Manufacturing method of rare earth sintered magnet and wet molding device

Abstract

The production method for a rare-earth sintered magnet according to the present disclosure comprises: a step for producing a molded article by compression-molding a slurry containing a rare-earth element-containing alloy powder and a dispersion medium using a wet-molding device; and a step for sintering the molded article. When the slurry is being poured into the inside of a space forming a cavity of the wet-molding device, a magnetic field is not applied. By pressing of the slurry, the dispersion medium contained in the slurry starts to be removed from the inside of the space.

Description

[Technical field]

[0001] The present disclosure relates to a method for producing a rare earth sintered magnet and a wet compacting apparatus. [Background technology]

[0002] In recent years, there has been high demand for rare earth sintered magnets, and among them, RTB sintered magnets (where R is at least one rare earth element, T is mainly iron, and B is boron) are known as the highest performance magnets and are used in a variety of motors such as voice coil motors (VCM) for hard disk drives, motors for electric vehicles (EV, HV, PHV, etc.), motors for industrial equipment, and home appliances.

[0003] RTB sintered magnets are mainly R2T 14 It is composed of a main phase made of B compounds and a grain boundary phase located at the grain boundary of this main phase. 14 B compounds are ferromagnetic materials with high saturation magnetization and anisotropic magnetic field. The grain boundary phase contains a non-magnetic, low-melting-point R-rich phase that is enriched in rare earth elements (R). Methods for improving the magnetic properties of RTB sintered magnets include (1) R2T 14 Refining the B phase, (2) R2T 14 Increasing the degree of orientation of the B phase, (3) Reducing the amount of oxygen, (4) R2T 14 It is known that the ratio of B phase is increased.

[0004] In the manufacture of rare earth sintered magnets such as RTB sintered magnets, alloy powder having a predetermined particle size is used, which is obtained by crushing a raw alloy casting material having a desired composition, such as an ingot obtained by melting raw materials such as metal and casting the molten metal into a mold, or flakes obtained by a strip casting method, and this alloy powder is compressed in an aligning magnetic field to produce a powder compact (green compact), which is then sintered to produce a rare earth sintered magnet. Note that if the powder particles are oxidized during the crushing and molding, the improvement of the magnetic properties is hindered.

[0005] Incidentally, there are two molding methods for producing powder compacts: dry and wet, and Patent Document 1 discloses a wet molding method. This wet molding method makes it possible to suppress oxidation of powder particles, and is therefore considered to be less likely to impede improvements in magnetic properties than the dry molding method. [Prior art documents] [Patent documents]

[0006] [Patent Document 1] Japanese Patent Application Publication No. 8-88133 Summary of the Invention [Problem to be solved by the invention]

[0007] In the wet compaction method disclosed in Patent Document 1, a slurry containing rare earth alloy powder is pressurized and injected into the cavity (space) of a die. However, the inventors' investigations have revealed that even in this case, "density variation in the powder compact" and "orientation disorder" tend to occur when the powder compact is compressed in an aligning magnetic field.

[0008] The former, "density variation in powder compacts," can lead to cracks or fissures when the powder compacts are removed or sintered thereafter. The latter, "disordered orientation," can lead to a deterioration in magnetic properties. In particular, the degree of density variation and disordered orientation of powder compacts varies depending on the relationship between the pressing direction and the direction of the magnetic field when the slurry is pressurized and injected into the cavity of the die, as well as the state of the slurry in the cavity of the die, making it difficult to stably produce the required high magnetic properties.

[0009] The present disclosure provides a new method for producing a rare earth sintered magnet and a wet molding apparatus that can solve the above problems. [Means for solving the problem]

[0010] In one non-limiting embodiment, the method for producing a rare earth sintered magnet disclosed herein is a method for producing a rare earth sintered magnet by supplying a slurry containing an alloy powder including a rare earth element and a dispersion medium into the space of a die, and pressing the supplied slurry to obtain a molded body, in which no magnetic field is applied while the slurry is being supplied into the space of the die, and when the dispersion medium is being discharged from the space of the die, application of a transverse magnetic field in a direction perpendicular to the pressing direction is started before the discharge.

[0011] In one embodiment, the molded body has dimensions of length 90 mm or more, width 90 mm or more, and height 90 mm or more.

[0012] In one embodiment, the method includes a first division step of cutting the green body to divide it into 10 or more green body pieces, and a sintered body material preparation step of producing a plurality of sintered body materials by sintering each of the plurality of green body pieces after the first division step.

[0013] In one embodiment, after the sintered body material preparation step, the method includes a second dividing step of cutting each of the plurality of sintered body materials to divide them into 100 or more sintered body pieces.

[0014] In one embodiment, before the application of the transverse magnetic field is started, a gap is formed between a device for pressing the slurry and the upper surface of the slurry.

[0015] In a non-limiting embodiment, a method for producing a rare earth sintered magnet according to the present disclosure includes the steps of: preparing a wet molding apparatus comprising: a die having a through hole; a lower punch that moves up and down relative to the die with at least a tip end inserted into the through hole; and an upper punch that moves up and down relative to the lower punch, the upper punch having a lower end with a plurality of discharge holes for passing a liquid therethrough; a cavity being formed inside the through hole by the upper end of the lower punch and the lower end of the upper punch; and a step of reducing the volume of the cavity by reducing the distance between the upper end of the lower punch and the lower end of the upper punch; and preparing a slurry containing an alloy powder containing a rare earth element and a dispersion medium. the step of forming a cavity filled with the slurry by closing the space with the lower end of the upper punch, the step of reducing a distance between the lower end of the upper punch and the upper end of the lower punch while applying a transverse magnetic field to the cavity in a direction perpendicular to a direction in which the lower punch moves up and down relatively, and discharging the dispersion medium contained in the slurry through the multiple discharge holes in the upper punch to produce a compact of the alloy powder, and the step of sintering the compact. While the slurry is being injected into the space, no magnetic field is applied to the space, and the space is temporarily or intermittently covered with a non-magnetic lid, and the non-magnetic lid is moved from a position covering the space before applying the transverse magnetic field to the cavity.

[0016] In one embodiment, in the process of producing a compact of the alloy powder while reducing the distance between the lower end of the upper punch and the upper end of the lower punch, a filter cloth or filter is placed between the slurry in the cavity and the lower end of the upper punch.

[0017] In one embodiment, the method includes a step of, after filling the space with the slurry, moving the non-magnetic lid from the position where it was covering the space, and, before starting application of at least the transverse magnetic field, lowering the lower punch relative to the die to form a gap between the slurry and at least one of the lower end of the upper punch and the filter cloth.

[0018] In one embodiment, the size of the gap is 2 mm or more and 4 mm or less. In one embodiment, after the space is filled with the slurry, the non-magnetic lid is moved from the position where it was covering the space, and application of the transverse magnetic field is initiated before starting to discharge the dispersion medium contained in the slurry through the multiple discharge holes in the upper punch.

[0019] In one embodiment, the method includes a step of temporarily connecting the inside of the space to the outside by moving the non-magnetic lid up and down when injecting the slurry into the inside of the space.

[0020] In one embodiment, the concentration of the alloy powder in the slurry at the time of pouring is 75 to 88 mass %.

[0021] The wet molding apparatus of the present disclosure is a wet molding apparatus for producing a compact of rare earth alloy powder, and includes a die having a through hole, a lower punch that moves up and down relative to the die with at least its tip inserted into the through hole, an upper punch that moves up and down relative to the lower punch and has a lower end with a plurality of discharge holes for passing liquid, and an electromagnetic coil that applies a transverse magnetic field in a direction perpendicular to the direction in which the lower punch moves up and down relative to the through hole of the die. The die has an injection port for injecting a slurry containing the rare earth alloy powder into a space formed by the inner wall of the through hole and the upper end of the lower punch. The wet molding apparatus further includes a non-magnetic lid that temporarily or intermittently covers the space while the slurry is being injected into the space.

