Particulate Filter

Abstract

The vehicle exhaust filter (2) comprises a porous substrate having an inlet face and an outlet face, the porous substrate having inlet channels extending from the inlet face and outlet channels extending from the outlet face. The inlet channels and outlet channels are separated by a plurality of filter walls having a porous structure. The vehicle exhaust filter (2) has a molecular weight of 0.10 g / cm. 3 and the vehicle exhaust filter has a mass loading of the refractory powder of less than 10 g / L.

Description

[Technical field]

[0001] The present disclosure relates to vehicle exhaust filters for filtering particulate matter from exhaust gases. In particular, the present invention relates to an improvement in a filter that includes a porous substrate having an inlet face and an outlet face, the inlet face being separated from the outlet face by a porous structure. The filter may be a wall-flow filter. [Background technology]

[0002] There are concerns regarding the emissions of particulate matter (PM), commonly referred to as soot, from internal combustion engines, particularly diesel and gasoline engines for automotive applications. The main concerns relate to potential health effects, especially for very small particles with sizes in the nanometre range.

[0003] Diesel particulate filters (DPFs) and gasoline particulate filters (GPFs) are manufactured using a variety of materials, including sintered metal, ceramic, or metal fibers, with the most common type in practical mass production being the wall-flow type, made from porous ceramic materials manufactured in the form of a monolithic array of many small channels running along the length of the body. The alternating channels are plugged at one end so that exhaust gases are forced through the porous ceramic channel walls that prevent the passage of most of the particulates, thus allowing only filtered gases to enter the environment. Commercially produced ceramic wall-flow filters include those made from cordierite, various forms of silicon carbide, and aluminum titanate. The actual shape and dimensions of the actual filter on the vehicle, as well as characteristics such as channel wall thickness and its porosity, depend on the application in question. The average size of the pores in the filter channel walls of ceramic wall-flow filters through which the gases pass typically ranges from 5 to 50 μm, and is usually around 20 μm. In stark contrast, most diesel particulate matter emitted by modern passenger car high speed diesel engines is very small in size, e.g., between 10 and 200 nm.

[0004] Some PM may be retained within the pore structure of the filter wall and in some applications may gradually accumulate until the pores are bridged by a network of PM, which can then easily form a cake of particulates on the inner walls of the filter channels. The particulate cake is an excellent filter medium and its presence results in very high filtration efficiency. In some applications, soot is continuously burned on the filter as it accumulates, which prevents the particulate cake from accumulating on the filter.

[0005] In some filters, e.g. low-load diesel particulate filters, trapped PM must be periodically removed from the filter to prevent excessive backpressure buildup that can be detrimental to engine performance and reduce fuel economy. Thus, in diesel applications, the retained PM is removed from the filter by combustion in air, and during the process, the amount of available air and the amount of excess fuel used are very carefully controlled to achieve the high temperatures required to ignite the retained PM. At the end of this process, usually called regeneration, removing the last remaining particulates from the filter can result in a significant loss of filtration efficiency and an explosive release of many small particles into the environment. Thus, a filter may have low filtration efficiency on first use, after each subsequent regeneration event, and at later stages of each regeneration process.

[0006] It would therefore be desirable to improve and / or maintain filtration efficiency at all times, for example, early in the life of a filter, upon first use, and / or during and immediately after regeneration, and / or when soot has built up on the filter.

[0007] Liu, X., Szente, J., Pakko, J., Lambert, C. et al., "Using Artificial Ash to Improve GPF Performance at Zero Mileage," SAE Technical Paper 2019-01-0974, 2019, doi:10.4271 / 2019-01-0974, describes a process for impregnating a bare filter substrate with submicron alumina particles generated by an atomizer to create an "artificial ash" coating to reduce soot emissions during cold start conditions. The process consists of generating aerosol particles by atomizing a liquid suspension with compressed air, drying the resulting ash-containing droplets by passing them through a furnace, and impregnating the dry ash particles onto the filter by capture by filtration. The process utilizes a high-volume atomizer (model PLG-2100, PALAS, Germany) to deliver a flow rate of 100 L / min to a full-size brick. Filter loading is monitored by the pressure drop and PM concentration across the filter recorded by a DustTrak aerosol monitor (TSI Inc, Minnesota, USA). The process has shown to reduce soot emissions during cold start conditions, but is limited to materials that can be spray dried, requires an atomizer, drying oven, and aerosol monitor, and artificial ash loading conditions may be constrained by the conditions necessary to obtain complete drying before the liquid aerosol reaches the filter substrate.

[0008] WO 2011 / 151711 describes a method of making a filter for filtering particulate matter from exhaust gases emitted from a lean-burn internal combustion engine. The filter comprises a porous substrate having an inlet face and an outlet face, the inlet face being separated from the outlet face by a porous structure having pores of a first average pore size. The inlet face includes a bridge network of particles of a refractory material interconnected across the pores of the porous structure. The method includes contacting the inlet face of the filter substrate with an aerosol including the refractory material in dry powder form. While the process has shown PM emission reductions for the filter upon first use and after each subsequent regeneration event, it would be desirable to provide an improved process, particularly with respect to controllability of the parameters of the filters produced.

[0009] US Patent Application Publication No. 2019 / 0048771 describes an engine exhaust particulate filter including a porous substrate having inert nanoparticles at a concentration ranging from 0.01 g / L to 60 g / L of filter volume of the substrate, a portion of the nanoparticles arranged to form a regeneration-resistant porous structure configured to capture particulates from the exhaust gas stream. The filter is intended to provide an improvement in the zero fuel consumption efficiency of particulate filters, but it would be desirable to provide an improved process, particularly to improve the controllability and flexibility of the process. Summary of the Invention

[0010] In a first aspect, the present disclosure provides a vehicle exhaust filter comprising a porous substrate having an inlet face and an outlet face, the porous substrate comprising an inlet channel extending from the inlet face and an outlet channel extending from the outlet face, the inlet channel and the outlet channel being separated by a plurality of filter walls having a porous structure; Vehicle exhaust filters are 0.10g / cm 3 impregnated with a refractory powder having a tap density before impregnation of less than The vehicle exhaust filter has a mass loading of refractory powder of less than 10 g / L; More than 40% of the refractory powder is disposed within a porous structure of the plurality of filter walls and less than 60% of the refractory powder is coated on an exterior surface of the plurality of filter walls.

[0011] Preferably, more than 50% of the refractory powder, optionally more than 65% of the refractory powder, optionally more than 75% of the refractory powder, optionally up to 100% of the refractory powder may be disposed within the porous structure of the plurality of filter walls.

[0012] The percentage of refractory powder disposed within the porous structure of the plurality of filter walls may be calculated by the following formula:

[0013]

number

[0014] The refractory powder is 0.08 g / cm 3 Less than, optionally 0.07g / cm 3 Less than, optionally 0.06g / cm 3 Less than, optionally 0.05g / cm 3 It may have a pre-impregnation tap density of less than 100 nm.

[0015] The mass loading of the refractory powder may be less than 7 g / L, optionally less than 5 g / L, optionally less than 3 g / L, optionally less than 1 g / L.

[0016] More than 0.5 g / L of refractory powder may be disposed within the porous structure of the filter walls.

[0017] In a second aspect, the present disclosure provides a vehicle exhaust filter comprising a porous substrate having an inlet face and an outlet face, the porous substrate comprising inlet channels extending from the inlet face and outlet channels extending from the outlet face, the inlet channels and outlet channels being separated by a plurality of filter walls having a porous structure; Vehicle exhaust filters are 0.10g / cm 3 impregnated with a refractory powder having a tap density before impregnation of less than The vehicle exhaust filter has a mass loading of refractory powder of less than 10 g / L; More than 0.5 g / L of refractory powder is disposed within the porous structure of the plurality of filter walls.

[0018] The refractory powder is 0.08 g / cm 3 Less than, optionally 0.07g / cm 3 Less than, optionally 0.06g / cm 3 Less than, optionally 0.05g / cm 3 It may have a pre-impregnation tap density of less than 100 nm.

[0019] The mass loading of the refractory powder may be greater than 1 g / L, optionally greater than 3 g / L, optionally greater than 5 g / L, optionally greater than 7 g / L.

[0020] The refractory powder may include one or more fumed refractory powders and / or one or more aerogels. The one or more fumed refractory powders may be made by a pyrogenic process, such as flame pyrolysis.

[0021] The one or more fumed refractory powders may include one or more of fumed alumina, fumed silica, fumed titania, other fumed metal oxides, and fumed mixed oxides.

[0022] The one or more aerogels may include one or more of silica aerogels, alumina aerogels, carbon aerogels, titania aerogels, zirconia aerogels, ceria aerogels, metal oxide aerogels, and mixed oxide aerogels.

[0023] In a third aspect, the present disclosure provides a vehicle exhaust filter comprising a porous substrate having an inlet face and an outlet face, the porous substrate comprising inlet channels extending from the inlet face and outlet channels extending from the outlet face, the inlet channels and outlet channels being separated by a plurality of filter walls having a porous structure; Vehicle exhaust filters are 0.10g / cm 3impregnated with a refractory powder having a tap density before impregnation of less than The refractory powder includes one or more aerogels.

[0024] The one or more aerogels may include one or more of silica aerogels, alumina aerogels, carbon aerogels, titania aerogels, zirconia aerogels, ceria aerogels, metal oxide aerogels, and mixed oxide aerogels.

[0025] In a fourth aspect, the present disclosure provides a vehicle exhaust filter comprising a porous substrate having an inlet face and an outlet face, the porous substrate comprising inlet channels extending from the inlet face and outlet channels extending from the outlet face, the inlet channels and outlet channels being separated by a plurality of filter walls having a porous structure; Vehicle exhaust filters are 0.10g / cm 3 impregnated with a refractory powder having a tap density before impregnation of less than The vehicle exhaust filter has a mass loading of refractory powder of less than 10 g / L; The vehicle exhaust filter exhibits a substantially linear load-backpressure response for soot loads greater than 0.1 g / L, preferably for soot loads greater than 0.05 g / L.

[0026] In any of the above aspects, the following features may be present.

[0027] The filter may have a filtration efficiency of greater than 90%, preferably greater than 95%, preferably greater than 98%, preferably greater than 99% at a soot loading of 0.02 g / L.

[0028] The filter is 600m 3 / hr flow rate may have a back pressure of 20-180 mbar.

[0029] The refractory powder may be an aerosol deposited refractory powder, preferably an aerosol deposited dry refractory powder.

[0030] The refractory powder may have a d50 (by volume) of less than 25 micrometers, preferably less than 20 micrometers, more preferably less than 10 micrometers.

[0031] The filter may be a wall-flow filter.

[0032] The wall-flow filter may be an asymmetric wall-flow filter. The design of an asymmetric wall-flow filter is known, for example, from WO 2005 / 030365, which discloses a honeycomb filter comprising an array of interconnected porous walls defining an array of first and second channels. The first channels are adjacent to the second channels at their sides and have a larger hydraulic diameter than the second channels. The first channels have a square cross section and the corners of the first channels are shaped such that the thickness of the porous walls adjacent the corners of the first channels is comparable to the thickness of the porous walls adjacent the edges of the first and second channels. In use, the first channel with the larger hydraulic diameter is positioned upstream. The Society of Automotive Engineers SAE Technical Paper Series 2007-01-0656 explains that "there is a pressure loss penalty in the clean state of the ACT design [in catalyzed asymmetric cell technology (ACT) wall-flow filters] due to gas contraction and expansion at the inlet and outlet of the filter channels. However, the filter can only remain totally clean (fully regenerated) for a small portion of the time during operation on a vehicle." WO 2005 / 030365 also explains that advantages of the asymmetric filter design include an increase in the effective surface area available for collecting soot and ash particles at the inlet section of the honeycomb filter, thus increasing the overall storage capacity of the honeycomb filter. The common general knowledge textbook "Catalytic Air Pollution Control-Commercial Technology", 3rd Edition, Ronald M. Heck et al, John Wiley & Sons, Inc. Hoboken, NJ, USA (2009) pp.338-340 explains that "Such [asymmetric filter] channel designs allow for higher ash storage capacity combined with lower post-ash loading back pressure due to the larger hydraulic diameter and larger inlet open volume. The ACT design also helps maintain the mechanical and thermal durability of the filter."

