Heavy duty pneumatic tires

Abstract

Provided is a heavy-duty pneumatic tire that maintains or improves rolling resistance, uneven wear resistance, and durability, and achieves a good balance between these. In the heavy-duty pneumatic tire, the tread rubber layer 10 is made of a tread rubber made of a rubber composition in which 100 parts by mass of a rubber component containing 90% by mass or more of isoprene-based rubber is blended with 60 parts by mass or less of a filler containing carbon black and silica, and the ratio of the amounts of carbon black and silica blended in the filler is 3:2 to 1:1, and the belt cushion layer 40 is made of a belt cushion rubber made of a rubber composition in which 100 parts by mass of a rubber component containing 90% by mass or more of isoprene-based rubber is blended with 45 parts by mass or less of carbon black, and the hardness Hc of the tread rubber and the hardness Hb of the belt cushion rubber satisfy the relationship of 1.2≦Hc / Hb≦1.5.

Description

[Technical field]

[0001] The present invention relates to a heavy-duty tire including a belt cushion layer disposed between the end portions of a belt layer in the tire width direction and a carcass layer. [Background technology]

[0002] Tires (heavy-duty pneumatic tires) used on vehicles such as trucks and buses are subject to a larger load than passenger vehicle tires, so it is important that they have excellent wear resistance. In addition, even for heavy-duty pneumatic tires, when there are many opportunities to drive at high speeds, uneven wear such as local wear on the shoulders tends to occur, so that the primary life of the tire may end due to uneven wear before the entire tread part wears out, and there is a demand for improving uneven wear resistance. On the other hand, as mentioned above, when there are many opportunities to drive at high speeds, there are fewer opportunities to brake and drive during high-speed driving (compared to when driving in urban areas, for example), so the rate at which wear progresses is slower, and as a result, the primary life of the tire tends to be longer (because the wear rate is slow, the period until the tire reaches the end of its life due to total wear or uneven wear tends to be longer). Therefore, there is also a demand for excellent durability of the tire body (tire frame). In addition, with the increasing interest in global environmental issues, environmental regulations are becoming stricter for heavy-duty tires as well, and further improvement in fuel efficiency is required.

[0003] For example, Patent Document 1 proposes that silica is blended into a rubber component mainly made of natural rubber, and that a specific silane coupling agent is blended to improve the dispersion of silica, thereby improving the wear resistance and fuel economy. However, such measures alone cannot sufficiently improve the above-mentioned uneven wear resistance, etc. In addition, as a means for improving uneven wear resistance, it is known to harden the tread rubber and belt cushion rubber placed in the shoulder part of the tire, and as a method for hardening rubber, increasing the crosslink density and increasing the amount of filler are known, but if the crosslink density is increased, there is a concern that the durability of the belt cushion will deteriorate, and if the amount of filler is increased, there is a concern that the heat generation will increase, which will affect the fuel economy. From the above points, it is difficult to achieve rolling resistance, uneven wear resistance, and durability at the same time in a tire equipped with tread rubber and belt cushion rubber, and measures are required to achieve these in a well-balanced and highly compatible manner. [Prior art documents] [Patent documents]

[0004] [Patent Document 1] Japanese Patent Application Publication No. 2019-056068 Summary of the Invention [Problem to be solved by the invention]

[0005] The object of the present invention is to provide a heavy-duty pneumatic tire having tread rubber and belt cushion rubber, which maintains or improves the rolling resistance, uneven wear resistance, and durability, and achieves a high degree of compatibility among these in a well-balanced manner. [Means for solving the problem]

[0006] The heavy-duty pneumatic tire of the present invention that achieves the above-mentioned object comprises a tread portion extending in a tire circumferential direction to form an annular shape, a pair of sidewall portions disposed on both sides of the tread portion, and a pair of bead portions disposed on the tire radially inward side of these sidewall portions, and has at least one carcass layer mounted between the pair of bead portions and a plurality of belt layers disposed on the outer peripheral side of the carcass layer in the tread portion, and a belt cushion layer is disposed between the tire width direction end portions of the belt layer and the carcass layer, wherein the tread rubber constituting the tread portion contains 90 mass % or more of isoprene-based rubber. The tread rubber is characterized in that it is made of a rubber composition in which 60 parts by mass or less of a filler containing carbon black and silica is blended per 100 parts by mass of a rubber component containing the tread rubber, and the ratio of the amount of the carbon black and the silica in the filler is 3:2 to 1:1; the belt cushion rubber constituting the belt cushion layer is made of a rubber composition in which 45 parts by mass or less of a filler containing carbon black and silica is blended per 100 parts by mass of a rubber component containing 90% by mass or more of an isoprene-based rubber; and the hardness Hc of the tread rubber at 20°C and the hardness Hb of the belt cushion rubber at 20°C satisfy the relationship of 1.2≦Hc / Hb≦1.5. Effect of the Invention

[0007] In the heavy-duty pneumatic tire of the present invention, the tread rubber is made of a rubber composition in which 100 parts by mass of a rubber component containing 90% by mass or more of isoprene-based rubber is blended with 60 parts by mass or less of a filler containing carbon black and silica, and the ratio of the amount of carbon black to silica in the filler is 3:2 to 1:1, thereby suppressing heat generation in the tread portion and improving rolling resistance. In addition, the belt cushion rubber is made of a rubber composition in which 100 parts by mass of a rubber component containing 90% by mass or more of isoprene-based rubber is blended with 45 parts by mass or less of a filler containing carbon black and silica, thereby making it possible to improve the shoulder portion and improve uneven wear resistance. Furthermore, since the hardness ratio Hc / Hb of the tread rubber and the belt cushion rubber is set to an appropriate range of 1.2 to 1.5, the aforementioned uneven wear resistance can be exhibited well while ensuring durability. Through these cooperations, the rolling resistance, uneven wear resistance, and durability can be maintained or improved, and these can be simultaneously achieved in a well-balanced manner.

