Bio-based EVA composition, articles thereof and methods thereof

Abstract

The copolymer can comprise ethylene and vinyl acetate, where the ethylene is derived at least in part from a renewable carbon source. Embodiments can also be directed to curable polymer compositions, expandable polymer compositions, articles, cured articles, and expanded articles formed from or comprising such ethylene and vinyl acetate copolymers, where the ethylene is derived at least in part from a renewable carbon source. Methods of making ethylene vinyl acetate copolymers are included.

Description

[Background technology]

[0001] Polyolefin copolymers such as ethylene vinyl acetate (EVA) can be used to make a variety of articles, including films, moldings, foams, etc. In general, polyolefins are widely used plastics around the world due to their versatility in a wide range of applications. EVA can have features such as excellent processability, low manufacturing cost, flexibility, low density, and recyclability. [Prior art documents] [Patent documents]

[0002] [Patent Document 1] U.S. Patent No. 9,181,143 [Patent Document 2] U.S. Patent No. 4,396,789 [Patent Document 3] U.S. Patent No. 5,840,971 [Patent Document 4] PCT / BR2017 / 050398 [Patent Document 5] WO201694161A1 [Non-patent literature]

[0003] [Non-Patent Document 1] "Selective catalytic oxidation of ethanol to acetic acid on dispersed Mo-V-Nb mixed oxides" Li X, Iglesia E., Chemistry 2007, 13(33), pp. 9324-30 [Non-Patent Document 2] “The Production of Vinyl Acetate Monomer as a Co-Product from the Non-Catalytic Cracking of Soybean Oil” Benjamin Jones, Michael Linnen, Brian Tande, and Wayne Seames, Processes, 2015, 3, 61-9-633 [Non-Patent Document 3] "Acetic acid bacteria: A group of bacteria with versatile biotechnological applications" Saichana N, Matsushita K, Adachi O, Frebort I, Frebortova J., Biotechnol Adv. November 2015 1;33(6Pt2):1260~71 [Non-Patent Document 4] "Biotechnological applications of acetic acid bacteria" Raspor P, Goranovic D., Crit Rev Biotechnol.2008;28(2):101-24 Summary of the Invention [Means for solving the problem]

[0004] This Summary is provided to introduce a selection of concepts that are further described below in the Detailed Description. This Summary is not intended to identify key features or essential features of the claimed subject matter, nor is it intended to be used as an aid in limiting the scope of the claimed subject matter.

[0005] In one aspect, embodiments disclosed herein relate to a copolymer of ethylene and vinyl acetate, wherein the ethylene is derived, at least in part, from a renewable carbon source.

[0006] In another aspect, embodiments disclosed herein relate to articles made from copolymers of ethylene and vinyl acetate, where the ethylene is derived, at least in part, from a renewable carbon source.

[0007] In another aspect, embodiments disclosed herein relate to a curable polymer composition comprising a copolymer of ethylene and vinyl acetate and at least a peroxidant, wherein the ethylene is derived, at least in part, from a renewable carbon source.

[0008] In yet another aspect, embodiments disclosed herein relate to a cured article made from a curable polymer composition comprising a copolymer of ethylene and vinyl acetate and at least a peroxidant, wherein the ethylene is derived, at least in part, from a renewable carbon source.

[0009] In yet another aspect, embodiments disclosed herein relate to an expandable polymer composition comprising a copolymer of ethylene and vinyl acetate and at least a blowing agent and a peroxidant, wherein the ethylene is derived, at least in part, from a renewable carbon source.

[0010] In another aspect, embodiments disclosed herein relate to an expanded article made from an expandable polymer composition comprising a copolymer of ethylene and vinyl acetate and at least a blowing agent and a peroxidant, wherein the ethylene is derived at least in part from a renewable carbon source.

[0011] In yet another aspect, embodiments disclosed herein relate to a method of producing an ethylene vinyl acetate copolymer, the method comprising polymerizing ethylene obtained at least in part from a renewable carbon source with vinyl acetate to produce the ethylene vinyl acetate copolymer.

[0012] In yet another aspect, embodiments disclosed herein relate to a method of producing ethylene vinyl acetate copolymer, the method including fermenting a renewable carbon source to produce ethanol, dehydrating the ethanol to produce ethylene, and polymerizing the ethylene and vinyl acetate to produce ethylene vinyl acetate copolymer.

[0013] Other aspects and advantages of the claimed subject matter will become apparent from the following description and the appended claims. [Brief description of the drawings]

[0014] [Figure 1] FIG. 1 illustrates an exemplary pathway for the production of bio-based vinyl acetate in one or more embodiments of the present disclosure. [Diagram 2] FIG. 1 illustrates several points related to the PFI method of measuring shrinkage of an article of one or more embodiments of the present disclosure. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] In one aspect, embodiments disclosed herein relate to a composition comprising an ethylene vinyl acetate (EVA) copolymer, wherein at least a portion of the ethylene of the elastomeric ethylene vinyl acetate copolymer is derived from a renewable carbon source, such as a plant-based material, i.e., forming a bio-based ethylene vinyl acetate copolymer.

[0016] EVA is a copolymer of the polyolefin family of elastomers formed by the random arrangement of units derived from the polymerization of ethylene and vinyl acetate at high temperature and pressure. EVA copolymers result in materials that can be processed like other thermoplastics, but can be endowed with rubber-like characteristics, including flexibility and elasticity. Furthermore, EVA copolymers can be used in a wide range of applications, such as adhesives, thin films, expanded articles, etc. The use of products derived from natural sources, as opposed to those obtained from fossil sources, has become increasingly popular as an effective means of reducing the increase in atmospheric carbon dioxide concentration, thus effectively limiting the expansion of the greenhouse effect. Thus, products obtained from natural raw materials differ in their renewable carbon content, as opposed to those derived from fossil sources. This renewable carbon content can be certified by the techniques described in the technical specification ASTM D 6866-18 "Standard Test Method for Determining Biobased Content of Solid, Liquid, and Gaseous Samples by Radiocarbon Analysis". Products obtained from renewable natural raw materials have the added property that they can be incinerated at the end of their life cycle, producing only non-fossil-derived CO2.

[0017] The polymer composition of the present disclosure may include an EVA copolymer in which the weight percent of ethylene in the EVA polymer ranges from a lower limit selected from one of 5 wt%, 25 wt%, 40 wt%, 60 wt%, 66 wt%, and 72 wt%, to an upper limit selected from one of 80 wt%, 85 wt%, 88 wt%, 92 wt%, and 95 wt%, any lower limit may be paired with any upper limit. It is further understood that of this total amount of ethylene, at least a portion of the ethylene is based on a renewable carbon source.

