Thermally initiated, acid-catalyzed reactions of silyl hydrides with α-β unsaturated esters.

Abstract

The composition comprises a silyl hydride, an α-β unsaturated ester, a Lewis acid catalyst, and a compound of the following formula: 1 R 2 R 3 N [wherein the nitrogen is not a member of an N=CN bond, R 1 , R 2 , and R 3 wherein each of R is independently selected from the group consisting of hydrogen, alkyl, substituted alkyl, and conjugated moieties; 1 , R 2 , and R 3 At least one of is a conjugated moiety connected to the nitrogen by a conjugated carbon.

Description

[Background technology]

[0001] FIELD OF THEINVENTION The present invention relates to a composition comprising a silyl hydride, an α-β unsaturated ester, a Lewis acid catalyst, and an amine blocking agent for the Lewis acid catalyst. By heating the composition, the Lewis acid catalyst is released from the amine blocking agent, which can induce a reaction between the silyl hydride and the α-β unsaturated ester.

[0002] Introduction Strong Lewis acids are known catalysts for many reactions. For example, the Piers-Rubinsztajn (PR) reaction of silyl hydrides with silyl ethers is a well-known reaction catalyzed by strong Lewis acids, particularly tris(pentafluorophenyl)borane ("BCF"). Similar Lewis acid-catalyzed reactions include the rearrangement reaction of silyl hydrides with polysiloxanes and the rearrangement reaction of silyl hydrides with silanols. See, for example, Chem.Eur.J.2018,24,8458-8469.

[0003] Lewis acid catalyzed reactions such as the PR reaction tend to react rapidly even at 23 degrees Celsius (°C). These reactive systems are highly reactive, limiting their applications. This reaction can be desirable in applications such as coatings and adhesives, but the reactive system must be stored in a multi-part system to eliminate reaction before application. Yet, as soon as the components are combined, the reaction can occur so rapidly that there is little time to apply the reactive system. It would be desirable to identify ways to control Lewis acid catalyzed reactions and ideally provide them as one-part reactive systems containing reactants and Lewis acid catalyst that are storage stable at 23°C to allow batch preparation, storage, and use, but in a form that can be triggered to react as desired.

[0004] Ultraviolet (UV) photosensitive blocking agents are combined with Lewis acids to form blocked Lewis acids that release the Lewis acid upon exposure to UV light. Upon exposure to UV light, the blocking agent dissociates from the Lewis acid, freeing it to catalyze the reaction. A challenge with systems containing these blocked Lewis acids is that they must be kept in the dark to maintain stability. Additionally, exposure to UV light is required to initiate the reaction, and in thick compositions it can be difficult to get UV light transmission throughout the composition to rapidly initiate cure.

[0005] In particular, amines have been of interest in combination with Lewis acids in PR reaction-type systems. However, amines have been reported to completely inhibit the reaction. See, e.g., Chem.Comm. 2010, 46, 4988-4990 at 4988. While most amines essentially complex irreversibly with Lewis acid catalysts, triarylamines were found to be an exception and were later identified as not impairing Lewis acids when catalyzing the PR reaction. See, Chem.Eur.J. 2018, 24, 8458-8469 at 8461 and 8463. Summary of the Invention [Problem to be solved by the invention]

[0006] It is desirable to identify a method for preparing a one-component reaction system for Lewis acid catalyzed reactions that is storage stable at 23° C. upon exposure to UV light, but can be induced to react, if desired, at temperatures preferably below 100° C.

[0007] The present invention provides a solution to the problem of identifying a method for preparing a one-part reactive system for Lewis acid catalyzed reactions that is storage stable at 23° C. even when exposed to UV light, but can be triggered to react when desired. In particular, the present invention provides a solution to such a problem in the reaction of silyl hydrides with α-β unsaturated esters. Furthermore, the present invention provides such solutions that can be triggered to react when heated. The compositions of the present invention simultaneously avoid gelling at 23° C. for 8 hours or more, preferably 10 hours or more, but at the same time gel (or cure) at 90° C. within 10 minutes, preferably within 5 minutes, more preferably within 1 minute. Such compositions are desirable because their stability against gelling at 23° C. means that larger batches can be made at one time, since it allows the one-part reactive system to be formed and stored for longer periods of time. Rapid gelling / curing times at 90° C. are important in applications where exposure to high temperatures (e.g., 100° C. or higher) for extended periods of time is undesirable, such as release coating applications where the substrate to which the composition is applied may degrade at high temperatures.

[0008] Hydrosilylation reaction is one way to react silyl hydrides and unsaturated bonds in a curing reaction. Hydrosilylation typically requires the presence of a transition metal catalyst, which tends to remain undesirably in the reaction product. However, it has been discovered that silyl hydrides and α-β unsaturated esters undergo reductive curing reactions in the presence of Lewis acid catalysts without the need for transition metal catalysts. The reductive curing reaction of silyl hydrides with α-β unsaturated esters is an addition reaction that either adds silicon to the carbonyl oxygen of the α-β unsaturated ester to form a new silyl ether bond, or adds silicon to the α-carbon of the α-β unsaturated ester to form a new silicon-carbon bond. The reaction produces these addition products without producing any by-products, especially gaseous substances, other than the new addition products. It also has the advantage of not requiring expensive platinum catalysts and providing a milder and faster addition reaction than platinum-catalyzed hydrosilylation.

