Adhesive composition, adhesive layer, and adhesive sheet

Abstract

The present invention pertains to: an adhesive agent composition that includes a compound having a substituent represented by general formula (1) described in the specification, the distance between the oxygen atom of -OR1 and the oxygen atom of -OR2 being 1.31-4.70 Å (inclusive), where R1 and R2 each represent hydrogen atoms in the substituent represented by general formula (1); an adhesive agent layer composed of the adhesive agent composition; and an adhesive sheet equipped with the adhesive agent layer.

Description

[Technical field]

[0001] The present invention relates to a pressure-sensitive adhesive composition, a pressure-sensitive adhesive layer comprising the pressure-sensitive adhesive composition, and a pressure-sensitive adhesive sheet comprising the pressure-sensitive adhesive layer. [Background technology]

[0002] 2. Description of the Related Art Conventionally, adhesives and pressure-sensitive adhesives have been used for bonding and fixing in various fields, and efforts are underway to develop adhesives that exhibit sufficient adhesive strength even to adherends in a wet state, where it is difficult to obtain sufficient adhesive strength.

[0003] For example, Patent Document 1 describes a curable resin composition containing a boronic acid derivative with a specific structure, which has good adhesion to a substrate and is capable of forming an adhesive layer with excellent water resistance even under harsh conditions such as a condensation environment or immersion in water. Patent Document 2 describes a pressure-sensitive adhesive that quickly adheres to a wet or dry substrate surface, comprising a polymerization product of a hydrophilic acidic comonomer and a non-reactive plasticizer, and a method for producing the same. Furthermore, Patent Document 3 describes a polymer that can be used as an underwater adhesive, in which at least three types of side chains are bonded to a main chain made of polyacrylate. Non-Patent Document 1 describes a copolymer of catechol and an acrylic monomer that can be used as an underwater adhesive. [Prior art documents] [Patent documents]

[0004] [Patent Document 1] Japanese Patent Application Publication No. 2017-194633 [Patent Document 2] Japan Special Publication No. 2017-514005 [Patent Document 3] Japanese Patent Application Publication No. 2012-233059 [Non-patent literature]

[0005] [Non-Patent Document 1] Polym. Chem., 2017, 8, 1654-1663 Summary of the Invention [Problem to be solved by the invention]

[0006] Patent Document 1 studies a curable resin composition capable of forming an adhesive layer that has excellent water resistance even under conditions such as condensation or immersion in water. However, there is room for improvement with respect to the adhesive strength to adherends in a wet state, such as adherends in water, and there is a demand for the development of a pressure-sensitive adhesive layer that exhibits sufficient adhesive strength to adherends in a wet state.

[0007] Therefore, an object of the present invention is to provide a pressure-sensitive adhesive composition that contains a compound having a specific substituent and thereby exhibits high adhesive strength to an adherend in water or in a wet state, a pressure-sensitive adhesive layer made of the pressure-sensitive adhesive composition, and a pressure-sensitive adhesive sheet comprising the pressure-sensitive adhesive layer. [Means for solving the problem]

[0008] The present inventors have conducted extensive research with the aim of providing a pressure-sensitive adhesive composition that exhibits high adhesion to an adherend in water or in a wet state, and have come up with the idea of ​​using a compound containing a substituent capable of chemically bonding with an adherend as one component of the pressure-sensitive adhesive composition that forms the pressure-sensitive adhesive layer. As a result, they have found that in order to obtain a pressure-sensitive adhesive layer that exhibits high adhesion to an adherend in a wet state and is peelable, it is important that the pressure-sensitive adhesive composition contains a compound containing a substituent with a hydroxyl group distance in a specific range, and have completed the present invention. That is, the present invention is as follows.

[0009] [1] The compound includes a compound having a substituent represented by the following general formula (1): In the substituent represented by the general formula (1), R 1 and R 2 -OR where each represents a hydrogen atom 1 Oxygen atom and -OR2 The pressure-sensitive adhesive composition according to claim 1, wherein the distance between the oxygen atom and the

[0010] [ka]

[0011] (In general formula (1), L represents an aryl group, a phosphorus atom, or a boron atom. R 1 and R 2 each independently represents a hydrogen atom, or an aliphatic hydrocarbon group, an aryl group, or a heterocyclic group which may have a substituent. [2] The pressure-sensitive adhesive composition according to [1], wherein the compound is a polymer containing a structure derived from compound A represented by the following general formula (2) or compound B represented by the following general formula (3):

[0012] [ka]

[0013] In the general formulas (2) and (3), X is a functional group containing a reactive group, and R 1 and R 2 each independently represents a hydrogen atom, or an aliphatic hydrocarbon group, an aryl group, or a heterocyclic group which may have a substituent; and M represents a phosphorus atom or a boron atom. [3] The pressure-sensitive adhesive composition according to [1] or [2], wherein the compound is a polymer containing a structure derived from a (meth)acrylic acid ester monomer having a homopolymer glass transition temperature of 10° C. or lower. [4] The pressure-sensitive adhesive composition according to [2] or [3], wherein the polymer is a copolymer of 90 to 99 parts by mass of at least one (meth)acrylic acid ester monomer and 1 to 10 parts by mass of the compound A or the compound B, and a homopolymer of the (meth)acrylic acid ester monomer has a glass transition temperature of 10°C or lower. [5] R 1 and the above R2 and each of them is a hydrogen atom. [6] The pressure-sensitive adhesive composition according to any one of [2] to [5], wherein the X is a functional group having at least one hydrogen donor group selected from the group consisting of an acrylic group, a methacrylic group, or an organic group having an active methylene group. [7] A pressure-sensitive adhesive layer comprising the pressure-sensitive adhesive composition according to any one of [1] to [6]. [8] An adhesive sheet comprising the adhesive layer according to [7]. [9] The pressure-sensitive adhesive sheet according to [8], wherein the pressure-sensitive adhesive layer is formed on a substrate. Effect of the Invention

[0014] According to the present invention, it is possible to provide a pressure-sensitive adhesive composition that exhibits high adhesive strength to an adherend in water or in a wet state, a pressure-sensitive adhesive layer made of the pressure-sensitive adhesive composition, and a pressure-sensitive adhesive sheet including the pressure-sensitive adhesive layer. [Brief description of the drawings]

[0015] [Figure 1] FIG. 1 is an example of a schematic cross-sectional view of a pressure-sensitive adhesive sheet according to an embodiment of the present invention. [Diagram 2] FIG. 2 is an example of a schematic cross-sectional view of a pressure-sensitive adhesive sheet according to an embodiment of the present invention. [Diagram 3] FIG. 3 is an example of a schematic cross-sectional view of a pressure-sensitive adhesive sheet according to an embodiment of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0016] Hereinafter, an embodiment of the present invention will be described in detail. Note that the present invention is not limited to the embodiment described below.