[0022] In one embodiment, the wet molding apparatus includes a control device that controls operations of the upper punch, the lower punch, the die, the electromagnetic coil, and the non-magnetic lid. The control device executes the steps of forming the space with the inner wall of the through hole in the wet molding device and the upper end of the lower punch, injecting the slurry into the space and filling the space with the slurry, forming a cavity filled with the slurry by blocking the space with the lower end of the upper punch, and reducing the distance between the lower end of the upper punch and the upper end of the lower punch while applying the transverse magnetic field to the cavity in a direction perpendicular to the direction in which the lower punch moves up and down relatively, and discharging the dispersion medium contained in the slurry through the multiple discharge holes in the upper punch, thereby producing a molded body of the rare earth alloy powder, and further, while the slurry is being injected into the space, no magnetic field is applied to the space, and the space is temporarily or intermittently covered with the non-magnetic lid, and before the transverse magnetic field is applied to the cavity, the non-magnetic lid is moved from the position where it covered the space. Effect of the Invention

[0023] According to the embodiment of the present disclosure, the slurry can be uniformly supplied into the space of the die while suppressing the variation in concentration, which suppresses the variation in density and the disturbance in orientation of the powder compact, and suppresses the occurrence of cracks and fissures caused by these, thereby enabling the stable production of the desired high magnetic properties. [Brief description of the drawings]

[0024] [Figure 1] FIG. 1 is a diagram showing an example of a basic configuration of a wet molding apparatus 100 according to this embodiment. [Diagram 2] FIG. 2 is a perspective view showing a schematic configuration example of a mold 10 provided in the wet molding apparatus 100. As shown in FIG. [Diagram 3] FIG. 3 is a perspective view that illustrates a schematic example of the non-magnetic cover 34. As shown in FIG. [Figure 4]FIG. 4 is an explanatory diagram for explaining the method for producing a rare earth sintered magnet in this embodiment. [Diagram 5] FIG. 5 is an explanatory diagram for explaining the method for producing a rare earth sintered magnet in this embodiment. [Figure 6] FIG. 6 is an explanatory diagram for explaining some steps of the manufacturing method in this embodiment. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0025] As a result of their investigations, the inventors have found that by not applying a magnetic field when supplying the slurry into the space in the mold, and by applying the transverse magnetic field molding method described below after supplying the slurry, it is possible to supply the slurry evenly into the space in the mold with reduced concentration variation.

[0026] Before describing the embodiments of the present disclosure, the findings of the present inventors and the technical background thereof will be described.

[0027] There are two methods for producing powder compacts for rare earth sintered magnets: a dry compaction method in which rare earth alloy powder is pressed while it is still dry, and a wet compaction method in which a slurry of the alloy powder dispersed in a dispersion medium such as oil is fed into a die cavity and pressed. Magnetic field press compaction can be divided into a transverse magnetic field compaction method in which the direction of compression by pressing (press direction) and the direction of the magnetic field applied to the alloy powder are perpendicular, and a vertical magnetic field compaction method in which the direction of the magnetic field applied to the alloy powder is parallel to the press direction.

[0028] In the dry compaction method, the structure of the press (compacting device) is relatively simple, and there is no need for processes such as removing the dispersion medium during press compaction (removal of the dispersion medium) and removing the dispersion medium from the compact after pressing. In particular, in the transverse magnetic field compaction method, the pressing direction and the magnetic field application direction are perpendicular to each other, so that the orientation of the alloy powder oriented in the magnetic field application direction is not disturbed, and a compact with a high degree of orientation can be produced. In the vertical magnetic field compaction method, the pressing direction and the magnetic field application direction are parallel, so that the orientation of the alloy powder is easily disturbed during press compaction, and the degree of orientation is lower than that of the transverse magnetic field compaction method. Therefore, in the dry compaction method, the transverse magnetic field compaction method is mainly used, and shapes such as disks, rings, and thin plates that are difficult to form using the transverse magnetic field compaction method are mainly produced using the vertical magnetic field compaction method.

[0029] However, in the dry compaction method, it is unavoidable that the alloy powder is exposed to the air when it is supplied to the cavity and during press compaction. In addition, the compact is also exposed to the air when it is removed after the press compaction is completed. This increases the oxygen content of the compact, leading to a deterioration in magnetic properties. In addition, it is difficult to avoid large friction between the alloy powder particles or between the alloy powder and the die, so the resistance when the alloy powder rotates and is oriented by the applied magnetic field becomes large, and there is a limit to how high the orientation can be.

[0030] On the other hand, in the wet compacting method, since it is necessary to supply the slurry and remove the dispersion medium, the structure of the compacting device is relatively complicated, but the dispersion medium suppresses the oxidation of the alloy powder and the compact, and the oxygen content of the compact can be reduced. In addition, since the dispersion medium is present between the alloy powder during press compacting in a magnetic field, the alloy powder can rotate more easily in the direction of the applied magnetic field because the constraint by frictional force is weak. This allows a higher degree of orientation to be obtained. Therefore, there is an advantage that a rare earth sintered magnet with better magnetic properties can be produced than by the dry compacting method. In this way, the wet compacting method can obtain a higher degree of orientation and a better oxidation suppression effect than the dry compacting method, and the obtained rare earth sintered magnet tends to have better magnetic properties.

[0031] However, such wet compaction methods also have problems. In wet compaction methods, when a slurry is placed in a cavity and press compaction is performed in a magnetic field, it is necessary to discharge most of the dispersion medium (oil, etc.) in the slurry to the outside of the cavity. For this reason, a discharge hole for the dispersion medium is provided in at least one of the upper punch or the lower punch. Then, when the volume of the cavity decreases due to the movement of the upper punch and / or the lower punch, the dispersion medium contained in the pressurized slurry is discharged from this discharge hole. At this time, the dispersion medium in the slurry is filtered and discharged from the part close to the discharge hole, so in the initial stage of press compaction, a layer called a "cake layer" with a high density of alloy powder is formed in the part close to the discharge hole.

[0032] As the upper and / or lower punches move and the press molding progresses, more of the dispersion medium is filtered out and the cake layer area in the cavity expands. Eventually, the entire cavity layer becomes a cake layer with a high alloy powder density (low dispersion medium concentration), and a compact is obtained in which the alloy powder particles are relatively weakly bonded to each other.

[0033] In the early stage of press molding, when a cake layer is formed near the discharge hole, the direction of the magnetic field tends to bend in the horizontal magnetic field molding method. This is because the cake layer has a high density of alloy powder (a large amount of alloy powder per unit volume), and therefore has a higher magnetic permeability than the parts of the slurry other than the cake layer (parts with a small amount of alloy powder per unit volume). Therefore, the magnetic field tends to be focused on the cake layer. For this reason, even if the magnetic field is applied almost perpendicularly to the side surface of the cavity outside the cavity, the magnetic field inside the cavity is bent toward the cake layer. Therefore, since the alloy powder is oriented along this bent magnetic field, there may be a part with a bent orientation in the compact after press molding. If there is a part with a bent orientation, the degree of orientation in the compact decreases, and the rare earth sintered magnet may not have sufficient magnetic properties. This problem of the magnetic properties of the rare earth sintered magnet decreasing due to the bending of the magnetic field becomes more pronounced the larger the dimension of the cavity in the magnetic field application direction (for example, when it exceeds 15 mm or more, typically 30 mm or more). Furthermore, when the dimension of the cavity in the pressing direction is 90 mm or more, the magnetic field is significantly bent, which significantly reduces the magnetic properties of the rare earth sintered magnet and causes many cracks after sintering, making it impossible to mass-produce compacts of such large size using the wet compacting method. Therefore, in order to elongate the compact in the pressing direction, it is necessary to solve the above problems. The inventors' investigations have revealed that such problems are particularly likely to occur when the slurry concentration inside the cavity varies or when the slurry is not uniformly supplied inside the cavity.

[0034] On the other hand, in the vertical magnetic field compaction method, the magnetic field is applied in a direction parallel to the pressing direction, i.e., parallel to the direction from the upper punch to the lower punch. Therefore, even if a cake layer is formed near the dispersion medium outlet of the upper punch and / or lower punch, the magnetic field is not easily bent, and it is easy for the magnetic field to advance straight from the part without the cake layer into the cake layer. Therefore, unlike the horizontal magnetic field compaction method, there are no restrictions on the dimensions of the cavity in the direction of magnetic field application. However, in the vertical magnetic field compaction method, the particles of the alloy powder tend to rotate during press compaction, causing a disturbance in the orientation, and a high residual magnetic flux density Br It is difficult to achieve this uniformly.

[0035] Until now, compacts with large dimensions in the direction of magnetic field application have mainly been produced by the transverse magnetic field dry compaction method, but the dry compaction method increases the oxygen content of the compact, leading to a deterioration in magnetic properties and also having a limit to how high the degree of orientation can be.