[0009] Lewis acid catalyzed reductive cure of silyl hydrides and α-β unsaturated esters may be desirable for curing siloxanes in coating, adhesive, and sealant applications. However, reductive cure reactions tend to be rapid, necessitating the need to supply and store the reaction systems as two-part systems in which the catalyst is kept separate from the Si-H and / or α-β unsaturated esters until reaction is desired. One-part reaction systems are easier to handle and more desirable than two-part systems, providing storage stability for storage, but it is desirable to be able to store the reaction components together in a one-part reaction system in such a way that they have a way to trigger the reductive cure reaction when it is desired to cure the system.

[0010] The present invention is the result of the surprising and unexpected discovery of certain amines that complex with Lewis acid catalysts at 23°C, blocking the activity of the Lewis acid catalyst, but release the Lewis acid catalyst when heated. As a result, certain amines are heat-triggerable blocking agents for Lewis acid catalysts that block the Lewis acid catalyst at 23°C, but release the Lewis acid catalyst and catalyze reactions at high temperatures, such as 90°C or higher. This is surprising in light of previous understanding in the art. As mentioned above, the current understanding is that amines either irreversibly complex with Lewis acid catalysts or are unable to impair the Lewis acid catalyst in Lewis acid catalyzed reactions. See Chem.Comm. 2010, 46, 4988-4990 at 4988 and Chem.Eur.J. 2018, 24, 8458-8469 at 8461 and 8463.

[0011] The present discovery of amines that act as thermally induced blocking agents for Lewis acid catalysts makes available the compositions of the present invention that function as one-component reactive systems that include, in addition to the amine blocking agent, a Lewis acid catalyst, a silyl hydride, and an α-β unsaturated ester.

[0012] In a first aspect, the present invention provides a method for the preparation of a silyl hydride, an α-β unsaturated ester, a Lewis acid catalyst, and a compound having the following formula: 1 R 2 R 3N [wherein, R 1 , R 2 , and R 3 each of which is independently selected from the group consisting of hydrogen, alkyl, substituted alkyl, and conjugated moieties, 1 , R 2 , and R 3 At least one of is a conjugated moiety attached to the nitrogen by a conjugated carbon.

[0013] In a second aspect, the invention is a process comprising: (a) providing a composition of the first aspect; and (b) heating the composition to a temperature sufficient to dissociate the Lewis acid catalyst from the amine.

[0014] The compositions of the present invention are suitable as one-part reactive systems for, for example, coatings, encapsulants, and adhesives. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] Test methods refer to the most recent test method as of the priority date of this document unless a date is given with the test method number. Reference to a test method includes both a reference to the testing society and the test method number. The following test method abbreviations and identifiers apply herein: ASTM refers to ASTM International, EN refers to European Norm, DIN refers to Deutsches Institut fuer Normung, and ISO refers to the International Organization for Standardization.

[0016] "Plurality" means two or more. "And / or" means "and, or alternatively." All ranges are inclusive of endpoints unless otherwise indicated. Products identified by trade names refer to compositions available from suppliers under those trade names as of the priority date of this document, unless otherwise indicated herein.

[0017] "Siloxane" refers to a molecule that contains at least one siloxane (Si-O-Si) bond. Desirably, the siloxanes of the present invention are "polysiloxanes," which refers to molecules that contain multiple Si-O-Si bonds. Polysiloxanes typically contain siloxane units, referred to as M, D, T, or Q units. The standard M unit has the formula (CH3)3SiO 1 / 2 The standard D unit has the formula (CH3)2SiO 2 / 2 The standard T unit has the formula (CH3)SiO 3 / 2 The standard Q unit has the formula SiO 4 / 2 The M, D, and T units have one or more methyl groups replaced with hydrogen or some other moiety.

[0018] A "silyl hydride" is a molecule that contains a silicon-hydrogen (Si-H) bond and can contain multiple Si-H bonds.

[0019] "α-β unsaturated ester" refers to a molecule containing an ester group and a double bond between the α and β carbons in the chain, where the carbon atom is named based on its proximity to the carbonyl group of the ester. Acrylates and methacrylates are examples of α-β unsaturated esters. Alpha-β unsaturated esters may also include silicon, such as polysiloxanes containing α-β unsaturated esters.

[0020] "(Meth)acrylate" refers to the group consisting of methacrylates and acrylates, including silicon-containing molecules that contain acrylate and / or methacrylate functional groups.

[0021] An "alkyl" is a hydrocarbon group derived from an alkane by removing a hydrogen atom. A "substituted alkyl" is an alkyl having an atom or chemical moiety other than carbon and hydrogen in place of at least one carbon or hydrogen.

[0022] An "aryl" is a group derived from an aromatic hydrocarbon by removing a hydrogen atom. A "substituted aryl" is an aryl that has an atom or chemical moiety other than carbon and hydrogen in place of at least one carbon or hydrogen.

[0023] "Conjugated" refers to a set of alternating carbon-carbon single and double and / or triple bonds whose p-orbitals are connected in a manner that allows for delocalized electrons between the carbon bonds. "Conjugated carbon" refers to a set of alternating carbon-carbon single and double bonded carbons that are conjugated. "Non-conjugated" refers to a carbon that is not part of a conjugated system. "Aromatic" refers to a cyclic, planar conjugated molecule.

[0024] A "blocking agent" is a moiety that binds to a second moiety to prevent activity of the second moiety in some way. For example, a blocking agent on a catalyst will exclude the catalyst from catalytic activity by complexing with the blocking agent.

[0025] Lewis acids catalyze the reaction of silyl hydrides with α-β unsaturated esters, generally as shown below: [ka] where two optional reaction products are shown: This reaction forms new siloxane bonds and is useful for forming crosslinked polysiloxane systems.

