Trisamide compounds and compositions comprising the same

Abstract

To provide clarifying agents that can both produce desirably low haze levels in polyolefin polymers and exhibit minimal extraction from the polyolefin polymer to which they are added, and to provide polymer compositions that incorporate such clarifying agents and exhibit the desired combination of low haze and minimal extraction of the clarifying agent.SOLUTION: There is provided a polymer composition comprising a trimesic acid derivative, which is a trisamide compound formally derived from trimesic acid (i.e., benzene-1,3,5-tricarboxylic acid). The trimesic acid derivative is specifically N,N,N-tri(cis-4-methylcyclohexyl)-1,3,5-benzenetricarboxamide, N,N,N-tri(cis-4-n-propylcyclohexyl)-1,3,5-benzenetricarboxamide, or the like.SELECTED DRAWING: None

Description

TECHNICAL FIELD OF THEINVENTION

[0001]

[0001] This application relates to trisamide compounds (specifically, trisamide derivatives formally derived from trimesic acid [i.e., benzene-1,3,5-tricarboxylic acid]) and compositions containing trisamide compounds. FIELD OF THEINVENTION The present application relates to trisamide compounds (specifically, trisamide derivatives formally derived from trimesic acid [i.e., benzene-1,3,5-tricarboxylic acid]) and compositions containing trisamide compounds.

[0002]

[0002] Polymer resins are widely used in various fields due to, among other things, their excellent processability, mechanical properties (especially on a relative weight basis) and electrical properties. Although the polymer itself may have beneficial properties, additives may be used to further enhance the properties of the polymer and / or to mitigate its disadvantages.

[0003] Polyolefins are a particularly versatile group of polymer resins. Polyolefins are semicrystalline polymers. Polyolefins cooled relatively slowly (such as occurs during the manufacture of molded plastic parts) contain amorphous regions in which the polymer chains are randomly arranged and crystalline regions in which the polymer chains are ordered. Within these crystalline regions of polyolefins, the polymer chains are aligned in domains commonly referred to as "crystalline lamellae." Under normal processing conditions, as polyolefin polymers cool from the molten state, the crystalline lamellae grow radially in all directions. This radial growth results in the formation of spherulites, which are spherical semicrystalline regions composed of multiple crystalline lamellae interrupted by amorphous regions. The size of the spherulites is influenced by several parameters and can range from hundreds of nanometers to several millimeters in diameter. If the spherulite size is significantly larger than the wavelength of visible light, the spherulites scatter the visible light passing through the polymer. This scattering of visible light results in a cloudy appearance commonly referred to as "polymer haze" or simply "haze." While in some applications a significant level of polymer haze may be acceptable, there are certain applications (e.g., storage containers) where the consumer desires a relatively clear plastic and accordingly requires a low haze level.

[0004] Over the years, several approaches have been developed to reduce haze in polyolefins. One approach that has met with much commercial success involves the use of clarifying agents. Clarifying agents are additives, often organic compounds, that when melt processed with a polymer, nucleate the crystallization of the cooling polymer, reducing spherulite size or even substantially preventing the formation of these effective light scatterers. For example, bis(3,4-dimethylbenzylidene) sorbitol has met with much commercial success due to its ability to reduce haze in polypropylene polymers. However, bis(3,4-dimethylbenzylidene) sorbitol has not been without its limitations. In particular, clarifying agents are unable to reduce haze in polypropylene polymers to levels comparable to those of more transparent polymers, such as polystyrene and acrylics. The residual haze of polymers clarified with bis(3,4-dimethylbenzylidene) sorbitol limits the applications and end uses of those polymers.

[0005]

[0005] To address the limitations of sorbitol acetals (e.g., bis(3,4-dimethylbenzylidene)sorbitol), other clarifying agents have been developed. For example, trisamide compounds (e.g., trisamide derivatives formally derived from 1,3,5-benzenetriamine, 3,5-diaminobenzoic acid, 5-aminoisophthalic acid, or trimesic acid) initially showed promise due to the fact that relatively low loadings of such compounds could produce haze levels in polypropylene polymers comparable to those achieved by bis(3,4-dimethylbenzylidene)sorbitol. Despite their initial promise, the disclosed trisamide compounds still fail to produce haze levels comparable to those of more transparent polymers. Furthermore, many of the disclosed trisamide compounds can be extracted from the polypropylene to which they are added. These undesirable levels of extraction make such trisamide compounds less suitable for use in food contact and medical applications (i.e., applications in which the polymer clarified with the trisamide compounds comes into contact with food [e.g., food storage or packaging] or is used in medical devices [e.g., syringes]) where industry preferences and / or regulatory requirements call for additives that exhibit minimal extraction from the polymer.

[0006]

[0006] Thus, there is a need for clarifying agents that can both produce desirably low haze levels in polyolefin polymers and exhibit minimal extraction from the polyolefin polymers to which they are added. There is also a need for polymer compositions incorporating such clarifying agents that exhibit the desired combination of low haze and minimal extraction of the clarifying agent. The various embodiments described herein seek to provide such clarifying agents and compositions. BRIEF SUMMARY OF THE DISCLOSURE

[0007] In a first aspect, the present invention provides a compound of formula (I):

[0008] [ka]

[0009] [In the formula, R 1 , R 2 , and R 3 is independently selected from the group consisting of alkyl groups.

[0010] In a second aspect, the present invention provides a polymer composition comprising the composition described above (i.e., a composition comprising one or more trimesic acid derivatives of formula (I)) and a polyolefin polymer.

[0011] In a first aspect, the present invention provides a trimesic acid derivative of formula (I), which is a trisamide compound formally derived from trimesic acid (i.e., benzene-1,3,5-tricarboxylic acid), the structure of which is as follows:

[0012] [ka]

[0013] In formula (I), R 1 , R 2 , and R 3 The groups are independently selected from the group consisting of alkyl groups.

