1. A preparation comprising: (A) 30 to 90 wt. % of at least one organic solvent; (B) 10 to 70 wt. % of at least one noble metal complex comprising a diolefin ligand and a C6 to C18 monocarboxylate ligand, [LPd[O(CO)R1]X] n Type, [LRh[O(CO)R1]] m type and [LIr[O(CO)R1]] m wherein L represents a compound acting as a diolefin ligand, X is selected from bromide, chloride, iodide and -O(CO)R2, -O(CO)R1 and -O(CO)R2 are the same or different non-aromatic C6 to C18 monocarboxylic acid residues, n is an integer of 1 or more, and m is an integer of 2 or more; and (C) 0 to 10% by weight of at least one additive.

Description

[Technical field]

[0001] The present invention relates to the preparation of precious metal complexes and the use of the preparation for producing precious metal-containing layers on substrates.

[0002] WO 90 / 07561 A1 discloses platinum complexes having the formula LM[O(CO)R]2, in which L represents a nitrogen-free cyclic polyolefin ligand, preferably cyclooctadiene (COD) or pentamethylcyclopentadiene, M represents platinum or iridium, and R represents benzyl, aryl or alkyl having 4 or more carbon atoms, particularly preferably phenyl.

[0003] The object of the present invention was to find a formulation which can be used for the production of precious metal-containing layers, in particular on temperature-sensitive substrates.

[0004] This object can be achieved by providing a preparation of a noble metal complex of palladium, rhodium or iridium, each of which comprises a diolefin ligand and a C6-C18 monocarboxylate ligand. More precisely, what is provided is (A) 30 to 90 weight percent (wt%) of at least one organic solvent; (B) 10 to 70% by weight of at least one precious metal complex comprising a diolefin ligand and a C6 to C18 monocarboxylate ligand, [LPd[O(CO)R1]X] n Type, [LRh[O(CO)R1]] m Type and [LIr[O(CO)R1]] m and a noble metal complex of the type: wherein L represents a compound acting as a diolefin ligand, X is selected from among bromide, chloride, iodide and -O(CO)R2, -O(CO)R1 and -O(CO)R2 preferably represent identical or different non-aromatic C6-C18 monocarboxylic acid residues, except in each case the phenylacetic acid residue, n is an integer greater than or equal to 1, and m is an integer greater than or equal to 2, (C) 0 to 10% by weight of at least one additive, and a preparation comprising or consisting of them.

[0005] The expression "compound acting as a diolefinic ligand" as used herein refers to a compound that, in a precious metal complex, provides two of its olefinic double bonds or two of its olefinic double bonds to a precious metal central atom to form a complex or provides two precious metal central atoms in a bridging manner to form a complex.

[0006] In the case of polynuclear precious metal complexes, the numbers n and m generally represent integers, for example in the range of 2 to 5. In other words, the integer n>1 generally lies in the range of 2 to 5, and therefore n is in particular equal to 2, in which case the precious metal complex is a dinuclear palladium complex. The integer m also generally lies in the range of 2 to 5, and therefore m is in particular equal to 2, in which case the precious metal complex is a dinuclear rhodium complex or a dinuclear iridium complex.

[0007] In the preparation according to the invention, component (B) is present in dissolved form in component (A). In the presence of optional component (C) in the preparation according to the invention, this component (C) is also preferably present in dissolved form in component (A). In other words, in the absence of optional component (C), the preparation according to the invention is an organic solution, more precisely a true, i.e. non-colloidal organic solution, and the same applies in the presence of optional component (C) in preferred form, i.e. dissolved form in component (A).