[0026] This rearrangement reaction is useful for forming new siloxane bonds and forming crosslinked polysiloxane systems.The particularly desirable property of this reaction over other Lewis acid catalyzed reactions, such as the Piers-Rubinsztajn (PR) reaction, is that this reaction typically does not produce volatile by-products that can generate bubbles when the reaction is used to cure siloxane polymers.Therefore, this reaction is ideal for making transparent cured compositions and films.

[0027] The present invention includes compositions comprising a mixture of a silyl hydride, an α-β unsaturated ester, a Lewis acid catalyst, and a particular amine. It has been discovered that the particular amine of the present invention acts as a blocking agent for the Lewis acid catalyst at 23° C., but releases the Lewis acid catalyst at elevated temperatures (e.g., 80° C. or higher, or 90° C. or higher). The composition of the present invention is a one-part Lewis acid catalyzed reaction system that is storage stable at 23° C., but undergoes Lewis acid catalysis to gel within 10 minutes, preferably within 5 minutes, and more preferably within 1 minute at elevated temperatures. Such compositions achieve the objective of the present invention to provide a one-part system that is “storage stable” for Lewis acid catalyzed reactions. By “storage stable” is meant that the reaction system does not gel within 8 hours or less, even more preferably within 10 hours or less, yet more preferably within 12 hours or less, and yet even more preferably within 24 hours or less at 23° C. Storage stability is evaluated using the “23° C. shelf life” in the Examples section below. The composition of the present invention further provides a one-part reaction system for Lewis acid catalyzed reactions that is storage stable at 23° C., but is heat-induced as desired. In particular, the compositions of the present invention gel in 10 minutes or less, more preferably 5 minutes or less, and even more preferably 1 minute or less at 90° C. The “Cure Rate at 90° C.” test in the Examples section below is used to determine the cure rate at 90° C.

[0028] α-β unsaturated ester The α-β unsaturated ester has the following composition structure (α-β unsaturated ester group) at one or more positions in the molecule: [ka] where R contains the carbon bonded to the oxygen shown and may contain any other atoms. By way of example, R may be an alkyl, substituted alkyl, benzyl, or a polymeric group having a carbon connected to an oxygen.

[0029] Desirably, the α-β unsaturated ester group may be part of a polymer. Such a polymer may contain one or more α-β unsaturated ester groups. The α-β unsaturated ester is desirably selected from (meth)acrylates, i.e., compounds having acrylate and / or methacrylate groups, as shown below, where the (meth)acrylate group is attached to the polymer via an oxygen having a single bond. [ka] [ka]

[0030] The α-β unsaturated ester group may be connected to a silicon atom, which is typically part of a siloxane group (Si-O-Si) or a polysilane group (Si-Si), and the silicon atom itself is typically part of a polysiloxane chain. When the α-β unsaturated ester group is connected to a silicon atom, the connection between oxygen and silicon is via one or more (generally 2 or more, 3 or more, but at the same time 6 or less, 5 or less, or even 4 or less) carbon atoms through a single-bonded oxygen atom in the α-β unsaturated ester group.

[0031] Examples of suitable α-β unsaturated esters include those of the formula MD x D MA y M, wherein D MA is a D-type siloxane unit, in which one of the methyl groups of a standard D-siloxane unit is replaced with methacryloxypropyl; [ka] where the subscript x is the average number of D units per molecule and can be 10 or more, 20 or more, 30 or more, 40 or more, 50 or more, 60 or more, 70 or more, 80 or more, 90 or more, 100 or more, 110 or more, 120 or more, 130 or more, 140 or more, 150 or more, 160 or more, 170 or more, 180 or more, 190 or more, and even 200 or more, but at the same time generally a value of 1000 or less, 800 or less, 600 or less, 400 or less, or even 200 or less, and the subscript y is the average number of D units per molecule and can be 10 or more, 20 or more, 30 or more, 40 or more, 50 or more, 60 or more, 70 or more, 80 or more, 90 or more, 100 or more, 110 or more, 120 or more, 130 or more, 140 or more, 150 or more, 160 or more, 170 or more, 180 or more, 190 or more, and even 200 or more. MA is the average number of siloxane units and is 1 or more, 2 or more, 3 or more, 4 or more, 5 or more, 6 or more, 7 or more, 8 or more, 9 or more, 10 or more, 12 or more, 14 or more, 16 or more, 18 or more, or even 20 or more, while generally being a value of 50 or less, 40 or less, 30 or less, 20 or less, or even 10 or less. 29 Determine subscript values ​​by Si nuclear magnetic resonance spectroscopy.

[0032] Examples of suitable α-β unsaturated esters that are methacryloxypropyl-terminated polydimethylsiloxanes include those available from Gelest under the trade names DMS-R11 (125-250 cSt), DMS-R18 (50-90 cSt), DMS-R11 (8-14 cSt), and DMS-R31 (1,000 cSt), as well as an acrylate-functional silane available from Gelest under the designation SIVATE™ A200.

[0033] Typically, the concentration of the α-β unsaturated ester in the composition is 70 weight percent (wt%) or more, 75 wt% or more, 80 wt% or more, 85 wt% or more, or even 90 wt% or more, based on the combined weight of the silyl hydride, the α-β unsaturated ester, the Lewis acid catalyst, and the amine, while at the same time typically is 90 wt% or less, 85 wt% or less, 80 wt% or less, or even 75 wt% or less.

[0034] Silyl hydride Silyl hydrides contain one, preferably two or more Si-H bonds. The Si-H bonds are typically part of polysilanes (molecules containing multiple Si-H bonds) or polysiloxanes. Silyl hydrides containing multiple Si-H bonds are desirable as crosslinkers in the compositions of the present invention because they can react with multiple siloxane bonds.