[0008] In the present invention, the rubber composition constituting the tread rubber contains a guanidine-based vulcanization accelerator and a sulfenamide-based vulcanization accelerator, and the blending amount of the guanidine-based vulcanization accelerator is Ac G and the amount of sulfenamide vulcanization accelerator Ac S and 0.3≦Ac G / Ac S It is preferable to satisfy the relationship of ≦5.0. This improves the rubber physical properties of the tread rubber, which is advantageous in achieving both low rolling resistance and chipping resistance.

[0009] In the present invention, when a plurality of circumferential grooves extending along the tire circumferential direction are formed on the surface of the tread portion and a pair of the plurality of circumferential grooves arranged on the outermost sides in the tire width direction are defined as shoulder main grooves, shoulder land portions are defined on the outer sides of each shoulder main groove in the tire width direction, and it is preferable that the width Wsh of each shoulder land portion satisfies the relationship 0.15≦Wsh / W≦0.27 with respect to the contact width W of the tread portion. This optimizes the land portions (amount of rubber) arranged in the shoulder regions that contribute to uneven wear resistance, which is advantageous for improving uneven wear resistance.

[0010] In the present invention, it is preferable that the multiple circumferential grooves include a shoulder main groove and a center circumferential groove disposed on the inner side of the shoulder main groove in the tire width direction, and the groove width Wo of the shoulder main groove and the groove width Wi of the center circumferential groove satisfy the relationship of 0.15≦Wi / Wo≦0.24. Providing grooves in this manner is advantageous for improving uneven wear resistance.

[0011] In the present invention, the tread gauge Gcc measured on the tire equator is preferably 12.0 mm or more and 30.0 mm or less. This is advantageous for improving uneven wear resistance because a sufficient amount of rubber can be secured in the tread rubber. The tread gauge Gcc is the thickness of the tread rubber measured on the tire equator, and is the distance measured on the tire equator from the outer surface of the tread layer to the outermost surface in the tire radial direction of the layer located at the outermost position in the tire radial direction among the various reinforcing layers (carcass layer, belt layer, belt reinforcing layer, etc.) that constitute the tire.

[0012] In the present invention, the contact length of the tread center land row is Maximum ground length Lc is the contact length of the axially outermost land row of the tire. External ground length When Ls is used, it is preferable that the maximum contact length Lc and the outer contact length Ls satisfy the relationship of 0.80≦Ls / Lc≦1.05. This ensures a sufficient contact length at the shoulder when the tire is in contact with the ground, which is advantageous for improving uneven wear resistance.

[0013] In the present invention, the "contact width" and "contact length" of the tread portion refer to the axial length (contact width) and circumferential length (contact length) of the contact area when the tire is mounted on a standard rim, inflated to a standard internal pressure, placed vertically on a flat surface, and a standard load is applied. Specifically, the contact width W is the distance in the tire width direction between the contact ends measured under the above conditions, and the shoulder land portion width Wsh is the distance in the tire width direction between the inner end of each shoulder land portion in the tire width direction (the groove wall on the outer side in the tire width direction of the shoulder main groove that defines the shoulder land portion) and the contact end. The contact length Lc is measured as the circumferential length at the center position in the tire width direction of the tread center land portion included in the contact area under the above conditions. The contact length Ls is measured as the circumferential length at the center position in the tire width direction of the axially outermost land portion row included in the contact area under the above conditions. "Regular rim" refers to the rim that is specified for each tire by the standard system that includes the standard on which the tire is based, for example, the standard rim for JATMA, "Design Rim" for TRA, or "Measuring Rim" for ETRTO. "Regular internal pressure" refers to the air pressure that is specified for each tire by the standard system that includes the standard on which the tire is based, for example, the maximum air pressure for JATMA, the maximum value listed in the table "TIRE LOAD LIMITS AT VARIOUS COLD INFLATION PRESSURES" for TRA, and "INFLATION PRESSURE" for ETRTO, but if the tire is for a passenger car, it is 180kPa. "Normal load" refers to the load determined for each tire by each standard in the system of standards on which the tire is based. In the case of JATMA, this is the maximum load capacity. In the case of TRA, this is the maximum value described in the table "TIRE LOAD LIMITS AT VARIOUS COLD INFLATION PRESSURES." In the case of ETRTO, this is the "LOAD CAPACITY." However, when the tire is for a passenger car, this is a load equivalent to 88% of the above load. [Brief description of the drawings]

[0014] [Figure 1]FIG. 1 is a meridian cross-sectional view showing an example of a heavy duty pneumatic tire of the present invention. [Diagram 2] FIG. 2 is a front view showing an example of a tread portion of a heavy duty pneumatic tire of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] The configuration of the present invention will be described in detail below with reference to the accompanying drawings.