[0008] The preparation according to the invention contains 30-90% by weight of at least one organic solvent (A). The organic solvent(s) can be selected from several common organic solvents, since the noble metal complexes dissolve in such organic solvents in high to unlimited concentrations. Advantageously, the organic solvent(s) are essentially volatile under the processing conditions of the preparation according to the invention, which applies in particular to the stage after the preparation according to the invention is applied to the substrate. The boiling point of the organic solvent(s) is generally in the range of 50-200°C or higher, for example 50-300°C. Examples of organic solvents (A) include aliphatic and cycloaliphatic, each having 6-12 carbon atoms; halogenated hydrocarbons such as di-, tri- and tetrachloromethane; aromatics; araliphatics such as toluene or xylol; alcohols such as ethanol, n-propanol and isopropanol; ethers; mono- and di-C1-C4 alkylene glycol ethers, for example ethylene glycol mono-C1-C4 alkylene ether, ethylene glycol di ... glycol ethers such as diethylene glycol mono C1-C4 alkylene ether, diethylene glycol di C1-C4 alkylene ether, propylene glycol mono C1-C4 alkylene ether, propylene glycol di C1-C4 alkylene ether, dipropylene glycol mono C1-C4 alkylene ether and dipropylene glycol di C1-C4 alkylene ether; esters having 2 to 12 carbon atoms; and ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone and cyclohexanone.In this respect, preference is given to araliphatic solvents such as toluene or xylol, alcohols such as ethanol, n-propanol and isopropanol, and also to mono- and di-C1-C4 alkylene glycol ethers, such as, for example, glycol ethers such as ethylene glycol mono-C1-C4 alkylene ether, ethylene glycol di-C1-C4 alkylene ether, diethylene glycol mono-C1-C4 alkylene ether, diethylene glycol di-C1-C4 alkylene ether, propylene glycol mono-C1-C4 alkylene ether, propylene glycol di-C1-C4 alkylene ether, dipropylene glycol mono-C1-C4 alkylene ether and dipropylene glycol di-C1-C4 alkylene ether. Component (A) or at least one organic solvent (A), respectively, particularly preferably consists of at least one alcohol, in particular at least one of the alcohols mentioned by way of example, and / or at least one glycol ether, in particular at least one of the glycol ethers mentioned by way of example. A corresponding mixture of 30 to 70 parts by weight of an alcohol and the missing part by weight of a glycol ether is particularly preferred as component (A).

[0009] As already mentioned, the preparation according to the invention comprises, as component B, 10 to 70% by weight of at least one noble metal complex comprising a diolefin ligand and a C6 to C18 monocarboxylate ligand, [LPd[O(CO)R1]X] n Type, [LRh[O(CO)R1]] m Type and [LIr[O(CO)R1]] m wherein L represents a compound acting as a diolefin ligand; X is selected from bromide, chloride, iodide and -O(CO)R2; -O(CO)R1 and -O(CO)R2 preferably represent identical or different non-aromatic C6-C18 monocarboxylic acid residues, except in each case for phenylacetic acid residues; n is an integer of 1 or more; and m is an integer of 2 or more.

[0010] The precious metal content of the preparation according to the invention, which results from at least one mobile metal complex, may for example be in the range from 2.5 to 25% by weight.

[0011] In the embodiment of mononuclear palladium complexes of the type [LPd[O(CO)R1]X], L is a compound acting as a diolefinic ligand at the palladium central atom, X represents bromide, chloride, iodide or -O(CO)R2, -O(CO)R1 and -O(CO)R2 preferably represent identical or different non-aromatic C6-C18 monocarboxylic acid residues in each case, except for the phenylacetic acid residue, and n here is equal to 1.

[0012] [LPd[O(CO)R1]X] n In the case of a preferred embodiment of the dinuclear or polynuclear palladium complexes of the type, L represents a compound acting as a diolefin ligand, X represents bromide, chloride, iodide or -O(CO)R2, n represents 2, 3, 4 or 5, preferably 2, -O(CO)R1 and -O(CO)R2 preferably represents the same or different non-aromatic C6 to C18 monocarboxylic acid residues, except in each case of a phenylacetic acid residue.

[0013] [LRh[O(CO)R1]] m Type or [LIr[O(CO)R1]] m In the case of a preferred embodiment of a dinuclear or polynuclear precious metal complex of the type, L represents a compound acting as a diolefin ligand, m represents 2, 3, 4 or 5, preferably 2, and -O(CO)R1 represents a non-aromatic C6-C18 monocarboxylic acid residue, preferably with the exception of a phenylacetic acid residue.