[0018] The polymer composition of the present disclosure can include EVA copolymers incorporating various ratios of ethylene and vinyl acetate, in addition to including one or more optional additional copolymers. The polymer composition of the present disclosure can include EVA copolymers in which the mass percentage of vinyl acetate content in the copolymer, as determined by ASTM D5594, ranges from a lower limit selected from one of 5 wt%, 8 wt%, 12 wt%, 15 wt%, and 20 wt%, to an upper limit selected from 25 wt%, 30 wt%, 35 wt%, 40 wt%, 60 wt%, 75 wt%, and 95 wt%, any lower limit can be paired with any upper limit. It is further understood that of this total amount of vinyl acetate, at least a portion of the vinyl acetate is based on a renewable carbon source.

[0019] Specifically, in one or more embodiments, the EVA copolymer exhibits a bio-based carbon content of at least 5% as determined by ASTM D6866-18B method. Additionally, other embodiments may include at least 10%, 20%, 40%, 50%, 60%, 80%, or 100% bio-based carbon. As previously mentioned, all of the bio-based or renewable carbon in the EVA polymer may be contributed from bio-based ethylene and / or bio-based vinyl acetate. Each of these is described below.

[0020] For example, in one or more embodiments, the renewable carbon source is one or more plant materials selected from the group consisting of sugar cane and sugar beet, maple, dates, palm sugar, sorghum, American agave, corn, wheat, barley, sorghum, rice, potatoes, cassava, sweet potatoes, algae, fruits, cellulose-containing materials, wine, hemicellulose-containing materials, lignin-containing materials, wood, straw, sugar cane bagasse, sugar cane leaves, corn stover, wood residues, paper, and combinations thereof.

[0021] In one or more embodiments, bio-based ethylene can be obtained by fermenting a renewable carbon source to produce ethanol, which can then be dehydrated to produce ethylene. It is further understood that the fermenting process also produces higher alcohol by-products in addition to ethanol. If higher alcohol by-products are present during dehydration, higher alkene impurities can be formed simultaneously with the ethanol. Thus, in one or more embodiments, the ethanol can be purified prior to dehydration to remove higher alcohol by-products, or in other embodiments, the ethylene can be purified to remove higher alkene impurities after dehydration.

[0022] Thus, ethanol of biological origin, known as bioethanol, is obtained by fermentation of sugars derived from cultures such as sugarcane and beet, or from hydrolyzed starch associated with other cultures, such as corn. It is also recalled that biobased ethylene can be obtained from products based on the hydrolysis of cellulose and hemicellulose, which can be found in many agricultural by-products, such as straw and sugarcane husks. This fermentation is carried out in the presence of various microorganisms, the most important of which is the yeast Saccharomyces cerevisiae. The ethanol obtained therefrom can be converted to ethylene by catalytic reactions, usually at temperatures above 300°C. Various catalysts, such as high surface area gamma-alumina, can be used for this purpose. Other examples include the teachings described in US Pat. No. 9,181,143 and US Pat. No. 4,396,789, which are incorporated herein by reference in their entirety.

[0023] On the other hand, bio-based vinyl acetate can also be used in one or more embodiments of the EVA copolymer of the present disclosure. Bio-based vinyl acetate can be produced by the oxidation of ethanol to produce acetic acid (which may be produced as described above), and then reacting ethylene and acetic acid to acyloxylate the ethylene to vinyl acetate. It is further understood that the ethylene reacted with acetic acid can also be produced from renewable resources as described above.

[0024] An exemplary pathway to obtain bio-based vinyl acetate is shown in FIG. 1. As shown initially, renewable starting materials, including those mentioned above, can be fermented and optionally purified to produce at least one alcohol (either ethanol or a mixture of alcohols including ethanol). The alcohol can be split into two portions, where the first portion can be introduced into a first reactor and the second portion can be introduced into a second reactor. In the first reactor, the alcohol can be dehydrated to produce an alkene (ethylene or a mixture of alkenes including ethylene, depending on whether purification was performed after fermentation), which can then be optionally purified to obtain ethylene. Those skilled in the art can recognize that if purification occurs before dehydration, there is no need to purify after dehydration, and vice versa. In the second reactor, the alcohol can be oxidized to obtain acetic acid, which can optionally be purified. In the third reactor, the ethylene produced in the first reactor and the acetic acid produced in the second reactor can be combined and reacted to acyloxylate the ethylene and produce vinyl acetate, which can then be isolated and optionally purified. Additional details on the oxidation of ethanol to produce acetic acid can be found in U.S. Pat. No. 5,840,971 and in "Selective catalytic oxidation of ethanol to acetic acid on dispersed Mo-V-Nb mixed oxides," Li X, Iglesia E., Chemistry 2007, 13(33), 9324-30.

[0025] However, the present disclosure is not so limited with respect to the pathway for producing acetic acid, but rather contemplates obtaining acetic acid from fatty acids as illustrated in Figure 1 and described in "The Production of Vinyl Acetate Monomer as a Co-Product from the Non-Catalytic Cracking of Soybean Oil" Benjamin Jones, Michael Linnen, Brian Tande, and Wayne Seames, Processes, 2015, 3, 61-9-633. Furthermore, the production of acetic acid from fermentation is carried out by acetogenic bacteria as described in "Acetic acid bacteria: A group of bacteria with versatile biotechnological applications" Saichana N, Matsushita K, Adachi O, Frebort I, Frebortova J., Biotechnol Adv. 2015 Nov 1;33(6Pt2):1260-71 and "Biotechnological applications of acetic acid bacteria" Raspor P, Goranovic D., Crit Rev Biotechnol. 2008;28(2):101-24. Furthermore, while FIG. 1 is directed to the production of vinyl acetate, it is understood that the ethylene production used to produce vinyl acetate can also be used to produce ethylene, which is then reacted with vinyl acetate to produce the EVA copolymer of the present disclosure. Thus, for example, the amount of ethanol fed to the first and second reactors, respectively, can vary depending on the relative amounts of ethylene and vinyl acetate to be polymerized.

[0026] The polymer composition of the present disclosure can include an EVA copolymer having a number average molecular weight (Mn) in kilodaltons (kDa) ranging from a lower limit selected from one of 5 kDa, 10 kDa, 20 kDa, and 25 kDa to an upper limit selected from one of 30 kDa, 35 kDa, 40 kDa, and 50 kDa, any lower limit can be paired with any upper limit.

