Electrolyte, secondary battery, and power consumption device

Abstract

To provide an electrolyte, a secondary battery, and a power consumption device.SOLUTION: An electrolyte includes a solution and an additive. The solvent includes a compound of the formula I. The mass ratio of the compound of the formula I in the solvent is 35% or more. In the formula I, R1 and R2 are each independently selected from any one of a hydrogen atom, a C1-C3 chain alkyl group, and a C2-C3 alkenyl group. The additive includes a compound of the formula II. In formula II, R3, R4, and R5 are each independently selected from any one of a hydrogen atom, a fluorine atom, a phenyl group, a cyano group, a C1-C6 chain alkyl group, a C3-C6 cyclic alkyl group, and a C2-C6 alkenyl group. The present application can simultaneously consider the good dynamics performance, high-temperature performance, and over-charge prevention performance of a battery.SELECTED DRAWING: Figure 1

Description

[Technical field]

[0001] The present application relates to the technical field of batteries, and in particular to electrolytes, secondary batteries and power consuming devices. [Background technology]

[0002] 2. Description of the Related Art In recent years, secondary batteries have been widely applied in energy storage power supply systems such as hydroelectric, thermal, wind and solar power stations, as well as in multiple fields such as power tools, electric bicycles, electric motorcycles, electric vehicles, military equipment, aerospace, etc.

[0003] With the great development of secondary batteries, the requirements for their energy density, cycle performance, safety performance, etc. are increasing. Summary of the Invention [Problem to be solved by the invention]

[0004] The present application has been made in view of the above problems, and aims to provide an electrolyte, a secondary battery, and a power consuming device. The secondary battery using the electrolyte of the present invention can simultaneously take into consideration good kinetic performance, high temperature performance, and excellent overcharge prevention performance. [Means for solving the problem]

[0005] To achieve the above object, a first aspect of the present application provides an electrolyte solution comprising a solvent and an additive, the solvent comprising a compound of formula I, and a mass ratio of the compound of formula I in the solvent being 35% or more.

[0006] [ka]

[0007] (R1 and R2 are each independently any one selected from a hydrogen atom, a C1-C3 linear alkyl group, and a C2-C3 alkenyl group.)

[0008] The additive comprises a compound of formula II.

[0009] [ka]

[0010] (R3, R4, and R5 are each independently any one selected from a hydrogen atom, a fluorine atom, a phenyl group, a cyano group, a C1-C6 linear alkyl group, a C3-C6 cyclic alkyl group, and a C2-C6 alkenyl group.)

[0011] The present application considers good kinetic performance, high temperature performance and excellent overcharge prevention performance by including the compound of formula I and the compound of formula II in the electrolyte.

[0012] In any embodiment, the mass ratio of the compound of formula I in the solvent may be 40% to 70%. By setting the mass ratio of the compound of formula I in the solvent in the above range, the present application can ensure that the electrolyte has high conductivity and low viscosity, and can be applied to a thick coating system, thereby further improving the dynamic performance of the battery.

[0013] In any embodiment, the mass ratio of the compound of formula II in the electrolyte may be 9% or less, and preferably 3% to 5%. In the present application, by setting the mass ratio of the compound of formula II in the electrolyte within the above range, the overcharge prevention performance can be further improved.

[0014] In any embodiment, the compound of formula I may include at least one selected from methyl formate, methyl acetate, ethyl acetate, propyl acetate, methyl acrylate and ethyl acrylate. The present application can further improve the dynamics performance by selecting the compound.

[0015] In any embodiment, the compound of formula II may include at least one selected from biphenyl, fluorobenzene, and cyclohexylbenzene. By selecting the compound, the present application can further improve the overcharge prevention performance.

[0016] In any embodiment, the electrolyte may satisfy a / b≧11, and preferably 11≦a / b≦35 (wherein a is the mass ratio of the compound of formula I in the solvent, and b is the mass ratio of the compound of formula II in the electrolyte). In the present application, by setting the a / b in the above range, the kinetic performance and overcharge prevention performance can be further improved.

[0017] In any embodiment, the electrolyte solution may further include an electrolyte salt, and the electrolyte salt may include a compound of formula III, and the molar ratio of the compound of formula III in the electrolyte salt is 10% or more, preferably 20% or more.

[0018] [ka]

[0019] (R6 and R7 are each independently an F atom or a fluoroalkyl group, and R6 and R7 may be linked to form a ring.)

[0020] In the present invention, by adding the compound of the above formula III to the electrolyte solution and setting the molar ratio of the compound of the above formula III in the electrolyte salt within the above range, the water resistance of the electrolyte solution can be improved and the high-temperature cycle characteristics of the battery can be improved.

[0021] In any embodiment, the compound of formula III may include at least one selected from lithium bisfluorosulfonyl imide and lithium bis(trifluoromethanesulfonyl)imide. By selecting the compound, the water resistance of the electrolyte can be further improved, and the high-temperature cycle characteristics of the battery can be improved.

[0022] In any embodiment, the solvent may further contain a carbonate ester, and the mass ratio of the carbonate ester in the solvent is 30% or more, preferably 35% to 65%, and more preferably 40% to 50%.

[0023] In an optional embodiment, the solvent further comprises ethylene carbonate, and the mass ratio of the ethylene carbonate in the solvent is 30% or more.

[0024] By further including a carbonate ester in the solvent and setting the mass ratio of the carbonate ester in the solvent within the above range, sufficient dissociation of the electrolyte, particularly the lithium salt, can be ensured, and a stable film can be formed on the negative electrode, thereby improving the stability of the negative electrode interface.

[0025] In any embodiment, the additive may further include at least one selected from vinylene carbonate (VC), fluoroethylene carbonate (FEC), ethylene sulfate (DTD), 1,3-propane sultone (PS), lithium difluorobisoxalatophosphate (LiDFOP), lithium difluorooxalatoborate (LiDFOB) and lithium bisoxalatoborate (LiBOB). By adding the additive, the cycle characteristics and thermal stability of the battery can be further improved.

[0026] A second aspect of the present application provides a secondary battery comprising the electrolyte solution according to the first aspect. The secondary battery of the present invention can simultaneously take into account good kinetic performance, high temperature performance and excellent overcharge prevention performance.

[0027] In any embodiment, the secondary battery may include a positive electrode plate, the positive electrode plate may include a positive electrode coating layer, the positive electrode coating layer may include a positive electrode active material, and the positive electrode active material may include a lithium-containing phosphate having an olivine structure. By using the lithium-containing phosphate having an olivine structure as the positive electrode active material, the cycle life can be improved.