[0014] However, the noble metal complexes may also be present in the preparation according to the invention in an individualized but related form, thus alone or as a mixture of several different species. Thus, the palladium complexes may be present in the preparation according to the invention in an individualized or related form, thus [LPd[O(CO)R1]X] nIn each case of the type, it can be present alone or as a mixture of several different species. The rhodium complexes can also be present in the preparations according to the invention in individualized or associated form, thus [LRh[O(CO)R1]] m In each case of the form, it can be present alone or as a mixture of several different species. In the same way, the iridium complexes can also be present in the preparations according to the invention in individualized or associated form, thus [LIr[O(CO)R1]] m Each of the types may be present alone or as a mixture of several different species. In other words, component (B) is [LPd[O(CO)R1]X] n Type and / or [LRh[O(CO)R1]] m Type and / or [LIr[O(CO)R1]] m Thus, component (B) may contain compounds of only one, two or all three of the types disclosed herein, each type being represented in only one individual form (individualized) or in multiple individual forms (related). The term "individual form" as used in this context herein refers to a formula type having a specific index n or m, respectively, e.g., [LRh[O(CO)R1]]2 is the general type [LRh[O(CO)R1]] with m=2. m are individual forms of.

[0015] The composition according to the invention also comprises [LPt[O(CO)R1]X] n In such platinum complexes, n is a group of the formula [LPd[O(CO)R1]X] n Such platinum compounds are disclosed in the PCT application having application number PCT / EP2020 / 068465.

[0016] Examples of diolefins or compounds of type L, respectively, which can function as diolefin ligands include hydrocarbons such as COD (1,5-cyclooctadiene), NBD (norbornadiene), COT (cyclooctatetraene) and 1,5-hexadiene, in particular COD and NBD. They are preferably purely hydrocarbons, however the presence of heteroatoms, for example in the form of functional groups, is also possible.

[0017] X may represent bromide, chloride, iodide or -O(CO)R2, preferably represents chloride or -O(CO)R2, especially -O(CO)R2.

[0018] Each non-aromatic monocarboxylic acid residue -O(CO)R1 and -O(CO)R2 represents an identical or different non-aromatic C6-C18 monocarboxylic acid residue, in each case preferably with the exception of a phenylacetic acid residue. The term "non-aromatic" as used in this context excludes purely aromatic monocarboxylic acid residues, but not araliphatic monocarboxylic acid residues in which the carboxyl functional group(s) are attached to an aliphatic carbon. -O(CO)R1 and -O(CO)R2 preferably do not represent a phenylacetic acid residue. -O(CO)R1 and -O(CO)R2 preferably represent an identical non-aromatic C6-C18 monocarboxylic acid residue, but in that respect preferably do not represent a phenylacetic acid residue. Monocarboxylic acid residues having 8 to 18 carbon atoms, i.e. non-aromatic C8-C18 monocarboxylic acid residues, are preferred among the non-aromatic C6-C18 monocarboxylic acid residues.

[0019] Examples of non-aromatic C6-C18 monocarboxylic acids having the residue -O(CO)R1 or -O(CO)R2 or preferred C8-C18 monocarboxylic acids include isomeric hexanoic acids including n-hexanoic acid, isomeric heptanoic acids including n-heptanoic acid, isomeric octanoic acids including n-octanoic acid and 2-ethylhexanoic acid, isomeric nonanoic acids including n-nonanoic acid, and isomeric decanoic acids including n-decanoic acid, to name a few. Not only linear representatives but also those with branched and / or cyclic structures, such as, for example, 2-ethylhexanoic acid, cyclohexanecarboxylic acid, and neodecanoic acid, are included. Residues R1 and R2, which are in each case bound to the carboxyl group, contain, respectively, 5 to 17 or 7 to 17 carbon atoms, in which respect benzyl residues are preferably excluded in each case.

[0020] A preferred example of the palladium complex is [(COD)Pd[O(CO)R1]2] n and [(NBD)Pd[O(CO)R1]2] n where n is equal to 1 or 2, in particular equal to 1, and R1 in each case preferably represents a non-aromatic C5 to C17 hydrocarbon residue, with the exception of benzyl.