[0014]

[0010] R 1 , R 2 , and R 3 The group can be any suitable alkyl group. In a preferred embodiment, R 1 , R 2 , and R 3 is C1~C 20 Alkyl groups (e.g., C3-C 20 alkyl group), more preferably C1 to C 12 Alkyl groups (e.g., C3-C 12More preferably, R is independently selected from the group consisting of C1-C8 alkyl groups (e.g., C3-C8 alkyl groups), even more preferably C1-C5 alkyl groups (e.g., C2-C5 alkyl groups or C3-C5 alkyl groups). Suitable alkyl groups can be either linear or branched. In a preferred embodiment, R 1 , R 2 , and R 3 In another preferred embodiment, at least one of R 1 , R 2 , and R 3 In yet another preferred embodiment, at least two of R 1 , R 2 , and R 3 are each independently selected from branched alkyl groups. In those embodiments containing branched alkyl groups, the alkyl groups can contain any suitable number of carbon atoms, with preferred examples being C3-C 20 Branched alkyl groups, C3-C 12 branched alkyl groups, C3-C8 branched alkyl groups, and C3-C5 branched alkyl groups. Suitable branched alkyl groups preferably contain a branch point located at the alpha or beta carbon relative to the cyclohexanediyl moiety.

[0015] In a preferred embodiment, R 1 , R 2 , and R 3is independently selected from the group consisting of n-propyl, isopropyl, n-butyl, sec-butyl (i.e., butan-2-yl or 1-methylpropyl), isobutyl (i.e., 2-methylpropyl), tert-butyl (i.e., 1,1-dimethylethyl), n-pentyl, tert-pentyl (i.e., 2-methylbutan-2-yl or 1,1-dimethylpropyl), neopentyl (i.e., 2,2-dimethylpropyl), isopentyl (i.e., 3-methylbutyl), sec-pentyl (i.e., pentan-2-yl or 1-methylbutyl), sec-isopentyl (i.e., 3-methylbutan-2-yl or 1,2-dimethylpropyl), pentan-3-yl (i.e., 1-ethylpropyl), and 2-methylbutyl. In a more preferred embodiment, R 1 , R 2 , and R 3 is independently selected from the group consisting of n-propyl, isopropyl, n-butyl, sec-butyl (i.e., butan-2-yl or 1-methylpropyl), isobutyl (i.e., 2-methylpropyl), tert-butyl (i.e., 1,1-dimethylethyl), tert-pentyl (i.e., 2-methylbutan-2-yl or 1,1-dimethylpropyl), sec-pentyl (i.e., pentan-2-yl or 1-methylbutyl), sec-isopentyl (i.e., 3-methylbutan-2-yl or 1,2-dimethylpropyl), and pentan-3-yl (i.e., 1-ethylpropyl). 1 , R 2 , and R 3 is independently selected from the group consisting of n-propyl, isopropyl, n-butyl, isobutyl (i.e., 2-methylpropyl), tert-butyl (i.e., 1,1-dimethylethyl), and tert-pentyl (i.e., 2-methylbutan-2-yl or 1,1-dimethylpropyl).

[0016] As mentioned above, R 1 , R 2 and R 3At least one of R is preferably a branched alkyl group. 1 , R 2 and R 3 At least one of R is selected from the group consisting of isopropyl, sec-butyl (i.e., butan-2-yl or 1-methylpropyl), isobutyl (i.e., 2-methylpropyl), tert-butyl (i.e., 1,1-dimethylethyl), tert-pentyl (i.e., 2-methylbutan-2-yl or 1,1-dimethylpropyl), neopentyl (i.e., 2,2-dimethylpropyl), isopentyl (i.e., 3-methylbutyl), sec-pentyl (i.e., pentan-2-yl or 1-methylbutyl), sec-isopentyl (i.e., 3-methylbutan-2-yl or 1,2-dimethylpropyl), pentan-3-yl (i.e., 1-ethylpropyl), and 2-methylbutyl. In another preferred embodiment, R 1 , R 2 and R 3 At least one of R is selected from the group consisting of isopropyl, sec-butyl (i.e., butan-2-yl or 1-methylpropyl), isobutyl (i.e., 2-methylpropyl), tert-butyl (i.e., 1,1-dimethylethyl), tert-pentyl (i.e., 2-methylbutan-2-yl or 1,1-dimethylpropyl), sec-pentyl (i.e., pentan-2-yl or 1-methylbutyl), sec-isopentyl (i.e., 3-methylbutan-2-yl or 1,2-dimethylpropyl), and pentan-3-yl (i.e., 1-ethylpropyl). 1 , R 2 and R 3 In yet another preferred embodiment, at least one of R is selected from the group consisting of isopropyl, isobutyl (i.e., 2-methylpropyl), tert-butyl (i.e., 1,1-dimethylethyl), and tert-pentyl (i.e., 2-methylbutan-2-yl or 1,1-dimethylpropyl). 1 , R 2 , and R3 In another preferred embodiment, at least one of R is selected from the group consisting of tert-butyl (i.e., 1,1-dimethylethyl) and tert-pentyl (i.e., 2-methylbutan-2-yl or 1,1-dimethylpropyl). 1 , R 2 , and R 3 At least two of R are branched alkyl groups independently selected from one of the groups defined in this section. 1 , R 2 and R 3 Each of is a branched alkyl group independently selected from one of the groups described in this paragraph.