[0036] According to the manufacturing method and wet molding device for rare earth sintered magnets disclosed herein, it is possible to solve the above problems of wet molding that occur when horizontal magnetic field molding is performed, and therefore it is possible to stably manufacture rare earth sintered magnets with a press direction of 90 mm or more by horizontal magnetic field molding, specifically, rare earth sintered magnets with dimensions of 90 mm length x 90 mm width x 90 mm height or more (either the length or width is the magnetic field application direction, and the height is the press direction), preferably 100 mm length x 100 mm width x 90 mm height or more. Here, "dimensions of 90 mm length x 90 mm width x 90 mm height or more" means that the vertical size is 90 mm or more, the horizontal size is 90 mm or more, and the height size is 90 mm or more. The same applies to "100 mm length x 100 mm width x 90 mm height or more". The shape of the molded body is preferably a rectangular parallelepiped. If it is a rectangular parallelepiped, it is easy to divide it into multiple molded body pieces. However, the molded body may have other shapes.

[0037] Hereinafter, embodiments of the present disclosure will be described with reference to the drawings.

[0038] <Basic configuration example> First, a basic configuration example of a wet molding apparatus in an embodiment of the present disclosure will be described with reference to Figs. 1 and 2. Fig. 1 is a diagram showing a basic configuration example of a wet molding apparatus 100 in this embodiment. Fig. 2 is a perspective view showing a schematic configuration example of a mold 10 provided in the wet molding apparatus 100. In the figure, for reference, an X-axis, a Y-axis, and a Z-axis that are perpendicular to each other are shown. The Z-axis is parallel to the vertical direction, and the Y-axis is perpendicular to the paper surface of the figure. The XY plane including the X-axis and the Y-axis is horizontal.

[0039] The wet molding apparatus 100 in this embodiment includes a mold 10 having a through hole 10H, as illustrated in FIG. 2(a), for example. The mold 10 is made of a magnetic material that transmits magnetic flux. The through hole 10H penetrates the mold 10 in the Z-axis direction from the upper end to the lower end. The through hole 10H has an inner wall 10W. The cross section of the through hole 10H perpendicular to the Z-axis has a certain shape and size along the Z-axis direction. In this example, the through hole 10H has a rectangular parallelepiped shape, but the shape of the through hole 10H is not limited to this example. The inner wall 10W of the through hole 10H is not limited to a flat surface, and may include a curved surface in part or in whole.

[0040] The shape and dimensions of the molded body to be produced depend on the shape and dimensions of the through hole 10H. For example, when the dimensions of the molded body are 100 mm long x 100 mm wide x 90 mm high, the dimensions of the cross section parallel to the XY plane of the through hole 10H can be 100 mm long or less x 100 mm wide or less. When a larger molded body is produced, for example, when the dimensions of the molded body are 150 mm long x 150 mm wide x 100 mm high or more, the dimensions of the cross section parallel to the XY plane of the through hole 10H can be 150 mm long or less x 150 mm wide or less.

[0041] 1 again, the wet molding apparatus 100 includes a lower punch 12 that moves up and down relative to the die 10 with at least its tip inserted into the through hole 10H, and an upper punch 14 that moves up and down relative to the lower punch 12. The upper punch 14 in this embodiment has a lower end 14U with a plurality of discharge holes 14H through which liquid (liquid components) contained in the slurry passes. The slurry contains, for example, an alloy powder (RTB-based alloy powder) containing a rare earth element, iron, and boron, and a dispersion medium.

[0042] In this disclosure, "up and down movement" means moving in the vertical direction. Also, "A moves up and down relative to B" means that the distance between A and B in the vertical direction increases or decreases. Therefore, the form in which the lower punch 12 moves up and down relative to the die 10 includes a case in which the lower punch 12 moves up and down while the die 10 is stationary, a case in which the die 10 moves up and down while the lower punch 12 is stationary, and a case in which the die 10 and the lower punch 12 move up and down in the same or opposite directions. In the state of FIG. 1(b), the die 10 and the upper punch 14 move down while the lower punch 12 remains stationary, compared to the state of FIG. 1(a). As a result, the lower punch 12 rises relative to the die 10.

[0043] In the state shown in FIG. 1(a), a space 16 is formed by the inner wall 10W of the through hole 10H of the mold 10 and the upper end 12T of the lower punch 12. The space 16 has a volume for receiving a slurry. The upper punch 14 is located above the space 16, but the upper surface of the space 16 is open. In other words, a part of the lower punch 12 is inserted into the lower part of the through hole 10H of the mold 10, but the space 16 is not blocked by the upper punch 14. FIG. 2(b) shows a schematic diagram of a state in which the space 16 is formed by the inner wall 10W of the through hole 10H of the mold 10 and the upper end 12T of the lower punch 12. The lower punch 12 inserted into the through hole 10H of the mold 10 and the inner wall 10W of the through hole 10H are in contact with each other in a slidable state. The inner wall 10W and the lower punch 12 are in contact with each other so that the space 16 can hold the liquid component of the slurry without leaking.

[0044] Refer to FIG. 1(b). In the state of FIG. 1(b), the lower end 14U of the upper punch 14 descends so as to press the die 10 downward. As a result, the space 16 is blocked by the upper punch 14, and a cavity is formed. In the example of FIG. 1(b), a "filter cloth" 32 is disposed between the upper punch 14 and the die 10. The filter cloth 32 is a cloth-like filter material made by weaving synthetic fibers or the like, and may be called a filter. Examples of filters include filter cloth, filter paper, porous filters, and metal filters. By providing such a filter, it is possible to more reliably prevent particles of the alloy powder from entering the discharge holes 14H and to allow only the dispersion medium to pass through. The size of the small holes present in the filter cloth 32 is determined so that almost no particles of the rare earth alloy powder pass through. Specifically, the filter cloth 32 is attached to the upper punch 14 so as to cover a plurality of discharge holes 14H provided at the lower end 14U of the upper punch 14. For simplicity, only a portion of the filter cloth is shown in the figure, but the filter cloth may be used by extending long along the X-axis direction and being wound around a roller. By rotating such a roller, it is possible to switch the portion of the filter cloth 32 that contacts the lower end 14U of the upper punch 14. As a result, it becomes easy to switch the area of ​​the filter cloth that has become soiled during the pressing process to a new area and perform the next pressing process.

[0045] In the example of Fig. 1(b), not only the upper punch 14 but also the die 10 is lowered compared to the state of Fig. 1(a). By shortening the distance between the upper end 12T of the lower punch 12 and the lower end 14U of the upper punch 14, the volume of the cavity 10C can be reduced. After filling the space 16 of Fig. 1(a) with slurry, in the process of changing to the state of Fig. 1(b), the liquid component in the slurry is discharged from the inside to the outside of the cavity 10C through the filter cloth 32 and the discharge hole 14H of the upper punch 14.

[0046] As shown in FIG. 1, the mold 10 has an injection port 10P for injecting a slurry into the space 16 formed by the inner wall 10W of the through hole 10H and the upper end 12T of the lower punch 12. The number of injection ports 10P is not limited to one, and may be multiple. The number of through holes 10H in one mold 10 is also not limited to one, and may be multiple. When one mold 10 has multiple through holes 10H, the wet molding apparatus 100 includes multiple sets of lower punches 12 assigned to the respective through holes 10H. The injection port 10P is connected to a slurry supply device (hydraulic device having a hydraulic cylinder), and the slurry 30 pressurized by a hydraulic cylinder or the like is supplied into the space 16 through the injection port 10P.

[0047] The wet molding apparatus 100 includes an electromagnetic coil 20 that applies a transverse magnetic field in a direction (horizontal transverse direction) perpendicular to the direction in which the lower punch 12 moves up and down (Z-axis direction, i.e., vertical direction) to the inside of the through-hole 10H of the die 10. In the example of FIG. 1, the electromagnetic coil 20 can form a transverse magnetic field in which the magnetic flux extends in the X-axis direction in the cavity 10C. As will be described later, in this embodiment, when the slurry is injected into the space 16 from the injection port 10P, the upper punch 14 is located away from the die 10 as shown in FIG. 1(a), and no magnetic field is applied to it.

[0048] The wet molding apparatus 100 in this embodiment further includes a "non-magnetic lid" not shown in FIG. 1. This non-magnetic lid covers the space 16 temporarily or intermittently when the slurry is injected into the space 16. FIG. 3 is a perspective view showing a schematic example of the non-magnetic lid 34. In the example of FIG. 3, the non-magnetic lid 34 completely covers the through-hole 10H of the mold 10. The dashed line in FIG. 3 shows a schematic state in which the non-magnetic lid 34 is in the retracted position. The role of the non-magnetic lid 34 will be described later.