[0033] The vehicle exhaust filter may be a fired filter.

[0034] The porous substrate may include one or more washcoats.

[0035] The porous substrate can be an asymmetric substrate.

[0036] The porous substrate may include an adhesion promoter and / or a binder.

[0037] In a fifth aspect, the present disclosure provides an exhaust system comprising the vehicle exhaust filter of any of the preceding aspects.

[0038] The exhaust system may further include additional components, such as further catalysts or filters. Examples of further components include NOx traps, hydrocarbon traps, selective catalytic reduction (SCR) catalysts, ammonia slip catalysts (ASC), and combinations of two or more thereof. Such components are well known in the art.

[0039] In a sixth aspect, the present disclosure provides a method for treating exhaust gases from an internal combustion engine, comprising passing the exhaust gases through an exhaust system as described above.

[0040] The internal combustion engine may be a diesel engine or a gasoline engine.

[0041] In a seventh aspect, the present disclosure provides a vehicle including the vehicle exhaust filter of any of the first to fourth aspects.

[0042] In an eighth aspect, the present disclosure provides a plurality of vehicle exhaust filters, each vehicle exhaust filter comprising a porous substrate having an inlet face and an outlet face, the porous substrate comprising an inlet channel extending from the inlet face and an outlet channel extending from the outlet face, the inlet channel and the outlet channel being separated by a plurality of filter walls having a porous structure; Each vehicle exhaust filter is 0.10g / cm 3impregnated with a refractory powder having a tap density before impregnation of less than Each vehicle exhaust filter has a mass loading of fire-resistant powder of less than 10 g / L; Each vehicle exhaust filter is 600m 3 / hr flow rate of 20 to 180 mbar, and the relative standard deviation of the backpressures of the plurality of vehicle exhaust filters is less than 0.04, preferably less than 0.025.

[0043] For each vehicle exhaust filter, more than 40% of the refractory powder may be disposed within the porous structure of the plurality of filter walls and less than 60% of the refractory powder may be coated on the exterior surface of the plurality of filter walls.

[0044] The refractory powder may be an aerosol deposited refractory powder, preferably an aerosol deposited dry refractory powder.

[0045] As used herein, the term "filter" refers to a porous substrate having a porous structure suitable for filtering particulate matter from exhaust gases. The porous substrate may be formed, for example, from sintered metal, ceramic, or metal fibers. The filter may be a wall-flow type made from a porous material, such as a ceramic, manufactured in the form of a monolithic array of many small channels that run along the length of the body. For example, the filter may be formed from cordierite, various forms of silicon carbide, or aluminum titanate.

[0046] The filter may be a "bare" filter, or alternatively may incorporate catalytic functionality such as oxidation, NOx trap, or selective catalytic reduction activity. The porous substrate may include a composition (known as a washcoat) that coats the porous structure of the filter. The washcoat may be a catalytic washcoat. The catalytic washcoat may include a catalyst selected from the group consisting of a hydrocarbon trap, a three-way catalyst (TWC), a NOx absorbent, an oxidation catalyst, a selective catalytic reduction (SCR) catalyst, a lean NOx catalyst, and a combination of any two or more thereof. The catalyst, e.g., the TWC, the NOx absorbent, the oxidation catalyst, the hydrocarbon trap, and the lean NOx catalyst, may contain one or more platinum group metals, particularly those selected from the group consisting of platinum, palladium, and rhodium.

[0047] As a result, the coated filter may be, for example, a catalyzed soot filter (CSF), a selective catalytic reduction filter (SCRF), a lean NOx trap filter (LNTF), a gasoline particulate filter (GPF), an ammonia slip catalyst filter (ASCF), or a combination of two or more of these (e.g., a filter including a selective catalytic reduction (SCR) catalyst and an ammonia slip catalyst (ASC)).

[0048] The shape and dimensions of the filter, such as its channel wall thickness and its porosity and other properties, may vary depending on the intended use of the filter. The filter may be configured for use with an internal combustion engine to filter exhaust gases emitted by the internal combustion engine. The internal combustion engine may be a gasoline spark ignition engine. However, the filter finds particular application when configured for use with an internal combustion engine in the form of a diesel or gasoline engine.

[0049] As used herein, the term "dry powder" refers to a particulate composition that is not suspended or dissolved in a liquid. It does not necessarily imply the complete absence of all water molecules. Dry powders are preferably free-flowing.

[0050] As used herein, the term "bulk density" refers to bulk density measured according to method 1 of section 2.9.34 of the European Pharmacopoeia 7.0, in which an amount of powder sufficient to complete the test is first passed through a sieve with openings of 1.0 mm or greater, if necessary to break up any agglomerates that may have formed during storage. Approximately 5 g(m) of the test sample, weighed to within 0.1 percent accuracy, is then introduced without compression into a dry graduated 250 mL cylinder (readable to 2 mL). If necessary, the powder is carefully leveled without compression and the unsettled apparent volume (V0) is read to the nearest graduation unit. Bulk density (g / cm 3 ) is calculated using the formula m / V0.

[0051] As used herein, the term "tap density" refers to the tap density of a powder measured at 1250 taps according to Method 1 of Section 2.9.35 of the European Pharmacopoeia 7.0.

[0052] As used herein, the term "g / L" (grams per liter) refers to the mass of dry powder divided by the volume of the filter.

[0053] As used herein, the terms "loading" and "mass loading" when referring to the amount of refractory powder refer to the mass of powder added to the filter, which may be measured by weighing the filter before and after applying the powder to the filter.

[0054] As used herein, the term "envelope volume" refers to the surface volume of a filter as obtained by sealing a film to encompass the filter, not including the volume of the channels. It includes the solid material of the filter, the open and closed pores of the porous structure of the filter, and surface defects / voids. The envelope volume of a filter can be measured by MIP. For example, this can be performed using the following process: 1. Take six equally spaced samples from the filter. 2. The envelope volume of each sample is determined by MIP and divided by the sample mass. 3. Take the average of these and multiply by the filter mass. 4. This is the envelope volume of the filter.

[0055] As used herein, the term "d50 (by volume)" refers to d50 (by volume) measurements measured by a Malvern Mastersizer® 3000 equipped with an Aero s dispersion unit available from Malvern Panalytical Ltd, Malvern, UK. Dispersion conditions: air pressure = 2 barg, feed rate = 65%, hopper gap = 1.2 mm. Refractive index and absorption parameters are set according to the instructions provided in the Malvern Mastersizer® 3000 User Manual.

[0056] As used herein, the term "filtration efficiency" refers to filtration efficiency measured using a Cambustion® Diesel Particulate Filter Testing System available from Cambustion Ltd. Cambridge, UK under the following test conditions: 1. Precondition the filter in a 700°C oven for 2 hours. 2. Place the filter in the test fixture. a) Stabilization - mass flow 250 kg / h, 50°C, 5 minutes b) Warm-up – mass flow rate 250 kg / hour, 240°C, 5 min c) Weighing - The filter is removed from the apparatus and weighed. d) Warm-up - Put the filter back into the device, mass flow rate 250 kg / hr, 240°C, 5 min. e) Deposition stage - mass flow rate 250 kg / hr, 240°C, deposition rate: for GPF filters - 2 g / hr until 2 g / L soot deposition is reached, for SCRF / CSF filters - 10 g / hr until 6 g / L soot is reached f) Weighing - The filter is removed from the apparatus and weighed.

[0057] Fuel used during testing: Carcal RF-06-08 B5 During the test, a particle counter continuously samples downstream of the filter. Just before and after testing a batch of filters, the instrument runs an "upstream" test, allowing the particle counter to sample the raw soot product from the instrument. The upstream test is 20 minutes in length and uses the same conditions as the deposition phase described above. The average of the two upstream tests (before and after the filter test) is compared with the data from the deposition phase of the filter test to obtain the filtration efficiency. Filtration efficiency is given at a specified soot load.

[0058] As used herein, the term "vacuum generator" refers to a device or combination of devices that function to create a reduced pressure. Non-limiting examples of suitable devices include vacuum generators that operate on the Venturi principle, vacuum pumps, such as rotary vane and liquid ring vacuum pumps, and regenerative blowers.

[0059] As used herein, the term "pressure sensor" refers to a device or combination of devices that function to measure absolute and / or relative pressure. Non-limiting examples of suitable devices include pressure transducers, which may be diaphragm pressure transducers. For example, a Wika® P30 pressure transmitter available from WIKA Alexander Wiegand SE & Co. KG, Klingenberg, Germany may be used.

[0060] As used herein, the term "controller" refers to a function that may include hardware and / or software. A controller may include a control unit or may be a computer program executing on a dedicated or shared computational resource. A controller may include a single unit or may be composed of multiple operatively connected sub-units. A controller may be located in one processing resource or distributed across spatially separated processing resources. A controller may include a microcontroller, one or more processors (such as one or more microprocessors), memory, configurable logic, firmware, etc. [Brief description of the drawings]

[0061] Aspects and embodiments of the present disclosure will now be described, by way of example only, with reference to the accompanying drawings. [Figure 1] 1 is a schematic diagram of an apparatus for treating a filter for filtering particulate matter from an exhaust gas according to the present disclosure; [Diagram 2] FIG. 2 is a flow diagram illustrating a method for manufacturing a filter according to the present disclosure, incorporating a method for treating the filter using the apparatus of FIG. 1. [Diagram 3] FIG. 2 is a flow diagram illustrating a method of treating a filter for filtering particulate matter from an exhaust gas using the apparatus of FIG. 1. [Figure 4] 1 is a graph showing soot load-backpressure response curves for various filters. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0062] Those skilled in the art will understand that one or more features of one aspect or embodiment of the present disclosure may be combined with one or more features of any other aspect or embodiment of the present disclosure, unless the adjacent context teaches otherwise.

[0063] An example of an apparatus according to the present disclosure will now be described with reference to Figure 1, which shows a schematic diagram of an apparatus 1 for treating a filter 2 for filtering particulate matter from exhaust gases. The filter 2 is of the type comprising a porous substrate having an inlet face and an outlet face, the inlet face and the outlet face being separated by a porous structure.

[0064] The apparatus 1 comprises a reservoir 3 for containing a dry powder 4. A filter holder 5 is provided for holding the filter 2. A vacuum generator 6 is provided for establishing a primary gas flow through the porous structure of the filter 2 in use by applying a reduced pressure to the outlet face of the filter 2. A transport device 8 is provided for transporting the dry powder 4 from the reservoir 3 to a spray device 7. The spray device 7 is provided for receiving the dry powder 4 from the transport device 8 and spraying the dry powder 4 towards the inlet face of the filter 2. A controller 9 is provided configured to control the operation of the apparatus 1.

