Skin patch and method for producing the skin patch

Abstract

The present invention relates to a skin patch and a method for manufacturing the skin patch, comprising: a base sheet; and a film disposed on the base and having a preset thickness deviation range.

Description

[Technical field]

[0001] The present invention relates to a patch that adheres to the skin and a method for using the patch. [Background technology]

[0002] Skin patches are generally used for cosmetic purposes such as blocking UV rays and moisturizing the skin. They are made by impregnating ordinary nonwoven fabric with various essences or other preparations and attaching them to the skin, or by attaching them to the skin in a hydrogel state.

[0003] In addition, gel-type patches using agar seaweed, starch, etc. are used as skin patches. However, when general nonwoven fabric is impregnated with various essences or other preparations and attached to the skin of the face, etc., as described above, a large amount evaporates into the atmosphere and dries out completely within about 15 to 20 minutes, causing problems such as a deterioration in adhesiveness and detachment from the skin or a deterioration in transdermal absorption of the preparation.

[0004] In addition, in the case of the hydrogel-type patch, adhesion to the skin is reduced, and the adhesive formulation that provides adhesion often causes chemical skin troubles. Also, the product can be produced with only limited formulations, and the manufacturing process is complicated and takes a long time for maturation, etc., which increases the manufacturing cost.

[0005] In addition, in the case of gel-type patches using agar seaweed, starch, etc., mesh or the like is used as a support for the gel, and since the support cannot completely support the gel, the gel may become distorted or damaged while it is attached to the user's skin, and after drying, the residue turns into powder, making it difficult to maintain cleanliness.

[0006] Recently, as leisure industries such as golf, mountain climbing and hiking have become more active, there is a demand for patches that can be used not only indoors but also outdoors. Summary of the Invention [Problem to be solved by the invention]

[0007] The present invention aims to provide a skin patch having high skin adhesion and transparency and a method for producing the same, but the above objects are merely examples and are not intended to limit the scope of the present invention. [Means for solving the problem]

[0008] One aspect of the present invention provides a skin patch including a base sheet and a film disposed on the base sheet and having a preset thickness deviation range. Effect of the Invention

[0009] In the skin patch and its manufacturing method according to an embodiment of the present invention, the film of the skin patch is manufactured to have a thickness deviation, and the thin area can improve the moisture and gas permeability, thereby improving the feeling of use and increasing the comfort when attached to the skin.

[0010] The skin patch and its manufacturing method according to one embodiment of the present invention can improve functionality. Since the part that comes into contact with the skin contains the active ingredient to be delivered to the skin, it can improve the cosmetic effect without causing skin trouble. In addition, the film containing the UV blocking material has high waterproof performance, waterproof retention, and high UV blocking performance. [Brief description of the drawings]

[0011] [Figure 1] FIG. 1 shows a skin patch according to one embodiment of the present invention. [Diagram 2] FIG. 2 is a cross-sectional view taken along line II-II of FIG. 1 and an enlarged view. [Diagram 3] FIG. 3 is an enlarged view showing a modification of FIG. [Figure 4] FIG. 4 is a diagram showing a process for printing the first layer of FIG. [Diagram 5] FIG. 5 is a diagram showing a process for printing the second layer of FIG. [Figure 6] 6 to 9 are enlarged views showing modifications of FIG. [Figure 7] 6 to 9 are enlarged views showing modifications of FIG. [Figure 8] 6 to 9 are enlarged views showing modifications of FIG. [Figure 9] 6 to 9 are enlarged views showing modifications of FIG. [Figure 10] 10 and 11 are diagrams illustrating a method for manufacturing a skin patch according to one embodiment of the present invention. [Figure 11] 10 and 11 are diagrams illustrating a method for manufacturing a skin patch according to one embodiment of the present invention. [Figure 12] 12 and 13 are graphs showing the UV blocking effect of the skin patch of FIG. [Figure 13] 12 and 13 are graphs showing the UV blocking effect of the skin patch of FIG. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0012] One aspect of the present invention provides a skin patch including a base sheet and a film disposed on the base sheet and having a preset thickness deviation range.

[0013] Furthermore, the film may have moisture permeability or gas permeability, and the moisture permeability or gas permeability may be higher in a region where the film is thinner than in a region where the film is thicker.