[0035] The silyl hydrides of the present invention may be polymeric. The silyl hydrides may be linear, branched, or contain a combination of linear and branched silyl hydrides. The silyl hydrides may be polysilanes, polysiloxanes, or combinations of polysilanes and polysiloxanes.

[0036] Desirably, the silyl hydride is a polysiloxane molecule with one Si-H bond or two or more Si-H bonds. When the silyl hydride is a polysiloxane, the Si-H bond is on the silicon atom of an M-type or D-type siloxane unit. The polysiloxane may be linear and may contain only M-type and D-type units. Alternatively, the polysiloxane may be branched and may contain T-type and / or Q-type units.

[0037] Examples of suitable silyl hydrides include pentamethyldisiloxane, bis(trimethylsiloxy)methyl-silane, tetramethyldisiloxane, DMS-H03, DMS-H25, DMS-H31, and DMS-H41 available from Gelest. H Containing poly(dimethylsiloxane) (e.g., MD H 65 M), tetramethylcyclotetrasiloxane, and hydride-terminated poly(dimethylsiloxane).

[0038] The concentration of the silyl hydride is typically sufficient to provide a molar ratio of Si-H groups to combination of α-β unsaturated ester groups that is 0.2 or more, 0.5 or more, 0.7 or more, 0.8 or more, 0.9 or more, 1.0 or more, 1.2 or more, 1.4 or more, 1.6 or more, 1.8 or more, 2.0 or more, 2.2 or more, or even 2.5 or more, while at the same time being typically 5.0 or less, 4.5 or less, 4.0 or less, 3.5 or less, 3.0 or less, 2.8 or less, 2.5 or less, 2.3 or less, 2.0 or less, 1.8 or less, 1.6 or less, 1.4 or less, 1.2 or less, or even 1.0 or less.

[0039] Either the α-β unsaturated ester or the silyl hydride (or both) can function as a crosslinker in the reaction. A crosslinker has at least two reactive groups in one molecule and reacts with two different molecules through these reactive groups to crosslink them together. Increasing the length of the linear chain between the reactive groups in the crosslinker tends to increase the flexibility of the resulting crosslinked product. In contrast, shortening the length of the linear chain between the reactive groups in the crosslinker tends to reduce the flexibility of the resulting crosslinked product. In general, to obtain a more flexible crosslinked product, a linear crosslinker is desired, and the length between the reactive sites is selected to obtain the desired flexibility. To obtain a less flexible crosslinked product, a shorter linear crosslinker or even a branched crosslinker is desired to reduce the flexibility between the crosslinked molecules.

[0040] The silyl hydride may be the same molecule as the α-β unsaturated ester, i.e., a single molecule containing both α-β unsaturated ester and silyl hydride functional groups may function as both a silyl hydride and an α-β unsaturated ester. Alternatively, the silyl hydride may be a different molecule from the α-β unsaturated ester. The silyl hydride may not include an α-β unsaturated ester group. The α-β unsaturated ester may not include a silyl hydride group.

[0041] The compositions (and reaction processes) of the present invention may include two or more silyl hydrides, two or more α-β unsaturated esters, and / or two or more components that function as both silyl hydrides and α-β unsaturated esters.

[0042] Typically, the concentration of the silyl hydride in the composition is 5% by weight or more, 10% by weight or more, 15% by weight or more, 20% by weight or more, or even 25% by weight or more, while at the same time, typically is 30% by weight or less, 25% by weight or less, 20% by weight or less, 15% by weight or less, or even 5% by weight or less, based on the combined weight of the silyl hydride, the α-β unsaturated ester, the Lewis acid catalyst, and the amine.

[0043] Lewis Acid Catalyst The Lewis acid catalyst is desirably selected from the group consisting of aluminum alkyls, aluminum aryls, aryl boranes, aryl boranes including triaryl boranes (including substituted aryl and triaryl boranes such as tris(pentafluorophenyl)borane), boron halides, aluminum halides, gallium alkyls, gallium aryls, gallium halides, silium cations, and phosphonium cations. Examples of suitable aluminum alkyls include trimethylaluminum and triethylaluminum. Examples of suitable aluminum aryls include triphenylaluminum and tris-pentafluorophenylaluminum. Examples of triaryl boranes include the following formula: [ka] where R is independently selected at each occurrence from H, F, Cl, and CF3. Examples of suitable boron halides include (CH3CH2)2BCl and boron trifluoride. Examples of suitable aluminum halides include aluminum trichloride. Examples of suitable gallium alkyls include trimethylgallium. Examples of suitable gallium aryls include triphenylgallium. Examples of suitable gallium halides include trichlorogallium. Examples of suitable silium cations include (CH3CH2)3Si + X - and Ph3Si + X - Examples of suitable phosphonium cations include FP(C6F5)3 + X - Examples include:

[0044] The Lewis acid is typically present in the composition at a concentration of 10 parts per million (ppm) by weight or more, 50 ppm or more, 150 ppm or more, 200 ppm or more, 250 ppm or more, 300 ppm or more, 350 ppm or more, 400 ppm or more, 450 ppm or more, 500 ppm or more, 550 ppm or more, 600 ppm or more, 70 ppm or more, 750 ppm or more, 1000 ppm or more, 1500 ppm or more, 2000 ppm or more, 4000 ppm or more, 5000 ppm or more, or even 7500 ppm or more, but at the same time, typically 10,000 ppm or less, 7500 ppm or less, 5000 ppm or less, 1500 ppm or less, 1000 ppm or less, or 750 ppm or less, based on the combined weight of the silyl hydride and the α-β unsaturated ester.