[0028] In any embodiment, the secondary battery has a density of 1 g / 1000 m2 ≦L≦5g / 1000m 2 and preferably satisfies 1 g / 1000 m 2 ≦L≦4g / 1000m 2 More preferably, it satisfies 1.5g / 1000m 2 ≦L≦4g / 1000m 2 L = M1 / ​​[M2 × B × (a + c)] * 1000 (M1 is the mass of the compound of formula II, in g; M2 is the mass of the positive electrode active material, in g; B is the specific surface area of ​​the positive electrode active material, in m 2 / g, a is the mass ratio of the compound of formula I in the solvent, and c is the molar ratio of the compound of formula III in the electrolyte salt. By setting L in the above range, the dynamic performance, high temperature performance, and overcharge prevention performance of the battery can be further improved.

[0029] In any embodiment, 8 m 2 / g≦B≦16m 2 / g, preferably 10m 2 / g≦B≦14m 2 By setting the specific surface area of ​​the positive electrode active material within the above range, solid-phase diffusion inside the positive electrode plate can be improved, which contributes to improving the dynamic performance of the cell.

[0030] In any embodiment, the thickness of the positive electrode coating layer on one side is 0.08 mm or more, preferably 0.09 mm to 0.3 mm.

[0031] A third aspect of the present application provides a power consumption device including the secondary battery according to the second aspect. Because the power consumption device includes the secondary battery, it has all the beneficial effects of the secondary battery. Effect of the Invention

[0032] According to the present invention, good kinetic performance, high temperature performance and excellent overcharge prevention performance of the battery can be simultaneously taken into consideration. [Brief description of the drawings]

[0033] [Figure 1] FIG. 1 is a schematic diagram of a secondary battery according to an embodiment of the present application. [Diagram 2] FIG. 2 is an exploded view of the secondary battery according to the embodiment of the present application shown in FIG. [Diagram 3] FIG. 1 is a schematic diagram of a battery module according to an embodiment of the present application. [Figure 4] FIG. 1 is a schematic diagram of a battery pack according to an embodiment of the present application. [Diagram 5] FIG. 5 is an exploded view of the battery pack according to the embodiment of the present application shown in FIG. 4. [Figure 6] 1 is a schematic diagram of a power consuming device that uses a secondary battery as a power source according to an embodiment of the present application. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0034] Hereinafter, with reference to the drawings as appropriate, an embodiment specifically disclosing the electrolyte, secondary battery, and power consumption device of the present application will be described in detail. However, unnecessary detailed description may be omitted. For example, detailed description of known matters and repeated description of substantially the same structure may be omitted. This is to avoid the following description becoming unnecessarily long and to make it easy for those skilled in the art to understand. In addition, the drawings and the following description are provided to enable those skilled in the art to fully understand the present application, and are not intended to limit the subject matter described in the claims.

[0035] The "ranges" disclosed herein are defined in the form of lower and upper limits, and a given range is defined by selecting one lower limit and one upper limit, with the selected lower and upper limits defining the boundaries of the particular range. The ranges thus defined may or may not include the endpoint values ​​and may be arbitrarily combined, i.e., any lower limit and any upper limit may be combined to form a range. For example, if ranges of 60-120 and 80-110 are listed for a particular parameter, it is understood that the ranges of 60-110 and 80-120 are also contemplated. Also, if 1 and 2 are listed as the minimum range values ​​and 3, 4, and 5 are listed as the maximum range values, all of the ranges of 1-3, 1-4, 1-5, 2-3, 2-4, and 2-5 are contemplated. In this application, unless otherwise specified, the numerical range "a-b" represents a shorthand notation for any combination of real numbers between a and b, where a and b are both real numbers. For example, the numerical range "0-5" means that all real numbers between "0-5" are listed herein, with "0-5" being merely a shorthand for combinations of these numbers. Also, when a parameter is described as an integer ≧2, this is equivalent to disclosing that the parameter is, for example, the integers 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, etc.

[0036] Unless otherwise specified, all and any embodiments of the present application can be combined with each other to form a new technical solution.

[0037] Unless otherwise specified, all and any technical features of this application can be combined with each other to form a new technical solution.

[0038] Unless otherwise specified, all steps in the present application may be performed in sequence or randomly, preferably in sequence. For example, the method includes steps (a) and (b) indicating that the method may include steps (a) and (b) performed in sequence, or may include steps (b) and (a) performed in sequence. For example, the method may further include step (c) indicating that step (c) can be added to the method in any order, for example, the method may include steps (a), (b) and (c), may include steps (a), (c) and (b), may include steps (c), (a) and (b), etc.

[0039] Unless otherwise specified, the terms "comprise" and "inclusion" in this application may be open or closed. For example, the terms "comprise" and "inclusion" may mean that the term further includes or includes other components not listed, or that the term only includes or includes the components listed.

[0040] In this application, unless otherwise specified, the term "or" is inclusive. For example, the phrase "A or B" means "A, B, or both A and B." More specifically, the condition A is true (or exists) and B is false (or does not exist), the condition A is false (or does not exist) and B is true (or exists), or the condition A and B are both true (or exist) all satisfy the condition "A or B."

[0041] The present application provides an electrolyte, a secondary battery including the electrolyte, and a power consuming device including the secondary battery. The electrolyte, the secondary battery, and the power consuming device of the present application are described in detail below.

[0042] electrolyte In one embodiment of the present application, there is provided an electrolyte solution comprising a solvent and an additive, the solvent comprising a compound of formula I, and the mass ratio of the compound of formula I in the solvent is 35% or more.

[0043] [ka]

[0044] (In the formula, R1 and R2 are each independently any one selected from a hydrogen atom, a C1-C3 linear alkyl group, and a C2-C3 alkenyl group.)

[0045] The additive comprises a compound of formula II.

[0046] [ka]

[0047] (In the formula, R3, R4, and R5 are each independently any one selected from a hydrogen atom, a fluorine atom, a phenyl group, a cyano group, a C1-C6 linear alkyl group, a C3-C6 cyclic alkyl group, and a C2-C6 alkenyl group.)

[0048] Although the mechanism is not yet clear, the applicant has unexpectedly discovered that by combining the compound of formula I and the compound of formula II in the electrolyte and setting the content of the compound of formula I at a predetermined amount, it is possible to simultaneously consider the good dynamic performance, high temperature characteristics and excellent overcharge prevention performance of the battery.

[0049] In batteries that use lithium iron phosphate (e.g., LiFePO4 (also called LFP)) as the positive electrode active material, the most common method for improving the energy density is to increase the thickness of the coating on the positive electrode plate to improve the space utilization rate inside the cell, but a new problem occurs when the coating is made thicker. Increasing the thickness of the positive electrode coating means that the transport path of lithium ions in the plate becomes longer, making the transport of lithium ions more difficult, and requiring further improvement in the conductivity of the electrolyte. This problem becomes more serious as the positive electrode coating becomes thicker.

[0050] To solve this problem, the applicant has found that the use of a low-viscosity, high-dielectric constant solvent (such as the compound of formula I) in the electrolyte can greatly improve the conductivity of the electrolyte, improving the current situation in which lithium ions are difficult to transport due to thick coating. However, the oxidation potential of the compound of formula I is low, which greatly affects the overcharge performance of LFP cells. In order to reduce safety issues such as thermal runaway in the overcharged state of the battery, the applicant has found that the purpose of improving the safety of the battery can be achieved by adding the compound of formula II to the electrolyte as an overcharge prevention additive. However, the addition of an overcharge prevention additive such as the compound of formula II affects the kinetic performance of the battery.

