Dust-free cold water dispersible preparation

Abstract

The present invention relates to cold-water dispersible dust-free preparations. These preparations consist of water-insoluble or slightly water-soluble particles containing a water-insoluble or slightly water-soluble active substance, the particles being coated with one or more layers, the outermost layer of which mainly comprises one or more hydrophobic powdering agents absorbed with at least one dispersing agent. The present invention also relates to a method for producing these particles and their use in food supplements, foods, animal feed, body care products, and pharmaceuticals. [Selection diagram] None

Description

[Technical field]

[0001] The present invention relates to a dust-free preparation which is dispersible in cold water, and to its manufacture and use. [Background technology]

[0002] The difficulty in the manufacture of preparations containing water-insoluble or only slightly water-soluble active substances (which according to the invention also includes preparations containing vitamin A, vitamin D, vitamin E and vitamin K and their derivatives, as well as preparations containing carotenoids, and mixtures of such preparations) is that during the final drying step carried out by spray agglomeration, the preparations form blackberry-like, brittle, highly branched, heavily dusting structures with an average particle size of about 150 μm, the high fines fraction (particles <100 μm) of which increases even further upon mechanical stress through the destruction of the very brittle structure. Summary of the Invention

[0003] Against this background, the object of the present invention was to provide a preparation consisting of mainly dust-free particles which are dispersible in cold water.

[0004] This object is achieved by a preparation consisting of particles having at least one shell layer which contains one or more hydrophobic powdering agents as main constituents and which encases an active substance-containing particle core, the proportion of this shell layer in the particle being preferably in the range of 0.5% to 8% by weight, more preferably in the range of 0.8% to 6% by weight, particularly preferably in the range of 1% to 5% by weight. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0005] Suitable hydrophobic powdering agents are finely divided oxides which have been hydrophobized according to the invention, in particular here hydrophobized oxides of the elements silicon, aluminum or titanium, or mixed oxides of said elements, or mixtures of said oxides. Preference is given here to hydrophobized fumed or precipitated silicas, in particular here to hydrophobized precipitated silicas.

[0006] The hydrophobizing oxides according to the invention, in particular here the hydrophobizing oxides of the elements silicon, aluminum or titanium, their mixed oxides and mixtures of said oxides, have a hydrophobizing effect of at least 80 m. 2 / g and / or an average particle size d50 of 20 μm or less. The average particle size is generally between 10 nm and 20 μm.

[0007] According to the invention, it is preferred that the distance is at least 80 m. 2 / g and / or an average particle size d50 of 20 μm or less, in particular hydrophobized precipitated silicas, e.g. 2 / g and an average particle size d50 of 10 μm (measured by laser diffraction according to ISO 13320-1).

[0008] The shell layer of hydrophobic powdering agent is preferably applied to completely encase the particle core, the particle coverage is at least 70%, preferably at least 75%, more preferably at least 80% according to SEM image analysis, and the particle core has an average particle size of 140-400 μm.

[0009] SEM images were generated using a Zeiss Ultra55 instrument. Detector: Topography using secondary electrons (8 kV).

[0010] Sample preparation: a) Surface preparation: Fixation: Leit C-Tab, Coating: ~12 nm Pt b) Preparation of the sections: Fixation: embedding in epoxy resin (EpoFix from Struers, no. 40200029), sectioning with an ultramicrotome at room temperature, coating: ca. 1 carbon filament

[0011] The shell layer containing the hydrophobic powdering agent can be applied directly onto the particle core or over one or more additional underlying shell layers.

[0012] The production results in largely dust-free particles, characterized by a low dust number of less than 15, but preferably a dust number of less than 10, more preferably a dust number of less than 8. The dust number of the coated particles is measured using a DustView II dust measuring device from Palas GmbH, Karlsruhe, Germany.

[0013] The apparatus used for the measurements consists of a sample funnel with a hatch, a downpipe, and a dust chamber with a removable dust box.

[0014] In dust count measurements, the dust solids formed after subjecting the material to a given stress (free fall and impact) are quantitatively recorded.

[0015] The evaluation is carried out optoelectronically, since the dusting solids result in an attenuation of the light beam, which is detected photometrically. The measured values ​​are recorded and evaluated in a control unit. The following measured values ​​are indicated numerically in the control unit: 1. Measurement value after 0.5 seconds (maximum value) 2. Measurement value after 30 seconds (dust value) 3. Dust count (sum of maximum value and dust value)

[0016] The dust count is determined as follows: Dust count: 25-100 Dust generation - Strong dust generation Dust count: 12-25 Weak dust emission - dust emission Dust count 8-12 Weak dust emission Dust count <8 Almost dust-free to dust-free.