[0045] Amine The choice of amine is important because it must complex with the Lewis acid at 23°C and inhibit the catalytic activity of the Lewis acid in the reaction composition at that temperature, and must release the Lewis acid at such a high temperature that the reaction composition gels rapidly (within 10 minutes, preferably within 5 minutes, more preferably within 1 minute) at 90°C. The reaction composition can be monitored at 23°C and 90°C to determine the gel time (see Examples section below). Alternatively, or additionally, the temperature at which the curing reaction exotherm occurs can be characterized by differential scanning calorimetry (Tpeak, see Examples section below for procedure). The Tpeak value of the composition should increase relative to the Tpeak of the same amine-free composition when a suitable amine is present, but desirably remains below 130°C, preferably below 120°C, more preferably below 110°C, to reflect sufficient dissociation to cure rapidly at 90°C.

[0046] Amines are reported to irreversibly complex with Lewis acid catalysts, except for triarylamines, which are reported to not damage the Lewis acid catalyst. Without being bound by theory, the present invention appears to be the result of the discovery that by having one or more conjugated moieties attached to the nitrogen of the amine through a conjugated carbon, the conjugated moieties help delocalize the free electrons of the amine, making it weaker as a Lewis base. As a result, it has been discovered that amines having at least one conjugated moiety attached to the nitrogen of the amine through a conjugated carbon complex and block the Lewis acid catalyst at 23°C in such a way as to damage the gelation of the reaction composition in 4 hours or less, preferably 8 hours or less, more preferably 10 hours or less, and even more preferably less than 12 hours at 23°C, but at the same time complex weakly enough to release the Lewis acid catalyst when heated at 90°C and gel the composition in 10 minutes or less, preferably 5 minutes or less, and more preferably 1 minute or less.

[0047] To be sufficiently weak Lewis bases, the amines of the present invention have at least one, preferably at least two, and may have three conjugated moieties attached to the nitrogen of the amine through a conjugated carbon such that the free electron pair on the nitrogen can dissociate with the conjugated moiety and weaken the amine as a Lewis base. Preferably, the conjugated moiety is an aromatic moiety.

[0048] Triarylamines have three aromatic conjugated moieties, each attached to the amine nitrogen through a conjugated carbon. As a result, triarylamines are examples of amines that optimally delocalize the nitrogen free electrons to produce a weak Lewis base. This is consistent with prior art reporting that triarylamines do not impair Lewis acid catalysis. Nevertheless, triarylamines have surprisingly been found to have a blocking effect on Lewis acid catalysis at 23°C and inhibit Lewis acid catalysis at 23°C, within the broadest range of amines suitable for use in the present invention. Desirably, the amines of the present invention are stronger Lewis bases than triarylamines to achieve a greater blocking effect (and therefore longer storage stability) at 23°C. In that regard, the amines of the present invention may have one, two, or three conjugated moieties attached to the nitrogen of the amine through a conjugated carbon, but desirably the amine is other than a triarylamine. The compositions of the present invention may be free of triarylamines.

[0049] The ability of the conjugated moiety to weaken the strength of the amine as a Lewis base can be further tuned with substituents that can be attached to the conjugated moiety. The inclusion of an electron-withdrawing group (such as a halogen) on the conjugated moiety will further pull the nitrogen electron into the delocalized conjugated system, weakening the strength of the amine as a Lewis base. The inclusion of an electron-donating group on the conjugated moiety has the opposite effect, increasing the strength of the resulting amine as a Lewis base compared to the same amine with a conjugated moiety without the electron-donating group.

[0050] To achieve storage stability, the amine must be strong enough to bind and block the Lewis acid catalyst at 23° C. If the amine is a weak Lewis base, it will release the acid at a lower temperature than if it is a strong Lewis base. Thus, the choice of moiety attached to the nitrogen of the amine may be selected to achieve storage stability and reactivity at the desired temperature.

[0051] It has further been discovered that suitable amines must have an amine nitrogen that is not a member of an N=CN bond, such as amidines, guanidines, and N-methylimidazole. Desirably, the composition does not include amines with N=CN bonds. For example, the composition may be free of amidines and guanidines.

[0052] Generally, the amine has the following formula: 1 R 2 R 3 N, where the nitrogen is not a member of an N=CN bond, 1 , R 2 , and R 3 Each of R is independently selected from the group consisting of hydrogen, alkyl, substituted alkyl, and a conjugated moiety; 1 , R 2 , and R 3 At least one of R is a conjugated moiety connected to the nitrogen by a conjugated carbon. 1 , R 2 , and R 3 may be conjugated moieties connected to the nitrogen by a conjugated carbon. Desirably, the conjugated moieties are aromatic moieties.

[0053] Examples of amines suitable for use in the present invention include any one amine or any combination of two or more amines selected from the group consisting of aniline, 4-methylaniline, 4-fluoroaniline, 2-chloro-4-fluoroaniline, diphenylamine, diphenylmethylamine, triphenylamine, 1-naphthylamine, 2-naphthylamine, 1-aminoanthracene, 2-aminoanthracene, 9-aminoanthracene, β-aminostyrene, 1,3,5-hexatrien-1-amine, N,N-dimethyl-1,3,5-hexatrien-1-amine, 3-amino-2-propenal, and 4-amino-3-buten-2-one.

