Flame-resistant polyamide molding compound for insulating electrical components

Abstract

The intellectual property right relates to flame-retardant polyamide molding compounds with a low phosphorus content.

Description

[Technical field]

[0001] The present invention relates to a flame-retardant polyamide molding composition having a low phosphorus content. [Background technology]

[0002] EP 150511 A1 discloses powdered polyamide compositions containing alkyl phosphonates for use in 3D printing.

[0003] EP 3127937 A1 demonstrates the effectiveness of metal phosphinates for imparting flame retardancy to polyamides. According to verbal evaluation of the examples, the addition of melamine cyanurate should be avoided.

[0004] EP 1 731 559 proposes phosphorus compounds in combination with melamine cyanurate and alcohols as flame retardants for polyamides. They achieve a V-0 grade according to UL 94, but comparative tests in the present invention show increased mass loss due to migration. EP 1 731 559 does not take into account this mass loss or the elongation at break of the composition.

[0005] US 2018 / 003771 recommends using only melamine cyanurate and polyols to impart flame retardancy to polyamides. No mechanical requirements are disclosed. [Prior art documents] [Patent documents]

[0006] [Patent Document 1] European Patent Application Publication No. 150511 [Patent Document 2] European Patent Application Publication No. 3127937 [Patent Document 3] European Patent Application Publication No. 1731559 [Patent Document 4] US Patent Application Publication No. 2018 / 003771 Summary of the Invention [Problem to be solved by the invention]

[0007] The object of the present invention was to provide polyamide molding materials which have a low phosphorus content, very good flame retardancy and very low mass loss at high temperatures, which should also be distinguished by a high elongation at break.

[0008] It has surprisingly been found that flame retardants with a low content of phosphorus-containing compounds can be advantageously used in polyamide moulding compositions.

[0009] The present invention relates to (A) a polyamide matrix comprising one or more polyamides having at least 8 carbon atoms per amide unit; (B) Below: (B1) at least one metal-free aryl phosphate; (B2) at least one aryl phosphonate, (B3) carbohydrate polyols, (B4) melamine cyanurate, (B5) Non-phosphorus-containing flame retardants, if necessary A flame retardant composition comprising A polyamide molding material comprising: The polyamide molding material is provided, in which the phosphorus content of the entire flame-retardant composition is 0.5% by weight to 1.5% by weight, preferably 0.75% by weight to 1.25% by weight, based on the polyamide molding material.

[0010] The present invention further provides the use of the polyamide molding material according to the invention for the production of a part.

[0011] The present invention further provides a method for insulating a current-bearing component.

[0012] The invention further provides a hybrid part comprising a coated metal body, the coating comprising a polyamide molding compound.

[0013] The present invention further provides the use of a hybrid component for conducting electrical current, preferably in high and low voltage systems, more preferably in high voltage systems.

[0014] The polyamide molding material of the invention, the hybrid parts comprising the molding material of the invention, and the use according to the invention are described below by means of illustrative examples, without intending the invention to be limited to these exemplary embodiments. Where ranges, general formulae, or compound groups are described below, these are intended to encompass not only the corresponding ranges or compound groups explicitly mentioned, but also all subranges and subcompound groups obtained by excluding individual values ​​(ranges) or compounds. Where documents are cited in the context of this specification, the entire contents are intended to form part of the disclosure of the present invention. Where % values ​​are given below, these are values ​​in % by weight, unless otherwise stated. Percentage values ​​relating to compositions are values ​​relative to the entire composition, unless otherwise stated. Where average values ​​are given below, these are mass averages (weight averages), unless otherwise stated. Where measured values ​​are given below, these were measured at a pressure of 101325 Pa and at a temperature of 25° C., unless otherwise stated.

[0015] The scope of protection includes finished products and packaging conventionally used in commerce for the products of the invention as such, as well as possible crushed products, unless otherwise defined in the claims.

[0016] Any of the various polyamide units follow a statistical distribution. The statistical distribution can be block-like, with the desired number of blocks and the desired order, or randomly distributed. They can have an alternating structure or else form a gradient throughout the polymer chain. In particular, they can form all mixed forms in which groups with various distributions can follow each other in any way. In certain embodiments, the statistical distribution can be limited as a result of the embodiment. In all areas not affected by the limit, the statistical distribution remains unchanged.

[0017] An advantage of the polyamide molding materials according to the invention is that they have very good fire resistance, with a V-0 grade according to the flame retardant standard UL94.

[0018] A further advantage of the polyamide molding compositions according to the invention is that they have a high elongation at break.

[0019] A further advantage of the polyamide moulding compositions according to the invention is that even after relatively long storage periods at high temperatures there is very little migration of low molecular weight components at the surface (efflorescence, mass loss).

[0020] A further advantage of the polyamide molding composition according to the invention is that there is no loss of flame retardancy due to mass loss caused by migration.