[0021] A preferred example of a rhodium complex is [(COD)Rh[O(CO)R1]] m and [(NBD)Rh[O(CO)R1]] m where m is equal to 2 and R1 in each case preferably represents a non-aromatic C5 to C17 hydrocarbon residue, with the exception of benzyl.

[0022] A preferred example of an iridium complex is [(COD)Ir[O(CO)R1]] m and [(NBD)Ir[O(CO)R1]] m where m is equal to 2 and R1 in each case preferably represents a non-aromatic C5 to C17 hydrocarbon residue, with the exception of benzyl.

[0023] Noble metal complexes can be produced in a simple manner by ligand exchange, in particular without using carboxylates of silver. The production process involves the mixing or suspension, or emulsification, respectively, of a two-phase system. Therefor, one phase contains starting materials of LPdX2 type or [LRhX]2 type or [LIrX]2 type, respectively, where X is in each case selected from bromides, chlorides and iodides, preferably chlorides, either as such starting materials themselves or, preferably, in the form of an organic solution of such starting materials that is at least essentially water-immiscible. In addition to aromatic and chlorinated hydrocarbons such as toluene, xylene, dichloromethane, trichloromethane and tetrachloromethane, examples of organic solvents that are suitable for producing this type of organic solution and are at least essentially water-immiscible also include oxygen-containing solvents, such as the corresponding water-immiscible ketones, esters and ethers. The other phase, by contrast, comprises an aqueous solution of alkali salts (in particular sodium or potassium salts) and / or magnesium salts of C6-C18 monocarboxylic acids, for example of type R1COOH and optionally additionally of type R2COOH. The choice of the type of monocarboxylic acid salt(s) depends on the type of precious metal complex to be produced or on the association of precious metal complexes to be produced. The two phases are vigorously mixed, for example by shaking and / or stirring, to form a suspension or emulsion. For the purpose of maintaining the suspension or emulsion state, the mixing is carried out for a period of, for example, 0.5 to 24 hours, for example at a temperature in the range of 20 to 50° C. A ligand exchange is thereby carried out, the precious metal complex(es) formed dissolving in the organic phase and the alkali X salt or MgX2 salt likewise formed dissolving in the aqueous phase. After completion of the suspension or emulsion, the organic and aqueous phases are separated from each other. The precious metal complex(es) formed can be obtained from the organic phase and, optionally, can be subsequently purified by conventional methods.

[0024] For example, to take one specific example, (COD)Pd[O(CO)CH(C2H5)C4H9]2 can be prepared by standard emulsification, for example, by combining a dichloromethane solution of (COD)PdCl2 with an aqueous solution of sodium 2-ethylhexanoate. After the emulsification is completed, the sodium chloride-containing solution formed by the ligand exchange can then be separated from the dichloromethane phase, from which (COD)Pd[O(CO)CH(C2H5)C4H9]2 can be isolated and, optionally, purified by standard purification processes. For example, in the case of a corresponding selected stoichiometry, the palladium complex (COD)Pd[O(CO)CH(C2H5)C4H9]Cl can also be prepared in a similar manner.

[0025] In addition to the abovementioned solubility in common organic solvents, a key property is the relatively low decomposition temperature of the precious metal complex(es) of component (B), which starts for example already at 150° C.-250° C. and is often below 200° C. This combination of properties makes it possible to use such precious metal complexes as component (B) of the preparation according to the invention for the production of precious metal-containing layers on substrates, in which case the preparation according to the invention represents a coating agent, i.e. it can then be prepared and used as a covering agent.

[0026] The preparation according to the invention contains 0 to 10% by weight, preferably 0 to 3% by weight, of at least one additive (C). The preparation according to the invention may therefore be additive-free or contain up to 10% by weight of at least one additive. Examples of additives include wetting additives, rheological additives, antifoaming agents, degassing agents, additives influencing surface tension, and odorants.

[0027] The preparations according to the invention can be prepared by simple mixing of components (A), (B) and, if necessary, (C), whereby the expert selects the proportions of the components adapted to the respective intended purpose and / or application method thereby used.