[0054] The concentration of the amine in the composition is at least molar equivalent to the concentration of the Lewis acid catalyst so that it is able to complex and block all of the Lewis acid catalyst at 23° C. The concentration of the amine may exceed the molar concentration of the Lewis acid catalyst, but is preferably present in a concentration of 110 mole percent (mol %) or less, preferably 105 mol % or less, more preferably 103 mol % or less, and most preferably 101 mol % or less, based on the total moles of Lewis acid catalyst, but may be present in a concentration of 100 mol % or more.

[0055] The amine and Lewis acid form a complex in the composition that sufficiently shields the Lewis acid from catalyzing reactions with other composition components to be storage stable at 23° C. Upon heating, the amine releases the Lewis acid, allowing the Lewis acid to catalyze reactions.

[0056] Optional Ingredients The composition of the present invention may consist of a silyl hydride, an α-β unsaturated ester, a Lewis acid catalyst, and an amine. Alternatively, the composition of the present invention may further comprise one optional ingredient or a combination of two or more optional ingredients. The optional ingredients are desirably present in a concentration of 50% by weight or less, 40% by weight or less, 30% by weight or less, 20% by weight or less, 10% by weight or less, 5% by weight or less, or even 1% by weight or less based on the weight of the composition.

[0057] Examples of possible optional components include one or a combination of two or more components selected from the group consisting of hydrocarbyl solvents (typically at a concentration of 10% by weight or less, 5% by weight or less, or even 1% by weight or less based on the weight of the composition), pigments such as carbon black or titanium dioxide, fillers such as metal oxides including SiO2 (typically at a concentration of 50% by weight or less based on the weight of the composition), moisture scavengers, optical brighteners, stabilizers (such as antioxidants and UV stabilizers), and corrosion inhibitors. The composition of the present invention may also be free of one or a combination of two or more of such additional components.

[0058] In particular, the composition of the invention may contain up to 1% by weight of water, up to 0.5% by weight of water, relative to the weight of the composition. Desirably, the composition is free of water.

[0059] Reaction process The invention includes a chemical reaction process comprising the steps of: (a) providing a composition of the invention; and (b) heating the composition to a temperature sufficient to dissociate the Lewis acid catalyst from the amine.

[0060] Step (a) may include mixing together an amine, a Lewis acid catalyst, a silyl hydride, and an α-β unsaturated ester. However, the Lewis acid catalyst and the amine are combined such that the amine can complex and block the catalytic activity of the Lewis acid before combining with both the silyl hydride and the α-β unsaturated ester. If the Lewis acid does not catalyze the reaction with the other reactant, it is possible to prepare a Lewis acid / amine complex in the presence of one of the reactants (i.e., the silyl hydride or the α-β unsaturated ester). The amine and the Lewis acid may be combined in a solvent such as toluene to form a blocked Lewis acid complex, which may then be combined with the silyl hydride and the α-β unsaturated ester.

[0061] Step (b) generally requires heating the composition to a temperature of 80°C or more, preferably 90°C or more, but may also be accomplished by heating to a temperature that is generally no greater than 300°C, no greater than 250°C, no greater than 200°C, no greater than 150°C, or even no greater than 100°C.

[0062] The composition of the present invention is particularly useful as a coating or encapsulant. The composition can also be in a useful form to form a molded article. In such applications, the process of the present invention can further comprise applying the composition to a substrate after step (a) and before or during step (b). EXAMPLES

[0063] MD H 65 M Silylhydride. Equip a three-neck flask with a mechanical stirrer and add 40 grams (g) of deionized water, 10 g of heptane, and 0.05 g of tosylic acid. Add a mixture of 200 g of methyldichlorosilane and 10 g of trimethylchlorosilane dropwise to this with stirring over 30 minutes. Stir for an additional 60 minutes at 23°C. Wash the reaction solution three times with 50 milliliters (mL) of deionized water each time. Dry the solution with anhydrous sodium sulfate and filter through activated charcoal. Remove the volatiles by rotary evaporation (Rotovap) to obtain MD H 65 M Obtain silyl hydride.

[0064] MD 166 D MA 14M α-β Unsaturated Ester. A four-necked, one-liter flask is equipped with a thermal couple, mechanical stirrer, a Dean-Stark trap fitted with a water-cooled condenser, and a nitrogen bubbler. To the flask, add 558.9 grams (g) of silanol-terminated polydimethylsiloxane (XIAMETER™ PMX-0930 available from Dow Chemical Company), 18.5 g of 3-methacryloxypropylmethyldimethoxysilane, 6.1 g of Dow Corning 200 Fluid (0.65 cSt), and 121 g of heptane. With vigorous stirring, add 0.35 mL of trifluoromethanesulfonic acid. Apply heat to raise the temperature to 73° C. Collect the water, methanol, and heptane in the Dean-Stark trap. The reflux temperature is gradually increased to 90° C. after approximately 1 hour. Add 11.0 g of water to the flask and continue the azeotropic distillation. The reflux temperature rises to 96° C. after about 2 hours. The heat source is removed and 22.8 g of calcium carbonate and 50 g of sodium sulfate are added to the flask. The flask contents are cooled to 23° C. After stirring for 3 hours, the contents are filtered through a 0.45 micrometer filter membrane. The filtrate is rotary evaporated at 80° C. and less than 1 torr pressure for 1 hour to obtain 586.9 g of MD 166 D MA 14 M α-β unsaturated ester is obtained as a colorless, transparent liquid product. MD 166 D MA 14 The M α-β unsaturated ester has the following structure: (CH3)3SiO 1 / 2 ((CH3)2SiO 2 / 2 ) 166 ((CH3)(CH2CH2CH2OC(O)C(CH2)CH3)SiO 2 / 2 ) 14 O 1 / 2 Si(CH3)3