[0017] In a preferred embodiment, the composition comprises: (i) N,N,N-tri(4-methylcyclohexyl)-1,3,5-benzenetricarboxamide; (ii) N,N,N-tri(4-n-propylcyclohexyl)-1,3,5-benzenetricarboxamide; (iii) N,N,N-tri(4-isopropylcyclohexyl)-1,3,5-benzenetricarboxamide; (iv) N,N,N-tri(4-n-butylcyclohexyl)-1,3,5-benzenetricarboxamide; (v) N,N,N-tri(4-isobutylcyclohexyl)-1,3,5-benzenetricarboxamide; (vi) N,N,N-tri(4-tert-butylcyclohexyl)-1,3,5-benzenetricarboxamide; (vii) N,N,N-tri(4-tert-pentylcyclohexyl)-1,3,5-benzenetricarboxamide; and (viii) Trimesic acid derivatives selected from the group consisting of mixtures thereof (i.e., mixtures of two or more of any of the foregoing compounds).

[0018] In a preferred embodiment, the composition comprises N,N,N-tri(4-methylcyclohexyl)-1,3,5-benzenetricarboxamide. In another preferred embodiment, the composition comprises N,N,N-tri(4-n-propylcyclohexyl)-1,3,5-benzenetricarboxamide. In yet another preferred embodiment, the composition comprises N,N,N-tri(4-isopropylcyclohexyl)-1,3,5-benzenetricarboxamide. In another preferred embodiment, the composition comprises N,N,N-tri(4-n-butylcyclohexyl)-1,3,5-benzenetricarboxamide. In yet another preferred embodiment, the composition comprises N,N,N-tri(4-isobutylcyclohexyl)-1,3,5-benzenetricarboxamide. In another preferred embodiment, the composition comprises N,N,N-tri(4-tert-butylcyclohexyl)-1,3,5-benzenetricarboxamide. In yet another preferred embodiment, the composition comprises N,N,N-tri(4-tert-pentylcyclohexyl)-1,3,5-benzenetricarboxamide.

[0019] As can be seen in formula (I), each cyclohexanediyl moiety contains non-hydrogen substituents (i.e., R 1 , R 2 , or R 3 The non-hydrogen substituents attached to each cyclohexanediyl moiety can be arranged in two different spatial configurations with respect to each other. Both non-hydrogen substituents can be on the same side of the average plane of the cyclohexane ring, which corresponds to a cis configuration, or both non-hydrogen substituents can be on opposite sides of the average plane of the cyclohexane ring, which corresponds to a trans configuration. R 1 , R 2 , and R 3 Each of the groups may be positioned either cis or trans relative to the non-hydrogen substituent attached to the 1-position of the corresponding cyclohexanediyl moiety (i.e., relative to the bond to the nitrogen atom attached to the cyclohexanediyl moiety). 1 , R 2, and R 3 At least one of the groups is positioned cis to the non-hydrogen substituent attached to the 1-position of the corresponding cyclohexanediyl moiety. 1 , R 2 , and R 3 At least two of the groups are oriented cis to the non-hydrogen substituent attached to the 1-position of the corresponding cyclohexanediyl moiety. 1 , R 2 , and R 3 Each of the groups is positioned cis to the non-hydrogen substituent attached to the 1-position of the corresponding cyclohexanediyl moiety.

[0020] In a preferred embodiment, the composition comprises: (i) N,N,N-tri(cis-4-methylcyclohexyl)-1,3,5-benzenetricarboxamide; (ii) N,N,N-tri(cis-4-n-propylcyclohexyl)-1,3,5-benzenetricarboxamide; (iii) N,N,N-tri(cis-4-isopropylcyclohexyl)-1,3,5-benzenetricarboxamide; (iv) N,N,N-tri(cis-4-n-butylcyclohexyl)-1,3,5-benzenetricarboxamide; (v) N,N,N-tri(cis-4-isobutylcyclohexyl)-1,3,5-benzenetricarboxamide; (vi) N,N,N-tri(cis-4-tert-butylcyclohexyl)-1,3,5-benzenetricarboxamide; (vii) N,N,N-tri(cis-4-tert-pentylcyclohexyl)-1,3,5-benzenetricarboxamide; and (viii) Trimesic acid derivatives selected from the group consisting of mixtures thereof (i.e., mixtures of two or more of any of the foregoing compounds).

[0021] In a preferred embodiment, the composition comprises N,N,N-tri(cis-4-methylcyclohexyl)-1,3,5-benzenetricarboxamide. In another preferred embodiment, the composition comprises N,N,N-tri(cis-4-n-propylcyclohexyl)-1,3,5-benzenetricarboxamide. In yet another preferred embodiment, the composition comprises N,N,N-tri(cis-4-isobutylcyclohexyl)-1,3,5-benzenetricarboxamide. In another preferred embodiment, the composition comprises N,N,N-tri(cis-4-n-butylcyclohexyl)-1,3,5-benzenetricarboxamide. In yet another preferred embodiment, the composition comprises N,N,N-tri(cis-4-isobutylcyclohexyl)-1,3,5-benzenetricarboxamide. In another preferred embodiment, the composition comprises N,N,N-tri(cis-4-tert-butylcyclohexyl)-1,3,5-benzenetricarboxamide. In yet another preferred embodiment, the composition comprises N,N,N-tri(cis-4-tert-pentylcyclohexyl)-1,3,5-benzenetricarboxamide.