[0028] The preparation according to the invention can be used for the production of precious metal-containing layers on substrates, in particular on temperature-sensitive substrates. Thereby, the preparation according to the invention can be used first for the production of a covering layer (coating) and then subjected to pyrolysis. [LPd[O(CO)R1]X] n When working with preparations according to the invention based on palladium complexes of the type [LRh[O(CO)R1]]n, essentially metallic palladium in the form of a layer is formed in response to thermal decomposition even in the presence of air as the surrounding atmosphere, whereas when working with preparations according to the invention based on rhodium complexes of the type [LRh[O(CO)R1]]n or [LIr[O(CO)R1]] n When the preparation according to the invention based on iridium complexes of the type 1, ...

[0029] The preparation according to the invention may optionally further comprise [LPt[O(CO)R]X] n combinations of two or several of the noble metal complex types disclosed herein as component (B) in combination with one or several of the above-mentioned platinum complexes of the type [LPt[O(CO)R1]X] nIn the case of the combination of one or several of the above-mentioned platinum complexes of the type, layers containing multiple precious metals can also be produced on the substrate at the same time to some extent.Thereby, the proportion of metallic palladium, rhodium oxide, iridium oxide and optionally trapped metallic platinum in the corresponding layer can be variably set in a very simple manner via the respective proportions of the precious metal complexes in the preparation according to the invention used to produce the corresponding layer.In particular, the following types of layers containing multiple precious metals can be produced on the substrate: - layers comprising metallic palladium and metallic platinum, for example in the form of a platinum / palladium alloy, a layer comprising metallic palladium and rhodium oxide, a layer comprising metallic palladium and iridium oxide, a layer comprising metallic palladium, rhodium oxide and iridium oxide, a layer comprising metallic platinum and rhodium oxide, a layer comprising metallic platinum and iridium oxide, a layer comprising metallic platinum, rhodium oxide and iridium oxide, a layer comprising metallic palladium, metallic platinum and rhodium oxide, a layer comprising metallic palladium, metallic platinum and iridium oxide, - a layer containing metallic palladium, metallic platinum, rhodium oxide and iridium oxide, a layer comprising rhodium oxide and iridium oxide which is free of metallic palladium and free of metallic platinum;

[0030] In response to the heat treatment, the coating layer decomposes as described above under the formation of a precious metal-containing layer, i.e., the coating layer is ultimately transformed into a precious metal-containing layer. Thus, the present invention also provides a method for producing a precious metal-containing layer on a substrate, the method comprising: (1) applying a coating layer of the preparation according to the invention to a substrate; (2) pyrolyzing the coating layer by forming a precious metal-containing layer.

[0031] The substrate provided with the coating layer in step (1) can be a substrate comprising a wide variety of materials. Thereby, the substrate can comprise only one or several materials. Examples of materials include, inter alia, glass; carbide substrates, such as titanium carbide, molybdenum carbide, tungsten carbide, silicon carbide; nitride substrates, such as aluminum nitride, titanium nitride, silicon nitride; boride substrates, such as titanium boride, zirconium boride; ceramic substrates, including those based on oxide ceramics and those common as catalyst supports in heterogeneous catalysis; semiconductor substrates, such as silicon substrates; metals; plastics; modified or unmodified polymers of natural origin; carbon substrates; wood; cardboard and paper. The substrate can be provided with a coating layer on the inner and / or outer surface and / or on a portion of the inner and / or outer surface.

[0032] For the preparation of the coating layer according to step (1), application methods known per se can also be used.

[0033] The first application method is immersion, whereby the substrate to be provided with a coating layer or, respectively, with a precious metal-containing layer is immersed in the preparation according to the invention and removed therefrom. The proportion of component (A) during immersion is preferably in the range of 30-90% by weight of the preparation according to the invention and the proportion of component (B) is in the range of 10-70% by weight.

[0034] The second application method is spray application, whereby the substrate to be provided with a coating layer or the substrate to be finally provided with a precious metal-containing layer, respectively, is spray-coated with the preparation according to the invention using common spray-coating equipment. Examples of spray-coating equipment include pneumatic spray guns, airless spray guns, rotary sprayers, etc. The proportion of component (A) during spray application is preferably in the range of 50-90% by weight of the preparation according to the invention, and the proportion of component (B) is in the range of 10-50% by weight.