[0014] Further, the film may comprise a first layer adjacent to the base sheet, the first layer having a first base having a first thickness and a first recess that is thinner than the first thickness, and a second layer disposed on the side of the first layer, the second layer having a second base having a second thickness and a second recess that is thinner than the second thickness.

[0015] The first recess and the second recess may be disposed so as to at least partially overlap each other.

[0016] Furthermore, the second recesses may be disposed between adjacent ones of the first recesses.

[0017] Furthermore, at least one of the first recess and the second recess may have a mesh shape on a plane of the base sheet.

[0018] Additionally, the second layer may include an active ingredient to be delivered to the skin.

[0019] Another aspect of the present invention provides a method for manufacturing a skin patch, comprising the steps of preparing a base sheet and printing a raw material on an upper surface of the base sheet by screen printing to form a film, the step of forming the film comprising the steps of printing a first layer in which the raw material is printed onto a first mesh to form a first recess, and printing a second layer in which the raw material is printed onto a second mesh to be placed on the first layer to form a second recess.

[0020] In addition, in the step of printing the second layer, the second mesh may be disposed so as to overlap the first mesh, or the second mesh may be disposed between the first meshes.

[0021] Additionally, the step of printing the second layer may include printing the raw material containing an active ingredient to be delivered to the skin.

[0022] Since the present invention can be modified in various ways and can have various embodiments, specific embodiments are shown in the drawings and will be described in detail in the detailed description of the invention. The effects and features of the present invention, and methods for achieving them, will become apparent by referring to the embodiments described in detail below together with the drawings. However, the present invention is not limited to the embodiments disclosed below, and can be implemented in various forms.

[0023] Hereinafter, an embodiment of the present invention will be described in detail with reference to the accompanying drawings. When describing with reference to the drawings, the same or corresponding components are given the same reference numerals, and duplicate descriptions thereof will be omitted.

[0024] In the following embodiments, the terms "first", "second", etc. are not used in a limiting sense but are used for the purpose of distinguishing one component from another.

[0025] In the following embodiments, singular expressions include plural expressions unless the context clearly indicates otherwise.

[0026] In the following embodiments, terms such as "comprise" or "have" mean the presence of features or components described in this specification, but do not preclude the possibility that one or more other features or components may be added.

[0027] In the following embodiments, when a part such as a film, region, or component is said to be "on" or "above" another part, this includes not only when it is directly on top of the other part, but also when there is another film, region, component, etc. in between.

[0028] In the drawings, the size of components may be exaggerated or reduced for the convenience of explanation. For example, the size and thickness of each component shown in the drawings are arbitrarily shown for the convenience of explanation, and the present invention is not necessarily limited to those shown in the drawings.

[0029] FIG. 1 is a diagram showing a skin patch according to one embodiment of the present invention, and FIG. 2 is a cross-sectional view taken along line II-II in FIG. 1 and an enlarged view.

[0030] 1 and 2, the skin patch 1 has a film 100 attached to the skin, and can deliver an active ingredient to the skin or protect the skin from the external environment depending on the function of the film 100.

[0031] The skin patch 1 may be flexible to improve adhesion to the skin, and may be elastic to allow it to be attached to various positions on the body.

[0032] The skin patch 1 may have various shapes and sizes depending on the position where it is attached and the purpose of use. For example, the skin patch 1 may have various shapes such as a polygonal shape, a circular shape, an elliptical shape, etc. Also, the skin patch 1 may have various sizes depending on the area to be covered. However, for the convenience of explanation, the following description will be centered on an embodiment in which the skin patch 1 has a rectangular shape as shown in FIG. 1.

[0033] The skin patch 1 can have a base sheet 10 and a film 100 .

[0034] The base sheet 10 supports the film 100 , and one surface of the base sheet 10 is exposed to the outside, and the other surface of the base sheet 10 can face the film 100 .

[0035] In an optional embodiment, an intermediate layer 15 can be disposed between the base sheet 10 and the film 100. The intermediate layer 15 can have adhesive properties such that the film 100 is attached to the base sheet 10. The film 100 can be supported to the base sheet 10 by the intermediate layer 15.

[0036] The adhesive strength of the intermediate layer 15 can be changed by adding a substance. The adhesive strength of the intermediate layer 15 can be reduced so that the base sheet 10 can be easily removed from the film 100 after the film 100 is attached to the skin. For example, the adhesive strength of the intermediate layer 15 can be reduced by contacting the intermediate layer 15 with a solution, and when the adhesive strength of the intermediate layer 15 is reduced, the base sheet 10 can be easily separated from the film 100.