[0022] As mentioned above, the present application also encompasses compositions containing one or more trimesic acid derivatives of formula (I), for example, compositions containing a mixture of two or more trimesic acid derivatives of formula (I). (In this context, the cis and trans isomers are considered to be different compounds, and therefore a mixture of two or more isomers constitutes a composition containing a mixture of two or more trimesic acid derivatives of formula (I).) In such an embodiment, the R of all trimesic acid derivatives of formula (I) present in the composition is 1 , R 2 and R 3 It is preferred that 60% or more of the groups are cis to the non-hydrogen substituent bonded to the 1-position of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety). More preferably, the R of all trimesic acid derivatives of formula (I) present in the composition 1 , R 2 , and R 3In another preferred embodiment, at least about 65% of the R groups of all trimesic acid derivatives of formula (I) present in the composition are cis to the non-hydrogen substituent bonded to the 1-position of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety). 1 , R 2 , and R 3 In yet another preferred embodiment, at least about 70% of the R groups of all trimesic acid derivatives of formula (I) present in the composition are cis to the non-hydrogen substituent bonded to the 1-position of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety). 1 , R 2 , and R 3 In another preferred embodiment, at least about 75% of the R groups of all trimesic acid derivatives of formula (I) present in the composition are cis to the non-hydrogen substituent bonded to the 1-position of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety). 1 , R 2 , and R 3 In yet another preferred embodiment, at least about 80% of the R groups are cis to the non-hydrogen substituent bonded to the 1-position of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety). 1 , R 2 , and R 3 In another preferred embodiment, at least about 85% of the R groups of all trimesic acid derivatives of formula (I) present in the composition are cis to the non-hydrogen substituent bonded to the 1-position of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety). 1 , R 2 , and R 3In yet another preferred embodiment, at least about 90% of the R groups of all trimesic acid derivatives of formula (I) present in the composition are cis to the non-hydrogen substituent bonded to the 1-position of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety). 1 , R 2 , and R 3 At least about 95% (e.g., at least about 96%, at least about 97%, at least about 98%, or at least about 99%) of the groups are cis to the non-hydrogen substituent bonded to position 1 of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety).

[0023] In another preferred embodiment of the composition containing a mixture of two or more compounds of formula (I), about 60 mol % or more of the trimesic acid derivatives of formula (I) present in the composition are each cis to the non-hydrogen substituent bonded to the 1-position of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety). 1 , R 2 , and R 3 More preferably, about 65 mol % or more of the trimesic acid derivatives of formula (I) present in the composition have R groups each cis to the non-hydrogen substituent bonded to the 1-position of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety). 1 , R 2 , and R 3 In yet another preferred embodiment, about 70 mol % or more of the trimesic acid derivatives of formula (I) present in the composition have R groups that are each cis to the non-hydrogen substituent bonded to the 1-position of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety). 1 , R 2 , and R 3In yet another preferred embodiment, about 75 mol % or more of the trimesic acid derivatives of formula (I) present in the composition have R groups that are each cis to the non-hydrogen substituent bonded to the 1-position of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety). 1 , R 2 , and R 3 In yet another preferred embodiment, about 80 mol % or more of the trimesic acid derivatives of formula (I) present in the composition have R groups that are each cis to the non-hydrogen substituent bonded to the 1-position of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety). 1 , R 2 , and R 3 In another preferred embodiment, about 85 mol % or more of the trimesic acid derivatives of formula (I) present in the composition have R groups that are each cis to the non-hydrogen substituent bonded to the 1-position of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety). 1 , R 2 , and R 3 In yet another preferred embodiment, about 90 mol % or more of the trimesic acid derivatives of formula (I) present in the composition have R groups that are each cis to the non-hydrogen substituent bonded to the 1-position of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety). 1 , R 2 , and R 3 In another preferred embodiment, about 95 mol % or more (e.g., about 96 mol % or more, about 97 mol % or more, about 98 mol % or more, or about 99 mol % or more) of the trimesic acid derivatives of formula (I) present in the composition have R groups that are each cis to the non-hydrogen substituent bonded to the 1-position of the corresponding cyclohexanediyl moiety (i.e., cis to the bond to the nitrogen atom bonded to the cyclohexanediyl moiety). 1 , R 2 , and R 3 It has a group.

[0024] The trimesic acid derivative of formula (I) can be prepared using any suitable method or synthetic process. For example, the compound can be prepared by reacting the desired 4-alkylcyclohexylamine with 1,3,5-benzenetricarbonyl trichloride (i.e., the acid chloride of trimesic acid) to produce the trimesic acid derivative of formula (I).

[0025]

[0019] R 1 , R 2 , and R 3 The trimesic acid derivative of formula (I) having any of the following formula (J) can be prepared by first reacting 5-alkoxycarbonylisophthalic acid (e.g., 5-methoxycarbonylisophthalic acid) with oxalyl chloride to obtain a trimesic acid derivative of formula (I) having any of the following formula (J):

[0026] [ka]

[0027] [In the formula, R 11 is an alkyl group (e.g., a methyl group). The acid chloride compound of formula (J) can then be reacted with the desired 4-alkylcyclohexylamine to produce the following compound of formula (K):

[0028] [ka]

[0029] The intermediate compound of formula (K) can then be saponified with a suitable base (e.g., lithium hydroxide) to produce the corresponding carboxylate (e.g., lithium salt of carboxylic acid) and alcohol (i.e., structure R 11 Alcohols with OH, such as R 11 If methyl is used, methanol can be obtained. The corresponding carboxylate can then be hydrolyzed with an appropriate acid (e.g., hydrochloric acid) to give the following formula (L):

[0030] [ka]

[0031] The acid of formula (L) can then be reacted with oxalyl chloride to produce the corresponding acid of formula (M):

[0032] [ka]

[0033] Finally, the acid chloride of formula (M) can be reacted with the desired 4-alkylcyclohexylamine to produce the desired trimesic acid derivative of formula (I).

[0034]

[0020] R 1 , R 2 , and R 3 The trimesic acid derivatives of formula (I), each with a different R, can be produced in several ways. One possible approach would be to react 1,3,5-benzenetricarbonyl trichloride with a mixture of three different 4-alkylcyclohexylamines. This procedure produces the desired asymmetric trimesic acid derivatives (i.e., R 1 , R 2 , and R 3 A reaction product containing several trimesic acid derivatives, including several derivatives of trimesic acid (each of which is a different derivative), will be obtained. The desired trimesic acid derivative can then be separated from the reaction product using known separation techniques.