[0065] The reservoir 3 may receive the dry powder 4 from a dry powder inlet 11. The dry powder inlet 11 may be an outlet for an upstream bulk supply of dry powder. For example, the dry powder inlet 11 may be a conduit connected upstream to a further reservoir of dry powder 4. The dry powder inlet 11 may indicate manual, semi-automatic or automatic refilling of the reservoir 3 through a lid or opening in the reservoir 3.

[0066] The reservoir 3 may comprise one or more hoppers. The reservoir 3 may comprise one hopper. In the illustrated example of FIG. 1, the reservoir 3 comprises a first hopper 12 and a second hopper 13. The second hopper 13 may be downstream of the first hopper 12 to receive the dry powder 4 discharged from the first hopper 12. The one or more hoppers may be provided in separate housings. Alternatively, the one or more hoppers may be provided in a single housing. The one or more hoppers may comprise one or more chambers of a single container.

[0067] The reservoir 3 may include a dosing device 15. The dosing device 15 may dosing the dry powder 4 by one or more of weight, volume, particle number, time. The dosing device 15 may be located at or near the outlet of the reservoir 3. The dosing device 15 may be located at or near the outlet of one or more hoppers of the reservoir 3. The dosing device may be located at or near the outlet of the first hopper 12.

[0068] The dosing device 15 is capable of gravimetrically dispensing the dry powder 4 from the reservoir 3 .

[0069] The dosing device 15 may be a loss-in-weight feeder. Non-limiting examples of suitable dosing devices include the Coperion® feeder available from Coperion GmbH, Stuttgart, Germany. K-Tron Type K2-ML-T35 Gravimetric Twin Axis Feeder and All-Fill® available from All-Fill International Ltd, Sandy, UK One example is the Series S1 Micro-Fill.

[0070] The transport device 8 transports the dry powder 4 from the reservoir 3 to the spray device 7. The transport device 8 may gravimetrically supply the dry powder 4 at least a portion of the way towards the spray device 7.

[0071] The transport device 8 may comprise one or more components. The transport device 8 may comprise one or more conduits, such as passageways, pipes, hoses, and the like.

[0072] If the reservoir 3 comprises two or more hoppers, the transport device 8 may transport the dry powder 4 between the hoppers. The transport device 8 may gravimetrically feed the dry powder 4 between the hoppers. The transport device 8 may comprise a first conduit 14 extending between the first hopper 12 and the second hopper 13. The first conduit 14 may extend from the first housing to the second housing. Alternatively, the first conduit 14 may extend from the first chamber to the second chamber of the single container. The dry powder 4 may be gravimetrically fed along the first conduit 14.

[0073] The transport device 8 may comprise a second conduit 16 extending from the second hopper 13 to the spray device 7 .

[0074] The spraying device 7 is provided for receiving the dry powder 4 from the transport device 8 and spraying the dry powder 4 towards the inlet face of the filter 2. The spraying device 7 may comprise a secondary gas flow generator for generating a secondary gas flow that may be used to spray the dry powder 4 towards the inlet face of the filter 2.

[0075] The spray device 7 may further comprise one or more outlets for releasing the dry powder 4 towards the inlet face of the filter 2. The one or more outlets of the spray device may comprise an opening size of 1-10 mm. The openings may be circular, part circular, or slot shaped. The one or more outlets may be one or more fixed outlets. Alternatively, the one or more outlets may be one or more movable outlets, for example one or more vibrating outlets.

[0076] The one or more outlets may be provided in one or more nozzles, each of which may include one or more spray outlets. In the illustrated example of Figure 1, a single nozzle 25 is provided with multiple spray outlets.

[0077] The secondary gas flow generator may comprise a compressed gas generator. In the illustrated example of Fig. 1, the secondary gas flow generator comprises a compressed air generator which may comprise a compressor 22. The compressor 22 may take in air from an air inlet 21 and supply compressed air via a supply line 23 to one or more outlets of the spraying device 7. A return line 24 may be provided. Valves and controls necessary for operation may be provided as known to those skilled in the art.

[0078] An interconnection may be provided between the transport device 8 and the spray device 7 through which the dry powder 4 is transferred from the transport device 8 to the spray device 7. The interconnection may be provided at or near one or more outlets of the spray device 7. In one example, the interconnection may be provided at the nozzle 25. Alternatively, the interconnection may be provided at or near the reservoir 3, for example at or near the second hopper 13 of the reservoir 3. In one example, the interconnection is a fluid connection between the supply line 23 and the second conduit 16. For example, the secondary gas flow of the spray device 7 may be fluidly connected to the second conduit 16 at or near the outlet of the second hopper 13 to fluidize the dry powder 4 and assist in transporting the dry powder along at least a portion of the second conduit 16. For example, the secondary gas flow of the spray device 7 may take up the dry powder 4 from the second conduit 16. For example, the secondary gas flow of the spray device 7 may create a suction force on the second conduit to draw the dry powder 4 into the secondary gas flow.

[0079] In one example, the spraying device 7 includes a compressed air gun. A non-limiting example of a suitable compressed air gun is the STAR Professional Gravity Feed Spray Gun 1.4 mm, part number STA2591100C.

[0080] The filter holder 5 may function to maintain the filter 2 in a stationary position during processing. The filter holder 5 may grip the upper and / or lower ends of the filter 2. The filter holder 5 may include an inflatable upper seal bladder 31 (also referred to as an upper inflatable collar) and / or an inflatable lower seal bladder 30 (also referred to as a lower inflatable collar) that support the respective upper and lower ends of the filter 2. The inflatable upper seal bladder 31 and the inflatable lower seal bladder 30 may contact and / or engage with an outer surface of the filter 2. Each may form a liquid-tight or air-tight seal around the filter 2. The inflatable upper seal bladder 31 and the inflatable lower seal bladder 30 may be supported by one or more housings (e.g., may be supported by the inner walls of one or more housings).

[0081] The device 1 may be configured such that the filter 2 is placed in the filter holder 5 in a vertical orientation with the inlet face of the filter uppermost. At least a portion of the spray device 7 may be located vertically above the inlet face. The spray direction of the spray device 7 may be coaxial with the longitudinal axis of the filter 2. The spray direction and the longitudinal axis of the filter 2 may be coincident.

[0082] The apparatus 1 may further comprise a flow conduit 10 located between the spray device 7 and the inlet face of the filter 2. The flow conduit 10 may function to steer the primary gas flow towards the inlet face of the filter 2. The flow conduit 10 may function to straighten the primary gas flow such that the flow direction of the primary gas flow is perpendicular to the inlet face of the filter 2 when it contacts the inlet face.

[0083] The flow conduit 10 may be empty to provide an unobstructed flow path between the spray device 7 and the inlet face of the filter 2. Alternatively, the flow conduit 10 may include a flow conditioner interposed between the spray device 7 and the inlet face of the filter 2, the flow conditioner serving to facilitate dispersion of the dry powder 4. For example, the flow conditioner may include one or more of a static mixer, a mesh, a sieve, a baffle, and an orifice plate.

[0084] The flow conduit 10 may comprise a tube. The flow conduit 10 may have a cross-sectional shape that matches the cross-sectional shape of the inlet face of the filter 2. The flow conduit 10 may have a size that matches the size of the inlet face of the filter 2.

[0085] The spray device 7 may extend into the flow conduit 10. One or more outlets of the spray device 7 may be located within the flow conduit 10. For example, the nozzle 25 may be located in an upper region of the flow conduit 10. The nozzle 25 may be located in line with the longitudinal axis of the filter 2.

[0086] The inlet face of the filter 2 may be located 10-80 cm, preferably 15-20 cm, from the spraying device, for example from the nozzle 25 of the spraying device 7. Additionally or alternatively, the spraying device may be located at a distance from the inlet face of the filter 2, for example from the nozzle 25 of the spraying device 7, up to four times the diameter of the inlet face 2 of the filter.

[0087] A vacuum generator 6 is provided for establishing a primary gas flow, in use, through the porous structure of the filter 2 by applying a reduced pressure to the outlet face of the filter 2. The vacuum generator 6 may include a vacuum cone 40 which may define a funnel for engaging the outlet face of the filter 2. The inflatable lower seal bladder 30 may form a seal between the outlet face of the filter 2 and the vacuum cone 40. The vacuum generator 6 may include a vacuum pump 42 connected to the flow cone by a conduit 43. The vacuum pump 42 may be controlled to control the volumetric flow rate of the primary gas stream.

[0088] The vacuum generator 6 may include a volumetric flow sensor, which may be an orifice plate 44 in combination with a pressure sensor 45 disposed along the conduit 43. The vacuum generator 6 may include a bypass conduit 46 that extends to an intake port 47.

[0089] The apparatus 1 may further comprise a pressure sensor 41 for monitoring the back pressure of the filter 2. A single pressure sensor 41 may be used. The single pressure sensor 41 may be located in the vacuum generator 6, preferably in a filter holder or other housing of the vacuum generator, such as the vacuum cone 40.

[0090] The controller 9 controls the operation of at least the vacuum generator 6 and the spray device 7. In Figure 1, for clarity, the operational connections between the controller 9 and the remainder of the device 1 have been omitted. However, a person skilled in the art will recognise that any suitable means may provide the necessary connections. Such connections may be wired or wireless.

[0091] The controller 9 may be configured to control the transfer of the dry powder 4 from the reservoir 3 to the spray device 7 by the transport device 8 independently of controlling the primary gas flow generated by the vacuum generator 6. For example, the controller 9 may control the operation of the dosing device 15.

[0092] The controller 9 may be configured to control the spraying of the dry powder 4 toward the inlet face of the filter 2 independently of controlling the primary gas flow. The use of the term "independently" herein refers to the ability of the controller 9 to control each of the variables of the spraying of the dry powder 4 and the primary gas flow individually and without regard to the state of the other variable. For example, the controller 9 may establish the primary gas flow without simultaneously spraying the dry powder 4. For example, the controller 9 may increase or decrease the spray rate of the dry powder 4 without changing the volumetric flow rate of the primary gas flow. For example, the controller 9 may increase or decrease the volumetric flow rate of the primary gas flow without changing the spray rate of the dry powder 4. For example, the controller 9 may control the operation of the spray device 7 independently of controlling the operation of the vacuum pump 42.

[0093] The controller 9 may be configured to activate the vacuum generator 6 to establish a primary gas flow before the dry powder 4 is transferred to the spray device 7 and sprayed towards the inlet face of the filter 2 .

[0094] The controller 9 may be configured to control the secondary gas flow generator, e.g., compressor 22, independently of the vacuum generator 6. The controller 9 may be configured to operate the vacuum generator 6 to maintain the primary gas flow as a continuous gas flow through the porous structure, and to operate the secondary gas flow generator, e.g., compressor 22, only for a portion of the period of the primary gas flow.

[0095] The controller 9 may be configured to control the vacuum generator 6 to control the level of reduced pressure applied to the outlet face of the filter 2 independently of controlling the transport device 8 and / or the spray device 7 to control the rate or mass fraction of the dry powder 4 sprayed towards the inlet face of the filter 2.

[0096] The controller 9 may be configured to stop spraying of the dry powder 4 towards the inlet face of the filter 2 when a predetermined backpressure of the filter 2 is reached, for example as detected by the pressure sensor 41. The predetermined backpressure may be an absolute backpressure or it may be a relative backpressure.

[0097] The controller 9 may be configured to stop spraying of the dry powder 4 towards the inlet face of the filter 2 when a predetermined total spraying time is reached.