[0017] The resulting particles after coating with a hydrophobic powdering agent meet the dust-free criteria, but are not water-dispersible due to the hydrophobic coating.

[0018] In order to make the particles dispersible in cold water, according to the invention, it is necessary to apply an additional substance, hereinafter called dispersant, to the hydrophobic shell layer of the powdering agent and to apply it uniformly to the hydrophobic shell layer, which is absorbed by the hydrophobic shell layer but may also form an additional shell layer depending on the amount applied.

[0019] The dispersant (mixtures of such dispersants can of course also be used) results in a particle spreading (°) of less than 75°, preferably less than 70°, more preferably less than 60°, determined by contact angle measurements after 0.1 seconds at 25°C, carried out on pellets of the pure powdering agent, in the present case on pellets of Sipernat D17.

[0020] In addition to the base dispersant or dispersant mixture, further substances can be added to the dispersant, however, if used, the selected substance should not increase the contact angle by more than 15% compared to the pure base.

[0021] The contact angle of the dispersant is measured on a pellet of Sipernat D17. Substances that are liquid at room temperature are measured at RT (25° C.), substances that are highly viscous or semi-solid at RT are heated to 60° C. and then measured at RT. For this, a small drop of the sample substance is dropped onto the pellet from a height of 1.5 cm at RT using a disposable syringe (needle diameter 1.65 mm). The contact angle formed between the drop and the pellet is measured using an OCAH150 plus from Dataphysics. This is done using the sessile drop method and the measurement data are evaluated by ellipse fitting.

[0022] By applying a dispersant or a mixture of dispersants to the hydrophobic shell layer, the dust count of the resulting particles is further reduced. The production results in particles characterized by a dust count of less than 10, but preferably a dust count of less than 8, and more preferably a dust count of less than 5.

[0023] Surprisingly, suitable as dispersants according to the invention are in particular substances which, in addition to the aforementioned spread, have an HLB value of 0.5 to 13, preferably an HLB value of 1 to 12.5, more preferably an HLB value of 1 to 5.5. Particularly preferred dispersants are MCT oil and / or propylene glycol monolaurate (Lauroglycol FCC), i.e. hydrophobic substances which would not be expected to enhance dispersibility in cold water, and / or Lutensol, which is amphiphilic in nature.

[0024] The proportion of the dispersant in the entire particles of the preparation is preferably in the range of 0.5% by weight to 6% by weight, more preferably in the range of 1% by weight to 4.5% by weight, and particularly preferably in the range of 1.5% by weight to 3% by weight.

[0025] The average diameter d50 of the produced coated particles is preferably <400 μm. In one particular embodiment, 140 μm≦d50≦300 μm, more preferably 150 μm≦d50≦275 μm. The d10 value of the cumulative distribution of the particle size distribution curve of the used granules is preferably >90 μm. In one particular embodiment, 90 μm≦d10≦125 μm, more preferably 95 μm≦d10≦110 μm. The d90 value of the cumulative distribution of the particle size distribution curve of the used granules is preferably <550 μm. In one particular embodiment, 275 μm≦d90≦540 μm, more preferably 285 μm≦d90≦500 μm.

[0026] In comparison, the particle sizes of a dusting preparation in which the final drying step was performed by spray agglomeration, forming a blackberry-like, brittle, highly branched structure, are d10=84 μm, d50=137 μm, and d90=217 μm.

[0027] For the present invention, the particle size of the particles was measured by laser diffraction using a Mastersizer 2000 instrument from Malvern.

[0028] When using a silicon-containing hydrophobic powdering agent, such as Sipernat D-17, and applying it using MCT oil as a dispersant, the Si / MCT ratio calculated from the quotient of g / 100g Si and %MCT is in the range of 0.2-1.2, preferably in the range of 0.25-1.0, more preferably has a value of 0.35-0.9. The Si content is measured by ICP-OES (inductively coupled plasma optical emission spectroscopy) (instrument: Varian Vista 725-ES IP-OES (emission)) at Si wavelengths of 251 nm and 611 nm.