[0021] A further advantage is the particularly good adhesion of the polyamide molding compositions according to the invention to metal surfaces.

[0022] Polyamide matrix (A) Preferably, the polyamide of the polyamide matrix (A) has, as a statistical average over the whole polymer, from 8 to 16 carbon atoms per amide unit, more preferably from 9 to 14 carbon atoms, and particularly preferably from 10 to 12 carbon atoms. More preferably, the polyamide of the polyamide matrix (A) has at least 8 carbon atoms per amide unit in all monomer units.

[0023] The polyamides may be homopolymers, copolymers, or blends of different polyamides, the differences of which may manifest themselves, for example, in the use of different monomers in the polymerization, in different molar mass distributions (which may be expressed, for example, in different viscosities), or in different end groups.

[0024] Preference is given to polyamides selected from PA8, PA9, PA10, PA11, PA12, PA6.10, PA6.12, PA6.14, PA8.10, PA9.10, PA9.12, PA10.10, PA10.12, PA12.12, PA6.16, PA10.16, more preferably PA6.12, PA10.10, PA10.12, PA11 and PA12, particularly preferably PA11 and PA12.

[0025] The polyamide moulding material preferably does not contain any other polyamides apart from the polyamide of the polyamide matrix (A).

[0026] Flame retardant composition (B) The flame-retardant composition of the polyamide molding material according to the invention preferably comprises - 15 to 55% by weight, preferably 25 to 50% by weight, more preferably 30 to 45% by weight of melamine cyanurate (B4), - 10 to 30% by weight, preferably 15 to 25% by weight, more preferably 17 to 23% by weight of carbohydrate polyol (B3), - 5 to 30% by weight, preferably 7 to 25% by weight, more preferably 13 to 23% by weight, of aryl phosphonates (B2), - 5 to 30% by weight, preferably 7 to 25% by weight, more preferably 13 to 23% by weight, of metal-free aryl phosphate (B1), - 0 to 15% by weight, preferably 3 to 12% by weight, more preferably 5 to 10% by weight of a non-phosphorus-based flame retardant (B5) Including, The sum of (B1), (B2), (B3), (B4) and (B5) comprises 100% by weight of component (B).

[0027] In the flame-retardant composition for the polyamide molding material of the present invention, the mass ratio of (B1) to (B2) is 0.25 to 4, preferably 0.33 to 3, more preferably 0.5 to 2, and particularly preferably 0.75 to 1.5.

[0028] Non-phosphorus-containing flame retardants (B5) are different from those according to B3 and B4. Urea and urea derivatives, magnesium hydroxide, aluminium hydroxide, aluminium sulphate, borax, boric acid and its salts (e.g. zinc borate), ammonium sulphate and calcium hydroxide are preferred. Halogenated flame retardants may also be added.

[0029] Preferably, the non-phosphorus based flame retardant (B5) is free of halogenated materials.

[0030] Melamine cyanurate (B4) is also understood to mean the melamine condensation products melem, melam, melon, but preferably exclusively melamine cyanurate (CA-RN37640-57-6) itself. The melamine cyanurate is used in the form of a powder. It preferably has a particle size D50 of 0.5 to 100 μm, more preferably 0.6 to 50 μm, particularly preferably 0.7 to 25 μm, very particularly preferably 0.8 to 5 μm, very particularly preferably 0.9 to 4 μm, measured by laser diffraction using a laser granulometer in accordance with the 2000-03-15 edition of BSISO 13320-1. The measurement is preferably carried out using a Cilas 715 / 920 laser granulometer. Small particle size is preferred as it results in a smoother finish to the molded product.

[0031] The carbohydrate polyol (B3) is preferably a hydrocarbon substituted with at least 3, preferably at least 4, more preferably at least 5, even more preferably at least 6 hydroxy groups, and optionally has an ether group, preferably at least one ether group.

[0032] The carbohydrate polyol is more preferably selected from triols such as trimethylolpropane or glycerol, or derivatives thereof such as ditrimethylolpropane or diglycerol (produced by monoetherification of two molecules of the aforementioned compounds); or tetrols such as erythritol, pentaerythritol, or derivatives thereof containing ether groups such as dipentaerythritol or tripentaerythritol; pentols such as xylitol or arabitol; hexols such as mannitol, sorbitol. It is also possible to use higher adducts of the aforementioned molecules, such as branched or hyperbranched polyglycerols. Of course, it is also possible to use mixtures of polyols. Erythritol, pentaerythritol or dipentaerythritol or tripentaerythritol are more preferred, in particular dipentaerythritol.

[0033] Aryl phosphonates (B2), for purposes of the present invention, are polymers or oligomers having at least three repeat units, preferably three identical repeat units, and containing aromatic substituents in the backbone of the molecule.