[0049] It should be noted that the "non-magnetic lid" is not necessarily an essential element for carrying out the method for producing a rare earth sintered magnet according to the present disclosure.

[0050] The wet molding apparatus in the embodiment of the present disclosure includes a control device that controls the operations of the upper punch 14, the lower punch 12, the die 10, the electromagnetic coil 20, and the non-magnetic lid 34. Such a control device can be realized by a computer that operates according to a program stored in a storage device.

[0051] <Manufacturing method> Hereinafter, a method for producing a rare earth sintered magnet according to an embodiment of the present disclosure will be described with reference to Fig. 4 and Fig. 5. Fig. 4 is an explanatory diagram for explaining the method for producing a rare earth sintered magnet according to the present embodiment. Fig. 5 is an explanatory diagram for explaining the method for producing a rare earth sintered magnet according to the present embodiment. In Fig. 4, the electromagnetic coil 20 is omitted.

[0052] In the method for producing a rare earth sintered magnet in this embodiment, the following steps are carried out.

[0053] (1): Preparation of slurry For example, a step of preparing a slurry containing an alloy powder containing a rare earth element (preferably an alloy powder containing a rare earth element, iron, and boron) and a dispersion medium is carried out.

[0054] Alloy powder composition The composition of the alloy powder may have the composition of known rare earth sintered magnets including, for example, RTB sintered magnets (R is at least one rare earth element (a concept including yttrium (Y)), T is iron (Fe) or iron and cobalt (Co), and B is boron) and samarium-cobalt sintered magnets.

[0055] RTB sintered magnets are preferred because they have the highest magnetic energy product among all types of magnets and are relatively inexpensive.

[0056] A preferred composition of the RTB based sintered magnet is shown below.

[0057] R is selected from at least one of Nd, Pr, Dy, and Tb. However, R preferably includes either Nd or Pr. More preferably, a combination of rare earth elements represented by Nd-Dy, Nd-Tb, Nd-Pr-Dy, or Nd-Pr-Tb is used.

[0058] Among R, Dy and Tb are particularly cJ In addition to the above elements, a small amount of other rare earth elements such as Ce or La may be contained, and misch metal or didymium may also be used. R does not have to be a pure element, and may contain impurities that are unavoidable during production within the range available industrially. The content may be any content that has been known in the past, and is preferably in the range of 25% by mass or more and 35% by mass or less, for example. If it is less than 25% by mass, high magnetic properties, particularly high H cJ If it exceeds 35 mass%, B r This is because there is a possibility that the

[0059] T contains iron (including the case where T is substantially composed of iron), and up to 50% by mass of iron may be replaced with cobalt (Co) (including the case where T is substantially composed of iron and cobalt). Co is effective for improving temperature characteristics and corrosion resistance, and the alloy powder may contain up to 10% by mass of Co. The content of T may be the remainder of R and B, or R, B, and M described below.

[0060] The content of B may be a known content, and for example, a preferable range is 0.8% by mass to 1.2% by mass. cJ If it exceeds 1.2 mass%, B may not be obtained. r The B content may decrease. A part of the B may be substituted with C (carbon). Substitution with C may improve the corrosion resistance of the magnet. When the total content is B+C (containing both B and C), the number of C substituted atoms is converted into the number of B atoms, and it is preferable that the total content is set within the above B concentration range.

[0061] In addition to the above elements, H cJIn order to improve the properties, an M element can be added. The M element is one or more selected from the group consisting of Al, Si, Ti, V, Cr, Mn, Ni, Cu, Zn, Ga, Zr, Nb, Mo, In, Sn, Hf, Ta and W. The amount of the M element added is preferably 5.0 mass% or less. If it exceeds 5.0 mass%, the B r In addition, unavoidable impurities can be tolerated.

[0062] ·Method of manufacturing alloy powder The alloy powder is produced, for example, by producing an ingot or flakes of a raw alloy for rare earth magnets (preferably a raw alloy for RTB magnets) having the desired composition by a melting method, and then causing the alloy ingot and flakes to absorb (occlude) hydrogen, thereby performing hydrogen pulverization to produce a coarsely pulverized powder.

[0063] The coarsely pulverized powder can then be further pulverized using a jet mill or the like to produce a fine powder (alloy powder).

[0064] A method for producing a raw alloy for an RTB magnet will be described below.

[0065] An alloy ingot can be produced by an ingot casting method in which metals previously adjusted to the final required composition are melted and placed in a mold.

[0066] Additionally, alloy flakes can be produced by a quenching method, such as a strip casting method or a centrifugal casting method, in which a molten alloy is quenched by contacting it with a single roll, twin rolls, a rotating disk, or a rotating cylindrical mold, to produce a solidified alloy that is thinner than an alloy produced by an ingot method.

[0067] In the present invention, alloys produced by either the ingot method or the quenching method can be used, but alloys produced by the quenching method are preferred.

[0068] The thickness of the raw alloy for RTB magnets (quenched alloy) produced by the quenching method is usually in the range of 0.03 mm to 10 mm, and it is in the form of flakes or plates. The molten alloy starts to solidify from the surface that comes into contact with the cooling roll (roll contact surface), and crystals grow columnarly from the roll contact surface in the thickness direction. Compared to alloys (ingot alloys) produced by the conventional ingot casting method (mold casting method), quenched alloys are cooled in a short time, so the structure is finer and the crystal grain size is smaller. In addition, the area of ​​the grain boundaries is large. Since the R-rich phase spreads widely within the grain boundaries, the quenching method has excellent dispersion of the R-rich phase.

[0069] For this reason, the alloy is prone to fracture at the grain boundaries when subjected to hydrogen pulverization. By subjecting the quenched alloy to hydrogen pulverization, the size of the hydrogen pulverized powder (coarsely pulverized powder) can be reduced to, for example, 1.0 mm or less.

[0070] The coarsely pulverized powder thus obtained can be pulverized by a jet mill or the like to obtain a D 50 It is possible to produce RT-B alloy powder with a particle size of 2 to 7 μm.

[0071] The jet mill is preferably carried out in (a) an atmosphere of nitrogen gas and / or argon gas (Ar gas) with an oxygen content of substantially 0% by mass, or (b) an atmosphere of nitrogen gas and / or Ar gas with an oxygen content of 0.005 to 0.5% by mass.

[0072] In order to control the amount of nitrogen in the resulting sintered body, it is more preferable to use Ar gas as the atmosphere inside the jet mill and introduce a small amount of nitrogen gas therein to adjust the concentration of nitrogen gas in the Ar gas.

[0073] ·Dispersion medium The dispersion medium is a liquid in which the alloy powder can be dispersed to produce a slurry.

[0074] The preferred dispersion medium for use in the present invention includes mineral oils and synthetic oils.

[0075] The type of mineral oil or synthetic oil is not limited, but if the kinetic viscosity at room temperature exceeds 10 cst, the increased viscosity will strengthen the bonding force between the alloy powder particles, which may have an adverse effect on the orientation of the alloy powder during wet compaction in a magnetic field.

[0076] For this reason, the kinetic viscosity of the mineral oil or synthetic oil at room temperature is preferably 10 cst or less. If the fractional point of the mineral oil or synthetic oil exceeds 400°C, it becomes difficult to remove the oil after obtaining the compact, and the amount of residual carbon in the sintered body increases, which may result in a deterioration of the magnetic properties.

[0077] Therefore, the fractional point of the mineral oil or synthetic oil is preferably 400° C. or lower.

[0078] Vegetable oil may also be used as the dispersion medium. Vegetable oil refers to oil extracted from plants, and the type of plant is not limited to a specific plant. Examples of the oil include soybean oil, rapeseed oil, corn oil, safflower oil, and sunflower oil.

[0079] - Preparation of slurry The obtained alloy powder is mixed with a dispersion medium to prepare a slurry.

[0080] The mixing ratio of the alloy powder and the dispersion medium is not particularly limited, but the concentration of the alloy powder in the slurry is preferably 70% or more (i.e., 70% by mass or more) in terms of mass ratio. 3 This is because at a flow rate of 1000 / sec, the alloy powder can be efficiently supplied into the space and excellent magnetic properties can be obtained.

[0081] Moreover, the concentration of the alloy powder in the slurry is preferably 90% or less in terms of mass ratio in order to reliably ensure the fluidity of the slurry.