[0029] A further advantage of the particles according to the invention is that they do not foam, or do not foam to any appreciable extent, which is evidenced by measuring how quickly the bubbles formed during the dispersion of the particles collapse. For the measurement, a 250 ml beaker is filled with 90 g of demineralized water, which is thermally equilibrated in a water bath at a nominal temperature of 25° C. Then, 10 g of the appropriate particles are added with magnetic stirring, and stirring is continued until no solids are anymore visible on the liquid surface. The magnetic stirrer is then removed and the mixture is thoroughly mixed with an Ultra-Turrax at setting 1 (4000 rpm) for 2 minutes, taking care to ensure that both the liquid and the air pass through the slots in the shaft and into the dispersion device. Immediately after mixing with the Ultra-Turrax, the foamy solution is transferred to a 250 ml graduated cylinder and the initial volume is measured. Further readings are taken 10 minutes after the transfer time, as well as 1 hour, 2 hours, 3 hours, and 4 hours later. The foaming rate is calculated by dividing the total fill height, i.e. the total volume of air bubbles and liquid, by the volume of liquid. It is characteristic of the particles according to the invention that during dispersion they form not very stable bubbles, which collapse almost completely after standing for just 1 hour, so that the foaming ratio measured after 1 hour is below 1.2.

[0030] For the purposes of the present invention, a water-insoluble or only slightly water-soluble active substance is to be understood as meaning a substance whose saturation solubility at RT (25° C.) in at least one of the following media: water, 0.1 M aqueous hydrochloric acid, aqueous phosphate buffer solution pH 7.2, 0.9% by weight aqueous sodium chloride solution is less than 1% by weight.

[0031] Water-insoluble or only slightly water-soluble active substances suitable for use according to the invention therefore include many active substances and effective substances, in particular pharmaceutical or cosmetic active substances, food supplements or dietary agents or active substances for food additives.

[0032] Examples of poorly soluble (slightly water soluble) substances for the purposes of the present invention are piroxicam, clotrimazole, carbamazepine, 17-β-estradiol, sulfathiazole, fenofibrate, benzocaine, lidocaine, dimethindene, biperiden, bisacodyl, clioquinol, droperidol, haloperidol, nifedipine, nitrendipine, tetracycline, phenytoin, glafenine, floctafenine, indomethacin, ketoprofen, ibuprofen, dipyridamole, mefenamic acid, amiodarone, felodipine, itraconazole ... Toconazole, danazol, furosemide, tolbutamide, ritonavir, lopinavir, naproxen, spironolactone, propafenone, progesterone, paclitaxel, docetaxel, theophylline, hydrocortisone, β-carotene, canthaxanthin, astaxanthin, zeaxanthin, lutein, lycopene, capsanthin, capsorubin, α-cryptoxanthin and β-cryptoxanthin, citraquinanthin, bixin, echinenone, β-apo-4-carotenal, β-apo-8-carotenal, β-apo-8-carotene ester, bixin, echinenone, β-apo-4-carotenal, β-apo-8-carotene ester, bixin, Vitamin A, tocopherol acetate, riboflavin, vitamin Q10, vitamin D, vitamin K, disulfiram, nimodipine, chlorothiazide, chlorpropamide, dicoumarol, chloramphenicol, digoxin, lonidamine, pizotifen, atovaquone, amprenavir, bexarotene, calcitriol, clofazimine, doxorcalciferol, dronabinol, dutasteride, etoposide, loratadine, risperidone, saquinavir, sirolimus, valproic acid, amphotericin, alprostadil, carmustine, chlordiazepoxide, Fenoldopam, melphalan, methocarbamol, oxytetracycline, docetaxel, fulvestrant, propofol, voriconazole, ziprasidone, leuprorelin acetate, Viadur, valrubicin, tramadol, celecoxib, etodolac, rofecoxib, oxaprozin, leflunomide, diclofenac, nabumetone, ibuprofen, flurbiprofen, tetrahydrocannabinol, capsaicin, ketorolac, albendazole, ivermectin, amiodarone, zileuton, zafirlukast, salbutamol,Montelukast, azithromycin, ciprofloxacin, clarithromycin, dirithromycin, rifabutin, rifapentine, trovafloxacin, baclofen, ritonavir, saquinavir, nelfinavir, efavirenz, dicoumarol, tirofiban, cilostazol, ticlopidine, clopidogrel, oprelvekin, paroxetine, sertraline, venlafaxine, bupropion, clomipramine, miglitol, repaglinide, glimepiride, pioglitazone, rosiglitazone, troglitazone, glyburide, glipizide, glybexil fosphenytoin, tiagabine, topiramate, lamotrigine, vigabatrin, amphotericin B, butenafine, terbinafine, itraconazole, fluconazole, miconazole, ketoconazole, metronidazole, griseofulvin, nitrofurantoin, lisinopril, benazepril, nifedipine, nisoldipine, telmisartan, irbesartan, eprosartan, valsartan, candesartan, minoxidil, terazosin, halofantrine, mefloquine, dihydroergotamine, ergotamine, frovatriptan, pi Zotifen, sumatriptan, zolmitriptan, naratriptan, rizatriptan, aminoglutethimide, busulfan, cyclosporine, mitoxantrone, irinotecan, etoposide, teniposide, paclitaxel, tacrolimus, sirolimus, tamoxifen, camptothecin, topotecan, nilutamide, bicalutamide, toremifene, atovaquone, metronidazole, furazolidone, paricalcitol, benzonatate, midazolam, zolpidem, gabapentin, zopiclone, digoxin, beclomethasone, budesonide, betamethasone, prednisolone Nisolone, cisapride, cimetidine, loperamide, famotidine, lansoprazole, rabeprazole, nizatidine, omeprazole, cetirizine, cinnarizine, dexchlorpheniramine, loratadine, clemastine, fexofenadine, chlorpheniramine, acitretin, tazarotene, calcipotriol, calcitriol, targretin, ergocalciferol, cholecalciferol, isotretinoin, tretinoin, calcifediol, fenofibrate, probucol, gemfibrozil, cerivastatin, pravastatin,Simvastatin, fluvastatin, atorvastatin, tizanidine, dantrolene, isosorbide dinitrate, dihydrotachysterol, essential fatty acids, codeine, fentanyl, methadone, nalbuphine, pentazocine, clomiphene, danazol, dihydroepiandrosterone, medroxyprogesterone, progesterone, rimexolone, megestrol acetate, estradiol, finasteride, mifepristone, l-thyroxine, tamsulosin, methoxsalen, tacrine, donepezil, raloxifene, verteporfin, sibutramine, pyridostigmine, and isomers, derivatives, salts, or mixtures thereof.