[0034] The aryl phosphonate preferably has the formula (III):

[0035] [ka]

[0036] (wherein each R1 is independently an alkyl group having 1 to 4 carbon atoms, preferably methyl; Each BAr is independently an aromatic group, preferably an aromatic group having at least two ring members, more preferably biphenylene or 4,4'-(propane-2,2-diyl)diphenylene. The repeating unit includes the repeating unit shown in Preferably, the aryl phosphonate comprises a -BAr-OH group as a terminal group.

[0037] Particularly preferably, the aryl phosphonate has the formula (IV):

[0038] [ka]

[0039] and thus the aryl phosphonate preferably contains a bisphenol A end group.

[0040] The aryl phosphonates preferably have an MVR (melt volume rate) (measured in accordance with ISO 1133 at 240°C and a load of 1.2 kg) of less than 100 mL / 10 min, more preferably at least 10 mL / 10 min, even more preferably at least 25 mL / 10 min, particularly preferably at least 50 mL / 10 min, and especially preferably from 65 to 90 mL / 10 min.

[0041] The metal-free aryl phosphate (B1) preferably contains at least two phosphate groups. More preferably, the metal-free aryl phosphate has the formula (I):

[0042] [ka]

[0043] and preferably one or two units of formula (I) and a unit of formula (II):

[0044] [ka]

[0045] and preferably contains two or three units of formula (II). The units of formula (I) or the units of formula (II) are alternately present, The number of units of formula (II) is always one more than the number of units of formula (I), In formula (I), Ar is ortho-, meta-, para-phenylene, naphthylene or biphenylene; In formula (II), Ph is a phenyl group, which may have a desired substituent selected from C1 to C4 alkyl groups as necessary. More preferably, the metal free aryl phosphate has the formula (V):

[0046] [ka]

[0047] Contains the components of. Particularly preferably, the metal free aryl phosphate has the formula (VI):

[0048] [ka]

[0049] Includes the structure of. In the formula, Ar is meta- or para-phenylene and Ph is phenyl. Preferably, Ar is not a 4,4'-(propane-2,2-diyl)diphenylene group.

[0050] The flame retardant composition preferably does not contain any polyphosphates, reaction products of melamine and polyphosphoric acid, or derivatives of phosphoric (III) acid and / or phosphoric (I) acid. It is preferred that the flame retardant composition does not contain any further phosphorus-containing components other than components (B1) and (B2).

[0051] Preferred combinations of the flame retardant composition (B) are as follows: at least one compound of formula (I):

[0052] [ka]

[0053] preferably one or two units of formula (I) and at least two units of formula (II):

[0054] [ka]

[0055] and at least one metal-free aryl phosphate (B1) comprising a unit of formula (II), preferably two or three units of formula (II). (The units of formula (I) or the units of formula (II) are present alternately, The number of units of formula (II) is always one more than the number of units of formula (I), In formula (I), Ar is ortho-, meta-, para-phenylene, naphthylene or biphenylene, but is not a 4,4'-(propane-2,2-diyl)diphenylene group; In formula (II), Ph is a phenyl group, which may have a desired substituent selected from C1 to C4 alkyl groups as necessary. -Formula (IV):

[0056] [ka]

[0057] and bisphenol A as a terminal group; - a carbohydrate polyol (B3) substituted with at least 3, preferably at least 4, more preferably at least 5 and even more preferably at least 6 hydroxy groups and optionally carrying an ether group, preferably at least one ether group; melamine cyanurate (B4), - optionally non-phosphorus-containing flame retardants (B5) selected from urea and urea derivatives, magnesium hydroxide, aluminium hydroxide, aluminium sulphate, borax, boric acid and salts of boric acid (e.g. zinc borate), ammonium sulphate, calcium hydroxide, or optionally halogenated flame retardants.

[0058] More preferred combinations of the flame retardant composition (B) are as follows: -Formula (V):

[0059] [ka]

[0060] (wherein Ar is ortho-, meta-, para-phenylene, naphthylene or biphenylene, but is not a 4,4'-(propane-2,2-diyl)diphenylene group; Ph is a phenyl group, which may have a desired substituent selected from C1 to C4 alkyl groups as necessary. At least one metal-free aryl phosphate (B1) containing the component -Formula (IV):

[0061] [ka]

[0062] and bisphenol A as a terminal group, - a carbohydrate polyol (B3) substituted with at least 3, preferably at least 4, more preferably at least 5 and even more preferably at least 6 hydroxy groups and optionally containing an ether group, preferably at least one ether group; melamine cyanurate (B4) having a particle size D50, measured by laser diffraction using a laser granulometer in accordance with the 2000-03-15 edition of BSISO 13320-1, of 0.5 to 100 μm, more preferably 0.6 to 50 μm, particularly preferably 0.7 to 25 μm, very particularly preferably 0.8 to 5 μm and especially preferably 0.9 to 4 μm, - optionally non-phosphorus-containing flame retardants (B5) selected from urea and urea derivatives, magnesium hydroxide, aluminium hydroxide, aluminium sulphate, borax, boric acid and salts of boric acid (e.g. zinc borate), ammonium sulphate, calcium hydroxide, or optionally halogenated flame retardants. The mass ratio of (B1) to (B2) is from 0.25 to 4, preferably from 0.33 to 3, more preferably from 0.5 to 2, and particularly preferably from 0.75 to 1.5.