[0051] As a result of intensive research, the applicant has found that adding a specific content of the compound of formula I to an electrolyte containing the compound of formula II can improve the kinetic performance and high temperature performance of a battery, and thus the synergistic effect of the specific content of the compound of formula I and the compound of formula II can simultaneously take into account good kinetic performance, high temperature performance and overcharge prevention performance.

[0052] In some embodiments, the compound of formula I above includes methyl formate, methyl acetate, ethyl acetate, propyl acetate, methyl propionate, ethyl propionate, propyl propionate, methyl acrylate, ethyl acrylate, etc. The compound of formula I above preferably includes at least one selected from methyl formate, methyl acetate, ethyl acetate, propyl acetate, methyl acrylate, and ethyl acrylate. More preferably, it includes methyl formate and ethyl acetate. These compounds are used as a solvent for the electrolyte, and these compounds have a lower viscosity than linear carbonate esters and a higher dielectric constant than linear carbonate esters. Adding these compounds to the electrolyte to replace linear carbonate esters can effectively improve the conductivity of the electrolyte, thereby further improving the dynamic performance of the battery.

[0053] The solvent of the electrolyte of the present application includes the compound of formula I, and the mass ratio of the compound of formula I in the solvent is 35% or more, preferably, the mass ratio of the compound of formula I in the solvent is 40% to 70%, preferably, 50% to 60%. If the mass ratio of the compound of formula I in the solvent is less than 35%, the conductivity decreases, the initial DCR (Direct Current Resistance) increases, and the dynamic performance of the battery decreases. Therefore, the present application can ensure that the electrolyte has high conductivity and low viscosity and can be applied to a thick coating system by setting the mass ratio of the compound of formula I in the solvent within the above range, thereby further improving the dynamic performance of the battery. In addition, if the mass ratio of the compound of formula I in the solvent is greater than 70%, it is disadvantageous to the overcharge prevention performance.

[0054] In the present application, the solvent of the electrolyte may further contain one or more carbonate esters selected from ethylene carbonate (EC), propylene carbonate (PC), dimethyl carbonate (DMC), ethyl methyl carbonate (EMC) and diethyl carbonate (DEC). The mass ratio of the carbonate ester in the solvent may be 30% or more, preferably 35% to 65%, and more preferably 40% to 50%. It is preferable that the solvent contains ethylene carbonate, and more preferably, the mass ratio of the ethylene carbonate in the solvent is 30% or more. By including ethylene carbonate in the solvent and setting the mass ratio of the ethylene carbonate in the solvent within the above range, sufficient dissociation of the electrolyte, particularly the lithium salt, can be ensured, and a film can be stably formed on the negative electrode, thereby improving the stability of the negative electrode interface.

[0055] In some embodiments, the electrolyte of the present application includes the compound of formula II as an additive, and the compound of formula II functions as an overcharge inhibitor. Preferably, the compound of formula II may include at least one selected from biphenyl, fluorobenzene, and cyclohexylbenzene. The present application can further improve the overcharge prevention performance by using the compound as an overcharge inhibitor. The present application preferably includes fluorobenzene. When the cell is overcharged, the voltage increases, the overcharge prevention additive polymerizes, and an insulating film is formed on the surface of the electrode through polymerization, which increases the internal resistance of the battery, reduces or cuts off the overcharge current, and improves the safety performance of the battery. Meanwhile, a large amount of heat is released, and the fluorobenzene-based material is polymerized at high voltage to become a fluorine-containing polymer, which has better high temperature resistance. In addition, compared with other benzene ring-based materials, the fluorobenzene-based material is easy to bond with electrons due to fluorine substitution, and can suppress the reduction side reaction of the compound of formula I at the negative electrode to a certain extent.

[0056] In addition, the mass ratio of the compound of the formula II in the electrolyte is 9% or less, preferably 3% to 8%, more preferably 3% to 7%, even more preferably 3% to 6%, and particularly preferably 3% to 5%. If the content of the compound of the formula II is too high, it is disadvantageous to the conductivity of the electrolyte, and therefore to the dynamic performance of the battery. If the content of the compound of the formula II is too low, it is disadvantageous to the overcharge prevention performance. In the present application, by setting the mass ratio of the compound of the formula II in the electrolyte within the above range, the overcharge prevention performance can be further improved without affecting the conductivity of the electrolyte.

[0057] In some embodiments, the electrolyte satisfies a / b≧11, preferably 11≦a / b≦35, more preferably 11≦a / b≦33, even more preferably 15≦a / b≦30, and particularly preferably 16≦a / b≦27. a is the mass ratio of the compound of formula I in the solvent, and b is the mass ratio of the compound of formula II in the electrolyte. In the present application, the dynamic performance can be further improved by setting the a / b in the above range.

[0058] Meanwhile, since the LFP material itself is prone to water absorption, during the cell production process, the moisture in the positive electrode plate cannot be completely removed when packaging before injection. During the subsequent use process, the moisture in the positive electrode plate gradually diffuses into the electrolyte, and a side reaction occurs with lithium hexafluorophosphate (LiPF6) in the electrolyte, generating hydrogen fluoride, destroying the solid electrolyte interphase (SEI) film, reducing the stability of the negative electrode interface, and accelerating cycle decay. The applicant has found that the use of a lithium salt that is not sensitive to water (such as the compound of the following formula III) can reduce the effect of moisture on the electrode plate and avoid the side reaction between the lithium salt and water. However, like the compound of formula I, the compound of formula III also has a low oxidation potential, which greatly affects the overcharge performance of the LFP cell. The purpose of improving the safety of the battery can be achieved by adding the compound of formula II to the electrolyte as an overcharge prevention additive.

[0059] Thus, in some embodiments, the present electrolyte solution comprises an electrolyte salt, which preferably comprises a compound of formula III.

[0060] [ka]

[0061] (R6 and R7 are each independently an F atom or a fluoroalkyl group. The alkyl group of the fluoroalkyl group may be a methyl group, an ethyl group, a propyl group, or the like. The fluoroalkyl group may be a partially fluorinated alkyl group or a completely fluorinated alkyl group, and examples of such fluoroalkyl groups include lithium bis(trifluoromethanesulfonyl)imide, lithium bis(nonafluorobutanesulfonyl)imide, and lithium bis(pentafluoroethanesulfonyl)imide (CF 10 LiNO4S2). R6 and R7 can also be linked to form a ring, for example, 1,1,2,2,3,3-hexafluoropropane-1,3-disulfonimide lithium (C3F6LiNO4S2).