[0017] The pressure-sensitive adhesive composition according to the embodiment of the present invention is 1 -OR 2 (R 1 and R2 each independently represents a hydrogen atom, or an aliphatic hydrocarbon group, an aryl group, or a heterocyclic group, each of which may have a substituent; 1 -OR 2 In the substituent containing 1 and R 2 -OR where each represents a hydrogen atom 1 Oxygen atom and -OR 2 The distance between the oxygen atom of (hereinafter, sometimes referred to as the "distance between OO") is 1.31 Å or more and 4.70 Å or less.

[0018] The pressure-sensitive adhesive layer according to the embodiment of the present invention is made of the pressure-sensitive adhesive composition according to the embodiment of the present invention. Moreover, the pressure-sensitive adhesive sheet according to the embodiment of the present invention includes the pressure-sensitive adhesive layer according to the embodiment of the present invention, and the pressure-sensitive adhesive layer is preferably formed on a substrate. In this specification, the term "adhesive sheet" may include what are called "adhesive tape," "adhesive label," "adhesive film," and the like. The "adhesive surface" refers to the surface of the adhesive sheet that is attached to an adherend (application surface). The adhesive sheet of the present invention may have an adhesive surface on only one side or on both sides. Also, "distance between OO" means -OR 1 -OR 2 -OR in substituents containing 1 Oxygen atom and -OR 2 The distance between the oxygen atom and the molecule is calculated by the molecular modeling method MOPAC (Molecular Orbital PACkage). WINMOSTAR (V9,2,3 for 64bit Windows) was used as the calculation program for MOPAC.

[0019] FIG. 1 is an example of a schematic cross-sectional view of a pressure-sensitive adhesive sheet according to an embodiment of the present invention. The pressure-sensitive adhesive sheet 10 of the present embodiment comprises a substrate 11 and a pressure-sensitive adhesive layer 12 , and the surface of the pressure-sensitive adhesive layer 12 opposite the substrate 11 may be releasably covered with a release liner 13 . The pressure-sensitive adhesive sheet 10 of the present embodiment is used by peeling off and removing the release liner 13, and attaching it to an adherend via the pressure-sensitive adhesive layer 12. That is, in the pressure-sensitive adhesive layer 12 of the present embodiment, the surface facing the release liner 13 is the pressure-sensitive adhesive surface.

[0020] The pressure-sensitive adhesive sheet according to the embodiment of the present invention may comprise pressure-sensitive adhesive layers on both sides of a substrate as shown in FIG. 2, and the pressure-sensitive adhesive layers may be protected by a release liner. Adhesive sheet 30 of the present embodiment may comprise, in this order, first release liner 33A, first adhesive layer 32A, substrate 31, second adhesive layer 32B, and second release liner 33B. The pressure-sensitive adhesive sheet 30 of this embodiment is used by peeling off and removing the first release liner 33A and the second release liner 33B, and attaching the first pressure-sensitive adhesive layer 32A and the second pressure-sensitive adhesive layer 32B to different adherends. That is, in this embodiment, both the surface of the first pressure-sensitive adhesive layer 32A facing the first release liner 33A and the surface of the second pressure-sensitive adhesive layer 32B facing the second release liner 33B are adhesive surfaces.

[0021] In this embodiment, the substrate 31, the first and second pressure-sensitive adhesive layers 32A and 32B, and the first and second release liners 33A and 33B are the same as the substrate 11, the pressure-sensitive adhesive layer 12, and the release liner 13 described above.

[0022] Furthermore, the adhesive sheet 30 of the present embodiment may be rolled up. That is, the adhesive sheet 30 of the present embodiment may not include the second release liner 33B, for example, and may be rolled up so that the adhesive surface of the second adhesive layer 32B is attached to the surface of the first release liner 33A opposite to the first adhesive layer 32A.

[0023] The pressure-sensitive adhesive sheet according to the embodiment of the present invention may not include a substrate as shown in FIG. 3, and both sides of the pressure-sensitive adhesive layer may be protected by release liners. That is, adhesive sheet 40 of the present embodiment may comprise first release liner 43A, adhesive layer 42, and second release liner 43B in this order. The pressure-sensitive adhesive sheet 40 of the present embodiment is used by peeling off and removing the first release liner 43A and the second release liner 43B, and attaching one side and the other side of the pressure-sensitive adhesive layer 42 to different adherends. That is, in the present embodiment, both the side of the pressure-sensitive adhesive layer 42 facing the first release liner 43A and the side of the pressure-sensitive adhesive layer 42 facing the second release liner 43B are adhesive surfaces.

[0024] The pressure-sensitive adhesive composition that forms the pressure-sensitive adhesive layer 12 of this embodiment will be described in detail below.

[0025] [Adhesive composition] The pressure-sensitive adhesive composition in this embodiment contains a compound having a substituent represented by general formula (1) (hereinafter referred to as compound Z), and R 1 and R 2 -OR where each represents a hydrogen atom 1 Oxygen atom and -OR 2 The distance between the oxygen atom of (hereinafter, sometimes referred to as the distance between OO) is 1.31 Å or more and 4.70 Å or less.

[0026] [ka]

[0027] (In general formula (1), L represents an aryl group, a phosphorus atom, or a boron atom. R 1 and R 2 each independently represents a hydrogen atom, or an aliphatic hydrocarbon group, an aryl group, or a heterocyclic group which may have a substituent.

[0028] When the distance between O--O in the substituents of the compound according to this embodiment is 1.31 Å or more and 4.70 Å or less, excellent adhesive strength can be exhibited through hydrogen bonding with the adherend, and high adhesive strength can be expressed not only to wet surfaces but also to adherends in water.

[0029] The compound Z may be a monomer or a polymer. If it is a polymer, it may be -OR 1-OR 2 It is preferable that the polymer has a structure derived from a monomer having a substituent containing the following formula: Among them, it is more preferable that the polymer has a substituent represented by the following formula (1) in the side chain.

[0030] [ka]

[0031] (In general formula (1), L represents an aryl group, a phosphorus atom, or a boron atom. R 1 and R 2 each independently represents a hydrogen atom, or an aliphatic hydrocarbon group, an aryl group, or a heterocyclic group which may have a substituent.

