Method for manufacturing intermittently connected optical fiber ribbon and intermittently connected optical fiber ribbon

Abstract

Provided is a method for manufacturing an intermittent connection-type optical fiber tape core wire (10) comprising: arranging a plurality of optical fiber core wires (11A-11L) in parallel in a direction orthogonal to the longitudinal direction of the plurality of optical fiber core wires (11A-11L); covering all of the plurality of optical fiber core wires (11A-11L) with a connection resin (15); and forming slits (14) by intermittently inserting a cutting blade (117) in the connection resin (15) between some adjacent optical fiber core wires among the plurality of optical fiber core wires (11A-11L). The outer diameter of each of the optical fiber core wires (11A-11L) is 220 μm or less, and a distance (g) between the adjacent optical fibers between which the cutting blade (117) is inserted is 10-100 μm inclusive.

Description

[Technical field]

[0001] The present disclosure relates to a method for manufacturing an intermittently connected optical fiber ribbon and an intermittently connected optical fiber ribbon. This application claims priority to Japanese Application No. 2020-128531, filed on July 29, 2020, and incorporates by reference all of the contents of said Japanese application. [Background technology]

[0002] Conventionally, one example of a method for manufacturing an intermittently connected optical fiber ribbon is a method in which a plurality of optical fiber cores are arranged in parallel in a direction perpendicular to the longitudinal direction, all of the arranged optical fiber cores are coated with resin, and a cutting blade is intermittently inserted between some of the coated adjacent optical fiber cores to form slits (non-connected portions) (e.g., Patent Documents 1 and 4). Patent Documents 2 and 3 also describe the optical fiber core distance (center-to-center distance) of an intermittently structured ribbon core. [Prior art documents] [Patent documents]

[0003] [Patent Document 1] Japanese Patent Publication No. 2004-206048 [Patent Document 2] Japanese Patent Publication No. 2014-157382 [Patent Document 3] Japanese Patent Publication No. 2013-088617 [Patent Document 4] Japanese Patent Publication No. 2012-208310 Summary of the Invention

[0004] The method for producing an intermittently connected optical fiber ribbon according to the present disclosure includes the steps of: A plurality of optical fiber cores are arranged in parallel in a direction perpendicular to a longitudinal direction of the plurality of optical fiber cores; All of the optical fibers are coated with a connecting resin; A method for manufacturing an intermittently connected optical fiber ribbon, comprising: intermittently inserting a cutting blade into the connecting resin between some adjacent optical fiber cores among the plurality of optical fiber cores to form slits, The outer diameter of each of the optical fibers is 220 μm or less, Among the adjacent optical fiber core wires, the distance between the optical fiber core wires into which the cutting blade is inserted is 10 μm or more and 100 μm or less. the law of nature, The connecting resin is an ultraviolet curing resin, After the connecting resin has hardened to a gel fraction of 90% or more, the cutting blade is inserted.

[0005] The intermittently connected optical fiber ribbon according to the present disclosure includes: A plurality of optical fiber cores arranged in parallel in a direction perpendicular to the longitudinal direction; a connecting resin that covers all of the optical fiber cores, An intermittently connected optical fiber ribbon in which a cutting blade is intermittently inserted into the connecting resin between some adjacent optical fiber cores among the plurality of optical fiber cores to form slits, The outer diameter of each of the optical fibers is 220 μm or less, Among the adjacent optical fiber core wires, the distance between the optical fiber core wires into which the cutting blade is inserted is 10 μm or more and 100 μm or less. the law of nature, The connecting resin is an ultraviolet curing resin, The connecting resin has a gel fraction of 90% or more. [Brief description of the drawings]

[0006] [Figure 1] FIG. 1 is a configuration diagram of an apparatus for manufacturing an intermittently connected optical fiber ribbon according to a first embodiment of the present disclosure. [Diagram 2] FIG. 2 is a cross-sectional view perpendicular to the longitudinal direction of the optical fiber ribbon manufactured by the manufacturing apparatus of FIG. [Diagram 3] FIG. 3 is a partial development view showing the intermittently connected optical fiber ribbon in the longitudinal direction. [Figure 4]FIG. 4 is a schematic diagram of a printing device used in a modified example of the intermittently connected type optical fiber ribbon manufacturing apparatus. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0007] [Problem that this disclosure aims to solve] In order to pack a plurality of optical fiber ribbons in a cable at high density, it is preferable to arrange the optical fibers in each optical fiber ribbon so that the distance between adjacent optical fiber ribbons is as small as possible. However, if the distance is too small, the optical fiber ribbons may be damaged by the cutting blade when the slits are formed.