[0033] Particularly preferred are the carotenoids β-carotene, canthaxanthin, astaxanthin, zeaxanthin, lutein, lycopene, capsanthin, capsorubin, α-cryptoxanthin and β-cryptoxanthin, citranaxanthin, bixin, echinenone, β-apo-4-carotenal, β-apo-8-carotenal, β-apo-8-carotene esters, vitamin A, vitamin D, vitamin K, and tocopherol acetate, as well as isomers, derivatives, salts, or mixtures thereof.

[0034] The content of water-insoluble or only slightly water-soluble active substances in the preparations according to the invention is in the range from 0.1% to 60% by weight, preferably in the range from 0.2% to 50% by weight, particularly preferably in the range from 0.5% to 25% by weight and very particularly preferably in the range from 1% to 20% by weight, based on the dry mass of the preparation.

[0035] In the case of the carotenoids β-carotene, canthaxanthin, astaxanthin, zeaxanthin, lutein, lycopene, capsanthin, capsorubin, α-cryptoxanthin and β-cryptoxanthin, citranaxanthin, bixin, echinenone, β-apo-4-carotenal, β-apo-8-carotenal, β-apo-8-carotene esters, vitamin A, vitamin D, vitamin K and tocopherol acetate, as well as their isomers, derivatives, salts or mixtures, their content in the preparations according to the invention is particularly preferably 0.5% to 25% by weight, very particularly preferably 1% to 20% by weight.

[0036] To increase the stability of preparations containing water-insoluble or only slightly water-soluble active substances, it is advantageous to incorporate protective colloids, softeners and / or stabilizers into the active substance formulation.

[0037] The protective colloids used are vegetable gums, modified vegetable gums, gelatin, modified gelatin, starch, modified starch, lignosulfonates, chitosan, carrageenan, casein, caseinates, whey protein, zein, modified cellulose, pectin, modified pectin, vegetable proteins, and modified vegetable proteins, or mixtures thereof, but polyvinyl alcohol, polyvinylpyrrolidone, methylcellulose, carboxymethylcellulose, hydroxypropylcellulose, and alginates may also be used.

[0038] To increase the mechanical stability of the preparation, it is advantageous to add softeners to the colloid, such as sugars or sugar alcohols, such as sucrose, glucose, lactose, invert sugar, sorbitol, mannitol, glycerol, palatinose, or mixtures thereof.

