Liquid crystal alignment agent, liquid crystal alignment film, and liquid crystal display element using the same

Abstract

To provide a liquid crystal alignment agent with which it is possible to obtain a liquid crystal alignment film that has both good liquid crystal alignment and stored charge mitigation characteristic.SOLUTION: A liquid crystal alignment agent contains a polymer that is obtained by polymerizing a diamine component including diamine selected from a group consisting of diamine having a partial skeleton expressed by a formula (ND-2) and diamine expressed by a formula (ND-5) and a tetracarboxylic acid component and then reacting with a terminal sealant, and that is selected from a group consisting of a first polyimide precursor with its terminals sealed and the imidized polymer of the same.SELECTED DRAWING: None

Description

[Technical field]

[0001] The present invention relates to a liquid crystal aligning agent, a liquid crystal alignment film, and a liquid crystal display element using the same. [Background technology]

[0002] Currently, polyimide films are often used as liquid crystal alignment films for liquid crystal display elements. These polyimide liquid crystal alignment films are produced by applying a solution of polyamic acid, which is a precursor of polyimide, or a solution of a solvent-soluble polyimide to a substrate, baking the film obtained, and then performing an alignment treatment such as rubbing. These polyamic acids and solvent-soluble polyimides are generally produced by a condensation polymerization reaction between a tetracarboxylic acid derivative, such as a tetracarboxylic dianhydride, and a diamine compound.

[0003] It has been proposed to cap the ends of polyamic acid or polyimide in order to improve the liquid crystal alignment properties of a liquid crystal alignment film obtained from polyamic acid or polyimide and the property of erasing residual images that occur due to the application of voltage.

[0004] For example, Patent Document 1 describes the use of a liquid crystal aligning agent containing a terminal-capped polymer (1) selected from terminal-capped polyamic acids and the like, and an uncapped polymer (2) selected from uncapped polyamic acids and the like, in order to shorten the time required for erasing residual images in liquid crystal display elements, characterized in that the proportion of the terminal-capped polymer (1) in the total polymer in the liquid crystal aligning agent is 5 to 60% by weight. Furthermore, Patent Document 2 describes the use of a varnish for photoalignment films that contains a first polyamic acid-based compound having a terminal skeleton that does not contain a primary amino group in order to prevent DC afterimages from occurring in liquid crystal display elements. [Prior art documents] [Patent documents]

[0005] [Patent Document 1] Japanese Patent No. 4336922 [Patent Document 2] Japanese Patent Publication No. 2017-90781 Summary of the Invention [Problem to be solved by the invention]

[0006] In recent years, the performance of liquid crystal display elements has improved, the area has increased, and the power consumption of display devices has become more efficient. In addition, liquid crystal display elements have come to be used in various environments, and the characteristics required for liquid crystal alignment films have become more stringent. In particular, as the use of liquid crystal display elements increases, problems such as charge accumulation in the liquid crystal alignment film and difficulty in ensuring good liquid crystal alignment have become prominent.

[0007] When electric charge accumulates in the liquid crystal alignment film, afterimages are likely to occur even after a short period of operation. Furthermore, if good liquid crystal alignment cannot be ensured, light leakage and alignment defects are likely to occur. Therefore, although there is a strong demand for good accumulated charge relaxation characteristics and liquid crystal alignment, the technologies proposed so far have not always been able to fully satisfy both of these demands.

[0008] The present invention has been made in consideration of the above circumstances, and has an object to provide a liquid crystal aligning agent which can provide a liquid crystal alignment film having both good liquid crystal alignment properties and accumulated charge relaxation properties. [Means for solving the problem]

[0009] As a result of intensive research, the present inventors have found that a liquid crystal aligning agent that uses a specific diamine and contains a specific polyimide polymer whose ends are blocked can achieve the above-mentioned object. The present invention is based on such findings and includes a liquid crystal aligning agent having the following gist. A liquid crystal aligning agent comprising at least one polymer (P1) selected from the group consisting of a terminal-capped first polyimide precursor and its imidized polymer, the polymer being obtained by polymerizing a diamine component containing at least one diamine selected from the group consisting of a diamine containing a partial skeleton represented by any one of the following formulae (ND-1) to (ND-4) and a diamine represented by (ND-5) with a tetracarboxylic acid component, and then reacting the diamine component with a terminal-capping agent. [ka] (R 1 , R 21 , R 22 each independently represents a hydrogen atom or a methyl group; R 51 , R 52 Each of S independently represents a hydrogen atom or a methyl group. p3 , S p4 each independently represents a divalent organic group. A5 represents a single bond or a divalent organic group. Effect of the Invention

[0010] According to the liquid crystal aligning agent of the present invention, it is possible to obtain a liquid crystal alignment film having both excellent liquid crystal alignment properties and accumulated charge relaxation properties. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0011] <Polymer (P1)> The liquid crystal aligning agent of the present invention contains at least one polymer (P1) selected from the group consisting of a terminal-capped first polyimide precursor and its imidized polymer, which is obtained by polymerizing a diamine component containing at least one diamine selected from the group consisting of a diamine having a partial skeleton represented by any one of the above formulas (ND-1) to (ND-4) and a diamine represented by (ND-5) with a tetracarboxylic acid component, and then reacting the diamine component with a terminal-cap agent.

[0012] Each of the components serving as the raw materials for the polymer (P1) will be described below. (Specific diamine) The specific diamine is at least one diamine selected from the group consisting of diamines having a partial skeleton represented by the following formulas (ND-1) to (ND-4) and diamines represented by any one of (ND-5).

[0013] [ka] In the above formula, R 1 , R 21 , R 22 R each independently represents a hydrogen atom or a methyl group. 51 , R 52 Each independently represents a hydrogen atom or a methyl group. p3 , S p4 represents a divalent organic group. A5 represents a single bond or a divalent organic group.

[0014] S p3 , S p4 Preferred examples of the divalent organic group include phenylene, pyrrolidine, piperidine, piperazine, a divalent chain hydrocarbon group having 2 to 20 carbon atoms, or a divalent chain hydrocarbon group in which -CH2- is substituted with a group selected from -O-, -CO-, -CO-O-, -O-CO-, -NRCO- (R represents a hydrogen atom or a methyl group), -NRCOO- (R represents a hydrogen atom or a methyl group), -CONR- (R represents a hydrogen atom or a methyl group), -COS-, -NR- (R represents a methyl group), pyrrolidine, piperidine and piperazine.

[0015] Above S p3 , S p4 Examples of the divalent chain hydrocarbon group in include an ethylene group, a propanediyl group, a butanediyl group, a pentanediyl group, a hexanediyl group, a heptanediyl group, an octanediyl group, a nonanediyl group, and a decanediyl group.

[0016] Preferred examples of the divalent organic group for A5 include a divalent chain hydrocarbon group having 1 to 20 carbon atoms, or a group in which -CH2- of the divalent chain hydrocarbon group is substituted with -O-, -CO-, -CO-O-, -O-CO-, -NRCO- (R represents a hydrogen atom or a methyl group), -NRCOO- (R represents a hydrogen atom or a methyl group), or -CONR- (R represents a hydrogen atom or a methyl group). Specific examples of the divalent chain hydrocarbon group in A5 include a methylene group and the divalent chain hydrocarbon groups exemplified in Sp3 and Sp4 above.

[0017] Preferred examples of diamines having a partial skeleton represented by formula (ND-1) include those represented by the following formulas (ND-1-1) and (ND-1-2). [ka]

[0018] In the above formula, R 1 , R 2 R represents a hydrogen atom or a methyl group. 11 , R 22 are each independently a single bond, or *1-R 3 -Ph-*2. R 3 is a single bond, -O-, -COO-, -OCO-, -(CH2) l -, -O(CH2) m It represents a divalent organic group selected from -O-, -CONH-, and -NHCO- (l and m represent integers of 1 to 5). In addition, *1 represents the site of bonding to the benzene ring in formula (ND-1-1) or (ND-1-2), and *2 represents the site of bonding to the amino group in formula (ND-1-1) or (ND-1-2). Ph represents a phenylene group. n represents 1 to 3. In the above formulas (ND-1-1) and (ND-1-2), the substitution positions of the pyrrole ring are preferably the 2-position and the 5-position from the viewpoint of ease of synthesis.

[0019] Specific examples of the diamines represented by the above formulas (ND-1-1) and (ND-1-2) include diamines represented by any of the following formulas (n1-1) to (n1-14). [ka] [ka]

[0020] Examples of diamines having a partial skeleton represented by formula (ND-2) include diamines represented by the following formulas (ND-2-1) to (ND-2-3). [ka]

[0021] In the above formula, R 21 , R 22 are R in the above formula (ND-2), 21 , R 22 The same meaning is used including preferred examples. 24 represents a single bond or a structure of the following formula (Ar), where n represents an integer of 1 to 3. * represents a bond. Furthermore, any hydrogen atom in the benzene ring may be substituted with a monovalent organic group such as an alkyl group having 1 to 3 carbon atoms, an alkoxy group having 1 to 3 carbon atoms, or a halogen atom (a fluorine atom, a chlorine atom, a bromine atom, or an iodine atom). [ka] In the above formula (Ar), R 5 is a single bond, -O-, -COO-, -OCO-, -(CH2) l -, -O(CH2) m It represents a divalent organic group selected from -O-, -CONR-, and -NRCO-, and k is an integer of 1 to 5. In addition, R represents hydrogen or a monovalent organic group, and l and m represent integers of 1 to 5. *1 and *2 represent bonds, and *1 bonds to the benzene ring in Formulae (ND-2-1) to (ND-2-3). The monovalent organic group for R in the above formula (Ar) includes, for example, an alkyl group having 1 to 3 carbon atoms.