[0008] For example, when a thin optical fiber core wire with an outer diameter of 200 μm is used for an optical fiber ribbon, the coating layer of the thin optical fiber core wire is generally thin and the distance between adjacent thin optical fiber core wires is small, so even a slight deviation in the insertion position of the cutting blade when forming a slit may cause damage to the thin optical fiber core wire.

[0009] In view of the above, the present disclosure provides a manufacturing method for an intermittently connected optical fiber ribbon that can be mounted at a high density while preventing external damage to the optical fiber ribbon, and the intermittently connected optical fiber ribbon.

[0010] (Description of one embodiment of the present disclosure) First, embodiments of the present disclosure will be listed and described. (1) A method for producing an intermittently connected optical fiber ribbon according to one embodiment of the present disclosure includes the steps of: A plurality of optical fiber cores are arranged in parallel in a direction perpendicular to a longitudinal direction of the plurality of optical fiber cores; All of the optical fibers are coated with a connecting resin; A method for manufacturing an intermittently connected optical fiber ribbon, comprising: intermittently inserting a cutting blade into the connecting resin between some adjacent optical fiber cores among the plurality of optical fiber cores to form slits, The outer diameter of each of the optical fibers is 220 μm or less, Among the adjacent optical fiber core wires, the distance between the optical fiber core wires into which the cutting blade is inserted is 10 μm or more and 100 μm or less. the law of nature, The connecting resin is an ultraviolet curing resin, After the connecting resin has hardened to a gel fraction of 90% or more, the cutting blade is inserted.

[0011] According to the manufacturing method of the intermittently connected optical fiber ribbon of the present disclosure, the distance between the optical fiber core wires into which the cutting blade is inserted is 10 μm or more among the adjacent optical fiber core wires, so that the optical fiber core wires are not damaged even when the cutting blade is inserted. Also, since the distance between the optical fiber core wires into which the cutting blade is inserted is 100 μm or less, a plurality of optical fiber core wires can be arranged in the ribbon core wire at high density. Furthermore, if the cutting blade is inserted when the connecting resin is not yet cured, the connecting resin is highly elastic, making it difficult to break the connecting resin with the cutting blade, and its weak strength may cause separation of the optical fiber core wires within the ribbon. According to the present disclosure, the cutting blade is inserted after the connecting resin is cured to a gel fraction of 90% or more, so that the connecting resin can be easily broken with the cutting blade and separation of the optical fiber core wires within the ribbon core wire does not occur.

[0012] (2) The breaking strength of the connecting resin may be greater than 20 MPa and less than or equal to 50 MPa. If the breaking strength of the connecting resin is too low, when the intermittently connected optical fiber ribbon is squeezed by rollers in the line during the manufacturing process, the connecting resin is too soft and the optical fibers may separate within the ribbon. However, according to the present disclosure, the breaking strength of the connecting resin is greater than 20 MPa, so that separation of the optical fibers due to weak breaking strength is unlikely to occur. Also, since the breaking strength of the connecting resin is 50 MPa or less, the connecting resin is not too hard and can be easily broken by a cutting blade.

[0013] (3) The Young's modulus of the outermost layer of each of the optical fibers may be 800 MPa or more and 2000 MPa or less. According to the present disclosure, since the Young's modulus of the outermost coating layer of each optical fiber is 800 MPa or more, the optical fiber is unlikely to be damaged by the cutting blade. Also, since the Young's modulus of the outermost coating layer of each optical fiber is 2000 MPa or less, the intermittently connected optical fiber ribbon is not easily deformed due to the influence of the rigidity of the resin, and the cable loss characteristics are not deteriorated.

[0015] (5) curing the connecting resin covering the optical fibers; The hardened connecting resin is heated to soften it, The cutting blade may be inserted into the softened interlocking resin. If the cutting blade is inserted into the connecting resin when it is not softened, the connecting resin cannot be easily broken, and the connecting resin may peel off from the multiple optical fiber cores when the slit is formed. According to the present disclosure, the cutting blade is inserted into the softened connecting resin, so that the connecting resin can be easily broken.