[0016] As shown in Fig. 1, the heavy-duty pneumatic tire of the present invention includes a tread portion 1 that contacts the road surface, a pair of sidewall portions 2 arranged on both sides of the tread portion 1, and a pair of bead portions 3 arranged on the tire radially inward side of the sidewall portions 2. In Fig. 1, the symbol CL indicates the tire equator, and the symbol E indicates the ground contact edge. Although not depicted in Fig. 1 because it is a meridian cross section, the tread portion 1, the sidewall portions 2, and the bead portions 3 each extend in the tire circumferential direction to form an annular shape, thereby forming a basic toroidal structure of a pneumatic tire. The following explanation using Fig. 1 is basically based on the meridian cross section shown in the figure, but each tire component extends in the tire circumferential direction to form an annular shape.

[0017] A carcass layer 4 is installed between a pair of left and right bead portions 3. This carcass layer 4 includes a plurality of reinforcing cords extending in the tire radial direction, and is folded back from the inside to the outside in the tire width direction around a bead core 5 arranged in each bead portion 3. In addition, a bead filler 6 is arranged on the outer periphery of the bead core 5, and this bead filler 6 is sandwiched between the main body portion and the folded back portion of the carcass layer 4.

[0018] A plurality of belt layers 7 (four layers in FIG. 1) are embedded on the outer circumferential side of the carcass layer 4 in the tread portion 1. Each belt layer 7 includes a plurality of reinforcing cords (steel cords) oriented in a predetermined direction. The plurality of belt layers 7 may include a cross belt pair. The cross belt pair is a combination of at least two belt layers in which the inclination angle of the reinforcing cords with respect to the tire circumferential direction is set in the range of 10° to 40°, and the inclination direction of the reinforcing cords is reversed between the layers so that the reinforcing cords cross each other. In addition to the cross belt pair, a high-angle belt layer in which the inclination angle of the reinforcing cords with respect to the tire circumferential direction is set in the range of 40° to 70°, a protective belt layer arranged in the outermost layer and having a width of 85% or less of the other belt layers, a circumferential reinforcing layer in which the angle of the reinforcing cords with respect to the tire circumferential direction is set in the range of 0° to 5°, and the like may be optionally provided. For example, in FIG. 1, one protective belt layer is arranged in the outermost layer, one high-angle belt layer is arranged in the innermost layer, and the other two layers are cross belt pairs. Furthermore, a belt reinforcing layer (not shown) may be provided on the outer circumferential side of the belt layer 7. The belt reinforcing layer may be made of, for example, organic fiber cords oriented in the tire circumferential direction. The organic fiber cords constituting the belt reinforcing layer 8 may be set at an angle of, for example, 0° to 5° with respect to the tire circumferential direction.

[0019] A tread rubber layer 10 is disposed on the outer peripheral side of the carcass layer 4 in the tread portion 1, a side rubber layer 20 is disposed on the outer peripheral side (outside in the tire width direction) of the carcass layer 4 in the sidewall portion 2, and a rim cushion rubber layer 30 is disposed on the outer peripheral side (outside in the tire width direction) of the carcass layer 4 in the bead portion 3. A belt cushion layer 40 is disposed in a region having a substantially triangular cross section between the tire width direction end portion of the belt layer 7 and the carcass layer 4. The tread rubber layer 10 may have a structure in which two types of rubber layers with different physical properties (a cap tread layer 11 constituting the tread surface of the tread portion 1 and an under tread layer 12 disposed on its inner peripheral side) are laminated in the tire radial direction.

[0020] Since the present invention mainly relates to the tread rubber layer 10 (particularly the cap tread layer 11) and the belt cushion layer 40, as long as the tread portion 1 (tread rubber layer 10) is composed of the cap tread layer 11 and the under tread layer 12 and is provided with the belt cushion layer 40, the basic structures of the other parts are not limited to the above-mentioned structures.

[0021] In the present invention, the tread rubber refers to the rubber constituting the above-mentioned tread rubber layer 10. When the tread portion 1 (tread rubber layer 10) is composed of a cap tread layer 11 and an under tread layer 12, the tread rubber refers to the rubber constituting the cap tread layer 11. The rubber composition constituting the tread rubber contains a diene rubber as a rubber component, and in particular, necessarily contains an isoprene rubber. In addition, it may contain butadiene rubber or styrene butadiene rubber as an option.

[0022] The isoprene-based rubber used in the tread rubber can be any rubber that is commonly used in rubber compositions for tires. For example, various natural rubbers, epoxidized natural rubbers, and various synthetic polyisoprene rubbers can be mentioned. The content of the isoprene-based rubber is 90% by mass or more, preferably 93% by mass to 100% by mass, when the total rubber components in the rubber composition constituting the tread rubber are taken as 100% by mass. By containing a specific amount of isoprene-based rubber in this way, it is possible to achieve a good balance between wear resistance and fuel economy. If the content of the isoprene-based rubber is less than 90% by mass, chipping resistance is deteriorated.

[0023] In the tread rubber, silica and carbon black are always blended as fillers. When the tread rubber contains silica as a filler, it is advantageous to improve fuel efficiency. Also, when the tread rubber contains carbon black as a filler, it is advantageous to improve uneven wear resistance. As described above, the filler always contains silica and carbon black, but other fillers can also be blended. Examples of other fillers include calcium carbonate, magnesium carbonate, talc, clay, alumina, aluminum hydroxide, titanium oxide, and calcium sulfate. These other fillers may be used alone or in combination of two or more.

[0024] The amount of the filler used in the tread rubber (total amount of silica and carbon black) is 60 parts by mass or less, preferably 40 to 60 parts by mass, and more preferably 45 to 60 parts by mass, per 100 parts by mass of the rubber component. If the amount of the filler exceeds 60 parts by mass, heat buildup and processability are reduced.