[0065] MD 50 D MA 2.6M α-β Unsaturated Ester. Equip a four-necked, 1-liter flask with a thermocouple, mechanical stirrer, Dean-Stark trap fitted with a water-cooled condenser, and nitrogen bubbler. Add 466.6 g of silanol-terminated polydimethylsiloxane (XIAMETER™ PMX-0930 available from Dow Chemical Company), 75.8 g of methacryloxypropylmethyldimethoxysilane, 21.4 g of Dow Corning 200 Fluid (0.65 cSt), and 124 g of heptane to the flask. With vigorous stirring, add 0.40 mL of trifluoromethanesulfonic acid. Apply heat to raise the temperature to 76° C. Collect the water, methanol, and heptane in the Dean-Stark trap. The reflux temperature gradually increases to 117° C. after approximately 4 hours. The heat source is removed and the contents are cooled to 101° C., after which 15.6 g of calcium carbonate and 32 g of sodium sulfate are added to the flask. The flask contents are cooled to 23° C. After stirring for 2 hours, the contents are filtered through a 0.45 micrometer filter membrane. The filtrate is rotary evaporated at 80° C. and less than 1 torr pressure for 30 minutes to obtain 456.7 g of MD 50 D MA 2.6 The M α-β unsaturated ester is obtained as a clear, colorless liquid product.

[0066] MD 182 D MA3M α-β Unsaturated Ester. Equip a four-necked, 1-liter flask with a thermocouple, mechanical stirrer, Dean-Stark trap fitted with a water-cooled condenser, and nitrogen bubbler. Add 616.6 g of silanol-terminated polydimethylsiloxane (XIAMETER™ PMX-0930 available from Dow Chemical Company), 29.5 g of methacryloxypropylmethyldimethoxysilane, 6.1 g of Dow Corning 200 Fluid (0.65 cSt), and 75 g of heptane to the flask. Add 0.35 mL of trifluoromethanesulfonic acid with vigorous stirring. Apply heat to raise the temperature to 85° C. Collect the water, methanol, and heptane in the Dean-Stark trap. The reflux temperature is gradually increased to 90° C. after approximately 1 hour. Add 8.8 g of water to the flask and continue the azeotropic distillation. The reflux temperature rises to 99°C after approximately 2 hours. The heat source is removed and 20 g of calcium carbonate and 50.8 g of sodium sulfate are added to the flask. The flask contents are cooled to 23°C. After stirring for 3 hours, the contents are filtered through a 0.45 micrometer filter membrane. The filtrate is rotary evaporated at 80°C and less than 1 torr pressure for 1 hour to obtain 583.6 g of MD 182 D MA The 3M α-β unsaturated ester is obtained as a clear, colorless liquid product.

[0067] M Vi D 78 M Vi This material is commercially available from Gelest as DMS-V21.

[0068] Catalyst Solution. Prepare a catalyst solution by combining 5 wt. % BCF in toluene with 5 wt. % of the specified amine (see Table 1) in toluene in an amount sufficient to provide equimolar amounts of BCF and amine (1:1 molar ratio) and approximately 12 grams of final solution. Sonicate the final solution for 30 seconds and allow to stand at 23°C for 12 hours. Add 0.5-1.0 grams of tetrahydrofuran to the final solution to aid in dissolving the BCF-amine complex and form the catalyst solution for use in the example compositions.

[0069] 23°C Shelf Life. The composition is prepared in a vial which is then sealed and stored at 23°C. The flowability of the vial contents is confirmed by inverting the vial and observing the contents to determine if the contents are flowing. Flowability is confirmed at 1 hour intervals, 8 hours, and after 24 hour intervals. The time at which gelling occurs is recorded as evidenced by the vial contents no longer flowing within 1-2 seconds upon inversion. The time at which gelling occurs is the "23°C Shelf Life."

[0070] Cure Speed ​​at 90°C. The cure speed at 90°C is the time it takes to form a tack-free gel or cured film on a surface at 90°C. Coat a 125 micrometer film of the composition on a glassine paper substrate. Place the film in a 90°C oven. Check the film for tack every 30 seconds. The time required to achieve a tack-free film is the cure speed at 90°C.

[0071] Tpeak. Tpeak is the temperature at which there is maximum reaction exotherm in a reaction system. Tpeak is determined by differential scanning calorimetry (DSC) of a sample composition. A 10 milligram sample of the composition is characterized by DSC by loading it into a DSC pan and running the DSC at a rate of 10°C per minute using a temperature ramp of 10°C to 250°C. Tpeak is the temperature at which the maximum exotherm is evident in the DSC curve.

[0072] Comparative Example (Comp Ex) A: Lewis acid without blocking agent 2 grams of MD in a 10 g dental cup 166 D MA 14 M, M D 0.348 g H 65M silyl hydride and a solution of 500 ppm BCF dissolved in a minimum amount of toluene are combined. The molar ratio of SiH functional groups to α-β unsaturated ester groups is 3:1. The 23°C shelf life is 4 hours and the 90°C cure rate is 5 minutes. The results are shown in Table 1. Comparative Example (Comp Ex) A serves as a benchmark for uninhibited cure. Note: The concentration of BCF in this sample and the other samples below is based on the total weight of the sample (composition).

[0073] Comparative Examples B-D: Lewis Acids with Amine Blockers with No Aromatic Carbon Bonded to the Amine Nitrogen Comparative Examples B-D are prepared in a similar manner to Comparative Example A, except using a catalyst solution containing 500 ppm BCF complexed with an equal molar amount of an amine inhibitor (see Table 1). The amine inhibitor lacks a conjugated carbon bonded to an amine nitrogen. The 23°C shelf life and 90°C cure speed are characterized. The results are shown in Table 1.