[0082] More preferably, the concentration of the alloy powder in the slurry is 75% to 88% by mass. This is because the alloy powder can be supplied more efficiently and the fluidity of the slurry can be more reliably ensured. Even more preferably, the concentration of the alloy powder in the slurry is 84% ​​or more by mass. The method of mixing the alloy powder and the dispersion medium is not particularly limited. The alloy powder and the dispersion medium may be prepared separately, and the alloy powder and the dispersion medium may be weighed and mixed in a predetermined amount. In addition, when preparing the alloy powder by dry-pulverizing the coarsely pulverized powder with a jet mill or the like, a container containing the dispersion medium may be placed at the alloy powder outlet of the pulverizing device such as a jet mill, and the alloy powder obtained by pulverization may be directly collected in the dispersion medium in the container to obtain a slurry. In this case, it is preferable that the atmosphere inside the container is also made of nitrogen gas and / or argon gas, and the obtained alloy powder is directly collected in the dispersion medium without being exposed to the air to obtain a slurry. Furthermore, it is also possible to wet-pulverize the coarsely pulverized powder in the dispersion medium using a vibration mill, ball mill, attritor, or the like to prepare a slurry consisting of the alloy powder and the dispersion medium.

[0083] (2): Pressurized injection of slurry 4(a) and 4(b), from a state in which a lower punch 12 is inserted into a through hole 10H of a mold 10 in a wet molding apparatus 100, the mold 10 is raised to form a space 16 between an inner wall 10W and an upper end 12T of the lower punch 12. As shown in FIG. 4(b), when the mold 10 has been sufficiently raised, the inside of the space 16 communicates with an injection port 10P of the mold 10.

[0084] Next, as shown in FIG. 4(c), the slurry 30 is injected into the space 16 through the injection port 10P. The supply amount of the slurry 30 is, for example, 20 to 150 cm 3 / sec. The feed rate can be set in the range of 20 cm 3 If the flow rate is less than 150 cm3 / sec, it is difficult to adjust the flow rate, and the slurry may not be able to be supplied into the space 16 due to piping resistance. 3If the rate exceeds 1 / sec, the density of each part of the powder compact will vary, and the compact may crack when it is removed from the press or may crack due to shrinkage during sintering. Also, the possibility of disturbance of orientation in the vicinity of the injection port 10P increases.

[0085] The amount of slurry supplied is preferably 30 to 100 cm 3 / sec, more preferably 40 to 80 cm 3 The slurry supply amount can be controlled by adjusting the flow rate control valve of the hydraulic device functioning as a slurry supply device to change the flow rate of oil fed to the hydraulic cylinder of the hydraulic device, thereby changing the speed of the hydraulic cylinder. The supply pressure of the slurry 30 is, for example, 1.96 MPa to 14.71 MPa (20 kgf / cm 2 ~150kgf / cm 2 The injection port 10P for the slurry 30 is a hole having a diameter of, for example, 2 mm to 30 mm.

[0086] One of the features of this embodiment is that while the slurry 30 is being injected into the space 16, the space 16 is temporarily or intermittently covered with a non-magnetic lid .

[0087] By using the non-magnetic lid 34, the slurry 30 can be uniformly supplied to the space 16 while suppressing the variation in concentration. This makes it possible to suppress the disturbance of the orientation in the powder compact produced by compressing it in the subsequent aligning magnetic field. This will be described in detail below.

[0088] Usually, when the slurry 30 is poured into the space 16 without using a non-magnetic cover, the space 16 is covered by the upper punch 14. When the space 16 is filled with the slurry 30 in such a normal manner, at least a part of the slurry 30 on the upper surface of the space 16 may come into contact with the multiple discharge holes 14H of the upper punch 14 or the filter cloth 32 arranged between the upper punch 14 and the die 10, and the dispersion medium contained in the slurry 30 may be absorbed. As a result, the concentration of the slurry at a position close to the upper punch 14 in the space 16 may become high, causing concentration variations. In addition, even if a magnetic field is applied after the slurry is poured, the powder particles in the slurry 30 on the upper surface of the space 16 are difficult to be oriented. In addition, if the space 16 is not covered by the upper punch or the like, the slurry 30 may fly out of the space 16 due to the pouring of the slurry 30, or the upper surface of the slurry may become uneven, causing concentration variations, or the slurry may not be supplied to the cavity uniformly. In contrast, by covering the space 16 with the non-magnetic lid 34, even if the space 16 is filled with the slurry 30 and at least a portion of the slurry 30 comes into contact with the non-magnetic lid 34, the dispersion medium contained in the slurry is not absorbed by the non-magnetic lid 34. Furthermore, since the space 16 is covered with the non-magnetic lid 34, the slurry 30 does not fly out of the space 16 when the slurry is injected, and no unevenness is formed on the upper surface of the slurry. Therefore, it is possible to uniformly supply the slurry 30 to the space 16 while suppressing concentration variations. This makes it possible to suppress density variations and orientation disturbances in the powder compact.

[0089] The non-magnetic lid 34 is made of, for example, rubber or resin. The non-magnetic lid 34 made of rubber can be tightly attached to the upper end of the mold 10. The non-magnetic lid 34 can be made of, for example, silicon, non-magnetic aluminum, stainless steel, or the like, other than rubber. The non-magnetic lid 34 does not have a through hole for passing the slurry 30. This is because the dispersion medium contained in the slurry 30 may be absorbed into the through hole, causing concentration variations. Furthermore, if the non-magnetic lid 34 is not non-magnetic, the lid may become magnetic during the transverse magnetic field pressing process or the like, causing the slurry 30 to adhere to the lid. This may result in the slurry 30 not being supplied to the space 16 while suppressing concentration variations.

[0090] As mentioned above, the non-magnetic lid 34 is not necessarily an essential element for carrying out the method for producing a rare earth sintered magnet according to the present disclosure. If the slurry 30 is poured into the space 16 without using the non-magnetic lid 34 and then stirred using, for example, a rod-shaped member, the concentration variation of the slurry 30 can be reduced and the uniformity can be increased. Furthermore, the slurry 30 is particularly unlikely to enter the four corners of the space 16. Therefore, for example, the concentration variation of the slurry 30 can also be reduced by pouring the slurry 30 until it overflows from the space 16.

[0091] 4(d) shows a schematic diagram of a state in which the non-magnetic lid 34 is slightly raised from the die 10 so that the space 16 is in communication with the atmosphere, forming a gap between them. Through this gap, the atmospheric components contained inside the space 16 are pushed out as the amount of the slurry 30 increases. By forming intermittent gaps between the non-magnetic lid 34 and the die 10, the pressure inside the space 16 can be maintained at approximately atmospheric pressure, making it possible to smoothly supply the slurry 30.

[0092] 4(e) shows the state in which the space 16 has been filled with the slurry 30. At this time, the space 16 is closed with the non-magnetic lid 34, and the amount of the slurry 30 filled has reached a predetermined value. If the slurry 30 is supplied to the space 16 without the non-magnetic lid 34, as described above, there is a possibility that unevenness will be formed on the upper surface of the slurry 30 when it is filled. The non-magnetic lid 34 makes it possible to fill the interior of the space 16, which has a desired volume, with the slurry 30.

[0093] The timing for closing the space 16 with the non-magnetic lid 34 is, for example, when about half of the space 16 is filled with the slurry 30. Thereafter, as the amount of slurry 30 supplied to the space 16 increases, the internal pressure of the space 16 rises, and the non-magnetic lid 34 is lifted once or multiple times to reduce the internal pressure to a level equal to atmospheric pressure. This operation can be achieved, for example, by attaching the top surface of the non-magnetic lid 34 to a cylinder and mechanically or electrically driving the cylinder in the vertical direction.

[0094] When the interior of the space 16 is filled with a predetermined amount of the slurry 30, the space 16 is closed by the non-magnetic lid 34. At this time, it is desirable that the slurry 30 be in contact with the bottom surface of the non-magnetic lid 34, but a small gap (less than 1 mm) may exist in some parts.