[0032] Examples of the aryl group represented by L include a phenyl group having 6 to 20 carbon atoms which may have a substituent, and a naphthyl group having 10 to 20 carbon atoms which may have a substituent. R 1 and R 2 Examples of the aliphatic hydrocarbon group represented by include a linear or branched alkyl group having 1 to 20 carbon atoms which may have a substituent, a cyclic alkyl group having 3 to 20 carbon atoms which may have a substituent, and an alkenyl group having 2 to 20 carbon atoms, examples of the aryl group include a phenyl group having 6 to 20 carbon atoms which may have a substituent, and a naphthyl group having 10 to 20 carbon atoms which may have a substituent, and examples of the heterocyclic group include a 5- or 6-membered ring group which contains at least one hetero atom and may have a substituent. These may be linked to each other to form a ring.

[0033] In general formula (1), R 1 and R 2 is preferably a hydrogen atom or a linear or branched alkyl group having 1 to 3 carbon atoms, and most preferably a hydrogen atom. R 1 and R 2 When represents a hydrogen atom, the hydrogen bonding property becomes strong, and strong adhesiveness is obtained. For example, if the adherend contains oxygen atoms, the oxygen atoms in the adherend and -OR 1 -OR2 The adhesive composition is easily hydrogen bonded. 1 AND -OR 2 By including a polymer having a substituent group including -OR 1 AND -OR 2 It is possible to exert excellent adhesive strength through hydrogen bonding between the adhesive and the adherend, and it is possible to exert high adhesive strength not only to wet surfaces but also to adherends in water.

[0034] When the pressure-sensitive adhesive sheet 10 of the present embodiment is applied to a wet surface of an adherend, the pressure-sensitive adhesive composition (pressure-sensitive adhesive layer 12) is converted into -OR 1 -OR 2 However, by forming hydrogen bonds with the surface of the adherend, the adhesive strength to the adherend is improved. As a result, high adhesive strength can be exhibited not only to wet surfaces but also to adherends in water. When compound Z is capable of chemically bonding with the adherend, it is preferable because the adhesive strength to the adherend is further improved by the progress of chemical bonding between compound Z capable of chemically bonding with the adherend contained in the adhesive composition (adhesive layer 12) and the adherend.

[0035] From the viewpoint of hydrogen bonding with the adherend, compound Z is preferably a polymer containing a structure derived from a compound having two hydroxyl groups in the molecule. Specifically, compound Z is preferably a polymer containing a structure derived from compound A represented by the following general formula (2) or compound B represented by the following general formula (3), and more preferably a polymer containing a structure derived from compound A represented by general formula (2). The pressure-sensitive adhesive composition according to the embodiment of the present invention preferably contains a structure derived from compound A, which strengthens hydrogen bonds with the adherend.

[0036] [ka]

[0037] (In the above general formula, X is a functional group containing a reactive group, and R 1 and R2 each independently represents a hydrogen atom, or an aliphatic hydrocarbon group, an aryl group, or a heterocyclic group which may have a substituent; and M represents a phosphorus atom or a boron atom.

[0038] When M in compound A represented by general formula (2) represents boron, the distance between O--O is 2.26 Å, and when M in compound A represented by general formula (2) represents phosphorus atom, the distance between O--O is 2.94 Å. In addition, the distance between O--O in compound A represented by general formula (3) is 2.77 Å.

[0039] <Compound A> Compound A is represented by the following general formula (2). Compound A may be used as compound Z, or may be used as a raw material monomer when compound Z is a polymer containing a structure derived from compound A.

[0040] [ka]

[0041] (In the above general formula (2), X is a functional group containing a reactive group, and R 1 and R 2 each independently represents a hydrogen atom, or an aliphatic hydrocarbon group, an aryl group, or a heterocyclic group which may have a substituent; and M represents a phosphorus atom or a boron atom.

[0042] R in general formula (2) 1 and R 2 R in general formula (1) 1 and R 2 The same is true for the preferred ones.

[0043] X in compound A is a functional group containing a reactive group (hereinafter may be referred to as functional group X), which is a functional group that can react with other curable components contained in the pressure-sensitive adhesive composition. Examples of the reactive group contained in the functional group X include a hydroxyl group, an amino group, an aldehyde, a carboxyl group, a vinyl group, a (meth)acrylic group, a styryl group, a (meth)acrylamide group, an organic group having an ether bond (e.g., a vinyl ether group, an epoxy group, an oxetane group), a mercapto group, an amino group, an active methylene group, and a benzyl group. The reactive group contained in the functional group X may be a hydrogen donor group. The hydrogen donor group is a functional group having a structure in which hydrogen in the molecule is abstracted by the action of a polymerization initiator having a hydrogen abstracting action, and a free radical is generated. Specific examples of the hydrogen donor group include a mercapto group, an amino group, an active methylene group, a benzyl group, a hydroxyl group, and an organic group having an ether bond. The reactive group contained in the functional group X is preferably a functional group containing at least one reactive group selected from the group consisting of an acrylic group, a methacrylic group, and an active methylene group.

[0044] When the compound Z used in the adhesive composition is active energy ray curable, the reactive group contained in the functional group X is preferably at least one reactive group selected from the group consisting of vinyl group, (meth)acrylic group, styryl group, (meth)acrylamide group, vinyl ether group, epoxy group, oxetane group and mercapto group, and particularly when the compound Z is radical polymerizable, the reactive group contained in X is preferably at least one reactive group selected from the group consisting of (meth)acrylic group, styryl group and (meth)acrylamide group, and when the compound A has a (meth)acrylamide group, it is more preferable because it has high reactivity and increases the copolymerization rate with the active energy ray curable resin composition. In addition, it is also preferable from the viewpoint that the effect of the present invention can be efficiently obtained because the polarity of the (meth)acrylamide group is high and the adhesiveness is excellent. When compound Z used in the pressure-sensitive adhesive composition is cationically polymerizable, the reactive group contained in functional group X preferably has at least one functional group selected from a hydroxyl group, an amino group, an aldehyde, a carboxyl group, a vinyl ether group, an epoxy group, an oxetane group, and a mercapto group. In particular, when the functional group X has an epoxy group, this is preferred because the resulting pressure-sensitive adhesive layer will have excellent adhesion to the adherend, and when the functional group X has a vinyl ether group, this is preferred because the pressure-sensitive adhesive composition will have excellent curability.

[0045] The reactive group contained in the functional group X is preferably linked to the phosphorus atom or boron atom represented by M via a linking group. Examples of the linking group include a phenylene group, an alkylene group, a tolylene group, a naphthylene group, and a bisphenylene group, and a phenylene group or an alkylene group is preferable. Moreover, M in the general formula (2) preferably represents a boron atom.

[0046] Examples of the alkylene group include linear or branched alkylene groups having 1 to 10 carbon atoms (preferably 2 to 6), such as ethylene, propylene, trimethylene, tetramethylene, pentamethylene, and hexamethylene groups.

[0047] The compound A represented by the general formula (2) is preferably represented by the following general formula (2-1).