[0016] (6) curing the connecting resin covering the optical fibers; Heating the cutting blade; The heated cutting blade may be inserted into the hardened interlocking resin. According to the present disclosure, even if the connecting resin is cured and hard, the cutting blade is inserted into the connecting resin in a heated state, so that the connecting resin can be easily broken.

[0017] (7) Marking the surface of each of the optical fibers; The optical fibers having the marks may be covered with the connecting resin. According to the present disclosure, since a mark is provided on the surface of each optical fiber core, the ribbon core can be more easily identified.

[0018] (8) An intermittently connected optical fiber ribbon according to one embodiment of the present disclosure comprises: A plurality of optical fiber cores arranged in parallel in a direction perpendicular to the longitudinal direction; a connecting resin that covers all of the optical fiber cores, An intermittently connected optical fiber ribbon in which a cutting blade is intermittently inserted into the connecting resin between some adjacent optical fiber cores among the plurality of optical fiber cores to form slits, The outer diameter of each of the optical fibers is 220 μm or less, Among the adjacent optical fiber core wires, the distance between the optical fiber core wires into which the cutting blade is inserted is 10 μm or more and 100 μm or less. the law of nature, The connecting resin is an ultraviolet curing resin, The connecting resin has a gel fraction of 90% or more.

[0019] According to the intermittently connected optical fiber ribbon of the present disclosure, the distance between adjacent optical fiber core wires into which the cutting blade is inserted is 10 μm or more, so that the optical fiber core wire is not damaged even when the cutting blade is inserted. Also, since the distance between the optical fiber core wires into which the cutting blade is inserted is 100 μm or less, a plurality of optical fiber core wires can be arranged in the ribbon core wire at high density. Furthermore, if a cutting blade is inserted when the connecting resin is not yet cured, the connecting resin is highly elastic, making it difficult to break the connecting resin with the cutting blade, and its weak strength may cause separation of the optical fiber core wires within the ribbon. According to the present disclosure, the gel fraction of the connecting resin is 90% or more, so the connecting resin can be easily broken with the cutting blade, and separation of the optical fiber core wires within the ribbon core wire does not occur.

[0020] (9) The breaking strength of the connecting resin may be greater than 20 MPa and less than or equal to 50 MPa. If the breaking strength of the connecting resin is too low, when the intermittently connected optical fiber ribbon is squeezed by rollers in the line during the manufacturing process, the connecting resin is too soft and the optical fibers may separate within the ribbon. However, according to the present disclosure, the breaking strength of the connecting resin is greater than 20 MPa, so that separation of the optical fibers due to weak breaking strength is unlikely to occur. Also, since the breaking strength of the connecting resin is 50 MPa or less, the connecting resin is not too hard and can be easily broken by a cutting blade.

[0021] (10) The Young's modulus of the outermost layer of each of the optical fibers may be 800 MPa or more and 2000 MPa or less. According to the present disclosure, since the Young's modulus of the outermost coating layer of each optical fiber is 800 MPa or more, the optical fiber is unlikely to be damaged by the cutting blade. Also, since the Young's modulus of the outermost coating layer of each optical fiber is 2000 MPa or less, the intermittently connected optical fiber ribbon is not easily deformed due to the influence of the rigidity of the resin, and the cable loss characteristics are not deteriorated. [Effects of this disclosure]

[0022] According to the present disclosure, it is possible to provide a manufacturing method for an intermittently connected optical fiber ribbon that can be mounted at a high density while preventing external damage to the optical fiber ribbon, and an intermittently connected optical fiber ribbon.

[0023] (Details of the first embodiment of the present disclosure) An intermittently connected optical fiber ribbon 1 and a method for manufacturing the intermittently connected optical fiber ribbon 1 according to an embodiment of the present disclosure will be described with reference to the drawings. It should be noted that the present disclosure is not limited to these examples, but is defined by the scope of the claims, and is intended to include all modifications within the meaning and scope equivalent to the scope of the claims.

[0024] Fig. 1 is a configuration diagram of a manufacturing apparatus 100 for an intermittently connected optical fiber ribbon 1 according to one embodiment of the present disclosure. As shown in Fig. 1, the manufacturing apparatus 100 includes a supply 101, a coating device 110, a delivery capstan 115, a slitting device 116, a winding tension control dancer 118, and a winding device 119. The manufacturing apparatus 100 further includes a wire concentrating roller 105 provided between the supply 101 and the coating device 110, and a turn roller 114 provided between the coating device 110 and the delivery capstan 115.