[0063] Particularly preferred combinations of the flame retardant composition (B) are as follows: - Formula (VI):

[0064] [ka]

[0065] wherein Ar is meta- or para-phenylene; Ph is a phenyl group, which may have a desired substituent selected from C1 to C4 alkyl groups as necessary. At least one metal-free aryl phosphate (B1) having the structure: -Formula (IV):

[0066] [ka]

[0067] and 5% by weight to 30% by weight of at least one aryl phosphonate (B2) containing a repeating unit of the formula: - 10% to 30% by weight of a carbohydrate polyol (B3) substituted with at least 3, preferably at least 4, more preferably at least 5 and even more preferably at least 6 hydroxy groups and preferably having at least one ether group, - 15% to 55% by weight of melamine cyanurate (B4) having a particle size D50 of 0.5 to 100 μm, more preferably 0.6 to 50 μm, particularly preferably 0.7 to 25 μm, very particularly preferably 0.8 to 5 μm, and especially preferably 0.9 to 4 μm, measured by laser diffraction using a laser granulometer according to the 2000-03-15 edition of BSISO 13320-1, - 0% to 15% by weight of a non-phosphorus-containing flame retardant (B5) selected from urea and urea derivatives, magnesium hydroxide, aluminum hydroxide, aluminum sulfate, borax, boric acid and salts of boric acid (e.g. zinc borate), ammonium sulfate, calcium hydroxide. (B1), (B2), (B3), (B4) and (B5) together make up 100% by weight of component (B). The mass ratio of (B1) to (B2) is from 0.25 to 4, preferably from 0.33 to 3, more preferably from 0.5 to 2, and particularly preferably from 0.75 to 1.5.

[0068] Preferably, the polyamide molding composition according to the invention contains, besides the phosphorus-containing flame retardant, not more than 5000 ppm, preferably not more than 1000 ppm, more preferably not more than 500 ppm, particularly preferably not more than 250 ppm, of phosphorus from other sources, such as stabilizers, processing aids or catalysts.

[0069] If necessary, the polyamide molding compositions of the invention contain customary processing aids, such as stabilizers, oxidation retardants, other protective agents against thermal and ultraviolet degradation, lubricants and release agents, colorants such as dyes and pigments, nucleating agents, plasticizers, etc.

[0070] If desired, the polyamide molding composition of the present invention comprises, in addition to the components described, one or more typical additives such as stabilizers, other polymers, impact modifiers, plasticizers, colorants (e.g. pigments and dyes), processing aids, etc., optionally further additives selected from two or more typical additives.

[0071] Suitable oxidation stabilizers are aromatic amines, sterically hindered phenols, hydroquinones, phosphites, phosphonites, thiosynergists, hydroxylamines, benzofuranone derivatives, acryloyl modified phenols, etc. A wide variety of such oxidation stabilizers are commercially available, for example under the trade names Naugard 445, Irganox 1010, Irganox 1098, Irgafos 168, P-EPQ or Lowinox DSTDP. In general, the molding material contains about 0.01% to about 2% by weight of the oxidation stabilizer, preferably about 0.1% to about 1.5% by weight.

[0072] Furthermore, the molding material may also contain UV stabilizers or light stabilizers. Suitable UV stabilizers are organic UV absorbers, such as benzophenone derivatives, benzotriazole derivatives, resorcinol, salicylates, oxalanilides and phenyltriazines. Light stabilizers of the HALS type are tetramethylpiperidine derivatives. UV stabilizers and light stabilizers may be advantageously used in combination. Both are commercially available in a wide variety. The manufacturer's instructions regarding dosage may be followed.

[0073] Furthermore, the molding materials may contain hydrolysis stabilizers, for example monomeric, oligomeric or polymeric carbodiimides or bisoxazolines. Examples of other polymers which may be present in the molding material as additives are polyetheramides or polytetrafluoroethylene (PTFE).

[0074] Impact modifiers are known to those skilled in the art. They contain functional groups derived from unsaturated functional compounds incorporated into the backbone polymer or grafted onto the backbone. The most commonly used are EPM or EPDM rubbers free-radical grafted with maleic anhydride. This type of rubber can be used together with non-functionalized polyolefins, such as isotactic polypropylene, as described in EP-A-0 683 210.