[0025] When silica and carbon black are blended as fillers, the ratio of the amount of carbon black to silica in the filler is set to 3:2 to 1:1, preferably 4:3 to 1:1. In other words, the amount of carbon black in the filler is set to 1 to 1.5 times, preferably 1 to 1.3 times, the amount of silica in the filler. Blending carbon black and silica in an appropriate ratio like this is advantageous for achieving both low rolling resistance and uneven wear resistance. If the ratio of the amount of carbon black to silica in the filler is out of the above range, low rolling resistance or uneven wear resistance will deteriorate.

[0026] The amount of carbon black used as a filler in the tread rubber is preferably 50% by mass to 60% by mass, more preferably 50% by mass to 56% by mass, when the entire filler used in the tread rubber is taken as 100% by mass. If the carbon black content is less than 50% by mass, the effect of improving uneven wear resistance is limited. If the carbon black content exceeds 60% by mass, the effect of improving low rolling resistance is limited. In addition, the amount of carbon black to be mixed with respect to 100 parts by mass of the rubber component constituting the tread rubber is preferably 23 parts by mass to 35 parts by mass, more preferably 28 parts by mass to 35 parts by mass. If the amount of carbon black to be mixed with respect to 100 parts by mass of the rubber component is less than 23 parts by mass, the effect of improving uneven wear resistance is limited. If the amount of carbon black to be mixed with respect to 100 parts by mass of the rubber component is more than 36 parts by mass, the effect of improving low rolling resistance is limited.

[0027] The nitrogen adsorption specific surface area N2SA of the carbon black used in the tread rubber is not particularly limited, but is preferably 85 m 2 / g~150m 2 / g, more preferably 85m 2 / g~120m 2 / g. In this way, the use of carbon black with an appropriate particle size is advantageous in achieving both resistance to uneven wear and low rolling resistance. The nitrogen adsorption specific surface area (N2SA) of carbon black is 85m 2 If the nitrogen adsorption specific surface area (N2SA) of carbon black is less than 150 m 2 If it exceeds 1 / g, the effect of improving low rolling resistance cannot be expected to be sufficient. The nitrogen adsorption specific surface area N2SA of carbon black is measured in accordance with JIS K6217-2.

[0028] As the silica used as a filler in the tread rubber, those generally used in rubber compositions for tires can be used. For example, wet silica (hydrated silicic acid), dry silica (anhydrous silicic acid), calcium silicate, aluminum silicate, etc. can be mentioned, and these may be used alone or in combination of two or more kinds.

[0029] The content of silica used in the tread rubber is preferably 40% by mass to 50% by mass, more preferably 40% by mass to 45% by mass, when the entire filler is taken as 100% by mass. If the content of silica is less than 40% by mass, the effect of improving fuel economy performance is limited. If the content of silica exceeds 50% by mass, the effect of improving uneven wear resistance is limited. In addition, the compounding amount of silica to 100 parts by mass of the rubber component constituting the tread rubber is 18 parts by mass to 30 parts by mass, preferably 20 parts by mass to 28 parts by mass. In this way, by containing sufficient silica in the entire tread rubber, it is possible to further improve the fuel economy performance. If the compounding amount of silica is less than 18 parts by mass, the effect of improving fuel economy performance is limited. If the compounding amount of silica exceeds 30 parts by mass, the effect of improving uneven wear resistance is limited.

[0030] The CTAB adsorption specific surface area of ​​the silica used in the tread rubber is not particularly limited, but is preferably 150 m 2 / g~220m 2 / g, more preferably 150m 2 / g~180m 2 / g. The CTAB adsorption specific surface area of ​​silica is preferably 150m 2 If the specific surface area of ​​the silica by CTAB adsorption is less than 220 m 2 When the specific surface area exceeds 1 / g, the effect of improving low rolling resistance may not be sufficiently obtained. In this specification, the CTAB adsorption specific surface area of ​​silica is a value measured according to ISO 5794.

[0031] In the tread rubber, it is preferable to compound a silane coupling agent together with silica. By compounding a silane coupling agent, the dispersibility of silica in the rubber component can be improved, and abrasion resistance and fuel economy performance can be improved in a well-balanced manner. The type of silane coupling agent is not particularly limited as long as it can be used in a rubber composition containing silica, and examples of the silane coupling agent include sulfur-containing silane coupling agents such as bis-(3-triethoxysilylpropyl) tetrasulfide, bis(3-triethoxysilylpropyl) disulfide, 3-trimethoxysilylpropyl benzothiazole tetrasulfide, γ-mercaptopropyl triethoxysilane, and 3-octanoylthiopropyl triethoxysilane.

[0032] When a silane coupling agent is blended in the tread rubber, the blending amount is not particularly limited, but is preferably 1% by mass to 20% by mass, more preferably 5% by mass to 15% by mass, based on the blending amount of the silica. If the blending amount of the silane coupling agent is less than 1% by mass of the silica blending amount, the dispersion of the silica cannot be sufficiently improved. If the blending amount of the silane coupling agent is more than 20% by mass of the silica blending amount, the silane coupling agent condenses with itself, and the desired tensile strength of the rubber composition cannot be obtained.

[0033] In the tread rubber, it is preferable to compound a guanidine-based vulcanization accelerator and a sulfenamide-based vulcanization accelerator as a vulcanization accelerator. Examples of the guanidine-based vulcanization accelerator include diphenyl guanidine (DPG), di(o-tolyl)guanidine, and o-tolyl bigianide. Examples of the sulfenamide-based vulcanization accelerator include N,N-dicyclohexyl-1,3-benzothiazole-2-sulfenamide (DZ), N-cyclohexyl-2-benzothiazole sulfenamide (CZ), N-oxydiethylene-2-benzothiazole sulfenamide (OBS), and N-(tert-butyl)benzothiazole-2-sulfenamide (NS). In this way, the combined use of two types of vulcanization accelerators, a guanidine-based vulcanization accelerator and a sulfenamide-based vulcanization accelerator, is advantageous in achieving both low rolling resistance and chipping resistance.