[0022] Preferred specific examples of the diamines represented by the above formulas (ND-2-1) to (ND-2-3) include diamines represented by the following formulas (n2-1) to (n2-6). [ka] [ka]

[0023] Specific examples of diamines having a partial skeleton represented by the above formula (ND-3) or (ND-4) include diamines represented by the following formula (ND-3-1) or (ND-4-1). [ka]

[0024] Preferred specific examples of the diamine represented by the above formula (ND-3-1) include diamines represented by the following formulas (n3-1) to (n3-7). [ka]

[0025] Preferred specific examples of the diamine represented by the above formula (ND-4-1) include diamines represented by the following formulas (n4-1) to (n4-6). [ka]

[0026] Preferred specific examples of the diamine represented by the above formula (ND-5) include diamines represented by the following formulas (n5-1) to (n5-8). [ka]

[0027] The content of the specific diamine is preferably 5 mol % or more, more preferably 10 mol % or more, further preferably 20 mol % or more, and particularly preferably 50 mol % or more, of the entire diamine component. The specific diamine may be used alone or in combination with other compounds depending on the solubility of the polymer (P1) in a solvent, the coatability of the liquid crystal alignment agent, the alignment of the liquid crystal when formed into a liquid crystal alignment film, the voltage holding rate, the stored charge, and other properties.

[0028] The diamine component for obtaining the polymer (P1) may contain a diamine other than the specific diamine (hereinafter, also referred to as other diamine). Examples of the other diamine include a diamine represented by the following general formula (2). [ka]

[0029] In the above formula (2), A1 and A2 are each independently a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 2 to 5 carbon atoms, or an alkynyl group having 2 to 5 carbon atoms. From the viewpoint of liquid crystal alignment, A1 and A2 are preferably a hydrogen atom or a methyl group. Examples of the structure of Y1 are as shown in the following formulae (Y-1) to (Y-68).

[0030] [ka]

[0031] [ka]

[0032] [ka]

[0033] [ka] (In the above formula, Boc represents a tert-butoxycarbonyl group. * represents a bond.)

[0034] Other diamines include diamines having a thiophene or furan structure as described in International Publication WO2018 / 092759, preferably diamines represented by the following formula (sf): 2,3-diaminopyridine, 2,6-diaminopyridine, 3,4-diaminopyridine, 2,4-diaminopyrimidine, diaminoorganosiloxane such as 1,3-bis(3-aminopropyl)-tetramethyldisiloxane, aliphatic diamines such as metaxylenediamine, alicyclic diamines such as 4,4-methylenebis(cyclohexylamine), etc. Other diamines can be used alone or in combination of two or more. [ka]

[0035] In the above formula (sf), Y1 represents a sulfur atom or an oxygen atom, and each R2 independently represents a single bond or *1-R 5 -Ph-*2, R 5 is a single bond, -O-, -COO-, -OCO-, -(CH2) l -, -O(CH2) m represents a divalent organic group selected from -O-, -CONH-, and -NHCO- (l and m are integers of 1 to 5). In addition, *1 represents a site bonded to the benzene ring in formula (sf), and *2 represents a site bonded to the amino group in formula (sf). Ph represents a phenylene group. n is 1 to 3.)

[0036] (Tetracarboxylic acid component) As the tetracarboxylic acid component for obtaining the polymer (P1), a tetracarboxylic acid dianhydride represented by the following formula (1) or a derivative thereof (tetracarboxylic acid, tetracarboxylic acid dihalide, tetracarboxylic acid dialkyl ester, or tetracarboxylic acid dialkyl ester dihalide) (collectively referred to as a first tetracarboxylic acid component) can be used.

[0037] [ka] In the above formula, X represents a tetravalent organic group, examples of which include at least one selected from the group consisting of the following formulae (X-1) to (X-14):

[0038] [ka] (x and y each independently represent a single bond, methylene, ethylene, propylene, ether (-O-), carbonyl (-CO-), ester (-COO-), phenylene, sulfonyl (-SO2-) or amide group (-CONH-). 1 ~Z 4 each independently represents a hydrogen atom, a methyl group, an ethyl group, a propyl group, a chlorine atom or a phenyl group. each of j and k independently represents an integer of 0 or 1. m is an integer of 0 to 5. * represents a bond.

[0039] Preferred examples of the above formula (X-1) include structures represented by the following formulae (X1-1) to (X1-4). [ka]

[0040] Preferred examples of the above formula (X-13) include the following formulae (X13-1) to (X13-4). [ka]

[0041] The content of the first tetracarboxylic acid component is preferably 5 mol % or more of the total tetracarboxylic acid components, preferably 10 mol % or more, more preferably 20 mol % or more, and particularly preferably 50 mol % or more.

[0042] The first tetracarboxylic acid component can be used alone or in combination with two or more other materials depending on the solubility of the polymer (P1) in a solvent, the coatability of the liquid crystal alignment agent, and the properties such as the alignment of the liquid crystal when formed into a liquid crystal alignment film, the voltage holding ratio, and the stored charge.

[0043] The tetracarboxylic acid component for obtaining the polymer (P1) of the present invention may be any other tetracarboxylic acid component than the first tetracarboxylic acid component. Examples of the other tetracarboxylic acid component include the following tetracarboxylic acid dianhydrides, tetracarboxylic acid dihalides derived from the tetracarboxylic acid dianhydrides, tetracarboxylic acid dialkyl esters, and tetracarboxylic acid dialkyl ester dihalides. Specific examples include 1,2,5,6-naphthalenetetracarboxylic dianhydride, 1,4,5,8-naphthalenetetracarboxylic dianhydride, 1,2,5,6-anthracenetetracarboxylic dianhydride, 4,4'-(hexafluoroisopropylidene)diphthalic anhydride, bis(3,4-dicarboxyphenyl)dimethylsilane dianhydride, bis(3,4-dicarboxyphenyl)diphenylsilane dianhydride, and 2,6-bis(3,4-dicarboxyphenyl)pyridine dianhydride. The other tetracarboxylic acid components can be used alone or in combination of two or more.

[0044] (End-capping agent) In the present invention, the term "terminal blocking agent" refers to a compound capable of reacting with unreacted acid terminals and / or amine terminals of a polyimide precursor or an imidized polymer thereof to block these terminals. The terminal capping agent is not particularly limited as long as it is a compound capable of capping the acid terminal and / or amine terminal, but is preferably a monoamine or an acid anhydride. The monoamine is capable of capping the acid terminal of the polyimide precursor or its imidized polymer, and the acid anhydride is capable of capping the amine terminal of the polyimide precursor or its imidized polymer.

[0045] Preferred examples of monoamines include aniline, 2-aminophenol, 3-aminophenol, 2-amino-m-cresol, 2-amino-p-cresol, 3-amino-o-cresol, 4-amino-o-cresol, 4-amino-m-cresol, 5-amino-o-cresol, 6-amino-m-cresol, 4-amino-2,3-xylenol, 4-amino-3,5-xylenol, 6-amino-2,4-xylenol, 2-amino-4-ethylphenol, 3-amino-4-ethylphenol, and 2-amino-4-tert-butylphenol. , 2-amino-4-phenylphenol, 4-amino-2,6-diphenylphenol, 4-aminosalicylic acid, 5-aminosalicylic acid, 6-aminosalicylic acid, 2-aminobenzoic acid, 3-aminobenzoic acid, 4-aminobenzoic acid, 2-amino-m-toluene acid, 3-amino-o-toluene acid, 3-amino-p-toluene acid, 4-amino-m-toluene acid, 6-amino-o-toluene acid, 6-amino-m-toluene acid, 3-aminobenzenesulfonic acid, 4-aminobenzenesulfonic acid, 4-aminotoluene-3-sulfonic acid, etc. Two or more of these may be used.

[0046] The acid anhydride is preferably an acid anhydride having a cyclic structure or an acid anhydride having a crosslinkable group. Examples of the acid anhydride include phthalic anhydride, maleic anhydride, nadic anhydride, cyclohexanedicarboxylic anhydride, 3-hydroxyphthalic anhydride, trimellitic anhydride, and compounds represented by the following formulas (m-1) to (m-6). Two or more of these may be used. [ka]

[0047] <Polymer (P2)> The liquid crystal aligning agent of the present invention may further contain at least one polymer (P2) selected from the group consisting of a second polyimide precursor and its imidized polymer, which are obtained by reacting a diamine component with a tetracarboxylic acid component, together with the polymer (P1). In this case, it is preferable in that, for example, the polymer (P1) has an excellent function of accumulated charge relaxation property, and the polymer (P2) has an excellent function of liquid crystal alignment. The polyimide precursor of the polymer (P2) or the imidized polymer thereof may be end-capped, in which case the diamine component of the polymer (P2) contains a diamine other than the specific diamine. Specific examples include, in addition to the other diamines exemplified in the polymer (P1), diamines described in International Publication WO2018-159733 and specific diamines (1) described in International Publication WO2016-104365 in order to vertically align the liquid crystal, and specific diamines (4) described in International Publication WO2016-104365 and diamines having a polymerization initiation function described in Japanese Patent Application Laid-Open No. 2018-081225 in order to increase the response speed of the liquid crystal.