[0025] The supply 101 includes a plurality of reels 102, a dancer roller 103, and a conveying roller 104. An optical fiber 11 is wound around each of the reels 102. The outer diameter of each optical fiber 11 is, for example, 220 μm or less. The optical fibers 11 are unwound from the reels 102 and a predetermined tension is applied to them by the dancer roller 103. After that, they are arranged on a single arrangement surface as they pass through the conveying roller 104, and are sent to the wire collecting roller 105.

[0026] The collecting roller 105 has a plurality of grooves (not shown) arranged at predetermined intervals, through which the plurality of optical fiber cores 11 pass. As a result, the plurality of optical fiber cores 11 are collected and arranged in parallel in a direction perpendicular to the longitudinal direction of the optical fiber cores 11.

[0027] The optical fibers 11 collected on the collection roller 105 are sent to a coating device 110. The coating device 110 includes a resin storage tank 111, a coating device 112, and an ultraviolet ray irradiation device 113.

[0028] The coating device 112 inserts all of the optical fiber cores 11 and coats them with connecting resin 15 supplied from a resin storage tank 111 to form a coating layer 12 (see FIG. 2). The connecting resin 15 is preferably an ultraviolet curing resin, but may be a thermoplastic resin, an adhesive resin, or other coating resin. The ultraviolet irradiation device 113 cures the connecting resin 15 by irradiating it with ultraviolet light. As a result, the multiple optical fiber cores 11 become the optical fiber ribbon 10.

[0029] The optical fiber ribbon 10 is sent to a delivery capstan 115 via a turn roller 114. Thereafter, a slit is formed in the optical fiber ribbon 10 by a slitting device 116.

[0030] The slitting device 116 includes a plurality of cutting blades 117. Each cutting blade 117 has a tapered tip, and the thickness of the blade is, for example, 0.2 mm. A cam mechanism is connected to each cutting blade 117, and the cutting blade 117 is provided along the longitudinal direction of the optical fiber ribbon 10 and configured to swing in conjunction with the cam mechanism. The swinging motion of the cutting blade 117 causes the cutting blade 117 to be intermittently inserted into the connecting resin 15 between some of the adjacent optical fibers in the optical fiber ribbon 10, forming slits. Here, the cutting blade 117 is preferably inserted in a state where the connecting resin 15 has a gel fraction of 90% or more and is cured. The optical fiber ribbon 10 in which the slits are intermittently formed becomes the intermittently connected optical fiber ribbon 1.

[0031] The intermittently connected optical fiber ribbon 1 is sent to a winding tension control dancer 118, where the tension is controlled. Then, the optical fiber ribbon 1 is wound onto a winding reel R by a winding device 119.

[0032] Next, the manufacturing process of the intermittently connected optical fiber ribbon 1 from the optical fiber ribbon 10 will be described in detail. FIG. 2 shows a cross section perpendicular to the longitudinal direction of the optical fiber ribbon 10. As shown in FIG. 2, the optical fiber ribbon 10 has a plurality of optical fibers 11A to 11L (12 fibers in this example) arranged in parallel in a direction perpendicular to the longitudinal direction and coated with a coating layer 12. The breaking strength of the coupling resin 15 forming the coating layer 12 is greater than 20 MPa and less than 50 MPa. Each of the optical fibers 11A to 11L includes a glass fiber 16 at the center and an outer layer 17 (outermost layer) that covers the glass fiber 16. The diameter of the glass fiber 16 is, for example, 200 μm, and the thickness of the outer layer 17 is 37.5 μm. The Young's modulus of the outer layer 17 is greater than 800 MPa and less than 2000 MPa.

[0033] In this example, two optical fiber cores are almost in contact with each other to form an optical fiber core set, and a distance g is provided between adjacent optical fiber core sets. In Fig. 2, a distance g is provided between the set of optical fiber cores 11A and 11B and the set of optical fiber cores 11C and 11D, between the set of optical fiber cores 11C and 11D and the set of optical fiber cores 11E and 11F, between the set of optical fiber cores 11E and 11F and the set of optical fiber cores 11G and 11H, between the set of optical fiber cores 11G and 11H and the set of optical fiber cores 11I and 11J, and between the set of optical fiber cores 11I and 11J and the set of optical fiber cores 11L and 11L. In this example, a distance g is provided for every two optical fiber cores, but it may be provided for every single optical fiber core.