[0075] Plasticizers are known to the skilled artisan from Gächter / Müller, Kunststoffadditive [Plastic Additives], C. Hanser Verlag, 2nd edition, p. 296. Examples of conventional compounds suitable for use as plasticizers are esters of p-hydroxybenzoic acid having 2 to 20 carbon atoms in the alcohol component or amides of arylsulfonic acids having 2 to 12 carbon atoms in the amine component, preferably amides of benzenesulfonic acid. Useful plasticizers include ethyl p-hydroxybenzoate, octyl p-hydroxybenzoate, i-hexadecyl p-hydroxybenzoate, Nn-octyltoluenesulfonamide, Nn-butylbenzenesulfonamide or N-2-ethylhexylbenzenesulfonamide.

[0076] Examples of suitable pigments and / or dyes are mixed oxides, titanium dioxide, iron oxide, zinc sulfide, ultramarine, organic pigments such as nigrosine, phthalocyanine, quinacridone, perylene, nigrosine, anthraquinone, pearlescent pigments.

[0077] Examples of suitable processing aids are paraffin, fatty alcohols, fatty acid amides, stearates such as calcium stearate, paraffin waxes, montanates, or polysiloxanes.

[0078] The polyamide moulding compositions according to the invention are preferably free of halogenated substances.

[0079] The molding material of the present invention has a V0 grade of flame retardant standard UL 94. This classification is made according to the UL guidelines, preferably in accordance with DIN EN 60695-11-10:2014, on test specimens with dimensions 125 mm x 13 mm x 0.8 mm, taking into account the revision 1 of said standard (October 2015).

[0080] The molding material of the present invention preferably has an elongation at break of at least 50%, preferably at least 100%, more preferably at least 150%, particularly preferably at least 200%. The elongation at break is measured on tensile test specimens of type 1A (DINEN ISO 527-2) according to DINEN ISO 527-1.

[0081] The molding material of the present invention preferably has very little migration of low molecular weight components even after relatively long storage at high temperatures.In this regard, test pieces with dimensions of 125 mm x 13 mm x 0.8 mm were stored at 150 ° C for 24 hours and the amount of material that migrated was measured.The measurement method is explained in more detail in the examples.The mass loss due to migration is preferably less than 1.1 wt %, more preferably less than 1.0 wt %, and particularly preferably less than 0.9 wt %, based on the entire molding material.

[0082] Preferably, the molding material of the present invention has a UL94 V-0 grade, a migration mass loss of less than 1.1% by weight, and an elongation at break of at least 50%.

[0083] The polyamide moulding compositions of the invention preferably do not contain additives which increase the electrical conductivity, in particular conductive carbon black or carbon nanotubes.

[0084] Preferred polyamide moulding compounds include: (A) a polyamide matrix comprising one or more polyamides having, as a statistical average throughout the polymer, from 8 to 16 carbon atoms, more preferably from 9 to 14 carbon atoms, and most preferably from 10 to 12 carbon atoms per amide unit; (B) A flame retardant composition comprising: (B1) Formula (V):

[0085] [ka]

[0086] (wherein Ar is ortho-, meta-, para-phenylene, naphthylene or biphenylene, but is not a 4,4'-(propane-2,2-diyl)diphenylene group; Ph is a phenyl group, which may have a desired substituent selected from C1 to C4 alkyl groups as necessary. At least one metal-free aryl phosphate comprising the component (B2) Formula (IV):

[0087] [ka]

[0088] and bisphenol A as a terminal group, (B3) carbohydrate polyols substituted with at least three, preferably at least four, more preferably at least five, even more preferably at least six hydroxy groups and optionally having an ether group, preferably at least one ether group; (B4) Melamine cyanurate having a particle size D50 measured by laser diffraction using a laser granulometer in accordance with the 2000-03-15 edition of BSISO 13320-1 of 0.5 to 100 μm, more preferably 0.6 to 50 μm, particularly preferably 0.7 to 25 μm, very particularly preferably 0.8 to 5 μm, and especially preferably 0.9 to 4 μm; (B5) Optionally, non-phosphorus-containing flame retardants selected from urea and urea derivatives, magnesium hydroxide, aluminum hydroxide, aluminum sulfate, borax, boric acid and salts of boric acid (e.g. zinc borate), ammonium sulfate, calcium hydroxide, or, optionally, halogenated flame retardants. A preferred polyamide molding material has a mass ratio of (B1) to (B2) of 0.25 to 4, preferably 0.33 to 3, more preferably 0.5 to 2, and particularly preferably 0.75 to 1.5. The phosphorus content of the entire flame-retardant composition is 0.5% by weight to 1.5% by weight based on the polyamide molding material.