[0095] Another characteristic feature of this embodiment is that no magnetic field is applied to the space 16 when the slurry 30 is injected into the space 16 (non-magnetic field injection). If the slurry is injected while a magnetic field is being applied (magnetic field injection), there is a possibility that the density of each part of the powder compact obtained after pressing will vary greatly. This is considered to be due to the fact that, when the slurry 30 is being injected, the alloy powder in the slurry is attracted to the die 10 or the lower punch 12, causing the solid alloy powder and the liquid dispersion medium to separate (solid-liquid separation), and the separated dispersion medium gathers around the space 16. If the slurry 30 is supplied in this state and the inside of the space 16 is filled with the slurry 30 and then press-molded, the press molding will be performed in a state in which the density of the alloy powder (the amount of alloy powder present per unit volume) is lower around the cavity 10C than at the center and bottom of the cavity 10C. As a result, there is a possibility that the density of the upper and surrounding parts of the obtained compact will be lower than that of the center and bottom. If the density differs in each part of the molded body, the magnetic properties of the sintered magnet obtained by sintering the molded body will decrease and vary depending on the location. In addition, if there is such a density variation, cracks may occur in the molded body when it is removed after press molding, and even if there are no cracks in the molded body, cracks may occur due to shrinkage during sintering. In this embodiment, since a magnetic field is not applied when the slurry is supplied, it is possible to solve the problem of such density variation. In the past, it was thought that in order to obtain high magnetic properties, it was necessary to inject the slurry while a magnetic field is applied. This is because, compared to injection in a magnetic field, injection in a non-magnetic field makes it difficult to orient the center part of the magnet. However, as a result of the study by the inventors, it was found that if the slurry 30 is supplied to the space 16 while suppressing the concentration variation by the method using the non-magnetic cover described above, and then the horizontal magnetic field molding method is applied, the center part of the magnet is also uniformly oriented and the magnetic properties do not decrease. On the other hand, if the vertical magnetic field molding method is applied, the magnetic properties decrease due to the influence of the disturbance of the orientation caused by the press molding.

[0096] Preferably, after filling the space 16 with the slurry, as shown in FIG. 4(f), the lower punch 12 is lowered relative to the die 10 so that when the upper punch 14 is lowered as shown in FIG. 5(a) to close the space 16, a gap is formed between the lower end of the upper punch 14 or between the filter cloth (if a filter cloth 32 is used) and the slurry 30. Specifically, the position of the lower punch 12 is lowered relative to the die 10 by a distance of 1 mm to 30 mm (e.g., 3 mm). As a result, after the filling of the slurry 30 is completed, the space 16 expands and an air layer gap is formed in the upper part of the space 16. The size of the gap is preferably 2 mm to 4 mm, and may be, for example, about 3 mm. In the example of FIG. 4(f), the die 10 is raised relative to the lower punch 12, but the method of forming such an air layer gap on the upper surface of the slurry 30 is not limited to this example. For example, the lower punch 12 may be lowered with the die 10 in a fixed position. Also, a "spigot structure" of a size and shape that fits into the through-hole 10H of the mold 10 may be formed on the lower surface of the non-magnetic lid 34. Specifically, the non-magnetic lid 34 is retracted from the position covering the mold 10 before or after forming the air layer gap (FIG. 3). That is, the non-magnetic lid 34 is moved from the position covering the space 16 before the transverse magnetic field is applied to the cavity 10C.

[0097] In the state of Fig. 4(f), the upper punch 14 is located away from the die 10, but the upper punch 14 may start to descend as the die 10 starts to rise. The important point is to ensure that the filter cloth 32 provided at the lower end of the upper punch 14 does not come into contact with the slurry 30 even if the upper punch 14 starts to descend when the die 10 starts to rise or immediately before that. If the upper punch 14 is separated from the die 10, the filter cloth 32 will not come into contact with the slurry 30.

[0098] (3): Preparation before starting press forming in a transverse magnetic field Next, the space 16 is closed with the lower end 14U of the upper punch 14 to form a cavity 10C filled with the slurry 30. Specifically, as shown in FIG. 5(a), the upper punch 14 is lowered relative to the die 10 to close the space 16. At this time, the filter cloth 32 is disposed between the die 10 and the upper punch 14, but as described above, it is preferable to form an air gap between the filter cloth 32 and the slurry 30 so that the filter cloth 32 does not come into contact with the slurry 30. This reliably prevents the filter cloth 32 from coming into contact with the slurry 30 before the application of the magnetic field, causing the dispersion medium contained in the slurry 30 to be absorbed by the filter cloth 32, and the concentration of the alloy powder near the upper surface of the slurry 30 to increase excessively, causing concentration variations, or preventing the powder particles from being easily oriented even when a magnetic field is applied.

[0099] (4): Press molding in a transverse magnetic field Next, while a "transverse magnetic field" perpendicular to the direction in which the lower punch 12 moves up and down is applied to the cavity 10C, the distance between the lower end 14U of the upper punch 14 and the upper end 12T of the lower punch 12 is reduced. Figures 5(b) and 5(c) show how the distance between the lower end 14U of the upper punch 14 and the upper end 12T of the lower punch 12 is reduced. The dispersion medium contained in the slurry 30 is discharged through the multiple discharge holes 14H in the upper punch 14, and a compact 50 of the alloy powder is obtained. The magnitude of the magnetic field formed inside the cavity 10C is, for example, 1.0T or more and 1.5T or less. When the transverse magnetic field is applied, it is preferable that a gap G of an air layer exists between the filter cloth 32 and the slurry 30. When the application of the transverse magnetic field is started, some of the alloy powder particles contained in the slurry 30 are moved by the magnetic force, and a convex or concave portion may be formed on the upper surface of the slurry 30. However, since the direction of the magnetic field is horizontal and perpendicular to the pressing direction, the orientation direction is aligned by the pressing process.

[0100] If the strength of the magnetic field is 1.0 T or more, the magnetization direction of the alloy powder contained in the slurry 30 is more reliably oriented in the direction of the magnetic field, and a high degree of orientation is obtained. If the strength is less than 1.0 T, the degree of orientation of the alloy powder decreases, or the orientation of the alloy powder is easily disturbed during press molding. The strength of the magnetic field inside the cavity 10C can be measured with a gauss meter or obtained by magnetic field analysis.

[0101] The electromagnetic coil 20 is disposed near the side surface of the die 10 and is capable of forming a uniform magnetic field perpendicular to the pressing direction within the cavity 10C.

[0102] The state inside the cavity 10C will be described in more detail. When the volume of the cavity 10C decreases during the magnetic field press molding process, as described above, the dispersion medium in the slurry 30 is filtered and discharged through the discharge hole 14H from the portion close to the discharge hole 14H of the upper punch 14, but the alloy powder contained in the slurry 30 remains in the cavity 10C. Therefore, a "cake layer" is formed from the portion close to the discharge hole 14H. As described above, the cake layer is a layer in which the dispersion medium in the slurry is discharged to the outside of the cavity 10C and the concentration of the alloy powder is increased. As the pressing process progresses, the cake layer eventually spreads throughout the cavity 10C, and a powder compact in which the particles of the alloy powder are in contact with each other is obtained. In this embodiment, when the application of the transverse magnetic field is started, the cake layer is not formed, and as a result, the disturbance of the orientation at the position close to the upper punch 14 can be suppressed.

[0103] After the green body 50 is formed, the die 10 is lowered as shown in Fig. 5(d) to expose the green body 50 to the outside of the die 10 as shown in Fig. 5(e). Thereafter, the upper punch 14 is raised as shown in Fig. 5(f), making it possible to remove the green body 50.

[0104] The green body obtained by the above-mentioned process has residual dispersion medium such as mineral oil or synthetic oil. If the green body in this state is suddenly heated from room temperature to a sintering temperature of, for example, 950 to 1150 ° C, the internal temperature of the green body will rise suddenly, and the residual dispersion medium in the green body and the rare earth element of the green body may react to generate rare earth carbide. If rare earth carbide is formed in this way, the generation of a sufficient amount of liquid phase for sintering may be prevented, and a sintered body with sufficient density may not be obtained, resulting in a deterioration of magnetic properties. For this reason, it is preferable to perform a deoiling treatment on the green body before sintering. This is because the residual dispersion medium in the green body can be sufficiently removed.

[0105] (5): Step of dividing the molded body into pieces (first dividing step) In this embodiment, the green body produced by the press molding in a transverse magnetic field may be divided into a plurality of green body pieces. For example, after the step of producing the green body described above and before the step of sintering the green body, a first division step of cutting each green body and dividing it into 10 or more green body pieces can be performed.

[0106] In this embodiment, for example, a molded body having a length of 100 mm, a width of 100 mm, and a height of 90 mm can be sliced ​​into plate-shaped molded body pieces having a length of 9.5 mm (in the magnetization direction) x a width of 100 mm, and a height of 90 mm by using a wire saw. The number, size, and shape of the molded body pieces are not limited to this example. Also, cutting may be performed using a known cutting blade instead of the wire saw.