[0027] The polymer composition of the present disclosure can include an EVA copolymer having a weight average molecular weight (Mw) in kilodaltons (kDa) ranging from a lower limit selected from one of 25 kDa, 50 kDa, 70 kDa, 90 kDa, and 110 kDa to an upper limit selected from one of 120 kDa, 140 kDa, 150 kDa, and 180 kDa, any lower limit can be paired with any upper limit.

[0028] The polymer composition of the present disclosure can include an EVA copolymer, the dispersity (Mw / Mn) of the EVA copolymer ranging from a lower limit selected from one of 1.0, 1.5, 3.0, and 4.0 to an upper limit selected from one of 5.0, 6.0, 7.0, and 8.0, any lower limit can be paired with any upper limit.

[0029] Molecular weight properties can be measured by GPC (gel permeation chromatography) experiments. Such experiments can be coupled in three directions, for example with an infrared detector IR5, a 4-bridge capillary viscometer (PolymerChar) and an 8-angle light scattering detector (Wyatt). A set of 4 mixed bed, 13 μm columns (Tosoh) can be used at a temperature of 140° C. The experiments can use a concentration of 1 mg / mL, a flow rate of 1 mL / min, dissolution temperature and dissolution time of 160° C. and 90 min, respectively, an injection volume of 200 μL, and a solvent of trichlorium benzene stabilized with 100 ppm BHT.

[0030] The polymer composition of the present disclosure can include an EVA copolymer, which exhibits a melt index, as determined by ASTM D1238, measured at 190° C. with a load of 2.16 kg, that can range from a lower limit selected from one of 0.1 g / 10 min, 1 g / 10 min, 2 g / 10 min, 5 g / 10 min, 10 g / 10 min, 20 g / 10 min, or 50 g / 10 min, to an upper limit selected from one of 50 g / 10 min, 100 g / 10 min, 200 g / 10 min, 300 g / 10 min, or 400 g / 10 min, where any lower limit can be paired with any upper limit.

[0031] The polymer composition of the present disclosure can include an EVA copolymer, the density of the EVA copolymer as determined by ASTM D792 being 0.91 g / cm 3 , 0.95g / cm 3 , 0.97g / cm 3 , or 1.1 g / cm 3 1.1 g / cm 3 , 1.5g / cm 3 , 1.9g / cm 3 , 1.21g / cm 3 , or 1.25 g / cm 3 to a selected upper limit, and any lower limit can be paired with any upper limit.

[0032] The polymer compositions of the present disclosure can include an EVA copolymer, the copolymer exhibiting a Shore A hardness, as determined by ASTM D2240, ranging from a lower limit of any of Shore A60, Shore A65, Shore A70, Shore A75, or Shore A80 to an upper limit of Shore A70, Shore A75, Shore A80, Shore A100, any lower limit can be paired with any upper limit.

[0033] The polymer composition of the present disclosure can include an EVA copolymer, which exhibits a Vicat softening temperature, as determined by the ASTM D1525A50 method, that can range from a lower limit of any of 35°C, 40°C, 45°C, 50°C, or 55°C, to an upper limit of any of 65°C, 70°C, 75°C, 85°C, or 90°C, where any lower limit can be paired with any upper limit.

[0034] The polymer composition of the present disclosure can include an EVA copolymer, the copolymer exhibiting a Mooney viscosity ML(1+4) in the range of 15-50 MU at 100° C. as determined by ASTM D1646. Such a Mooney viscosity can be obtained when the vinyl acetate contact is greater than 50% of the copolymer.

[0035] As previously mentioned, it is also envisioned that the EVA copolymers of the present disclosure may include one or more additional comonomers by reacting an EVA polymer resin, EVA prepolymer, or EVA monomer with one or more additional comonomers, including, but not limited to, one or more polar monomers, such as those of the type described in PCT / BR2017 / 050398, which is incorporated herein by reference in its entirety.

[0036] The polymer composition of the present disclosure can include one or more peroxidizing agents capable of generating free radicals during polymer processing. For example, the peroxidizing agent can be combined with the EVA resin while reacting the polymer during polymerization and / or curing. In one or more embodiments, the peroxidizing agent is a difunctional peroxide, such as benzoyl peroxide; dicumyl peroxide; di-tert-butyl peroxide; OO-Tert-amyl-O-2-ethylhexyl monoperoxycarbonate; tert-butyl cumyl peroxide; tert-butyl 3,5,5-trimethylhexanoate peroxide; tert-butyl peroxybenzoate; 2-ethylhexyl carbonate tert-butyl peroxide; 2,5-dimethyl-2,5-di(tert-butyl) peroxide; peroxide)hexane; 1,1-di(tert-butylperoxide)-3,3,5-trimethylcyclohexane; 2,5-dimethyl-2,5-di(tert-butylperoxide)hexyne-3; 3,3,5,7,7-pentamethyl-1,2,4-trioxepane; butyl 4,4-di(tert-butylperoxide)valerate; di(2,4-dichlorobenzoyl)peroxide; di(4-methylbenzoyl)peroxide; peroxide di(tert-butylperoxyisopropyl)benzene, and the like.