[0098] The apparatus 1 may be used to treat a filter with a dry powder 4, which may include one or more refractory powders, preferably one or more fumed refractory powders, and / or one or more aerogels. The one or more fumed refractory powders may include one or more of fumed alumina, fumed silica, fumed titania, other fumed metal oxides, and fumed mixed oxides. The one or more aerogels may include one or more of silica aerogels, alumina aerogels, carbon aerogels, titania aerogels, zirconia aerogels, ceria aerogels, metal oxide aerogels, and mixed oxide aerogels.

[0099] Dry powder 4 is 0.10 g / cm 3Less than, optionally 0.08g / cm 3 Less than, optionally 0.07g / cm 3 Less than, optionally 0.06g / cm 3 Less than, optionally 0.05g / cm 3 The dry powder 4 preferably has a d50 (by volume) of less than 25 micrometers, preferably less than 20 micrometers, more preferably less than 10 micrometers.

[0100] An example of a method for treating a filter according to the present disclosure will now be described with reference to Figure 2, which shows a flow diagram illustrating a method for manufacturing a filter 2 incorporating the use of the apparatus 1. By way of example only, the method will be described with reference to a filter 2 that is provided with a catalytic coating.

[0101] In step S21, a catalyst slurry is prepared by methods well known in the art.

[0102] In step S22, a washcoat is prepared from the catalyst slurry by methods well known in the art. The washcoat may be, for example, a hydrocarbon trap, a three-way catalyst (TWC), a NOx absorbent, an oxidation catalyst, a selective catalytic reduction (SCR) catalyst, a lean NOx catalyst, and combinations of any two or more thereof.

[0103] In step S23, a washcoat is dispensed and applied to the bare filter 2 by methods well known in the art. For example, the washcoat may be applied to a first side (e.g., top side) of the filter 2, and an opposite second side (e.g., bottom side) of the filter 2 may be exposed to at least a partial vacuum to effect migration of the washcoat through the porous structure of the filter 2. The filter 2 may be coated in one dispense, or the washcoat may be applied to the filter 2 in a single step while the filter 2 remains in one orientation. Alternatively, the filter 2 may be coated in two dispenses. For example, in the first dispense, the filter 2 may be in a first orientation with the first side on top and the second side on the bottom. A coating may be applied to the first side, coating a portion of the length of the filter 2. The filter 2 may then be turned upside down so that the second side is on top. A coating may then be applied to the second side to coat the portions of the filter 2 that were not coated by the first dispense. Advantageously, the two dispense process allows different coatings to be applied to each end of the filter 2.

[0104] In step S24, the filter 2 may be dried.

[0105] In step S25, the filter 2 may be fired by methods well known in the art.

[0106] In optional step S26, the back pressure of the filter 2 before processing may be measured.

[0107] In optional step S27, filter 2 can be stocked to await processing. Filter 2 can then be removed from stock and proceeded to processing in step S28. Alternatively, filter 2 can be processed immediately, i.e., proceeding directly to step S29 for processing.

[0108] In step S29, Filter 2 is processed in accordance with the present disclosure, as described in more detail below with reference to FIG.

[0109] In step S30, after processing, the filter 2 may be fired by methods well known in the art.

[0110] In an optional step S31, the back pressure of the filter 2 after treatment may be measured.

[0111] In step S32, the completed filter 2 may be prepared for delivery to a customer.

[0112] FIG. 3 shows a flow diagram illustrating the process of step S29 in FIG.

[0113] In step S29-1, a filter may be loaded into the filter holder 5. The filter 2 may be held in a stationary position during processing. The filter 2 may be gripped by the filter holder 5 at the top and / or bottom ends of the filter 2. The inflatable top seal bladder 31 and the inflatable bottom seal bladder 30 may be inflated to contact and / or engage an outer surface of the filter 2. The filter 2 may be held in a vertical orientation with the inlet face of the filter uppermost. The operation of the filter holder 5, such as the inflation of the inflatable top seal bladder 31 and the inflatable bottom seal bladder 30, may be controlled by the controller 9.

[0114] In step S29-2, the vacuum generator 6 may be activated by the controller 9 to establish a primary gas flow through the filter 2. Preferably, the primary gas flow is established before the dry powder 4 is transferred to the sprayer 7 and sprayed towards the inlet face of the filter 2. The level of reduced pressure generated by the vacuum generator 6 may be controlled by the controller 9 independently of the rate or mass rate of the dry powder 4 being transferred from the reservoir 3 to the sprayer 7. The primary gas flow may be greater than 10 m 3 / hour ~5,000m 3 / hour, preferably 400m 3 / hour ~2,000m 3 / hour, preferably 600m 3 / hour~1000m 3 / time volume flow rate.

[0115] In step S29-3, the backpressure of filter 2 may be measured after the primary gas flow is established and before the secondary gas flow is established. The backpressure may be measured by use of pressure sensor 41. The backpressure measurement in step S29-3 may be in addition to or instead of the backpressure measurement in step S26. Alternatively, the backpressure measurement in step S26 may be used instead of the backpressure measurement in step S29-3. The backpressure measurement in step S26 and / or the backpressure measurement in step S29-3 may be used by controller 9 as a measure of the first backpressure of filter 2 before processing.

[0116] In step S29-4, the dry powder 4 is sprayed by the spraying device 7 onto the inlet face of the filter 2. The dry powder 4 can be fed to the spraying device 7 by the transport device 8 while the dry powder 4 is being sprayed.

[0117] The spray of dry powder 4 towards the inlet face of the filter 2 is preferably controllable by a controller 9 independently from establishing and controlling the primary gas flow.

[0118] During step S29-4, the dry powder 4 may be transferred from the reservoir 3 to the spraying device 7 using a secondary gas flow separate from the primary gas flow, for example provided by the compressor 22. Preferably, the secondary gas flow is controllable by the controller 9 independently of the primary gas flow. For example, the controller 9 may control the operation of the compressor 22 and / or the valves and / or nozzles 25 of the spraying device 7 independently of controlling the operation of the vacuum pump 42. The dry powder 4 may be sprayed towards the inlet face of the filter 2 by use of a secondary gas flow. The secondary gas flow may comprise a compressed gas flow, preferably a compressed air flow.

[0119] During step S29-4, the primary gas flow is preferably maintained as a continuous flow. During step S29-4, the secondary gas flow may be applied as a single burst or multiple intermittent bursts.

[0120] In step S29-5, the back pressure of the filter 2 may be monitored. The back pressure may be monitored by use of pressure sensor 41. The controller 9 may be configured to stop spraying of the dry powder 4 towards the inlet face of the filter 2 when a predetermined back pressure is reached. If the predetermined back pressure has not yet been reached, the controller 9 is configured to return to step S29-4 to continue spraying of the dry powder 4. This feedback may be continuous and need not involve any pause in the spraying of the dry powder 4, i.e. the controller 9 may continuously monitor the back pressure of the filter 2 while the spraying of the dry powder 4 is in progress.

[0121] The predetermined back pressure may be an absolute back pressure. The absolute back pressure may be 600 m 3 The flow rate can be 20-180 mbar / hour.

[0122] Alternatively, the predetermined backpressure may be a relative backpressure. For example, the backpressure relative to the first backpressure of the filter 2 before processing measured in step S26 and / or step S29-3 may be used. The backpressure may be measured as a percentage of the first backpressure. The predetermined backpressure when the spraying of the dry powder 4 is stopped may be 105% to 200%, preferably 125% to 150%, of the first backpressure.

[0123] Additionally or alternatively, spraying of the dry powder 4 towards the inlet face of the filter 2 may be stopped when a predetermined total spraying time is reached. The predetermined total spraying time may be between 1 and 60 seconds, preferably between 1 and 10 seconds, preferably between 1 and 5 seconds, preferably between 2 and 5 seconds, preferably 3 seconds.

[0124] The controller 9 can be configured to stop spraying of the dry powder 4 towards the inlet face of the filter 2 either when a predetermined total spray time or a predetermined back pressure of the filter is first reached, or when a target mass of dry powder has been sprayed towards the inlet face of the filter.

[0125] In step S29-6, the spraying of the dry powder 4 is stopped. For example, this may be achieved by the controller 9 stopping the transfer of the dry powder by the transport device 8 and / or stopping the secondary gas flow of the spraying device 7. Preferably, in step S29-6, the primary gas flow through the porous structure of the filter 2 is maintained for a period of time after the spraying of the dry powder 4 has stopped. The controller 9 may be configured to operate the vacuum generator 6 for a period of time after the spraying of the dry powder 4 has stopped.

[0126] Optionally, in step S29-6, the amount of dry powder 4 delivered towards the inlet face of the filter 2 may be measured. The controller 9 is configured to determine the delivered amount of dry powder 4 from a signal output from the dosing device 15, for example from an output from a loss-in-weight feeder.

[0127] The method may be configured to deliver a maximum loading of filter 2 of less than 10 g / L of dry powder 4 , preferably less than 5 g / L of dry powder 4 , preferably less than 2 g / L of dry powder 4 .

[0128] In step S29-7, the primary gas flow through filter 2 is stopped. This may be accomplished by the controller 9 shutting down the vacuum generator 6, i.e., by shutting down the vacuum pump 42. Alternatively, this may be accomplished by the controller manipulating a valve on the vacuum generator 6 to divert suction through bypass conduit 46 and draw air through inlet 47. This eliminates the need to shut down the vacuum pump 42 between processing of successive filters 2, allowing for faster cycle times.

[0129] In step S29-8, the filter 2 is released from the filter holder 5, for example by deflating the upper and lower inflatable seal bladder 31, 30. The filter 2 can then be removed and processing can proceed to step S30 as described above.

[0130] FIG. 4 is a graph showing the soot load-back pressure response curves of a reference filter that is not treated with fireproofing power and two example filters (Example A and Example B) that are treated with fireproofing powder. The reference filter shows a back pressure response that increases sharply with respect to soot load from the beginning to about 0.4 g / L. After that, the response curve becomes a substantially linear load-back pressure response for soot loads above about 0.4 g / L. In comparison, the filters of Example A and Example B show a substantially linear load-back pressure response for soot loads only above 0.1 g / L. Furthermore, the absolute back pressure at a particular soot load level is significantly less than the reference filter. As a result, the treated filters of Example A and Example B have a substantially linear back pressure-soot load response, except for a very small initial soot load of only about 0.05 g / L.

[0131] In accordance with the present disclosure, a processing filter may be provided that has one or more advantages over prior art filters. Preferably, but not by way of limitation, the processing filter may be processed in accordance with the present disclosure and / or may be processed using an apparatus in accordance with the present disclosure. EXAMPLES

[0132] Standard Attachment Process In the following examples, unless otherwise specified, the treatment filters were impregnated with refractory powder using the type of apparatus shown in FIG. 1 and the following "standard" impregnation process. 1 The diameter of the flow conduit was the same as the inlet face of the filter. 2. 550m of air 3 The primary gas flow / hour was pulled through the filter using a downstream regenerative blower. 3 Backpressure was monitored with a Wika® P30 pressure transmitter located below the filter. 4 The refractory powder was dispersed into the primary gas stream using a STAR Professional gravity feed spray gun 1.4 mm, part number STA2591100C. The STAR Professional gravity feed spray gun was mounted 100 mm from the inlet face of the filter. 5 After the impregnation was completed, the filter was baked at 500°C for 1 hour.

[0133] When the back pressure parameter was used to determine when to stop spraying the refractory powder, the back pressure was monitored using the pressure transmitter described above.When the mass of refractory powder sprayed was used to determine when to stop spraying the refractory powder, the mass was monitored by periodically removing the spray gun hopper for weighing.

[0134] In the following examples, "CFBP" is 600m 3 The filtration efficiencies refer to cold flow backpressure (mbar) at 1000 s / hr and all filtration efficiencies are given at a soot loading of 0.02 g / L.