[0048] [ka]

[0049] (In the above general formula, Y is a phenylene group or an alkylene group, and X 1 represents a reactive group, R 1 and R 2 is the same as above.)

[0050] Examples of the alkylene group represented by Y include linear or branched alkylene groups having 1 to 10 carbon atoms (preferably 2 to 6), such as ethylene, propylene, trimethylene, tetramethylene, pentamethylene, and hexamethylene. X 1 The reactive group represented by may be the same as the reactive group contained in the above-mentioned X, and preferred examples thereof are also the same.

[0051] More preferable examples of compound A include the following compounds (1a) to (1d).

[0052] [ka]

[0053] In the present invention, the compound A may be one in which a reactive group and a boron atom are directly bonded, but as shown in the above specific example, it is preferable that the compound A is one in which a reactive group and a boron atom are bonded via a linking group such as a phenylene group or an alkylene group, that is, a compound represented by general formula (2-1). When the compound A does not have a boron-oxygen bond, but has a boron atom bonded to a phenylene group or an alkylene group, and thus has a boron-carbon bond and a reactive group (general formula (2-1)), it is preferable because the adhesion water resistance is improved. Furthermore, in the present invention, even if Compound A is one in which a reactive group and a boron atom are bonded via an organic group having 1 to 20 carbon atoms which may have a substituent, this is still preferred because it improves the adhesive water resistance of the pressure-sensitive adhesive layer obtained after curing. Examples of the organic group having 1 to 20 carbon atoms which may have a substituent include a linear or branched alkylene group having 1 to 20 carbon atoms which may have a substituent, a cyclic alkylene group having 3 to 20 carbon atoms which may have a substituent, a phenylene group having 6 to 20 carbon atoms which may have a substituent, and a naphthylene group having 10 to 20 carbon atoms which may have a substituent.

[0054] In addition to the compounds exemplified above, examples of compound A include esters of (meth)acrylates and boric acid, such as esters of hydroxyethylacrylamide and boric acid, esters of methylol acrylamide and boric acid, esters of hydroxyethyl acrylate and boric acid, and esters of hydroxybutyl acrylate and boric acid.

[0055] <Compound B> Compound B is preferably represented by the following general formula (3). Compound B may be used as compound Z, or may be used as a raw material monomer when compound Z is a polymer containing a structure derived from compound B.

[0056] [ka]

[0057] (In the above general formula, X represents a functional group containing a reactive group.) X in the general formula (3) has the same meaning as X in the general formula (2), and the preferred meanings are also the same. The compound B represented by the general formula (3) is preferably represented by the following general formula (3-1).

[0058] [ka]

[0059] (In the above general formula, Y is a phenylene group or an alkylene group, and X 1 represents a reactive group.)

[0060] X in general formula (3-1) 1 and Y is X in general formula (2-1). 1 and Y, and the preferred examples thereof are also the same.

[0061] In the pressure-sensitive adhesive composition, the content of compound Z is more than 0% by mass, and from the viewpoint of elastic modulus, it is preferably 1% by mass or more, more preferably 3% by mass or more, and is preferably 35% by mass or less, more preferably 33% by mass or less, and even more preferably 30% by mass or less.

[0062] When compound A is used as compound Z, the content of compound A in the pressure-sensitive adhesive composition is preferably 1% by mass or more, more preferably 3% by mass or more, from the viewpoint of elastic modulus, and is preferably 10% by mass or less, more preferably 5% by mass or less.

[0063] When compound B is used as compound Z, the content of compound (B) in the pressure-sensitive adhesive composition is preferably 1% by mass or more, more preferably 3% by mass or more, from the viewpoint of elastic modulus, and is preferably 10% by mass or less, more preferably 5% by mass or less.

[0064] (Base polymer) In the pressure-sensitive adhesive composition according to the present embodiment, a known polymer used in pressure-sensitive adhesives can be used as the base polymer. Here, the base polymer refers to the main component of the polymer contained in the pressure-sensitive adhesive composition. In addition, in this specification, the "main component" refers to a component contained in an amount of more than 50 mass % unless otherwise specified. The base polymer may be a polymer containing a structure derived from compound Z, and more preferably is a copolymer of a monomer component constituting a known polymer and a monomer having a substituent represented by general formula (1), i.e., compound Z as a monomer. Alternatively, a mixture of a polymer containing a structure derived from compound Z and a known polymer may be used as the base polymer.

[0065] The base polymer contained in the pressure-sensitive adhesive composition in this embodiment is not particularly limited, and examples thereof include acrylic polymers, rubber polymers, vinyl alkyl ether polymers, silicone polymers, polyester polymers, polyamide polymers, urethane polymers, fluorine polymers, epoxy polymers, etc. Among the above-listed polymers, acrylic polymers and rubber polymers are preferred from the viewpoint of adhesiveness, and acrylic polymers are more preferred from the viewpoint of adhesiveness.

[0066] The acrylic polymer is a polymer containing a (meth)acrylic acid ester as a main monomer component, and one containing an alkyl (meth)acrylate ester (an alkyl (meth)acrylate ester having a linear or branched alkyl group) as a main monomer component can be suitably used. Examples of the alkyl (meth)acrylate ester include methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, isopropyl (meth)acrylate, butyl (meth)acrylate, isobutyl (meth)acrylate, s-butyl (meth)acrylate, t-butyl (meth)acrylate, pentyl (meth)acrylate, isopentyl (meth)acrylate, hexyl (meth)acrylate, heptyl (meth)acrylate, octyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, isooctyl (meth)acrylate, ...ethyl (meth)acrylate, ethyl (meth)acrylate, ethyl (meth)acrylate, ethyl (meth)acrylate, ethyl (meth)acrylate, ethyl (meth)acrylate, ethyl (meth)acrylate, ethyl ( Examples of the alkyl (meth)acrylate esters include alkyl (meth)acrylate esters having an alkyl group having 1 to 20 carbon atoms, such as nonyl acrylate, isononyl (meth)acrylate, decyl (meth)acrylate, isodecyl (meth)acrylate, undecyl (meth)acrylate, dodecyl (meth)acrylate, tridecyl (meth)acrylate, tetradecyl (meth)acrylate, pentadecyl (meth)acrylate, hexadecyl (meth)acrylate, heptadecyl (meth)acrylate, octadecyl (meth)acrylate, nonadecyl (meth)acrylate, and eicosyl (meth)acrylate. Among these, alkyl (meth)acrylate esters having an alkyl group having 1 to 14 carbon atoms are preferred, and alkyl (meth)acrylate esters having an alkyl group having 2 to 10 carbon atoms are more preferred. The above-mentioned "(meth)acrylic acid ester" refers to "acrylic acid ester" and / or "methacrylic acid ester", and the same applies to others.