[0037] Peroxidizing agents may also be used, for example, benzoyl peroxide, 2,5-di(cumylperoxy)-2,5-dimethylhexane, 2,5-di(cumylperoxy)-2,5-dimethylhexyne-3,4-methyl-4-(t-butylperoxy)-2-pentanol, butyl-peroxy-2-ethyl-hexanoate, tert-butyl peroxypivalate, tertiary butyl peroxyneodecanoate, t-butyl-peroxy-benzoate, t-butyl-peroxy-2-ethyl-hexanoate, 4-methyl-4-(t-amylperoxy)-2-pentanol, 4-Methyl-4-(cumylperoxy)-2-pentanol, 4-Methyl-4-(t-butylperoxy)-2-pentanone, 4-Methyl-4-(t-amylperoxy)-2-pentanone, 4-Methyl-4-(cumylperoxy)-2-pentanone, 2,5-dimethyl-2,5-di(t-butylperoxy)hexane, 2,5-dimethyl-2,5-di(t-amylperoxy)hexane, 2,5-dimethyl-2,5-di(t-butylperoxy)hexyne-3,2,5-dimethyl-2,5-di(t-amylperoxy)hexyne-3,2,5-dimethyl 2-t-butylperoxy-5-hydroperoxyhexane, 2,5-dimethyl-2-cumylperoxy-5-hydroperoxyhexane, 2,5-dimethyl-2-t-amylperoxy-5-hydroperoxyhexane, m / p-alpha,alpha-di[(t-butylperoxy)isopropyl]benzene, 1,3,5-tris(t-butylperoxyisopropyl)benzene, 1,3,5-tris(t-amylperoxyisopropyl)benzene, 1,3,5-tris(cumylperoxyisopropyl)benzene, di[1,3-dimethyl-3 -(t-butylperoxy)butyl]carbonate, di[1,3-dimethyl-3-(t-amylperoxy)butyl]carbonate, di[1,3-dimethyl-3-(cumylperoxy)butyl]carbonate, di-t-amyl peroxide, t-amyl cumyl peroxide, t-butyl-isopropyl cumyl peroxide, 2,4,6-tri(butylperoxy)-s-triazine, 1,3,5-tri[1-(t-butylperoxy)-1-methylethyl]benzene, 1,3,5-tri-[(t-butylperoxy)-isopropyl]benzene, 1,3-Dimethyl-3-(t-butylperoxy)butanol, 1,3-Dimethyl-3-(t-amylperoxy)butanol, Di(2-phenoxyethyl)peroxydicarbonate, Di(4-t-butylcyclohexyl)peroxydicarbonate, Dimyristylperoxydicarbonate, Dibenzylperoxydicarbonate, Di(isobornyl)peroxydicarbonate, 3-Cumylperoxy-1,3-dimethylbutylmethacrylate, 3-t-Butylperoxy-1,3-dimethylbutylmethacrylate, 3-t-Amylperoxy Oxy-1,3-dimethylbutyl methacrylate, tri(1,3-dimethyl-3-t-butylperoxybutyloxy)vinylsilane, 1,3-dimethyl-3-(t-butylperoxy)butyl N-[1-{3-(1-methylethenyl)-phenyl)1-methylethyl]carbamate, 1,3-dimethyl-3-(t-amylperoxy)butyl N-[1-{3(1-methylethenyl)-phenyl}-1-methylethyl]carbamate, 1,3-dimethyl-3-(cumylperoxy))butyl N-[1-{3-(1-methylethenyl)-phenyl}-1-methylethyl]carbamate n-butyl-4,4-di(t-amylperoxy)valerate, ethyl 3,3-di(t-butylperoxy)butyrate, 2,2-di(t-amylperoxy)propane, 3,6,6,9,9-pentamethyl-3-ethoxycarbonyl(cabonyl)methyl-1,2,4,5-tetraoxacyclononane, n-butyl-4,4-bis(t-butylperoxy) C) valerate, ethyl-3,3-di(t-amylperoxy)butyrate, benzoyl peroxide, OO-t-butyl-O-hydrogen-monoperoxy-succinate, OO-t-amyl-O-hydrogen-monoperoxy-succinate, 3,6,9,triethyl-3,6,9-trimethyl-1,4,7-triperoxynonane (or methyl ethyl ketone peroxide cyclic trimer), methyl ethyl ketone peroxide cyclic dimer, 3,3,6,6,9,9-hexamethyl-1,2,4,5-tetraoxacyclononane, 2,5-dimethyl-2,5-Di(benzoylperoxy)hexane, t-butyl perbenzoate, t-butyl peroxyacetate, t-butylperoxy-2-ethylhexanoate, t-amyl perbenzoate, t-amyl peroxyacetate, t-butylperoxyisobutyrate, 3-hydroxy-1,1-dimethyl t-butylperoxy-2-ethylhexanoate, OO-t-amyl-O-hydrogen-monoperoxysuccinate, OO-t-butyl ... -Hydrogen-monoperoxysuccinate, di-t-butyl diperoxyphthalate, t-butylperoxy(3,3,5-trimethylhexanoate), 1,4-bis(t-butylperoxycarbo)cyclohexane, t-butylperoxy-3,5,5-trimethylhexanoate, t-butyl-peroxy-(cis-3-carboxy)propionate, allyl 3-methyl-3-t-butylperoxybutyrate, OO-t-butyl-O-isopropyl-1,2-dihydro-1,2-trimethyl ... Propyl monoperoxycarbonate, OO-t-butyl-O-(2-ethylhexyl) monoperoxycarbonate, 1,1,1-tris[2-(t-butylperoxycarbonyloxy)ethoxymethyl]propane, 1,1,1-tris[2-(t-amylperoxycarbonyloxy)ethoxymethyl]propane, 1,1,1-tris[2-(cumylperoxycarbonyl(cabonyl)oxy)ethoxymethyl]propane, O Also included are O-t-amyl-O-isopropyl monoperoxycarbonate, di(4-methylbenzoyl) peroxide, di(3-methylbenzoyl) peroxide, di(2-methylbenzoyl) peroxide, didecanoyl peroxide, dilauroyl peroxide, 2,4-dibromo-benzoyl peroxide, succinic peroxide, dibenzoyl peroxide, di(2,4-dichloro-benzoyl) peroxide, and combinations thereof.

[0038] In one or more embodiments, the polymer composition of the present disclosure may include one or more peroxidizers in a weight percent (wt%) of the total composition ranging from a lower limit selected from one of 0.01 wt%, 0.1 wt%, 0.15 wt%, 0.4 wt%, 0.6 wt%, 0.75 wt%, and 1 wt%, to an upper limit selected from one of 0.5 wt%, 1.25 wt%, 2 wt%, 4 wt%, and 5 wt%, any lower limit may be used along with any upper limit. It is further envisioned that the concentration of the peroxidizer may be more or less depending on the application of the final material.

[0039] It is also envisioned that a crosslinking coagent can be incorporated into the polymer composition during the curing process. The crosslinking coagent creates additional crosslinking reaction sites. Thus, the degree of crosslinking of the polymer is significantly increased beyond that normally obtained by adding more peroxide. In general, the coagent increases the crosslinking rate. In one or more embodiments, the crosslinking coagent includes triallyl isocyanurate (TAIC), trimethylolpropane-tris-methacrylate (TRIM), triallyl cyanurate (TAC), and combinations thereof.

[0040] In one or more embodiments, the polymer composition of the present disclosure may include one or more crosslinking coagents in a percentage of resin (phr) ranging from a lower limit selected from one of 0.01 phr, 0.25 phr, 0.5 phr, 1 phr to an upper limit selected from one of 1.5 phr and 2 phr.