[0034] The distance g is the distance between the outer layer 17 of the optical fiber core wire (11B) located near an adjacent optical fiber core wire set (e.g., 11C and 11D) among the sets of optical fiber core wires (e.g., 11A and 11B) and the outer layer 17 of the adjacent optical fiber core wire (11C) on a straight line L passing through the center of the core wires in the parallel direction of the multiple optical fiber core wires 11A to 11L. In this example, the distance g is 10 μm or more and 100 μm or less. In this example, a cutting blade 117 is inserted into the connecting resin 15 portion spaced apart by the distance g to form a slit. As a result, the slit becomes the non-connected portion 14 (see FIG. 3) of the intermittently connected optical fiber ribbon 1.

[0035] Fig. 3 is a partial development view showing the intermittently connected optical fiber ribbon 1 in its longitudinal direction. As shown in Fig. 3, the optical fiber ribbon 10 that has passed through the slitting device 116 becomes an intermittently connected optical fiber ribbon 1 in which the optical fiber ribbons 11A to 11L are arranged in parallel in a direction perpendicular to the longitudinal direction of the optical fibers 11A to 11L, and in which connecting portions 13 where adjacent optical fibers are connected and non-connecting portions 14 where adjacent optical fibers are not connected are intermittently provided in the longitudinal direction among some or all of the optical fibers 11A to 11L. In this way, the optical fiber ribbon 10 sent to the slitting device 116 becomes an intermittently connected optical fiber ribbon 1 by intermittently inserting a cutting blade 117.

[0036] As described above, in the optical fiber ribbon 10 of this embodiment, the optical fiber 11 is arranged so that the distance g is 10 μm or more and 100 μm or less, and the connecting resin 15 is hardened. In general, if the distance g is too small, the glass fiber 16 may be damaged by the cutting blade 117 when the cutting blade 117 is inserted. If the distance g is too large, the optical fiber ribbon 10 cannot have a plurality of optical fiber 11 arranged at a high density. However, according to this embodiment, since the distance g is 10 μm or more, the possibility of damaging the optical fiber 11 even when the cutting blade 117 is inserted is reduced. Furthermore, since the distance g is 100 μm or less, the optical fiber ribbon 10 can have a plurality of optical fiber 11 arranged at a high density. Therefore, it is possible to provide an intermittently connected optical fiber ribbon 1 in which the optical fiber 11 is arranged at a high density while suppressing the possibility of damaging the optical fiber 11.

[0037] It is preferable that the breaking strength of the connecting resin 15 is not too low or too high. If the breaking strength is too low, for example, when the optical fiber ribbon 10 is rolled by the turn roller 114, the connecting resin 15 is too soft, so that the optical fibers 11 in the optical fiber ribbon 10 may be separated. On the other hand, if the breaking strength is too high, the connecting resin 15 is too hard, so that it is difficult to break the connecting resin 15 with the cutting blade 117. In the optical fiber ribbon 10 of this example, the breaking strength of the connecting resin 15 is greater than 20 MPa, so that separation of the optical fibers 11 due to weak breaking strength is unlikely to occur. In addition, since the breaking strength of the connecting resin 15 is 50 MPa or less, the connecting resin 15 is not too hard, so that the connecting resin 15 can be easily broken by the cutting blade 117. Therefore, the slit, i.e., the non-connecting portion 14 can be easily formed while preventing separation of the optical fiber 11.

[0038] If the Young's modulus of the outer layer 17 is too low (the outer layer 17 is too soft), the glass fiber 16 may be damaged by the cutting blade 117 when the cutting blade 117 is inserted. On the other hand, if the Young's modulus of the outer layer 17 is too high (the outer layer 17 is too hard), the intermittently connected optical fiber ribbon is less likely to deform due to the rigidity of the resin, and the cable loss characteristics may deteriorate. However, since the Young's modulus of the outer layer 17 of each optical fiber core wire 11 in this example is 800 MPa or more, the cutting blade 117 is less likely to cause external damage to the outer layer 17. In addition, since the Young's modulus of the outer layer 17 is 2000 MPa or less, the intermittently connected optical fiber ribbon 1 is not less likely to deform due to the rigidity of the resin, and the possibility of the cable loss characteristics deteriorating can be suppressed. Therefore, it is possible to provide an intermittently connected optical fiber ribbon 1 that has good cable loss characteristics while preventing external damage to the outer layer 17.

