylene acrylic acid copolymer (EAA).

[0231] Alternatively, the bulk layer 31 may be laminated to the barrier coated paper substrate described in Figure 2a by wet lamination with an intermediate adhesive layer 36b, a thin layer of adhesive polymer, obtained by applying an aqueous dispersion of PVOH or polyvinyl acetate adhesive to one of the surfaces to be bonded together and then pressing with a roller nip. Thanks to the relatively thick absorbent bulk layer of cellulosic structure, this lamination process can be carried out in an efficient cold or ambient lamination process at industrial speeds, without the energy-consuming drying operations normally required to promote the evaporation of water. The dry coating weight of the intermediate adhesive layer 36b is several g / m2. 2 , for example 2 to 6 g / m 2 , no drying or evaporation is required.

[0232] Therefore, the amount of thermoplastic polymer in the laminate layer can be significantly reduced compared to conventional polyethylene 36 melt extrusion laminate adhesive layers.

[0233] In an alternative embodiment not shown, the gas barrier coated dense paper substrate 20c of FIG. 2c may be laminated to the same laminate structure in place of the coated dense paper 35, ie, 20a.

[0234] FIG. 4 shows another laminate packaging material 40 of the present invention for liquid carton packaging, which has a bending force of 80 mN and a strength of about 200 g / m 2 The packaging laminate comprises a paperboard core layer 41 having a basis weight of 12 g / m2 and further comprises a liquid-tight, heat-sealable outer layer 42 of polyolefin applied to the outside of the bulk layer 41, which layer will be directed towards the outside of a package produced from the packaging laminate. The polyolefin of the outer layer 42 is a conventional low density polyethylene (LDPE) of heat-sealable quality, having a basis weight of 12 g / m2. 2 but may include further similar polymers including LLDPE.

[0235] A liquid-tight, heat-sealable innermost layer 43 is located opposite the bulk layer 41 and is directed towards the inside of the packaging container produced from the packaging laminate, i.e. the innermost layer 43 is in direct contact with the packaged product. Such heat-sealable innermost layer 43, which will form a strong heat seal of the liquid packaging container produced from the laminate packaging material, comprises one or more combinations of polyethylenes selected from the group consisting of LDPE, linear low density polyethylene (LLDPE) and LLDPE produced by polymerizing ethylene monomers with C4-C8, more preferably C6-C8, α-olefin alkylene monomers in the presence of a metallocene catalyst, i.e. the so-called metallocene-LLDPE (mLLDPE).

[0236] The barrier coated high density paper substrate 20b, i.e. 45, of Figure 2b is further laminated by melt extrusion lamination with an intermediate tie layer 49 of low density polyethylene (LDPE) to a complementary barrier film 44 consisting of a polymeric film substrate 44a, which is a film of biaxially oriented polypropylene (BOPP) coated with an aluminized barrier coating 44b.

[0237] The bulk layer 41 is then laminated to the non-laminated face of the barrier coated high density paper substrate 20b depicted in Figure 2b by wet lamination with a thin layer of adhesive polymer intermediate tie layer 46 obtained by applying an aqueous dispersion of PVOH or polyvinyl acetate adhesive to one of the surfaces to be bonded together and then pressing with a roller nip. This lamination step can be an efficient low or ambient temperature lamination step, as depicted in Figure 3, and can be performed at a density of a few g / m2 so that no drying and evaporation is required. 2 Alternatively, only the intermediate bonding layer 46 may be used.

[0238] Therefore, in this laminate packaging material, the amount of thermoplastic polymer in the laminate layer can also be reduced, as compared with the conventional melt-extrusion laminate adhesive layer of polyethylene as described in FIG.

[0239] An innermost layer 43 is applied over the barrier coated film 44, optionally with an adjacent adhesive polymer layer, in a coextrusion coating operation.

[0240] According to a further embodiment not shown, the uncoated high density paper substrate 10a or 10b of FIG. 1a or FIG. 1b may be laminated in the same laminate structure as described above instead of the coated high density paper substrate 45, i.e. 20b.

[0241] FIG. 5 shows a laminate packaging material 50 for liquid carton packaging, which has a bending force of 80 mN and a compressibility of about 200 g / m 2 The packaging laminate comprises a bulk layer 51 of paperboard having a basis weight of about 12 g / m2, and further comprises a liquid-tight, heat-sealable outer layer 52 of polyolefin applied to the outside thereof so as to face the outside of the package produced from the packaging laminate. This outer layer 52 is transparent to allow a printed decorative pattern 57 to be visible on the outside, thereby informing the contents of the package, the package brand, and other information targeted to consumers in retail establishments and food establishments. The polyolefin of the outer layer 52 is a conventional low density polyethylene (LDPE) of heat-sealable quality, but may also include more similar polymers, including LLDPE. The application weight is about 12 g / m2. 2 It is.