[0048] When the ends of the polymer (P2) are not blocked, the diamine component for obtaining the polymer (P1) can be used as the diamine component for obtaining the polymer (P2) in addition to the diamines exemplified above. The diamine component for obtaining the polymer (P2) may contain at least one diamine selected from the following formulae (3), (4) and (5) in order to enhance the liquid crystal alignment property.

[0049] [ka]

[0050] In the above formula, A1 and A4 each independently represent a single bond or a divalent organic group, A2 represents a hydrogen atom, a halogen atom, a hydroxyl group, an amino group, a thiol group, a nitro group, a phosphate group, or a monovalent organic group having 1 to 20 carbon atoms, and A3 represents a divalent organic group. a is an integer of 1 to 4, and when a is 2 or more, the structure of A2 may be the same or different. b and c each independently represent an integer of 1 or 2. d is an integer of 0 or 1.

[0051] The divalent organic group in A1 and A4 above is a divalent chain hydrocarbon group having 2 to 20 carbon atoms, or a group (h1) in which -CH2- of the divalent chain hydrocarbon group is substituted with a group selected from -O-, -CO-, -CO-O-, -NRCO- (R represents a hydrogen atom or a methyl group), -NRCOO- (R represents a hydrogen atom or a methyl group), -CONR- (R represents a hydrogen atom or a methyl group), -COS-, -NR1-CO-NR2- (R1 and R2 each independently represent a hydrogen atom or a methyl group), -NR- (R represents a methyl group), pyrrolidine, piperidine, and piperazine. Note that some or all of the hydrogen atoms in the chain hydrocarbon group and group (h1) may be substituted with an alkyl group having 1 to 3 carbon atoms such as a methyl group, or a halogen atom such as a fluorine atom or a chlorine atom.

[0052] The divalent organic group in A3 above is a divalent chain hydrocarbon group having 1 to 20 carbon atoms, or a group (h2) in which -CH2- of the divalent chain hydrocarbon group is substituted with a group selected from -O-, -CO-, -CO-O-, -NRCO- (R represents a hydrogen atom or a methyl group), -NRCOO- (R represents a hydrogen atom or a methyl group), -CONR- (R represents a hydrogen atom or a methyl group), -COS-, -NR1-CO-NR2- (R1 and R2 each independently represent a hydrogen atom or a methyl group), -NR- (R represents a methyl group), pyrrolidine, piperidine, and piperazine. Note that some or all of the hydrogen atoms in the chain hydrocarbon group and group (h2) in A3 above may be substituted with an alkyl group having 1 to 3 carbon atoms such as a methyl group, or a halogen atom such as a fluorine atom or a chlorine atom.

[0053] Examples of the divalent chain hydrocarbon group having 1 to 20 carbon atoms include alkanediyl groups such as a methanediyl group, an ethanediyl group, an n-propanediyl group, an i-propanediyl group, an n-butanediyl group, an i-butanediyl group, a sec-butanediyl group, and a t-butanediyl group; Examples of the groups include alkenediyl groups such as ethenediyl group, propenediyl group, and butenediyl group; and alkynediyl groups such as ethynediyl group, propynediyl group, and butynediyl group.

[0054] Examples of the monovalent organic group having 1 to 20 carbon atoms in A2 include the divalent chain hydrocarbon group having 1 to 20 carbon atoms in A3 above, group (h2), and groups in which one hydrogen atom has been added to any of the exemplified groups in which some or all of the hydrogen atoms in the divalent chain hydrocarbon group having 1 to 20 carbon atoms and group (h2) have been substituted with an alkyl group having 1 to 3 carbon atoms, such as a methyl group, or a halogen atom, such as a fluorine atom or a chlorine atom.

[0055] A preferred specific example of the at least one diamine selected from the above formula (3), the following formula (4), and the following formula (5) is at least one diamine selected from the group consisting of the following formulae (DA-3-1), (DA-4-1) to (DA-4-23), and (DA-5-1) to (DA-5-3). [ka] [ka] [ka] [ka]

[0056] From the viewpoint of improving the liquid crystal alignment property, the total amount of at least one diamine selected from the above formulae (3), (4) and (5) is preferably 10 mol % or more of the total diamine components for obtaining the polymer (P2).

[0057] From the viewpoint of enhancing the functional separation between the polymer (P1) and the polymer (P2), the diamine component for obtaining the polymer (P1) and / or the polymer (P2) preferably contains a diamine represented by the following formula (6). [ka] In the above formula, Y6 represents a divalent organic group containing a structure represented by the following formula (7). Each A6 independently represents a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 2 to 5 carbon atoms, or an alkynyl group having 2 to 5 carbon atoms. From the viewpoint of liquid crystal alignment, A6 is preferably a hydrogen atom or a methyl group. [ka] (D is a t-butoxycarbonyl group.)

[0058] Examples of the divalent organic group containing the structure represented by formula (7) above include groups represented by formula (J-1) or (J-2) below. [ka]

[0059] In the above formula, R5 is a single bond, -(CH2) n -(n is an integer from 1 to 20), or -(CH2) n represents a group in which any -CH2- in - is replaced with -O-, -COO-, -OCO-, -NR-, -NRCO-, -CONR-, -NRCONR-, -NRCOO-, or -OCOO-, provided that they are not adjacent to each other. R represents a hydrogen atom or a monovalent organic group. R6 and R7 each independently represent -H, -NHD, -N(D)2, a group having -NHD, or a group having -N(D)2. R8 represents -NHD, -N(D)2, a group having -NHD, or a group having -N(D)2. D represents a t-butoxycarbonyl group. However, at least one of R5, R6, and R7 has a t-butoxycarbonyl group in the group.

[0060] More preferred specific examples of the divalent organic group represented by the above formula (J-1) or formula (J-2) are the divalent organic groups represented by the following formulas (J-1-a) to (J-1-d) and (J-2-1), where Boc represents a t-butoxycarbonyl group. [ka]

[0061] As the tetracarboxylic acid component for obtaining the polymer (P2), the tetracarboxylic acid component for obtaining the polymer (P1) can be used. Specifically, from the viewpoint of improving the liquid crystal alignment, the first tetracarboxylic acid component can be used. More preferably, the first tetracarboxylic acid component is used in an amount of 10 mol % or more of the total tetracarboxylic acid components used in the polymer (P2).

[0062] <Method for producing polymer (P1)> The polymer (P1) is selected from the group consisting of a first polyimide precursor having blocked terminals and its imidized polymer, and is obtained by subjecting a diamine component containing at least one diamine selected from specific diamines to a (condensation) polymerization reaction with a tetracarboxylic acid component, and then reacting the diamine component with a terminal blocking agent. Here, the polyimide precursor refers to a polyamic acid or a polyamic acid alkyl ester. In the liquid crystal aligning agent of the present invention, the polymer (P1) is preferably a polyimide precursor having a blocked end, and more preferably a polyamic acid having a blocked end.

[0063] In an embodiment of the present invention, the polymer (P1) is preferably obtained by polymerizing a diamine component containing at least one diamine selected from specific diamines with a tetracarboxylic acid component to obtain a polyimide precursor or an imidized polymer thereof, and further reacting the polyimide precursor or the imidized polymer thereof with an end-capping agent. The polymer (P1) can also be obtained by supplying an end-capping agent when or during polymerization of a diamine component containing at least one diamine selected from specific diamines and a tetracarboxylic acid component.

[0064] The reaction between the diamine component and the tetracarboxylic acid component is usually carried out in a solvent. The solvent used in this reaction is not particularly limited as long as it dissolves the polyimide precursor produced. Specific examples of the solvent used in the reaction are listed below, but are not limited to these examples. Examples of the solvent include N-methyl-2-pyrrolidone, N-ethyl-2-pyrrolidone, γ-butyrolactone, N,N-dimethylformamide, N,N-dimethylacetamide, 3-methoxy-N,N-dimethylpropanamide, 3-butoxy-N,N-dimethylpropanamide, dimethylsulfoxide, and 1,3-dimethyl-imidazolidinone. When the polyimide precursor has high solvent solubility, methyl ethyl ketone, cyclohexanone, cyclopentanone, 4-hydroxy-4-methyl-2-pentanone, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monopropyl ether, and the like can be used.

[0065] These solvents may be used alone or in combination. Furthermore, even if the solvent does not dissolve the polyimide precursor, it may be mixed with the above-mentioned solvent to the extent that the generated polyimide precursor does not precipitate. Furthermore, since moisture in the solvent inhibits the polymerization reaction and further causes hydrolysis of the generated polyimide precursor, it is preferable to use a solvent that has been dehydrated and dried.

[0066] When the diamine component and the tetracarboxylic acid component are reacted in a solvent, a method of stirring a solution in which the diamine component is dispersed or dissolved in a solvent and adding the tetracarboxylic acid component as it is or after being dispersed or dissolved in the solvent, a method of adding the diamine component to a solution in which the tetracarboxylic acid component is dispersed or dissolved in a solvent, a method of adding the diamine component alternately to the reaction system, etc. may be used, and any of these methods may be used. In addition, when a plurality of diamine components or tetracarboxylic acid components are used for reaction, they may be reacted in a premixed state, or may be reacted individually in sequence, or low molecular weight substances that have been reacted individually may be mixed and reacted to form a polymer.