[0135] refractory powder In the examples below, the following refractory powders were used: 1 Aeroxide® Alu 130 fumed aluminum oxide available from Evonik Industries AG, Essen, Germany. The tap density was 0.05 g / L and the d50 was 5.97 micrometers. 2 Silica aerogel. The tap density was less than 0.10 g / L and the d50 was less than 10 micrometers. Silica aerogel is available, for example, from The Dow Chemical Company, Midland, MI, USA, Enersens SAS, Bourgoin Jallieu, France, and JIOS Aerogel Corporation, Gyeonggi-do, Korea. 3 AEI zeolite. The tap density was 0.30 g / L and the d50 was 0.9 micrometers.

[0136] Examples 1 and 2 Three SCRF filters were prepared from the same SiC, 300 / 12, and 3.76 L substrate types. Each filter was loaded with the same small pore Cu-exchanged zeolite SCR catalyst at 1.93 g / in 3The filters of Example 1 and Example 2 were impregnated with Aeroxide® Alu 130 as described above using the standard impregnation process described above, using back pressure to determine when to stop spraying the refractory powder. The filter of Comparative 1 was not impregnated with any refractory powder. The following results were obtained:

[0137] [Table 1]

[0138] As can be seen from the results, the treatment of the filter according to the present disclosure results in a substantial improvement in the initial filtration efficiency of the filter.In particular, the inventors have found that the treatment of the filter with a refractory powder having a tap density of less than 0.10 g / L can obtain a substantial improvement in filtration efficiency even at a very low loading level of less than 3 g / L.Without being bound by theory, it is believed that the refractory powder, preferably aerosol-deposited, provides the filter with a highly efficient filter medium even at a very low soot loading level during initial use, when soot particulate cake has not yet accumulated, and after regeneration, if appropriate.

[0139] Examples 3 and 4 Three GPF filters were prepared from the same cordierite, 300 / 8, 1.26L substrate type. Each filter was 14.8 g / ft 3 Using the same TWC catalyst with a PGM loading of 1.1 g / in and a PGM ratio of 0:10:1 (Pt:Pd:Rh), 3 The filters of Example 3 and Example 4 were impregnated with the silica aerogel described above using the standard impregnation process described above, using back pressure to determine when to stop spraying the refractory powder. The filter of Comparative Example 2 was not impregnated with any refractory powder. The following results were obtained:

[0140] [Table 2]

[0141] As can be seen from the results, treatment of the filter according to the present disclosure resulted in a substantial improvement in the initial filtration efficiency of the filter. In particular, the inventors have found that treatment of the filter with a refractory powder having a tap density of less than 0.10 g / L can result in a substantial improvement in filtration efficiency even at very low loading levels of less than 2 g / L.

[0142] Example 5 Two SCRF filters were prepared from the same SiC, 300 / 12, 3.00 L substrate type. Each filter was loaded with the same small pore Cu-exchanged zeolite SCR catalyst at 1.52 g / in 3 The Example 5 filter was impregnated with the AEI zeolite described above using the standard impregnation process described above, using the mass of refractory powder to determine when to stop spraying the refractory powder. The Comparative 3 filter was not impregnated with any refractory powder. The following results were obtained:

[0143] [Table 3]

[0144] As can be seen from the results, the use of a refractory powder with a relatively high tap density of 0.30 g / L (outside the scope of this disclosure) in the filter of Example 5 does not achieve the same substantial increase in filtration efficiency as shown by Examples 1-4. The inventors theorize that using a refractory powder with a very low tap density of less than 0.10 g / L is particularly beneficial. This is especially true when the primary gas flow is used to pull the powder through the filter. It is theorized that the very low tap density of the refractory powder, and therefore the very low momentum of the refractory powder particles, promotes better dispersion of the powder in the primary gas flow and in the porous substrate, and is particularly beneficial for depositing a greater proportion of the refractory powder within the porous structure of the multiple filter walls.

[0145] Example 6 An SCRF filter was prepared from the same SiC, 300 / 12, 3.76 L substrate type as in Examples 1 and 2. The filter was then cooled to 1.93 g / in using the same small pore Cu-exchanged zeolite SCR catalyst as in Examples 1 and 2. 3 The filter of Example 6 was impregnated with Aeroxide® Alu130, as described above, using a modified impregnation process. The modified impregnation process was the same as the standard impregnation process described above, except that no primary gas flow was used to draw the powder into the filter. Instead, only a secondary gas flow from the spray gun was used to blow the powder into the filter. This secondary gas flow was approximately 3.5 m 3 / hour. The mass of the refractory powder was used to determine the stopping point of the spraying of the refractory powder. The following results were obtained:

[0146] [Table 4]

[0147] During the powder impregnation of Example 6, it was observed that there was significant backflow / turbulence visible on the inlet face of the filter, as seen from the movement of the powder in the gas stream. At the end of the impregnation, it was further observed that there was powder accumulation on the inlet face of the filter. When split in half, it was observed that there was significant powder accumulation filling the inlet channel at the outlet end of the filter. It is theorized that the effect of the primary gas flow in Examples 1 and 2, combined with the very low tap density of the refractory powder, promotes better distribution of the powder in the primary gas flow and in the porous substrate, and is particularly beneficial for depositing a greater proportion of the refractory powder within the porous structure of the multiple filter walls. Without the primary gas flow, as in Example 6, the powder has a deleterious tendency to accumulate on the inlet face and at the outlet end of the clogged inlet channel. As a result, the incorporation of the refractory powder into the primary gas flow that is pulled through the filter promotes better distribution of the powder within the porous structure of the multiple filter walls.

[0148] Example 7 Two filters were prepared from the same substrate type, cordierite, 200 / 8, 3.2L, respectively. Neither filter was coated with a washcoat, i.e., the substrate was left bare. The filter of Example 7 was impregnated with the silica aerogel described above using a modified impregnation process. The modified impregnation process was the same as the standard impregnation process described above, except that the refractory powder was dispersed in the primary gas stream using a mesh sieve rather than a spray gun. The mass of the refractory powder was used to determine when the spraying of the refractory powder was stopped. The filter of Comparative 4 was not impregnated with any refractory powder. The following results were obtained:

[0149] [Table 5]

[0150] As can be seen from the results, treatment of the filters according to the present disclosure resulted in a substantial improvement in the initial filtration efficiency of the filters, even when bare, uncoated filters were used.

[0151] Examples 8 and 9 An SCRF filter was prepared from the same SiC, 300 / 12, 3.76 L substrate type as in Examples 1 and 2. The filter was then cooled to 1.93 g / in using the same small pore Cu-exchanged zeolite SCR catalyst as in Examples 1 and 2. 3 The filters of Example 8 were impregnated with Aeroxide® Alu 130 using the standard impregnation process described above. Back pressure was used to determine when to stop spraying the refractory powder.

[0152] GPF filters were prepared from the same 300 / 8, 1.26 L substrate type as in Examples 3 and 4. The filters contained 14.8 g / ft 3 and a PGM ratio of 0:10:1 (Pt:Pd:Rh). 3The filters of Example 9 were impregnated with Aeroxide® Alu 130 using the standard impregnation process described above. Back pressure was used to determine when to stop spraying the refractory powder.

[0153] The following results were obtained.

[0154] [Table 6]

[0155] The envelope volume was calculated using Mercury Intrusion Porometry (MIP), with the following results:

[0156] [Table 7]

[0157] Next, the powder 壁内 The percentage was calculated using the following formula:

[0158]

number

[0159] The results are shown in Table 1. 壁内 % was 50.6% in Example 9 and 70.1% in Example 10, proving that the method and apparatus of the present disclosure are effective in obtaining filters in which more than 40% of the refractory powder is disposed within the porous structure of the filter walls.

[0160] Examples 10 to 13 Six GPF filters were prepared from substrate types of cordierite, 300 / 8, and 1.68L, respectively. Three filters had low average pore size and three had high average pore size. As used herein, "high average pore size" refers to a filter average pore size that is more than 2 micrometers above the nominal or average average pore size of the substrate type (as quoted by the substrate manufacturer). Similarly, as used herein, "low average pore size" refers to a filter average pore size that is more than 2 micrometers below the nominal or average average pore size of the substrate type (as quoted by the substrate manufacturer).

[0161] Each filter was packed in the same 22g / ft 3 and a PGM ratio of 0:20:2 (Pt:Pd:Rh) of 0.8 g / in 3 Example Filters 10-13 were impregnated with the above silica aerogel using the standard impregnation process described above. Example Filters 10 and 12 used back pressure to determine when to stop spraying the refractory powder. Example Filters 11 and 13 used the mass of the refractory powder to determine when to stop spraying the refractory powder. Comparative Filters 5 and 6 did not have any refractory powder impregnated. The following results were obtained:

[0162] [Table 8]

[0163] As can be seen from the results, the treatment of the filter according to the present disclosure has resulted in a substantial improvement in the initial filtration efficiency. In addition, the treatment can reduce the variation in the filter back pressure, thus reducing the effect of the change in average pore size on the filter back pressure. For example, it can be seen that the CFBP of comparative filters 5 and 6 differs by more than 27%. In comparison, the CFBP of example filters 10 and 12 differs by only 7%, but still achieves the same 96.8% filtration efficiency improvement. Thus, the results demonstrate that the method and apparatus of the present disclosure are effective in obtaining a reduction in the relative standard deviation of the filter back pressure, even when the filter has a variation in average pore size.

[0164] Further aspects and embodiments of the present disclosure are described in the following sections. Clause A1. A method of treating a filter for filtering particulate matter from an exhaust gas, comprising: a) containing a dry powder in a reservoir; b) placing a filter in a filter holder, the filter comprising a porous substrate having an inlet face and an outlet face, the inlet face and the outlet face being separated by a porous structure; c) establishing a primary gas flow through the porous structure of the filter by applying a reduced pressure to the outlet face of the filter; d) transferring the dry powder from the reservoir to a spray device located upstream of the inlet face of the filter; e) using a spray device to spray a dry powder towards the inlet face of the filter, whereby the dry powder is entrained in the primary gas flow and passes through the inlet face of the filter into contact with the porous structure.

[0165] Clause A2. The method of clause A1, wherein the transfer of the dry powder from the reservoir to the spraying device is controllable independently of the establishment and control of the primary gas flow, and optionally, the spraying of the dry powder towards the inlet face of the filter is controllable independently of the establishment and control of the primary gas flow.

[0166] Clause A3. The method of clause A1 or clause A2, wherein a primary gas flow is established before the dry powder is transferred to the atomizer and sprayed towards the inlet face.

[0167] Clause A4. The method of any of clauses A1-A3, wherein in step d) a secondary gas flow separate from the primary gas flow is used to transport the dry powder from the reservoir to the spray device.

[0168] Clause A5. The method of clause A4, wherein the secondary gas flow is controllable independently of the primary gas flow.

[0169] Clause A6. The method according to clause A4 or clause A5, further comprising step f) of stopping the spraying of the dry powder towards the inlet face of the filter, wherein the primary gas flow is a continuous gas flow from step c) to step f) and the secondary gas flow is applied only for a portion of the period from step c) to step f).

[0170] Clause A7. The method of clause A6, wherein the secondary gas flow is applied as a single burst or multiple intermittent bursts during a portion of the period from step c) to step f) above.

[0171] Clause A8. The method of clause A6 or clause A7, further comprising the step g) of maintaining a primary gas flow through the porous structure of the filter for a period of time after cessation of spraying of the dry powder in step f).