[0035] Alternatively, the synthesis of such a trimesic acid derivative may be carried out by first reacting a compound represented by the following formula (P):

[0036] [ka]

[0037] [In the formula, R 11is an alkyl group (e.g., a methyl group). The compound of formula (P) can be reacted with oxalyl chloride to give the compound of formula (Q):

[0038] [ka]

[0039] The acid chloride compound of formula (Q) can then be reacted with the desired 4-alkylcyclohexylamine to produce the corresponding acid chloride of formula (R):

[0040] [ka]

[0041] The intermediate compound of formula (R) can then be saponified with a suitable base (e.g., lithium hydroxide) to produce the corresponding carboxylate (e.g., lithium salt of carboxylic acid) and alcohol (i.e., structure R 11 Alcohols with OH, such as R 11 If the carboxylate is methyl, methanol can be obtained. The corresponding carboxylate can then be hydrolyzed with an appropriate acid (e.g., hydrochloric acid) to give the following formula (S):

[0042] [ka]

[0043] The acid of formula (S) can be reacted with oxalyl chloride to give the corresponding acid chloride compound, which can be reacted with the desired 4-alkylcyclohexylamine to give the acid of formula (T):

[0044] [ka]

[0045] The intermediate bisamide compound of formula (T) can then be converted to an intermediate bisamide compound of formula (U) by any of a number of suitable techniques, such as palladium catalyzed addition of carbon monoxide and treatment with acid:

[0046] [ka]

[0047] The carboxylic acid of formula (U) can then be reacted with oxalyl chloride to give the corresponding acid chloride. Finally, the acid chloride can be reacted with the desired 4-alkylcyclohexylamine to give the trimesic acid derivative of formula (I).

[0048] In a second aspect, the present invention provides a polymer composition comprising a composition as described above (i.e. a composition comprising one or more trimesic acid derivatives of formula (I)) and a polymer. In such an aspect, the trimesic acid derivative of formula (I) may be any of the aspects discussed above in relation to the first aspect of the invention (e.g. a composition comprising a particular compound or mixture of compounds).

[0049]

[0023] The polymer composition may comprise any suitable polymer. Preferably, the polymer is a thermoplastic polymer, such as a polyolefin, polyester, polyamide, polylactic acid, polycarbonate, acrylic polymer, or a mixture thereof. More preferably, the polymer is a polyolefin polymer, such as a polypropylene polymer, a polyethylene polymer, a polymethylpentene polymer (e.g., poly(4-methyl-1-pentene)), a polybutylene polymer, a poly(vinylcyclohexane) polymer, and a mixture thereof. In a preferred embodiment, the polymer is a polypropylene polymer. More preferably, the polymer is selected from the group consisting of polypropylene homopolymers (e.g., atactic polypropylene homopolymer, isotactic polypropylene homopolymer, and syndiotactic polypropylene homopolymer), polypropylene copolymers (e.g., polypropylene random copolymers), polypropylene impact copolymers, and mixtures thereof. Suitable polypropylene copolymers include, but are not limited to, random copolymers made from the polymerization of propylene in the presence of a comonomer selected from the group consisting of ethylene, but-1-ene (i.e., 1-butene), and hex-1-ene (i.e., 1-hexene). In such polypropylene random copolymers, the comonomer can be present in any suitable amount, but is typically present in an amount of less than about 10% by weight (e.g., from about 1 to about 7% by weight). Suitable polypropylene impact copolymers include, but are not limited to, those produced by the addition of a copolymer selected from the group consisting of ethylene-propylene rubber (EPR), ethylene propylene-diene monomer (EPDM), polyethylene, and plastomer to a polypropylene homopolymer or polypropylene random copolymer. In such polypropylene impact copolymers, the copolymer can be present in any suitable amount, but is typically present in an amount of from about 5 to about 25% by weight.In a preferred embodiment, the polymer composition comprises a polyolefin polymer selected from the group consisting of polypropylene homopolymer, polypropylene random copolymer, and mixtures thereof. More preferably, the polymer composition comprises a polypropylene random copolymer.

[0050] The polymer composition of the present invention may contain any suitable amount of the trimesic acid derivative of formula (I) described above. In a preferred embodiment, the polymer composition contains at least 0.0001 wt % (e.g., at least 0.001 wt %) of the trimesic acid derivative of formula (I) relative to the total weight of the composition. In another preferred embodiment, the polymer composition contains at least 0.002 wt %, at least 0.003 wt %, at least 0.004 wt %, at least 0.005 wt %, at least 0.01 wt %, at least 0.02 wt %, at least 0.03 wt %, at least 0.04 wt %, at least 0.05 wt %, at least 0.1 wt %, at least 0.3 wt %, at least 0.5 wt %, at least 1 wt %, at least 5 wt %, or at least 10 wt % of the trimesic acid derivative of formula (I) relative to the total weight of the composition. In another embodiment, the polymer composition preferably contains less than 99 wt % of the trimesic acid derivative of formula (I) relative to the total weight of the composition. In another preferred embodiment, the polymer composition comprises less than 95 wt%, less than 80 wt%, less than 50 wt%, less than 25 wt%, less than 10 wt%, less than 5 wt%, less than 2 wt%, less than 1 wt%, less than 0.5 wt%, less than 0.2 wt%, less than 0.1 wt%, or less than 0.07 wt%, based on the total weight of the composition. In a series of particularly preferred embodiments, the polymer composition comprises, relative to the total weight of the composition, 0.001% to 0.5% by weight (e.g., 0.01% to 0.5% by weight or 0.05% to 0.5% by weight), 0.001% to 0.2% by weight (e.g., 0.01% to 0.2% by weight or 0.05% to 0.2% by weight), 0.001% to 0.1% by weight (e.g., 0.01% to 0.1% by weight or 0.05% to 0.1% by weight), or 0.001% to 0.07% by weight (e.g., 0.01% to 0.07% by weight) of the trimesic acid derivative of formula (I). As mentioned above, the polymer composition of the present invention may comprise more than one trimesic acid derivative of formula (I).In those embodiments in which the polymer composition comprises two or more trimesic acid derivatives of formula (I), each trimesic acid derivative can be present in an amount that falls within one of the ranges recited above, or the combined amount of all trimesic acid derivatives in the composition can fall within one of the ranges recited above.