[0062] In some embodiments, the compound of formula III preferably comprises at least one selected from lithium bisfluorosulfonyl imide (LiFSI) and lithium bis(trifluoromethanesulfonyl)imide (LiTFSI). More preferably, it comprises lithium bisfluorosulfonyl imide (LiFSI). The lithium salt is not sensitive to moisture and can mitigate the adverse effect of moisture increase caused by thickening coating of the electrode plate. Therefore, by selecting the compound of formula III as the electrolyte salt, the resistance of the electrolyte to water can be further improved, and the thermal cycle characteristics of the battery, especially the thermal cycle characteristics at 45°C, can be improved.

[0063] The molar ratio of the compound of the above formula III in the electrolyte salt may be 10% or more, preferably 20% or more, more preferably 30% or more, even more preferably 40%, particularly preferably 50% or more, and is preferably 80% or less, more preferably 75% or less, even more preferably 70% or less, particularly preferably 60% or less. In the present application, the molar ratio of the compound of the above formula III in the electrolyte salt is set within the above range, thereby improving the water resistance of the electrolyte.

[0064] The electrolyte salt may further include lithium hexafluorophosphate (LiPF6), which has high oxidation resistance but low thermal stability and is easily decomposed when in contact with water. The electrolyte solution of the present application includes the lithium salt of the compound of formula III, which has high thermal stability. Therefore, by adding lithium hexafluorophosphate and the lithium salt of the compound of formula III, oxidation resistance and thermal stability can be obtained.

[0065] In some embodiments, the electrolyte of the present application may further include additives such as vinylene carbonate (VC), fluoroethylene carbonate (FEC), ethylene sulfate (DTD), 1,3-propane sultone (PS), lithium difluorobisoxalatophosphate (LiDFOP), lithium difluorooxalatoborate (LiDFOB) and lithium bisoxalatoborate (LiBOB). Vinylene carbonate (VC), fluoroethylene carbonate (FEC), ethylene sulfate (DTD), and 1,3-propane sultone (PS) can function as film-forming additives, and when vinylene carbonate (VC) and 1,3-propane sultone (PS) function as film-forming additives, the impedance is large but the film-forming stability is high, and when fluoroethylene carbonate (FEC) and ethylene sulfate (DTD) function as film-forming additives, the impedance is small but the film-forming stability is low. In addition, additives such as lithium difluorobisoxalatophosphate (LiDFOP), lithium difluorooxalatoborate (LiDFOB), and lithium bisoxalatoborate (LiBOB) are not sensitive to moisture and can mitigate the adverse effects of moisture increase caused by thickening of the electrode plate. Therefore, by adding the above additives, the cycle characteristics and stability of the battery can be further improved.

[0066] In some embodiments, the conductivity of the electrolyte of the present application at 25 ° C. is 13 mS / cm or more, and may be, for example, 14 mS / cm to 18 mS / cm, 15 mS / cm to 17 mS / cm, or 16 mS / cm to 17 mS / cm. If the conductivity of the electrolyte is too small, the kinetic performance of the electrolyte is insufficient, and if the coating thickness of the positive electrode plate is large, the kinetic performance of the battery is affected, and if the conductivity of the electrolyte is too large, the thermal stability of the electrolyte is insufficient, and the high-temperature performance of the battery is affected. When the conductivity of the electrolyte of the present application at 25 ° C. is within the above range, the kinetic performance of the electrolyte can be improved, and the high and low-temperature performance of the battery and the energy density of the battery can be improved.

[0067] secondary battery A second aspect of the present application provides a secondary battery including the above electrolyte, which can simultaneously provide good kinetic performance, high temperature performance, and excellent overcharge prevention performance.

[0068] The secondary battery of the present application may be a lithium ion secondary battery or the like. In general, the secondary battery includes a positive electrode plate, a negative electrode plate, an electrolyte, and a separator. During the charging and discharging process of the battery, active ions are inserted and removed by reciprocating between the positive electrode plate and the negative electrode plate. The electrolyte serves to conduct ions between the positive electrode plate and the negative electrode plate. The separator is interposed between the positive electrode plate and the negative electrode plate, and serves mainly to prevent short-circuiting between the positive and negative electrodes and allows the passage of ions.

[0069] [Positive electrode plate] The positive electrode plate includes a positive electrode current collector and a positive electrode coating layer disposed on at least one surface of the positive electrode current collector, the positive electrode coating layer including a positive electrode active material.

[0070] As an example, the positive electrode current collector has two opposing surfaces in the thickness direction of the positive electrode current collector, and the positive electrode coating layer is provided on any one or two of the two opposing surfaces of the positive electrode current collector.

[0071] The positive electrode current collector may be a metal foil sheet or a composite current collector. For example, an aluminum foil may be used as the metal foil sheet. The composite current collector may include a polymeric material substrate and a metal layer formed on at least one surface of the polymeric material substrate. The composite current collector may be formed by forming a metal material (such as aluminum, aluminum alloy, nickel, nickel alloy, titanium, titanium alloy, silver, and silver alloy) on a polymeric material substrate (such as a substrate of polypropylene (PP), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polystyrene (PS), polyethylene (PE), etc.).

[0072] The positive electrode active material may be a positive electrode active material for batteries known in the art. As an example, the positive electrode active material may include a lithium-containing phosphate having an olivine structure, which can extend the cycle life of the battery. The positive electrode active material may further include a lithium transition metal oxide and a modified compound thereof. However, the present application is not limited to these materials, and other conventional materials used as positive electrode active materials for batteries may be used. These positive electrode active materials may be used alone or in combination of two or more. Examples of lithium-containing phosphates having an olivine structure may include at least one of lithium iron phosphate (e.g., LiFePO4 (which may be referred to as LFP)), a composite of lithium iron phosphate and carbon, lithium manganese phosphate (e.g., LiMnPO4), a composite of lithium manganese phosphate and carbon, lithium manganese iron phosphate, and a composite of lithium manganese iron phosphate and carbon, but are not limited thereto. Examples of lithium transition metal oxides include lithium cobalt oxide (e.g., LiCoO2), lithium nickel oxide (e.g., LiNiO2), lithium manganese oxide (e.g., LiMnO2, LiMn2O4), lithium nickel cobalt oxide, lithium manganese cobalt oxide, lithium nickel manganese oxide, and lithium nickel cobalt manganese oxide (e.g., LiNi 1 / 3 Co 1 / 3 Mn 1 / 3 O2(NCM 333 (may also be referred to as LiNi 0.5 Co 0.2 Mn 0.3 O2(NCM 523 (may also be referred to as LiNi 0.5 Co 0.25 Mn 0.25 O2(NCM 211 (may also be referred to as LiNi 0.6 Co 0.2 Mn 0.2 O2(NCM 622 (may also be referred to as LiNi 0.8 Co 0.1 Mn 0.1 O2(NCM 811 Lithium nickel cobalt aluminum oxide (e.g., LiNi0.85 Co 0.15 Al 0.05 O2) and modified compounds thereof, but are not limited thereto.