[0067] The temperature at which the diamine component and the tetracarboxylic acid component are polycondensed can be selected from any temperature between -20 and 150°C, but is preferably in the range of -5 to 100°C. The reaction can be carried out at any concentration, but if the concentration is too low, it becomes difficult to obtain a polymer with a high molecular weight, and if the concentration is too high, the viscosity of the reaction liquid becomes too high, making it difficult to stir uniformly. Therefore, the polymer concentration is preferably 1 to 50% by mass, more preferably 5 to 30% by mass. The reaction can be carried out at a high concentration in the early stages, and then a solvent can be added. In the polymerization reaction to obtain the polyimide precursor, the ratio of the total number of moles of the tetracarboxylic acid components to the total number of moles of the diamine components is preferably 0.8 to 1.2. As in the case of a normal polycondensation reaction, the closer this molar ratio is to 1.0, the higher the molecular weight of the polyimide precursor produced will be.

[0068] An imidized polymer is a polyimide obtained by ring-closing a polyimide precursor. In this polyimide, the ring-closure rate (also called the imidization rate) of amic acid groups (amide acid groups) does not necessarily have to be 100% and can be adjusted as desired depending on the application or purpose. Methods for imidizing the polyimide precursor include thermal imidization, in which a solution of the polyimide precursor is heated as is, and catalytic imidization, in which a catalyst is added to a solution of the polyimide precursor.

[0069] The temperature when thermally imidizing the polyimide precursor in a solution is preferably 100 to 400° C., more preferably 120 to 250° C., and is preferably a method in which the imidization reaction is carried out while removing water generated by the imidization reaction from the system. Catalytic imidization of the polyimide precursor can be carried out by adding a basic catalyst and an acid anhydride to a solution of the polyimide precursor and stirring the mixture at −20 to 250° C., preferably 0 to 180° C.

[0070] The amount of the basic catalyst is preferably 0.5 to 30 times by mole, more preferably 2 to 20 times by mole, the amic acid group, and the amount of the acid anhydride is preferably 1 to 50 times by mole, more preferably 3 to 30 times by mole, the amic acid group. Examples of the basic catalyst include pyridine, triethylamine, trimethylamine, tributylamine, trioctylamine, etc. Among these, pyridine is preferred because it has an appropriate basicity for promoting the reaction. Examples of the acid anhydride include acetic anhydride, trimellitic anhydride, and pyromellitic anhydride. In particular, the use of acetic anhydride is preferred because it facilitates purification after the reaction. The imidization rate by catalytic imidization can be controlled by adjusting the amount of catalyst, reaction temperature, and reaction time.

[0071] When recovering the polyimide precursor or its imidized polymer produced from the reaction solution, the reaction solution may be poured into a solvent to cause precipitation. Examples of the solvent used for precipitation include methanol, ethanol, isopropyl alcohol, acetone, hexane, butyl cellosolve, heptane, methyl ethyl ketone, methyl isobutyl ketone, toluene, benzene, and water. The polymer precipitated by pouring into the solvent can be recovered by filtration, and then dried at room temperature or by heating under normal or reduced pressure. In addition, the recovered polymer can be redissolved in a solvent and the reprecipitation recovery operation can be repeated 2 to 10 times to reduce impurities in the polymer. Examples of the solvent used in this case include alcohols, ketones, and hydrocarbons. It is preferable to use three or more types of solvents selected from these because the efficiency of purification is further improved.

[0072] In the present invention, when the polyimide precursor is a polyamic acid alkyl ester, specific methods for producing it include, for example, the techniques described in paragraphs

[0054] to

[0062] of International Publication WO2011-115077.

[0073] Next, in order to cap the acid terminals or amine terminals of the polyimide precursor or its imidized polymer, a terminal capping agent may be added and reacted either during or after the production of the polyimide precursor or its imidized polymer. The amount of the end-capping agent used is not particularly limited, but is preferably 0.001 to 0.8 equivalents, and more preferably 0.01 to 0.2 equivalents, per equivalent of the amino group in the diamine component involved in the polymerization reaction of the polyimide precursor or its imidized polymer. Furthermore, the amount is preferably 0.001 to 0.8 equivalents, more preferably 0.01 to 0.2 equivalents, relative to 1 equivalent of a carboxyl group (or a derivative structure thereof) in a tetracarboxylic acid component involved in the polymerization reaction of a polyimide precursor or an imidized polymer thereof. The reaction temperature when the ends are blocked is preferably −50 to 150° C., more preferably −30 to 100° C. The reaction time is usually 0.1 to 100 hours.

[0074] <Method for producing polymer (P2)> The polymer (P2) is selected from the group consisting of a second polyimide precursor and its imidized polymer, and is obtained by reacting a diamine component with a tetracarboxylic acid component. The reaction between the diamine component and the tetracarboxylic acid component is the same as that described in the above-mentioned method for producing the polymer (P1).

[0075] When the polymer (P2) is selected from the group consisting of terminally-capped polyimide precursors and imidized polymers thereof, the polyimide precursor or the imidized polymer thereof may be reacted with a terminal-capping agent selected from the following formulae (R-1) to (R-2) during or after the production of the polyimide precursor or the imidized polymer thereof, or both.

[0076] [ka] (R2 and R2' represent a monovalent organic group. n is an integer of 1 to 2.)

[0077] Specific examples of R2 and R2' include a methyl group, a 9-fluorenylmethyl group, a 2,2,2-trichloroethyl group, a 2-trimethylsilylethyl group, a 1,1-dimethylpropynyl group, a 1-methyl-1-phenylethyl group, a 1-methyl-1-(4-biphenylyl)ethyl group, a 1,1-dimethyl-2-haloethyl group, a 1,1-dimethyl-2-cyanoethyl group, a tert-butyl group, a cyclobutyl group, a 1-methylcyclobutyl group, a 1-adamantyl group, a vinyl group, an allyl group, a cinnamyl group, an 8-quinolyl group, an N-hydroxypiperidinyl group, a benzyl group, a p-nitrobenzyl group, a 3,4-dimethoxy-6-nitrobenzyl group, and a 2,4-dichlorobenzyl group. Among these, in terms of the relationship with the firing temperature in the liquid crystal display element production process, a tert-butyl group, a 2,2,2-trichloroethyl group, a 2-trimethylsilylethyl group, a 1,1-dimethylpropynyl group, a 1-methyl-1-(4-biphenylyl)ethyl group, a 1,1-dimethyl-2-haloethyl group, a 1,1-dimethyl-2-cyanoethyl group, a t-butyl group, a cyclobutyl group, a 1-methylcyclobutyl group, a vinyl group, an allyl group, a cinnamyl group, and an N-hydroxypiperidinyl group are more preferable, and a 1,1-dimethyl-2-haloethyl group, a 1,1-dimethyl-2-cyanoethyl group, and a tert-butyl group are particularly preferable.

[0078] <Liquid crystal alignment agent> The liquid crystal aligning agent of the present invention contains a polymer (P1) and, if necessary, a polymer (P2). The content of the polymer (P1) in the liquid crystal aligning agent is preferably 2 to 10 mass %, more preferably 3 to 8 mass %, in the liquid crystal aligning agent. When the liquid crystal alignment agent contains a polymer (P2), the content of the polymer (P1) is preferably 30 parts by mass or more, more preferably 50 parts by mass or more, even more preferably 60 parts by mass or more, and most preferably 70 parts by mass or more, per 100 parts by mass of the total amount of the polymer (P1) and the polymer (P2).

[0079] The liquid crystal aligning agent of the present invention may contain other polymers in addition to the polymer (P1) and the polymer (P2). Examples of other polymers include cellulose-based polymers, acrylic polymers, methacrylic polymers, polystyrene, polyamide, polysiloxane, etc. The content of other polymers is preferably 0.5 to 15 parts by mass, more preferably 1 to 10 parts by mass, based on 100 parts by mass of the total of the polymer (P1) and the polymer (P2).

[0080] The liquid crystal alignment agent usually contains an organic solvent, and the content of the organic solvent is preferably 70 to 99.9% by mass relative to the liquid crystal alignment agent. This content can be appropriately changed depending on the coating method of the liquid crystal alignment agent and the intended thickness of the liquid crystal alignment film. The organic solvent used in the liquid crystal alignment agent is preferably a solvent (also called a good solvent) that dissolves the polymer (P1) and the polymer (P2). For example, N,N-dimethylformamide, N,N-dimethylacetamide, N-methyl-2-pyrrolidone, N-ethyl-2-pyrrolidone, dimethylsulfoxide, γ-butyrolactone, 1,3-dimethyl-imidazolidinone, methyl ethyl ketone, cyclohexanone, cyclopentanone, 4-hydroxy-4-methyl-2-pentanone, 3-methoxy-N,N-dimethylpropanamide, 3-butoxy-N,N-dimethylpropanamide, etc. Among them, N-methyl-2-pyrrolidone, N-ethyl-2-pyrrolidone, 3-methoxy-N,N-dimethylpropanamide, 3-butoxy-N,N-dimethylpropanamide, or γ-butyrolactone is preferred. The good solvent in the liquid crystal aligning agent of the present invention is preferably 20 to 99 mass %, more preferably 20 to 90 mass %, and particularly preferably 30 to 80 mass % of the total solvent contained in the liquid crystal aligning agent.