[0039] The cutting blade 117 is inserted to form a slit after the connecting resin 15 has hardened to a predetermined value or more. If the cutting blade 117 is inserted when the connecting resin 15 is not hardened, it is difficult to break the connecting resin 15 because the connecting resin 15 has high elasticity. Furthermore, if the connecting resin 15 is not hardened, it has low strength, so there is a risk that the multiple optical fibers 11 in the optical fiber ribbon 10 will separate. In the optical fiber ribbon 10 of this example, the cutting blade 117 is inserted into the connecting resin 15 to form a slit after the connecting resin has hardened to a gel fraction of 90% or more, so that the connecting resin 15 can be easily broken by the cutting blade 117 and separation of the optical fibers 11 in the ribbon can be prevented.

[0040] In this example, the optical fiber ribbon 10 in which the linking resin 15 has been hardened by the coating device 110 is intermittently inserted with the cutting blade 117 of the slitting device 116 to form the intermittently connected optical fiber ribbon 1, but the manufacturing process is not limited to this. For example, the manufacturing device 100 may include a first heating section 121 ( FIG. 1 ) for heating the linking resin 15 between the coating device 110 and the slitting device 116. The optical fiber ribbon 10 in which the linking resin 15 has been hardened by passing through the ultraviolet irradiator 113 of the coating device 110 has the linking resin 15 heated and softened by the first heating section 121. The cutting blade 117 is inserted into the softened linking resin 15 to form a slit.

[0041] If the cutting blade 117 is inserted when the connecting resin 15 is not softened, the connecting resin 15 cannot be easily broken. Furthermore, the connecting resin 15 may peel off from the optical fiber cores 11 when the slit is formed. According to this example, the cutting blade 117 is inserted into the connecting resin 15 softened by the first heating unit 121, so that the connecting resin 15 can be easily broken. The heating temperature by the first heating unit 121 is preferably about 40°C or higher. If the heating temperature is about 40°C, the effect of softening the connecting resin 15 is recognized. However, the heating temperature needs to be lower than the melting point of the connecting resin 15, and specifically, it is preferable that the heating temperature is lower than about 95°C.

[0042] The slitting device 116 of the manufacturing apparatus 100 may also include a second heating section 122 for heating the cutting blade 117 (FIG. 1). The optical fiber ribbon 10, which has passed through the ultraviolet irradiation device 113 of the coating device 110 and has the connecting resin 15 cured, is sent to the slitting device 116. The cutting blade 117 heated by the second heating section 122 is inserted into the cured connecting resin 15 to form a slit. Therefore, according to this example, even if the connecting resin 15 is cured, the cutting blade 117 is inserted into the connecting resin 15 in a heated state, so that the connecting resin 15 can be easily broken. In this example as well, the temperature at which the second heating section 122 heats the connecting resin 15 is preferably about 40° C. or higher and about 95° C. or lower. Note that both the first heating section 121 and the second heating section 122 may be provided to heat both the cutting blade 117 and the connecting resin 15.

[0043] (Modification) The manufacturing apparatus 100 of this embodiment may apply a mark M to the multiple optical fibers 11 in order to improve the identification of the intermittently connected type optical fiber ribbon 1. Fig. 4 is a schematic diagram of a printer 123 that can be provided in the manufacturing apparatus 100 of the intermittently connected type optical fiber ribbon 1.

[0044] 4, the manufacturing apparatus 100 may include a printer 123 that marks the surfaces of the multiple optical fiber cores 11, in addition to the configuration shown in Fig. 1. The printer 123 may be disposed between the supply 101 and the coating device 110, and is preferably provided between the wire concentrating roller 105 and the coating device 110. The printer 123 is, for example, an inkjet printer.

[0045] The printer 123 prints markings on the surfaces of the multiple optical fiber cores 11 sent from the supply 101 to form marks M. The shape of the marks M may be, for example, a bar shape perpendicular to the longitudinal direction. Also, a ring-shaped ring mark may be provided on each optical fiber core 11.

[0046] The multiple optical fiber cores 11 with the marks M formed thereon are then sent to a coating device 112. The coating device 112 applies a connecting resin 15 onto the marks M, and an ultraviolet irradiation device 113 hardens the connecting resin 15, including the marks M. The subsequent manufacturing steps overlap with the explanation of FIG. 1, so illustrations and explanations are omitted.