[0089] Likewise preferred polyamide molding compositions include: (A) a polyamide matrix comprising one or more polyamides selected from PA8, PA9, PA10, PA11, PA12, PA6.10, PA6.12, PA6.14, PA8.10, PA9.10, PA9.12, PA10.10, PA10.12, PA12.12, PA6.16, PA10.16, more preferably PA6.12, PA10.10, PA10.12, PA11 and PA12, particularly preferably PA11 and PA12, (B) A flame retardant composition comprising: (B1) at least one compound of formula (I):

[0090] [ka]

[0091] preferably one or two units of formula (I) and at least two units of formula (II):

[0092] [ka]

[0093] and at least one metal-free aryl phosphate comprising a unit of formula (II), preferably two or three units of formula (II) (The units of formula (I) or the units of formula (II) are present alternately, The number of units of formula (II) is always one more than the number of units of formula (I), In formula (I), Ar is ortho-, meta-, para-phenylene, naphthylene or biphenylene, but is not a 4,4'-(propane-2,2-diyl)diphenylene group; In formula (II), Ph is a phenyl group, which may have a desired substituent selected from C1 to C4 alkyl groups as necessary. (B2) Formula (IV):

[0094] [ka]

[0095] and bisphenol A as a terminal group, (B3) carbohydrate polyols substituted with at least three, preferably at least four, more preferably at least five, even more preferably at least six hydroxy groups and optionally having an ether group, preferably at least one ether group; (B4) melamine cyanurate, (B5) Optionally, non-phosphorus-containing flame retardants selected from urea and urea derivatives, magnesium hydroxide, aluminum hydroxide, aluminum sulfate, borax, boric acid and salts of boric acid (e.g. zinc borate), ammonium sulfate, calcium hydroxide, or, optionally, halogenated flame retardants. A preferred polyamide molding material has a mass ratio of (B1) to (B2) of 0.25 to 4, preferably 0.33 to 3, more preferably 0.5 to 2, and particularly preferably 0.75 to 1.5. The phosphorus content of the entire flame-retardant composition is 0.5% by weight to 1.5% by weight based on the polyamide molding material.

[0096] Further preferred polyamide moulding materials include: (A) a polyamide matrix comprising one or more polyamides having, as a statistical average throughout the polymer, from 8 to 16 carbon atoms, more preferably from 9 to 14 carbon atoms, and particularly preferably from 10 to 12 carbon atoms per amide unit; (B) A flame retardant composition comprising: (B1) at least one compound of formula (I):

[0097] [ka]

[0098] preferably one or two units of formula (I) and at least two units of formula (II):

[0099] [ka]

[0100] and at least one metal-free aryl phosphate comprising a unit of formula (II), preferably two or three units of formula (II) (The units of formula (I) or the units of formula (II) are present alternately, The number of units of formula (II) is always one more than the number of units of formula (I), In formula (I), Ar is ortho-, meta-, para-phenylene, naphthylene or biphenylene, but is not a 4,4'-(propane-2,2-diyl)diphenylene group; In formula (II), Ph is a phenyl group, which may have a desired substituent selected from C1 to C4 alkyl groups as necessary. (B2) Formula (IV):

[0101] [ka]

[0102] and bisphenol A as a terminal group, (B3) carbohydrate polyols substituted with at least three, preferably at least four, more preferably at least five, even more preferably at least six hydroxy groups and optionally having an ether group, preferably at least one ether group; (B4) melamine cyanurate, (B5) Optionally, non-phosphorus-containing flame retardants selected from urea and urea derivatives, magnesium hydroxide, aluminum hydroxide, aluminum sulfate, borax, boric acid and salts of boric acid (e.g. zinc borate), ammonium sulfate, calcium hydroxide, or, optionally, halogenated flame retardants. More preferably, the polyamide molding material has a mass ratio of (B1) to (B2) of 0.25 to 4, preferably 0.33 to 3, more preferably 0.5 to 2, and particularly preferably 0.75 to 1.5. The phosphorus content of the entire flame-retardant composition is 0.5% by weight to 1.5% by weight based on the polyamide molding material. The molding material has a UL94 V-0 grade, a migration mass loss of less than 1.1% by weight, and an elongation at break of at least 50%.

[0103] The present invention relates to the use of the polyamide molding materials according to the invention for the production of parts and the parts themselves, preferably as coatings, covers, films, profiles, tubes, corrugated tubes, hollow bodies, seals, claddings, brackets, housings, sheathing, electrical and electronic components, such as preferably current-bearing metal components, in particular for fire protection applications in the automotive sector.

[0104] In the inventive method for insulating a current-bearing part, the part is preferably produced by compression molding, foaming, extrusion, coextrusion, blow molding, 3D blow molding, coextrusion blow molding, coextrusion 3D blow molding, coextrusion suction blow molding, extrusion coating, powder coating or injection molding. Methods of this kind are known to the person skilled in the art.

[0105] Preferably, the hybrid component of the present invention comprises a coated metal body, the coating of which comprises a polyamide molding compound comprising: (A) a polyamide matrix comprising one or more polyamides having at least 8 carbon atoms per amide unit; (B) A flame retardant composition comprising: (B1) at least one metal-free aryl phosphate; (B2) at least one aryl phosphonate, (B3) carbohydrate polyols, (B4) melamine cyanurate, (B5) Optionally, a non-phosphorus-containing flame retardant. The phosphorus content of the entire flame-retardant composition is between 0.5% and 1.5% by weight, preferably between 0.75% and 1.25% by weight, based on the polyamide moulding material, the components of which are described above.