[0041] The polymer composition of the present disclosure can include one or more blowing agents to produce expanded polymer compositions and foams. The blowing agents can include solid blowing agents, liquid blowing agents, or gaseous blowing agents. In embodiments using solid blowing agents, the blowing agents can be combined with the polymer composition as a powder or granules.

[0042] Blowing agents of the present disclosure include chemical blowing agents that decompose at polymer processing temperatures and release a blowing gas, e.g., N2, CO, CO2, etc. Examples of chemical blowing agents include organic blowing agents including hydrazines, e.g., toluenesulfonylhydrazine, hydrazides, e.g., oxydibenzenesulfonylhydrazide, diphenyloxide-4,4'-disulfonic acid hydrazide, etc., nitrates, azo compounds, e.g., azodicarbonamide, cyanovaleric acid, azobis(isobutyronitrile), and N-nitroso compounds, and other nitrogen-based materials, and other compounds known in the art.

[0043] Inorganic chemical foaming agents can include carbonates such as sodium hydrogen carbonate (sodium bicarbonate), sodium carbonate, potassium bicarbonate, potassium carbonate, ammonium carbonate, etc., which may be used alone or in combination with weak organic acids such as citric acid, lactic acid, or acetic acid.

[0044] In one or more embodiments, the polymer composition of the present disclosure may include one or more blowing agents in a resin percentage (phr) ranging from a lower limit selected from one of 1 phr, 1.5 phr, 2 phr, 2.5 phr, and 3 phr to an upper limit selected from one of 3.5 phr, 4 phr, 4.5 phr, 5 phr, 5.5 phr, and 6 phr, any lower limit may be used in conjunction with any upper limit.

[0045] The polymer composition of the present disclosure may include one or more foaming accelerators (also known as kickers) that enhance or initiate the action of the foaming agent by lowering the associated activation temperature. For example, if the selected foaming agent reacts or decomposes at a temperature higher than 170°C, such as 220°C or higher, the surrounding polymer will decompose if heated to the activation temperature, and a foaming accelerator may be used. The foaming accelerator may include any suitable foaming accelerator that can activate the selected foaming agent. In one or more embodiments, suitable foaming accelerators include cadmium salts, cadmium-zinc salts, lead salts, lead-zinc salts, barium salts, barium-zinc (Ba-Zn) salts, zinc oxide, titanium dioxide, triethanolamine, diphenylamine, sulfonated aromatic acids, and salts thereof, and the like.

[0046] In one or more embodiments, the polymer composition of the present disclosure may include one or more foaming promoters in a resin percentage (phr) ranging from a lower limit selected from one of 0.1 phr, 0.25 phr, 0.5 phr, 1 phr, 2 phr, and 2.5 phr to an upper limit selected from one of 1.5 phr, 2 phr, 2.5 phr, 3 phr, 3.5 phr, 4 phr, 4.5 phr, and 5 phr, any lower limit may be used in conjunction with any upper limit.

[0047] Additives The polymeric composition of the present disclosure may include fillers and additives that modify various physical and chemical properties when added to the polymeric composition during blending, including one or more polymeric additives such as processing aids, lubricants, antistatic agents, clarifiers, nucleating agents, beta-nucleating agents, slip agents, antioxidants, compatibilizers, antacids, light stabilizers, e.g., HALS, IR absorbers, brighteners, inorganic fillers, organic and / or inorganic dyes, antiblocking agents, processing aids, flame retardants, plasticizers, biocides, adhesion promoters, metal oxides, mineral fillers, flow promoters, oils, antioxidants, antiozonants, accelerators, and vulcanizing agents.

[0048] The polymeric compositions of the present disclosure may include one or more inorganic fillers, such as talc, glass fiber, marble dust, cement dust, clay, carbon black, feldspar, silica or glass, fumed silica, silicates, calcium silicate, silicic acid powder, glass microspheres, mica, metal oxide particles and nanoparticles, such as magnesium oxide, antimony oxide, zinc oxide, inorganic salt particles and nanoparticles, such as barium sulfate, wollastonite, alumina, aluminum silicate, titanium oxide, calcium carbonate, polyhedral oligomeric silsesquioxanes (POSS), or recycled EVA. As defined herein, recycled EVA may be obtained from regrind material that has been subjected to at least one processing method, such as molding or extrusion, after which the sprues, runners, flashings, stamped sections, etc., are ground or chopped.

[0049] In one or more embodiments, the polymer compositions of the present disclosure can include one or more fillers in a weight percent (wt%) of the total composition ranging from a lower limit selected from one of 0.02 wt%, 0.05 wt%, 1.0 wt%, 5.0 wt%, 10.0 wt%, 15.0 wt%, and 20.0 wt%, to an upper limit selected from one of 25.0 wt%, 30.0 wt%, 40.0 wt%, 50.0 wt%, 60.0 wt%, and 70.0 wt%, any lower limit can be used in conjunction with any upper limit.

[0050] In-reactor synthesis In one or more embodiments, the polymer composition of the present disclosure can be prepared in a reactor. Ethylene and vinyl acetate are added to the reactor and polymerized. In some embodiments, ethylene and vinyl acetate, and optionally one or more polar comonomers, are polymerized by high pressure radical polymerization, with a peroxidant acting as a polymerization initiator. In some embodiments, ethylene and vinyl acetate and a peroxidant are added at high pressure in an autoclave or tubular reactor at a temperature between 80° C. and 300° C., with the pressure in the reactor being between 500 bar and 3000 bar in some embodiments, and between 1000 bar and 2600 bar in some embodiments. In other embodiments, the copolymer is produced by a solution polymerization method.

[0051] In embodiments including additional comonomers, it is understood that such additional comonomers may be added to the reactor along with the ethylene and vinyl acetate, but may also react with the produced EVA copolymer during reactive extrusion.

[0052] As mentioned above, one or more free radical generators, including any of those previously mentioned, may be included during polymerization.

[0053] Post-polymerization method It is further understood that the EVA copolymer can also be cured, for example, in the presence of a peroxide, including those previously described, and optionally a crosslinking coagent. For embodiments including an expanding composition, the expanding and curing steps can be in the presence of a blowing agent and a peroxide, and optionally a kicker and / or a crosslinking coagent, as described below. During any of these curing steps (whether expanding or not), in one or more embodiments, the curing of the EVA copolymer can be carried out in an oxygen-filled or partially oxygen-containing state, as described, for example, in WO201694161A1, which is incorporated by reference in its entirety.