[0051] The polymer compositions described herein may contain other polymer additives in addition to the trimesic acid derivatives of formula (I). Suitable additional polymer additives include, but are not limited to, antioxidants (e.g., phenolic antioxidants, phosphite antioxidants, and combinations thereof), antiblocking agents (e.g., amorphous silica and diatomaceous earth), pigments (e.g., organic and inorganic pigments) and other colorants (e.g., dyes and polymeric colorants), fillers and reinforcing agents (e.g., glass, fiberglass, talc, calcium carbonate, and magnesium oxysulfate whiskers), nucleating agents, clarifying agents, acid scavengers (metal salts of fatty acids, e.g., metal salts of stearic acid), polymer processing additives (e.g., polymer processing additives for fluoropolymers), polymer crosslinking agents, slip agents (e.g., fatty acid amide compounds derived from the reaction of a fatty acid with ammonia or an amine-containing compound), fatty acid ester compounds (e.g., fatty acid ester compounds derived from the reaction of a fatty acid with a hydroxyl-containing compound, e.g., glycerin, diglycerol, and combinations thereof), and combinations of the foregoing.

[0052]

[0026] The polymer compositions described herein can be produced by any suitable method. For example, the polyolefin composition can be produced by simple mixing (e.g., high shear or high intensity mixing) of a polyolefin polymer, a composition comprising a trimesic acid derivative of formula (I), and any additional optional ingredients. Alternatively, the additive composition comprising a trimesic acid derivative of formula (I) and any additional optional ingredients (e.g., as described above) can be preblended to provide a preblend composition. This preblend composition can then be mixed with a polymer to produce the polymer composition described above. The polymer composition can be provided in any form suitable for use in further processing to produce an article. For example, the polymer composition can be provided in the form of a powder (e.g., a free-flowing powder), flakes, pellets, prills, tablets, agglomerates, and the like.

[0053]

[0027] The polymer compositions described herein are believed to be useful for producing thermoplastic articles. The polymer compositions can be formed into the desired thermoplastic articles by any suitable technique, such as injection molding, injection rotomolding, blow molding (e.g., injection blow molding or injection stretch blow molding), extrusion (e.g., sheet extrusion, film extrusion, cast film extrusion, or foam extrusion), extrusion blow molding, thermoforming, rotomolding, film blowing (blowing film), film casting (cast film), and the like.

[0054] The polymer compositions described herein can be used to manufacture any suitable article or product. Suitable articles include, but are not limited to, medical devices (e.g., pre-filled syringes for retort applications, intravenous supply containers, and blood collection devices), food packaging, liquid containers (e.g., containers for beverages, drugs, personal care compositions, shampoos, etc.), dressing cases, microwaveable articles, shelving, cabinet doors, machine parts, automotive parts, sheets, pipes, tubes, rotational molded parts, blow molded parts, films, fibers, etc.

[0055]

[0029] The polymer compositions of the present invention have been found to exhibit a highly desirable combination of low haze and low extraction of the trimesic acid derivatives of formula (I). Polymer compositions (e.g., polypropylene random copolymer compositions) containing trimesic acid derivatives of formula (I) generally exhibit haze levels at least 15% lower than those exhibited by polymer compositions containing structurally similar trimesic acid derivatives not encompassed by formula (I). Furthermore, polymer compositions containing specific trimesic acid derivatives of formula (I) have been found to exhibit haze levels one order of magnitude comparable to those exhibited by more transparent polymers, such as polystyrene and acrylic polymers. As mentioned above, these polymer compositions also exhibit exceptionally good (i.e., low) extraction of the trimesic acid derivatives of formula (I) from the polymer compositions. In fact, polymer compositions containing specific trimesic acid derivatives of formula (I) have been found to exhibit extraction levels one to two orders of magnitude lower than those exhibited by polymer compositions containing structurally similar trimesic acid derivatives not encompassed by formula (I). It is believed that these properties exhibited by the polymer compositions of the present invention make them particularly well suited for use in the manufacture of thermoplastic articles or products requiring low haze levels and low extractables, such as articles and products for food contact and medical applications.

[0056] The following examples further illustrate the above-described subject matter but, of course, should not be construed as in any way limiting its scope.

[0057] Example 1 This example illustrates the preparation of trimesic acid derivatives according to the invention.

[0058] 6.53 g (57.7 mmol) of cis-4-methylcyclohexylamine, 0.10 g of LiCI, and 25.62 g (253.2 mmol) of triethylamine (TEA) were added to 550 mL of anhydrous N,N-dimethylformamide (DMF) under an inert atmosphere.

[0059] 4.52 g (17.0 mmol) of 1,3,5-benzenetricarbonyl trichloride dissolved in 100 mL of anhydrous DMF was added to the above cis-4-methylcyclohexylamine, LiCl, TEA reaction mixture over 15 minutes with stirring under inert atmosphere at 25° C. The reaction solution was then heated to 80° C. and stirred for 48 hours.

[0060] After the reaction mixture was cooled to 25° C., 700 mL of methanol was charged to the reaction slurry and stirred for 48 hours. The precipitated solid was then collected by suction filtration and then washed with methanol (2×200 mL).