[0106] Preferably, the non-phosphorus-containing flame retardant (B5) does not contain halogenated flame retardants. More preferably, the entire coating is free of halogenated substances. This is associated with the advantages of better corrosion protection and better environmental compatibility. Also, no halogen-containing substances are released even in the case of extreme heating, such as in a metal fire.

[0107] The invention also relates to a method for producing such a part, characterized in that a polyamide molding compound is molded into the part by extrusion or blow extrusion, injection molding or insert molding.

[0108] Particularly in the case of hybrid components, these can be molded after coating of the metal bodies. It is also possible to attach further accessories, such as plugs and sockets, screw connections, connecting elements to the hybrid components.

[0109] During molding, the polyamide molding composition of the invention has the advantageous feature of very good moldability, which means that during molding of the hybrid component, the coating of the polyamide molding composition (hereinafter also simply referred to as the polyamide coating) does not peel off, crack, shrink wrinkle and similar effects.

[0110] In particular, due to its good formability, the polyamide coating reliably provides effective electrical insulation, especially in the high voltage range, where large amounts of charge are transferred over long periods of time. In this context, a notable feature of the coating with the molding material of the invention is its excellent temperature stability. This is manifested in two ways: firstly, no significant mass loss due to transfer occurs. This maintains good insulating properties between the outside world and the current-bearing metal and at the surface of the polyamide coating (prevention of leakage currents). Secondly, even after long periods and high temperatures, the polyamide coating remains mechanically stable, for example against vehicle vibrations, which means that no cracks occur, which would reduce the insulating effect, especially in the above-mentioned moldings.

[0111] The hybrid component of the present invention can preferably be used in vehicles.Vehicles are understood to mean all means of transport, i.e. all means of transport for water, land, air and space.The hybrid component is used, for example, in charge transfer in a power source, both in the component that generates current and in the conduction to the receiving side.Preferred applications are in electric powered vehicles, for example in series or parallel connection of storage or generation systems, charge transfer from storage or generation systems to drive devices, charge transfer to further power consumption systems, preferably high voltage systems.

[0112] The hybrid components of the present invention may also preferably be used in stationary systems such as power plants (e.g. wind turbines, fuel cells or electrolysis cells, hydroelectric or other power plants), or intermediate processing facilities such as substations, or in transmission equipment such as cable and line systems underground, underwater or in structures such as bridges (especially the latter which are exposed to weather and vibrations during use).

[0113] The phosphorus content value of the articles of the present invention refers to the content of elemental phosphorus. EXAMPLES

[0114] method Differential Scanning Calorimetry (DSC) DSC measurements were performed in accordance with DIN ISO 11357-1:2016. Relative solution viscosity (η rel ) The samples are dissolved in m-cresol at 30° C. (0.005 g / mL) and measured at 25.00° C. in a viscosity measurement system (LAUDA PVS or Schott AVS Pro).

[0115] The molding material of the present invention has a V-0 grade according to the flame retardant standard UL 94. This classification is carried out according to the UL guidelines, preferably according to DIN EN 60695-11-10:2014 on test specimens with dimensions 125 mm x 13 mm x 0.8 mm, taking into account the revision 1 (October 2015) of said standard.

[0116] To measure the mass loss due to migration, a test specimen (125 mm x 13 mm x 0.8 mm) is weighed at 23°C and then heat treated in an oven at 150°C for 24 hours according to IEC 60216-4. The bar is then cooled for 30 minutes at 23°C and mechanically cleaned with a wet sheet of acetone until no wipeable coating remains (mirror sample). The bar is then dried for 15 minutes at 23°C and any static electricity is discharged using a static negator. The mass loss is calculated as the average value of three repeated weighings of the specimen. Negative values ​​indicate mass loss due to migration.

[0117] The elongation at break is measured according to DIN ISO 527-1. Dumbbell test pieces A1 according to part 2 of the cited standard were used. The measurements were carried out at 23°C and at a speed of 50 mm / min.

[0118] The elongation at break is particularly important in the context of the present invention, since particularly high requirements must be met for use as electrical insulators for covering electrical conductors, especially in the high voltage range. These conductors act as current bridges and must therefore bend up to 180 degrees without cracking the insulation. These requirements, for example in automotive applications, must be met with the greatest possible reliability in order not to endanger people working in the engine compartment.

[0119] material: PA6.10: Moderate viscosity PA6.12: Moderate viscosity PA10.12: Moderate viscosity PA12: High viscosity PA12 / 6: Moderate viscosity

[0120] Melamine cyanurate (MC), Melapur MC25 (BASF) Dipentaerythritol, Perstorp Fyrolflex® Sol-DP and -RDP, trademarks of ICL IP America Inc. (USA) ADKSTABFP-600, product of ADEKA Polymer Additives Europe (France) Disflamoll (registered trademark) DPK, a trademark of Lanxess GmbH (Germany) Aflammit® PCO900, a trademark of Thor Specialities Limited (UK) Amgard® CU, a trademark of Lanxess GmbH (Germany) Nofia® HM7000, a trademark of FRX polymers, Inc.