[0073] The positive electrode coating layer preferably further includes an adhesive. For example, the adhesive may include at least one of polyvinylidene fluoride (PVDF), polytetrafluoroethylene (PTFE), vinylidene fluoride-tetrafluoroethylene-propylene terpolymer, vinylidene fluoride-hexafluoropropylene-tetrafluoroethylene terpolymer, tetrafluoroethylene-hexafluoropropylene copolymer, and fluorine-containing acrylic resin.

[0074] The positive electrode coating layer preferably further includes a conductive agent. For example, the conductive agent may include at least one of superconducting carbon, acetylene black, carbon black, ketjen black, carbon dots, carbon nanotubes, graphene, and carbon nanofibers.

[0075] In some embodiments, the thickness of the positive electrode coating layer on one side is 0.08 mm or more, preferably 0.09 mm to 0.3 mm.

[0076] In some embodiments, the positive electrode plate may be manufactured by dispersing the above-mentioned components for manufacturing a positive electrode plate, such as a positive electrode active material, a conductive agent, an adhesive, and any other components, in a solvent (e.g., N-methylpyrrolidone) to form a positive electrode slurry, applying the positive electrode slurry to a positive electrode current collector, and performing steps such as drying and cold pressing to obtain a positive electrode plate.

[0077] [Negative electrode plate] The negative electrode plate includes a negative electrode current collector and a negative electrode coating layer disposed on at least one surface of the negative electrode current collector, the negative electrode coating layer including a negative electrode active material.

[0078] As an example, the negative electrode current collector has two surfaces opposing each other in the thickness direction of the negative electrode current collector, and the negative electrode coating layer is provided on any one or two of the two opposing surfaces of the negative electrode current collector.

[0079] The negative electrode current collector may be a metal foil sheet or a composite current collector. For example, the metal foil sheet may be a copper foil. The composite current collector may include a polymeric material substrate and a metal layer formed on at least one surface of the polymeric material substrate. The composite current collector may be formed by forming a metal material (such as copper, copper alloy, nickel, nickel alloy, titanium, titanium alloy, silver, and silver alloy) on a polymeric material substrate (such as a substrate of polypropylene (PP), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polystyrene (PS), polyethylene (PE), etc.).

[0080] The negative electrode active material may be a negative electrode active material for batteries known in the art. As an example, the negative electrode active material may include at least one of artificial graphite, natural graphite, soft carbon, hard carbon, silicon material, tin material, and lithium titanate. The silicon material may be at least one selected from silicon alone, silicon oxygen compound, silicon carbon composite, silicon nitrogen composite, and silicon alloy. The tin material may be at least one selected from tin alone, tin oxygen compound, and tin alloy. However, the present application is not limited to these materials, and other conventional materials used as negative electrode active materials for batteries may be used. These negative electrode active materials may be used alone or in combination of two or more.

[0081] The negative electrode coating layer preferably further includes an adhesive, which may be at least one selected from styrene butadiene rubber (SBR), polyacrylic acid (PAA), sodium polyacrylate (PAAS), polyacrylamide (PAM), polyvinyl alcohol (PVA), sodium alginate (SA), polymethyl methacrylate (PMAA), and carboxymethyl chitosan (CMCS).

[0082] The negative electrode coating layer preferably further includes a conductive agent, which may be at least one selected from the group consisting of superconducting carbon, acetylene black, carbon black, ketjen black, carbon dots, carbon nanotubes, graphene, and carbon nanofibers.

[0083] The negative electrode coating layer preferably further contains other auxiliary agents such as a thickener (eg, sodium carboxymethylcellulose (CMC-Na)).

[0084] In some embodiments, the negative electrode plate may be manufactured by dispersing the above-mentioned components for manufacturing a negative electrode plate, such as a negative electrode active material, a conductive agent, an adhesive, and any other components, in a solvent (e.g., deionized water) to form a negative electrode slurry, applying the negative electrode slurry to a negative electrode current collector, and performing processes such as drying and cold pressing to obtain a negative electrode plate.

[0085] [Electrolyte] The electrolyte serves to conduct ions between the positive electrode plate and the negative electrode plate. The electrolyte used is one described in the "Electrolyte" section above.

[0086] [Separator] In some embodiments, the secondary battery further includes a separator. The present application does not particularly limit the type of separator, and any known separator having a porous structure with excellent chemical stability and mechanical stability can be selected.

[0087] In some embodiments, the material of the separator may be at least one selected from glass fiber, nonwoven fabric, polyethylene, polypropylene, and polyvinylidene fluoride. The separator may be a single-layer thin film or a multi-layer composite thin film, and is not particularly limited. When the separator is a multi-layer composite thin film, the materials of each layer may be the same or different, and is not particularly limited.

[0088] [Secondary battery] In some embodiments, the positive and negative plates and the separator can be formed into an electrode assembly by a winding or stacking process.

[0089] In some embodiments, the secondary battery may include an exterior body that can be used to hermetically package the electrode assembly and the electrolyte.

[0090] In some embodiments, the exterior of the secondary battery may be a hard case, such as a hard plastic case, an aluminum case, a steel case, etc. The exterior of the secondary battery may be a soft pack, such as a pouch soft pack, etc. The material of the soft pack may be plastic, and examples of the plastic include polypropylene, polybutylene terephthalate, and polybutylene succinate.

[0091] The present application does not particularly limit the shape of the secondary battery, which may be cylindrical, rectangular, or any other shape. For example, FIG. 1 shows a secondary battery 5 having a rectangular structure as an example.

[0092] In some embodiments, referring to FIG. 2, the exterior body may include a housing 51 and a cover plate 53. The housing 51 may include a bottom plate and a side plate connected to the bottom plate, and the bottom plate and the side plate define a receiving cavity. The housing 51 has an opening communicating with the receiving cavity, and the cover plate 53 can cover the opening to seal the receiving cavity. The positive electrode plate, the negative electrode plate and the separator can form an electrode assembly 52 by a winding process or a stacking process. The electrode assembly 52 is packaged in the receiving cavity. The electrolyte is impregnated into the electrode assembly 52. ​​The number of electrode assemblies 52 included in the secondary battery 5 may be one or more, and may be selected by those skilled in the art according to specific practical needs.

[0093] In some embodiments, the secondary batteries may be assembled into a battery module, and the number of secondary batteries included in the battery module may be one or more, with the specific number being selectable by those skilled in the art according to the application and capacity of the battery module.

[0094] Fig. 3 shows an example of a battery module 4. Referring to Fig. 3, in the battery module 4, the multiple secondary batteries 5 may be arranged in order along the length direction of the battery module 4. Of course, they may be arranged in any other manner. Furthermore, the multiple secondary batteries 5 may be fixed by a fastener.

[0095] Preferably, the battery module 4 may further include a casing having an accommodation space, and the multiple secondary batteries 5 are accommodated in the accommodation space.