[0061] The isolated solid was then dried in a vacuum oven at 140° C. for 18 hours. The reaction yielded 6.62 g (78.4%) of a fine white powder. The product was confirmed to be N,N,N-tri(cis-4-methylcyclohexyl)-1,3,5-benzenetricarboxamide.

[0062] Example 2 This example illustrates the preparation of a polymer composition according to the present invention and the properties of such a polymer composition.

[0063]

[0037] First, seven trimesic acid derivatives were synthesized according to the general procedure shown in Example 1 above. These trimesic acid derivatives are shown in Table 1 below. Compounds 1 to 6 each represent the R 1 , R 2 and R 3Compound 7 was obtained in the form of a composition (e.g., reaction product) in which more than 99% of the R groups were in the cis position relative to the bond to the nitrogen atom attached to the cyclohexanediyl moiety. 1 , R 2 , and R 3 Approximately 54% of the groups were obtained in the form of compositions (e.g., reaction products) in which they were cis to the bond to the nitrogen atom attached to the cyclohexanediyl moiety. 1 , R 2 and R 3 The proportion of groups in the cis position is 1 1 H NMR was used to measure.

[0064] [Table 1]

[0065]

[0038] The polymer compositions were made by compounding each trimesic acid derivative with a 12 MFR polypropylene random copolymer (SA849 RCP from LyondellBasell). The trimesic acid derivatives (i.e., compounds 1-7) were each added gravimetrically to pellets of the polymer (0.80 grams of powder additive per 1000 grams of additive / polymer mixture to give 800 ppm of trimesic acid derivative) and then mixed in a Henschel high intensity mixer. The resulting mixtures were melt compounded at 260°C in a Deltaplast single screw compounding extruder with a screw diameter of 25 mm and a length / diameter ratio of 30:1. The extrudates (in the form of strands) of each sample were cooled in a water bath and subsequently pelletized. The melt compounded polymer composition was then injection molded using a 40 ton ARBURG ALLROUNDER 221K injection molding machine at a flat profile barrel temperature of 260°C and 100 bar back pressure to produce plaques with dimensions of approximately 51 mm x 76 mm and a thickness of 0.76 mm. After aging for 24 hours, the plaque dimensions were verified with a micrometer.

[0066] The percent haze of the plaques (including control plaques made without the trimesic acid derivative) was then measured using BYK-Gardner Haze-Guard Plus in accordance with ASTM standard D1103-92.

[0067] The plaques were also tested using a set of conditions to determine the amount of trimesic acid derivatives extracted. In particular, extraction was performed at 100°C for 2 hours using a 550 mL stainless steel vessel lined with Teflon and with a stainless steel lid. A glass spacer was used to ensure separation of the polymer samples during the migration test. Extraction was performed using a 25% ethanol solution. The ethanol was of anhydrous grade. Water was obtained by deionization using an ion exchange purification system. A double migration test in solvent was performed using two plaques immersed in 250 mL of solvent. A control plaque was also prepared without trimesic acid derivatives and extracted using the conditions mentioned above. Aliquots (approximately 1 mL) were removed from the extraction solvent after each heating time into vials for LC analysis.

[0068] A 1000 ppm solution of each trimesic acid derivative was prepared by dissolving 0.100 g in NMP and dilutions were made in 100% ethanol. Using these solutions, calibration plots for each trimesic acid derivative were obtained. A Water ACQUITY UPLC with Phenomenex Kinetex (particle size 2.6 μm) as analytical column and both PDA and MS as detectors was used as the LC instrument. The column temperature was 40° C. The mobile phase used was methanol and water. The flow rate was set at 0.4 mL / min. Sample injection volume was 1-5 μL. The mass spectrometer was used in single ion recording (SIR) mode using an SQD2 detector. The wavelengths in the PDA detector were set at 200-800 nm. Each trimesic acid derivative was identified by comparison of its retention time with the corresponding peak in the standard solution, as well as its MS and UV spectra. Quantification was performed using the calibration plots of external standards. The limit of detection (LOD) was determined by extrapolation to a signal-to-noise ratio of 3:1.

[0069] The results of the haze and extraction measurements are shown below in Table 2. In the column Amount Extracted, the designation "ND" means "Not Detected" and indicates that the amount (if any) of extracted trimesic acid derivatives could not be quantified since the measurement did not return a signal above the limit of detection (LOD) as stated above.

[0070] [Table 2]

[0071] As can be seen from the data in Table 2, the polymer compositions made with compounds 1-6 each showed very low extractable levels (i.e., below 50 ppb). In fact, the polymer compositions made with compounds 1-3 and 5 showed extractable levels (if any) below the detection limit. In contrast, the polymer composition made with compound 7 showed extractable levels of over 200 ppb, which is more than four times the extraction exhibited by the polymer composition made with compound 6. This extraction result is surprising considering that the only difference between compounds 6 and 7 is the cis content of the two samples. Moreover, this result indicates that these extremely low extractable levels were consistently exhibited by trimesic acid derivatives with relatively high cis content.

[0072]

[0044] Furthermore, the data in Table 2 show that each of compounds 1-7 significantly reduced the haze level of the polymer composition compared to the control that did not contain the trimesic acid derivative. However, the haze level of the polymer composition made with compound 7 is nearly 40% higher than the haze level of the polymer composition made with compound 6, the next closest sample in terms of haze. These results indicate that trimesic acid derivatives having a relatively high cis content consistently provide improved haze performance over similar trimesic acid derivatives having a lower cis content (e.g., less than 60% cis content).

[0073]

[0045] In view of the above, the inventors believe that the trimesic acid derivatives of the present invention are exceptional due to their highly desirable combination of low haze and low extractables, and polymer compositions made with such trimesic acid derivatives will be suitable for a wide range of applications requiring polymer compositions exhibiting low haze and extractable levels, such as food contact and medical device applications.