[0172] Clause A9. The method of any one of clauses A4-A8, wherein the secondary gas stream comprises a compressed gas stream, preferably a compressed air stream.

[0173] Clause A10. The method of any one of clauses A4-A9, wherein a secondary gas flow is used to transport the dry powder from the reservoir to the atomizer and to dispense the dry powder from the atomizer.

[0174] Clause A11. The method of any one of clauses A4 to A10, wherein the spray device is a compressed air gun.

[0175] Clause A12. The method of any of clauses A1-A11, comprising using a vacuum generator to establish a primary gas flow through the porous structure of the filter.

[0176] Clause A13. The method of clause A12, wherein the level of reduced pressure generated by the vacuum generator is controllable independently of the rate or mass rate of transfer of the dry powder from the reservoir to the atomizing device.

[0177] Article A14. Primary gas flow is 10m 3 / hour ~5,000m3 / hour, preferably 400m 3 / hour ~2,000m 3 / hour, preferably 600m 3 / hour~1000m 3 The method according to any of clauses A1 to A13, having a volumetric flow rate of 1 / hour.

[0178] Clause A15. The method of any of clauses A1-A14, further comprising monitoring the back pressure of the filter during at least step e).

[0179] Clause A16. The method of clause A15, further comprising using a pressure sensor, preferably a single pressure sensor, to monitor the backpressure.

[0180] Clause A17. The method of clause A16, wherein the pressure sensor, preferably a single pressure sensor, is disposed in a filter holder or other housing fluidly connected to the outlet face of the filter.

[0181] Clause A18. The method of any one of clauses A15-A17, further comprising the step of ceasing spraying of the dry powder towards the inlet face of the filter when a predetermined back pressure in the filter is reached.

[0182] Clause A19. The method of clause A18, wherein the predetermined backpressure is an absolute backpressure.

[0183] Clause A20. The method of any one of clauses A15-A19, further comprising monitoring the back pressure of the filter during at least step c) and step e), preferably during at least steps c), d) and e).

[0184] Clause A21. The method of clause A20, further comprising using a pressure sensor, preferably a single pressure sensor, to monitor the backpressure.

[0185] Clause A22. The method of clause A21, wherein the pressure sensor, preferably a single pressure sensor, is disposed in a filter holder or other housing fluidly connected to the outlet face of the filter.

[0186] Clause A23. The method of clause A21 or clause A22, wherein the same pressure sensor, preferably the same single pressure sensor, is used to monitor the back pressure of the filter during at least steps c) and e).

[0187] Clause A24. The method of any one of clauses A20-A23, further comprising the step of ceasing spraying of the dry powder towards the inlet face of the filter when a predetermined back pressure in the filter is reached.

[0188] Clause A25. The method of clause A24, wherein the predetermined backpressure is a relative backpressure.

[0189] Clause A26. The method of clause A25, wherein a first backpressure of the filter is measured in step c) before the dry powder is deposited on the porous structure, and a second backpressure of the filter is measured in step e) while the dry powder is being deposited on the porous structure, and spraying of the dry powder is stopped when the second backpressure reaches a predetermined percentage of the first backpressure.

[0190] Clause A27. The method according to clause A26, wherein the predetermined percentage is between 105% and 200%, preferably between 125% and 150%.

[0191] Clause A28. The method of any one of clauses A1-A14, further comprising the step of ceasing spraying of the dry powder towards the inlet face of the filter when a predetermined total spraying time has been reached.

[0192] Clause A29. The method according to clause A28, wherein the predetermined total spray time is from 1 to 60 seconds, preferably from 1 to 10 seconds, preferably from 1 to 5 seconds, preferably from 2 to 5 seconds, preferably from 3 seconds.

[0193] Clause A30. The method of any of clauses A1-A29, further comprising the step of ceasing spraying of the dry powder towards the inlet face of the filter when a target mass of dry powder has been sprayed towards the inlet face of the filter.

[0194] Clause A31. The method of any one of clauses A1-A14, further comprising monitoring the back pressure of the filter during at least step e) and ceasing spraying of the dry powder towards the inlet face of the filter when either a predetermined total spray time or a predetermined back pressure of the filter is reached first.

[0195] Clause A32. The method of clause A31, wherein the predetermined backpressure is an absolute backpressure.

[0196] Clause A33. The method of clause A31 or clause A32, further comprising monitoring the back pressure of the filter during at least steps c) and e), preferably during at least steps c), d) and e).

[0197] Clause A34. The method of clause A33, wherein the predetermined backpressure is a relative backpressure.

[0198] Clause A35. The method of any of clauses A1-A34 comprising providing a maximum filter loading of less than 10 g / L of dry powder, preferably less than 5 g / L of dry powder, preferably less than 2 g / L of dry powder.

[0199] Article A36. Dry powders have a density of 0.10 g / cm 3 Less than, optionally 0.08g / cm 3 Less than, optionally 0.07g / cm 3 Less than, optionally 0.06g / cm 3 Less than, optionally 0.05g / cm 3 The method of any of clauses A1-A35, wherein the dry powder has a tap density of less than 25 micrometers, preferably less than 20 micrometers, more preferably less than 10 micrometers.

[0200] Clause A37. The method of any of clauses A1-A36, wherein the dry powder comprises one or more refractory powders, preferably one or more fumed refractory powders, and / or one or more aerogels.

[0201] Clause A38. The method of clause A37, wherein the one or more fumed refractory powders include one or more of fumed alumina, fumed silica, fumed titania, other fumed metal oxides, and fumed mixed oxides.

[0202] Clause A39. The method of clause A37, wherein the one or more aerogels include one or more of silica aerogels, alumina aerogels, carbon aerogels, titania aerogels, zirconia aerogels, ceria aerogels, metal oxide aerogels, and mixed oxide aerogels.

[0203] Clause A40. The method of any of clauses A1-A39, wherein in step e) the dry powder is sprayed from one or more outlets of a spray device.

[0204] Clause A41. The method of clause A40, wherein one or more outlets of the spray device have an opening size of 1-10 mm.

[0205] Clause A42. The method of clause A40 or clause A41, wherein the dry powder is sprayed from one or more fixed outlets of the spray device.

[0206] Clause A43. The method of clause A40 or clause A41, wherein the dry powder is sprayed from one or more moving outlets of the spray device, preferably from one or more vibrating outlets.

[0207] Clause A44. The method of any of clauses A1-A43, further comprising in step e) delivering dry powder from a spray device within the flow conduit to the inlet face of the filter.

[0208] Clause A45. The method of clause A44, wherein the flow conduit provides an unobstructed flow path between the spray device and the inlet face of the filter.

[0209] Clause A46. The method of clause A44, wherein the flow conduit comprises a flow conditioner interposed between the atomizer and the inlet face of the filter, the flow conditioner serving to promote dispersion of the dry powder within the gas stream.

[0210] Clause A47. The method of clause A46, wherein the flow conditioner comprises one or more of a static mixer, a mesh, a sieve, a baffle, and an orifice plate.

[0211] Clause A48. The method according to any of clauses A1 to A47, wherein the inlet face of the filter is located 10 to 80 cm, preferably 15 to 20 cm, from the spraying device and / or the spraying device is located at a distance from the inlet face of the filter up to 4 times the diameter of the inlet face of the filter.

[0212] Clause A49. The method of any of clauses A1-A48, further comprising in step d) dispensing dry powder from a reservoir.

[0213] Clause A50. The method of clause A49, wherein dosing includes dosing by one or more of weight, volume, number of particles, and time.

[0214] Clause A51. A method according to clause A49 or clause A50 comprising gravimetrically feeding dry powder to a dosing device.

[0215] Clause A52. The method according to any one of clauses A49 to A52, wherein the feeding uses a loss-in-weight feeder.

[0216] Clause A53. The method of any of clauses A1-A52, wherein in step a) the dry powder is contained in one or more hoppers.

[0217] Clause A54. The method according to any of clauses A1-A53, wherein in step b) the filter is placed in the holder in a vertical orientation with the inlet surface uppermost.

[0218] Clause A55. The method according to clause A54, wherein in step d) the spraying device is positioned vertically above the inlet face, and preferably the spraying direction of the spraying device is coaxial with the longitudinal axis of the filter, and preferably the spraying direction and the longitudinal axis are coincident.

[0219] Clause A56. The method of any of clauses A1-A55, further comprising after step e) baking the filter.

[0220] Clause A57. The method of any of clauses A1-A56, further comprising coating the filter with a washcoat, preferably a catalytic washcoat, prior to step b).

[0221] Clause A58. The method of any of clauses A1-A57, wherein the porous substrate is a wall-flow filter.

[0222] Clause B1. A device for treating a filter for filtering particulate matter from exhaust gas, comprising: i) a reservoir for containing a dry powder; ii) a filter holder for holding a filter, the filter being of a type comprising a porous substrate having an inlet face and an outlet face, the inlet face and the outlet face being separated by a porous structure; iii) a vacuum generator for establishing, in use, a primary gas flow through the porous structure of the filter by applying a reduced pressure to an outlet face of the filter; iv) a transport device for transporting the dry powder from the reservoir towards the filter; iv) a spraying device for receiving the dry powder from the transport device and spraying the dry powder towards the inlet face of the filter; v) a controller configured to control operation of at least the vacuum generator and the spray device.

[0223] Clause B2. The apparatus of clause B1, wherein the controller is configured to control the transfer of dry powder from the reservoir to the spraying device by the transport device independently of controlling the primary gas flow generated by the vacuum generator, and optionally, the controller is configured to control spraying of the dry powder toward the inlet face of the filter independently of controlling the primary gas flow.

[0224] Clause B3. The apparatus of clause B1 or clause B2, wherein the controller is configured to activate the vacuum generator to establish a primary gas flow before the dry powder is transferred to the atomizer and atomized towards the inlet surface.

[0225] Clause B4. An apparatus according to any one of clauses B1 to B3, wherein the transport device and / or the spray device comprises a secondary gas flow generator separate from the vacuum generator, which assists in the transfer of the dry powder to the spray device.

[0226] Clause B5. The apparatus of clause B4, wherein the controller is configured to control the secondary gas flow generator independently of the vacuum generator.

[0227] Clause B6. The apparatus of clause B4 or clause B5, wherein the controller is configured to operate the vacuum generator to maintain the primary gas flow as a continuous gas flow through the porous structure and to operate the secondary gas flow generator only during a portion of the period of the primary gas flow.

[0228] Clause B7. The apparatus of clause B6, wherein the controller is configured to operate the secondary gas flow generator in a single burst or multiple intermittent bursts during the period of the primary gas flow.

[0229] Clause B7. The apparatus of any one of clauses B4-B6, wherein the secondary gas flow generator comprises a compressed gas generator, preferably a compressed air generator.

[0230] Clause B8. An apparatus according to any one of clauses B4 to B7, wherein the spray device is a compressed air gun.

[0231] Clause B9. An apparatus as described in any one of clauses B1 to B8, wherein the controller is configured to control the vacuum generator to control the level of reduced pressure applied to the outlet face of the filter independently of controlling the transport device and / or the spray device to control the rate or mass fraction of dry powder sprayed towards the inlet face of the filter.

[0232] Clause B10. The controller shall 3 / hour ~5,000m 3 / hour, preferably 400m 3 / hour ~2,000m 3 / hour, preferably 600m 3 / hour~1000m 3 The apparatus of any one of clauses B1 to B9, configured to operate the vacuum generator to have a volumetric flow rate of 1 / hour.

[0233] Clause B11. The apparatus of any one of clauses B1-B10, further comprising a pressure sensor, preferably a single pressure sensor, for monitoring back pressure of the filter, and the controller configured to receive an output from the pressure sensor.