[0037] In one embodiment, the intermediate layer 15 has a decomposition property and can be decomposed by liquid. For example, the intermediate layer 15 can be dissolved by water, and when the base sheet 10 is sufficiently immersed in water, a part of the intermediate layer 15 can be decomposed. When the intermediate layer 15 is decomposed, the adhesive force between the base sheet 10 and the film 100 can be reduced, and the base sheet 10 can be easily separated from the film 100.

[0038] In other embodiments, intermediate layer 15 can have a lower adhesive strength than second layer 120 of film 100. When base sheet 10 is removed after second layer 120 of film 100 has been attached to the skin, base sheet 10 can be easily separated because the adhesive strength between second layer 120 and the skin is lower than the adhesive strength between base sheet 10 and first layer 110 and intermediate layer 15.

[0039] In any embodiment, the skin patch 1 may further include a liner sheet 20. The liner sheet 20 may cover one side of the film 100 and protect the surface of the film 100 that is to be attached to the skin. The liner sheet 20 may be separated from the film 100 when the film 100 is to be attached to the skin.

[0040] The film 100 can be disposed on the base sheet 10. The film 100 can be disposed between the base sheet 10 and the liner sheet 20. The film 100 can be flexible and elastic so as to adhere closely to the skin to which it is attached, and can be formed of a biocompatible material.

[0041] The film 100 can have a multi-layer structure; as an example, the film 100 can include a first layer 110 and a second layer 120 .

[0042] The first layer 110 can be disposed adjacent to the base sheet 10. The first layer 110 can be formed of a biocompatible material.

[0043] The first layer 110 may additionally contain beneficial agents (not shown) depending on the intended use of the skin patch 1 .

[0044] In one embodiment, the first layer 110 can include an ultraviolet light blocking material, so that the skin patch 1 can block ultraviolet light in the area where the film 100 is attached.

[0045] In other embodiments, the first layer 110 may be provided as transparent and may have a mark or symbol (not shown) printed therein. Depending on the transparency of the first layer 110 of the film 100 adhered to the skin, the mark or symbol may be clearly visible.

[0046] The second layer 120 contacts the skin and may be adhesive. The second layer 120 may be supported by the liner sheet 20 and may secure the first layer 110 to the skin S.

[0047] In any embodiment, the second layer 120 may include an active ingredient EM. An active ingredient EM may be defined as a substance that is delivered into the body through the skin to which the film 100 is attached, and may be variously set to include drugs, cosmetics, functional substances, and the like.

[0048] The first layer 110 can have a first thickness T1 and the second layer 120 can have a second thickness T2 that is less than the first layer 110.

[0049] The intermediate layer 15 has a third thickness T3, which can be set to be thinner than the second thickness T2. The intermediate layer 15 is disposed between the first layer 110 and the base sheet 10, and can have a lower adhesive strength than the second layer 120.

[0050] The adhesive strength of the intermediate layer 15 can be changed by an additive substance. When the additive substance is absorbed into the intermediate layer 15, the adhesive strength of the intermediate layer 15 may decrease. As an example, when a liquid additive substance is absorbed into the intermediate layer 15, the intermediate layer 15 changes its shape to a gel or liquid, and the base sheet 10 can slide easily within the film 100.

[0051] Fig. 3 is an enlarged view showing a modified example of Fig. 2. Fig. 3 is an enlarged view of region A of Fig. 2.

[0052] 3, the skin patch can include a film 100A disposed between a base sheet 10 and a liner sheet 20. An intermediate layer 15 can be disposed between the base sheet 10 and the film 100A.

[0053] The film 100A can have a single layer construction, with the area adjacent to the liner sheet 20 having adhesive properties and capable of adhering to the skin.

[0054] In one example, the film 100A can be made from polyurethane, as the first layer 110 described above.

[0055] In any embodiment, the film 100A may include an active ingredient EM. In one example, the active ingredient EM may be a drug, cosmetic, functional substance, or the like that can be delivered into the body through the skin S.

[0056] In another example, the active ingredient EM may include a substance that protects the skin S. In one example, the active ingredient EM is not delivered to the skin S, and can be set to a substance that can protect the skin from the external environment, such as an ultraviolet blocking agent.