[0096] In some embodiments, the battery modules may be further assembled into a battery pack, and the number of battery modules included in the battery pack may be one or more, and the specific number can be selected by those skilled in the art according to the application and capacity of the battery pack.

[0097] 4 and 5 show an example of a battery pack 1. Referring to Fig. 4 and Fig. 5, the battery pack 1 may include a battery housing and a plurality of battery modules 4 installed in the battery housing. The battery housing may include an upper housing 2 and a lower housing 3, and the upper housing 2 may be covered by the lower housing 3 to form an enclosed space for accommodating the battery modules 4. The plurality of battery modules 4 may be arranged in the battery housing in any manner.

[0098] In some embodiments, the secondary battery of the present application has a density of 1 g / 1000 m 2 ≦L≦5g / 1000m 2 and preferably 1g / 1000m 2 ≦L≦4g / 1000m 2 More preferably, it satisfies 1.5g / 1000m 2 ≦L≦4g / 1000m 2 More preferably, it satisfies 1.5g / 1000m 2More than 3.5g / 1000m 2 L=M1 / [M2×B×(a+c)]*1000. M1 is the mass of the compound of formula II in g, M2 is the mass of the positive electrode active material in g, and B is the specific surface area of ​​the positive electrode active material in m 2 / g, a is the mass ratio of the compound of formula I in the solvent, and c is the molar ratio of the compound of formula III in the electrolyte salt. By setting L in the above range, the kinetic performance, high temperature performance, and overcharge prevention performance of the battery can be further improved.

[0099] In some embodiments, 8 m 2 / g≦B≦16m 2 / g, preferably 10m 2 / g≦B≦14m 2 / g. If the specific surface area of ​​the positive electrode active material is too large, side reactions increase, affecting battery performance. If the specific surface area of ​​the positive electrode active material is too small, the transport of lithium ions inside the particles is hindered, affecting battery performance. By setting the specific surface area of ​​the positive electrode active material within the above range, solid-phase diffusion inside the positive electrode plate can be improved, contributing to improved dynamic performance of the cell.

[0100] power consumption equipment A third aspect of the present application provides a power consuming device including the above-mentioned secondary battery. The power consuming device of the present application includes the above-mentioned secondary battery, and therefore has all the beneficial effects of the secondary battery.

[0101] The secondary battery may be used as a power source for the power consuming device, or may be used as an energy storage unit for the power consuming device, which may include, but is not limited to, mobile devices (e.g., mobile phones, laptops, etc.), electric vehicles (e.g., pure electric vehicles, hybrid vehicles, plug-in hybrid vehicles, electric bicycles, electric scooters, electric golf carts, electric trucks, etc.), trains, ships and satellites, energy storage systems, etc.

[0102] The power consumption device may be a secondary battery, a battery module or a battery pack according to the needs of its use.

[0103] 6 is an example of a power consuming device, such as a pure electric vehicle, a hybrid vehicle, or a plug-in hybrid vehicle, etc. A battery pack or a battery module may be used to meet the need for high power and high energy density of the secondary battery of the power consuming device.

[0104] Another example of the device may be a mobile phone, a tablet PC, a notebook computer, etc. Such devices usually need to be lightweight and thin, and therefore can use a secondary battery as a power source.

[0105] Working Example The following examples of the present application are described. The examples described below are illustrative and are only for interpreting the present application, and should not be understood as limiting the present application. If no specific techniques or conditions are shown in the examples, they are carried out according to the techniques, conditions or product instructions described in the literature of this field. If no manufacturer is shown, the reagents or equipment used are all ordinary products available on the market.

[0106] Example 1 Positive electrode plate manufacturing Lithium iron phosphate with an olivine structure (LFP), polyvinylidene fluoride (PVDF), and carbon black (SP) were mixed with a solvent in a mass ratio of 97:2.5:0.5, and dispersed uniformly by stirring to obtain a positive electrode slurry. The positive electrode slurry was then uniformly applied to two sides of an aluminum foil, which was then dried, cold pressed, and cut to obtain a positive electrode plate. Lithium iron phosphate with an olivine structure was used as the positive electrode active material, and its specific surface area was 12 m 2 / g, and the thickness of the cold-pressed monolayer membrane plate was 0.1 mm.

[0107] Negative electrode plate manufacturing The negative electrode active material (artificial graphite): carbon black (SP): styrene butadiene rubber (SBR): carboxymethyl fiber (CMC) was mixed with a solvent in a ratio of 97:0.5:1.5:1, and stirred to disperse uniformly to obtain a negative electrode slurry. The negative electrode slurry was uniformly applied to two sides of a copper foil, dried, cold pressed, and cut to obtain a negative electrode plate. The thickness of the cold pressed single-layer film plate was 0.07 mm.

[0108] Separator A polyethylene film was used as a separator.

[0109] Electrolyte production In a glove box under an argon atmosphere, 35% by mass of ethyl acetate, 30% by mass of ethylene carbonate, and 35% by mass of dimethyl carbonate were mixed to obtain an organic solvent mixture, then fluorobenzene was added to the organic solvent mixture so that the mass ratio in the obtained electrolyte was 3%, and then lithium hexafluorophosphate (LiPF6) with a concentration of 1 mol / L was slowly added as an electrolyte salt. Next, the mixture was stirred until completely dissolved to obtain an electrolyte.

[0110] Manufacture of lithium-ion secondary batteries The positive electrode plate, separator, and negative electrode plate were stacked in order, a separator was placed between the positive electrode plate and the negative electrode plate to separate them, and then the stack was wound to obtain an electrode assembly, which was then placed in an outer casing, dried, and injected with an electrolyte, and then formed and left to stand to obtain a secondary battery. The final lithium-ion battery contained 1,400 g of positive electrode active material and 620 g of electrolyte.

[0111] Example 2 In the preparation of the electrolyte solution, 40 mass % of ethyl acetate, 30 mass % of ethylene carbonate, and 30 mass % of dimethyl carbonate were mixed to obtain an organic solvent mixture. The rest was the same as in Example 1.

[0112] Example 3 In the preparation of the electrolyte solution, 50% by mass of ethyl acetate, 30% by mass of ethylene carbonate, and 20% by mass of dimethyl carbonate were mixed to obtain an organic solvent mixture.

[0113] Example 4 In the preparation of the electrolyte solution, 60 mass % of ethyl acetate, 30 mass % of ethylene carbonate, and 10 mass % of dimethyl carbonate were mixed to obtain an organic solvent mixture. The rest was the same as in Example 1.

[0114] Example 5 In the preparation of the electrolyte solution, 70% by mass of ethyl acetate and 30% by mass of ethylene carbonate were mixed to obtain an organic solvent mixture.

[0115] Example 6 In the preparation of the electrolyte solution, 80% by mass of ethyl acetate and 20% by mass of ethylene carbonate were mixed to obtain an organic solvent mixture. The rest was the same as in Example 1.