[0242] A liquid-tight, heat-sealable innermost layer 53 is arranged opposite the bulk layer 51, this layer being directed towards the inside of the packaging container produced from the packaging laminate, i.e. the innermost layer 53 is in direct contact with the packaged product. This innermost heat-sealable layer 53, which will form a strong transverse heat seal of the liquid packaging container produced from the laminate packaging material, comprises one or more combinations of polyethylenes selected from the group consisting of LDPE, linear low density polyethylene (LLDPE) and LLDPE produced by polymerizing ethylene monomers with C4-C8, more preferably C6-C8, α-olefin alkylene monomers in the presence of a metallocene catalyst, the so-called metallocene-LLDPE (mLLDPE). It has a mass of about 29 g / m2 is applied in an amount of

[0243] The bulk layer 51 is laminated to the barrier coated high density paper substrate by the coated paper substrate 20c as illustrated in Fig. 2c, where the vapor deposited barrier coating is an aluminum metallized coating or a transparent aluminum oxide (AlOx) coating. The coated paper substrate is laminated to the outside of the bulk layer 51 and is between the bulk layer and the outermost liquid tight layer 52, which acts as a combined barrier and printed paper substrate. Thus, according to this embodiment, the printed decoration is printed on the barrier coated top surface of the high density paper substrate.

[0244] In this way, the uncoated side of the barrier coated paper substrate 20c in Fig. 2c, i.e. 55a of 55, is laminated to the outer side of the bulk layer by wet lamination with an intermediate tie layer 56 of a thin layer of adhesive polymer, obtained by applying an aqueous dispersion of PVOH or polyvinyl acetate adhesive to one of the sides to be bonded together and then pressing with a roller nip. The dry coating weight of the intermediate tie layer 56 is a few g / m2 so that no drying and evaporation is required. 2 It is.

[0245] The inside of the bulk layer has a complementary barrier vapor deposition coated onto a polymeric film substrate, such as that used in laminate material 40 of Figure 4. The complementary barrier film 54 is a polymeric film substrate 54a, which is a film of biaxially oriented polypropylene (BOPP), coated with a barrier coating 54b, which is an aluminum vapor deposition coating. It is laminated to the inside of the bulk layer in a wet lamination operation similar to that used to laminate the outside of the bulk layer to the high density paper substrate 55, but instead uses an acrylic adhesive 57.

[0246] The heat-sealable innermost layer 53 may consist of one layer or may consist of two or more partial layers of the same or different types of LDPE or LLDPE or blends thereof, and is well adhered to the metallized barrier film 55 by an intermediate coextruded tie layer 58, for example of ethylene acrylic acid copolymer (EAA), that is applied together with the innermost layer 53 in a single melt coextrusion coating process.

[0247] In an alternative embodiment not shown, the complementary barrier inside the bulk layer 51 is a high density paper that is further barrier coated as shown in 20a or 20c in Figure 2a or 2c. With such a material structure, the sandwich arrangement of the barrier coated high density paper substrate on both sides can contribute with its relatively high Young's modulus to compensate for the weaker bulk layer having a lower bending stiffness than usual, providing a high overall oxygen barrier performance.

[0248] In FIG. 6a, the process of aqueous dispersion coating 60a is shown, which may be used to apply a gas barrier coating 12 from a water gas barrier composition onto a substrate, or to apply an aqueous adhesive composition for wet laminating two webs together, at least one of which has a fibrous cellulosic surface. A paper substrate web 61a (e.g., paper substrate 11a; 11b in FIG. 1) is fed to a dispersion coating station 62a, where an aqueous dispersion composition is applied by a roller onto the upper surface of the substrate. The aqueous composition has an aqueous content of 80-99% by weight, and on the wet coated substrate there is a lot of water that needs to be dried and evaporated off by heat to form a continuous coating that is homogenous and has uniform quality in terms of barrier and surface properties, i.e. uniformity and wettability. Drying is performed by a hot air dryer 63a, which evaporates off the water from the surface of the paper substrate. The temperature of the substrate is kept constant at a temperature of 60°C to 80°C as it passes through the dryer. Alternatively, drying may be partially assisted by radiation heat from infrared IR lamps in combination with hot air convection drying.

[0249] The resulting barrier coated paper substrate web 64a is cooled and wound onto a reel for intermediate storage prior to further deposition coating of the barrier deposition coating onto the paper substrate 61a (23a; 20b).