[0057] FIG. 4 is a diagram showing a process for printing the first layer of FIG. 2, and FIG. 5 is a diagram showing a process for printing the second layer of FIG.

[0058] 4 and 5, the film 200 can be formed using screen printing methods well known in the art.

[0059] As an example, the first layer 210 and the second layer 220 that make up the film 200 can be laminated and printed.

[0060] The first layer 210 may be formed by printing the first raw material RM1 on the base sheet 10 via the first mesh SC1. In this case, the first layer 210 may be provided to have moisture permeability or gas permeability.

[0061] Referring to the enlarged view of part B of FIG. 4, the first layer 210 can be formed of a first base 211 having a first thickness D1 and a first recess 212 having a first recess thickness D1' depending on the number and spacing of the holes provided in the first mesh SC1.

[0062] The first layer 210 may have a thickness deviation depending on the width W1 and the arrangement interval of the first recesses 212. Depending on the thickness deviation, the first layer 210 may be provided with different degrees of moisture permeability and gas permeability in each portion.

[0063] With reference to FIG. 5, the second layer 220 may be disposed over the first layer 210 .

[0064] The second layer 220 may be formed by printing the second raw material RM2 on the first layer 210 through the second mesh SC2. In this case, the second layer 220 may be provided to have moisture permeability or gas permeability.

[0065] As shown in the enlarged view of portion C of Figure 5, the second layer 220 can be formed from a second base 221 having a second thickness D2 and a second recess 222 having a second recess thickness D2' depending on the number and spacing of the multiple holes provided in the second mesh SC2.

[0066] Since the first layer 210 and the second layer 220 are laminated in sequence to form a single film 200, the second layer 220 can be formed to have a thickness deviation depending on the width W2 and spacing of the second recesses 222, the width W1 and spacing of the first recesses 212, and the overlap between the second recesses 222 and the first recesses 212.

[0067] The film 200 has a thickness equal to the combined thickness of the first layer 210 and the second layer 220 described above, and may have a predetermined thickness deviation range. The above-mentioned predetermined thickness range refers to a thickness range from the minimum recess thickness Dd to the film thickness Df.

[0068] Therefore, the moisture permeability and gas permeability of the film 200 are increased relative to the portion having the minimum recess thickness Dd and the portion having a thickness less than the film thickness Df. That is, the moisture permeability and gas permeability are improved in the portions of the film 200 where the thickness is relatively thin.

[0069] According to one embodiment, the film 200 may be positioned such that the first recess 212 and the second recess 222 overlap, as shown in FIG.

[0070] The first layer 210 is printed via a first mesh SC1, and a first base 211 and a first recess 212 are formed. The second layer 220 is printed on the first layer 210 via a second mesh SC2, and can be formed such that the second recess 222 faces the first recess 212 and the second base 221 faces the first base 211.

[0071] The first recess 212 and the second recess 222 may have a depth and width that are preset according to the application amount of each raw material and the type of mesh screen.

[0072] For example, the first recess thickness D1' plus the second recess thickness D2' may be the minimum recess thickness Dd, and the first thickness D1 plus the second thickness D2 may be the film thickness Df.

[0073] By overlapping the first recesses 212 and the second recesses 222, the film 200 can improve the moisture permeability and gas permeability in the portion having the minimum recess thickness Dd.

[0074] In one embodiment, the recess depth of the first recess 212 may be set to be smaller than the recess depth of the second recess 222 .

[0075] The second recess 222 overlaps the first recess 210 and is recessed deeper, so that a second recess thickness D2' between the second recess 222 and the first recess 212 can be thinner.

[0076] The second layer 220 may have lower moisture permeability and gas permeability than the first layer 210. As the second recess thickness D2′ becomes thinner, the specific gravity of the second layer 220 in the portion having the minimum recess thickness Dd becomes smaller, and the moisture permeability and gas permeability of the film 200 can be improved.

[0077] In one embodiment, the width W1 of the first recess 212 may be provided to be equal to or greater than the width W2 of the second recess 222.

[0078] The second recess 222 may be provided so as to overlap the first recess 212, and the width W2 of the second recess 222 overlaps within the width W1 of the first recess 212. By overlapping the first recess 212 and the second recess 222, the recess is further recessed, and the layered structure of the first layer 210 and the second layer 220 can be made stronger.