[0034] When using a guanidine vulcanization accelerator and a sulfenamide vulcanization accelerator in combination, the amount of the guanidine vulcanization accelerator, Ac G and the amount of sulfenamide vulcanization accelerator Ac S and preferably 0.3≦Ac G / Ac S ≦5.0, more preferably 0.4≦Ac G / Ac S It is preferable that the relationship of Ac≦2.0 is satisfied. This improves the rubber properties of the tread rubber, which is advantageous in achieving both low rolling resistance and chipping resistance. G / Ac S If the blend ratio Ac is less than 0.3, the reaction between the sulfenamide vulcanization accelerator and the silane coupling agent will result in excessive tread hardness, and the effect of improving uneven wear resistance will be limited. G / Ac S If the ratio exceeds 5.0, the vulcanization speed will be so fast that the tread portion will be over-vulcanized, and the effect of improving low rolling resistance will be limited.

[0035] The amount of each of the guanidine-based vulcanization accelerator and the sulfenamide-based vulcanization accelerator is not particularly limited, but the amount of the guanidine-based vulcanization accelerator is preferably 0.2 to 1.2 parts by mass, more preferably 0.4 to 1.0 parts by mass, relative to 100 parts by mass of the rubber composition constituting the tread rubber. The amount of the sulfenamide-based vulcanization accelerator is preferably 0.6 to 1.6 parts by mass, more preferably 0.8 to 1.2 parts by mass, relative to 100 parts by mass of the rubber composition constituting the tread rubber. Furthermore, the total amount of the guanidine-based vulcanization accelerator and the sulfenamide-based vulcanization accelerator is preferably 1.4 to 2.0 parts by mass, more preferably 1.6 to 2.0 parts by mass, relative to 100 parts by mass of the rubber composition constituting the tread rubber. By blending an appropriate amount of the vulcanization accelerator in this way, it is advantageous to achieve both low rolling resistance and uneven wear resistance.

[0036] In the present invention, the belt cushion rubber is a rubber constituting the above-mentioned belt cushion layer 40. The rubber composition constituting this belt cushion rubber contains a diene rubber as a rubber component, and in particular, necessarily contains an isoprene rubber. In addition, it may contain a butadiene rubber as an option.

[0037] The isoprene-based rubber used in the belt cushion rubber can be any rubber that is commonly used in rubber compositions for tires. For example, various natural rubbers, epoxidized natural rubbers, and various synthetic polyisoprene rubbers can be mentioned. The content of the isoprene-based rubber is 90% by mass or more, preferably 93% by mass to 100% by mass, when the total rubber components in the rubber composition constituting the belt cushion rubber are taken as 100% by mass. By containing a specific amount of isoprene-based rubber in this way, it is possible to achieve a good balance between abrasion resistance and fuel economy. If the content of the isoprene-based rubber is less than 90% by mass, durability is deteriorated.

[0038] In the belt cushion rubber, carbon black is always blended as a filler. The inclusion of carbon black as a filler in the belt cushion rubber is advantageous in improving durability. As described above, the filler always contains carbon black, but other fillers can also be blended. Examples of other fillers include silica, calcium carbonate, magnesium carbonate, talc, clay, alumina, aluminum hydroxide, titanium oxide, and calcium sulfate. These other fillers may be used alone or in combination of two or more.

[0039] The amount of carbon black used in the belt cushion rubber is 45 parts by mass or less, preferably 30 to 45 parts by mass, and more preferably 35 to 45 parts by mass, per 100 parts by mass of the rubber component constituting the belt cushion rubber. If the amount of carbon black exceeds 45 parts by mass, heat generation and processability are reduced. A plurality of types of carbon black may be compounded in the belt cushion rubber, and in that case, the total amount of the plurality of types of carbon black may satisfy the above range. When carbon black is used in combination with another filler, particularly when carbon black is used in combination with silica, the amount of the filler (the total amount of silica and carbon black) is preferably set to 45 parts by mass or less per 100 parts by mass of the rubber component constituting the belt cushion rubber.

[0040] The nitrogen adsorption specific surface area N2SA of the carbon black used in the belt cushion rubber is not particularly limited, but is preferably 40 m 2 / g~95m 2 / g, more preferably 65m 2 / g~80m 2 / g. In this way, the use of carbon black with an appropriate particle size is advantageous in achieving both low rolling resistance and durability. The nitrogen adsorption specific surface area (N2SA) of carbon black is 40m 2 If the nitrogen adsorption specific surface area (N2SA) of carbon black is less than 95 m 2If it exceeds 1 / g, the effect of improving low rolling resistance cannot be expected to be sufficient. The nitrogen adsorption specific surface area N2SA of carbon black is measured in accordance with JIS K6217-2.

[0041] The carbon black used in the belt cushion rubber preferably has a particle size different from that of the carbon black used in the tread rubber. Specifically, the nitrogen adsorption specific surface area N2SA of the carbon black used in the belt cushion rubber is preferably smaller than the nitrogen adsorption specific surface area N2SA of the carbon black used in the tread rubber. By using different types of carbon black in the tread rubber and the belt cushion rubber, it is possible to impart rubber physical properties suitable for each member.