[0035] A third application method is printing, whereby the substrate to be provided with a coating layer or, finally, with a precious metal-containing layer, respectively, is imprinted with the preparation according to the invention. In that respect, a preferred printing method is inkjet printing, the preparation according to the invention here representing the coating agent in the form of an ink. A further preferred printing method is screen printing. The proportion of component (A) during printing is preferably in the range of 50-90% by weight of the preparation according to the invention, and the proportion of component (B) is in the range of 10-50% by weight.

[0036] A fourth application method is application by means of an applicator, such as a paint brush, brush, felt or cloth, which is immersed in the preparation according to the invention. The applicator thereby transfers the preparation according to the invention to the substrate provided with a coating layer or finally to the substrate provided with a precious metal-containing layer, respectively. In the case of this type of application technique, the proportion of component (A) is preferably in the range of 30-90% by weight of the preparation according to the invention and the proportion of component (B) is in the range of 10-70% by weight.

[0037] The coating layer applied from the preparation according to the invention and comprising at least one component (B) can first be dried, thereby partially or completely removing the organic solvent (A), and then it or the dry residue is subjected to pyrolysis by forming, respectively, a precious metal-containing layer.

[0038] The heat treatment carried out for the purpose of pyrolysis involves heating to an object temperature above the decomposition temperature of at least one noble metal complex (B). In the presence of several different noble metal complexes (B), the expert selects an object temperature above the decomposition temperature of the noble metal complex of the (B) type with the highest decomposition temperature. For example, heating to an object temperature above the decomposition temperature is generally carried out for this purpose for a short time, for example to an object temperature in the range of more than 150°C to 200°C or more than 150 to 250°C or more, for example up to 1000°C, for a time period of 1 minute to 30 minutes. Heating can be carried out in particular in a furnace and / or by infrared radiation. Generally, object temperatures slightly above the respective decomposition temperatures are selected. Generally, heating, more precisely, the maintenance of the object temperature does not have to exceed 15 minutes.

[0039] In particular, [LPd[O(CO)R1]X] n When working with embodiments of the preparations according to the invention based on palladium complexes of this type, it is advantageously not necessary to use preparations containing colloidal or nanopalladium, thereby making it possible to avoid the risks associated therewith.

[0040] In the second and third cases of the abovementioned application methods, clogging of the applicator, more precisely of the fine openings or nozzles of the spray applicator or inkjet nozzles, respectively, can be avoided by the use of the preparations according to the invention, and finally, the problem of colloidal palladium or nanopalladium starting to dry out or agglomerating, for example, does not arise here.

[0041] The palladium layer obtainable according to the invention is characterized by a high metallic luster, comparable to that of a mirror, provided that the work is carried out with a substrate having a smooth, not too rough, surface, and thus the palladium layer is homogeneous in terms of its smooth, non-grainy outer surface.

[0042] The thickness of the precious metal-containing layer obtainable according to the present invention may be, for example, in the range of 50 nm to 5 μm, and the precious metal-containing layer may be of a flat nature with or without desired interruptions in the surface area, or may have a desired pattern or design. As can be seen from the above examples of substrates, the precious metal-containing layer may be produced even on temperature-sensitive substrates, i.e. on substrates that are not temperature-stable, for example above 200° C., for example, these may be based on temperature-sensitive polymer substrates, such as polyolefins or polyesters. EXAMPLES

[0043] Example 1 (Applying a Palladium Layer to a Polyimide Film): A solution of 35 mmol of (COD)PdCl2 in 200 mL of dichloromethane was stirred and a solution of 140 mmol of sodium 2-ethylhexanoate in 150 mL of water was added. The two-phase mixture was emulsified for 24 hours at 20° C. by vigorous stirring. The dichloromethane phase thereby turned yellow.

[0044] The dichloromethane phase was separated and the solvent was distilled off. The viscous yellow residue was taken up in petroleum benzine (40-60), the solution was dried and filtered over magnesium sulfate. The petroleum benzine was then completely distilled off. A viscous yellow residue (COD)Pd[O(CO)CH(C2H5)C4H9]2 remained.