[0079] This allows the film 200 to be formed with a thinner minimum recess thickness Dd, while improving the durability and elasticity of the portion having the film thickness Df.

[0080] Since the film 200 is provided to have thickness variation, durability, and elasticity, the film 200 has an improved ability to adhere to the curves of the skin, improving the wearability of the film 200 for the user.

[0081] Figures 6 to 9 are enlarged views showing modifications of Figure 5. The film thickness deviation will be described with reference to Figures 6 to 9.

[0082] Referring to FIG. 6, the second recesses 222A of the film 200A may be disposed between adjacent first recesses 212A.

[0083] As an example, the film 200A may be formed so that the second recess 222A faces the first base 211A, and the second base 221A faces the first recess 212A.

[0084] A first layer 210A is formed on the base sheet 10 by screen printing, and a second layer 220A is printed thereon, where the second recesses 222A may be alternated with the first recesses 212A.

[0085] The first recess 212A and the second recess 222A may have a depth and a width that are preset according to the amount of applied raw material and the type of mesh screen, respectively.

[0086] For example, the first thickness D1 and the second recess thickness D2' may be the minimum recess thickness Dd, and the first recess thickness D1' and the second thickness D2 may be the film thickness Df.

[0087] The film 200A can improve moisture permeability and gas permeability in the portion having the minimum recess thickness Dd.

[0088] In one embodiment, the recess depth of the first recess 212A can be set to be smaller than the recess depth of the second recess 222A.

[0089] The second recess 222A is deeply recessed and faces the first base 211A, so that the second recess thickness D2' can be made thin.

[0090] The second layer 220A may have lower moisture permeability and gas permeability than the first layer 210A. As the second recess thickness D2′ becomes thinner, the specific gravity of the second layer 220A in the portion having the minimum recess thickness Dd becomes smaller, and the moisture permeability and gas permeability of the film 200A can be significantly improved.

[0091] The second layer 220A may be provided with a higher durability so that the moisture and / or gas permeability is lower. In this way, the second base 221A is located above the first recess 212A, and the durability and elasticity of the film 200A can be improved. The film 200A can improve the wearability when attached to the skin.

[0092] On the other hand, the second layer 220A may be provided with higher moisture permeability and gas permeability than the first layer 210A. In this case, in the portion having the film thickness Df, the thickness D2 of the second layer 220A is maximum and the thickness D1' of the first layer 210A is minimum, so that the moisture permeability and gas permeability can be improved.

[0093] In one embodiment, the width W1 of the first recess 212A may be provided to be equal to or smaller than the width W2 of the second recess 222A.

[0094] Since the second recess 222A is supported by the first base 211A located below, it is possible to strengthen the layered structure of the first layer 210 and the second layer 220. This allows the film 200A to improve the durability and elasticity of the portion having the film thickness Df.

[0095] 7, the second recess 222B is disposed between the adjacent first recesses 212B as shown in FIG. 6, but the width W1 of the first recess 212B may be smaller than the width W2 of the second recess 222.

[0096] Since the width of the second base 221B is greater than the width W1 of the first recess 212B, a depression is induced in the center of the second base 221B by the first recess 212B, and a third recess 223B can be formed.

[0097] Film 200B can have an induced recess thickness DB due to the overlap of first recess 212B and third recess 223B.

[0098] For example, the first thickness D1 plus the second recess thickness D2' may be the minimum recess thickness Dd, the first thickness D1' plus the third recess thickness D2" may be the induced recess thickness DB, and the first thickness D1 plus the second thickness D2 may be the film thickness Df. The film 200B can be thinned at the portions having the minimum recess thickness Dd and at the portions having the induced recess thickness DB. The number of portions of the film 200B having a reduced thickness can be increased, thereby improving the moisture and gas permeability.

[0099] 8, the width W1 of the first recess 212C is set larger than the width W2 of the second recess 222C, and a plurality of second recesses 222C can be arranged in a stacked manner within the width W1 of the first recess 212C.

[0100] In one embodiment, the film 200C may be formed such that the spacing between the first recesses 212C of the first layer 210C is greater than the spacing between the second recesses 222C of the second layer 220C.