[0067] Examples of (meth)acrylic acid esters other than the above-mentioned (meth)acrylic acid alkyl esters include (meth)acrylic acid esters having an alicyclic hydrocarbon group, such as cyclopentyl (meth)acrylate, cyclohexyl (meth)acrylate, and isobornyl (meth)acrylate, and (meth)acrylic acid esters having an aromatic hydrocarbon group, such as phenyl (meth)acrylate.

[0068] The above (meth)acrylic acid esters can be used alone or in combination of two or more thereof. Also, a monomer other than the acrylic monomer may be copolymerized with the (meth)acrylic acid ester.

[0069] In this embodiment, of the monomer components constituting the acrylic polymer, 80% by mass or more is preferably a (meth)acrylic acid alkyl ester, more preferably 90% by mass or more, and even more preferably 95% by mass or more.

[0070] From the viewpoint of elastic modulus, among the above monomer components, a (meth)acrylic acid ester monomer having a homopolymer glass transition temperature (Tg) of 10° C. or less is preferred. As the above monomer component, a (meth)acrylic acid ester monomer having a homopolymer Tg of, more preferably, −20° C. or less, further preferably −50° C. or less is preferred. When the glass transition temperature (Tg) of the homopolymer is 10° C. or lower, the elastic modulus is low, and the effect of good conformability can be obtained even for adherends having uneven surfaces. Here, the "glass transition temperature (Tg) of a homopolymer" means the "glass transition temperature (Tg) of a polymer made solely of a monomer", that is, the glass transition temperature (Tg) of a polymer made solely of a certain monomer as a monomer component.

[0071] It is also preferred that the polymer (base polymer) contained in the pressure-sensitive adhesive composition according to this embodiment is a copolymer of 90 to 99 parts by mass of at least one (meth)acrylic acid ester monomer and 1 to 10 parts by mass of the compound A or the compound B, and that the Tg of a homopolymer of the (meth)acrylic acid ester monomer is 10° C. or lower.

[0072] In addition to the base polymer, polymers such as modifiers (hereinafter also referred to as other polymers) may be contained within the range in which the effects of the present invention are not significantly impaired. In this case, the content ratio of the other polymers to the total base polymer (100 parts by mass) is preferably 75 parts by mass or less, more preferably 60 parts by mass or less.

[0073] The content of the base polymer in the pressure-sensitive adhesive composition according to the present embodiment is not particularly limited, but from the viewpoint of initial adhesive strength, it is preferably 5% by mass or more, more preferably 10% by mass or more, and even more preferably 20% by mass or more, based on the total components of the pressure-sensitive adhesive composition excluding the solvent, i.e., based on the total amount of the components of the pressure-sensitive adhesive composition excluding the solvent. The content of the base polymer is preferably 90% by mass or less, more preferably 80% by mass or less, and even more preferably 70% by mass or less, based on the total components of the pressure-sensitive adhesive composition excluding the solvent.

[0074] The method for obtaining the acrylic polymer is not particularly limited, and various polymerization methods known as a synthesis method for acrylic polymers, such as solution polymerization, emulsion polymerization, bulk polymerization, suspension polymerization, and photopolymerization, can be appropriately adopted. In some embodiments, the solution polymerization method can be preferably adopted. The polymerization temperature when carrying out the solution polymerization can be appropriately selected depending on the type of monomer and solvent used, the type of polymerization initiator, and the like, and can be, for example, about 20°C to 170°C (typically about 40°C to 140°C).

[0075] The initiator used for the polymerization can be appropriately selected from conventionally known thermal polymerization initiators, photopolymerization initiators, etc., depending on the polymerization method. The polymerization initiators can be used alone or in combination of two or more.

[0076] Examples of the thermal polymerization initiator include azo-based polymerization initiators (e.g., 2,2'-azobisisobutyronitrile, 2,2'-azobis-2-methylbutyronitrile, 2,2'-azobis(2-methylpropionic acid) dimethyl, 4,4'-azobis-4-cyanovaleric acid, azobisisovaleronitrile, 2,2'-azobis(2-amidinopropane) dihydrochloride, 2,2'-azobis[2-(5-methyl-2 -imidazolin-2-yl)propane]dihydrochloride, 2,2'-azobis(2-methylpropionamidine)disulfate, 2,2'-azobis(N,N'-dimethyleneisobutylamidine)dihydrochloride, etc.); persulfates such as potassium persulfate; peroxide-based polymerization initiators (e.g., dibenzoyl peroxide, t-butyl permaleate, lauroyl peroxide, etc.); redox-based polymerization initiators, etc. The amount of the thermal polymerization initiator used is not particularly limited, but can be, for example, within the range of 0.01 parts by mass to 5 parts by mass, preferably 0.05 parts by mass to 3 parts by mass, relative to 100 parts by mass of the monomer components used in the preparation of the acrylic polymer.

[0077] The photopolymerization initiator is not particularly limited, but for example, a benzoin ether-based photopolymerization initiator, an acetophenone-based photopolymerization initiator, an α-ketol-based photopolymerization initiator, an aromatic sulfonyl chloride-based photopolymerization initiator, a photoactive oxime-based photopolymerization initiator, a benzoin-based photopolymerization initiator, a benzyl-based photopolymerization initiator, a benzophenone-based photopolymerization initiator, a ketal-based photopolymerization initiator, a thioxanthone-based photopolymerization initiator, an acylphosphine oxide-based photopolymerization initiator, etc. can be used. The amount of the photopolymerization initiator used is not particularly limited, but for example, it can be in the range of 0.01 to 5 parts by mass, preferably 0.05 to 3 parts by mass, relative to 100 parts by mass of the monomer component used in the preparation of the acrylic polymer.

[0078] In some embodiments, the acrylic polymer may be included in the pressure-sensitive adhesive composition for forming the pressure-sensitive adhesive layer in the form of a partially polymerized product (acrylic polymer syrup) obtained by irradiating a mixture of the monomer components as described above with a polymerization initiator with ultraviolet (UV) light to polymerize a part of the monomer components. The pressure-sensitive adhesive composition containing such an acrylic polymer syrup may be applied to a predetermined substrate and irradiated with ultraviolet light to complete the polymerization. That is, the acrylic polymer syrup may be regarded as a precursor of the acrylic polymer.