[0042] The heavy-duty pneumatic tire of the present invention comprises a tread rubber layer 10 made of the above-mentioned tread rubber and a belt cushion layer 40 made of the above-mentioned belt cushion rubber, and in providing these two layers, the hardness Hc of the tread rubber at 20°C and the hardness Hb of the belt cushion rubber at 20°C satisfy the relationship of 1.20≦Hc / Hb≦1.50, preferably 1.20≦Hc / Hb≦1.40. By setting the hardness ratio Hc / Hb of the tread rubber and the belt cushion rubber within an appropriate range in this way, the aforementioned uneven wear resistance can be exhibited well while ensuring durability. If the hardness ratio Hc / Hb is less than 1.20 or exceeds 1.50, durability decreases.

[0043] Although the hardness of each rubber layer is not particularly limited, the hardness Hc of the tread rubber at 20°C is preferably 62 to 72, more preferably 64 to 70. In this way, the tread rubber having a suitable hardness is advantageous for improving uneven wear resistance. If the hardness Hc is less than 62 or exceeds 72, the uneven wear resistance decreases. Similarly, the hardness Hb of the belt cushion rubber at 20°C is preferably 50 to 60, more preferably 50 to 57. In this way, the belt cushion rubber having a suitable hardness is advantageous for improving durability. If the hardness Hb is less than 50 or exceeds 60, the durability decreases.

[0044] The heavy-duty pneumatic tire of the present invention is not particularly limited in structure as long as it has a tread rubber layer 10 made of the above-mentioned tread rubber and a belt cushion layer 40 made of the above-mentioned belt cushion rubber, but preferably has a structure as shown in Figs. 1 and 2, in which a plurality of circumferential grooves 50 (four in the figure) extending along the tire circumferential direction are formed on the surface of the tread portion, and a pair of the plurality of circumferential grooves 50 arranged on the outermost side in the tire width direction is defined as a shoulder main groove 51, and a shoulder land portion 60 is defined on the outer side of each shoulder main groove 51 in the tire width direction. In this case, the width Wsh of each shoulder land portion 60 preferably satisfies the relationship of 0.15 ≦ Wsh / W ≦ 0.27, more preferably 0.18 ≦ Wsh / W ≦ 0.24 with respect to the contact width W of the tread portion 1. By having such a structure, the land portion (amount of rubber) arranged in the shoulder region that contributes to uneven wear resistance is optimized, which is advantageous for improving uneven wear resistance. If the ratio Wsh / W is less than 0.15, the amount of rubber in the shoulder land portion 60 that contributes to uneven wear resistance is insufficient, resulting in poor uneven wear resistance. If the ratio Wsh / W exceeds 0.27, wet performance (traction performance on wet roads) is poor.

[0045] In particular, as shown in FIG. 1, the multiple circumferential grooves 50 may include a pair of shoulder main grooves 51 and multiple (two in the figure) center circumferential grooves 52 arranged on the inner side of the shoulder main grooves 51 in the tire width direction. When such a center circumferential groove 52 is included, the center circumferential groove 52 preferably has a groove width smaller than that of the shoulder main groove 51. Specifically, the groove width Wo of the shoulder main groove 51 and the groove width Wi of the center circumferential groove 52 preferably satisfy the relationship of 0.20≦Wi / Wo≦1.20, more preferably 0.20≦Wi / Wo≦0.90. In this way, setting the groove width of the multiple circumferential grooves 50 within an appropriate range is advantageous for achieving both wet performance and low rolling resistance. If the groove width ratio Wi / Wo is less than 0.20, wet performance is reduced. If the groove width ratio Wi / Wo exceeds 1.20, low rolling resistance is reduced. Although the individual groove widths of the respective grooves are not particularly limited, the groove width Wo of the shoulder main grooves 51 can be set to, for example, 10.5 mm to 14.0 mm, and the groove width Wi of the center circumferential groove 52 can be set to, for example, 3.5 mm to 14.5 mm.

[0046] Also, as shown in FIG. 1, when the thickness of the tread rubber measured on the tire equator CL is defined as the tread rubber gauge Gcc, this tread gauge Gcc is preferably 12.0 mm or more and 30.0 mm or less, more preferably 16.0 mm or more and 30.0 mm or less. In this way, it is advantageous to improve wear resistance by ensuring a sufficient amount of rubber in the tread rubber. If the tread gauge Gcc is less than 12.0 mm, wear resistance decreases. If the tread gauge Gcc is more than 30.0 mm, low rolling resistance decreases.

[0047] In Fig. 2, the area indicated by the dashed line is a schematic diagram showing the contact shape (contact area) when the heavy-duty pneumatic tire of the present invention is mounted on a regular rim, inflated to the regular internal pressure, placed vertically on a flat surface and subjected to a regular load, and when the contact length of the tread center land row in this contact shape is Lc and the contact length of the land row on the outermost side in the tire axial direction is Ls, the heavy-duty pneumatic tire of the present invention preferably has a maximum contact length Lc and an outer contact length Ls that satisfy the relationship of 0.80 ≦ Ls / Lc ≦ 1.05, and more preferably 0.85 ≦ Ls / Lc ≦ 1.00. This ensures a sufficient contact length of the shoulder portion when the tire is in contact with the ground, which is advantageous for improving uneven wear resistance.

[0048] The heavy-duty pneumatic tire of the present invention maintains or improves each of the rolling resistance, uneven wear resistance, and durability, and achieves a good balance between these, through the cooperation of the compositions and physical properties of the tread rubber and belt cushion rubber described above, as well as the effects of the tire structure.