[0101] The first layer 210C is printed on the base sheet 10 via a first mesh SC1, and a first base 211C and a first recess 212C are formed. The second layer 220C is printed on the first layer 210C via a second mesh SC2, and the mesh spacing of the second mesh SC2 may be narrower than the mesh spacing of the first mesh SC1.

[0102] The film 200C may have a minimum recess thickness Dd where the first recess 212C and the second recess 222C overlap, and a maximum film thickness Df where the first base 211C and the second base 221C overlap.

[0103] For example, the first recess thickness D1' and the second recess thickness D2' may be combined to form a minimum recess thickness Dd, and the first thickness D1 and the second thickness D2 may be combined to form a film thickness Df.

[0104] The film 200C includes more portions that are thinner than the film thickness Df by the number of second recesses 222C, and can improve moisture permeability and gas permeability.

[0105] In one embodiment, the second layer 220C may have a lower moisture or gas permeability than the first layer 210C. The film 200C may have improved moisture or gas permeability, especially in the plurality of second recesses 222C facing the first base 211C.

[0106] The second layer 220C may be provided with a higher durability as the moisture and / or gas permeability is lower. The film 200C can improve durability, elasticity, and wearability by providing a plurality of finely arranged second bases 221C.

[0107] On the other hand, the second layer 220C can have higher moisture permeability and gas permeability than the first layer 210C. The film 200C can improve moisture permeability and gas permeability, particularly in the multiple second recesses 222C that overlap the first recesses 212C.

[0108] 9, the width W1 of the first recess 212D is set smaller than the width W2 of the second recess 222D, and a plurality of first recesses 212D can be arranged in a stacked manner within the width W2 of the second recess 222D.

[0109] In one embodiment, the film 200D may be formed such that the spacing between the first recesses 212D of the first layer 210D is narrower than the spacing between the second recesses 222D of the second layer 220D. The first layer 210D is printed on the base sheet 10 via a first mesh SC1, and a first base 211D and a first recess 212D are formed. The second layer 220D is printed on the first layer 210D via a second mesh SC2, and the mesh spacing of the second mesh SC2 may be wider than the mesh spacing of the first mesh SC1.

[0110] The film 200D may have a minimum recess thickness Dd where the first recess 212D and the second recess 222D overlap, and a maximum film thickness Df where the first base 211D and the second base 221D overlap.

[0111] For example, the first recess thickness D1' plus the second recess thickness D2' may be the minimum recess thickness Dd, and the first thickness D1 plus the second thickness D2 may be the film thickness Df.

[0112] The overlapping portion of the second recess 222D and the first recess 212D is included in the second recess 222D, and the moisture permeability and gas permeability of the film 200D can be improved in the portion of the film 200D that is thinner due to the second recess 222D.

[0113] In one embodiment, the second layer 220D may have lower moisture permeability or gas permeability than the first layer 210D. In this case, since the portion of the first layer 210D having the first thickness D1′ has high moisture and / or gas permeability, the film 200D can have improved moisture permeability or gas permeability in the portions where the plurality of first recesses 212D overlap with the second recesses 222D.

[0114] The second layer 220D may be provided with higher durability as the moisture and / or gas permeability is lower. The first layer 210D includes a plurality of first recesses 212D, which reduces durability, but the second layer 220D supports the first layer 210D to make the layered structure stronger. This can improve the durability, elasticity, and wearability of the film 200D.

[0115] 10 and 11 are diagrams illustrating a method for manufacturing a skin patch according to one embodiment of the present invention.

[0116] 4, 5, 10 and 11, a method for manufacturing the skin patch 1 can include a step S10 of preparing a base sheet and a step S20 of forming a film. In the step S10 of preparing the base sheet, the base sheet 10 is in a state suitable for screen printing of the film 200, and peeling between the base sheet 10 and the film 200 can be facilitated.

[0117] The step S20 of forming the film can include a step S21 of printing a first layer and a step S22 of printing a second layer.

[0118] Returning to FIG. 5, in the step S21 of printing the first layer, a first raw material RM1 is printed on a first mesh SC1 to form a first layer 210, which may have a thickness range set from a first thickness D1 to a first recess thickness D1'.

[0119] In a step S22 of printing a second layer, a second source material RM2 can be printed onto a second mesh SC2 to form a second layer 220 on the top surface of the first layer 210.

[0120] In the step S22 of printing the second layer, the second mesh SC2 can be disposed on top of the first mesh SC1, or the second mesh SC2 can be disposed between the first meshes SC1.