[0079] The adhesive composition according to the present embodiment may contain a tackifier (tackifier) ​​for the purpose of adjusting the elastic modulus and imparting tackiness during initial adhesion. Examples of tackifiers include polybutenes, rosin-based resins, terpene-based resins, petroleum-based resins (e.g., petroleum-based aliphatic hydrocarbon resins, petroleum-based aromatic hydrocarbon resins, petroleum-based aliphatic-aromatic copolymerized hydrocarbon resins, petroleum-based alicyclic hydrocarbon resins (hydrogenated aromatic hydrocarbon resins), etc.), and coumarone-based resins. In terms of compatibility with the base polymer, petroleum-based resins and rosin-based resins are preferred. One or more types of tackifiers may be used in combination.

[0080] When a tackifier is contained in the pressure-sensitive adhesive composition, the content is preferably 10 parts by mass or more, more preferably 30 parts by mass or more, and even more preferably 50 parts by mass or more relative to 100 parts by mass of the base polymer from the viewpoint of decreasing the elastic modulus. Also, the content of the tackifier is preferably 500 parts by mass or less, more preferably 400 parts by mass or less, and even more preferably 250 parts by mass or less relative to 100 parts by mass of the base polymer from the viewpoint of imparting an appropriate cohesive force to the pressure-sensitive adhesive.

[0081] In addition, the adhesive composition of this embodiment may further contain additives that are typically added to adhesive compositions, such as a viscosity modifier, a release modifier, a plasticizer, a softener, a filler, a colorant (pigment, dye, etc.), an antioxidant, a surfactant, a leveling agent, an antifoaming agent, a light stabilizer, etc., within the range that does not impair the effects of the present invention. Examples of the filler include inorganic fillers such as talc, titanium oxide, calcium oxide, magnesium oxide, zinc oxide, titanium oxide, calcium carbonate, carbon, silica, clay, mica, barium sulfate, whiskers, and magnesium hydroxide. From the viewpoint of rough surface adhesion, the content of the filler is preferably 500 parts by mass or less, and more preferably 300 parts by mass or less, per 100 parts by mass of the base polymer.

[0082] In addition, various common solvents can be used as the solvent (solvent) used in the pressure-sensitive adhesive composition. Examples of the solvent include organic solvents such as esters such as ethyl acetate and n-butyl acetate; aromatic hydrocarbons such as toluene and benzene; aliphatic hydrocarbons such as n-hexane and n-heptane; alicyclic hydrocarbons such as cyclohexane and methylcyclohexane; and ketones such as methyl ethyl ketone and methyl isobutyl ketone. The solvents may be used alone or in combination of two or more.

[0083] In the pressure-sensitive adhesive composition according to the present embodiment, the Young's modulus of the pressure-sensitive adhesive layer at 25°C when the pressure-sensitive adhesive layer is formed is preferably 0.1 kPa or more, more preferably 1 kPa or more, even more preferably 5 kPa or more, and particularly preferably 10 kPa or more. If the Young's modulus is 0.1 kPa or more, the pressure-sensitive adhesive layer is less likely to deform, and the pressure-sensitive adhesive sheet has good shape stability. In addition, problems such as glue overflow due to stress applied after adhesion are less likely to occur. From the viewpoint of adhesion to a wet surface, the Young's modulus is preferably 400 kPa or less, more preferably 200 kPa or less, and more preferably 100 kPa or less. If the Young's modulus is 400 kPa or less, the adhesive can conform well to the rough surface of a wet adherend. In addition, the adhesive can show good adhesive strength and excellent water resistance even when used underwater.

[0084] Here, the Young's modulus of the adhesive layer when it is formed can be calculated from the stress-strain curve measured when a sample is prepared by forming the adhesive layer into a string shape and pulling it at a speed of 50 mm / min using a tensile tester (AG-IS manufactured by Shimadzu Corporation).

[0085] [Adhesive Layer] The pressure-sensitive adhesive layer of the present embodiment is formed using the pressure-sensitive adhesive composition. The forming method is not particularly limited and can adopt a known method, but can be performed according to the manufacturing method of the pressure-sensitive adhesive sheet described below. The preferred range of the amount of each component in the pressure-sensitive adhesive layer is the same as the preferred range of the amount of each component in the pressure-sensitive adhesive composition excluding the solvent.

[0086] The adhesive layer in this embodiment is formed using the above adhesive composition. The formation method is not particularly limited, and a known method can be adopted. For example, the adhesive composition can be applied to a substrate described later using a known coating method, and dried to obtain the form of an adhesive sheet. In addition, the adhesive composition can be applied to a surface having releasability, dried or cured to form an adhesive layer on the surface, and then the adhesive layer can be attached to a non-releasable substrate to be transferred. The method of applying the adhesive composition to the substrate is not particularly limited, and can be performed using, for example, a gravure roll coater, a reverse roll coater, a kiss roll coater, a dip roll coater, a bar coater, a knife coater, a spray coater, a fountain die coater, a closed edge die coater, etc. The drying temperature can be, for example, 50 to 150°C.

[0087] The pressure-sensitive adhesive layer may also be formed by applying the pressure-sensitive adhesive composition to a release liner (which may be a sheet-like substrate having a release surface).

[0088] The thickness of the pressure-sensitive adhesive layer after drying is not particularly limited, but from the viewpoint of exhibiting good conformability to an adherend having an uneven surface, it is preferably 5 to 5000 μm, and more preferably 10 to 1000 μm. The adhesive layer may be formed by a solventless coating method such as rolling or extrusion. In this case, the adhesive composition can be heated and kneaded to obtain a kneaded product. For kneading, for example, a batch type kneader such as a kneader, a Banbury mixer, or a mixing roll, or a continuous kneader such as a biaxial kneader, is used. The heating temperature in kneading can be, for example, 80 to 180°C. The pressure-sensitive adhesive composition obtained as described above can be heated by a molding device such as an extruder, a calendar roll, or a press (heat press) to form the pressure-sensitive adhesive layer 12 into a sheet shape.

[0089] The pressure-sensitive adhesive sheet of the present embodiment has the above-described pressure-sensitive adhesive layer. The concept of adhesive sheet here includes what are called adhesive tapes, adhesive labels, adhesive films, and the like. The pressure-sensitive adhesive sheet of the present embodiment may be a substrate-attached pressure-sensitive adhesive sheet having the pressure-sensitive adhesive layer on one or both sides of a sheet-like substrate (support), or may be a substrate-less pressure-sensitive adhesive sheet having the pressure-sensitive adhesive layer supported on a release liner, for example. The pressure-sensitive adhesive sheet of the present embodiment may also include another pressure-sensitive adhesive layer having a composition different from that of the above-mentioned pressure-sensitive adhesive layer. The adhesive sheet of the present embodiment may be an adhesive sheet with a substrate in a form having another adhesive layer on one or both sides of a sheet-like substrate (support) and having an adhesive layer (wet adhesive layer) according to an embodiment of the present invention on the other adhesive layer. Alternatively, the adhesive sheet may be a substrate-attached adhesive sheet having other adhesive layers on both sides of a sheet-like substrate (support) and a wet adhesive layer on one of the other adhesive layers. The pressure-sensitive adhesive sheet may be a substrate-less pressure-sensitive adhesive sheet having a wet pressure-sensitive adhesive layer on one or both sides of another pressure-sensitive adhesive layer.