[0054] physical properties Cured non-expanding articles comprising the EVA copolymers of the present disclosure have a compressibility of 0.7 g / cm as determined by ASTM D-792. 3 , 0.8g / cm 3 , 0.9g / cm 3 , or 1.0 g / cm 3 From the lower limit of either of the above, 1.0 g / cm 3 , 1.1g / cm 3 , or 1.2 g / cm 3 and any lower limit can be used in conjunction with any upper limit.

[0055] Cured non-expanded articles produced with the polymeric compositions of the present disclosure can have a Shore A hardness as determined by ASTM D2240 in a range having a lower limit selected from one of Shore A40, Shore A50, or Shore A60 to an upper limit selected from one of Shore A60, Shore A70, Shore A80, and Shore A90, any lower limit can be paired with any upper limit.

[0056] The cured non-expanding articles produced with the polymer compositions of the present disclosure have an abrasion resistance of 20 mm, as determined by ISO 4649:2017, measured at a load of 10 N. 3 , 40mm 3 , 60mm 3 , 70mm 3 , 90mm 3 , or 100mm 3 120 mm from the lower limit selected from one of 3 , 140mm 3 , 170mm 3 , 200mm 3 to an upper limit selected from one of the following, where any lower limit can be paired with any upper limit.

[0057] It is further envisioned that, as previously mentioned, the EVA copolymer can be expanded and cured, for example, with the blowing agents and peroxides described. Expanded articles produced with the polymer compositions of the present disclosure have a density of 0.05 g / cm3 or less as determined by ASTM D-792. 3 , 0.12g / cm 3 , 0.2g / cm 3 , 0.25g / cm 3 , 0.5g / cm 3 0.4 g / cm 3 , 0.5g / cm 3 , 0.6g / cm 3 , 0.65g / cm 3 , and 0.70 g / cm 3 to an upper limit selected from one of the above, and any lower limit can be paired with any upper limit.

[0058] Expanded articles produced with the polymer compositions of the present disclosure can have an Asker C hardness, as determined by ABNT NBR 14455:2015, in a range having a lower limit of any of Asker C20, Asker C30, Asker C40, or Asker C50, and an upper limit of any of Asker C50, Asker C60, Asker C70, or Asker C95, provided that any lower limit can be paired with any upper limit.

[0059] Expanded articles produced with the polymer compositions of the present disclosure can have a compression set (PCS) as determined by ASTM D395:2016B method in a range having a lower limit selected from one of 20%, 30%, 40%, or 50% to an upper limit selected from one of 50%, 60%, 70%, 80%, or 90%, any lower limit can be paired with any upper limit.

[0060] The expanded articles produced with the polymer compositions of the present disclosure can have a rebound as determined by ABNT NBR 8619:2015 ranging from a lower limit selected from one of 20%, 30%, 35%, 40%, 45%, and 50% to an upper limit selected from one of 50%, 60%, 70%, 80%, and 90%, any lower limit can be paired with any upper limit.

[0061] Expanded articles produced with the polymer composition of the present disclosure can have a shrinkage at 70° C.×1 hour using the PFI method (PFI “Testing and Research Institute for the Shoe Manufacturing Industry”, Pirmesens, Germany) within a range having a lower limit selected from one of 0.1%, 1%, 1.5%, and 5% to an upper limit selected from one of 4%, 5%, 6%, and 7%, any lower limit can be paired with any upper limit.

[0062] The PFI method can be used in the industry for shrinkage measurements and is described in detail below.

[0063] Device Oven with forced air circulation Pachymeter A ruler for marking the test specimen or template Thickness gauge

[0064] sample Three test pieces, measuring at least 100 x 100 mm, should be evaluated for each sample.

[0065] procedure The test specimens are allowed to condition for 1 hour at a temperature of 23±2° C. and a relative humidity of 50±5%. The approximate thickness of the sample is measured.

[0066] Using a ruler or template, points A, B, C, and D were marked on each of the test specimens as shown in FIG.

[0067] Initial length (C i ) is measured to the nearest 0.01 mm in direction A (segments AB and CD) and in direction B (segments AC and BD) using a pachymeter.

[0068] The specimens are then kept in a forced air oven at 70° C. for 1 hour.

[0069] After the exposure period, the specimens are removed from the oven and conditioned for 60 minutes at a temperature of 23±2°C and a relative humidity of 50±5%.

[0070] Final length (C f ) is measured to the nearest 0.01 mm in the A direction (sections AB and CD) and in the B direction (sections AC and BD) using calipers.

[0071] Average initial length (C im ) is calculated for each specimen as the average of the AB and CD sections in the A direction, and the average of the AC and BD sections in the B direction.

[0072] Average final length (C fm ) is calculated for each specimen as the average of the AB and CD sections in the A direction, and the average of the AC and BD sections in the B direction.

[0073] result The shrinkage of expanded EVA is given by the following formula, expressed as a percentage to the nearest 0.1%:

[0074] Shrinkage% = (C im -C fm )×100 / C im During the ceremony, C im = initial length average (mm) C fm = Average final length (mm)

[0075] The final EVA shrinkage result is calculated as the average of the shrinkage values ​​calculated for each specimen in the A and B directions. Note: PFI recommends maximum allowable values ​​for intumescent material shrinkage in directions A and B (Figure 1): 0.6g / cm 3 -3% for materials with densities up to 0.6g / cm 3 -2% for materials with a density above

[0076] Expanded articles produced with the polymer compositions of the present disclosure have abrasion resistance of 40, 80, 120 mm, as determined by ISO 4649 at a load of 5 N. 3 , 150mm 3 , 200mm 3 , or 400mm 3 300 mm from the lower limit selected from one of 3 , 600mm 3 , 700mm 3 , or 800mm 3 to an upper limit selected from one of the above, and any lower limit can be paired with any upper limit.

[0077] Purpose In one or more embodiments, the polymer composition can be used in a variety of molding processes to produce products, including extrusion, compression molding, injection molding, thermoforming, cast film extrusion, inflation molding, foaming, extrusion blow molding, injection blow molding, ISBM (injection stretch blow molding), 3D printing, rotational molding, pultrusion, double expansion processes, and the like.

[0078] The polymer compositions of the present disclosure can be used to manufacture adhesive films for woven and nonwoven materials, including textiles, nonwovens, polyurethanes, EVA, polypropylene, polyethylene, polyvinyl chloride polymers, polyesters, polyamides, and the like. In some embodiments, the polymer compositions can be incorporated into adhesive films that are used to form multi-layer articles that include one or more adhesive layers and one or more substrate layers, including textiles and nonwovens. In various embodiments, the substrate layer can be in the form of a thin film, block, or sheet. In certain embodiments where the EVA copolymer is present as a thin film, the polymer can be selected from the narrower melt index and vinyl acetate content ranges shown above. For example, when the vinyl acetate content is 5-19 wt%, the selected melt index can be in the narrower range of 1-6 g / 10 min, although it is also recognized that a higher vinyl acetate content can be combined with a different melt flow index.