[0107] The larger the dimensions of the green body, the more sintered magnets can be produced from one green body. In conventional methods, the larger the green body, the more the density of the slurry varies, making it difficult to increase the size. According to the embodiment of the present disclosure, it is possible to make the dimensions of the green body 90 mm or more in length, 90 mm or more in width, and 90 mm or more in height (preferably 100 mm or more, 100 mm or more in width, and 90 mm or more in height, more preferably 120 mm or more in length, 120 mm or more in width, and 100 mm or more in height, and most preferably 150 mm or more in length, 150 mm or more in width, and 100 mm or more in height).

[0108] (6): Sintering process (sintered body material preparation process) Next, the green body (the cut green body piece) is sintered to produce a rare earth sintered magnet body. In this disclosure, when the sintered green body of the green body piece is further cut, the sintered green body of the green body piece is referred to as a "sintered body material." Hereinafter, the green body piece may be simply referred to as a "green body" for simplicity.

[0109] The compact is preferably sintered at a pressure of 0.13 Pa (10 -3 Torr) or less, preferably 0.07 Pa (5.0 x 10 -4 The sintering is carried out under a pressure of 0.1 MPa (0.2 Torr) or less at a temperature in the range of 1000°C to 1150°C. To prevent oxidation due to sintering, residual gas in the atmosphere may be replaced with an inert gas such as helium or argon. The dimensions of the sintered body obtained by sintering the compact pieces may be, for example, 4 mm or more in the vertical direction, 40 mm or more in the horizontal direction, and 5 mm or more in the height direction.

[0110] (7): Step of dividing into sintered pieces (second dividing step) In this embodiment, a second division step is performed in which each sintered body material obtained by sintering the green compact pieces is cut to divide each sintered body material into a plurality of sintered body pieces. This second division step makes it possible to produce 100 or more sintered body pieces from one sintered body material. The sintered body material can be cut using, for example, a dicing saw. According to this embodiment, more than 1000 (=10×100) rare earth sintered magnets can be produced from one large green compact (length 90 mm or more, width 90 mm or more, height 90 mm or more), improving mass productivity.

[0111] In this embodiment, a diffusion step may be further performed on the sintered body material before cutting, in which the heavy rare earth element RH (RH is at least one of Tb, Dy, and Ho) is diffused from the surface to the inside. Diffusion of the heavy rare earth element RH from the surface to the inside of the sintered body can efficiently increase the coercive force. Such a diffusion step is particularly effective when the sintered body material has a plate-like shape with a thickness of 1 mm to 20 mm. By diffusing from two surfaces facing each other in the thickness direction, it is possible to efficiently diffuse the heavy rare earth element RH deep inside the sintered body material. If the heavy rare earth element RH is diffused after the sintered body material is divided into sintered body pieces, the amount of the heavy rare earth element RH consumed to obtain the required magnetic properties tends to increase. For this reason, it is preferable to diffuse the heavy rare earth element RH on the sintered body material before it is divided into sintered body pieces.

[0112] With reference to Fig. 6, the process flow from the cutting step of the green body pieces to the cutting step of the sintered body material in a preferred embodiment can be summarized as follows. In Fig. 6, the direction of the aligning magnetic field (magnetic field orientation direction) M is indicated by an arrow. Ultimately, the magnetization is performed in a direction parallel to the magnetic field orientation direction M.

[0113] The process flow is shown diagrammatically in FIG. A step (S10) of preparing a molded body 50; A step (S20) of cutting the molded body 50 and dividing the molded body 50 into a plurality of molded body pieces 52; a sintering step (S30) of sintering each of the plurality of compact pieces 52 to produce a plurality of sintered bodies 54; a step (S40) of bringing a powder 56 of a diffusion source containing a heavy rare earth element RH into contact with at least one of the upper surface 54a and the lower surface 54b in the thickness direction of each sintered body material 54 and performing a heat treatment, thereby diffusing at least a part of R contained in the powder of the diffusion source from the upper surface 54a and / or the lower surface 54b of each sintered body material to the inside; A step (S50) of dividing each sintered body material 54 into a plurality of sintered body pieces 58 by cutting from the upper surface 54a to the lower surface 54b; Includes.

[0114] After the sintering step, the sintered body (including the sintered body material or sintered body pieces) is preferably subjected to a heat treatment at a temperature lower than the sintering temperature. The magnetic properties can be improved by the heat treatment. Known conditions can be adopted for the heat treatment temperature, heat treatment time, and other heat treatment conditions. The rare earth sintered magnet body thus obtained is, for example, subjected to a grinding / polishing step, a surface treatment / coating step, as necessary, and then subjected to a magnetization step to complete the final rare earth sintered magnet. EXAMPLES

[0115] Example 1 The composition is Nd 22 Pr6Dy3B 0.94 Co2Al 0.25 Cu 0.1 The raw alloy was melted in a high-frequency melting furnace so that the balance was Fe (mass%), and the molten raw alloy was then quenched by strip casting to obtain flakes of the alloy with a thickness of 0.5 mm. The alloy was coarsely crushed by a hydrogen crushing method and further finely crushed by a jet mill. The particle size D of the obtained RTB alloy powder was 50 The RTB alloy powder was immersed in a nitrogen atmosphere in a mineral oil having a distillation point of 250° C. and a kinetic viscosity of 2 cSt at room temperature to prepare a slurry. The slurry concentration was 85% by mass.

[0116] For the wet molding, a wet molding apparatus shown in FIG. 1 was used. The mold 10 used had a space 16 with dimensions of 100 mm in length and 100 mm in width (in the direction of magnetic field application). The depth of the space 16 was 90 mm. A slurry supply device was used to supply a slurry with a slurry concentration of 85% by mass and a slurry supply rate of 50 cm. 3 Slurry was supplied from supply port 15 to space 16 at 1 / sec. Then, when the inside of space 16 was filled about half with slurry 30, space 16 was covered with non-magnetic lid 34. Thereafter, as the amount of slurry 30 supplied to space 16 increased, non-magnetic lid 34 was lifted multiple times by a cylinder (not shown) to maintain the internal pressure at a level equal to atmospheric pressure. After space 16 was filled with slurry, non-magnetic lid 34 was removed from space 16.

[0117] Thereafter, as shown in Fig. 4(f), the position of the lower punch 12 was lowered by 3 mm relative to the die 10 in order to form a gap between the filter cloth 32 and the slurry 30 when the upper punch 14 was lowered. Next, as shown in Fig. 5(a), the upper punch 14 was lowered relative to the die 10 to close the space 16 and form a cavity 10C. Then, a magnetic field of 1.5 T was applied inside the cavity 10C in the lateral direction (100 mm direction) of the cavity 10C to reduce the distance between the lower end 14U of the upper punch 14 and the upper end 12T of the lower punch 12, and press molding was performed in the lateral magnetic field.

[0118] The density of the molded body produced under these conditions was measured at 17 different positions, and the variance was 0.04 g / cm 3 was a sufficiently low value.

[0119] Next, before the step of sintering each compact, each of these compacts was cut by wire machining and divided into 20 compact pieces.

[0120] The obtained molded pieces were heated in a vacuum from room temperature to 150°C at a rate of 1.5°C / min, held at that temperature for 1 hour, then heated to 500°C at a rate of 1.5°C / min to remove the mineral oil in the molded pieces, and further heated from 500°C to 1100°C at a rate of 20°C / min, held at 1100°C for 2 hours for sintering. In this way, sintered body materials were obtained from each molded piece. It was confirmed that the obtained sintered body had no cracks. After this, a process was carried out to divide the sintered body material into 200 sintered body pieces.

[0121] The obtained sintered pieces were heat-treated at 900°C for 1 hour, and then further heat-treated at 600°C for 1 hour to obtain RTB-based sintered magnets. The obtained RTB-based sintered magnets were machined to have dimensions of 7 x 7 x 7 (mm), and the magnetic properties of 10 pieces were measured using a BH tracer. r By subtracting the minimum value from the maximum value of B r The variation was found to be a sufficiently low value of 0.011T.

[0122] Example 2 The composition is Nd 30.1 Pr 0.5 Dy 1.0 B 1.0 Co 1.0 Al 0.1 Cu 0.1 The raw alloy was melted in a high-frequency melting furnace so that the balance was Fe (mass%), and the molten raw alloy was then quenched by strip casting to obtain flakes of the alloy with a thickness of 0.5 mm. The alloy was coarsely crushed by a hydrogen crushing method and further finely crushed by a jet mill. The particle size D of the obtained RTB alloy powder was 50 The RTB alloy powder was immersed in a nitrogen atmosphere in a mineral oil having a distillation point of 250° C. and a kinetic viscosity of 2 cSt at room temperature to prepare a slurry. The slurry concentration was 85% by mass.