[0116] Example 7 In the preparation of the electrolyte solution, 50% by mass of methyl formate, 30% by mass of ethylene carbonate, and 20% by mass of dimethyl carbonate were mixed to obtain an organic solvent mixture.

[0117] Example 8 In the preparation of the electrolyte solution, 50% by mass of methyl acetate, 30% by mass of ethylene carbonate, and 20% by mass of dimethyl carbonate were mixed to obtain an organic solvent mixture.

[0118] Example 9 In the preparation of the electrolyte solution, 50% by mass of propyl acetate, 30% by mass of ethylene carbonate, and 20% by mass of dimethyl carbonate were mixed to obtain an organic solvent mixture.

[0119] Example 10 In the preparation of the electrolyte solution, 50% by mass of methyl acrylate, 30% by mass of ethylene carbonate, and 20% by mass of dimethyl carbonate were mixed to obtain an organic solvent mixture. The rest was the same as in Example 1.

[0120] Example 11 In the preparation of the electrolyte solution, 50% by mass of ethyl acrylate, 30% by mass of ethylene carbonate, and 20% by mass of dimethyl carbonate were mixed to obtain an organic solvent mixture. The rest was the same as in Example 1.

[0121] Example 12 In the preparation of the electrolyte solution, fluorobenzene was added to the organic solvent mixture so that the mass ratio of the resulting electrolyte solution was 1%. Other than that, the procedure was the same as in Example 3.

[0122] Example 13 In the preparation of the electrolyte solution, fluorobenzene was added to the organic solvent mixture so that the mass ratio of the resulting electrolyte solution was 2%. Other than that, the procedure was the same as in Example 3.

[0123] Example 14 In the preparation of the electrolyte solution, fluorobenzene was added to the organic solvent mixture so that the mass ratio of the resulting electrolyte solution was 4%. Other than that, the procedure was the same as in Example 3.

[0124] Example 15 In the preparation of the electrolyte solution, fluorobenzene was added to the organic solvent mixture so that the mass ratio of the resulting electrolyte solution was 5%. Other than that, the procedure was the same as in Example 3.

[0125] Example 16 In the preparation of the electrolyte solution, fluorobenzene was added to the organic solvent mixture so that the mass ratio of the resulting electrolyte solution was 9%. Other than that, the procedure was the same as in Example 3.

[0126] Example 17 In the preparation of the electrolyte solution, biphenyl was added to the organic solvent mixture so that the mass ratio of the resulting electrolyte solution was 3%. Other than that, the procedure was the same as in Example 3.

[0127] Example 18 In the preparation of the electrolyte solution, cyclohexylbenzene was added to the organic solvent mixture so that the mass ratio of the resulting electrolyte solution was 3%. Other than that, the procedure was the same as in Example 3.

[0128] Example 19 In the preparation of the electrolyte, lithium hexafluorophosphate (LiPF6) with a concentration of 0.5 mol / L and lithium bisfluorosulfonyl imide with a concentration of 0.5 mol / L were slowly added as electrolyte salts, and the molar ratios of lithium hexafluorophosphate (LiPF6) and lithium bisfluorosulfonyl imide in the electrolyte salts were 50% each.Other than that, the same as in Example 3.

[0129] Example 20 In the preparation of the electrolyte, lithium hexafluorophosphate (LiPF6) with a concentration of 0.5 mol / L and lithium bis(trifluoromethanesulfonyl)imide with a concentration of 0.5 mol / L were slowly added as electrolyte salts, and the molar ratios of lithium hexafluorophosphate (LiPF6) and lithium bis(trifluoromethanesulfonyl)imide in the electrolyte salts were 50%, respectively.Other than that, the same as in Example 3.

[0130] Example 21 In producing the electrolyte solution, fluorobenzene was added to the organic solvent mixture so that the mass ratio in the obtained electrolyte solution was 3%, and vinylene carbonate was added so that the mass ratio in the obtained electrolyte solution was 2%, and the rest was the same as in Example 19.

[0131] Example 22 In the preparation of the electrolyte solution, fluorobenzene was added to the organic solvent mixture so that the mass ratio in the obtained electrolyte solution was 3%, and fluoroethylene carbonate was added so that the mass ratio in the obtained electrolyte solution was 1%, and the rest was the same as in Example 19.

[0132] Example 23 In the preparation of the electrolyte solution, fluorobenzene was added to the organic solvent mixture so that the mass ratio of the resulting electrolyte solution was 3%, and ethylene sulfate was added to the organic solvent mixture so that the mass ratio of the resulting electrolyte solution was 1%, and the rest was the same as in Example 19.

[0133] Comparative Example 1 In the preparation of the electrolyte solution, 30% by mass of ethyl acetate, 30% by mass of ethylene carbonate, and 40% by mass of dimethyl carbonate were mixed to obtain an organic solvent mixture.

[0134] Comparative Example 2 In the preparation of the electrolyte solution, 30% by mass of ethylene carbonate and 70% by mass of dimethyl carbonate were mixed to obtain an organic solvent mixture. The rest was the same as in Example 1.

[0135] Comparative Example 3 In the preparation of the electrolyte, fluorobenzene was not added, and the rest was the same as in Example 3.

[0136] The relevant parameters for the above Examples 1 to 23 and Comparative Examples 1 to 3 are shown in Table 1 below.

[0137] [Table 1A] [Table 1B] [Table 1C] [Table 1D] [Table 1E] [Table 1F]

[0138] Note: In Table 1, The content of each solvent is the mass ratio of each solvent to the total solvent mass. The content of each additive is the mass ratio of each additive in the electrolyte, a is the mass ratio of the solvent of the compound of formula I in the total solvent mass; b is the mass ratio of the additive of the compound of formula II in the electrolyte; L=M1 / [M2×B×(a+c)]*1000 (wherein M1 is the mass of the additive of the compound of formula II in g, M2 is the mass of the positive electrode active material in g, and B is the specific surface area of ​​the positive electrode active material in m 2 / g, a has the same meaning as above, and c is the molar ratio of the compound of formula III in the electrolyte salt).

[0139] The test method is as follows.

[0140] (1) Initial DCR (Direct Current Resistance) At room temperature, the batteries of each embodiment and comparative example were charged to 3.65V at a constant current of 0.5C, then charged at a constant voltage so that the current was 0.05C, and the batteries were discharged at a constant current of 0.5C for 30 minutes to adjust the batteries to 50% SOC, with the battery voltage at this time being U1, and the batteries were discharged at a constant current of 4C for 30 seconds, with the collected points every 0.1 seconds being used to obtain the end-of-discharge voltage U2. The initial DCR of the battery was expressed as the discharge DCR at 50% SOC of the battery, and the initial DCR of the battery was expressed as (U1-U2) / 4C.