[0090] (base material) Examples of materials for forming the substrate include polyolefin films such as polyethylene, polypropylene, and ethylene-propylene copolymers, polyester films such as polyethylene terephthalate, plastic films such as polyvinyl chloride, papers such as craft paper and Japanese paper, fabrics such as cotton cloth and staple cloth, woven fabrics such as polyester nonwoven fabric and vinylon woven fabric, and metal foils. The thickness of the substrate is not particularly limited.

[0091] The plastic film may be a non-stretched film or a stretched (uniaxially or biaxially stretched) film. The surface of the substrate on which the pressure-sensitive adhesive layer is to be provided may be subjected to a surface treatment such as application of a primer or corona discharge treatment.

[0092] In this embodiment, the pressure-sensitive adhesive sheet may be perforated to provide through-holes, which allows moisture on the wet surface of the adherend to escape through the through-holes to the back side of the pressure-sensitive adhesive sheet (the side opposite to the application surface) when the pressure-sensitive adhesive sheet is attached to the adherend, thereby allowing more moisture to be removed from the wet surface of the adherend.

[0093] (Release liner) In the pressure-sensitive adhesive sheet of the present embodiment, the pressure-sensitive adhesive layer according to the embodiment of the present invention and other pressure-sensitive adhesive layers may be protected by a release liner (separator, release film) until use.

[0094] As the release liner, a conventional release paper or the like can be used, and is not particularly limited. For example, a substrate having a release treatment layer, a low adhesion substrate made of a fluorine-based polymer, a low adhesion substrate made of a non-polar polymer, etc. can be used. Examples of substrates having a release treatment layer include plastic films and papers that have been surface-treated with a release treatment agent such as a silicone-based, long-chain alkyl-based, fluorine-based, or molybdenum sulfide-based release treatment agent. Examples of the fluoropolymer of the low-adhesion substrate made of a fluoropolymer include polytetrafluoroethylene, polychlorotrifluoroethylene, polyvinyl fluoride, polyvinylidene fluoride, tetrafluoroethylene-hexafluoropropylene copolymer, and chlorofluoroethylene-vinylidene fluoride copolymer. Examples of the non-polar polymer of the low adhesive substrate made of a non-polar polymer include olefin resins (e.g., polyethylene, polypropylene, etc.). The release liner can be formed by a known or conventional method. The thickness of the release liner is not particularly limited.

[0095] (adherent) The adherend to which the pressure-sensitive adhesive sheet of the present embodiment is attached is not particularly limited, but is preferably one that can form a hydrogen bond with the structure derived from compound Z in the pressure-sensitive adhesive composition (pressure-sensitive adhesive layer). Examples of the adherend include concrete, mortar, asphalt, metals (e.g., SUS plates, Al plates, etc.), wood, tiles, plastic materials (e.g., acrylic plates, bakelite plates, etc.), architectural exterior and interior materials such as coating surfaces and bathroom interior walls, underwater and water surface structures such as ships and buoys, aquariums, bathtubs, sports equipment, etc., fabrics such as woven fabrics and nonwoven fabrics, paper, electrolyte membranes, separation membranes, filters, and other porous bodies, etc. The adherend may also be a living organism, and may be the exterior of the organism (e.g., skin, shell, scales, etc.) or the interior of the organism (e.g., teeth, bones, etc.). EXAMPLES

[0096] The present invention will be specifically described below with reference to examples, but the present invention is not limited to these examples in any way.

[0097] <Adhesiveness> The pressure-sensitive adhesive sheet (test piece) prepared in each example was attached to the surface of a test plate (glass plate) underwater by pressing it back and forth once with a 2 kg roller. After application, the adhesive sheet was aged in water for 30 minutes. After aging, the adhesive sheet was peeled off from the test plate at a tensile tester (Autograph AGS-X, manufactured by Shimadzu Corporation) in accordance with JIS Z0237 at an atmosphere of 23°C and 50% RH, a tensile speed of 300 mm / min, and a peel angle of 180°, to measure the 180° peel adhesion (N / 20 mm). A glass plate (product name "Soda-lime glass #0050", manufactured by Matsunami Glass Industry Co., Ltd.) was used as the test plate.

[0098] Example 1 Into a three-neck flask equipped with a stirring blade, a thermometer, a nitrogen gas inlet tube, and a condenser, 95 parts by mass of butyl acrylate (BA) (manufactured by Toa Gosei Co., Ltd.), 5 parts by mass of 3-acrylamidobenzeneboronic acid (AAPBA) (manufactured by Junsei Chemical Co., Ltd.), 0.2 parts by mass of AIBN (2,2'-azobisisobutyronitrile) as a thermal polymerization initiator, and 250 parts by mass of MEK (methyl ethyl ketone) (manufactured by FUJIFILM Wako Pure Chemical Industries, Ltd.) were added. After stirring at 63° C. for 1 hour under a nitrogen atmosphere, 0.2 parts of AIBN was added as a thermal polymerization initiator and the reaction was carried out at 63° C. for 7 hours. The distance between O-O in AAPBA is 2.26 Å. The glass transition temperature of the homopolymer of butyl acrylate is -55°C.

[0099] The reacted solution was directly applied to a PET release liner (MRF38, manufactured by Mitsubishi Chemical Corporation) as a substrate, dried in an oven at 120°C for 5 minutes, and then covered with a PET release liner (MRE38, manufactured by Mitsubishi Chemical Corporation) to produce an adhesive sheet with a thickness of approximately 50 μm. Several of the above-mentioned pressure-sensitive adhesive sheets were attached to an S10 Lumirror #75 (manufactured by Toray Industries, Inc.) and the adhesive thickness was adjusted to produce an adhesive sheet with an adhesive thickness of 200 μm.

[0100] [Examples 2 and 3] The adhesive compositions of Examples 2 and 3 were prepared and adhesive sheets were produced in the same manner as in Example 1, except that the amounts of 3-acrylamidobenzeneboronic acid (AAPBA) and butyl acrylate (BA) used were changed as shown in Table 1.

[0101] Comparative Example 1 An adhesive composition of Comparative Example 1 was prepared in the same manner as in Example 1, except that 3-acrylamidobenzeneboronic acid (AAPBA) was changed to acrylic acid (AA), and an adhesive sheet was produced.