[0079] Films made from the polymeric composition may be suitable for dubbing woven and nonwoven fabrics (NWFs) derived from natural fibers such as cotton and wool, or synthetic fibers such as polyolefins, including polyester and polypropylene. In one or more embodiments, the adhesive film comprising the EVA of the present disclosure may be used in multi-layer articles, where the adhesive film may be applied to a substrate, such as, for example, a film, sheet, or block. Thus, for example, in certain embodiments, a multi-layer article of the present disclosure may include at least one layer of bio-based EVA with at least a second layer, which may be, for example, a substrate made of a material selected from a woven fabric, a nonwoven fabric, a polyurethane, another EVA, polypropylene, polyethylene, a polyvinyl chloride polymer, polyester, and polyamide.

[0080] In one or more embodiments, the polymer composition can be formulated as an adhesive composition having a maximum adhesive strength of greater than 20 N as measured by ABNT NBR10456:2012. In some embodiments, the polymer composition can exhibit an adhesive strength of greater than 30 N. For example, the maximum adhesive strength can range from 20 N to 50 N.

[0081] The polymer compositions of the present disclosure can also be formulated into many polymer articles, including insoles, midsoles, soles, hot melt adhesives, primers, linings, industrial floors, sound insulation in civil engineering and construction. The polymer compositions of the present disclosure can be formed into articles for a wide variety of end uses, including soles, midsoles, outsoles, unisoles, insoles, monoblock sandals, and flip-flops, full EVA footwear, sporting goods, and the like. In certain embodiments, such articles can have a vinyl content of at least 17 wt%, for example, a vinyl content in the range of 18-40 wt%.

[0082] Other uses include seals, hoses, gaskets, foam, foam mattresses, furniture, electrical-electronic, automotive, packaging, EVA tires, bras, mats, paperboard, sporting goods, toys, swimming accessories, leg floats, yoga blocks, dumbbell gloves, gym steps, rodo sheets, kimono strings, sandpaper, finger protectors, wall protectors, finger gaps, educational games and products, decorative panels, EVA balls, twisted hex stools, slippers, pillows, sponges, chairs, cycling bib pads, protective covers, carpets, aprons, and others.

[0083] In one or more embodiments, the modified EVA composition can be compounded as a concentrated masterbatch to produce a blend with other resins. The masterbatch composition can then be combined with other polymers to produce a polymer processing stock. The mixing to obtain the blend can be performed in any conventional resin mixing method, such as the melting and extrusion methods described above. In one or more embodiments, the polymer composition can be compounded as a masterbatch that is added to a polymer resin at a weight percentage of 1 wt% to 20 wt% to produce a processing stock.

[0084] Polymer Resin In one or more embodiments, the polymer composition can include other polymer resins in addition to the EVA copolymers of the present disclosure. In some embodiments, one or more bio-based EVA copolymers can be combined with a petrochemical-based polymer, such as a petrochemical-based EVA.

[0085] In some embodiments, masterbatch formulations can be prepared from EVA resin (or ethylene and vinyl acetate monomers) that are subsequently combined with polymer resins to produce adhesives or processing stock for the manufacture of polymeric articles. Thus, it is envisioned that the EVA copolymers of the present disclosure can act as compatibilizers for other polymeric resins in addition to the use of EVA as an adhesive.

[0086] In one or more embodiments, the EVA copolymers can act as a compatibilizer between incompatible or thermodynamically immiscible polymer resins, where the compatibilizer reduces the interfacial tension between the two phases, producing blends that exhibit good mechanical properties and processing for a variety of polymer resins.

[0087] Polymer resins of the present disclosure include, for example, polyethylene, polyethylene copolymers such as ethylene maleic anhydride, polypropylene, polystyrene, polybutadiene, polyvinyl chloride, ethylene-vinyl acetate copolymer (EVA), polyesters such as polyethylene terephthalate (PET), polyhydroxyalkanoates (PHAs), high impact polystyrene (HIPS), and acrylonitrile butadiene styrene (ABS), polyurethanes, elastomers such as 5-vinyl-2-norbornene-EPDM, polysulfide rubber, ethylene propylene rubber (EPM), poly(ethylene-methyl acrylate), poly(ethylene-acrylate), ethylene propylene diene rubber (EPDM), vinyl silicone rubber (VMQ), fluorosilicone (FVMQ), nitrile rubber (NBR), acrylonitrile-butadiene rubber (BMP), ethylene propylene diene rubber (EPDM ... Examples of suitable rubbers include diene-styrene (ABS), styrene butadiene rubber (SBR), styrene-butadiene-styrene block copolymer (SBS), styrene-ethylene-butylene-styrene triblock copolymer (SEBS), polybutadiene rubber (BR), styrene-isoprene-styrene block copolymer (SIS), partially hydrogenated acrylonitrile butadiene (HNBR), natural rubber (NR), synthetic polyisoprene rubber (IR), neoprene rubber (CR), polychloropropene, bromobutyl rubber, chlorobutyl rubber, chlorinated poly(ethylene), vinylidene fluoride copolymer (CFM), silicone rubber, vinyl silicone rubber, chlorosulfonated poly(ethylene), fluoroelastomers, elastomeric polyolefins, such as ethylene C3 to C12 alpha-olefin copolymers, and combinations thereof.

[0088] In some embodiments, the EVA copolymers can act as compatibilizers in polyolefin and biopolymer blends, including but not limited to starch, polysaccharides such as cellulose and methylcellulose, polylactic acid (PLA), polyhydroxyalkanoic acid (PHAs) such as polyhydroxybutyric acid (PHB), polyhydroxyvaleric acid (PHV), polyhydroxyhexanoic acid (PHH), polyhydroxyoctanoic acid (PHO), and copolymers thereof, and combinations thereof. EXAMPLES

[0089] In the following examples, formulations of polymer compositions were prepared and analyzed to study various physical properties.

[0090] Example 1 Production of bio-based copolymers of ethylene vinyl acetate The bio-based copolymer of ethylene and vinyl acetate of the present invention was produced using ethylene obtained from the dehydration of ethanol obtained from sugar cane. The dehydration of ethanol to produce ethylene was carried out in a series of four fixed-bed adiabatic reactors connected in series at temperatures varying from 350° C. to 480° C. and pressures ranging from 3 to 10 atm using an alumina catalyst. The reaction product was then purified by cryogenic distillation to obtain polymer grade ethylene.