[0141] (2) High-temperature cycle performance of the battery At 45°C, the batteries of each Example and Comparative Example are charged to 3.65V at a constant current of 1.0C, then charged at a constant voltage to a current of 0.05C, the batteries are left to stand for 5 minutes, and discharged to 2.5V at a constant current of 1.0C. This is the first charge / discharge cycle of the battery, and the discharge capacity at this time is the discharge capacity of the first cycle of the battery. Using the above method, the battery is subjected to 100 charge / discharge cycles, and the discharge capacity of the battery after 100 cycles is recorded. The capacity retention rate (%) of the battery after 100 cycles at 45°C = (discharge capacity of the battery after 100 cycles / discharge capacity of the battery in the first cycle) x 100%.

[0142] (3) Battery overcharge prevention function At 25°C, the batteries of each embodiment and comparative example are charged to 3.65V at a constant current and voltage of 1C, with a cutoff current of 0.05C. When the battery is fully charged, it is charged at a constant current of 1C until the voltage reaches 6V, and observed for 1 hour to check whether the battery ignites and explodes. If there is no ignition or explosion and only smoke, it indicates that the test has been passed. If there is ignition or explosion, it indicates that the test has not been passed, and the above operation is repeated 30 times, and the number of times the test has been passed (number of overcharge passes) is recorded.

[0143] As can be seen from the above results, all of Examples 1 to 23 have good kinetic performance, high temperature performance, and excellent overcharge prevention performance of the battery, and can achieve good effects.

[0144] In contrast, in Comparative Example 1, the content of the compound of formula I was not within the range of the present application, so the desired effect was not obtained. In particular, the initial DCR increased to 3.6. In Comparative Example 2, the compound of formula I was not added, so the desired effect was not obtained. In particular, the initial DCR increased significantly to 6.0, and the dynamics of the battery were significantly lowered. In Comparative Example 3, the compound of formula II was not added, so the promising effect was not obtained. In particular, the overcharge prevention performance was significantly lowered. As can be seen from the above, by combining a specific amount of the compound of formula I and the compound of formula II, it is possible to consider good dynamics performance, high temperature performance, and excellent overcharge prevention performance of the battery.

[0145] It should be noted that the present application is not limited to the above-mentioned embodiment. The above-mentioned embodiment is merely an example, and any embodiment having substantially the same configuration as the technical idea and exhibiting the same effect within the scope of the technical proposal of the present application is included in the technical scope of the present application. In addition, various modifications that a person skilled in the art can make to the embodiment without departing from the gist of the present application, and other forms combining some of the components in the embodiment are also included in the scope of the present application. [Explanation of symbols]

[0146] 1: Battery pack 2: Upper case 3: Lower case 4: Battery module 5: Secondary battery 51: Housing 52: Electrode assembly 53: Top cover assembly

Claims

1. Contains solvents and additives, the solvent comprises a compound of formula I, and the mass ratio of the compound of formula I in the solvent is 35% or more; The additive comprises a compound of Formula II. 【Chemistry 1】 (In the formula, R １ , R ２ are each independently any one selected from a hydrogen atom, a C1-C3 linear alkyl group, and a C2-C3 alkenyl group. 【Chemistry 2】 (In the formula, R ３ , R ４ , R ５ are each independently any one selected from a hydrogen atom, a fluorine atom, a phenyl group, a cyano group, a C1-C6 linear alkyl group, a C3-C6 cyclic alkyl group, and a C2-C6 alkenyl group.

2. 2. The electrolyte according to claim 1, wherein the mass ratio of the compound of formula I in the solvent is 40% to 70%.

3. 3. The electrolyte according to claim 1, wherein the mass ratio of the compound of formula II in the electrolyte is less than or equal to 9%, preferably between 3% and 5%.

4. The electrolyte solution according to any one of claims 1 to 3, wherein the compound of formula I comprises at least one selected from methyl formate, methyl acetate, ethyl acetate, propyl acetate, methyl acrylate and ethyl acrylate.

5. The electrolyte according to any one of claims 1 to 4, wherein the compound of formula II comprises at least one of biphenyl, fluorobenzene, and cyclohexylbenzene.

6. The electrolyte solution satisfies a / b≧11, preferably 11≦a / b≦35, wherein a is the mass ratio of the compound of formula I in the solvent, and b is the mass ratio of the compound of formula II in the electrolyte solution. The electrolyte solution according to any one of claims 1 to 5.

7. 2. The electrolyte solution according to claim 1, wherein the electrolyte salt comprises an electrolyte salt, the electrolyte salt comprises a compound of formula III, and preferably, a molar ratio of the compound of formula III in the electrolyte salt is 10% or more. 【Chemistry 3】 (In the formula, R ６ , R ７ are each independently an F atom or a fluoroalkyl group; R ６ , R ７ can also be linked to form a ring.)

8. 8. The electrolyte solution according to claim 7, wherein the compound of formula III comprises at least one selected from lithium bisfluorosulfonylimide and lithium bis(trifluoromethanesulfonyl)imide.

9. The electrolyte solution according to any one of claims 1 to 8, wherein the solvent further contains a carbonate ester, and the mass ratio of the carbonate ester in the solvent is 30% or more, preferably 35% to 65%.

10. 9. The electrolyte solution according to claim 1, wherein the solvent further contains ethylene carbonate, and a mass ratio of the ethylene carbonate in the solvent is 30% or more.

11. The electrolyte solution according to any one of claims 1 to 10, further comprising at least one selected from the group consisting of vinylene carbonate (VC), fluoroethylene carbonate (FEC), ethylene sulfate (DTD), 1,3-propane sultone (PS), lithium difluorobisoxalatophosphate (LiDFOP), lithium difluorooxalatoborate (LiDFOB) and lithium bisoxalatoborate (LiBOB).

12. A secondary battery comprising the electrolyte solution according to any one of claims 1 to 11.

13. The secondary battery according to claim 12 , wherein the secondary battery comprises a positive electrode plate, the positive electrode plate comprises a positive electrode coating layer, the positive electrode coating layer comprises a positive electrode active material, and the positive electrode active material comprises a lithium-containing phosphate having an olivine structure.

14. The secondary battery has a thickness of 1 g / 1000 m ２ ≦L≦5g / 1000m ２ and preferably 1.5 g / 1000 m ２ ≦L≦4g / 1000m ２ The secondary battery according to claim 13 , which satisfies the above. L=M1 / [M2×B×(a+c)]*1000 (M1 is the mass of the compound of formula II in g; M2 is the mass of the positive electrode active material, in g; B is the specific surface area of ​​the positive electrode active material, with the unit m ２ / g, a is the mass ratio of the compound of formula I in the solvent; c is the molar ratio of the compound of formula III in the electrolyte salt.

15. 8m ２ / g≦B≦16m ２ / g, preferably 10m ２ / g≦B≦14m ２ The secondary battery according to claim 14, wherein the molecular weight is 1 / g.

16. The secondary battery according to any one of claims 14 to 15, wherein the thickness of the positive electrode coating layer on one side is 0.08 mm or more, preferably 0.09 mm to 0.3 mm.

17. A power consuming device comprising the secondary battery according to any one of claims 12 to 16.