[0039] The ratio of colloid and softener to carotenoid solution is generally selected to obtain a dry product containing by weight 3% to 20% active substance, 10% to 50% colloid, and 20% to 70% softener.

[0040] To increase the stability of the active substance against oxidative degradation, it may be advantageous to add one or more stabilizers, such as α-tocopherol, t-butyl-hydroxytoluene, t-butyl-hydroxyanisole, ascorbic acid, propyl gallate or ethoxyquin, in an amount of 0% to 10% by weight, preferably 0.5% to 8% by weight, based on the dry mass of the formulation.

[0041] Emulsifiers, such as ascorbyl palmitate, polyglycerol esters of fatty acids, sorbitan esters of fatty acids, propylene glycol esters of fatty acids or lecithin, may additionally be used in concentrations of 0% to 200% by weight, preferably 5% to 150% by weight, more preferably 10% to 80% by weight, based on the active substance used.

[0042] In some cases it may be advantageous to additionally use a physiologically acceptable oil, such as sesame oil, corn kernel oil, cottonseed oil, soybean oil or peanut oil or an ester of a medium-chain vegetable fatty acid, in a concentration of 0% to 500% by weight, preferably 10% to 300% by weight, more preferably 20% to 100% by weight, based on the active substance.

[0043] The present invention also provides methods for producing the formulations of the present invention.

[0044] The method involves the following steps: a) dissolving a water-insoluble or only slightly water-soluble active substance(s) in a volatile water-miscible organic solvent or in a mixture of water and a water-miscible organic solvent at a temperature between 50° C. and 200° C., optionally under high pressure, in a time of less than 10 seconds; b) rapidly mixing the solution obtained after a) with an aqueous or colloidally dispersed solution of a colloid at a temperature between 0° C. and 50° C., whereby the water-insoluble or only slightly water-soluble active substance(s) precipitate in colloidally dispersed form, c) converting the colloidal dispersion into a dry powder by spraying it with the additional use of a hydrophobic powdering agent, removing most of the solvent and then drying; and d) applying at least one dispersant to the free-flowing particles; Or, a2) dissolving the water-insoluble or only slightly water-soluble active substance(s) in a volatile, water-immiscible organic solvent at a temperature between 30 and 150° C., optionally under high pressure; b2) mixing the solution obtained after a) with an aqueous solution or a colloidal dispersion of a colloid to produce an emulsion; c2) removing the organic solvent from the emulsion and converting the resulting suspension / dispersion into a dry powder by adding a hydrophobic powdering agent and removing the water followed by drying; and d2) applying at least one dispersant to the free-flowing particles; Includes.

[0045] Suitable solvents for carrying out the method of the present invention are mainly water-miscible, heat-stable, volatile solvents that contain only carbon, hydrogen and oxygen, such as alcohols, ethers, esters, ketones and acetals.Preference is given to using ethanol, n-propanol, isopropanol, butane-1,2-diol 1-methyl ether, propane-1,2-diol 1-n-propyl ether or acetone.In general, it is advantageous to use a solvent that is at least 10% miscible with water, has a boiling point below 200°C and / or has less than 10 carbon atoms.

[0046] Depending on the type and amount of protective colloid used, after process step b) or b2), a dark colored viscous liquid is obtained. The solvent can be removed, for example, by extraction with a water-immiscible solvent, or, depending on the boiling point, by methods known per se, for example, by distillation (optionally under reduced pressure). In this case, it has been found to be convenient and possible to use the azeotrope obtained when using isopropanol directly as solvent, without removing water. However, it is preferred to remove the solvent in parallel with the removal of water by spray drying or spray granulation.

[0047] The powder preparations of the invention are particularly suitable as additives to food preparations (e.g. additives to food preparations for coloring foods such as beverages), as a means for producing pharmaceutical and cosmetic preparations and as a means for producing food supplement preparations (e.g. multivitamin preparations in the human and animal domain).

[0048] The present invention further provides the use of the aforementioned powder formulation of the present invention as an additive to animal feed, food, food supplements, personal care products, or pharmaceutical compositions.

[0049] The invention also provides an animal feed, a food, a food supplement, a personal care product, or a pharmaceutical composition comprising the powder preparation of the invention. EXAMPLES

[0050] The present invention is illustrated by the following examples, which are not intended to limit the invention in any way.