[0234] Clause B12. The apparatus of clause B11, wherein the pressure sensor, preferably a single pressure sensor, is disposed in the vacuum generator, preferably in a vacuum cone of the vacuum generator.

[0235] Clause B13. The apparatus of clause B11 or clause B12, wherein the controller is configured to stop spraying of the dry powder towards the inlet face of the filter when a predetermined back pressure in the filter is reached.

[0236] Clause B14. The apparatus of clause B13, wherein the predetermined backpressure is an absolute backpressure.

[0237] Clause B15. The apparatus of clause B13, wherein the predetermined backpressure is a relative backpressure.

[0238] Clause B16. The apparatus of clause B15, wherein the controller is configured to acquire a first backpressure of the filter from the pressure sensor before the dry powder is deposited on the porous structure and a second backpressure of the filter from the pressure sensor while the dry powder is deposited on the porous structure, and the controller is configured to stop spraying of the dry powder when the second backpressure reaches a predetermined percentage of the first backpressure.

[0239] Clause B17. The apparatus according to clause B16, wherein the predetermined percentage is between 105% and 200%, preferably between 125% and 150%.

[0240] Clause B18. The apparatus of any one of clauses B1-B17, wherein the controller is configured to stop spraying of the dry powder towards the inlet face of the filter when a predetermined total spraying time is reached.

[0241] Clause B19. The device according to clause B18, wherein the predetermined total spray time is between 1 and 60 seconds, preferably between 1 and 10 seconds, preferably between 1 and 5 seconds, preferably between 2 and 5 seconds, preferably 3 seconds.

[0242] Clause B20. The apparatus of any one of clauses B1-B19, wherein the controller is configured to stop spraying the dry powder towards the inlet face of the filter when a target mass of dry powder has been sprayed towards the inlet face of the filter.

[0243] Clause B21. The apparatus of any one of clauses B1-B20, further comprising a pressure sensor, preferably a single pressure sensor, for monitoring the back pressure of the filter, the controller configured to receive an output from the pressure sensor, and the controller configured to stop spraying of the dry powder towards the inlet face of the filter when either a predetermined total spraying time or a predetermined back pressure of the filter is reached first.

[0244] Clause B22. The apparatus of clause B21, wherein the predetermined backpressure is an absolute backpressure.

[0245] Clause B23. The apparatus of clause B21, wherein the predetermined backpressure is a relative backpressure.

[0246] Clause B24. The apparatus of any one of clauses B1-B23, wherein the reservoir contains a dry powder comprising one or more refractory powders, preferably one or more fumed refractory powders, and / or one or more aerogels.

[0247] Clause B25. The apparatus of clause B24, wherein the one or more fumed refractory powders include one or more of fumed alumina, fumed silica, fumed titania, other fumed metal oxides, and fumed mixed oxides.

[0248] Clause B26. The apparatus of clause B25, wherein the one or more aerogels include one or more of silica aerogel, alumina aerogel, carbon aerogel, titania aerogel, zirconia aerogel, ceria aerogel, metal oxide aerogel, and mixed oxide aerogel.

[0249] Clause B27. The device according to any one of clauses B1 to B26, wherein the spray device comprises one or more outlets.

[0250] Clause B28. The device of clause B27, wherein one or more outlets of the spray device have an opening size of 1-10 mm.

[0251] Clause B29. Apparatus according to clause B27 or clause B28, wherein the one or more outlets are one or more fixed outlets.

[0252] Clause B30. An apparatus according to clause B27 or clause B28, wherein the one or more outlets are one or more movable outlets, preferably one or more vibrating outlets.

[0253] Clause B31. The apparatus of any one of clauses B1-B30, wherein the transport device comprises a conduit extending at least partially from the reservoir to the spraying device, the spraying device including a compressed air supply of a compressed air gun configured to fluidize the dry powder in at least a portion of the conduit.

[0254] Clause B32. The apparatus of any one of clauses B1-B31, further comprising a flow conduit located between the spray device and the inlet face of the filter.

[0255] Clause B33. The apparatus of clause B32, wherein the flow conduit is empty to provide an unobstructed flow path between the spray device and the inlet face of the filter.

[0256] Clause B34. The apparatus of clause B32, wherein the flow conduit comprises a flow conditioner interposed between the atomizing device and the inlet face of the filter, the flow conditioner serving to promote dispersion of the dry powder within the gas stream.

[0257] Clause B35. The apparatus of clause B34, wherein the flow conditioner comprises one or more of a static mixer, a mesh, a sieve, a baffle, and an orifice plate.

[0258] Clause B36. A device according to any one of clauses B1 to B35, wherein the inlet face of the filter is located 10 to 80 cm, preferably 15 to 20 cm, from the spraying device and / or the spraying device is located at a distance from the inlet face of the filter up to 4 times the diameter of the inlet face of the filter.

[0259] Clause B37. The apparatus according to any one of clauses B1 to B36, further comprising a dosing device for dosing dry powder from the reservoir.

[0260] Clause B38. The apparatus of clause B37, wherein the dosing device is configured to dosing by one or more of weight, volume, particle number, and time.

[0261] Clause B39. Apparatus according to clause B37 or B38, wherein the dosing device is a gravimetric dosing device.

[0262] Clause B40. The apparatus according to any one of clauses B37 to B39, wherein the feeding device is a loss-in-weight feeder.

[0263] Clause B41. The apparatus of any one of clauses B1-B40, wherein the reservoir comprises one or more hoppers.

[0264] Clause B42. The apparatus of any one of clauses B1-B41, wherein the filter is disposed in the holder in a vertical orientation with the inlet surface uppermost.

[0265] Clause B43. The device according to clause B42, wherein the spray device is located vertically above the inlet face, and preferably the spray direction of the spray device is coaxial with the longitudinal axis of the filter, and preferably the spray direction and the longitudinal axis are coincident.

[0266] Clause C1. A processing filter obtainable by the method according to any one of clauses A1 to A58.

[0267] Clause C2. The treatment filter of clause C1, wherein the treatment filter is one or more of a catalyzed soot filter (CSF), a selective catalytic reduction filter (SCRF), a lean NOx trap filter (LNTF), and a gasoline particulate filter (GPF).

[0268] Clause D1. A vehicle exhaust filter comprising a porous substrate having an inlet face and an outlet face, the porous substrate comprising an inlet channel extending from the inlet face and an outlet channel extending from the outlet face, the inlet channel and the outlet channel being separated by a plurality of filter walls having a porous structure; Vehicle exhaust filters are 0.10g / cm 3 impregnated with a refractory powder having a tap density before impregnation of less than The vehicle exhaust filter has a mass loading of refractory powder of less than 10 g / L; 1. A vehicle exhaust filter, wherein greater than 40% of a refractory powder is disposed within a porous structure of the plurality of filter walls, and less than 60% of the refractory powder is coated on an exterior surface of the plurality of filter walls.

[0269] Clause D2. The vehicle exhaust filter of clause D1, wherein more than 50% of the refractory powder, optionally more than 65% of the refractory powder, optionally more than 75% of the refractory powder, optionally up to 100% of the refractory powder is disposed within the porous structure of the plurality of filter walls.

[0270] Clause D3. The vehicle exhaust filter of clause D1 or clause D2, wherein a percentage of the refractory powder disposed within the porous structure of the plurality of filter walls is calculated according to the following formula:

[0271]

number

[0272] Article D4. Refractory powder, 0.08 g / cm 3 Less than, optionally 0.07g / cm 3 Less than, optionally 0.06g / cm 3 Less than, optionally 0.05g / cm 3 The vehicle exhaust filter of any one of clauses D1-D3, having a pre-impregnation tap density of less than 1000 nm.

[0273] Clause D5. The vehicle exhaust filter of any one of clauses D1-D4, wherein the mass loading of the fire resistant powder is less than 7 g / L, optionally less than 5 g / L, optionally less than 3 g / L, optionally less than 1 g / L.

[0274] Clause D6. The vehicle exhaust filter of any one of clauses D1-D5, wherein greater than 0.5 g / L of the fire resistant powder is disposed within the porous structure of the plurality of filter walls.

[0275] Clause E1. A vehicle exhaust filter comprising a porous substrate having an inlet face and an outlet face, the porous substrate comprising an inlet channel extending from the inlet face and an outlet channel extending from the outlet face, the inlet channel and the outlet channel being separated by a plurality of filter walls having a porous structure; Vehicle exhaust filters are 0.10g / cm 3 impregnated with a refractory powder having a tap density before impregnation of less than The vehicle exhaust filter has a mass loading of refractory powder of less than 10 g / L; 1. A vehicle exhaust filter, comprising: a refractory powder having greater than 0.5 g / L disposed within a porous structure of a plurality of filter walls.

[0276] Article E2. Refractory powder, 0.08 g / cm 3 Less than, optionally 0.07g / cm 3 Less than, optionally 0.06g / cm 3 Less than, optionally 0.05g / cm 3 The vehicle exhaust filter of claim E1 having a pre-impregnation tap density of less than 100 nm.

[0277] Clause E3. A vehicle exhaust filter as described in clause E1 or E2, wherein the mass loading of the refractory powder is greater than 1 g / L, optionally greater than 3 g / L, optionally greater than 5 g / L, optionally greater than 7 g / L.

[0278] Clause F1. The vehicle exhaust filter of any one of clauses D1-D6 or E1-E3, wherein the refractory powder comprises one or more fumed refractory powders and / or one or more aerogels.

[0279] Clause F2. The vehicle exhaust filter of clause F1, wherein the one or more fumed refractory powders include one or more of fumed alumina, fumed silica, fumed titania, other fumed metal oxides, and fumed mixed oxides.

[0280] Clause F3. The vehicle exhaust filter of clause F1, wherein the one or more aerogels include one or more of silica aerogel, alumina aerogel, carbon aerogel, titania aerogel, zirconia aerogel, ceria aerogel, metal oxide aerogel, and mixed oxide aerogel.

[0281] Clause G1. A vehicle exhaust filter comprising a porous substrate having an inlet face and an outlet face, the porous substrate comprising an inlet channel extending from the inlet face and an outlet channel extending from the outlet face, the inlet channel and the outlet channel being separated by a plurality of filter walls having a porous structure; Vehicle exhaust filters are 0.10g / cm 3 impregnated with a refractory powder having a tap density before impregnation of less than The fire-resistant powder comprises one or more aerogels in a vehicle exhaust filter.

[0282] Clause G2. The vehicle exhaust filter of clause G1, wherein the one or more aerogels include one or more of silica aerogel, alumina aerogel, carbon aerogel, titania aerogel, zirconia aerogel, ceria aerogel, metal oxide aerogel, and mixed oxide aerogel.

[0283] Clause H1. A vehicle exhaust filter comprising a porous substrate having an inlet face and an outlet face, the substrate comprising an inlet channel extending from the inlet face and an outlet channel extending from the outlet face, the inlet channel and the outlet channel being separated by a plurality of filter walls having a porous structure; Vehicle exhaust filters are 0.10g / cm 3 impregnated with a refractory powder having a tap density before impregnation of less than The vehicle exhaust filter has a mass loading of refractory powder of less than 10 g / L; The vehicle exhaust filter exhibits a substantially linear load-backpressure response for soot loads greater than 0.1 g / L, preferably for soot loads greater than 0.05 g / L.

[0284] Clause J1. A vehicle exhaust filter according to any one of clauses D1-D6, or E1-E3, or F1-F3, or G1-G2, H1, having a filtration efficiency of greater than 90%, preferably greater than 95%, preferably greater than 98%, preferably greater than 99% at a soot load of 0.02 g / L.