[0123] For the wet molding, a wet molding apparatus shown in FIG. 1 was used. The mold 10 used had a space 16 with dimensions of 90 mm in length and 100 mm in width (in the direction of magnetic field application). The depth of the space 16 was 85 mm. A slurry supply device was used to supply a slurry with a slurry concentration of 85% by mass and a slurry supply rate of 50 cm. 3 Slurry was supplied from supply port 15 to space 16 at 1 / sec. Then, when the inside of space 16 was filled about half with slurry 30, space 16 was covered with non-magnetic lid 34. Thereafter, as the amount of slurry 30 supplied to space 16 increased, non-magnetic lid 34 was lifted multiple times by a cylinder (not shown) to maintain the internal pressure at a level equal to atmospheric pressure. After space 16 was filled with slurry, non-magnetic lid 34 was removed from space 16.

[0124] Thereafter, as shown in Fig. 4(f), the position of the lower punch 12 was lowered by 3 mm relative to the die 10 in order to form a gap between the filter cloth 32 and the slurry 30. Next, as shown in Fig. 5(a), the upper punch 14 was lowered relative to the die 10 to close the space 16 and form a cavity 10C. Then, a magnetic field of 1.5 T was applied inside the cavity 10C in the lateral direction (100 mm direction) of the cavity 10C, and the distance between the lower end 14U of the upper punch 14 and the upper end 12T of the lower punch 12 was reduced to perform press molding in a lateral magnetic field (condition A).

[0125] For comparison, press molding in a vertical magnetic field was performed under the same conditions as in Condition A, except that the magnetic field was applied in the depth direction (85 mm direction) (Condition B). Furthermore, press molding in a horizontal magnetic field was performed under the same conditions, except that the non-magnetic cover 34 was not used and the space 16 was covered with the upper punch (Condition C).

[0126] Under these conditions A, B and C, 200 pieces of each molded body were produced. The obtained molded body was heated in a vacuum from room temperature to 150°C at a rate of 1.5°C / min, held at 1100°C for 1 hour, and then heated to 500°C at a rate of 1.5°C / min to remove the mineral oil in the molded body. The temperature was then raised from 500°C to 1100°C at a rate of 20°C / min and held at that temperature for 2 hours for sintering. The obtained sintered body was heat treated at 900°C for 1 hour, and then further heat treated at 600°C for 1 hour to obtain an RTB-based sintered magnet. The obtained RTB-based sintered magnet was machined to a size of 7 x 7 x 7 (mm), and the magnetic properties were measured using a BH tracer. 200 pieces of each of conditions A, B and C were produced. r and H cJ The results are shown in Table 1. r By subtracting the minimum value from the maximum value of B r Measured H cJ By subtracting the minimum value from the maximum value of H cJ The variance was calculated, and the results are also shown in Table 1.

[0127] [Table 1]

[0128] As shown in Table 1, the present invention example is B r and H cJ The variation in the magnetic properties is small, and high magnetic properties can be stably produced. r is significantly decreased, and condition C is B compared to the present invention example (condition B). r and H cJ There is a large variation. [Industrial Applicability]

[0129] The manufacturing method and wet molding apparatus for rare earth sintered magnets disclosed herein are suitable for use in manufacturing rare earth sintered magnets with reduced oxygen concentration. Such rare earth sintered magnets can be used in voice coil motors (VCMs) for hard disk drives, motors for electric vehicles (EVs, HVs, PHVs, etc.), various motors such as motors for industrial equipment, and home appliances. [Explanation of symbols]

[0130] 10... mold, 10H... through hole, 10W... inner wall, 12... lower punch, 12T... upper end of lower punch, 14... upper punch, 14H... discharge hole of upper punch, 14U... lower end of upper punch, 20... electromagnetic coil, 16... space, 30... slurry, 100... wet molding device

Claims

1. a step of preparing a wet molding apparatus comprising: a die having a through hole; a lower punch which moves up and down relative to the die with at least its tip inserted into the through hole; and an upper punch which moves up and down relative to the lower punch, the upper punch having a lower end with a plurality of discharge holes for passing a liquid therethrough; a cavity being formed inside the through hole by the upper end of the lower punch and the lower end of the upper punch; and a volume of the cavity being reduced by reducing the distance between the upper end of the lower punch and the lower end of the upper punch; A step of preparing a slurry containing an alloy powder containing a rare earth element and a dispersion medium; forming a space between an inner wall of the through hole in the wet molding apparatus and the upper end of the lower punch, and injecting the slurry into the space to fill the space with the slurry; closing the space with the lower end of the upper punch to form the cavity filled with the slurry; a step of reducing a distance between the lower end of the upper punch and the upper end of the lower punch while applying a transverse magnetic field to the cavity in a direction perpendicular to a direction in which the lower punch moves up and down relative to the cavity, and discharging the dispersion medium contained in the slurry through the multiple discharge holes in the upper punch, thereby producing a compact of the alloy powder; sintering the compact; Including, When the slurry is being injected into the space, no magnetic field is applied to the space, and the space is temporarily or intermittently covered with a non-magnetic lid; Prior to applying the transverse magnetic field to the cavity, the non-magnetic lid is moved from its position covering the space. A method for producing sintered rare earth magnets.

2. In the step of producing a compact of the alloy powder while reducing the distance between the lower end of the upper punch and the upper end of the lower punch, a filter cloth or a filter is disposed between the slurry in the cavity and the lower end of the upper punch. A method for producing the rare earth sintered magnet according to claim 1.

3. After filling the space with the slurry, the non-magnetic lid is moved from its position covering the space; The method includes a step of forming a gap between the slurry and at least one of the lower end of the upper punch and the filter cloth by lowering the lower punch relative to the die before starting application of the transverse magnetic field. A method for producing a rare earth sintered magnet according to claim 1 or 2.

4. The size of the gap is 2 mm or more and 4 mm or less. A method for producing the rare earth sintered magnet according to claim 3.

5. After filling the space with the slurry, the non-magnetic lid is moved from its position covering the space; application of the transverse magnetic field is started before starting to discharge the dispersion medium contained in the slurry through the multiple discharge holes in the upper punch; A method for producing a rare earth sintered magnet according to any one of claims 1 to 4.

6. When the slurry is injected into the space, the non-magnetic lid is moved up and down to temporarily connect the inside of the space to the outside. A method for producing a rare earth sintered magnet according to any one of claims 1 to 5.

7. 7. The method for producing a rare earth sintered magnet according to claim 1, wherein the concentration of said alloy powder in said slurry at the time of pouring is 75 to 88 mass %.

8. A wet compaction apparatus for producing a compact of rare earth alloy powder, comprising: A mold having a through hole; a lower punch that moves up and down relative to the die with at least a tip end of the lower punch inserted into the through hole; an upper punch that moves up and down relative to the lower punch, the upper punch having a lower end with a plurality of drain holes for allowing liquid to pass therethrough; an electromagnetic coil that applies a transverse magnetic field to the inside of the through hole of the die in a direction perpendicular to the direction in which the lower punch moves up and down relatively; Equipped with the die has an injection port for injecting a slurry containing the rare earth alloy powder into a space formed by an inner wall of the through hole and an upper end of the lower punch, The wet molding apparatus further comprises: a non-magnetic lid that temporarily or intermittently covers the space while the slurry is being injected into the space; Wet molding equipment.

9. The wet molding apparatus includes: A control device is provided for controlling the operations of the upper punch, the lower punch, the die, the electromagnetic coil, and the non-magnetic cover, The control device includes: forming a space between the inner wall of the through hole in the wet molding apparatus and the upper end of the lower punch, and injecting the slurry into the space to fill the space with the slurry; closing the space with the lower end of the upper punch to form a cavity filled with the slurry; a step of reducing a distance between the lower end of the upper punch and the upper end of the lower punch and discharging a dispersion medium contained in the slurry through the multiple discharge holes in the upper punch while applying the transverse magnetic field to the cavity in a direction perpendicular to a direction in which the lower punch moves up and down relatively; and Run Furthermore, while the slurry is being injected into the space, no magnetic field is applied to the space, and the space is temporarily or intermittently covered with the non-magnetic lid; before applying the transverse magnetic field to the cavity, the non-magnetic lid is moved from a position covering the space; The wet molding apparatus according to claim 8.