[0250] FIG. 6b shows the process (60b) of the final lamination process in the production of a laminated packaging material such as 30 or 40 in FIGS. 3 and 4 after the bulk layer 31, 41 has first been laminated to the barrier coated paper substrate 20a, 20b, 20c of FIGS. 2a-c, i.e. 35 or 44 in FIGS. 3 and 4, respectively.

[0251] Bulk ply paperboard may be laminated to a barrier coated paper substrate by wet cold dispersion adhesive lamination or by melt extrusion lamination.

[0252] The resulting paper prelaminate web 61b is transported from an intermediate storage reel or directly from a lamination station for laminating the paper prelaminate. The non-laminate side, i.e. the printed side, of the bulk layer 31;41 is bonded in a cooled roller nip 63 to a molten polymer curtain 62 of LDPE forming the outermost layer 32;42 of the laminate material, the LDPE being extruded from an extruder feedblock and die 62b. The paper prelaminate web with the outermost layer 62;32;42 coated on the printed side, i.e. on the outside, then passes through a second extruder feedblock and die 64b and a lamination nip 65, where the molten polymer curtain 64 is bonded and coated on the other side of the prelaminate, i.e. the barrier-coated side of the paper substrate. Thus, a heat-sealable innermost layer 64:33;43 is coextrusion coated onto the inside of the pre-laminate web of paper to ultimately form a laminate wrapper 66 which is wound up on a storage reel (not shown).

[0253] These two co-extrusion steps in the lamination roller nips 63 and 65 may alternatively be performed as two successive steps in the reverse order.

[0254] According to another embodiment, one or both of the outermost layers may instead be applied at a pre-lamination station, where a co-extrusion coating layer is first applied to the outside of a (printed) bulk paperboard layer or onto a barrier coated paper substrate, and then the two pre-laminated paper webs may be bonded together as described above.

[0255] Figure 7a is a perspective view of an example of a plant 70a for physical vapor deposition (PVD) of, for example, aluminum metal coatings on a web substrate of the invention. A coated or uncoated high density paper substrate 71 is subjected on its precoated side to a continuous vapor deposition 72 of evaporated aluminum, forming a metallized layer of aluminum, or alternatively to a mixture of oxygen and aluminum vapor, forming a vapor deposition coating of aluminum oxide. The coating is provided with a thickness of 5-100 nm, preferably 10-50 nm, so that a barrier coated paper substrate 73 of the invention is formed. The aluminum vapor is formed by ion bombardment of an evaporation source of solid pieces of aluminum 72. In the case of a coating of aluminum oxide, a portion of oxygen gas may be injected into the plasma chamber via an inlet port.

[0256] FIG. 7b is a perspective view of an example of a plant 70b for plasma enhanced chemical vapor deposition coating (PECVD) of, for example, hydrogenated amorphous diamond-like carbon coatings on web substrates of the present invention. A web substrate 74a is subjected on one surface to continuous PECVD of plasma in a plasma reaction zone 75 formed in the space between a magnetron electrode 76 and a cooled web transport drum 77, which also functions as an electrode, and the film is advanced by the rotating drum along the circumference of the drum through the plasma reaction zone. The plasma for the deposition coating of the amorphous DLC coating layer can be generated from injecting a gas precursor composition consisting of, for example, organic hydrocarbon gases such as acetylene or methane into the plasma reaction chamber. Other gas barrier coatings may also be applied by the same main PECVD method, such as silicon oxide coatings (SiOx) starting from precursor gases of organosilicon compounds. The PECVD plasma chamber is kept under vacuum by continuously evacuating the chamber at outlet ports 78a and 78b.

[0257] FIG. 8A shows an embodiment of a packaging container 50a made from a packaging laminate according to the invention. This packaging container is particularly suitable for beverages, sauces, soups, etc. Typically, such a packaging container has a volume of about 100-1000 ml. It may be of any shape, but is preferably brick-shaped, with longitudinal seals 81a and transverse seals 82a, respectively, and optionally with an opening device 83. In another embodiment, not shown, the packaging container may be wedge-shaped. To obtain such a "wedge shape", only the bottom of the package is folded, and the transverse heat seal at the bottom is formed so as to be hidden under triangular corner flaps that are folded and sealed against the bottom of the package. The transverse seal at the top remains unfolded. In this way, the packaging container, only partially folded, is easy to handle and dimensionally stable enough to be placed on a shelf in a food store or on a flat surface.