[0285] Article J2. 600m 3 10. The vehicle exhaust filter of any one of clauses D1-D6, or E1-E3, or F1-F3, or G1-G2, or H1, or J1, having a back pressure of 20-180 mbar at a flow rate of 100 rpm / hour.

[0286] Clause J3. The vehicle exhaust filter according to any one of clauses D1-D6, or E1-E3, or F1-F3, or G1-G2, or H1, or J1-J2, wherein the refractory powder is an aerosol deposited refractory powder, preferably an aerosol deposited dry refractory powder.

[0287] Clause J4. The vehicle exhaust filter of any one of clauses D1-D6, or E1-E3, or F1-F3, or G1-G2, or H1, or J1-J3, wherein the refractory powder has a d50 (by volume) of less than 25 micrometers, preferably less than 20 micrometers, more preferably less than 10 micrometers.

[0288] Clause J5. The vehicle exhaust filter of any one of clauses D1-D6, or E1-E3, or F1-F3, or G1-G2, or H1, or J1-J4 which is a wall-flow filter.

[0289] Clause J6. The vehicle exhaust filter according to any one of clauses D1-D6, or E1-E3, or F1-F3, or G1-G2, or H1, or J1-J5, wherein the vehicle exhaust filter is a fired filter.

[0290] Clause J7. The vehicle exhaust filter of any one of clauses D1-D6, or E1-E3, or F1-F3, or G1-G2, or H1, or J1-J6, wherein the porous substrate comprises one or more washcoats.

[0291] Clause J8. The vehicle exhaust filter of any one of clauses D1-D6, or E1-E3, or F1-F3, or G1-G2, or H1, or J1-J7, wherein the porous substrate comprises an adhesion promoter and / or a binder.

[0292] Clause J9. An exhaust system comprising a vehicle exhaust filter according to any one of clauses D1-D6, or E1-E3, or F1-F3, or G1-G2, or H1, or J1-J8.

[0293] Clause J10. A vehicle comprising a vehicle exhaust filter according to any one of clauses D1 to D6, or E1 to E3, or F1 to F3, or G1 to G2, or H1, or J1 to J8.

[0294] Clause K1. A plurality of vehicle exhaust filters, each vehicle exhaust filter comprising a porous substrate having an inlet face and an outlet face, the porous substrate comprising an inlet channel extending from the inlet face and an outlet channel extending from the outlet face, the inlet channel and the outlet channel being separated by a plurality of filter walls having a porous structure; Each vehicle exhaust filter is 0.10g / cm 3 impregnated with a refractory powder having a tap density before impregnation of less than Each vehicle exhaust filter has a mass loading of fire-resistant powder of less than 10 g / L; Each vehicle exhaust filter is 600m 3 a plurality of vehicle exhaust filters having a backpressure of 20 to 180 mbar at a flow rate of 100 s / hr, and a relative standard deviation of the backpressures of the plurality of vehicle exhaust filters is less than 0.04, preferably less than 0.025.

[0295] Clause K2. The vehicle exhaust filters of clause K1, wherein for each vehicle exhaust filter, more than 40% of the fire-resistant powder is disposed within a porous structure of the plurality of filter walls and less than 60% of the fire-resistant powder is coated on an outer surface of the plurality of filter walls.

[0296] Clause K3. A vehicle exhaust filter according to clause K1 or clause K2, wherein the fire-resistant powder is an aerosol-deposited fire-resistant powder, preferably an aerosol-deposited dry fire-resistant powder.

Claims

1. 1. A vehicle exhaust filter comprising a porous substrate having an inlet face and an outlet face, the porous substrate comprising an inlet channel extending from the inlet face and an outlet channel extending from the outlet face, the inlet channel and the outlet channel being separated by a plurality of filter walls having a porous structure; The vehicle exhaust filter has a resistance of 0.10 g / cm ３ impregnated with a refractory powder having a tap density before impregnation of less than The vehicle exhaust filter has a mass loading of the refractory powder of 0.06 g / L or more and less than 10 g / L; 1. A vehicle exhaust filter, wherein greater than 40% of the refractory powder is disposed within the porous structure of the plurality of filter walls and less than 60% of the refractory powder is coated on an exterior surface of the plurality of filter walls.

2. 2. The vehicle exhaust filter of claim 1, wherein more than 50% of the refractory powder is disposed within the porous structure of the plurality of filter walls, optionally more than 65% of the refractory powder, optionally more than 75% of the refractory powder, optionally up to 100% of the refractory powder.

3. 3. The vehicle exhaust filter of claim 1 or 2, wherein the percentage of the refractory powder disposed within the porous structure of the plurality of filter walls is calculated according to the following formula: [0010]

4. The refractory powder has a density of 0.08 g / cm ３ less than, optionally 0.07 g / cm ３ less than, optionally 0.06 g / cm ３ less than, optionally 0.05 g / cm ３ The vehicle exhaust filter of any one of claims 1 to 3, having a pre-impregnation tap density of less than 100 nm.

5. 5. The vehicle exhaust filter of any one of claims 1 to 4, wherein the mass loading of the refractory powder is less than 7 g / L, optionally less than 5 g / L, optionally less than 3 g / L, optionally less than 1 g / L.

6. The vehicle exhaust filter of any one of claims 1 to 5, wherein greater than 0.5 g / L of said refractory powder is disposed within said porous structure of said plurality of filter walls.

7. 1. A vehicle exhaust filter comprising a porous substrate having an inlet face and an outlet face, the porous substrate comprising an inlet channel extending from the inlet face and an outlet channel extending from the outlet face, the inlet channel and the outlet channel being separated by a plurality of filter walls having a porous structure; The vehicle exhaust filter has a resistance of 0.10 g / cm ３ impregnated with a refractory powder having a tap density before impregnation of less than The vehicle exhaust filter has a mass loading of the refractory powder of 0.06 g / L or more and less than 10 g / L; 13. A vehicle exhaust filter, wherein greater than 0.5 g / L of said refractory powder is disposed within said porous structure of said plurality of filter walls.

8. The refractory powder has a density of 0.08 g / cm ３ less than, optionally 0.07 g / cm ３ less than, optionally 0.06 g / cm ３ less than, optionally 0.05 g / cm ３ 8. The vehicle exhaust filter of claim 7 having a pre-impregnation tap density of less than 1.0 μm.

9. 9. The vehicle exhaust filter of claim 7 or 8, wherein the mass loading of the refractory powder is greater than 1 g / L, optionally greater than 3 g / L, optionally greater than 5 g / L, optionally greater than 7 g / L.

10. The vehicle exhaust filter of any one of claims 1 to 9, wherein the refractory powder comprises one or more fumed refractory powders and / or one or more aerogels.

11. 11. The vehicle exhaust filter of claim 10, wherein the one or more fumed refractory powders include one or more of fumed alumina, fumed silica, fumed titania, other fumed metal oxides, and fumed mixed oxides.

12. 11. The vehicle exhaust filter of claim 10, wherein the one or more aerogels comprise one or more of silica aerogel, alumina aerogel, carbon aerogel, titania aerogel, zirconia aerogel, ceria aerogel, metal oxide aerogel, and mixed oxide aerogel.

13. 1. A vehicle exhaust filter comprising a porous substrate having an inlet face and an outlet face, the porous substrate comprising an inlet channel extending from the inlet face and an outlet channel extending from the outlet face, the inlet channel and the outlet channel being separated by a plurality of filter walls having a porous structure; The vehicle exhaust filter has a resistance of 0.10 g / cm ３ impregnated with a refractory powder having a tap density before impregnation of less than The vehicle exhaust filter has a mass loading of the refractory powder of 0.06 g / L or more and less than 10 g / L; 1. A vehicle exhaust filter, wherein the refractory powder comprises one or more aerogels.

14. 14. The vehicle exhaust filter of claim 13, wherein the one or more aerogels comprise one or more of silica aerogel, alumina aerogel, carbon aerogel, titania aerogel, zirconia aerogel, ceria aerogel, metal oxide aerogel, and mixed oxide aerogel.

15. 1. A vehicle exhaust filter comprising a porous substrate having an inlet face and an outlet face, the porous substrate comprising an inlet channel extending from the inlet face and an outlet channel extending from the outlet face, the inlet channel and the outlet channel being separated by a plurality of filter walls having a porous structure; The vehicle exhaust filter has a resistance of 0.10 g / cm ３ impregnated with a refractory powder having a tap density before impregnation of less than The vehicle exhaust filter has a mass loading of the refractory powder of 0.06 g / L or more and less than 10 g / L; The vehicle exhaust filter exhibits a substantially linear load-backpressure response for soot loads greater than 0.1 g / L, preferably for soot loads greater than 0.05 g / L.

16. A vehicle exhaust filter according to any one of the preceding claims having a filtration efficiency of more than 90%, preferably more than 95%, preferably more than 98%, preferably more than 99% at a soot loading of 0.02g / L.

17. 600m ３ 17. A vehicle exhaust filter according to any one of claims 1 to 16 having a back pressure of 20 to 180 mbar at a flow rate of 1 / hr.

18. A vehicle exhaust filter according to any one of claims 1 to 17, wherein the refractory powder is an aerosol deposited refractory powder, preferably an aerosol deposited dry refractory powder.

19. A vehicle exhaust filter according to any one of the preceding claims, wherein the refractory powder has a d50 (by volume) of less than 25 micrometers, preferably less than 20 micrometers, more preferably less than 10 micrometers.

20. A vehicle exhaust filter according to any preceding claim which is a wall-flow filter.

21. A wall-flow filter according to any one of claims 1 to 20 which is an asymmetric wall-flow filter.

22. The vehicle exhaust filter according to any one of claims 1 to 21, wherein the vehicle exhaust filter is a sintered filter.

23. The vehicle exhaust filter of any one of claims 1 to 22, wherein the porous substrate comprises one or more washcoats.

24. The vehicle exhaust filter of any one of claims 1 to 23, wherein the porous substrate comprises an adhesion promoter and / or a binder.

25. An exhaust system comprising a vehicle exhaust filter according to any one of the preceding claims.

26. A vehicle comprising a vehicle exhaust filter according to any one of claims 1 to 24.

27. A plurality of vehicle exhaust filters, each vehicle exhaust filter comprising a porous substrate having an inlet face and an outlet face, the porous substrate comprising an inlet channel extending from the inlet face and an outlet channel extending from the outlet face, the inlet channel and the outlet channel separated by a plurality of filter walls having a porous structure; Each vehicle exhaust filter has a density of 0.10 g / cm ３ impregnated with a refractory powder having a tap density before impregnation of less than Each vehicle exhaust filter has a mass loading of said refractory powder equal to or greater than 0.06 g / L and less than 10 g / L; Each vehicle exhaust filter is 600m ３ 13. A plurality of vehicle exhaust filters having a backpressure of 20-180 mbar at a flow rate of 100 / hr, and a relative standard deviation of said backpressures for said plurality of vehicle exhaust filters is less than 0.04, preferably less than 0.

025.

28. 30. The plurality of vehicle exhaust filters of claim 27, wherein for each vehicle exhaust filter, greater than 40% of the fire resistant powder is disposed within the porous structure of the plurality of filter walls and less than 60% of the fire resistant powder is coated on an exterior surface of the plurality of filter walls.

29. 29. A plurality of vehicle exhaust filters according to claim 27 or 28, wherein the refractory powder is an aerosol deposited refractory powder, preferably an aerosol deposited dry refractory powder.

Images