[0121] Thus, the second layer 220 may be formed to have a second thickness D2 and a second recess thickness D2' depending on the location and width of the second recesses 222 and the first recesses 212.

[0122] In the step S22 of printing the second layer, a second raw material RM2 containing an active ingredient to be delivered to the skin can be printed. The active ingredient is defined as a substance to be delivered into the body through the skin, and can be set in various ways, such as a drug, a cosmetic, or a functional substance. Thus, when a user adheres the film 200 to the skin, the active ingredient is delivered to the skin from the second layer 220, and the skin can exhibit a skin beauty and health supplement effect.

[0123] Since the film 200 is intended to be attached to the skin, it is provided so that moisture such as sweat generated from the skin is discharged and evaporated to the outside of the film 200. Therefore, a performance test of moisture permeability is required.

[0124] The moisture permeability test of the film 200 was carried out according to the water film contact method. In the water film contact method, the experimental container is filled with water to the maximum extent possible, and the container is configured so that there is almost no air space between the film 200 placed at the top of the container and the water. This eliminates air resistance to the film 200, allowing the moisture permeability test to be performed.

[0125] As a result of carrying out the moisture permeability test by the above-mentioned method under a temperature condition of 32.2°C, the moisture permeability of the film 200 was 7460 g / m 2 *These results were measured over a 30-day period. Comparing these results with the actual amount of sweat produced, the performance of the film 200 in terms of sweat evacuation and evaporation can be confirmed.

[0126] In general, the amount of sweat lost while resting in a cool environment is 270 g / m 2 *The sweat loss during vigorous exercise is 2880g / m 2 *The sweat loss during exercise in a relatively hot environment is 5500g / m 2 *day. According to the present invention, the moisture permeability of the film 200 according to one embodiment is 7460 g / m 2 It was confirmed that most of the sweat generated on the skin was discharged outside the film 200 and evaporated because it was a *day.

[0127] 12 and 13 are graphs showing the UV blocking effect of the skin patch of FIG.

[0128] The skin patches of Figures 12 and 13 contain a UV blocking material in the film, and have UV blocking properties, water resistance (Figure 12), and blocking retention (Figure 13). In the graphs, the x-axis represents the wavelength, and the y-axis is defined as the blocking rate.

[0129] For a 25-μm-thick skin patch film, the ultraviolet protection factor (UPF) of the film was measured to be 343, blocking 99.9% of UV-B and 95.8% of UV-A.

[0130] For a 35-μm-thick skin patch film, the ultraviolet protection factor (UPF) of the film was measured to be 429, blocking 99.9% of UV-B and 97.4% of UV-A.

[0131] In the water resistance test, the skin patch was fixed to a 96-well plate, and the experimental environment was configured so that both the inner and outer surfaces of the film of the skin patch were immersed in water. Water immersion (20 min) and drying (20 min) were repeated.

[0132] In the graph of Figure 12, the skin patch was immersed in water and dried 8 times in 160 minutes, immersed in water and dried 16 times in 320 minutes, immersed in water and dried 24 times in 480 minutes, and immersed in water and dried 32 times in 640 minutes. The UV blocking effect did not decrease even when the skin patch was immersed in water and dried repeatedly. In particular, it was confirmed that the skin patch maintained almost 100% blocking effect in the UV-B wavelength band and the UV-A wavelength band below 390 nm even after repeated immersion in water and drying.

[0133] Furthermore, the UV blocking effect does not decrease even when physical stimulation is applied to the skin patch using ultrasound.

[0134] In the blocking retention test, the skin patch was attached to the skin and the UV blocking effect was measured at the initial time and after 12 hours. The UV blocking effect did not decrease even after 12 hours of attaching the skin patch to the skin.

[0135] UV-blocking products that are applied to the skin must be applied continuously at two-hour intervals to maintain their UV-blocking performance. Even if a cream-type UV-blocking product is applied, the blocking rate decreases due to sweat, physical contact, a decrease in the effectiveness of the UV-blocking agent, and the agent being absorbed by the skin.

[0136] In the case of the skin patch of the present invention, the UV blocking effect is maintained while the patch is attached to the skin. Unlike conventional cream-type UV blocking agents, the UV blocking effect of the skin patch of the present invention does not decrease due to external environments such as water after being attached once, and it can continuously block UV rays.