[0081] The liquid crystal aligning agent of the present invention can use a solvent (also called a poor solvent) that improves the coating property and surface smoothness of the liquid crystal alignment film when the liquid crystal aligning agent is applied. Specific examples thereof are given below. For example, diisopropyl ether, diisobutyl ether, diisobutyl carbinol (2,6-dimethyl-4-heptanol), ethylene glycol dimethyl ether, ethylene glycol diethyl ether, ethylene glycol dibutyl ether, 1,2-butoxyethane, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, 4-hydroxy-4-methyl-2-pentanone, diethylene glycol methyl ethyl ether, diethylene glycol dibutyl ether, 3-ethoxybutyl acetate, 1-methylpentyl acetate, 2-ethylbutyl acetate, 2-ethylhexyl acetate, ethylene glycol monoacetate, ethylene glycol diacetate, propylene carbonate, ethylene carbonate, ethylene glycol monobutyl ether, ethylene glycol monoisoamyl ether, ethylene glycol monohexyl ether, propylene glycol monobutyl ether, 1-(2-butoxyethoxy)-2-propanol, 2-(2-butoxyethoxy)-2-propanol, Examples of the dimethyl ether include 1-propanol, propylene glycol monomethyl ether acetate, dipropylene glycol monomethyl ether, dipropylene glycol monoethyl ether, dipropylene glycol dimethyl ether, ethylene glycol monobutyl ether acetate, ethylene glycol monoacetate, ethylene glycol diacetate, diethylene glycol monoethyl ether acetate, diethylene glycol monobutyl ether acetate, 2-(2-ethoxyethoxy)ethyl acetate, diethylene glycol acetate, propylene glycol diacetate, n-butyl acetate, propylene glycol monoethyl ether acetate, methyl 3-methoxypropionate, ethyl 3-ethoxypropionate, ethyl 3-methoxypropionate, propyl 3-methoxypropionate, butyl 3-methoxypropionate, n-butyl lactic acid ester, isoamyl lactic acid ester, diethylene glycol monoethyl ether, and diisobutyl ketone (2,6-dimethyl-4-heptanone).

[0082] Among them, preferred combinations of solvents include N-methyl-2-pyrrolidone and ethylene glycol monobutyl ether, N-methyl-2-pyrrolidone, γ-butyrolactone, and ethylene glycol monobutyl ether, N-methyl-2-pyrrolidone, γ-butyrolactone, and propylene glycol monobutyl ether, N-ethyl-2-pyrrolidone and propylene glycol monobutyl ether, and N-methyl-2-pyrrolidone, γ-butyrolactone, 4-hydroxy-4-methyl-2-pentanone, and diethylene glycol diethyl ether. Examples of poor solvents include ether, N-methyl-2-pyrrolidone, γ-butyrolactone, propylene glycol monobutyl ether, and 2,6-dimethyl-4-heptanone, N-methyl-2-pyrrolidone, γ-butyrolactone, propylene glycol monobutyl ether, and diisopropyl ether, N-methyl-2-pyrrolidone, γ-butyrolactone, propylene glycol monobutyl ether, and 2,6-dimethyl-4-heptanol, and N-methyl-2-pyrrolidone, γ-butyrolactone, and dipropylene glycol dimethyl ether. These poor solvents are preferably 1 to 80% by mass, more preferably 10 to 80% by mass, and particularly preferably 20 to 70% by mass, of the total solvent contained in the liquid crystal alignment agent. The type and content of such solvents are appropriately selected depending on the coating device, coating conditions, coating environment, etc. of the liquid crystal alignment agent.

[0083] The liquid crystal aligning agent of the present invention may contain a dielectric material for changing the electric properties such as the dielectric constant and the conductivity of the liquid crystal alignment film, a silane coupling agent for improving the adhesion between the liquid crystal alignment film and the substrate, a crosslinking compound for increasing the hardness and density of the film when made into a liquid crystal alignment film, and an imidization promoter for efficiently promoting imidization by heating the polyimide precursor when baking the coating film.

[0084] Compounds that improve the adhesion between the liquid crystal alignment film and the substrate include functional silane-containing compounds and epoxy group-containing compounds, such as 3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane, 3-glycidoxypropyltriethoxysilane, 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropylmethyldiethoxysilane, 2-aminopropyltrimethoxysilane, 2-aminopropyltriethoxysilane, N-(2-aminoethyl)-3-aminopropyltrimethoxy ... Ethyl)-3-aminopropylmethyldimethoxysilane, 3-ureidopropyltrimethoxysilane, 3-ureidopropyltriethoxysilane, N-ethoxycarbonyl-3-aminopropyltrimethoxysilane, N-ethoxycarbonyl-3-aminopropyltriethoxysilane, N-triethoxysilylpropyltriethylenetriamine, N-trimethoxysilylpropyltriethylenetriamine, 10-trimethoxysilyl-1,4,7-triazadecane, 10-triethoxysilyl-1,4,7-triazadecane, 9-trimethoxysilylpropyltriethylenetriamine Silyl-3,6-diazanonyl acetate, 9-triethoxysilyl-3,6-diazanonyl acetate, N-benzyl-3-aminopropyltrimethoxysilane, N-benzyl-3-aminopropyltriethoxysilane, N-phenyl-3-aminopropyltrimethoxysilane, N-phenyl-3-aminopropyltriethoxysilane, N-bis(oxyethylene)-3-aminopropyltrimethoxysilane, N-bis(oxyethylene)-3-aminopropyltriethoxysilane, ethylene glycol diglycidyl ether, polyethylene Glycol diglycidyl ether, propylene glycol diglycidyl ether, tripropylene glycol diglycidyl ether, polypropylene glycol diglycidyl ether, neopentyl glycol diglycidyl ether, 1,6-hexanediol diglycidyl ether, glycerin diglycidyl ether, 2,2-dibromoneopentyl glycol diglycidyl ether, 1,3,5,6-tetraglycidyl-2,4-hexanediol, N,N,N',N',-tetraglycidyl-m-xylylenediamine, 1,3-bis(N,N-diglycidylaminomethyl)cyclohexane, or N,N,N',N'-tetraglycidyl-4,4'-diaminodiphenylmethane.

[0085] The liquid crystal aligning agent of the present invention may contain the following additives (CL-1) to (CL-15) in order to increase the mechanical strength of the liquid crystal alignment film. [ka]

[0086] The amount of the above additives is preferably 0.1 to 30 parts by mass, more preferably 0.5 to 20 parts by mass, based on 100 parts by mass of the polymer component contained in the liquid crystal alignment agent.

[0087] <Method of manufacturing liquid crystal alignment film> The liquid crystal alignment film is obtained by forming a coating of the liquid crystal alignment agent on a substrate by coating or the like, preferably drying, and then baking. As the substrate, a substrate with high transparency is preferable, and as the material thereof, glass, ceramics such as silicon nitride, plastics such as acrylic resin and polycarbonate, etc. can be used. From the viewpoint of simplifying the process, it is preferable to use a substrate on which an ITO (Indium Tin Oxide) electrode for driving the liquid crystal is formed as the substrate. In addition, in a reflective liquid crystal display element, an opaque substrate such as a silicon wafer can be used for one substrate, and a light-reflecting material such as aluminum can be used for the electrode.

[0088] Methods for forming a coating on a substrate from a liquid crystal alignment agent include screen printing, offset printing, flexographic printing, and inkjet printing. In addition, a dip method, a roll coater method, a slit coater method, a spinner method, and a spray method can also be used depending on the purpose. After forming a coating of the liquid crystal alignment agent on the substrate, the coating is preferably dried by a heating means such as a hot plate, a heat circulation oven, or an IR (infrared) oven at preferably 30 to 120°C, more preferably 50 to 120°C, for preferably 1 to 10 minutes, more preferably 1 to 5 minutes, to evaporate the solvent.

[0089] When the imide precursor in the polymer is thermally imidized, the coating film obtained from the liquid crystal aligning agent is then baked by the same heating means as in the drying treatment, preferably at 120 to 250° C., more preferably at 150 to 230° C. The baking time varies depending on the baking temperature, but is preferably 5 minutes to 1 hour, more preferably 5 minutes to 40 minutes.

[0090] The thickness of the coating after the above-mentioned baking treatment is not particularly limited, but if it is too thin, the reliability of the liquid crystal display element may decrease, and if it is too thick, the electrical resistance of the obtained liquid crystal alignment film will be high, so that the thickness is preferably 5 to 300 nm, and more preferably 10 to 200 nm. After the baking treatment, the resulting coating film is subjected to an alignment treatment, which may be performed by a rubbing treatment method, a photoalignment method, or the like.