[0102] Comparative Example 2 (Preparation of adhesive sheet (C2)) In a reaction vessel equipped with a stirrer, a thermometer, a nitrogen gas inlet tube, a reflux condenser, and a dropping funnel, 100 parts by mass of n-butyl acrylate (BA), 8 parts by mass of vinyl acetate (VAc), 3 parts by mass of acrylic acid (AA), 0.1 parts by mass of 2-hydroxyethyl acrylate (HEA), 0.2 parts by mass of 2,2'-azobisisobutyronitrile (AIBN) as a polymerization initiator, and a mixed solvent of toluene and ethyl acetate mixed in a mass ratio of 5:5 as a polymerization solvent were charged, and nitrogen reflux was performed at room temperature for 1 hour, followed by a solution polymerization reaction at about 58 ° C. for 6 hours. Next, an aging reaction was performed at 65 ° C. for 2 hours and at 72 ° C. for 2 hours. After that, it was allowed to cool to obtain a solution of an acrylic polymer. The Mw of this acrylic polymer was about 60 × 10 4 The Mw / Mn was 5.0, and the proportion of polymers with Mw of 100,000 or less was approximately 20%. To the acrylic polymer solution obtained above, 2 parts by mass of an isocyanate-based crosslinking agent (product name "Coronate L", manufactured by Nippon Polyurethane Industry Co., Ltd.) was added as a crosslinking agent per 100 parts by mass of the acrylic polymer to prepare a pressure-sensitive adhesive composition (C2). A sheet-shaped release liner was prepared by laminating a 25 μm-thick polyethylene layer on one side of wood-free paper, and then performing a release treatment with a silicone-based release agent on the polyethylene layer. The pressure-sensitive adhesive composition (C2) was applied to the release surface of this release liner, and dried at 120° C. for 3 minutes to form a 75 μm-thick pressure-sensitive adhesive layer (C2). Two sheets were then prepared, and the support (mass 14 g / m 2The adhesive sheet (C2) was prepared by laminating the adhesive sheet (C1) to both sides of a sheet of pulp rayon paper (manufactured by Daifuku Paper Co., Ltd.).

[0103] Comparative Example 3 (Preparation of Pressure-Sensitive Adhesive Composition (C3)) A monomer mixture consisting of 90 parts by mass of 2-ethylhexyl acrylate (2EHA) and 10 parts by mass of AA was mixed with 0.05 parts by mass of 2,2-dimethoxy-1,2-diphenylethan-1-one (manufactured by BASF, product name "Irgacure 651") and 0.05 parts by mass of 1-hydroxycyclohexyl-phenyl-ketone (manufactured by BASF, product name "Irgacure 184") as photopolymerization initiators, and then irradiated with UV light until the viscosity reached approximately 15 Pa s to produce a monomer syrup (partially polymerized product) in which part of the monomer mixture was polymerized.

[0104] (Preparation of adhesive sheet (C3)) 0.08 parts by mass of 1,6-hexanediol diacrylate (HDDA) was added as a crosslinking agent to 100 parts by mass of the monomer syrup, and degassing treatment was performed. After the degassing treatment, 0.7 parts by mass of a fluorine-based surfactant was added to obtain a pressure-sensitive adhesive composition (C3). Two PET films with a thickness of 38 μm, one side of which had been treated with a silicone-based release agent to form a release surface, were prepared. 0.03 parts by mass of "Irgacure 651" was added to 100 parts by mass of the above pressure-sensitive adhesive composition (C3), and this was applied to the release surface of the first PET film, and the release surface of the second PET film was placed on top of it, and the illuminance was 5 mW / cm. 2 The adhesive was cured by irradiating both sides with UV for 3 minutes. A Toshiba product called "Black Light" was used for UV irradiation. UV was measured using an industrial UV checker with a peak sensitivity wavelength of about 350 nm (Topcon product called "UVR-T1", light receiving unit type UD-T36). In this way, a 400 μm thick adhesive layer (C3) was formed, and an adhesive sheet (C3) was produced.

[0105] [Table 1] [Industrial Applicability]

[0106] According to the present invention, it is possible to provide a pressure-sensitive adhesive composition that exhibits high adhesive strength to an adherend in water or in a wet state, a pressure-sensitive adhesive layer made of the pressure-sensitive adhesive composition, and a pressure-sensitive adhesive sheet including the pressure-sensitive adhesive layer.

[0107] Although the present invention has been described in detail and with reference to specific embodiments, it will be apparent to those skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope of the invention. This application is based on a Japanese patent application (Patent Application No. 2019-140059) filed on July 30, 2019, the contents of which are incorporated herein by reference. [Explanation of symbols]

[0108] 10, 30, 40 Adhesive Sheet 11, 31 Base material 12, 42 Adhesive layer 32A First adhesive layer 32B Second adhesive layer 13 Release Liner 33A, 43A First release liner 33B, 43B Second release liner

Claims

1. The compound includes a compound having a substituent represented by the following general formula (1): In the substituent represented by the general formula (1), R １ and R ２ -OR when each represents a hydrogen atom １ The oxygen atom of -OR ２ The distance between the oxygen atom is 2.26 Å, The compound is a polymer including a structure derived from a (meth)acrylic acid ester monomer and a structure derived from a compound A represented by the following general formula (2), The polymer is a copolymer of 95 to 97 parts by mass of at least one (meth)acrylic acid ester monomer and 3 to 5 parts by mass of the compound A, and the glass transition temperature of the homopolymer of the (meth)acrylic acid ester monomer is 10° C. or lower. Adhesive composition. 【Chemistry 1】 (In the general formula (1), L represents a boron atom. １ and R ２ each independently represents a hydrogen atom, or an aliphatic hydrocarbon group, an aryl group, or a heterocyclic group which may have a substituent. 【Chemistry 2】 (In general formula (2), X is a functional group containing a reactive group, R 1 and R 2 each independently represent a hydrogen atom, or an aliphatic hydrocarbon group, an aryl group, or a heterocyclic group which may have a substituent, and M represents a boron atom.)

2. The R １ and the R ２ The pressure-sensitive adhesive composition according to claim 1 , wherein each of

3. 3. The pressure-sensitive adhesive composition according to claim 1, wherein the X is a functional group having at least one hydrogen donor group selected from the group consisting of an acrylic group, a methacrylic group, or an organic group having an active methylene group.

4. A pressure-sensitive adhesive layer comprising the pressure-sensitive adhesive composition according to any one of claims 1 to 3.

5. A pressure-sensitive adhesive sheet comprising the pressure-sensitive adhesive layer according to claim 4 .

6. The pressure-sensitive adhesive sheet according to claim 5 , wherein the pressure-sensitive adhesive layer is formed on a substrate.