[0047] As described above, according to this embodiment, since a mark is applied to the surface of the optical fiber 11 by the printer 123, the ribbon can be more easily identified.

[0048] The manufacturing apparatus 100 of this embodiment may include a plasma processing apparatus 124 that performs plasma processing on the surfaces of the multiple optical fiber cores 11. The plasma processing apparatus 124 may be disposed between the supply 101 and the printer 123, and is preferably provided between the wire collection roller 105 and the printer 123. The plasma processing by the plasma processing apparatus 124 increases the wettability of the core wire surface, improving the adhesion of the marking material to the core wire surface. Therefore, when the mark M is subsequently applied by the printer 123, the mark M can be prevented from peeling off from the core wire surface.

[0049] (Evaluation experiment) An evaluation was carried out on an optical fiber cable manufactured by the manufacturing method of the present disclosure. The optical fiber cable used in this evaluation experiment was a slotless type optical fiber cable with 432 cores, in which a 12-core intermittently connected optical fiber ribbon 1 was mounted. The cable outer diameter was 11 mm, and the core density was 4.55 cores / mm 2 The distance g of the intermittently connected optical fiber ribbon 1 mounted in each optical fiber cable, the breaking strength of the connecting resin 15 at 23°C, and the Young's modulus of the outer layer at 23°C were individually set, and samples No. 1 to No. 12 were prepared. In this evaluation experiment, the presence or absence of damage to the optical fiber core 11 of each sample, whether it could be cut, whether it separated when cut, and the cable loss characteristics were evaluated. Here, the cable loss characteristics were evaluated by whether the attenuation per unit distance when a wavelength of 1.55 μm was input into the cable was less than 0.3 dB / km. The evaluation results are shown in Table 1.

[0050] [Table 1]

[0051] In Table 1, the distance g was 0 μm for all samples No. 1 to No. 3, and damage to the optical fiber was confirmed. This is because the distance g was too small, causing the optical fiber to be damaged by the cutting blade 117. Damage to the optical fiber was also confirmed in sample No. 10, in which the Young's modulus of the outer layer was 600 MPa. This is because the Young's modulus of the outer layer was too soft, causing the optical fiber to be damaged by the cutting blade 117. No damage to the optical fiber was confirmed in the other samples No. 4 to 9 and 11 to 15. From the above, it was confirmed that damage to the optical fiber can be prevented when the distance g is 10 μm or more and the Young's modulus of the outer layer is 800 MPa or more.

[0052] In Table 1, it was confirmed that the breaking strength of connecting resin 15 in both samples No. 9 and No. 13 was 70 MPa, and cutting blade 117 was unable to cut connecting resin 15 (a portion was left uncut). This is because connecting resin 15 was too hard. On the other hand, cutting by cutting blade 117 was confirmed in other samples No. 1 to 8, 10 to 12, 14, and 15, in which connecting resin 15 had a breaking strength of 50 MPa or less. From the above, it was confirmed that cutting blade 117 can cut connecting resin 15 when the breaking strength of connecting resin 15 is 50 MPa or less.

[0053] In addition, in sample No. 4, in which the breaking strength of connecting resin 15 is 20 MPa, the optical fiber core was separated when cut. Separation was not observed in the other samples. From the above, it was confirmed that when the breaking strength of connecting resin 15 is greater than 20 MPa, separation of the optical fiber core when cut can be suppressed.

[0054] In Table 1, for both samples No. 14 and No. 15, the distance g was 150 μm, and an attenuation of 0.3 dB / km or more was confirmed as the cable loss characteristics. If the distance g is too long, the same optical fiber core wires cannot be densely packed in the cable. In other words, the cross-sectional area of ​​each intermittently connected optical fiber ribbon increases, so that the optical fiber core wires in the cable are packed so closely together that lateral pressure is applied to each other. This lateral pressure increases the cable loss characteristics. In addition, for sample No. 8, whose outer layer has a Young's modulus of 2500 MPa, the intermittently connected optical fiber ribbon core wire is difficult to deform due to the rigidity of the resin, so an attenuation of 0.3 dB / km or more was confirmed as the cable loss characteristics. For the other samples No. 1 to 7 and 9 to 13, whose distance g is 100 μm or less, the cable loss characteristics were less than 0.3 dB / km. In particular, even in sample No. 7, where the distance g was 100 μm or less and the Young's modulus of the outer layer was 2000 MPa, the cable loss characteristics were less than 0.3 dB / km. From the above, it was confirmed that when the distance g is 100 μm or less and the Young's modulus of the outer layer is 2000 MPa or less, it is possible to realize an optical fiber cable with low cable loss characteristics while densely packaging optical fiber cores in the cable.