[0091] As a specific example of the photo-alignment treatment, the surface of the coating is irradiated with radiation deflected in a certain direction. As the radiation, ultraviolet light having a wavelength of 100 to 800 nm or visible light can be used. Among them, ultraviolet light having a wavelength of 100 to 400 nm is preferred, and ultraviolet light having a wavelength of 200 to 400 nm is more preferred. In order to improve the liquid crystal alignment, the substrate coated with the liquid crystal alignment film may be irradiated with ultraviolet light while being heated at 50 to 250°C. The radiation dose is 1 to 10,000 mJ / cm. 2 Among them, 100 to 5,000 mJ / cm is preferable. 2 The liquid crystal alignment film thus prepared can stably align liquid crystal molecules in a certain direction. The higher the extinction ratio of the polarized UV light, the higher the anisotropy that can be imparted, which is preferable. Specifically, the extinction ratio of the linearly polarized UV light is preferably 10:1 or more, and more preferably 20:1 or more.

[0092] The coating that has been subjected to the above-mentioned alignment treatment may further be subjected to at least one treatment selected from the group consisting of a heat treatment and a contact treatment with a solvent. The heat treatment after the alignment treatment can be carried out by the same heating means as in the drying treatment and baking treatment, and is preferably carried out at 180 to 250° C., more preferably 180 to 230° C. When the heat treatment temperature is within the above range, the contrast of the liquid crystal display element obtained by the obtained liquid crystal alignment film can be improved. The heat treatment time varies depending on the heating temperature, but is preferably 5 minutes to 1 hour, more preferably 5 to 40 minutes.

[0093] The solvent used in the contact treatment with the solvent is not particularly limited as long as it dissolves impurities and the like attached to the liquid crystal alignment film. Specific examples include water, methanol, ethanol, 2-propanol, acetone, methyl ethyl ketone, 1-methoxy-2-propanol, 1-methoxy-2-propanol acetate, butyl cellosolve, ethyl lactate, methyl lactate, diacetone alcohol, methyl 3-methoxypropionate, ethyl 3-ethoxypropionate, propyl acetate, butyl acetate, cyclohexyl acetate, etc. Among these, water, 2-propanol, 1-methoxy-2-propanol, or ethyl lactate is preferred from the viewpoint of versatility and solvent safety. More preferred are water, 1-methoxy-2-propanol, or ethyl lactate. These solvents may be one or more kinds.

[0094] The contact treatment may be an immersion treatment or a spray treatment (also called a spray treatment). The treatment time in these treatments is preferably from 10 seconds to 1 hour, and particularly, an embodiment in which the treatment is performed by immersion for 1 to 30 minutes is exemplified. The temperature during the contact treatment may be at room temperature or heated, and is preferably from 10 to 80°C, and may be from 20 to 50°C. During the contact treatment, ultrasonic treatment or the like may be further performed as necessary.

[0095] After the contact treatment, rinsing with a low boiling point solvent such as water, methanol, ethanol, 2-propanol, acetone, or methyl ethyl ketone (also called "rinsing") or drying may be performed. In this case, either rinsing or drying may be performed, or both may be performed. The drying temperature is preferably 50 to 150°C, and can be 80 to 120°C. The drying time is preferably 10 seconds to 30 minutes, and more preferably 1 to 10 minutes. After the contact treatment with the solvent, the alignment film may be subjected to a heat treatment after the alignment treatment. By adopting such an embodiment, a liquid crystal alignment film having excellent liquid crystal alignment properties can be obtained.

[0096] <Liquid crystal display element> The liquid crystal alignment film of the present invention can be applied to various driving modes such as TN mode, STN mode, IPS mode, FFS mode, VA mode, MVA mode, PSA mode, etc., but is suitable as a liquid crystal alignment film for a liquid crystal display element of a horizontal electric field mode such as IPS mode or FFS mode, and is particularly useful for a liquid crystal display element of an FFS mode. The liquid crystal display element of the present invention is obtained by preparing a liquid crystal cell by a known method after obtaining a substrate with a liquid crystal alignment film obtained from the above liquid crystal alignment agent, and using the liquid crystal cell to form an element. As an example of a method for fabricating a liquid crystal cell, a liquid crystal display element having a passive matrix structure will be described below. However, a liquid crystal display element having an active matrix structure in which a switching element such as a TFT is provided in each pixel portion constituting an image display may also be used.

[0097] Specifically, a transparent glass substrate is prepared, a common electrode is provided on one substrate, and a segment electrode is provided on the other substrate. These electrodes can be, for example, ITO electrodes, and are patterned so as to display a desired image. Next, an insulating film is provided on each substrate so as to cover the common electrode and the segment electrode. The insulating film can be, for example, a film made of SiO2-TiO2 formed by the sol-gel method. Next, under the above-mentioned conditions, a liquid crystal alignment film is formed on each substrate, and one substrate is superimposed on the other substrate so that the liquid crystal alignment film surfaces face each other, and the periphery is bonded with a sealant. In order to control the substrate gap, it is usually preferable to mix a spacer into the sealant. It is also preferable to scatter spacers for controlling the substrate gap even in the in-plane portion where the sealant is not provided. It is preferable to provide an opening in a part of the sealant that can be filled with liquid crystal from the outside.

[0098] Thereafter, a liquid crystal material is injected into the space surrounded by the two substrates and the sealant through an opening provided in the sealant. The opening is then sealed with an adhesive. The injection may be performed by a vacuum injection method or a method utilizing capillary action in the atmosphere, or an ODF (One Drop Fill) method may be used. The liquid crystal material may have either positive or negative dielectric anisotropy. In the present invention, liquid crystals having negative dielectric anisotropy are preferred from the viewpoint of liquid crystal alignment, but they may be used according to the application. After the liquid crystal material is injected into the liquid crystal cell, polarizing plates are placed. Specifically, it is preferable to attach a pair of polarizing plates to the surfaces of the two substrates opposite to the liquid crystal layer. EXAMPLES

[0099] The present invention will be described in more detail below with reference to examples, but the present invention is not limited thereto. The abbreviations of compounds and the measuring methods of each property are as follows.

[0100] NMP: N-methyl-2-pyrrolidone, GBL: γ-butyrolactone BCS: Butyl cellosolve [ka] [ka] [ka] [ka]

[0101] [viscosity] Measurements were performed using an E-type viscometer TVE-22H (manufactured by Toki Sangyo Co., Ltd.) with a sample volume of 1.1 mL, a cone rotor TE-1 (1°34', R24), and a temperature of 25°C. [Molecular weight] The measurements were carried out using a GPC (room temperature gel permeation chromatography) device, and the number average molecular weight (Mn) and weight average molecular weight (Mw) were calculated as values ​​calculated in terms of polyethylene oxide. GPC apparatus: Shodex (GPC-101), column: Shodex (KD803, KD805 in series), column temperature: 50°C, eluent: N,N-dimethylformamide (containing 30 mmol / L lithium bromide hydrate (LiBr·H2O), 30 mmol / L phosphoric acid anhydrous crystal (o-phosphoric acid), and 10 ml / L tetrahydrofuran (THF) as additives), flow rate: 1.0 ml / min. Standard samples for creating a calibration curve: TSK standard polyethylene oxide manufactured by Tosoh Corporation (weight average molecular weight (Mw) approximately 900,000, 150,000, 100,000, 30,000), and polyethylene glycol manufactured by Polymer Laboratory Co., Ltd. (peak top molecular weight (Mp) approximately 12,000, 4,000, 1,000). In order to avoid overlapping peaks, measurements were performed separately on two samples: a sample made by mixing four types of 900,000, 100,000, 12,000, and 1,000, and a sample made by mixing three types of 150,000, 30,000, and 4,000.

[0102] [Preparation of liquid crystal cells] A liquid crystal cell having a fringe field switching (FFS) mode liquid crystal display element configuration is fabricated. First, a substrate with electrodes was prepared. The substrate was a glass substrate with a size of 30 mm x 50 mm and a thickness of 0.7 mm. An ITO electrode with a solid pattern was formed on the substrate as the first layer, which constituted the counter electrode. A SiN (silicon nitride) film formed by a CVD method was formed on the first layer of the counter electrode as the second layer. The thickness of the second layer of the SiN film was 500 nm, and it functions as an interlayer insulating film. A comb-shaped pixel electrode formed by patterning the ITO film as the third layer was arranged on the second layer of the SiN film, forming two pixels, a first pixel and a second pixel. The size of each pixel was 10 mm in length and about 5 mm in width. At this time, the first layer of the counter electrode and the third layer of the pixel electrode were electrically insulated by the action of the second layer of the SiN film. The pixel electrode in the third layer has a comb-like shape composed of multiple electrode elements arranged in a "L" shape with the center bent at an internal angle of 160°. The width of each electrode element in the short direction is 3 μm, and the distance between the electrode elements is 6 μm. Since the pixel electrode forming each pixel is composed of multiple electrode elements arranged in a "L" shape with a bent center, the shape of each pixel is not rectangular, but has a shape similar to a bold "L" shape that is bent in the center like the electrode elements. Each pixel is divided into upper and lower parts by the bent part in the center, and has a first region above the bent part and a second region below the bent part.