[0074] Examples 1-3: Lewis Acid with Amine Blockers with Aromatic Carbons Bonded to the Amine Nitrogen Examples 1-3 are prepared in a manner similar to Comparative Example A, except using a catalyst solution containing 500 ppm BCF complexed with an α-β unsaturated ester and an equal molar amount of an amine inhibitor as specified in Table 1 (see Table 1). The amine inhibitor contains a conjugated carbon to which an amine nitrogen is attached. The 23°C shelf life and 90°C cure speed are characterized. The results are shown in Table 1.

[0075] Comparative Example E: Lewis Acid with an Amine Blocker Having an Aromatic Carbon Bonded to the Amine Nitrogen, Vinyl Reactant Other than an α-β Unsaturated Ester MD 166 D MA 14 M instead of M Vi D 78 M ViPrepare Comparative Example E in a manner similar to Example 1, except use. Comparative Example E does not contain an alpha-beta unsaturated ester reactant, but does contain a terminal, final functionalized siloxane to see if it will react like an alpha-beta unsaturated ester. The amine inhibitor contains a conjugated carbon bonded to an amine nitrogen. Characterize the 23°C shelf life and 90°C cure speed. Results are shown in Table 1.

[0076] Comparative Example F: Lewis Acid with Amine Blocker with Aromatic Carbon Bonded to the Amine Nitrogen, Alpha-Beta Unsaturated Ester with No Silyl Hydride MD H 65 Comparative Example F is prepared in a similar manner to Comparative Example A, except that no M silyl hydride is used. This comparative example explores the need to include silyl hydride. The 23°C shelf life and 90°C cure speed are characterized. The results are shown in Table 1. [Table 1]

[0077] Comparative Example A demonstrates that in the presence of an unblocked Lewis acid, a composition of a silyl hydride and an α-β unsaturated ester has a 23° C. shelf life that is insufficient to meet storage stability (a 23° C. shelf life of at least 8 hours is required to meet "storage stability").

[0078] Comparative Examples B-D demonstrate that blocking Lewis acids with amines lacking a conjugated carbon bonded to the amine nitrogen and / or having an N=CN bond results in too strong a blocking to have the desired 90° C. cure speed of less than 10 minutes.

[0079] Examples 1-3 demonstrate that blocking the Lewis acid with an amine having a conjugated carbon attached to the amine nitrogen provides compositions that are storage stable and have 90° C. cure speeds well below the 10 minute or less requirement.

[0080] Comparative Example E demonstrates that the α-β unsaturated ester is an essential component of this composition, and that having only terminal vinyl functionality in place of the α-β unsaturated ester would result in a composition that is too stable to achieve the desired 90° C. cure speed of 10 minutes or less.

[0081] Comparative Example F demonstrates that the silyl hydride is also an essential component of the composition, and that just having an α-β unsaturated ester, even without an inhibitor on the Lewis acid, is too stable to achieve the desired 90° C. cure speed of 10 minutes or less.

Claims

1. A silyl hydride, an α-β unsaturated ester, a Lewis acid catalyst, and a compound of the following formula: １ R ２ R ３ N [wherein the nitrogen is not a member of an N=C-N bond and R １ , R ２ , and R ３ each of which is independently selected from the group consisting of hydrogen, alkyl, substituted alkyl, and conjugated moieties; or 1. A composition comprising a mixture of a compound having both a silyl hydride functional group and an α-β unsaturated ester functional group, a Lewis acid catalyst, and an amine having the following formula: R 1 R 2 R 3 N, wherein nitrogen is not a member of an N═C—N bond, and each of R 1 , R 2 , and R 3 is independently selected from the group consisting of hydrogen, alkyl, substituted alkyl, and conjugated moieties; R １ , R ２ , and R ３ is a conjugated moiety connected to said nitrogen by a conjugated carbon; A composition wherein the amine is complexed with the Lewis acid catalyst, blocking the catalytic activity of the Lewis acid.

2. The composition of claim 1 , wherein the conjugated moiety is an aromatic moiety.

3. R １ , R ２ , and R ３ The composition of claim 1 or 2, wherein at least two of are conjugated moieties attached to N by a conjugated carbon.

4. 4. The composition of claim 1, wherein the Lewis acid catalyst is selected from the group consisting of aluminum alkyls, aluminum aryls, aryl boranes, fluorinated aryl boranes, boron halides, aluminum halides, gallium alkyls, gallium aryls, gallium halides, silium cations, and phosphonium cations.

5. The composition of claim 4 , wherein the Lewis acid catalyst is a fluorinated aryl borane.

6. The composition of any one of claims 1 to 5, wherein the composition does not include a UV photosensitive blocker for the Lewis acid catalyst.

7. (a) providing a composition according to any one of claims 1 to 6; (b) heating said composition to a temperature sufficient to dissociate said Lewis acid catalyst from said amine.

8. 8. The process of claim 7, wherein step (a) comprises mixing all of the ingredients by combining the Lewis acid catalyst and the amine followed by combining with the remaining ingredients, or by combining the Lewis acid catalyst, the amine, and one of the silyl hydride and the α-β unsaturated ester followed by combining with the other of the silyl hydride and the α-β unsaturated ester.

9. 9. The process of claim 7 or claim 8, wherein the process further comprises the step of applying the composition to a substrate or placing the composition in a mold after step (a) and before step (b), or during step (b).