[0049] The present invention will be further described below with reference to examples, but the scope of the present invention is not limited to these examples. EXAMPLES

[0050] Ten types of tread rubber (CAP1-10) with the composition shown in Table 1 and five types of belt cushion rubber (BC1-5) with the composition shown in Table 2 were prepared, and a test tire (tire size: 11R22.5) was produced using a tread layer composed of any of the tread rubbers (CAP1-10) and a belt cushion layer composed of any of the belt cushion rubbers (BC1-5) in combination as shown in Tables 3-5. Each test tire has a basic structure shown in FIG. 1 and a tread pattern shown in FIG. 2, and the hardness Hc of the tread rubber, the hardness Hb of the belt cushion rubber, the hardness ratio Hc / Hb, the tread width W, the width Wsh of the shoulder land portion, the ratio Wsh / W of these widths, the tread gauge Gcc, the groove width Wo of the shoulder main groove, the groove width Wi of the center circumferential groove, the ratio Wi / Wo of these groove widths, and the ground contact length ratio Ls / Lc are set as shown in Tables 3-5, respectively.

[0051] Using each test tire, evaluation of low rolling resistance, resistance to uneven wear, and durability was performed by the methods described below.

[0052] Low rolling resistance Each test tire was mounted on a wheel with a rim size of 22.5 x 9.0, and the rolling resistance coefficient of the test tire was measured using a drum testing machine with a drum diameter of 1707 mm in accordance with ISO28580 under conditions of a load of 28.76 kN, air pressure of 900 kPa, and speed of 60 km / h. The evaluation results were expressed as an index with standard example 1 being 100. The smaller the index value, the lower the rolling resistance, meaning that the tire has excellent low rolling resistance.

[0053] Resistant to uneven wear Each test tire was mounted on a wheel with a rim size of 22.5 x 9.0, and the air pressure was set to 830 kPa before being attached to a test vehicle (2-D tractor head). After driving 50,000 km on a test course consisting of a paved road surface, the wear amount of the center circumferential groove and the shoulder main groove (difference in groove depth before and after driving) was measured at five points on the circumference of the tire, and the difference between the wear amount of the center circumferential groove and the wear amount of the shoulder main groove was calculated. The evaluation results were expressed as an index using the reciprocal of the measured value, with standard example 1 being 100. The higher the index value, the smaller the difference in wear amount between the center region and the shoulder region, and the better the resistance to uneven wear.

[0054] durability Each test tire was mounted on a wheel with a rim size of 22.5 x 9.0, and a drum testing machine with a drum diameter of 1707 mm was used to measure the distance traveled until the tire broke down under the following conditions: load 41.19 kN, air pressure 830 kPa, speed 45 km / h, slip angle ±2° (frequency 0.1 Hz). The evaluation results were expressed as an index with standard example 1 being 100. The higher the index value, the longer the tire's distance traveled until it broke down, meaning that it had better durability.

[0055] [Table 1]

[0056] The types of raw materials used in Table 1 are shown below. NR: Natural rubber, RSS No.3 BR: Butadiene rubber, Zeon Nipol 1220 CB1: Carbon black (grade: ISAF), Niteron #300IH (Dst: 83 nm, nitrogen adsorption specific surface area N2SA: 115 m 2 / g) CB2: Carbon black (grade: HAF), Niteron #200IN manufactured by Nippon Steel Carbon Co., Ltd. (Dst: 114 nm, nitrogen adsorption specific surface area N2SA: 72 m 2 / g) Silica: ZEOSIL 1165MP manufactured by Solvay Japan (CTAB adsorption specific surface area: 165 m 2 / g) Anti-aging agent: Santoflex 6PPD manufactured by Solutia Europe Wax: Nippon Seiro OZOACE-0015A Zinc oxide: 3 types of zinc oxide manufactured by Seido Chemical Industry Co., Ltd. Stearic acid: Stearic acid YR manufactured by NOF Corporation Vulcanization accelerator 1: Sulfenamide vulcanization accelerator Noccela NS-P (NS) manufactured by Ouchi Shinko Chemical Co., Ltd. Vulcanization accelerator 2: Guanidine-based vulcanization accelerator, Sumitomo Chemical Co., Ltd., Soxinol DG (DPG) Sulfur: Oil-treated sulfur manufactured by Karuizawa Refinery

[0057] [Table 2]

[0058] The types of raw materials used in Table 2 are shown below. NR: Natural rubber, RSS No.3 BR: Butadiene rubber, Zeon Nipol 1220 CB1: Carbon black (grade: ISAF), Niteron #300IH (Dst: 83 nm, nitrogen adsorption specific surface area N2SA: 115 m 2 / g) CB2: Carbon black (grade: HAF), Niteron #200IN manufactured by Nippon Steel Carbon Co., Ltd. (Dst: 114 nm, nitrogen adsorption specific surface area N2SA: 72 m 2 / g) CB3: Carbon black (grade: FAF), Nitelon #10N manufactured by Nippon Steel Carbon Co., Ltd. (Dst: 166 nm, nitrogen adsorption specific surface area N2SA: 41 m 2 / g) Anti-aging agent: Santoflex 6PPD manufactured by Solutia Europe Oil: Idemitsu Kosan Diana Process NH-70S Zinc oxide: 3 types of zinc oxide manufactured by Seido Chemical Industry Co., Ltd. Stearic acid: NOF Corporation YR stearic acid Vulcanization accelerator 1: Noccela NS-P (NS) manufactured by Ouchi Shinko Chemical Co., Ltd. Sulfur: Oil-treated sulfur manufactured by Karuizawa Refinery

[0059] [Table 3]

[0060] [Table 4]

[0061] [Table 5]

[0062] As is clear from Tables 3 to 5, compared to Reference Example 1, Examples 1 to 18 maintained or improved low rolling resistance, uneven wear resistance, and durability, and achieved a good balance between these performance properties.