[0051] [example] 1. Astaxanthin, ascorbyl palmitate, and tocopherol are dissolved in an azeotropic mixture of water and isopropanol at a temperature between 100°C and 200°C and a pressure between 20 bar (2 MPa) and 100 bar (10 MPa) in a time of less than 10 seconds. 2. Dissolve sodium caseinate, glucose syrup, sodium ascorbate, and preservatives in water. 3. Treat the mixture from 2. with approximately 1% NaOH. 4. When the preparations from 1. and 2. are mixed at a temperature between 20°C and 80°C, the astaxanthin precipitates and becomes encapsulated / encased. 5. The isopropanol and a portion of the water are removed in multiple stages at subatmospheric pressure to form a 15-65 weight percent (suspension) dispersion. 6. This dispersion is sprayed with hydrophobic silica at the top of a spray tower to form fine droplets enveloped in hydrophobic silica. 7. The drying step is carried out in a downstream fluidized bed. 8. In a subsequent step, MCT oil is sprayed.

[0052] The coated free-flowing particles obtained as the final product according to the invention have a dust value of 2.4 and a D50 of 170 μm. The silicon content is 1.4% and the MCT content is 2.4%, which corresponds to a ratio of Si (%) to MCT (%) of 0.58. The contact angle of the particles measured at 25°C after 0.1 seconds against the surface of a Sipernat D17 pellet is 54°. Aspects of the present disclosure include the following. [1] Particles containing a water-insoluble or only slightly water-soluble active substance(s) coated with one or more layers, the outermost layer(s) comprising primarily one or more hydrophobic powdering agents having absorbed thereon at least one dispersing agent. [2] 2. The coated particles of embodiment 1, wherein the contact angle of the dispersant and / or dispersants with the surface of a pellet made of pure powdering agent is 75° or less, measured after 0.1 seconds at 25°C. [3] The coated particles according to embodiment 1 or 2, wherein the dispersant and / or the dispersants have an HLB value of 0.5-13, more preferably 1-12.5, and particularly preferably 1-5. [4] 4. Coated particles according to any one of the preceding aspects, wherein the dispersing agent comprises MCT oil and / or Lauroglycol and / or Lutensol. [5] 5. The coated particle according to any one of the preceding aspects, wherein the coverage of the particle surface with the hydrophobic powdering agent is at least 70%. [6] 5. The coated particle according to any one of the preceding aspects, wherein the coverage of the particle surface with the hydrophobic powdering agent is at least 80%. [7] 7. The coated particle of any one of the preceding aspects, wherein the hydrophobic powdering agent is a hydrophobized finely divided oxide. [8] 8. The coated particles of embodiment 7, wherein the hydrophobic finely divided oxide is selected from the group consisting of hydrophobized oxides of aluminum, silicon, zinc, and titanium. [9] The coated particle of embodiment 8, wherein the hydrophobized oxide is hydrophobized silica.

[10] Hydrophobic powders are at least 80m 2 10. The coated particle of any one of embodiments 7 to 9, having a surface area of ​​1 / g.

[11] 11. The coated particle of any one of embodiments 7 to 10, wherein the hydrophobic powdering agent has an average particle size of 20 μm or less.

[12] 12. The coated particles of embodiment 11, wherein the hydrophobic powdering agent has an average particle size of 10 nm to 20 μm.

[13] 13. The coated particles according to any one of aspects 1 to 12, wherein the ratio of hydrophobized silica to MCT oil per 100 g of particles is 0.2 to 1.2.

[14] 14. A preparation of coated particles according to any one of the preceding aspects, having a dust value of less than 10 after 30 seconds.

[15] A method for producing a particle according to any one of the preceding aspects, comprising the steps of: a) dissolving a water-insoluble or only slightly water-soluble active agent(s) in a volatile water-miscible organic solvent or in a mixture of water and a water-miscible organic solvent at a temperature between 50° C. and 200° C., optionally under high pressure, in a time of less than 10 seconds; b) rapidly mixing the solution obtained after a) with an aqueous or colloidal dispersion of a colloid at a temperature between 0° C. and 50° C., in which the water-insoluble or only slightly water-soluble active substance(s) precipitate in colloidal dispersion form, c) converting the colloidal dispersion into a dry powder by spraying it with the additional use of a hydrophobic powdering agent, removing most of the solvent and then drying; and d) applying at least one dispersant to the free-flowing particles; Or, a2) dissolving the water-insoluble or only slightly water-soluble active substance(s) in a volatile water-immiscible organic solvent at a temperature between 30 and 150° C., optionally under high pressure; b2) mixing the solution obtained after a) with an aqueous solution or a colloidal dispersion of a colloid to produce an emulsion; c2) removing the organic solvent from the emulsion and converting the resulting suspension / dispersion into a dry powder by adding a hydrophobic powdering agent and removing the water followed by drying; and d2) applying at least one dispersant to the free-flowing particles. A method comprising:

[16] Use of the coated particles according to any one of aspects 1 to 13 and the preparation according to aspect 14 in the form of food supplements, food, animal feed, personal care products, and pharmaceuticals.

Claims

1. Particles containing a water-insoluble or only slightly water-soluble active substance(s) coated with one or more layers, the outermost layer(s) comprising as a base one or more hydrophobic powdering agents having absorbed thereon at least one dispersing agent, A water-insoluble or only slightly water-soluble active substance means a substance that has a saturation solubility of less than 1% by weight at 25° C. in at least one of water, 0.1 M aqueous hydrochloric acid, aqueous phosphate buffer at pH 7.2, or 0.9% by weight aqueous sodium chloride solution; the proportion of at least one dispersant in the particles is in the range of 1% by weight to 4.5% by weight, Particles, wherein at least one dispersant is MCT oil.

2. 2. The coated particles according to claim 1, wherein the contact angle of the dispersant and / or dispersants with the surface of a pellet made of pure powdering agent is 75° or less, measured after 0.1 seconds at 25°C.

3. 3. The coated particle according to claim 1, wherein the coverage of the particle surface with the hydrophobic powdering agent is at least 70%.

4. 3. The coated particle according to claim 1, wherein the coverage of the particle surface with the hydrophobic powdering agent is at least 80%.

5. 5. The coated particle according to claim 1, wherein the hydrophobic powdering agent is a hydrophobized finely divided oxide.

6. 6. The coated particle of claim 5, wherein the hydrophobic finely divided oxide is selected from the group consisting of hydrophobized oxides of aluminum, silicon, zinc, and titanium.

7. 7. The coated particle of claim 6, wherein the hydrophobized oxide is hydrophobized silica.

8. Hydrophobic powders are at least 80m 2 The coated particle of claim 5, having a surface area of ​​1 / g.

9. 9. Coated particles according to any one of claims 5 to 8, wherein the hydrophobic powdering agent has an average particle size of 20 μm or less.

10. 10. The coated particles of claim 9, wherein the hydrophobic powdering agent has an average particle size of 10 nm to 20 μm.

11. The coated particles according to any one of claims 1 to 10, wherein the weight ratio of the hydrophobized silica content in 100 g of the particles to the MCT oil content in 100 g of the particles is 0.2 to 1.

2.

12. 12. A preparation consisting of coated particles according to any one of claims 1 to 11, having a dust value of less than 10 after 30 seconds.

13. A method for producing particles according to any one of claims 1 to 11, comprising the steps of: a) dissolving a water-insoluble or only slightly water-soluble active substance(s) in a volatile water-miscible organic solvent or in a mixture of water and a water-miscible organic solvent, optionally under high pressure, at a temperature between 50° C. and 200° C. in a time of less than 10 seconds; b) rapidly mixing the solution obtained after a) with an aqueous or colloidal dispersion of colloids at a temperature between 0° C. and 50° C., whereby the water-insoluble or only slightly water-soluble active substance(s) precipitate in colloidal dispersion form, c) converting the colloidal dispersion into a dry powder by spraying it with the additional use of a hydrophobic powdering agent, removing most of the solvent and then drying; and d) applying at least one dispersant to the dry powder; Or, a2) dissolving the water-insoluble or only slightly water-soluble active substance(s) in a volatile water-immiscible organic solvent at a temperature between 30 and 150° C., optionally under high pressure; b2) mixing the solution obtained after a) with an aqueous or colloidal dispersion of a colloid to produce an emulsion; c2) removing the organic solvent from the emulsion and converting the resulting suspension / dispersion into a dry powder by adding a hydrophobic powdering agent and removing the water followed by drying; and d2) applying at least one dispersant to the dry powder A method comprising:

14. Use of the coated particles according to any one of claims 1 to 11 and the preparations according to claim 12 in the form of food supplements, food, animal feed, personal care products and pharmaceuticals, except as a method for treating humans.