[0137] Table 1 below shows the experimental results of whether the following test items were detected after exposing the skin patch of the present invention to water for 24 hours.

[0138] The skin patch of the present invention can be selected from among ingredients that have ultraviolet absorbing / blocking functions. In this test, multiple skin patches containing at least one of the ingredients in Table 1 were targeted, and in each test, the following ingredients were not detected even after prolonged exposure to water.

[0139] [Table 1]

[0140] The skin patch of the present invention does not detect the component even when exposed to water for a long period of time. It has been confirmed that the component is contained inside the film and does not leak out.

[0141] The skin patch according to the present invention does not leak ingredients even when exposed to the external environment, and can reduce skin troubles.

[0142] Thus, the present invention has been described with reference to the embodiment shown in the drawings, but this is merely illustrative, and those skilled in the art will appreciate that various modifications and equivalent embodiments are possible. Therefore, the true technical scope of the present invention should be determined by the technical ideas of the appended claims. Some embodiments are given below. Item 1 A skin patch comprising a base sheet and a film disposed on the base sheet and having a preset thickness deviation range. Section 2 The film has moisture permeability and gas permeability, Item 2. The skin patch described in item 1, wherein the moisture permeability or the gas permeability is higher in an area where the film is thinner than in an area where the film is thicker. Section 3 The film is a first layer adjacent to the base sheet, the first layer having a first thickness and a first recess less than the first thickness; Item 1. The skin patch described in item 1, comprising a second base arranged on one side of the first layer and having a second thickness, and a second layer having a second recess that is thinner than the second thickness. Section 4 Item 4. The skin patch described in item 3, wherein the first recess and the second recess are arranged so as to overlap at least partially. Section 5 Item 4. The skin patch described in item 3, wherein the second recess is disposed between adjacent first recesses. Section 6 At least one of the first recess and the second recess is Item 4. The skin patch according to item 3, having a mesh shape on the plane of the base sheet. Section 7 The second layer is Item 4. The skin patch according to item 3, comprising an active ingredient to be delivered to the skin. Section 8 Providing a base sheet; and printing a raw material on the upper surface of the base sheet by screen printing to form a film. In the step of forming the film, printing a first layer in which the raw material is printed onto a first mesh to form a first recess; A method for manufacturing a skin patch comprising the steps of printing the raw material onto a second mesh and printing a second layer disposed on the first layer to form a second recess. Section 9 In the step of printing the second layer, Item 9. The method for producing a skin patch according to item 8, wherein the second mesh is placed so as to overlap the first mesh or the second mesh is placed between the first meshes. Item 10 In the step of printing the second layer, Item 9. The method for producing a skin patch according to item 8, comprising printing the raw material containing the active ingredient to be delivered to the skin.

Claims

1. A skin patch comprising a base sheet and a film disposed on the base sheet and having a preset thickness deviation range, The film is a first layer adjacent to the base sheet, the first layer having a first thickness and a first recess less than the first thickness; a second base disposed on one side of the first layer and having a second thickness; and a second layer having a second recess that is thinner than the second thickness; The first recess and the second recess overlap each other, The width of the first recess is greater than the width of the second recess. Skin patch.

2. The film has moisture permeability and gas permeability, The skin patch of claim 1 , wherein the moisture permeability or the gas permeability is higher in areas where the film is thinner than in areas where the film is thicker.

3. The skin patch of claim 1 , wherein the second recesses are disposed at least partially between adjacent first recesses.

4. The skin patch of claim 1 , wherein at least one of the first recess and the second recess has a mesh shape on a plane of the base sheet.

5. The skin patch of claim 1 , wherein the second layer comprises an active ingredient to be delivered to the skin.

6. Providing a base sheet; and printing a raw material on the upper surface of the base sheet by screen printing to form a film. In the step of forming the film, printing a first layer in which the raw material is printed onto a first mesh and a first recess is formed; and printing a second layer, the second layer being disposed on the first layer, the second layer having a second recess formed therein, the source material being printed onto a second mesh. In the step of printing the second layer, the second mesh is disposed in the first recess such that the first recess and the second recess overlap each other; The width of the first recess is greater than the width of the second recess. Method for manufacturing a skin patch.

7. In the step of printing the second layer, 7. The method of claim 6, further comprising printing the source material containing the active ingredient to be delivered to the skin.