[0258] Figure 8b shows an alternative packaging container 80b made from an alternative packaging laminate according to the present invention. The alternative packaging laminate is thinner by having a thinner paper bulk layer and therefore is not dimensionally stable enough to form a parallelepiped or wedge shaped package and no creases are formed after the transverse seal 82b. The package remains a pillow-like bag and is distributed and sold in this form.

[0259] 8c shows a gable-top package 50c that is folded and formed from pre-cut sheets or blanks of a laminate packaging material that includes a bulk layer of paperboard and a barrier-coated paper substrate of the present invention. Flat-top packages may also be formed from similar blanks.

[0260] Figure 8d shows a bottle-like package 50d which is a combination of a sleeve 54 formed from a pre-cut blank of the laminate packaging material of the present invention and a top 55 formed from injection-molded plastic in combination with an opening device such as a screw cork. Packages of this kind are sold, for example, under the trade names Tetra Top® and Tetra Evero®. These special packages are formed by fitting a molded top 55 with an opening device in a closed state to a cylindrical sleeve 54 of laminate packaging material, sterilizing the bottle-top capsule thus formed, filling it with food, and finally folding and sealing the bottom of the package.

[0261] Figure 9 illustrates the principle described in the introduction to this application: a web of packaging material is formed into a tube 91 by overlapping longitudinal ends 92a, 92b of the web and heat sealing them together, thereby forming an overlap joint 93. The tube is continuously filled 94 with the liquid food to be filled and divided into individual filled packages by repeating double transverse sealing 95 of the tube at predetermined intervals below the level of the filled contents in the tube. The packages 96 are separated by cutting between the double transverse seals (top seal and bottom seal) and finally formed into the desired geometric shape by forming folds along preformed crease lines in the material.

[0262] FIG. 10 compares the loss of oxygen barrier properties of a laminate made from a high density paper substrate of the present invention with a laminate material made from a reference paper, and is further described in Example 2.

[0263] Finally, it should be noted that the invention is not limited to the embodiments shown and described above, but various modifications are possible within the scope of the claims.

Claims

1. A coated high density paper substrate (20a; 20b; 20c) for use as a gas barrier material in a laminated packaging material for liquid, semi-liquid or viscous food or water, comprising: The coated high density paper substrate comprises a high density paper substrate (10a; 10b) and at least one coating (22a, 24a; 22b; 24c) of at least one gas barrier material on an upper surface of the high density paper substrate, The high density paper substrate has a basis weight of 30 to 75 g / m2 measured according to ISO 536:2012. ２ , density measured according to ISO 534:2011 is 1000 kg / m ３ and the advanced paper substrate is impregnated (11a) on its upper surface (12a; 12b) with an impregnation composition comprising an impregnation polymer selected from the group consisting of polyvinyl alcohol, PVOH, ethylene vinyl alcohol, EVOH, starch, starch derivatives, carboxymethyl cellulose, nanocrystalline cellulose, NCC, and blends of two or more thereof, the amount of said impregnation polymer being 0.3-4.0 g / m2 by dry weight. A coated high density paper substrate (20a; 20b; 20c).

2. The high density paper substrate (10a; 10b) is formed from cellulose fibers containing at least 50% by dry weight of kraft pulp; The coated high density paper substrate of claim 1.

3. The high density paper substrate is formed from cellulose fibers containing 35-100% softwood pulp, 0-65% hardwood pulp, and optionally 0-15% CTMP pulp, based on the dry weight of the pulp used to form the high density paper. The coated high density paper substrate of claim 1.

4. the high density paper substrate has a Shopper-Riegler (SR) number, measured according to ISO 5267-1:1999, of 30 to 50 after repulping according to ISO 5263-1:2004; The coated high density paper substrate of claim 1.

5. the high density paper substrate has, after repulping according to ISO 5263-1:2004, an average fines content measured according to ISO 16065-2:2014 with an L&W Fibretester+ (ABB, Lorentzen&Wettre, Sweden) of less than 40%, fines being defined as fibrous particles shorter than 0.2 mm; The coated high density paper substrate of claim 1.

6. the cellulose fibers of said high density paper substrate exhibit a Canadian Standard Freeness (CSF) value of greater than 200 ml, measured according to ISO 5267-2:2001, after repulping according to the Valmet repulping process carried out on a Valmet pulper of type HD400; The coated high density paper substrate of claim 1.

7. The high density paper substrate (10a; 10b) is impregnated from the top side, after which the top side surface roughness (12a; 12b) is less than 100 ml / min Bendtsen, as measured according to SS-ISO 8791-2:2013; The coated high density paper substrate of claim 1.