[0091] Ethylene and vinyl acetate copolymers were produced in a high pressure tubular reactor with a length of 1.110 m and a diameter of 50 mm. Ethylene was injected into the reactor at a flow rate of 8.5 tonnes / hour and vinyl acetate was injected at a flow rate of 2000 kg / hour. The mixture was compressed to 2400 bar in a hyper compressor and preheated at 130°C. A mixture of tert-butyl peroxypivalate / t-butyl peroxy-2-ethyl-hexanoate / OO-Tert-amyl-O-2-ethylhexyl monoperoxycarbonate was used as initiator. The reaction temperature was varied between 190°C and 250°C and EVA copolymer was produced at a rate of 8.5 tonnes / hour. The following table shows the properties of the resulting bio-based EVA.

[0092] [Table 1]

[0093] Example 2 Preparation of Cured Non-Expanding Articles In the following examples, the curable polymer composition formulations were prepared in a kneader XSN-5 type QUANZHOU YUCHENGSHENG MACHINE CO.,LTD at a temperature of 100°C, then sliced ​​in a cylinder (open mixing), pressed in a hydraulic press LPB-100-AQ-EVA type from Luxor Industria de Maquinas Ltda at 175°C for 7 minutes, and cured to produce 10x10 cm plaques, which were analyzed to investigate various physical properties. The curable polymer composition formulations, including the mixture of bio-based EVA and petrochemical-based EVA, are shown in Table 2.

[0094] [Table 2]

[0095] The samples were analyzed for hardness (Shore A), density, abrasion resistance, and bio-based carbon content, and the results are shown in Table 3.

[0096] [Table 3]

[0097] Example 3 Preparation of Expanded Articles In the following examples, the expandable polymer composition formulations were prepared in a kneader XSN-5 type QUANZHOU YUCHENGSHENG MACHINE CO.,LTD at a temperature of 105°C, then sliced ​​in a cylinder (open mixing), pressed in a hydraulic press LPB-100-AQ-EVA type from Luxor Industria de Maquinas Ltda at 175°C for 7 minutes, cured, and expanded at different expansion rates to produce plaques, which were analyzed to investigate various physical properties. The expandable polymer composition formulations are shown in Table 4.

[0098] [Table 4]

[0099] The samples were analyzed for hardness (Shore A and Asker C), density, abrasion resistance, compression set, shrinkage, elastic rebound, and bio-based carbon content, and the results are shown in Table 5.

[0100] [Table 5]

[0101] Although only a few exemplary embodiments have been detailed above, one skilled in the art will readily recognize that many modifications are possible in the exemplary embodiments without substantially departing from the present invention. Accordingly, all such modifications are intended to be included within the scope of the present disclosure, as defined by the following claims. In the claims, means-plus-function claims are intended to cover the structures described herein as performing the recited functions, and not only structural equivalents, but also equivalent structures. Thus, while nails and screws may not be structural equivalents in that nails use cylindrical surfaces to fasten wood pieces together, while screws use helical surfaces in the context of attaching wood pieces, nails and screws may be equivalent structures. It is the express intent of applicants not to invoke 35 U.S.C. § 112, paragraph 6, to limit any of the claims described herein, except to those that expressly use the term "means for" with the relevant function in the claims.

Claims

1. 1. A foam prepared from an expandable polymer composition comprising a copolymer of ethylene and vinyl acetate and at least a blowing agent and a peroxidant, The ethylene and vinyl acetate copolymer is having a biobased carbon content of at least 60% as determined by ASTM D6866-18B method, and at least a portion of the ethylene is derived from renewable carbon sources; the copolymer produces reduced amounts of carbon dioxide derived from fossil sources compared to a copolymer exhibiting 0% biobased carbon content, and exhibits a Shore A hardness ranging from Shore A60 to Shore A100 as determined by ASTM D2240; the copolymer has a number average molecular weight (Mn) of 5 kDa to 50 kDa; and A foamed article, wherein the foam exhibits a density in the range of 0.25 to 0.7 g / cm 3 as determined by ASTM D-792.

2. 10. The inflatable article of claim 1, exhibiting an Asker C hardness in the range of Asker C 20 to 95 as determined by ABNT NBR 14455:2015.

3. 3. The inflatable article of claim 1 or 2, exhibiting a compression set in the range of 20% to 95% as determined by ASTM D395:2016B method.

4. 4. The inflatable article of any one of claims 1 to 3, exhibiting a rebound resilience in the range of 20% to 80% as determined by ABNT NBR 8619:2015.

5. 40 mm as determined by ISO 4649, measured with a load of 5 N 3 ~400mm 3 5. The inflatable article of claim 1 , exhibiting an abrasion resistance in the range of

6. 6. The inflatable article of claim 1, exhibiting a shrinkage of between 0.1% and 7% when measured at 70°C for 1 hour according to the PFI method.

7. 7. The inflatable article of any one of claims 1 to 6, exhibiting a bio-based carbon content of at least 60% as determined by ASTM D6866-18B method.

8. 8. The inflatable article of any one of claims 1 to 7, selected from the group consisting of shoe soles, midsoles, outsoles, unisoles, insoles, monoblock sandals, flip-flops, full EVA footwear, sporting goods, seals, hoses, gaskets, foams, foam mattresses, and automotive parts.

9. 1. A method for producing an expanded ethylene vinyl acetate copolymer, comprising the steps of: polymerizing ethylene, at least in part, derived from a renewable carbon source, with vinyl acetate to produce said ethylene vinyl acetate copolymer; and expanding and curing the ethylene vinyl acetate copolymer in the presence of at least a blowing agent and a peroxidizer; the ethylene is produced by dehydrating ethanol produced by fermenting a renewable carbon source; the copolymer exhibits a biobased carbon content of at least 60% as determined by ASTM D6866-18B method; and the copolymer produces reduced amounts of carbon dioxide derived from fossil sources compared to a copolymer exhibiting 0% biobased carbon content; the copolymer exhibits a Shore A hardness ranging from Shore A60 to Shore A100 as determined by ASTM D2240; The copolymer has a number average molecular weight (Mn) of 5 kDa to 50 kDa; and The foam exhibits a density in the range of 0.25 to 0.7 g / cm 3 as determined by ASTM D-792; Manufacturing method.