[0045] 5 g of the yellow residue was dissolved in 5.60 g of a solvent mixture (50 wt % ethanol and 50 wt % propylene glycol monopropyl ether). The solution was sprayed onto a Kapton® film (polyimide) by airbrush spray gun. The coated film was heated in a laboratory oven to an object temperature of 200° C. and held at this temperature for 5 minutes. A shiny conductive layer of palladium was formed on the film.

[0046] Example 2 (Applying a Patterned Palladium Layer to a Polyimide Film): A Kapton® film was imprinted with the solution from Example 1 using an inkjet printer at a resolution of 1270 dpi in a serpentine design. The film imprinted in this way was heated in a laboratory oven to an object temperature of 200° C. and held at this temperature for 5 minutes. A shiny conductive layer of palladium in the form of a serpentine design with a conductor path width of 2.5 mm was formed on the film.

[0047] Example 3 (Applying a Palladium Layer to a Polyimide Film): Example 1 was repeated in a completely similar manner, with the only difference being that (NBD)PdCl2 was used instead of (COD)PdCl2, whereby a yellow residue of (NBD)Pd[O(CO)CH(C2H5)C4H9]2 and finally a polyimide film with a palladium layer corresponding to the coated film obtained in Example 1 was obtained as a result of the synthesis.

[0048] Example 4 (Applying a Patterned Palladium Layer to a Polyimide Film): Example 2 was repeated in a completely similar manner, with the only difference being that (NBD)PdCl2 was used instead of (COD)PdCl2, whereby a yellow residue of (NBD)Pd[O(CO)CH(C2H5)C4H9]2 and finally a polyimide film with a patterned palladium layer corresponding to the film obtained in Example 2 with a patterned palladium layer was obtained as a result of the synthesis.

[0049] Example 5 (Applying a Rhodium Oxide Layer to a Polyimide Film): A solution of 16.3 mmol of [(COD)RhCl] in 200 mL of dichloromethane was stirred and a solution of 65.3 mmol of sodium 2-ethylhexanoate in 100 mL of water was added. The two-phase mixture was emulsified for 24 hours at 20° C. by vigorous stirring. The dichloromethane phase thereby turned yellow.

[0050] The dichloromethane phase was separated and the solvent was distilled off. The viscous yellow residue was taken up in petroleum benzine (40-60), the solution was dried and filtered over magnesium sulfate. The petroleum benzine was then completely distilled off. What remained was [(COD)Rh[O(CO)CH(C2H5)C4H9]] m The residue was a viscous yellow residue of

[0051] Five grams of the yellow residue was dissolved in 5 grams of petroleum benzine. The solution was sprayed onto a Kapton® film by an airbrush spray gun. The coated film was heated in a laboratory oven to an object temperature of 250° C. and held at this temperature for 3 minutes. A matte layer, essentially rhodium oxide, was formed on the film.

[0052] Example 6 (Applying a Patterned Rhodium Oxide Layer to a Polyimide Film): A Kapton® film was imprinted with the solution from Example 5 using an inkjet printer at a resolution of 1270 dpi in a serpentine design. The film imprinted in this way was heated in a laboratory oven to an object temperature of 250° C. and held at this temperature for 5 minutes. A matte layer, essentially of rhodium oxide, in the form of a serpentine design with a conductor path width of 2.5 mm was formed on the film.

[0053] Example 7 (Applying a Rhodium Oxide Layer to a Polyimide Film): Example 5 was repeated in full analogy, with the only difference being that (NBD)RhCl2 was used instead of (COD)RhCl2, thereby obtaining (NBD)Rh[O(CO)CH(C2H5)C4H9] m As a result of the synthesis, a polyimide film with a yellow residue of 100% and finally a non-glossy layer of essentially rhodium oxide corresponding to the coated film obtained in Example 5 was obtained.

[0054] Example 8 (Applying a Patterned Rhodium Oxide Layer to a Polyimide Film): Example 6 was repeated in full analogy, with the only difference being that (NBD)RhCl2 was used instead of (COD)RhCl2, thereby obtaining (NBD)Rh[O(CO)CH(C2H5)C4H9] m The synthesis resulted in a yellow residue of about 1000 nm and finally a polyimide film with a patterned layer of essentially rhodium oxide corresponding to the film obtained in Example 6 with a patterned layer of essentially rhodium oxide.