8. The high density paper substrate is further impregnated (13a) on the opposite, back surface (14a) of the paper with an impregnation composition comprising an impregnation polymer selected from the same group of polymers impregnated for the upper surface of the paper, The paper is impregnated from the back side and then calendered so that the roughness of the back surface is lower than 200 ml / min Bendtsen, measured according to SS-ISO 8791-2:2013. The coated high density paper substrate of claim 1.

9. The impregnation composition comprises, in addition to the polymer, a clay selected from the group consisting of bentonite, kaolin and barite, and talcum, CaCO ３ and silica particles, The coated high density paper substrate of claim 1.

10. The thickness of the high-density paper base material is 35 to 75 μm. The coated high density paper substrate of claim 1.

11. The high density paper base material (10b) has an upper layer (11b) and a lower layer (13b); The coated high density paper substrate of claim 1.

12. The upper layer (11b) is formed from at least 50% by dry weight of hardwood pulp; The coated high density paper substrate of claim 10.

13. The lower layer (13b) is formed from at least 50% by dry weight of softwood pulp. The coated high density paper substrate of claim 10.

14. the upper surface of said high density paper substrate having said at least one coating (22a, 24a; 22b; 24c) to a total coating thickness of 2 to 5000 nm; The coated high density paper substrate of claim 1.

15. the upper surface of said high density paper substrate is coated with a gas barrier material (22a; 22b) to a dry coating thickness of 100-5000 nm (0.1-5 μm), said gas barrier material comprising a polymer selected from the group consisting of vinyl alcohol polymers and copolymers; 15. The coated high density paper substrate of claim 14.

16. the upper surface of the high density paper substrate being provided with a vapor deposition coating (24c) of a gas barrier material selected from a metal, a metal oxide, an inorganic oxide, and an amorphous diamond-like carbon coating; 15. The coated high density paper substrate of claim 14.

17. The upper surface of the high-density paper substrate has a first coating (22a) of a gas barrier material formed by applying a dispersion or solution of a water gas barrier composition and then drying it, and further has a vapor deposition coating (24a) of a gas barrier material selected from a metal, a metal oxide, an inorganic oxide, and amorphous diamond-like carbon applied on the first coating.

15. The coated high density paper substrate of claim 14.

18. A laminated packaging material (30; 40; 50) for packaging liquid, semi-liquid or viscous food or water, comprising 2. A coated high density paper substrate (20a; 20b; 20c) according to claim 1, further comprising a first outermost layer (32; 42; 52) of liquid-tight material and a second innermost layer (33; 43; 53) of liquid-tight material. Laminated packaging materials (30; 40; 50).

19. a bulk layer (31; 41; 51) of paper or paperboard or other cellulosic material, with the coated high density paper substrate (20a; 20b; 20c) laminated between the bulk layer and the second innermost layer, 20. The laminate packaging material of claim 18.

20. The coated high density paper substrate has a density of 0.5 to 5 g / m ２ said intermediate adhesive composition (36; 46; 57) comprising a binder selected from the group consisting of acrylic polymers and copolymers, starch, starch derivatives, cellulose derivatives, polymers and copolymers of vinyl acetate, copolymers of vinyl alcohol, and copolymers of styrene-acrylic or styrene-butadiene latex; 20. The laminate packaging material of claim 18.

21. A prefabricated polymer film is laminated between the coated high density paper substrate and the second innermost layer to improve the robustness of the mechanical properties of the laminate packaging material.

20. The laminate packaging material of claim 18.

22. a prefabricated polymer film (44, 44a) laminated to an inner side of the coated high density paper substrate (20a; 20b; 20c), the prefabricated polymer film (44, 44a) having a vapor deposition coating (44b) of a gas barrier material selected from metals, metal oxides, inorganic oxides, and amorphous diamond-like carbon coatings; 20. The laminate packaging material of claim 18.

23. a bulk layer (51) of paper or paperboard or other cellulosic material, with the coated high density paper substrate (20a; 20b; 20c) laminated between the bulk layer and the first outermost layer (52); 20. The laminate packaging material of claim 18.

24. The upper surface of the high density paper substrate (55a) is coated with an aluminum metallized coating (55b) and faces the first outermost layer of the laminate packaging material; 24. The laminate packaging material of claim 23.

25. a further high density paper substrate (10a; 10b) or a coated high density paper substrate (20a; 20b; 20c) laminated between the bulk layer (31; 41; 51) and the first outermost layer (32; 42; 52); 20. The laminate packaging material of claim 18.

26. A packaging container (50a; 50b; 50c; 50d) for packaging liquid, semi-liquid or viscous food or water, comprising a laminate packaging material (30; 40; 50) according to claim 18.