[0103] Next, the liquid crystal alignment agent was filtered through a filter with a pore size of 1.0 μm, and then applied by spin coating to the above-prepared electrode-attached substrate and a glass substrate having a columnar spacer with a height of 4 μm and an ITO film formed on the back side. After drying for 2 minutes on a hot plate at 80° C., it was baked for 30 minutes in a hot air circulation oven at 230° C. to form a coating film with a thickness of 100 nm. The coating surface was irradiated with linearly polarized ultraviolet light with a wavelength of 254 nm and an extinction ratio of 10:1 or more through a polarizing plate. This substrate was baked for another 30 minutes in a hot air circulation oven at 230° C. to obtain a substrate with a liquid crystal alignment film. The liquid crystal alignment film formed on the electrode-attached substrate was oriented so that the direction that equally divides the inner angle of the pixel bend portion and the alignment direction of the liquid crystal were orthogonal to each other, and the liquid crystal alignment film formed on the second glass substrate was oriented so that the alignment direction of the liquid crystal on the first substrate and the alignment direction of the liquid crystal on the second substrate were aligned when a liquid crystal cell was produced. The above two substrates were combined into a set, a sealant was printed on one substrate, and the other substrate was attached so that the liquid crystal alignment film faces each other and the alignment direction was 0°. The sealant was then cured to prepare an empty cell. Liquid crystal MLC-3019 (Merck) was injected into this empty cell by the reduced pressure injection method, and the injection port was sealed to obtain an FFS-driven liquid crystal cell. The obtained liquid crystal cell was then heated at 110°C for 1 hour and left overnight before being used for each evaluation.

[0104] [Evaluation of image lag due to long-term AC drive] A liquid crystal cell having the same structure as the liquid crystal cell used in the above-mentioned afterimage evaluation was prepared. Using this liquid crystal cell, an AC voltage of ±5 V at a frequency of 60 Hz was applied for 120 hours in a constant temperature environment of 60° C. After that, the pixel electrode and the counter electrode of the liquid crystal cell were shorted, and the liquid crystal cell was left at room temperature for one day. After leaving it, the liquid crystal cell was placed between two polarizing plates arranged so that the polarization axes were perpendicular to each other, and the backlight was turned on with no voltage applied, and the angle of the liquid crystal cell was adjusted so that the brightness of the transmitted light was minimized. The angle of rotation when the liquid crystal cell was rotated from the angle at which the second region of the first pixel was the darkest to the angle at which the first region was the darkest was calculated as the angle Δ. Similarly, the second region and the first region of the second pixel were compared to calculate the same angle Δ.

[0105] <Synthesis Example 1> (Unterminated polyamic acid) In a 3L four-neck flask equipped with a stirrer and a nitrogen inlet tube, 17.30g (159.98mmol) of diamine DA-1, 58.63g (240.0mmol) of diamine DA-2, 76.89g (240.0mmol) of diamine DA-3 and 54.63g (159.99mmol) of diamine DA-4 were weighed out, 2458.13g of NMP was added, and the mixture was stirred and dissolved while feeding nitrogen. While stirring this diamine solution, 171.27g (764.02mmol) of tetracarboxylic dianhydride TA-1 was added, and further, NMP was added so that the solid content concentration was 12% by mass, and the mixture was stirred at 40 ° C. for 20 hours to obtain a polyamic acid solution (PAA-1). The viscosity of this polyamic acid solution was 426 mPa s, and the molecular weight of this polyamic acid was Mn = 12,380, Mw = 33,250.

[0106] <Synthesis Example 2> (Unterminated polyamic acid) In a 100 mL four-neck flask equipped with a stirrer and a nitrogen inlet tube, 5.29 g (26.98 mmol) of tetracarboxylic dianhydride TA-2 was weighed out, 80.13 g of NMP was added, and the mixture was stirred and dissolved while feeding nitrogen. While stirring this carboxylic dianhydride solution, 2.96 g (14.86 mmol) of diamine DA-5, 2.28 g (5.41 mmol) of diamine DA-6, and 1.61 g (5.43 mmol) of diamine DA-7 were added, and NMP was further added so that the solid content concentration became 12 mass%, and the mixture was stirred at 40 ° C. for 20 hours to obtain a polyamic acid solution (PAA-2). The viscosity of this polyamic acid solution was 437 mPa s, and the molecular weight of this polyamic acid was Mn = 16,331, Mw = 35,853.

[0107] <Synthesis Example 3> (Unterminated polyamic acid) In a 100mL four-neck flask equipped with a stirrer and a nitrogen inlet tube, 2.98g (14.96mmol) of diamine DA-5, 2.11g (5.00mmol) of diamine DA-6, and 1.49g (4.99mmol) of diamine DA-7 were weighed out, 74.16g of NMP was added, and the mixture was stirred and dissolved while feeding nitrogen. While stirring this diamine solution, 4.64g (23.66mmol) of tetracarboxylic dianhydride TA-2 was added, and further, NMP was added so that the solid content concentration became 12% by mass, and the mixture was stirred at 40°C for 20 hours to obtain a polyamic acid solution (PAA-3). The viscosity of this polyamic acid solution was 443 mPa s, and the molecular weight of this polyamic acid was Mn = 12,155, Mw = 35,725.

[0108] [Table 1]

[0109] <Synthesis Example 4> (Terminally Capped Polyamic Acid) 20.0 g of polyamic acid (PAA-2) was weighed out into a 50 mL Erlenmeyer flask, and 0.035 g (0.38 mmol, 0.04 equivalents per equivalent of amino group in the diamine involved in the polymerization reaction) of end-capping agent MA-1 was added, and the mixture was stirred at 40°C for 20 hours to obtain a polyamic acid solution (PAA-4). The acid ends of the polyamic acid solution (PAA-4) were capped.

[0110] <Synthesis Examples 5 to 8> (Terminally Capped Polyamic Acid) The polyamic acid solutions (PAA-5) to (PAA-8) shown in Table 2 were obtained by carrying out the same procedure as in Synthesis Example 4 using the polyamic acid solutions and end-capping agents shown in Table 2 below. The polyamic acid solution (PAA-5) had its acid ends capped, and the polyamic acid solutions (PAA-6) to (PAA-8) had their amine ends capped.

[0111] [Table 2]

[0112] (Liquid crystal alignment agent with a blend ratio (mass ratio) of component 1:component 2 of 5:5) <Example 1> 2.29g of 12% by mass polyamic acid solution (PAA-4) (component 1) and 2.29g of 12% by mass polyamic acid solution (PAA-1) (component 2) were placed in a 50ml Erlenmeyer flask, 2.41g of NMP and 3.00g of BCS were added, and mixed at 25°C for 2 hours to obtain a liquid crystal alignment agent (A1). No abnormalities such as turbidity or precipitation were observed in this liquid crystal alignment agent, and it was confirmed that it was a uniform solution.

[0113] <Examples 4, 7, 10, and 13> The liquid crystal alignment agents (A4), (A7), (A10), and (A13) were obtained by carrying out the same procedure as in Example 1, except that the polyamic acid solutions (PAA-5) to (PAA-8) were used instead of the polyamic acid solution (PAA-4). <Comparative Examples 1 and 4> Liquid crystal alignment agents (B1) and (B4) were obtained by carrying out the same procedure as in Example 1, except that the polyamic acid solutions (PAA-2) to (PAA-3) were used instead of the polyamic acid solution (PAA-4).

[0114] (Liquid crystal alignment agent in which the blend ratio (mass ratio) of component 1:component 2 is 6:4) <Example 2> 2.75g of 12% by mass polyamic acid solution (PAA-4) (component 1) and 1.83g of 12% by mass polyamic acid solution (PAA-1) (component 2) were placed in a 50ml Erlenmeyer flask, 2.41g of NMP and 3.00g of BCS were added, and mixed at 25°C for 2 hours to obtain a liquid crystal alignment agent (A2). No abnormalities such as turbidity or precipitation were observed in this liquid crystal alignment agent, and it was confirmed that it was a uniform solution.

[0115] <Examples 5, 8, 11, and 14> The liquid crystal alignment agents (A5), (A8), (A11), and (A14) were obtained by carrying out the same procedure as in Example 2, except that the polyamic acid solutions (PAA-5) to (PAA-8) were used instead of the polyamic acid solution (PAA-4). <Comparative Examples 2 and 5> Liquid crystal alignment agents (B2) and (B5) were obtained by carrying out the same procedure as in Example 2, except that the polyamic acid solutions (PAA-2) to (PAA-3) were used instead of the polyamic acid solution (PAA-4).

[0116] (Liquid crystal alignment agent with a blend ratio (mass ratio) of component 1:component 2 of 7:3) <Example 3> 3.21g of 12% by mass polyamic acid solution (PAA-4) (component 1) and 1.38g of 12% by mass polyamic acid solution (PAA-1) (component 2) were placed in a 50ml Erlenmeyer flask, 2.41g of NMP and 3.00g of BCS were added, and mixed at 25°C for 2 hours to obtain a liquid crystal alignment agent (A3). No abnormalities such as turbidity or precipitation were observed in this liquid crystal alignment agent, and it was confirmed that it was a uniform solution.

[0117] <Examples 6, 9, 12, and 15> The liquid crystal alignment agents (A6), (A9), (A12), and (A15) were obtained by carrying out the same procedure as in Example 3, except that the polyamic acid solutions (PAA-5) to (PAA-8) were used instead of the polyamic acid solution (PAA-4). <Comparative Examples 3 and 6> Liquid crystal alignment agents (B3) and (B6) were obtained by carrying out the same procedure as in Example 3, except that the polyamic acid solutions (PAA-2) to (PAA-3) were used instead of the polyamic acid solution (PAA-4).