[0055] Example 9 (Applying an Iridium Oxide Layer to a Polyimide Film): A solution of 16.3 mmol of [(COD)IrCl] in 200 mL of dichloromethane was stirred and a solution of 65.3 mmol of sodium neodecanoate in 100 mL of water was added. The two-phase mixture was emulsified for 24 hours at 20° C. by vigorous stirring. The dichloromethane phase thereby turned yellow.

[0056] The dichloromethane phase was separated and the solvent was evaporated. The viscous yellow residue was taken up in petroleum benzine (40-60), the solution was dried and filtered over magnesium sulfate. The petroleum benzine was then completely evaporated. [(COD)Ir[O(CO)(CH2)5C(CH3)3]] m The residue was a viscous yellow residue of

[0057] Five grams of the yellow residue was dissolved in 5 grams of petroleum benzine. The solution was sprayed onto a Kapton® film by an airbrush spray gun. The coated film was heated in a laboratory oven to an object temperature of 250° C. and held at this temperature for 3 minutes. A matte layer, essentially of iridium oxide, was formed on the film.

[0058] Example 10 (Applying a Patterned Iridium Oxide Layer to a Polyimide Film): A Kapton® film was imprinted with the solution from Example 9 using an inkjet printer at a resolution of 1270 dpi in a serpentine design. The film imprinted in this way was heated in a laboratory oven to an object temperature of 250° C. and held at this temperature for 5 minutes. A matte layer, essentially of iridium oxide, in the form of a serpentine design with a conductor path width of 2.5 mm was formed on the film.

Claims

1. (A) 30 to 90% by weight of at least one organic solvent; (B) 10 to 70% by weight of [(NBD)Pd[O(CO)R1] ２ ] ｎ type, [(NBD)Rh[O(CO)R1]] ｍ Type and [(NBD)Ir[O(CO)R1]] ｍ NBD is norbornadiene, n is equal to 1 or 2, m is equal to 2, and R1 represents a non-aromatic C5 to C17 hydrocarbon residue; (C) 0 to 10% by weight of at least one additive, A formulation, wherein the decomposition temperature of said at least one precious metal complex is in the range of 150-250°C.

2. 2. The preparation of claim 1 in the form of a non-colloidal organic solution.

3. 3. The formulation according to claim 1 or 2, comprising a precious metal content from said at least one mobile metal complex in the range of 2.5 to 25% by weight.

4. 4. The formulation according to claim 1, wherein the at least one additive (C) is selected from the group consisting of wetting additives, rheological additives, antifoaming agents, degassing agents, additives influencing surface tension and odorants.

5. 1. A method for producing a precious metal-containing layer on a substrate, comprising: (1) applying a coating layer of the formulation according to any one of claims 1 to 4 to a substrate; (2) pyrolyzing the coating layer to form the precious metal-containing layer.

6. 6. The method of claim 5, wherein the substrate comprises one or more materials selected from the group consisting of glass, carbide substrates, nitride substrates, boride substrates, ceramic substrates, semiconductor substrates, metals, plastics, modified or unmodified polymers of natural origin, carbon substrates, wood, cardboard, and paper.

7. 7. The method of claim 5 or 6, wherein the substrate is provided with a coating layer on the inner and / or outer surface and / or on a portion of the inner and / or outer surface.

8. 8. The method according to any one of claims 5 to 7, wherein the application method used for preparing the coating layer is selected from the group consisting of dipping, spray application, printing, application with a paint brush, application with a brush, application with a felt and application with a cloth.

9. 9. The method according to any one of claims 5 to 8, wherein the coating layer applied in step (1) is first dried, whereby the organic solvent (A) is partially or completely removed, before being subjected to the pyrolysis in step (2).

10. 10. The method according to any one of claims 5 to 9, wherein the thermal decomposition according to step (2) is carried out by a heat treatment comprising heating to a body temperature above the decomposition temperature of the at least one precious metal complex.

11. The method according to any one of claims 5 to 10, wherein the noble metal-containing layer has a thickness of from 50 nm to 5 μm.