[0063] On the other hand, in Comparative Example 1, the hardness ratio Hc / Hb was small, so the durability was reduced. In Comparative Example 2, CAP1 (the ratio of the compounding amount of carbon black and silica is outside the range of the present invention: the carbon black amount is excessive) which does not satisfy the conditions of the present invention is used as the tread rubber, so the uneven wear resistance and durability were reduced. In Comparative Example 3, CAP2 (the ratio of the compounding amount of carbon black and silica is outside the range of the present invention: the silica amount is excessive) which does not satisfy the conditions of the present invention is used as the tread rubber, so the uneven wear resistance was reduced. In Comparative Example 4, CAP3 (the compounding amount of filler is excessive) which does not satisfy the conditions of the present invention is used as the tread rubber, so the low rolling resistance was deteriorated. In Comparative Example 5, CAP4 (the content of isoprene-based rubber is too small) which does not satisfy the conditions of the present invention is used as the tread rubber, so the uneven wear resistance was reduced. In Comparative Example 6, BC1 (the compounding amount of filler (total amount of carbon black) is excessive) which does not satisfy the conditions of the present invention is used as the belt cushion rubber, so the durability was reduced. In Comparative Example 7, durability was reduced because BC2 (content of isoprene-based rubber is too small) which does not satisfy the conditions of the present invention was used as the belt cushion rubber. In Comparative Example 8, durability was reduced because the hardness ratio Hc / Hb was large. [Explanation of symbols]

[0064] 1 Tread section 2 Sidewall 3 Bead section 4 Carcass layer 5 Bead Core 6 Bead Filler 7 Belt layer 8 Belt reinforcement layer 10 Tread rubber layer 11 Cap tread layer 12 Undertread layer 20 Side rubber layer 30 Rim cushion rubber layer 40 Belt cushion layer 50 Circumferential groove 51 Shoulder main groove 52 Center circumferential groove CL Tire Equator

Claims

1. A heavy-duty pneumatic tire comprising a tread portion extending in a circumferential direction of the tire and forming an annular shape, a pair of sidewall portions disposed on both sides of the tread portion, and a pair of bead portions disposed on the tire radially inward side of the sidewall portions, at least one carcass layer mounted between the pair of bead portions, and a plurality of belt layers disposed on the outer peripheral side of the carcass layer in the tread portion, with a belt cushion layer disposed between the tire width direction end portions of the belt layer and the carcass layer, the tread rubber constituting the tread portion is made of a rubber composition in which 100 parts by mass of a rubber component containing 90% by mass or more of an isoprene-based rubber is blended with 60 parts by mass or less of a filler containing carbon black and silica, and the blending ratio of the carbon black to the silica in the filler is 3:2 to 1:1; The belt cushion rubber constituting the belt cushion layer is made of a rubber composition in which 45 parts by mass or less of carbon black is blended with 100 parts by mass of a rubber component containing 90% by mass or more of isoprene-based rubber, A heavy-duty pneumatic tire, characterized in that the hardness Hc of said tread rubber at 20° C. and the hardness Hb of said belt cushion rubber at 20° C. satisfy the relationship: 1.2≦Hc / Hb≦1.

5.

2. The rubber composition constituting the tread rubber contains a guanidine-based vulcanization accelerator and a sulfenamide-based vulcanization accelerator, and the blending amount Ac of the guanidine-based vulcanization accelerator is G and the blending amount Ac of the sulfenamide vulcanization accelerator S and 0.3≦Ac G / Ac S 2. The heavy duty pneumatic tire according to claim 1, wherein the relationship of ≦5.0 is satisfied.

3. 3. The heavy-duty pneumatic tire according to claim 1, wherein a plurality of circumferential grooves extending along the tire circumferential direction are formed on the surface of the tread portion, and a pair of the plurality of circumferential grooves arranged on the outermost sides in the tire width direction are shoulder main grooves. When these grooves are defined as shoulder main grooves, shoulder land portions are defined on the outer sides in the tire width direction of each shoulder main groove, and a width Wsh of each shoulder land portion satisfies the relationship 0.15≦Wsh / W≦0.27 with respect to a ground contact width W of the tread portion.

4. 4. The heavy-duty pneumatic tire according to claim 3, wherein the plurality of circumferential grooves include the shoulder main groove and a center circumferential groove disposed more inward in the tire width direction than the shoulder main groove, and a groove width Wo of the shoulder main groove and a groove width Wi of the center circumferential groove satisfy a relationship of 0.20≦Wi / Wo≦1.

20.

5. 5. The heavy-duty pneumatic tire according to claim 1, wherein a tread gauge Gcc measured at the tire equator is 12.0 mm or more and 30.0 mm or less.

6. The heavy-duty pneumatic tire according to any one of claims 1 to 5, characterized in that, when the contact length in the tread center land row is defined as a maximum contact length Lc, and the contact length in the land row at the outermost side of the tire axial direction is defined as an outer contact length Ls, the maximum contact length Lc and the outer contact length Ls satisfy the relationship of 0.80≦Ls / Lc≦1.05.

Images