[0055] Although the present disclosure has been described in detail and with reference to specific embodiments, it is clear to those skilled in the art that various changes and modifications can be made without departing from the spirit and scope of the present disclosure. Furthermore, the number, position, shape, etc. of the components described above are not limited to the above embodiments, and can be changed to the number, position, shape, etc. that are suitable for implementing the present disclosure. [Explanation of symbols]

[0056] 1: Intermittently connected optical fiber ribbon 10: Optical fiber ribbon 11, 11A to 11L: Optical fiber core 12: Covering layer 13:Connection part 14: Unconnected part 15: Interlocking resin 16: Glass fiber 17: Outer layer (outermost layer) 100: Manufacturing equipment 101: Supply 102: Reel 103: Dancer Roller 104: Transport roller 105: Wire collection roller 110: Coating device 111: Resin storage tank 112: Coating device 113: Ultraviolet irradiation device 114: Turn Roller 115: Output capstan 116: Cutting device 117: Cutting blade 118: Winding tension control dancer 119: Winding device 121:First heating section 122:Second heating section 123: Printing device 124: Plasma processing equipment R: Take-up reel M: Mark

Claims

1. A plurality of optical fiber cores are arranged in parallel in a direction perpendicular to a longitudinal direction of the plurality of optical fiber cores; All of the optical fibers are coated with a connecting resin; A method for manufacturing an intermittently connected optical fiber ribbon, comprising: intermittently inserting a cutting blade into the connecting resin between some adjacent optical fiber cores among the plurality of optical fiber cores to form slits, The outer diameter of each of the optical fibers is 220 μm or less, Among the adjacent optical fiber core wires, the distance between the optical fiber core wires into which the cutting blade is inserted is 10 μm or more and 100 μm or less, The connecting resin is an ultraviolet curing resin, the cutting blade is inserted after the connecting resin has been cured to a gel fraction of 90% or more.

2. 2. The method for producing an intermittently connected optical fiber ribbon according to claim 1, wherein the breaking strength of the connecting resin is greater than 20 MPa and less than or equal to 50 MPa.

3. 3. The method for producing an intermittently connected optical fiber ribbon according to claim 1, wherein the Young's modulus of the outermost layer of each of the optical fibers is 800 MPa or more and 2000 MPa or less.

4. hardening the connecting resin covering the plurality of optical fiber cores; The hardened connecting resin is heated to soften it, 4. The method for producing an intermittently connected optical fiber ribbon according to claim 1, wherein the cutting blade is inserted into the softened connecting resin.

5. hardening the connecting resin covering the plurality of optical fiber cores; Heating the cutting blade; 5. The method for producing an intermittently connected optical fiber ribbon according to claim 1, further comprising inserting the heated cutting blade into the hardened connecting resin.

6. Marking the surface of each of the optical fibers; 6. The method for producing an intermittently connected optical fiber ribbon according to claim 1, further comprising covering the optical fibers having the marks with the connecting resin.

7. A plurality of optical fiber cores arranged in parallel in a direction perpendicular to the longitudinal direction; a connecting resin that covers all of the optical fiber cores, An intermittently connected optical fiber ribbon in which a cutting blade is intermittently inserted into the connecting resin between some adjacent optical fiber cores among the plurality of optical fiber cores to form slits, The outer diameter of each of the optical fibers is 220 μm or less, Among the adjacent optical fiber core wires, the distance between the optical fiber core wires into which the cutting blade is inserted is 10 μm or more and 100 μm or less, The connecting resin is an ultraviolet curing resin, The intermittently connected optical fiber ribbon has a gel fraction of 90% or more.

8. 8. The intermittently connected optical fiber ribbon according to claim 7, wherein the breaking strength of the connecting resin is greater than 20 MPa and equal to or less than 50 MPa.

9. 9. The intermittently connected optical fiber ribbon according to claim 7, wherein the Young's modulus of the outermost layer of each of the optical fibers is 800 MPa or more and 2000 MPa or less.