[0121] The stabilizer mixture includes an impact modifier, a stabilizer (thermal and / or oxidative) and a dye / pigment.

[0122] Example 1: General procedure for compounding polyamide molding materials The molding materials were produced in a co-rotating twin screw extruder. The solid components were metered in the main feeder and the liquid components were metered downstream into the melt. The housing temperatures are shown in Table 1. Pelletization was carried out by strand pelletization followed by drying in a dry air chamber dryer at 80°C for 12 hours.

[0123] Experimental Example 2: Preparation of test specimens The test pieces were prepared by injection molding according to DINENISO294-1 and DINENISO16396-2. The injection speed was 200 mm / s, the material temperatures were all 240 °C, and the corresponding mold temperatures are shown in Table 1. The following samples were obtained to measure typical material properties: - Type 1A multipurpose specimen for mechanical testing according to DIN ISO 527-2 - UL94V and UL94 test specimens for mass loss due to movement (172mm x 12.7mm x 0.8mm) - Plate for electrical measurements (130mm x 130mm x 1mm)

[0124] Experimental example 3: Mechanical and electrical tests The elongation at break was measured according to DIN EN ISO 527-1. The dielectric strength was measured in accordance with DIN EN60243-1, ACK20 / K20.

[0125] [Table 1]

[0126] [Table 2]

[0127] [Table 1-1]

[0128] [Table 1-2]

[0129] Surprisingly, the experimental examples show that when the aryl phosphates of the present invention are used, mass loss due to migration is less than when high molecular weight aryl phosphates containing 4,4'-(propane-2,2-diyl)diphenylene groups are used, especially aryl phosphates containing phenylene groups.

[0130] The experimental examples show that the desired properties in terms of flame retardancy and mass loss due to migration can only be achieved by combining metal-free aryl phosphates with aryl phosphonates. In this context, the combination of metal-free aryl phosphates with alkyl phosphonates is not suitable.

Claims

1. (A) a polyamide matrix comprising one or more polyamides having at least 8 carbon atoms per amide unit; (B) Below: (B1) at least one metal-free aryl phosphate; (B2) at least one aryl phosphonate; (B3) carbohydrate polyols, (B4) melamine cyanurate, (B5) Optionally, a non-phosphorus-containing flame retardant A flame retardant composition comprising A polyamide molding material comprising: The metal-free aryl phosphate (B1) is At least one compound of formula (I): 【Chemistry 1】 With units of At least two of formula (II): 【Chemistry 2】 With units of Including, The units of formula (I) or the units of formula (II) are alternately present, the number of units of formula (II) is always one more than the number of units of formula (I); In the formula (I), Ar is ortho-, meta-, para-phenylene, naphthylene, or biphenylene; In the formula (II), Ph is a phenyl group, which may have a desired substituent selected from C1 to C4 alkyl groups as required. the phosphorus content of the entire flame retardant composition is 0.5% by weight to 1.5% by weight based on the polyamide molding material; The mass loss is less than 1.1% by weight. Polyamide molding compound.

2. 2. The polyamide molding composition according to claim 1, wherein the polyamide is selected from PA8, PA9, PA10, PA11, PA12, PA6.10, PA6.12, PA6.14, PA8.10, PA9.10, PA9.12, PA10.10, PA10.12, PA12.12, PA6.16 and PA10.

16.

3. 2. The polyamide molding material according to claim 1, wherein the mass ratio of (B1) to (B2) is 0.25 to 4.

4. The aryl phosphonate (B2) has the formula (III): 【Chemistry 3】 (In the formula, R １ is an alkyl group having 1 to 4 carbon atoms, Each BAr is independently an aromatic group.

2. The polyamide molding material according to claim 1, which comprises a repeating unit represented by the formula:

5. 2. Use of the polyamide molding composition according to claim 1 for the production of components.

6. 2. A method for insulating a current-bearing part, comprising molding the polyamide molding material according to claim 1 into the current-bearing part by extrusion or hollow extrusion, injection molding or insert molding.

7. It is a hybrid part consisting of a coated metal body, The coating comprises: (A) a polyamide matrix comprising one or more polyamides having at least 8 carbon atoms per amide unit; (B) Below: (B1) at least one metal-free aryl phosphate; (B2) at least one aryl phosphonate; (B3) carbohydrate polyols, (B4) melamine cyanurate, (B5) Optionally, a non-phosphorus-containing flame retardant A flame retardant composition comprising The polyamide molding material according to claim 1, The phosphorus content of the entire flame retardant composition is 0.5% to 1.5% by weight based on the polyamide molding material.

8. Use of a hybrid component according to claim 7 for conducting electrical current.