[0118] [Table 3]

[0119] (Results of image retention evaluation using long-term AC drive) <Example 16> The liquid crystal alignment agent (A1) obtained in Example 1 was filtered through a filter with a pore size of 1.0 μm, and then applied by spin coating to the above-prepared electrode-attached substrate and a glass substrate having a columnar spacer with a height of 4 μm and an ITO film formed on the back side. After drying for 2 minutes on a hot plate at 80°C, it was baked for 30 minutes in a hot air circulation oven at 230°C to form a coating film with a thickness of 100 nm. Linearly polarized ultraviolet light with an extinction ratio of 26:1 and a wavelength of 254 nm was irradiated on the coating surface through a polarizer at a rate of 0.3 J / cm. 2 This substrate was baked in a hot air circulating oven at 230° C. for 30 minutes to obtain a substrate with a liquid crystal alignment film.

[0120] The two substrates obtained above were combined into a set, a sealant was printed on one substrate, and the other substrate was attached so that the liquid crystal alignment film faces each other and the alignment direction was 0°. The sealant was then cured to produce an empty cell. Liquid crystal MLC-3019 (Merck) was injected into this empty cell by a reduced pressure injection method, and the injection port was sealed to obtain an FFS drive liquid crystal cell. The obtained liquid crystal cell was then heated at 110°C for 1 hour and left overnight to perform an afterimage evaluation due to long-term AC drive. The angle Δ of this liquid crystal cell after long-term AC drive was 0.26 degrees.

[0121] <Examples 17 to 21 and Comparative Examples 7 to 9> Except for using the liquid crystal alignment agent A2 to A5 and B1 to B3 shown in Table 3 instead of the liquid crystal alignment agent (A1), the FFS drive liquid crystal cell was prepared in the same manner as in Example 16, and the afterimage evaluation was carried out by long-term AC drive. The angle Δ of this liquid crystal cell after long-term AC drive in each case is shown in Table 4.

[0122] [Table 4]

[0123] <Examples 22 to 30, Comparative Examples 10 to 12> Except for using the liquid crystal alignment agent A7 to A15 and B4 to B6 shown in Table 4 instead of the liquid crystal alignment agent (A1), the FFS drive liquid crystal cell was prepared in the same manner as in Example 16, and the afterimage evaluation was carried out by long-term AC drive. The angle Δ of this liquid crystal cell after long-term AC drive in each case is shown in Table 5.

[0124] [Table 5]

[0125] In Table 4, when Comparative Example 7 is compared with Examples 16 and 19, Comparative Example 8 with Examples 17 and 20, and Comparative Example 9 with Examples 18 and 21, it can be seen that when a polyamic acid whose acid terminal is modified with a monoamine is blended, the afterimage caused by AC driving tends to be reduced. Furthermore, in Table 5, when Comparative Example 10 is compared with Examples 22, 25, and 28, Comparative Example 11 with Examples 23, 26, and 29, and Comparative Example 12 with Examples 24, 26, and 30, it is confirmed that when a polyamic acid whose amine end is modified with a carboxylic acid anhydride is blended, there is a tendency for the afterimage caused by long-term AC operation to be reduced. When the difference in Δ value between the Comparative Example and the Example with the same blend ratio was taken, the difference in Δ value between the Comparative Example and the Example tended to be larger as the blend ratio of component 1 was higher. For this reason, this method is particularly useful when it is desired to increase the ratio of component 1. [Industrial Applicability]

[0126] The liquid crystal alignment film obtained from the liquid crystal alignment agent of the present invention has a high yield in liquid crystal panel manufacturing, and can reduce residual images caused by AC driving in IPS driving type or FFS driving type liquid crystal display elements, thereby obtaining IPS driving type or FFS driving type liquid crystal display elements with excellent residual image characteristics. Therefore, it is used particularly in liquid crystal display elements that require high display quality. The entire contents of the specification, claims, drawings, and abstract of Japanese Patent Application No. 2018-214005, filed on November 14, 2018, are hereby incorporated by reference as the disclosure of the specification of the present invention.

Claims

1. The polymer (P1) is obtained by polymerizing a diamine component containing 50 mol % or more of at least one diamine selected from the group consisting of a diamine having a partial skeleton represented by the following formula (ND-2) and a diamine represented by the following formula (ND-5), with a tetracarboxylic acid component, and then reacting the diamine component with a terminal-capping agent, and the polymer (P1) is selected from the group consisting of a terminal-capping first polyimide precursor and an imidized polymer thereof; The end-capping agent is an acid anhydride or a monoamine, and is selected from the group consisting of aniline, 2-aminophenol, 3-aminophenol, 2-amino-m-cresol, 2-amino-p-cresol, 3-amino-o-cresol, 4-amino-o-cresol, 4-amino-m-cresol, 5-amino-o-cresol, 6-amino-m-cresol, 4-amino-2,3-xylenol, 4-amino-3,5-xylenol, 6-amino-2,4-xylenol, 2-amino-4-ethylphenol, 3-amino-4-ethylphenol, 2-amino-4-tert-butylphenol, 2-amino-4-phenylphenol, 4-amino-2,6-diphenylphenol, 4-aminosalicylic acid, and 5-aminosalicylic acid. , 6-aminosalicylic acid, 2-aminobenzoic acid, 3-aminobenzoic acid, 4-aminobenzoic acid, 2-amino-m-toluene acid, 3-amino-o-toluene acid, 3-amino-p-toluene acid, 4-amino-m-toluene acid, 6-amino-o-toluene acid, 6-amino-m-toluene acid, 3-aminobenzenesulfonic acid, 4-aminobenzenesulfonic acid, 4-aminotoluene-3-sulfonic acid, phthalic anhydride, maleic anhydride, nadic anhydride, cyclohexanedicarboxylic anhydride, 3-hydroxyphthalic anhydride, trimellitic anhydride, and compounds represented by the following formulas (m-1), (m-2), and (m-4) to (m-6). A liquid crystal aligning agent comprising at least one terminal blocking agent selected from the group consisting of: 【Chemistry 1】 (R ２１ , R ２２ each independently represents a hydrogen atom or a methyl group. 【Chemistry 2】 (R ５１ , R ５２ Each of A and B independently represents a hydrogen atom. ５ represents a single bond or a divalent organic group. 【Chemistry 3】

2. The liquid crystal aligning agent according to claim 1, wherein the diamine component comprises the diamine represented by (ND-5).

3. The liquid crystal aligning agent according to claim 1 or 2, wherein the tetracarboxylic acid component comprises a tetracarboxylic dianhydride represented by the following formula (1): 【Chemistry 4】 (X represents a tetravalent organic group selected from the following formulae (X-1) to (X-6) and (X-8) to (X-14).) 【Chemistry 5】 (x and y each independently represent a single bond, methylene, ethylene, propylene, ether, carbonyl, ester, phenylene, sulfonyl, or amide group. Z １ ~Z ４ each independently represents a hydrogen atom, a methyl group, an ethyl group, a propyl group, a chlorine atom, or a phenyl group; j and k are integers of 0 or 1; m is an integer of 0 to 5; * represents a bond.

4. The liquid crystal aligning agent according to claim 3, wherein the content of the tetracarboxylic dianhydride represented by the formula (1) is 5 mol % or more of the total tetracarboxylic acid component.

5. The diamine component contains at least two diamines selected from the group consisting of diamines containing a partial skeleton represented by the formula (ND-2) and diamines represented by the formula (ND-5). The liquid crystal aligning agent according to any one of claims 1, 3 to 4.

6. The liquid crystal alignment agent according to any one of claims 1 to 5, further comprising at least one polymer (P2) different from the polymer (P1), selected from the group consisting of a second polyimide precursor obtained by reacting a diamine component with a tetracarboxylic acid component and an imidized polymer thereof.

7. The diamine component, which is a raw material of the polymer (P2), contains at least one diamine selected from the group consisting of the following formula (3), the following formula (4), and the following formula (5). The liquid crystal aligning agent according to claim 6. 【Chemistry 6】 (A １ , A ４ each independently represents a single bond or a divalent organic group; A ２ represents a hydrogen atom, a halogen atom, a hydroxyl group, an amino group, a thiol group, a nitro group, a phosphate group, or a monovalent organic group having 1 to 20 carbon atoms; A ３ represents a divalent organic group. a is an integer of 1 to 4, and when a is 2 or more, A ２ may be the same or different. b and c are each independently an integer of 1 to 2. d is an integer of 0 or 1.

8. The diamine component, which is a raw material of the polymer (P2), contains at least one diamine selected from the group consisting of the following formulas (DA-3-1), (DA-4-1) to (DA-4-23), and (DA-5-1) to (DA-5-3). The liquid crystal aligning agent according to any one of claims 6 to 7. 【Chemistry 7】 【Chemistry 8】 【Chemistry 9】 【Chemistry 10】

9. The content of the polymer (P1) is 30 parts by mass or more relative to 100 parts by mass of the total amount of the polymer (P1) and the polymer (P2). The liquid crystal alignment agent according to any one of claims 6 to 8.

10. A liquid crystal alignment film obtained by applying the liquid crystal aligning agent according to any one of claims 1 to 9, baking the resulting film, and irradiating the film with polarized ultraviolet light.

11. A liquid crystal display device comprising the liquid crystal alignment film according to claim 10.