[0074]

[0046] All references cited herein, including publications, patent applications, and patents, are incorporated by reference herein to the same extent as if each reference was individually and specifically indicated to be incorporated by reference and was set forth in its entirety herein.

[0075]

[0047] The use of the terms "a" and "an" and "the" and similar referents in the context of describing the subject matter of this application (especially in the context of the claims below) should be construed to include both the singular and the plural, unless otherwise indicated herein or clearly contradicted by context. The terms "comprising," "having," "including," and "containing" should be construed as open-ended terms (i.e., meaning "including, but not limited to"), unless otherwise noted. The recitation of ranges of values ​​herein is merely intended to serve as a shorthand method of individually referring to each separate value contained within the range, unless otherwise indicated herein, and each separate value is incorporated herein as if it were individually recited herein. All methods described herein may be performed in any suitable order, unless otherwise indicated herein or clearly contradicted by context. The use of any and all examples or exemplary language (e.g., "for example") provided herein is intended merely to better clarify the subject matter of the present application and does not limit the scope of the subject matter unless otherwise claimed. No language in the specification should be construed as indicating any non-claimed element as essential to the practice of the subject matter described herein.

[0076]

[0048] Preferred embodiments of the subject matter of this application are described herein, including the best mode known to the inventors for carrying out the claimed subject matter. Variations of these preferred embodiments may become apparent to those of skill in the art upon reading the foregoing description. The inventors expect that those of skill in the art will utilize these variations as appropriate, and the inventors intend that the subject matter described herein may be practiced otherwise than as specifically described herein. Accordingly, this disclosure includes all modifications and equivalents of the subject matter recited in the claims appended hereto as permitted by applicable law. Moreover, any combination of the above-described elements in all possible variations thereof is encompassed by this disclosure unless otherwise indicated herein or otherwise clearly contradicted by context.

Claims

1. Formula (I) 【Chemistry 1】 [In the formula, R １ , R ２ , and R ３ is independently selected from the group consisting of alkyl groups, R of the trimesic acid derivative of formula (I) present in the composition; １ , R ２ , and R ３ wherein 60% or more of the groups are in the cis position relative to the bond to the nitrogen atom attached to the cyclohexanediyl moiety.

2. R １ , R ２ , and R ３ But, C １ ~C ８ 2. The composition of claim 1, wherein the alkyl group is independently selected from the group consisting of alkyl groups.

3. R １ , R ２ , and R ３ The composition of claim 1 or claim 2, wherein at least one of the following is a branched alkyl group:

4. R １ , R ２ , and R ３ The composition of claim 3, wherein at least two of are branched alkyl groups.

5. R １ , R ２ , and R ３ The composition of claim 4 , wherein each of is a branched alkyl group.

6. The composition, N,N,N-tri(4-methylcyclohexyl)-1,3,5-benzenetricarboxamide; N,N,N-tri(4-n-propylcyclohexyl)-1,3,5-benzenetricarboxamide; N,N,N-tri(4-isopropylcyclohexyl)-1,3,5-benzenetricarboxamide; N,N,N-tri(4-n-butylcyclohexyl)-1,3,5-benzenetricarboxamide; N,N,N-tri(4-isobutylcyclohexyl)-1,3,5-benzenetricarboxamide; N,N,N-tri(4-tert-butylcyclohexyl)-1,3,5-benzenetricarboxamide; N,N,N-tri(4-tert-pentylcyclohexyl)-1,3,5-benzenetricarboxamide; and mixtures thereof The composition according to any one of claims 1 to 5, comprising a trimesic acid derivative selected from the group consisting of:

7. The composition of claim 6, wherein the composition comprises N,N,N-tri(4-methylcyclohexyl)-1,3,5-benzenetricarboxamide.

8. The composition of claim 6, wherein the composition comprises N,N,N-tri(4-n-propylcyclohexyl)-1,3,5-benzenetricarboxamide.

9. The composition of claim 6, wherein the composition comprises N,N,N-tri(4-isopropylcyclohexyl)-1,3,5-benzenetricarboxamide.

10. The composition of claim 6, wherein the composition comprises N,N,N-tri(4-n-butylcyclohexyl)-1,3,5-benzenetricarboxamide.

11. The composition of claim 6, wherein the composition comprises N,N,N-tri(4-isobutylcyclohexyl)-1,3,5-benzenetricarboxamide.

12. The composition of claim 6, wherein the composition comprises N,N,N-tri(4-tert-butylcyclohexyl)-1,3,5-benzenetricarboxamide.

13. The composition of claim 6, wherein the composition comprises N,N,N-tri(4-tert-pentylcyclohexyl)-1,3,5-benzenetricarboxamide.

14. R of the trimesic acid derivative of formula (I) present in the composition １ , R ２ , and R ３ The composition of any one of claims 1 to 5, wherein greater than 90% of the groups are in the cis position relative to the bond to the nitrogen atom attached to the cyclohexanediyl moiety.

15. At least about 50 mole percent of the trimesic acid derivatives of formula (I) present in the composition are R １ , R ２ , and R ３ The composition according to any one of claims 1 to 14, comprising a group.

16. (a) a composition according to any one of claims 1 to 15; (b) a polyolefin polymer; 1. A polymer composition comprising:

17. 17. The polymer composition of claim 16, wherein the polyolefin polymer is a polypropylene polymer.

18. 18. The polymer composition of claim 17, wherein the polyolefin polymer is selected from the group consisting of polypropylene homopolymer, polypropylene random copolymer, and mixtures thereof.

19. 20. The polymer composition of claim 18, wherein the polyolefin polymer is a polypropylene random copolymer.

20. The composition according to any one of claims 16 to 19, wherein the composition contains about 0.001 wt% or more of the trimesic acid derivative of formula (I) based on the total weight of the polymer composition.